KR102307234B1 - Bone cement composition for periodontal tissue - Google Patents

Bone cement composition for periodontal tissue Download PDF

Info

Publication number
KR102307234B1
KR102307234B1 KR1020190082419A KR20190082419A KR102307234B1 KR 102307234 B1 KR102307234 B1 KR 102307234B1 KR 1020190082419 A KR1020190082419 A KR 1020190082419A KR 20190082419 A KR20190082419 A KR 20190082419A KR 102307234 B1 KR102307234 B1 KR 102307234B1
Authority
KR
South Korea
Prior art keywords
tooth
calcium
bone cement
cement composition
teeth
Prior art date
Application number
KR1020190082419A
Other languages
Korean (ko)
Other versions
KR20210006600A (en
Inventor
나태용
장명철
Original Assignee
나태용
장명철
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 나태용, 장명철 filed Critical 나태용
Priority to KR1020190082419A priority Critical patent/KR102307234B1/en
Publication of KR20210006600A publication Critical patent/KR20210006600A/en
Application granted granted Critical
Publication of KR102307234B1 publication Critical patent/KR102307234B1/en

Abstract

본 발명은 인산칼슘(calcium phosphate); 석고(calcium sulfate); 칼슘카보네이트(CaCO3); 실리콘다이옥사이드(SiO2); 알루미늄산화물; 및 칼슘 지르코니아 복합체;를 포함하는 치주용 골시멘트 조성물에 관한 것이다. 이에 의하여, 이식 치아의 고정이 수일 내 안정적으로 이루어질 수 있어 치아 이식에 따른 불편함을 최소화할 수 있고, 치아 이식의 성공률을 향상시킬 수 있다.The present invention is calcium phosphate (calcium phosphate); gypsum (calcium sulfate); calcium carbonate (CaCO 3 ); silicon dioxide (SiO 2 ); aluminum oxide; and calcium zirconia complex; to a periodontal bone cement composition comprising. Thereby, since the implanted teeth can be stably fixed within a few days, discomfort due to dental implantation can be minimized, and the success rate of dental implantation can be improved.

Description

치주용 골시멘트 조성물{Bone cement composition for periodontal tissue}Bone cement composition for periodontal tissue

본 발명은 치주용 골시멘트 조성물에 관한 것으로, 더욱 상세하게는 자기 치아 이식(autoimplantation, reimplantation)을 안정적으로 높은 성공율로 수행할 수 있는 치주용 골시멘트 조성물에 관한 것이다.The present invention relates to a periodontal bone cement composition, and more particularly, to a periodontal bone cement composition capable of stably performing autoimplantation and reimplantation with a high success rate.

자가치아이식은 상실된 치아를 대신하여 사랑니나 기타 매복치 등 이용이 가능하다고 판단되는 치아를 빠진 곳에 옮겨 치유를 얻어 기능을 하게 하는 방법이다. 여기에는 특히, 사랑니가 많이 활용이 되고 있고, 치아를 뽑아서 옮겨오므로 자가이식을 하는 치아는 생활력을 잃게 되어 신경치료를 하여야 하며 이식 후에는 이식치아를 주변에 교정용 철사나 레진 접착과 같은 방법으로 고정하여 6-8주정도 뼈에 완전히 붙을 때까지 고정을 유도하게 된다. 그리고 고정이 되어 안정적인 사용이 가능하게 되면 금관을 씌어 치아을 보호해 주어야 한다. 이와 같은 자가치아이식은 자신의 치아를 사용하게 되므로 관리가 잘 된다면 임플란트에 비해 여러모로 장점을 가질 수 있다.Autogenous tooth implantation is a method that replaces lost teeth by moving a tooth that can be used, such as a wisdom tooth or other impacted tooth, to a missing place to recover and function. In particular, wisdom teeth are used a lot here, and since the teeth are pulled and moved, the teeth that are autografted lose their vitality and need nerve treatment. Fixation is induced until it is completely attached to the bone for about 6-8 weeks. And when it is fixed and stable use is possible, a gold crown should be placed to protect the teeth. Since this type of autogenous dental implant uses one's own teeth, it can have many advantages compared to implants if well-maintained.

일반적으로 치아가 결손 되면 주위 치아를 삭제한 후 양쪽 지대치를 연결하여 계속가공의치(bridge)를 하는데 건강한 인접치를 손상시키는 문제가 발생할 수 있다. 그러나 치아이식을 하게 되면 건강한 인접치의 손상을 피할 수 있다. 인접치를 손상시키지 않고 결손치를 수복할 수 있는 방법으로 최근에 임플란트를 많이 이용하고 있지만 치료비가 비싸고 치료기간 또한 상대적으로 긴 문제점이 있다.In general, when a tooth is missing, a problem of damaging the healthy adjacent tooth may occur when the surrounding teeth are removed and then both abutments are connected to continue to make a bridge. However, with dental implants, damage to healthy adjacent teeth can be avoided. Recently, implants have been widely used as a method to restore missing teeth without damaging adjacent teeth, but they have problems in that the treatment cost is high and the treatment period is relatively long.

이에 비해, 자가치아이식은 임플란트에 비해 치료비가 저렴하며 치료기간도 짧고 치조골이 많이 파괴된 부위에 이식을 하여 치조골형성유도 효과도 기대할 수 있다. 이식된 치아가 고정된 후에는 자신의 치아와 같은 감각을 느낄 수 있다.On the other hand, autogenous dental implants have a lower treatment cost and shorter treatment period than implants. After the implanted teeth are fixed, they can feel the same sensation as their own teeth.

이와 같은 자가치아이식의 방법으로는 치아를 발치하고 염증의 원인이 되는 치아뿌리를 일부 잘라내고 상용화된 MTA(Mineral Trioxide Aggregate)로 뿌리 끝부분을 충전하여, 다시 재식립하는 수술로　인공치아를 이식하는 시술 없이 자신의 원래 치아를 회복할 수 있는 방법이 실시된 바 있다.In this self-dentition method, the tooth is extracted, part of the root of the tooth that is the cause of inflammation is cut, and the tip of the root is filled with commercially available MTA (Mineral Trioxide Aggregate), and then the artificial tooth is implanted again. A method that can restore one's original teeth without surgery has been practiced.

그러나, 본 발명자의 치과에서 종래 방법과 동일한 방법으로 환자들에게 MTA 임상시술을 했으나 성공율이 매우 낮았으며, 시술 후 MTA 골시멘트가 융해되어 버리는 문제가 발생하였고, 상용화된 골시멘트를 사용하는 경우에는 치아 이식 후 약 6개월간 이식 치아를 전혀 사용할 수 없어 식사시 불편을 초래할 뿐 아니라, 부주의에 의한 이식이 실패할 수 있는 문제점이 있었다. 이에 따라, 골시멘트가 융해되지 않고, 이식 치아가 빠른 시간 안에 안정적으로 고정되어 이식 성공률이 향상되고, 환자의 불편함을 최소화할 수 있는 치주용 골시멘트 물질의 개발이 필요한 실정이다.However, the present inventor's dentist performed MTA clinical treatment on patients in the same way as the conventional method, but the success rate was very low, and there was a problem that the MTA bone cement was melted after the procedure. Since the implanted teeth cannot be used at all for about 6 months after dental implantation, there is a problem that not only causes inconvenience while eating, but also implantation may fail due to carelessness. Accordingly, there is a need for the development of a bone cement material for periodontal use, which does not melt the bone cement, stably fixes the implanted teeth in a short time, improves the implantation success rate, and minimizes patient discomfort.

한국등록특허 제10-1868873호Korean Patent No. 10-1868873

본 발명의 목적은 자가치아이식에 사용되는 치주용 골시멘트로서 시술 후 융해되지 않고 모양을 유지하며, 이식 치아가 빠른 시간 안에 안정적으로 고정되어 시술 후 곧바로 부드러운 식사가 가능하고 단 2 내지 3일 후에 정상적인 식사를 가능하게 할 수 있는 치주용 골시멘트 조성물을 제공하는 데 있다. An object of the present invention is to maintain its shape without melting after the procedure as periodontal bone cement used for autogenous tooth implantation, and the implanted tooth is stably fixed within a short period of time so that a soft meal is possible immediately after the procedure, and after only 2 to 3 days An object of the present invention is to provide a periodontal bone cement composition that can enable a normal diet.

본 발명의 하나의 측면에 따르면, According to one aspect of the invention,

인산칼슘(calcium phosphate); 석고(calcium sulfate); 칼슘카보네이트(CaCO3); 실리콘다이옥사이드(SiO2); 알루미늄산화물; 및 칼슘 지르코니아 복합체;를 포함하는 치주용 골시멘트 조성물이 제공된다.calcium phosphate; gypsum (calcium sulfate); calcium carbonate (CaCO 3 ); silicon dioxide (SiO 2 ); aluminum oxide; And calcium zirconia complex; is provided for periodontal bone cement composition comprising a.

바람직하게는, 상기 치주용 골시멘트 조성물은.Preferably, the periodontal bone cement composition.

인산칼슘(calcium phosphate) 100중량부에 대하여, 석고(calcium sulfate) 30 내지 40중량부; 칼슘카보네이트(CaCO3) 9 내지 12중량부; 실리콘다이옥사이드(SiO2) 0.5 내지 2.5중량부; 알루미늄산화물 0.5 내지 1.5중량부; 및 칼슘 지르코니아 복합체 3 내지 4.5중량부;를 포함할 수 있다.30 to 40 parts by weight of gypsum based on 100 parts by weight of calcium phosphate; Calcium carbonate (CaCO 3 ) 9 to 12 parts by weight; Silicon dioxide (SiO 2 ) 0.5 to 2.5 parts by weight; 0.5 to 1.5 parts by weight of aluminum oxide; and 3 to 4.5 parts by weight of the calcium zirconia complex.

상기 치주용 골시멘트 조성물은, The periodontal bone cement composition,

과인산(perphosphoric acid); 및 증류수 또는 식염수;를 추가로 포함할 수 있다.perphosphoric acid; And distilled water or saline; may further include.

상기 인산칼슘은 산성 인산칼슘 또는 염기성 인산칼슘일 수 있다.The calcium phosphate may be acidic calcium phosphate or basic calcium phosphate.

상기 인산칼슘은 β-트리칼슘포스페이트(β-TCP), 디칼슘 포스페이트 디하이드레이트(CaHPO4 ··2H2O, DCPD), 테트라칼슘 디하이드로겐 포스페이트(Ca4H2P6O20, TCHP), 하이드록시아파타이트(HAp), 옥타칼슘 포스페이트(OCP), α-트리칼슘포스페이트(α-TCP) 및 테트라 칼슘 포스페이트(TTCP) 중에서 선택된 1종 이상일 수 있다.The calcium phosphate is β- tricalcium phosphate (β-TCP), dicalcium phosphate dihydrate (CaHPO 4 · · 2H 2 O , DCPD), tetra-calcium dihydrogen phosphate (Ca 4 H 2 P 6 O 20, TCHP) , hydroxyapatite (HAp), octacalcium phosphate (OCP), α- tricalcium phosphate (α-TCP), and may be at least one selected from tetra calcium phosphate (TTCP).

상기 인산칼슘은 β-트리칼슘포스페이트(β-TCP)일 수 있다.The calcium phosphate may be β-tricalcium phosphate (β-TCP).

상기 석고(calcium sulfate)는 반수 석고(calcium sulfate hemihydrate), 이수 석고(calcium sulfate dehydrate), 및 무수 석고(calcium sulfate anhydrate) 중에서 선택된 1종 이상일 수 있다.The gypsum may be at least one selected from calcium sulfate hemihydrate, calcium sulfate dehydrate, and calcium sulfate anhydrate.

상기 석고(calcium sulfate)는 반수 석고(calcium sulfate hemihydrate)일 수 있다.The gypsum (calcium sulfate) may be hemihydrate (calcium sulfate hemihydrate).

상기 치주용 골시멘트 조성물은 자연 치아 이식용 또는 치아 부식 치료용으로 사용될 수 있다.The periodontal bone cement composition may be used for natural tooth transplantation or tooth decay treatment.

본 발명의 치주용 골시멘트 조성물은 자가치아이식에 사용되는 치주용 골시멘트로서 시술 후 융해되지 않고 모양을 유지하며, 이식 치아가 빠른 시간 안에 안정적으로 고정되어 시술 후 곧바로 부드러운 식사가 가능하고 단 2 내지 3일 후에 정상적인 식사를 가능하게 할 수 있다.The periodontal bone cement composition of the present invention is a periodontal bone cement used for autogenous tooth implantation. It does not melt after the procedure and maintains its shape, and the implanted tooth is stably fixed within a short period of time so that a smooth meal is possible immediately after the procedure. Normal diet can be allowed after to 3 days.

도 1 내지 도 5는 환자 A의 치아 이식 치료 경과를 보여주는 X선 파노라마 사진이다.
도 6 내지 도 11은 환자 B의 치아 이식 치료의 경과를 보여주는 X선 파노라마 사진이다.
도 12 내지 도 15는 환자 C의 치아 이식 치료 경과를 나타낸 X선 파노라마 사진이다.1 to 5 are X-ray panoramic photographs showing the progress of patient A's dental implant treatment.
6 to 11 are X-ray panoramic photographs showing the progress of the dental implant treatment of patient B.
12 to 15 are X-ray panoramic photographs showing the progress of dental implant treatment of patient C. FIG.

본 발명은 다양한 변환을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.Since the present invention can apply various transformations and can have various embodiments, specific embodiments are illustrated in the drawings and described in detail. However, this is not intended to limit the present invention to specific embodiments, and it should be understood to include all modifications, equivalents and substitutes included in the spirit and scope of the present invention. In describing the present invention, if it is determined that a detailed description of a related known technology may obscure the gist of the present invention, the detailed description thereof will be omitted.

이하, 본 발명의 치주용 골시멘트 조성물에 대해 설명하도록 한다.Hereinafter, the periodontal bone cement composition of the present invention will be described.

본 발명의 치주용 골시멘트 조성물은 인산칼슘(calcium phosphate); 석고(calcium sulfate); 칼슘카보네이트(CaCO3); 실리콘다이옥사이드(SiO2); 알루미늄산화물; 및 칼슘 지르코니아 복합체;를 포함하는 것을 특징으로 한다.Periodontal bone cement composition of the present invention is calcium phosphate (calcium phosphate); gypsum (calcium sulfate); calcium carbonate (CaCO 3 ); silicon dioxide (SiO 2 ); aluminum oxide; and a calcium zirconia complex.

바람직하게는, 상기 치주용 골시멘트 조성물은 인산칼슘(calcium phosphate) 100중량부에 대하여, 석고(calcium sulfate) 30 내지 40중량부; 칼슘카보네이트(CaCO3) 9 내지 12중량부; 실리콘다이옥사이드(SiO2) 0.5 내지 2.5중량부; 알루미늄산화물 0.5 내지 1.5중량부; 및 칼슘 지르코니아 복합체 3 내지 4.5중량부;를 포함할 수 있다. Preferably, the periodontal bone cement composition comprises 30 to 40 parts by weight of gypsum based on 100 parts by weight of calcium phosphate; Calcium carbonate (CaCO 3 ) 9 to 12 parts by weight; Silicon dioxide (SiO 2 ) 0.5 to 2.5 parts by weight; 0.5 to 1.5 parts by weight of aluminum oxide; and 3 to 4.5 parts by weight of the calcium zirconia complex.

상기 치주용 골시멘트 조성물은 리퀴드 성분으로 과인산(perphosphoric acid); 및 증류수 또는 식염수;를 추가로 포함할 수 있다.The periodontal bone cement composition includes: perphosphoric acid as a liquid component; And distilled water or saline; may further include.

상기 인산칼슘은 산성 인산칼슘 또는 염기성 인산칼슘일 수 있다.The calcium phosphate may be acidic calcium phosphate or basic calcium phosphate.

구체적으로, 상기 인산칼슘은 β-트리칼슘포스페이트(β-TCP), 디칼슘 포스페이트 디하이드레이트(CaHPO4 ··2H2O, DCPD), 테트라칼슘 디하이드로겐 포스페이트(Ca4H2P6O20, TCHP), 하이드록시아파타이트(HAp), 옥타칼슘 포스페이트(OCP), α-트리칼슘포스페이트(α-TCP) 및 테트라 칼슘 포스페이트(TTCP) 중에서 선택된 1종 이상일 수 있으나, β-트리칼슘포스페이트(β-TCP)인 것이 바람직하다.Specifically, the calcium phosphate is β- tricalcium phosphate (β-TCP), dicalcium phosphate dihydrate (CaHPO 4 · · 2H 2 O , DCPD), tetra-calcium dihydrogen phosphate (Ca 4 H 2 P 6 O 20 , TCHP), hydroxyapatite (HAp), octacalcium phosphate (OCP), α- tricalcium phosphate (α-TCP) and tetra calcium phosphate (TTCP) may be at least one selected from, but β-tricium phosphate (β -TCP) is preferable.

인산칼슘을 포함하는 상업적 상품으로는 RENEW 메티컬의 합성골 제품 “Vital” 등을 사용하는 것이 바람직하나, 본 발명의 범위가 여기에 한정되지 않는다.As a commercial product containing calcium phosphate, RENEW Medical's synthetic bone product “Vital” is preferably used, but the scope of the present invention is not limited thereto.

상기 인산칼슘은 pH 조건에 따라서 변화하는 칼슘의 과포화 농도 및 인산과의 반응에 의해 다양한 pH 조건에 따라서 상평형을 이루어 생성하는 물질이 변화할 수 있다.In the calcium phosphate, a material produced by achieving phase equilibrium according to various pH conditions by a reaction with a supersaturated concentration of calcium and phosphoric acid that changes depending on pH conditions may be changed.

구체적으로, 상기 인산칼슘은 pH 4.2 이하에서는 디칼슘 포스페이트 디하이드레이트(CaHPO4··2H2O, DCPD)가 가장 안정한 상으로서 최다량 형성되고, pH 5.5 이상인 경우에서는 하이드록시아파타이트(HAp)가 가장 안정하여 최다량 형성되며, pH 4.2 내지 4.8 사이의 범위에서는 β-트리칼슘포스페이트(β-TCP), 하이드록시 아파타이트(Hap), 옥타칼슘 포스페이트(OCP), α-트리칼슘포스페이트(α-TCP) 및 테트라 칼슘 포스페이트(TTCP)의 혼합상이 형성된다. 또한 pH 환경을 4.8 내지 5.5 로 형성하였을 경우에는 다량의 β-TCP가 형성되어 과포화를 이룬 뒤 석출된다. 첨가되는 인산의 양을 조절함으로써 이러한 pH 범위를 설정할 수 있지만, 대량화된 공정에서는 매뉴얼화 된 용량으로써 간편하게 이를 구현할 수 있다.Specifically, in the calcium phosphate, dicalcium phosphate dihydrate (CaHPO 4 ··2H 2 O, DCPD) is formed in the largest amount as the most stable phase at pH 4.2 or lower, and hydroxyapatite (HAp) is the most stable at pH 5.5 or higher. It is stable and formed in the highest amount, and in the range of pH 4.2 to 4.8, β-tricium phosphate (β-TCP), hydroxyapatite (Hap), octacalcium phosphate (OCP), α-tricalcium phosphate (α-TCP) and a mixed phase of tetra calcium phosphate (TTCP). In addition, when a pH environment of 4.8 to 5.5 is formed, a large amount of β-TCP is formed and supersaturated and then precipitated. This pH range can be set by controlling the amount of phosphoric acid added, but in a mass-produced process, it can be easily implemented with a manual capacity.

칼슘 수용액과 인산 수용액의 혼합은 발열 반응을 일으킨다. 추가적인 온도형성 장치를 이용하지 않아도 본 발명을 실시할 수는 있으나, 온건 환경으로써 β-TCP를 수득하기 위해 20 내지 125℃의 온도환경을 유지시키는 것이 바람직하고, 더욱 바람직하게는 60 내지 95℃의 온도조건을 유지시키는 것이 용해도, 반응 및 석출의 수율 면에서 유리하다. 즉, 온도환경이 125℃를 초과하는 경우, 형성되는 β-TCP의 용해도가 지나치게 높아져 만족스러울 만큼의 수득이 어렵고, 20℃ 미만의 온도에서는 칼슘 수용액과 인산의 충분한 반응이 이루어지기 어렵다. 이러한 결과와 여러 차례의 추가적인 시험을 거쳐, 60 내지 95℃의 온도에서 최적의 수율을 달성할 수 있다.Mixing of aqueous calcium solution and aqueous phosphoric acid solution causes an exothermic reaction. Although the present invention can be practiced without using an additional temperature forming device, it is preferable to maintain a temperature environment of 20 to 125°C in order to obtain β-TCP as a moderate environment, and more preferably 60 to 95°C. Maintaining the temperature condition is advantageous in terms of solubility, reaction and yield of precipitation. That is, when the temperature environment exceeds 125 ℃, the solubility of the formed β-TCP is too high, it is difficult to obtain satisfactory enough, and at a temperature of less than 20 ℃, it is difficult to make a sufficient reaction between the aqueous calcium solution and phosphoric acid. Through these results and several additional tests, an optimal yield can be achieved at a temperature of 60 to 95°C.

아울러 반응에 사용되는 상기 칼슘 수용액은, pH 및 온도환경에 따라서 칼슘이온이 과포화된 용액일 수 있다. 상기 “과포화”라는 표현은 당업계 통상의 기술적 지식과 같이, 용질이 수용액에 용해될 수 있는 한계량을 초과하는 만큼 첨가되었음을 의미한다. 과포화된 칼슘이온은 인산이온과 반응하여 β-TCP를 포함하는 생성물이 석출될 수 있다. 전술한 pH 또는 온도환경(20 내지 125℃)에서, 용해되어 과포화된 칼슘이온의 농도는 7 내지 10 mM 일 수 있고, 더욱 바람직한 범위(온도환경 60 내지 95℃)에서는 7.8 내지 10 mM 일 수 있다.In addition, the calcium aqueous solution used for the reaction may be a solution in which calcium ions are supersaturated depending on the pH and temperature environment. The expression “supersaturated” means that the solute has been added in excess of the limit amount that can be dissolved in the aqueous solution, as is common technical knowledge in the art. Supersaturated calcium ions may react with phosphate ions to precipitate a product including β-TCP. In the aforementioned pH or temperature environment (20 to 125 ° C), the concentration of dissolved and supersaturated calcium ions may be 7 to 10 mM, and in a more preferred range (temperature environment 60 to 95 ° C), 7.8 to 10 mM .

또한 상기 반응은, 이산화탄소와의 접촉이 차단된 이산화탄소 비함유 분위기에서 수행되는 것이 바람직하다. Ca2 + 또는 Ca 화합물은 주위 환경 중의 CO2와 쉽게 반응하는 성질이 있는데, 이로써 생성된 탄산기는 후에 이루어져야 할 β-TCP 결정화의 방해 요인으로 작용하기 때문이다. 따라서 본 발명을 구현 또는 재현하려는 자는, 질소 분위기 또는 진공 환경을 조성함으로써 이러한 부수적인 반응을 차단하는 것이 바람직하다. Ar 등의 불활성 기체 분위기를 조성하거나 비용의 효율과 편의성을 고려하여 N2 환경을 설정할 수 있다.In addition, the reaction is preferably performed in a carbon dioxide-free atmosphere in which contact with carbon dioxide is blocked. Ca 2 +, or Ca compounds is due to act as a disturbance of the β-TCP crystallization can be done after the acid group there is a property that easily react with CO 2 in the environment, thereby generating. Therefore, it is preferable for those who want to implement or reproduce the present invention to block such ancillary reactions by creating a nitrogen atmosphere or a vacuum environment. An inert gas atmosphere such as Ar may be created, or an N 2 environment may be set in consideration of cost efficiency and convenience.

상기 석고(calcium sulfate)는 반수 석고(calcium sulfate hemihydrate), 이수 석고(calcium sulfate dehydrate), 및 무수 석고(calcium sulfate anhydrate) 중에서 선택된 1종 이상일 수 있으나, 반수 석고(calcium sulfate hemihydrate) 인 것이 바람직하다.The gypsum (calcium sulfate) may be at least one selected from among calcium sulfate hemihydrate, calcium sulfate dehydrate, and calcium sulfate anhydrate, but is preferably calcium sulfate hemihydrate. .

본 발명의 치주용 골시멘트 조성물에 포함되는 성분으로서 인산칼슘 및 석고를 제외한 칼슘카보네이트, 실리콘다이옥사이드, 알루미늄산화물, 및 칼슘지르코니아 복합체는 상용화된 다양한 MTA(Mineral Trioxide Aggregate)에 포함되는 성분이므로, MTA를 포함시켜 본 발명의 치주용 골시멘트 조성물을 용이하게 제조할 수 있다.As a component included in the bone cement composition for periodontal use of the present invention, calcium carbonate, silicon dioxide, aluminum oxide, and calcium zirconia complex excluding calcium phosphate and gypsum are components included in various commercially available MTA (Mineral Trioxide Aggregate). By including the bone cement composition for periodontal use of the present invention can be easily prepared.

상기 MTA는 수경성(hydraulic) 바이오세라믹 물질이다. 본 발명에서 사용되는 MTA는 시중에 유통되는 다양한 MTA가 사용될 수 있고, 바람직하게는 BioMTA사의 “Retro MTA” 또는 Dentsply Sirona사의“ProRoot MTA”를 사용할 수 있으나 본 발명의 범위가 여기에 한정되는 것은 아니다. The MTA is a hydraulic bioceramic material. As the MTA used in the present invention, various commercially available MTAs may be used, and preferably BioMTA's "Retro MTA" or Dentsply Sirona's "ProRoot MTA" may be used, but the scope of the present invention is not limited thereto. .

특히 “Retro MTA”또는 “ProRoot MTA”는 Portland cement를 정제한 시멘트가 아니며 수경성 시멘트 제조공정으로 생산된 것이고, 인체에 유해한 중금속이 없고 경화시간이 빠르며, 수화시 적당한 점도를 유지할 수 있어 임상시술이 용이하다. In particular, “Retro MTA” or “ProRoot MTA” is not a cement that has been refined from Portland cement, it is produced by a hydraulic cement manufacturing process. Easy.

아래의 표 1은 “Retro MTA” 또는 “ProRoot MTA”의 물리적 특성을 정리한 것이다.Table 1 below summarizes the physical characteristics of “Retro MTA” or “ProRoot MTA”.

물성Properties Retro MTARetro MTA ProRoot MTAProRoot MTA 표면적(m2/kg)Surface area (m 2 /kg) 961961 409409 평균입경(㎛)Average particle diameter (㎛) 2.622.62 6.96.9 90wt% finer than(㎛)90wt% finer than(㎛) 4.644.64 19.9719.97 50wt% finer than (㎛)50wt% finer than (㎛) 2.362.36 6.856.85 10wt% finer than (㎛)10wt% finer than (㎛) 1.181.18 0.970.97 응고시간(시작)coagulation time (start) 180초180 seconds 74분74 minutes 응고시간(종결)Coagulation time (final) 360분360 minutes 210분210 minutes Free CaO 함량(wt%)Free CaO content (wt%) 0.660.66 1.741.74 총결정상(total crystalline phases)total crystalline phases 96.996.9 94.394.3 팽창계수(expansion coefficient)expansion coefficient 0.090.09 0.270.27 컬러color whitewhite Yellow & GrayYellow & Gray 중금속heavy metal 없음does not exist Cr, As, NiCr, As, Ni

표 2는 본 발명의 골시멘트 조성물에 포함될 수 있는 바람직한 MTA의 성분을 정리한 것이다.Table 2 summarizes preferred MTA components that may be included in the bone cement composition of the present invention.

화학성분chemical composition 함량(wt%)Content (wt%) 칼슘카보네이트(CaCO3)Calcium carbonate (CaCO 3 ) 60-8060-80 실리콘다이옥사이드(SiO2)Silicon dioxide (SiO 2 ) 5-155-15 알루미늄산화물aluminum oxide 5-105-10 칼슘 지르코니아 복합체Calcium Zirconia Composite 20-3020-30 총계sum 100100

상기 TMA는 WMTA(White Mineral Trioxide Aggregate), GMTA(Gray Mineral Trioxide Aggregate) 및 YMTA(Yellow Mineral Trioxide Aggregate) 중에서 선택된 1종 이상일 수 있고, 바람직하게는 WMTA 일 수 있다. 통상적으로 WMTA의 입자가 GMTA의 입자에 비하여 입자 크기가 더욱 균일하기 때문이다.The TMA may be at least one selected from White Mineral Trioxide Aggregate (WMTA), Gray Mineral Trioxide Aggregate (GMTA), and Yellow Mineral Trioxide Aggregate (YMTA), preferably WMTA. This is because, in general, the particle size of WMTA particles is more uniform than that of GMTA particles.

본 발명의 치주용 골시멘트 조성물은 자연 치아 이식용 또는 치아 부식 치료용으로 사용될 수 있다.
The periodontal bone cement composition of the present invention may be used for natural tooth transplantation or tooth decay treatment.

이하, 바람직한 실시예를 들어 본 발명을 더욱 상세하게 설명한다. 그러나 이들 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것으로, 본 발명의 범위가 이에 의하여 제한되지 않는다는 것은 당업계의 통상의 지식을 가진 자에게 자명할 것이다.
Hereinafter, the present invention will be described in more detail with reference to preferred embodiments. However, these Examples are intended to explain the present invention in more detail, it will be apparent to those skilled in the art that the scope of the present invention is not limited thereby.

[[ 실시예Example ]]

제조예manufacturing example 1: One: 치주용periodontal 시멘트 조성물( cement composition ( GEMMAGEMMA ) 제조) Produce

하기 조성을 갖는 파우더 성분과 리퀴드 성분으로 이루어진 치주용 시멘트 조성물 GEMMA를 제조하였다.A cement composition GEMMA for periodontal consisting of a powder component and a liquid component having the following composition was prepared.

파우더 성분powder ingredients

β-TCP(β-tricalcium phosphate) 6.8 g, 6.8 g of β-tricalcium phosphate (β-TCP);

CSH(calcium sulfate hemihydrate) 2.4 g, 2.4 g of calcium sulfate hemihydrate (CSH);

bioMTA사의 Retro MTA 0.8 g0.8 g of Retro MTA from bioMTA

리퀴드liquid 성분 ingredient

과인산 0.001392 g0.001392 g of superphosphate

saline 1 cc
saline 1 cc

제조비교예Manufacturing comparative example 1: One: VITALVITAL

RENEW 메티컬의 합성골 제품으로 5 내지 6개월 후 완전히 분해되어 흡수되는 제품이며 구성은 아래와 같다.As a synthetic bone product of RENEW Medical, it is completely decomposed and absorbed after 5 to 6 months, and the composition is as follows.

파우더 성분powder ingredients

β-TCP(β-tricalcium phosphate)β-TCP (β-tricalcium phosphate)

Calcium SulphateCalcium Sulphate

리퀴드liquid 성분 ingredient

Saline + HPMC(Hydroxypropyl Methylcellulose)
Saline + HPMC (Hydroxypropyl Methylcellulose)

제조비교예Manufacturing comparative example 2: 2: POLYBONEPOLYBONE

SK바이오랜드㈜의 골대체제인 POLYBONE의 파우더형을 준비하였다.A powder type of POLYBONE, a bone substitute of SK Bioland, was prepared.

파우더 성분powder ingredients

β-TCP(β-tricalcium phosphate) 6.8 g, 6.8 g of β-tricalcium phosphate (β-TCP);

CSH(calcium sulfate hemihydrate) 2.4 g, 2.4 g of calcium sulfate hemihydrate (CSH);

MCPM(Monocalcium phosphate monohydrate) 0.8 g0.8 g of Monocalcium phosphate monohydrate (MCPM)

리퀴드liquid 성분 ingredient

Poly-P(폴리 인산) 0.001392 gPoly-P (polyphosphoric acid) 0.001392 g

증류수 1 cc
distilled water 1 cc

실시예Example 1: One: GEMMAGEMMA 이용한 치아 이식 dental implants using

먼저, 환자의 흔들리는 치아를 발치한 후 차아염소산나트륨(NaOCl) 용액에 2 내지 4시간 동안 침지시켜 치은, 치석을 제거한 후 캐비트론(Cavitron)으로 세척하였다. 세척된 발치 치아는 치아 뿌리 끝 구멍인 치근단공의 입구로부터 2 내지 3mm만큼 치과용 레진으로 밀폐하여 재이식할 수 있도록 준비하여 두었다.First, the patient's shaking teeth were extracted and then immersed in sodium hypochlorite (NaOCl) solution for 2 to 4 hours to remove gingiva and calculus, and then washed with Cavitron. The cleaned extracted teeth were sealed with dental resin by 2 to 3 mm from the entrance of the apical foramen, which is the end hole of the tooth root, and prepared for re-implantation.

발치 후 2주 경과하면 환자의 염증이 완화되고, 잇몸이 아물며 치주뼈가 회복된다. 이후, 잇몸의 치아 발치 부분이 덮이면 발치되었던 부분을 절개하고 긁어내어 발치하였던 치아를 이식할 수 있는 구멍을 확보하고, 지혈제로 소독하였다. Two weeks after tooth extraction, the patient's inflammation is relieved, the gums heal, and the periodontal bone is restored. After that, when the tooth extraction portion of the gum is covered, the extracted portion is incised and scraped to secure a hole for implanting the extracted tooth, and disinfected with a hemostatic agent.

이후, 제조예 1의 GEMMA의 파우더 성분 1 g과 리퀴드 성분 0.6cc 비율로 혼합하여 1분간 수화시킨 후 물기를 제거한 치주용 시멘트 조성물을 상기 발치 위치 즉 발치와에 충전하고, 충전된 치주용 시멘트 조성물에 준비된 발치 치아를 이식하였다. 이식 후, 5분 정도 유지함으로써 치주용 시멘트 조성물이 경화되어 이식된 치아가 고정되도록 하였다. Thereafter, 1 g of the powder component of GEMMA of Preparation Example 1 and the liquid component of 0.6cc were mixed in a ratio of 0.6cc and hydrated for 1 minute. The prepared extraction teeth were implanted in the After implantation, the periodontal cement composition was hardened by holding for about 5 minutes so that the implanted teeth were fixed.

치료 후 곧바로 죽과 같은 부드러운 식사가 가능하고, 2 내지 3일 내에 치아가 고정되어 일반 식사가 가능하며, 6개월 후 치아 고정이 성공적으로 이루어졌는지 확인하였다.
After treatment, soft meals such as porridge are possible, teeth are fixed within 2 to 3 days, and normal meals are possible, and it was confirmed that teeth fixation was successful after 6 months.

비교예comparative example 1: One: VITALVITAL 을 이용한 치아 이식dental implantation using

실시예 1의 GEMMA 대신에 VITAL 제품을 사용한 것을 제외하고는 실시예 1과여 동일한 방법으로 치아 이식을 하였다. 이때, 이식 후 6개월간 치료치아의 사용을 금지하였으며, 6개월 후 치아 고정이 성공적으로 이루어졌는지 확인하였다.
A tooth was implanted in the same manner as in Example 1, except that VITAL products were used instead of GEMMA of Example 1. At this time, the use of the treated teeth was prohibited for 6 months after transplantation, and it was confirmed that the teeth were fixed successfully after 6 months.

비교예comparative example 2: 2: POLYBONEPOLYBONE 을 이용한 치아 이식 dental implantation using

실시예 1의 GEMMA 대신에 POLYBONE 제품을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치아 이식을 수행하였다. 이때. 이식 초기에는 죽 같은 부드러운 식사를 하도록 하고 2개월이 경과하면 생선, 김치 등을 곁들인 식사를 할 수 있으며, 3개월 경과 후에는 질긴 고기 섭취를 할 수 있도록 하였다.
Dental implantation was performed in the same manner as in Example 1, except that a POLYBONE product was used instead of the GEMMA of Example 1. At this time. In the early stage of transplantation, a soft meal such as porridge was allowed, and after 2 months, a meal with fish and kimchi was allowed, and after 3 months, it was allowed to eat tough meat.

[[ 시험예test example ]]

실험예Experimental example 1: 치아 이식 성공률 분석 1: Analysis of the success rate of dental implantation

실시예 1, 비교예 1 및 비교예 2에 따라 수행된 치아 이식에서 치아이식의 성공률을 비교해 보기 위하여 1차 치아이식, 1차 치아이식이 실패한 경우 동일한 방법으로 2차 치아이식, 2차 치아이식이 실패한 경우 3차 치아이식을 시술한 치아 이식 환자의 수, 최종 치아이식 성공률을 비교하여 그 결과를 아래의 표 3에 나타내었다.In order to compare the success rate of dental implantation in the dental implantation performed according to Example 1, Comparative Example 1, and Comparative Example 2, when the primary dental implantation and the primary dental implantation fail, the secondary dental implantation and the secondary dental implantation are performed in the same manner. In the case of this failure, the number of dental implant patients who underwent tertiary dental implantation and the final dental implant success rate were compared, and the results are shown in Table 3 below.

항목item 실시예 1(GEMMA)Example 1 (GEMMA) 비교예 1(VITAL)Comparative Example 1 (VITAL) 비교예 2(POLYBONE)Comparative Example 2 (POLYBONE) 최초 치아이식 환자수Number of first dental transplant patients 3939 4242 2727 1차 치아이식 성공 환자수Number of successful primary dental implantation patients 1919 2121 00 2차 치아이식 성공 환자수Number of successful secondary dental implantation patients 1313 22 22 3차 치아이식 성공 환자수Number of successful 3rd dental implantation patients 33 1One 00 치아이식 성공 총 환자수Total number of successful dental implantation patients 3535 2424 22 치아이식 실패 총 환자수Total number of failed dental implants 44 1818 2525 치아이식 성공률(%)Dental implant success rate (%) 89.789.7 57.157.1 7.47.4

이에 따르면, 실시예 1의 치주용 시멘트 조성물 GEMMA를 이용한 치아 이식을 수행한 경우 1차 > 2차 > 3차 이식 순으로 성공 환자수가 많은 것으로 나타났으며, 최종 치아이식 성공률은 89.7%로 나타나 대부분의 환자가 치아이식에 성공한 것으로 나타났다. 뿐만 아니라, 실시예 1의 GEMMA는 치아이식 시술 후 2 내지 3일 이내에 정상적인 식사가 가능한 점에서, 치아고정 기간이 수개월 소요되는 비교예 1의 VITAL, 비교예 2의 Polybone에 비하여 시술환자의 불편을 최소화할 뿐 아니라 치아고정 기간 동안 실수로 인한 충격 등으로 치아 이식이 실패되는 위험을 최소화할 수 있다. According to this, when a tooth transplant using the periodontal cement composition GEMMA of Example 1 was performed, the number of successful patients was large in the order of 1st > 2nd > 3rd implantation, and the final tooth transplantation success rate was 89.7%, mostly of patients have been successful in dental implantation. In addition, in that GEMMA of Example 1 can eat normally within 2 to 3 days after the dental implant procedure, compared to VITAL of Comparative Example 1, which takes several months of dental fixation, and Polybone of Comparative Example 2, the patient's discomfort is reduced. Not only can it be minimized, but it can also minimize the risk of dental implant failure due to an accidental impact during the period of dental fixation.

한편, 비교예 1의 VITAL을 이용한 치아이식은 초기 이식 성공률이 50%로 높았으나, 실패 후 2차 내지 3차 치아이식 시술에서는 성공률이 매우 낮게 나타났다. 그리고 최종 성공률은 57.1%로 낮지 않았지만, 실시예 1의 GEMMA에 비하여 현저히 낮은 최종 성공률을 나타냈다. 또한, 비교예 1의 VITAL은 치아 이식 후 6개월간 이식치를 사용할 수 없어 시술환자의 불편이 크고, 긴 치아고정 및 골재생 기간으로 인하여 부주의로 인한 충격으로 치아 이식이 실패할 위험이 큰 단점이 있다.On the other hand, the dental implantation using VITAL of Comparative Example 1 had a high initial implantation success rate of 50%, but the success rate was very low in the second to tertiary dental implantation procedures after failure. And although the final success rate was not as low as 57.1%, the final success rate was significantly lower than that of GEMMA of Example 1. In addition, VITAL of Comparative Example 1 has a disadvantage in that the implant cannot be used for 6 months after dental implantation, so there is a large inconvenience to the surgical patient, and there is a large risk of dental implant failure due to an impact caused by carelessness due to a long period of fixation and bone regeneration. .

또한, 비교예 2의 Polybone을 이용한 치아이식의 경우 치아고정이 매우 어려워 치아이식 성공률이 7.4%에 불과하였으며, 시술 후 5 내지 6개월이 경과하여 치근이 악골에 고착되지 않는 것으로 나타나 치주용 시멘트로서는 적합하지 않는 것을 확인할 수 있다.
In addition, in the case of dental implantation using Polybone of Comparative Example 2, it was very difficult to fix the teeth, so the success rate of dental implantation was only 7.4%. You can see what doesn't fit.

시험예test example 2: 환자 A의 치아 이식 2: Transplantation of patient A's teeth 임상예clinical example

실시예 1의 GEMMA 처치군 중 이식 성공한 환자 A의 각 시기별 X선 촬영 파노라마 사진을 도 1 내지 도 5에 나타내었으며, 치료 과정 및 치아 상태를 아래에 설명하였다.Among the GEMMA treatment groups of Example 1, the X-ray panoramic photographs for each period of the successful transplantation patient A are shown in FIGS. 1 to 5, and the treatment process and dental condition are described below.

2018. 8. 132018. 8. 13

도 1의 (a)는 내원 환자 A의 치아 상태를 살펴본 X선 파노라마 사진이고, (b)는 노란색으로 표시한 우측 제1 대구치 부분을 확대하여 본 것이다.Fig. 1 (a) is an X-ray panoramic photograph examining the dental condition of the visiting patient A, and (b) is an enlarged view of the right first molar portion marked in yellow.

상악 우측 제1 대구치가 심하게 흔들려 불편을 호소하며 내원하였고, 파노라마 상에서 치아를 둘러싼 뼈가 전혀 없어 까맣게 보였다.The maxillary right first molar was severely shaken and complained of discomfort.

2018. 8. 162018. 8. 16

치근박리 소파술을 하여 주위 치아도 염증을 완화시켰다. Root dissection curettage was also performed to relieve inflammation of the surrounding teeth.

2018. 9. 72018. 9. 7

도 2의 (a)는 염증 완화 후 환자 A 치아의 X선 파노라마 사진으로 우측 제1 대구치 부분을 표시한 것이며, (b)의 표시 부분은 환자의 우측 과두가 정상임을 보여준다.Fig. 2 (a) is an X-ray panoramic image of patient A's tooth after inflammation relief, showing the right first molar portion, and the marked portion in (b) shows that the patient's right condyle is normal.

2018. 9. 202018. 9. 20

의도적 재식술을 위해 발치하였으며, 발치 치아를 NaOCl에 3 시간 담궈 치석과 뿌리에 침출된 내독소를 제거하고 Saline 에 2 주간 보관하였다.The tooth was extracted for intentional replantation, and the extracted tooth was immersed in NaOCl for 3 hours to remove the tartar and endotoxin leached from the root, and stored in Saline for 2 weeks.

도 3의 (a)는 발치 전 환자 A의 치아의 X선 파노라마 사진으로 발치될 부분을 표시하였으며, (b)는 발치할 부위를 확대한 것이고, 이 사진은 좌우 역전상이다.3 (a) is an X-ray panoramic photograph of patient A's tooth before extraction, showing the portion to be extracted, (b) is an enlarged view of the extraction site, and this photograph is a left and right reverse image.

2018. 10. 52018. 10. 5

발치와를 절개하고 소파 후 지혈하고 제조예 1에 따른 Gemma를 치아 뿌리 면에 바르고 발치와에 내재시킨 후 옆치아와 함께 브릿지 고정시켰다. After incision of the orbit, hemostasis was performed, and Gemma according to Preparation Example 1 was applied to the root surface of the tooth, and the bridge was fixed together with the side teeth after being embedded in the orbit.

도 4의 (a)는 2018. 10. 5 GEMMA를 이용한 치아 이식 시술 후, (b)는 최초 내원한 당시 2018. 8. 13일 동일한 부분의 X선 사진이다.Figure 4 (a) is an X-ray photograph of the same part on August 13, 2018 at the time of the first visit to the hospital, after a tooth transplantation using GEMMA on October 5, 2018.

시술 후 바로 죽으로 무른 식사를 하였고 2일 후 보통 식사가 가능하였다.A soft meal was eaten with porridge immediately after the procedure, and normal meals were possible 2 days later.

2018. 11. 192018. 11. 19

도 5의 (a)는 2018. 11. 19 GEMMA를 이용한 치아 이식 상태, (b)는 최초 내원한 당시 2018. 8. 13일 동일한 부분의 X선 사진이다.Figure 5 (a) is a dental implant state using GEMMA on November 19, 2018, (b) is an X-ray photograph of the same part on August 13, 2018 at the time of the first visit.

김치찌개 식사 5일이 경과한 시점이었으나 타진(percussion) 반응과 치아동요가 전혀 없었으며, (a)에 의하면, X선 사진상 치조골이 하얗게 형성되었음을 확인할 수 있었다.Although 5 days had elapsed since the kimchi stew meal, there was no percussion reaction or tooth shake.

2019. 4. 242019. 4. 24

파노라마 사진 촬영을 하여 치근 주위에 안정한 골 상태 확인하였다. GEMMA 코팅 치료 부위가 하얀색으로 X선 사진으로 선명하게 나타났고, 치아고정이 안정적으로 되었으며, 골 재생이 이루어졌음을 확인할 수 있었다. 또한, 제반 식사에 어려움이 없어졌다.
Panoramic photos were taken to confirm the stable bone condition around the root. It was confirmed that the GEMMA-coated treatment area was white and clearly visible on the X-ray image, the teeth were fixed, and bone regeneration was achieved. In addition, difficulties in all meals were eliminated.

실험예Experimental example 3: 3: 환자 B의 치아 이식 Patient B's tooth transplant 임상예clinical example

도 6 내지 도 11은 환자 B의 치아 이식 치료의 경과를 보여주는 사진이다.6 to 11 are photographs showing the progress of the dental implant treatment of patient B.

2016.08.17 2016.08.17

환자 B는 만성치주염 판정을 받고 비교제조예 2의 Vital을 이용하여 치아 이식을 하기로 결정하였다. 발치 후 치아소독 및 멸균하고, 바로 발치와에 Vital을 채우고 치아를 끼워 넣었다.Patient B was diagnosed with chronic periodontitis and decided to implant a tooth using Vital of Comparative Preparation Example 2. After tooth extraction, the teeth were disinfected and sterilized, and the Vital was immediately filled in the extraction fossa and the teeth were inserted.

도 6의 (a)는 2014. 12. 20 만성치주염 판정을 받기 전 환자 B의 치아 X선 사진이고, (b)는 2016. 8. 17 Vital을 이용한 치아 이식 직후의 환자 B의 치아 X선 사진이며, (c)는 2016. 8. 26 Vital을 이용한 치아 이식 9일 후의 환자 B의 치아 X선 사진으로 이식 전후 상태를 비교한 것이다.Figure 6 (a) is a tooth X-ray photograph of patient B before being diagnosed with chronic periodontitis on December 20, 2014, and (b) is a tooth X-ray photograph of patient B immediately after dental implantation using Vital on August 17, 2014. and (c) is an X-ray image of patient B's teeth 9 days after dental implantation using Vital on August 26, 2016, comparing the state before and after implantation.

2017. 11. 302017. 11. 30

도 7은 Vital을 이용한 치아 이식 후 약 3개월 후인 2017. 11. 30 환자 B의 이식 치아의 X선 사진이다. 이에 따르면 이식 치아의 Vital 코팅 부위에 흰색이 분명해 짐을 확인할 수 있었다.7 is an X-ray photograph of implanted teeth of patient B on November 30, 2017, approximately 3 months after dental implantation using Vital. According to this, it was confirmed that the whiteness of the Vital coating area of the implanted tooth became clear.

2018. 5. 302018. 5. 30

Vital을 이용한 치아 이식 후 6개월 이상 이상이 없었으나, 환자 B가 2018. 5 30 치아가 흔들리고 통증을 호소하였다. There were no abnormalities for more than 6 months after dental implantation using Vital, but patient B complained of shaking teeth and pain on May 30, 2018.

2018. 6. 282018. 6. 28

도 8은 2018. 6. 28 환자 B의 치아 X선 사진이다. 진료 결과 치주염이 재발하였음을 확인하였다.8 is a tooth X-ray photograph of patient B on June 28, 2018. As a result of treatment, it was confirmed that periodontitis had recurred.

2018. 12. 132018. 12. 13

Vital을 이용한 치아 이식은 실패 판정되었다. Dental implantation using Vital was judged to be a failure.

GEMMA 시술을 결정하고, 발치 후 발치 치아를 NaOCl에 3 시간 담궈 치석과 뿌리에 침출된 내독소를 제거하고 Saline 에 2 주간 보관하였다.The GEMMA procedure was decided, and after tooth extraction, the extracted tooth was immersed in NaOCl for 3 hours to remove the calculus and endotoxin leached from the root, and stored in Saline for 2 weeks.

2019. 12. 282019. 12. 28

도 9는 환자 B의 GEMMA를 이용한 재의재 시술 직후의 X선 사진이다.9 is an X-ray photograph of patient B immediately after reconstructive surgery using GEMMA.

발치와를 외과술로 소파 후 지혈시키고, GEMMA를 채운 후, 뿌리면에 GEMMA를 바른 발치치아를 발치와에 바로 끼워 넣고 치아가 제 위치에 고정되게 하였다. 환자 B는 시술 후 바로 죽으로 이루어진 부드러운 식사가 가능해졌고 빠르게 치아가 고정되어 3일 내에 밥 등을 포함하는 일반 식사가 가능해졌다. After curing the extraction fossa surgically, hemostasis was performed, and after filling with GEMMA, the extracted tooth with GEMMA applied to the root surface was inserted directly into the extraction foyer, and the tooth was fixed in place. Patient B was able to eat a soft meal made of porridge immediately after the procedure, and her teeth were fixed quickly so she could eat a regular meal including rice within 3 days.

2019. 3. 282019. 3. 28

도 10은 환자 B의 GEMMA를 이용한 재의재 시술 후 3개월 경과한 2019. 3. 28시점에서의 이식 치아의 X선 사진이다. 시술 3개월 가량 경과한 시점에서 통증이나 치아 흔들림이 없고 정상적인 식사가 가능하였다.10 is an X-ray photograph of the implanted tooth at the time of March 28, 2019, 3 months after the re-revision procedure using GEMMA of patient B. At about 3 months after the procedure, there was no pain or tooth shake, and normal eating was possible.

2019. 5. 32019. 5. 3

도 11은 환자 B의 GEMMA를 이용한 재의재 시술 후 4개월 이상 경과한 2019. 5. 3 이식 치아의 X선 사진이다. 이에 따르면 치아 상태가 잘 유지되고 있고, 골재생이 잘 진행되어 GEMMA 접합 부위가 검정색에서 점차 흰색으로 변화하고 있음을 확인하였다.
11 is an X-ray photograph of a tooth implanted on May 3, 2019, which has elapsed more than 4 months after reconstructive surgery using GEMMA of patient B. According to this, it was confirmed that the tooth condition is well maintained and bone regeneration is progressing well, so that the GEMMA joint site is gradually changing from black to white.

실험예Experimental example 4: 환자 C 치아 이식 4: Patient C tooth transplantation 임상예clinical example

도 12 내지 도 15는 환자 C의 치아 이식 치료 경과를 나타낸 사진이다.12 to 15 are photographs showing the progress of dental implant treatment of patient C. FIG.

2019. 4. 192019. 4. 19

20년 전 충격으로 아래턱의 앞니가 흔들렸으나 어느 정도 잘 유지되어 오다가 만성치주염으로 흔들림이 심해 발치하였으며, 발치 치아를 NaOCl에 3 시간 담궈 치석과 뿌리에 침출된 내독소를 제거하고 식염수에 2 주간 보관하였다.The incisors of the lower jaw were shaken due to the shock 20 years ago, but they were maintained well to some extent, and the shaking was severe due to chronic periodontitis. Stored weekly.

도 12는 발치하여 치석 및 내독소가 제거된 치아 사진이다.12 is a photograph of a tooth from which tartar and endotoxin have been removed by extraction.

2019. 5. 22019. 5. 2

치아 재이식 직전에 치아를 꺼내 세정하여 GEMMA로 도포하였다.Just before the tooth re-implantation, the tooth was taken out and cleaned and applied with GEMMA.

발치 부위는 소파 후 세정하고, GEMMA로 도포 후 앞서 준비한 발치 치아를 끼워 넣고, 재이식 치아 좌우의 치아에 금속메쉬로 양쪽 치아를 함께 걸고 슈퍼본드로 고착하는 브릿지 작업을 하고, 이식 치아가 주변치아와 색상 및 모양이 매칭하도록 치아 표면 그라인딩 작업을 하였으며 시술 시간은 약 1시간 20분 소요되었다.The extraction site is cleaned after couching, applied with GEMMA, and the previously prepared extraction teeth are inserted. The tooth surface was ground to match the color and shape, and the procedure took about 1 hour and 20 minutes.

도 13은 발치 2주 후인 2019. 5. 2 GEMMA 이용한 치아 이식 시술 전(a)과 시술 직후(b)의 환자 C의 치아 X선 사진이다.13 is an X-ray photograph of patient C's teeth before (a) and immediately after (b) dental implantation using GEMMA on May 2, 2019, 2 weeks after tooth extraction.

2019. 5. 102019. 5. 10

도 14는 GEMMA 이용한 치아 이식 일주일 경과된 2019. 5. 10 환자 C의 치아 X선 사진이다. 이에 따르면 단 일주일 만에 치아 이식 직후에 비하여 더 흰색을 띠며 치아 고정이 잘 이루어졌음을 확인할 수 있었다.14 is a tooth X-ray photograph of patient C on May 10, 2019, after a week of dental implantation using GEMMA. According to this, it was confirmed that the teeth were fixed well with a whiter color than immediately after implantation in just one week.

도 15는 환자 C의 GEMMA 이용한 치아 이식 시술 전(a), 발치 후(b), 시술 후(c)의 사진이다.
15 is a photograph of patient C before (a), after tooth extraction (b), and after (c) dental implantation using GEMMA.

비교실험예Comparative Experimental Example 1: One: 환자 D의 치아 이식 Patient D's dental implant 임상예clinical example

2016. 5. 112016. 5. 11

발치 후 NaOCl 수용액 중에 넣어 유기물 용해 및 멸균한 후 식염수에 담궈 두었다. 비교제조예 1의 Vital로 발치와 부위에 코팅한 후 식염수로부터 치아를 꺼내어 식립하고, 5분 후 치아가 고정되는 것으로 치료 완료하였다. 이식 후 6개월 간 치료치아의 사용을 금지시켰다. 6개월 경과 후 이식 치아의 사용이 가능해져 이식 완료를 통보하였다.
After tooth extraction, it was placed in NaOCl aqueous solution to dissolve and sterilize organic matter, and then soaked in saline. After coating the tooth extraction and site with Vital of Comparative Preparation Example 1, the tooth was removed from the saline and placed, and the treatment was completed by fixing the tooth after 5 minutes. The use of treatment teeth was prohibited for 6 months after implantation. After 6 months, the use of the implanted teeth became possible, and the completion of the implantation was notified.

비교실험예Comparative Experimental Example 2: 환자 E의 치아 이식 2: Transplantation of patient E's teeth 임상예clinical example

2017. 11. 172017. 11. 17

발치 치아를 NaOCl 수용액에 담구어 멸균한 후 식염수에 7일간 담궈 두었다. 비교제조예 2의 Polybone으로 발치와 부위에 코팅한 후 식염수로부터 치아를 꺼내어 식립하고, 10분 후 치아가 고정되는 것으로 치료를 완성하였다.The extracted tooth was sterilized by immersing it in NaOCl aqueous solution and then immersed in saline for 7 days. After coating the tooth extraction and site with Polybone of Comparative Preparation Example 2, the tooth was taken out from the saline and placed, and the treatment was completed by fixing the tooth after 10 minutes.

2017. 11. 182017. 11. 18

치아 이식 다음날 치아가 고정 안되고 고통을 호소하였다. The next day after dental implantation, the teeth were not fixed and complained of pain.

2017. 12. 172017. 12. 17

치아 이식 한달 후 치료 효과가 없음을 확인하였으며, Polybone을 긁어내고 Gemma를 사용하여 실시예 1과 동일한 방법으로 재시술 하였으나 재시술 후 6개월이 경과하는 동안 치근이 악골에 고착되지 않았다.
It was confirmed that there was no treatment effect after one month of dental implantation, and the polybone was scraped off and the treatment was repeated in the same manner as in Example 1 using Gemma.

Claims (6)

β-트리칼슘포스페이트(β-tricalcium phosphate);
반수 석고(calcium sulfate hemihydrate);
칼슘카보네이트(CaCO3);
실리콘다이옥사이드(SiO2);
알루미늄산화물; 및
칼슘 지르코니아 복합체;를 포함하고,
자연치아 이식시 발치 위치인 발치와 충전용으로 사용되는 치주용 골시멘트 조성물.β-tricalcium phosphate;
calcium sulfate hemihydrate;
calcium carbonate (CaCO 3 );
silicon dioxide (SiO 2 );
aluminum oxide; and
Calcium zirconia complex;
A bone cement composition for periodontal use for extraction and filling, which is the extraction location for natural tooth transplantation. 제1항에 있어서,
상기 치주용 골시멘트 조성물은.
β-트리칼슘포스페이트(β-tricalcium phosphate) 100중량부에 대하여,
반수 석고(calcium sulfate hemihydrate) 30 내지 40중량부;
칼슘카보네이트(CaCO3) 9 내지 12중량부;
실리콘다이옥사이드(SiO2) 0.5 내지 2.5중량부;
알루미늄산화물 0.5 내지 1.5중량부; 및
칼슘 지르코니아 복합체 3 내지 4.5중량부;를 포함하는 것을 특징으로 하는 치주용 골시멘트 조성물.According to claim 1,
The periodontal bone cement composition.
Based on 100 parts by weight of β-tricalcium phosphate,
30 to 40 parts by weight of calcium sulfate hemihydrate;
Calcium carbonate (CaCO 3 ) 9 to 12 parts by weight;
Silicon dioxide (SiO 2 ) 0.5 to 2.5 parts by weight;
0.5 to 1.5 parts by weight of aluminum oxide; and
Calcium zirconia complex 3 to 4.5 parts by weight; periodontal bone cement composition comprising a. 제1항에 있어서,
상기 치주용 골시멘트 조성물은,
과인산(perphosphoric acid); 및
증류수 또는 식염수;를 추가로 포함하는 것을 특징으로 하는 치주용 골시멘트 조성물.According to claim 1,
The periodontal bone cement composition,
perphosphoric acid; and
Distilled water or saline; periodontal bone cement composition, characterized in that it further comprises. 삭제delete 삭제delete 삭제delete
KR1020190082419A 2019-07-09 2019-07-09 Bone cement composition for periodontal tissue KR102307234B1 (en)