KR102470778B1 - Thermoplastic polyester elastomer resin composition, method for preparing thereof and molding products comprising the composition - Google Patents
Thermoplastic polyester elastomer resin composition, method for preparing thereof and molding products comprising the composition Download PDFInfo
- Publication number
- KR102470778B1 KR102470778B1 KR1020180163102A KR20180163102A KR102470778B1 KR 102470778 B1 KR102470778 B1 KR 102470778B1 KR 1020180163102 A KR1020180163102 A KR 1020180163102A KR 20180163102 A KR20180163102 A KR 20180163102A KR 102470778 B1 KR102470778 B1 KR 102470778B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- thermoplastic polyester
- polyester elastomer
- elastomer resin
- parts
- Prior art date
Abstract
본 발명은 열가소성 폴리에스테르 엘라스토머 수지 조성물, 이의 제조방법 및 이를 포함하는 성형품에 관한 것으로 보다 상세하게는 활제로서 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지 중에 선택된 1종 이상을 첨가하여 열가소성 폴리에스테르 엘라스토머 수지와의 상용성을 높여 표면 품질이 개선된 이점을 제공하며 이에 더하여 내마찰성, 내스크래치성, 내소음성이 크게 향상됨에 따라 자동차의 등속조인트 부츠에 요구되는 물성을 제공할 수 있는 열가소성 폴리에스테르 엘라스토머 수지 조성물, 이의 제조방법 및 이를 포함하는 성형품에 관한 것이다. The present invention relates to a thermoplastic polyester elastomer resin composition, a method for preparing the same, and a molded product including the same, and more particularly, by adding at least one selected from a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin as a lubricant to obtain a thermoplastic polyester Thermoplastic polyester that provides the advantage of improved surface quality by increasing compatibility with elastomer resin, and in addition, greatly improves friction resistance, scratch resistance, and noise resistance, which can provide the physical properties required for automobile constant velocity joint boots It relates to an elastomeric resin composition, a method for preparing the same, and a molded article including the same.
Description
본 발명은 열가소성 폴리에스테르 엘라스토머 수지 조성물, 이의 제조방법 및 이를 포함하는 성형품에 관한 것으로, 보다 상세하게는 특정 활제 및 보조 활제를 함께 처방하여 표면 품질을 개선시키고, 내마찰성, 내스크래치성, 내소음성이 크게 향상되어 자동차의 등속조인트 부츠용 소재로 활용할 수 있는 열가소성 폴리에스테르 엘라스토머 수지 조성물 등에 관한 것이다. The present invention relates to a thermoplastic polyester elastomer resin composition, a method for preparing the same, and a molded product including the same, and more particularly, by prescribing a specific lubricant and an auxiliary lubricant together to improve surface quality, abrasion resistance, scratch resistance, and noise resistance This is greatly improved and relates to a thermoplastic polyester elastomer resin composition that can be utilized as a material for constant velocity joint boots of automobiles.
자동차 기술이 점점 고도화되면서 부품은 모듈화 되어 가고 있다. 특히 전륜구동(Front Engine Front Drive, FF) 방식 차량의 경우 전륜의 모듈에서 가속 및 감속, 충격의 흡수, 조향 등의 여러가지 기능을 담당하게 된다. 차량의 엔진에서 발생한 힘이 직접적으로 바퀴에 작용하게 되면 바퀴를 통해 흡수된 충격이 모두 엔진으로 전달되어 내구성에 심각한 손상을 초래하게 된다. 이때 필요로 하는 장치가 등속조인트(Constant velocity joint, CVJ)이며, 이는 엔진에서 발생한 힘이 출력축을 통해 변속기에 전달되고, 변속기에 전달된 이 힘을 각 바퀴에 서로 다른 축을 통해서 균일하게 전달하여 양쪽 바퀴가 등속으로 회전할 수 있도록 한다. 등속조인트는 등속성을 확보하기 위해 내부 구성 부품이 일정 위치에 있도록 설정되어 있고, 그 기능을 확보하도록 내부 구성 부품간 마찰이 쉼 없이 일어나 내부에서 열이 발생하며, 이러한 내부의 열이 일정 온도 이상 상승하는 것을 방지하고 내부 구성 부품들의 정해진 운동을 원활하게 하기 위해 윤활제로써 그리스(Grease)가 도포된다. As automobile technology becomes more advanced, parts are being modularized. In particular, in the case of a front engine front drive (FF) type vehicle, the front wheel module takes charge of various functions such as acceleration and deceleration, shock absorption, and steering. When the force generated from the engine of a vehicle directly acts on the wheels, all shocks absorbed through the wheels are transmitted to the engine, resulting in serious damage to durability. The device required at this time is a constant velocity joint (CVJ), which transmits the force generated from the engine to the transmission through the output shaft, and evenly transmits this force transmitted to the transmission through different shafts to each wheel, Allows the wheel to turn at a constant speed. The constant velocity joint is set so that the internal components are in a certain position to secure constant velocity, and friction between the internal components is constantly generated to generate internal heat to secure its function, and this internal heat is generated over a certain temperature. Grease is applied as a lubricant to prevent it from rising and to facilitate the predetermined movement of internal components.
상기와 같이 등속조인트에서 발생하는 열을 견디면서 그리스의 유출을 막는 기본 기능과 함께 외부 이물질로부터 보호하는 역할을 수행하는 내부 구성 부품이 등속조인트 부츠(CVJ boots)이다. 이는 바퀴로 힘을 전달하는 과정에서 함께 회전하며, 이때 부츠의 주름에서 면과 면 사이의 마찰이 발생하여 소음을 유발한다. 또한, 노면으로부터 차량 하부로 물, 염수(염화칼슘 등), 모래 등의 각종 이물질이 유입되어 부츠가 오염되면, 90dB 이상의 큰 소음이 발생할 수 있다. As described above, the constant velocity joint boots (CVJ boots) are internal components that perform a role of protecting from external foreign substances along with the basic function of preventing leakage of grease while enduring heat generated from the constant velocity joint. It rotates together in the process of transmitting power to the wheel, and at this time, friction occurs between surfaces in the creases of the boots, causing noise. In addition, if various foreign substances such as water, salt water (calcium chloride, etc.), sand, etc. flow into the lower part of the vehicle from the road surface and the boot is contaminated, a loud noise of 90 dB or more may be generated.
한편, 등속조인트 부츠 소재로 과거에는 클로로프로펜 고무와 같은 가교 고무가 사용되었으나, 차량의 경량화 및 친환경화 추세에 부합하여 비중이 낮고 재활용이 용이한 열가소성 폴리에스테르 엘라스토머 수지로 대체되어 사용되고 있으며, 내마찰성, 내스크래치성, 내소음성 등을 확보하기 위해 폴리에스테르 엘라스토머 수지에 활제를 컴파운딩하여 등속조인트 부츠를 제조한다. On the other hand, cross-linked rubber such as chloropropene rubber was used in the past as a material for constant velocity joint boots, but it is being replaced with thermoplastic polyester elastomer resin, which has a low specific gravity and is easy to recycle, in line with the trend of weight reduction and eco-friendliness of vehicles. , In order to secure scratch resistance and noise resistance, a lubricant is compounded with polyester elastomer resin to manufacture constant velocity joint boots.
그러나, 종래 알려진 에틸렌 비스 아미드 등의 아미드계 활제, 몬탄계 왁스, 폴리에틸렌 등의 올레핀계 왁스는 균일하게 분산되지 않아 물성의 균일성을 기대하기 어렵고, 활제가 성형품 외부로 마이그레이션(이행)되어 표면 불량 현상이 발생하기 쉬우며, 소음 개선 효과가 미비하였다. 또한, 상용성이 떨어져 소량 첨가하여도 등속조인트 부츠의 내열성, 기계적 강도 등의 물성을 저하시키는 문제점이 있었다.However, conventionally known amide-based lubricants such as ethylene bisamide, montan-based waxes, and olefin-based waxes such as polyethylene are not uniformly dispersed, making it difficult to expect uniformity of physical properties. The phenomenon is easy to occur, and the noise improvement effect is insufficient. In addition, there is a problem in that physical properties such as heat resistance and mechanical strength of constant velocity joint boots are deteriorated even when a small amount is added due to poor compatibility.
최근 깨끗하고 매끄러운 표면에 대한 요구와, 회전 시 발생하는 소재 간의 마찰로 인한 소음 및 이물질 유입으로 인한 소음 저하에 대한 요구가 더욱 증가하고 있으며, 따라서 표면 품질이 우수하면서도 보다 우수한 내마찰성 및 내소음성을 제공할 수 있는 열가소성 폴리에스테르 엘라스토머 수지에 대한 기술 개발이 시급한 실정이다.Recently, the demand for a clean and smooth surface and the demand for noise reduction due to friction between materials generated during rotation and noise reduction due to the inflow of foreign substances are increasing. There is an urgent need to develop technologies for thermoplastic polyester elastomer resins that can be provided.
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 특정한 활제 처방으로 활제와 수지 간의 상용성을 높여 물성을 저하시키지 않으면서도 외관이 매끄럽고 효과적으로 내마찰성 및 내소음성을 향상시킬 수 있는 열가소성 폴리에스테르 엘라스토머 수지 조성물을 제공하는 것을 목적으로 한다. In order to solve the problems of the prior art as described above, the present invention is a thermoplastic polyester elastomer that has a smooth appearance without deteriorating physical properties by increasing the compatibility between the lubricant and the resin with a specific lubricant formulation and can effectively improve friction resistance and noise resistance. It aims at providing a resin composition.
또한, 본 발명은 상기 열가소성 폴리에스테르 엘라스토머 수지 조성물의 제조방법 및 이를 포함하는 성형품을 제공하는 것을 목적으로 하며, 이를 등속조인트 부츠 소재로 사용하여 종래 대비 고품질의 등속조인트 부츠를 제공하는데 기여하고자 한다. In addition, an object of the present invention is to provide a method for manufacturing the thermoplastic polyester elastomer resin composition and a molded product including the same, and to contribute to providing a high-quality constant-velocity joint boot compared to the prior art by using it as a constant-velocity joint boot material.
본 발명의 상기 목적 및 기타 목적들은 하기 설명된 본 발명에 의하여 모두 달성될 수 있다.The above and other objects of the present invention can all be achieved by the present invention described below.
상기의 목적을 달성하기 위하여, 본 발명은 열가소성 폴리에스테르 엘라스토머 수지 100중량부에, 활제 1 내지 3중량부, 보조 활제 0.5 내지 1.5중량부 및 사슬연장제 1 내지 6중량부를 포함하되, 상기 활제는 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 것을 특징으로 하는 열가소성 폴리에스테르 엘라스토머 수지 조성물을 제공한다. In order to achieve the above object, the present invention includes 100 parts by weight of thermoplastic polyester elastomer resin, 1 to 3 parts by weight of a lubricant, 0.5 to 1.5 parts by weight of an auxiliary lubricant, and 1 to 6 parts by weight of a chain extender, wherein the lubricant is A thermoplastic polyester elastomer resin composition comprising a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin is provided.
또한, 본 발명은 열가소성 폴리에스테르 엘라스토머 수지 100중량부에, 활제 1 내지 3중량부, 보조 활제 0.5 내지 1.5중량부 및 사슬연장제 1 내지 6중량부를 포함하여 혼련 및 압출하는 단계를 포함하되, 상기 활제는 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 것을 특징으로 하는 열가소성 폴리에스테르 엘라스토머 수지 조성물의 제조방법을 제공하는 것을 목적으로 한다. In addition, the present invention includes the steps of kneading and extruding by including 100 parts by weight of thermoplastic polyester elastomer resin, 1 to 3 parts by weight of a lubricant, 0.5 to 1.5 parts by weight of an auxiliary lubricant, and 1 to 6 parts by weight of a chain extender, An object of the present invention is to provide a method for producing a thermoplastic polyester elastomer resin composition, wherein the lubricant comprises a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin.
또한, 본 발명은 상기 열가소성 폴리에스테르 엘라스토머 수지 조성물을 포함하는 것을 특징으로 하는 성형품을 제공하는 것을 목적으로 한다. Another object of the present invention is to provide a molded article characterized by comprising the thermoplastic polyester elastomer resin composition.
본 발명에 따른 열가소성 폴리에스테르 엘라스토머 수지 조성물은 수지와의 상용성이 우수한 특정 활제를 포함하여 물성을 저하시키지 않으면서도 표면이 매끄러워 외관품질이 우수하면서도 내마찰성, 내스크래치성 및 내소음성이 크게 향상된 열가소성 폴리에스테르 엘라스토머 수지 조성물을 제공한다. The thermoplastic polyester elastomer resin composition according to the present invention includes a specific lubricant having excellent compatibility with the resin, so that the surface is smooth without deteriorating physical properties, so the surface quality is excellent, and the friction resistance, scratch resistance, and noise resistance are greatly improved. A thermoplastic polyester elastomer resin composition is provided.
또한, 본 발명의 열가소성 폴리에스테르 엘라스토머 수지 조성물을 포함하는 성형품은 등속조인트 부츠의 요구되는 물성을 충족하면서 종래 대비 향상된 내마찰성, 내스크래치성, 내소음성을 제공할 수 있어 등속조인트 부츠로 활용되어 이의 품질 향상에 크게 기여할 수 있다. In addition, the molded article comprising the thermoplastic polyester elastomer resin composition of the present invention can provide improved friction resistance, scratch resistance, and noise resistance compared to the prior art while satisfying the required physical properties of constant velocity joint boots, and is used as constant velocity joint boots. It can greatly contribute to quality improvement.
도 1은 본 발명의 일실시예에 따른 열가소성 폴리에스테르 엘라스토머 수지 조성물로 제조된 등속조인트 부츠가 등속조인트에 장착된 것을 보여주는 사진이다. 1 is a photograph showing that a constant velocity joint boot made of a thermoplastic polyester elastomer resin composition according to an embodiment of the present invention is mounted on a constant velocity joint.
이하 본 기재의 열가소성 폴리에스테르 엘라스토머 수지 조성물에 대해 상세하게 설명하기로 한다. Hereinafter, the thermoplastic polyester elastomer resin composition of the present disclosure will be described in detail.
본 발명자들은 상술한 종래기술의 문제점을 해소하기 위해, 열가소성 폴리에스테르 엘라스토머 수지에, 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 활제를 특정 함량 범위 내로 배합하고, 이에 보조 활제 및 사슬연장제를 특정 함량 범위 내로 첨가하여 수지 조성물을 제조할 경우, 물성을 저하시키지 않으면서도 표면이 매끄러워 외관품질이 우수하면서도 내마찰성, 내스크래치성 및 내소음성이 크게 향상되는 것을 확인하고 이를 토대로 더욱 매진하여 본 발명을 완성하였다. In order to solve the problems of the prior art, the inventors of the present invention blended a thermoplastic polyester elastomer resin with a lubricant containing a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin within a specific content range, thereby adding an auxiliary lubricant and a chain. When the resin composition is prepared by adding an extender within a specific content range, it is confirmed that the surface is smooth without deteriorating the physical properties and the appearance quality is excellent, and the friction resistance, scratch resistance, and noise resistance are greatly improved. Sold out to complete the present invention.
본 발명의 열가소성 폴리에스테르 엘라스토머 수지 조성물은 일례로, 열가소성 폴리에스테르 엘라스토머 수지 100중량부에, 활제 1 내지 3중량부, 보조 활제 0.5 내지 1.5중량부 및 사슬연장제 1 내지 6중량부를 포함하되, 상기 활제는 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 것을 특징으로 하며, 내마찰성 및 내소음성이 뛰어나 등속조인트 부츠 소재로서 적합한 물성을 제공한다. The thermoplastic polyester elastomer resin composition of the present invention includes, for example, 100 parts by weight of the thermoplastic polyester elastomer resin, 1 to 3 parts by weight of a lubricant, 0.5 to 1.5 parts by weight of an auxiliary lubricant, and 1 to 6 parts by weight of a chain extender, The lubricant is characterized in that it includes a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin, and has excellent friction resistance and noise resistance, providing suitable physical properties as a constant velocity joint boot material.
본 기재의 조성물은 일례로 열안정제, 광안정제, 페닐렌 비스 옥사졸린, 카본 블랙 등으로부터 선택된 1종 이상을 더 포함할 수 있다. The composition of the present substrate may further include at least one selected from, for example, a heat stabilizer, a light stabilizer, phenylene bisoxazoline, carbon black, and the like.
이하 본 기재의 수지 조성물을 구성하는 각 구성 성분별로 구체적으로 설명하기로 한다. Hereinafter, each constituent component constituting the resin composition of the present disclosure will be described in detail.
열가소성 폴리에스테르 엘라스토머 수지 Thermoplastic Polyester Elastomer Resin
상기 열가소성 폴리에스테르 엘라스토머 수지는 방향족 디카르복실산 또는 이의 에스테르 형성 유도체와 지방족 디올로부터 형성된 결정성 하드 세그먼트와, 폴리알킬렌 옥사이드로부터 형성된 연질 소프트 세그먼트를 포함하는 열가소성 탄성 중합체이다. The thermoplastic polyester elastomer resin is a thermoplastic elastomer comprising a crystalline hard segment formed from an aromatic dicarboxylic acid or an ester-forming derivative thereof and an aliphatic diol, and a soft soft segment formed from polyalkylene oxide.
상기 결정성 하드 세그먼트 및 연질 소프트 세그먼트는 일례로 랜덤하게 배열될 수 있다. The crystalline hard segment and the soft soft segment may be randomly arranged, for example.
상기 열가소성 폴리에스테르 엘라스토머 수지는 일례로 방향족 디카르복실산 또는 이의 에스테르 형성 유도체, 지방족 디올 및 폴리알킬렌 옥사이드를 용융 중합하여 제조된 것일 수 있으며, 이 경우 유연성, 기계적 강도 및 내열성 등이 높고 밸런스가 우수한 이점을 제공할 수 있다. For example, the thermoplastic polyester elastomer resin may be prepared by melt polymerization of an aromatic dicarboxylic acid or an ester-forming derivative thereof, an aliphatic diol, and a polyalkylene oxide. It can provide great benefits.
상기 열가소성 폴리에스테르 엘라스토머 수지는 상기 융융 중합으로 제조된 수지를 추가로 고상 중합하여 제조된 것일 수 있으며, 이 경우 유연성, 기계적 강도 및 내열성 등의 물성 밸런스가 우수하면서도 성형성이 더욱 우수한 이점을 제공한다. The thermoplastic polyester elastomer resin may be prepared by further solid-state polymerization of the resin prepared by the melt polymerization, and in this case, the balance of physical properties such as flexibility, mechanical strength and heat resistance is excellent, while providing further excellent moldability. .
상기 방향족 디카르복실산은 일례로 테레프탈산, 이소프탈산, 2,6-나프탈렌 디카르복실산, 1,5-나프탈렌 디카르복실산 및 1,4-사이클로헥산 디카르복실산 중에서 선택된 1종 이상일 수 있고, 바람직하게는 테레프탈산 또는 이소프탈산 중에서 선택될 수 있다. The aromatic dicarboxylic acid may be, for example, at least one selected from terephthalic acid, isophthalic acid, 2,6-naphthalene dicarboxylic acid, 1,5-naphthalene dicarboxylic acid, and 1,4-cyclohexane dicarboxylic acid, and , preferably terephthalic acid or isophthalic acid.
상기 방향족 디카르복실산의 에스테르 형성 유도체는 일례로 디메틸 테레프탈레이트, 디메틸 이소프탈레이트, 2,6-디메틸 나프탈렌 디카르복실레이트 및 디메틸 1,4-사이클로헥산 디카르복실레이트 중에서 선택된 1종 이상일 수 있고, 바람직하게는 디메틸 테레프탈레이트 또는 디메틸 이소프탈레이트 중에서 선택될 수 있다. The ester-forming derivative of the aromatic dicarboxylic acid may be, for example, at least one selected from dimethyl terephthalate, dimethyl isophthalate, 2,6-dimethyl naphthalene dicarboxylate, and dimethyl 1,4-cyclohexane dicarboxylate, , preferably dimethyl terephthalate or dimethyl isophthalate.
상기 방향족 디카르복실산 또는 이의 에스테르 형성 유도체는 상기 열가소성 폴리에스테르 엘라스토머 수지 총 중량에 대하여 25 내지 70중량%로 포함될 수 있고, 바람직하게는 45 내지 65중량% 또는 40 내지 70중량%로 포함될 수 있으며, 이 범위 내에서 반응 밸런스가 우수하여 반응이 용이하고 물성 밸런스가 우수한 이점을 제공한다. The aromatic dicarboxylic acid or its ester-forming derivative may be included in 25 to 70% by weight, preferably 45 to 65% by weight or 40 to 70% by weight based on the total weight of the thermoplastic polyester elastomer resin, , The reaction balance is excellent within this range, so the reaction is easy and the physical property balance is excellent.
상기 지방족 디올은 일례로 수평균분자량이 300g/mol 이하 또는 62 내지 300g/mol인 디올일 수 있고, 바람직하게는 에틸렌 글리콜, 프로필렌 글리콜, 1,2-프로판디올, 1,3-프로판디올, 1,4-부탄디올, 1,5-펜탄디올, 1,6-헥산디올 및 1,4-사이클로헥산디메탄올 중에서 선택된 1종 이상일 수 있으며, 더욱 바람직하게는 1,4-부탄디올일 수 있다. The aliphatic diol may be, for example, a diol having a number average molecular weight of 300 g/mol or less or 62 to 300 g/mol, and preferably ethylene glycol, propylene glycol, 1,2-propanediol, 1,3-propanediol, 1 It may be at least one selected from 4-butanediol, 1,5-pentanediol, 1,6-hexanediol, and 1,4-cyclohexanedimethanol, and more preferably 1,4-butanediol.
본 기재에서 지방족 디올의 수평균분자량은 특별한 언급이 없는 한 일례로 시료를 테트라하이드로퓨란에 녹인 뒤, 겔투과크로마토그래피(GPC)법으로 40℃에서 측정할 수 있고, 이때 폴리스티렌을 표준 물질로 사용할 수 있다. In this description, unless otherwise specified, the number average molecular weight of the aliphatic diol can be measured at 40 ° C. by gel permeation chromatography (GPC) after dissolving the sample in tetrahydrofuran as an example, at which time polystyrene is used as a standard material. can
상기 지방족 디올은 일례로 상기 열가소성 폴리에스테르 엘라스토머 수지 총 중량에 대하여 20 내지 40중량% 또는 25 내지 35중량%로 포함될 수 있으며, 이 범위 내에서 반응이 원활하게 진행될 수 있고 유연성, 기계적 강도 등의 물성 밸런스가 우수하다. The aliphatic diol may be included, for example, in an amount of 20 to 40% by weight or 25 to 35% by weight based on the total weight of the thermoplastic polyester elastomer resin, and the reaction may proceed smoothly within this range, and physical properties such as flexibility and mechanical strength The balance is excellent.
상기 폴리알킬렌 옥사이드는 지방족 폴리에스테르로 연질 소프트 세그먼트로서, 일례로 폴리에틸렌 글리콜, 폴리프로필렌 글리콜, 폴리테트라메틸렌 에테르 글리콜, 폴리헥사메틸렌 글리콜, 에틸렌 옥사이드와 프로필렌 옥사이드의 공중합체, 폴리프로필렌 글리콜의 에틸렌 옥사이드 부가 중합체 및 에틸렌 옥사이드와 테트라하이드로퓨란의 공중합체 중에서 선택된 1종 이상일 수 있으며, 바람직하게는 폴리테트라메틸렌 글리콜일 수 있다. The polyalkylene oxide is an aliphatic polyester as a soft soft segment, for example, polyethylene glycol, polypropylene glycol, polytetramethylene ether glycol, polyhexamethylene glycol, copolymers of ethylene oxide and propylene oxide, ethylene oxide of polypropylene glycol It may be at least one selected from an addition polymer and a copolymer of ethylene oxide and tetrahydrofuran, preferably polytetramethylene glycol.
상기 폴리알킬렌 옥사이드는 일례로 상기 열가소성 폴리에스테르 엘라스토머 수지 총 중량에 대하여 10 내지 50중량%, 15 내지 45중량% 또는 10 내지 40중량%로 포함될 수 있으며, 이 범위 내에서 유연성이 우수하면서도 기계적인 강도 및 내열성이 우수하여 물성 밸런스가 뛰어나다. The polyalkylene oxide may be included, for example, in an amount of 10 to 50% by weight, 15 to 45% by weight, or 10 to 40% by weight based on the total weight of the thermoplastic polyester elastomer resin. Excellent strength and heat resistance, excellent physical property balance.
상기 폴리알킬렌 옥사이드는 수평균분자량이 일례로 600 내지 3000g/mol 또는 1000 내지 2000g/mol인 것이 바람직하며, 이 범위 내에서 중합 반응이 안정적이며 물성 밸런스가 우수한 열가소성 폴리에스테르 엘라스토머 수지를 수득할 수 있다. The polyalkylene oxide preferably has a number average molecular weight of, for example, 600 to 3000 g/mol or 1000 to 2000 g/mol, and within this range, a thermoplastic polyester elastomer resin having a stable polymerization reaction and excellent physical property balance can be obtained. have.
상기 폴리알킬렌 옥사이드의 수평균분자량은 특별한 언급이 없는 한 일례로 시료를 테트라하이드로퓨란에 녹인 뒤, 겔투과크로마토그래피(GPC)법으로 40℃에서 측정할 수 있고, 이때 폴리스티렌을 표준 물질로 사용할 수 있다. Unless otherwise specified, the number average molecular weight of the polyalkylene oxide may be measured at 40° C. by gel permeation chromatography (GPC) after dissolving the sample in tetrahydrofuran, for example, unless otherwise specified. In this case, polystyrene is used as a standard material. can
상기 열가소성 폴리에스테르 엘라스토머 수지는 용융지수(230℃, 2.16kg)가 일례로 0.5 내지 10g/10min 또는 0.5 내지 6g/10min일 수 있으며, 이 범위 내에서 성형성이 우수한 이점이 있다. The thermoplastic polyester elastomer resin may have a melt index (230° C., 2.16 kg) of, for example, 0.5 to 10 g/10 min or 0.5 to 6 g/10 min, and has excellent moldability within this range.
본 기재에서 특별한 언급이 없는 한 용융지수는 ASTM D1238에 명시된 방법에 따라 230℃, 하중 2.16kg 조건하에 측정할 수 있다. Unless otherwise specified in this description, the melt index can be measured under the conditions of 230 ° C. and a load of 2.16 kg according to the method specified in ASTM D1238.
상기 열가소성 폴리에스테르 엘라스토머 수지는 일례로 쇼어 경도가 30D 내지 50D, 35D 내지 47D 또는 35D 내지 40D일 수 있으며, 이 범위 내에서 조성물의 유연성 및 기계적인 강도가 우수하다. The thermoplastic polyester elastomer resin may have a shore hardness of, for example, 30D to 50D, 35D to 47D, or 35D to 40D, and within this range, the composition has excellent flexibility and mechanical strength.
본 기재에서 특별한 언급이 없는 한 쇼어 경도는 ASTM D2240(D 타입)에 명시된 방법에 따라 측정할 수 있다. Shore hardness can be measured according to the method specified in ASTM D2240 (Type D) unless otherwise specified in the present description.
활제lubricant
본 기재의 활제는 엘라스토머 수지와의 상용성을 높여 기존 활제의 마이그레이션 현상에 의한 표면 불량 현상을 저감하고, 내마찰성 및 내소음성을 개선하기 위한 목적으로 사용된다. The lubricant of the present substrate is used for the purpose of improving compatibility with the elastomer resin, reducing surface defects caused by migration of existing lubricants, and improving friction resistance and noise resistance.
상기 활제는 폴리에스테르 변성 실록산 수지, 폴리올레핀 변성 방향족 비닐계 수지 또는 이들 모두일 수 있으며, 이를 첨가할 경우 최종품의 표면이 매끄러워 외관이 우수하면서도 내마찰성 및 내소음성이 효과적으로 개선되는 이점을 제공한다. The lubricant may be a polyester-modified siloxane resin, a polyolefin-modified aromatic vinyl-based resin, or both, and when added thereto, the surface of the final product is smooth and the appearance is excellent, while friction resistance and noise resistance are effectively improved.
상기 활제는 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 1 내지 3중량부, 1.5 내지 3중량부, 1.8 내지 2.5중량부 또는 2 내지 2.5중량부로 포함될 수 있으며, 이 범위 내에서 최종품의 외관 품질이 우수하면서도 물성이 높게 유지되고 내마찰성, 내소음성이 크게 개선될 수 있다. The lubricant may be included in an amount of, for example, 1 to 3 parts by weight, 1.5 to 3 parts by weight, 1.8 to 2.5 parts by weight, or 2 to 2.5 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin. While excellent, physical properties are maintained high, and friction resistance and noise resistance can be greatly improved.
상기 폴리에스테르 변성 실록산 수지는 일례로 주사슬이 폴리디메틸실록산이며, 상기 폴리디메틸실록산의 유기기(organic group)가 폴리에스테르로 치환되어, 폴리디메틸실록산을 주사슬로하고, 폴리에스테르를 곁사슬로서 포함할 수 있으며, 이 경우 폴리에스테르 엘라스토머 수지와의 상용성이 우수하여 조성물의 물성을 저하시키지 않으면서 외관 품질, 내마찰성 및 내소음성이 효과적으로 개선되는 이점을 제공한다. The polyester-modified siloxane resin is, for example, a main chain of which is polydimethylsiloxane, and an organic group of the polydimethylsiloxane is substituted with polyester to include polydimethylsiloxane as a main chain and polyester as a side chain. In this case, it has excellent compatibility with the polyester elastomer resin, so that the appearance quality, friction resistance and noise resistance are effectively improved without deteriorating the physical properties of the composition.
상기 폴리에스테르 변성 실록산 수지는 일례로 융점이 50 내지 55℃, 바람직하게는 53 내지 55℃일 수 있고 이 범위 내에서 내마찰성, 내스크래치성, 내소음성이 우수하다. The polyester-modified siloxane resin may have a melting point of, for example, 50 to 55° C., preferably 53 to 55° C., and within this range, it has excellent abrasion resistance, scratch resistance, and noise resistance.
본 기재에서 융점은 시차주사 열량계(DSC)를 이용하여 측정할 수 있다. In the present description, the melting point can be measured using a differential scanning calorimeter (DSC).
상기 폴리에스테르 변성 실록산 수지는 다른 일례로 말단에 하이드록시기를 갖는 폴리에스테르 변성 실록산 수지일 수 있다. As another example, the polyester-modified siloxane resin may be a polyester-modified siloxane resin having a hydroxyl group at the terminal.
상기 폴리올레핀 변성 방향족 비닐계 수지는 일례로 폴리올레핀과 방향족 비닐계 수지의 그라프트 공중합체일 수 있다. The polyolefin-modified aromatic vinyl-based resin may be, for example, a graft copolymer of polyolefin and aromatic vinyl-based resin.
상기 폴리올레핀 변성 방향족 비닐계 수지는 다른 일례로 폴리올레핀을 주사슬로하고, 방향족 비닐계 수지를 곁사슬로서 포함하는 수지일 수 있다. As another example, the polyolefin-modified aromatic vinyl-based resin may be a resin including a polyolefin as a main chain and an aromatic vinyl-based resin as a side chain.
상기 폴리올레핀은 일례로 폴리에틸렌일 수 있고, 바람직한 일례로 저밀도 폴리에틸렌일 수 있으며, 이 경우 조성물의 물성을 저하시키지 않으면서 외관 품질, 내마찰성 및 내소음성이 효과적으로 개선되는 이점을 제공한다. The polyolefin may be, for example, polyethylene, and may be, for example, low-density polyethylene, and in this case, the appearance quality, friction resistance and noise resistance are effectively improved without degrading the physical properties of the composition.
본 기재에서 저밀도 폴리에틸렌은 일례로 밀도가 0.94g/cm3 미만 또는 0.91 내지 0.94 g/cm3인 폴리에틸렌을 의미한다.In the present disclosure, low-density polyethylene means, for example, polyethylene having a density of less than 0.94 g/cm 3 or 0.91 to 0.94 g/cm 3 .
상기 방향족 비닐계 수지는 일례로 방향족 비닐 화합물의 호모 중합체; 또는 방향족 비닐 화합물과 비닐시안 화합물을 포함하는 공중합체 중에서 선택될 수 있다. The aromatic vinyl-based resin may be, for example, a homopolymer of an aromatic vinyl compound; or a copolymer containing an aromatic vinyl compound and a vinyl cyan compound.
상기 방향족 비닐 화합물은 일례로 스티렌, 알파 메틸스티렌, 비닐 톨루엔 등으로부터 선택된 1종 이상일 수 있으며 바람직하게는 스티렌일 수 있다. The aromatic vinyl compound may be, for example, at least one selected from styrene, alpha methyl styrene, vinyl toluene, and the like, and may be preferably styrene.
상기 비닐시안 화합물은 일례로 아크릴로니트릴, 에타크릴로니트릴, 메타크릴로니트릴 중에서 선택된 1종 이상일 수 있으며, 바람직하게는 아크릴로니트릴일 수 있다.The vinyl cyanide compound may be, for example, at least one selected from acrylonitrile, ethacrylonitrile, and methacrylonitrile, preferably acrylonitrile.
상기 폴리올레핀 변성 방향족 비닐계 수지는 일례로 폴리에틸렌 변성 방향족 비닐계 수지일 수 있으며, 이 경우 조성물의 물성을 저하시키지 않으면서 외관품질, 내마찰성 및 내소음성이 효과적으로 개선될 수 있다. The polyolefin-modified aromatic vinyl-based resin may be, for example, a polyethylene-modified aromatic vinyl-based resin, and in this case, appearance quality, friction resistance, and noise resistance can be effectively improved without deteriorating physical properties of the composition.
보다 바람직한 일례로 상기 폴리올레핀 변성 방향족 비닐계 수지는 저밀도 폴리에틸렌 변성 스티렌-아크릴로니트릴 공중합체일 수 있으며, 이 경우 조성물의 물성을 저하시키지 않으면서 외관품질, 내마찰성 및 내소음성이 효과적으로 개선될 수 있다. As a more preferred example, the polyolefin-modified aromatic vinyl-based resin may be a low-density polyethylene-modified styrene-acrylonitrile copolymer, and in this case, the appearance quality, friction resistance, and noise resistance can be effectively improved without degrading the physical properties of the composition. .
상기 변성은 일례로 스티렌-아크릴로니트릴 공중합체에 저밀도 폴리에틸렌이 그라프트된 것을 의미한다.The modification means, for example, that low-density polyethylene is grafted onto a styrene-acrylonitrile copolymer.
상기 폴리올레핀 변성 방향족 비닐계 수지는, 일례로 폴리에틸렌 50 내지 80중량% 또는 60 내지 80중량%; 및 방향족 비닐계 수지 20 내지 50중량% 또는 20 내지 40중량%;를 포함할 수 있다. The polyolefin-modified aromatic vinyl-based resin, for example, 50 to 80% by weight or 60 to 80% by weight of polyethylene; and 20 to 50% by weight or 20 to 40% by weight of an aromatic vinyl-based resin.
보조 assistant 활제lubricant
상기 보조 활제는 일례로 지방산 아미드계 화합물, 몬탄계 왁스, 올레핀계 왁스 및 상업적으로 입수 가능한 Croda사의 Incroslip G 중에서 선택된 1종 이상일 수 있으며, 이 경우 내마찰성, 내소음성이 더욱 개선될 수 있다. 바람직한 일례로 상기 보조 활제는 Croda사의 Incroslip G과 지방산 아미드계 화합물의 혼합 또는 Croda사의 Incroslip G와 몬탄계 왁스의 혼합일 수 있다. The auxiliary lubricant may be, for example, at least one selected from among fatty acid amide-based compounds, montan-based waxes, olefin-based waxes, and commercially available Croda's Incroslip G. In this case, friction resistance and noise resistance may be further improved. As a preferred example, the auxiliary lubricant may be a mixture of Croda's Incroslip G and a fatty acid amide-based compound or a mixture of Croda's Incroslip G and a montan-based wax.
상기 보조 활제는 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.5 내지 1.5중량부, 0.5 내지 1.2중량부, 0.5 내지 1중량부 또는 0.8 내지 1중량부로 포함될 수 있으며, 이 범위 내에서 최종품의 외관 품질이 우수하면서도 물성이 높게 유지되고 내마찰성, 내소음성이 크게 개선될 수 있다. The auxiliary lubricant may be included in, for example, 0.5 to 1.5 parts by weight, 0.5 to 1.2 parts by weight, 0.5 to 1 parts by weight, or 0.8 to 1 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin, and within this range, the appearance quality of the final product While this is excellent, physical properties are maintained high, and friction resistance and noise resistance can be greatly improved.
상기 지방산 아미드계 화합물은 일례로 스테르아미드(stearamide), 비핸아미드(behanamide), 에틸렌 비스 스테르아미드[ethylene bis(stearamide)], 에틸렌 비스 12-하이드록시 스테르아미드[N,N'-ethylene bis(12-hydroxy stearamide)], 에루카미드(erucamide), 올레아미드(oleamide), 에틸렌 비스 올레아미드(ethylene bis oleamide) 등으로부터 선택될 수 있다. The fatty acid amide-based compound is, for example, stearamide (stearamide), behanamide (behanamide), ethylene bis steramide [ethylene bis (stearamide)], ethylene bis 12-hydroxy steramide [N, N'-ethylene bis(12-hydroxy stearamide)], erucamide, oleamide, ethylene bis oleamide, and the like.
상기 몬탄계 왁스는 활제와 함께 제품 표면의 마모 및 소음 발생을 방지하는 역할을 수행하며, 일례로 몬탄 왁스 또는 몬탄 에스테르 왁스일 수 있고, 상기 올레핀계 왁스는 일례로 폴리에틸렌 왁스 또는 폴리프로필렌 왁스일 수 있으나 이에 한정되는 것은 아니다.The montan-based wax serves to prevent abrasion and noise generation of the product surface together with a lubricant, and may be, for example, montan wax or montan ester wax, and the olefin-based wax may be polyethylene wax or polypropylene wax, for example. However, it is not limited thereto.
구체적인 일례로 상기 몬탄 에스테르 왁스는 몬탄계 왁스가 에틸렌 글리콜과 몬탄산으로 에스테르화된 왁스, 글리세린과 몬탄산으로 에스테르화된 왁스, 몬탄산 에스테르가 포함된 칼슘 몬타네이트, 몬탄산을 기초로한 에스테르 혼합 왁스 중에서 선택된 1종 이상일 수 있다. As a specific example, the montan ester wax is a wax obtained by esterifying montanic wax with ethylene glycol and montanic acid, a wax esterified with glycerin and montanic acid, calcium montanate containing montanic acid ester, and an ester based on montanic acid It may be one or more selected from mixed waxes.
상기 보조 활제는 본 기재에서 활제로 예시된 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 제외하고 당업계에서 통상적으로 사용되는 종류이면 특별히 제한되지 않고 적절히 선택하여 사용할 수 있다. The auxiliary lubricant is not particularly limited and may be appropriately selected and used as long as it is a type commonly used in the art, except for polyester-modified siloxane resins or polyolefin-modified aromatic vinyl-based resins exemplified as lubricants in this description.
구체적인 일례로 상기 Incroslip G는, 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.1 내지 1중량부 또는 0.3 내지 0.5중량부로 포함될 수 있고, 상기 지방산 아미드계 화합물은, 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.1 내지 1중량부 또는 0.1 내지 0.5중량부로 포함될 수 있고, 상기 몬탄계 왁스 또는 상기 올레핀계 왁스 각각은 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.1 내지 1중량부 또는 0.1 내지 0.5중량부로 포함될 수 있으며, 이 경우 표면 품질이 우수하면서도 내마찰성 및 내소음성이 효과적으로 개선될 수 있다. As a specific example, the Incroslip G may be included in an amount of 0.1 to 1 part by weight or 0.3 to 0.5 part by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin, and the fatty acid amide compound is based on 100 parts by weight of the thermoplastic polyester elastomer resin For example, it may be included in 0.1 to 1 part by weight or 0.1 to 0.5 parts by weight, and each of the montan-based wax or the olefin-based wax is 0.1 to 1 part by weight or 0.1 to 0.5 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin. In this case, friction resistance and noise resistance can be effectively improved while surface quality is excellent.
사슬연장제 chain extender
본 기재에서 사슬연장제는 수지 조성물의 용융점도 및 용융장력을 높여 블로우 성형 등의 성형 공정을 용이하게 하기 위해 첨가된다. In the present description, the chain extender is added to increase the melt viscosity and melt tension of the resin composition to facilitate a molding process such as blow molding.
상기 사슬연장제는 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 1 내지 6중량부, 1 내지 5중량부, 1.5 내지 5중량부, 1.5 내지 3중량부 또는 3 내지 5중량부로 포함될 수 있으며, 이 범위 내에서 조성물의 물성이 저하되지 않으면서 성형성이 개선되는 이점을 제공한다. The chain extender may be included in an amount of, for example, 1 to 6 parts by weight, 1 to 5 parts by weight, 1.5 to 5 parts by weight, 1.5 to 3 parts by weight, or 3 to 5 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin. It provides an advantage of improving moldability without deteriorating the physical properties of the composition within the range.
상기 사슬연장제는 일례로 1,3-페닐렌 비스 옥사졸린 또는 글리시딜기 변성 올레핀계 공중합체 중에서 선택된 1종 이상일 수 있다. The chain extender may be, for example, at least one selected from 1,3-phenylene bisoxazoline or a glycidyl group-modified olefin-based copolymer.
바람직한 일례로 상기 사슬연장제는 1,3-페닐렌 비스 옥사졸린 및 글리시딜기 변성 올레핀계 공중합체의 혼합일 수 있고, 상기 1,3-페닐렌 비스 옥사졸린은 일례로 0 내지 0.5중량부 또는 0.1 내지 0.3중량부로 포함될 수 있으며, 상기 글리시딜기 변성 올레핀계 공중합체는 일례로 1 내지 5.5중량부, 1.5 내지 4.5중량부 또는 2 내지 4.5중량부로 포함될 수 있고, 이 범위 내에서 물성 밸런스가 높게 유지되면서도 조성물의 성형성이 개선되는 이점을 제공한다. 본 기재에서 특별한 언급이 없는 한 각 성분의 중량부는 열가소성 폴리에스테르 엘라스토머 수지 100중량부를 기준으로 한다. In a preferred example, the chain extender may be a mixture of 1,3-phenylene bisoxazoline and a glycidyl group-modified olefin-based copolymer, and 0 to 0.5 parts by weight of the 1,3-phenylene bisoxazoline, for example. Alternatively, it may be included in 0.1 to 0.3 parts by weight, and the glycidyl group-modified olefin-based copolymer may be included in, for example, 1 to 5.5 parts by weight, 1.5 to 4.5 parts by weight, or 2 to 4.5 parts by weight, and the balance of physical properties within this range It provides the advantage that the formability of the composition is improved while remaining high. Unless otherwise specified in this description, the weight of each component is based on 100 parts by weight of the thermoplastic polyester elastomer resin.
상기 글리시딜기 변성 올레핀계 공중합체는 구체적인 일례로 글리시딜 메타크릴레이트를 그라프트시켜 변성된 에틸렌-옥텐계 공중합체일 수 있으며, 이 경우 조성물의 성형성이 개선되는 이점을 제공한다.As a specific example, the glycidyl group-modified olefin-based copolymer may be an ethylene-octene-based copolymer modified by grafting glycidyl methacrylate, and in this case, moldability of the composition is improved.
상기 글리시딜 메타크릴레이트는 일례로 상기 변성된 에틸렌-옥텐계 공중합체 총량 기준 5 내지 20중량% 또는 8 내지 20중량%의 비율로 포함될 수 있다. The glycidyl methacrylate may be included in an amount of, for example, 5 to 20% by weight or 8 to 20% by weight based on the total amount of the modified ethylene-octene-based copolymer.
안정제stabilizator
본 기재에서 안정제는 수지 조성물 제조 중 또는 성형품의 사용 중에 수지가 빛, 열 등의 외부 요인에 의해 변질되는 것을 방지하기 위해 첨가되며, 일례로 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 0.1 내지 5중량부, 0.1 내지 3중량부, 0.5 내지 2중량부 또는 0.5 내지 1.5중량부로 포함될 수 있으며, 이 범위 내에서 물성을 높게 유지하면서도 내열안정성 및 내산화성이 우수한 이점을 제공한다. In the present disclosure, the stabilizer is added to prevent deterioration of the resin by external factors such as light and heat during the manufacture of the resin composition or use of the molded product, and for example, 0.1 to 5 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin. , 0.1 to 3 parts by weight, 0.5 to 2 parts by weight, or 0.5 to 1.5 parts by weight, while maintaining high physical properties within this range, it provides excellent heat stability and oxidation resistance.
일례로 상기 안정제는 내열안정제, 광안정제 및 산화방지제 중에서 선택된 1종 이상일 수 있고, 바람직하게는 이들 모두를 포함하는 것이며 이 경우 내열성 및 내산화성이 우수한 이점을 제공한다. For example, the stabilizer may be at least one selected from a heat-resistant stabilizer, a light stabilizer, and an antioxidant, and preferably includes all of them, and in this case, excellent heat resistance and oxidation resistance are provided.
상기 내열안정제는 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.5 내지 1.5중량부 또는 0.6 내지 1.0중량부로 포함될 수 있으며, 이 범위 내에서 조성물의 물성에 악영향을 미치지 않으면서 내열안정성이 개선되는 이점이 있다. The heat-resistant stabilizer may be included in an amount of, for example, 0.5 to 1.5 parts by weight or 0.6 to 1.0 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin, and within this range, the heat resistance stability is improved without adversely affecting the physical properties of the composition. have.
상기 내열안정제는 일례로 페놀계 화합물일 수 있고, 필요에 따라 선택적으로 금속계 내열안정제를 더 포함할 수 있다. The heat-resistant stabilizer may be, for example, a phenol-based compound, and may optionally further include a metal-based heat-resistant stabilizer, if necessary.
상기 페놀계 화합물은 일례로 펜타에리트리톨 테트라키스(3-(3,5-디-터셔리-부틸-4-하이드록시페닐)프로피오네이트 일 수 있으며, 이 경우 물성 밸런스가 높게 유지되면서도 내열안정성이 크게 개선될 수 있다. The phenolic compound may be, for example, pentaerythritol tetrakis (3-(3,5-di-tertiary-butyl-4-hydroxyphenyl) propionate, in which case, while maintaining a high physical property balance, heat resistance stability This can be greatly improved.
상기 금속계 내열안정제는 일례로 당업계에서 통상적으로 사용되는 내열안정성 금속착화합물 또는 금속 아이오딘화물일 수 있으며, 구체적인 일례로 내열안정성 금속착화합물은 니켈계 착화합물일 수 있고, 금속 아이오딘화물은 아이오딘화 칼륨 또는 아이오딘화 구리 또는 이들 모두일 수 있다.The metal-based heat-resistant stabilizer may be, for example, a heat-resistant stable metal complex or metal iodide commonly used in the art. As a specific example, the heat-resistant stable metal complex may be a nickel-based complex, and the metal iodide may be iodide. It may be potassium or copper iodide or both.
상기 광안정제는 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.01 내지 0.5중량부, 0.05 내지 0.3중량부 또는 0.1 내지 0.3중량부로 포함할 수 있고, 이 범위 내에서 조성물의 내노화성이 향상되는 이점이 있다. The light stabilizer may be included in an amount of, for example, 0.01 to 0.5 parts by weight, 0.05 to 0.3 parts by weight, or 0.1 to 0.3 parts by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin, and within this range, the aging resistance of the composition is improved. have.
상기 광안정제는 일례로 힌더드 아민계 광안정제일 수 있으며, 이 경우 조성물의 내노화성이 우수하다. The light stabilizer may be, for example, a hindered amine light stabilizer, and in this case, the aging resistance of the composition is excellent.
상기 산화방지제는 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 일례로 0.1 내지 1중량부, 0.3 내지 0.8중량부 또는 0.5 내지 0.8중량부로 포함될 수 있으며, 이 범위 내에서 수지 조성물의 물성이 높게 유지되면서도 내노화성이 우수한 이점이 있다. The antioxidant may be included in an amount of, for example, 0.1 to 1 part by weight, 0.3 to 0.8 part by weight, or 0.5 to 0.8 part by weight based on 100 parts by weight of the thermoplastic polyester elastomer resin, and within this range, while maintaining high physical properties of the resin composition, aging resistance This has great advantages.
상기 산화방지제는 일례로 아민계 산화방지제 일 수 있고, 구체적인 일례로 4,4'-비스(α,α-디메틸벤질 디페닐아민)일 수 있다. The antioxidant may be, for example, an amine-based antioxidant, and as a specific example, it may be 4,4'-bis(α,α-dimethylbenzyl diphenylamine).
본 기재에서 힌더드 아민계 광안정제 및 아민계 산화방지제는 서로 동일하지 않다. In this description, hindered amine light stabilizers and amine antioxidants are not identical to each other.
기타 첨가제 Other Additives
본 기재의 열가소성 폴리에스테르 엘라스토머 수지 조성물은 필요에 따라 선택적으로 첨가제를 더 포함할 수 있으며, 상기 첨가제는 일례로 조색제, 가소제, 카본블랙, 이형제, 무기 충진제, 핵제, 안료, 대전방지제, 항균제, 가공조제, 금속 불활성화제, 난연제, 커플링제 중에서 선택된 1종 이상일 수 있으나 이에 한정되는 것은 아니다. The thermoplastic polyester elastomer resin composition of the present substrate may optionally further include additives as needed, and the additives include, for example, colorants, plasticizers, carbon black, release agents, inorganic fillers, nucleating agents, pigments, antistatic agents, antibacterial agents, and processing agents. It may be at least one selected from an auxiliary agent, a metal deactivator, a flame retardant, and a coupling agent, but is not limited thereto.
일례로 상기 조성물은 열가소성 폴리에스테르 엘라스토머 수지 100중량부 기준 카본 블랙 1 내지 3중량부 또는 1 내지 2.5중량부를 첨가제로 더 포함할 수 있다. For example, the composition may further include 1 to 3 parts by weight or 1 to 2.5 parts by weight of carbon black based on 100 parts by weight of the thermoplastic polyester elastomer resin as an additive.
일례로 상기 카본 블랙은 폴리에스테르 엘라스토머 수지를 캐리어 수지로 하는 카본 블랙 마스터 배치일 수 있으며, 이 경우 엘라스토머 수지와의 상용성이 우수하여 카본 블랙이 균일하게 분산될 수 있고, 컴파운딩이 용이한 이점을 제공한다. For example, the carbon black may be a carbon black master batch using a polyester elastomer resin as a carrier resin. In this case, the compatibility with the elastomer resin is excellent, so that the carbon black can be uniformly dispersed and compounding is easy. provides
이하에서는 본 기재의 열가소성 폴리에스테르 엘라스토머 수지 조성물의 제조방법을 설명하기로 한다. 상기 제조방법은 전술한 열가소성 폴리에스테르 엘라스토머 수지 조성물의 모든 기술적 특징을 포함하는 바, 위와 중첩되는 설명은 생략하기로 한다. Hereinafter, a method for preparing the thermoplastic polyester elastomer resin composition of the present substrate will be described. The manufacturing method includes all the technical features of the thermoplastic polyester elastomer resin composition described above, and thus, overlapping descriptions above will be omitted.
본 기재의 열가소성 폴리에스테르 엘라스토머 수지 조성물의 제조방법은 일례로 열가소성 폴리에스테르 엘라스토머 수지 100중량부에, 활제 1 내지 3중량부, 보조 활제 0.5 내지 1.5중량부, 사슬연장제 1 내지 6중량부를 포함하여 혼련 및 압출하는 단계를 포함하되, 상기 활제는 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 것을 특징으로 하며, 이 경우 조성물의 표면 품질이 우수하면서도 기계적인 물성이 높게 유지되고, 내마찰성, 내스크래치성, 내소음성이 향상되는 이점을 제공한다. The method for producing the thermoplastic polyester elastomer resin composition of the present disclosure includes, for example, 100 parts by weight of the thermoplastic polyester elastomer resin, 1 to 3 parts by weight of a lubricant, 0.5 to 1.5 parts by weight of an auxiliary lubricant, and 1 to 6 parts by weight of a chain extender. Kneading and extruding, wherein the lubricant comprises a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin. In this case, the surface quality of the composition is excellent while maintaining high mechanical properties, It provides the advantage of improving friction, scratch resistance, and noise resistance.
상기 혼련 및 압출은 당업계에서 통상적으로 사용되는 종류의 압출기를 사용할 수 있고, 바람직한 일례로 일축 압출기 또는 이축 압출기를 사용할 수 있다. The kneading and extruding may use an extruder of a type commonly used in the art, and a single screw extruder or a twin screw extruder may be used as a preferred example.
상기 혼련 및 압출은 일례로 200 내지 300℃ 또는 210 내지 250℃의 온도 범위; 및 100 내지 600rpm 또는 200 내지 400rpm의 회전속도 하에서 수행될 수 있고, 이 범위 내에서 압출 효율 및 조성물의 물성이 우수하다. The kneading and extrusion are, for example, in a temperature range of 200 to 300 ° C or 210 to 250 ° C; And it can be carried out under a rotational speed of 100 to 600 rpm or 200 to 400 rpm, and the extrusion efficiency and physical properties of the composition are excellent within this range.
상기 압출을 통해 수득된 열가소성 폴리에스테르 엘라스토머 수지 조성물은 필요에 따라 선택적으로 펠렛타이저를 사용하여 펠렛으로 제조될 수 있다. The thermoplastic polyester elastomer resin composition obtained through the extrusion may be selectively formed into pellets as needed using a pelletizer.
나아가, 상기 수지 조성물은 블로우 공정, 사출 공정 등의 성형 공정을 통해 각종 산업 분야의 성형품으로 제조될 수 있다. Furthermore, the resin composition may be manufactured into molded articles in various industrial fields through molding processes such as a blow process and an injection process.
본 기재의 성형품은 상기 열가소성 폴리에스테르 엘라스토머 수지 조성물을 포함하는 것을 특징으로 할 수 있고, 일례로 상기 성형품은 자동차 부품일 수 있으며, 보다 바람직하게는 등속 조인트 부츠일 수 있다. The molded article of the present substrate may be characterized by including the thermoplastic polyester elastomer resin composition, and for example, the molded article may be an automobile part, more preferably a constant velocity joint boot.
상기 성형품은 표면이 매끄러워 외관품질이 우수하면서도 내마찰성, 내스크래치성 및 내소음성이 크게 향상된 이점을 제공하여 등속 조인트 부츠 소재에 요구되는 물성을 제공한다. The molded article has a smooth surface and has excellent appearance quality, but also provides greatly improved friction resistance, scratch resistance, and noise resistance, thereby providing physical properties required for a constant velocity joint boot material.
본 기재의 열가소성 폴리에스테르 엘라스토머 수지 조성물, 이의 제조방법 및 이를 포함하는 성형품을 설명함에 있어서, 명시적으로 기재하지 않은 다른 첨가제나, 제조 공정 조건, 제조 설비 등은 당업계에서 통상적으로 실시되는 범위 내에서 적절히 선택할 수 있고, 특별히 제한되지 않음을 명시한다. In describing the thermoplastic polyester elastomer resin composition of the present disclosure, its manufacturing method, and molded products including the same, other additives, manufacturing process conditions, manufacturing equipment, etc. not explicitly described are within the range commonly practiced in the art. It can be appropriately selected from, and it is specified that it is not particularly limited.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다.Hereinafter, preferred embodiments are presented to aid understanding of the present invention, but the following examples are merely illustrative of the present invention, and various changes and modifications are possible within the scope and spirit of the present invention. It is obvious to those skilled in the art, It goes without saying that these variations and modifications fall within the scope of the appended claims.
하기 실시예 및 비교예에서 사용된 재료는 다음과 같다. Materials used in the following Examples and Comparative Examples are as follows.
A) 열가소성 폴리에스테르 엘라스토머 수지A) thermoplastic polyester elastomer resin
방향족 디카르복실산, 지방족 디올 및 폴리알킬렌옥사이드 총 중량을 기준으로 방향족 디카르복실산 40 내지 70중량%, 지방족 디올 20 내지 40중량% 및 폴리알킬렌옥사이드 10 내지 40중량%를 포함하여 중합되고, 용융지수(230℃, 2.16kg)가 0.5 내지 6g/10min이며, 쇼어 경도가 35 내지 47D인 엘지화학사의 열가소성 폴리에스테르 엘라스토머 수지를 사용하였다. Polymerization including 40 to 70% by weight of aromatic dicarboxylic acid, 20 to 40% by weight of aliphatic diol and 10 to 40% by weight of polyalkylene oxide based on the total weight of aromatic dicarboxylic acid, aliphatic diol and polyalkylene oxide , and a melt index (230 ° C, 2.16 kg) of 0.5 to 6 g / 10 min and a shore hardness of 35 to 47 D, a thermoplastic polyester elastomer resin from LG Chem was used.
B) B) 활제lubricant
B1) 폴리에스테르 변성 실록산 B1) polyester modified siloxane
말단에 하이드록시기를 갖는 폴리에스테르 변성 실록산을 사용하였으며, 융점이 54℃이고, 펠렛 형태의 제품(Evonik사의 TEGOMER H-Si 6441P)을 사용하였다. A polyester-modified siloxane having a hydroxyl group at the terminal was used, and a melting point of 54° C., and a pellet-type product (TEGOMER H-Si 6441P from Evonik) was used.
B2) 폴리올레핀 변성 방향족 비닐계 수지B2) Polyolefin-modified aromatic vinyl resin
저밀도 폴리에틸렌 변성 스티렌-아크릴로니트릴 공중합체로, NOF사의 MODIPER A1400 제품을 사용하였다. As a low-density polyethylene-modified styrene-acrylonitrile copolymer, NOF's MODIPER A1400 product was used.
C) 보조 C) secondary 활제lubricant
C1) Croda사의 Incroslip G 제품을 사용하였다. C1) Croda's Incroslip G product was used.
C2) 에틸렌 비스 올레아미드로 Croda사의 EBO 제품을 사용하였다.C2) Croda's EBO product was used as ethylene bis oleamide.
C3) 몬탄계 왁스를 사용하였다. C3) A montan-based wax was used.
D) 사슬연장제 D) chain extenders
D1) 1,3-페닐렌 비스 옥사졸린을 사용하였다. D1) 1,3-phenylene bis oxazoline was used.
D2) 글리시딜기 변성 에틸렌-옥텐계 공중합체로서, 글리시딜메타크릴레이트(공중합체 중 8 내지 20중량%로 포함됨)로 그라프팅시켜 변성시킨 에틸렌-옥텐계 공중합체를 사용하였다. D2) As the glycidyl group-modified ethylene-octene-based copolymer, an ethylene-octene-based copolymer modified by grafting with glycidyl methacrylate (included in 8 to 20% by weight of the copolymer) was used.
E) 안정제 E) Stabilizers
E1) 페놀계 내열안정제 E1) Phenol-based heat stabilizer
펜타에리트리톨 테트라키스(3-(3,5-디-터셔리-부틸-4-하이드록시페닐)프로피오네이트를 사용하였다. Pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate was used.
E2) 힌더드 아민계 광안정제E2) Hindered Amine Light Stabilizers
Poly[[6-[(1,1,3,3-tetramethylbutyl)amino]-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidinyl)imino]-1,6-exanediyl[(2,2,6,6-tetramethyl-4-piperidinyl)imino]])를 사용하였다. Poly[[6-[(1,1,3,3-tetramethylbutyl)amino]-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidinyl) imino]-1,6-exanediyl[(2,2,6,6-tetramethyl-4-piperidinyl)imino]]) was used.
E3) 아민계 산화방지제 E3) Amine-based antioxidant
4,4'-비스(α,α-디메틸벤질 디페닐아민)을 사용하였다. 4,4'-bis(α,α-dimethylbenzyl diphenylamine) was used.
E4) 내열안정성 금속착화합물E4) Heat stable metal complex
니켈-디부틸 디티오카바메이트로 Ouchi Shinko Chemical사의 Nocrac NBC 제품을 사용하였다. A Nocrac NBC product from Ouchi Shinko Chemical was used as the nickel-dibutyl dithiocarbamate.
E5) 금속 아이오딘화물 E5) metal iodides
아이오딘화구리(CuI) 및 아이오딘화칼륨(KI)을 2:1의 중량비로 혼합하여 사용하였다. Copper iodide (CuI) and potassium iodide (KI) were mixed at a weight ratio of 2:1 and used.
F) 기타 첨가제 F) Other additives
카본 블랙 안료로, 열가소성 폴리에스테르 엘라스토머 수지 베이스에 카본 블랙이 30중량% 농도로 함유된 마스터 배치를 사용하였다. As the carbon black pigment, a master batch containing 30% by weight of carbon black in a thermoplastic polyester elastomer resin base was used.
[[ 실시예Example 및 and 비교예comparative example ]]
실시예Example 1 내지 3 및 1 to 3 and 비교예comparative example 1 내지 2 1 to 2
하기 표 1에 나타낸 성분 및 함량대로 배합하고, 이축 압출기를 사용하여 압출(압출 조건: 230℃, 300rpm)하고, 펠렛타이저를 사용하여 펠렛을 수득하였다. 이 펠렛을 성형하여 물성 측정용 시편을 제조하였다. The ingredients and contents shown in Table 1 below were blended, extruded using a twin screw extruder (extrusion conditions: 230 ° C, 300 rpm), and pellets were obtained using a pelletizer. The pellets were molded to prepare specimens for measuring physical properties.
[[ 시험예test example ]]
상기 실시예 및 비교예에서 제조된 시편의 물성을 하기의 방법으로 측정하였고, 그 결과를 하기 표 1에 나타내었다. The physical properties of the specimens prepared in the above Examples and Comparative Examples were measured by the following method, and the results are shown in Table 1 below.
* * 내소음성noise resistance 평가 evaluation
내소음성 평가를 위해 각 실시예 및 비교예를 통해 수득된 펠렛을 블로우 성형하여 등속조인트 부츠를 제조하고, 이를 등속조인트에 장착하여 시편을 준비하였다. 도 1은 본 발명에 따라 제조된 등속조인트 부츠를 장착한 등속조인트의 사진이다. 도 1에서 부츠는 원으로 표시된 부분에 해당한다. To evaluate noise resistance, the pellets obtained in each Example and Comparative Example were blow molded to manufacture a constant velocity joint boot, and a specimen was prepared by mounting it on a constant velocity joint. 1 is a photograph of a constant velocity joint equipped with a constant velocity joint boot manufactured according to the present invention. In FIG. 1 , the boot corresponds to a portion marked with a circle.
준비된 시편을 사용하여 길들이기 10초 -> 염수 도포 10초 -> 모래 도포 10초 -> 염수 및 모래 미도포 60초를 1 사이클(cycle)로 하여 사이클을 반복하면서 75dB 이상의 소음(이때, 주변 소음은 65dB 이하로 유지) 발생한 사이클의 횟수로 내소음성을 평가하였다. Using the prepared specimen, 10 seconds of taming -> 10 seconds of application of salt water -> 10 seconds of application of sand -> 60 seconds of application of salt water and no sand as one cycle, repeating the cycle, making noise of 75 dB or more (At this time, ambient noise is 65dB or less) noise resistance was evaluated by the number of cycles that occurred.
이때, 염수는 염화칼슘 15중량% 및 수산화칼슘 15중량%를 포함하는 수용액을 사용하였다. At this time, as the brine, an aqueous solution containing 15% by weight of calcium chloride and 15% by weight of calcium hydroxide was used.
* * 쇼어shore 경도 Hardness
ASTM D2240에 명시된 방법에 따라 D타입의 쇼어 경도를 측정하였다. Shore hardness of type D was measured according to the method specified in ASTM D2240.
* 유동지수(단위: g/* Flow index (unit: g/ 10min10min ))
ASTM D1238에 명시된 방법에 따라 230℃, 하중 10kg인 조건 하에 측정하였다. According to the method specified in ASTM D1238, it was measured under the conditions of 230 ° C. and a load of 10 kg.
* 인장강도 * The tensile strength
ISO527-1 및 2에 명시된 방법에 따라 두께 2mm인 시편을 사용하여 인장속도 500mm/min인 조건하에 상온(23℃)에서 측정하였다. According to the method specified in ISO527-1 and 2, it was measured at room temperature (23 ° C) under the condition of a tensile speed of 500 mm / min using a specimen having a thickness of 2 mm.
(상기 표 1에서 각 성분의 함량 단위는 중량부이며, B 내지 F 성분의 함량은 A 성분 100중량부를 기준으로 한다.)(In Table 1, the unit of content of each component is parts by weight, and the content of components B to F is based on 100 parts by weight of component A.)
상기 표 1을 참조하면, 특정 활제 및 보조 활제를 포함하는 실시예 1 내지 3을 비교예 1 및 2와 대비하면 경도, 유동지수, 인장강도를 동등 수준으로 유지하면서도 내소음성이 매우 개선된 것을 확인할 수 있다. Referring to Table 1, when Examples 1 to 3 including specific lubricants and auxiliary lubricants are compared with Comparative Examples 1 and 2, it can be confirmed that the noise resistance is greatly improved while maintaining the hardness, flow index, and tensile strength at the same level. can
무엇보다도 본 발명에 따른 실시예 1 내지 3의 경우, 비교예 1 및 2 대비 활제의 총 함량이 2~2.5배 과량임에도 불구하고 열가소성 폴리에스테르 엘라스토머 수지 고유의 기저물성(경도, 유동지수, 인장강도)은 높게 유지하면서도 내소음성 개선 효과가 탁월한 것을 확인할 수 있다. Above all, in the case of Examples 1 to 3 according to the present invention, despite the total content of the lubricant compared to Comparative Examples 1 and 2 being 2 to 2.5 times excessive, the basic physical properties inherent in the thermoplastic polyester elastomer resin (hardness, flow index, tensile strength ) It can be seen that the effect of improving noise resistance is excellent while maintaining a high level.
또한, 본 기재에서 내소음성 평가는 염수 및 모래와 같은 이물질이 도포되는 가혹한 환경에서 수행되었으며, 본 발명에 따를 경우 이러한 가혹한 조건하에서도 내소음성 개선 효과가 상당히 우수한 것을 확인할 수 있다. In addition, in the present description, the noise resistance evaluation was performed in a harsh environment in which foreign substances such as salt water and sand were applied, and it can be confirmed that the noise resistance improvement effect is considerably excellent even under such harsh conditions according to the present invention.
나아가 본 기재의 조성물을 등속조인트 부츠 용도로 활용할 시, 노면으로부터 차량 하부로 유입되는 염수, 모래 등의 각종 이물질로 인해 부츠가 오염되어 큰 소음이 발생하고, 부츠의 성능이 저하되는 종래 문제점을 해소하는데 기여할 수 있다. Furthermore, when the composition of the present disclosure is used for constant velocity joint boots, the boots are contaminated due to various foreign substances such as salt water and sand flowing from the road surface to the lower part of the vehicle, causing loud noise and solving the conventional problems of deteriorating the performance of the boots. can contribute to
Claims (14)
상기 활제는 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.Including 100 parts by weight of thermoplastic polyester elastomer resin, 1.8 to 2.5 parts by weight of a lubricant, 0.5 to 1.2 parts by weight of an auxiliary lubricant, and 1 to 5 parts by weight of a chain extender,
Characterized in that the lubricant comprises a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin.
A thermoplastic polyester elastomer resin composition.
상기 조성물은 안정제 0.1 내지 5중량부를 더 포함하는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 1,
The composition further comprises 0.1 to 5 parts by weight of a stabilizer
A thermoplastic polyester elastomer resin composition.
상기 안정제는 내열안정제, 광안정제 및 산화방지제 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 2,
The stabilizer is characterized in that it comprises at least one selected from a heat-resistant stabilizer, light stabilizer and antioxidant
A thermoplastic polyester elastomer resin composition.
상기 내열안정제는 0.5 내지 1.5중량부로 포함되는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 3,
The heat-resistant stabilizer is characterized in that contained in 0.5 to 1.5 parts by weight
A thermoplastic polyester elastomer resin composition.
상기 광안정제는 0.01 내지 0.5중량부로 포함되는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 3,
The light stabilizer is characterized in that contained in 0.01 to 0.5 parts by weight
A thermoplastic polyester elastomer resin composition.
상기 산화방지제는 0.1 내지 1중량부로 포함되는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 3,
Characterized in that the antioxidant is contained in 0.1 to 1 part by weight
A thermoplastic polyester elastomer resin composition.
상기 사슬연장제는 1,3-페닐렌 비스 옥사졸린 또는 글리시딜기 변성 올레핀계 공중합체 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 1,
Characterized in that the chain extender includes at least one selected from 1,3-phenylene bisoxazoline or glycidyl group-modified olefin-based copolymer.
A thermoplastic polyester elastomer resin composition.
상기 보조 활제는 지방산 아미드계 화합물, 몬탄계 왁스 및 올레핀계 왁스 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 1,
Characterized in that the auxiliary lubricant comprises at least one selected from fatty acid amide-based compounds, montan-based waxes, and olefin-based waxes.
A thermoplastic polyester elastomer resin composition.
상기 폴리올레핀 변성 방향족 비닐계 수지는 폴리에틸렌 변성 방향족 비닐계 수지인 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 1,
Characterized in that the polyolefin-modified aromatic vinyl-based resin is a polyethylene-modified aromatic vinyl-based resin
A thermoplastic polyester elastomer resin composition.
상기 방향족 비닐계 수지는 방향족 비닐 화합물의 호모 중합체; 또는 방향족 비닐 화합물과 비닐시안 화합물을 포함하는 공중합체;인 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물. According to claim 1,
The aromatic vinyl resin may be a homopolymer of an aromatic vinyl compound; or a copolymer containing an aromatic vinyl compound and a vinyl cyan compound;
A thermoplastic polyester elastomer resin composition.
상기 폴리에스테르 변성 실록산 수지는 융점이 50 내지 55℃인 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물.According to claim 1,
The polyester-modified siloxane resin is characterized in that the melting point of 50 to 55 ℃
A thermoplastic polyester elastomer resin composition.
상기 활제는 폴리에스테르 변성 실록산 수지 또는 폴리올레핀 변성 방향족 비닐계 수지를 포함하는 것을 특징으로 하는
열가소성 폴리에스테르 엘라스토머 수지 조성물의 제조방법.Kneading and extruding 100 parts by weight of thermoplastic polyester elastomer resin, 1.8 to 2.5 parts by weight of a lubricant, 0.5 to 1.2 parts by weight of an auxiliary lubricant, and 1 to 5 parts by weight of a chain extender,
Characterized in that the lubricant comprises a polyester-modified siloxane resin or a polyolefin-modified aromatic vinyl-based resin.
Method for producing a thermoplastic polyester elastomer resin composition.
상기 성형품은 자동차의 등속조인트 부츠인 것을 특징으로 하는
성형품.According to claim 13,
Characterized in that the molded article is a constant velocity joint boot of an automobile
molding.