KR102242135B1 - D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coated metal foam. outside - Google Patents

D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coated metal foam. outside Download PDF

Info

Publication number
KR102242135B1
KR102242135B1 KR1020190069292A KR20190069292A KR102242135B1 KR 102242135 B1 KR102242135 B1 KR 102242135B1 KR 1020190069292 A KR1020190069292 A KR 1020190069292A KR 20190069292 A KR20190069292 A KR 20190069292A KR 102242135 B1 KR102242135 B1 KR 102242135B1
Authority
KR
South Korea
Prior art keywords
boron nitride
chalcogenide
nitride nano
metal foam
hydrophobic
Prior art date
Application number
KR1020190069292A
Other languages
Korean (ko)
Other versions
KR20200142261A (en
Inventor
이성균
이혜경
이연수
Original Assignee
이성균
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이성균 filed Critical 이성균
Priority to KR1020190069292A priority Critical patent/KR102242135B1/en
Publication of KR20200142261A publication Critical patent/KR20200142261A/en
Application granted granted Critical
Publication of KR102242135B1 publication Critical patent/KR102242135B1/en

Abstract

본 발명은 메탈폼을 보다 내식성, 항균성, 열전도성 등이 우수하면서 필요시 소수성의 특성이 나타나도록 구성하여 보다 효능적인 수소 저장체나 에너지 저장체, 건축용 거푸집, 수질 및 공기 정화용 필터, 매연 저감 필터 등을 구성할수 있는 보다 효능적인 메탈폼인 1) A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼이나 2) B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 3) C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 4) D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성한것이다The present invention makes the metal foam more excellent in corrosion resistance, antibacterial properties, thermal conductivity, etc., and has hydrophobic properties when necessary, so that more efficient hydrogen storage or energy storage, construction forms, water and air purification filters, smoke reduction filters, etc. 1) A. Chalcogenide (boron nitride nano-based) coated metal foam or 2) B. Chalcogenide (boron nitride nano-based) carbon coated metal foam 3 ) C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam 4) D. Hydrophobic/chalcogenide (boron nitride nano-based) carbon coated metal foam

Description

D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼. 외{omitted}D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coated metal foam. External{omitted}

본 발명은 메탈폼을 보다 내식성, 항균성, 강도성 등이 우수하면서 필요시 소수성의 특성이 나타나도록 구성하여 보다 효능적인 수소 저장체 및 에너지 저장체 등을 구성할수 있는 보다 효능적인 메탈폼을 구성하고자The present invention is to construct a more efficient metal foam that can constitute a more efficient hydrogen storage body and energy storage body by configuring the metal foam to exhibit more excellent corrosion resistance, antibacterial properties, strength, and hydrophobic properties when necessary.

1. 1) 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드) ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브), ①~⑦ 중에서 1가지 이상을 선택하여 a. 칼코게 나이드(질화 붕소 나노계)를 구성하거나 또는 2) a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소를 혼합시켜서 b. 칼코게 나이드(질화 붕소 나노계)·탄소를 구성한후
2. 1) a. 칼코게 나이드(질화 붕소 나노계)를 용매에 첨가하고 분산시켜서

Figure 112020502935482-pat00001
칼코게 나이드(질화 붕소 나노계) 용액을 구성하거나 또는 2) b. 칼코게 나이드(질화 붕소 나노계)·탄소를 용매에 첨가 분산시켜서
Figure 112020502935482-pat00002
칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성하면서 또한
3)
Figure 112020502935482-pat00003
칼코게 나이드(질화 붕소 나노계) 용액에 소수성 실란 용액을 첨가 혼합시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00004
소수성/칼코게 나이드(질화 붕소 나노계) 용액을 구성하거나 또는 4)
Figure 112020502935482-pat00005
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 소수성 실란 용액을 첨가 혼합시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00006
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후1. 1) Consisting of nanosheets or nanopowder ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide) ⑤ BNN (boron nitride nanopowder) ) ⑥ BNNS (boron nitride nanosheets) ⑦ BNNT (boron nitride nanotubes), select one or more of ①~⑦ and a. Constituting chalcogenide (boron nitride nano-based) or 2) a. Chalcogenide (boron nitride nano-based) is mixed with carbon composed of at least one carbon nanotube or graphene b. After forming chalcogenide (boron nitride nano-based) carbon
2. 1) a. By adding chalcogenide (boron nitride nano-based) to the solvent and dispersing it
Figure 112020502935482-pat00001
Comprising a chalcogenide (boron nitride nano-based) solution or 2) b. By adding and dispersing chalcogenide (boron nitride nano-based) carbon in a solvent
Figure 112020502935482-pat00002
While constituting a chalcogenide (boron nitride nano-based) carbon solution,
3)
Figure 112020502935482-pat00003
A hydrophobic silane solution is added to the chalcogenide (boron nitride nano-based) solution to show hydrophobic properties.
Figure 112020502935482-pat00004
Constituting a hydrophobic/chalcogenide (boron nitride nano-based) solution or 4)
Figure 112020502935482-pat00005
A hydrophobic silane solution is added and mixed with a chalcogenide (boron nitride nano-based) carbon solution to show hydrophobic properties.
Figure 112020502935482-pat00006
After forming a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution

3. 1) 메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을

Figure 112020502935482-pat00007
칼코게 나이드(질화 붕소 나노계) 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하거나 2) 메탈폼을
Figure 112020502935482-pat00008
칼코게 나이드(질화 붕소 나노계)·탄소 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하거나 또는
3) 메탈폼을
Figure 112020502935482-pat00009
소수성/칼코게 나이드(질화 붕소 나노계) 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하거나3. 1) Metal foam (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal out of stainless steel, but two or more metals It is composed of microporous foam of the desired shape with an alloy)
Figure 112020502935482-pat00007
After coating with chalcogenide (boron nitride nano-based) solution and drying, a. By coating a chalcogenide (boron nitride nano-based) coating film a. A. Chalcogenide (boron nitride nano-based) exhibiting the characteristics of A. Compose a metal foam coated with chalcogenide (boron nitride nano-based) or 2) a metal foam
Figure 112020502935482-pat00008
After coating with a chalcogenide (boron nitride nano-based) carbon solution and drying, b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. B. Chalcogenide (boron nitride nano-based), which exhibits the characteristics of carbon, constitutes a carbon-coated metal foam, or
3) Metal foam
Figure 112020502935482-pat00009
After coating with a hydrophobic/chalcogenide (boron nitride nano-based) solution and drying, c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam has hydrophobic properties and a. C. Hydrophobic/chalcogenide (boron nitride nano-based), which exhibits the characteristics of a metal foam coated with hydrophobic/chalcogenide (boron nitride nano-based), or

4) 메탈폼을

Figure 112020502935482-pat00010
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하고자 하는것이다4) Metal foam
Figure 112020502935482-pat00010
After coating with a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution and drying, d. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coating film is coated to make the metal foam hydrophobic and b. It is intended to construct a metal foam coated with chalcogenide (boron nitride nano-based), D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated carbon.

본 발명은 메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을 보다 내식성, 항균성, 강도성, (전기 전도성), 방열성, 내화학성, 내마모성, 내열성, 열전도성 등이 우수하고 보다 에너지 저장 및 수소 저장 기능, 담수화 기능, 수질 및 공기 정화 기능, 매연 저감 기능, 방음기능, 발열기능, 충격 흡수 기능, 수소 제조 기능, 산소 제조 기능이 우수하면서 필요시 전자파 차폐나 소수성의 특성이 나타나도록 구성하여 보다 안전하고 효능적인 수소 저장체나 에너지 저장체, 건축용 거푸집, 슈퍼 커패시터 전극재, 방열판, 수질 및 공기 정화용 필터, 담수화 필터, 매연 저감 필터, 방음재, 충격 흡수재, 발열재, 수소 제조제, 산소 제조제 등을 구성할수 있는 보다 효능적인 메탈폼을 구성하는것이 목적인바The present invention is a metal form (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels It is composed of microporous foam of the desired shape) with superior corrosion resistance, antibacterial properties, strength, (electrical conductivity), heat dissipation, chemical resistance, abrasion resistance, heat resistance, thermal conductivity, and more energy storage and hydrogen storage functions, and desalination functions. , Water quality and air purification function, smoke reduction function, sound insulation function, heat generation function, shock absorption function, hydrogen production function, oxygen production function are excellent. More that can constitute storage or energy storage, construction form, super capacitor electrode material, heat sink, filter for water and air purification, desalination filter, smoke reduction filter, soundproofing material, shock absorber, heating material, hydrogen production agent, oxygen production agent, etc. The purpose is to construct an effective metal foam.

본 발명을 구성하는데 있어In constructing the present invention

1) 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드) 중에서 1가지 이상을 선택하여 구성한 칼코게 나이드의 특성: 광촉매이며 반도체로써 내식성, 항균성, 강도성, 전기 전도성, 방열성, 내화학성, 내마모성, 내열성, 열전도성, 자외선 차단이 우수하고 금속 표면에 점착성이 우수하며 수소 저장 및 에너지 저장 기능이 우수하고 담수화 기능, 수질 및 공기 정화 기능 등이 우수하며 근적외선 및 자외선의 빛을 흡수하여 광촉매 작용을 하여 공기 중의 수분(H2O)을 분해하여 슈퍼 항균성의 특성을 나타내는 히드록실 라디칼(OH-)을 발생시켜서 항균성을 나타낸다.1) A knife composed of nanosheets or nano powders ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide). Characteristics of cogenide: It is a photocatalyst, and as a semiconductor, it has excellent corrosion resistance, antibacterial properties, strength, electrical conductivity, heat dissipation, chemical resistance, abrasion resistance, heat resistance, thermal conductivity, UV protection, excellent adhesion to metal surfaces, and hydrogen storage and energy storage functions. hydroxyl radical (OH -) excellent and showing a desalination capabilities, water and air purification functions such as excellent, and the characteristics of the super antimicrobial by the photocatalytic action to absorb light in the near infrared and ultraviolet light degradation of moisture (H 2 O) in the air To generate antimicrobial properties.

2) ⑤BNN(질화 붕소 나노 분말) ⑥BNNS(질화 붕소 나노시트) ⑦BNNT(질화 붕소 나노 튜브) 중에서 1가지 이상을 선택하여 구성한 질화 붕소 나노계의 특성: 절연체로써 내식성, 강도성, 방열성, 내화학성, 내마모성, 내열성, 열전도성 등이 우수하고 방사능 차폐 기능, 수소 저장 및 에너지 저장 기능, 담수화 기능 등이 우수하다.2) ⑤BNN (boron nitride nanopowder) ⑥BNNS (boron nitride nanosheet) ⑦BNNT (boron nitride nanotubes). Characteristics of boron nitride nano-based composition consisting of at least one selected from: Corrosion resistance, strength, heat dissipation, chemical resistance as an insulator, It has excellent abrasion resistance, heat resistance, and thermal conductivity, and has excellent radiation shielding function, hydrogen storage and energy storage function, and desalination function.

3) 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소의 특성: 전기 전도성, 강도성, 방열성, 열전도성이 우수하고 수소 저장 기능, 에너지 저장 기능, 담수화 기능이 우수하고, 칼코게 나이드(① MoS2 ② WS2 ③ MoSe2 ④ WSe2 중에서 1가지 이상을 선택하여 구성)에 그래핀을 혼합시키게 되면 광촉매이며 반도체인 칼코게 나이드는 그래핀과 반응하여 근적외선 및 자외선의 빛은 물론 가시광선의 빛까지 보다 많은 빛을 흡수하여 공기중의 수분(2H2O)을 분해하여 수소(2H2)와 산소(O2)를 발생시키면서 또한 항균성의 특성을 나타내는 히드록실 라디칼(OH-)을 발생시켜서 항균성을 나타낸다.3) Characteristics of carbon composed by selecting one or more of carbon nanotubes or graphene: excellent electrical conductivity, strength, heat dissipation, thermal conductivity, hydrogen storage function, energy storage function, desalination function, and chalcogenide When graphene is mixed with (① MoS 2 ② WS 2 ③ MoSe 2 ④ WSe 2 ), it is a photocatalyst, and chalcogenide, a semiconductor, reacts with graphene to produce visible light as well as near-infrared and ultraviolet light. generate - a hydroxyl radical (OH) and absorbs more light from the line light decomposition of moisture (2H 2 O) in the air, while generating hydrogen (2H 2) and oxygen (O 2) also indicates the characteristics of the antimicrobial To show antibacterial properties.

4) 실란의 특성: 소수성의 특성을 나타낸다.4) Characteristics of silane: It shows hydrophobic properties.

본 발명은 위에서 서술한 특성을 메탈폼에 나타나도록 구성하고자,The present invention is intended to be configured so that the above-described properties appear on the metal foam

1. 1) 광촉매이며 반도체인 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드)나 ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브), ①~⑦ 중에서 1가지 이상을 선택하여 a. 칼코게 나이드(질화 붕소 나노계)를 구성하거나 또는 2) a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소를 혼합시켜서 b. 칼코게 나이드(질화 붕소 나노계)·탄소를 구성한후,
2. 1) a. 칼코게 나이드(질화 붕소 나노계)를 용매에 첨가 분산시켜서

Figure 112020502935482-pat00011
칼코게 나이드(질화 붕소 나노계) 용액을 구성하거나 또는 2) b. 칼코게 나이드(질화 붕소 나노계)·탄소를 용매에 첨가 분산시켜서
Figure 112020502935482-pat00012
칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성하면서 또한
3)
Figure 112020502935482-pat00013
칼코게 나이드(질화 붕소 나노계) 용액에 소수성 실란 용액을 첨가 혼합시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00014
소수성/칼코게 나이드(질화 붕소 나노계) 용액을 구성하거나 또는 4)
Figure 112020502935482-pat00015
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 소수성 실란 용액을 첨가 혼합시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00016
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후,1. 1) Photocatalyst and semiconductor composed of nanosheets or nano powders ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide) or ⑤ BNN (Boron nitride nanopowder) ⑥ BNNS (boron nitride nanosheet) ⑦ BNNT (boron nitride nanotube), select one or more of ①~⑦ and a. Constituting chalcogenide (boron nitride nano-based) or 2) a. Chalcogenide (boron nitride nano-based) is mixed with carbon composed of at least one carbon nanotube or graphene b. After forming chalcogenide (boron nitride nano-based) carbon,
2. 1) a. By adding and dispersing chalcogenide (boron nitride nano-based) in a solvent
Figure 112020502935482-pat00011
Comprising a chalcogenide (boron nitride nano-based) solution or 2) b. By adding and dispersing chalcogenide (boron nitride nano-based) carbon in a solvent
Figure 112020502935482-pat00012
While constituting a chalcogenide (boron nitride nano-based) carbon solution,
3)
Figure 112020502935482-pat00013
A hydrophobic silane solution is added to the chalcogenide (boron nitride nano-based) solution to show hydrophobic properties.
Figure 112020502935482-pat00014
Constituting a hydrophobic/chalcogenide (boron nitride nano-based) solution or 4)
Figure 112020502935482-pat00015
A hydrophobic silane solution is added and mixed with a chalcogenide (boron nitride nano-based) carbon solution to show hydrophobic properties.
Figure 112020502935482-pat00016
After forming a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution,

3. 1) 메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)에

Figure 112020502935482-pat00017
칼코게 나이드(질화 붕소 나노계) 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성이 나타나도록 구성하여 보다 내식성, 항균성, 강도성 등이 우수하고 자외선 차단이나 방사능 차단 기능을 나타내면서 수소 저장체나 에너지 저장체, 담수화 필터, 수질 및 공기 정화용 필터, 건축용 거푸집 등을 구성할수 있는 보다 효능적인 메탈폼인 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하거나
2) 메탈폼에
Figure 112020502935482-pat00018
칼코게 나이드(질화 붕소 나노계)·탄소 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성이 나타나도록 구성하여 A. 칼코게 나이드(질화 붕소 나노계) 코팅 메탈폼 보다 전자파 차폐 기능과 원적외선이나 음이온을 방출하는 보다 효능적인 메탈폼인 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하거나
3) 메탈폼에
Figure 112020502935482-pat00019
소수성/칼코게 나이드(질화 붕소 나노계) 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성과 소수성의 특성을 나타내는 보다 효능적인 소수성 메탈폼인 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하거나3. 1) Metal foam (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal out of stainless steel, but two or more metals Alloy, composed of microporous foam of the desired shape)
Figure 112020502935482-pat00017
After coating with chalcogenide (boron nitride nano-based) solution and drying, a. By coating a chalcogenide (boron nitride nano-based) coating film, the metal foam a. It is composed to show the characteristics of chalcogenide (boron nitride nano-based), which is more excellent in corrosion resistance, antibacterial properties, strength, etc., and has a function to block UV rays or radiation, while a hydrogen storage body or energy storage body, a desalination filter, a filter for water quality and air purification , A. Chalcogenide (boron nitride nano-based) coated metal foam, which is a more effective metal foam capable of constructing architectural forms, etc.
2) On the metal foam
Figure 112020502935482-pat00018
After coating with a chalcogenide (boron nitride nano-based) carbon solution and drying, b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. It is composed to show the characteristics of chalcogenide (boron nitride nano-based) and carbon, so that A. B, which is a more effective metal foam that has an electromagnetic wave shielding function and emits far-infrared rays or negative ions than chalcogenide (boron nitride nano-based) coated metal foam. Compose a metal foam coated with chalcogenide (boron nitride nano-based) and carbon
3) On the metal foam
Figure 112020502935482-pat00019
After coating with a hydrophobic/chalcogenide (boron nitride nano-based) solution and drying, c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam a. C. Hydrophobic/chalcogenide (boron nitride nano-based), a more effective hydrophobic metal foam that exhibits the characteristics and hydrophobic properties of a chalcogenide (boron nitride nano-based), or

4) 메탈폼에

Figure 112020502935482-pat00020
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액으로 코팅하고 건조시켜서 메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성과 소수성의 특성을 나타내는 보다 효능적인 소수성 메탈폼인 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하고자 하는것이다4) On the metal foam
Figure 112020502935482-pat00020
After coating with a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution and drying, d. Hydrophobic/chalcogenide (boron nitride nano-based)·carbon coating film is coated to make the metal foam b. D. Hydrophobic/chalcogenide (boron nitride nano-based), a more effective hydrophobic metal foam that exhibits the characteristics of carbon and hydrophobicity. will be

메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을 보다 내식성, 항균성, 강도성,(전기 전도성), 방열성, 내화학성, 내마모성, 내열성, 열전도성 등이 우수하고, 보다 에너지 저장 및 수소 저장 기능, 담수화 기능, 수질 및 공기 정화 기능, 매연 저감 기능, 방음기능, 발열기능, 충격 흡수 기능, 수소 제조 기능, 산소 제조 기능이 우수하면서 필요시 전자파 차폐나 소수성의 특성이 나타나도록 구성하여 보다 안전하고 효능적인 수소 저장체나 에너지 저장체, 건축용 거푸집, 슈퍼 커패시터 전극재, 방열판, 수질 및 공기 정화용 필터, 담수화 필터, 매연 저감 필터, 방음재, 충격 흡수재, 발열재, 수소 제조제, 산소 제조제 등을 구성할수 있는 보다 효능적인 메탈폼을 구성하는것이 해결하고자 하는 과제이다.Metal form (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels. (Composed of microporous foam) has better corrosion resistance, antibacterial properties, strength, (electrical conductivity), heat dissipation, chemical resistance, abrasion resistance, heat resistance, thermal conductivity, and more energy storage and hydrogen storage functions, desalination functions, and water quality. And air purification function, smoke reduction function, sound insulation function, heat generation function, shock absorption function, hydrogen production function, and oxygen production function are excellent. Energy storage, construction form, super capacitor electrode material, heat sink, water and air purification filter, desalination filter, smoke reduction filter, sound insulation, shock absorber, heating material, hydrogen production agent, oxygen production agent, etc. Constructing metal foam is a task to be solved.

따라서 본 발명은,Therefore, the present invention,

1. <A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성>1. <A. Composition of metal foam coated with chalcogenide (boron nitride nano-based)>

1단계: a. 칼코게 나이드(질화 붕소 나노계) 제조 단계.Step 1: a. Chalcogenide (boron nitride nano-based) preparation step.

광촉매이며 반도체인 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드)나 ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브) 중에서 1가지 이상을 선택하여 a. 칼코게 나이드(질화 붕소 나노계)를 구성한후Photocatalyst and semiconductor composed of nanosheets or nano powders ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide) or ⑤ BNN (boron nitride nanoparticles) Powder) ⑥ BNNS (boron nitride nanosheets) ⑦ BNNT (boron nitride nanotubes) by selecting one or more of a. After constructing chalcogenide (boron nitride nano-based)

2단계 :

Figure 112020502935482-pat00021
칼코게 나이드(질화 붕소 나노계) 용액 제조 단계Step 2:
Figure 112020502935482-pat00021
Steps for preparing a chalcogenide (boron nitride nano-based) solution

a. 칼코게 나이드(질화 붕소 나노계)를 NMP(1-메틸-2-피롤리돈)이나 DMF(디메틸 포름 아마이드) 또는 THF(테트라 하이드로 퓨란), 알콜, 물, PVA(폴리비닐알콜), PEG(폴리에틸렌 글리콜) 중에서 1가지 이상을 선택하여 구성한 용매에 첨가하고 소듐 도데이도 설페스트(SDS)와 같은 계면 활성제를 첨가 교반 및 초음파로 분산시켜서

Figure 112020502935482-pat00022
칼코게 나이드(질화 붕소 나노계) 용액을 구성한후a. Chalcogenide (boron nitride nano-based) NMP (1-methyl-2-pyrrolidone), DMF (dimethyl formamide) or THF (tetrahydrofuran), alcohol, water, PVA (polyvinyl alcohol), PEG ( Polyethylene glycol), and add a surfactant such as sodium dodeido sulfest (SDS) to the solvent, and disperse by stirring and ultrasonic waves.
Figure 112020502935482-pat00022
After forming a chalcogenide (boron nitride nano-based) solution

3단계: A. 칼코게 나이드(질화 붕소 나노계) 코팅가 코팅된 메탈폼 제조 단계Step 3: A. Manufacturing step of metal foam coated with chalcogenide (boron nitride nano-based) coating

메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을

Figure 112020502935482-pat00023
칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 메탈폼으로 구성한 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼Metal form (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels. Of microporous foam)
Figure 112020502935482-pat00023
After being immersed in a chalcogenide (boron nitride nano-based) solution and dried, a. By coating a chalcogenide (boron nitride nano-based) coating film, the metal foam a. A. A metal foam coated with chalcogenide (boron nitride nano-based) consisting of metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based)

2. <B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성>2. <B. Composition of metal foam coated with chalcogenide (boron nitride nano-based) and carbon>

1단계: b. 칼코게 나이드(질화 붕소 나노계)·탄소 제조 단계.
A. 칼코게 나이드(질화 붕소 나노계) 코팅 메탈폼 구성에 있어서 1단계에서 구성한 a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소를 혼합시켜서 b. 칼코게 나이드(질화 붕소 나노계)·탄소를 구성한후Step 1: b. Chalcogenide (boron nitride nano-based), carbon manufacturing step.
A. In the composition of the chalcogenide (boron nitride nano-based) coated metal foam, a. Chalcogenide (boron nitride nano-based) is mixed with carbon composed of at least one carbon nanotube or graphene b. After forming chalcogenide (boron nitride nano-based) carbon

2단계:

Figure 112020502935482-pat00024
칼코게 나이드(질화 붕소 나노계)·탄소 용액 제조 단계
b. 칼코게 나이드(질화 붕소 나노계)·탄소를 NMP, DMF, THF, 알콜, 물, 폴리비닐알콜, 폴리에틸렌 글리콜 중에서 1가지 이상을 선택하여 구성한 용매에 첨가하고 계면 활성제(SDS)를 첨가 교반 및 초음파로 분산시켜서
Figure 112020502935482-pat00025
칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후,Step 2:
Figure 112020502935482-pat00024
Preparation of chalcogenide (boron nitride nano-based) carbon solution
b. Add chalcogenide (boron nitride nano-based) carbon to a solvent composed of at least one selected from NMP, DMF, THF, alcohol, water, polyvinyl alcohol, and polyethylene glycol, and a surfactant (SDS) is added to the solution, stirring and ultrasonic waves. By dispersing it into
Figure 112020502935482-pat00025
After forming a chalcogenide (boron nitride nano-based) carbon solution,

3단계: B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 제조 단계
메탈폼을

Figure 112020502935482-pat00026
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 메탈폼으로 구성한 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼Step 3: B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00026
After being immersed in a chalcogenide (boron nitride nano-based) carbon solution and dried, b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam composed of metal foam that exhibits the characteristics of carbon

3. <C. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅가 코팅된 메탈폼 구성>3. <C. Composition of metal foam coated with hydrophobic/chalcogenide (boron nitride nano-based) coating>

1단계:

Figure 112020502935482-pat00027
소수성/칼코게 나이드(질화 붕소 나노계) 용액 제조 단계.
A. 칼코게 나이드(질화 붕소 나노계) 코팅 메탈폼 구성에 있어서 2단계에서 구성한
Figure 112020502935482-pat00028
칼코게 나이드(질화 붕소 나노계 용액에 (메톡시 실란이나 에톡시 실란을 알콜이나 물 중에서 1가지 이상으로 구성한 용매에 첨가 분산시켜 구성한)소수성 실란 용액을 첨가 분산시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00029
소수성/칼코게 나이드(질화 붕소 나노계) 용액을 구성한후Stage 1:
Figure 112020502935482-pat00027
Hydrophobic/chalcogenide (boron nitride nano-based) solution preparation step.
A. Chalcogenide (boron nitride nano-based) coated metal foam composition was constructed in step 2
Figure 112020502935482-pat00028
A hydrophobic silane solution (consisting of adding and dispersing methoxy silane or ethoxy silane in a solvent consisting of at least one in alcohol or water) to a boron nitride nano-based solution is added and dispersed to exhibit hydrophobic properties.
Figure 112020502935482-pat00029
After forming a hydrophobic/chalcogenide (boron nitride nano-based) solution

2단계: C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 제조 단계
메탈폼을

Figure 112020502935482-pat00030
소수성/칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 보다 효능적인 소수성 메탈폼으로 구성한 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼.Step 2: C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00030
It is immersed in a hydrophobic/chalcogenide (boron nitride nano-based) solution, dried, and then c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam has hydrophobic properties and a. C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam composed of more efficient hydrophobic metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based).

4. <D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성>4. <D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam composition>

1단계:

Figure 112020502935482-pat00031
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액 제조 단계
B. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅 메탈폼 구성에 있어서 2단계에서 구성한
Figure 112020502935482-pat00032
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 (메톡시 실란이나 에톡시 실란을 알콜이나 물 중에서 1가지 이상으로 구성한 용매에 첨가 분산시켜 구성한)소수성 실란 용액을 첨가 분산시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00033
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후Stage 1:
Figure 112020502935482-pat00031
Hydrophobic/chalcogenide (boron nitride nano-based) carbon solution manufacturing step
B. Chalcogenide (boron nitride nano-based) carbon coating
Figure 112020502935482-pat00032
A hydrophobic silane solution (consisting of adding and dispersing methoxysilane or ethoxysilane in a solvent consisting of one or more in alcohol or water) is added and dispersed to a chalcogenide (boron nitride nano-based) carbon solution to exhibit hydrophobic properties.
Figure 112020502935482-pat00033
After forming a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution

2단계: D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 제조 단계
메탈폼을

Figure 112020502935482-pat00034
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 소수성 메탈폼으로 구성한 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼Step 2: D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00034
It is dipped in a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution, dried, and placed on the surface of the pores of the metal foam. d. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coating film is coated to make the metal foam hydrophobic and b. D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam composed of a more efficient hydrophobic metal foam that exhibits the characteristics of carbon.

1. 본 발명인 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼은1. The present invention, A. Chalcogenide (boron nitride nano-based) coated metal foam

메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nd, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)에 1) 광촉매이며 반도체인 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드)나 2) ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브), ①~⑦ 중에서 1가지 이상을 선택하여 구성한 a. 칼코게 나이드(질화 붕소 나노계) 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성이 나타나도록 구성하여 메탈폼이 보다 내식성, 항균성, 강도성, 열전도성, 방열성 등이 우수하고 자외선 차단이나 방사능 차단 기능을 나타내면서 수소 저장체나 에너지 저장체, 담수화 필터, 수질 및 공기 정화용 필터, 건축용 거푸집, 슈퍼 커패시터 전극재, 방열판, 수질 및 공기 정화용 필터, 담수화 필터, 매연 저감 필터, 방음재, 충격 흡수재, 발열재, 수소 제조제, 산소 제조제 등을 구성할수 있는 보다 효능적인 메탈폼으로 구성되어서 기존 메탈폼 보다 여러 분야에 활용할수 있어 효과적이다Metal foam (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nd, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels. 1) Photocatalyst and semiconductor composed of nanosheets or nano powders ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten Diselenide) or 2) ⑤ BNN (boron nitride nanopowder) ⑥ BNNS (boron nitride nanosheet) ⑦ BNNT (boron nitride nanotubes), composed of at least one selected from ①~⑦. The metal foam is formed by coating with chalcogenide (boron nitride nano-based) a. It is composed to show the characteristics of chalcogenide (boron nitride nano-based), so that the metal foam is more excellent in corrosion resistance, antibacterial properties, strength, thermal conductivity, and heat dissipation, and shows UV blocking or radiation blocking functions, while hydrogen storage or energy storage, Desalination filter, water and air purification filter, building formwork, super capacitor electrode material, heat sink, water quality and air purification filter, desalination filter, smoke reduction filter, soundproofing material, shock absorber, heating material, hydrogen manufacturing agent, oxygen manufacturing agent, etc. It is composed of more effective metal foam that can be used, so it is effective because it can be used in various fields than existing metal foam.

2. B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼은
메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소를 혼합시켜 구성한 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 A. 칼코게 나이드(질화 붕소 나노계) 코팅 메탈폼 보다 탄소(탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성)의 특성인 전자파 차폐 기능과 원적외선 및 음이온을 발생시키는 보다 효능적인 메탈폼으로 구성하여서 여러 분야에 사용할수 있어 효과적이다2. B. Chalcogenide (boron nitride nano-based), carbon coated metal foam
On the metal foam pore surface a. B. Consisting of mixing chalcogenide (boron nitride nano-based) with carbon composed of at least one selected from carbon nanotubes or graphene b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, A. Compared to a chalcogenide (boron nitride nano-based) coated metal foam, the characteristic of carbon (composed by selecting at least one of carbon nanotubes or graphene) It is effective because it can be used in various fields as it is composed of more effective metal foam that generates electromagnetic wave shielding function and far infrared rays and negative ions.

3. C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼은
메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성과 소수성의 특성이 나타나도록 구성하여서 내식성, 항균성, 강도성, 열전도성, 방열성 등이 우수하면서 소수성을 나타내는 메탈폼으로 구성되어서 소수성이 필요한 여러 분야에 사용할수 있어 효과적이다3. C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam
On the surface of the pores of the metal foam c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam a. It is composed of a metal foam that exhibits excellent corrosion resistance, antibacterial properties, strength, thermal conductivity, heat dissipation, and hydrophobic properties by showing the characteristics of chalcogenide (boron nitride nano-based) and hydrophobic properties. Can be effective

4. D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼은
메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성과 소수성의 특성이 나타나도록 구성하여서 내식성, 항균성, 강도성, 열전도성 등이 우수하면서 전자파 차폐 기능을 나타내며 또한 소수성을 나타내는 메탈폼으로 되어서 여러 분야에 사용할수 있어 효과적이다4. D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam
On the surface of the pores of the metal foam d. Hydrophobic/chalcogenide (boron nitride nano-based)·carbon coating film is coated to make the metal foam b. It is composed of chalcogenide (boron nitride nano-based), carbon and hydrophobic properties, so it has excellent corrosion resistance, antibacterial properties, strength, and thermal conductivity, as well as electromagnetic wave shielding function, and is a metal foam that exhibits hydrophobic properties. It is effective because it can be used for

본 발명은 메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을 보다 내식성, 항균성, 강도성, (전기 전도성), 방열성, 내화학성, 내마모성, 내열성, 열전도성 등이 우수하고 보다 에너지 저장 및 수소 저장 기능, 담수화 기능, 수질 및 공기 정화 기능, 매연 저감 기능, 방음기능, 발열기능, 충격 흡수 기능, 수소 제조 기능, 산소 제조 기능이 우수하면서 필요시 전자파 차폐나 소수성의 특성이 나타나도록 구성하여 보다 안전하고 효능적인 수소 저장체나 에너지 저장체, 건축용 거푸집, 슈퍼 커패시터 전극재, 방열판 수질 및 공기 정화용 필터, 담수화 필터, 매연 저감 필터, 방음재, 충격 흡수재, 발열재, 수소 제조제, 산소 제조제 등을 구성할 수 있는 보다 효능적인 메탈폼인 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼이나 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 또는 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하는것이 목적으로The present invention is a metal form (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels It is composed of microporous foam of the desired shape) with superior corrosion resistance, antibacterial properties, strength, (electrical conductivity), heat dissipation, chemical resistance, abrasion resistance, heat resistance, thermal conductivity, and more energy storage and hydrogen storage functions, and desalination functions. , Water quality and air purification function, smoke reduction function, sound insulation function, heat generation function, shock absorption function, hydrogen production function, oxygen production function are excellent. More that can constitute storage or energy storage, construction form, super capacitor electrode material, heat sink filter for water and air purification, desalination filter, smoke reduction filter, sound insulation material, shock absorber, heating material, hydrogen production agent, oxygen production agent, etc. Efficient metal foam A. Chalcogenide (boron nitride nano-based) coated metal foam or B. Chalcogenide (boron nitride nano-based) carbon coated metal foam or C. Hydrophobic/chalcogenide (nitridation) Boron nano-based) coated metal foam D. To construct a hydrophobic/chalcogenide (boron nitride nano-based)-carbon coated metal foam

본 발명을 구성하는데 있어In constructing the present invention

1. 1) 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드) 중에서 1가지 이상을 선택하여 구성한 칼코게 나이드의 특성: 광촉매이며 반도체로써 내식성, 항균성, 강도성, 전기 전도성, 방열성, 내화학성, 내마모성, 내열성, 열전도성, 자외선 차단이 우수하고 금속 표면에 점착성이 우수하며, 수소 저장 기능 및 에너지 저장 기능이 우수하고, 담수화 기능, 수질 및 공기 정화 기능이 우수하며 근적외선 및 자외선의 빛을 흡수하여 광촉매 작용을 하여 공기 중의 수분(H2O)을 분해하여 슈퍼 항균성의 특성을 나타내는 히드록실 라디칼(OH-)을 발생시켜서 항균성을 나타낸다1. 1) Composition of nanosheets or nano powders ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide). Characteristics of the composed chalcogenide: As a photocatalyst, it is a semiconductor and has excellent corrosion resistance, antibacterial properties, strength, electrical conductivity, heat dissipation, chemical resistance, abrasion resistance, heat resistance, thermal conductivity, UV protection, excellent adhesion to metal surfaces, and hydrogen storage function and Hydroxyl radical showing super antibacterial properties by decomposing moisture (H 2 O) in the air by acting as a photocatalyst by absorbing near-infrared and ultraviolet light, and has excellent energy storage function, desalination function, water quality and air purification function. (OH -) by generating a shows an antimicrobial

2) ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브) 중에서 1가지 이상을 선택하여 구성한 질화 붕소 나노계의 특성: 절연체로써 내식성, 강도성, 방열성, 내화학성, 내마모성, 내열성, 열전도성이 우수하고 수소 저장 기능, 에너지 저장 기능, 담수화 기능이 우수하고 칼코게 나이드(① MoS2 ② WS2 ③ MoSe2 ④ WSe2 중에서 1가지 이상을 선택하여 구성)에 그래핀을 혼합시키게 되면 광촉매이며 반도체인 칼코게 나이드는 그래핀과 반응하여 근적외선 및 자외선의 빛은 물론 가시광선의 빛까지 보다 많은 빛을 흡수하여 공기중의 수분(2H2O)을 분해하여 수소(2H2)와 산소(O2)를 발생시키면서 또한 항균성의 특성을 나타내는 히드록실 라디칼(OH-)을 발생시켜서 항균성을 나타낸다.2) ⑤ BNN (boron nitride nanopowder) ⑥ BNNS (boron nitride nanosheet) ⑦ BNNT (boron nitride nanotubes) selected from one or more boron nitride nano-based characteristics: corrosion resistance as an insulator, strength, heat dissipation, Excellent chemical resistance, abrasion resistance, heat resistance, thermal conductivity, hydrogen storage function, energy storage function, desalination function, and chalcogenide (1 or more selected from among ① MoS 2 ② WS 2 ③ MoSe 2 ④ WSe 2) When graphene is mixed with graphene, the chalcogenide, which is a photocatalyst and a semiconductor, reacts with graphene to absorb more light from near-infrared and ultraviolet light as well as visible light to decompose moisture in the air (2H 2 O) to decompose hydrogen. (2H 2) and by raising the oxygen (O 2) in addition, the hydroxyl radical (OH -) represents the characteristics of the antimicrobial by generating a shows an antimicrobial.

4) 실란의 특성: 소수성의 특성을 나타낸다.4) Characteristics of silane: It shows hydrophobic properties.

본 발명은 위에서 서술한 특성을 메탈폼에 나타나도록 구성하여 메탈폼을 보다 내식성, 항균성, 강도성 등이 우수하면서 필요시 소수성의 특성이 나타나도록 구성하여 보다 효능적인 수소 저장체 및 에너지 저장체 등을 구성할수 있는 보다 효능적인 메탈폼을 구성하고자The present invention is constructed so that the above-described properties appear on the metal foam, so that the metal foam has more excellent corrosion resistance, antibacterial properties, strength, etc., and has hydrophobic properties when necessary, so that a more efficient hydrogen storage body and an energy storage body, etc. To construct a more efficient metal foam that can be used

1) 나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드) ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브) 중에서 1가지 이상을 선택하여 a. 칼코게 나이드(질화 붕소 나노계)를 구성하거나 또는1) Consisting of nanosheets or nanopowder ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide) ⑤ BNN (boron nitride nanopowder) ⑥ BNNS (boron nitride nanosheets) ⑦ Select one or more of BNNTs (boron nitride nanotubes) to a. Constituting chalcogenide (boron nitride nano-based), or

2) a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소를 혼합시켜서 b. 칼코게 나이드(질화 붕소 나노계)·탄소를 구성한후,2) a. Chalcogenide (boron nitride nano-based) is mixed with carbon composed of at least one carbon nanotube or graphene b. After forming chalcogenide (boron nitride nano-based) carbon,

2. 1) a. 칼코게 나이드(질화 붕소 나노계)를 용매에 첨가하고 분산시켜서

Figure 112020502935482-pat00035
칼코게 나이드(질화 붕소 나노계) 용액을 구성하거나 2) b. 칼코게 나이드(질화 붕소 나노계)·탄소를 용매에 첨가하고 분산시켜서
Figure 112020502935482-pat00036
칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성하면서 또한2. 1) a. By adding chalcogenide (boron nitride nano-based) to the solvent and dispersing it
Figure 112020502935482-pat00035
Constituting a chalcogenide (boron nitride nano-based) solution or 2) b. By adding chalcogenide (boron nitride nano-based) carbon to the solvent and dispersing it
Figure 112020502935482-pat00036
While constituting a chalcogenide (boron nitride nano-based) carbon solution,

3)

Figure 112020502935482-pat00037
칼코게 나이드(질화 붕소 나노계) 용액에 소수성 실란 용액을 첨가 혼합시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00038
소수성/칼코게 나이드(질화 붕소 나노계) 용액을 구성하거나 또는
Figure 112020502935482-pat00039
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 소수성 실란 용액을 첨가 혼합시켜서 소수성의 특성을 나타내는
Figure 112020502935482-pat00040
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후3)
Figure 112020502935482-pat00037
A hydrophobic silane solution is added to the chalcogenide (boron nitride nano-based) solution to show hydrophobic properties.
Figure 112020502935482-pat00038
Constituting a hydrophobic/chalcogenide (boron nitride nano-based) solution, or
Figure 112020502935482-pat00039
A hydrophobic silane solution is added and mixed with a chalcogenide (boron nitride nano-based) carbon solution to show hydrophobic properties.
Figure 112020502935482-pat00040
After forming a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution

3. 1) 메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을

Figure 112020502935482-pat00041
칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성이 나타나도록 구성하여 - 메탈폼이 보다 내식성, 항균성, 강도성, (전기 전도성), 방열성, 내화학성, 내마모성, 내열성, 열전도성, (자외선 차단)이 우수하고 수소 저장 기능 및 에너지 저장 기능이 우수하며, 담수화 기능, 수질 및 공기 정화 기능이 우수하면서 보다 효능적인 수소 저장체나 에너지 저장체, 건축용 거푸집, 슈퍼 커패시터 전극재, 방열판, 수질 및 공기 정화용 필터, 담수화 필터, 매연 저감 필터, 방음재, 충격 흡수재, 발열재, 수소 제조제, 산소 제조제 등을 구성할수 있는 보다 효능적인 메탈폼인 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하거나3. 1) Metal foam (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal out of stainless steel, but two or more metals It is composed of microporous foam of the desired shape with an alloy)
Figure 112020502935482-pat00041
After being immersed in a chalcogenide (boron nitride nano-based) solution and dried, a. By coating a chalcogenide (boron nitride nano-based) coating film, the metal foam a. It is composed to show the characteristics of chalcogenide (boron nitride nano-based)-Metal foam is more resistant to corrosion, antibacterial, strength, (electrical conductivity), heat dissipation, chemical resistance, abrasion resistance, heat resistance, thermal conductivity, and (ultraviolet ray blocking). Excellent hydrogen storage function and energy storage function, excellent desalination function, water quality and air purification function, and more efficient hydrogen storage or energy storage body, building formwork, super capacitor electrode material, heat sink, filter for water and air purification, Metal foam coated with A. Chalcogenide (boron nitride nano-based), a more effective metal foam that can constitute desalination filters, smoke reduction filters, sound insulation materials, shock absorbers, heating materials, hydrogen production agents, oxygen production agents, etc. Configure or

2) 메탈폼을

Figure 112020502935482-pat00042
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성이 나타나도록 구성하여 - A. 칼코게 나이드(질화 붕소 나노계) 코팅 메탈폼의 특성외에 탄소(탄소나노 튜브나 그래핀 중에서 1가지 이상)의 특성이 나타나도록 구성하여 전자파 차폐 기능을 나타내면서, 원적외선 및 음이온을 방출하는 보다 효능적인 메탈폼인 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하거나 또는2) Metal foam
Figure 112020502935482-pat00042
After being immersed in a chalcogenide (boron nitride nano-based) carbon solution and dried, b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. Chalcogenide (boron nitride nano-based) and carbon characteristics appear-A. In addition to the characteristics of chalcogenide (boron nitride nano-based) coated metal foam, carbon (one or more of carbon nanotubes or graphene) B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam, which is a more effective metal foam that emits far-infrared rays and negative ions while showing the electromagnetic wave shielding function or

3) 메탈폼을

Figure 112020502935482-pat00043
소수성/칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성과 소수성의 특성을 나타내는 보다 효능적인 소수성 메탈폼인 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하거나 또는3) Metal foam
Figure 112020502935482-pat00043
It is immersed in a hydrophobic/chalcogenide (boron nitride nano-based) solution, dried, and then on the surface of the pores of the metal foam c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam a. C. Hydrophobic / Chalcogenide (boron nitride nano-based) is a more effective hydrophobic metal foam that exhibits the characteristics and hydrophobic properties of a chalcogenide (boron nitride nano-based), or

4) 메탈폼을

Figure 112020502935482-pat00044
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성과 소수성의 특성을 나타내는 보다 효능적인 소수성 메탈폼인 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하고자 하는것이다4) Metal foam
Figure 112020502935482-pat00044
After immersion in a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution and drying, the metal foam b. D. Hydrophobic/chalcogenide (boron nitride nano-based), a more effective hydrophobic metal foam that exhibits the characteristics of carbon and hydrophobicity. will be

따라서 본 발명은Therefore, the present invention

1. <A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성> 1. <A. Composition of metal foam coated with chalcogenide (boron nitride nano-based)>

1단계: a. 칼코게 나이드(질화 붕소 나노계) 제조 단계Step 1: a. Chalcogenide (boron nitride nano-based) manufacturing step

나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드)나 ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브), ①~⑦ 중에서 1가지 이상을 선택하여 a. 칼코게 나이드(질화 붕소 나노계)를 구성한후Consisting of nanosheets or nanopowder ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide) or ⑤ BNN (boron nitride nanopowder) ⑥ BNNS (Boron nitride nanosheet) ⑦ Select one or more of BNNT (boron nitride nanotubes), ①~⑦, and a. After constructing chalcogenide (boron nitride nano-based)

2단계:

Figure 112020502935482-pat00045
칼코게 나이드(질화 붕소 나노계) 용액 제조 단계Step 2:
Figure 112020502935482-pat00045
Steps for preparing a chalcogenide (boron nitride nano-based) solution

a. 칼코게 나이드(질화 붕소 나노계)(1~5wt%)을 NMP(1-메틸-2-피롤리돈)이나 DMF(디메틸 포름 아마이드) 또는 THF(테트라 하이드로 퓨란), 알콜, 물, PVA(폴리비닐알콜), PEG(폴리에틸렌 글리콜) 중에서 1가지 이상을 선택하여 구성한 용매에 첨가하고 소듐 도데이도 설페스트(SDS)와 같은 계면 활성제(0.0001~0.002wt%)를 첨가하고 교반 및 초음파로 분산시켜서

Figure 112020502935482-pat00046
칼코게 나이드(질화 붕소 나노계) 용액을 구성한후a. Chalcogenide (boron nitride nano-based) (1 to 5 wt%) is mixed with NMP (1-methyl-2-pyrrolidone) or DMF (dimethyl formamide) or THF (tetrahydrofuran), alcohol, water, PVA (poly). Vinyl alcohol), PEG (polyethylene glycol), one or more selected and added to the composition solvent, and a surfactant (0.0001~0.002wt%) such as sodium dodeido sulfest (SDS) is added, stirred and dispersed by ultrasonic waves.
Figure 112020502935482-pat00046
After forming a chalcogenide (boron nitride nano-based) solution

3단계: A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 제조 단계
메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을

Figure 112020502935482-pat00047
칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 보다 효능적인 메탈폼으로 구성한 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼Step 3: A. Manufacturing step of metal foam coated with chalcogenide (boron nitride nano-based)
Metal form (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels. Of microporous foam)
Figure 112020502935482-pat00047
After being immersed in a chalcogenide (boron nitride nano-based) solution and dried, a. By coating a chalcogenide (boron nitride nano-based) coating film, the metal foam a. A. A metal foam coated with chalcogenide (boron nitride nano-based), which is composed of a more efficient metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based).

2. <B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성>2. <B. Composition of metal foam coated with chalcogenide (boron nitride nano-based) and carbon>

1단계: b. 칼코게 나이드(질화 붕소 나노계)·탄소 제조 단계.
A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성에 있어서 1단계에서 구성한 a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소(0.1~5wt%)를 첨가하여 혼합시켜서 b. 칼코게 나이드(질화 붕소 나노계)·탄소를 구성한후Step 1: b. Chalcogenide (boron nitride nano-based), carbon manufacturing step.
A. In the composition of the metal foam coated with chalcogenide (boron nitride nano-based), a. Chalcogenide (boron nitride nano-based) is mixed by adding carbon (0.1 to 5 wt%) composed of one or more selected carbon nanotubes or graphene b. After forming chalcogenide (boron nitride nano-based) carbon

2단계:

Figure 112020502935482-pat00048
칼코게 나이드(질화 붕소 나노계)·탄소 용액 제조 단계
b. 칼코게 나이드(질화 붕소 나노계)·탄소(1~5wt%)를 NMP, DMF, THF, 알콜, 물, 폴리비닐알콜, 폴리에틸렌 글리콜 중에서 1가지 이상을 선택하여 구성한 용매에 첨가하고 소듐 도데이도 설페스트(SDS)와 같은 계면 활성제(0.0001~0.02wt%)를 첨가하고 교반 및 초음파로 분산시켜서
Figure 112020502935482-pat00049
칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후Step 2:
Figure 112020502935482-pat00048
Preparation of chalcogenide (boron nitride nano-based) carbon solution
b. Add chalcogenide (boron nitride nano-based) and carbon (1-5 wt%) to a solvent composed of at least one selected from NMP, DMF, THF, alcohol, water, polyvinyl alcohol, and polyethylene glycol. By adding a surfactant (0.0001~0.02wt%) such as pest (SDS) and dispersing it by stirring and ultrasonication,
Figure 112020502935482-pat00049
After forming a chalcogenide (boron nitride nano-based) carbon solution

3단계: B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 제조 단계
메탈폼을

Figure 112020502935482-pat00050
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 메탈폼으로 구성한 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼Step 3: B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00050
After being immersed in a chalcogenide (boron nitride nano-based) carbon solution and dried, b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam composed of more efficient metal foam that exhibits the properties of carbon

3. <C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성>3. <C. Composition of metal foam coated with hydrophobic/chalcogenide (boron nitride nano-based)>

1단계:

Figure 112020502935482-pat00051
소수성/칼코게 나이드(질화 붕소 나노계) 용액 제조 단계.
A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성에 있어서 2단계에서 구성한
Figure 112020502935482-pat00052
칼코게 나이드(질화 붕소 나노계) 용액에 소수성 실란 용액(알콜이나 물 중에서 1가지 이상으로 구성한 용매에 에톡시 실란이나 메톡시 실란(2~6wt%)을 첨가 교반하여 구성)을 1:1 중량비로 첨가 교반하여 소수성의 특성을 나타내는
Figure 112020502935482-pat00053
소수성/칼코게 나이드(질화 붕소 나노계) 용액을 구성한후Stage 1:
Figure 112020502935482-pat00051
Hydrophobic/chalcogenide (boron nitride nano-based) solution preparation step.
A. In the composition of the metal foam coated with chalcogenide (boron nitride nano-based),
Figure 112020502935482-pat00052
A 1:1 weight ratio of a hydrophobic silane solution (consisting of adding ethoxy silane or methoxy silane (2 to 6 wt%) to a solvent composed of one or more in alcohol or water) to a chalcogenide (boron nitride nano-based) solution. Addition to and stirring to show the hydrophobic properties
Figure 112020502935482-pat00053
After forming a hydrophobic/chalcogenide (boron nitride nano-based) solution

2단계: C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 제조 단계.
메탈폼을

Figure 112020502935482-pat00054
소수성/칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 보다 효능적인 소수성 메탈폼으로 구성한 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼Step 2: C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam manufacturing step.
Metal foam
Figure 112020502935482-pat00054
It is immersed in a hydrophobic/chalcogenide (boron nitride nano-based) solution, dried, and then on the surface of the pores of the metal foam c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam has hydrophobic properties and a. C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam composed of more efficient hydrophobic metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based)

4. <D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성>4. <D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam composition>

1단계:

Figure 112020502935482-pat00055
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액 제조 단계
B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성에 있어서 2단계에서 구성한
Figure 112020502935482-pat00056
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 소수성 실란 용액(알콜이나 물 중에서 1가지 이상으로 구성한 용매에 에톡시 실란이나 메톡시 실란(2~6wt%)을 첨가 교반하여 구성)을 1:1 중량비로 첨가 교반하여 소수성의 특성을 나타내는
Figure 112020502935482-pat00057
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성한후Stage 1:
Figure 112020502935482-pat00055
Hydrophobic/chalcogenide (boron nitride nano-based) carbon solution manufacturing step
B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam composition in the second step
Figure 112020502935482-pat00056
A hydrophobic silane solution (consisting of adding ethoxy silane or methoxy silane (2 to 6 wt%) to a solvent composed of at least one in alcohol or water and stirring) to a carbon solution of chalcogenide (boron nitride nano-based): 1: Addition and stirring at a weight ratio of 1 to show hydrophobic properties
Figure 112020502935482-pat00057
After forming a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution

2단계: D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 제조 단계Step 2: D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam manufacturing step

메탈폼을

Figure 112020502935482-pat00058
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 소수성 메탈폼으로 구성한 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼Metal foam
Figure 112020502935482-pat00058
It is dipped in a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution, dried, and placed on the surface of the pores of the metal foam. d. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coating film is coated to make the metal foam hydrophobic and b. D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam composed of a more efficient hydrophobic metal foam that exhibits the characteristics of carbon.

Claims (4)

<A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성>
1단계: a. 칼코게 나이드(질화 붕소 나노계) 제조 단계
나노시트나 나노 분말로 구성된 ① MoS2(이황화 몰리브덴) ② WS2(이황화 텅스텐) ③ MoSe2(몰리브덴 디셀레나이드) ④ WSe2(텅스텐 디셀레나이드)나 ⑤ BNN(질화 붕소 나노 분말) ⑥ BNNS(질화 붕소 나노시트) ⑦ BNNT(질화 붕소 나노 튜브), ①~⑦ 중에서 1가지 이상을 선택하여 a. 칼코게 나이드(질화 붕소 나노계)를 구성하는 1단계
2단계:
Figure 112020502935482-pat00059
칼코게 나이드(질화 붕소 나노계) 용액 제조 단계.
a. 칼코게 나이드(질화 붕소 나노계)(1~5wt%)를 NMP, DMF, THF, 알콜, 물, 폴리비닐알콜, 폴리에틸렌 글리콜 중에서 1가지 이상을 선택하여 구성한 용매에 첨가하고 교반 및 초음파로 분산시켜서
Figure 112020502935482-pat00060
칼코게 나이드(질화 붕소 나노계) 용액을 구성하는 2단계
3단계: A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 제조 단계
메탈폼(Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, 스테인리스강 중에서 1가지 금속이나 2가지 이상의 금속 합금으로 원하는 형태의 미세다공의 폼으로 구성)을
Figure 112020502935482-pat00061
칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 보다 효능적인 메탈폼인 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하는 3단계
본 발명은 위에서 서술한 1단계, 2단계, 3단계 제조 공정을 거쳐서 메탈폼 기공 표면에 a. 칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 a. 칼코게 나이드(질화 붕소 나노계)의 특성이 나타나도록 구성하여 보다 효능적인 메탈폼으로 구성한 A. 칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼<A. Composition of metal foam coated with chalcogenide (boron nitride nano-based)>
Step 1: a. Chalcogenide (boron nitride nano-based) manufacturing step
Consisting of nanosheets or nanopowder ① MoS 2 (molybdenum disulfide) ② WS 2 (tungsten disulfide) ③ MoSe 2 (molybdenum diselenide) ④ WSe 2 (tungsten diselenide) or ⑤ BNN (boron nitride nanopowder) ⑥ BNNS (Boron nitride nanosheet) ⑦ Select one or more of BNNT (boron nitride nanotubes), ①~⑦, and a. Step 1 to construct chalcogenide (boron nitride nano-based)
Step 2:
Figure 112020502935482-pat00059
Chalcogenide (boron nitride nano-based) solution preparation step.
a. Chalcogenide (boron nitride nano-based) (1~5wt%) is added to the composition solvent by selecting at least one of NMP, DMF, THF, alcohol, water, polyvinyl alcohol, and polyethylene glycol, and dispersing it by stirring and ultrasonication.
Figure 112020502935482-pat00060
Two steps to construct a chalcogenide (boron nitride nano-based) solution
Step 3: A. Manufacturing step of metal foam coated with chalcogenide (boron nitride nano-based)
Metal form (Mg, Al, Cu, Ni, Ag, Pt, Fe, Ti, Zn, Sn, Pd, Nb, Co, Cr, Si, In, one metal or two or more metal alloys among stainless steels. Of microporous foam)
Figure 112020502935482-pat00061
After being immersed in a chalcogenide (boron nitride nano-based) solution and dried, a. By coating a chalcogenide (boron nitride nano-based) coating film, the metal foam a. A. A more effective metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based). Three steps to construct a metal foam coated with chalcogenide (boron nitride nano-based)
In the present invention, through the first, second, and third step manufacturing processes described above, a. By coating a chalcogenide (boron nitride nano-based) coating film, the metal foam a. A. A metal foam coated with chalcogenide (boron nitride nano-based), which is composed of a more effective metal foam with the characteristics of chalcogenide (boron nitride nano-based). <B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성>
1단계: b. 칼코게 나이드(질화 붕소 나노계)·탄소 제조 단계
청구항 1에 있어서 1단계에서 구성한 a. 칼코게 나이드(질화 붕소 나노계)에 탄소나노 튜브나 그래핀 중에서 1가지 이상을 선택하여 구성한 탄소(0.1~5wt%)를 첨가 혼합시켜서 b. 칼코게 나이드(질화 붕소 나노계)·탄소를 구성하는 1단계
2단계:
Figure 112020502935482-pat00062
칼코게 나이드(질화 붕소 나노계)·탄소 용액 제조 단계
b. 칼코게 나이드(질화 붕소 나노계)·탄소(1~5wt%)를 NMP, DMF, THF, 알콜, 물, 폴리비닐알콜, 폴리에틸렌 글리콜 중에서 1가지 이상을 선택하여 구성한 용매에 첨가하고 교반 및 초음파로 분산시켜서
Figure 112020502935482-pat00063
칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성하는 2단계
3단계: B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 제조 단계
메탈폼을
Figure 112020502935482-pat00064
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 메탈폼인 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하는 3단계
본 발명은 위에서 서술한 1단계, 2단계, 3단계 제조 공정을 거쳐서 메탈폼 기공 표면에 b. 칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 메탈폼으로 구성한 B. 칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼<B. Composition of metal foam coated with chalcogenide (boron nitride nano-based) and carbon>
Step 1: b. Chalcogenide (boron nitride nano-based) carbon manufacturing step
The method according to claim 1, configured in step 1 a. By adding and mixing carbon (0.1-5wt%) composed of one or more selected carbon nanotubes or graphene to chalcogenide (boron nitride nano-based) b. The first step of forming chalcogenide (boron nitride nano-based) and carbon
Step 2:
Figure 112020502935482-pat00062
Preparation of chalcogenide (boron nitride nano-based) carbon solution
b. Chalcogenide (boron nitride nano-based) carbon (1-5 wt%) was added to a solvent composed of at least one selected from NMP, DMF, THF, alcohol, water, polyvinyl alcohol, and polyethylene glycol, followed by stirring and ultrasonication. By dispersing
Figure 112020502935482-pat00063
Chalcogenide (boron nitride nano-based), two steps of forming a carbon solution
Step 3: B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00064
After being immersed in a chalcogenide (boron nitride nano-based) carbon solution and dried, b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. Chalcogenide (boron nitride nano-based), a more effective metal foam that exhibits the properties of carbon, B. Chalcogenide (boron nitride nano-based), three steps of forming a carbon-coated metal foam
In the present invention, the metal foam pores surface b. By coating a chalcogenide (boron nitride nano-based) carbon coating film, the metal foam b. B. Chalcogenide (boron nitride nano-based), carbon-coated metal foam composed of more efficient metal foam that exhibits the properties of carbon <C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 구성>
1단계:
Figure 112020502935482-pat00065
소수성/칼코게 나이드(질화 붕소 나노계) 용액 제조 단계
청구항 1에 있어서 2단계에서 구성한 칼코게 나이드(질화 붕소 나노계) 용액에 소수성 실란 용액(알콜이나 물 중에서 1가지 이상으로 구성한 용매에 에톡시 실란이나 메톡시 실란(2~6wt%)을 첨가 교반하여 구성)을 1:1 중량비로 첨가 교반하여 소수성의 특성을 나타내는
Figure 112020502935482-pat00066
소수성/칼코게 나이드(질화 붕소 나노계) 용액을 구성하는 1단계
2단계: C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼 제조 단계
메탈폼을
Figure 112020502935482-pat00067
소수성/칼코게 나이드(질화 붕소 나노계) 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 보다 효능적인 소수성 메탈폼인 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼을 구성하는 2단계
본 발명은 위에서 서술한 1단계, 2단계 제조 공정을 거쳐서 메탈폼 기공 표면에 c. 소수성/칼코게 나이드(질화 붕소 나노계) 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 a. 칼코게 나이드(질화 붕소 나노계)의 특성을 나타내는 보다 효능적인 소수성 메탈폼으로 구성한 C. 소수성/칼코게 나이드(질화 붕소 나노계)가 코팅된 메탈폼.<C. Composition of metal foam coated with hydrophobic/chalcogenide (boron nitride nano-based)>
Stage 1:
Figure 112020502935482-pat00065
Hydrophobic/chalcogenide (boron nitride nano-based) solution preparation step
The stirring of adding a hydrophobic silane solution (ethoxy silane or methoxy silane (2 to 6 wt%) to a solvent composed of at least one in alcohol or water) to the chalcogenide (boron nitride nano-based) solution configured in step 2 according to claim 1 Composition) in a 1:1 weight ratio and agitated to show the hydrophobic properties.
Figure 112020502935482-pat00066
Step 1 of constructing a hydrophobic/chalcogenide (boron nitride nano-based) solution
Step 2: C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00067
It is immersed in a hydrophobic/chalcogenide (boron nitride nano-based) solution, dried, and then c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam has hydrophobic properties and a. C. A more efficient hydrophobic metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based). The second step of constructing a metal foam coated with hydrophobic/chalcogenide (boron nitride nano-based)
According to the present invention, the metal foam pores surface c. By coating a hydrophobic/chalcogenide (boron nitride nano-based) coating film, the metal foam has hydrophobic properties and a. C. Hydrophobic/chalcogenide (boron nitride nano-based) coated metal foam composed of more efficient hydrophobic metal foam that exhibits the characteristics of chalcogenide (boron nitride nano-based). <D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 구성>
1단계:
Figure 112020502935482-pat00068
소수성/칼코게 나이드(질화 붕소 나노계) 용액 제조 단계
청구항 2에 있어서 2단계에서 구성한
Figure 112020502935482-pat00069
칼코게 나이드(질화 붕소 나노계)·탄소 용액에 소수성 실란 용액(알콜이나 물 중에서 1가지 이상으로 구성한 용매에 에톡시 실란이나 메톡시 실란(2~6wt%)을 첨가 교반하여 구성)을 첨가 교반하여 소수성의 특성을 나타내는
Figure 112020502935482-pat00070
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액을 구성하는 1단계
2단계: D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼 제조 단계
메탈폼을
Figure 112020502935482-pat00071
소수성/칼코게 나이드(질화 붕소 나노계)·탄소 용액에 침지시키고 건조시켜서 메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 소수성 메탈폼인 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼을 구성하는 2단계
본 발명은 위에서 서술한 1단계, 2단계 제조 공정을 거쳐서 메탈폼 기공 표면에 d. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소 코팅막을 코팅시켜서 메탈폼이 소수성의 특성과 b. 칼코게 나이드(질화 붕소 나노계)·탄소의 특성을 나타내는 보다 효능적인 소수성 메탈폼으로 구성한 D. 소수성/칼코게 나이드(질화 붕소 나노계)·탄소가 코팅된 메탈폼.<D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam composition>
Stage 1:
Figure 112020502935482-pat00068
Hydrophobic/chalcogenide (boron nitride nano-based) solution preparation step
The composition of claim 2 in step 2
Figure 112020502935482-pat00069
Addition of a hydrophobic silane solution (consisting of adding and stirring ethoxy silane or methoxy silane (2-6 wt%) to a solvent composed of one or more in alcohol or water) to the chalcogenide (boron nitride nano-based) carbon solution and stirring Indicating the hydrophobic properties by
Figure 112020502935482-pat00070
Hydrophobic/chalcogenide (boron nitride nano-based), the first step of forming a carbon solution
Step 2: D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam manufacturing step
Metal foam
Figure 112020502935482-pat00071
It is dipped in a hydrophobic/chalcogenide (boron nitride nano-based) carbon solution, dried, and placed on the surface of the pores of the metal foam. d. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coating film is coated to make the metal foam hydrophobic and b. D. Hydrophobic/chalcogenide (boron nitride nano-based), a more effective hydrophobic metal foam that exhibits the characteristics of carbon, 2 steps to construct a carbon-coated metal foam
In the present invention, the metal foam pores surface d. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coating film is coated to make the metal foam hydrophobic and b. D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon-coated metal foam composed of more efficient hydrophobic metal foam that exhibits the characteristics of carbon.
KR1020190069292A 2019-06-12 2019-06-12 D. Hydrophobic/chalcogenide (boron nitride nano-based), carbon coated metal foam. outside KR102242135B1 (en)