KR102300291B1 - A solidified composition and the preparation method thereof - Google Patents

A solidified composition and the preparation method thereof Download PDF

Info

Publication number
KR102300291B1
KR102300291B1 KR1020210012719A KR20210012719A KR102300291B1 KR 102300291 B1 KR102300291 B1 KR 102300291B1 KR 1020210012719 A KR1020210012719 A KR 1020210012719A KR 20210012719 A KR20210012719 A KR 20210012719A KR 102300291 B1 KR102300291 B1 KR 102300291B1
Authority
KR
South Korea
Prior art keywords
solidified composition
solidified
polyoctenamer
trans
liquid material
Prior art date
Application number
KR1020210012719A
Other languages
Korean (ko)
Inventor
황용경
Original Assignee
황용경
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 황용경 filed Critical 황용경
Priority to KR1020210012719A priority Critical patent/KR102300291B1/en
Application granted granted Critical
Publication of KR102300291B1 publication Critical patent/KR102300291B1/en
Priority to PCT/KR2022/001722 priority patent/WO2022164298A1/en

Abstract

The present invention relates to a solidified composition which comprises trans-polyoctenamer and a highly viscous liquid material having a viscosity greater than or equal to a predetermined value, wherein the solidified composition may be solid at room temperature. Since the solidified composition of the present invention does not undergo phase separation and is easily redispersed, the solidified composition has stable properties and can be uniformly mixed when mixed with other materials.

Description

고형화된 조성물과 그 제조 방법{A SOLIDIFIED COMPOSITION AND THE PREPARATION METHOD THEREOF}Solidified composition and method for producing the same

본 발명은 액체 물질의 편리한 저장, 운반 및 보관을 위해 고형화된 조성물과 그 제조 방법에 관한 것이다.The present invention relates to solidified compositions for convenient storage, transport and storage of liquid substances and methods for their preparation.

우리는 실생활에서 다양한 액체를 저장, 운반 및 보관한다. 물과 같은 점성의 정도(점도)가 낮은 액체는 이러한 저장, 운반 및 보관에 별다른 문제가 발생하지 않는다. 하지만, 소정의 값 이상의 점도를 갖는 고점도 액체의 경우에는 보관되는 용기로부터 다른 용기로 액체를 옮길 때 상당한 양이 용기 내에 남아 있을 수 있다. 또한, 고점도 액체의 혼합을 위해 다른 공정의 용기로 옮기는 경로에 액체가 남아 있을 수 있다. 점도가 높을수록 운반을 위한 설비비용 및 잔여 되어 발생하는 손실의 정도가 크다.We store, transport and store various liquids in real life. Liquids with a low degree of viscosity (viscosity), such as water, do not pose any major problems for such storage, transport and storage. However, in the case of a highly viscous liquid having a viscosity above a predetermined value, a significant amount may remain in the container when the liquid is transferred from the container in which it is stored to another container. In addition, liquid may remain in the path of transfer to the vessel of another process for mixing of the high viscosity liquid. The higher the viscosity, the greater the equipment cost for transportation and the degree of residual loss.

용기 표면이나 공정 경로에 남아있는 액체의 경우 그 남아 있는 부분을 가열하여 액체의 손실을 줄이는 방법을 사용해 왔다. 하지만, 이러한 가열은 운반 비용 또는 공정 비용이 매우 상승하며, 공정이 비효율적이게 되는 단점이 있다.In the case of liquid remaining on the surface of the vessel or in the process path, a method has been used to reduce the loss of liquid by heating the remaining portion. However, such heating has a disadvantage in that transport cost or process cost is very high, and the process becomes inefficient.

한국 공개 특허 10-2011-0086799에서는 고점도 조성물을 수송하는 동안 내용물을 혼합하는 믹서가 개시된다. 히터는 믹서에 의한 도관의 내용물의 혼합 이전에 또는 이후에 도관의 내용물을 가열하기 위해 위치될 수 있다. 하지만, 이러한 구성은 상술한 것과 같은 단점을 극복할 수 없을 것이다.Korean Patent Laid-Open Patent Publication No. 10-2011-0086799 discloses a mixer for mixing contents while transporting a high-viscosity composition. A heater may be positioned to heat the contents of the conduit prior to or after mixing of the contents of the conduit by the mixer. However, such a configuration will not be able to overcome the above-described disadvantages.

위의 단점을 극복하기 위하여 고점도 액체 물질의 고형화가 시도되었다. 예를 들어, 일반적인 폴리프로필렌(PP) 또는 폴리에틸렌(PE)과 고점도 액체 물질을 혼합하여 고점도 액체 물질의 고형화를 위한 시도가 있었다. 하지만, 이러한 혼합은 (i) 두 개의 물질의 상의 분리되어 안정하지 못한 조성물이 형성되며, (ii) 고형화된 조성물을 다른 물질과의 혼합을 위해 다시 사용할 때 재분산이 용이하지 않아 불균일한 혼합이 이루어지며, (iii) 유리 전이 온도(glass transition temperature, Tg)가 높아 혼합하기 힘들며, (iv) 고형화된 조성물이 응용 배합(예를 들어, 타이어 트레드 배합, 벨트 배합, 매트 배합 등)에 적용되었을 때 가교반응에 참여하지 못하여 물성이 급격하게 하락하는 단점을 가진다.In order to overcome the above disadvantages, solidification of high-viscosity liquid materials has been attempted. For example, there have been attempts to solidify high viscosity liquid materials by mixing common polypropylene (PP) or polyethylene (PE) with high viscosity liquid materials. However, such mixing (i) the phases of the two substances separate to form an unstable composition, and (ii) when the solidified composition is reused for mixing with other substances, it is not easy to redisperse, resulting in non-uniform mixing. (iii) difficult to mix due to high glass transition temperature (T g ), and (iv) solidified composition is applied to application formulations (eg, tire tread formulation, belt formulation, mat formulation, etc.) It has a disadvantage in that it cannot participate in the cross-linking reaction when it becomes high, and the physical properties drop rapidly.

공개특허공보 제10-2011-0086799호 (2011.08.01)Laid-Open Patent Publication No. 10-2011-0086799 (2011.08.01)

이러한 문제점을 해결하기 위하여, 고점도 액체 물질이 균일하게 혼합되고 상분리가 일어나지 않으면서, 재분산이 잘 일어나게 하는 고형화된 조성물과 그 제조 방법을 제공하는데 목적이 있다.In order to solve this problem, an object of the present invention is to provide a solidified composition in which a high-viscosity liquid material is uniformly mixed and phase separation does not occur, and redispersion occurs well, and a method for preparing the same.

본 발명에 따른 고형화된 조성물은, 소정의 값 이상의 점도를 갖는 고점도성 액체 물질 및 트랜스-폴리옥테나머를 포함하며, 고형화된 조성물은 실온에서 고체일 수 있다.The solidified composition according to the present invention comprises a trans-polyoctenamer and a highly viscous liquid material having a viscosity equal to or greater than a predetermined value, and the solidified composition may be solid at room temperature.

일 실시예에서, 고형화된 조성물은 80 내지 95 중량부의 고점도성 액체 물질 및 5 내지 20 중량부의 트랜스-폴리옥테나머를 포함할 수 있다.In one embodiment, the solidified composition may comprise 80 to 95 parts by weight of the highly viscous liquid material and 5 to 20 parts by weight of the trans-polyoctenamer.

일 실시예에서, 고형화된 조성물은 모든 부분에서 36 내지 40℃의 연화점을 가질 수 있다.In one embodiment, the solidified composition may have a softening point of 36 to 40° C. in all parts.

일 실시예에서, 고점도성 액체 물질은 오일, 석유수지, 왁스, 모노머, 올리고머, 액상 폴리머, 꿀, 조청 및 이들 중 둘 이상의 혼합물을 포함할 수 있다.In one embodiment, the high-viscosity liquid material may include oil, petroleum resin, wax, monomer, oligomer, liquid polymer, honey, coarse powder, and mixtures of two or more thereof.

본 발명에 따른 고형화된 조성물을 제조하는 방법은, 소정의 값 이상의 점도를 갖는 고점도성 액체 물질을 가열하는 단계, 고점도성 액체 물질에 트랜스-폴리옥테나머를 첨가형 혼합하는 단계, 및 혼합된 조성물을 원하는 형상으로 고형화시키는 단계를 포함할 수 있다.A method for preparing a solidified composition according to the present invention comprises the steps of heating a high-viscosity liquid material having a viscosity equal to or greater than a predetermined value, adding trans-polyoctenamer to the high-viscosity liquid material, and mixing the mixed composition. It may include the step of solidifying into a desired shape.

일 실시예에서, 가열하는 단계, 혼합하는 단계 및 고형화시키는 단계는 모두 교반을 동반할 수 있다.In one embodiment, heating, mixing, and solidifying may all be accompanied by agitation.

일 실시예에서, 혼합하는 단계는 150 내지 170℃에서 수행될 수 있다.In one embodiment, the mixing may be performed at 150 to 170°C.

일 실시예에서, 고형화시키는 단계는 혼합된 조성물을 성형시키는 단계를 포함하며, 성형시키는 단계는 교반과 함께 80℃에서 수행될 수 있다.In one embodiment, the solidifying step includes molding the mixed composition, and the molding step may be performed at 80° C. with stirring.

일 실시예에서, 혼합의 비율은 고점도성 액체 물질 70 내지 95 중량부에 대해 트랜스-폴리옥테나머 5 내지 20 중량부일 수 있다.In one embodiment, the mixing ratio may be 5 to 20 parts by weight of trans-polyoctenamer based on 70 to 95 parts by weight of the high-viscosity liquid material.

일 실시예에서, 성형은 압출 성형, 압축 성형, 사출 성형, 캘린더링, 회전 성형 및 열성형을 포함할 수 있다.In one embodiment, molding may include extrusion molding, compression molding, injection molding, calendering, rotational molding and thermoforming.

본 발명의 고형화된 조성물은 (i) 상이 분리되지 않으며, (ii) 재분산이 용이하기 때문에, 안정한 특성을 가지며 다른 물질과 혼합을 할 때 균일한 혼합이 이루어질 수 있다.The solidified composition of the present invention has stable properties because (i) phases are not separated and (ii) redispersion is easy, and uniform mixing can be achieved when mixing with other materials.

본 발명의 고형화된 조성물을 제조하는 방법은 (i) 녹는점이 낮으며, (ii) 적당한 결정성을 가지고 있어 상온에서 플라스틱과 같은 성질을 갖고, 이형성이 있는 트랜스-폴리옥테나머(trans-polyoctenamer, TOR)를 첨가하는 단계를 포함하기 때문에, 혼합이 쉬우며 고점도 액체 물질의 물성이 고형화되도록 변화되는 이점을 갖는다.The method for preparing the solidified composition of the present invention (i) has a low melting point, (ii) has moderate crystallinity and has plastic-like properties at room temperature, and is a trans-polyoctenamer with releasability. , TOR), it is easy to mix and has the advantage of changing the physical properties of the high-viscosity liquid material to be solidified.

도 1은 본 발명에 따른 고형화된 조성물을 제조하기 위한 방법을 도시하는 흐름도이다.
도 2는 본 발명에 따른 고형화된 조성물의 특정 부분의 연화점 측정 결과를 나타내는 도면이다.1 is a flow diagram illustrating a method for preparing a solidified composition according to the present invention.
2 is a view showing the measurement result of the softening point of a specific portion of the solidified composition according to the present invention.

이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세하게 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, with reference to the accompanying drawings, the embodiments of the present invention will be described in detail so that those of ordinary skill in the art to which the present invention pertains can easily implement them. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein.

본 발명에 따른 고형화된 조성물은 고점도 액체 물질 및 트랜스-폴리옥테나머 수지를 포함할 수 있다. 예를 들어, 본 발명에 따른 고형화된 조성물은 고점도 액체 물질 80 내지 95 중량부, 트랜스-폴리옥테나머 수지 5 중량부 내지 20 중량부를 포함할 수 있다.The solidified composition according to the present invention may comprise a high viscosity liquid material and a trans-polyoctenamer resin. For example, the solidified composition according to the present invention may include 80 to 95 parts by weight of a high-viscosity liquid material and 5 to 20 parts by weight of a trans-polyoctenamer resin.

고점도 액체 물질은 소정의 점도 이상의 액체 물질을 포함할 수 있다. 예를 들어, 고점도 액체 물질은 오일, 석유수지(hydrocarbon resin), 왁스, 모노머, 올리고머, 액상 폴리머, 꿀, 조청 및 이들 중 둘 이상의 혼합물을 포함할 수 있다.The high viscosity liquid material may include a liquid material having a predetermined viscosity or higher. For example, the highly viscous liquid material may include oils, hydrocarbon resins, waxes, monomers, oligomers, liquid polymers, honey, crude oil, and mixtures of two or more thereof.

트랜스-폴리옥테나머 수지는 시클로옥텐(cyclooctene)으로부터의 개화 복분해 중합에 의해 수득되며, 메크로시클릭(macrocyclic) 및 선형 중합체 둘 다를 포함할 수 있다. 트랜스-폴리옥테나머 수지는 양봉형 분자량 분포를 갖는 저 분자량 특수 고무일 수 있다. 트랜스-폴리옥테나머 수지의 양봉형 분자량 분포는 저 분자량 구성성분이 일반적으로 200 내지 6000 g/mol의 중량-평균 분자량의 범위 내에 있고, 고 중합체성 구성성분이 8000 내지 400,000 g/mol의 중량-평균 분자량의 범위 내에 있다는 사실에서 발생할 수 있다.Trans-polyoctenamer resins are obtained by open metathesis polymerization from cyclooctene and may include both macrocyclic and linear polymers. The trans-polyoctenamer resin may be a low molecular weight special rubber having a bimodal molecular weight distribution. The bimodal molecular weight distribution of the trans-polyoctenamer resin is such that the low molecular weight constituents are generally in the range of weight-average molecular weights of 200 to 6000 g/mol, and the high polymeric constituents are in the weight-average range of 8000 to 400,000 g/mol. may arise from the fact that it is within a range of average molecular weights.

트랜스-폴리옥테나머 수지는 Evonik사 VESTENAMER 제품일 수 있다. 트랜스-폴리옥테나머 수지는 분자구조 비율에 따라 용융점을 다양하게 조율할 수 있다. 이중 VESTENAMER 8012 제품은 용융점이 55℃로 낮기 때문에 낮은 온도에서도 용융이 일어나 다른 물질과의 혼합이 용이할 수 있다. 트랜스-폴리옥테나머 수지는 결정성을 갖는 비극성 고분자로서 다양한 극성을 갖는 물질과의 혼합이 용이할 수 있다. 트랜스-폴리옥테나머 수지는 가교 화학 반응을 하기 때문에 다양한 응용처에서 혼합하여 사용이 가능하며, 첨가되었을 때에 물성의 저해를 초래하지 않는다. 트랜스-폴리옥테나머 수지는 고점도의 액체 물질의 물성을 변화시켜 고형화가 가능하게 할 수 있다. 또한, 트랜스-폴리옥테나머 수지는 실온(1 내지 35℃)에서는 결정성을 갖기 때문에 다른 물질과의 혼합 후에 고형화가 용이할 수 있다.The trans-polyoctenamer resin may be a product of VESTENAMER from Evonik. Trans-polyoctenamer resins can adjust the melting point in various ways according to the molecular structure ratio. Among them, the VESTENAMER 8012 product has a low melting point of 55℃, so it melts even at a low temperature, so it can be easily mixed with other materials. The trans-polyoctenamer resin is a non-polar polymer having crystallinity and may be easily mixed with materials having various polarities. Because trans-polyoctenamer resin undergoes a crosslinking chemical reaction, it can be mixed and used in various applications, and when added, physical properties are not impaired. The trans-polyoctenamer resin may change the physical properties of a high-viscosity liquid material to enable solidification. In addition, since the trans-polyoctenamer resin has crystallinity at room temperature (1 to 35° C.), it may be easily solidified after mixing with other materials.

본 발명에 따른 고형화된 조성물에서, 5 중량부 미만의 트랜스-폴리옥테나머 수지가 포함되는 경우 고형화가 힘들며, 20 중량부 초과의 트랜스-폴리옥테나머 수지가 포함되는 경우 원료 단가가 높아지므로 바람직하지 않을 수 있다.In the solidified composition according to the present invention, when less than 5 parts by weight of the trans-polyoctenamer resin is included, solidification is difficult, and when more than 20 parts by weight of the trans-polyoctenamer resin is included, the raw material cost increases. This may not be desirable.

도 1는 본 발명에 따른 고형화된 조성물의 제조 방법의 흐름도룰 도시한다. 도 1을 참조하면, 우선 고점도 액체 물질을 가열할 수 있다(S10). 예를 들어, 고점도 액체 물질을 소정의 온도로 가열할 수 있다. 상기 가열은 고점도 액체 물질을 교반시키면서 진행될 수 있다.1 shows a flow chart of a method for preparing a solidified composition according to the present invention. Referring to FIG. 1 , first, a high-viscosity liquid material may be heated ( S10 ). For example, a highly viscous liquid material may be heated to a predetermined temperature. The heating may proceed while stirring the high-viscosity liquid material.

그 후에, 고점도 액체 물질에 트랜스-폴리옥테나머를 첨가하여 혼합할 수 있다(S20). 트랜스-폴리옥테나머를 첨가하여 고점도 액체 물질과 함께 교반할 수 있다. 교반은 150 내지 170℃에서 수행될 수 있다. 150℃ 미만의 온도에서 교반한다면, 고점도 액체 물질과 트랜스-폴리옥테나머의 층이 분리될 수 있으며, 170℃ 초과의 온도에서 교반한다면 고점도 액체 물질이 분해될 수 있다.After that, trans-polyoctenamer may be added to the high-viscosity liquid material and mixed (S20). Trans-polyoctenamer can be added and stirred with the high viscosity liquid material. Stirring may be performed at 150 to 170 °C. If stirring at a temperature of less than 150° C., the layer of the high-viscosity liquid material and the trans-polyoctenamer may separate, and if stirred at a temperature above 170° C., the high-viscosity liquid material may decompose.

다음으로, 혼합된 조성물을 원하는 형상으로 고형화시킬 수 있다(S30). 예를 들어, 혼합된 조성물을 성형(molding)함으로써 원하는 형상으로 고형화시킬 수 있다. 예를 들어, 성형은 압출 성형, 압축 성형, 사출 성형, 캘린더링(calendaring), 회전 성형 및 열성형을 포함할 수 있다. 이러한 성형은 다시 상 분리가 일어나는 것을 방지하기 위해 교반과 함께 진행될 수 있다. 높은 온도에서 고형화가 이루어 질 때, 분자 간의 이동이 커서 고점도 액체 물질과 트랜스-폴리옥테나머 사이에 층 분리가 일어나고 트랜스-폴리옥테나머의 분산도가 낮아질 수 있다. 따라서, 낮은 온도에서 고형화하는 것이 바람직하다. 예를 들어, 교반 및 성형은 80℃에서 진행될 수 있다.Next, the mixed composition may be solidified into a desired shape (S30). For example, the mixed composition can be solidified into a desired shape by molding. For example, molding may include extrusion molding, compression molding, injection molding, calendaring, rotational molding, and thermoforming. This shaping may proceed with stirring to prevent phase separation from occurring again. When solidification is performed at a high temperature, intermolecular movement is large, causing layer separation between the high-viscosity liquid material and the trans-polyoctenamer, and the dispersibility of the trans-polyoctenamer may be lowered. Therefore, it is preferable to solidify at a low temperature. For example, stirring and molding may proceed at 80°C.

이러한 제조 공정을 통해 제조된 고형화된 조성물은 실온에서 고체일 수 있다. 따라서, 고형화된 조성물은 저장, 운반 및 보관이 편리하며, 고점도 액체 물질과 비교하여 운반시에 손실이 현저하게 줄어들 수 있다. 또한, 고형화된 조성물은 고점도 액체 물질과 비교하여 다른 물질과의 혼합 시에도 공정이 상당히 간단해질 수 있다. 따라서, 비용 측면에서 상당한 이점을 가져올 수 있다.The solidified composition prepared via this manufacturing process may be solid at room temperature. Accordingly, the solidified composition is convenient to store, transport and store, and loss during transport can be significantly reduced as compared to a high-viscosity liquid material. In addition, the solidified composition can be considerably simplified in the process even when mixed with other materials compared to highly viscous liquid materials. Therefore, it can bring a significant advantage in terms of cost.

이하, 본 발명의 실시예를 통하여 상세히 설명한다. 그러나 이들 실시예는 본 발명을 구체적으로 설명하기 위한 것일 뿐, 본 발명의 범위가 이들 실시예에 의해 한정되는 것은 아니다.Hereinafter, it will be described in detail through embodiments of the present invention. However, these examples are only for explaining the present invention in detail, and the scope of the present invention is not limited by these examples.

실시예Example

석유수지(제품명: 코오롱 수지) 93 중량부를 700 rpm의 속도로 교반하며 200℃로 가열하였다. 석유수지를 가열한 후 트랜스-폴리옥테나머(제품명: VESTENAMER 8012)를 7 중량부 첨가하여 150℃에서 700 rpm의 속도로 교반하였다. 그 후에, 트윈 스크류 압출기를 통해 80℃에서 500 rpm의 속도로 교반하면서 압출하여 고형화 조성물을 생성하였다.93 parts by weight of petroleum resin (product name: Kolon resin) was heated to 200° C. while stirring at a speed of 700 rpm. After heating the petroleum resin, 7 parts by weight of trans-polyoctenamer (product name: VESTENAMER 8012) was added and stirred at 150° C. at a speed of 700 rpm. Thereafter, the solidified composition was produced by extruding through a twin screw extruder at 80° C. with stirring at a speed of 500 rpm.

비교예 1Comparative Example 1

트랜스-폴리옥테나머를 첨가하여 150℃가 아닌 120℃에서 700rpm의 속도로 교반한 점을 제외하고는 실시예와 동일한 방법으로 제조하였다.It was prepared in the same manner as in Example, except that trans-polyoctenamer was added and the mixture was stirred at a speed of 700 rpm at 120° C. instead of 150° C.

비교예 2 및 3Comparative Examples 2 and 3

트윈 스크류 압출기를 통해 80℃가 아닌 100℃ 및 120℃에서 500 rpm의 속도로 교반하면서 압출한 점을 제외하고는 실시예와 동일한 방법으로 제조하였다.It was prepared in the same manner as in Example, except that it was extruded while stirring at a speed of 500 rpm at 100° C. and 120° C. instead of 80° C. through a twin screw extruder.

비교예 1에 의해 얻은 고형화 조성물은 석유수지와 트랜스-폴리옥테나머 사이에 층 분리가 관찰되었다. 즉, 혼합 온도가 낮아서 혼합이 충분이 이루어지지 않은 것을 확인할 수 있었다. 비교예 2 및 3에 의해 얻은 고형화 조성물은 각각 47℃ 및 50℃의 연화점을 가졌으며, 측정 위치에 따라 연화점이 달라지는 것을 확인할 수 있었다.In the solidified composition obtained by Comparative Example 1, layer separation was observed between the petroleum resin and the trans-polyoctenamer. That is, it was confirmed that the mixing was not performed sufficiently because the mixing temperature was low. The solidified compositions obtained by Comparative Examples 2 and 3 had softening points of 47° C. and 50° C., respectively, and it was confirmed that the softening points varied depending on the measurement location.

이와 달리, 실시예에 의해 얻은 고형화 조성물은 층 분리가 관찰되지 않았으며, 도 2에 도시된 바와 같이, 연화점을 측정한 결과 모든 부분에서 38±2℃를 나타내었다. 결과적으로, 실시예에 의해 얻은 고형화 조성물은 비교예 2 및 3에 의해 얻은 고형화 조성물과 비교하여 낮은 연화점을 가졌다.On the other hand, in the solidified composition obtained in Example, no layer separation was observed, and as shown in FIG. 2 , as a result of measuring the softening point, 38±2° C. was exhibited in all parts. As a result, the solidified composition obtained by Example had a lower softening point compared with the solidified composition obtained by Comparative Examples 2 and 3.

연화점이 55℃로부터 더 낮아진다는 것는, 녹는점이 55℃인 트랜스-폴리옥테나머가 마이너스 값의 녹는점을 갖는 석유수지에 더 잘 혼합되었다는 것을 의미한다. 따라서, 실시예에 의해 얻은 고형화 조성물은 비교예 1 내지 3의 경우보다 2 개의 상이 층분리가 일어나지 않고 균일하게 잘 혼합되었다는 것을 확인할 수 있다. 고점도 액체 물질과 트랜스-폴리옥테나머 수지가 균일하게 잘 혼합되었으므로, 본 발명의 고형화된 조성물이 다른 물질과 혼합되는 경우에, 고형화된 조성물의 재분산이 용이하여 다른 물질과 균일하게 혼합될 수 있다.The lowering of the softening point from 55°C means that the trans-polyoctenamer having a melting point of 55°C was better mixed with the petroleum resin having a negative melting point. Therefore, it can be confirmed that the solidified composition obtained in Examples 1 to 3 was uniformly well mixed without separation of the two phases compared to Comparative Examples 1 to 3. Since the high-viscosity liquid material and the trans-polyoctenamer resin are uniformly and well mixed, when the solidified composition of the present invention is mixed with other materials, it is easy to redisperse the solidified composition and can be uniformly mixed with other materials. have.

본 발명은 명세서에 기재된 실시예를 참고로 설명되었으나 이는 예시적인 것에 불과하며 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 다른 실시예가 가능한 점을 이해할 것이다. 따라서, 본 발명의 진정한 기술적 보호범위는 첨부된 특허청구범위의 기술적 사상에 의하여 정해져야 할 것이다.Although the present invention has been described with reference to the embodiments described in the specification, these are merely exemplary and those of ordinary skill in the art will understand that various modifications and equivalent other embodiments are possible therefrom. Accordingly, the true technical protection scope of the present invention should be determined by the technical spirit of the appended claims.

Claims (10)

고형화된 조성물로서,
소정의 값 이상의 점도를 갖는 고점도성 액체 물질; 및
트랜스-폴리옥테나머;를 포함하며,
상기 고형화된 조성물은 실온에서 고체이며,
상기 고점도성 액체 물질은 트랜스-폴리옥테나머와의 화학 결합에 의해 고형화되며,
상기 고형화된 조성물은:
80 내지 95 중량부의 고점도성 액체 물질; 및
5 내지 20 중량부의 트랜스-폴리옥테나머;를 포함하는,
고형화된 조성물.A solidified composition comprising:
a highly viscous liquid substance having a viscosity equal to or greater than a predetermined value; and
Trans-polyoctenamer; contains,
The solidified composition is a solid at room temperature,
The highly viscous liquid material is solidified by chemical bonding with trans-polyoctenamer,
The solidified composition comprises:
80 to 95 parts by weight of a highly viscous liquid substance; and
5 to 20 parts by weight of trans-polyoctenamer; containing,
Solidified composition. 제1항에 있어서,
상기 고형화된 조성물은 모든 부분에서 36 내지 40℃의 연화점을 갖는,
고형화된 조성물.According to claim 1,
wherein the solidified composition has a softening point of 36 to 40° C. in all parts;
Solidified composition. 제1항에 있어서,
상기 고점도성 액체 물질은 오일, 석유수지, 왁스, 모노머, 올리고머, 액상 폴리머, 꿀, 조청 또는 이들 중 둘 이상의 혼합물을 포함하는,
고형화된 조성물.According to claim 1,
The highly viscous liquid material comprises oil, petroleum resin, wax, monomer, oligomer, liquid polymer, honey, coarse powder, or a mixture of two or more thereof,
Solidified composition. 고형화된 조성물을 제조하는 방법으로서,
소정의 값 이상의 점도를 갖는 고점도성 액체 물질을 소정의 온도로 가열하는 단계;
상기 고점도성 액체 물질에 트랜스-폴리옥테나머를 첨가하여 150 내지 170℃에서 혼합하는 단계; 및
혼합된 조성물을 원하는 형상으로 고형화시키는 단계;를 포함하며,
상기 고점도성 액체 물질은 트랜스-폴리옥테나머와의 화학 결합에 의해 고형화되며,
상기 혼합의 비율은 상기 고점도성 액체 물질 80 내지 95 중량부에 대해 트랜스-폴리옥테나머 5 내지 20 중량부인,
고형화된 조성물을 제조하는 방법.A method of preparing a solidified composition comprising:
heating a highly viscous liquid material having a viscosity equal to or greater than a predetermined value to a predetermined temperature;
adding trans-polyoctenamer to the high-viscosity liquid material and mixing at 150 to 170°C; and
Including; solidifying the mixed composition into a desired shape;
The highly viscous liquid material is solidified by chemical bonding with trans-polyoctenamer,
The mixing ratio is 5 to 20 parts by weight of trans-polyoctenamer based on 80 to 95 parts by weight of the high-viscosity liquid material,
A method for preparing a solidified composition. 제4항에 있어서,
상기 가열하는 단계, 혼합하는 단계 및 고형화시키는 단계는 모두 교반을 동반하는,
고형화된 조성물을 제조하는 방법.5. The method of claim 4,
The heating step, the mixing step, and the solidifying step are all accompanied by stirring,
A method for preparing a solidified composition. 제4항에 있어서,
상기 고형화시키는 단계는 상기 혼합된 조성물을 성형시키는 단계를 포함하며,
상기 성형시키는 단계는 교반과 함께 80℃에서 수행되는,
고형화된 조성물을 제조하는 방법.5. The method of claim 4,
The solidifying step comprises molding the mixed composition,
The forming step is carried out at 80 ℃ with stirring,
A method for preparing a solidified composition. 제6항에 있어서,
상기 성형은 압출 성형, 압축 성형, 사출 성형, 캘린더링, 회전 성형 또는 열성형을 포함하는,
고형화된 조성물을 제조하는 방법.7. The method of claim 6,
wherein said molding comprises extrusion molding, compression molding, injection molding, calendering, rotational molding or thermoforming,
A method for preparing a solidified composition. 삭제delete 삭제delete 삭제delete
KR1020210012719A 2021-01-29 2021-01-29 A solidified composition and the preparation method thereof KR102300291B1 (en)