KR102303652B1 - Cememnt concrete composition and repairing method for road pavement therewith - Google Patents

Cememnt concrete composition and repairing method for road pavement therewith Download PDF

Info

Publication number
KR102303652B1
KR102303652B1 KR1020210019691A KR20210019691A KR102303652B1 KR 102303652 B1 KR102303652 B1 KR 102303652B1 KR 1020210019691 A KR1020210019691 A KR 1020210019691A KR 20210019691 A KR20210019691 A KR 20210019691A KR 102303652 B1 KR102303652 B1 KR 102303652B1
Authority
KR
South Korea
Prior art keywords
cement
weight
durability
fast
concrete composition
Prior art date
Application number
KR1020210019691A
Other languages
Korean (ko)
Inventor
이선목
Original Assignee
이선목
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이선목 filed Critical 이선목
Priority to KR1020210019691A priority Critical patent/KR102303652B1/en
Application granted granted Critical
Publication of KR102303652B1 publication Critical patent/KR102303652B1/en

Abstract

The present invention provides a fast hardening cement concrete with excellent workability and durability and a road pavement repair method using a fast hardening cement concrete with excellent workability and durability. Provided is a fast hardening cement concrete with excellent workability and durability, comprising 3 to 40 wt% of a performance-improving binder, 5 to 70 wt% of fine aggregate, 5 to 65 wt% of coarse aggregate, 1 to 34 wt% of latex synthetic polymer, and 0.1 to 30 wt% of water, wherein the performance-improving binder comprises 10 to 70 wt% of mixed cement obtained by mixing normal Portland cement and micro cement having the fineness of 6,000 cm^2/g or more, the powder particles of the mixed cement, in the particle size distribution, satisfy the formula, 1.50 <= D90/D50 <= 1.55, and the standard deviation (σ) of the total powder particle size of the mixed cement satisfies the formula, 1.0 μm <= σ <= 3.0 μm.

Description

작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 보수 공법{CEMEMNT CONCRETE COMPOSITION AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH}A fast-diameter cement concrete composition with excellent workability and durability and a road pavement repair method using the same

본 발명은 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 보수 공법에 관한 것으로, 보다 구체적으로는 성능 개선 결합재 및 점도 조절제를 이용하여 산계 지연제의 함량을 최대한 줄이더라도 작업성이 우수하게 제조된 교량 오버레이 포장, 콘크리트 포장의 증설, 콘크리트 포장 보수공사 등의 콘크리트로 이루어진 토목 구조물 보수공사에 사용되는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 보수 공법에 관한 것이다.The present invention relates to a fast-diameter cement concrete composition having excellent workability and durability, and a road pavement repair method using the same, and more particularly, workability is improved even when the content of the acid-based retardant is reduced as much as possible using a performance-improving binder and a viscosity modifier. It relates to a fast-diameter cement concrete composition with excellent workability and durability used in the repair work of civil structures made of concrete such as bridge overlay pavement, concrete pavement extension, and concrete pavement repair work, and a road pavement repair method using the same. .

일반적으로 콘크리트 구조물은 열화 등에 의해 콘크리트에 균열이 발생하면 방수 성능 저하, 철근부식, 내구성 저하, 강도 저하 등으로 치명적인 결함을 초래할 수 있다. In general, when cracks occur in concrete due to deterioration of concrete structures, it can cause fatal defects such as deterioration of waterproofing performance, corrosion of reinforcing bars, deterioration of durability, and deterioration of strength.

그리고, 콘크리트의 균열은 염해, 열화와 같은 외적 환경원인, 설계하중, 소성수축 또는 건조수축과 같은 재료 특성, 배합조건, 시공적인 요인 등의 여러 가지 요인에 의하여 많이 발생한다. In addition, cracks in concrete are frequently caused by various factors such as external environmental factors such as salt damage and deterioration, material properties such as design load, plastic shrinkage or drying shrinkage, mixing conditions, and construction factors.

이와 같은 여러 가지 요인에 의해 콘크리트 구조물에 균열이 발생하게 되면 콘크리트 구조물은 하중을 견디지 못하고 붕괴될 수도 있으므로 균열이 발생된 콘크리트 구조물에 대해서는 방수성, 내구성 등을 회복하기 위하여 혹은 구조물의 안정성, 미관성 등을 고려하여 보수가 필요하다.When a crack occurs in a concrete structure due to these various factors, the concrete structure cannot withstand the load and may collapse. compensation is necessary taking into account.

한편, 교량의 바닥판, 도로의 노면 및 교량 하부 부분의 부식이나 침식이 많이 일어나는 부위를 보수 및 보강하기 위한 보수공사에는 폴리머 시멘트 모르타르가 널리 사용되고 있다. On the other hand, polymer cement mortar is widely used in repair work for repairing and reinforcing the base plate of bridges, road surfaces of roads, and areas where corrosion or erosion occurs frequently in the lower part of the bridge.

초조강 포틀랜드 시멘트는 보통 포틀랜드 시멘트에 비하여 경화시간이 빠르고 초기 강도 발현 등의 우수한 장점이 있는 데 반하여, 원활한 작업시간 확보를 위해 산계 지연제 및 시멘트 조성물이 포함하고 있는 석고를 통해 수화를 억제함으로써, 오히려 과도한 경화 시간 지연 및 내구성 저하 등의 문제가 초래되고 있다. Super-strength Portland cement has excellent advantages such as faster curing time and initial strength expression compared to normal Portland cement, but by inhibiting hydration through gypsum containing acid-based retardant and cement composition to secure smooth working time, Rather, problems such as excessive curing time delay and reduced durability are caused.

즉, 시멘트는 물과 만나 수화 과정을 통해 구조체를 형성하고 이를 통해 내구성을 가지는 물질로서, 수화 과정은 크게 응결과 경화 과정으로 나눌 수 있다. 시멘트를 물로 반죽하면 시멘트를 구성하는 화합물은 곧 수화를 시작하고, 수화가 진행되면서 점차 굳어진다.That is, cement meets with water to form a structure through a hydration process and is a material having durability through this, and the hydration process can be largely divided into a setting process and a hardening process. When cement is kneaded with water, the compounds constituting the cement immediately begin to hydrate and gradually harden as the hydration proceeds.

속경형 시멘트는 시멘트의 성분 중 가장 빠르게 수화하는 C3A (Ca3Al2O6, 3CaO·Al2O3)가 주를 이를 이루고 있다. 원활한 작업시간 확보를 위해 산계 지연제 및 시멘트 조성물이 포함하고 있는 석고를 통해 C3A의 수화를 억제하고 있다. C 3 A (Ca 3 Al 2 O 6 , 3CaO·Al 2 O 3 ), which hydrates the fastest among cement components, is the main component of fast-setting cement. Hydration of C 3 A is suppressed through the acid-based retardant and gypsum contained in the cement composition to ensure smooth working time.

그러나, 이러한 방법은 1) 시멘트 반응을 강제로 저해하여 응결 시간을 과도하게 늘리는 방법으로서, 시멘트 수화물의 생성을 억제하고 응결 시간(작업 시간) 확보와 비교하여 과도하게 경화 시간이 지연되는 부작용이 생겨 결과적으로 내구성 저하로 이어질 수 있으며, 2) 속경형 시멘트를 결합재로 사용하는 경우 반죽할 때 급격히 가소성을 잃고 굳는 이상 응결 현상이 빈번히 발생하며, 이를 제어하기 위하여 산계 지연제를 사용하지만 이는 콘크리트의 반응을 일시적으로 억제하여 지연 효과를 발생시키는 방법으로서 결과적으로 수화물의 절대량이 줄어들어 내구성 및 역학 특성에 악영향을 미칠 수 있다.However, this method is a method of excessively prolonging the setting time by 1) forcibly inhibiting the cement reaction, and has the side effect of suppressing the formation of cement hydrate and excessively delaying the setting time compared to securing the setting time (working time). As a result, it may lead to a decrease in durability. 2) When fast-diameter cement is used as a binder, abnormal setting occurs frequently, which rapidly loses plasticity and hardens during kneading. To control this, an acid-based retardant is used, but it As a method of generating a delay effect by temporarily suppressing

따라서, 속경형 시멘트 조성물에 있어서, 산계 지연제의 사용량을 증가시키지 않더라도 원활한 작업시간을 확보할 수 있으며, 우수한 작업성을 발현할 수 있는 속경형 시멘트 조성물의 연구가 필요한 실정이다.Therefore, in the fast-setting cement composition, it is necessary to study a fast-setting cement composition capable of securing a smooth working time and exhibiting excellent workability even without increasing the amount of the acid-based retarder.

한국등록특허 제10-1819478호Korean Patent Registration No. 10-1819478

따라서, 본 발명에서 해결하고자 하는 기술적 과제는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 제공하기 위한 것이다.Accordingly, the technical problem to be solved in the present invention is to provide a fast-diameter cement concrete composition having excellent workability and durability.

또한, 본 발명에서 해결하고자 하는 다른 기술적 과제는 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 이용한 도로 포장 보수공법을 제공하기 위한 것이다.In addition, another technical problem to be solved in the present invention is to provide a road pavement repair method using the fast-diameter cement concrete composition having excellent workability and durability.

상기한 기술적 과제를 해결하기 위하여, 본 발명에서는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물로서, 성능 개선 결합재 3∼40 중량%, 잔골재 5∼70 중량%, 굵은골재 5∼65 중량%, 라텍스 합성 폴리머 1~34 중량% 및 물 0.1∼30 중량%를 포함하며, 상기 성능 개선 결합재는, 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트 10∼70 중량%, 칼슘 또는 마그네슘 설포알루미네이트 3∼40 중량%, 칼슘 또는 마그네슘 알루미나 시멘트 0.1∼30 중량%, 무수석고, 반수석고 및 이수석고 중 어느 하나 이상인 석고 0.1∼20 중량%, 소석회 및 생석회 중 어느 하나 이상인 활성 촉진제 1.0 ~ 10.0 중량%, 탄산리튬, 황산리튬 및 수산화리튬 중 어느 하나 이상인 경화 촉진제 0.01~10 중량%, 나프탈렌계, 멜라민계 및 폴리카르본산계 중 어느 하나 이상인 감수제 0.1~5.0 중량%, 애터풀자이트(Attapulgite) 1.0~5.0 중량%, 및 구연산, 주석산 및 글루콘산 중 어느 하나 이상인 지연제 0.1∼5.0 중량%를 포함하며, 상기 혼합 시멘트의 분말 입자는 입도 분포(Particle Size Distribution)에 있어서, 1.50 ≤D90/D50≤ 1.55를 만족하며, 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)는 1.0 μm ≤σ≤ 3.0 μm를 만족하는 것을 특징으로 하는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 제공한다.In order to solve the above technical problem, in the present invention, as a fast-diameter cement concrete composition having excellent workability and durability, 3 to 40 wt% of a performance-improving binder, 5 to 70 wt% of fine aggregate, 5 to 65 wt% of coarse aggregate, and latex 1 to 34% by weight of a synthetic polymer and 0.1 to 30% by weight of water, and the performance-improving binder is usually 10 to 70% by weight of mixed cement mixed with Portland cement and microcement having a fineness of 6,000 cm2/g or more, calcium or 3 to 40 wt% of magnesium sulfoaluminate, 0.1 to 30 wt% of calcium or magnesium alumina cement, 0.1 to 20 wt% of gypsum at least any one of anhydrite, hemihydrite and dihydrate gypsum, slaked lime and quicklime at least one activity promoter 1.0 ~ 10.0% by weight, 0.01 to 10% by weight of a curing accelerator at least one of lithium carbonate, lithium sulfate and lithium hydroxide, 0.1 to 5.0% by weight of a water reducing agent at least one of naphthalene, melamine, and polycarboxylic acid, attapulgite ( Attapulgite) 1.0 to 5.0% by weight, and 0.1 to 5.0% by weight of a retarder of any one or more of citric acid, tartaric acid and gluconic acid, wherein the powder particles of the mixed cement have a particle size distribution of 1.50 ≤ D90 /D50≤1.55, and the standard deviation (σ) of the total powder particle size of the mixed cement is 1.0 μm ≤ σ≤ 3.0 μm To provide a fast-diameter cement concrete composition with excellent workability and durability do.

상기 혼합 시멘트에서 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트는 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부를 포함하는 것을 특징으로 한다.In the mixed cement, the micro cement having a fineness of 6,000 cm 2 /g or more is characterized in that it contains 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement.

상기 혼합 시멘트는 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부를 포함하는 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 더 포함할 수 있다.The mixed cement may further include crude Portland cement having a fineness of 4,500 cm 2 /g or more including 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement.

상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)의 함량비는 3:1인 점도 조절제 0.1 중량% 내지 1.0 중량%를 더 포함하는 것을 특징으로 한다.The fast-diameter cement concrete composition having excellent workability and durability includes polyether modified polydimethylsiloxane and polyglycol, and the polyether modified polydimethylsiloxane and polyglycol ( Polyglycol) content ratio of 3:1 is characterized in that it further comprises 0.1 wt% to 1.0 wt% of a viscosity modifier.

상기 점도 조절제는 알코올 알콕시레이트(Alcohol alkoxylates)를 더 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane) 및 폴리 글리콜 (Polyglycol)을 포함하는 성분과 상기 알코올 알콕시레이트(Alcohol alkoxylates)를 포함하는 성분의 함량비가 1:1인 것을 특징으로 한다.The viscosity modifier further includes alcohol alkoxylates, and a component including the polyether modified polydimethylsiloxane and polyglycol and the alcohol alkoxylates. It is characterized in that the content ratio of the components is 1:1.

또한, 본 발명에서는 상기한 다른 기술적 과제를 해결하기 위하여, 하기 단계를 포함하는 것을 특징으로 하는 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 이용한 도로 포장 보수 공법을 제공한다.In addition, the present invention provides a road pavement repair method using the fast-diameter cement concrete composition excellent in workability and durability, comprising the following steps in order to solve the other technical problems described above.

콘크리트 구조물의 열화된 부위 및 아스팔트 콘크리트를 노면 파쇄기를 이용하여 제거하는 단계와, 제거된 부위를 워터젯, 고압세척기, 핸드 워터젯 등으로 열화된 부위까지 제거한 후 진공흡입차량으로 청소하는 단계와, 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물이 구체 콘크리트에 부착되기 용이하게 하고 표층강화, 유해물질, 물, 염소이온 등의 침투를 억제하고 내수성을 개선하기 위하여 상기 청소된 부위에 프라이머 또는 블루밍 처리를 하는 단계와, 상기 프라이머 또는 블루밍이 처리 된 상부에 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 타설하여 열화된 부위의 단면을 보수 또는 보강하는 단계와, 타설된 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 표면의 미끄럼 저항성을 개선시키기 위하여 종·횡방향의 타이닝을 실시하는 단계; 및 상기 타이닝된 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 상부에 수분 증발을 방지하여 소성균열을 억제하기 위하여 피막 양생제를 도포하는 단계를 포함한다.The steps of removing the deteriorated part of the concrete structure and the asphalt concrete using a scarifier, removing the removed part to the degraded part with a water jet, a high pressure washer, a hand water jet, etc. and then cleaning with a vacuum suction vehicle; Primer or blooming treatment is applied to the cleaned area to facilitate adhesion of the fast-setting cement concrete composition with excellent properties and durability to concrete concrete, to strengthen the surface layer, to suppress the penetration of harmful substances, water, chlorine ions, etc., and to improve water resistance. and pouring the fast-diameter cement concrete composition excellent in workability and durability on the top treated with the primer or blooming to repair or reinforce the cross section of the deteriorated area, and the poured excellent workability and durability performing longitudinal and transverse tinting to improve the slip resistance of the surface of the fast-diameter cement concrete composition; and applying a film curing agent to the top of the tinned fast-diameter cement concrete composition having excellent workability and durability to suppress plastic cracks by preventing moisture evaporation.

본 발명에 의하면, 성능 개선 결합재를 사용함으로써 콘크리트의 작업성 및 시공성을 향상시킬 수 있고, 콘크리트의 인성 및 부착강도를 개선하며, 수축을 저감시켜 수축 균열을 방지하고 내구성을 개선시킨다. 또한, 포졸란 반응에 의하여 수화 및 내부 조직의 치밀화를 촉진하여 밀실한 콘크리트를 만들 수 있어 콘크리트의 강도 및 내구성, 특히 방수성, 내식성을 개선할 수 있다. According to the present invention, it is possible to improve the workability and constructability of concrete by using the performance-improving binder, improve the toughness and adhesion strength of concrete, and reduce shrinkage to prevent shrinkage cracking and improve durability. In addition, by promoting hydration and densification of internal tissues by the pozzolan reaction, tight concrete can be made, thereby improving the strength and durability of concrete, in particular, waterproofness and corrosion resistance.

특히, 본 발명의 일 실시형태에 따르면, 성능 개선 결합재가 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트 10∼70 중량%를 포함하고, 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부로 포함됨으로써, 지연제의 증량 없이도 충분한 응결 시간을 확보할 수 있다.In particular, according to an embodiment of the present invention, the performance-improving binder contains 10 to 70 wt% of a mixed cement obtained by mixing normal Portland cement and micro cement with a fineness of 6,000 cm / g or more, and the powder has a fineness of 6,000 cm / g or more. Since the micro cement is included in an amount of 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement, it is possible to secure sufficient setting time without increasing the amount of the retarder.

또한, 본 발명의 일 실시형태에 따르면, 상기 혼합 시멘트의 분말 입자는 입도 분포(Particle Size Distribution)에 있어서, 1.50 ≤D90/D50≤ 1.55를 만족하며, 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)가 1.0 μm ≤σ≤ 3.0 μm를 만족하기 때문에, 분말 입자의 입경이 고르게 분포할 수 있어, 지연제 함량을 줄이더라도 가응결 현상을 방지할 수 있고, 적절한 입도를 구성함으로써, 베어링 효과에 의해 우수한 작업성을 발현할 수 있다.In addition, according to an embodiment of the present invention, the powder particles of the mixed cement satisfy 1.50 ≤ D90/D50 ≤ 1.55 in particle size distribution, and the standard deviation of the total powder particle size of the mixed cement Since (σ) satisfies 1.0 μm ≤ σ≤ 3.0 μm, the particle size of the powder particles can be evenly distributed, and even if the retardant content is reduced, it is possible to prevent the phenomenon of pre-condensation, and by configuring the appropriate particle size, the bearing effect excellent workability can be expressed by

종래와 같이 조강 및 초속경 시멘트 조성물의 응결시간을 지연시키기 위해 과도하게 지연제를 사용할 경우 경화 시간까지도 지연시켜 초기 강도 발현이 늦어지고, 경화전 내구성 저하 및 균열 등이 발생할 수 있었으나, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 사용할 경우, 지연제 함량을 줄이더라도 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.In the case of excessive use of a retarder to delay the setting time of the crude steel and super-velocity cement composition as in the prior art, the initial strength expression is delayed by delaying even the curing time, and deterioration of durability before hardening and cracking may occur, but the present invention When the fast-diameter cement concrete composition having excellent workability and durability according to the embodiment is used, the initial strength expression is excellent even when the content of the retarder is reduced, and problems such as reduced durability and cracks can be solved.

또한, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 점도 조절제를 포함하고 그 함량을 제어함으로써, 산계 지연제의 사용량을 증가시키지 않더라도 원활한 작업시간을 확보할 수 있으며, 우수한 작업성을 발현할 수 있고, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.In addition, the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention includes a viscosity modifier and controls its content, thereby securing smooth working time without increasing the amount of the acid-based retardant. , excellent workability can be expressed, and the initial strength expression is excellent, and problems such as durability deterioration and crack generation can be solved.

도 1은 본 발명의 실시예 1, 2 및 비교예 1, 2의 시멘트 콘크리트 조성물에 따른 관입 저항시험 그래프이다.
도 2는 본 발명의 실시예 3, 4 및 비교예 3, 4의 시멘트 콘크리트 조성물에 따른 관입 저항시험 그래프이다.
도 3은 본 발명의 실시예 1, 2 및 비교예 1, 2의 입도분포곡선을 나타내는 그래프이다.1 is a graph showing the penetration resistance test according to the cement concrete compositions of Examples 1 and 2 and Comparative Examples 1 and 2 of the present invention.
Figure 2 is a penetration resistance test graph according to the cement concrete compositions of Examples 3 and 4 and Comparative Examples 3 and 4 of the present invention.
3 is a graph showing the particle size distribution curves of Examples 1 and 2 and Comparative Examples 1 and 2 of the present invention.

본 발명의 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 성능 개선 결합재 3∼40 중량%, 잔골재 5∼70 중량%, 굵은골재 5∼65 중량%, 라텍스 합성 폴리머 1~34 중량%, 점도 조절제 0.1 중량% 내지 1.0 중량% 및 물 0.1∼30 중량%를 포함하는 것을 특징으로 한다.The fast-diameter cement concrete composition excellent in workability and durability of the present invention contains 3 to 40 wt% of a performance-improving binder, 5 to 70 wt% of fine aggregate, 5 to 65 wt% of coarse aggregate, 1 to 34 wt% of latex synthetic polymer, and a viscosity modifier It is characterized in that it contains 0.1 to 1.0% by weight and 0.1 to 30% by weight of water.

본 발명에서 사용하는 골재는 잔골재와 굵은 골재로 구분되며, 입경이 5mm 이하인 것을 잔골재라 하고 입경이 5mm 보다 큰 것을 굵은 골재로 구분한다. 잔골재는 본 발명의 점도 개선 초속경 시멘트 콘크리트 조성물에 대하여 5∼70 중량% 함유되는 것이 바람직하고, 굵은 골재는 본 발명의 점도 개선 초속경 시멘트 콘크리트 조성물에 대하여 5∼65 중량% 함유되는 것이 바람직하다. The aggregate used in the present invention is divided into fine aggregate and coarse aggregate. Those having a particle diameter of 5 mm or less are called fine aggregates, and those having a particle diameter greater than 5 mm are classified as coarse aggregates. The fine aggregate is preferably contained in an amount of 5 to 70% by weight based on the viscosity-improved cementitious velocity of the present invention, and the coarse aggregate is preferably contained in an amount of 5 to 65% by weight based on the cemented concrete composition of the present invention. .

상기 성능 개선 결합재는, 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트 10∼70 중량%, 칼슘 또는 마그네슘 설포알루미네이트 3∼40 중량%, 칼슘 또는 마그네슘 알루미나 시멘트 0.1∼30 중량%, 무수석고, 반수석고 및 이수석고 중 어느 하나 이상인 석고 0.1∼20 중량%, 소석회 및 생석회 중 어느 하나 이상인 활성 촉진제 1.0 ~ 10.0 중량%, 탄산리튬, 황산리튬 및 수산화리튬 중 어느 하나 이상인 경화 촉진제 0.01~10 중량%, 나프탈렌계, 멜라민계 및 폴리카르본산계 중 어느 하나 이상인 감수제 0.1~5.0 중량%, 애터풀자이트(Attapulgite) 1.0~5.0 중량% 및 구연산, 주석산 및 글루콘산 중 어느 하나 이상인 지연제 0.1∼5.0 중량%를 포함한다. The performance-improving binder includes 10 to 70% by weight of mixed cement mixed with normal Portland cement and microcement having a fineness of 6,000 cm2/g or more, 3 to 40% by weight of calcium or magnesium sulfoaluminate, 0.1 to 30% by weight of calcium or magnesium alumina cement % by weight, 0.1 to 20% by weight of gypsum at least any one of anhydrite, hemihydrate gypsum, and dihydrate gypsum, 1.0 to 10.0% by weight of an activity accelerator at least one of slaked lime and quicklime, curing at least any one of lithium carbonate, lithium sulfate and lithium hydroxide 0.01 to 10% by weight of an accelerator, 0.1 to 5.0% by weight of a water reducing agent at least one of naphthalene, melamine, and polycarboxylic acid, 1.0 to 5.0% by weight of Attapulgite, and any one or more of citric acid, tartaric acid and gluconic acid 0.1 to 5.0% by weight of a retarder.

상기 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트는 KS에 규정된 것을 사용하는 것이 바람직하며, 상기 성능 개선 결합재에 대하여 10∼70 중량% 함유되는 것이 바람직하다. It is preferable to use the normal Portland cement and micro cement with a fineness of 6,000 cm2/g or more as specified in the KS, and it is preferable to contain 10 to 70% by weight based on the performance-improving binder.

본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물의 성능 개선 결합재는, 종래 속경형 시멘트 콘크리트 조성물의 성능 개선 결합재와 달리 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트 10∼70 중량%를 포함하는 것을 특징으로 한다.The performance-improving binder of the fast-setting cement concrete composition having excellent workability and durability according to an embodiment of the present invention, unlike the performance-improving binder of the conventional fast-setting cement concrete composition, is different from normal Portland cement and micro cement having a fineness of 6,000 cm 2 /g or more It is characterized in that it contains 10 to 70% by weight of mixed cement mixed with

또한, 본 발명의 일 실시형태에 따르면, 상기 혼합 시멘트에서 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트는 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부를 포함한다.In addition, according to one embodiment of the present invention, in the mixed cement, the micro cement having a fineness of 6,000 cm 2 /g or more contains 50 parts by weight to 400 parts by weight based on 100 parts by weight of the ordinary Portland cement.

종래 속경형 시멘트 콘크리트 조성물은 조강 포틀랜드 시멘트로부터 CaO를 공급받고, 칼슘 또는 마그네슘 설포알루미네이트로부터 Al2O3를 공급 받아, 초기 반응시 급격한 에트린자이트의 발생으로 강도를 발현하게 된다. 이때, 속경형 시멘트의 응결 현상에 관여하는 중요한 요소는 시멘트와 물을 반죽했을 때 생성되는 Ca2+의 농도이다. The conventional fast-setting cement concrete composition receives CaO from crude steel portland cement and Al 2 O 3 from calcium or magnesium sulfoaluminate, and expresses strength due to the rapid generation of etrinzite during the initial reaction. At this time, an important factor involved in the setting of the fast-setting cement is the concentration of Ca 2+ produced when the cement and water are kneaded.

종래 속경형 시멘트 콘크리트 조성물은 보통 포틀랜드 시멘트와 다르게 초기 급격한 에트린자이트의 생성을 유도하기 위하여 C3A의 공급원인 칼슘 또는 마그네슘 설포알루미네이트 또는 알루미나 시멘트(CA: Calcium Aluminate cement)를 주요 원료로 사용하고 있다.The conventional fast-setting cement concrete composition uses calcium or magnesium sulfoaluminate or alumina cement (CA: Calcium Aluminate cement), which is a source of C 3 A, as the main raw material in order to induce rapid initial formation of ethringite, unlike normal Portland cement. are using

따라서, 충분한 가사 시간(작업 시간)을 확보하기 위해 불가피하게 산계 지연제를 사용하여 가사 시간을 확보하고 있다.Therefore, in order to secure a sufficient pot life (working time), the pot life is inevitably secured by using an acid-based retarder.

그러나, 산계 지연제를 사용하여 가사 시간을 확보하는 상기 방법은 1) 시멘트 반응을 강제로 저해하여 응결 시간을 과도하게 늘리는 방법으로서, 시멘트 수화물의 생성을 억제하고 응결 시간(작업 시간) 확보와 비교하여 과도하게 경화 시간이 지연되는 부작용이 생겨 결과적으로 내구성 저하로 이어질 수 있으며, 2) 속경형 시멘트를 결합재로 사용하는 경우 반죽할 때 급격히 가소성을 잃고 굳는 이상 응결 현상이 빈번히 발생하며, 이를 제어하기 위하여 산계 지연제를 사용하지만 이는 콘크리트의 반응을 일시적으로 억제하여 지연 효과를 발생시키는 방법으로서 결과적으로 수화물의 절대량이 줄어들어 내구성 및 역학 특성에 악영향을 미칠 수 있다.However, the above method of securing pot life using an acid-based retarder is 1) a method of excessively increasing the setting time by forcibly inhibiting the cement reaction, which is compared with suppressing the formation of cement hydrate and securing setting time (working time). As a result, the side effect of excessively delaying the curing time can occur, which can lead to a decrease in durability. To this end, an acid-based retardant is used, but this is a method that temporarily suppresses the reaction of concrete to generate a retardation effect. As a result, the absolute amount of hydrate is reduced, which may adversely affect durability and mechanical properties.

또한, 종래의 속경형 시멘트 콘크리트 조성물은 물과 반죽하는 경우에 발생하는 Ca2+ 이온의 농도가 낮아 가응결 현상이 빈번히 발생하고, 이로 인하여 작업성 저하의 문제가 있었다. In addition, the conventional fast-setting cement concrete composition has a low concentration of Ca 2+ ions that are generated when kneading with water, so that a temporary setting phenomenon frequently occurs, thereby reducing workability.

상기 가응결 현상은 Ca2+ 이온의 농도가 낮아 발생하는 현상으로서, 시멘트에 물을 가하고 있을 때 또는 그 직후에 정상적으로 수화작용에 따르지 않고 일시적으로 응결한 것 같은 혹은 경화된 상태를 나타내는 현상을 말한다. The temporary setting phenomenon is a phenomenon that occurs due to a low concentration of Ca 2+ ions, and refers to a phenomenon that does not follow normal hydration when water is added to cement or immediately after it is temporarily condensed or shows a hardened state. .

본 발명은 상기 문제를 해결하기 위하여 안출된 것으로서, 지연제의 증량 없이도 충분한 응결 시간을 확보할 수 있다.The present invention has been devised to solve the above problem, and it is possible to secure a sufficient setting time without increasing the amount of the retarder.

즉, 본 발명의 일 실시형태에 따르면, 성능 개선 결합재가 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트 10∼70 중량%를 포함하고, 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부로 포함됨으로써, 지연제의 증량 없이도 충분한 응결 시간을 확보할 수 있다.That is, according to one embodiment of the present invention, the performance-improving binder contains 10 to 70% by weight of mixed cement obtained by mixing normal Portland cement and micro cement with a fineness of 6,000 cm / g or more, and the powder has a fineness of 6,000 cm / g or more. Since the micro cement is included in an amount of 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement, it is possible to secure sufficient setting time without increasing the amount of the retarder.

또한, 종래와 같이 조강 및 초속경 시멘트 조성물의 응결시간을 지연시키기 위해 과도하게 지연제를 사용할 경우 경화 시간까지도 지연시켜 초기 강도 발현이 늦어지고, 경화전 내구성 저하 및 균열 등이 발생할 수 있었으나, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 사용할 경우, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.In addition, when excessively used to delay the setting time of the crude steel and super-velocity cement composition as in the prior art, the initial strength expression is delayed by delaying even the curing time, and deterioration of durability before hardening and cracking may occur. When using the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention, it is possible to solve problems such as excellent initial strength expression and reduced durability and cracks.

또한, 본 발명의 일 실시형태에 따르면 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트, 특히 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부로 포함됨으로써, 시멘트 분말 입자의 비표면적을 높여 Ca2+ 이온의 농도를 빠르게 높임으로써, 가응결 현상을 방지하고 적절한 입도를 구성함으로써, 베어링 효과에 의해 우수한 작업성을 발현할 수 있다. In addition, according to an embodiment of the present invention, a mixed cement obtained by mixing ordinary Portland cement and microcement having a fineness of 6,000 cm2/g or more, in particular, microcement having a fineness of 6,000 cm2/g or more, is used with respect to 100 parts by weight of the ordinary Portland cement. By being included in 50 to 400 parts by weight, the specific surface area of the cement powder particles is increased to rapidly increase the concentration of Ca 2+ ions, thereby preventing the phenomenon of temporary setting and configuring an appropriate particle size, thereby exhibiting excellent workability due to the bearing effect. can do.

상기 보통 포틀랜드 시멘트는 분말도가 3,200 ㎠/g 정도로서, 보통 포틀랜드 시멘트만 사용하고 속경형 결합재 추가를 통해 초속경 (타설 후 4시간 21 MPa 강도 발현) 및 조강 (타설 후 12시간 21 KPa 강도 발현)시멘트 조성물을 구현할 경우 과도한 지연제가 필요하게 되고, 과도하게 지연제를 사용할 경우 경화 시간까지도 지연시켜 초기 강도 발현이 늦어지고, 경화전 내구성 저하 및 균열 등이 발생할 수 있어 문제가 있다.The normal Portland cement has a fineness of about 3,200 ㎠/g, and only ordinary Portland cement is used and the super-fast diameter (21 MPa strength is developed at 4 hours after pouring) and crude steel (21 KPa strength is developed for 12 hours after pouring) through the addition of a fast-diameter binder. When the cement composition is implemented, an excessive retarder is required, and when the retarder is used excessively, even the curing time is delayed, so that the initial strength expression is delayed, and there is a problem in that durability before hardening and cracks may occur.

상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 미만으로 포함될 경우에는, 비표면적이 높은 마이크로 시멘트의 함량이 적어 가응결 현상이 발생하여 작업성이 저하될 수 있으며, 초기 강도 발현이 늦어져 공용중인 도로에 타설시 진동으로 인하여 경화전 데미지를 입을 수 있다.When the fineness of the micro cement of 6,000 cm2/g or more is included in less than 50 parts by weight based on 100 parts by weight of the normal Portland cement, the content of micro cement with a high specific surface area is small, so that the workability may be deteriorated due to the occurrence of a temporary setting phenomenon. Also, the initial strength development is delayed, and damage before hardening can occur due to vibration when pouring on a public road.

상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 400 중량부를 초과하여 포함될 경우, 비표면적 증가로 Ca2+ 이온의 농도를 빠르게 높임으로써, 가응결 현상을 방지할 수 있으나, 상기 마이크로 시멘트를 과량 사용할 경우 재료 단가가 상승하는 문제가 있다.When the fineness of the micro cement of 6,000 cm 2 / g or more is contained in excess of 400 parts by weight based on 100 parts by weight of the normal Portland cement, the concentration of Ca 2+ ions is increased rapidly by increasing the specific surface area, thereby preventing temporary setting. However, when the micro cement is used in excess, there is a problem in that the material cost increases.

본 발명의 일 실시형태에 따르면, 상기 혼합 시멘트는 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부를 포함하는 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 더 포함할 수 있다.According to an embodiment of the present invention, the mixed cement may further include crude Portland cement having a fineness of 4,500 cm 2 /g or more, including 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement.

본 발명은 보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트가 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 더 포함하고, 특히 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부로 포함하고, 상기 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부 포함함으로써, 시멘트 분말 입자의 비표면적을 높여 Ca2+ 이온의 농도를 빠르게 높임으로써, 가응결 현상을 방지하고 적절한 입도를 구성함으로써, 베어링 효과에 의해 우수한 작업성을 발현할 수 있다.According to the present invention, the mixed cement obtained by mixing ordinary Portland cement and micro cement having a fineness of 6,000 cm / g or more further includes crude Portland cement having a fineness of 4,500 cm / g or more, and in particular, the micro cement having a fineness of 6,000 cm / g or more is the above. By including 50 to 400 parts by weight based on 100 parts by weight of ordinary Portland cement, and 50 to 400 parts by weight of crude Portland cement having a fineness of 4,500 cm 2 /g or more based on 100 parts by weight of the ordinary Portland cement, cement By increasing the specific surface area of the powder particles and rapidly increasing the concentration of Ca 2+ ions, the phenomenon of provisional condensing is prevented and an appropriate particle size is formed, thereby exhibiting excellent workability due to the bearing effect.

또한, 지연제를 과도하게 사용하지 않아도 우수한 작업성을 발현할 수 있기 때문에, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다. In addition, since excellent workability can be expressed without excessive use of the retarder, the initial strength expression is excellent, and problems such as durability deterioration and crack generation can be solved.

상기 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 미만으로 포함될 경우에는, 비표면적이 높은 조강 포틀랜드 시멘트의 함량이 적어 가응결 현상이 발생하여 작업성이 저하될 수 있으며, 초기 강도 발현이 늦어져 공용중인 도로에 타설시 진동으로 인하여 경화전 데미지를 입을 수 있다.When the crude Portland cement having a fineness of 4,500 cm 2 /g or more is included in an amount of less than 50 parts by weight based on 100 parts by weight of the normal Portland cement, the content of the crude Portland cement having a high specific surface area is small, so that a temporary setting phenomenon occurs and workability is reduced. It may be lowered, and the initial strength development may be delayed, and damage may occur before hardening due to vibration when pouring on a public road.

상기 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트가 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 400 중량부를 초과하여 포함될 경우, 비표면적 증가로 Ca2+ 이온의 농도를 빠르게 높임으로써, 가응결 현상을 방지할 수 있으나, 상기 조강 포틀랜드 시멘트를 과량 사용할 경우 재료 단가가 상승하는 문제가 있다.When the crude Portland cement with a fineness of 4,500 cm 2 / g or more is included in excess of 400 parts by weight based on 100 parts by weight of the normal Portland cement, by increasing the concentration of Ca 2+ ions rapidly by increasing the specific surface area, it is possible to prevent the phenomenon of pre-setting. However, if the crude Portland cement is used in excess, there is a problem in that the material cost increases.

본 발명의 일 실시형태에 따르면, 상기 혼합 시멘트의 분말 입자는 입도 분포(Particle Size Distribution)에 있어서, 1.50 ≤D90/D50≤ 1.55를 만족하며, 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)는 1.0 μm ≤σ≤ 3.0 μm를 만족하는 것을 특징으로 한다. 바람직하게는 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)는 2.0 μm ≤σ≤ 2.7 μm를 만족할 수 있다.According to one embodiment of the present invention, the powder particles of the mixed cement satisfy 1.50 ≤ D90/D50 ≤ 1.55 in particle size distribution, and the standard deviation (σ) of the total powder particle diameter of the mixed cement. ) is characterized in that 1.0 μm ≤σ≤ 3.0 μm. Preferably, the standard deviation (σ) of the total powder particle diameter of the mixed cement may satisfy 2.0 μm ≤ σ≤ 2.7 μm.

상기 혼합 시멘트의 분말 입자는 입도 분포(Particle Size Distribution)에 있어서, 1.50 ≤D90/D50≤ 1.55를 만족하기 때문에, 분말 입자의 입경이 고르게 분포할 수 있어, 지연제 함량을 줄이더라도 가응결 현상을 방지할 수 있고, 적절한 입도를 구성함으로써, 베어링 효과에 의해 우수한 작업성을 발현할 수 있다.Since the powder particles of the mixed cement satisfy 1.50 ≤ D90/D50 ≤ 1.55 in the particle size distribution, the particle size of the powder particles can be evenly distributed, so that even if the retardant content is reduced, the pre-setting phenomenon is prevented. It can be prevented, and by comprising an appropriate particle size, excellent workability can be expressed by the bearing effect.

상기 혼합 시멘트의 분말 입자는 입도 분포(Particle Size Distribution)에 있어서, D90/D50의 값이 1.50 미만일 경우에는 더욱 우수한 작업성을 얻을 수 있으나, 상기 값을 만족하기 위하여 과도한 사전 작업 및 비용이 소요되는 문제가 있고, D90/D50의 값이 1.55를 초과하는 경우에는 입도 분포가 고르지 못하기 때문에, 가응결 현상이 발생할 수 있고, 작업성이 저하되는 문제가 있다. 또한, 작업성 향상을 위해 지연제 함량을 증가시킬 경우 초기 강도 발현이 늦어져 공용중인 도로에 타설시 진동으로 인하여 경화전 데미지를 입을 수 있다.In the particle size distribution of the powder particles of the mixed cement, when the value of D90/D50 is less than 1.50, better workability can be obtained, but excessive pre-work and cost are required to satisfy the value. There is a problem, and when the value of D90/D50 exceeds 1.55, since the particle size distribution is uneven, there is a problem that a temporary setting phenomenon may occur and workability is deteriorated. In addition, if the content of the retarder is increased to improve workability, the initial strength expression is delayed, and damage before hardening may be caused due to vibration when pouring on a public road.

또한, 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)는 1.0 μm ≤σ≤ 3.0 μm를 만족하기 때문에, 분말 입자의 입경의 편차가 작아, 지연제 함량을 줄이더라도 가응결 현상을 방지할 수 있고, 베어링 효과에 의해 우수한 작업성을 발현할 수 있다.In addition, since the standard deviation (σ) of the total powder particle size of the mixed cement satisfies 1.0 μm ≤ σ ≤ 3.0 μm, the variation in the particle size of the powder particles is small, and even if the retarder content is reduced, it is possible to prevent the phenomenon of temporary setting. and excellent workability can be expressed by the bearing effect.

상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)가 1.0 μm 미만일 경우에는 더욱 우수한 작업성을 얻을 수 있으나, 상기 값을 만족하기 위하여 과도한 사전 작업 및 비용이 소요되는 문제가 있고, 3.0 μm를 초과하는 경우에는 입도 분포가 고르지 못하기 때문에, 가응결 현상이 발생할 수 있고, 작업성이 저하되는 문제가 있다. 또한, 작업성 향상을 위해 지연제 함량을 증가시킬 경우 초기 강도 발현이 늦어져 공용중인 도로에 타설시 진동으로 인하여 경화전 데미지를 입을 수 있다.When the standard deviation (σ) of the total powder particle size of the mixed cement is less than 1.0 μm, better workability can be obtained, but there is a problem that excessive pre-work and cost are required to satisfy the above value, and 3.0 μm When it exceeds, since the particle size distribution is not even, there is a problem that a temporary setting phenomenon may occur, and workability is deteriorated. In addition, if the content of the retarder is increased to improve workability, the initial strength expression is delayed, and damage before hardening may be caused due to vibration when pouring on a public road.

특히, 바람직하게 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)는 2.0 μm ≤σ≤ 2.7 μm를 만족할 경우, 가응결 현상 방지 효과와 작업성 향상 효과가 보다 우수할 수 있다. 이로 인하여, 지연제 함량을 줄이더라도 우수한 작업성을 발현할 수 있기 때문에, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.In particular, preferably, when the standard deviation (σ) of the total powder particle diameter of the mixed cement satisfies 2.0 μm ≤ σ≤ 2.7 μm, the effect of preventing temporary setting and improving workability may be more excellent. For this reason, since excellent workability can be expressed even when the content of the retarder is reduced, the initial strength expression is excellent, and problems such as durability deterioration and crack generation can be solved.

상기 성능 개선 결합재는, 칼슘 또는 마그네슘 설포알루미네이트 3∼40 중량%를 포함한다.The performance-improving binder comprises 3 to 40% by weight of calcium or magnesium sulfoaluminate.

상기 칼슘 또는 마그네슘 설포알루미네이트의 중량비가 증가하면 빠른 경화특성을 나타낸다. 상기 칼슘 또는 마그네슘 설포알루미네이트는 상기 성능 개선 결합재에 대하여 3∼40 중량% 함유되는 것이 바람직하다. 상기 칼슘 또는 마그네슘 설포알루미네이트의 함량이 3 중량% 미만일 경우에는 콘크리트 강도 개선 효과 및 균열발생 억제 효과가 미약할 수 있고, 상기 칼슘 또는 마그네슘 설포알루미네이트의 함량이 40 중량%를 초과할 경우에는 조기 강도 발현은 우수하나 작업성 불량 및 제조원가가 높아져 경제적이지 못하다.When the weight ratio of the calcium or magnesium sulfoaluminate increases, it exhibits fast curing properties. The calcium or magnesium sulfoaluminate is preferably contained in an amount of 3 to 40% by weight based on the performance-improving binder. When the content of calcium or magnesium sulfoaluminate is less than 3% by weight, the effect of improving concrete strength and inhibiting cracking may be weak, and when the content of calcium or magnesium sulfoaluminate exceeds 40% by weight, premature aging Although the strength expression is excellent, it is not economical due to poor workability and high manufacturing cost.

상기 성능 개선 결합재는, 칼슘 또는 마그네슘 알루미나 시멘트 0.1∼30 중량%를 포함한다.The performance-improving binder includes 0.1 to 30% by weight of calcium or magnesium alumina cement.

상기 알루미나 시멘트는 초기 강도 발현 및 수축 방지를 위하여 사용한다. 상기 알루미나 시멘트는 조직을 치밀하게 하여 콘크리트의 균열을 방지하고 콘크리트의 수축을 방지하기 위하여 사용한다. 상기 알루미나 시멘트는 상기 성능 개선 결합재에 대하여 0.1∼30 중량% 함유되는 것이 바람직하다. 상기 알루미나 시멘트는 중량비가 증가하면 빠른 경화 특성을 나타내며, 상기 알루미나 시멘트의 함량이 상기 성능 개선 결합재에 대하여 0.1 중량% 미만일 경우 콘크리트 초기 강도 및 균열 발생 억제 효과가 미약할 수 있고, 상기 알루미나 시멘트의 함량이 30 중량%를 초과할 경우에는 빠른 경화 특성으로 인해 좋은 물성을 얻을 수 있으나 제조 원가가 높아져 경제적이지 못하다. The alumina cement is used to develop initial strength and prevent shrinkage. The alumina cement is used to prevent cracks in concrete and to prevent shrinkage of concrete by making the structure dense. The alumina cement is preferably contained in an amount of 0.1 to 30% by weight based on the performance-improving binder. The alumina cement exhibits rapid hardening properties when the weight ratio is increased, and when the content of the alumina cement is less than 0.1% by weight based on the performance-improving binder, the initial strength of concrete and the effect of inhibiting crack occurrence may be weak, and the content of the alumina cement If it exceeds 30% by weight, good physical properties can be obtained due to fast curing characteristics, but the manufacturing cost is high, which is not economical.

상기 성능 개선 결합재는 무수석고, 반수석고 및 이수석고 중 어느 하나 이상인 석고 0.1∼20 중량%를 포함한다.The performance-improving binder includes 0.1 to 20% by weight of gypsum at least one of anhydrite, hemihydrate gypsum, and dihydrate gypsum.

상기 석고는 초기 강도 발현 및 수축 방지를 위하여 사용한다. 상기 석고는 조직을 치밀하게 하여 콘크리트의 균열을 방지하고 콘크리트의 수축을 방지하기 위하여 사용한다. 상기 석고는 상기 성능 개선 결합재에 대하여 0.1∼20 중량% 함유되는 것이 바람직하다. 상기 석고의 함량이 상기 성능 개선 결합재에 대하여 0.1 중량% 미만일 경우 콘크리트 강도 및 균열 발생 억제 효과가 미약할 수 있고, 상기 석고의 함량이 20 중량%를 초과할 경우에는 빠른 경화 특성으로 인해 좋은 물성을 얻을 수 있으나 과 팽창 및 내수성이 저하된다. The gypsum is used to develop initial strength and prevent shrinkage. The gypsum is used to prevent cracks in concrete and to prevent shrinkage of concrete by making the structure dense. The gypsum is preferably contained in an amount of 0.1 to 20% by weight based on the performance-improving binder. When the content of the gypsum is less than 0.1% by weight with respect to the performance-improving binder, the concrete strength and cracking inhibitory effect may be weak. However, over-expansion and water resistance are reduced.

상기 성능 개선 결합재는 소석회 및 생석회 중 어느 하나 이상인 활성 촉진제 1.0 ~ 10.0 중량%를 포함한다.The performance-improving binder includes 1.0 to 10.0% by weight of an activity accelerator of at least one of slaked lime and quicklime.

상기 소석회 및 생석회 중 어느 하나 이상인 활성 촉진제는 초기 수화 반응시 Ca(OH)2의 농도를 높여 주어 칼슘 알루미네이트 수화물의 생성 속도를 빠르게 하는 작용을 한다. 상기 소석회 및 생석회 중 어느 하나 이상인 활성 촉진제의 함량이 1.0 중량% 미만일 경우 응결 속도 저하로 초기 강도 발현이 늦어지고, 10 중량%를 초과할 경우에는 초기에 물과 접촉하여 급속한 위 응결을 발생시키며 숏크리트의 응집을 방해하므로 숏크리트가 시공 부위에 접착되지 못하고 탈락되는 경우가 생길 수 있다. The activity promoter of at least one of slaked lime and quicklime serves to increase the concentration of Ca(OH) 2 during the initial hydration reaction to speed up the production rate of calcium aluminate hydrate. When the content of the activity promoter of any one or more of the slaked lime and quicklime is less than 1.0 wt%, the initial strength expression is delayed due to a decrease in the setting rate, and when it exceeds 10 wt%, it is initially in contact with water to cause rapid gastric setting, and shotcrete Because it interferes with the cohesion of the shotcrete, the shotcrete may not adhere to the construction site and may fall off.

상기 성능 개선 결합재는 탄산리튬, 황산리튬 및 수산화리튬 중 어느 하나 이상인 경화 촉진제 0.01~10 중량%를 포함한다. The performance-improving binder includes 0.01 to 10% by weight of a curing accelerator at least one of lithium carbonate, lithium sulfate, and lithium hydroxide.

상기 탄산리튬, 황산리튬 및 수산화리튬 중 어느 하나 이상인 경화 촉진제는 응결(종결) 이후 시멘트 수화물의 생성을 촉진하여 강도발현에 영향을 미치는 역할을 한다.The hardening accelerator at least one of lithium carbonate, lithium sulfate, and lithium hydroxide promotes the formation of cement hydrate after setting (termination), thereby affecting strength development.

상기 탄산리튬, 황산리튬, 수산화리튬 중 어느 하나 이상인 경화 촉진제 0.01 중량% 미만을 포함할 경우 강도 발현을 기대 하기 어렵고 10.0 중량%를 초과하면 에트린자이트의 과도한 형성으로 균열이 발생할 수 있다.When less than 0.01 wt% of the curing accelerator of any one or more of lithium carbonate, lithium sulfate, and lithium hydroxide is included, it is difficult to expect strength expression, and when it exceeds 10.0 wt%, cracks may occur due to excessive formation of ethrinzite.

상기 성능 개선 결합재는 나프탈렌계, 멜라민계 및 폴리카르본산계 중 어느 하나 이상인 감수제 0.1~5.0 중량%를 포함한다. The performance improvement binder includes 0.1 to 5.0% by weight of a water reducing agent at least one of naphthalene-based, melamine-based and polycarboxylic acid-based.

상기 감수제는 물-시멘트비를 감소시킴으로써 강도 및 내구성이 개선됨과 동시에 조강 시멘트의 수화반응을 지연시켜 초기 작업성을 향상시킬 수 있는 역할을 한다. 상기 감수제는 상기 성능 개선 결합재에 대하여 0.1∼5.0 중량%함유되는 것이 바람직하다. 상기 감수제는 폴리카르본산계 감수제를 사용하는 것이 바람직하다.The water reducing agent serves to improve the strength and durability by reducing the water-cement ratio, and at the same time delay the hydration reaction of the crude steel cement to improve the initial workability. The water reducing agent is preferably contained in an amount of 0.1 to 5.0% by weight based on the performance improvement binder. The water-reducing agent is preferably a polycarboxylic acid-based water-reducing agent.

본 발명의 일 실시형태에 따르면, 상기 성능 개선 결합재는 애터풀자이트(Attapulgite) 1.0~5.0 중량%를 포함한다.According to one embodiment of the present invention, the performance-improving binder comprises 1.0 to 5.0 wt% of Attapulgite.

상기 성능 개선 결합재가 애터풀자이트(Attapulgite) 1.0~5.0 중량%를 포함함으로써, 별도의 증점제를 첨가하지 않더라도 초속경 콘크리트의 유동성과 분리 저항성을 동시에 충족시켜 우수한 작업성과 강도를 확보할 수 있다.Since the performance-improving binder contains 1.0 to 5.0% by weight of Attapulgite, it is possible to secure excellent workability and strength by simultaneously satisfying the fluidity and separation resistance of ultra-high-speed concrete without adding a separate thickener.

상기 애터풀자이트(Attapulgite)의 함량이 5.0 중량%를 초과하면 성능은 개선되나, 점도가 높아져 작업성이 떨어질 수 있고, 상기 애터풀자이트(Attapulgite)의 함량이 1.0 중량% 미만이면 작업성 개선 및 강도 개선 효과가 미약할 수 있다. When the content of attapulgite exceeds 5.0 wt%, performance is improved, but workability may be deteriorated due to increased viscosity, and if the content of attapulgite is less than 1.0 wt%, workability is improved and The strength improvement effect may be weak.

상기 성능 개선 결합재는 구연산, 주석산 및 글루콘산 중 어느 하나 이상인 지연제 0.1∼5.0 중량%를 포함한다. The performance-improving binder includes 0.1 to 5.0% by weight of a retardant of at least one of citric acid, tartaric acid, and gluconic acid.

상기 지연제는 일정 시간 동안 작업성을 확보하고 급격하게 경화되는 것을 지연하기 위하여 사용될 수 있다. 상기 지연제는 상기 성능 개선 결합재에 대하여 0.1∼5.0 중량% 함유되는 것이 바람직하다. 상기 지연제로는 구연산, 주석산 및 글루콘산 중 어느 하나 이상을 사용할 수 있다. The retarder may be used to secure workability for a certain period of time and delay rapid curing. The retarder is preferably contained in an amount of 0.1 to 5.0% by weight based on the performance-improving binder. Any one or more of citric acid, tartaric acid, and gluconic acid may be used as the retarder.

상기 구연산, 주석산 및 글루콘산 중 어느 하나 이상인 지연제의 함량이 5.0 중량% 초과일 경우 초기 반응 시점이 과도하게 지연되어 강도 발현이 지연될 수 있으며, 0.1 중량% 미만일 경우 급격한 반응으로 인하여 작업이 불가능하다. If the content of any one or more of the citric acid, tartaric acid and gluconic acid is more than 5.0 wt%, the initial reaction time may be excessively delayed and the strength expression may be delayed. do.

본 발명의 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 라텍스 합성 폴리머 1~34 중량%를 포함한다.The fast-diameter cement concrete composition having excellent workability and durability of the present invention contains 1 to 34% by weight of a latex synthetic polymer.

상기 라텍스 합성 폴리머는 에멀전 형태로서 콘크리트 조성물의 응결 과정에서 시멘트 입자에 흡착하여 수화 반응이 진행됨에 따라 필름막을 형성하여 콘크리트의 물성을 개선시킨다.The latex synthetic polymer, in the form of an emulsion, is adsorbed to cement particles during the coagulation process of the concrete composition to form a film film as the hydration reaction proceeds, thereby improving the physical properties of concrete.

본 발명의 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 라텍스 합성 폴리머 1~34 중량%를 포함하는 것이 바람직하며, 1.0 중량% 미만이거나, 34 중량%를 초과하면 최종 제조된 콘크리트의 강도나 내구성이 좋지 않을 수 있다. 이 때, 본 발명에서 사용하는 라텍스 합성 폴리머의 농도는 40~60 (w/v)인 것이 바람직하다. 상기 라텍스 합성 폴리머는 약 -10℃ 내지 30℃의 유리 전이 온도(Tg)를 가지며, 바람직하게는 분자량 86.1 g/mol의 아세트산 비닐로 이루어지며, 최종 입자 크기 30 nm 내지 1500 nm 상태로 수분산된 상태이다.The fast-diameter cement concrete composition having excellent workability and durability of the present invention preferably contains 1 to 34% by weight of the latex synthetic polymer, and when it is less than 1.0% by weight or exceeds 34% by weight, the strength or durability of the final manufactured concrete This may not be good. At this time, the concentration of the latex synthetic polymer used in the present invention is preferably 40 to 60 (w/v). The latex synthetic polymer has a glass transition temperature (Tg) of about -10°C to 30°C, preferably made of vinyl acetate having a molecular weight of 86.1 g/mol, and is dispersed in water with a final particle size of 30 nm to 1500 nm. is the state

본 발명의 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 점도 조절제 0.1 중량% 내지 1.0 중량%를 포함한다.The fast-diameter cement concrete composition having excellent workability and durability of the present invention contains 0.1 wt% to 1.0 wt% of a viscosity modifier.

상기 점도 조절제는 상기 라텍스 합성 폴리머 에멀전과 함께 혼합하여 상기 시멘트 콘크리트 조성물에 포함될 수 있다.The viscosity modifier may be mixed with the latex synthetic polymer emulsion to be included in the cement concrete composition.

상기 점도 조절제는 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)의 함량비는 3:1인 것을 특징으로 한다.The viscosity modifier includes polyether modified polydimethylsiloxane and polyglycol, and the content ratio of the polyether modified polydimethylsiloxane and polyglycol is 3:1 characterized by being.

상기 점도 조절제는 알코올 알콕시레이트(Alcohol alkoxylates)를 더 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane) 및 폴리 글리콜 (Polyglycol)을 포함하는 성분과 상기 알코올 알콕시레이트(Alcohol alkoxylates)를 포함하는 성분의 함량비가 1:1인 것을 특징으로 한다.The viscosity modifier further includes alcohol alkoxylates, and a component including the polyether modified polydimethylsiloxane and polyglycol and the alcohol alkoxylates. It is characterized in that the content ratio of the components is 1:1.

상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물이 점도 조절제 0.1 중량% 내지 1.0 중량%를 포함함으로써, 라텍스 합성 폴리머 에멀전에 포함된 점도 조절제가 콘크리트 구조체의 미세 공극 내의 물의 표면 장력을 저감시켜 수용액에 의한 시멘트의 응집 현상을 개선하여 작업성을 현저하게 개선할 수 있다.Since the fast-diameter cement concrete composition excellent in workability and durability contains 0.1 wt% to 1.0 wt% of a viscosity modifier, the viscosity modifier included in the latex synthetic polymer emulsion reduces the surface tension of water in the micropores of the concrete structure to be added to the aqueous solution. It is possible to remarkably improve workability by improving the agglomeration phenomenon of cement.

본 발명과 같은 속경형 시멘트 조성물의 경우 라텍스 합성 폴리머를 포함함으로써, 부착 성능 및 내수성, 내구성을 발현할 수 있으나, 사용되는 라텍스 합성 폴리머의 높은 점도로 인하여 작업성이 저하되는 문제가 있다.In the case of a fast-diameter cement composition as in the present invention, adhesion performance, water resistance, and durability can be expressed by including the latex synthetic polymer, but there is a problem in that workability is reduced due to the high viscosity of the latex synthetic polymer used.

이러한 작업성 향상을 위해 사용하는 유동화제 및 감수제의 경우에는 시멘트 입자의 표면에 정전기적 반발력을 만들어 콘크리트의 유동성을 좋게 하지만 동시에 콘크리트의 점도가 높아지기 때문에 물/시멘트 비율에 민감해지고 미장칼에 시멘트 콘크리트 조성물이 붙는 등 작업성이 어려워지는 문제가 있다.In the case of a fluidizing agent and water reducing agent used to improve workability, it creates an electrostatic repulsive force on the surface of the cement particles to improve the fluidity of concrete, but at the same time, the viscosity of concrete increases, so it becomes sensitive to the water/cement ratio and is applied to cement concrete with a plasterer. There is a problem that the workability becomes difficult, such as sticking of the composition.

한편, 작업성 향상을 위해 사용하는 유기산계 지연제의 경우에는 응결과 함께 경화도 지연시키기 때문에 강도 발현이 늦어져서 속경형 시멘트 조성물에 과량 사용할 경우 문제가 생길 수 있다.On the other hand, in the case of an organic acid-based retarder used to improve workability, since it retards hardening together with setting, the strength expression is delayed, so that when used in an excessive amount in a fast-setting cement composition, a problem may occur.

이에 본 발명의 일 실시형태에 따르면, 점도 조절제를 적정 함량으로 포함함으로써, 물에 비해 표면 장력이 낮은 점도 조절제가 시멘트 입자의 주위에 필름막을 형성하게 되고, 이 경우 콘크리트 구조체 내의 미세 공극 내 물의 표면장력을 더욱 저감할 수 있게 된다.Accordingly, according to one embodiment of the present invention, by including the viscosity modifier in an appropriate amount, the viscosity modifier having a low surface tension compared to water forms a film film around the cement particles, and in this case, the surface of the water in the micropores in the concrete structure The tension can be further reduced.

이로 인하여, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 산계 지연제의 사용량을 증가시키지 않더라도 원활한 작업시간을 확보할 수 있으며, 우수한 작업성을 발현할 수 있고, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.For this reason, the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention can secure a smooth working time without increasing the amount of the acid-based retardant, and can exhibit excellent workability, It has excellent initial strength expression and can solve problems such as durability deterioration and cracking.

또한, 작업성 개선을 위해 감수제의 함량을 증가시키지 않더라도 작업성 개선이 가능하여 물/시멘트 비율에 대한 민감도가 낮아지고, 물의 절대적 사용량이 감소하였음에도 불구하고, 슬럼프가 감소하지 않아 이에 따른 작업성(Workability) 개선 효과를 얻을 수 있다.In addition, even if the content of the water reducing agent is not increased to improve workability, workability can be improved, so the sensitivity to the water/cement ratio is lowered, and despite the absolute amount of water used, the slump does not decrease, resulting in workability ( Workability) improvement effect can be obtained.

또한, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)의 함량비는 3:1인 점도 조절제를 포함함으로써, 작업성 개선과 더불어 역학적 특성(강도)이 증가하고, 내구성이 우수하며, 특히, 동결융해저항성 및 염소이온침투 저항성이 우수할 수 있다. In addition, the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention includes polyether-modified polydimethylsiloxane and polyglycol, and the polyether-modified polydimethylsiloxane (Polyether modified polydimethylsiloxane) and polyglycol (Polyglycol) content ratio of 3:1 contains a viscosity modifier, which improves workability and increases mechanical properties (strength), excellent durability, Chloride ion penetration resistance may be excellent.

상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물이 점도 조절제를 0.1 중량% 미만으로 포함할 경우, 작업성 개선 효과가 미비한 문제가 있으며, 점도 조절제를 1.0 중량% 초과하여 포함할 경우, 과도한 함량 사용으로 인하여 재료 분리 현상이 발생할 수 있다.When the fast-diameter cement concrete composition having excellent workability and durability contains less than 0.1 wt% of a viscosity modifier, there is a problem in that the workability improvement effect is insufficient. This may cause material separation.

한편, 본 발명의 일 실시형태에 따르면, 상기 점도 조절제는 알코올 알콕시레이트(Alcohol alkoxylates)를 더 포함할 수 있다.Meanwhile, according to an embodiment of the present invention, the viscosity modifier may further include alcohol alkoxylates.

상기 점도 조절제가 알코올 알콕시레이트(Alcohol alkoxylates)를 더 포함함으로써, 산계 지연제의 함량을 줄이더라도 원활한 작업시간을 확보할 수 있으며, 우수한 작업성을 발현할 수 있고, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.Since the viscosity modifier further includes alcohol alkoxylates, smooth working time can be secured even if the content of the acid-based retardant is reduced, excellent workability can be expressed, and initial strength expression is excellent and durability is reduced and cracks can be solved.

상기와 같이 작업성이 우수하고, 초기 강도 발현이 우수하며, 내구성 저하 및 균열 발생 등의 문제를 해결하기 위하여, 본 발명에서 바람직하게는 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane) 및 폴리 글리콜 (Polyglycol)을 포함하는 성분과 상기 알코올 알콕시레이트(Alcohol alkoxylates)를 포함하는 성분의 함량비가 1:1인 것을 특징으로 하나, 반드시 이에 제한되는 것은 아니다.As described above, in order to solve problems such as excellent workability, excellent initial strength expression, reduced durability, and cracking, in the present invention, preferably, the polyether modified polydimethylsiloxane and polyglycol It is characterized in that the content ratio of the component containing (Polyglycol) and the component containing the alcohol alkoxylates is 1:1, but is not necessarily limited thereto.

본 발명의 바람직한 실시예에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 성능 성능 개선 결합재 3∼40 중량%, 잔골재 5∼70 중량%, 굵은골재 5∼65 중량% 및 라텍스 합성 폴리머 1~34 중량% 및 점도 조절제 0.1 중량% 내지 1.0 중량%를 강제 믹서에서 교반시킨 후, 물 0.1∼30 중량%를 더 혼합하여 소정시간(예컨대, 1∼10 분) 동안 교반하여 제조할 수 있다. The fast-diameter cement concrete composition having excellent workability and durability according to a preferred embodiment of the present invention contains 3 to 40 wt% of a performance-improving binder, 5 to 70 wt% of fine aggregate, 5 to 65 wt% of coarse aggregate, and 1 to latex synthetic polymer After stirring 34 wt% and 0.1 wt% to 1.0 wt% of the viscosity modifier in a forced mixer, 0.1 to 30 wt% of water may be further mixed and stirred for a predetermined time (eg, 1 to 10 minutes).

이하에서, 본 발명의 바람직한 실시예에 따른 도로 포장 보수 공법을 설명한다. Hereinafter, a road pavement repair method according to a preferred embodiment of the present invention will be described.

본 발명의 바람직한 실시예에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 이용한 도로 포장 보수 공법은, 콘크리트 구조물의 열화된 부위 및 아스팔트 콘크리트를 노면 파쇄기를 이용하여 제거하는 단계와, 제거된 부위를 워터젯, 고압세척기, 핸드 워터젯 등으로 열화된 부위까지 제거한 후 진공흡입차량으로 청소하는 단계와, 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물이 구체 콘크리트에 부착되기 용이하게 하고 표층강화, 유해물질, 물, 염소이온 등의 침투를 억제하고 내수성을 개선하기 위하여 상기 청소된 부위에 프라이머 또는 블루밍 처리를 하는 단계와, 상기 프라이머 또는 블루밍이 처리된 상부에 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 타설하여 열화된 부위의 단면을 보수 또는 보강하는 단계와, 타설된 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 표면의 미끄럼 저항성을 개선시키기 위하여 종·횡방향의 타이닝을 실시하는 단계; 및 상기 타이닝된 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 상부에 수분 증발을 방지하여 소성균열을 억제하기 위하여 피막 양생제를 도포하는 단계를 포함한다. A road pavement repair method using a fast-diameter cement concrete composition having excellent workability and durability according to a preferred embodiment of the present invention includes the steps of removing the deteriorated portion of the concrete structure and the asphalt concrete using a scarifier, and the removed portion cleaning with a vacuum suction vehicle after removing the deteriorated parts with a water jet, high pressure washer, hand water jet, etc.; A step of applying a primer or blooming treatment to the cleaned area in order to suppress penetration of substances, water, chlorine ions, etc. and improve water resistance, and a fast-setting cement excellent in workability and durability on the top treated with the primer or blooming The step of repairing or reinforcing the cross section of the deteriorated part by pouring the concrete composition, and performing longitudinal and transverse tinting to improve the slip resistance of the poured fast-diameter cement concrete composition having excellent workability and durability. step; and applying a film curing agent to the top of the tinned fast-diameter cement concrete composition having excellent workability and durability to inhibit plastic cracking by preventing moisture evaporation.

상기 열화 부위는 철근 하부까지 제거하고, 노출된 철근의 녹을 제거하는 단계를 더 포함할 수 있다. 상기 파쇄기 및 워터젯을 이용하여 치핑하는 경우에 정상적인 경우에는 콘크리트 구조물의 철근이 노출되지 않지만 열화가 심한 경우에는 열화된 부위에서 철근이 노출될 수도 있는데, 이렇게 철근이 노출되는 경우에는 방청 처리하여야 하나 본 발명에 의하면, 별도의 철근 방청 처리는 하지 않아도 된다. The deterioration portion may further include removing the lower portion of the reinforcing bar, and removing rust of the exposed reinforcing bar. In the case of chipping using the crusher and water jet, the reinforcing bars of the concrete structure are not exposed in normal cases. However, if the deterioration is severe, the reinforcing bars may be exposed at the deteriorated area. According to the invention, it is not necessary to perform a separate anti-rust treatment for reinforcing bars.

이하에서, 본 발명에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물의 실시예들을 더욱 구체적으로 제시하며, 다음에 제시하는 실시예들에 의하여 본 발명이 한정되는 것은 아니다. Hereinafter, examples of the fast-diameter cement concrete composition excellent in workability and durability according to the present invention are presented in more detail, and the present invention is not limited by the examples presented below.

<실시예 1><Example 1>

성능 개선 결합재 20 중량%, 라텍스 합성 폴리머 5 중량%를 강제식 믹서에 투입하여 교반한 후, 물 17.35 중량%를 더 혼합하여 다시 2분간 교반하여 점도 개선 초속경 시멘트 콘크리트 조성물을 제조하였다. 20% by weight of the performance-improving binder and 5% by weight of the latex synthetic polymer were added to a forced mixer and stirred, then 17.35% by weight of water was further mixed and stirred for 2 minutes to prepare a viscosity-improved super-fast cement concrete composition.

이때, 성능 개선 결합재는 보통 포틀랜드 시멘트 15 중량% 및 분말도 6,000 ㎠/g 이상의 마이크로 시멘트 15 중량%를 혼합한 혼합 시멘트 30 중량%, 칼슘 설포알루미네이트 40 중량%, 칼슘 알루미네이트 15 중량%, 석고 7.35 중량%, 소석회 5 중량%, 탄산리튬 1.0 중량%, 감수제 0.2 중량%, 애터풀자이트(Attapulgite)와 MgO 합산 1.15 중량%, 및 지연제 0.3 중량%를 혼합하여 사용하였다. 이때, 상기 감수제는 폴리칼본산계 감수제를, 상기 지연제는 구연산계 지연제를 사용하였다. At this time, the performance-improving binder is 30 wt% of mixed cement, 40 wt% of calcium sulfoaluminate, 15 wt% of calcium aluminate, and 15 wt% of normal Portland cement and 15 wt% of micro cement with a fineness of 6,000 cm2/g or more 7.35% by weight, 5% by weight of slaked lime, 1.0% by weight of lithium carbonate, 0.2% by weight of a water reducing agent, 1.15% by weight of a total of Attapulgite and MgO, and 0.3% by weight of a retarder were mixed and used. In this case, the water reducing agent used a polycarboxylic acid-based water reducing agent, and the retarder used a citric acid-based retarding agent.

<실시예 2><Example 2>

성능 개선 결합재 20 중량%, 라텍스 합성 폴리머 5 중량%를 강제식 믹서에 투입하여 교반한 후, 물 17.35 중량%를 더 혼합하여 다시 2분간 교반하여 점도 개선 초속경 시멘트 콘크리트 조성물을 제조하였다.20% by weight of the performance-improving binder and 5% by weight of the latex synthetic polymer were added to a forced mixer and stirred, then 17.35% by weight of water was further mixed and stirred for 2 minutes to prepare a viscosity-improved super-fast cement concrete composition.

이때, 성능 개선 결합재는 보통 포틀랜드 시멘트 10 중량%, 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트 10 중량% 및 분말도 6,000 ㎠/g 이상의 마이크로 시멘트 10 중량%를 혼합한 혼합 시멘트 30 중량%, 칼슘 설포알루미네이트 40 중량%, 칼슘 알루미네이트 15 중량%, 석고 7.45 중량%, 소석회 5 중량%, 탄산리튬 1.0 중량%, 감수제 0.2 중량%, 애터풀자이트(Attapulgite)와 MgO 합산 1.15 중량%, 및 지연제 0.2 중량%를 혼합하여 사용하였다. 이때, 상기 감수제는 폴리칼본산계 감수제를, 상기 지연제는 구연산계 지연제를 사용하였다. At this time, the performance-improving binder is usually 10% by weight of Portland cement, 10% by weight of crude Portland cement with a fineness of 4,500 cm2/g or more, and 10% by weight of micro cement with a fineness of 6,000 cm2/g or more. 30% by weight of mixed cement, calcium sulfo 40% by weight of aluminate, 15% by weight of calcium aluminate, 7.45% by weight of gypsum, 5% by weight of slaked lime, 1.0% by weight of lithium carbonate, 0.2% by weight of a water reducing agent, 1.15% by weight of a sum of Attapulgite and MgO, and a retardant 0.2 wt% was mixed and used. In this case, the water reducing agent used a polycarboxylic acid-based water reducing agent, and the retarder used a citric acid-based retarding agent.

<비교예 1><Comparative Example 1>

실시예 1 및 2와 비교하여, 성능 개선 결합재 중 보통 포틀랜드 시멘트 30 중량%만을 사용한 점과 지연제를 0.5 중량% 사용한 점만 차이가 있다. 이 때, 실시예 1 또는 2와 지연제 함량 차이는 다른 첨가제 예를 들어 석고의 함량을 줄임으로써, 조성물 함량 비율을 맞추었다.Compared with Examples 1 and 2, there is a difference only in that, among the performance-improving binders, only 30 wt% of Portland cement is used and 0.5 wt% of a retarder is used. At this time, the difference in the content of the retarder from Examples 1 or 2 was adjusted by reducing the content of other additives, for example, gypsum, thereby matching the composition content ratio.

<비교예 2><Comparative Example 2>

실시예 1 및 2와 비교하여, 성능 개선 결합재 중 보통 포틀랜드 시멘트 20 중량%와 조강 보통 시멘트 10 중량%를 혼합한 혼합 시멘트 30 중량%를 사용한 점과 지연제를 0.5 중량% 사용한 점만 차이가 있다. 이 때, 실시예 1 또는 2와 지연제 함량 차이는 다른 첨가제 예를 들어 석고의 함량을 줄임으로써, 조성물 함량 비율을 맞추었다.Compared with Examples 1 and 2, there is a difference only in that 30% by weight of a mixed cement obtained by mixing 20% by weight of ordinary Portland cement and 10% by weight of crude steel ordinary cement among the performance-improving binders is used and 0.5% by weight of a retarder is used. At this time, the difference in the content of the retarder from Examples 1 or 2 was adjusted by reducing the content of other additives, for example, gypsum, thereby matching the composition content ratio.

상기 실시예 1, 2 및 비교예 1, 2의 시멘트 콘크리트 조성물은 초속경 (타설 후 4시간 21 MPa 강도 발현) 시멘트 콘크리트 조성물에 해당하며, 성능 개선 결합재는 하기 [표 1]의 조성으로 표시될 수 있다.The cement concrete compositions of Examples 1 and 2 and Comparative Examples 1 and 2 correspond to cement concrete compositions with an initial velocity (increasing strength of 21 MPa in 4 hours after pouring), and the performance-improving binder is to be represented by the composition of [Table 1] below. can

비교예1
(중량%)Comparative Example 1
(weight%) 비교예2
(중량%)Comparative Example 2
(weight%) 실시예1
(중량%)Example 1
(weight%) 실시예2
(중량%)Example 2
(weight%) 속경재
Sok Kyung-jae
 보통 포틀랜드 시멘트Normal Portland Cement 3030 2020 1515 1010 조강 시멘트crude steel cement 00 1010 00 1010 마이크로 시멘트micro cement 00 1515 1010 칼슘설포알루미네이트Calcium sulfoaluminate 4040 4040 4040 4040 칼슘알루미네이트Calcium Aluminate 1515 1515 1515 1515 석고gypsum 무수석고anhydrite 7.157.15 7.157.15 7.357.35 7.457.45 활성촉진제activator 소석회slaked lime 55 55 55 55 경화촉진제hardening accelerator 탄산리튬lithium carbonate 1.01.0 1.01.0 1.01.0 1.01.0 감수제water reducing agent 폴리카르본산계polycarboxylic acid 0.20.2 0.20.2 0.20.2 0.20.2 애터풀자이트+MgO Attapulgite + MgO 1.151.15 1.151.15 1.151.15 1.151.15 지연제retardant 구연산citric acid 0.50.5 0.50.5 0.30.3 0.20.2

도 1은 본 발명의 실시예 1, 2 및 비교예 1, 2의 시멘트 콘크리트 조성물에 따른 관입 저항시험 그래프이다.1 is a graph showing the penetration resistance test according to the cement concrete compositions of Examples 1 and 2 and Comparative Examples 1 and 2 of the present invention.

도 1을 참고하면, 본 발명의 실시예 1, 2의 경우 비교예 1, 2의 경우보다 지연제의 함량이 감소하였으나, 초기 관입저항값이 낮고 이는 초기 응결 양상이 말랑말랑한 상태를 유지할 수 있어 작업성이 매우 우수함을 알 수 있다.Referring to Figure 1, in the case of Examples 1 and 2 of the present invention, the content of the retarder was reduced compared to the case of Comparative Examples 1 and 2, but the initial penetration resistance value was low, which can maintain the initial setting state in a soft state. It can be seen that the workability is very good.

구체적으로, 도 1의 관입 저항시험은 ksf 2436 관입저항침에 의한 콘크리트의 응결시간 시험방법에 의해 수행되었으며, 본 시멘트 콘크리트 조성물이 속경성임을 감안하여 측정시간은 종결 90분을 기준으로 10분 단위로 측정하였다.Specifically, the penetration resistance test of FIG. 1 was performed by the ksf 2436 penetration resistance test method for concrete setting time. Considering that this cement concrete composition is fast-hardening, the measurement time is 10 minutes based on 90 minutes of termination. was measured with

지연제 함량은 상기 [표 1]에서와 같이 비교예 1 및 2의 경우 0.5 중량%, 실시예 1의 경우 0.3 중량% 및 실시예 2의 경우 0.2 중량%로 실시예가 비교예에 비하여 지연제를 더 소량 첨가하였다.The retarder content was 0.5 wt% in Comparative Examples 1 and 2, 0.3 wt% in Example 1, and 0.2 wt% in Example 2, as shown in Table 1 above. A smaller amount was added.

그러나, 관입 저항시험은 도 1에 도시된 바와 같이 실시예 1과 2의 경우가 초기 응결 양상이 비교예에 비하여 보다 우수하기 때문에 (초기 관입 저항값이 낮음), 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 지연제의 증량 없이도 충분한 응결 시간을 확보할 수 있음을 알 수 있다.However, in the penetration resistance test, as shown in FIG. 1 , the initial setting of Examples 1 and 2 was superior to that of Comparative Example (lower initial penetration resistance), so according to an embodiment of the present invention It can be seen that the fast-setting cement concrete composition having excellent workability and durability can secure sufficient setting time without increasing the amount of retarder.

또한, 비교예 1 및 2와 같이 종래의 초속경 시멘트 조성물의 경우 응결시간을 지연시키기 위해 과도하게 지연제를 사용하기 때문에, 경화 시간까지도 지연시켜 초기 강도 발현이 늦어지고, 경화전 내구성 저하 및 균열 등이 발생할 수 있다.In addition, as in Comparative Examples 1 and 2, in the case of the conventional super-hardening cement composition, since the retardant is excessively used to delay the setting time, the initial strength expression is delayed by delaying even the curing time, and the durability before hardening decreases and cracks etc. may occur.

그러나, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 사용할 경우, 지연제 함량을 줄일 수 있어, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.However, when using the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention, the retarder content can be reduced, so that the initial strength expression is excellent, and problems such as durability deterioration and cracking can be solved. have.

다음으로, 상기 실시예 1, 2 및 비교예 1, 2의 시멘트 콘크리트 조성물에 대하여 결합재 종류별 결합 성질을 조사하기 위하여 수화 액상 중의 Ca2+ 이온 농도를 측정하였다. 각 시료 5 g에 대하여 증류수 100 ml (w/c 비 0.5)fmf 삼각 플라스크에 넣고 밀폐하여 현탁액 상태에서 일정시간 용출 과정을 거쳤다. 각 측정시간에 해당하는 시점에서 얻어진 수용액을 1차로 여과지를 통하여 여과한 다음 감압여과장치를 이용하여 채취한 이온 용출수를 ICP (Inductively Coupled Plasma)로 특정하였다. 그 결과는 하기 [표 2]와 같다.Next, the concentration of Ca 2+ ions in the hydrated liquid was measured in order to investigate the binding properties of each type of binder for the cement concrete compositions of Examples 1 and 2 and Comparative Examples 1 and 2 . For 5 g of each sample, 100 ml of distilled water (w/c ratio 0.5) was placed in an fmf Erlenmeyer flask, sealed, and elution was carried out in a suspension state for a certain period of time. The aqueous solution obtained at the time point corresponding to each measurement time was first filtered through a filter paper, and then the ion eluted water collected using a reduced pressure filtration device was specified as ICP (Inductively Coupled Plasma). The results are shown in [Table 2] below.

비교예1
Comparative Example 1
 비교예2Comparative Example 2 실시예1Example 1 실시예2Example 2 Ca2+ 이온 용출량
(ppm)Ca 2+ ion elution amount
(ppm) 15분15 minutes 30분30 minutes 45
분45
minute 60
분60
minute 15
분15
minute 30
분30
minute 45
분45
minute 60
분60
minute 15
분15
minute 30
분30
minute 45
분45
minute 60
분60
minute 15
분15
minute 30
분30
minute 45
분45
minute 60
분60
minute
480
480
300
300
400
400
380
380
470
470
400
400
450
450
400
400
490
490
550
550
800
800
850
850
500
500
700
700
950
950
1000
1000

상기 [표 2]를 참조하면, 비교예 1 및 2에 비하여 실시예 1과 2의 경우에 시간 경과에 따른 Ca2+ 이온 농도가 더 많이 증가함을 알 수 있다.Referring to [Table 2], it can be seen that the Ca 2+ ion concentration increases more with time in Examples 1 and 2 compared to Comparative Examples 1 and 2.

즉, 비교예 1 및 2의 경우 60분 경과 Ca2+ 이온 농도가 각각 380 ppm, 400 ppm인 반면, 실시예 1의 경우 60분 경과 Ca2+ 이온 농도가 850 ppm이고, 실시예 2의 경우에는 60분 경과 Ca2+ 이온 농도가 1,000 ppm으로서, 실시예 1 및 2가 비교예 1, 2에 비하여 Ca2+ 이온 농도가 훨신 증가하였음을 알 수 있다.That is, in the case of Comparative Examples 1 and 2, the Ca 2+ ion concentration after 60 minutes was 380 ppm and 400 ppm, respectively, whereas in Example 1, the Ca 2+ ion concentration after 60 minutes was 850 ppm, in the case of Example 2 It can be seen that the Ca 2+ ion concentration was 1,000 ppm after 60 minutes, and the Ca 2+ ion concentration was much increased in Examples 1 and 2 compared to Comparative Examples 1 and 2.

비교예 1 및 2와 같이, 종래의 속경형 시멘트 콘크리트 조성물은 물과 반죽하는 경우에 발생하는 Ca2+ 이온의 농도가 낮아 가응결 현상이 빈번히 발생하고, 이로 인하여 작업성 저하의 문제가 있다. 이는 비교예 1 및 2와 같이 지연제를 실시예에 비하여 더 과량을 첨가하더라도 Ca2+ 이온의 농도가 낮기 때문에 가응결 현상을 피할 수 없고 작업성 저하가 발생하게 되는 문제가 있다.As in Comparative Examples 1 and 2, the conventional fast-diameter cement concrete composition has a low concentration of Ca 2+ ions generated when kneading with water, so that the temporary setting phenomenon frequently occurs, thereby causing a problem in workability deterioration. As in Comparative Examples 1 and 2, even when an excessive amount of the retarder is added compared to the Example, the concentration of Ca 2+ ions is low, so that the temporary coagulation phenomenon cannot be avoided and workability is deteriorated.

반면 본 발명의 실시예 1 및 2의 경우에는, 지연제를 비교예보다 적은 소량을 첨가하였음에도 Ca2+ 이온의 농도가 높아 종래의 속경형 시멘트 콘크리트 조성물인 비교예와 비교하여 가응결 문제가 없으며, 충분한 응결 시간을 확보할 수 있다.On the other hand, in the case of Examples 1 and 2 of the present invention, the concentration of Ca 2+ ions was high even though a small amount of the retarder was added compared to the comparative example, and there was no problem of provisional setting compared to the comparative example, which is a conventional fast-diameter cement concrete composition. , sufficient setting time can be ensured.

즉, 본 발명의 실시예 1의 경우 분말도가 6,000 ㎠/g 이상의 마이크로 시멘트, 실시예 2의 경우 분말도가 6,000 ㎠/g 이상의 마이크로 시멘트와 분말도가 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 보통 포틀랜드 시멘트 100 중량부 대비 각각 100 중량부 및 200 중량부를 사용함으로써, 시멘트의 비표면적을 높일 수 있으므로, 이에 따라 Ca2+ 이온의 농도를 증가시킬 수 있다.That is, in the case of Example 1 of the present invention, micro cement having a fineness of 6,000 cm2/g or more, and in Example 2, micro cement having a fineness of 6,000 cm2/g or more and crude steel Portland cement having a fineness of 4,500 cm2/g or more are usually used. By using 100 parts by weight and 200 parts by weight, respectively, relative to 100 parts by weight of Portland cement, the specific surface area of the cement can be increased, and thus the concentration of Ca 2+ ions can be increased.

끝으로, 상기 실시예 1, 2 및 비교예 1, 2의 시멘트 콘크리트 조성물에 대하여, 일반적인 콘크리트의 역학적 특성을 측정하였다. 이 결과는 하기 [표 3]과 같다. Finally, for the cement concrete compositions of Examples 1 and 2 and Comparative Examples 1 and 2, the mechanical properties of general concrete were measured. The results are shown in [Table 3] below.

비교예1Comparative Example 1 비교예2Comparative Example 2 실시예1Example 1 실시예2Example 2 압축강도
(4h, MPa)compressive strength
(4h, MPa) 21.821.8 21.521.5 22.622.6 24.524.5 휨강도 (MPa)Flexural strength (MPa) 4.524.52 4.584.58 4.604.60 4.804.80 부착강도 (MPa)Adhesive strength (MPa) 1.351.35 1.401.40 1.501.50 1.541.54

상기 [표 3]을 참조하면, 비교예 1 및 2에 비하여 본 발명의 실시예 1 및 2의 경우가 압축 강도, 휨강도 및 부착강도의 물성이 모두 더 우수함을 알 수 있다.Referring to [Table 3], it can be seen that compared to Comparative Examples 1 and 2, the properties of Examples 1 and 2 of the present invention are superior to all of the physical properties of compressive strength, flexural strength and adhesion strength.

즉, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 사용할 경우, 종래 비교예 1 및 2에 비하여 지연제의 함량을 줄였음에도 불구하고, 작업성 유지 효과는 우수하며, 경화 후 압축 강도, 휨강도 및 부착강도의 역학적 특성 모두가 우수함을 알 수 있다.That is, when the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention is used, the workability maintenance effect is excellent, although the content of the retarder is reduced compared to Comparative Examples 1 and 2 of the related art. , it can be seen that all of the mechanical properties of compressive strength, flexural strength and adhesion strength after hardening are excellent.

<실시예 3><Example 3>

성능 개선 결합재 20 중량%, 라텍스 합성 폴리머 5 중량%를 강제식 믹서에 투입하여 교반한 후, 물 17.35 중량%를 더 혼합하여 다시 2분간 교반하여 점도 개선 조강형 시멘트 콘크리트 조성물을 제조하였다.20% by weight of the performance-improving binder and 5% by weight of the latex synthetic polymer were added to a forced mixer and stirred, then 17.35% by weight of water was further mixed and stirred for 2 minutes to prepare a viscosity-improving crude steel type cement concrete composition.

이때, 성능 개선 결합재는 보통 포틀랜드 시멘트 25 중량% 및 분말도 6,000 ㎠/g 이상의 마이크로 시멘트 25 중량%를 혼합한 혼합 시멘트 50 중량%, 칼슘 설포알루미네이트 30 중량%, 칼슘 알루미네이트 5 중량%, 석고 7.75 중량%, 소석회 5 중량%, 탄산리튬 0.7 중량%, 감수제 0.1 중량%, 애터풀자이트(Attapulgite)와 MgO 합산 1.15 중량%, 및 지연제 0.3 중량%를 혼합하여 사용하였다. 이때, 상기 감수제는 폴리칼본산계 감수제를, 상기 지연제는 구연산계 지연제를 사용하였다. At this time, the performance-improving binder is 50 wt% of mixed cement, 30 wt% of calcium sulfoaluminate, 5 wt% of calcium aluminate, and 25 wt% of normal portland cement and 25 wt% of micro cement with a fineness of 6,000 cm2/g or more 7.75% by weight, 5% by weight of slaked lime, 0.7% by weight of lithium carbonate, 0.1% by weight of a water reducing agent, 1.15% by weight of a total of Attapulgite and MgO, and 0.3% by weight of a retarder were mixed and used. In this case, the water reducing agent used a polycarboxylic acid-based water reducing agent, and the retarder used a citric acid-based retarding agent.

<실시예 4><Example 4>

성능 개선 결합재 20 중량%, 라텍스 합성 폴리머 5 중량%를 강제식 믹서에 투입하여 교반한 후, 물 17.35 중량%를 더 혼합하여 다시 2분간 교반하여 점도 개선 조강형 시멘트 콘크리트 조성물을 제조하였다.20% by weight of the performance-improving binder and 5% by weight of the latex synthetic polymer were added to a forced mixer and stirred, then 17.35% by weight of water was further mixed and stirred for 2 minutes to prepare a viscosity-improving crude steel type cement concrete composition.

이때, 성능 개선 결합재는 보통 포틀랜드 시멘트 10 중량%, 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트 20 중량% 및 분말도 6,000 ㎠/g 이상의 마이크로 시멘트 20 중량%를 혼합한 혼합 시멘트 50 중량%, 칼슘 설포알루미네이트 30 중량%, 칼슘 알루미네이트 5 중량%, 석고 7.85 중량%, 소석회 5 중량%, 탄산리튬 0.7 중량%, 감수제 0.1 중량%, 애터풀자이트(Attapulgite)와 MgO 합산 1.15 중량%, 및 지연제 0.2 중량%를 혼합하여 사용하였다. 이때, 상기 감수제는 폴리칼본산계 감수제를, 상기 지연제는 구연산계 지연제를 사용하였다. At this time, the performance-improving binder is usually 10% by weight of Portland cement, 20% by weight of crude Portland cement with a fineness of 4,500 cm2/g or more, and 20% by weight of micro cement with a fineness of 6,000 cm2/g or more. 50% by weight of mixed cement, calcium sulfo 30% by weight of aluminate, 5% by weight of calcium aluminate, 7.85% by weight of gypsum, 5% by weight of slaked lime, 0.7% by weight of lithium carbonate, 0.1% by weight of a water reducing agent, 1.15% by weight of a sum of Attapulgite and MgO, and a retardant 0.2 wt% was mixed and used. In this case, the water reducing agent used a polycarboxylic acid-based water reducing agent, and the retarder used a citric acid-based retarding agent.

<비교예 3><Comparative Example 3>

실시예 3 및 4와 비교하여, 성능 개선 결합재 중 보통 포틀랜드 시멘트 50 중량%만을 사용한 점과 지연제를 0.5 중량% 사용한 점만 차이가 있다. 이 때, 실시예 3 또는 4와 지연제 함량 차이는 다른 첨가제 예를 들어 석고의 함량을 줄임으로써, 조성물 함량 비율을 맞추었다.Compared with Examples 3 and 4, there is a difference only in that, among the performance-improving binders, only 50% by weight of ordinary Portland cement is used and 0.5% by weight of a retarder is used. At this time, the difference in the content of the retarder from Examples 3 or 4 was adjusted by reducing the content of other additives, for example, gypsum, thereby matching the composition content ratio.

<비교예 4><Comparative Example 4>

실시예 3 및 4와 비교하여, 성능 개선 결합재 중 보통 포틀랜드 시멘트 40 중량%와 조강 보통 시멘트 10 중량%를 혼합한 혼합 시멘트 50 중량%를 사용한 점과 지연제를 0.5 중량% 사용한 점만 차이가 있다. 이 때, 실시예 3 또는 4와 지연제 함량 차이는 다른 첨가제 예를 들어 석고의 함량을 줄임으로써, 조성물 함량 비율을 맞추었다.Compared with Examples 3 and 4, there is a difference only in that 50% by weight of a mixed cement obtained by mixing 40% by weight of ordinary Portland cement and 10% by weight of crude steel ordinary cement among the performance-improving binders is used and 0.5% by weight of a retarder is used. At this time, the difference in the content of the retarder from Examples 3 or 4 was adjusted by reducing the content of other additives, for example, gypsum, thereby matching the composition content ratio.

상기 실시예 3, 4 및 비교예 3, 4의 시멘트 콘크리트 조성물은 조강형 (타설 후 12시간 21 MPa 강도 발현) 시멘트 콘크리트 조성물에 해당하며, 성능 개선 결합재는 하기 [표 1]의 조성으로 표시될 수 있다.The cement concrete compositions of Examples 3 and 4 and Comparative Examples 3 and 4 correspond to the crude-strength type (21 MPa strength expression 12 hours after pouring) cement concrete composition, and the performance-improving binder may be represented by the composition of [Table 1] below. have.

비교예3
(중량%)Comparative Example 3
(weight%) 비교예4
(중량%)Comparative Example 4
(weight%) 실시예3
(중량%)Example 3
(weight%) 실시예4
(중량%)Example 4
(weight%) 속경재
Sok Kyung-jae
 보통 포틀랜드 시멘트Normal Portland Cement 5050 4040 2525 1010 조강 시멘트crude steel cement 00 1010 00 2020 마이크로 시멘트micro cement 00 2525 2020 칼슘설포알루미네이트Calcium sulfoaluminate 3030 3030 3030 3030 칼슘알루미네이트Calcium Aluminate 55 55 55 55 석고gypsum 무수석고anhydrite 7.557.55 7.557.55 7.757.75 7.857.85 활성촉진제activator 소석회slaked lime 55 55 55 55 경화촉진제hardening accelerator 탄산리튬lithium carbonate 0.70.7 0.70.7 0.70.7 0.70.7 감수제water reducing agent 폴리카르본산계polycarboxylic acid 0.10.1 0.10.1 0.10.1 0.10.1 애터풀자이트+MgO Attapulgite + MgO 1.151.15 1.151.15 1.151.15 1.151.15 지연제retardant 구연산citric acid 0.50.5 0.50.5 0.30.3 0.20.2

도 2는 본 발명의 실시예 3, 4 및 비교예 3, 4의 시멘트 콘크리트 조성물에 따른 관입 저항시험 그래프이다.2 is a penetration resistance test graph according to the cement concrete compositions of Examples 3 and 4 and Comparative Examples 3 and 4 of the present invention.

도 2를 참고하면, 본 발명의 실시예 3, 4의 경우 비교예 3, 4의 경우보다 지연제의 함량이 감소하였으나, 초기 관입저항값이 낮고 이는 초기 응결 양상이 말랑말랑한 상태를 유지할 수 있어 작업성이 매우 우수함을 알 수 있다.Referring to Figure 2, in the case of Examples 3 and 4 of the present invention, the content of the retarder was decreased compared to the case of Comparative Examples 3 and 4, but the initial penetration resistance value was low, which can maintain a soft state of the initial setting pattern. It can be seen that the workability is very good.

구체적으로, 도 2의 관입 저항시험은 ksf 2436 관입저항침에 의한 콘크리트의 응결시간 시험방법에 의해 수행되었으며, 본 시멘트 콘크리트 조성물이 조강형임을 감안하여 측정시간은 종결 240분을 기준으로 30분 단위로 측정하였다.Specifically, the penetration resistance test in FIG. 2 was performed by the ksf 2436 penetration resistance test method for concrete setting time. Considering that this cement concrete composition is a crude steel type, the measurement time is 30 minutes based on the final 240 minutes. was measured with

지연제 함량은 상기 [표 4]에서와 같이 비교예 3 및 4의 경우 0.5 중량%, 실시예 3의 경우 0.3 중량% 및 실시예 4의 경우 0.2 중량%로 실시예가 비교예에 비하여 지연제를 더 소량 첨가하였다.The retarder content was 0.5 wt% in Comparative Examples 3 and 4, 0.3 wt% in Example 3, and 0.2 wt% in Example 4, as shown in Table 4 above. A smaller amount was added.

그러나, 관입 저항시험은 도 2에 도시된 바와 같이 실시예 3과 4의 경우가 초기 응결 양상이 비교예에 비하여 보다 우수하기 때문에 (초기 관입 저항값이 낮음), 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 지연제의 증량 없이도 충분한 응결 시간을 확보할 수 있음을 알 수 있다.However, in the penetration resistance test, as shown in FIG. 2 , the initial setting of Examples 3 and 4 was superior to that of Comparative Example (lower initial penetration resistance), so according to an embodiment of the present invention It can be seen that the fast-setting cement concrete composition having excellent workability and durability can secure sufficient setting time without increasing the amount of retarder.

또한, 비교예 3 및 4와 같이 종래의 조강형 시멘트 조성물의 경우 응결시간을 지연시키기 위해 과도하게 지연제를 사용하기 때문에, 경화 시간까지도 지연시켜 초기 강도 발현이 늦어지고, 경화전 내구성 저하 및 균열 등이 발생할 수 있다.In addition, as in Comparative Examples 3 and 4, in the case of the conventional crude-strength cement composition, since the retardant is excessively used to delay the setting time, the initial strength expression is delayed by delaying even the curing time, and the durability before curing and cracking, etc. This can happen.

그러나, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 사용할 경우, 지연제 함량을 줄일 수 있어, 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.However, when using the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention, the retarder content can be reduced, so that the initial strength expression is excellent, and problems such as durability deterioration and cracking can be solved. have.

다음으로, 상기 실시예 3, 4 및 비교예 3, 4의 시멘트 콘크리트 조성물에 대하여 결합재 종류별 결합 성질을 조사하기 위하여 수화 액상 중의 Ca2+ 이온 농도를 측정하였다. 각 시료 5 g에 대하여 증류수 100 ml (w/c 비 0.5)fmf 삼각 플라스크에 넣고 밀폐하여 현탁액 상태에서 일정시간 용출 과정을 거쳤다. 각 측정시간에 해당하는 시점에서 얻어진 수용액을 1차로 여과지를 통하여 여과한 다음 감압여과장치를 이용하여 채취한 이온 용출수를 ICP (Inductively Coupled Plasma)로 특정하였다. 그 결과는 하기 [표 5]와 같다.Next, the concentration of Ca 2+ ions in the hydrated liquid was measured in order to investigate the binding properties of each type of binder for the cement concrete compositions of Examples 3 and 4 and Comparative Examples 3 and 4 . For 5 g of each sample, 100 ml of distilled water (w/c ratio 0.5) was placed in an fmf Erlenmeyer flask, sealed, and elution was carried out in a suspension state for a certain period of time. The aqueous solution obtained at the time point corresponding to each measurement time was first filtered through a filter paper, and then the ion eluted water collected using a reduced pressure filtration device was specified as ICP (Inductively Coupled Plasma). The results are shown in [Table 5] below.

비교예3
Comparative Example 3
 비교예4Comparative Example 4 실시예3Example 3 실시예4Example 4 Ca2+ 이온 용출량
(ppm)Ca 2+ ion elution amount
(ppm) 30분30 minutes 60분60 minutes 90
분90
minute 120
분120
minute 30
분30
minute 60
분60
minute 90
분90
minute 120
분120
minute 30
분30
minute 60
분60
minute 90
분90
minute 120
분120
minute 30
분30
minute 60
분60
minute 90
분90
minute 120
분120
minute
650
650
660
660
670
670
660
660
700
700
750
750
780
780
720
720
735
735
770
770
900
900
1000
1000
750
750
800
800
1100
1100
1200
1200

상기 [표 5]를 참조하면, 비교예 3 및 4에 비하여 실시예 3과 4의 경우에 시간 경과에 따른 Ca2+ 이온 농도가 더 많이 증가함을 알 수 있다.즉, 비교예 3 및 4의 경우 120분 경과 Ca2+ 이온 농도가 각각 660 ppm, 720 ppm인 반면, 실시예 3의 경우 120분 경과 Ca2+ 이온 농도가 1,000 ppm이고, 실시예 4의 경우에는 120분 경과 Ca2+ 이온 농도가 1,200 ppm으로서, 실시예 3 및 4가 비교예 3, 4에 비하여 Ca2+ 이온 농도가 훨신 증가하였음을 알 수 있다.Referring to [Table 5], it can be seen that the Ca 2+ ion concentration increased more with time in Examples 3 and 4 as compared to Comparative Examples 3 and 4. That is, Comparative Examples 3 and 4 when 120 minutes, while Ca 2+ ion concentration, respectively 660 ppm, 720 ppm, example 120 minutes, Ca 2+ ion concentration of 1,000 ppm for 3 and, in the case of example 4, 120 minutes, Ca 2+ As the ion concentration was 1,200 ppm, it can be seen that the Ca 2+ ion concentration was much increased in Examples 3 and 4 compared to Comparative Examples 3 and 4.

비교예 3 및 4와 같이, 종래의 조강형 시멘트 콘크리트 조성물은 물과 반죽하는 경우에 발생하는 Ca2+ 이온의 농도가 낮아 가응결 현상이 빈번히 발생하고, 이로 인하여 작업성 저하의 문제가 있다. 이는 비교예 3 및 4와 같이 지연제를 실시예에 비하여 더 과량을 첨가하더라도 Ca2+ 이온의 농도가 낮기 때문에 가응결 현상을 피할 수 없고 작업성 저하가 발생하게 되는 문제가 있다.As in Comparative Examples 3 and 4, the conventional coarse-strength cement concrete composition has a low concentration of Ca 2+ ions generated when kneading with water, so that the temporary setting phenomenon frequently occurs, and thus there is a problem of deterioration of workability. As in Comparative Examples 3 and 4, even if an excessive amount of the retarder is added compared to the Example, the concentration of Ca 2+ ions is low, so that the temporary coagulation phenomenon cannot be avoided and workability is deteriorated.

반면 본 발명의 실시예 3 및 4의 경우에는, 지연제를 비교예보다 적은 소량을 첨가하였음에도 Ca2+ 이온의 농도가 높아 종래의 조강형 시멘트 콘크리트 조성물인 비교예와 비교하여 가응결 문제가 없으며, 충분한 응결 시간을 확보할 수 있다.On the other hand, in the case of Examples 3 and 4 of the present invention, the concentration of Ca 2+ ions was high even though a small amount of the retardant was added compared to the comparative example, and there was no problem of provisional setting compared to the comparative example, which is a conventional crude steel type cement concrete composition, Sufficient setting time can be ensured.

즉, 본 발명의 실시예 3의 경우 분말도가 6,000 ㎠/g 이상의 마이크로 시멘트, 실시예 4의 경우 분말도가 6,000 ㎠/g 이상의 마이크로 시멘트와 분말도가 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 보통 포틀랜드 시멘트 100 중량부 대비 각각 100 중량부 및 200 중량부씩 총 400 중량부를 사용함으로써, 시멘트의 비표면적을 높일 수 있으므로, 이에 따라 Ca2+ 이온의 농도를 증가시킬 수 있다.That is, in the case of Example 3 of the present invention, micro cement having a fineness of 6,000 cm2/g or more, and in Example 4, micro cement having a fineness of 6,000 cm2/g or more and crude steel Portland cement having a fineness of 4,500 cm2/g or more are usually used. By using a total of 400 parts by weight (100 parts by weight and 200 parts by weight, respectively, relative to 100 parts by weight of Portland cement), the specific surface area of the cement can be increased, thereby increasing the concentration of Ca 2+ ions.

끝으로, 상기 실시예 3, 4 및 비교예 3, 4의 시멘트 콘크리트 조성물에 대하여, 일반적인 콘크리트의 역학적 특성을 측정하였다. 이 결과는 하기 [표 6]과 같다. Finally, for the cement concrete compositions of Examples 3 and 4 and Comparative Examples 3 and 4, the mechanical properties of general concrete were measured. The results are shown in [Table 6] below.

비교예3Comparative Example 3 비교예4Comparative Example 4 실시예3Example 3 실시예4Example 4 압축강도
(12h, MPa)compressive strength
(12h, MPa) 26.826.8 26.526.5 27.427.4 28.628.6 휨강도(MPa)Flexural strength (MPa) 4.704.70 4.754.75 4.804.80 4.804.80 부착강도(MPa)Adhesive strength (MPa) 1.501.50 1.601.60 1.801.80 1.751.75

상기 [표 6]을 참조하면, 비교예 3 및 4에 비하여 본 발명의 실시예 3 및 4의 경우가 압축 강도, 휨강도 및 부착강도의 물성이 모두 더 우수함을 알 수 있다.Referring to [Table 6], it can be seen that compared to Comparative Examples 3 and 4, the properties of Examples 3 and 4 of the present invention are all superior to those of compressive strength, flexural strength and adhesion strength.

즉, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 사용할 경우, 종래 비교예 3 및 4에 비하여 지연제의 함량을 줄였음에도 불구하고, 작업성 유지 효과는 우수하며, 경화 후 압축 강도, 휨강도 및 부착강도의 역학적 특성 모두가 우수함을 알 수 있다.That is, when the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention is used, the workability maintenance effect is excellent, although the content of the retarder is reduced compared to Comparative Examples 3 and 4 of the prior art. , it can be seen that all of the mechanical properties of compressive strength, flexural strength and adhesion strength after hardening are excellent.

다음으로, 본 발명의 일 실시형태에 따른 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물이 포함하는 점도 조절제에 의해 작업성(Workability) 및 경화 후 물성의 향상을 측정하기 위하여 다음과 같은 슬럼프 테스트 및 경화 후 압축강도 테스트를 수행하였다.Next, in order to measure the improvement of workability and physical properties after hardening by the viscosity modifier included in the fast-diameter cement concrete composition having excellent workability and durability according to an embodiment of the present invention, the following slump test and After curing, a compressive strength test was performed.

상기 슬럼프 테스트는 KS F 2402 [콘크리트 슬럼프 시험 방법]을 기초로 하여 수행되었다.The slump test was performed based on KS F 2402 [Concrete slump test method].

<실시예 5 내지 7><Examples 5 to 7>

성능 개선 결합재 16.7 중량%, 라텍스 합성 폴리머 4.2 중량%, 점도 조절제 0.1 중량%, 잔골재 39.6% 및 굵은 골재 36.0%를 강제식 믹서에 투입하여 교반한 후, 물 3.4 중량%를 더 혼합하여 다시 2분간 교반하여 점도 개선 초속경 시멘트 콘크리트 조성물을 제조하였다.Performance improvement binder 16.7% by weight, latex synthetic polymer 4.2% by weight, viscosity modifier 0.1% by weight, fine aggregate 39.6%, and coarse aggregate 36.0% were put into a forced mixer and stirred, then 3.4% by weight of water was further mixed for 2 minutes By stirring, a viscosity-improving cementitious cement concrete composition was prepared.

실시예 5와 6은 점도 조절제로 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 3:1 함량으로 혼합한 것을 사용하였으며, 실시예 7은 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 3:1 함량으로 혼합한 것 0.05 중량% 및 알코올 알콕시레이트(Alcohol alkoxylates) 0.05 중량%를 사용하였다.In Examples 5 and 6, a mixture of polyether modified polydimethylsiloxane and polyglycol in a 3:1 content was used as a viscosity modifier, and in Example 7, polyether modified polydimethylsiloxane (Polyether) was used. 0.05 wt% of a mixture of modified polydimethylsiloxane) and polyglycol (Polyglycol) in a 3:1 content and 0.05 wt% of alcohol alkoxylates were used.

이때, 성능 개선 결합재는 상기 실시예 5는 상기 실시예 1의 배합비에 맞춰서 제작하였으며, 실시예 6과 7은 상기 실시예 2의 배합비에 맞춰서 제작하였다.At this time, the performance improvement binder was prepared according to the compounding ratio of Example 5 in Example 1, and Examples 6 and 7 were prepared according to the compounding ratio of Example 2.

<비교예 5><Comparative Example 5>

비교예 5는 실시예 5 내지 7과 비교하여, 점도 조절제를 사용하지 않고 라텍스 합성 폴리머를 4.3 중량% 사용한 것을 제외하고는 상기 실시예 5 내지 7과 같은 함량비로 초속경 시멘트 콘크리트 조성물을 제조하였다. 비교예 5에서 성능 개선 결합재는 상기 비교예 1의 조성 및 함량과 동일하게 제작하였다. Comparative Example 5 was compared to Examples 5 to 7, except that 4.3% by weight of the latex synthetic polymer was used without using a viscosity modifier, and a cement concrete composition was prepared at the same content ratio as Examples 5 to 7 above. In Comparative Example 5, the performance-improving binder was prepared in the same composition and content as in Comparative Example 1.

비교예5Comparative Example 5 실시예5Example 5 실시예6Example 6 실시예7Example 7 지연제 사용량(중량%)Retardant usage (wt%) 0.50.5 0.30.3 0.30.3 0.30.3
슬럼프
slump 0분0 minutes 210210 210210 210210 210210 30분30 minutes 180180 210210 205205 200200 60분60 minutes 160160 200200 205205 200200 종결(분)Closing (minutes) 9090 100100 9595 100100 압축강도(4h, MPa)Compressive strength (4h, MPa) 22.222.2 22.822.8 23.623.6 23.523.5

상기 [표 7]을 참조하면, 실시예 5 내지 7과 같이 점도 조절제를 사용한 경우, 이를 사용하지 않은 비교예 5와 비교하여, 슬럼프가 시간별로 감소하지 않아 작업성(Workability)이 개선된 것을 알 수 있다.Referring to [Table 7], it can be seen that when a viscosity modifier was used as in Examples 5 to 7, the slump did not decrease over time, and workability was improved compared to Comparative Example 5 in which it was not used. can

또한, 실시예 5 내지 7의 경우 비교예 5에 비하여 지연제 사용량을 줄였음에도 불구하고, 작업성이 우수하기 때문에, 경화 후 압축 강도 역시 상승하였음을 알 수 있다.In addition, in the case of Examples 5 to 7, although the amount of the retarder was reduced compared to Comparative Example 5, since workability was excellent, it can be seen that the compressive strength after curing was also increased.

이 외에도, 지연제 사용량 감소로 인하여 점도 조절제를 사용한 실시예 5 내지 7의 경우 비교예 5에 비하여 초기 강도 발현이 우수하고 내구성 저하 및 균열 발생 등의 문제를 해결할 수 있다.In addition, in the case of Examples 5 to 7 in which the viscosity modifier was used due to a decrease in the amount of the retarder, the initial strength expression was superior to that of Comparative Example 5, and problems such as reduced durability and cracking could be solved.

또한, 점도 조절제로서, 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 3:1 함량으로 혼합한 것 0.05 중량% 및 알코올 알콕시레이트(Alcohol alkoxylates) 0.05 중량%를 사용한 실시예 7의 경우 작업성 및 경화 후 강도 등의 역학적 특성이 가장 우수하였다.In addition, as a viscosity modifier, a mixture of polyether modified polydimethylsiloxane and polyglycol in a 3:1 content was used in an Example using 0.05% by weight and 0.05% by weight of alcohol alkoxylates In case of 7, mechanical properties such as workability and strength after hardening were the best.

<실시예 8 내지 10><Examples 8 to 10>

성능 개선 결합재 16.5 중량%, 라텍스 합성 폴리머 4.5 중량%, 점도 조절제 0.1 중량%, 잔골재 40.6% 및 굵은 골재 34.9%를 강제식 믹서에 투입하여 교반한 후, 물 3.4 중량%를 더 혼합하여 다시 2분간 교반하여 점도 개선 조강형 시멘트 콘크리트 조성물을 제조하였다.16.5 wt% of performance improvement binder, 4.5 wt% of latex synthetic polymer, 0.1 wt% of a viscosity modifier, 40.6% of fine aggregate and 34.9% of coarse aggregate were put into a forced mixer and stirred, then 3.4 wt% of water was further mixed for 2 minutes By stirring, a viscosity-improving crude steel type cement concrete composition was prepared.

실시예 8과 9는 점도 조절제로 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 3:1 함량으로 혼합한 것을 사용하였으며, 실시예 10은 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 3:1 함량으로 혼합한 것 0.05 중량% 및 알코올 알콕시레이트(Alcohol alkoxylates) 0.05 중량%를 사용하였다.In Examples 8 and 9, a mixture of polyether modified polydimethylsiloxane and polyglycol in a 3:1 content was used as a viscosity modifier, and in Example 10, polyether-modified polydimethylsiloxane (Polyether) was used as a viscosity modifier. 0.05 wt% of a mixture of modified polydimethylsiloxane) and polyglycol (Polyglycol) in a 3:1 content and 0.05 wt% of alcohol alkoxylates were used.

이때, 성능 개선 결합재는 상기 실시예 8은 상기 실시예 3의 배합비에 맞춰서 제작하였으며, 실시예 9와 10은 상기 실시예 4의 배합비에 맞춰서 제작하였다.At this time, the performance improvement binder was prepared according to the compounding ratio of Example 8 in Example 3, and Examples 9 and 10 were prepared according to the compounding ratio of Example 4.

<비교예 6><Comparative Example 6>

비교예 6은 실시예 8 내지 10과 비교하여, 점도 조절제를 사용하지 않고 라텍스 합성 폴리머를 4.6 중량% 사용한 것을 제외하고는 상기 실시예 8 내지 10과 같은 함량비로 조강형 시멘트 콘크리트 조성물을 제조하였다. 비교예 6에서 성능 개선 결합재는 상기 비교예 3의 조성 및 함량과 동일하게 제작하였다. Comparative Example 6 was compared with Examples 8 to 10, except that 4.6% by weight of the latex synthetic polymer was used without using a viscosity modifier, and a crude cement concrete composition was prepared in the same content ratio as in Examples 8 to 10. In Comparative Example 6, the performance-improving binder was prepared in the same composition and content as in Comparative Example 3.

비교예6Comparative Example 6 실시예8Example 8 실시예9Example 9 실시예10Example 10 물/시멘트(W/C) 감소율Water/cement (W/C) reduction rate 00 -1.0%-1.0% -1.0%-1.0% -1.5%-1.5%
슬럼프
slump 0분0 minutes 190190 190190 190190 190190 30분30 minutes 160160 185185 185185 190190 60분60 minutes 160160 180180 185185 185185 종결(분)Closing (minutes) 180180 200200 210210 195195 압축강도(4h, MPa)Compressive strength (4h, MPa) 26.826.8 26.526.5 27.427.4 28.628.6

상기 [표 8]을 참조하면, 실시예 8 내지 10과 같이 점도 조절제를 사용한 경우, 이를 사용하지 않은 비교예 6과 비교하여, 슬럼프가 시간별로 감소하지 않아 작업성(Workability)이 개선된 것을 알 수 있다.Referring to [Table 8], it can be seen that when a viscosity modifier was used as in Examples 8 to 10, the slump did not decrease over time, and workability was improved, compared to Comparative Example 6 in which it was not used. can

또한, 실시예 8 내지 10의 경우 비교예 6에 비하여 물/시멘트 비율(W/C)이 각각 -1.0%, -1.0% 및 -1.5% 감소하여, 물의 절대적 사용량이 감소하였음에도 불구하고, 슬럼프가 감소하지 않아 이에 따른 작업성(Workability) 개선 효과를 얻을 수 있었다.In addition, in the case of Examples 8 to 10, compared to Comparative Example 6, the water/cement ratio (W/C) decreased by -1.0%, -1.0%, and -1.5%, respectively, so that, despite the decrease in the absolute amount of water used, the slump was As it did not decrease, the workability improvement effect was obtained.

이 외에도, 실시예 8 내지 10의 경우 비교예 6에 비하여 물/시멘트 비율(W/C) 감소로 인하여 점도 조절제를 사용한 실시예 8 내지 10의 경우 비교예 6에 비하여 작업성 개선과 더불어 역학적 특성(강도)가 증가하고, 내구성이 우수하며, 특히, 동결융해저항성 및 염소이온침투 저항성이 우수할 수 있다. In addition, in the case of Examples 8 to 10, in the case of Examples 8 to 10 using a viscosity modifier due to a decrease in the water/cement ratio (W/C) compared to Comparative Example 6, mechanical properties along with improvement of workability compared to Comparative Example 6 (strength) is increased, durability is excellent, in particular, it may be excellent in freeze-thaw resistance and chloride ion penetration resistance.

또한, 점도 조절제로서, 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 3:1 함량으로 혼합한 것 0.05 중량% 및 알코올 알콕시레이트(Alcohol alkoxylates) 0.05 중량%를 사용한 실시예 10의 경우 작업성 및 경화 후 강도, 내구성 등의 역학적 특성이 가장 우수하였다.In addition, as a viscosity modifier, a mixture of polyether modified polydimethylsiloxane and polyglycol in a 3: 1 content of 0.05 wt% and alcohol alkoxylates 0.05 wt% In case of 10, mechanical properties such as workability, strength and durability after hardening were the best.

이상, 본 발명의 바람직한 실시예를 들어 상세하게 설명하였으나, 본 발명은 상기 실시예에 한정되는 것은 아니며, 본 발명의 기술적 사상의 범위 내에서 당 분야에서 통상의 지식을 가진 자에 의하여 여러 가지 변형이 가능하다.As mentioned above, although preferred embodiments of the present invention have been described in detail, the present invention is not limited to the above embodiments, and various modifications can be made by those skilled in the art within the scope of the technical spirit of the present invention. This is possible.

Claims (6)

작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물로서,
성능 개선 결합재 3∼40 중량%, 잔골재 5∼70 중량%, 굵은골재 5∼65 중량%, 라텍스 합성 폴리머 1~34 중량% 및 물 0.1∼30 중량%를 포함하며,
상기 성능 개선 결합재는,
보통 포틀랜드 시멘트와 분말도 6,000 ㎠/g 이상의 마이크로 시멘트를 혼합한 혼합 시멘트 10∼70 중량%, 칼슘 또는 마그네슘 설포알루미네이트 3∼40 중량%, 칼슘 또는 마그네슘 알루미나 시멘트 0.1∼30 중량%, 무수석고, 반수석고 및 이수석고 중 어느 하나 이상인 석고 0.1∼20 중량%, 소석회 및 생석회 중 어느 하나 이상인 활성 촉진제 1.0 ~ 10.0 중량%, 탄산리튬, 황산리튬 및 수산화리튬 중 어느 하나 이상인 경화 촉진제 0.01~10 중량%, 나프탈렌계, 멜라민계 및 폴리카르본산계 중 어느 하나 이상인 감수제 0.1~5.0 중량%, 애터풀자이트(Attapulgite) 1.0~5.0 중량%, 및 구연산, 주석산 및 글루콘산 중 어느 하나 이상인 지연제 0.1∼5.0 중량%를 포함하며,
상기 혼합 시멘트의 분말 입자는 입도 분포(Particle Size Distribution)에 있어서, 1.50 ≤D90/D50≤ 1.55를 만족하며, 상기 혼합 시멘트의 전체 분말 입자 입경의 표준 편차(σ)는 1.0 μm ≤σ≤ 3.0 μm를 만족하는 것을 특징으로 하며,
상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물은 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)을 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane)과 폴리 글리콜 (Polyglycol)의 중량비는 3:1인 점도 조절제 0.1 중량% 내지 1.0 중량%를 더 포함하는 것을 특징으로 하는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물.As a fast-setting cement concrete composition with excellent workability and durability,
3 to 40% by weight of the performance-improving binder, 5 to 70% by weight of fine aggregate, 5 to 65% by weight of coarse aggregate, 1 to 34% by weight of latex synthetic polymer, and 0.1 to 30% by weight of water,
The performance improvement binder,
10 to 70% by weight of mixed cement mixed with ordinary Portland cement and microcement having a fineness of 6,000 cm2/g or more, 3 to 40% by weight of calcium or magnesium sulfoaluminate, 0.1 to 30% by weight of calcium or magnesium alumina cement, anhydrite, 0.1 to 20 wt% of gypsum at least any one of hemihydrate gypsum and dihydrate gypsum, 1.0 to 10.0 wt% of an activity accelerator at least any one of slaked lime and quicklime, 0.01 to 10 wt% of a curing accelerator at least any one of lithium carbonate, lithium sulfate and lithium hydroxide , naphthalene-based, melamine-based and polycarboxylic acid-based water reducing agent 0.1 to 5.0% by weight of any one or more, attapulgite (Attapulgite) 1.0 to 5.0% by weight, and citric acid, tartaric acid, and any one or more of gluconic acid retardant 0.1 to 5.0 % by weight,
The powder particles of the mixed cement satisfy 1.50 ≤ D90/D50 ≤ 1.55 in particle size distribution, and the standard deviation (σ) of the total powder particle size of the mixed cement is 1.0 μm ≤ σ ≤ 3.0 μm It is characterized by satisfying
The fast-diameter cement concrete composition having excellent workability and durability includes polyether modified polydimethylsiloxane and polyglycol, and the polyether modified polydimethylsiloxane and polyglycol ( Polyglycol) in a weight ratio of 3:1, the fast-diameter cement concrete composition having excellent workability and durability, characterized in that it further comprises 0.1 wt% to 1.0 wt% of a viscosity modifier. 제1항에 있어서,
상기 혼합 시멘트에서 상기 분말도 6,000 ㎠/g 이상의 마이크로 시멘트는 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부를 포함하는 것을 특징으로 하는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물.According to claim 1,
In the mixed cement, the micro cement having a fineness of 6,000 cm 2 /g or more is included in an amount of 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement. 제1항에 있어서,
상기 혼합 시멘트는 상기 보통 포틀랜드 시멘트 100 중량부에 대하여 50 중량부 내지 400 중량부를 포함하는 분말도 4,500 ㎠/g 이상의 조강 포틀랜드 시멘트를 더 포함하는 것을 특징으로 하는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물.According to claim 1,
The mixed cement is a fast-setting cement concrete with excellent workability and durability, characterized in that it further comprises crude steel Portland cement having a fineness of 4,500 cm 2 /g or more, which contains 50 to 400 parts by weight based on 100 parts by weight of the normal Portland cement. composition. 삭제delete 제1항에 있어서,
상기 점도 조절제는 알코올 알콕시레이트(Alcohol alkoxylates)를 더 포함하며, 상기 폴리에테르 개질 폴리디메틸실록산 (Polyether modified polydimethylsiloxane) 및 폴리 글리콜 (Polyglycol)을 포함하는 성분과 상기 알코올 알콕시레이트(Alcohol alkoxylates)를 포함하는 성분의 중량비가 1:1인 것을 특징으로 하는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물.According to claim 1,
The viscosity modifier further includes alcohol alkoxylates, and a component including the polyether modified polydimethylsiloxane and polyglycol and the alcohol alkoxylates. A fast-diameter cement concrete composition having excellent workability and durability, characterized in that the weight ratio of the components is 1:1. 제1항 내지 제3항 및 제5항 중 어느 한 항에 기재된 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 이용한 도로 포장 보수 공법으로서,
콘크리트 구조물의 열화된 부위 및 아스팔트 콘크리트를 노면 파쇄기를 이용하여 제거하고 청소하는 단계;
상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물이 구체 콘크리트에 부착되기 용이하게 하고 표층강화, 유해물질, 물, 염소이온 등의 침투를 억제하고 내수성을 개선하기 위하여 상기 청소된 부위에 프라이머 또는 블루밍 처리를 하는 단계;
상기 프라이머 또는 블루밍이 처리된 상부에 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 타설하여 열화된 부위의 단면을 보수 또는 보강하는 단계;
타설된 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 표면의 미끄럼 저항성을 개선시키기 위하여 종·횡방향의 타이닝을 실시하는 단계; 및
상기 타이닝된 상기 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물 상부에 수분 증발을 방지하여 소성균열을 억제하기 위하여 피막 양생제를 도포하는 단계를 포함하는 것을 특징으로 하는 작업성 및 내구성이 우수한 속경형 시멘트 콘크리트 조성물을 이용한 도로 포장 보수 공법.A road pavement repair method using the fast-diameter cement concrete composition having excellent workability and durability according to any one of claims 1 to 3 and 5,
removing and cleaning the deteriorated portion of the concrete structure and the asphalt concrete using a scarifier;
Primer or blooming on the cleaned area to facilitate attachment of the fast-diameter cement concrete composition with excellent workability and durability to concrete concrete, to strengthen the surface layer, to suppress penetration of harmful substances, water, chlorine ions, etc., and to improve water resistance processing;
repairing or reinforcing the cross section of the deteriorated area by pouring the fast-diameter cement concrete composition having excellent workability and durability on the primer or blooming-treated upper portion;
performing longitudinal and transverse tinting to improve the slip resistance of the poured fast-diameter cement concrete composition having excellent workability and durability; and
High workability and durability, characterized in that it comprises the step of applying a film curing agent to suppress plastic cracking by preventing moisture evaporation on the top of the tinned fast-diameter cement concrete composition having excellent workability and durability A road pavement repair method using a light cement concrete composition.
KR1020210019691A 2021-02-15 2021-02-15 Cememnt concrete composition and repairing method for road pavement therewith KR102303652B1 (en)