KR102461146B1 - Antibacterial plastic packaging box - Google Patents
Antibacterial plastic packaging box Download PDFInfo
- Publication number
- KR102461146B1 KR102461146B1 KR1020200185473A KR20200185473A KR102461146B1 KR 102461146 B1 KR102461146 B1 KR 102461146B1 KR 1020200185473 A KR1020200185473 A KR 1020200185473A KR 20200185473 A KR20200185473 A KR 20200185473A KR 102461146 B1 KR102461146 B1 KR 102461146B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- packaging box
- plastic packaging
- plastic
- Prior art date
Abstract
본 발명은 베이스 수지, 구리나노입자, 실란 커플링제, 대전방지제 및 유기용매를 포함하는 플라스틱 조성물을, 발포 성형 또는 사출 성형하여 형성됨으로써, 우수한 항균 효과 및 기계적 물성을 갖는 플라스틱 조성물 및 이로 형성된 플라스틱을 제공한다.The present invention is a plastic composition comprising a base resin, copper nanoparticles, a silane coupling agent, an antistatic agent and an organic solvent, formed by foam molding or injection molding, thereby providing a plastic composition having excellent antibacterial effect and mechanical properties, and a plastic formed therewith to provide.
Description
본 발명은 항균성이 우수한 플라스틱 포장박스에 관한 것이다.The present invention relates to a plastic packaging box having excellent antibacterial properties.
구체적으로, 본 발명은 항균성 및 인장강도, 충격강도 등의 기계적 물성이 우수한 플라스틱 조성물을 사출 성형 또는 발포 성형하여 형성된, 플라스틱 포장박스에 관한 것이다.Specifically, the present invention relates to a plastic packaging box formed by injection molding or foam molding of a plastic composition excellent in antibacterial properties, mechanical properties such as tensile strength and impact strength.
환경의 변화에 의해 인간의 건강을 위협하는 균, 바이러스, 박테리아 등이 확산됨에 따라, 여러 기술 분야에서 이를 효과적으로 차단하고자 하는 노력이 계속되고 있다. 특히, 아이들은 성인에 비해 면역력이 현저히 떨어지므로 바이러스 및 독성으로 인한 큰 문제를 야기시키는 것을 미리 방지하기 위한 다양한 시도들이 계속 되고 있다.As bacteria, viruses, and bacteria that threaten human health are spread due to changes in the environment, efforts to effectively block them are continuing in various technical fields. In particular, since children have significantly lower immunity than adults, various attempts are being made to prevent them from causing a big problem due to viruses and toxicity.
특히, 이사, 짐 정리 등에 사용되는 포장박스는 사용 기간이 길고, 다양한 물건이 수납되며, 주로 재사용되는데, 이러한 포장박스가 균, 바이러스, 박테리아 등에 노출될 경우에는, 이에 담겨진 짐 등이 균, 바이러스, 박테리아 등에 노출되어, 결과적으로 이를 사용하는 소비자들의 건강을 위협하는 문제가 있었다. 특히, 이사에 사용되는 포장박스의 경우, 불특정 다수가 사용하므로, 더욱이 항균 기능이 요구되고 있다. In particular, packaging boxes used for moving, organizing luggage, etc. have a long usage period, contain various items, and are mainly reused. , bacteria, etc., and consequently, there was a problem that threatens the health of consumers who use it. In particular, in the case of a packaging box used for moving, since it is used by an unspecified number of people, it is further required to have an antibacterial function.
이에, 포장박스를 비롯한 생활에 자주 사용되는 플라스틱 제품에는, 항균 기능을 부여하기 위하여, 주로 종래의 유기 항균제가 사용되어 왔다. 그러나, 유기 항균제는 인체에 유해하여, 사용이 제한적이었다. 최근에는, 상기와 같은 문제를 갖는 유기 항균제의 사용을 대체하고자, 은, 구리 등의 금속 물질을 포함하여 항균 효과를 구현하고자 하는 다양한 시도들이 계속되고 있다. 일례로, 대한민국 등록특허 제10-2096213호에서는 베이스 수지, 금속산화물, 아연피리티온, 경화제, 유기용매 등을 포함하는 항균성 조성물을 포함하는 플라스틱재 가구의 제조방법에 대해 개시하고 있다.Accordingly, in order to impart an antibacterial function to plastic products frequently used in daily life, including packaging boxes, conventional organic antibacterial agents have been mainly used. However, organic antibacterial agents are harmful to the human body, so their use is limited. Recently, in order to replace the use of organic antibacterial agents having the above problems, various attempts have been made to implement an antibacterial effect including metal materials such as silver and copper. For example, Korean Patent Registration No. 10-2096213 discloses a method for manufacturing plastic furniture including an antibacterial composition including a base resin, a metal oxide, zinc pyrithione, a curing agent, an organic solvent, and the like.
한편, 상기 등록특허를 포함하여, 금속 입자를 이용하는 종래의 항균 플라스틱의 경우에는, 항균 효과는 우수한 이점이 있으나, 금속 입자에 의해 고분자 결합의 치밀성이 저하되어 플라스틱의 제조 공정에서 크랙이 발생되거나, 최종적으로 제조된 제품의 내충격성, 강도 등이 충분히 구현되지 못하는 문제가 있었다.On the other hand, in the case of the conventional antibacterial plastic using metal particles, including the registered patent, there is an advantage in that the antibacterial effect is excellent, but the denseness of the polymer bond is lowered by the metal particles, so that cracks are generated in the manufacturing process of the plastic, There was a problem in that the impact resistance, strength, etc. of the finally manufactured product were not sufficiently implemented.
또한, 상기와 같은 문제를 해결하기 위해, 상기 등록특허에서는 소량의 금속 입자를 사용하고 있으나, 금속 입자를 소량 사용할 경우에는, 항균 효과가 충분히 구현되지 못하여, 항균 제품으로서의 특성 구현이 어려운 문제가 있었다.In addition, in order to solve the above problems, a small amount of metal particles is used in the registered patent, but when a small amount of metal particles is used, the antibacterial effect is not sufficiently implemented, so it is difficult to realize the properties as an antibacterial product. .
따라서, 충분한 향균 효과를 구현할 수 있도록 적정량의 금속 입자를 포함하여, 우수한 항균 효과를 구현하면서도 인장 강도, 충격 강도 등 기계적 물성이 향상된, 플라스틱 포장박스에 대한 개발이 요구되고 있는 실정이다.Therefore, the development of a plastic packaging box having improved mechanical properties such as tensile strength and impact strength while implementing an excellent antibacterial effect by including an appropriate amount of metal particles to realize a sufficient antibacterial effect is required.
본 발명의 목적은 항균 효과 및 인장강도, 충격강도 등의 기계적 물성이 우수한, 플라스틱 포장박스를 제공하는 데에 있다. 구체적으로, 본 발명의 목적은 적정량의 구리나노입자를 포함하는 플라스틱 조성물을 성형하여 형성된 것으로, 항균 효과, 인장강도, 충격강도 등이 우수한 플라스틱 포장박스를 제공하는 데에 있다.An object of the present invention is to provide a plastic packaging box having excellent antibacterial effect and mechanical properties such as tensile strength and impact strength. Specifically, an object of the present invention is to provide a plastic packaging box formed by molding a plastic composition containing an appropriate amount of copper nanoparticles and having excellent antibacterial effect, tensile strength, impact strength, and the like.
본 발명의 목적은 상기된 바와 같은 기술적 과제로 한정되지 않으며, 이하의 설명으로부터 또 다른 기술적 과제가 도출될 수 있다. The object of the present invention is not limited to the technical problem as described above, and another technical problem may be derived from the following description.
상기 목적을 달성하기 위하여, 본 발명은 베이스 수지, 구리나노입자, 실란 커플링제, 대전방지제 및 유기용매를 포함하는 플라스틱 조성물로 형성된 플라스틱 포장박스에 관한 것으로, 상기 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)으로 이루어진 군에서 선택되는 하나 이상을 포함하는, 항균성이 우수한 플라스틱 포장박스를 제공한다.In order to achieve the above object, the present invention relates to a plastic packaging box formed of a plastic composition comprising a base resin, copper nanoparticles, a silane coupling agent, an antistatic agent and an organic solvent, wherein the silane coupling agent is 3-glycidoxy From the group consisting of propyltrimethoxysilane ( 3 -Glycidoxy propyl trimethoxysilane), 3-amino propyl triethoxysilane and 3-methacryloxypropyl triethoxysilane (3-Methacryloxy propyl triethoxysilane) It provides a plastic packaging box with excellent antibacterial properties, including one or more selected.
상기 플라스틱 조성물은 상기 베이스 수지 100 중량부에 대해 상기 구리나노입자 9 ~ 20 중량부, 상기 실란 커플링제 5 ~ 15 중량부, 상기 대전방지제 10 ~ 20 중량부 및 상기 유기용매 50 ~ 150 중량부를 포함할 수 있다.The plastic composition comprises 9 to 20 parts by weight of the copper nanoparticles, 5 to 15 parts by weight of the silane coupling agent, 10 to 20 parts by weight of the antistatic agent, and 50 to 150 parts by weight of the organic solvent with respect to 100 parts by weight of the base resin can do.
상기 베이스 수지는 폴리카보네이트(PC), 폴리프로필렌(PP), 폴리에틸렌(PE), 폴리스티렌(PS) 및 에틸렌 비닐아세테이트(EVA)로 이루어지는 군에서 선택되는 하나 이상을 포함할 수 있다.The base resin may include at least one selected from the group consisting of polycarbonate (PC), polypropylene (PP), polyethylene (PE), polystyrene (PS), and ethylene vinyl acetate (EVA).
상기 구리나노입자는 평균 입자 크기가 500 ~ 700 나노미터(nm)인 것일 수 있다.The copper nanoparticles may have an average particle size of 500 to 700 nanometers (nm).
상기 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)을 1 : 7 ~ 8 : 0.1 ~ 1 의 중량비로 포함할 수 있다.The silane coupling agent is 3-glycidoxy propyl trimethoxysilane (3-Glycidoxy propyl trimethoxysilane), 3-aminopropyl triethoxysilane (3-amino propyl triethoxysilane) and 3-methacryloxypropyl triethoxysilane ( 3 -Methacryloxy propyl triethoxysilane) may be included in a weight ratio of 1: 7 to 8: 0.1 to 1.
상기 대전방지제는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The antistatic agent may include at least one selected from the group consisting of glyceryl monostearate and polyoxyethylene alkylamine.
상기 유기용매는 헥산, 톨루엔, 자일렌, 메탄올, 에탄올, 이소프로판올, 부탄올, 아세톤, 메틸에틸케톤, 메틸이소부틸케톤 및 디메틸아세트아미드로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다. The organic solvent may include at least one selected from the group consisting of hexane, toluene, xylene, methanol, ethanol, isopropanol, butanol, acetone, methyl ethyl ketone, methyl isobutyl ketone and dimethyl acetamide.
상기 플라스틱 포장박스는 상기 플라스틱 조성물을 발포 성형 또는 사출 성형하여 형성된 것일 수 있다.The plastic packaging box may be formed by foam molding or injection molding the plastic composition.
본 발명의 플라스틱 포장박스는 충분한 항균 효과를 구현할 수 있도록 적정량의 구리나노입자를 포함하는 플라스틱 조성물로 형성됨으로써, 항균 효과가 우수하면서도 인장 강도, 충격 강도 등의 기계적 물성이 우수할 수 있다. The plastic packaging box of the present invention is formed of a plastic composition containing an appropriate amount of copper nanoparticles to realize a sufficient antibacterial effect, and thus has excellent antibacterial effect and excellent mechanical properties such as tensile strength and impact strength.
특히, 본 발명의 플라스틱 포장박스는 항균 효과가 우수하여 이를 사용하는 소비자들이 균, 바이러스, 박테리아 등에 노출될 염려를 최소화하면서도 인장 강도, 충격 강도 등의 기계적 물성이 우수하여 내구성 및 사용성이 우수할 수 있다.In particular, the plastic packaging box of the present invention has excellent antibacterial effect and minimizes the risk that consumers who use it will be exposed to bacteria, viruses, bacteria, etc. have.
아래에서는 첨부한 도면을 참조하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예를 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. However, the present invention may be embodied in several different forms and is not limited to the embodiments described herein. And in order to clearly explain the present invention in the drawings, parts irrelevant to the description are omitted.
본 발명의 명세서 및 청구범위에 사용된 용어 또는 단어는 통상적이거나 사전적인 의미로 한정 해석되지 아니하며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms or words used in the specification and claims of the present invention are not to be construed as limited in their ordinary or dictionary meanings, and the inventor may appropriately define the concept of the term in order to best describe his invention. Based on the principle, it should be interpreted as meaning and concept consistent with the technical idea of the present invention.
본 발명의 명세서 전체에 있어서, 어떤 부분이 어떤 구성 요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. In the entire specification of the present invention, when a part "includes" a certain component, it means that other components may be further included, rather than excluding other components unless otherwise stated. .
본 발명의 명세서 전체에 있어서, "A 및/또는 B"는, A 또는 B, 또는 A 및 B를 의미한다.Throughout the specification of the present invention, "A and/or B" means A or B, or A and B.
이하에서 본 발명을 구체적으로 설명하였으나, 본 발명이 이에 제한되는 것은 아니다.Although the present invention has been specifically described below, the present invention is not limited thereto.
본 발명에서는 항균성이 우수한 플라스틱 포장박스를 제공한다.The present invention provides a plastic packaging box having excellent antibacterial properties.
본 발명의 일 실시예에서는 베이스 수지; 구리나노입자; 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)으로 이루어진 군에서 선택되는 하나 이상을 포함하는 실란 커플링제; 대전방지제; 및 유기용매;를 포함하는 플라스틱 조성물을 성형하여 형성된 플라스틱 포장박스를 제공한다.In one embodiment of the present invention, the base resin; copper nanoparticles; 3-Glycidoxy propyl trimethoxysilane, 3 -amino propyl triethoxysilane and 3-Methacryloxy propyl triethoxysilane ) a silane coupling agent comprising at least one selected from the group consisting of; antistatic agent; and an organic solvent; provides a plastic packaging box formed by molding a plastic composition comprising a.
구체적으로, 본 실시예의 플라스틱 조성물은 종래보다 구리 성분을 고함량으로 포함하여 우수한 항균 효과를 구현할 뿐 아니라, 향상된 기계적 물성을 가질 수 있다. 이에 따라, 상기 플라스틱 조성물을 성형하여 형성된 본 실시예의 플라스틱 포장박스는 항균 효과가 우수하여 이를 사용하는 소비자들이 균, 바이러스, 박테리아 등에 노출될 염려를 최소화하면서도 인장 강도, 충격 강도 등의 기계적 물성이 우수하여 내구성 및 사용성이 우수할 수 있다.Specifically, the plastic composition of this embodiment includes a copper component in a higher content than in the prior art, and not only implements an excellent antibacterial effect, but may also have improved mechanical properties. Accordingly, the plastic packaging box of this embodiment formed by molding the plastic composition has excellent antibacterial effect and thus has excellent mechanical properties such as tensile strength and impact strength while minimizing the concern that consumers who use it will be exposed to germs, viruses, bacteria, etc. Therefore, durability and usability can be excellent.
본 실시예의 베이스 수지는 본 실시예에 따르는 플라스틱 조성물의 주요 성분으로서, 예를 들어, 폴리카보네이트(PC), 폴리프로필렌(PP), 폴리에틸렌(PE), 폴리스티렌(PS) 및 에틸렌 비닐아세테이트(EVA)로 이루어지는 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다. 구체적으로, 본 실시예에서는 베이스 수지로 폴리카보네이트를 포함할 수 있으며, 이 경우 우수한 내충격성, 내열성, 내후성, 자기소화성, 투명성, 유연성, 가공성 등의 특성을 구현할 수 있다.The base resin of this embodiment is a main component of the plastic composition according to this embodiment, for example, polycarbonate (PC), polypropylene (PP), polyethylene (PE), polystyrene (PS) and ethylene vinyl acetate (EVA). It may include one or more selected from the group consisting of, but is not limited thereto. Specifically, in this embodiment, polycarbonate may be included as the base resin, and in this case, excellent impact resistance, heat resistance, weather resistance, self-extinguishing properties, transparency, flexibility, processability, etc. may be realized.
본 실시예의 구리나노입자는 구리입자로서, 평균 입자 크기가 나노미터 수준인 것 이라면, 특별히 제한되지 않는다.The copper nanoparticles of this embodiment are copper particles, and as long as the average particle size is at the nanometer level, it is not particularly limited.
예를 들어, 본 실시예의 구리나노입자는 산화구리(Ⅰ)(아산화구리, Cu2O) 및 산화구리(Ⅱ)(CuO)로 이루어진 군에서 선택되는 하나 이상을 포함하는 구리 화합물을 포함할 수 있으나, 이에 제한되지 않는다. 구체적으로, 본 실시예의 구리나노입자는 산화구리(Ⅰ)(아산화구리, Cu2O)를 포함할 수 있으며, 이때, 더욱 우수한 항균 효과를 구현할 수 있다.For example, the copper nanoparticles of this embodiment may include a copper compound including at least one selected from the group consisting of copper (I) oxide (copper oxide, Cu 2 O) and copper (II) oxide (CuO). However, it is not limited thereto. Specifically, the copper nanoparticles of this embodiment may include copper (I) oxide (copper oxide, Cu 2 O), and in this case, it is possible to implement a more excellent antibacterial effect.
본 실시예의 구리나노입자는 평균 입자 크기가 500 ~ 700 나노미터, 구체적으로는 520 ~ 650 나노미터, 더 구체적으로는 550 ~ 600 나노미터일 수 있다.The copper nanoparticles of this embodiment may have an average particle size of 500 to 700 nanometers, specifically 520 to 650 nanometers, and more specifically 550 to 600 nanometers.
특히, 본 실시예의 구리나노입자의 평균 입자 크기가 500 ~ 700 나노미터로 형성될 때, 구리나노입자의 평균 입자 크기가 500 나노미터 미만이거나 700 나노미터 초과인 경우 보다, 더욱 우수한 항균 효과 및 기계적 물성을 구현할 수 있다.In particular, when the average particle size of the copper nanoparticles of this embodiment is formed to be 500 to 700 nanometers, more excellent antibacterial effect and mechanical properties than when the average particle size of the copper nanoparticles is less than 500 nanometers or greater than 700 nanometers properties can be realized.
본 실시예의 플라스틱 조성물은 상기 베이스 수지 100 중량부에 대해 상기 구리나노입자 9 ~ 20 중량부, 구체적으로는 10 ~ 15 중량부, 더 구체적으로는 10 ~ 12 중량부를 포함할 수 있다.The plastic composition of this embodiment may contain 9 to 20 parts by weight of the copper nanoparticles, specifically 10 to 15 parts by weight, and more specifically 10 to 12 parts by weight, based on 100 parts by weight of the base resin.
특히, 본 실시예의 플라스틱 조성물이 상기 베이스 수지 100 중량부에 대해 상기 구리나노입자 9 ~ 20 중량부로 포함할 때, 상기 베이스 수지 100 중량부에 대해 상기 구리나노입자를 9 중량부 미만으로 포함하거나 20 중량부 초과로 포함하는 경우 보다, 더욱 우수한 항균 효과 및 기계적 물성을 구현할 수 있다. 한편, 본 실시예의 플라스틱 조성물이 상기 베이스 수지 100 중량부에 대해 상기 구리나노입자를 20 중량부로 초과하여도, 항균 효과의 향상 정도에 차이가 미미하여, 경제적이지 못할 수 있다.In particular, when the plastic composition of this embodiment contains 9 to 20 parts by weight of the copper nanoparticles with respect to 100 parts by weight of the base resin, less than 9 parts by weight of the copper nanoparticles with respect to 100 parts by weight of the base resin, or 20 When included in more than parts by weight, it is possible to implement more excellent antibacterial effect and mechanical properties. On the other hand, even if the plastic composition of this embodiment exceeds 20 parts by weight of the copper nanoparticles based on 100 parts by weight of the base resin, the difference in the degree of improvement in the antibacterial effect is insignificant, which may not be economical.
본 실시예의 실란 커플링제는 베이스 수지와 구리나노입자의 계면 간의 상용성을 높이는 것으로서, 공지의 실란계 성분이 포함될 수 있다.The silane coupling agent of this embodiment improves compatibility between the interface between the base resin and the copper nanoparticles, and a known silane-based component may be included.
예를 들어, 본 실시예의 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.For example, the silane coupling agent of this embodiment is 3-Glycidoxy propyl trimethoxysilane, 3-amino propyl triethoxysilane, and 3-methacryloxy. It may include at least one selected from the group consisting of propyl triethoxysilane ( 3 -Methacryloxy propyl triethoxysilane).
구체적으로, 본 실시예의 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)를 포함할 수 있다. 특히, 본 실시예에서는 실란 커플링제로 에폭시기를 포함하는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 아미노기를 포함하는 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 (메타)아크릴기를 포함하는 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)을 모두 포함함으로써, 항균 효과가 우수하면서도 기계적 물성이 우수한, 플라스틱 조성물을 제공할 수 있다.Specifically, the silane coupling agent of this embodiment is 3-Glycidoxy propyl trimethoxysilane, 3-aminopropyl triethoxysilane, and 3-methacryloxypropyl It may include triethoxysilane ( 3 -Methacryloxy propyl triethoxysilane). In particular, in this embodiment, as a silane coupling agent, 3-Glycidoxy propyl trimethoxysilane containing an epoxy group, 3-aminopropyl triethoxysilane containing an amino group, and 3-amino propyl triethoxysilane ) and 3 -methacryloxypropyl triethoxysilane including a (meth)acryl group, it is possible to provide a plastic composition having excellent antibacterial effect and excellent mechanical properties.
더 구체적으로, 본 실시예의 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)를 1 : 7 ~ 8 : 0.1 ~ 1 중량부로 포함할 수 있다. 특히, 본 실시예에서는 실란 커플링제를 상기의 비율로 포함함으로써, 더욱 우수한 항균 효과 및 기계적 물성을 갖는, 플라스틱 조성물을 제공할 수 있다.More specifically, the silane coupling agent of this embodiment is 3-Glycidoxy propyl trimethoxysilane, 3-aminopropyl triethoxysilane, and 3-methacryloxy. Propyl triethoxysilane ( 3 -Methacryloxy propyl triethoxysilane) may be included in an amount of 1: 7 to 8: 0.1 to 1 parts by weight. In particular, in this embodiment, by including the silane coupling agent in the above ratio, it is possible to provide a plastic composition having a more excellent antibacterial effect and mechanical properties.
가장 구체적으로, 본 실시예의 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)를 1 : 7 ~ 8 : 0.3 ~ 0.5 중량부로 포함할 수 있다. 특히, 본 실시예에서는 실란 커플링제를 상기의 비율로 포함함으로써, 현저히 우수한 항균 효과 및 기계적 물성을 갖는, 플라스틱 조성물을 제공할 수 있다.Most specifically, the silane coupling agent of this embodiment is 3-Glycidoxy propyl trimethoxysilane, 3-amino propyl triethoxysilane, and 3-methacryloxy. Propyltriethoxysilane ( 3 -Methacryloxy propyl triethoxysilane) may be included in an amount of 1: 7 to 8: 0.3 to 0.5 parts by weight. In particular, in this embodiment, by including the silane coupling agent in the above ratio, it is possible to provide a plastic composition having remarkably excellent antibacterial effect and mechanical properties.
본 실시예의 플라스틱 조성물은 상기 베이스 수지 100 중량부에 대해 상기 실란 커플링제 5 ~ 15 중량부, 구체적으로는 7 ~ 13 중량부, 더 구체적으로는 10 ~ 12 중량부로 포함할 수 있다.The plastic composition of this embodiment may include 5 to 15 parts by weight of the silane coupling agent, specifically 7 to 13 parts by weight, and more specifically 10 to 12 parts by weight based on 100 parts by weight of the base resin.
특히, 본 실시예의 플라스틱 조성물이 상기 베이스 수지 100 중량부에 대해 상기 실란 커플링제를 5 ~ 15 중량부로 포함할 때, 상기 베이스 수지 100 중량부에 대해 상기 실란 커플링제를 5 중량부 미만으로 포함하거나 15 중량부 초과로 포함하는 경우 보다, 더욱 우수한 항균 효과 및 기계적 물성을 가질 수 있다.In particular, when the plastic composition of this embodiment contains 5 to 15 parts by weight of the silane coupling agent with respect to 100 parts by weight of the base resin, less than 5 parts by weight of the silane coupling agent is included with respect to 100 parts by weight of the base resin, or When included in more than 15 parts by weight, it may have better antibacterial effect and mechanical properties.
본 실시예의 대전방지제는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.The antistatic agent of this embodiment may include one or more selected from the group consisting of glyceryl monostearate and polyoxyethylene alkylamine, but is not limited thereto.
구체적으로, 본 실시예의 대전방지제는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민을 포함할 수 있다.Specifically, the antistatic agent of this embodiment may include glyceryl monostearate and polyoxyethylenealkylamine.
더 구체적으로, 본 실시예의 대전방지제는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민을 1 : 2 의 중량비로 포함할 수 있다. 특히, 본 실시예의 대전방지제는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민을 1 : 2의 중량비로 포함할 때, 우수한 대전방지 효과를 구현할 수 있다.More specifically, the antistatic agent of this embodiment may include glyceryl monostearate and polyoxyethylenealkylamine in a weight ratio of 1:2. In particular, when the antistatic agent of this embodiment contains glyceryl monostearate and polyoxyethylene alkylamine in a weight ratio of 1: 2, an excellent antistatic effect can be realized.
본 실시예의 플라스틱 조성물은 상기 베이스 수지 100 중량부에 대해 상기 대전방지제를 10 ~ 20 중량부, 구체적으로는 12 ~ 15 중량부로 더 포함할 수 있다.The plastic composition of this embodiment may further include 10 to 20 parts by weight of the antistatic agent, specifically 12 to 15 parts by weight, based on 100 parts by weight of the base resin.
특히, 본 실시예의 플라스틱 조성물이 상기 베이스 100 중량부에 대해 상기 대전방지제를 10 ~ 20 중량부로 더 포함할 때, 상기 베이스 수지 100 중량부에 대해 상기 대전방지제를 10 중량부 미만으로 포함하거나 20 중량부 초과로 포함할 경우 보다, 본 실시예의 플라스틱 조성물은 우수한 항균 효과 및 기계적 물성과 함께 대전 방지 효과를 구현할 수 있다.In particular, when the plastic composition of this embodiment further comprises 10 to 20 parts by weight of the antistatic agent with respect to 100 parts by weight of the base, less than 10 parts by weight or 20 parts by weight of the antistatic agent with respect to 100 parts by weight of the base resin When included in more than part, the plastic composition of this embodiment can implement an antistatic effect with excellent antibacterial effect and mechanical properties.
본 실시예의 유기용매는 헥산, 톨루엔, 자일렌, 메탄올, 에탄올, 이소프로판올, 부탄올, 아세톤, 메틸에틸케톤, 메틸이소부틸케톤 및 디메틸아세트아미드로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않으며, 공지의 모든 유기용매를 포함할 수 있다.The organic solvent of this embodiment may include at least one selected from the group consisting of hexane, toluene, xylene, methanol, ethanol, isopropanol, butanol, acetone, methyl ethyl ketone, methyl isobutyl ketone and dimethyl acetamide, but this It is not limited, and may include all known organic solvents.
본 실시예의 플라스틱 조성물은 상기 베이스 수지 100 중량부에 대해 상기 유기용매 50 ~ 150 중량부, 구체적으로 55 ~ 90 중량부, 더 구체적으로는 60 ~ 80 중량부로 포함할 수 있다.The plastic composition of this embodiment may include 50 to 150 parts by weight of the organic solvent, specifically 55 to 90 parts by weight, and more specifically 60 to 80 parts by weight, based on 100 parts by weight of the base resin.
특히, 본 실시예의 플라스틱 조성물이 상기 베이스 수지 100 중량부에 대해 상기 유기용매를 50 ~ 150 중량부로 포함할 때, 상기 베이스 수지 100 중량부에 대해 상기 유기용매를 50 중량부 미만으로 포함하거나 150 중량부 초과로 포함하는 경우 보다, 더욱 우수한 항균 효과 및 기계적 물성을 구현할 수 있다.In particular, when the plastic composition of this embodiment contains 50 to 150 parts by weight of the organic solvent based on 100 parts by weight of the base resin, less than 50 parts by weight or 150 parts by weight of the organic solvent with respect to 100 parts by weight of the base resin When included in excess of parts, it is possible to implement a more excellent antibacterial effect and mechanical properties.
본 실시예의 플라스틱 조성물은 상기된 성분 이외에 경화제, 보조경화제, 경화안정제, 계면활성제, 무기필러, pH 조절제, 산화안정제, 열안정제, 유기산, 방염제, 난연제, 녹방지제, 방청제, 오일, 분산제, 분산안정제, 커플링제, 가소제 및 소포제로 이루어진 군에서 선택되는 하나 이상을 포함하는 첨가제를 더 포함할 수 있다. 이때, 첨가제의 사용량은 필요에 따라 적절하게 조절될 수 있다. In addition to the above components, the plastic composition of this embodiment contains a curing agent, an auxiliary curing agent, a curing stabilizer, a surfactant, an inorganic filler, a pH adjuster, an oxidation stabilizer, a heat stabilizer, an organic acid, a flame retardant, a flame retardant, a rust inhibitor, a rust inhibitor, an oil, a dispersant, a dispersion stabilizer , may further include an additive comprising at least one selected from the group consisting of a coupling agent, a plasticizer and an antifoaming agent. In this case, the amount of the additive used may be appropriately adjusted as necessary.
본 실시예의 플라스틱 포장박스는 상기된 플라스틱 조성물을 성형하여 형성된 것이며, 구체적으로는, 상기 플라스틱 조성물을 발포 성형 또는 사출 성형하여 형성된 것일 수 있다. 상기 성형은 공지의 방법과 조건에 따라 실시될 수 있다.The plastic packaging box of this embodiment is formed by molding the above-mentioned plastic composition, and specifically, it may be formed by foam molding or injection molding of the plastic composition. The molding may be performed according to known methods and conditions.
본 실시예의 플라스틱 포장박스는 물건의 수납이 가능한 공지된 박스 형태라면, 그 형태는 특별히 제한되지 않는다.The plastic packaging box of this embodiment is not particularly limited as long as it is in the form of a known box capable of accommodating things.
예를 들어, 본 실시예의 플라스틱 포장박스는 플라스틱 조성물을 성형하여 복수의 판을 제조하고, 이들 각각을 하판, 측판, 상판으로 하여 조립된 공지의 박스 형태로 형성될 수 있으나, 이에 제한되지 않는다.For example, the plastic packaging box of this embodiment may be formed in a known box shape assembled by manufacturing a plurality of plates by molding a plastic composition, and using each of these as a lower plate, a side plate, and an upper plate, but is not limited thereto.
이하 실시예, 비교예, 및 실험예를 통하여 본 발명의 항균성이 우수한 플라스틱 포장박스에 대해 구체적으로 설명하기로 한다. 이들 실시예는 단지 본 발명을 예시하기 위한 것이므로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다.Hereinafter, the plastic packaging box having excellent antibacterial properties of the present invention will be described in detail through Examples, Comparative Examples, and Experimental Examples. These examples are only for illustrating the present invention and should not be construed as limiting the scope of the present invention by these examples.
[ 실시예 ][Example]
실시예 1 내지 5Examples 1 to 5
폴리카보네이트 100 중량부에 대해 구리나노입자 12 중량부, 실란 커플링제 12 중량부, 대전방지제 15 중량부 및 유기용매 80 중량부를 혼합하여 플라스틱 조성물을 제조하였다.A plastic composition was prepared by mixing 12 parts by weight of copper nanoparticles, 12 parts by weight of a silane coupling agent, 15 parts by weight of an antistatic agent, and 80 parts by weight of an organic solvent based on 100 parts by weight of polycarbonate.
이어서, 상기 플라스틱 조성물을 공지된 방법에 의해 사출 성형함으로써, 플라스틱을 제조하였다.Then, by injection molding the plastic composition by a known method, a plastic was produced.
이때, 상기 구리나노입자는 평균 입자 크기가 550 ~ 600 나노미터인 것을 사용하였으며, 구체적으로는 산화구리(Ⅰ)(아산화구리, Cu2O)를 사용하였다.In this case, as the copper nanoparticles, those having an average particle size of 550 to 600 nanometers were used, and specifically, copper (I) oxide (copper oxide, Cu 2 O) was used.
또한, 유기용매로는 톨루엔 및 메틸에틸케톤을 동량 혼합하여 사용하였고, 상기 대전방지제로는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민을 1 : 2의 중량비로 혼합한 것을 사용하였다.In addition, as the organic solvent, toluene and methyl ethyl ketone were mixed in equal amounts, and as the antistatic agent, a mixture of glyceryl monostearate and polyoxyethylene alkylamine in a weight ratio of 1:2 was used.
또한, 실란 커플링제는 3-글리시독시프로필트리메톡시실란, 3-아미노프로필트리에톡시실란 및 3-메타크릴옥시프로필트리에톡시실란이 표 1[단위 : 중량비 ]에 개시된 비율로 혼합된 것을 사용하였다.In addition, the silane coupling agent is a mixture of 3-glycidoxypropyltrimethoxysilane, 3-aminopropyltriethoxysilane and 3-methacryloxypropyltriethoxysilane in the ratio disclosed in Table 1 [unit: weight ratio]. that was used
[ 비교예 ][ Comparative Example ]
비교예 1 내지 6Comparative Examples 1 to 6
표 2[단위 : 중량부]에 따라, 폴리카보네이트, 구리나노입자, 실란커플링제 및 유기용매를 혼합하여 플라스틱 조성물을 제조한 것을 제외하고는, 실시예 3과 동일하게 실시하였다.According to Table 2 [unit: parts by weight], polycarbonate, copper nanoparticles, a silane coupling agent and an organic solvent were mixed to prepare a plastic composition, and the same procedure as in Example 3 was performed.
비교예 7 내지 9Comparative Examples 7 to 9
표 3에 '○' 표시된 성분만을 실란 커플링제로 포함하는 것을 제외하고는, 실시예 3과 동일하게 실시하였다.Example 3 was carried out in the same manner as in Example 3, except that only the components indicated by '○' in Table 3 were included as the silane coupling agent.
비교예 10 내지 12Comparative Examples 10 to 12
표 4[단위 : 중량비]에 따라, 각 성분을 혼합하여 실란 커플링제로 포함하는 것을 제외하고는, 실시예 3과 동일하게 실시하였다.According to Table 4 [unit: weight ratio], it was carried out in the same manner as in Example 3, except that each component was mixed and included as a silane coupling agent.
비교예 13 내지 14Comparative Examples 13 to 14
표 5[단위 : 나노미터]의 평균 입자 크기를 가지는 구리나노입자를 포함하는 것을 제외하고는, 실시예 3과 동일하게 실시하였다.Example 3 was carried out in the same manner as in Example 3, except that copper nanoparticles having an average particle size of Table 5 [unit: nanometers] were included.
[ 실험예 ][Experimental example]
실험예 1 : 항균력 평가Experimental Example 1: Evaluation of antibacterial activity
[KCL-FIR-1003 : 2018]에 따라 항균성을 평가하였으며, 그 결과를 표 6[단위 : %]에 나타내었다.Antimicrobial properties were evaluated according to [KCL-FIR-1003: 2018], and the results are shown in Table 6 [unit: %].
구체적으로, 대장균 (Escherichia coli ATCC 8739) 3.7×105 CFU/㎖, 황색포도상구균(staphylococos aureus ATCC 6538P) 3.4×105 CFU/㎖ 을 초기농도(A0)로 접종하고, 37.0 ± 0.2 ℃에서 약 24 시간 동안 방치한 후의 농도(A1) 를 구하여, 하기 식을 이용하여 세균감소율(B)을 확인한 뒤, 그 결과를 하기 표 6에 기재하였다.Specifically, Escherichia coli ATCC 8739) 3.7 × 10 5 CFU / ㎖, Staphylococcus aureus ( staphylococos aureus ATCC 6538P) 3.4 × 10 5 CFU / ㎖ inoculated at the initial concentration (A 0 ), and inoculated at 37.0 ± 0.2 ℃ After standing for about 24 hours, the concentration (A 1 ) was obtained, and the bacterial reduction rate (B) was confirmed using the following formula, and the results are shown in Table 6 below.
상기 세균감소율은 (A0-A1)/A0×100으로 산출하였다. 이때, 대조군으로는 무처리군을 준비하였다.The bacterial reduction rate was calculated as (A 0 -A 1 )/A 0 × 100. At this time, an untreated group was prepared as a control group.
이때, 표 6에서 세균감소율은 소수점 이하 세 번째 자리에서 반올림하여, 소수점 이하 두 번째 자리까지만 표기하였다At this time, in Table 6, the bacterial reduction rate was rounded to the third decimal place, and only the second decimal place was indicated.
표 6을 보면, 본 실시예에 따를 경우, 항균 효과가 우수함을 알 수 있다. 구체적으로, 본 실시예에 따를 경우에는, 특정 조합의 실란 커플링제를 사용하여, 구리나노분말과 베이스 수지 간의 상용성을 향상시킴으로써, 균일하면서도 우수한 항균 효과를 구현할 수 있다.Referring to Table 6, it can be seen that, according to the present embodiment, the antibacterial effect is excellent. Specifically, according to this embodiment, by using a specific combination of a silane coupling agent to improve the compatibility between the copper nanopowder and the base resin, it is possible to implement a uniform and excellent antibacterial effect.
구체적으로, 실시예 및 비교예 2를 비교하면, 과량의 구리나노입자를 포함하여도 항균 효과의 향상 정도에 차이가 없어, 경제성을 위해서는 적정량의 구리나노입자를 포함하는 것이 바람직할 수 있다.Specifically, comparing Example and Comparative Example 2, even if an excessive amount of copper nanoparticles is included, there is no difference in the degree of improvement of the antibacterial effect, and it may be preferable to include an appropriate amount of copper nanoparticles for economic efficiency.
또한, 실시예 및 비교예 13 내지 14를 비교하면, 동량의 구리나노입자를 포함하더라도, 구리나노입자의 입자크기가 500 ~ 700 나노미터로 형성될 때, 구리나노입자가 조성물 내에 균일하게 분산되어, 항균 효과가 더욱 향상됨을 알 수 있다.In addition, comparing Examples and Comparative Examples 13 to 14, even if the copper nanoparticles are included in the same amount, when the copper nanoparticles have a particle size of 500 to 700 nanometers, the copper nanoparticles are uniformly dispersed in the composition. , it can be seen that the antibacterial effect is further improved.
실험예 2 : 기계적 물성 평가Experimental Example 2: Evaluation of mechanical properties
실시예 및 비교예의 플라스틱 조성물을 이용하여, 하기에 따라 (1)인장강도 및 (2)충격강도를 실시한 뒤, 그 결과를 표 7에 나타내었다.Using the plastic compositions of Examples and Comparative Examples, (1) tensile strength and (2) impact strength were performed according to the following, and the results are shown in Table 7.
(1) 인장 강도[단위 : kg/cm2] : ASTM D638에 준하여 측정하였다. (1) Tensile strength [unit: kg/cm 2 ]: It was measured according to ASTM D638.
(2) 충격 강도[단위 : kg·cm/cm] : ASTM D256에 준하여 측정하였다. (2) Impact strength [unit: kg·cm/cm]: measured according to ASTM D256.
[단위 : kg/cm[Unit: kg/cm
22
]]
[단위 : kg·cm/cm][Unit: kg cm/cm]
표 7을 보면, 본 실시예에 따를 경우, 인장 강도, 충격 강도 등의 기계적 물성이 우수함을 알 수 있다.Referring to Table 7, it can be seen that, according to the present embodiment, mechanical properties such as tensile strength and impact strength are excellent.
상기 실험예 1 및 2를 종합하면, 본 실시예에 따를 경우에는, 항균 효과가 우수하면서도 기계적 물성이 현저히 향상된, 플라스틱 조성물 및 이로 형성된 플라스틱 포장박스를 제공할 수 있음을 알 수 있다.Combining the above Experimental Examples 1 and 2, it can be seen that, according to the present embodiment, a plastic composition and a plastic packaging box formed therewith having excellent antibacterial effect and remarkably improved mechanical properties can be provided.
[ 제조예 ][ Manufacturing Example ]
제조예 1 : 플라스틱 포장박스의 제조Preparation Example 1: Preparation of plastic packaging box
상기 실시예 1에 따르는 플라스틱 조성물을 사출 성형하여, 하판, 측판, 상판을 각각 형성하였다.The plastic composition according to Example 1 was injection molded to form a lower plate, a side plate, and an upper plate, respectively.
구체적으로, 네 개의 모서리를 가지는 하판, 상기 하판의 네 개의 모서리에 수직으로 결합하는 네 개의 측판 및 네 개의 모서리를 가지는 상판을 각각 제조한 뒤, 이들을 공지의 박스 형상으로 조립함으로써, 플라스틱 포장박스를 제조하였다.Specifically, by manufacturing a lower plate having four corners, four side plates vertically coupled to the four corners of the lower plate, and an upper plate having four corners, respectively, and assembling them into a known box shape, a plastic packaging box prepared.
전술한 바와 같이, 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 기술을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.As described above, the description of the present invention is for illustration, and those of ordinary skill in the art to which the present invention pertains can easily transform into other specific forms without changing the technical spirit or essential features of the present invention. You will understand. Therefore, it should be understood that the embodiments described above are illustrative in all respects and not restrictive. For example, each component described as a single type may be implemented in a dispersed form, and likewise components described as distributed may be implemented in a combined form.
본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is indicated by the following claims rather than the above detailed description, and all changes or modifications derived from the meaning and scope of the claims and their equivalents should be interpreted as being included in the scope of the present invention. do.
Claims (8)
상기 플라스틱 조성물은 상기 베이스 수지 100 중량부에 대해 상기 구리나노입자 9 ~ 20 중량부, 상기 실란 커플링제 5 ~ 15 중량부, 상기 대전방지제 10 ~ 20 중량부 및 상기 유기용매 50 ~ 150 중량부를 포함하되,
상기 구리나노입자는 평균 입자 크기가 500 ~ 700 나노미터(nm)인 것이고,
상기 실란 커플링제는 3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)을 포함하며,
상기 대전방지제는 글리세릴 모노스테아레이트 및 폴리옥시에틸렌알킬아민을 포함하는 것을 특징으로 하는, 항균성이 우수한 플라스틱 포장박스
It relates to a plastic packaging box formed of a plastic composition comprising a base resin, copper nanoparticles, a silane coupling agent, an antistatic agent and an organic solvent,
The plastic composition comprises 9 to 20 parts by weight of the copper nanoparticles, 5 to 15 parts by weight of the silane coupling agent, 10 to 20 parts by weight of the antistatic agent, and 50 to 150 parts by weight of the organic solvent with respect to 100 parts by weight of the base resin but,
The copper nanoparticles have an average particle size of 500 to 700 nanometers (nm),
The silane coupling agent is 3-glycidoxy propyl trimethoxysilane (3-Glycidoxy propyl trimethoxysilane), 3-aminopropyl triethoxysilane (3-amino propyl triethoxysilane) and 3-methacryloxypropyl triethoxysilane ( 3 -Methacryloxy propyl triethoxysilane),
The antistatic agent, characterized in that it comprises glyceryl monostearate and polyoxyethylene alkylamine, plastic packaging box with excellent antibacterial properties
상기 베이스 수지는
폴리카보네이트(PC), 폴리프로필렌(PP), 폴리에틸렌(PE), 폴리스티렌(PS) 및 에틸렌 비닐아세테이트(EVA)로 이루어지는 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는, 항균성이 우수한 플라스틱 포장박스.
The method of claim 1,
The base resin is
Polycarbonate (PC), polypropylene (PP), polyethylene (PE), polystyrene (PS) and ethylene vinyl acetate (EVA), characterized in that it contains at least one selected from the group consisting of, plastic packaging box with excellent antibacterial properties .
상기 실란 커플링제는
3-글리시독시프로필트리메톡시실란(3-Glycidoxy propyl trimethoxysilane), 3-아미노프로필트리에톡시실란(3-amino propyl triethoxysilane) 및 3-메타크릴옥시프로필트리에톡시실란(3-Methacryloxy propyl triethoxysilane)을 1 : 7 ~ 8 : 0.1 ~ 1 의 중량비로 포함하는 것을 특징으로 하는, 항균성이 우수한 플라스틱 포장박스.
The method of claim 1,
The silane coupling agent
3-Glycidoxy propyl trimethoxysilane, 3 -amino propyl triethoxysilane and 3-Methacryloxy propyl triethoxysilane ) 1: 7 to 8: A plastic packaging box with excellent antibacterial properties, characterized in that it contains a weight ratio of 0.1 to 1.
상기 유기용매는
헥산, 톨루엔, 자일렌, 메탄올, 에탄올, 이소프로판올, 부탄올, 아세톤, 메틸에틸케톤, 메틸이소부틸케톤 및 디메틸아세트아미드로 이루어진 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는, 항균성이 우수한 플라스틱 포장박스.
The method of claim 1,
The organic solvent is
Plastic packaging with excellent antibacterial properties, characterized in that it contains at least one selected from the group consisting of hexane, toluene, xylene, methanol, ethanol, isopropanol, butanol, acetone, methyl ethyl ketone, methyl isobutyl ketone and dimethyl acetamide box.
상기 플라스틱 포장박스는
상기 플라스틱 조성물을 발포 성형 또는 사출 성형하여 형성된 것임을 특징으로 하는, 항균성이 우수한 플라스틱 포장박스.The method of claim 1,
The plastic packaging box
A plastic packaging box having excellent antibacterial properties, characterized in that it is formed by foam molding or injection molding of the plastic composition.