KR102348135B1 - A rubber composite for rubbe gasket equiped in air intake manifold - Google Patents
A rubber composite for rubbe gasket equiped in air intake manifold Download PDFInfo
- Publication number
- KR102348135B1 KR102348135B1 KR1020200055401A KR20200055401A KR102348135B1 KR 102348135 B1 KR102348135 B1 KR 102348135B1 KR 1020200055401 A KR1020200055401 A KR 1020200055401A KR 20200055401 A KR20200055401 A KR 20200055401A KR 102348135 B1 KR102348135 B1 KR 102348135B1
- Authority
- KR
- South Korea
- Prior art keywords
- polymer
- peak
- parts
- weight
- logm
- Prior art date
Abstract
본 발명은, FKM(Fluorelastomer) 고무를 포함하는 폴리머를 구비하는 것으로서, 상기 폴리머는 하기 측정 조건으로 얻어진 FKM 환산 중량평균분자량을 기초로 얻어진 Slice log Mw에 대한 dwt/d(logM)의 그래프 상에서 적어도 2개의 피크(peak)를 갖고, 상기 Slice log Mw에 대한 dwt/d(logM)의 그래프에서 Slice log Mw가 3.0 이상 5.0미만의 영역에서 제1 피크를 갖고, Slice log Mw가 5.0 이상 6.0미만의 영역에서 제2 피크를 갖는, 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물을 제공한다.The present invention provides a polymer comprising FKM (Fluorelastomer) rubber, wherein the polymer is at least on the graph of dwt/d (logM) for Slice log Mw obtained based on the FKM converted weight average molecular weight obtained under the following measurement conditions. It has two peaks, has a first peak in a region where Slice log Mw is 3.0 or more and less than 5.0 in the graph of dwt/d (logM) for the Slice log Mw, and Slice log Mw is 5.0 or more and less than 6.0 Provided is a rubber composition for a rubber gasket mounted on an air intake manifold, having a second peak in the region.
Description
본 발명은, 고무 가스켓의 고무 조성물에 관한 것으로, 보다 바람직하게는 자동차의 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물에 관한 것이다.The present invention relates to a rubber composition for a rubber gasket, and more preferably to a rubber composition for a rubber gasket mounted on an air intake manifold of an automobile.
자동차의 에어 인테이크(air intake)에는 가스켓이 장착된다. 상기 가스켓은 비산되는 연료 및 공기를 씰링한다. A gasket is mounted on an air intake of an automobile. The gasket seals fuel and air from flying off.
최근에는 상기 가스켓을 고무 소재로 제작될 수 있다. 그런데 상기 가스켓은 보편적으로 생산되어오는 오링 재료에 비해 형상이 크고 복잡하다. 따라서 성형시 흐름성 부족으로 제품 형상이 완전하지 않는 고무 부족 현상이 발생하고, 뜯김 현상과 같인 부적합이 지속적으로 발생한다. Recently, the gasket may be made of a rubber material. However, the gasket has a larger and more complex shape than the commonly produced O-ring materials. Therefore, due to lack of flowability during molding, there is a shortage of rubber in which the product shape is not perfect, and nonconformities such as tearing occur continuously.
또한, 제품 성형시 금형 오염으로 인하여 표면 형상이 고르지 않은 믈드 플래쉬 부적합이 발생된다. In addition, mold contamination in which the surface shape is not uniform occurs due to mold contamination during product molding.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 성형시의 흐름성이향상되고, 몰드프레쉬 부적합이 발생하지 않음과 동시에 이형성이 우수한 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물을 제공하는 것을 목적으로 한다. The present invention is to solve the above problems, and it is to provide a rubber composition for a rubber gasket mounted on an air intake manifold with improved flowability during molding, no mold fresh non-conformity, and excellent releasability. The purpose.
따라서, 본 발명의 바람직한 실시예에 따른 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물은, FKM(Fluorelastomer) 고무를 포함하는 폴리머를 구비하는 것으로서, 상기 폴리머는 하기 측정 조건으로 얻어진 FKM 환산 중량평균분자량을 기초로 얻어진 Slice log Mw에 대한 dwt/d(logM)의 그래프 상에서 적어도 2개의 피크(peak)를 갖고, 상기 Slice log Mw에 대한 dwt/d(logM)의 그래프에서 Slice log Mw가 3.0 이상 5.0미만의 영역에서 제1 피크를 갖고, Slice log Mw가 5.0 이상 6.0미만의 영역에서 제2 피크를 갖는다.Therefore, the rubber composition for a rubber gasket mounted on an air intake manifold according to a preferred embodiment of the present invention includes a polymer including FKM (Fluorelastomer) rubber, and the polymer is an FKM-converted weight average obtained under the following measurement conditions. It has at least two peaks on the graph of dwt / d (logM) for the Slice log Mw obtained based on the molecular weight, and the Slice log Mw in the graph of dwt / d (logM) for the Slice log Mw is 3.0 or more It has a first peak in a region less than 5.0, and has a second peak in a region where slice log Mw is 5.0 or more and less than 6.0.
그 측정 조건은 다음과 같다.The measurement conditions are as follows.
상기 FKM 고무를 디메틸포름아미드(DMF)에 1mg/ml의 농도로 용해하고, 65℃에서 0.01M 브로민화 리튬(LiBr)의 디메틸포름아미드 용리제(eluent)의 조건에서 측정. The FKM rubber was dissolved in dimethylformamide (DMF) at a concentration of 1 mg/ml, and measured at 65° C. under the condition of 0.01 M lithium bromide (LiBr) dimethylformamide eluent.
이 경우, 상기 제1 피크의 dwt/d(logM) 값은 상기 제2 피크의 dwt/d(logM) 값보다 큰 것이 바람직하다.In this case, it is preferable that the dwt/d(logM) value of the first peak is greater than the dwt/d(logM) value of the second peak.
또한, 상기 제1 피크 및 제2 피크의 dwt/d(logM) 값은 0.6 내지 0.8일 수 있다. In addition, dwt/d (logM) values of the first peak and the second peak may be 0.6 to 0.8.
상기 제1 피크에서의 Slice log Mw은 3 내지 4이고, 상기 제2 피크에서의 Slice log Mw은 5 내지 6일 수 있다. The slice log Mw at the first peak may be 3 to 4, and the slice log Mw at the second peak may be 5 to 6.
한편, 상기 폴리머 100중량부 대비 20 내지 30 중량부를 가지는 황산바륨(BaSO4); 상기 폴리머 100중량부 대비 2 내지 4 중량부를 갖는 산화마그네슘(MgO); 상기 폴리머 100 중량부 대비 1 내지 3 중량부를 갖는 CaOH2; 및 상기 폴리머 100 중량부 대비 0.5 내지 2 중량부를 갖는 에스테르(ester) 화합물을 더 포함할 수 있다. On the other hand, barium sulfate (BaSO4) having 20 to 30 parts by weight based on 100 parts by weight of the polymer; Magnesium oxide (MgO) having 2 to 4 parts by weight based on 100 parts by weight of the polymer; CaOH2 having 1 to 3 parts by weight based on 100 parts by weight of the polymer; and an ester compound having 0.5 to 2 parts by weight based on 100 parts by weight of the polymer.
본 발명에 따르면, 고무 가스켓의 흐름성이 개선되고, 몰드플래쉬 부적합이 감소되는 동시에, 이형성이 향상된다. According to the present invention, the flowability of the rubber gasket is improved, mold flash misfit is reduced, and the releasability is improved.
도 1은 본 발명에 포함된 폴리머의 Slice log Mw에 대한 dwt/d(logM)의 그래프이다.1 is a graph of dwt/d(logM) for Slice log Mw of a polymer included in the present invention.
이하, 도면을 참조하여 본 발명인 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물을 상세하게 설명한다.Hereinafter, a rubber composition for a rubber gasket mounted on an air intake manifold according to the present invention will be described in detail with reference to the drawings.
본 발명의 바람직한 실시예에 따른 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물은 폴리머와, 충전제와, 가교(조)제와, 가공조제를 포함하여 이루어진다. The rubber composition for a rubber gasket mounted on an air intake manifold according to a preferred embodiment of the present invention comprises a polymer, a filler, a crosslinking (coagulant) agent, and a processing aid.
폴리머는 FKM(Fluorelastomer) 고무를 포함한다. 상기 FKM 폴리머는 내열성, 내유성, 및 내약품성이 우수하다. 또한 가스켓을 고무 재질로 이루어져서, 탄성 및 유연성이 우수하고 낮은 체결력으로 체결이 잘 된다는 장점이 있다. Polymers include Fluorelastomer (FKM) rubber. The FKM polymer has excellent heat resistance, oil resistance, and chemical resistance. In addition, since the gasket is made of a rubber material, it has excellent elasticity and flexibility, and has the advantage of good fastening with low fastening force.
그러나, 일반 FKM 고무의 경우 흐름성이 부족하여 제품형상이 완전하지 않게 된다. However, in the case of general FKM rubber, the flowability is insufficient and the product shape is not perfect.
본 발명에 따르면, 상기 폴리머가 하기 측정 조건으로 얻어진 FKM 환산 중량평균분자량을 기초로 얻어진 Slice log Mw에 대한 dwt/d(logM)의 그래프 상에서 적어도 2개의 피크(peak)를 갖도록 한다. 이 경우, 상기 Slice log Mw는 분자량의 로그값이 해당하고, dwt/d(logM)는 상기 분자량의 로그값에 대한 분자량의 평균 분포에 해당한다. 다시 말하면 Slice log Mw는 용출되는 고분자의 질량 농도를 의미하며, 용출시간과 비례한다. dwt/d(logM)는 상기 질량 농도가 증가함에 따른 분자량의 분포 분포도를 의미한다.According to the present invention, the polymer has at least two peaks on the graph of dwt/d (logM) for Slice log Mw obtained based on the FKM converted weight average molecular weight obtained under the following measurement conditions. In this case, the Slice log Mw corresponds to a log value of molecular weight, and dwt/d (logM) corresponds to an average distribution of molecular weights with respect to the log value of the molecular weight. In other words, the slice log Mw means the mass concentration of the eluted polymer and is proportional to the elution time. dwt/d(logM) means the distribution of molecular weight as the mass concentration increases.
이 경우, 상기 FKM 고무를 디메틸포름아미드(DMF)에 1mg/ml의 농도로 용해하고, 65℃에서 0.01M 브로민화 리튬(LiBr)를 첨가한 디메틸포름아미드 용리제(eluent)의 조건에서 측정에서 측정하였다.In this case, the FKM rubber was dissolved in dimethylformamide (DMF) at a concentration of 1 mg/ml, and 0.01M lithium bromide (LiBr) was added at 65° C. measured.
도 1에 도시된 바와 같이, 본 발명의 폴리머는 상기 Slice log Mw에 대한 dwt/d(logM)의 그래프에서 Slice log Mw가 3.0 이상 5.0미만의 영역에서 제1 피크(pe1)를 갖고, Slice log Mw가 5.0 이상 6.0미만의 영역에서 제2 피크(pe2)를 갖는다. 1, the polymer of the present invention has a first peak (pe1) in the region where Slice log Mw is 3.0 or more and less than 5.0 in the graph of dwt/d (logM) for the Slice log Mw, and the Slice log It has a second peak pe2 in a region where Mw is 5.0 or more and less than 6.0.
상기 폴리머는 분자량이 서로 다른 제1 FKM 분자량부와 제2 FKM 분자량부를 포함한다. 이 경우, 제1 FKM 분자량부는 가교에 참여하여서 컴파운드 점도를 향상시키고, 제품의 이형성을 향상시킨다.The polymer includes a first FKM molecular weight portion and a second FKM molecular weight portion having different molecular weights. In this case, the first FKM molecular weight part participates in crosslinking to improve the compound viscosity and improve the releasability of the product.
또한, 제2 분자량부는 가교에 참여하기보다는 프로세스 지원제(polymeric process aids)로서의 기능을 하여서 흐름성을 향성시킨다. In addition, the second molecular weight moiety improves flowability by functioning as polymeric process aids rather than participating in crosslinking.
이 경우, 상기 제1 피크(pe1)의 dwt/d(logM) 값은 상기 제2 피크(pe2)의 dwt/d(logM) 값보다 큰 것이 바람직하다. 제1 피크의 dwt/d(logM) 값과 제2 피크의 dwt/d(logM)값은 고무 가스켓의 흐름성 및 이형성을 결정짓는 큰 인자이다. 만약, 1 피크의 dwt/d(logM) 값보다 제2 피크의 dwt/d(logM)값이 크게 되면 이형성이 열화되오서 몰드 플래쉬 부적합의 발생율이 높아지게 된다.In this case, the dwt/d(logM) value of the first peak pe1 is preferably greater than the dwt/d(logM) value of the second peak pe2. The dwt/d(logM) value of the first peak and the dwt/d(logM) value of the second peak are large factors that determine the flowability and releasability of the rubber gasket. If the dwt/d(logM) value of the second peak is greater than the dwt/d(logM) value of the first peak, the mold releasability deteriorates and the occurrence rate of mold flash mismatch increases.
상기 제1 피크(pe1) 및 제2 피크(pe2)의 dwt/d(logM) 값은 0.6 내지 0.8일 수 있다. 이 경우, 상기 제1 피크에서의 Slice log Mw은 3 내지 5이고, 상기 제2 피크에서의 Slice log Mw은 5 내지 6일 수 있다. The dwt/d (logM) values of the first peak pe1 and the second peak pe2 may be 0.6 to 0.8. In this case, the slice log Mw at the first peak may be 3 to 5, and the slice log Mw at the second peak may be 5 to 6.
충진제는 폴리머의 접착성을 향상시키는 한편, 가공성 및 보강성을 높이기 위한 것이다. 이 경우, 상기 충진제는 상기 폴리머 100 중량부 대비 20 내지 30 중량부를 포함할 수 있다. The filler is intended to improve the adhesiveness of the polymer, while improving the processability and reinforcing properties. In this case, the filler may include 20 to 30 parts by weight based on 100 parts by weight of the polymer.
상기 충진제는 황산바륨(BaSO4)을 포함한다. The filler includes barium sulfate (BaSO4).
가공조제는 고무 조성물을 혼합하여 믹싱(Mixing)하는 과정에서 폴리머들이 다른 배합 재료들과 균일하게 섞일 수 있도록 도와주고, 고무 조성물의 점도를 조절하여 과도한 점착성이나, 점착성이 부족해지는 현상을 방지하는 역할을 한다. 이 뿐만 아니라, 가공조제는 낮은 온도에서도 믹싱 작업이 순조롭게 이루어질 수 있게 한다. 본 실시예에 따르면, 가공조제는 폴리머 100 중량부에 대하여 1 내지 2 중량부로 이루어진 것이 바람직하다. 상기 가공조제는 인산 에테르일 수 있다. 상기 인산 에테르를 첨가함으로써, 플라스틱과 고무 사이의 접착력을 보다 향상시킬 수 있게 된다. The processing aid helps the polymers to be uniformly mixed with other compounding materials in the process of mixing and mixing the rubber composition, and controls the viscosity of the rubber composition to prevent excessive or insufficient adhesion. do In addition to this, the processing aid allows the mixing operation to be performed smoothly even at a low temperature. According to this embodiment, the processing aid is preferably made of 1 to 2 parts by weight based on 100 parts by weight of the polymer. The processing aid may be phosphoric acid ether. By adding the phosphoric acid ether, it is possible to further improve the adhesion between the plastic and the rubber.
가교(조)제는 폴리머의 가교 속도를 증가시키는 한편, 측쇄(side chain) 반응을 방지하여 가교 밀도를 증가시키기 위한 것이다. 본 실시예에 따르면, 가교(조)제는 산화마그네슘(MgO) 및 CaOH2를 구비할 수 있다. The crosslinking (coagulant) agent is for increasing the crosslinking rate of the polymer, while preventing side chain reaction to increase the crosslinking density. According to the present embodiment, the crosslinking (coagulant) agent may include magnesium oxide (MgO) and CaOH2.
이 경우, 산화마그네슘은 상기 폴리머 100중량부 대비 2 내지 4 중량부를 가질 수 있고, CaOH2는 상기 폴리머 100 중량부 대비 1 내지 3 중량부를 가질 수 있다. In this case, magnesium oxide may have 2 to 4 parts by weight based on 100 parts by weight of the polymer, and CaOH2 may have 1 to 3 parts by weight based on 100 parts by weight of the polymer.
가공조제는 배합제의 분산을 개선하고, 믹싱시간을 단축하며, 컴파운드의 흐름성과 이형성을 개선하는 기능을 한다. 이 경우, 가공조제는 에스테르(ester) 화합물을 포함할 수 있고, 그 함량은 상기 폴리머 100 중량부에 대하여 0.5 내지 2 중량부를 가질 수 있다.The processing aid functions to improve the dispersion of the compounding agent, shorten the mixing time, and improve the flowability and releasability of the compound. In this case, the processing aid may include an ester compound, and the content thereof may be 0.5 to 2 parts by weight based on 100 parts by weight of the polymer.
이하에서는, 상기와 같은 본 발명의 실시예에 따른 고무 가스켓용 고무 조성물(이하 편의상 "실시예"라고 칭함.)을 종래의 고무 가스켓용 고무 조성물(이하, 편의상 "비교예"라고 칭함.)간의 성질을 각종 테스트하여 서로 비교함으로써, 상기 효과를 더욱 명확하게 설명한다.Hereinafter, the rubber composition for a rubber gasket according to an embodiment of the present invention as described above (hereinafter referred to as "Example" for convenience) is compared with a conventional rubber composition for a rubber gasket (hereinafter referred to as "Comparative Example" for convenience). By comparing the properties with each other in various tests, the effect is more clearly explained.
표 1은 상기 각종 테스트에 적용되는 실시예와 비교예의 구성성분을 비교하여 나타낸 표이다. 표 1에 따르면, 실시예의 폴리머(sFKM)는 Slice log Mw에 대한 dwt/d(logM)의 그래프에서 Slice log Mw가 약 3.8에서 0.75 값의 제1 피크를 갖고, Slice log Mw가 약 5.5에서 0.7의 제2 피크를 갖는다.Table 1 is a table showing the comparison of the components of Examples and Comparative Examples applied to the various tests. According to Table 1, the polymer (sFKM) of the Example has a first peak with a slice log Mw value of about 3.8 to 0.75 in a graph of dwt/d (logM) for Slice log Mw, and a Slice log Mw of about 5.5 to 0.7 has a second peak of
반면, 비교예는, Slice log Mw에 대한 dwt/d(logM)의 그래프에서 Slice log Mw의 3 내지 5 구간에서 0.8의 단일 피크 값을 가진다. On the other hand, the comparative example has a single peak value of 0.8 in the 3 to 5 sections of the slice log Mw in the graph of dwt/d (logM) for the slice log Mw.
2) Bimodal Polymer2: FKM, dwt/d(logM) : Slice log Mw 제1피크=0.75 : 3.8, 제2 피크 0.7:5.5
3) FEF : N550, OCI
4) Blanc Fixe: BaSO4, Solvay
5) MgO #150 : MgO, KYOWA Chemical
6) Rhenofit: CaOH2, RHEIN CHEMIE
7) Carnaua Wax: Ester화합물, 브라질 ponts inds.1) Unimodal Polymer: FKM, 3M
2) Bimodal Polymer 2 : FKM, dwt/d(logM): Slice log Mw 1st peak = 0.75 : 3.8, 2nd peak 0.7:5.5
3) FEF: N550, OCI
4) Blanc Fixe: BaSO4, Solvay
5) MgO #150: MgO, KYOWA Chemical
6) Rhenofit: CaOH2, RHEIN CHEMIE
7) Carnaua Wax: Ester compounds, Brazilian ponts inds.
표 2는 본 발명의 비교예와, 실시예에 따른 고무 조성물과 그 비교예들을 기계적 물성과, 부적합율(%)의 결과를 나타낸다.Table 2 shows the results of mechanical properties and non-conformity (%) of the comparative examples of the present invention, the rubber compositions according to the examples, and the comparative examples.
기계적 물성은 경도(Shore A), 100% 모듈러스, 인장강도(Kgf/cm2), 신율(%)을 측정하였다. For mechanical properties, hardness (Shore A), 100% modulus, tensile strength (Kgf/cm2), and elongation (%) were measured.
상기 경도는 shore A 경도계를 이용한 경도시험을 실시하였고, 100% 모듈러스와 인장강도와 신율은 KS M 6518에 준하여 실시하였다.The hardness was tested using a shore A hardness tester, and 100% modulus, tensile strength, and elongation were performed according to KS M 6518.
비교예와 실시예는 기계적 물성치는 크게 차이가 없음을 알 수 있다. It can be seen that there is no significant difference in mechanical properties between Comparative Examples and Examples.
반면, 부적합율은 비교예가 12.3%임에 반해 실시예는 4.6%으로서 현저하게 실시예가 우수함을 알 수 있다. 양산Lot로 평가 결과 실제 부적합율(%)은 기존 8% 수준에서 2% 로 감소되어 75% 개선되는 효과를 나타났다.On the other hand, the non-conformity rate is 4.6% in the comparative example, whereas 12.3% in the comparative example, indicating that the example is remarkably excellent. As a result of the mass-production lot evaluation, the actual nonconformity rate (%) was reduced from the existing 8% level to 2%, resulting in a 75% improvement.
이와 같이 본 발명에 따르면 종래에 비하여, 부적합율은 우수함과 동시에, 기계적 물성치는 종래와 적어도 동등하게 되었다. As described above, according to the present invention, compared to the prior art, the non-conformity ratio is excellent and the mechanical properties are at least equal to those of the prior art.
상술한 바와 같이, 본 발명의 바람직한 실시예를 참조하여 설명하였지만 해당 기술분야의 숙련된 당업자라면 하기의 청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. As described above, although described with reference to preferred embodiments of the present invention, those skilled in the art can variously modify and change the present invention without departing from the spirit and scope of the present invention as set forth in the claims below. You will understand that it can be done.
pe1 : 제1 피크
pe2 : 제2 피크pe1: first peak
pe2: second peak
Claims (5)
상기 폴리머는 하기 측정 조건으로 얻어진 FKM 환산 중량평균분자량을 기초로 얻어진 Slice log Mw(용출되는 고분자의 질량 농도)에 대한 dwt/d(logM)(상기 질량 농도가 증가함에 따른 분자량의 분포도)의 그래프 상에서 적어도 2개의 피크(peak)를 갖고,
상기 Slice log Mw에 대한 dwt/d(logM)의 그래프에서 Slice log Mw가 3.8에서 제1 피크를 갖고, Slice log Mw가 5.5에서 제2 피크를 갖고,
상기 제1 피크의 dwt/d(logM) 값은 상기 제2 피크의 dwt/d(logM) 값보다 크고,
상기 제1 피크 및 제2 피크의 dwt/d(logM) 값은 0.6 내지 0.8이며,
상기 폴리머 100중량부 대비 20 내지 30 중량부를 가지는 황산바륨(BaSO4);
상기 폴리머 100중량부 대비 2 내지 4 중량부를 갖는 산화마그네슘(MgO);
상기 폴리머 100 중량부 대비 1 내지 3 중량부를 갖는 CaOH2; 및
상기 폴리머 100 중량부 대비 0.5 내지 2 중량부를 갖는 에스테르(ester) 화합물을 포함하는 에어 인테이크 매니폴드에 장착되는 고무 가스켓용 고무 조성물.
[측정 조건]
상기 FKM 고무를 디메틸포름아미드(DMF)에 1mg/ml의 농도로 용해하고, 65℃에서 0.01M 브로민화 리튬(LiBr)를 첨가한 디메틸포름아미드 용리제(eluent)의 조건에서 측정. As comprising a polymer that is FKM (Fluoroelastomer) rubber,
The polymer is a graph of dwt/d(logM) (distribution of molecular weight as the mass concentration increases) for Slice log Mw (mass concentration of eluted polymer) obtained based on FKM-converted weight average molecular weight obtained under the following measurement conditions. having at least two peaks in the phase,
In the graph of dwt/d (logM) for the Slice log Mw, Slice log Mw has a first peak at 3.8, Slice log Mw has a second peak at 5.5,
The dwt / d (logM) value of the first peak is greater than the dwt / d (logM) value of the second peak,
The dwt / d (logM) value of the first peak and the second peak is 0.6 to 0.8,
Barium sulfate (BaSO4) having 20 to 30 parts by weight based on 100 parts by weight of the polymer;
Magnesium oxide (MgO) having 2 to 4 parts by weight based on 100 parts by weight of the polymer;
CaOH2 having 1 to 3 parts by weight based on 100 parts by weight of the polymer; and
A rubber composition for a rubber gasket mounted on an air intake manifold comprising an ester compound having 0.5 to 2 parts by weight based on 100 parts by weight of the polymer.
[Measuring conditions]
The FKM rubber was dissolved in dimethylformamide (DMF) at a concentration of 1 mg/ml, and measured under the conditions of a dimethylformamide eluent to which 0.01M lithium bromide (LiBr) was added at 65°C.