KR102190580B1 - Complex pigments of Mica coated by Titanium dioxide and Cosmetics composition containing the same - Google Patents

Complex pigments of Mica coated by Titanium dioxide and Cosmetics composition containing the same Download PDF

Info

Publication number
KR102190580B1
KR102190580B1 KR1020180101335A KR20180101335A KR102190580B1 KR 102190580 B1 KR102190580 B1 KR 102190580B1 KR 1020180101335 A KR1020180101335 A KR 1020180101335A KR 20180101335 A KR20180101335 A KR 20180101335A KR 102190580 B1 KR102190580 B1 KR 102190580B1
Authority
KR
South Korea
Prior art keywords
titanium dioxide
coated
mica
pink
skin
Prior art date
Application number
KR1020180101335A
Other languages
Korean (ko)
Other versions
KR20200024531A (en
Inventor
김종근
조현대
한호영
최세범
남세희
Original Assignee
주식회사 코스메카코리아
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 코스메카코리아 filed Critical 주식회사 코스메카코리아
Priority to KR1020180101335A priority Critical patent/KR102190580B1/en
Publication of KR20200024531A publication Critical patent/KR20200024531A/en
Application granted granted Critical
Publication of KR102190580B1 publication Critical patent/KR102190580B1/en

Abstract

본 발명은 이산화티탄이 코팅된 복합안료 및 이를 포함한 화장료 조성물에 관한 것으로서, 마이카와 같은 안료에 이산화티탄을 코팅처리하되, 코어 마이카를 핑크 마이카로 대체하거나 또는 복합안료의 최외곽 코팅재로 핑크 마이카를 사용함으로써 과도한 광택이나 번들거림이 없이 적정한 은폐력과 광채를 주고, 피부색을 구현하여 자연스러운 화장을 제공할 수 있는 보정용 메이크업 소재이다.The present invention relates to a titanium dioxide-coated composite pigment and a cosmetic composition including the same, wherein titanium dioxide is coated on a pigment such as mica, but the core mica is replaced with pink mica, or pink mica is used as the outermost coating material of the composite pigment. It is a makeup material for correction that can provide natural makeup by realizing skin color and providing adequate hiding power and radiance without excessive gloss or greasyness.

Description

이산화티탄이 코팅된 복합안료 및 이를 포함한 화장료 조성물{Complex pigments of Mica coated by Titanium dioxide and Cosmetics composition containing the same}Complex pigments of Mica coated by Titanium dioxide and Cosmetics composition containing the same}

본 발명은 이산화티탄이 코팅된 복합안료 및 이를 포함한 화장료 조성물에 관한 것으로서, 더욱 상세하게는 마이카와 같은 안료에 이산화티탄을 코팅처리하되, 코어 마이카를 핑크 마이카로 대체하거나 또는 복합안료의 최외곽 코팅재로 핑크 마이카를 사용함으로써 과도한 광택이나 번들거림이 없이 적정한 은폐력과 광채를 주고, 피부색을 구현하여 자연스러운 화장을 제공할 수 있는 보정용 메이크업 소재로 사용되는 이산화티탄이 코팅된 복합안료 및 이를 포함한 화장료 조성물에 관한 것이다.The present invention relates to a composite pigment coated with titanium dioxide and a cosmetic composition including the same, and more particularly, a pigment such as mica is coated with titanium dioxide, but the core mica is replaced with pink mica, or the outermost coating material of the composite pigment A composite pigment coated with titanium dioxide used as a makeup material for correction that can provide natural makeup by realizing skin color and providing adequate hiding power and radiance without excessive gloss or grease by using pink mica will be.

화장료는 크게 베이스 메이크업 화장료와 색조메이크업 화장료로 구분한다. 베이스 메이크업 화장료는 얼굴 전체에 도포하여 기미, 주름, 점등을 가려주어 깨끗한 피부표현을 하는 것이 목적이며, 색조메이크업 화장료는 얼굴의 구성부분 만에 도포하는 것으로, 예를 들면 입술을 보다 아름답게 하기 위해 사용하는 립스틱, 눈매를 아름답게 하는 아이섀도우, 볼 주위에 음영과 함께 화사함을 주어 아름답게 보이도록 하는 블러셔 등이 있다.Cosmetics are largely divided into base makeup cosmetics and color makeup cosmetics. Base makeup cosmetics are applied to the entire face to hide spots, wrinkles, and lighting to express clean skin, while color makeup cosmetics are applied to only the components of the face, and are used to make lips more beautiful, for example. There are lipsticks, eye shadows that make the eyes beautiful, and blushers that give brightness with shades around the cheeks to make them look beautiful.

이와 같은 피부결점인 점, 기미, 주근깨 등을 커버하고 피부에 윤기를 주면서도 자연스러운 화장을 제공할 수 있는 메이크업 화장료에 대한 다양한 연구가 이루어지고 있다.Various studies are being conducted on makeup cosmetics that can cover such skin flaws, spots, spots, freckles, and provide natural makeup while giving skin shine.

특히, 최근 들어 통상적으로 굴절률이 높은 이산화티탄 즉, 백색안료를 이용한 화장료에 대한 시도가 활발하게 이루어지고 있는데, 이산화티탄의 높은 굴절률로 인하여 피부결점 커버는 되지만 그로 인하여 부자연스러운 피부표현이 나타나고, 간섭 펄의 매끄러운 표면으로 인하여 화사함이 떨어지며, 도포 후 피지에 의해 쉽게 번들거리는 단점을 보여주고 있다.In particular, recently, attempts have been actively made on cosmetics using titanium dioxide, that is, a white pigment, which has a high refractive index, and it covers skin flaws due to the high refractive index of titanium dioxide, but due to the high refractive index of the titanium dioxide, unnatural skin expression appears and interference. Due to the smooth surface of the pearl, the brightness is reduced, and after application, it is easily greasy by sebum.

또한, 백색 마이카에 기반을 둔 진주광택안료는 뛰어난 간섭 효과를 발생시키며, 즉각적인 밝기 및 휘도를 제공하는 톤업 제품에 일반적으로 사용되나, 사용자의 피부 톤의 변화없이 종래의 진주광택안료를 사용하여 자연스러운 피부 톤을 구현하는 것은 어려운 문제가 있다. 즉, 진주광택안료의 과도한 밝기와 광채는 사용자의 자연 피부톤과 광채가 자연스럽게 섞이도록 하기 위해서는 조정되어야 한다.In addition, pearlescent pigments based on white mica generate excellent interference effects and are generally used in tone-up products that provide immediate brightness and luminance, but natural pearlescent pigments are used without changing the user's skin tone. Implementing skin tone is a difficult problem. That is, the excessive brightness and luster of the pearlescent pigment must be adjusted in order to blend the natural skin tone and luster of the user naturally.

또한, 종래의 복합안료는 피부색 구현을 위하여 복합안료의 밝기를 조정하고 입사광의 투과를 증가시키고자, 이산화티탄(TiO2)으로 코팅된 얇은 판형 마이카에 코팅되는 이산화티탄의 함량 비율을 감소시키거나 불균일한 코팅면을 갖도록 제조되었다. 그러나, 이와 같은 복합안료는 종래의 진주광택안료의 부자연스러움은 개선하였으나, 밝기와 광채는 여전히 피부가 갖는 자연톤을 왜곡시켜 자연스런 피부톤 구현과는 거리가 있었다.In addition, in order to adjust the brightness of the complex pigment and increase the transmission of incident light in order to realize skin color, the conventional complex pigment reduces the content ratio of titanium dioxide coated on a thin plate mica coated with titanium dioxide (TiO2) or is uneven. It was made to have one coated side. However, such a complex pigment improved the unnaturalness of the conventional pearlescent pigment, but the brightness and luster still distorted the natural tone of the skin and were far from realizing a natural skin tone.

또한, 종래의 복합안료나 진주광택안료들은 과도한 광택이나 번들거림으로 인하여 피부색을 나타내는 자연스러운 화장을 제공하는 것이 어려운 문제가 있을 뿐만 아니라, 색상 구현을 위하여 산화철과 같은 별도의 색소염료로 코팅처리 하여야 하는 문제도 있다.In addition, conventional complex pigments or pearlescent pigments have a problem in that it is difficult to provide natural makeup that represents skin color due to excessive gloss or gloss, and a problem that requires coating treatment with a separate pigment dye such as iron oxide for color realization. There is also.

이에, 본 출원인은 이산화티탄의 코팅만으로 원래 피부 톤을 바꾸지 않으면서 "lit from within(내향 반사빛)"을 얻기 위해 피부 표면과 안료에서 반사되는 가시광선의 투과율과 반사율을 제어하여 투과 반사광이 기존 피부 톤과 유사하게 보정되도록 하였다.Therefore, the applicant of the present invention controls the transmittance and reflectance of visible light reflected from the skin surface and pigment in order to obtain "lit from within" without changing the original skin tone with only titanium dioxide coating. It was corrected to be similar to the tone.

독일연방공화국 특허 제 2,214,545호 및 제 2,522,572Federal Republic of Germany patents 2,214,545 and 2,522,572 미합중국 특허 제 4,038,099호United States Patent No. 4,038,099 대한민국공개특허 10-2013-0060583호Korean Patent Publication No. 10-2013-0060583 대한민국공개특허 10-2012-0019924호Korean Patent Publication No. 10-2012-0019924 대한민국공개특허 10-2014-0070035호Korean Patent Publication No. 10-2014-0070035 대한민국공개특허 10-2005-0093557호Korean Patent Publication No. 10-2005-0093557

본 발명은 상기의 문제점을 해결하기 위한 것으로, 제1목적은 마이카와 같은 안료에 이산화티탄을 코팅처리하되, 일반적인 백색의 코어 마이카를 핑크 마이카로 대체하여 적정한 은폐력을 주면서도 두께도 작고 자연스러운 광채와 피부톤 표현이 가능한 이산화티탄이 코팅된 복합안료 및 이를 포함한 화장료 조성물을 제공하는 것이다.The present invention is to solve the above problems, and the first purpose is to coat a pigment such as mica with titanium dioxide, but replace the general white core mica with pink mica to provide adequate hiding power while providing a small thickness and natural radiance and skin tone. It is to provide a composite pigment coated with titanium dioxide and a cosmetic composition including the same.

또한, 본 발명의 제2목적은 복합안료의 최외곽 코팅재로 핑크 마이카를 사용함으로써 과도한 광택이나 번들거림이 없이 적정한 은폐력과 자연스러운 광채를 주고, 피부색을 구현하여 자연스러운 화장을 제공할 수 있는 보정용 메이크업 소재로 사용되는 이산화티탄이 코팅된 복합안료 및 이를 포함한 화장료 조성물을 제공하는 것이다. In addition, the second object of the present invention is to use pink mica as the outermost coating material of the complex pigment to give proper hiding power and natural glow without excessive gloss or greasyness, and to provide a natural makeup material by realizing skin color. It is to provide a composite pigment coated with titanium dioxide and a cosmetic composition including the same.

그러나 본 발명의 목적들은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the objects of the present invention are not limited to the above-mentioned objects, and other objects that are not mentioned will be clearly understood by those skilled in the art from the following description.

상기의 목적을 달성하기 위해, To achieve the above object,

본 발명에 따른 이산화티탄이 코팅된 복합안료는, 핑크 마이카를 포함하여 구성되는 것을 특징으로 한다.The titanium dioxide-coated composite pigment according to the present invention is characterized in that it comprises pink mica.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료에서,In addition, in the titanium dioxide-coated composite pigment according to the present invention,

상기 핑크 마이카는 이산화티탄이 균일하게 코팅되는 코어재인 것을 특징으로 한다.The pink mica is characterized in that the core material is uniformly coated with titanium dioxide.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료에서,In addition, in the titanium dioxide-coated composite pigment according to the present invention,

상기 핑크 마이카는 이산화티탄이 불균일하게 코팅되는 코어재인 것을 특징으로 한다.The pink mica is characterized in that the core material is non-uniformly coated with titanium dioxide.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료에서,In addition, in the titanium dioxide-coated composite pigment according to the present invention,

상기 핑크 마이카는 상기 복합안료의 코팅된 이산화티탄의 코팅 표면에 코팅된 최외곽재인 것을 특징으로 한다.The pink mica is characterized in that the outermost material coated on the coated surface of titanium dioxide coated with the composite pigment.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료에서,In addition, in the titanium dioxide-coated composite pigment according to the present invention,

상기 복합안료의 이산화티탄이 코팅되는 코어재는 백색 마이카 또는 핑크 마이카인 것을 특징으로 한다.The core material coated with the titanium dioxide of the composite pigment is characterized in that white mica or pink mica.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료에서,In addition, in the titanium dioxide-coated composite pigment according to the present invention,

상기 핑크 마이카는 이산화티탄이 균일하게 코팅되는 코어재 및 코팅된 이산화티탄의 코팅 표면에 코팅된 최외곽재인 것을 특징으로 한다.The pink mica is characterized in that the core material is uniformly coated with titanium dioxide and the outermost material coated on the coated surface of the coated titanium dioxide.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료에서,In addition, in the titanium dioxide-coated composite pigment according to the present invention,

상기 복합안료는
이산화티탄이 코팅된 핑크 마이카를 포함하여 구성되어,
상기 핑크 마이카에서 직접 반사되는 핑크색채를 띠는 반사광과 이산화티탄에서 직접 반사되는 반사광 및 투과되어 피부에서 반사되는 반사광의 중첩 및 간섭에 의해, 투명성을 구비하면서도 자연 피부색 구현이 가능한 것을 특징으로 한다.The composite pigment is
Consists of titanium dioxide-coated pink mica,
It is characterized in that it is possible to realize a natural skin color while having transparency by overlapping and interference of the reflected light having a pink color directly reflected from the pink mica, the reflected light directly reflected from titanium dioxide, and the reflected light transmitted and reflected from the skin.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료를 포함하는 화장료 조성물인 것을 특징으로 한다.In addition, it is characterized in that it is a cosmetic composition comprising a composite pigment coated with titanium dioxide according to the present invention.

본 발명의 실시예에 따른 이산화티탄이 코팅된 복합안료는, 핑크 마이카를 코어재 또는 최외곽재로 사용함으로써 마이카 자체의 두께가 작더라도 적정한 은폐력을 주면서도 원래 피부색을 반사시키게 되므로 자연스러운 광채와 피부톤 표현이 가능한 효과가 있다.The titanium dioxide-coated composite pigment according to an embodiment of the present invention uses pink mica as a core material or outermost material, so that even if the thickness of the mica itself is small, it reflects the original skin color while providing an appropriate hiding power, thus expressing natural radiance and skin tone. This has a possible effect.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료는, 핑크 마이카로부터 직접 반사되는 반사광과 투과되어 반사되는 투과 반사광의 중첩 및 간섭에 의해 상용자의 피부색이 구현되므로 피부색상에 따른 보정용 메이크업 소재로 사용될 수 있고, 자연스러운 화장을 제공할 수 있는 효과가 있다.In addition, the titanium dioxide-coated composite pigment according to the present invention is used as a makeup material for correction according to the skin color because the skin color of the commercial person is realized by the overlap and interference of the reflected light reflected from the pink mica and the transmitted reflected light transmitted and reflected. It has the effect of being able to provide natural makeup.

도 1의 (a),(b),(c),(d),(e)는 본 발명에 따라 제조된 복합안료의 단면형상을 개략적으로 나타낸 도면으로서, (a)는 이산화티탄이 코팅된 제1 복합안료, (b)는 이산화티탄이 코팅된 제2 복합안료, (c)는 이산화티탄이 코팅된 제3 복합안료, (d),(e)는 제3 복합안료의 다른 실시예이다.
도 2의 (a),(b)는 분말화된 핑크 마이카(a)와 이산화티탄으로 코팅처리된 핑크 마이카(b) 및 이들의 표면처리상태 이미지(SEM이미지)를 나타낸 도면,
도 3의 (a),(b)는 핑크 마이카(a)와 이산화티탄으로 코팅처리된 핑크 마이카(b)가 피부에 적용한 예를 나타내는 도면,
도 4는 실시예와 비교예의 화장료를 바르기 전후의 피부의 변화를 표시하는 히스토그램.
도 5의 (a),(b),(c),(d),(e)는 입사되는 가시광선이 복합안료에서 반사되는 형태를 개략적으로 도시한 것으로, (a)는 핑크 마이카 코어재에 이산화티탄의 균일한 코팅면을 형성한 경우, (b)는 핑크 마이카 코어재에 이산화티탄의 불균일한 코팅면을 형성한 경우, (c)는 백색 마이카 코어재에 이산화티탄의 불균일한 코팅면을 형성하고 최외곽에 핑크 마이카를 얇고 균일하게 코팅한 경우, (d)는 핑크 마이카 코어재에 이산화티탄의 불균일한 코팅면을 형성하고 최외곽에 핑크 마이카를 얇고 균일하게 코팅한 경우, (e)는 핑크 마이카 코어재에 이산화티탄의 균일한 코팅면을 형성하고 최외곽에 핑크 마이카를 얇고 균일하게 코팅한 경우이다.Figure 1 (a), (b), (c), (d), (e) is a schematic view showing the cross-sectional shape of the composite pigment prepared according to the present invention, (a) is a titanium dioxide coated The first composite pigment, (b) is a second composite pigment coated with titanium dioxide, (c) is a third composite pigment coated with titanium dioxide, and (d) and (e) are other examples of the third composite pigment. .
2A and 2B are views showing powdered pink mica (a) and pink mica coated with titanium dioxide (b) and images of their surface treatment (SEM images);
3A and 3B are diagrams showing examples in which a pink mica (a) and a pink mica coated with titanium dioxide (b) are applied to the skin.
Fig. 4 is a histogram showing changes in skin before and after applying cosmetics of Examples and Comparative Examples.
Figure 5 (a), (b), (c), (d), (e) schematically shows the form in which the incident visible light is reflected from the composite pigment, and (a) is the pink mica core material. When a uniform coating surface of titanium dioxide is formed, (b) is a case where an uneven coating surface of titanium dioxide is formed on the pink mica core material, and (c) is a non-uniform coating surface of titanium dioxide on the white mica core material. In the case of forming and coating pink mica thinly and uniformly on the outermost part, (d) is a case where an uneven coating surface of titanium dioxide is formed on the pink mica core material, and pink mica is thinly and uniformly coated on the outermost part, Is a case where a uniform coating surface of titanium dioxide is formed on the pink mica core material and a thin and uniform coating of pink mica is applied on the outermost part.

이하, 본 발명의 바람직한 실시예의 상세한 설명은 첨부된 도면들을 참조하여 설명할 것이다. 하기에서 본 발명을 설명함에 있어서, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다.
Hereinafter, a detailed description of a preferred embodiment of the present invention will be described with reference to the accompanying drawings. In the following description of the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, a detailed description thereof will be omitted.

본 발명에 따른 이산화티탄이 코팅된 복합안료에서 핑크 마이카(pink mica)에 이산화티탄을 코팅하는 방법은 통상적인 아래의 코팅방법과 동일하므로, 이에 대한 구체적인 설명은 생략한다.
In the titanium dioxide-coated composite pigment according to the present invention, since the method of coating titanium dioxide on pink mica is the same as the conventional coating method below, a detailed description thereof will be omitted.

(a) 안료 현탁액 제조단계(a) pigment suspension preparation step

비이커에 증류수와 안료를 투입하여 교반하면서 가온하여 안료 현탁액을 제조한다.Distilled water and pigment are added to a beaker and heated while stirring to prepare a pigment suspension.

이때, 증류수는 7 ~12ℓ, 바람직하게는 10ℓ, 안료는 50 ~ 120g, 바람직하게는 100g이고, 안료 수용액의 온도는 75~85℃, 바람직하게는 80℃, pH는 1~3, 바람직하게는 1~2가 되도록 하는 것이 바람직하다.At this time, the distilled water is 7 to 12 ℓ, preferably 10 ℓ, the pigment is 50 to 120 g, preferably 100 g, the temperature of the pigment aqueous solution is 75 to 85 °C, preferably 80 °C, the pH is 1 to 3, preferably It is preferable to make it become 1-2.

여기서, 코어로 사용되는 안료 재료는 핑크 마이카, 특히 판상의 핑크 마이카가 바람직하다.Here, the pigment material used as the core is preferably a pink mica, particularly a plate-shaped pink mica.

핑크 마이카는 대한민국 전라남도에서 채굴된 천연운모로서, 광석 상태에서는 약한 광채와 함께 산화되어 색채를 나타낸다. 이 핑크 마이카 광석을 1,000메쉬로 분쇄하여 분말형태로 만들게 되면, 도 2의 (a)에 도시된 바와 같이 짙은 갈색(dark brown)을 나타내게 된다. 즉, 별도의 색소를 첨가하거나 이산화티탄으로 표면처리를 하지 않아도 천연 그대로의 핑크색 색상을 나타낼 뿐만 아니라 투명성을 유지하는 특징이 있다.
Pink mica is a natural mica mined in Jeollanam-do, Korea, and in the state of ore, it is oxidized with a weak glow to show its color. When the pink mica ore is pulverized into 1,000 mesh to form a powder, it exhibits dark brown as shown in Fig. 2(a). That is, even if a separate pigment is not added or surface treatment is performed with titanium dioxide, it not only exhibits a natural pink color but also maintains transparency.

(b) 핑크 마이카 안료에 이산화티탄 전구체 사염화티탄(TiCl4)을 가수분해 반응시켜 표면 처리하는 단계(b) treating the surface by hydrolysis reaction of titanium dioxide precursor titanium tetrachloride (TiCl 4 ) to pink mica pigment

본 발명에 따른 핑크 마이카에 이산화티탄의 전구체인 사염화티탄(TiCl4)을 처리하여 마이카가 균일한 코팅표면을 갖도록 표면처리하기 위하여, 사염화티탄(TiCl4)을 정제수에 완전 용해시켜 사염화티타늄 수용액을 준비하고, 또한 수산화나트륨(NaOH) 수용액을 준비한 다음, 상기 안료 현탁액에 준비한 사염화티타늄 수용액 및 수산화나트륨 수용액을 서서히 동시에 투입하여 가수분해 반응시킨다.
In order to treat the pink mica according to the present invention with titanium tetrachloride (TiCl 4 ), a precursor of titanium dioxide, so that the mica has a uniform coating surface, titanium tetrachloride (TiCl 4 ) is completely dissolved in purified water to prepare an aqueous titanium tetrachloride solution. After preparation, an aqueous sodium hydroxide (NaOH) solution was prepared, and then the prepared titanium tetrachloride aqueous solution and sodium hydroxide aqueous solution were gradually added to the pigment suspension at the same time to undergo a hydrolysis reaction.

이때, 핑크 마이카 안료가 불균일한 코팅표면을 갖도록 하기 위해서는, 표면처리된 안료에 이산화티탄 전구체 사염화티탄(TiCl4)을 가수분해 반응시키되 반응종료 후 교반시켜 불균일한 코팅표면을 갖도록 2차 표면처리 할 수 있다.
At this time, in order to make the pink mica pigment have a non-uniform coating surface, a titanium dioxide precursor titanium tetrachloride (TiCl 4 ) is hydrolyzed to the surface-treated pigment, but after the reaction is finished, a second surface treatment is performed to have a non-uniform coating surface by stirring. I can.

이때, 가수분해 반응하는 과정에서 온도는 75~85℃, 바람직하게는 80℃, pH는 2~5, 바람직하게는 3~4로 조정하여 유지시키는 것이 바람직하다. 반응이 종료된 후 25~40분간, 바람직하게는 30분간 추가 교반한다.
At this time, during the hydrolysis reaction, the temperature is preferably adjusted to 75 to 85°C, preferably 80°C, and the pH to 2 to 5, preferably 3 to 4 to maintain. After completion of the reaction, the mixture is further stirred for 25 to 40 minutes, preferably 30 minutes.

(c) 표면처리된 안료에서 TiO(OH)2를 TiO2로 전환하여 이산화티탄(TiO2)이 코팅된 복합안료 완성단계(c) Completion of a composite pigment coated with titanium dioxide (TiO 2 ) by converting TiO(OH) 2 to TiO 2 in the surface-treated pigment

표면처리된 Pink Mica/2TiO(OH)2 복합안료를 수세, 탈수하고 대략 80~100℃ 온도에서 대략 10~15시간 건조한 후 대략 550 ~ 750℃의 고온으로 대략 30분~1시간 동안 선택적으로 소성처리하여 핑크 마이카에 표면처리된 TiO(OH)2를 TiO2로 전환시킨다.The surface-treated Pink Mica/2TiO(OH) 2 complex pigment is washed with water, dehydrated, dried for about 10 to 15 hours at a temperature of about 80 to 100°C, then selectively fired at a high temperature of about 550 to 750°C for about 30 minutes to 1 hour Treatment to convert the surface-treated TiO(OH) 2 to TiO 2 on the pink mica.

그런 다음, 250메쉬로 된 분급기에서 1회에서 수회에 걸친 분급처리단계를 거쳐 이산화티탄의 함량을 30 ~ 50중량%, 바람직하게는 40 중량% 함유하는 피부톤과 유사한 부드러운 핑크빛 복합안료를 완성 시킨다.Then, through a classification treatment step from once to several times in a 250 mesh classifier, a soft pink complex pigment similar to skin tone containing 30 to 50% by weight, preferably 40% by weight of titanium dioxide is completed. .

또한, 이산화티탄이 코팅된 복합안료에 소수성 및 친수성 특성 또는 피부 친화성을 위한 특성을 부여하기 위한 추가 표면처리를 더 행할 수 있다.In addition, an additional surface treatment to impart properties for hydrophobic and hydrophilic properties or skin affinity to the titanium dioxide-coated composite pigment may be further performed.

상기 표면처리를 통해 제품에서의 상용성을 개선하거나 사용감 및 처방 안정성을 개선시킬 수 있다. 소수성 처리를 위해서는 실란, 실리콘 또는 실리콘 공중합체 등을 이용하고, 피부 친화성을 위해서는 라우로일 라이신, 레시틴 또는 아미노산 유도체를 사용하며, 처방 안정성을 위해서는 금속염을 표면처리하는 것을 포함한다.Through the surface treatment, it is possible to improve the compatibility in products or improve the usability and prescription stability. For hydrophobic treatment, silane, silicone or silicone copolymers are used, lauroyl lysine, lecithin or amino acid derivatives are used for skin affinity, and surface treatment of metal salts is included for formulation stability.

여기서, 이산화티탄이 코팅된 복합안료에 소수성 및 친수성 특성을 부여하기 위한 추가 표면처리는 다음과 같이 행할 수 있다.Here, the additional surface treatment for imparting hydrophobic and hydrophilic properties to the titanium dioxide-coated composite pigment may be performed as follows.

이산화티탄(40%)이 코팅된 복합안료 90 ~ 98 중량%와 소수성 및 친수성 물질인 실리콘, 실란 또는 실리콘 공중합체를 전체 복합안료 중량대비 2 ~ 10 중량%를 믹서기에 넣고 대략 2~10초동안 2~5회 분산처리하고, 이후 건조기에 투입하여 85~100℃로 대략 4~8시간 건조한 다음 추가 분쇄를 대략 3~10초 동안 진행하여 소수성 내지 친수성을 부여한다.Put 90 to 98% by weight of a composite pigment coated with titanium dioxide (40%) and 2 to 10% by weight of a hydrophobic and hydrophilic material, silicone, silane or silicone copolymer based on the total weight of the composite pigment, into a blender for about 2 to 10 seconds. Disperse treatment 2 to 5 times, and then put in a dryer and dried at 85 to 100°C for approximately 4 to 8 hours, and then further pulverized for approximately 3 to 10 seconds to impart hydrophobicity to hydrophilicity.

또한, 피부 친화성을 위한 특성을 부여하기 위한 추가 표면처리는 다음과 같이 행한다.In addition, the additional surface treatment to impart properties for skin affinity is performed as follows.

이산화티탄(40%)이 코팅된 복합안료 90 ~ 98 중량%를 정제수 7~10ℓ에 분산하면서 80℃로 가온시켜 복합안료 현탁액을 준비한다. 또한, 피부 친화성 물질인 라우로일 라이신, 레시틴, 레시틴 유도체, 아미노산 또는 아미노산 유도체를 전체 복합안료 중량대비 2 ~ 10중량%를 수산화나트륨 1중량% 수용액 50~200g에 가온시키면서 투명해질때까지 용해시킨다.A composite pigment suspension is prepared by dispersing 90 to 98% by weight of a composite pigment coated with titanium dioxide (40%) in 7 to 10ℓ of purified water and heating at 80°C. In addition, 2-10% by weight of lauroyl lysine, lecithin, lecithin derivatives, amino acids or amino acid derivatives, which are skin-friendly substances, are dissolved in 50-200 g of an aqueous solution of 1% by weight of sodium hydroxide in 50-200 g of an aqueous solution of 1% by weight of sodium hydroxide based on the weight of the total complex pigment. Let it.

완전하게 용해된 라우로일 라이신, 레시틴, 레시틴 유도체, 아미노산 또는 아미노산 유도체 수용액을 복합안료 현탁액에 정량투입기로 서서히 투입시킨다.A completely dissolved lauroyl lysine, lecithin, lecithin derivative, amino acid or amino acid derivative aqueous solution is slowly added to the complex pigment suspension by a quantitative dispenser.

그런 다음, AlCl3 6H20 2중량% 수용액 100g을 준비하여 정량투입기로 서서히 투입하여 반응을 완성한다. 완성된 반응물은 탈수 및 건조 처리후 믹서기를 사용하여 10~30초간 1~3회 분산시켜 피부 친화성을 부여한다.Then, 100 g of an AlCl 3 6H 2 0 2 wt% aqueous solution is prepared and slowly introduced into a quantitative injector to complete the reaction. The finished reactant is dehydrated and dried, and then dispersed 1 to 3 times for 10 to 30 seconds using a blender to give skin affinity.

본 발명에 따른 복합안료는 일반적인 베이스 메이크업 화장료인 비비크림, 파운데이션, 메이크업 베이스, 투웨이케익, 컴팩트, 루스파우더, 아이새도우 등의 제형 및 스킨케어 제형인 화장수, 로션, 크림, 에센스, 세럼 등에 사용될 수 있으며, 톤업이 개선되고 우수한 피부보정 효과를 얻을 수 있다.The complex pigment according to the present invention can be used in formulations such as BB cream, foundation, makeup base, two-way cake, compact, loose powder, eye shadow, etc., and skin care formulations such as lotions, lotions, creams, essences, serums, etc. In addition, tone-up is improved and excellent skin correction effects can be obtained.

또한, 본 발명에 따른 이산화티탄이 코팅된 복합안료는 뭉침 현상이 없이 고르게 도포되도록 플랫형태로 만들어져 모공이나 주름을 커버하여 매끈한 피부 연출과 맑은 피부톤 연출이 가능하다.In addition, the titanium dioxide-coated composite pigment according to the present invention is made in a flat shape so that it is evenly applied without clumping, so that it covers pores or wrinkles, so that smooth skin and clear skin tone can be produced.

이하, 구체적인 실시예를 결합하여 본 발명을 더 설명하고자 한다. 이러한 실시예는 본 발명을 설명하는 예에 불과하며 본 발명의 범위를 제한하지는 않는다. 아래, 실시예 중에서 구체적 조건을 표기하지 않은 실험방법은 통상의 조건, 또는 제조상에서 제의한 조건에 따라 진행한다. 특별한 설명이 있는 경우를 제외하고, 모든 부수는 중량부이며, 모든 백분비는 중량 백분비이다.
Hereinafter, the present invention will be further described by combining specific examples. These examples are only examples to illustrate the present invention and do not limit the scope of the present invention. In the examples below, the experimental method in which specific conditions are not indicated is carried out according to the usual conditions or the conditions suggested by the manufacturer. Except where otherwise specified, all parts are parts by weight, and all percentages are parts by weight.

<실시예 1><Example 1>

1-1. 이산화티탄이 코팅된 제1 복합안료 제조1-1. Manufacture of the first composite pigment coated with titanium dioxide

비이커에 증류수 10ℓ와 판상 핑크 마이카 안료 100g을 투입하여 교반하면서 가온하여 온도를 80℃, pH를 1 내지 2로 조정한 현탁액을 얻는다.10 L of distilled water and 100 g of plate-shaped pink mica pigment were added to a beaker, and the mixture was heated while stirring to obtain a suspension having a temperature of 80° C. and a pH of 1 to 2.

사염화티탄(TiCl4) 24.0g을 정제수 100g에 완전 용해시켜 사염화티타늄 수용액을 제조하고, 수산화나트륨은 30중량% 수용액으로 완전 용해시켜 준비한다. 상기 현탁액에 준비된 사염화티타늄 수용액과 수산화나트륨 수용액을 정량 투입기를 사용하여 동시에 서서히 투입하여 반응시키고, 반응을 종료한다.A titanium tetrachloride aqueous solution was prepared by completely dissolving 24.0 g of titanium tetrachloride (TiCl 4 ) in 100 g of purified water, and sodium hydroxide was completely dissolved in a 30% by weight aqueous solution. Titanium tetrachloride aqueous solution and sodium hydroxide aqueous solution prepared in the suspension are slowly added at the same time using a quantitative feeder for reaction, and the reaction is terminated.

반응이 종료된 후 증류수로 수세한 뒤 탈수하고, 100℃에서 12시간 건조하고, 750℃에서 1시간 동안 소성하여 코팅표면이 균일한 복합안료(도 1의 (a) 참조)를 완성한다.
After completion of the reaction, it was washed with distilled water, dehydrated, dried at 100° C. for 12 hours, and fired at 750° C. for 1 hour to complete a composite pigment having a uniform coating surface (see FIG. 1(a)).

1-2. 이산화티탄이 코팅된 제2 복합안료 제조1-2. Manufacture of a second composite pigment coated with titanium dioxide

비이커에 증류수 10ℓ와 판상 핑크 마이카 안료 100g을 투입하여 교반하면서 가온하여 온도를 80℃, pH를 1 내지 2로 조정한 현탁액을 얻는다.10 L of distilled water and 100 g of plate-shaped pink mica pigment were added to a beaker, and the mixture was heated while stirring to obtain a suspension having a temperature of 80° C. and a pH of 1 to 2.

사염화티탄(TiCl4) 24.0g을 정제수 100g에 완전 용해시켜 사염화티타늄 수용액을 제조하고, 수산화나트륨은 30중량% 수용액으로 완전 용해시켜 준비한다. 상기 현탁액에 준비된 사염화티타늄 수용액과 수산화나트륨 수용액을 정량 투입기를 사용하여 동시에 서서히 투입하여 반응시키고, 투입이 모두 완료되면 30분동안 추가 교반하고 반응을 종료한다.A titanium tetrachloride aqueous solution was prepared by completely dissolving 24.0 g of titanium tetrachloride (TiCl 4 ) in 100 g of purified water, and sodium hydroxide was completely dissolved in a 30% by weight aqueous solution. Titanium tetrachloride aqueous solution and sodium hydroxide aqueous solution prepared in the suspension were added slowly at the same time using a quantitative feeder to react, and when all the addition was completed, the reaction was further stirred for 30 minutes and the reaction was terminated.

반응이 종료된 후 증류수로 수세한 뒤 탈수하고, 100℃에서 12시간 건조하고, 750℃에서 1시간 동안 소성하여 코팅 표면이 불균일한 복합안료를 완성한다.(도 1의 (b) 참조)
After completion of the reaction, it is washed with distilled water, dehydrated, dried at 100°C for 12 hours, and calcined at 750°C for 1 hour to complete a composite pigment having a non-uniform coating surface (see Fig. 1(b)).

여기서, 판상 핑크 마이카 안료에 1차 이산화티탄을 균일하게 코팅한 다음, 이산화티탄의 균일한 코팅 표면위에 2차 불균일한 코팅 표면을 가진 복합안료를 갖도록 구성할 수도 있음은 물론이다.Here, it goes without saying that the plate-shaped pink mica pigment may be uniformly coated with primary titanium dioxide, and then a composite pigment having a secondary non-uniform coating surface may be formed on the uniform coating surface of titanium dioxide.

상술한 제1 복합안료, 제2 복합안료에서, 핑크 마이카의 두께는 제한은 없으나, 통상적인 백색 마이카에 비해 두께가 상대적으로 얇은 것을 사용해도 자연스러운 화장을 구현하는 적정한 은폐력을 줄 수 있음은 물론이다.
In the above-described first and second composite pigments, the thickness of the pink mica is not limited, but it is of course possible to provide an appropriate hiding power for realizing natural makeup even if a material having a relatively thin thickness compared to a conventional white mica is used. .

1-3. 이산화티탄이 코팅된 제3 복합안료 제조1-3. Manufacture of the third composite pigment coated with titanium dioxide

비이커에 증류수 10ℓ와 판상의 마이카 안료 100g을 투입하여 교반하면서 가온하여 온도를 80℃, pH를 1 내지 2로 조정한 현탁액을 얻는다.10 L of distilled water and 100 g of plate-shaped mica pigment were added to a beaker, and the mixture was heated while stirring to obtain a suspension in which the temperature was adjusted to 80°C and the pH to 1 to 2.

사염화티탄(TiCl4) 24.0g을 정제수 100g에 완전 용해시켜 사염화티타늄 수용액을 제조하고, 수산화나트륨은 30중량% 수용액으로 완전 용해시켜 준비한다. 상기 현탁액에 준비된 사염화티타늄 수용액과 수산화나트륨 수용액을 정량 투입기를 사용하여 동시에 서서히 투입하여 반응시키고, 투입이 모두 완료되면 30분동안 추가 교반하고 반응을 종료한다.A titanium tetrachloride aqueous solution was prepared by completely dissolving 24.0 g of titanium tetrachloride (TiCl 4 ) in 100 g of purified water, and sodium hydroxide was completely dissolved in a 30% by weight aqueous solution. Titanium tetrachloride aqueous solution and sodium hydroxide aqueous solution prepared in the suspension were added slowly at the same time using a quantitative feeder to react, and when all the addition was completed, the reaction was further stirred for 30 minutes and the reaction was terminated.

반응이 종료된 후 증류수로 수세한 뒤 탈수하고, 100℃에서 12시간 건조하고, 750℃에서 1시간 동안 소성하여 코팅 표면이 불균일한 마이카 복합안료를 완성한다.After completion of the reaction, it is washed with distilled water, dehydrated, dried at 100°C for 12 hours, and calcined at 750°C for 1 hour to complete a mica complex pigment having an uneven coating surface.

그런 다음, 완성된 복합안료에 코어 마이카에 비해 상대적으로 두께가 매우 얇은 판상 핑크 마이카 안료를 투입하여 복합안료의 최외곽 표면에 코팅시켜 최종 복합안료를 완성한다.(도 1의 (c) 참조) Then, a plate-shaped pink mica pigment, which has a relatively thin thickness compared to the core mica, is added to the finished composite pigment and coated on the outermost surface of the composite pigment to complete the final composite pigment (see Fig. 1(c)).

이때, 코팅되는 핑크 마이카 안료는, 불균일하게 코팅된 이산화티탄의 코팅면에 코어 마이카와 평행을 유지하도록 코팅되도록 하는 것이 바람직하다. 이는 이산화티탄에 의한 반사광을 줄이고 마이카와 이산화티탄에 의한 반사광들의 상쇄간섭 현상에 의해 자연스러운 피부 톤 구현이 가능하도록 하기 위함이다.
At this time, the pink mica pigment to be coated is preferably coated to maintain parallel to the core mica on the coated surface of the non-uniformly coated titanium dioxide. This is to reduce the reflected light by titanium dioxide and to realize natural skin tone by the destructive interference phenomenon of the reflected light by mica and titanium dioxide.

또한, 도 1의 (d) 및 (e)에 도시된 바와 같이, 제3 복합안료에서, 코어 마이카는 백색 마이카 또는 핑크 마이카 어느 것이나 무방하며, 코어재가 핑크 마이카인 경우에는 균일한 이산화티탄 코팅면을 형성하고 그 코팅면 위에 최외곽재로 두께가 매우 얇은 판상 핑크 마이카 안료를 코팅시키는 것도 가능함은 물론이다.In addition, as shown in (d) and (e) of Figure 1, in the third composite pigment, the core mica may be either white mica or pink mica, and when the core material is pink mica, a uniform titanium dioxide coating surface Of course, it is possible to form and coat the plate-shaped pink mica pigment with a very thin thickness as the outermost material on the coated surface.

여기서, 코어재 또는 최외곽재인 판상 핑크 마이카의 두께 치수가 제한적인 것은 아니다.
Here, the thickness dimension of the plate-shaped pink mica which is the core material or the outermost material is not limited.

도 2의 (a),(b)에는 대략 1,000메쉬의 크기로 분말화된 천연 핑크 마이카(a)와 40%의 이산화티탄으로 코팅처리된 핑크 마이카(b) 및 이들의 표면처리상태 이미지(SEM이미지)가 도시되어 있다.In Figure 2 (a) and (b), natural pink mica powdered to a size of approximately 1,000 mesh (a) and pink mica coated with 40% titanium dioxide (b) and their surface treatment state images (SEM Image) is shown.

또한, 도 3의 (a),(b)에는 핑크 마이카(a)와 이산화티탄으로 코팅처리된 핑크 마이카(b)의 색상과 광채를 확인하기 위하여 피부에 적용한 예를 보여주고 있다. 코어재로 핑크 마이카를 사용한 경우, (a)와 (b) 둘 다 피부 톤과 유사한 구현이 가능함을 확인할 수 있다. In addition, Fig. 3 (a), (b) shows an example applied to the skin in order to check the color and brightness of the pink mica (a) and the pink mica coated with titanium dioxide (b). In the case of using pink mica as the core material, it can be seen that both (a) and (b) can achieve similar skin tone.

즉, 도 2 및 도 3에 도시된 바와 같이, 이산화티탄으로 코팅처리된 핑크 마이카의 경우, 백색 마이카의 특징인 투명성이 어느 정도 유지되면서도, 코팅처리되지 않은 핑크 마이카에 비해 자연스러운 피부톤을 표현하는데 적합한 색상을 띄는 것을 확인할 수 있다.
That is, as shown in Figs. 2 and 3, in the case of a pink mica coated with titanium dioxide, while maintaining a certain degree of transparency, which is a characteristic of a white mica, it is suitable for expressing a natural skin tone compared to an uncoated pink mica. You can see that it stands out in color.

<실시예2><Example 2>

실시예1의 이산화티탄이 코팅된 복합안료들의 피부친화성을 부여하기 위하여, 다음과 같이 표면 처리를 할 수 있다.In order to impart skin affinity of the titanium dioxide-coated composite pigments of Example 1, the surface treatment may be performed as follows.

이산화티탄(40중량%)이 코팅된 복합안료 95 중량%를 정제수 7ℓ에 분산하면서 80℃로 가온시켜준다.95% by weight of a composite pigment coated with titanium dioxide (40% by weight) is dispersed in 7ℓ of purified water and heated to 80°C.

피부 친화성 물질인 라우로일라이신 5 중량%를 수산화나트륨 1% 수용액 100g에 가온시키면서 투명해질 때까지 용해시켜준다. 완전 용해된 라우로일라이신 수용액을 마이카 현탁액에 정량투입기로 서서히 투입시킨다.5% by weight of lauroyl lysine, which is a skin-friendly substance, is dissolved in 100 g of a 1% sodium hydroxide aqueous solution while heating until it becomes transparent. The completely dissolved lauroyl lysine aqueous solution is slowly added to the mica suspension by a metering dispenser.

여기에 AlCl3 6H20 2중량% 수용액 100g을 준비하여 정량투입기로 서서히 투입하여 반응을 완성한다. 완성된 반응물은 탈수 건조 후 후드 믹서기(한일전기)를 사용하여 20초간 1회 분산하여 소수성 및 피부 친화성을 부여한다.
Here, 100 g of an AlCl 3 6H 2 0 2% by weight aqueous solution is prepared and gradually introduced into a quantitative injector to complete the reaction. The finished reactant is dehydrated and dried and dispersed once for 20 seconds using a hood blender (Hanil Electric) to give hydrophobicity and skin affinity.

<비교예><Comparative Example>

이산화티탄 (40중량%) 일반 진주광택안료 제조Manufacture of titanium dioxide (40% by weight) general pearlescent pigment

비이커에 증류수 10ℓ 및 판상 마이카 안료 100g을 투입하여 교반하면서 가온하여 온도를 80℃, pH를 1 내지 2로 조정하여 현탁액을 제조한다.10 L of distilled water and 100 g of plate-shaped mica pigment were added to a beaker, heated while stirring, and the temperature was adjusted to 80° C. and the pH to 1 to 2 to prepare a suspension.

사염화티탄(TiCl4) 48.0g을 정제수 200g에 완전 용해시킨 사염화티타늄 수용액을 준비하고, 수산화나트륨은 30중량% 수용액 200g을 준비한다. 준비된 2가지 용액을 정량 투입기를 사용하여 현탁액에 서서히 동시 투입하고 반응을 종료한 다음, 증류수로 수세 및 탈수하고, 100℃에서 12시간 건조, 750℃에서 1시간 소성하여 일반 진주광택안료를 완성한다.
A titanium tetrachloride aqueous solution was prepared in which 48.0 g of titanium tetrachloride (TiCl4) was completely dissolved in 200 g of purified water, and 200 g of a 30% by weight aqueous solution of sodium hydroxide was prepared. The prepared two solutions are slowly added to the suspension at the same time using a quantitative injector, and the reaction is terminated, then washed and dehydrated with distilled water, dried at 100°C for 12 hours, and calcined at 750°C for 1 hour to complete a general pearlescent pigment. .

상술한 바와 같이 완성된 실시예의 복합안료의 효능을 비교예의 진주광택안료의 효능과 비교 시험하기 위하여, 아래와 같은 화장료를 제조하여 실험하였다.
In order to compare and test the efficacy of the composite pigment of Example completed as described above with that of the pearlescent pigment of Comparative Example, the following cosmetic was prepared and tested.

<실험예><Experimental Example>

1-1. 화장료 제조1-1. Cosmetic manufacturing

아래 표1의 실시예 및 비교예에 대해, 각각 A와 B를 별도의 용기에 넣고 각각 대략 80℃의 온도로 가열한다.For the Examples and Comparative Examples shown in Table 1 below, A and B are placed in separate containers and heated to a temperature of approximately 80°C, respectively.

다음, 가열된 B를 A에 첨가하고 교반하여 균일하게 될 때까지 혼합한다.Next, heated B is added to A, stirred and mixed until uniform.

A와 B의 혼합물의 온도가 대략 50℃가 되면, C를 첨가하고 교반 혼합시켜 실시예와 비교예의 화장료를 각각 제조한다.When the temperature of the mixture of A and B reaches approximately 50° C., C is added and stirred and mixed to prepare cosmetic compositions of Examples and Comparative Examples, respectively.

PhasePhase 구성성분Ingredients 중량(%)weight(%) 비교예Comparative example 실시예Example AA 하이드로지네이트 레시틴Hydrogenate Lecithin 5.005.00 5.005.00 바틸 이소스테아레이트Batyl isostearate 1.001.00 1.001.00 트리옥타노인Trioctanoine 4.004.00 4.004.00 부틸 파라벤Butyl paraben 0.100.10 0.100.10 BB 1,3-부틸렌글리콜1,3-butylene glycol 5.005.00 5.005.00 메틸파라벤Methylparaben 0.100.10 0.100.10 정제수Purified water 82.3082.30 82.3082.30 CC 이산화티탄이 코팅된 백색 마이카White mica coated with titanium dioxide 2.502.50 -- 이산화티탄이 코팅된 핑크 마이카Pink mica coated with titanium dioxide -- 2.502.50

1-2. 피부 톤 및 밝기 측정1-2. Skin tone and brightness measurement

실시예와 비교예의 피부 톤 표현효과 및 밝기 정도를 측정하기 위하여, 각 화장료를 바르기 전후의 피부의 변화를 도 4와 같이 Red, Green, Blue 피크의 이동정도를 표시하는 히스토그램으로 나타내었다.In order to measure the skin tone expression effect and brightness level of Examples and Comparative Examples, changes in the skin before and after applying each cosmetic are shown as a histogram indicating the degree of movement of the red, green, and blue peaks as shown in FIG. 4.

그 결과, 실시예가 더 밝아졌으며, 화장료 적용 전후의 피부의 색상 차이가 비교예보다 더 작은 것을 확인할 수 있었다. 이는 이산화티탄으로 코팅된 핑크 마이카가 이산화티탄으로 코팅된 백색 마이카에 비해 피부의 원래 색을 유지하면서 피부 톤을 개선시키는 보정기능을 한다는 것을 알 수 있다.
As a result, the Example became brighter, and it was confirmed that the difference in color of the skin before and after application of the cosmetic material was smaller than that of the Comparative Example. It can be seen that pink mica coated with titanium dioxide has a correction function to improve skin tone while maintaining the original color of the skin compared to white mica coated with titanium dioxide.

1-3. 피부 보정정도 측정1-3. Measurement of skin correction

실시예와 비교예의 피부 보정 정도를 측정하기 위하여, 페이셜 분석기를 이용하여 각 화장료를 바르기 전후의 피부의 보정효과(착색 감소효과)를 UV광의 단계별 세기를 적용하여 측정하였다.In order to measure the degree of skin correction in Examples and Comparative Examples, the correction effect (color reduction effect) of the skin before and after applying each cosmetic composition was measured by applying the intensity of UV light by step using a facial analyzer.

UV-rayUV-ray 비교예Comparative example 실시예Example 적용전Before application 적용후After application 적용전Before application 적용후After application 1One 4444 4343 99 55 22 1414 1515 1111 99 33 2727 2424 2727 2323 평균Average 28.3328.33 27.3327.33 15.6715.67 12.3312.33 손실율Loss rate 100100 96.4796.47 100100 78.7278.72

그 결과, 표2에 나타낸 바와 같이, 실시예가 비교예보다 화장료 적용 전후 화장료의 피부 착색 감소효과가 더 작은 것을 확인할 수 있었다. 이는 이산화티탄으로 코팅된 핑크 마이카가 이산화티탄으로 코팅된 백색 마이카에 비해 피부의 원래색을 유지한다는 것을 알 수 있다.
As a result, as shown in Table 2, it was confirmed that the effect of reducing skin coloration of the cosmetic before and after application of the cosmetic was smaller in the Example than in the Comparative Example. It can be seen that pink mica coated with titanium dioxide maintains the original color of the skin compared to white mica coated with titanium dioxide.

이하 도 5의 (a)~(e)를 참고하여, 핑크 마이카를 사용하는 경우, 과도한 광택이나 번들거림이 없고 적정한 피부 보정효과를 주어 자연스러운 화장을 제공하게 되는 이유를 살펴보면 다음과 같다.Hereinafter, referring to FIGS. 5A to 5E, when a pink mica is used, the reason why natural makeup is provided by providing an appropriate skin correction effect without excessive gloss or gloss will be described as follows.

(1) 코어재인 핑크 마이카에 이산화티탄이 균일하게 코팅된 경우(1) When titanium dioxide is uniformly coated on the core material, pink mica

균일하게 코팅된 이산화티탄으로 인하여 굴절율이 큰 이산화티탄에서 반사되는 반사광, 이산화티탄과 마이카의 굴절율 차에 따라 코어재인 핑크 마이카에서 직접 반사되는 핑크 색채를 띠는 반사광, 통상적인 백색 마이카에 비해 상대적으로 두께가 얇은 핑크 마이카를 관통한 후 이산화티탄에서 반사되는 투과 반사광, 피부 표면까지 투과되어 피부표면에서 반사되는 투과 반사광이 서로 중첩되고 간섭을 일으켜 적정한 광채와 함께 피부색과 유사한 색이 구현되도록 한다.Reflected light reflected from titanium dioxide having a large refractive index due to uniformly coated titanium dioxide, reflected light having a pink color directly reflected from pink mica, which is a core material, depending on the difference in refractive index between titanium dioxide and mica, relatively compared to ordinary white mica After passing through the thin pink mica, the transmitted and reflected light reflected from titanium dioxide and the transmitted reflected light reflected from the skin surface and reflected from the skin surface overlap each other and cause interference, so that a color similar to the skin color with appropriate radiance is realized.

즉, 핑크 마이카에서 반사되는 반사광은 피부색과 유사한 핑크 마이카의 핑크색 색상의 반사광을 반사시키고, 피부에서 반사되는 투과 반사광은 원래 피부색을 반사시킨다.That is, the reflected light reflected from the pink mica reflects the pink color of the pink mica similar to the skin color, and the transmitted reflected light reflected from the skin reflects the original skin color.

이때, 핑크 마이카에서 반사되는 반사광은 핑크 마이카의 색상 자체가 피부색과 매우 유사하여 백색 마이카와 같이 백색의 과도한 광택이 반사되지 않게 된다.In this case, the reflected light reflected from the pink mica has a very similar color to the skin color of the pink mica, so that excessive white gloss is not reflected like a white mica.

따라서, 본 발명에 따른 복합안료를 함유한 화장료 적용시, 외부에서 인식되는 반사광은 핑크 마이카에서 반사되는 핑크색 및 피부에서 반사되는 피부색이 중첩되고 간섭하여 표현되므로 원래 피부색과 유사한 매우 자연스러운 피부색 구현이 가능하게 되는 것이다.Therefore, when applying the cosmetic composition containing the complex pigment according to the present invention, since the reflected light perceived from the outside is expressed by overlapping and interfering with the pink color reflected from the pink mica and the skin color reflected from the skin, a very natural skin color similar to the original skin color can be realized. It is done.

(2) 코어재인 핑크 마이카에 이산화티탄이 불균일하게 코팅된 경우(2) When titanium dioxide is unevenly coated on the core material, pink mica

불균일하게 코팅된 이산화티탄으로 인하여 굴절율이 큰 이산화티탄에서 반사되는 반사광의 크기는 매우 작게 되고, 이산화티탄과 마이카의 굴절율 차에 따라 코어재인 핑크 마이카에서 직접 반사되는 핑크 색채를 띠는 반사광의 크기는 상대적으로 크고, 핑크 마이카를 관통한 후 불균일하게 코팅된 이산화티탄에서 반사되는 투과 반사광 역시 크기가 작고, 피부 표면까지 투과되어 피부표면에서 반사되는 상대적으로 크기가 큰 투과 반사광이 서로 중첩되고 간섭을 일으켜 적정한 광채와 함께 피부색과 유사한 색이 구현되도록 한다.
Due to the non-uniformly coated titanium dioxide, the size of the reflected light reflected from the titanium dioxide having a large refractive index becomes very small, and the size of the reflected light having a pink color reflected directly from the pink mica as the core material is according to the difference in refractive index between titanium dioxide and mica The transmitted reflected light, which is relatively large and reflected from the non-uniformly coated titanium dioxide after passing through the pink mica, is also small, and the transmitted and reflected light of a relatively large size that is transmitted to the skin surface and reflected from the skin surface overlaps and causes interference. A color similar to skin tone is realized with an appropriate glow.

즉, 불균일한 이산화티탄에서 반사되는 반사광의 크기는 작고, 코어재인 핑크 마이카에서 반사되는 반사광의 크기와, 핑크 마이카를 관통하여 피부 표면까지 투과되는 투과광의 크기는 상대적으로 크므로 그로 인하여 피부에서 반사되는 투과 반사광의 크기는 크게 된다.In other words, the size of the reflected light reflected from the non-uniform titanium dioxide is small, and the size of the reflected light reflected from the core material, the pink mica, and the size of the transmitted light transmitted through the pink mica to the skin surface, are relatively large. The size of transmitted and reflected light becomes large.

핑크 마이카에서 반사되는 반사광은 색상 자체가 피부색과 매우 유사하고, 피부에서 반사되는 투과 반사광은 원래 피부색을 반사시키므로 과도한 광택이 반사되지 않게 된다.The color of the reflected light reflected from the pink mica is very similar to the skin color itself, and the transmitted reflected light reflected from the skin reflects the original skin color, so excessive gloss is not reflected.

따라서, 본 발명에 따른 복합안료를 함유한 화장료 적용시, 외부에서 인식되는 반사광은 핑크 마이카에서 반사되는 핑크색 및 피부에서 반사되는 피부색이 중첩되어 표현되므로 원래 피부색과 유사한 매우 자연스러운 피부색 구현이 가능하게 되는 것이다.
Therefore, when applying the cosmetic composition containing the complex pigment according to the present invention, since the reflected light perceived from the outside is expressed by overlapping the pink color reflected from the pink mica and the skin color reflected from the skin, it is possible to realize a very natural skin color similar to the original skin color. will be.

(3) 백색 마이카에 이산화티탄이 불균일하게 코팅되고 불균일 코팅면에 코어 마이카와 평행하게 핑크 마이카가 얇고 균일하게 코팅된 경우(3) When titanium dioxide is unevenly coated on white mica, and pink mica is coated thinly and evenly on the non-uniform coated surface parallel to the core mica

최외곽 핑크 마이카에서 반사되는 반사광, 불균일하게 코팅된 이산화티탄에서 반사되는 반사광, 이산화티탄과 백색 마이카의 굴절율 차에 따라 코어재인 마이카에서 직접 반사되는 백색을 띠는 반사광, 마이카를 관통한 후 불균일한 이산화티탄에서 반사되는 투과 반사광, 핑크 마이카에서 반사되는 투과 반사광, 피부 표면까지 투과되어 피부표면에서 반사되는 투과 반사광이 서로 중첩되고 간섭을 일으켜 적정한 광채와 함께 피부색과 유사한 색이 구현되도록 한다.Reflected light reflected from the outermost pink mica, reflected light reflected from unevenly coated titanium dioxide, white reflected light directly reflected from the core material mica according to the difference in refractive index between titanium dioxide and white mica, uneven after passing through the mica The transmitted reflected light reflected from titanium dioxide, the transmitted reflected light reflected from the pink mica, and the transmitted reflected light reflected from the skin surface by being transmitted to the skin surface overlap each other and cause interference to achieve a color similar to the skin color with an appropriate glow.

즉, 입사광은 최외곽 코팅면인 핑크 마이카에서 반사되고, 핑크 마이카를 투과한 투과광은 불균일하게 코팅된 이산화티탄으로 인하여 이산화티탄에서 반사되는반사광의 크기는 작고, 또한 백색 마이카에서 반사되는 투과 반사광의 크기 역시 작으며, 백색 마이카를 투과한 투과광은 불균일한 이산화티탄 및 최외곽 코팅면인 핑크 마이카와 이와 접촉한 피부에서 각각 반사되며, 각 반사광은 서로 중첩 및 간섭하여 외부에 간섭색을 구현하게 된다.In other words, the incident light is reflected from the outermost coated surface of the pink mica, and the transmitted light transmitted through the pink mica has a small size of the reflected light reflected from the titanium dioxide due to the non-uniformly coated titanium dioxide. The size is also small, and the transmitted light transmitted through the white mica is reflected from the uneven titanium dioxide and the pink mica, which is the outermost coating surface, and the skin in contact with each other, and each reflected light overlaps and interferes with each other to realize an interference color to the outside.

여기서, 피부 및 이와 접촉한 핑크 마이카에서 반사되는 투과 반사광은 원래 피부색과 핑크색을 반사시키고, 최상부 핑크 마이카에서 직접 반사되는 반사광 역시 피부색과 매우 유사한 핑크색을 반사시키며, 백색 마이카 및 이산화티탄에서는 백색의 광택이 반사되게 된다.Here, the transmitted reflected light reflected from the skin and the pink mica in contact with it reflects the original skin color and pink, and the reflected light directly reflected from the top pink mica also reflects a pink color that is very similar to the skin color, and white mica and titanium dioxide have a white gloss. Will be reflected.

이들 각 경계면에서 반사되는 다수개의 반사광은 중첩되고 간섭하여 외부로 표현되므로, 백색 마이카에서 반사되는 반사광의 효과는 저감되게 된다.Since a plurality of reflected lights reflected from each of these interfaces overlap and interfere, and are expressed to the outside, the effect of the reflected light reflected from the white mica is reduced.

따라서, 본 발명에 따른 복합안료를 함유한 화장료 적용시, 외부에서 인식되는 반사광은 핑크 마이카에서 반사되는 핑크색 및 피부에서 반사되는 피부색이 표현되므로 원래 피부색과 유사한 매우 자연스러운 피부색 구현이 가능하게 되는 것이다.
Therefore, when applying the cosmetic material containing the complex pigment according to the present invention, since the reflected light perceived from the outside expresses the pink color reflected from the pink mica and the skin color reflected from the skin, it is possible to realize a very natural skin color similar to the original skin color.

또한, 도 5의 (d)와 같이 핑크 마이카 코어재에 이산화티탄의 불균일한 고팅면을 형성하고 최외곽에 핑크 마이카를 얇고 균일하게 코팅하거나, (e)와 같이 핑크 마이카 코어재에 이산화티탄의 균일한 코팅면을 형성하고 최외곽에 핑크 마이카를 얇고 균일하게 코팅한 경우에도 외부에서 인식되는 반사광은 핑크 마이카에서 반사되는 핑크색 및 피부에서 반사되는 피부색이 표현되므로 원래 피부색과 유사한 매우 자연스러운 피부색 구현이 가능하게 되는 것이다.
In addition, as shown in (d) of FIG. 5, a non-uniform coating surface of titanium dioxide is formed on the pink mica core material, and the pink mica is thinly and uniformly coated on the outermost part, or the pink mica core material is coated with titanium dioxide as shown in (e). Even when a uniform coating surface is formed and the outermost pink mica is coated thinly and evenly, the reflected light perceived from the outside expresses the pink color reflected from the pink mica and the skin color reflected from the skin, so it is possible to realize a very natural skin color similar to the original skin color. It becomes possible.

또한, 코어재로 핑크 마이카를 사용하게 되면, 핑크 마이카가 갖고 있는 고유의 색상에 의해 그 두께가 통상의 백색 마이카보다 얇아도 대응되는 적절한 은폐력 또는 보정효과를 가져올 수 있으므로, 피부에 가볍게 사용할 수 있는 장점이 있게 된다. 즉, 피부 보정을 위해 피부에 두껍게 바를 필요가 없는 효과가 있다.
In addition, if pink mica is used as a core material, it can provide appropriate hiding power or correction effect even if the thickness of pink mica is thinner than normal white mica due to the unique color of pink mica, so it can be used lightly on the skin. There is an advantage. In other words, there is an effect that there is no need to apply a thick layer to the skin for skin correction.

이상과 같이, 본 명세서와 도면에는 본 발명의 바람직한 실시예에 대하여 개시하였으며, 비록 특정 용어들이 사용되었으나, 이는 단지 본 발명의 기술 내용을 쉽게 설명하고 발명의 이해를 돕기 위한 일반적인 의미에서 사용된 것이지, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예 외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형 예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다.As described above, in the present specification and drawings, a preferred embodiment of the present invention has been disclosed, and although specific terms are used, this is only used in a general meaning to easily explain the technical content of the present invention and to aid understanding of the invention. , It is not intended to limit the scope of the present invention. In addition to the embodiments disclosed herein, it is apparent to those of ordinary skill in the art that other modified examples based on the technical idea of the present invention may be implemented.

Claims (8)

핑크 마이카를 코어재로 포함하여 구성되며,
상기 핑크 마이카에서 직접 반사되는 핑크색채를 띠는 반사광과 투과되어 피부에서 반사되는 반사광의 중첩 및 간섭에 의해, 투명성을 구비하면서도 자연 피부색 구현이 가능한 것을 특징으로 하는 이산화티탄이 코팅된 복합안료.
It is composed of pink mica as a core material,
Titanium dioxide-coated composite pigment, characterized in that it has transparency and realizes natural skin color by overlapping and interfering with reflected light having a pink color reflected directly from the pink mica and reflected light transmitted from the skin.
 제 1항에 있어서,
상기 핑크 마이카는 이산화티탄이 균일하게 코팅되는 코어재인 것을 특징으로 하는 이산화티탄이 코팅된 복합안료.
The method of claim 1,
The pink mica is a titanium dioxide-coated composite pigment, characterized in that the core material is uniformly coated with titanium dioxide.
 제 1항에 있어서,
상기 핑크 마이카는 이산화티탄이 불균일하게 코팅되는 코어재인 것을 특징으로 하는 이산화티탄이 코팅된 복합안료.
The method of claim 1,
The pink mica is a titanium dioxide-coated composite pigment, characterized in that the core material is non-uniformly coated with titanium dioxide.
 제 1항에 있어서,
상기 핑크 마이카는 상기 복합안료의 코팅된 이산화티탄의 코팅 표면에 코팅된 최외곽재인 것을 특징으로 하는 이산화티탄이 코팅된 복합안료.
The method of claim 1,
The pink mica is a titanium dioxide-coated composite pigment, characterized in that the outermost material coated on the coated surface of the coated titanium dioxide of the composite pigment.
 삭제delete 제 1항에 있어서,
상기 핑크 마이카는 이산화티탄이 균일하게 코팅되는 코어재 및 코팅된 이산화티탄의 코팅 표면에 코팅된 최외곽재인 것을 특징으로 하는 이산화티탄이 코팅된 복합안료.
The method of claim 1,
The pink mica is a titanium dioxide-coated composite pigment, characterized in that the core material coated with titanium dioxide and the outermost material coated on the coated surface of the coated titanium dioxide.
 제 1항 내지 제 4항, 제 6항 중 어느 한 항에 있어서,
상기 복합안료는,
이산화티탄이 코팅된 핑크 마이카를 코어재로 포함하여 구성되어,
상기 핑크 마이카에서 직접 반사되는 핑크색채를 띠는 반사광과 이산화티탄에서 직접 반사되는 반사광 및 투과되어 피부에서 반사되는 반사광의 중첩 및 간섭에 의해, 투명성을 구비하면서도 자연 피부색 구현이 가능한 것을 특징으로 하는 이산화티탄이 코팅된 복합안료.
The method according to any one of claims 1 to 4 and 6,
The composite pigment,
It is composed of titanium dioxide-coated pink mica as a core material,
Discrete characterized in that it is possible to realize natural skin color while having transparency by overlapping and interference of the reflected light having a pink color directly reflected from the pink mica, the reflected light directly reflected from titanium dioxide, and the reflected light transmitted and reflected from the skin. A composite pigment coated with titanium.
 제 1항 내지 제 4항, 제 6항 중 어느 한 항의 이산화티탄이 코팅된 복합안료를 포함하는 화장료 조성물.A cosmetic composition comprising a composite pigment coated with titanium dioxide according to any one of claims 1 to 4 and 6.
KR1020180101335A 2018-08-28 2018-08-28 Complex pigments of Mica coated by Titanium dioxide and Cosmetics composition containing the same KR102190580B1 (en)