KR102348390B1 - 논슬립 발포폼을 포함하는 타일형 바닥장식재 및 이의 제조방법 - Google Patents

논슬립 발포폼을 포함하는 타일형 바닥장식재 및 이의 제조방법 Download PDF

Info

Publication number
KR102348390B1
KR102348390B1 KR1020200015906A KR20200015906A KR102348390B1 KR 102348390 B1 KR102348390 B1 KR 102348390B1 KR 1020200015906 A KR1020200015906 A KR 1020200015906A KR 20200015906 A KR20200015906 A KR 20200015906A KR 102348390 B1 KR102348390 B1 KR 102348390B1
Authority
KR
South Korea
Prior art keywords
weight
parts
layer
flooring
stabilizer
Prior art date
Application number
KR1020200015906A
Other languages
English (en)
Other versions
KR20210101660A (ko
Inventor
오동진
Original Assignee
주식회사 동신포리마
신코카세이 카부시키카이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to KR1020200015906A priority Critical patent/KR102348390B1/ko
Application filed by 주식회사 동신포리마, 신코카세이 카부시키카이샤 filed Critical 주식회사 동신포리마
Priority to JP2022518741A priority patent/JP2022549313A/ja
Priority to AU2021219508A priority patent/AU2021219508B2/en
Priority to EP21753118.5A priority patent/EP4019710A4/en
Priority to PCT/KR2021/001166 priority patent/WO2021162296A1/ko
Priority to CA3151985A priority patent/CA3151985A1/en
Priority to CN202180005460.1A priority patent/CN114521220A/zh
Priority to US17/761,372 priority patent/US11987022B2/en
Publication of KR20210101660A publication Critical patent/KR20210101660A/ko
Application granted granted Critical
Publication of KR102348390B1 publication Critical patent/KR102348390B1/ko
Priority to JP2024019691A priority patent/JP2024059697A/ja

Abstract

본 발명은 표면처리층, 투명층, 디자인 인쇄층 및 하지층을 포함하는 바닥재부; 및 플라스틱 발포폼층 및 미세 엠보스를 갖는 밀착필름층을 포함하는 미세 엠보스 플라스틱 폼부;를 포함하는 타일형 바닥장식재에 관한 것으로, 접착제를 사용하지 않는 시공 공정에서 제품과 바닥면 사이의 미끄러짐을 현저하게 개선한 타일형 바닥장식재를 제공할 수 있다.

Description

논슬립 발포폼을 포함하는 타일형 바닥장식재 및 이의 제조방법{Tile type decorative flooring comprising non-slip foams and manufacturing method thereof}
본 발명은 건물의 바닥이나 마루에 적용될 수 있는 바닥장식재에 관한 것으로, 더욱 자세하게는 바닥장식재 제품 가운데 단위 크기로 절단하여 시공되는 타일구조 제품에 있어 접착제를 사용하지 않는 시공 공정에서 제품과 바닥면 사이의 미끄러짐을 현저하게 개선한 타일형 바닥장식재에 관한 것이다.
여기서는, 본 개시에 관한 배경기술이 제공되며, 이들이 반드시 공지기술을 의미하는 것은 아니다.
일반적으로 건물의 바닥이나 마루에는 장판이나 타일 등의 바닥(장식)재가 시공된다. 장판이나 타일 등의 바닥재로는 가볍고, 유연성이 있으며, 쿠션성 및 흡음성 등이 우수한 염화비닐을 주재료로 하여 제조된다. 예를 들어, 바닥재는 폴리염화비닐(PVC, Poly Vinyl Chloride) 또는 염화비닐에 다른 소재를 혼합하거나 합지하여 제조된다. 이러한 바닥재는 보통 투명층, 인쇄층, 수지함침 치수보강층, 발포층 및 하지층 등 복수층으로 적층하여 구성되며, 투명층은 인쇄층에 인쇄된 잉크면을 보호하는 기능을 갖고, 인쇄층은 색상이나 무늬를 부여하여 장식 기능을 갖고, 수지함침 치수보강층은 PVC 페이스트 졸로 함침처리된 글라스파이버(Glass-Fiber)로서 제품의 치수안전성을 보강하는 기능을 가지며, 발포층은 쿠션을 부여하는 기능을 하며, 하지층은 두께보강 및 바닥면과의 안착 기능을 한다.
또, 투명 필름층 상단에는 필요에 따라 내마모성이나 내스크래치성의 향상을 위한 표면처리층이 더 형성될 수 있다. 이와 같은 바닥재는 용도에 따라 각 층을 가감하여 제작되며, 광범위한 분야에서 사용된다.
예를 들어, 본 출원인이 특허출원하여 등록받은 하기의 특허문헌 1에는 상단 PVC층과 하단 PVC층 사이에 유리섬유나 암면을 시트화하여 제조된 유리섬유 매트층을 형성한 다음 열가압하여 제조된 기재층의 상단으로 인쇄층과 PVC 수지로 된 투명 필름층을 순차적으로 형성시키고, 기재층 하단으로 PVC 수지와 가소제 및 충진제로 이루어지는 밸런스층을 형성시키는 바닥장식재의 제조방법 기술이 개시되어 있다. 이와 같은 구성의 바닥재는 건물의 바닥을 마감 처리하는 과정에서 단독으로 사용하거나, 이를 다양한 종류의 피착물과 접착제로 부착시킨 후 사용된다.
또, 최근에는 접착제 사용으로 인한 냄새를 제거하고, 휘발성 유기화합물 등의 영향을 최소화하고자, 기재층 하부에 미끄럼을 방지하기 위한 기능층을 형성해서 시공시 접착제 사용을 최소화하는 미끄럼 방지 기능의 바닥재가 개발되고 있다.
한편, 일반적인 바닥재, 특히 단위크기로 절단되는 바닥타일의 경우 바닥에 접착제를 도포하고 그 위에 타일을 시공하므로 바닥면과 타일을 부착하게 하고, 치수의 변화를 최소화 하는 것이 일반적이었으나 최근, 접착제의 유해성이 부각되고 치수의 변화를 최소화 하는 바닥재를 개발하므로 접착제를 시공하지 않거나 소량의 점착제 시공 바닥위에 제품을 올려놓는 것만으로 시공되는 루스레이 제품이 다양하게 개발 되어 시공이 용이하고 비용을 절감하며, 접착제의 유해성이 없는 제품으로 각광 받고 있다.
이 루스레이 제품은 바닥재 이면에 바닥면과 밀착성이 우수한 기능이 있는 소재를 적층하는 것이 일반적인데 폴리에틸렌이나 폴리프로필렌 등을 조합한 올레핀계 발포체를 부착한 제품으로 충격음을 흡수할 수 있도록 하는 제품에서는 발포폼이 바닥면과의 밀착성이 떨어지기 때문에 그 미끄럼으로 인하여 루스레이 시공을 하지 못하고 접착제를 사용할 수밖에 없는 것이 현실이었다.
이를 개선하기 위하여 점착기능을 가지는 처리제를 플라스틱 폼 이면에 처리하거나 점착 시트를 적층하는 등의 다양한 시도가 진행되고 있으나 보관 시 부착되는 블로킹을 유발하거나 점착성분이 전이 되거나, 바닥재 표면층의 손상을 입히는 문제점이 있었다.
특히 이를 개선하기 위하여 특허 출원번호 제10-2010-0081283호 (2010.08.23)에서는 바닥재 이면에 점착층을 적층하고 이형지를 부착하여 손쉽게 시공하는 것을 특징으로 하는 제품을 개발하게 되었으나 점착제와 이형지를 부착하므로 취급이 불편하고, 공정이 복잡하며, 별도의 설비가 요구되어 원가가 상승하는 요인이 되는 등의 문제점이 있었다.
대한민국 특허등록공보 제10-0510836호(2005. 08. 30 등록) 대한민국 특허등록공보 제10-0600841호(2006. 07. 06 등록) 대한민국 특허등록공보 제10-1149890호(2012. 05. 18 등록)
본 발명은 충격음 흡수 기능이 있는 플라스틱 발포폼을 적층한 제품으로 시공시 접착제를 사용하지 않거나 소량의 점착제를 도장한 곳 위에 시공하는 제품에서의 제품과 바닥면 사이에서의 미끄러짐을 현저하게 개선한 타일형 바닥장식재를 제공하고자 한다.
그러나 본 발명의 목적들은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
본 발명은 표면처리층, 투명층, 디자인 인쇄층, 중지층, 치수보강층 하지층 및 밸런스층을 포함하는 바닥재부; 및 플라스틱 발포폼층 및 미세 엠보스를 갖는 밀착필름층을 포함하는 미세 엠보스 플라스틱 폼부;를 포함하는 타일형 바닥장식재를 제공한다.
또한 상기 플라스틱 발포폼층은 올레핀계 수지 100 중량부에 대하여 아조디카본아마이드 발포제 3 내지 10 중량부, 촉진제 0.2 내지 1.5 중량부, 발포안정제 0.1 내지 1 중량부 및 기타 첨가제를 포함하여 압출 가공 후 발포되어 형성된 층인 것을 특징으로 한다.
또한 상기 밀착필름층은 깊이(a)를 갖는 요철이 일정 간격(b)으로 구비되는 미세 엠보스를 가지며, 상기 미세 엠보스는 하기 식 1을 만족하는 것을 특징으로 한다.
[식 1] a ≥ 1/3 * b
(이 때, 0.08mm ≤ a ≤ 0.8mm이고, 0.2 ≤ b ≤ 2mm 이다.)
또한 상기 밀착필름층은 올레핀계 수지 100 중량부에 대하여 산화방지제 0.1 내지 1 중량부, 가공조제 0.1 내지 1 중량부 및 기타 첨가제를 포함하며, 10 내지 200μm 의 두께를 갖는 올레핀계 필름인 것을 특징으로 한다.
또한 상기 밀착필름층은 PVC 수지 100 중량부에 대하여 가소제 30 내지 60 중량부, 안정제 1 내지 5 중량부 및 기타 첨가제를 포함하며, 10 내지 200μm 의 두께를 갖는 PVC 필름인 것을 특징으로 한다.
또한 상기 표면처리층은 모노에스테르(Monoester) 20 내지 40중량%, 올리고머(Oligomer) 10 내지 20중량%, 폴리디아크릴레이트(Poly Diacrylate) 10 내지 20중량%, 실리콘(Silicon) 0.5 내지 5중량% 및 기타 첨가제를 포함하여 자외선에 의하여 5 내지 20μm의 두께로 코팅하고 자외선으로 경화된 층인 것을 특징으로 한다.
또한 상기 투명층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 50 중량부, 안정제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.1 내지 1mm 두께로 형성된 층인 것을 특징으로 한다.
또한 상기 디자인 인쇄층은 PVC 수지 100 중량부에 대하여 가소제 1 내지 20 중량부, 안정제 1 내지 5중량부, 충진재 0 내지 20 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.05 내지 0.2mm 두께로 형성된 층인 것을 특징으로 한다.
또한 상기 하지층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 600 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.5 내지 5mm 두께로 형성된 층인 것을 특징으로 한다.
또한 상기 바닥재부는 상기 디자인 인쇄층 및 상기 하지층 사이에 구비되는 중지층을 더 포함하며, 상기 중지층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.2 내지 2mm 두께로 형성된 층인 것을 특징으로 한다.
또한 상기 바닥재부는 중지층, 치수보강층 및 밸런스층으로 구성되는 군에서 선택되는 어느 1층 이상을 더 포함하며, 상기 중지층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.2 내지 2mm 두께로 형성된 층이고, 상기 치수보강층은 PVC 페이스트 수지 100 중량부에 대하여 가소제 50 내지 90 중량부, 안정제 1 내지 5 중량부, 충진재 10 내지 150 중량부, 점도조절제 2 내지 10 중량부 및 기타 첨가제를 포함하는 액상의 페이스트졸에 유리섬유 메트를 함침하여 가열 경화한 층이며, 상기 밸런스층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.3 내지 3mm 두께로 형성된 층인 것을 특징으로 한다.
또한 본 발명은 하지층, 디자인 인쇄층, 투명층 및 표면처리층을 적층하여 바닥재부를 형성하는 단계; 상기 하지층의 이면에 플라스틱 발포폼층 조성물을 압출 가공하고 전자선 가교 후 발포하거나 화학 발포하여 플라스틱 발포폼층을 형성하는 단계; 및 밀착필름층 조성물을 압출 가공하면서 상기 플라스틱 발포폼층의 이면에 부착하여 밀착필름층을 형성하는 단계;를 포함하는 타일형 바닥장식재의 제조방법을 제공한다.
본 발명은 바닥장식재 제품 가운데 단위 크기로 절단하여 시공되는 타일구조의 바닥장식재에 있어서 하단부에 화학적 발포로 플라스틱 폼을 구성하는 쿠션층을 포함하며, 이 쿠션층의 최하단부에는 미끄럼을 방지할 수 있는 미세 요철 엠보스를 포함한다. 이로써 플라스틱폼의 쿠션층에 의한 보행감 개선과 충격음 흡수효과가 있고, 최하단부의 미세 요철 엠보스에 의하여 접착제를 사용하지 않는 시공 공정에서 제품과 바닥면사이의 미끄러짐을 현저하게 개선한 바닥장식재를 제공한다.
특히 최근에 접착제의 유해성을 회피하여 개발된 접착제를 사용하지 않거나 소량의 점착제를 도장한 곳 위에 시공하는 루스레이(Loose lay) 타일의 시공 시 바닥면과 바닥재의 밀착도의 차이로 바닥재가 미끄러져 밀리는 현상을 현저하게 개선할 수 있는 것을 특징으로 한다.
도 1에 본 발명의 일실시예에 따른 타일형 바닥장식재의 구조를 나타내었다.
도 2에 본 발명의 일실시예에 따른 밀착필름층의 미세 엠보스 구조를 나타내었다.
본 명세서에 사용되는 모든 기술용어 및 과학용어는 다른 언급이 없는 한은 기술적으로 통상의 기술을 가진 자에게 일반적으로 이해되는 것과 동일한 의미를 가진다. 또한 본 명세서 및 청구범위의 전반에 걸쳐, 다른 언급이 없는 한 포함(comprise, comprises, comprising)이라는 용어는 언급된 물건, 단계 또는 일군의 물건, 및 단계를 포함하는 것을 의미하고, 임의의 어떤 다른 물건, 단계 또는 일군의 물건 또는 일군의 단계를 배제하는 의미로 사용된 것은 아니다.
이하에 본 발명을 상세하게 설명하기에 앞서, 본 명세서에 사용된 용어는 특정의 실시예를 기술하기 위한 것일 뿐 첨부하는 특허청구의 범위에 의해서만 한정되는 본 발명의 범위를 한정하려는 것은 아님을 이해하여야 한다.
한편, 본 발명의 여러 가지 실시예들은 명확한 반대의 지적이 없는 한 그 외의 어떤 다른 실시예들과 결합될 수 있다. 특히 바람직하거나 유리하다고 지시하는 어떤 특징도 바람직하거나 유리하다고 지시한 그 외의 어떤 특징 및 특징들과 결합될 수 있다. 이하, 첨부된 도면을 참조하여 본 발명의 실시예 및 이에 따른 효과를 설명하기로 한다.
본 발명의 일실시예에 따른 타일형 바닥장식재는 바닥재부(10) 및 미세 엠보스 플라스틱 폼부(20)를 포함한다. 도 1에 본 발명의 일실시예에 따른 타일형 바닥장식재의 구체적인 구성을 나타내었다.
상기 바닥재부(10)는 표면처리층(101), 투명층(102), 디자인 인쇄층(103), 중지층(104), 치수 보강층(105), 하지층(106), 밸런스층(107) 등을 포함한다. 상기 바닥재부(10)는 표면처리층(101), 투명층(102), 디자인 인쇄층(103) 및 하지층(106)을 포함하고, 중지층(104), 치수 보강층(105) 및 밸런스층(107)을 적절하게 추가하여 포함할 수 있다.
예를 들어, 상기 바닥재부(10)는 표면처리층(101), 투명층(102), 디자인 인쇄층(103), 중지층(104), 하지층(106), 밸런스층(107)으로 적층하여 구성하거나 표면처리층(101), 투명층(102), 디자인 인쇄층(103), 하지층(106), 밸런스층(107)으로 적층하여 구성하거나, 표면처리층(101), 투명층(102), 디자인 인쇄층(103), 하지층(106)으로 적층하여 구성하거나, 표면처리층(101), 투명층(102), 디자인 인쇄층(103), 중지층(104), 치수 보강층(105), 하지층(106), 밸런스층(107)으로 적층하여 구성하거나, 표면처리층(101), 투명층(102), 디자인 인쇄층(103), 중지층(104), 치수 보강층(105), 하지층(106)으로 적층하여 구성할 수 있다.
본 발명에 따른 타일형 바닥장식재는 바닥재부를 형성한 후 바닥재부의 최하단에 플라스틱 발포폼층 및 미세 엠보스를 갖는 밀착필름층을 포함하는 미세 엠보스 플라스틱 폼부를 형성함으로써 제조된다. 예를 들어 바닥재부가 표면처리층, 투명층, 디자인 인쇄층 및 하지층을 포함하는 경우 하지층, 디자인 인쇄층, 투명층 및 표면처리층을 적층하여 바닥재부를 형성한 후 상기 하지층의 이면에 플라스틱 발포폼층을 형성하고 플라스틱 발포폼층의 이면에 밀착필름층을 형성함으로써 제조할 수 있다.
상기 표면처리층(101)은 내스크레치성, 내오염성, 내마모성, 내구성 등의 표면물성을 개선하기 위한 층으로서, 모노에스테르(Monoester) 20 내지 40중량%, 올리고머(Oligomer) 10 내지 20중량%, 폴리디아크릴레이트(Poly Diacrylate) 10 내지 20중량%, 실리콘(Silicon) 0.5 내지 5중량% 및 기타 첨가제를 포함하여 구성되며, 롤코터 또는 에어나이프 코터로 도장하여 자외선에 의하여 5 내지 20μm의 두께로 코팅하고 자외선으로 경화된 층인 것을 일 특징으로 한다.
상기 투명층(102)은 바닥재의 디자인 인쇄 무늬를 보호하고, 바닥재의 마모, 마찰, 오염, 변형 등의 내구성을 유지하는 층으로서, PVC 수지 100 중량부에 대하여 가소제 10 내지 50 중량부, 안정제 1 내지 5 중량부 및 기타 첨가제를 포함하여 카렌다 공정으로 가공하여 형성된 층으로서 그 두께가 0.1 내지 1mm 인 것을 일 특징으로 한다.
상기 디자인 인쇄층(103)은 백색 또는 유색시트 표면에 전사 인쇄, 그라비어 인쇄, 스크린 인쇄, 오프셋 인쇄, 로터리 인쇄 또는 플렉소 인쇄하여 디자인 무늬를 부여함으로써 형성된 층인 것을 일 특징으로 한다. 디자인 인쇄층은 PVC 수지 100 중량부에 대하여 가소제 1 내지 20 중량부, 안정제 1 내지 5중량부, 충진재 0 내지 20 중량부, 가공조제 1 내지 5 중량부, 안료 0.5 내지 5 중량부 및 기타 첨가제를 포함하여 카렌다 공정으로 가공하며 그 두께가 0.05 내지 0.2mm 로 가공한 시트를 가열 합판하여 적층한다.
상기 중지층(104)은 상기 디자인 인쇄층의 요철을 최소화하고 평활성을 유지하기 위하여 포함되며, PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 카렌다 공정으로 가공하여 형성된 층으로서 그 두께가 0.2 내지 2mm 인 것을 일 특징으로 한다.
상기 치수 보강층(105)은 바닥재부의 치수변화를 최소화하기 위하여 유리섬유 메트를 활용하여 구성된다. 더욱 구체적으로 E 글라스로 섬유화한 유리 장섬유를 적정의 단위 길이로 절단하여 백수에 분산하고 초조하여 시트화하고 그 위에 바인더를 처리하여 가열 건조한 유리장섬유 메트를 기재로 하여 PVC 페이스트 수지 100 중량부에 대하여 가소제 50 내지 90 중량부, 안정제 1 내지 5중량부, 충진재 10 내지 150 중량부, 점도조절제 2 내지 10 중량부 및 기타 첨가제를 포함하여 액상의 페이스트졸로 가공하고, 유리장섬유 메트를 페이스트 졸에 함침하여 가열 경화한 시트로서 그 두께가 0.3 내지 6mm, 바람직하게는 0.3 내지 1mm 인 것을 일 특징으로 한다.
상기 하지층(106)은 바닥재의 중량감과 두께에 기여하고 경도를 확보할 수 있는 층으로서, PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 600 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 카렌다 공정으로 가공한 층으로서 그 두께가 0.5 내지 5mm 인 것을 일 특징으로 한다.
이때의 하지층은 각 배합별로 중량감을 부여하기도 하며, 경도를 부드럽거나 딱딱하게 하기도 하며, 발포층을 추가 하여 쿠션성을 부여하는 등의 다양한 구성과 두께로 그 기능을 부여할 수 있다.
상기 밸런스층(107)은 바닥재의 휘어짐을 조정하고 안착성을 유지할 수 있도록 하는 층으로서, PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 카렌다 공정으로 가공한 층으로서 그 두께가 0.3 내지 3mm 인 것을 일 특징으로 한다.
상기 미세엠보스 플라스틱 폼부(20)는 플라스틱 발포폼층(201) 및 밀착필름층(202)을 포함한다. 플라스틱 발포폼층(201)의 최하부에 단위 면적을 넓게 할 수 있는 미세 요철 엠보스를 부여하므로 바닥면과 바닥재와의 부착성을 높여 미끄럼을 방지하는 것을 일 특징으로 한다.
상기 플라스틱 발포폼층(201)은 올레핀계 수지 100 중량부에 대하여 아조디카본아마이드 발포제 3 내지 10 중량부, 촉진제 0.2 내지 1.5 중량부, 발포안정제 0.1 내지 1 중량부 및 기타 첨가제를 포함하여 압출 가공하고, 전자선 가교 후 발포 또는 화학 발포를 하여 형성된 층이며, 그 두께가 0.3 내지 2mm 이고, 밀도가 20 내지 200kg/m3 인 것을 일 특징으로 한다.
더욱 구체적으로 상기 플라스틱 발포폼층(201)은 폴리프로필렌, 폴리에틸렌 등의 올레핀계 수지, 발포제, 촉진제, 발포안정제, 기타 첨가제를 포함하여 압출 T 다이로 발포용 모판을 가공하고, 200 내지 700kw의 전압으로 1 내지 5Mrad 선량의 전자선을 조사한 다음 200℃ 내지 250℃의 발포오븐을 거치면서 발포하거나, 전자선 조사를 하지 않고 화학 발포를 함으로써 구성되며, 여기에 밀착필름층(202)을 적층하면서 엠보스롤을 이용하여 미세 엠보스를 부여하므로 부착과 엠보스를 동시에 구현할 수 있다.
상기 밀착필름층(202)은 올레핀계 수지 100 중량부에 대하여 산화방지제 0.1 내지 1 중량부, 가공조제 0.1 내지 1 중량부 및 기타 첨가제를 포함하는 10 내지 200μm 의 올레핀계 필름 또는 PVC 수지 100 중량부에 대하여 가소제 30 내지 60 중량부, 안정제 1 내지 5 중량부 및 기타 첨가제를 포함하여 그 두께가 10 내지 200μm인 PVC 필름을 T다이로 압출 가공하면서 동시에 부착하거나, T다이로 가공한 필름을 권취하여 재 합지하는 형태로 상기 플라스틱 발포폼층에 부착된다.
이때 밀착필름층(202)에 점착성을 추가할 수 있는 니트릴부타디엔 고무(Nitrile-butadiene rubber, NBR)이나 에틸렌비닐아세테이트(Ethylene-vinyl acetate, EVA), 점착성이 우수한 아크릴계 수지 등을 첨가하여 그 기능을 극대화 할 수 있다.
이때의 엠보스는 원형의 금속롤에 미세 음양각을 부여한 것으로 금속롤의 표면온도는 80 내지 160℃ 온도를 유지하고 플라스틱 발포폼 위에 올레핀계 수지 필름 또는 PVC 필름과 압착하여 부착하고 그와 동시에 엠보스를 부여하게 된다.
또한 엠보스는 단위 면적을 극대화하기 위하여 도 2에 나타낸 것과 같이 플라스틱 발포폼 이면에 요철을 기계방향과 폭방향으로 교대 배열하므로 凹부와 凸부가 전 폭에서 반복적으로 교대배열이 가능하게 하였다.
상기 미세 엠보스의 요철은 도 2에 나타낸 것과 같이 깊이(a)를 갖는 요철이 일정 간격(b)으로 구비된다. 이 때 요철의 깊이(a)는 0.08 내지 0.8mm 범위 내이며, 간격(b)의 1/3보다 큰 것을 일 특징으로 한다. 즉, 본 발명에 따른 미세 엠보스는 하기 식 1을 만족한다.
[식 1] a > 1/3 * b
(이 때, 0.08mm ≤ a ≤ 0.8mm이고, 0.2 ≤ b ≤ 2mm 이다.)
상기 식을 만족한 경우에 미세엠보스 플라스틱 폼부(20)의 단위 면적을 극대화 하여 미끄럼성을 현저하게 개선할 수 있는 바닥 장식재용 플라스틱 폼을 개발 하는 것이 가능하게 되었다.
이때 깊이(a) 및 간격(b)이 상기 범위를 벗어나는 경우 요철을 구현하기 어렵거나 단위 면적이 작아 미끄럼 개선효과가 미흡한 것을 확인하였으며, 요철의 깊이(a)가 간격(b)의 1/3 이하일 때에도 엠보스(凹凸)의 심도가 낮아 단위 면적이 작아지므로 미끄럼 개선 효과가 떨어지는 것으로 확인되었다.
상기 미세 엠보스 플라스틱 폼부(20)와 바닥재부(10)는 공지의 접착방법으로 접착하게 되는데 바닥재부(10) 이면에 아크릴 또는 우레탄계 접착제를 그라비아 방식이나 슬롯다이 방식으로 도장하고 가열 건조한 다음 미세 엠보스 플라스틱 폼부(20)를 부착하거나, 바닥재부(10) 이면에 핫멜트 타입의 접착제를 T다이를 통하여 고온 용융하여 도장하고 경화되기 전에 미세 엠보스 플라스틱 폼부(20)를 부착하는 방식 또는 핫멜트 타입의 접착제를 그라비아 방식으로 바닥재부(10) 또는 미세 엠보스 플라스틱 폼부(20)에 코팅하고 가열 건조한 다음 서로를 합지하는 방식 등 다양한 어떤 방식으로 합지하여도 되며, 이때 미세 엠보스 요철이 없어지거나 변화 되지 않도록 하는 것이 중요하다.
본 발명에 따른 바닥장식재는 폴리염화비닐수지나 폴리에틸렌, 폴리프로필렌 등의 폴리올레핀계 수지을 이용하여 가공하는 타일 형태의 바닥재 최하부에 미세 엠보스를 구현한 플라스틱 폼부를 적층하므로 플라스틱 쿠션에 의한 보행감과 충격음 흡수효과가 우수하고, 이면의 미세 엠보스에 의한 미끄럼성을 개선하여 접착제를 사용하지 않는 루스레이 시공에도 바닥과 제품의 밀착도를 높여 미끄러짐이 없는 바닥재를 제공할 수 있다.
실시예
아래로부터 밸런스층, 하지층, 중지층 디자인 인쇄층, 투명층 및 표면처리층을 적층하여 바닥재부를 형성하고 밸런스층 이면에 플라스틱 발포폼층(두께는 1.0mm) 및 밀착필름층(두께는 10μm)을 포함하는 미세 엠보스 플라스틱 폼부를 적층하였다.
이 때 밀도가 100kg/m3 이며 두께가 1.0mm인 올레핀계 발포폼에 올레핀계 수지로 형성된 밀착필름층을 적층할 때 금속롤을 이용하여 다양한 깊이(a) 및 간격(b)의 미세 엠보스를 형성하였다. 밀착필름층에 형성된 엠보스 조건은 하기 표 1에 나타낸 것과 같다.
실험예
상기 제조된 바닥재에 대하여 미끄럼성을 테스트하였다. 시험방법은 바닥면과 도로 등의 미끄럼 시험의 표준이 되고 있는 BS-7976-2의 Pendulum을 이용한 시험방법으로 플라스틱 발포폼이 부착된 면을 표면으로 하여 Pendulum이 미끄러지는 정도를 비교할 수 있도록 하였고, 슬립에 의한 영향을 극대화하기 위하여 슬라이더와의 밀착부 거리를 6mm로 하여 Test 하였으며, 측정된 Pendulum Test Value 를 하기 표 1에 나타내었다.
a b ① ② ③ 마찰계수
실시예 1 0.60 1.00 ○ ○ ○ 45
실시예 2 0.50 1.00 ○ ○ ○ 40
실시예 3 0.40 0.50 ○ ○ ○ 46
실시예 4 0.25 0.50 ○ ○ ○ 42
실시예 5 0.15 0.30 ○ ○ ○ 56
실시예 6 0.10 0.30 ○ ○ ○ 50
비교예 1 0 0 × × × 27
비교예 2 0.50 2.00 ○ ○ × 29
비교예 3 0.30 1.00 ○ ○ × 36
비교예 4 0.10 0.50 ○ ○ × 35
비교예 5 0.05 0.30 × ○ × 31
비교예 6 0.05 0.10 × × ○ 33
① 0.08≤a≤0.8
② 0.2≤b≤2
③ a≥1/3b
전술한 각 실시예에서 예시된 특징, 구조, 효과 등은 실시예들이 속하는 분야의 통상의 지식을 가지는 자에 의하여 다른 실시예들에 대해서도 조합 또는 변형되어 실시 가능하다. 따라서 이러한 조합과 변형에 관계된 내용들은 본 발명의 범 위에 포함되는 것으로 해석되어야 할 것이다.

Claims (12)

  1. 표면처리층, 투명층, 디자인 인쇄층 및 하지층을 포함하는 바닥재부; 및
    플라스틱 발포폼층 및 미세 엠보스를 갖는 밀착필름층을 포함하는 미세 엠보스 플라스틱 폼부;를 포함하며,
    상기 밀착필름층은 깊이(a)를 갖는 요철이 일정 간격(b)으로 구비되는 미세 엠보스를 가지며,
    상기 미세 엠보스는 하기 식 1을 만족하는 것을 특징으로 하는 타일형 바닥 장식재.
    [식 1] a ≥ 1/3 * b
    (이 때, 0.08mm ≤ a ≤ 0.8mm이고, 0.2 ≤ b ≤ 2mm 이다.)
  2. 제1항에 있어서,
    상기 플라스틱 발포폼층은 올레핀계 수지 100 중량부에 대하여 아조디카본아마이드 발포제 3 내지 10 중량부, 촉진제 0.2 내지 1.5 중량부, 발포안정제 0.1 내지 1 중량부 및 기타 첨가제를 포함하여 압출 가공 후 발포되어 형성된 층인 것을 특징으로 하는 타일형 바닥 장식재.
  3. 삭제
  4. 제1항에 있어서,
    상기 밀착필름층은 올레핀계 수지 100 중량부에 대하여 산화방지제 0.1 내지 1 중량부, 가공조제 0.1 내지 1 중량부 및 기타 첨가제를 포함하며, 10 내지 200μm 의 두께를 갖는 올레핀계 필름인 것을 특징으로 하는 타일형 바닥장식재.
  5. 제1항에 있어서,
    상기 밀착필름층은 PVC 수지 100 중량부에 대하여 가소제 30 내지 60 중량부, 안정제 1 내지 5 중량부 및 기타 첨가제를 포함하며, 10 내지 200μm 의 두께를 갖는 PVC 필름인 것을 특징으로 하는 타일형 바닥장식재.
  6. 제1항에 있어서,
    상기 표면처리층은 모노에스테르(Monoester) 20 내지 40중량%, 올리고머(Oligomer) 10 내지 20중량%, 폴리디아크릴레이트(Poly Diacrylate) 10 내지 20중량%, 실리콘(Silicon) 0.5 내지 5중량% 및 기타 첨가제를 포함하여 자외선에 의하여 5 내지 20μm의 두께로 코팅하고 자외선으로 경화된 층인 것을 특징으로 하는 타일형 바닥장식재.
  7. 제1항에 있어서,
    상기 투명층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 50 중량부, 안정제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.1 내지 1mm 두께로 형성된 층인 것을 특징으로 하는 타일형 바닥장식재.
  8. 제1항에 있어서,
    상기 디자인 인쇄층은 PVC 수지 100 중량부에 대하여 가소제 1 내지 20 중량부, 안정제 1 내지 5 중량부, 충진재 0 내지 20 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.05 내지 0.2mm 두께로 형성된 층인 것을 특징으로 하는 타일형 바닥장식재.
  9. 제1항에 있어서,
    상기 하지층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 600 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.5 내지 5mm 두께로 형성된 층인 것을 특징으로 하는 타일형 바닥장식재.
  10. 제1항에 있어서,
    상기 바닥재부는 상기 디자인 인쇄층 및 상기 하지층 사이에 구비되는 중지층을 더 포함하며,
    상기 중지층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.2 내지 2mm 두께로 형성된 층인 것을 특징으로 하는 타일형 바닥장식재.
  11. 제1항에 있어서,
    상기 바닥재부는 중지층, 치수보강층 및 밸런스층으로 구성되는 군에서 선택되는 어느 1층 이상을 더 포함하며, 상기 중지층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.2 내지 2mm 두께로 형성된 층이고,
    상기 치수보강층은 PVC 페이스트 수지 100 중량부에 대하여 가소제 50 내지 90 중량부, 안정제 1 내지 5 중량부, 충진재 10 내지 150 중량부, 점도조절제 2 내지 10 중량부 및 기타 첨가제를 포함하는 액상의 페이스트졸에 유리섬유 메트를 함침하여 가열 경화한 층이며,
    상기 밸런스층은 PVC 수지 100 중량부에 대하여 가소제 10 내지 60 중량부, 안정제 1 내지 5 중량부, 충진재 50 내지 500 중량부, 가공조제 1 내지 5 중량부 및 기타 첨가제를 포함하여 0.3 내지 3mm 두께로 형성된 층인 것을 특징으로 하는 타일형 바닥장식재.
  12. 하지층, 디자인 인쇄층, 투명층 및 표면처리층을 적층하여 바닥재부를 형성하는 단계;
    상기 하지층의 이면에 플라스틱 발포폼층 조성물을 압출 가공하고 전자선 가교 후 발포하거나 화학 발포하여 플라스틱 발포폼층을 형성하는 단계; 및
    밀착필름층 조성물을 압출 가공함과 동시에 엠보스롤을 이용하여 미세 엠보스를 부여하면서 상기 플라스틱 발포폼층의 이면에 부착하여 밀착필름층을 형성하는 단계;를 포함하며,
    상기 밀착필름층을 형성하는 단계는 깊이(a)를 갖는 요철이 일정 간격(b)으로 구비되는 미세 엠보스가 하기 식 1을 만족하도록 부여하는 단계인 것을 특징으로 하는 타일형 바닥장식재의 제조방법.
    [식 1] a ≥ 1/3 * b
    (이 때, 0.08mm ≤ a ≤ 0.8mm이고, 0.2 ≤ b ≤ 2mm 이다.)
KR1020200015906A 2020-02-10 2020-02-10 논슬립 발포폼을 포함하는 타일형 바닥장식재 및 이의 제조방법 KR102348390B1 (ko)