KR102359909B1 - coating composition, expanded polystyrene having good flame retardancy and water resistant, and manufacturing method of the coating composition - Google Patents
coating composition, expanded polystyrene having good flame retardancy and water resistant, and manufacturing method of the coating composition Download PDFInfo
- Publication number
- KR102359909B1 KR102359909B1 KR1020190171262A KR20190171262A KR102359909B1 KR 102359909 B1 KR102359909 B1 KR 102359909B1 KR 1020190171262 A KR1020190171262 A KR 1020190171262A KR 20190171262 A KR20190171262 A KR 20190171262A KR 102359909 B1 KR102359909 B1 KR 102359909B1
- Authority
- KR
- South Korea
- Prior art keywords
- flame retardant
- coating composition
- weight
- calcium
- parts
- Prior art date
Abstract
본 발명은 코팅 조성물 및 이의 제조방법에 관한 것으로, 구체적으로 본 발명은 칼슘 함유 물질, 생석회, 탄소 함유 물질 및 바인더 등을 포함하는 코팅 조성물을 발포 폴리스티렌에 적용하여 상기 발포 폴리스티렌의 난연성 및 내수성을 향상시키는 것을 특징으로 한다.The present invention relates to a coating composition and a method for manufacturing the same, and more specifically, the present invention improves the flame retardancy and water resistance of the expanded polystyrene by applying a coating composition including a calcium-containing material, quicklime, a carbon-containing material, and a binder to the expanded polystyrene. characterized by doing.
Description
본 발명은 코팅 조성물 및 이의 제조방법에 관한 것으로, 구체적으로 본 발명은 칼슘계 난연제, 탄소계 난연제 및 바인더 등을 포함하는 코팅 조성물을 발포 폴리스티렌에 적용하여 상기 발포 폴리스티렌의 난연성 및 내수성을 향상시키는 것을 특징으로 한다.The present invention relates to a coating composition and a method for producing the same, and more specifically, the present invention is to improve the flame retardancy and water resistance of the expanded polystyrene by applying a coating composition comprising a calcium-based flame retardant, a carbon-based flame retardant, and a binder to the expanded polystyrene. characterized.
발포성 폴리스티렌은 우수한 가공성과 경량성, 단열성, 낮은 원가로 인해 건출물의 내외장재, 포장재료 등 다양한 산업분야에 걸쳐 널리 사용되고 있다.Expandable polystyrene is widely used in various industrial fields such as interior and exterior materials for buildings and packaging materials due to its excellent processability, lightness, insulation, and low cost.
최근에는 건축물의 에너지 절약 설계 기준이 강화됨에 따라 단열 성능이 우수한 유기 단열재 사용이 증가하는 추세이다. 이와 함께 단열성능이 우수한 외단열 시공법이 선호되는 상황이다. 외단열 시공법은 단열재가 건물 전체를 감싸는 시공법으로 단열성능에서는 우수하지만 화재 발생시 건물 전체로 불길이 빠르게 확산될 위험이 있기에 사용되는 단열재의 난연 성능이 매우 중요하게 다뤄진다. 그러나 발포 폴리스티렌이나 폴리우레탄폼은 불에 타기 쉽고 연소되는 동안 유독가스가 발생되는 단점이 있다.Recently, as the energy saving design standards of buildings are strengthened, the use of organic insulation materials with excellent thermal insulation performance is increasing. At the same time, the external insulation construction method with excellent thermal insulation performance is preferred. The exterior insulation construction method is a construction method in which the insulation material covers the entire building, and although it is excellent in insulation performance, there is a risk that the flame spreads quickly throughout the building in case of a fire. However, expanded polystyrene or polyurethane foam has the disadvantage of being easily flammable and generating toxic gas during combustion.
한국 등록특허 제10-1345148호는 염소화파라핀이 첨부된 발포성 폴리스티렌 입자에 관한 것으로, 단열재를 이루는 고분자 수지에 난연제로 코팅을 한 뒤 발포 성형하는 방법을 제시하는 것이 특징이다. 하지만 상기와 같은 발포 및 성형 과정에서 코팅층이 탈락하여 분진이 발생하거나 단열 성능이 저하되는 문제가 있을 수 있다.Korean Patent Registration No. 10-1345148 relates to expandable polystyrene particles to which chlorinated paraffin is attached. However, there may be problems in that the coating layer falls off during the foaming and molding process as described above, thereby generating dust or lowering the thermal insulation performance.
본 발명은 발포 폴리스티렌이 난연성을 향상시킬 수 있는 코팅 조성물을 제공할 목적이 있다.An object of the present invention is to provide a coating composition in which expanded polystyrene can improve flame retardancy.
본 발명은 발포 폴리스티렌에 적용할 코팅 조성물 제조하는데 있어서 경재성을 향상시킬 방법을 제공할 목적이 있다.An object of the present invention is to provide a method for improving the hardenability in manufacturing a coating composition to be applied to expanded polystyrene.
본 발명은 발포 폴리스티렌의 난연성 저하없이 내수성을 향상시킬 방법을 제공할 목적이 있다.An object of the present invention is to provide a method for improving the water resistance of expanded polystyrene without lowering the flame retardancy.
본 발명의 목적은 이상에서 언급한 목적으로 제한되지 않는다. 본 발명의 목적은 이하의 설명으로 보다 분명해 질 것이며, 특허청구범위에 기재된 수단 및 그 조합으로 실현될 것이다.The object of the present invention is not limited to the object mentioned above. The object of the present invention will become clearer from the following description, and will be realized by means and combinations thereof described in the claims.
본 발명에 따르면, 칼슘계 난연제; 탄소계 난연제; 바인더; 및 용매; 를 포함하는 내수성이 향상된 난연 코팅 조성물을 제공한다.According to the present invention, calcium-based flame retardant; carbon-based flame retardants; bookbinder; and solvents; It provides a flame retardant coating composition with improved water resistance comprising a.
상기 칼슘계 난연제는 실리카(SiO2)를 포함하는 것일 수 있다.The calcium-based flame retardant may include silica (SiO 2 ).
상기 칼슘계 난연제는 평균 입도 80mesh 이하인 것일 수 있다.The calcium-based flame retardant may have an average particle size of 80 mesh or less.
상기 칼슘계 난연제는 수분 함량이 10% 미만인 것일 수 있다.The calcium-based flame retardant may have a moisture content of less than 10%.
상기 칼슘계 난연제의 함량은 상기 용매 100중량부를 기준으로 50 내지 500중량부 인 것일 수 있다.The content of the calcium-based flame retardant may be 50 to 500 parts by weight based on 100 parts by weight of the solvent.
상기 탄소계 난연제는 팽창 흑연; 및 코크스, 그래핀, 탄소섬유 및 그래핀옥사이드 중 적어도 어느 하나를 포함하는 보조 난연제;를 포함하는 것일 수 있다.The carbon-based flame retardant is expanded graphite; and an auxiliary flame retardant comprising at least one of coke, graphene, carbon fiber, and graphene oxide.
상기 팽창 흑연은 고정탄소 함량 80중량% 내지 90중량% 및 회분 10중량% 내지 20중량% 포함하는 것일 수 있다.The expanded graphite may include a fixed carbon content of 80 wt% to 90 wt% and ash content of 10 wt% to 20 wt%.
상기 보조 난연제는 고정탄소 92중량% 내지 95중량% 및 회분 5중량% 내지 8중량%를 포함하는 것일 수 있다.The auxiliary flame retardant may include 92 wt% to 95 wt% of fixed carbon and 5 wt% to 8 wt% of ash.
상기 팽창 흑연의 함량은 상기 용매 100중량부를 기준으로 30 내지 400중량부 포함되는 것일 수 있다.The content of the expanded graphite may be 30 to 400 parts by weight based on 100 parts by weight of the solvent.
상기 보조 난연제의 함량은 상기 용매 100중량부를 기준으로 5 내지 50중량부 포함되는 것일 수 있다.The content of the auxiliary flame retardant may be 5 to 50 parts by weight based on 100 parts by weight of the solvent.
상기 바인더는 폴리비닐아세테이트(PVAc), 에틸렌비닐아세테이트(EVA) 및 이들의 조합으로 이루어진 군에서 선택된 것일 수 있다.The binder may be selected from the group consisting of polyvinyl acetate (PVAc), ethylene vinyl acetate (EVA), and combinations thereof.
상기 바인더는 점도가 2000 내지 5000cps이고, 수소 이온 농도 지수가 pH4 내지 pH6인 것일 수 있다.The binder may have a viscosity of 2000 to 5000cps, and a hydrogen ion concentration index of pH4 to pH6.
상기 바인더의 함량은 상기 용매 100중량부를 기준으로 20 내지 120중량부일 수 있다.The content of the binder may be 20 to 120 parts by weight based on 100 parts by weight of the solvent.
본 발명에 따르면, 발포체; 및 상기 발포체 상에 형성된 난연 코팅 조성물 층을 포함하고, 상기 난연 코팅 조성물 층은 제1항 내지 제12항 중 어느 한 항의 코팅 조성물을 포함하는 것인 난연성 및 내수성이 우수한 발포 폴리스티렌을 제공한다.According to the present invention, foam; and a flame-retardant coating composition layer formed on the foam, wherein the flame-retardant coating composition layer provides an expanded polystyrene excellent in flame retardancy and water resistance comprising the coating composition of any one of claims 1 to 12.
본 발명에 따르면, 적어도 칼슘계 난연제 및 탄소계 난연제를 포함하는 제1 혼합물을 제조하는 단계; 바인더 및 용매를 포함하는 제2 혼합물을 제조하는 단계; 및 상기 제1 혼합물 및 제2 혼합물을 포함하는 제3 혼합물을 제조하는 단계; 를 포함하고, 상기 칼슘계 난연제는 실리카(SiO2) 입자를 포함하고, 상기 바인더 폴리비닐아세테이트(PVAc), 에틸렌비닐아세테이트(EVA) 및 이들의 조합으로 이루어진 군에서 선택된 하나를 포함하는 것을 특징으로 하는 내수성이 향상된 난연 코팅 조성물 제조방법을 제공한다.According to the present invention, there is provided a method comprising: preparing a first mixture comprising at least a calcium-based flame retardant and a carbon-based flame retardant; preparing a second mixture including a binder and a solvent; and preparing a third mixture including the first mixture and the second mixture; Including, the calcium-based flame retardant comprising silica (SiO 2 ) particles, the binder polyvinyl acetate (PVAc), ethylene vinyl acetate (EVA), and comprising one selected from the group consisting of combinations thereof It provides a method for producing a flame retardant coating composition with improved water resistance.
상기 칼슘계 난연제 및 탄소계 난연제를 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제1 혼합물을 제조하는 것일 수 있다.A first mixture may be prepared by stirring the calcium-based flame retardant and the carbon-based flame retardant at a speed of 100 to 400 rpm for 5 to 30 minutes.
상기 바인더 및 용매를 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제2 혼합물을 제조하는 것일 수 있다.A second mixture may be prepared by stirring the binder and the solvent at a speed of 100 to 400 rpm for 5 to 30 minutes.
상기 제1 혼합물 및 제2 혼합물을 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제3 혼합물을 제조하는 것일 수 있다.The first mixture and the second mixture may be stirred at a speed of 100 to 400 rpm for 5 to 30 minutes to prepare a third mixture.
상기 탄소계 난연제는 팽창 흑연; 및 코크스, 그래핀, 탄소섬유 및 그래핀옥사이드 중 적어도 어느 하나를 포함하는 보조 난연제; 를 포함하는 것일 수 있다.The carbon-based flame retardant is expanded graphite; and an auxiliary flame retardant comprising at least one of coke, graphene, carbon fiber, and graphene oxide; may include.
상기 제3 혼합물 중 상기 팽창 흑연의 함량은 상기 용매 100중량부를 기준으로 30 내지 400중량부일 수 있다.The content of the expanded graphite in the third mixture may be 30 to 400 parts by weight based on 100 parts by weight of the solvent.
상기 제3 혼합물 중 상기 보조 난연제의 함량은 상기 용매 100중량부를 기준으로 5 내지 50중량부일 수 있다.The content of the auxiliary flame retardant in the third mixture may be 5 to 50 parts by weight based on 100 parts by weight of the solvent.
본 발명에 따르면 발포 폴리스티렌이 내수성을 향상시킬 수 있는 코팅 조성물을 제공할 수 있다.According to the present invention, it is possible to provide a coating composition in which expanded polystyrene can improve water resistance.
본 발명에 따르면 발포 폴리스티렌에 적용할 코팅 조성물 제조하는데 있어서 경재성을 향상시킬 방법을 제공할 수 있다.According to the present invention, it is possible to provide a method for improving the hardenability in manufacturing a coating composition to be applied to expanded polystyrene.
본 발명에 따르면 발포 폴리스티렌의 난연성 저하없이 내수성을 향상시킬 방법을 제공할 수 있다.According to the present invention, it is possible to provide a method for improving the water resistance of expanded polystyrene without lowering the flame retardancy.
본 발명의 효과는 이상에서 언급한 효과로 한정되지 않는다. 본 발명의 효과는 이하의 설명에서 추론 가능한 모든 효과를 포함하는 것으로 이해되어야 할 것이다.The effects of the present invention are not limited to the above-mentioned effects. It should be understood that the effects of the present invention include all effects that can be inferred from the following description.
도 1은 본 발명의 코팅 조성물 제조방법에 관한 순서도를 나타낸 것이다.
도 2는 본 발명의 실시예1 내지 실시예3의 발포 폴리스티렌의 내수성 평가 결과를 나타낸 것이다.1 shows a flow chart relating to a method for preparing a coating composition of the present invention.
Figure 2 shows the water resistance evaluation results of the expanded polystyrene of Examples 1 to 3 of the present invention.
이상의 본 발명의 목적들, 다른 목적들, 특징들 및 이점들은 첨부된 도면과 관련된 이하의 바람직한 실시예들을 통해서 쉽게 이해될 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 통상의 기술자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다.The above objects, other objects, features and advantages of the present invention will be easily understood through the following preferred embodiments in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments described herein and may be embodied in other forms. Rather, the embodiments introduced herein are provided so that the disclosed subject matter may be thorough and complete, and that the spirit of the present invention may be sufficiently conveyed to those skilled in the art.
각 도면을 설명하면서 유사한 참조부호를 유사한 구성요소에 대해 사용하였다. 첨부된 도면에 있어서, 구조물들의 치수는 본 발명의 명확성을 위하여 실제보다 확대하여 도시한 것이다. 제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다.In describing each figure, like reference numerals have been used for like elements. In the accompanying drawings, the dimensions of the structures are enlarged than the actual size for clarity of the present invention. Terms such as first, second, etc. may be used to describe various elements, but the elements should not be limited by the terms. The above terms are used only for the purpose of distinguishing one component from another. For example, without departing from the scope of the present invention, a first component may be referred to as a second component, and similarly, a second component may also be referred to as a first component. The singular expression includes the plural expression unless the context clearly dictates otherwise.
본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 또한, 층, 막, 영역, 판 등의 부분이 다른 부분 "상에" 있다고 할 경우, 이는 다른 부분 "바로 위에" 있는 경우뿐만 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다. 반대로 층, 막, 영역, 판 등의 부분이 다른 부분 "하부에" 있다고 할 경우, 이는 다른 부분 "바로 아래에" 있는 경우뿐만 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다.In this specification, terms such as "comprise" or "have" are intended to designate that a feature, number, step, operation, component, part, or a combination thereof described in the specification exists, but one or more other features It is to be understood that it does not preclude the possibility of the presence or addition of numbers, steps, operations, components, parts, or combinations thereof. Also, when a part of a layer, film, region, plate, etc. is said to be “on” another part, it includes not only the case where the other part is “directly on” but also the case where there is another part in between. Conversely, when a part, such as a layer, film, region, plate, etc., is "under" another part, this includes not only cases where it is "directly under" another part, but also a case where another part is in the middle.
달리 명시되지 않는 한, 본 명세서에서 사용된 성분, 반응 조건, 폴리머 조성물 및 배합물의 양을 표현하는 모든 숫자, 값 및/또는 표현은, 이러한 숫자들이 본질적으로 다른 것들 중에서 이러한 값을 얻는 데 발생하는 측정의 다양한 불확실성이 반영된 근사치들이므로, 모든 경우 "약"이라는 용어에 의해 수식되는 것으로 이해되어야 한다. 또한, 본 기재에서 수치범위가 개시되는 경우, 이러한 범위는 연속적이며, 달리 지적되지 않는 한 이러한 범 위의 최소값으로부터 최대값이 포함된 상기 최대값까지의 모든 값을 포함한다. 더 나아가, 이러한 범위가 정수를 지칭하는 경우, 달리 지적되지 않는 한 최소값으로부터 최대값이 포함된 상기 최대값까지를 포함하는 모든 정수가 포함된다.Unless otherwise specified, all numbers, values, and/or expressions expressing quantities of ingredients, reaction conditions, polymer compositions and formulations used herein, contain all numbers, values and/or expressions in which such numbers essentially occur in obtaining such values, among others. Since they are approximations reflecting various uncertainties in the measurement, it should be understood as being modified by the term "about" in all cases. Also, where the disclosure discloses numerical ranges, such ranges are continuous and inclusive of all values from the minimum to the maximum inclusive of the range, unless otherwise indicated. Furthermore, when such ranges refer to integers, all integers inclusive from the minimum to the maximum inclusive are included, unless otherwise indicated.
본 발명은 코팅 조성물, 이를 적용한 난연성 및 내수성이 우수한 발포 폴리스티렌 및 상기 코팅 조성물의 제조방법에 관한 것이다.The present invention relates to a coating composition, expanded polystyrene excellent in flame retardancy and water resistance to which it is applied, and a method for preparing the coating composition.
본 발명의 코팅 조성물 제조방법은 칼슘계 난연제 및 탄소제 난연제를 포함하는 제1 혼합물을 제조하는 단계, 바인더 및 용매를 포함하는 제2 혼합물을 제조하는 단계 및 상기 제1 혼합물 및 제2 혼합물을 포함하는 제3 혼합물을 제조하는 단계를 포함하는 것이 특징이이며, 본 발명의 코팅 조성물은 칼슘계 난연제, 탄소계 난연제, 바인더 및 용매를 포함하는 것이 특징이다.The coating composition manufacturing method of the present invention includes the steps of preparing a first mixture including a calcium-based flame retardant and a carbon-based flame retardant, preparing a second mixture including a binder and a solvent, and the first mixture and the second mixture It is characterized in that it comprises the step of preparing a third mixture, and the coating composition of the present invention is characterized by including a calcium-based flame retardant, a carbon-based flame retardant, a binder and a solvent.
도 1에는 본 발명의 코팅 조성물의 제조방법에 관한 순서도가 나타나 있는데 이를 참고하여 코팅 조성물 제조방법의 각 단계별로 자세히 설명하고, 더불어 본 발명의 코팅 조성물에 관해 설명하도록 하겠다.1 shows a flowchart of a method for producing a coating composition of the present invention. With reference to this, each step of the method for preparing a coating composition will be described in detail, and also the coating composition of the present invention will be described.
제1 혼합물 제조 단계First mixture preparation step
칼슘계 난연제 및 탄소계 난연제를 포함하는 제1 혼합물을 제조하는 단계이다.It is a step of preparing a first mixture comprising a calcium-based flame retardant and a carbon-based flame retardant.
상기 칼슘계 난연제는 탄산칼슘, 산화칼슘, 황산칼슘 및 이들의 조합으로 이루어진 군에서 선택된 하나의 칼슘 화합물을 포함한다.The calcium-based flame retardant includes one calcium compound selected from the group consisting of calcium carbonate, calcium oxide, calcium sulfate, and combinations thereof.
상기 칼슘계 난연제는 바람직하게 실리카(SiO2) 입자를 포함하며, 이때의 실리카 입자는 평균 입도 80mesh 이하이다. 보다 바람직하게 상기 실리카 입자의 평균 입도는 100 내지 200 mesh이다.The calcium-based flame retardant preferably includes silica (SiO 2 ) particles, wherein the silica particles have an average particle size of 80 mesh or less. More preferably, the average particle size of the silica particles is 100 to 200 mesh.
상기 평균 입도는 시판의 레이저 회절 산란식 입도 분포 측정기, 예를 들어 마이크로 트랙 입도 분포 측정 장치를 이용하여 측정할 수 있다. 또한 전자현미경 사진에서 임의로 200개의 입자를 추출하고 평균 입자 지름을 산출해도 좋다.The average particle size may be measured using a commercially available laser diffraction scattering particle size distribution analyzer, for example, a micro track particle size distribution analyzer. In addition, 200 particles may be arbitrarily extracted from the electron micrograph and the average particle diameter may be calculated.
상기 칼슘계 난연제는 수분 함유량이 10% 미만인 것이 바람직하다. 바람직하게 수분 함유량은 0 내지 8 % 이다.The calcium-based flame retardant preferably has a moisture content of less than 10%. Preferably the moisture content is 0 to 8%.
상기 칼슘계 난연제는 제2 혼합물에 포함되는 용매를 기준으로 50 내지 500중량부 포함되고, 바람직하게 80 내지 400 중량부 포함된다.The calcium-based flame retardant is included in an amount of 50 to 500 parts by weight, preferably 80 to 400 parts by weight, based on the solvent included in the second mixture.
상기 탄소계 난연제는 팽창 흑연을 포함하고, 코크스, 그래핀, 탄소섬유 및 그래핀옥사이드 중 적어도 어느 하나를 포함하는 보조 난연제를 포함한다.The carbon-based flame retardant includes expanded graphite, and an auxiliary flame retardant including at least one of coke, graphene, carbon fiber, and graphene oxide.
상기 팽창 흑연은 제2 혼합물에 포함되는 용매를 기준으로 30 내지 400중량부 포함되는 것이 바람직하다.The expanded graphite is preferably included in an amount of 30 to 400 parts by weight based on the solvent included in the second mixture.
상기 팽창흑연은 평균 입도 40 내지 200mesh 이고, 고정탄소를 80중량% 내지 90중량% 포함하고, 회분은 10 내지 20중량% 포함한다.The expanded graphite has an average particle size of 40 to 200 mesh, contains 80 wt% to 90 wt% of fixed carbon, and contains 10 to 20 wt% of ash.
상기 보조 난연제는 코크스, 그래핀, 그래핀 옥사이드, 탄소섬유 및 이들의 조합으로 이루어진 군에서 선택된 하나를 포함할 수 있다.The auxiliary flame retardant may include one selected from the group consisting of coke, graphene, graphene oxide, carbon fiber, and combinations thereof.
상기 보조 난연제는 제2 혼합물에 포함되는 용매를 기준으로 5 내지 100중량부 포함되는 것이 바람직하다.The auxiliary flame retardant is preferably included in an amount of 5 to 100 parts by weight based on the solvent included in the second mixture.
상기 보조 난연제는 평균 입도 800mesh 이하이고, 고정탄소를 92중량% 내지 95중량% 포함하고, 회분은 5중량% 내지 8중량% 포함한다.The auxiliary flame retardant has an average particle size of 800 mesh or less, and includes 92 wt% to 95 wt% of fixed carbon, and 5 wt% to 8 wt% of ash.
본 발명에서는 칼슘계 난연제 및 탄소계 난연제를 교반기에 투입하고 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제1 혼합물을 제조하는 것이 특징이다.In the present invention, it is characterized in that the calcium-based flame retardant and the carbon-based flame retardant are added to a stirrer and stirred at a speed of 100 to 400 rpm for 5 to 30 minutes to prepare a first mixture.
제2 혼합물 제조 단계Second mixture preparation step
바인더 및 용매를 포함하는 제2 혼합물을 제조하는 단계이다.It is a step of preparing a second mixture including a binder and a solvent.
제2 혼합물을 제조하는 단계는 상기 제1 혼합물을 제조하는 단계와 순서적으로 앞서서 진행될 수 있고, 또는 동시에 진행될 수 있으며, 본 발명에서 제1 혼합물 및 제2 혼합물을 제조하는 단계에 대한 시간적 우선순위는 중요하지 않다.The step of preparing the second mixture may be sequentially preceded or proceeded simultaneously with the step of preparing the first mixture, and the temporal priority for the step of preparing the first mixture and the second mixture in the present invention is not important
상기 용매는 물을 포함하고, 상기 바인더는 폴리비닐아세테이트(PVAc), 에틸렌비닐아세테이트(EVA) 및 이들의 조합으로 이루어진 군에서 선택된 하나를 포함한다. 바람직하게 폴리비닐아세테이트 및 에틸렌비닐아세테이트를 포함할 수 있다.The solvent includes water, and the binder includes one selected from the group consisting of polyvinyl acetate (PVAc), ethylene vinyl acetate (EVA), and combinations thereof. Preferably, it may include polyvinyl acetate and ethylene vinyl acetate.
상기 바인더는 점도 2000 내지 5000cps 이고, 수소 이온 농도 지수는 pH4 내지 pH6 이다.The binder has a viscosity of 2000 to 5000cps, and a hydrogen ion concentration index of pH4 to pH6.
상기 바인더의 함량은 용매 100중량부 기준 20 내지 120중량부 포함되며, 바람직하게 30 내지 100 중량부 포함될 수 있다.The content of the binder is 20 to 120 parts by weight based on 100 parts by weight of the solvent, and preferably 30 to 100 parts by weight.
상기 바인더 및 용매를 교반기에 투입하고 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제2 혼합물을 제조할 수 있다.A second mixture may be prepared by adding the binder and the solvent to a stirrer and stirring at a speed of 100 to 400 rpm for 5 to 30 minutes.
제3 혼합물 제조 단계Third step of preparing mixture
앞서 제조된 제1 혼합물 및 제2 혼합물을 혼합하여 제3 혼합물을 제조하는 단계이다.It is a step of preparing a third mixture by mixing the first mixture and the second mixture prepared previously.
상기 제1 혼합물 및 제2 혼합물을 교반기에 각각 투입하고 100 내지 400rpm의 속도로 5 내지 30분 동안 교반을 수행하여 제3 혼합물을 제조하게 된다.The first mixture and the second mixture are respectively added to a stirrer and stirred at a speed of 100 to 400 rpm for 5 to 30 minutes to prepare a third mixture.
발포 폴리스티렌(EPS)Expanded Polystyrene (EPS)
본 발명에서는 상기 코팅 조성물을 적용하여 난연성 및 내수성이 우수한 발포 폴리스티렌(EPS)을 제조할 수 있다.In the present invention, expanded polystyrene (EPS) having excellent flame retardancy and water resistance can be prepared by applying the coating composition.
구체적으로 발포 폴리스티렌(EPS)을 성형한 후 본 발명의 코팅 조성물을 성형체의 일면에 도포하여 코팅한 후 이를 건조하여 난연성 및 내수성이 우수한 발포 폴리스티렌을 제조할 수 있다.Specifically, after molding expanded polystyrene (EPS), the coating composition of the present invention is applied to one surface of the molded body to be coated, and then dried to prepare expanded polystyrene having excellent flame retardancy and water resistance.
상기 건조는 50℃ 이상의 온도에서 5 내지 50분 동안 진행되는 것이 바람직하며, 건조 방법은 적외선 건조 또는 열풍 건조 등 특별히 한정하지 않고 다양한 방법에 의해 수행될 수 있다.The drying is preferably performed at a temperature of 50° C. or higher for 5 to 50 minutes, and the drying method is not particularly limited, such as infrared drying or hot air drying, and may be performed by various methods.
이하, 본 발명을 구체적인 실시예를 통해 더욱 상세히 설명한다. 그러나 이들 실시예는 본 발명을 예시하기 위한 것으로 본 발명의 범위가 이들에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail through specific examples. However, these examples are for illustrating the present invention, and the scope of the present invention is not limited thereto.
실시예1Example 1
SiO2 함량이 18중량%, 평균 입도 80mesh 및 수분 함량 9%인 석고, 고정탄소 90%, 회분 10% 및 평균 입도 80mesh을 갖는 팽창 흑연, 및 고정탄소 92%, 회분 8% 및 평균 입도 10㎛을 갖는 코크스를 교반기에 투입하고 400rpm으로 30분간 교반하여 제1 혼합물을 제조하였다.Gypsum having a SiO 2 content of 18% by weight, an average particle size of 80mesh and a moisture content of 9%, an expanded graphite having a fixed carbon of 90%, an ash of 10% and an average particle size of 80mesh, and a fixed carbon of 92%, an ash of 8% and an average particle size of 10 μm was put into a stirrer and stirred at 400 rpm for 30 minutes to prepare a first mixture.
점도 약 3000cps 및 수소 이온 농도 지수 pH6.0을 갖는 에틸렌비닐아세테이트(EVA) 바인더를 용매인 물과 함께 교반기에 투입후 400rpm의 속도로 30분간 교반하여 제2 혼합물을 제조하였다.An ethylene vinyl acetate (EVA) binder having a viscosity of about 3000 cps and a hydrogen ion concentration index of pH 6.0 was added to a stirrer together with water as a solvent, and stirred at a speed of 400 rpm for 30 minutes to prepare a second mixture.
상기 제조된 제1 혼합물 및 제2 혼합물을 하나의 교반기에 투입하여 400rpm의 속도로 30분간 교반하여 제3 혼합물(코팅 조성물)을 제조하였고, 이를 발포 폴리스티렌 성형품의 일면에 도포한 후 건조장치를 이용하여 60℃의 적외선 건조를 실행하였다.The prepared first mixture and the second mixture were put into one stirrer and stirred at a speed of 400 rpm for 30 minutes to prepare a third mixture (coating composition), which was applied to one side of the expanded polystyrene molded article and then dried using a drying device. to carry out infrared drying at 60°C.
이때 상기 칼슘계 난연제, 탄소계 난연제 및 바인더의 투입 함량은 용매(물) 100중량부 기준으로 각각 60중량부, 200중량부 및 60중량부가 되도록 조절하였다.At this time, the amounts of the calcium-based flame retardant, the carbon-based flame retardant and the binder were adjusted to be 60 parts by weight, 200 parts by weight, and 60 parts by weight, respectively, based on 100 parts by weight of the solvent (water).
실시예2 내지 실시예10 , 비교예1 내지 비교예7Examples 2 to 10, Comparative Examples 1 to 7
하기 표 1 및 표 2와 같이 칼슘계 난연제, 탄소계 난연제 및 바인더의 함량을 조절하여 코팅 조성물을 제조하였다. 이를 상기 실시예1과 동일하게 발포 폴리스티렌 성형품의 일면에 도포한 후 건조장치를 이용하여 적외선 건조를 실행하였다.As shown in Tables 1 and 2 below, the coating composition was prepared by adjusting the content of the calcium-based flame retardant, the carbon-based flame retardant, and the binder. This was applied to one surface of the expanded polystyrene molded article in the same manner as in Example 1, followed by infrared drying using a drying device.
난연제calcium
flame retardant
흑연expansion
black smoke
난연제calcium
flame retardant
흑연expansion
black smoke
난연제assistant
flame retardant
실험예 (난연성 평가, 코팅성 및 내수성 평가)Experimental example (flame retardancy evaluation, coating property and water resistance evaluation)
상기 실시예1 내지 실시예10 및 비교예1 내지 비교예7에서 제조된 발포 폴리스티렌을 이용하여 난연성, 코팅성 및 내수성 등을 평가하여 하기 표3 및 표4에 나타내었다. Using the expanded polystyrene prepared in Examples 1 to 10 and Comparative Examples 1 to 7, flame retardancy, coating properties, and water resistance were evaluated and shown in Tables 3 and 4 below.
코팅성: 발포 폴리스티렌에 코팅 조성물을 도포하여 균일한 난연 코팅 조성물 층이 형성되는지 여부 확인.Coatability: Check whether a uniform flame retardant coating composition layer is formed by applying the coating composition to the expanded polystyrene.
건조: 60℃, 10분 동안 건조를 수행한 후, 완전 건조 여부 확인.Drying: After drying at 60°C for 10 minutes, check whether it is completely dry.
내수성: 발포 폴리스티렌(시편)을 물속에 24시간 동안 침지 후 흰 바탕의 기재상에 마찰시켜 난연 코팅 조성물 층의 탈락 발생 유무 관찰.Water resistance: After immersing expanded polystyrene (specimen) in water for 24 hours, rubbing it on a white base material to observe whether the flame retardant coating composition layer fell off.
난연성: 콘칼로리미터 시험법을 적용하여 난연성을 측정.Flame retardancy: Measure the flame retardancy by applying the cone calorimeter test method.
상기 표 3의 실시예1 내지 실시예10의 결과를 참고하면, 코팅성, 건조, 내수성 및 난연성에 있어서 모두 본 발명이 목적하는 결과가 나왔음을 알 수 있다.Referring to the results of Examples 1 to 10 in Table 3, it can be seen that the desired results of the present invention were obtained in all of the coating properties, drying, water resistance and flame retardancy.
특히, 난연성에 있어서 열방출률은 2.1 내지 4.1MJ/m2 값을 보여줌으로써 비교적 난연성이 우수한 발포 폴리스티렌이 제조된 것을 확인할 수 있다.In particular, in terms of flame retardancy, the heat release rate showed a value of 2.1 to 4.1 MJ/m 2 , thereby confirming that expanded polystyrene having relatively excellent flame retardancy was prepared.
내수성과 관련하여 도 2에는 상기 실시예1 내지 실시예3의 발포 폴리스티렌에 대한 내수성 평가 결과가 나타나 있다. 이를 참고하면, 24시간 침지 후 마찰 테스트에서도 난연 코팅 조성물 층 표면의 탄소계 난연제인 팽창흑연에 의한 연필 효과 외 코팅층의 탈락이 없음을 확인할 수 있다.In relation to water resistance, FIG. 2 shows water resistance evaluation results for the expanded polystyrene of Examples 1 to 3 above. Referring to this, even in the friction test after immersion for 24 hours, it can be confirmed that there is no drop-off of the coating layer other than the pencil effect by the expanded graphite, which is a carbon-based flame retardant, on the surface of the flame-retardant coating composition layer.
결과적으로 본 발명의 코팅 조성물을 적용할 경우 종래의 발포 폴리스티렌과 난연성에 큰 차이 없이 내수성이 향상된 발포 폴리스티렌을 제조할 수 있음을 확인할 수 있다.As a result, it can be confirmed that, when the coating composition of the present invention is applied, expanded polystyrene with improved water resistance can be prepared without a significant difference in flame retardancy from conventional expanded polystyrene.
이상으로 본 발명의 실시예에 대해 상세히 설명하였는바, 본 발명의 권리범위는 상술한 실시예에 한정되지 않으며, 다음의 특허청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 포함된다.As the embodiments of the present invention have been described in detail above, the scope of the present invention is not limited to the above-described embodiments, and various modifications and An improved form is also included in the scope of the present invention.
Claims (21)
팽창 흑연; 및 코크스, 그래핀, 탄소섬유 및 그래핀 옥사이드 중 적어도 어느 하나를 포함하는 보조 난연제; 를 포함하는 탄소계 난연제;
바인더; 및 용매; 를 포함하고,
상기 칼슘계 난연제는 실리카(SiO2)를 포함하고,
상기 실리카 입자의 평균 입도 80mesh 이하이고,
상기 칼슘계 난연제의 함량은 상기 용매 100 중량부를 기준으로 50 내지 500중량부이고,
상기 팽창 흑연의 함량은 상기 용매 100중량부를 기준으로 30 내지 400중량부이고,
상기 보조 난연제의 함량은 상기 용매 100중량부를 기준으로 5 내지 50중량부이고,
상기 팽창 흑연은 고정탄소 함량 80중량% 내지 90중량% 및 회분 10중량% 내지 20중량% 포함하고,
상기 보조 난연제는 고정탄소 92중량% 내지 95중량% 및 회분 5중량% 내지 8중량%를 포함하는 것을 특징으로 하는 내수성이 향상된 난연 코팅 조성물.a calcium-based flame retardant comprising one calcium compound selected from the group consisting of calcium carbonate, calcium oxide, calcium sulfate, and combinations thereof;
expanded graphite; and an auxiliary flame retardant comprising at least one of coke, graphene, carbon fiber, and graphene oxide; A carbon-based flame retardant comprising;
bookbinder; and solvents; including,
The calcium-based flame retardant comprises silica (SiO 2 ),
The average particle size of the silica particles is 80 mesh or less,
The content of the calcium-based flame retardant is 50 to 500 parts by weight based on 100 parts by weight of the solvent,
The content of the expanded graphite is 30 to 400 parts by weight based on 100 parts by weight of the solvent,
The content of the auxiliary flame retardant is 5 to 50 parts by weight based on 100 parts by weight of the solvent,
The expanded graphite comprises 80% to 90% by weight of fixed carbon and 10% to 20% by weight of ash,
The auxiliary flame retardant is a flame retardant coating composition with improved water resistance, characterized in that it comprises 92 wt% to 95 wt% of fixed carbon and 5 wt% to 8 wt% of ash.
상기 바인더는 폴리비닐아세테이트(PVAc), 에틸렌비닐아세테이트(EVA) 및 이들의 조합으로 이루어진 군에서 선택된 것을 포함하는 내수성이 향상된 난연 코팅 조성물.According to claim 1,
The binder is polyvinyl acetate (PVAc), ethylene vinyl acetate (EVA), and a flame retardant coating composition with improved water resistance comprising one selected from the group consisting of combinations thereof.
상기 바인더는 점도가 2000 내지 5000cps이고, 수소 이온 농도 지수가 pH4 내지 pH6인 것인 내수성이 향상된 난연 코팅 조성물.According to claim 1,
The binder has a viscosity of 2000 to 5000cps, and a hydrogen ion concentration index of pH4 to pH6 of a flame retardant coating composition with improved water resistance.
상기 바인더의 함량은 상기 용매 100중량부를 기준으로 20 내지 120중량부인 내수성이 향상된 난연 코팅 조성물.According to claim 1,
The content of the binder is 20 to 120 parts by weight based on 100 parts by weight of the solvent, flame retardant coating composition with improved water resistance.
상기 발포체 상에 형성된 난연 코팅 조성물 층을 포함하고,
상기 난연 코팅 조성물 층은 제1항, 제11항 내지 제13항 중 어느 한 항의 코팅 조성물을 포함하는 것을 특징으로 하는 난연성 및 내수성이 우수한 발포 폴리스티렌.foam; and
a flame retardant coating composition layer formed on the foam;
The flame retardant coating composition layer is expanded polystyrene excellent in flame retardancy and water resistance, characterized in that it comprises the coating composition of any one of claims 1 and 11 to 13.
바인더 및 용매를 포함하는 제2 혼합물을 제조하는 단계; 및
상기 제1 혼합물 및 제2 혼합물을 포함하는 제3 혼합물을 제조하는 단계; 를 포함하고,
상기 칼슘계 난연제는 탄산칼슘, 산화칼슘, 황산칼슘 및 이들의 조합으로 이루어진 군에서 선택된 하나의 칼슘 화합물을 포함하고,
상기 칼슘계 난연제는 실리카(SiO2) 입자를 포함하고,
상기 탄소계 난연제는 팽창 흑연; 및 코크스, 그래핀, 탄소섬유 및 그래핀 옥사이드 중 적어도 어느 하나를 포함하는 보조 난연제; 를 포함하고,
상기 실리카 입자의 평균 입도 80mesh 이하이고,
상기 칼슘계 난연제의 함량은 상기 용매 100 중량부를 기준으로 50 내지 500 중량부이고,
상기 팽창 흑연의 함량은 상기 용매 100 중량부를 기준으로 30 내지 400 중량부이고,
상기 보조 난연제의 함량은 상기 용매 100 중량부를 기준으로 5 내지 50 중량부이고,
상기 팽창 흑연은 고정탄소 함량 80중량% 내지 90중량% 및 회분 10중량% 내지 20중량% 포함하고,
상기 보조 난연제는 고정탄소 92중량% 내지 95중량% 및 회분 5중량% 내지 8중량% 포함하고,
상기 바인더는 폴리비닐아세테이트(PVAc), 에틸렌비닐아세테이트(EVA) 및 이들의 조합으로 이루어진 군에서 선택된 하나를 포함하는 것을 특징으로 하는 내수성이 향상된 난연 코팅 조성물 제조방법.preparing a first mixture comprising a calcium-based flame retardant and a carbon-based flame retardant;
preparing a second mixture including a binder and a solvent; and
preparing a third mixture including the first mixture and the second mixture; including,
The calcium-based flame retardant includes one calcium compound selected from the group consisting of calcium carbonate, calcium oxide, calcium sulfate, and combinations thereof,
The calcium-based flame retardant comprises silica (SiO 2 ) particles,
The carbon-based flame retardant is expanded graphite; and an auxiliary flame retardant comprising at least one of coke, graphene, carbon fiber, and graphene oxide; including,
The average particle size of the silica particles is 80 mesh or less,
The content of the calcium-based flame retardant is 50 to 500 parts by weight based on 100 parts by weight of the solvent,
The content of the expanded graphite is 30 to 400 parts by weight based on 100 parts by weight of the solvent,
The content of the auxiliary flame retardant is 5 to 50 parts by weight based on 100 parts by weight of the solvent,
The expanded graphite comprises 80% to 90% by weight of fixed carbon and 10% to 20% by weight of ash,
The auxiliary flame retardant comprises 92 wt% to 95 wt% of fixed carbon and 5 wt% to 8 wt% of ash,
Wherein the binder comprises one selected from the group consisting of polyvinyl acetate (PVAc), ethylene vinyl acetate (EVA), and combinations thereof.
상기 칼슘계 난연제 및 탄소계 난연제를 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제1 혼합물을 제조하는 것인 내수성이 향상된 난연 코팅 조성물 제조방법.16. The method of claim 15,
The method for producing a flame retardant coating composition with improved water resistance to prepare a first mixture by stirring the calcium-based flame retardant and the carbon-based flame retardant at a speed of 100 to 400 rpm for 5 to 30 minutes.
상기 바인더 및 용매를 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제2 혼합물을 제조하는 것인 내수성이 향상된 난연 코팅 조성물 제조방법.16. The method of claim 15,
A method for producing a flame retardant coating composition having improved water resistance to prepare a second mixture by stirring the binder and the solvent at a speed of 100 to 400 rpm for 5 to 30 minutes.
상기 제1 혼합물 및 제2 혼합물을 100 내지 400rpm의 속도로 5 내지 30분 동안 교반하여 제3 혼합물을 제조하는 것인 내수성이 향상된 난연 코팅 조성물 제조방법.16. The method of claim 15,
A method for producing a flame retardant coating composition with improved water resistance to prepare a third mixture by stirring the first mixture and the second mixture at a speed of 100 to 400 rpm for 5 to 30 minutes.
상기 탄소계 난연제는 팽창 흑연; 및
코크스, 그래핀, 탄소섬유 및 그래핀옥사이드 중 적어도 어느 하나를 포함하는 보조 난연제; 를 포함하는 것인 내수성이 향상된 난연 코팅 조성물 제조방법.16. The method of claim 15,
The carbon-based flame retardant is expanded graphite; and
Auxiliary flame retardant comprising at least one of coke, graphene, carbon fiber and graphene oxide; A method for producing a flame-retardant coating composition with improved water resistance comprising a.