KR102456140B1 - Hfo 함유 셀 가스를 가진 단열 중간 파이프 - Google Patents
Hfo 함유 셀 가스를 가진 단열 중간 파이프 Download PDFInfo
- Publication number
- KR102456140B1 KR102456140B1 KR1020197001436A KR20197001436A KR102456140B1 KR 102456140 B1 KR102456140 B1 KR 102456140B1 KR 1020197001436 A KR1020197001436 A KR 1020197001436A KR 20197001436 A KR20197001436 A KR 20197001436A KR 102456140 B1 KR102456140 B1 KR 102456140B1
- Authority
- KR
- South Korea
- Prior art keywords
- pipe
- vol
- barrier
- hfo
- insulation
- Prior art date
Abstract
본 발명은 적어도 하나의 중간 파이프(4), 상기 중간 파이프 둘레에 배치된 적어도 하나의 단열재(3) 및 상기 단열재 둘레에 배치된 적어도 하나의 외부 재킷(2)을 포함하되, 옵션으로서 상기 외부 재킷(2)은 가능하게는 플라스틱으로 제조된 장벽(9)을 포함하며, 상기 단열재(3)는 발포체를 포함하고, 상기 발포체의 셀 가스는 적어도 10 vol%의 HFO를 함유하는, 단열 도관 파이프(1)에 관한 것이다. 이러한 도관 파이프는 양호한 절연 거동, 양호한 환경 밸런스를 갖고 있으며, 간단한 방식으로 생산할 수 있다.
Description
본 발명은 단열재, 특히 단열 중간 파이프를 함유하는 파이프 시스템 및 단열이 향상된 도관 파이프를 연결하기 위한 단열 커버 장치 또는 부싱(bushing)에 관한 것이다. 또한, 본 발명은 이러한 장치의 제조 방법 및 상기 장치에 사용되는 하이드로플루오로올레핀(HFO)을 함유하는 중합체 발포체의 용도 및 상기 장치의 제조 방법에 관한 것이다. 마지막으로, 본 발명은 단열재에 셀 가스(cell gas)로서 사용되는 HFO의 용도에 관한 것이다.
사전 절연된(pre-insulated) 파이프 시스템 또는 단열 파이프 시스템이라고도 불리는 단열재를 함유하는 파이프 시스템은 그 자체가 알려져 있고 입증되어 있다. 이러한 파이프 시스템은 단열재로 둘러싸인 가요성 또는 강성 중간 파이프를 포함하며, 상기 파이프는 단열재로 둘러싸여 있고, 즉 재킷, 및 또한 아마도 부싱 및/또는 커버 장치로 둘러싸여 있다. 구성에 따라 이러한 사전 절연된 파이프 시스템은 플라스틱 중간 파이프 시스템(PMP) 또는 플라스틱 재킷화된 파이프 시스템(PJP)이라고도 불린다. 전자의 경우, 사용된 중간 파이프는 특정한 가요성을 갖고 있어, 복합재 전체가 특정한 힘의 적용으로 드럼에 권선될 수 있다. 따라서, 이것은 가요성 파이프 시스템이라고도 지칭된다. 후자의 경우, 사용된 중간 파이프는 비가요성이어서, 전체 복합재의 경우에 강성 파이프 시스템이라고 지칭된다. 따라서, 하나 이상의 단열층을 갖는 단열된 중간 파이프 또는 도관 파이프는 공지되어 있고; 이의 생산 방법도 공지되어 있다. 즉 단열된 중간 파이프를 연속 생산하는 방법은 EP0897788 및 EP2213440에 공지되어 있다. 개별적인 강성 파이프 구역을 생산하는 방법은 EP2248648에 공지되어 있다.
이러한 파이프 시스템에서, 단열재로 일반적으로 사용되는 발포체(예, 폴리 우레탄, PU)는 시간이 지남에 따라 셀 가스의 조성이 변한다. 이는 질소와 산소가 주위 환경으로부터 발포체 내로 확산되고, 발포체에 원래 함유된 발포체 가스 및/또는 셀 가스, 특히 이산화탄소 및 기타 팽창제(blowing agent)가 발포체 외로 확산됨으로써 일어난다. 공기 기체는 원래 함유된 이산화탄소 및 다른 전형적으로 사용되는 팽창제보다 열전도도가 훨씬 더 높다.
외부 재킷에 소위 장벽(barrier) 층의 통합은 이러한 확산 공정을 최소화하기 위해 제안되었다.
장벽 층으로 금속 층이 사용될 수 있다. 금속층이 사용되면 희망하는 기체 교환이 완전히 억제될뿐만 아니라 수증기의 확산도 완전히 방지된다. 이것은 특히 중간 파이프가 플라스틱으로 제조된 것이 사용되는 경우에 문제가 되는데, 그 이유는 물이 일반적으로 매질처럼 파이프를 통해 흐르기 때문이며, 이로 인해 수증기가 소량일지라도 벽을 통해 연속적으로 이동한다. 상기 수증기는 외측으로 투과하고/투과하거나 주위환경과 평형에 이를 가능성을 가져야 하는데, 그 이유는 그렇지 않으면 물이 시간이 지남에 따라 단열된 도관 파이프의 단열재 내에 채워져서 열전도도가 상당히 상승하고 단열재가 장기적으로 손상될 위험이 있기 때문이다.
하나 이상의 중합체 물질로 이루어진 층이 장벽 층으로 사용될 수 있다. 따라서, EP1355103은 에틸렌 비닐 알콜(EVOH), 폴리아미드(PA) 또는 폴리비닐리덴 클로라이드(PVDC)로 만들어진 장벽 층을 함유하는 단열된 도관 파이프를 기술하고 있다. 또한, EP2340929는 외부 재킷이 다층 파이프로서 형성되고 내부에 가스 투과 장벽 층("장벽")을 갖는, 플라스틱 재킷화된 파이프를 기술하고 있다. 상기 문헌들에 기술된 파이프는 생산이 어렵고(어렵거나) 부적절한 절연 성능을 갖고 있다. 단열재 및 중합체 장벽층을 갖는 도관 파이프는 CH710709(후 공개) 및 WO2004/003423에 공지되어 있고; 이들 중합체는 폴리케톤 및/또는 EVOH를 함유한다.
성형 부품 및 연결 조각(piece)은 단열 파이프를 연결하는데 사용된다. 특히, 커버 셸(cover shell)은 WO2008/019791에 기술된 바와 같이 성형 부품으로 사용된다. 또는 부싱은 연결 조각으로, 특히 강성 파이프의 연결 시에 사용된다. 이러한 성형 부품 및 연결 조각의 경우에도 전술한 문제점들이 발생한다.
본 발명의 목적은 전술한 단점을 갖지 않는 단열 도관 파이프 및 또한 성형 부품 및 연결 조각도 제공하는 것이다.
상기 요약된 목적은 독립항에 따라 달성된다. 종속항은 유리한 구체예들을 나타낸다. 추가 유리한 구체예는 상세한 설명 및 도면으로부터 추론될 수 있다. 본 발명과 관련하여 제공되는 일반 구체예, 바람직한 구체예 및 특히 바람직한 구체예, 범위 등은 필요한 경우 서로 조합될 수 있다. 또한, 개별적인 정의들, 구체예들 등은 또한 생략될 수 있고 및/또는 무관할 수 있다.
이하, 본 발명이 상세히 설명된다. 이하 개시되고 설명되는 다양한 구체예, 선호도 및 범위는 필요한 경우 서로 조합될 수 있음은 분명하다. 또한, 개개의 정의, 선호도 및 범위는 구체예에 따라 적용되지 않을 수 있다. 또한, "포함하는"이라는 용어는 "함유하는" 및 "로 이루어지는"의 의미를 포함한다.
본 발명에 사용된 용어는 당업자에게 일반적으로 통상적인 의미로 사용된다. 직접적인 문맥에서 다른 의미가 나타나지 않는다면, 다음 용어들은 특히 이 경우에 여기에 제시된 의미/정의를 갖는다.
본 발명은 도면들에 의해 더 상세히 설명된다; 다음의 설명 외에도 본 발명의 다른 구체예가 이들 도면으로부터 추론될 수 있다.
도 1은 본 발명에 따른 도관 파이프(1)의 구성을 단면도로 개략적으로 도시한 것이다. 이 경우, (2)는 외측(6)이 주위 환경을 향하고 내측(5)이 단열재를 향하는 외부 재킷이고; (3)은 셀 가스를 가진 단열재를 나타내고; (4)는 중간 파이프이다.
도 2는 외부 재킷(2)의 바람직한 구체예의 구성을 개략적으로 도시한 것이다. 이 경우, (7)은 외부 중합체 층(특히, 열가소성)이고; (8)은 외부 접착 촉진제 층이고, (9)는 장벽 층이며, (10)은 내부 접착 촉진제 층이고, (11)은 내부 중합체 층(특히, 열가소성)이다.
도 3은 셀 가스의 조성(단위 vol%의 세로 좌표)에 따라 50℃에서 측정된 PU 발포체의 열전도도 값(단위 mW/m*K의 가로 좌표)의 의존성을 그래프로 나타낸 것이다. 사각형은 사이클로펜탄을 나타내고, 원은 CO2를 나타내며 삼각형은 HFO를 나타낸다.
도 4는 셀 가스 조성(단위 vol%의 세로 좌표)에 따라 PU 발포체의 평균 소공 크기(단위 ㎛의 가로 좌표)를 그래프로 나타낸 것이다. 사각형은 사이클로펜탄을 나타내고, 원은 CO2를 나타내며 삼각형은 HFO를 나타낸다.
도 5는 각각 사이클로펜탄 또는 HFO 1233zd의 다양한 함량(단위 wt%의 세로 좌표)을 가진 폴리올의 점도(단위 mP*sec의 가로 좌표)를 그래프로 도시한 것이다. 사각형은 사이클로펜탄을 나타내고 삼각형은 HFO를 나타낸다.
도 1은 본 발명에 따른 도관 파이프(1)의 구성을 단면도로 개략적으로 도시한 것이다. 이 경우, (2)는 외측(6)이 주위 환경을 향하고 내측(5)이 단열재를 향하는 외부 재킷이고; (3)은 셀 가스를 가진 단열재를 나타내고; (4)는 중간 파이프이다.
도 2는 외부 재킷(2)의 바람직한 구체예의 구성을 개략적으로 도시한 것이다. 이 경우, (7)은 외부 중합체 층(특히, 열가소성)이고; (8)은 외부 접착 촉진제 층이고, (9)는 장벽 층이며, (10)은 내부 접착 촉진제 층이고, (11)은 내부 중합체 층(특히, 열가소성)이다.
도 3은 셀 가스의 조성(단위 vol%의 세로 좌표)에 따라 50℃에서 측정된 PU 발포체의 열전도도 값(단위 mW/m*K의 가로 좌표)의 의존성을 그래프로 나타낸 것이다. 사각형은 사이클로펜탄을 나타내고, 원은 CO2를 나타내며 삼각형은 HFO를 나타낸다.
도 4는 셀 가스 조성(단위 vol%의 세로 좌표)에 따라 PU 발포체의 평균 소공 크기(단위 ㎛의 가로 좌표)를 그래프로 나타낸 것이다. 사각형은 사이클로펜탄을 나타내고, 원은 CO2를 나타내며 삼각형은 HFO를 나타낸다.
도 5는 각각 사이클로펜탄 또는 HFO 1233zd의 다양한 함량(단위 wt%의 세로 좌표)을 가진 폴리올의 점도(단위 mP*sec의 가로 좌표)를 그래프로 도시한 것이다. 사각형은 사이클로펜탄을 나타내고 삼각형은 HFO를 나타낸다.
제1 관점에서, 본 발명은 단열재를 함유하는 파이프 시스템(또한 사전 절연된 파이프 시스템 또는 단열 파이프 시스템이라고도 불림)으로서, 상기 단열재가 발포체(foam)를 포함하고, 상기 발포체의 셀 가스가 하이드로플루오로올레핀(HFO)을 함유하는 파이프 시스템에 관한 것이다. 이러한 파이프 시스템은 언급한 셀 가스가 없다면 그 자체는 공지된 것이며, 단열된 도관 파이프, 부싱 및 상기 도관 파이프를 연결하기 위한 커버 장치를 포함한다.
제1 구체예에서, 본 발명은 적어도 하나의 중간 파이프(4), 상기 중간 파이프 둘레에 배치된 적어도 하나의 단열재(3) 및 상기 단열재 둘레에 배치된 적어도 하나의 외부 재킷(2)을 포함하는 단열 도관 파이프(1)로서, 상기 외부 재킷(2)이 가능하게는 플라스틱으로 제조된 장벽(9)을 포함하고, 상기 단열재(3)는 발포체를 포함하며, 상기 발포체의 셀 가스는 이하에 정의된 성분을 함유하는 것을 특징으로 하는 단열 도관 파이프(1)에 관한 것이다.
제2 구체예에서, 본 발명은 플라스틱으로 제조되고, 특히 연결되는 적어도 두 파이프 부분의 연결 지점을 위한 커버 장치로서, 상기 커버 장치는 적어도 하나의 단열재(3) 및 상기 단열재 둘레에 배치된 적어도 하나의 외부 재킷(2)을 보유하며, 상기 외부 재킷(2)이 아마도 플라스틱으로 제조된 장벽을 포함하고, 상기 단열재(3)가 발포체를 포함하며, 상기 발포체의 셀 가스가 이하에 정의되는 성분을 함유하는 것을 특징으로 하는 커버 장치에 관한 것이다.
또 다른 구체예에서, 본 발명은 단열 도관 파이프를 연결하기 위한 플라스틱으로 제조된 부싱에 관한 것으로, 상기 부싱은 적어도 하나의 단열재(3) 및 상기 단열재 둘레에 배치된 적어도 하나의 외부 재킷(2)을 보유하고, 상기 외부 재킷(2)이 아마도 플라스틱으로 제조된 장벽을 포함하고, 상기 단열재(3)가 발포체를 포함하며, 상기 발포체의 셀 가스가 이하 정의되는 성분을 함유하는 것을 특징으로 하는 부싱에 관한 것이다.
이러한 본 발명의 관점은 이하에 더 상세히 설명될 것이다.
단열재(3): 단열재는 중간 파이프를 부분적으로 또는 완전히, 바람직하게는 완전히 둘러싼다. 특히 셀 내에 셀 가스를 함유하는 발포 플라스틱("발포체")이 단열재로서 적합하다. 단열재는 단면을 따라 균일하거나 또는 여러 층으로 구성될 수 있다. 도관 파이프의 단열재는 일반적으로 균일하게 구성된다.
셀 가스: 단열재에 존재하는 가스를 셀 가스라고 한다. 이들은 생산의 결과이며 화학적 및 물리적 팽창제 및/또는 이의 반응 산물로 구성된다. 이러한 셀 가스는 전형적으로 발포 공정 중에 첨가되거나, 또는 발포 공정 중에 형성된다.
본 출원에 따르면, 단열재의 발포체에 존재하는 셀 가스는 하이드로플루오로올레핀(HFO)을 함유하는 것을 특징으로 한다. 셀 가스는 하나의 HFO로만 또는 여러가지 HFO로 구성될 수 있고, 아마도 추가 다른 성분을 함유할 수도 있다. 셀 가스는 유리하게는 10 내지 100 vol% HFO, 바람직하게는 20 내지 100 vol% HFO, 더 바람직하게는 30 내지 100 vol% HFO, 특히 바람직하게는 40 내지 100 vol% HFO, 매우 특히 바람직하게는 50 내지 100 vol% HFO를 함유한다. 따라서 셀 가스는 추가 성분을 함유할 수 있다.
하나의 구체예에서, 셀 가스는 0 내지 50 vol% (사이클로)-알칸, 바람직하게는 0 내지 45 vol% (사이클로)-알칸, 보다 바람직하게는 0 내지 40 vol% (사이클로)-알칸, 특히 바람직하게는 0 내지 35 vol% (사이클로)-알칸을 함유한다. HFO 대 (사이클로)-알칸의 비율은 바람직하게는 적어도 2.5:1, 바람직하게는 적어도 3:1이다.
추가 구체예에서, 셀 가스는 추가적으로 또는 대안적으로 CO2 50 vol% 이하, 바람직하게는 0 내지 40 vol% CO2, 특히 바람직하게는 0 내지 30% CO2를 함유한다.
추가 구체예에서, 셀 가스는 추가적으로 또는 대안적으로 5 vol% 이하의 질소(N2) 및/또는 산소(O2)를 함유한다.
이러한 추가 성분은 예를 들어 언급된 (사이클로)알칸과 같은 팽창제에 첨가 될 수 있다; 이는 CO2와 같은 발포체의 생산 중에 일어날 수 있다; 예를 들어, 공기, O2, N2와 같이 생산 공정 중에 발포체에 유입될 수 있다.
놀랍게도, 셀 가스 내 10 vol% HFO와 같은 낮은 비율에서도, 파이프 시스템의 성질, 특히 단열 도관 파이프의 성질은 일련의 특징들이 향상되는 것으로 밝혀졌다. 특히, 여기에 설명된 도관 파이프는 놀라울 정도로 향상된 절연 거동을 가진 것으로 발견되었다. 이론에 한정하려는 것은 아니지만, 향상된 절연 성질은 HFO의 재료 성질(열전도도)에 의한 것일 뿐만 아니라 변한 점도에 의해 유도된 향상된 발포에 의해서도 수립되는 것으로 추정된다.
PU 발포체 및 PIR 발포체의 경우, 두 출발 성분(각각 이소시아네이트 또는 폴리올) 중 하나에 HFO의 첨가 및/또는 혼합 헤드에서의 직접 혼합 동안 현저한 점도 감소가 초래된다. 이론적으로 한정하려는 것은 아니지만, 감소된 점도는 두 성분의 혼합을 향상시키고, 이에 따라 비교적 더 작은 셀의 형성을 촉진하는 것으로 추정된다.
팽창제로서 사이클로펜탄을 사용하여 유사한 정도의 점도 감소를 달성하기 위해, 대안적으로 그 함량을 예컨대 1.86배 증가시킬 수도 있다. 이것은 HFO 1233zd(130.5g/mol)와 사이클로펜탄(70.2g/mol)의 분자량 차이를 나타내는 인수일 수도 있지만, 이것은 여러 불리한 결과를 나타낼 것이다:
a) 한편으로, 2배량의 팽창제 가스는 발포 공정 중에 팽창하여 발포체 구조의 제어불가능한 변화를 초래할 것이다. 기존의 PU 발포체 및 생산 설비는 더 소량의 사이클로펜탄에 최적화되어 있고, 팽창하는 팽창제와 관련하여 다량과 연관된 변화는 광범위한 신규 개발을 초래할 것이다.
b) 사이클로펜탄은 PU 발포체의 가소제 역할을 한다. 1.86배 증가한 양은 현저한 연화를 초래한다. 이는 한편으로는 발포체가 지지 역할을 하기 때문에, 즉 발포체가 전체 복합재의 기계적 안정성에 필수적이기 때문에 바람직하지 않다. 다른 한편, 생산 공정에서 발포체의 연화도 증가는 전체 파이프 복합재가 이상적인 둥근 단면 기하형상에서 더욱더 벗어나는 결과를 초래하기 때문에 바람직하지 않다. 따라서, HFO에 의한 사이클로펜탄의 완전 또는 부분 치환은 발포체의 기계적 성질을 향상시키는 것으로 밝혀졌다. 사이클로펜탄은 전형적으로 점도를 감소시키기 위해 출발 물질에 첨가된다; 그러나, 생산된 발포체가 충분한 기계적 강도를 가져야 한다는 점에서 최대 양은 제한된다. 이러한 모순된 목표는 사이클로펜탄을 HFO로 치환시킴으로써 달성할 수 있다. 비슷한 양의 HFO의 사용은 출발 물질의 저하된 점도와 최종 발포체의 균일한 기계적 강도를 초래한다. 따라서, 균일 한 제품 품질로 인해 생산성이 향상될 수 있다.
또한, 출발 성분 중 하나에 HFO의 첨가 및/또는 혼합 헤드 중의 두 출발 성분에 직접 첨가는 HFO의 연소성을 감소시키는 것으로 밝혀졌다. 상기 효과는 이러한 생산 설비에 대한 안전성-기술 요구사항이 감소되어 해당 생산 설비의 설계가 상당히 단순화될 수 있고, 이에 따라 연소성 팽창제가 사용될 때 발생하는 비용을 절약할 수 있기 때문에 매우 유리하다.
요약하면, 공지된 문제점들은 HFO에 의한 사이클로펜탄(Cp)의 부분 또는 완전 치환에 의해 명쾌한 방식으로 해결될 수 있다고 말할 수 있다. 한편으로는 바람직한 점도 감소를 초래하는 더 많은 팽창제가 첨가될 수 있다. 그러나, 동시에 팽창 효과는 거의 변하지 않아서, 포뮬라 및 생산 설비에 대한 기본적인 개정은 필요하지 않다. 마지막으로, 연소성 사이클로펜탄이 비연소성 HFO로 치환되어 작업 보호가 향상되고 이러한 생산 설비에 대한 투자 비용이 감소된다.
또한, (사이클로)-알칸, 특히 사이클로펜탄의 높은 함량은 제품 품질에 부정적인 영향을 미치는 것으로 밝혀졌다. 경험에 의하면, 폴리올 중에 사이클로펜탄의 과도하게 높은 함량은 발포체 내에 큰 기포를 형성시키는데, 이는 형성되는 PU 발포체의 온도에 의해 팽창제(특히 사이클로펜탄)가 발포체로부터 추방되기 때문에 일어나는 것으로 관찰되었다. 연속적으로 작동하는 생산 공정에서, 외부 재킷은 일반적으로 압출에 의해 적용되고, 상기 시점에서는 일반적으로 80 내지 250℃의 고온으로 인해 쉽게 변형될 수 있는 상태인 것으로 발견된다. 그 후 기포는 탈출하는 팽창제가 외부 재킷을 팽창시키기 때문에, 단열 파이프의 외측에서 관찰할 수 있게 된다. 이것은 파형(wavy), 평활형(smooth) 및 골판형(corrugated) 외부 재킷을 가진 단열 파이프에서도 마찬가지이다. 팽창제의 탈출은 압출된(extruded-on) 외부 재킷의 온도에 의해 촉진된다. 이러한 결함을 가진 파이프는 폐기물로 간주되어야 하고 더 이상 실제 목적에 공급될 수 없다.
최종 단열 발포체의 셀 가스 조성에서 사이클로펜탄의 함량이 0 내지 50 vol%, 바람직하게는 0 내지 45 vol%, 특히 바람직하게는 0 내지 40 vol%, 가장 바람직하게는 0 내지 35 vol%이면 기포 형성이 방지된다.
놀랍게도 HFO를 팽창제로 사용 시, 언급한 기포 형성은 일어나지 않는 것으로 입증되었다. 이는 특히 최종 단열 발포체의 셀 가스 조성에서 HFO의 함량이 상기 한도 내인 경우에 해당한다. 기술된 거동은 비등점이 각각 HFO 1233zd의 경우 19℃이고, HFO 1336mzz의 경우 33℃이기 때문에 더욱 놀라운 것이다. 이것은 비등점이 49℃인 사이클로펜탄과 비교된다. 이러한 비등점들로 인해, 고 비등점인 (사이클로)-알칸, 예컨대 Cp의 사용 시보다 팽창제로써 저 비등점인 HFO의 사용 시에 기포 형성이 더욱 현저할 것으로 예상되지만, 그 반대가 관찰되었다.
하이드로플루오로올레핀(HFO)은 공지되어 있고, 시중에서 입수할 수 있고(있거나) 공지된 방법에 따라 생산할 수 있다. 이는 팽창제 가스로서, 특히 지구 온난화 지수(GWP)가 낮고 대기 오존층(Ozone Depleting Potential, ODP)에 무해하기 때문에 적합하다. 상기 용어는 탄소, 수소 및 불소만을 포함하는 화합물 및 추가로 염소를 포함하는 화합물(또한 HFCO로도 지칭됨)을 포함하고, 각각의 경우 분자 내 적어도 하나의 불포화 결합을 포함한다. HFO는 다양한 성분의 혼합물로 제공되거나, 또는 순수 성분들로 제공될 수 있다. HFO는 또한 이성질체 혼합물, 특히 E/Z 이성질체 또는 이성질체-순수 화합물로서 제공될 수 있다.
본 발명의 범위 내에서 특히 적합한 HFO는 하기 화학식 (I)의 화합물을 함유하는 그룹 중에서 선택된다:
화학식 (I)
여기서, R5는 H, F, Cl, CF3, 바람직하게는 Cl, CF3을 나타내고, R6은 H, F, Cl, CF3, 바람직하게는 H를 나타낸다.
특히 적합한 HFO는 R1233zd(예컨대, solstice LBA, Honeywell) 및 R1336mzz(예컨대, Formacel 1100, DuPont)이다.
놀랍게도, 여기에 기술된 도관 파이프는 단열재의 셀 가스가 적어도 10 vol%, 바람직하게는 적어도 30 vol%, 특히 바람직하게는 적어도 50 vol%의 HFO를 함유한다면 향상된 절연 거동을 가진 것으로 밝혀졌다. 또한, 발포체 절연의 출발 물질에 상기 HFO의 첨가는 생산성을 향상시키는 것으로 밝혀졌다.
(사이클로)알칸은 단열 파이프에서 절연 셀 가스로 알려져 있다. 상기 알칸 또는 사이클로알칸은 프로판, 부탄, 펜탄, 사이클로펜탄, 헥산 및 사이클로헥산을 포함하는 그룹 중에서 선택되는 것이 유리하다. (사이클로)알칸과 HFO의 조합에 의해, 제품 성질의 미세 조정이 수행될 수 있고, 및/또는 생산성이 향상될 수 있고, 및/또는 허용되는 품질 손실로 인해 비용을 절감할 수 있다. 언급된 (사이클로)알칸은 순수 화합물로서 또는 혼합물로서 제공될 수 있다; 지방족 알칸은 이성질체-순수 화합물로서 또는 이성질체 혼합물로서 제공될 수 있다. 특히 적합한 (사이클로)알칸은 사이클로펜탄이다.
이산화탄소 : 발포체가 PU 또는 폴리이소시아누레이트(PIR)로 제조된다면, 산업용 품질의 출발 물질 폴리올은 일반적으로 소량의 물을 함유하기 때문에 CO2가 일반적으로 특정 양으로 발생한다. 그 후, 상기 물은 이소시아네이트와 반응하여 카르밤산을 형성하며, 상기 카르밤산은 자발적으로 CO2를 분리한다. 따라서, 셀 가스의 CO2 함량은 출발 물질의 순도와 관련이 있고, 전형적으로 50 vol% 미만이다. 출발 물질이 무수물이라면, 예컨대 폴리올레핀이 형성된다면, 셀 가스의 CO2 함량은 따라서 0 vol%이다. 따라서, 셀 가스의 CO2 함량은 출발 물질(및/또는 이의 순도)의 선택을 통해 영향을 받을 수 있다.
추가 셀 가스: 구성성분들은 생산으로 인한 대기/주위 공기로부터 셀 가스를 유입할 수 있다. 이들은 실질적으로 N2 및/또는 O2, 예컨대 공기이다. 셀 가스의 함량은 일반적으로 5 vol% 미만이다. 생산 설비가 특수하게 구성된다면, 대기/주위 공기와의 접촉을 피할 수 있으며 추가 셀 가스의 함량은 0 vol%이다.
발포체: 상기 단열재(3)는 발포체를 포함한다(즉, 발포체를 함유하거나, 발포체로 이루어진다). 이러한 발포체는 그 자체는 공지되어 있으며, 표준 DIN EN 253:2015-12 (특히 PJP의 경우) 및 EN15632-1:2009/A1:2014, EN15632-2:2010/A1:2014 및 EN15632-3:2010/A1:2014 (특히 PMP의 경우)를 충족하는 발포체가 특히 적합하다. 상기 용어는 경질 발포체 및 연질 발포체를 포함한다. 발포체는 폐쇄형 셀 또는 연속 셀, 바람직하게는 폐쇄형 셀, 특히 표준 DIN EN 253:2015-12에 표현된 것과 같은 셀일 수 있다. 이러한 발포체는 바람직하게는 폴리우레탄(PU), 폴리이소시아누레이트(PIR), 열가소성 폴리에스테르(특히 PET) 및 열가소성 폴리올레핀(특히 PE 및 PP)의 그룹 중에서 선택된다.
발포체와 셀 가스의 다음과 같은 조합이 특히 유리한 것으로 밝혀졌다:
- 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol% Cp를 함유하는 PU;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol% Cp를 함유하는 PU;
- 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol% Cp를 함유하는 PIR;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol% Cp를 함유하는 PIR;
- 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol% Cp를 함유하는 PET;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol% Cp를 함유하는 PET;
- 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol% Cp를 함유하는 PE;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol% Cp를 함유하는 PE.
하나의 구체예에서, 언급된 셀 가스는 100 vol%까지 첨가된다. 추가 구체예에서, 이들 셀 가스는 CO2 및 공기와 함께 100%까지 첨가된다. 또 다른 구체예에서, HFO:Cp의 비는 적어도 2.5:1이다.
또한, 다음과 같은 발포체와 셀 가스의 조합이 특히 유리한 것으로 밝혀졌다:
- 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol% Cp 및 0 내지 50 vol% CO2를 함유하는 PU;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol% Cp 및 0 내지 50 vol% CO2를 함유하는 PU;
- 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol% Cp 및 0 내지 50 vol% CO2를 함유하는 PIR;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol% Cp 및 0 내지 50 vol% CO2를 함유하는 PIR;
- 50 내지 100 vol%의 R1233zd 및 0 내지 45 vol% Cp 및 10 내지 40 vol% CO2를 함유하는 PU;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 45 vol% Cp 및 10 내지 40 vol% CO2를 함유하는 PU;
- 50 내지 100 vol%의 R1233zd 및 0 내지 45 vol% Cp 및 10 내지 40 vol% CO2를 함유하는 PIR;
- 50 내지 100 vol%의 R1336mzz 및 0 내지 45 vol% Cp 및 10 내지 40 vol% CO2를 함유하는 PIR.
하나의 구체예에서, 언급된 셀 가스는 100 vol%까지 첨가된다. 추가 구체예에서, 이들 셀 가스는 공기와 함께 100%까지 첨가된다. 추가 구체예에서, HFO:Cp의 비는 적어도 3:1이다.
추가의 구체예에서, 단열재는 언급된 발포체 및 언급된 셀 가스로 이루어진다.
장벽(9): 확산 장벽 그 자체는 도관 파이프/파이프 시스템 분야에 공지되어 있다. 장벽이 존재한다면, 상기 장벽은 층으로 형성된다. 이하에 설명되는 적어도 하나의 장벽(9)이 제공되는 것이 바람직하다. 특히 후술되는 하나의 장벽(9)이 제공되는 것이 바람직하다.
이 층(9)은 단열재 밖으로 셀 가스의 확산 및 단열재 내로 도관 파이프 외측의 기체(특히, 공기)의 확산이 감소될 수 있게 한다. 상기 성질은 장시간 동안 도관 파이프/파이프 시스템의 절연 성능을 보장하는데 중요하다.
하나의 유리한 구체예에서, 상기 층은 또한 단열재 외부로 물의 확산을 가능하게 한다. 상기 성질은 특히 중간 파이프(4)가 플라스틱으로 이루어진 도관 파이프/파이프 시스템에 중요하다. 이러한 도관 파이프/파이프 시스템에서 수성 매질이 이송된다면 물이 상기 매질로부터 도관 파이프를 통해 단열재로 유입되어 단열 성능을 감소시키고 단열재를 손상시킬 수 있다.
하나의 유리한 구체예에서, 상기 층은 또한 CO2에 대한 특정한 투과성이 제공될 수 있게 한다. CO2 투과성에 특히 적합한 값은 0.5 내지 100 ㎤/㎡*일*bar 범위이다.
따라서, 선택적 성질을 가진 장벽이 유리하고, 특히 (i) 물 및 수증기에 대한 투과성, (ii) 열전도도가 낮은 셀 가스에 대한 불투과성, (iii) 생산으로 인해 발생하지만 비교적 높은 고유 열전도도를 가진 셀 가스(예, CO2)에 대한 투과성, (iv) 주위환경의 기체, 특히 질소, 산소 및 공기에 대한 불투과성인 것이 유리하다.
장벽이 이하에 언급된 하나 이상의 중합체를 포함하는, 처음에 언급된 종류의 도관 파이프가 상기 요건들을 매우 잘 충족시키는 것으로 밝혀졌다. 본 발명에 따르면, 장벽은 단일 층으로 제공되거나 또는 서로 분리된 여러 층으로 제공될 수 있다. 또한, 장벽은 추가 층에 의해 단열재 또는 외부 재킷에 부착되거나 또는 외부 재킷 내("접착 촉진제 층"(8), (10))에 부착될 수 있다.
장벽(9)은 외부 재킷(2) 내에 하나의 층으로 배치될 수 있다; 이것이 바람직하고, 특히 상기 구체예는 도 2에 예시된 바와 같이 장벽(9)에 인접하는 2개의 접착 촉진제 층(8, 10)을 보유하는 것이 바람직하다. 또한, 장벽은 외부 재킷의 외측 및/또는 내측에 층으로써 배치될 수 있다. 또한, 장벽은 외부 재킷에 의해 형성될 수 있다. 또한, 장벽(9)은 단열재(3)와 외부 재킷(2) 사이에 층으로써 배치될 수 있다. 상기 구체예에서, 접착 촉진제 층은 일반적으로 생략된다.
장벽 층(9)은 층 두께가 0.05 내지 0.5 mm, 바람직하게는 0.1 내지 0.3 mm인 것이 유리하다. 장벽이 외부 재킷을 형성하는 경우, 장벽은 층 두께가 0.5 내지 5 mm인 것이 유리하다. 접착 촉진제 층(8, 10)이 제공된다면, 상기 층들은 서로 독립적으로 층 두께가 0.02 내지 0.2 mm인 것이다.
장벽은 에틸렌과 일산화탄소 또는 비닐 알코올의 공중합체를 포함하는 것이 바람직하다.
하나의 유리한 구체예에서, 장벽은 폴리케톤을 함유하거나 폴리케톤으로 이루어진 중합체를 포함한다. 따라서, 중합체 층은 폴리케톤 및 폴리케톤의 블렌드 및 폴리케톤을 함유하는 적층체도 포함한다. 폴리케톤 자체는 공지된 물질이며 중합체 사슬 중의 케토 기(C=O)를 특징으로 한다. 상기 구체예에서, 중합체는 최대 50 내지 100 중량%, 바람직하게는 최대 80 내지 100 중량%의 화학식 (II) 또는 화학식 (III)의 구조 단위를 가진 것이 유리하다.
화학식 (II)
화학식 (III)
이 식에서,
o는 1 또는 2, 바람직하게는 1을 나타내고,
p는 1 또는 2, 바람직하게는 1을 나타내며,
q는 1 내지 20을 나타내고,
r은 1 내지 20을 나타낸다.
폴리케톤은 일산화탄소와 대응하는 알켄, 예컨대 프로펜 및/또는 에텐과의 촉매적 반응에 의해 수득할 수 있다. 이러한 케톤은 또한 지방족 케톤이라 지칭되기도 한다. 이들 중합체는 예를 들어 효성의 폴리케톤 공중합체(화학식 II) 또는 폴리케톤 삼원중합체(화학식 III)와 같이 시중에서 입수할 수 있다. 이러한 폴리 케톤은 또한 상표명 Akrotek® PK로 시중에서 입수할 수도 있다. 적당한 중합체는 융점이 200℃ 초과(ISO 11357-1/3에 따라 DSC 10K/분을 사용하여 측정 시)이고(이거나), 흡수율이 DIN EN ISO 62(23℃에서 물에 포화 시)에 따라 측정 시, 3% 미만인 것이다.
하나의 유리한 구체예에서, 장벽은 에틸 비닐 알코올을 함유하거나, 또는 에틸 비닐 알코올로 이루어진 중합체를 포함한다.
이 구체예에서, 중합체는 최대 50 내지 100 중량%, 바람직하게는 최대 80 내지 100 중량%의 화학식 (IV)의 구조 단위를 가진다.
화학식 (IV)
이 식에서,
m은 1 내지 10을 나타내고,
n은 2 내지 20을 나타낸다.
적합한 에틸 비닐 알코올은 특히 m/n 비가 30/100 내지 50/100 인 랜덤 공중 합체이다. 이러한 중합체는 예를 들어 Kuraray의 EVAL FP 시리즈 또는 EP 시리즈와 같이 시중에서 입수할 수 있다. 이들은 양호한 가공 성능에 의해 구별되며, 특히 용융 점도 및 용융 온도가 유사한 범위에 있기 때문에 통상적으로 사용되는 재킷 재료 폴리에틸렌(PE)과 함께 공압출에 의해 매우 잘 가공처리될 수 있다.
하이드로플루오로올레핀 그룹 유래의 셀 가스와 전술한 화학식 (II), (III), (IV)에 따른 장벽 층의 조합은 단열 도관 파이프의 특히 양호한 상승적(superadditive) 절연 성질을 초래한다. 이러한 성분들의 긍정적인 상호작용은 놀라운 것이다. 하나의 이론에 한정하려는 것은 아니지만, 이러한 상승적 효과는 화학식 (II), (III), (IV)에 따른 물질의 장벽 성질에 기인하는 것일 수 있다.
중간 파이프 (4): 원칙적으로 단열 파이프에 적합한 모든 중간 파이프가 사용될 수 있다. 따라서, 중간 파이프는 파형 파이프, 평활형 파이프 또는 골판형 재킷을 가진 파이프로 형성될 수 있다; 즉, 강성 선형 파이프 부분, 강성 굽은 파이프 부분 또는 가요성 파이프 부분일 수 있다.
중간 파이프는 중합체 재료 또는 금속 재료, 바람직하게는 중합체 재료로 이루어질 수 있다. 이러한 재료 자체는 공지되어 있고 시중에서 입수할 수 있거나 공지된 방법에 따라 생산할 수 있다. 상기 재료는 의도된 용도에 따라, 아마도 통상적인 실험 후 당업자에 의해 선택된다.
하나의 구체예에서, 상기 중간 파이프(4)는 가요성 플라스틱 파이프이고, 상기 플라스틱은 아크릴로니트릴-부타디엔-스티렌(ABS), 가교 폴리에틸렌(PEXa, PEXb, PEXc), PE, 폴리부텐(PB), 온수난방관용 폴리에틸렌(PE-RT) 및 폴리케톤(PK)으로 이루어진 그룹 중에서 선택된다.
추가 구체예에서, 상기 중간 파이프(4)는 외부 금속층을 갖는 가요성 플라스틱 파이프이고, 상기 플라스틱은 ABS, PEXa, PEXb, PEXc, PE, PB, PE-RT 및 PK 그룹으로부터 선택되며, 상기 금속은 알루미늄 합금을 비롯한 알루미늄 그룹 중에서 선택된다. 이러한 내부 파이프는 복합재 파이프로도 알려져 있다.
추가 구체예에서, 상기 중간 파이프(4)는 강성 플라스틱 파이프이고, 상기 플라스틱은 ABS, PEXa, PEXb, PEXc, PE, PB, PE-RT 및 PK 그룹으로부터 선택된다.
추가 구체예에서, 상기 중간 파이프(4)는 가요성 금속 파이프이고, 상기 금속은 구리 합금을 비롯한 구리, 철 합금을 비롯한 철(예를 들어, 방청 강) 및 알루미늄 합금을 비롯한 알루미늄 그룹으로부터 선택된다.
추가 구체예에서, 상기 중간 파이프(4)는 강성 금속 파이프이고, 상기 금속은 구리 합금을 비롯한 구리, 철 합금을 비롯한 철(예를 들어, 방청 강) 및 알루미늄 합금을 비롯한 알루미늄으로부터 선택된다.
중간 파이프(4)의 추가 구체예에서, 플라스틱으로 제조된 전술한 장벽은 내부 파이프의 외측에 배치될 수 있거나 또는 중간 파이프 자체로 형성될 수 있다. 중간 파이프 상의 장벽 또는 중간 파이프 자체로 형성된 장벽은 중간 파이프로부터 단열재 내로 증기의 확산을 감소시킨다. 본 발명에 따르면, 이러한 ("제2") 장벽은 단열재 상의 추가("제1") 장벽과 조합된다.
외부 재킷 (2): 원칙적으로 단열 파이프에 적합한 모든 외부 재킷이 사용될 수 있다. 따라서, 외부 재킷은 골판형 파이프 또는 평활형 파이프 또는 골판형 재킷을 가진 파이프로서 형성될 수 있다. 강성 선형 파이프 부분, 강성 굽은 파이프 부분 또는 가요성 파이프 부분일 수 있다.
외부 재킷은 중합체 재료 또는 금속 재료, 바람직하게는 중합체 재료로 이루어질 수 있다. 이러한 재료 자체는 공지되어 있고, 시중에서 입수할 수 있거나, 공지된 방법에 따라 생산될 수 있다. 재료는 의도된 용도에 따라 당업자에 의해, 아마도 통상적인 실험 후에 선택될 수 있다. 시판되는 PE 종류와 같은 열가소성 중합체가 유리하게 사용된다. 고밀도 PE(HDPE), 저밀도 PE(LDPE) 및 선형 저밀도 PE(LLDPE)가 적합하다. 외부 재킷(2)의 층 두께는 넓은 범위에서 변동될 수 있지만, 아마도 제공된 장벽 및 장벽 층을 포함해서 일반적으로 0.5 내지 20 mm이다.
본 발명의 일 구체예에서, 외부 재킷은 전술한 바와 같이 여기에 기술된 장벽을 함유한다. 상기 구체예는 재킷 및 장벽이 공압출에 의해 동시에 비용 효과적으로 제조될 수 있기 때문에 유리하다.
본 발명의 다른 구체예에서, 외부 재킷은 전술한 바와 같이 여기에 기술된 장벽을 함유하지 않는다. 상기 구체예에서, 장벽은 별개의 층으로서 제공된다. 이러한 구체예는 재킷 및 장벽이 별도로 유연하게 제조될 수 있기 때문에 유리하다.
하나의 유리한 구체예에서, 본 발명은 여기에 기술된 바와 같은 도관 파이프에 관한 것으로, 상기 외부 재킷(2)은 파형 파이프로 형성되고; 상기 중간 파이프는 가요성 파이프 부분으로서 형성되며, 특히 폴리에틸렌을 기반으로 하는 적어도 하나의 중간 파이프 및 PU를 기반으로 하는 단열재 및 폴리에틸렌을 기반으로 하는 외부 재킷을 보유한다.
또 다른 유리한 구체예에서, 본 발명은 여기에 기술된 바와 같은 도관 파이프에 관한 것으로, 상기 도관 파이프는 강성 선형 파이프 부분이고, 특히 폴리에틸렌 또는 강철을 기반으로 하는 적어도 하나의 중간 파이프 및 PU를 기반으로 한 단열재 및 폴리에틸렌을 기반으로 한 외부 재킷을 보유한다.
또 다른 유리한 구체예에서, 본 발명은 외부 재킷(2)이 골판형 파이프로 형성된, 여기에 설명된 도관 파이프에 관한 것이다. 이러한 도관 파이프는 가요성 파이프 부분으로서 형성되고 특히 폴리에틸렌 또는 가교 폴리에틸렌을 기반으로 하는 적어도 하나의 중간 파이프를 포함하는 중간 파이프와 조합되는 것이 유리하다. 또한, 이러한 도관 파이프는 셀 가스가 상기 언급한 조성을 갖는 발포체(셀 가스는 특히 바람직하게는 최대 35% (사이클로)알칸을 함유함)를 포함하는 단열재(3)를 추가로 구비하는 것이 유리하다.
제2 관점 에서, 본 발명은 여기에 기술된 바와 같은 단열 도관 파이프, 부싱 및 커버 장치를 생산하는 방법에 관한 것이다. 따라서, 본 발명은 연속 및 불연속 중 어느 방식으로든지 수행될 수 있는 도관 파이프, 부싱 또는 커버 장치를 생산하기 위한 개량 방법을 제공하는 목적을 기반으로 한다.
이러한 본 발명의 관점은 이하에 더 상세히 설명될 것이다.
원칙적으로, 여기에 기술된 단열 장치(본 발명의 제1 관점 참조)는 공지된 방법과 유사하게 제조될 수 있다. 이 경우, 공지된 팽창제(예컨대, 사이클로펜탄, CO2)는 여기에 기술된 HFO로 부분적으로 또는 완전하게 치환된다. 따라서, 당업자가 통상적인 수법으로 수행할 수 있는 것처럼, 아마도 신규 파라미터들에 대한 개정 후 공지된 설비가 그대로 생산에 사용될 수 있다. EP0897788 및 EP2213440 및 EP2248648 및 WO2008/019791 및 EP1355103 및 EP2340929에 기술된 방법은 본원에 참고로 포함된다.
상기 방법의 하나의 유리한 구체예에서, 단열재(3)는 발포체 형성을 위한 중합체 성분 및 팽창제로서 HFO를 함유하는 플라스틱 조성물을 발포시킴으로써 형성된다. 본 발명에 따르면, HFO는 상기 성분들 중 하나에 첨가된 다음 가공처리될 수 있거나 또는 출발 성분과 HFO가 계량 장치(예를 들어, 혼합 헤드)에서 동시에 조합된다.
상기 방법의 또 다른 유리한 구체예에서, 플라스틱 조성물은 2종의 액체 성분을 포함하되, 제1 성분은 폴리올 및 HFO를 함유하고 제2 성분은 이소시아네이트를 함유한다. 이소시아네이트 성분은 바람직하게는 메틸렌 디이소시아네이트를 기반으로 한 것이다. 그러나, 다른 이소시아네이트, 예를 들어 톨루엔-2,4-디이소시아네이트 또는 지방족 이소시아네이트를 기반으로 한 이소시아네이트도 사용될 수 있다.
상기 방법의 또 다른 유리한 구체예에서, 플라스틱 조성물은 2종의 액체 성분을 포함하되, 제1 성분은 폴리올을 함유하고 제2 성분은 이소시아네이트 및 HFO를 함유한다. 특히, 상기 HFO 성분은 상기 2종의 액체 성분과 혼화성이 양호하고 비등점이 너무 낮지 않은(특히 10℃ 이상) 것이 바람직하다. 따라서, 생산에서 장치 비용이 적고; 냉각 시스템이 약간만 제공되어야 한다.
상기 방법의 또 다른 유리한 구체예에서, 플라스틱 조성물은 용융된 성분으로 이루어지며, 상기 용융물은 가압하에 HFO와 조합된다.
변형예 1: 본 발명의 단열 파이프가 하나 이상의 가요성 중간 파이프(들)를 포함하고 외부 재킷(13)이 플라스틱으로 제조된 장벽을 포함한다면, 다음과 같은 방법 변형예가 유리하다:
(a) 적어도 하나의 중간 파이프가 연속적으로 공급되고 튜브로 형성된 플라스틱 필름으로 포위되고,
(b) 발포성 플라스틱 조성물이 중간 파이프와 튜브 사이의 공간으로 단열층으로서 도입되고,
(c) 상기 중간 파이프와 튜브를 수반하는 주형 부품으로 제조된 주형 내로 도입시키고, 상기 주형을 끝에 남겨두고, 그 다음
(d) 튜브의 표면 위로 외부 재킷을 압출시키고,
이때, 발포성 플라스틱 조성물은 발포체 형성을 위한 중합체 성분(들) 및 팽창제로서 HFO를 함유한다. 상기 방법 변형예에서,
- 장벽은 중합체로 형성되어 있는 튜브에 의해, 발포 단열층과 외부 재킷의 내측 사이에 도입될 수 있거나; 또는
- 장벽은 외부 재킷과 함께 공압출에 의해 적용될 수 있거나; 또는
- 장벽을 튜브에 직접 적용할 수 있거나; 또는
- 먼저, 외측 재킷 층을 적용할 수 있고, 그 다음 장벽 및 그 다음 외부 재킷의 적어도 하나의 제2 층을 적용할 수 있다.
이 방법 변형예에서, 또한 단계 (a)에서, 내부 파이프는
- 공급원으로부터 지속적으로 인출할 수 있거나; 또는
- 압출에 의해 연속적으로 생산할 수 있다.
변형예 2: 본 발명의 단열 파이프가 하나 이상의 강성 중간 파이프(들)를 포함하고 장벽을 가진 외부 재킷(2)이 플라스틱으로 제조된다면, 다음과 같은 방법 변형예가 유리하다:
(a) 중간 파이프가 외부 재킷 내부 중심에 위치하며
(b) 발포성 플라스틱 조성물이 중간 파이프와 외부 파이프 사이의 공간으로 단열층으로서 도입되고,
상기 발포성 플라스틱 조성물이 발포체 형성을 위한 중합체 성분 및 팽창제로서 HFO를 함유하는 것을 특징으로 한다. 이미 언급한 바와 같이, 상기 HFO는 혼합 헤드에서 2종의 액체 성분과 혼합될 수 있거나, 또는 상기 HFO는 2종 성분 중 하나와 사전에 혼합된 다음 혼합 헤드에 공급된다. 상기 방법 변형예에서,
- 장벽은 발포 단열재와 외부 재킷의 외측 사이에 튜브 형태로 도입될 수 있거나; 또는
- 장벽은 외부 파이프의 내측에 적용될 수 있거나; 또는
- 장벽은 외부 파이프에 제공될 수 있거나; 또는
- 장벽은 외부 파이프의 외측에 적용될 수 있다.
변형예 3: 본 발명의 단열 파이프가 열가소성 발포체, 예를 들어 PET, PE 또는 PP로 제조된 단열재를 함유한다면, 방법 변형예는 HFO가 용융된 중합체 매트릭스 내로 바로 압입되고, 이어서 팽창으로 인해 사용된 열가소성 수지를 발포시키는 것이 유리하다. 이것은 예를 들어, 중합체 혼합물이 압출기에서 용융되고 상기 용융물 내로 HFO가 가압하에 공급됨으로써 일어날 수 있다. 주형을 떠나자마자, 상기 제공된 팽창제는 발포를 초래한다.
제3 관점에서, 본 발명은 HFO의 신규 용도에 관한 것이다.
이러한 본 발명의 관점은 이하에 더 상세히 설명될 것이다.
제1 구체예에서, 본 발명은 단열 파이프 시스템, 특히 플라스틱 중간 파이프 시스템(PMP) 및 플라스틱 재킷화된 파이프 시스템(PJP)에서 발포체 절연의 셀 가스로서 사용되는 하이드로플루오로올레핀의 용도에 관한 것이다.
HFO는 도관 파이프, 커버 장치 및 부싱, 특히 여기에 기술된 도관 파이프, 커버 장치 및 부싱(제1 관점)의 발포체 절연에서 셀 가스로 유리하게 사용될 수 있다.
본 발명은 하기 실시예 에 기초하여 더욱 상세하게 설명될 것이다; 이들은 임의의 방식으로 본 발명을 제한하는 것이 아니다.
실시예 1: 본 발명에 따른 도관 파이프의 제조
외경 63 mm 및 벽 두께 5.8 mm이고 PExa로 이루어진 중간 파이프를 공급 드럼으로부터 연속적으로 풀어냈다. 발포 스테이션 직전에, 상기 중간 파이프는 공급 장치에서 풀어 성형 숄더를 통해 공급되는 PE 필름으로 둘러쌌다. NCO 함량이 31% 인 디페닐메틸렌 디이소시아네이트(MDI)를 기반으로 하는 중합체 이소시아네이트와 OH가가 410mg KOH/g(ASTMD4274D에 따라 측정 시)이고 수분 함량이 0.8%인 폴리올로 제조된 혼합물의 해당량을 상부 측이 여전히 열려 있는 튜브 필름 내로 분배했다.이 경우 이소시아네이트 성분은 반응성 OH 기에 비해 약간 초과화학양론적으로 사용되었다. 두 성분은 분배하기 전에 150 bar의 압력 하에 고압 혼합 헤드에서 강력하게 혼합했다. 즉, HFO/사이클로펜탄의 해당량이 사전에 폴리올 성분 내로 교반 되었다. 2 성분 혼합물의 분배 직후, 튜브 필름은 상단부를 용접했다. 그 직후에 발생한 PU 발포체는 성형 조(jaw)에 의해 원통형 기하구조 내로 압입되고 경화 후 PE로 제조된 재킷이 계속해서 압출되었다.
수득된 파이프를 발포체에 함유된 셀 가스에 대하여 분석하였다. 상기 목적을 위해, 발포체로부터 약 3 ㎤ 크기의 작은 샘플을 찍어냈고, 셀 가스가 측정 장치로 들어갈 수 있도록 밀폐 시스템에서 기계적으로 파괴했다. 존재하는 가스는 가스 크로마토그래프에서 정성적 및 정량적으로 측정되었다.
또한, 열전도도 값은 표준 DIN EN 253:2015-12 및 EN ISO 8497:1996(λ50 값)에 따라 3m 길이의 파이프 부분에 대해 50℃에서 측정했다. 또한, 셀 가스의 조성을 측정했고(Chalmers 법에 따라; Ramnas et al, J. Cellular Plastics, 31, 375-388, 1995에 기술됨); 상기 방법은 다음 실시예들에도 사용되었다. 결과는 다음 표에 정리했고, 도 3에서는 그래프로 분명하게 나타냈다:
셀 가스 | 단위 | No1.1 | No1.2 | No1.3 | No1.4 | No1.5 |
CO2 * | [vol%] | 100 | 51 | 34 | 31 | 32 |
Cp | [vol%] | 0 | 46 | 14 | 9 | 0 |
HFO 1233zd | [vol%] | 0 | 0 | 49 | 59 | 65 |
O2 + N2 | [vol%] | 0 | 3 | 3 | 1 | 3 |
λ50 값 | [mW/m*K] | 25.8 | 23.1 | 21.7 | 20.2 | 19.6 |
* CO2는 출발 성분으로부터 부산물로 자동 형성되며 첨가되지 않는다(화학적 팽창제).
이 데이터는 열전도도에 미치는 HFO의 긍정적인 영향을 분명히 증명한다.
실시예 2 : 발포성 혼합물의 모델 실험
각 경우마다, 380 내지 420g 양의 폴리올을 비이커에 제공하고, 표에 제시된 팽창제의 양이 교반되었다. 용액의 점도는 Brookfield 제품인 점도계 DV I-Prime 타입의 회전 점도계에서 측정했다. 3회 측정의 평균값을 기록했다.
결과는 이하 표에 정리했고 도 5에 그래프로 나타냈다.
팽창제 | 첨가된 팽창제 함량 | 온도 | 점도 |
[mol/100g 폴리올] | [K] | [mPa*s] | |
폴리올 | 순수 폴리올, 팽창제 무첨가 |
292.8 | 2005 |
Cp | 0.043 | 293.2 | 1245 |
0.071 | 293.1 | 946 | |
HFO 1233zd | 0.041 | 293.0 | 1151 |
0.071 | 293.1 | 815 |
상기 데이터는 점도에 미치는 HFO의 긍정적인 영향을 분명하게 입증한다.
실시예 3: PU 발포체의 소공 크기
상이한 셀 가스를 함유한 PU 발포체의 평균 소공 크기는 DIN EN 253:2015-12에 따라 측정했다. 평균은 각 경우마다 3회 측정으로부터 수득했다.
결과는 이하 표에 정리했고, 도 4에 그래프로 나타냈다.
셀 가스 | 단위 | No3.1 | No3.2 | No3.3 |
CO2 | [Vol%] | 100 | 51 | 32 |
Cp | [Vol%] | 0 | 46 | 0 |
HFO 1233zd | [Vol%] | 0 | 0 | 65 |
O2 + N2 | [Vol%] | 0 | 3 | 3 |
소공 크기 | [㎛] | 151.0 | 138.1 | 130.6 |
데이터는 셀 크기에 미치는 HFO의 긍정적인 영향을 분명히 입증한다.
실시예 4 : 출발 물질의 인화점 측정
Pensky-Martens(DIN EN ISO 2719:2003-9)의 방법에 따라 시편 번호 1과 번호 3의 인화점을 측정했다. 시편 번호 2는 Abel-Pensky(DIN 51755)의 방법에 따라 측정했다. 실시예 1에서와 같이 각 경우마다 동일한 폴리올을 사용했다. 결과는 표에 정리했다.
성분 | 단위 | No4.1 | No4.2 | No4.3 |
폴리올 | [g/100g 폴리올] | 100 | 100 | 100 |
Cp | [g/100g 폴리올] | 0 | 4.8 | 0 |
HFO 1233zd | [g/100g 폴리올] | 0 | 0 | 8.9 |
1013mbar로 평가된 인화점 | [℃] | 102.8 | < - 21 | > 56 |
샘플 번호 3은 등몰의 사이클로펜탄 함량을 함유하는 비교 샘플 번호 2보다 인화점이 상당히 높았다. 특히, 샘플 번호 3은 EG 440/2008 규정에 따라 인화성으로 분류되지 않아야 한다.
실시예 5 : 팽창제에 따른 기포 형성
일반 사항: 다양한 셀 가스 조성을 가진 단열 도관 파이프가 실시예 1에 따라 제조되었다.
실시예 5.1(비교 실험): 사이클로펜탄(Cp)은 정치식 혼합기의 보조하에 폴리올 성분에 상기 폴리올의 양 대비 7 중량%의 함량이 되도록 첨가했다. 이와 같이 제조된 파이프의 표면에서, 직경이 10 mm를 초과하고 특히 다른 도움 없이도 쉽게 인식되는 기포 12개가 30cm의 길이에서 계수되었다.
실시예 5.2 : 사이클로펜탄 2 중량% 및 HFO 1233zd 11 중량%의 양을 폴리올에 첨가했다. 이렇게 제조된 파이프의 표면에서는 생산된 400m의 길이에서 기포가 전혀 발견되지 않았다.
실시예 5.3 : 15 중량%의 HFO 1233zd의 양을 폴리올에 첨가했다. 이렇게 제조된 파이프의 표면에서는 생산된 350m의 길이에서 기포가 전혀 발견되지 않았다.
실시예 5.1 내지 5.3의 결과 : 이와 같이 수득된 셀 가스의 조성은 실시예 1에서와 같이 GC로 측정하고, 수득한 파이프를 육안으로 점검했다.
실시예 | 셀 가스의 조성 | 점검 |
5.1(비교) | 69% Cp 29% CO2 0% HFO 2% H2+N2 |
0.3m 길이에서 기포 12개 사용불가능 |
5.2 | 17% Cp 27% CO2 55% HFO 1% H2+N2 |
400m 길이에서 기포 0개 무결점 |
5.3 | 0% Cp 27% CO2 71% HFO 2% H2+N2 |
350m 길이에서 기포 0개 무결점 |
상기 데이터는 다량의 Cp가 사용불가능한 절연 도관 파이프를 생산하는 반면, HFO에 의한 부분 또는 완전 치환이 무결점의 절연 파이프를 생산한다는 것을 입증한다.
본 발명의 바람직한 구체예들이 본 명세서에 설명되지만, 본 발명은 여기에 제한되지 않고 이하 청구항 범위 내에서 다른 방식으로도 실행될 수 있음을 유의해야 한다.
1: 단열 도관 파이프 2: 외부 재킷
3: 단열재 4: 중간 파이프
5: 내측 6: 외측
7: 외부 중합체 층 8: 외부 접착 촉진제 층
9: 장벽 층 10: 내부 접착 촉진제 층
11: 내부 중합체 층
3: 단열재 4: 중간 파이프
5: 내측 6: 외측
7: 외부 중합체 층 8: 외부 접착 촉진제 층
9: 장벽 층 10: 내부 접착 촉진제 층
11: 내부 중합체 층
Claims (21)
- 적어도 하나의 중간 파이프(4), 상기 중간 파이프 둘레에 배치된 적어도 하나의 단열재(3) 및 상기 단열재 둘레에 배치된 적어도 하나의 외부 재킷(2)을 포함하는 단열 도관 파이프(1)로서,
상기 중간 파이프(4)는 가요성 파이프로 형성되고,
상기 외부 재킷(2)은 가요성 파이프로 형성되고, 플라스틱으로 제조된 장벽(9)을 포함하는 것이 가능하며,
상기 단열재(3)는 발포체를 포함하고, 상기 발포체의 셀 가스가 10 내지 100 vol%의 하이드로플루오로올레핀(HFO) 및 0 내지 50 vol%의 알칸, 사이클로알칸 또는 둘 다 및 0 내지 50 vol%의 CO2를 함유하며,
상기 HFO는 R1233zd, R1336mzz, 또는 둘 다로부터 선택되고,
상기 알칸은 프로판, 부탄, 펜탄, 헥산을 포함하는 그룹 중에서 선택되고, 상기 사이클로알칸은 사이클로펜탄 및 사이클로헥산을 포함하는 그룹 중에서 선택되며,
상기 단열재(3)는 폴리우레탄(PU)의 그룹 중에서 선택된 발포체를 함유하는 것을 특징으로 하는 단열 도관 파이프. - 제1항에 있어서, 상기 셀 가스가 10 내지 100 vol%의 HFO 및 0 내지 50 vol%의 알칸, 사이클로알칸 또는 둘 다 및 0 내지 50 vol%의 CO2를 함유하고, 단 상기 0 내지 50 vol%의 알칸, 사이클로알칸 또는 둘 다 대 HFO의 부피비가 1/2.5 이하인 것을 특징으로 하는 단열 도관 파이프.
- 제1항에 있어서, 상기 단열재(3)가 폴리우레탄(PU)으로 이루어지는 것을 특징으로 하는 단열 도관 파이프.
- 제1항 또는 제2항에 있어서, 상기 발포체가
- 셀 가스로서 50 내지 100 vol%의 R1233zd 및 0 내지 50 vol%의 사이클로펜탄을 함유하는 PU;
- 셀 가스로서 50 내지 100 vol%의 R1336mzz 및 0 내지 50 vol%의 사이클로 펜탄을 함유하는 PU 중에서 선택되는 것을 특징으로 하는 단열 도관 파이프. - 제1항 또는 제2항에 있어서, 장벽(9)이 제공되고, 상기 장벽은 층(layer)으로 형성되어,
- 상기 단열재의 외부로 셀 가스의 확산 및 단열재의 내부로 도관 파이프 외측의 가스의 확산을 감소시키고,
- 상기 단열재의 외부로 물의 확산을 가능하게 하는 것을 특징으로 하는 단열 도관 파이프. - 제5항에 있어서, 상기 장벽(9)이 하기 i), ii), 및 iii) 중 하나 이상을 만족시키는 것을 특징으로 하는 단열 도관 파이프.
i) 장벽(9)이 상기 단열재 위에 층으로 배치된다.
ii) 장벽(9)이 상기 외부 재킷의 내측에 층으로 배치된다.
iii) 장벽(9)이 상기 외부 재킷 중의 층으로 배치된다. - 제5항에 있어서, 상기 장벽(9)이,
- 에틸렌과 비닐 알코올의 공중합체 또는 에틸렌과 일산화탄소의 공중합체 또는 에틸렌과 일산화탄소와 프로필렌의 공중합체를 포함하고,
- 층 두께가 0.05 내지 0.5mm인 것을 특징으로 하는 단열 도관 파이프. - 제1항 또는 제2항에 있어서, 상기 중간 파이프(4)는,
- 플라스틱이 ABS, PEXa, PEXb, PEXc, PE, 폴리부텐(PB), PE-RT (polyethylene raised temperature) 및 폴리케톤(PK)의 그룹에서 선택되는 가요성 플라스틱 파이프; 또는
- 플라스틱이 ABS, PEXa, PEXb, PEXc, PE, 폴리부텐(PB), PE-RT (polyethylene raised temperature) 및 폴리케톤(PK)의 그룹에서 선택되고, 금속이 알루미늄 그룹에서 선택되는, 외부 금속층을 갖는 가요성 플라스틱 파이프; 또는
- 금속이 구리 합금을 비롯한 구리, 철 합금을 비롯한 철, 알루미늄 합금을 비롯한 알루미늄의 그룹에서 선택되는 가요성 금속 파이프인 것을 특징으로 하는 단열 도관 파이프. - 제1항 또는 제2항에 있어서,
- 상기 외부 재킷(2)은 파형 파이프로 형성되고; 상기 중간 파이프는 가요성 파이프 부분으로 형성되고; 또는
- 상기 외부 재킷(2)은 골판형 파이프로서 형성되고; 상기 중간 파이프는 가요성 파이프 부분으로 형성되는 것을 특징으로 하는 단열 도관 파이프. - 제1항 또는 제2항에 있어서,
상기 단열재(3)는 폐쇄형 셀 발포체를 포함하고, 상기 폐쇄형 셀 발포체의 셀 가스가
- 50 내지 100 vol%의 하이드로플루오로올레핀(HFO),
- 0 내지 50 vol%의 알칸, 사이클로알칸 또는 둘 다,
- 0 내지 50 vol%의 CO2, 및
- 0 내지 5 vol%의 질소, 산소, 또는 둘 다를 함유하는 것을 특징으로 하는 단열 도관 파이프. - 제1항 또는 제2항에 따른 단열 도관 파이프를 제조하는 방법으로서,
상기 단열재(3)는 발포체 형성을 위한 중합체 성분 및 팽창제로서 HFO를 함유하는 플라스틱 조성물을 발포시킴으로써 형성되는 것을 특징으로 하는 방법. - 제12항에 있어서,
- 상기 플라스틱 조성물은 2종의 액체 성분을 포함하되, 제1 성분은 폴리올 및 HFO를 함유하고 제2 성분은 이소시아네이트를 함유하며; 또는
- 상기 플라스틱 조성물은 2종의 액체 성분을 포함하되, 제1 성분은 폴리올을 함유하고 제2 성분은 이소시아네이트 및 HFO를 함유하는 것을 특징으로 하는 방법. - 제12항에 있어서, 적어도 하나의 가요성 중간 파이프(4), 단열재 층(3) 및 외부 재킷(2)을 보유하고, 상기 외부 재킷이 가능하게는 플라스틱으로 제조된 장벽(9)을 갖되,
(a) 상기 적어도 하나의 중간 파이프가 연속적으로 공급되고 튜브로 형성된 플라스틱 필름으로 포위되고,
(b) 발포성 플라스틱 조성물이 상기 중간 파이프와 튜브 사이의 공간으로 단열재 층으로서 도입되고,
(c) 상기 중간 파이프와 튜브는 수반하는 성형 부품으로 제조된 주형 내로 도입되고, 상기 주형을 그 끝에 남겨두고, 그 후
(d) 상기 외부 재킷이 상기 튜브의 표면 위로 압출되고,
상기 발포성 플라스틱 조성물이 발포체 형성을 위한 중합체 성분(들) 및 팽창제로서 HFO를 함유하는 것을 특징으로 하는 방법. - 제14항에 있어서, 장벽(9)이 제공되고,
- 상기 장벽이 발포된 단열재 층과 상기 외부 재킷의 내측 사이에 중합체로 제조된 튜브에 의해 도입되고; 또는
- 상기 장벽이 상기 외부 재킷과 함께 공압출에 의해 적용되고; 또는
- 상기 장벽이 상기 튜브에 직접 적용되고; 또는
- 먼저 상기 외부 재킷의 층이 적용되고, 그 다음 상기 장벽, 그 다음 상기 외부 재킷의 적어도 하나의 제2 층이 적용되는 것을 특징으로 하는 방법. - 단열 파이프 시스템, 또는 플라스틱 중간 파이프 시스템(PMP)에서의 발포체 절연재의 셀 가스로서,
상기 셀 가스가 10 내지 100 vol%의 하이드로플루오로올레핀(HFO) 및 0 내지 50 vol% 알칸, 사이클로알칸 또는 둘 다 및 0 내지 50 vol%의 CO2를 함유하되,
상기 HFO는 R1233zd, R1336mzz, 또는 둘 다로부터 선택되고,
상기 알칸은 프로판, 부탄, 펜탄, 헥산을 포함하는 그룹 중에서 선택되고, 상기 사이클로알칸은 사이클로펜탄 및 사이클로헥산을 포함하는 그룹 중에서 선택되는 셀 가스. - 단열재를 함유하는 플라스틱 중간 파이프 시스템(PMP)으로서, 상기 단열재가 발포체를 포함하고, 상기 발포체의 셀 가스가 제16항에 정의된 셀 가스인 것을 특징으로 하는 파이프 시스템.
- 삭제
- 삭제
- 삭제
- 삭제