KR102323573B1 - Copper nanoparticles of uniform shape and size, and method for synthesis thereof - Google Patents

Copper nanoparticles of uniform shape and size, and method for synthesis thereof Download PDF

Info

Publication number
KR102323573B1
KR102323573B1 KR1020200068763A KR20200068763A KR102323573B1 KR 102323573 B1 KR102323573 B1 KR 102323573B1 KR 1020200068763 A KR1020200068763 A KR 1020200068763A KR 20200068763 A KR20200068763 A KR 20200068763A KR 102323573 B1 KR102323573 B1 KR 102323573B1
Authority
KR
South Korea
Prior art keywords
copper
copper nanoparticles
temperature
solution
nanoparticles
Prior art date
Application number
KR1020200068763A
Other languages
Korean (ko)
Inventor
백태종
이다원
우호영
Original Assignee
중앙대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 중앙대학교 산학협력단 filed Critical 중앙대학교 산학협력단
Priority to KR1020200068763A priority Critical patent/KR102323573B1/en
Application granted granted Critical
Publication of KR102323573B1 publication Critical patent/KR102323573B1/en

Abstract

The present invention relates to copper nanoparticles and a synthesis method thereof, the synthesis method including a first step of preparing a first solution containing a copper precursor, a stabilizer and a reducing agent, a second step of preparing a second solution by raising the temperature of the first solution to a first temperature and vacuum-treating the same, and a third step of adding a polar solvent to the second solution under an inert gas atmosphere and raising the temperature to a second temperature to cause reaction. The polar solvent is used to control the shape of copper nanoparticles. Accordingly, copper nanoparticles with improved uniformity in size and shape compared to copper nanoparticles synthesized in conventional synthesis methods can be provided.

Description

모양과 크기가 균일한 구리 나노입자 및 이의 합성 방법{COPPER NANOPARTICLES OF UNIFORM SHAPE AND SIZE, AND METHOD FOR SYNTHESIS THEREOF}Copper nanoparticles with uniform shape and size and method for synthesizing the same

본 발명은 극성용매를 이용하여 환원 경향성이 낮은 구리의 불균등화 반응을 통해 합성된 모양과 크기가 균일한 구리 나노입자 및 이의 합성 방법에 관한 것이다.The present invention relates to copper nanoparticles having a uniform shape and size synthesized through a disproportionation reaction of copper having a low reduction tendency using a polar solvent and a method for synthesizing the same.

구리 나노입자는 다른 전이 금속입자들에 비해 가격이 저렴하고, 뛰어난 전기 전도성과 같은 우수한 물리적, 화학적 특성을 갖고 있기 때문에 전자기기용 전극, 촉매, 바이오 센서와 같은 응용 분야에 많이 이용되고 있다. 특히, 촉매 분야에 이용되는 경우, 이산화탄소의 환원, 알콜 산화 반응 등 에너지 전환 반응용 전기화학 촉매로서 높은 반응성을 나타내는 것으로 알려져 있다. 촉매에서 대부분의 화학 반응은 촉매의 표면에서 일어나게 되는데, 나노입자는 부피 대비 표면적이 매우 크기 때문에 이러한 특성으로 인해 높은 촉매 활성을 나타낼 수 있는 것이다. 이와 같이, 나노입자의 표면 구조, 노출면에 따라 촉매 활성이 달라진다. 따라서 나노입자의 형상을 정밀하게 제어하는 합성 방법을 개발하는 것은 매우 중요하다. Copper nanoparticles are widely used in applications such as electrodes for electronic devices, catalysts, and biosensors because they are inexpensive compared to other transition metal particles and have excellent physical and chemical properties such as excellent electrical conductivity. In particular, when used in the catalytic field, it is known to exhibit high reactivity as an electrochemical catalyst for energy conversion reactions such as reduction of carbon dioxide and oxidation of alcohol. Most of the chemical reactions in the catalyst take place on the surface of the catalyst, and since nanoparticles have a very large surface area to volume ratio, they can exhibit high catalytic activity due to these properties. As such, the catalytic activity varies depending on the surface structure and exposed surface of the nanoparticles. Therefore, it is very important to develop a synthetic method that precisely controls the shape of nanoparticles.

현재 구리 나노입자를 합성하는 방법은 팔라듐(Pd) 등의 나노입자 시드를 이용한 환원법 (ACS Nano 2015, 9 (3), 3307-3313., Adv. Funct. Mater. 2016, 26 (8), 1208-1216. Chemistry of Materials 2018, 30, 6469-6477.)과 환원제를 이용한 직접 환원법 (J. Am. Chem. Soc. 2017, 139, 3027-3032., Angew. Chem. Int. Ed. 2011, 50 (10560-10564), 10560. Adv. Funct. Mater. 2005, 15 (8), 1277-1284.) 등이 알려져 있다. 그러나 구리의 경우 높은 환원 전이로 인하여 이온의 환원을 유도하기가 쉽지 않기 때문에 모양이나 크기가 불균일하거나 다양한 형상으로 합성하기 어려운 단점이 있다. Cu+ 이온이 Cu2+ 이온과 Cu0 금속으로 전이되는 불균등화 반응을 이용하여 상대적으로 저온의 분위기에서 높은 크기 균일성을 갖는 구리 나노입자를 합성하는 방법이 보고되고는 있으나, 아직까지 구리 나노입자의 높은 균일성을 유지하며 형태를 용이하게 제어할 수 있는 합성 방법에 대해서는 보고된 바 없다.Currently, a method for synthesizing copper nanoparticles is a reduction method using a nanoparticle seed such as palladium (Pd) (ACS Nano 2015, 9 (3), 3307-3313., Adv. Funct. Mater. 2016, 26 (8), 1208) -1216. Chemistry of Materials 2018, 30, 6469-6477.) and direct reduction using a reducing agent (J. Am. Chem. Soc. 2017, 139, 3027-3032., Angew. Chem. Int. Ed. 2011, 50 (10560-10564), 10560. Adv. Funct. Mater. 2005, 15 (8), 1277-1284.) and the like are known. However, in the case of copper, since it is not easy to induce reduction of ions due to high reduction transition, it has a disadvantage in that it is difficult to synthesize it in a non-uniform shape or size or in various shapes. A method for synthesizing copper nanoparticles with high size uniformity in a relatively low-temperature atmosphere using a disproportionation reaction in which Cu + ions are transferred to Cu 2+ ions and Cu 0 metal has been reported, but so far, copper nanoparticles There has been no report on a synthesis method that can easily control the shape while maintaining high uniformity of particles.

본 발명의 일 목적은 극성용매를 사용함으로써 구리 나노입자의 형태를 쉽게 제어할 수 있을 뿐만 아니라 크기 및 모양 균일성을 향상시킬 수 있는, 구리 나노입자의 합성 방법을 제공하는 것이다.One object of the present invention is to provide a method for synthesizing copper nanoparticles, which can easily control the shape of copper nanoparticles and improve size and shape uniformity by using a polar solvent.

본 발명의 다른 목적은 상기 구리 나노입자의 합성 방법을 통해 합성된 크기 및 모양이 균일한 구리 나노입자를 제공하는 것이다.Another object of the present invention is to provide copper nanoparticles having a uniform size and shape synthesized through the method for synthesizing copper nanoparticles.

본 발명의 일 목적을 위한 구리 나노입자의 합성 방법은 구리전구체, 안정제 및 환원제를 포함하는 제1 용액을 제조하는 제1 단계, 상기 제1 용액을 제1 온도로 승온시키고 진공처리하여 제2 용액을 제조하는 제2 단계 및 불활성화 기체 분위기 하에서 상기 제2 용액에 극성용매를 첨가하고 제2 온도로 승온시켜 반응시키는 제3 단계를 포함한다.The method for synthesizing copper nanoparticles for one purpose of the present invention comprises a first step of preparing a first solution containing a copper precursor, a stabilizer and a reducing agent, and a second solution by heating the first solution to a first temperature and vacuuming. and a third step of reacting by adding a polar solvent to the second solution under an inert gas atmosphere and raising the temperature to a second temperature.

일 실시예에 있어서, 상기 제1 및 제2 온도는 100 내지 300 ℃일 수 있다.In one embodiment, the first and second temperatures may be 100 to 300 ℃.

일 실시예에 있어서, 상기 구리전구체는 CuBr, CuBr2, CuCl, CuCl2, Cu(NO3)2, CuSO4 및 CuCo3 중에서 선택된 어느 하나일 수 있다.In an embodiment, the copper precursor may be any one selected from CuBr, CuBr 2 , CuCl, CuCl 2 , Cu(NO 3 ) 2 , CuSO 4 and CuCo 3 .

일 실시예에 있어서, 상기 안정제는 트리옥틸포스핀옥사이드(trioctylphoshineoxide, TOPO), 트리옥틸포스핀 (trioctylphosphine, TOP), 트리페닐포스핀(triphenylphosphine, TPP), 트리페닐포스핀옥사이드(triphenylphosphine oxide, TPPO), 트리옥틸포스핀 셀레나이드(trioctylphosphine selenide, TOP-Se), 다이페닐포스핀(diphenylphophine, DPP) 및 다이페닐포스핀옥사이드(diphenylphosphine oxide, DPPO) 중에서 선택된 어느 하나일 수 있다.In one embodiment, the stabilizer is trioctylphoshineoxide (TOPO), trioctylphosphine (TOP), triphenylphosphine (TPP), triphenylphosphine oxide (triphenylphosphine oxide, TPPO) ), trioctylphosphine selenide (TOP-Se), diphenylphosphine (DPP) and diphenylphosphine oxide (diphenylphosphine oxide, DPPO) may be any one selected from.

일 실시예에 있어서, 상기 환원제는 탄화수소계 아민으로서 구체적으로는 올레일아민(oleylamine), 옥틸아민(octylamine), 노닐아민 (nonylamine), 헵틸아민(heptylamine), 헥실아민(hexylamine), 펜틸아민(pentylamine), 도데실아민(dodecylamine), 옥타데실아민(octadecylamine), 헥사데실아민 (hexadecylamine), 세틸아민(cetylamine), 디옥틸아민(dioctylamine), 디데실아민(didecylamine), 디도데실아민(didodecylamine) 및 디세틸아민(dicetylamine)중에서 선택된 어느 하나일 수 있다.In one embodiment, the reducing agent is a hydrocarbon-based amine, specifically oleylamine, octylamine, nonylamine, heptylamine, hexylamine, pentylamine ( pentylamine, dodecylamine, octadecylamine, hexadecylamine, cetylamine, dioctylamine, didecylamine, didodecylamine And it may be any one selected from dicetylamine (dicetylamine).

일 실시예에 있어서, 상기 극성용매는 디메틸포름아마이드(Dimethylformamide, DMF), 디메틸아세트아마이드(Dimethylacetamide, DMAC) 및 디메틸설폭사이드(dimethylsulfoxide, DMSO) 중에서 선택된 어느 하나일 수 있다.In an embodiment, the polar solvent may be any one selected from dimethylformamide (DMF), dimethylacetamide (DMAC), and dimethylsulfoxide (DMSO).

일 실시예에 있어서, 상기 극성용매는 디메틸포름아마이드이고, 상기 제3 단계에서, 상기 디메틸포름아마이드가 구리전구체 중량 100 대비 300 내지 310의 중량부로 첨가되는 경우, 상기 구리 나노입자는 나노 스피어 형태로 합성될 수 있다.In one embodiment, the polar solvent is dimethylformamide, and in the third step, when the dimethylformamide is added in an amount of 300 to 310 parts by weight based on the copper precursor weight of 100, the copper nanoparticles are in the form of nanospheres. can be synthesized.

일 실시예에 있어서, 상기 극성용매는 디메틸포름아마이드이고, 상기 제3 단계에서, 상기 디메틸포름아마이드가 구리전구체 중량 100 대비 120 내지 130의 중량부로 첨가되는 경우, 상기 구리 나노입자는 나노 큐브 형태로 합성될 수 있다.In one embodiment, the polar solvent is dimethylformamide, and in the third step, when the dimethylformamide is added in an amount of 120 to 130 parts by weight based on the copper precursor weight of 100, the copper nanoparticles are in the form of nanocubes. can be synthesized.

일 실시예에 있어서, 상기 극성용매는 디메틸포름아마이드이고, 상기 제3 단계에서, 상기 디메틸포름아마이드가 구리전구체 중량 100 대비 380 내지 390의 중량부로 첨가되는 경우, 상기 구리 나노입자는 나노 팔면체 형태로 합성될 수 있다.In one embodiment, the polar solvent is dimethylformamide, and in the third step, when the dimethylformamide is added in an amount of 380 to 390 parts by weight based on the copper precursor weight of 100, the copper nanoparticles are in the form of nano-octahedrons. can be synthesized.

본 발명의 다른 목적을 위한 구리 나노입자는 상기 구리 나노입자의 합성 방법에 따라 제조된다.Copper nanoparticles for another purpose of the present invention are prepared according to the method for synthesizing copper nanoparticles.

일 실시예에서, 상기 구리 나노입자가 나노 스피어인 경우, 상기 나노 스피어의 크기는 54 내지 63 nm일 수 있다.In one embodiment, when the copper nanoparticles are nanospheres, the size of the nanospheres may be 54 to 63 nm.

일 실시예에서, 상기 구리 나노입자가 나노 큐브인 경우, 상기 나노 큐브의 크기는 50 내지 70 nm일 수 있다.In one embodiment, when the copper nanoparticles are nanocubes, the size of the nanocubes may be 50 to 70 nm.

일 실시예에서, 상기 구리 나노입자가 나노 팔면체인 경우, 상기 나노 팔면체의 크기는 40 내지 56 nm일 수 있다.In one embodiment, when the copper nanoparticles are nano-octahedron, the size of the nano-octahedron may be 40 to 56 nm.

본 발명에 따르면, 합성 시 극성용매를 이용함으로써 크기 및 모양 균일성이 향상된 구리 기반 나노입자를 제공할 수 있을 뿐만 아니라 극성용매의 양을 다양하게 조절함으로써 구리 기반 나노 입자의 모양을 구형, 정육면체형, 깎은 정팔면체 및 정팔면체형 등으로 다양한 형태로 용이하게 제어할 수 있다.According to the present invention, copper-based nanoparticles with improved size and shape uniformity can be provided by using a polar solvent during synthesis, and the shape of the copper-based nanoparticles can be changed to a spherical or cube-shaped shape by varying the amount of the polar solvent. , can be easily controlled in various shapes such as truncated octahedron and octahedron type.

도 1은 본 발명의 실시예 1에 따라 합성한 구리 나노 스피어를 설명하기 위한 도면이다. 도 1의 (a)는 FE-SEM 분석을 통해 얻은 저배율에서의 구리 나노 스피어 입자의 이미지이고, (b) 및 (c)는 TEM 분석을 통해 얻은 고배율에서의 구리 나노 스피어 입자의 이미지이고, (d)는 합성된 구리 나노 스피어 입자의 평균 크기 및 표준 편차를 나타내는 그래프이고, (d)는 합성된 구리 나노 스피어의 X선 회절(XRD) 그래프이다.
도 2는 본 발명의 실시예 2에 따라 합성한 구리 나노 큐브를 설명하기 위한 도면이다. 도 2의 (a)는 FE-SEM 분석을 통해 얻은 저배율에서의 구리 나노 큐브 입자의 이미지이고, (b) 및 (c)는 TEM 분석을 통해 얻은 고배율에서의 구리 나노 큐브 입자의 이미지이고, (d)는 합성된 구리 나노 큐브 입자의 평균 크기 및 표준 편차를 나타내는 그래프이고, (d)는 합성된 구리 나노 큐브 입자의 X선 회절(XRD) 그래프이다.
도 3은 본 발명의 실시예 3에 따라 합성한 구리 나노 팔면체를 설명하기 위한 도면이다. 도 3의 (a)는 FE-SEM 분석을 통해 얻은 저배율에서의 구리 나노 팔면체 입자의 이미지이고, (b) 및 (c)는 TEM 분석을 통해 얻은 고배율에서의 구리 나노 팔면체 입자의 이미지이고, (d)는 합성된 구리 나노 팔면체 입자의 평균 크기 및 표준 편차를 나타내는 그래프이고, (d)는 합성된 구리 나노 팔면체 입자의 X선 회절(XRD) 그래프이다.
도 4는 본 발명의 비교예 1에 따라 합성된 구리 나노입자를 설명하기 위한 도면이다. 도 4의 (a)는 FE-SEM 분석을 통해 얻은 구리 나노입자의 이미지이고, (b)는 TEM 분석을 통해 얻은 구리 나노입자의 이미지이다.1 is a view for explaining a copper nanosphere synthesized according to Example 1 of the present invention. 1 (a) is an image of copper nanosphere particles at low magnification obtained through FE-SEM analysis, (b) and (c) are images of copper nanosphere particles at high magnification obtained through TEM analysis, ( d) is a graph showing the average size and standard deviation of the synthesized copper nanosphere particles, (d) is an X-ray diffraction (XRD) graph of the synthesized copper nanosphere particles.
2 is a view for explaining a copper nanocube synthesized according to Example 2 of the present invention. 2(a) is an image of copper nanocube particles at low magnification obtained through FE-SEM analysis, (b) and (c) are images of copper nanocube particles at high magnification obtained through TEM analysis, ( d) is a graph showing the average size and standard deviation of the synthesized copper nanocube particles, (d) is an X-ray diffraction (XRD) graph of the synthesized copper nanocube particles.
3 is a view for explaining a copper nano-octahedron synthesized according to Example 3 of the present invention. 3 (a) is an image of copper nano-octahedral particles at low magnification obtained through FE-SEM analysis, (b) and (c) are images of copper nano-octahedral particles at high magnification obtained through TEM analysis, ( d) is a graph showing the average size and standard deviation of the synthesized copper nano-octahedral particles, (d) is an X-ray diffraction (XRD) graph of the synthesized copper nano-octahedral particles.
4 is a view for explaining the copper nanoparticles synthesized according to Comparative Example 1 of the present invention. 4 (a) is an image of copper nanoparticles obtained through FE-SEM analysis, (b) is an image of copper nanoparticles obtained through TEM analysis.

이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대해 상세히 설명한다. 본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 본문에 상세하게 설명하고자 한다. 그러나 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 각 도면을 설명하면서 유사한 참조부호를 유사한 구성요소에 대해 사용하였다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. Since the present invention can have various changes and can have various forms, specific embodiments are illustrated in the drawings and described in detail in the text. However, this is not intended to limit the present invention to the specific disclosed form, it should be understood to include all modifications, equivalents and substitutes included in the spirit and scope of the present invention. In describing each figure, like reference numerals have been used for like elements.

본 출원에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로서 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terms used in the present application are used only to describe specific embodiments and are not intended to limit the present invention. The singular expression includes the plural expression unless the context clearly dictates otherwise. In the present application, terms such as “comprise” or “have” are intended to designate that a feature, step, operation, component, part, or combination thereof described in the specification is present, and includes one or more other features or steps. , it should be understood that it does not preclude the possibility of the existence or addition of , operation, components, parts, or combinations thereof.

다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless defined otherwise, all terms used herein, including technical and scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries should be interpreted as having a meaning consistent with the meaning in the context of the related art, and should not be interpreted in an ideal or excessively formal meaning unless explicitly defined in the present application. does not

본 발명은 극성용매를 이용하여 형태를 제어할 수 있는 구리 나노입자 합성 방법과 상기 합성 방법을 통해 합성된 크기 및 모양이 균일한 구리 나노입자를 제공한다.The present invention provides a method for synthesizing copper nanoparticles capable of controlling the shape using a polar solvent, and copper nanoparticles having a uniform size and shape synthesized through the synthesis method.

먼저, 본 발명의 구리나노입자 합성 방법은 구리전구체, 안정제 및 환원제를 포함하는 제1 용액을 제조하는 제1 단계 및 상기 제1 용액을 제1 온도로 승온시키고 진공처리하여 제2 용액을 제조하는 제2 단계를 포함할 수 있다.First, the method for synthesizing copper nanoparticles of the present invention includes a first step of preparing a first solution containing a copper precursor, a stabilizer and a reducing agent, and heating the first solution to a first temperature and vacuum processing to prepare a second solution It may include a second step.

구리 전구체는 최종 반응 후에 구리가 될 수 있는 원료물질을 의미하는 것으로, 본 발명에서는 구리를 직접 가공하거나 반응시키지 않고 이들의 원료 물질인 구리 전구체를 사용하여 반응시킴으로써 구리 나노입자를 제조할 수 있다. 일례로, 구리 전구체는 브롬화구리, 염화구리, 질산구리, 황산구리, 탄산구리 등을 일 수 있다. 구체적으로, 구리 전구체는 CuBr, CuBr2, CuCl, CuCl2, Cu(NO3)2, CuSO4 및 CuCo3 중에서 선택된 어느 하나일 수 있다. 바람직하게는, 구리 전구체는 CuBr일 수 있다. 그러나 본 발명에서 구리 전구체는 반드시 이에 제한되는 것은 아니며, 반응 후 구리가 될 수 있는 물질이라면 어느 물질이나 제한 없이 사용될 수 있다.The copper precursor refers to a raw material that can become copper after the final reaction, and in the present invention, copper nanoparticles can be prepared by reacting using a copper precursor, which is a raw material thereof, without directly processing or reacting copper. For example, the copper precursor may be copper bromide, copper chloride, copper nitrate, copper sulfate, copper carbonate, or the like. Specifically, the copper precursor may be any one selected from CuBr, CuBr 2 , CuCl, CuCl 2 , Cu(NO 3 ) 2 , CuSO 4 and CuCo 3 . Preferably, the copper precursor may be CuBr. However, in the present invention, the copper precursor is not necessarily limited thereto, and any material that can be copper after the reaction may be used without limitation.

안정제는 입자의 합성에서 높은 표면 에너지를 갖는 나노입자의 표면을 안정화시켜 응집을 제어하며 불균등화 반응에서 결정 성장 속도를 제어하는 역할을 하는 것으로, 본 발명에서 안정제는 불균등화 반응을 유도할 수 있다. 일례로, 안정제는 트리옥틸포스핀옥사이드(trioctylphoshineoxide, TOPO), 트리옥틸포스핀 (trioctylphosphine, TOP), 트리페닐포스핀(triphenylphosphine, TPP), 트리페닐포스핀옥사이드(triphenylphosphine oxide, TPPO), 트리옥틸포스핀 셀레나이드(trioctylphosphine selenide, TOP-Se), 다이페닐포스핀(diphenylphophine, DPP) 및 다이페닐포스핀옥사이드(diphenylphosphine oxide, DPPO) 중에서 선택된 어느 하나를 사용할 수 있다. 바람직하게는, 안정제는 트리옥틸포스핀옥사이드(trioctylphoshine oxide, TOPO)일 수 있다.The stabilizer serves to stabilize the surface of nanoparticles having high surface energy in the synthesis of particles to control aggregation and to control the crystal growth rate in the disproportionation reaction, and in the present invention, the stabilizer can induce disproportionation. . For example, the stabilizer is trioctylphoshineoxide (TOPO), trioctylphosphine (TOP), triphenylphosphine (TPP), triphenylphosphine oxide (TPPO), trioctyl Any one selected from phosphine selenide (trioctylphosphine selenide, TOP-Se), diphenylphophine (DPP), and diphenylphosphine oxide (DPPO) may be used. Preferably, the stabilizer may be trioctylphoshine oxide (TOPO).

환원제는 구리 이온의 환원을 용이하게 하기 위해 첨가되는 물질을 의미하며, 환원제를 사용하여 합성 반응을 수행하는 경우 구리 전구체를 환원시켜 구리 나노입자를 제조할 수 있다. 일례로, 환원제는 탄화수소계 아민으로서 구체적으로는 올레일아민(oleylamine), 옥틸아민(octylamine), 노닐아민 (nonylamine), 헵틸아민(heptylamine), 헥실아민(hexylamine), 펜틸아민(pentylamine), 도데실아민(dodecylamine), 옥타데실아민(octadecylamine), 헥사데실아민 (hexadecylamine), 세틸아민(cetylamine), 디옥틸아민(dioctylamine), 디데실아민(didecylamine), 디도데실아민(didodecylamine) 및 디세틸아민(dicetylamine) 중에서 선택된 어느 하나일 수 있다. 바람직하게는, 환원제는 올레일아민(oleylamine)일 수 있다.The reducing agent refers to a material added to facilitate the reduction of copper ions, and when the synthesis reaction is performed using the reducing agent, copper nanoparticles may be prepared by reducing the copper precursor. For example, the reducing agent is a hydrocarbon-based amine, specifically oleylamine, octylamine, nonylamine, heptylamine, hexylamine, pentylamine, dode Dodecylamine, octadecylamine, hexadecylamine, cetylamine, dioctylamine, didecylamine, didodecylamine and dicetylamine (dicetylamine) may be any one selected from. Preferably, the reducing agent may be oleylamine.

상기 제1 용액을 제1 온도로 승온시키고 진공처리하여 제2 용액을 제조하는 단계는 상기 제1 용액 내에서 합성 반응에 영향을 줄 수 있는 불순물 및 수분 등을 제거하기 위해 수행될 수 있다. 이 때, 제1 온도는 약 100 내지 300 ℃일 수 있고, 바람직하게는 제1 온도는 100 내지 130 ℃일 수 있다. 그러나 제1 용액의 불순물 및 수분을 제거할 수 있는 온도라면 특별히 제한되지는 않는다. 일 실시예에서, 구리 전구체로 CuBr, 안정제로 TOPO, 환원제로 올레일아민을 이용하여 제조하는 경우, 제2 단계에서 제1 온도는 약 125 ℃일 수 있다.The step of preparing the second solution by heating the first solution to a first temperature and vacuuming may be performed to remove impurities and moisture that may affect the synthesis reaction in the first solution. At this time, the first temperature may be about 100 to 300 ℃, preferably, the first temperature may be 100 to 130 ℃. However, it is not particularly limited as long as it is a temperature at which impurities and moisture of the first solution can be removed. In one embodiment, when preparing using CuBr as a copper precursor, TOPO as a stabilizer, and oleylamine as a reducing agent, the first temperature in the second step may be about 125 °C.

그런 다음, 불활성화 기체 분위기 하에서 상기 제2 용액에 극성용매를 첨가하고 제2 온도로 승온시켜 반응시키는 제3 단계를 포함할 수 있다. 본 발명에서 극성용매를 사용함으로써 구리 나노입자의 크기 및 모양 균일도를 향상시킬 수 있다. 또한, 극성용매의 양을 다양하게 조절하여 구리 나노입자의 모양을 구형, 정육면체형, 정팔면체형 등 다양한 형태로 합성할 수 있다. 이러한 효과를 극대화시키기 위해 본 발명에서 극성용매는 높은 끓는점을 갖는 물질일 수 있다. 예를 들어, 극성용매는 디메틸포름아마이드(Dimethylformamide,DMF), 디메틸아세트아미드 (Dimethylacetamide, DMA) 및 디메틸설폭사이드 (Dimehyl sulfoxide, DMSO) 중에서 선택된 어느 하나 일 수 있고, 바람직하게는. 극성용매는 디메틸포름아마이드(DMF)일 수 있다. 디메틸포름아마이드는 대표적인 극성 유기용매 중 하나로, 끓는점은 약 153℃이다.Then, a third step of reacting by adding a polar solvent to the second solution under an inert gas atmosphere and raising the temperature to a second temperature may be included. The size and shape uniformity of copper nanoparticles can be improved by using the polar solvent in the present invention. In addition, by variously controlling the amount of the polar solvent, the shape of the copper nanoparticles can be synthesized in various forms, such as a spherical shape, a cube shape, and an octahedron shape. In order to maximize this effect, the polar solvent in the present invention may be a material having a high boiling point. For example, the polar solvent may be any one selected from dimethylformamide (Dimethylformamide, DMF), dimethylacetamide (DMA) and dimethyl sulfoxide (Dimehyl sulfoxide, DMSO), preferably. The polar solvent may be dimethylformamide (DMF). Dimethylformamide is one of the representative polar organic solvents, and has a boiling point of about 153°C.

이 때, 제2 용매에 첨가되는 극성용매의 양에 따라 구리 나노입자의 형태를 용이하게 제어할 수 있다. 구체적으로는, 극성용매와 구리전구체 중량비에 따라 구리 나노입자의 형태를 용이하게 제어할 수 있다.In this case, the shape of the copper nanoparticles can be easily controlled according to the amount of the polar solvent added to the second solvent. Specifically, the shape of the copper nanoparticles can be easily controlled according to the weight ratio of the polar solvent and the copper precursor.

일 실시예에서, 극성용매로 디메틸포름아마이드(DMF)를 사용하고, 상기 디메틸포름아마이드가 구리전구체 중량 100 대비 300 내지 310의 중량부로 첨가되는 경우, 상기 구리 나노입자는 나노 스피어 형태로 합성될 수 있다. 이 때, 나노 스피어의 크기는 약 54 내지 63 nm일 수 있고, 바람직하게는, 나노 스피어의 크기는 약 55 내지 60 nm일 수 있다.In one embodiment, when dimethylformamide (DMF) is used as a polar solvent and the dimethylformamide is added in an amount of 300 to 310 parts by weight based on 100 weight of the copper precursor, the copper nanoparticles can be synthesized in the form of nanospheres. have. At this time, the size of the nanosphere may be about 54 to 63 nm, preferably, the size of the nanosphere may be about 55 to 60 nm.

다른 실시예에서, 극성용매로 디메틸포름아마이드(DMF)를 사용하고, 상기 디메틸포름아마이드가 구리전구체 중량 100 대비 120 내지 130의 중량부로 첨가되는 경우, 상기 구리 나노입자는 나노 큐브 형태로 합성될 수 있다. 이 때, 나노 큐브의 크기는 약 50 내지 70 nm일 수 있고, 바람직하게는, 나노 큐브의 크기는 약 55 nm 내지 65 nm 일 수 있다.In another embodiment, when dimethylformamide (DMF) is used as the polar solvent and the dimethylformamide is added in an amount of 120 to 130 parts by weight based on the copper precursor weight 100, the copper nanoparticles can be synthesized in the form of nanocubes. have. At this time, the size of the nanocubes may be about 50 to 70 nm, preferably, the size of the nanocubes may be about 55 nm to 65 nm.

또 다른 실시예에서, 극성용매로 디메틸포름아마이드(DMF)를 사용하고, 상기 디메틸포름아마이드가 구리전구체 중량 100 대비 380 내지 390의 중량부로 첨가되는 경우, 상기 구리 나노입자는 나노 팔면체 형태로 합성될 수 있다. 이 때, 나노 팔면체의 크기는 약 40 내지 56 nm일 수 있고, 바람직하게는, 나노 팔면체의 크기는 약 44 nm 내지 65 nm 일 수 있다.In another embodiment, when dimethylformamide (DMF) is used as a polar solvent and the dimethylformamide is added in an amount of 380 to 390 parts by weight based on 100 weight of the copper precursor, the copper nanoparticles are synthesized in the form of nano-octahedrons. can At this time, the size of the nano-octahedron may be about 40 to 56 nm, preferably, the size of the nano-octahedron may be about 44 nm to 65 nm.

불활성화 기체는 다른 원소와 반응을 하지 않는 안정한 기체로, 예를 들어, 헬륨, 질소, 아르곤 및 제논 등과 같은 기체를 의미한다. 본 발명에서는 불활성화 기체 종류를 특별히 한정하지는 않으나, 바람직하게는 본 발명에서 불활성화 기체는 질소일 수 있다.The inert gas is a stable gas that does not react with other elements, and means, for example, gases such as helium, nitrogen, argon, and xenon. In the present invention, the type of inert gas is not particularly limited, but preferably, the inert gas in the present invention may be nitrogen.

제2 온도는 극성용매의 끓는점보다 높은 온도일 수 있다. 일 실시예에서, 상기 제2 온도는 약 100 내지 300 ℃일 수 있고, 바람직하게는 제2 온도는 270 내지 280 ℃일 수 있다. 그러나 반드시 이에 제한되지는 않는다. 일례로, 본 발명에서 제2 온도는 제1 온도보다 높은 온도일 수 있다. 구체적으로, 본 발명의 일 실시예에서, 구리 전구체로 CuBr, 안정제로 TOPO, 환원제로 올레일아민, 극성용매로 디메틸포름아마이드를 사용하는 경우, 제1 온도는 약 125 ℃일 수 있고, 제2 온도는 약 270 ℃일 수 있다.The second temperature may be a temperature higher than the boiling point of the polar solvent. In one embodiment, the second temperature may be about 100 to 300 ℃, preferably, the second temperature may be 270 to 280 ℃. However, it is not necessarily limited thereto. For example, in the present invention, the second temperature may be a temperature higher than the first temperature. Specifically, in one embodiment of the present invention, when CuBr as a copper precursor, TOPO as a stabilizer, oleylamine as a reducing agent, and dimethylformamide as a polar solvent are used, the first temperature may be about 125 °C, and the second The temperature may be about 270 °C.

본 발명의 구리 나노입자 합성 방법으로 합성된 구리 나노입자는 종래의 합성 방법에 따라 합성된 구리 나노입자보다 모양과 크기가 균일하게 합성될 수 있다. Copper nanoparticles synthesized by the method for synthesizing copper nanoparticles of the present invention can be synthesized in a more uniform shape and size than copper nanoparticles synthesized according to a conventional synthesis method.

본 발명에 따르면, 구리 나노입자의 형태를 용이하게 조절할 수 있고, 크기 및 모양이 균일한 구리 나노입자를 합성할 수 있다. 합성된 구리 나노입자는 촉매 분야, 전자기기 분야, 광학 분야 및 의학 분야 등에서 응용될 수 있다. 특히, 촉매 분야는 나노입자의 형태 및 크기 의존성이 높기 때문에, 본 발명의 합성 방법으로 합성된 크기 및 모양이 균일한 구리 나노입자를 촉매 분야에 응용하는 경우, 촉매의 효율성을 향상시킬 수 있다. 촉매 사용 환경에 따라 사용되는 구리 나노입자의 형태를 용이하게 제어할 수 있다.According to the present invention, the shape of copper nanoparticles can be easily controlled, and copper nanoparticles having a uniform size and shape can be synthesized. The synthesized copper nanoparticles can be applied in the catalytic field, the electronic device field, the optical field, and the medical field. In particular, in the catalyst field, since the shape and size dependence of nanoparticles is high, when copper nanoparticles having a uniform size and shape synthesized by the synthesis method of the present invention are applied to the catalyst field, the efficiency of the catalyst can be improved. The shape of the copper nanoparticles used can be easily controlled according to the environment in which the catalyst is used.

실시예 1: 구리 나노 스피어의 합성Example 1: Synthesis of copper nanospheres

250ml 3구 플라스크에 0.7746 g의 CuBr와 11.595 g의 TOPO, 및 73.17 g의 올레일아민을 넣어 제1 용액을 제조한 후, 상기 제1 용액을 125 ℃까지 승온한 뒤, 3 시간 동안 진공 처리를 하여 용액 내에서 합성 반응에 영향을 줄 수 있는 불순물 및 수분을 제거한 제2 용액을 제조하였다. 질소 분위기 하에서, 상기 제2 용액에 극성용매인 디메틸포름아마이드(DMF) 2.36 g(CuBr 대비 1:3.05 비율)을 첨가한 후, 270℃까지 승온시킨 뒤 120분 동안 반응시킴으로써, 수 나노미터의 입자 크기를 가지는 구리 기반 나노 스피어를 합성하였다. 상기 반응 후 상온까지 식힌 후에 헥산(hexane)을 이용하여 원심분리를 통해 총 2회 정제하였고, 정제한 구리기반 나노 입자를 무수 톨루엔에 분산시켜 보관함으로써, 본 발명의 실시예 1에 따른 구리 나노 스피어를 얻었다.After preparing a first solution by putting 0.7746 g of CuBr, 11.595 g of TOPO, and 73.17 g of oleylamine in a 250ml three-necked flask, the temperature of the first solution was raised to 125° C., and vacuum treatment was performed for 3 hours. Thus, a second solution was prepared in which impurities and moisture that may affect the synthesis reaction were removed from the solution. In a nitrogen atmosphere, after adding 2.36 g of dimethylformamide (DMF) as a polar solvent (ratio of 1:3.05 to CuBr) to the second solution, the temperature was raised to 270° C. and reacted for 120 minutes, whereby particles of several nanometers Copper-based nanospheres having a size were synthesized. After the reaction was cooled to room temperature, it was purified twice by centrifugation using hexane, and the copper nanospheres according to Example 1 of the present invention were dispersed and stored in anhydrous toluene by dispersing the purified copper-based nanoparticles. got

도 1은 본 발명의 실시예 1에 따라 합성한 구리 나노 스피어를 설명하기 위한 도면이다.1 is a view for explaining a copper nanosphere synthesized according to Example 1 of the present invention.

도 1을 참조하면, (a), (b) 및 (c)에서 크기 및 모양이 균일한 구리 나노 스피어가 합성된 것을 확인할 수 있고, (d)를 통해 합성된 구리 나노 스피어의 평균 크기는 약 57.9 nm이고, 표준편차는 약 2.2 nm임을 알 수 있다. 또한, (e)를 통해 합성된 입자가 구리 입자인 것을 확인할 수 있다.Referring to FIG. 1 , it can be confirmed that copper nanospheres having a uniform size and shape were synthesized in (a), (b) and (c), and the average size of the copper nanospheres synthesized in (d) was about It can be seen that 57.9 nm, and the standard deviation is about 2.2 nm. In addition, it can be confirmed that the particles synthesized through (e) are copper particles.

실시예 2: 구리 나노 큐브의 합성Example 2: Synthesis of copper nanocubes

디메틸포름아마이드(DMF)를 0.944 g(CuBr 대비 1:1.22 비율) 첨가하는 것을 제외하고는, 본 발명의 실시예 1과 동일한 방법을 수행하여 구리 나노 큐브를 합성하였다.Copper nanocubes were synthesized in the same manner as in Example 1 of the present invention, except for adding 0.944 g of dimethylformamide (DMF) (ratio of 1:1.22 to CuBr).

도 2는 본 발명의 실시예 2에 따라 합성한 구리 나노 큐브를 설명하기 위한 도면이다.2 is a view for explaining a copper nanocube synthesized according to Example 2 of the present invention.

도 2를 참조하면, (a), (b) 및 (c)에서 크기 및 모양이 균일한 구리 나노 큐브가 합성된 것을 확인할 수 있고, (d)를 통해 합성된 구리 나노 큐브의 평균 크기는 약 60.2 nm이고, 표준편차는 약 4.5 nm임을 알 수 있다. 또한, (e)를 통해 합성된 입자가 구리 입자인 것을 확인할 수 있다.Referring to FIG. 2 , it can be confirmed that copper nanocubes having a uniform size and shape are synthesized in (a), (b) and (c), and the average size of the copper nanocubes synthesized in (d) is about It can be seen that 60.2 nm and the standard deviation is about 4.5 nm. In addition, it can be confirmed that the particles synthesized through (e) are copper particles.

실시예 3: 구리 나노 팔면체의 합성Example 3: Synthesis of copper nano octahedron

디메틸포름아마이드(DMF)를 2.982 g(CuBr 대비 1:3.85 비율) 첨가하는 것을 제외하고는, 본 발명의 실시예 1과 동일한 방법을 수행하여 구리 나노 팔면체를 합성하였다.A copper nano-octahedron was synthesized in the same manner as in Example 1 of the present invention, except for adding 2.982 g (ratio of 1:3.85 to CuBr) of dimethylformamide (DMF).

도 3은 본 발명의 실시예 3에 따라 합성한 구리 나노 팔면체를 설명하기 위한 도면이다.3 is a view for explaining a copper nano-octahedron synthesized according to Example 3 of the present invention.

도 3을 참조하면, (a), (b) 및 (c)에서 크기 및 모양이 균일한 구리 나노 팔면체가 합성된 것을 확인할 수 있고, (d)를 통해 합성된 구리 나노 팔면체의 평균 크기는 약 47.8 nm이고, 표준편차는 약 3.6 nm임을 알 수 있다. 또한, (e)를 통해 합성된 입자가 구리 입자인 것을 확인할 수 있다.Referring to FIG. 3 , it can be seen that copper nano-octahedrons with uniform size and shape are synthesized in (a), (b) and (c), and the average size of the copper nano-octahedron synthesized through (d) is about It can be seen that 47.8 nm, and the standard deviation is about 3.6 nm. In addition, it can be confirmed that the particles synthesized through (e) are copper particles.

비교예 1: 구리 나노입자의 합성Comparative Example 1: Synthesis of copper nanoparticles

극성용매인 디메틸포름아마이드(DMF)를 첨가하는 것을 제외하고는, 본 발명의 실시예 1과 동일한 방법을 수행하여 구리 나노 입자를 합성하였다.Copper nanoparticles were synthesized in the same manner as in Example 1 of the present invention, except that dimethylformamide (DMF), a polar solvent, was added.

도 4는 본 발명의 비교예 1에 따라 합성된 구리 나노입자를 설명하기 위한 도면이다.4 is a view for explaining the copper nanoparticles synthesized according to Comparative Example 1 of the present invention.

도 4를 참조하면, 도 1 내지 3과 비교해볼 때, (a) 및 (b)에서 크기와 모양이 균일하지 않은 구리 입자가 합성된 것을 확인할 수 있다.Referring to FIG. 4 , as compared with FIGS. 1 to 3 , it can be seen that copper particles having non-uniform sizes and shapes were synthesized in (a) and (b).

상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.Although the above has been described with reference to the preferred embodiments of the present invention, those skilled in the art can variously modify and change the present invention without departing from the spirit and scope of the present invention as set forth in the following claims. You will understand that you can.

Claims (13)

구리전구체, 안정제 및 환원제를 포함하는 제1 용액을 제조하는 제1 단계;
상기 제1 용액을 제1 온도로 승온시키고 진공처리하여 제2 용액을 제조하는 제2 단계; 및
불활성화 기체 분위기 하에서 상기 제2 용액에 극성용매를 첨가하고 제2 온도로 승온시켜 반응시키는 제3 단계;를 포함하며,
상기 극성용매는 디메틸포름아마이드이고,
상기 제3 단계에서 상기 디메틸포름아마이드의 첨가되는 양이 구리전구체 중량 100 대비 300 내지 310의 중량부인 경우에는 구리 나노입자는 나노 스피어 형태로 합성되는 것을 특징으로 하는,
구리 나노입자의 합성 방법.
A first step of preparing a first solution comprising a copper precursor, a stabilizer and a reducing agent;
a second step of heating the first solution to a first temperature and vacuuming to prepare a second solution; and
A third step of reacting by adding a polar solvent to the second solution under an inert gas atmosphere and raising the temperature to a second temperature;
The polar solvent is dimethylformamide,
When the amount of dimethylformamide added in the third step is 300 to 310 parts by weight based on the copper precursor weight of 100, the copper nanoparticles are synthesized in the form of nanospheres,
Method for synthesizing copper nanoparticles.
 구리전구체, 안정제 및 환원제를 포함하는 제1 용액을 제조하는 제1 단계;
상기 제1 용액을 제1 온도로 승온시키고 진공처리하여 제2 용액을 제조하는 제2 단계; 및
불활성화 기체 분위기 하에서 상기 제2 용액에 극성용매를 첨가하고 제2 온도로 승온시켜 반응시키는 제3 단계;를 포함하며,
상기 극성용매는 디메틸포름아마이드이고,
상기 제3 단계에서 상기 디메틸포름아마이드의 첨가되는 양이 구리전구체 중량 100 대비 120 내지 130의 중량부인 경우에는 구리 나노입자는 나노 큐브 형태로 합성되는 것을 특징으로 하는,
구리 나노입자의 합성 방법.
A first step of preparing a first solution comprising a copper precursor, a stabilizer and a reducing agent;
a second step of heating the first solution to a first temperature and vacuuming to prepare a second solution; and
A third step of reacting by adding a polar solvent to the second solution under an inert gas atmosphere and raising the temperature to a second temperature;
The polar solvent is dimethylformamide,
In the third step, when the amount of dimethylformamide added is 120 to 130 parts by weight based on the copper precursor weight of 100, the copper nanoparticles are synthesized in the form of nanocubes,
Method for synthesizing copper nanoparticles.
 구리전구체, 안정제 및 환원제를 포함하는 제1 용액을 제조하는 제1 단계;
상기 제1 용액을 제1 온도로 승온시키고 진공처리하여 제2 용액을 제조하는 제2 단계; 및
불활성화 기체 분위기 하에서 상기 제2 용액에 극성용매를 첨가하고 제2 온도로 승온시켜 반응시키는 제3 단계;를 포함하며,
상기 극성용매는 디메틸포름아마이드이고,
상기 제3 단계에서 상기 디메틸포름아마이드의 첨가되는 양이 구리전구체 중량 100 대비 380 내지 390의 중량부인 경우에는 구리 나노입자는 나노 팔면체 형태로 합성되는 것을 특징으로 하는,
구리 나노입자의 합성 방법.
A first step of preparing a first solution comprising a copper precursor, a stabilizer and a reducing agent;
a second step of heating the first solution to a first temperature and vacuuming to prepare a second solution; and
A third step of reacting by adding a polar solvent to the second solution under an inert gas atmosphere and raising the temperature to a second temperature;
The polar solvent is dimethylformamide,
When the amount of dimethylformamide to be added in the third step is 380 to 390 parts by weight based on 100 parts by weight of the copper precursor, the copper nanoparticles are synthesized in the form of nano-octahedrons,
Method for synthesizing copper nanoparticles.
 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 제1 및 제2 온도는 100 내지 300 ℃인 것을 특징으로 하는,
구리 나노입자의 합성 방법.
4. The method according to any one of claims 1 to 3,
The first and second temperatures are characterized in that 100 to 300 ℃,
Method for synthesizing copper nanoparticles.
 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 구리전구체는 CuBr, CuBr2, CuCl, CuCl2, Cu(NO3)2, CuSO4 및 CuCo3 중에서 선택된 어느 하나인,
구리 나노입자의 합성 방법.
4. The method according to any one of claims 1 to 3,
The copper precursor is any one selected from CuBr, CuBr 2 , CuCl, CuCl 2 , Cu(NO 3 ) 2 , CuSO 4 and CuCo 3 ,
Method for synthesizing copper nanoparticles.
 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 안정제는 트리옥틸포스핀옥사이드(trioctylphosphine oxide, TOPO), 트리옥틸포스핀 (trioctylphosphine, TOP), 트리페닐포스핀(triphenylphosphine, TPP), 트리페닐포스핀옥사이드(triphenylphosphine oxide, TPPO), 트리옥틸포스핀 셀레나이드(trioctylphosphine selenide, TOP-Se), 다이페닐포스핀(diphenylphosphine, DPP) 및 다이페닐포스핀옥사이드(diphenylphosphine oxide, DPPO) 중에서 선택된 어느 하나인 것인,
구리 나노입자의 합성 방법.
4. The method according to any one of claims 1 to 3,
The stabilizer is trioctylphosphine oxide (TOPO), trioctylphosphine (TOP), triphenylphosphine (TPP), triphenylphosphine oxide (TPPO), trioctylphosphine Pin selenide (trioctylphosphine selenide, TOP-Se), diphenylphosphine (diphenylphosphine, DPP) and diphenylphosphine oxide (diphenylphosphine oxide, DPPO) will be any one selected from,
Method for synthesizing copper nanoparticles.
 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 환원제는 올레일아민(oleylamine), 옥틸아민(octylamine), 노닐아민 (nonylamine), 헵틸아민(heptylamine), 헥실아민(hexylamine), 펜틸아민(pentylamine), 도데실아민(dodecylamine), 옥타데실아민(octadecylamine), 헥사데실아민 (hexadecylamine), 세틸아민(cetylamine), 디옥틸아민(dioctylamine), 디데실아민(didecylamine), 디도데실아민(didodecylamine) 및 디세틸아민(dicetylamine) 중에서 선택된 어느 하나인 것인,
구리 나노입자의 합성 방법.
4. The method according to any one of claims 1 to 3,
The reducing agent is oleylamine, octylamine, nonylamine, heptylamine, hexylamine, pentylamine, dodecylamine, octadecylamine (octadecylamine), hexadecylamine (hexadecylamine), cetylamine (cetylamine), dioctylamine (dioctylamine), didecylamine (didecylamine), didodecylamine (didodecylamine) and any one selected from dicetylamine (dicetylamine) sign,
Method for synthesizing copper nanoparticles.
 삭제delete 삭제delete 제1항 내지 제3항 중 어느 한 항에 따라 제조된,
구리 나노입자.
Prepared according to any one of claims 1 to 3,
copper nanoparticles.
 제10항에 있어서,
상기 구리 나노입자가 나노 스피어인 경우,
상기 나노 스피어의 크기는 54 내지 63 nm인 것을 특징으로 하는,
구리 나노입자.
11. The method of claim 10,
When the copper nanoparticles are nanospheres,
The size of the nanosphere is characterized in that 54 to 63 nm,
copper nanoparticles.
 제10항에 있어서,
상기 구리 나노입자가 나노 큐브인 경우,
상기 나노 큐브의 크기는 50 내지 70 nm인 것을 특징으로 하는,
구리 나노입자.
11. The method of claim 10,
When the copper nanoparticles are nanocubes,
The size of the nanocube is characterized in that 50 to 70 nm,
copper nanoparticles.
 제10항에 있어서,
상기 구리 나노입자가 나노 팔면체인 경우,
상기 나노 팔면체의 크기는 40 내지 56 nm인 것을 특징으로 하는,
구리 나노입자.11. The method of claim 10,
When the copper nanoparticles are nano-octahedrons,
The size of the nano-octahedron is characterized in that 40 to 56 nm,
copper nanoparticles.
KR1020200068763A 2020-06-08 2020-06-08 Copper nanoparticles of uniform shape and size, and method for synthesis thereof KR102323573B1 (en)