KR102155825B1 - The high-performance or fast hardening concrete and manufacturing method thereof - Google Patents

The high-performance or fast hardening concrete and manufacturing method thereof Download PDF

Info

Publication number
KR102155825B1
KR102155825B1 KR1020140016537A KR20140016537A KR102155825B1 KR 102155825 B1 KR102155825 B1 KR 102155825B1 KR 1020140016537 A KR1020140016537 A KR 1020140016537A KR 20140016537 A KR20140016537 A KR 20140016537A KR 102155825 B1 KR102155825 B1 KR 102155825B1
Authority
KR
South Korea
Prior art keywords
concrete
fast
performance
mixed
shorting
Prior art date
Application number
KR1020140016537A
Other languages
Korean (ko)
Other versions
KR20150095347A (en
Inventor
윤경구
Original Assignee
강원대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강원대학교산학협력단 filed Critical 강원대학교산학협력단
Priority to KR1020140016537A priority Critical patent/KR102155825B1/en
Publication of KR20150095347A publication Critical patent/KR20150095347A/en
Application granted granted Critical
Publication of KR102155825B1 publication Critical patent/KR102155825B1/en

Abstract

본 발명은 보통콘크리트에 유동혼화제가 혼합된 고성능 또는 속경성 콘크리트를 형성하고, 이 고성능 또는 속경성 콘크리트에 혼합재료를 혼합한 고성능 또는 속경성 콘크리트를 배출할 때, 고압의 공기로 숏팅하여 혼합재료의 비산 및 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트로 숏팅하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치 및 이의 제조방법에 관한 것이다.The present invention forms high-performance or fast-hardening concrete in which a fluid admixture is mixed with ordinary concrete, and when discharging high-performance or fast-hardening concrete obtained by mixing a mixed material with the high-performance or fast-hardening concrete, it is shot with high-pressure air High-performance or fast-hardening concrete shorting the slump with increased fluidity due to the scattering of and fluid admixtures to close to the slump range of ordinary concrete before the fluid admixture is mixed, and high performance through shorting after mixing fluid admixtures and mixed materials Or it relates to a fast-setting concrete manufacturing apparatus and a manufacturing method thereof.

Description

보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치 및 이의 제조방법{The high-performance or fast hardening concrete and manufacturing method thereof}High-performance or fast-hardening concrete manufacturing apparatus and manufacturing method thereof through shorting after mixing fluid admixtures and mixed materials into ordinary concrete {The high-performance or fast hardening concrete and manufacturing method thereof}

본 발명은 고성능 또는 속경성 콘크리트 제조장치 및 방법에 관한 것으로, 보다 상세하게는, 보통콘크리트에 유동혼화제가 혼합된 고성능 또는 속경성 콘크리트를 형성하고, 이 고성능 또는 속경성 콘크리트에 혼합재료를 혼합한 고성능 또는 속경성 콘크리트를 배출할 때, 고압의 공기로 숏팅하여 혼합재료의 비산 및 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트로 숏팅하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치 및 이의 제조방법에 관한 것이다.
The present invention relates to an apparatus and method for producing high-performance or fast-setting concrete, and more particularly, to form high-performance or fast-setting concrete in which a fluid admixture is mixed with ordinary concrete, and a mixed material is mixed with the high-performance or fast-setting concrete. When discharging high-performance or fast-setting concrete, it is shortened with high-pressure air to reduce the slump of increased fluidity due to the scattering of mixed materials and fluid admixtures, close to the slump range of ordinary concrete before fluid admixtures are mixed. It relates to an apparatus for producing high-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete for shorting with concrete, and a method for producing the same.

고성능 콘크리트는 물, 시멘트, 골재 등이 배합되는 보통콘크리트에 비해 고강도, 고내구성, 고유동성을 가진 콘크리트를 말한다. 이때, 고강도는 35MPa 이상의 강도를 의미하고, 고내구성은 90% 이상의 동결-융해 저항성을 요구하며, 고유동성은 작업성이 아주 우수한 콘크리트를 의미한다. 상기 고성능 콘크리트는 실리카퓸, 플라이애쉬, 슬래브미분말, 메타카올린 등의 미분말 혼합재료와 공기연행제, 고유동화제, 라텍스 등의 화학혼화제를 사용하여 상기의 성능을 발휘시키며, 고강도와 고내구성 조건을 동시에 만족시켜야 하기 때문에 내부구조를 치밀하게 하여야 하고, 동결-융해 저항성을 위해 공기량을 보통 3~6% 정도로 조절한다.High-performance concrete refers to concrete that has high strength, high durability, and high fluidity compared to ordinary concrete in which water, cement, and aggregate are mixed. At this time, high strength means a strength of 35 MPa or more, high durability requires a freeze-thaw resistance of 90% or more, and high fluidity means concrete with excellent workability. The high-performance concrete exhibits the above performance by using a mixture of fine powders such as silica fume, fly ash, slab fine powder, and metakaolin, and chemical admixtures such as air entraining agent, superplasticizer, and latex, and achieves high strength and high durability conditions. At the same time, since it has to be satisfied, the internal structure must be elaborate, and the amount of air is usually adjusted to 3-6% for freeze-thaw resistance.

상기 재료 중 실리카퓸과 고유동화제가 대표적인 고성능 콘크리트에 사용되는 것으로, 상기 실리카퓸은 보통콘크리트를 형성하는 시멘트 분말 대비 1/80~1/100 정도로 미세하여 콘크리트에 충전된 후, 포졸란반응으로 내부를 더욱 밀실하게 만들어 고강도와 고내구성으로 만든다. 상기 실리카퓸은 보통콘크리트를 형성하는 시멘트 중량대비 7~10%를 사용하는 것으로, 시멘트에 미리 배합(pre-blending)하여 혼합시멘트 형태로 사용된다. 이는 실리카퓸이 너무 미세한 분말이기 때문에 현장 배처플랜트(BP)에서 콘크리트배합 시, 타 콘크리트재료와 함께 투압하여 배합하면, 실리카퓸이 골고루 분산되지 않아 오히려 많은 문제점을 야기한다. 더욱이 이미 배합된 콘크리트에 실리카퓸을 분말 형태로 투입하고 배합하면 실리카퓸은 거의 분산되지 않는다.Among the above materials, silica fume and a superplasticizer are used in typical high-performance concrete, and the silica fume is about 1/80 to 1/100 of that of the cement powder forming ordinary concrete, and is filled in the concrete, and the interior is changed through a pozzolanic reaction. It makes it tighter and makes it high strength and high durability. The silica fume is usually used in the form of 7 to 10% of the weight of cement forming concrete, and is pre-blended with cement and used in the form of mixed cement. This is because silica fume is a very fine powder, so when mixing concrete in an on-site batching plant (BP), if it is mixed by permeating pressure with other concrete materials, silica fume is not evenly dispersed, causing many problems. Moreover, if silica fume is added in powder form to the already mixed concrete and mixed, silica fume is hardly dispersed.

그리고 상기 고성능 콘크리트를 생산하기 위하여 실리카퓸, 플라이애쉬, 고로슬래그미분말, 메타카올린 등의 미분말 혼합재료를 이용하는데, 상기 혼합재료의 분산을 위해 혼합시멘트를 사용하며, 상기 혼합시멘트의 사용량이 많을 경우, 공장에서 벌크로 생산하여 현장으로 이송할 수 있도록 별도의 사이로를 설치하여 사용하며, 사용량이 중급이나 소규모일 경우는 톤백으로 공급하기도 하므로 별도의 공정과 별도의 수송으로 생산단가를 상승시키는 문제점이 있었다.And in order to produce the high-performance concrete, a mixture of fine powders such as silica fume, fly ash, blast furnace slag fine powder, and metakaolin is used, and a mixed cement is used to disperse the mixed material, and when the amount of the mixed cement is large , A separate silo is installed and used so that the factory can produce it in bulk and transport it to the site, and if the amount is medium or small, it is supplied as a ton bag, so there is a problem of increasing the production cost through a separate process and separate transportation. there was.

또한, 고성능 콘크리트를 현장 배처플랜트에서 일괄 생산 및 공급하여 대상구조물의 전 단면을 고성능 콘크리트로 시공해야 함으로써 시공단가가 상승하는 문제점이 있었다.
In addition, there is a problem in that the construction cost increases as high-performance concrete has to be produced and supplied in batches at the on-site batching plant to construct the entire section of the target structure with high-performance concrete.

삭제delete

대한민국 등록특허 제10-0875240호Korean Patent Registration No. 10-0875240

본 발명은 상술된 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은, 물, 시멘트, 골재 등을 혼합하여 현장 이송된 보통콘크리트에 유동혼화제를 혼입하여 고성능 또는 속경성 콘크리트를 형성하고, 이 고성능 또는 속경성 콘크리트에 혼합재료를 혼입한 고성능 또는 속경성 콘크리트를 배출할 때, 고압의 공기로 숏팅하여 혼합재료의 비산 및 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트로 숏팅하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치 및 이의 제조방법을 제공함에 있다.The present invention was conceived to solve the above-described problem, and an object of the present invention is to form high-performance or fast-hardening concrete by mixing water, cement, aggregate, etc. When discharging high-performance or fast-setting concrete mixed with high-performance or fast-setting concrete, the slump with increased fluidity due to the scattering of the mixed material and the fluid admixture is shot with high-pressure air. It is intended to provide an apparatus for producing high-performance or fast-setting concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete that is shortened with high-performance or fast-setting concrete that is reduced close to the slump range, and a manufacturing method thereof.

또한, 본 발명의 다른 목적은, 기존의 배처플랜트와 레미콘트럭을 이용하여 고성능 또는 속경성 콘크리트를 제조할 수 있으므로 생산 및 시공단가를 절감하여 경제성을 향상시킬 수 있는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치 및 이의 제조방법을 제공함에 있다.
In addition, another object of the present invention is to produce high-performance or fast-hardening concrete using an existing batcher plant and ready-mixed concrete truck, so it is possible to reduce production and construction costs and improve economic efficiency. It is to provide a high-performance or fast-hardening concrete manufacturing apparatus and a manufacturing method thereof through shorting after mixing.

본 발명 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치는,The apparatus for producing high-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete of the present invention,

물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성부와;An ordinary concrete forming unit for forming ordinary concrete by mixing water, cement, and aggregate in a certain ratio;

상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입부와;A fluid admixture and a mixed material input unit for mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete;

상기 보통콘크리트가 적재되는 레미콘트럭 내부에 형성되어 모터의 동력으로 회전하는 축이 구비되고, 상기 축에 적어도 1단 이상 방상으로 형성되어 보통콘크리트와 유동혼화제 및 혼합재료 투입부로부터 투입되는 유동혼화제 및 혼합재료를 혼합부재로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성부와;It is formed inside the ready-mixed concrete truck in which the ordinary concrete is loaded and has a shaft that rotates with the power of a motor, and is formed in at least one stage on the shaft, and a fluid admixture that is introduced from the input unit of the common concrete and the fluid admixture and the mixed material, and A high-performance or fast-hardening concrete forming unit for forming high-performance or fast-hardening concrete by mixing mixed materials with a mixing member;

상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅부를 포함하여 구성되는 것을 특징으로 하는 것이다.
When discharging the high-performance or fast-setting concrete, the slump whose fluidity is increased due to the fluid admixture while the mixed material is dispersed through the scattering and impact of the material by shorting it with air of 5 atm or higher before the fluid admixture is mixed by the dissipation of the fluid admixture. It is characterized in that it comprises a high-performance or fast-setting concrete shorting unit for shorting the high-performance or fast-setting concrete reduced close to the slump range of the concrete.

또한, 본 발명 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법은,In addition, the method for producing high-performance or fast-hardening concrete through shorting after mixing a fluid admixture and a mixed material into the ordinary concrete of the present invention,

물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성단계와;Ordinary concrete forming step of forming ordinary concrete by mixing water, cement, and aggregate in a certain ratio;

상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입단계와;A flow admixture and a mixed material input step of mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete;

상기 보통콘크리트가 적재되는 레미콘트럭 내부에 형성되어 모터의 동력으로 회전하는 축이 구비되고, 상기 축에 적어도 1단 이상 방상으로 형성되어 보통콘크리트와 유동혼화제 및 혼합재료 투입부로부터 투입되는 유동혼화제 및 혼합재료를 혼합부재로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성단계와;It is formed inside the ready-mixed concrete truck in which the ordinary concrete is loaded and has a shaft that rotates with the power of a motor, and is formed in at least one stage on the shaft, and a fluid admixture that is introduced from the input unit of the common concrete and the fluid admixture and the mixed material, and A high-performance or fast-hardening concrete forming step of mixing the mixed material with a mixing member to form high-performance or fast-hardening concrete;

상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅단계를 포함하여 이루어지는 것을 특징으로 하는 것이다.
When discharging the high-performance or fast-setting concrete, the slump whose fluidity is increased due to the fluid admixture while the mixed material is dispersed through the scattering and impact of the material by shorting it with air of 5 atm or higher before the fluid admixture is mixed by the dissipation of the fluid admixture. It characterized in that it comprises a high-performance or fast-setting concrete shorting step of shorting the high-performance or fast-setting concrete reduced close to the slump range of the concrete.

본 발명에 의하면, 고성능 또는 속경성 콘크리트를 제조함에 있어 배처플랜트에서 배합되어 레미콘트럭으로 현장 이송된 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하여 고루 분산시킴으로써 고강도, 고내구성, 속경성을 확보할 수 있는 이점을 가질 수 있는 것이다.According to the present invention, in manufacturing high-performance or fast-hardening concrete, high strength, high durability, and fast-hardening properties can be secured by mixing and dispersing fluid admixtures and mixed materials in ordinary concrete mixed at a batcher plant and transferred to the field to a ready-mixed concrete truck. You can have the advantage that you have.

또한, 본 발명에 의하면, 기존의 배처플랜트와 레미콘트럭을 이용하여 고성능 또는 속경성 콘크리트를 제조함으로 생산 및 시공단가를 절감하여 경제성을 향상시킬 수 있는 이점을 가질 수 있는 것이다.
In addition, according to the present invention, by manufacturing high-performance or fast-hardening concrete using an existing batcher plant and ready-mixed concrete truck, it is possible to have the advantage of reducing production and construction costs and improving economic efficiency.

도 1은 본 발명의 흐름도
도 2는 본 발명의 개략도
도 3은 본 발명 보통콘크리트 형성부를 나타낸 도면
도 4 내지 도 5은 본 발명 고성능 또는 속경성 콘크리트 형성부를 나타낸 도면
도 6은 본 발명 다른 실시예의 고성능 또는 속경성 콘크리트 형성부를 나타낸 도면
도 7 내지 도 8은 본 발명에 적용되는 보통콘크리트 및 본 발명이 적용된 고성능 또는 속경성 콘크리트의 슬럼프 사진
도 9 내지 도 11은 본 발명 고성능 또는 속경성 콘크리트 숏팅부로 고성능 또는 속경성 콘크리트를 숏팅하는 도면
도 12는 본 발명 속경성 콘크리트 숏팅부의 평단면 구성도
도 13은 본 발명 속경성 콘크리트의 슬럼프 사진1 is a flow chart of the present invention
Figure 2 is a schematic diagram of the present invention
Figure 3 is a view showing the present invention common concrete forming part
4 to 5 are views showing the present invention high-performance or fast-setting concrete forming part
Figure 6 is a view showing a high-performance or fast-setting concrete forming part of another embodiment of the present invention
7 to 8 are slump photographs of ordinary concrete applied to the present invention and high-performance or fast-hardening concrete to which the present invention is applied
9 to 11 are views for shorting high-performance or fast-setting concrete with the high-performance or fast-setting concrete shorting unit of the present invention
12 is a schematic cross-sectional view of the present invention fast-setting concrete shorting unit
13 is a photograph of the slump of the present invention fast-hardening concrete

이하, 첨부된 도면에 의거하여 본 발명을 상세히 설명한다. 도 1은 본 발명의 흐름도이고, 도 2는 본 발명의 개략도이다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings. Figure 1 is a flow chart of the present invention, Figure 2 is a schematic diagram of the present invention.

본 발명 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치(100)는, 물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성부(110)가 구성되고, 상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입부(120)가 구성되며, 상기 보통콘크리트가 적재되는 레미콘트럭(111) 내부에 형성되어 모터의 동력으로 회전하는 축(131)이 구비되고, 상기 축(131)에 적어도 1단 이상 방상으로 형성되어 보통콘크리트와 유동혼화제 및 혼합재료 투입부(120)로부터 투입되는 유동혼화제 및 혼합재료를 혼합부재(132)로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성부(130)가 구성되며, 상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅부(140)를 포함하여 구성된다.In the present invention, the apparatus 100 for producing high-performance or fast-hardening concrete through shorting after mixing a fluid admixture and a mixed material into ordinary concrete is a general concrete forming unit 110 that forms ordinary concrete by mixing water, cement, and aggregate at a certain ratio. Is configured, and a fluid admixture and a mixed material input unit 120 for mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete, and a ready-mixed concrete truck 111 in which the ordinary concrete is loaded. ) A shaft 131 that is formed inside and rotates with the power of a motor is provided, and is formed in at least one stage on the shaft 131 so that the flow is input from the input unit 120 of common concrete and fluid admixtures and mixed materials. A high-performance or fast-setting concrete forming unit 130 is formed by mixing an admixture and a mixed material with a mixing member 132 to form high-performance or fast-setting concrete, and when the high-performance or fast-setting concrete is discharged, air of 5 atm or more High-performance or fast-hardening concrete that is reduced to close to the slump range of ordinary concrete before the fluid admixture is mixed by dissipation of the fluid admixture while dispersing the mixed material due to the scattering and impact of the material. It is configured to include a high-performance or fast-setting concrete shorting unit 140 for shorting.

또한, 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치(100')는, 물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성부(110)가 구성되고, 상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입부(120)가 구성되며, 상기 보통콘크리트와 유동혼화제 및 혼합재료를 공급받는 호퍼(133)가 구비되고, 상기 호퍼(133)로 공급되는 보통콘크리트와 유동혼화제 및 혼합재료 투입부(120)로부터 투입되는 유동혼화제와 혼합재료를 스크류(134)의 회전으로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성부(130')가 구성되며, 상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅부(140)를 포함하여 구성된다.In addition, the high-performance or fast-hardening concrete manufacturing apparatus 100 ′ through shorting after mixing fluid admixtures and mixed materials into ordinary concrete is a general concrete forming unit 110 that forms ordinary concrete by mixing water, cement, and aggregate at a certain ratio. ), and a fluid admixture and a mixed material input unit 120 for mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete, and the ordinary concrete and the fluid admixture and a mixed material A hopper 133 is provided, and a fluid admixture and a mixed material input from the flow admixture and the mixed material input unit 120 are mixed with the rotation of the screw 134 to be provided with the normal concrete supplied to the hopper 133. A high-performance or fast-setting concrete forming unit 130 ′ is configured to form high-performance or fast-setting concrete, and when the high-performance or fast-setting concrete is discharged, it is shot with air of 5 atm or higher to form a mixture of materials through scattering and impact of the material. High-performance or fast-setting concrete shorting unit 140 for shorting high-performance or fast-hardening concrete that has reduced the slump with increased fluidity due to the flow admixture while dispersing to close to the slump range of ordinary concrete before the fluid admixture is mixed by dissipation of the fluid admixture. Consists of including.

상기 유동혼화제는, AE감수제, 감수제, 고성능감수제, 유동화제, 고유동화제 중 어느 하나이거나 하나 이상 혼합하여 형성된다.The fluid admixture is formed by mixing one or more of an AE water reducing agent, a water reducing agent, a high performance water reducing agent, a fluidizing agent, and a high fluidizing agent.

상기 유동혼화제는, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5 중량부 이하로 혼합되는 것이 바람직하다.The fluid admixture is preferably mixed in an amount of 5 parts by weight or less based on 100 parts by weight of cement forming the ordinary concrete.

상기 혼합재료는, 실리카퓸, 메타카올린, 플라이애쉬, 고로슬래그미분말, 라텍스, 폴리머, 조강혼합재료 중 어느 하나이거나 하나 이상 혼합하여 형성된다.The mixed material is formed by mixing one or more of silica fume, metakaolin, fly ash, blast furnace slag powder, latex, polymer, and crude steel mixed material.

상기 실리카퓸은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~15 중량부로 혼합된다.The silica fume is mixed in an amount of 5 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

상기 메타카올린은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 7~20 중량부로 혼합된다.The metakaolin is mixed in an amount of 7 to 20 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

상기 플라이애쉬와 고로슬래그미분말은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합된다.The fly ash and the blast furnace slag fine powder are mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

상기 라텍스와 폴리머는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 3~15 중량부로 혼합된다.The latex and polymer are mixed in an amount of 3 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

상기 조강혼합재료는, 알루미나계 초속경클링커분말, 비정질알루미나계 초속경클링커분말, 아윈계 초속경클링커분말 중 어느 하나 또는 하나 이상 혼합하여 형성된다.The crude steel mixture material is formed by mixing one or more of alumina-based ultrafast hard clinker powder, amorphous alumina ultrafast hard clinker powder, and Arwin ultrafast hard clinker powder.

조강콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~20 중량부로 혼합된다.In order to manufacture the crude steel concrete, the crude steel mixture is mixed in an amount of 5 to 20 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

초조강콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합된다.In order to manufacture ultra-rough steel concrete, the crude steel mixture material is mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

초속경콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 25~40 중량부로 혼합된다.In order to produce ultra-fast-hard concrete, the crude steel mixture is mixed in an amount of 25 to 40 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.

상기 보통콘크리트에 유동혼화제와 혼합재료를 순차적으로 투입하는 것이 바람직하다.It is preferable to sequentially add a fluid admixture and a mixed material to the ordinary concrete.

상기 속경성 콘크리트 숏팅부(140)는, 상기 고성능 또는 속경성 콘크리트가 압축되어 배출되도록 내부가 관통된 양단부보다 중앙부의 직경이 작게 형성되어 고성능 또는 속경성 콘크리트 형성부(130)에 착탈가능하게 장착되는 숏팅안내부재(141)가 구비되고, 상기 숏팅안내부재(141)로 이동되는 고성능 또는 속경성 콘크리트에 포함된 기포를 소산시키면서 공기량을 감소시키도록 5기압 이상의 고압의 공기를 공급하도록 숏팅안내부재에 관통된 공기공급공(142)을 포함하여 구비된다.The fast-setting concrete shorting unit 140 has a diameter smaller in the central portion than both ends through which the high-performance or fast-setting concrete is compressed and discharged, so that it is detachably mounted on the high-performance or fast-setting concrete forming unit 130 The shorting guide member 141 is provided, and a shorting guide member to supply high pressure air of 5 atm or more to reduce the amount of air while dissipating air bubbles contained in the high-performance or fast-hardening concrete that is moved to the shorting guide member 141 It is provided including an air supply hole 142 penetrated in.

상기 공기공급공(142)은, 상기 숏팅안내부재의 외주면에 방사상으로 경사지게 형성된다.
The air supply hole 142 is formed to be radially inclined on the outer peripheral surface of the shorting guide member.

다음은 상기와 같이 구성된 본 발명의 제조과정을 설명한다.The following describes the manufacturing process of the present invention configured as described above.

먼저, 도 3에 도시된 바와 같이, 배처플랜트(BP)에서 각각 공급되는 물, 시멘트, 골재 등을 일정비율로 배합 및 혼합하여 슬럼프 60mm 이상의 보통콘크리트를 보통콘크리트 형성부(110)에서 형성한 후, 레미콘트럭(111)에 의해 시공현장으로 이송한다.First, as shown in FIG. 3, after mixing and mixing water, cement, aggregate, etc. each supplied from the batcher plant (BP) at a predetermined ratio, ordinary concrete of slump 60 mm or more is formed in the ordinary concrete forming unit 110 , Transfer to the construction site by ready-mixed concrete truck 111.

시공현장으로 이송되는 레미콘트럭(111)의 보통콘크리트에 유동혼화제 및 혼합재료 투입부(120)로부터 유동혼화제와 혼합재료를 순차적으로 투입하는데, 상기 유동혼화제는, AE감수제, 감수제, 고성능감수제, 유동화제, 고유동화제 중 어느 하나이거나 하나 이상 혼합한 것이 바람직하며, 이는 보통콘크리트의 유동성을 크게 하여 슬럼프가 200mm 이상 되도록 함으로써 혼합재료의 분산을 증진시키기 위한 것으로, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5 중량부 이하로 혼합된다.The fluid admixture and the mixed material are sequentially introduced from the fluid admixture and the mixed material input unit 120 to the general concrete of the ready-mixed concrete truck 111 that is transferred to the construction site, and the fluid admixture is an AE water reducing agent, a water reducing agent, a high-performance water reducing agent, and fluidizing. First, it is preferable to mix one or more of the superfluidizing agents, and this is to increase the fluidity of the ordinary concrete so that the slump is 200 mm or more to increase the dispersion of the mixed material, and 100 weight of the cement forming the ordinary concrete It is mixed in 5 parts by weight or less based on parts.

또한, 상기 유동혼화제가 투입된 보통콘크리트에 추가 투입되는 혼합재료는, 실리카퓸, 메타카올린, 플라이애쉬, 고로슬래그미분말, 라텍스, 폴리머, 조강혼합재료 중 어느 하나이거나 하나 이상 혼합하며, 상기 실리카퓸은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~15 중량부로 혼합하고, 상기 메타카올린은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 7~20 중량부로 혼합하며, 상기 플라이애쉬와 고로슬래그미분말은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합하고, 상기 라텍스와 폴리머는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 3~15 중량부로 혼합한다.In addition, the mixed material additionally added to the general concrete into which the fluid admixture is added is one or more of silica fume, metakaolin, fly ash, blast furnace slag powder, latex, polymer, and crude steel mixed material, and the silica fume is , 5 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and the metakaolin is mixed in 7 to 20 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and the fly ash The blast furnace slag powder is mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete, and the latex and polymer are mixed in an amount of 3 to 15 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.

상기 조강혼합재료는, 알루미나계 초속경클링커분말, 비정질알루미나계 초속경클링커분말, 아윈계 초속경클링커분말 중 어느 하나 또는 하나 이상 혼합하여 형성하는데, 상기 조강혼합재료는, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~20 중량부로 혼합하여 조강콘크리트를 제조할 수 있고, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합하여 초조강콘크리트를 제조할 수 있으며, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 25~40 중량부로 혼합하여 초속경콘크리트를 제조할 수 있다.The crude steel mixture material is formed by mixing any one or one or more of alumina-based ultra-fast hard clinker powder, amorphous alumina-based ultra-fast hard clinker powder, and Arwin-based ultra-fast hard clinker powder. Crude steel concrete can be prepared by mixing 5 to 20 parts by weight based on 100 parts by weight of cement, and 15 to 25 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete can be mixed to produce ultra-rough steel concrete. Super fast-hardening concrete can be prepared by mixing in 25 to 40 parts by weight based on 100 parts by weight of cement forming ordinary concrete.

여기서, 상기 조강혼합재료는 최종 콘크리트의 슬럼프와 강도를 고려하여 결정하는 것이 바람직하다.Here, it is preferable to determine the crude steel mixture in consideration of the slump and strength of the final concrete.

상기의 과정으로 유동혼화제 및 혼합재료 투입부(120)로부터 투입되는 유동혼화제 및 혼합재료와 보통콘크리트를 고성능 또는 속경성 콘크리트 형성부(130)(130')에서 혼합하여 고성능 또는 속경성 콘크리트를 형성한다.High-performance or fast-hardening concrete is formed by mixing the fluid admixture and the mixed material and ordinary concrete, which are introduced from the fluid admixture and mixed material input unit 120 through the above process, in the high-performance or fast-hardening concrete forming unit 130 and 130 ′. do.

상기 고성능 또는 속경성 콘크리트 형성부(130)는, 도 4 내지 도 5에 도시된 바와 같이, 레미콘트럭(111) 내부에 모터(미도시)의 동력으로 축(131)이 회전함과 동시에 상기 축(131)에 적어도 1단 이상 방사상으로 형성된 혼합부재(132)가 회전하면서 보통콘크리트와 유동혼화제 및 혼합재료를 혼합하여 유동혼화제의 유동성 증진효과를 이용해 혼합재료가 보통콘크리트 내에 고루 분산되어 혼합되는 고성능 또는 속경성 콘크리트를 형성하게 된다.The high-performance or fast-hardening concrete forming unit 130, as shown in Figs. 4 to 5, the shaft 131 rotates with the power of a motor (not shown) inside the ready-mixed concrete truck 111 The mixing member 132 formed radially in at least one stage in (131) rotates and mixes the normal concrete, the fluid admixture, and the mixed material to increase the fluidity of the fluid admixture. Or it will form fast-hardening concrete.

또한, 도 6에 도시된 바와 같이, 상기 고성능 또는 속경성 콘크리트 형성부(130')는, 배처플랜트(BP)에서 각각 공급되는 물, 시멘트, 골재 등을 일정비율로 배합 및 혼합하여 슬럼프 40mm 이상의 보통콘크리트를 보통콘크리트 형성부(110)에서 형성한 후, 덤프트럭(미도시)에 의해 시공현장으로 이송된 보통콘크리트를 호퍼(133)로 공급하여 스크류(134)의 회전으로 혼합부재(135)로 이동시킴과 동시에 상기 호퍼(133)에 유동혼화제 및 혼합재료 투입부(120)로부터 유동혼화제와 혼합재료를 투입하여 보통콘크리트와 스크류(134)의 회전으로 혼합되도록 한다.In addition, as shown in Figure 6, the high-performance or fast-hardening concrete forming unit (130') is, by mixing and mixing water, cement, aggregate, etc., respectively supplied from the batcher plant (BP) at a predetermined ratio, slump 40mm or more After forming the ordinary concrete in the ordinary concrete forming unit 110, the ordinary concrete transferred to the construction site by a dump truck (not shown) is supplied to the hopper 133, and the mixing member 135 is rotated by the screw 134. At the same time, the fluid admixture and the mixed material are introduced into the hopper 133 from the fluid admixture and the mixed material input unit 120 to be mixed by rotation of the normal concrete and the screw 134.

이때, 상기 유동혼화제와 혼합재료는 별도의 투입이 가능하나, 스크류(134)의 회전에 따른 유동혼화제와 혼합재료 및 보통콘크리트의 혼합시간이 짧으므로 보통콘크리트 및 유동혼화제와 혼합재료를 호퍼(133)에 동시에 투입하는 것이 바람직하다.At this time, the fluid admixture and the mixed material can be separately added, but since the mixing time of the fluid admixture, the mixed material, and the ordinary concrete according to the rotation of the screw 134 is short, the normal concrete and the fluid admixture and the mixed material are added to the hopper 133. ), it is desirable to put it in at the same time.

여기서, 상기 고성능 또는 속경성 콘크리트 형성부(130')는, 상하교반식 믹서로, 입구측보다 출구측이 더 높도록 경사지게 형성되어 혼합부재(135)의 높이차에 의해 유동혼화제와 혼합재료 및 보통콘크리트가 용이하게 혼합될 수 있도록 한다.Here, the high-performance or fast-hardening concrete forming unit 130 ′ is a vertical agitation mixer, and is formed to be inclined so that the outlet side is higher than the inlet side, and the fluid admixture and the mixed material and the mixed material by the height difference of the mixing member 135 It allows ordinary concrete to be easily mixed.

도 7은 물, 시멘트, 골재 등의 혼합비는 일반적으로 널리 사용되는 보통콘크리트의 표준 배합비에 따른 보통콘크리트의 슬럼프를 나타낸 것으로, 슬럼프가 70mm 상태를 보여주고 있으나, 도 8은 보통콘크리트에 유동혼화제를 혼입하여 혼합한 슬럼프를 나타낸 것으로, 슬럼프가 대폭 커진 230mm임을 보여주고 있다.FIG. 7 shows the slump of ordinary concrete according to the standard mixing ratio of commonly used ordinary concrete in the mixing ratio of water, cement, aggregate, etc., and the slump shows a state of 70 mm, but FIG. 8 shows a fluid admixture in ordinary concrete. It shows the mixed and mixed slump, showing that the slump is significantly increased 230mm.

이렇게 대폭 증가된 유동성에 의해 보통콘크리트에 후 혼입된 혼합재료를 분산시킬 수 있으나, 유동혼화제가 다량 혼합된 고성능 또는 속경성 콘크리트는 혼합재료의 혼입로 유동성을 줄일 수 있으나, 고성능 또는 속경성 콘크리트 강도가 저하되어 구조용 재료로 사용하기 어려울 뿐만 아니라 슬럼프의 증가로 고성능 또는 속경성 콘크리트 타설에 따른 소요의 작업성 범위를 벗어나게 된다.This greatly increased fluidity can disperse the mixed material mixed with ordinary concrete, but high-performance or fast-setting concrete mixed with a large amount of fluid admixture can reduce the fluidity by mixing the mixed material, but high-performance or fast-setting concrete strength It is difficult to use as a structural material due to the decrease in slump, and due to the increase in slump, it is out of the range of workability required for high-performance or fast-setting concrete pouring.

따라서, 본 발명은, 도 9 내지 도 11에 도시된 바와 같이, 상기 고성능 또는 속경성 콘크리트 형성부(130)(130')에서 혼합된 혼합 콘크리트에 포함된 유동혼화제를 감소시키기 위하여 고성능 또는 속경성 콘크리트 숏팅부(140)로 숏팅을 실시하게 된다.Therefore, the present invention, as shown in Figs. 9 to 11, in order to reduce the flow admixture contained in the mixed concrete mixed in the high-performance or fast-setting concrete forming unit 130, 130' Shorting is performed with the concrete shorting part 140.

상기 고성능 또는 속경성 콘크리트 숏팅부(140)로 고성능 또는 속경성 콘크리트를 숏팅할 경우, 고성능 또는 속경성 콘크리트 형성부(130)의 레미콘트럭(111) 및 콘크리트 펌프카(111')나 고성능 또는 속경성 콘크리트 형성부(130')의 혼합부재(135)에 착탈가능하게 장착된 숏팅안내부재(141)의 입구로 공급된다.In the case of shorting high-performance or fast-setting concrete with the high-performance or fast-setting concrete shorting unit 140, the ready-mixed concrete truck 111 and the concrete pump car 111' of the high-performance or fast-setting concrete forming unit 130 or high-performance or fast-setting It is supplied to the inlet of the shorting guide member 141 detachably mounted to the mixing member 135 of the concrete forming part (130').

여기서, 상기 숏팅안내부재(141)는 내부가 관통된 입,출구의 양단부보다 중앙부의 직경이 작게 형성되어 있으므로 숏팅안내부재(141)로 공급되는 고성능 또는 속경성 콘크리트는 압축되면서 압력이 발생한다.Here, the shorting guide member 141 has a diameter smaller in the central portion than both ends of the inlet and outlet through which the inside is penetrated, so that the high-performance or fast-hardening concrete supplied to the shorting guide member 141 is compressed while generating pressure.

또한, 도 12에 도시된 바와 같이, 상기 숏팅안내부재(141)의 중앙부를 경유하여 중앙부의 직경보다 큰 숏팅안내부재(141)의 출구로 고성능 또는 속경성 콘크리트가 통과함과 동시에 5기압 이상의 고압의 압축공기가 숏팅안내부재(141)의 외주면에 방사상으로 경사지게 형성된 공기공급공(142)으로 공급되면서 숏팅안내부재(141)의 출구로 와류되어 숏팅되는데, 상기 압축공기와 고성능 또는 속경성 콘크리트는 스프레이방식으로 펼쳐짐은 물론 스프레이방식으로 압축공기와 고성능 또는 속경성 콘크리트가 펼쳐질 때, 압축공기와 고성능 또는 속경성 콘크리트가 부딪히면서 고성능 또는 속경성 콘크리트 내부에 포함된 다량의 유동혼화제가 소산되는 것이다.In addition, as shown in FIG. 12, high-performance or fast-hardening concrete passes through the central portion of the shorting guide member 141 to the outlet of the shorting guide member 141 that is larger than the diameter of the central portion, and at the same time, a high pressure of 5 atm or more. The compressed air of the shorting guide member 141 is supplied to the air supply hole 142 formed to be inclined radially on the outer circumferential surface of the shorting guide member 141 and is vortexed to the outlet of the shorting guide member 141 to be shot. When the compressed air and high-performance or fast-hardening concrete are spread by the spray method as well as the spray method, a large amount of fluid admixture contained in the high-performance or fast-setting concrete is dissipated as the compressed air and the high-performance or fast-setting concrete collide.

이때, 상기 고성능 또는 속경성 콘크리트에 포함된 물입자의 분산 및 비산으로 인해 유동혼화제가 감소하게 되고, 혼합재료의 분산 및 비산과 충격 등올 혼합재료의 완전 분산을 이룰 수 있으며, 도 13에 도시된 바와 같이, 상기 유동혼화제가 소산되어 유동성이 줄어든 고성능 또는 속경성 콘크리트의 슬럼프는 120mm 로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소하는 고성능 또는 속경성 콘크리트를 숏팅할 수 있는 것이다.At this time, the fluid admixture is reduced due to the dispersion and scattering of water particles contained in the high-performance or fast-setting concrete, and complete dispersion of the mixed material such as dispersion and scattering and impact of the mixed material can be achieved, as shown in FIG. As described above, the slump of high-performance or fast-hardening concrete with reduced fluidity due to the dissipation of the fluid admixture is 120 mm, and high-performance or fast-hardening concrete that decreases close to the slump range of ordinary concrete before the fluid admixture is mixed can be shot.

상기 고성능 또는 속경성 콘크리트는, 혼합재료 중 조강혼합재료의 혼합량에 따라 조강콘크리트, 초조강콘크리트 및 초속경콘크리트를 형성하여 고강도, 고내구성 및 속경성을 확보할 수 있는 것이다.The high-performance or fast-hardening concrete is capable of securing high strength, high durability, and fast-hardening by forming coarse steel concrete, ultra-rough steel concrete, and ultra-fast hard concrete according to the mixing amount of the coarse steel mixed material among the mixed materials.

본 발명에서 상기 실시 형태는 하나의 예시로서 본 발명이 여기에 한정되는 것은 아니다. 본 발명의 특허청구범위에 기재된 기술적 사상과 실질적으로 동일한 구성을 갖고 동일한 작용효과를 이루는 것은 어떠한 것이라도 본 발명의 기술적 범위에 포함된다 할 것이다.In the present invention, the above embodiments are merely examples, and the present invention is not limited thereto. Anything that has substantially the same configuration as the technical idea described in the claims of the present invention and achieves the same operation and effects will be included in the technical scope of the present invention.

특히, 본 발명은 상기 실시예에서 조강혼합재료로서 알루미나계 초속경클링커분말, 비정질알루미나계 초속경클링커분말, 아윈계 초속경클링커분말 등을 예로 들었지만, 이러한 조강혼합재료 이외에 속경성의 성질을 나타내고 경제성이 인정되는 다른 조강혼합재료에도 본 발명의 제조장치 및 제조방법이 적용될 수 있음은 물론이다.
In particular, the present invention exemplifies alumina-based ultrafast hard clinker powder, amorphous alumina ultrafast hard clinker powder, Arwin-based ultrafast hard clinker powder, etc. as a crude steel mixture material, but exhibits fast hardening properties in addition to these crude steel mixture materials. It goes without saying that the manufacturing apparatus and manufacturing method of the present invention can be applied to other crude steel mixed materials that are recognized economically.

100: 고성능 또는 속경성 콘크리트 제조장치
110: 보통콘크리트 형성부
120: 유동혼화제 및 혼합재료 투입부
130: 고성능 또는 속경성 콘크리트 형성부
140: 고성능 또는 속경성 콘크리트 숏팅부100: High-performance or fast-hardening concrete manufacturing equipment
110: ordinary concrete forming part
120: fluid admixture and mixed material input unit
130: high-performance or fast-hardening concrete formation
140: high-performance or fast-hardening concrete shorting part

Claims (32)

물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성부와;
상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입부와;
상기 보통콘크리트가 적재되는 레미콘트럭 내부에 형성되어 모터의 동력으로 회전하는 축이 구비되고, 상기 축에 적어도 1단 이상 방상으로 형성되어 보통콘크리트와 유동혼화제 및 혼합재료 투입부로부터 투입되는 유동혼화제 및 혼합재료를 혼합부재로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성부와;
상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅부를 포함하여 구성되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
An ordinary concrete forming unit for forming ordinary concrete by mixing water, cement, and aggregate in a certain ratio;
A fluid admixture and a mixed material input unit for mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete;
It is formed inside the ready-mixed concrete truck in which the ordinary concrete is loaded and has a shaft that rotates with the power of a motor, and is formed in at least one stage on the shaft, and a fluid admixture that is introduced from the input unit of the common concrete and the fluid admixture and the mixed material, and A high-performance or fast-hardening concrete forming unit for forming high-performance or fast-hardening concrete by mixing mixed materials with a mixing member;
When discharging the high-performance or fast-setting concrete, the slump whose fluidity is increased due to the fluid admixture while the mixed material is dispersed through the scattering and impact of the material by shorting it with air of 5 atm or higher before the fluid admixture is mixed by the dissipation of the fluid admixture. High-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized by comprising a high-performance or fast-setting concrete shorting unit that shortens the slump range of concrete and shorting high-performance or fast-setting concrete. Manufacturing equipment.
물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성부와;
상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입부와;
상기 보통콘크리트와 유동혼화제 및 혼합재료를 공급받는 호퍼가 구비되고, 상기 호퍼로 공급되는 보통콘크리트와 유동혼화제 및 혼합재료 투입부로부터 투입되는 유동혼화제와 혼합재료를 스크류의 회전으로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성부와;
상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅부를 포함하여 구성되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
An ordinary concrete forming unit for forming ordinary concrete by mixing water, cement, and aggregate in a certain ratio;
A fluid admixture and a mixed material input unit for mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete;
A hopper to receive the normal concrete, fluid admixture, and mixed material is provided, and the fluid admixture and the mixed material input from the input unit of the ordinary concrete, fluid admixture, and mixed material supplied to the hopper are mixed with rotation of a screw. A high-performance or fast-setting concrete forming unit for forming hard concrete;
When discharging the high-performance or fast-setting concrete, the slump whose fluidity is increased due to the fluid admixture while the mixed material is dispersed through the scattering and impact of the material by shorting it with air of 5 atm or higher before the fluid admixture is mixed by the dissipation of the fluid admixture. High-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized by comprising a high-performance or fast-setting concrete shorting unit that shortens the slump range of concrete and shorting high-performance or fast-setting concrete. Manufacturing equipment.
청구항 1 또는 청구항 2에 있어서, 상기 유동혼화제는,
AE감수제, 감수제, 고성능감수제, 유동화제, 고유동화제 중 어느 하나이거나 하나 이상 혼합한 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 1 or 2, wherein the fluid admixture,
A high-performance or fast-setting concrete manufacturing device through shorting after mixing a fluid admixture and a mixed material into ordinary concrete, characterized in that any one or more of an AE water reducing agent, a water reducing agent, a high performance water reducing agent, a fluidizing agent, and a high fluidizing agent is mixed.
청구항 1 또는 청구항 2에 있어서, 상기 유동혼화제는,
상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5 중량부 이하로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 1 or 2, wherein the fluid admixture,
An apparatus for producing high-performance or fast-hardening concrete through shorting after mixing a fluid admixture and a mixed material into ordinary concrete, characterized in that 5 parts by weight or less are mixed based on 100 parts by weight of cement forming the ordinary concrete.
청구항 1 또는 청구항 2에 있어서, 상기 혼합재료는,
실리카퓸, 메타카올린, 플라이애쉬, 고로슬래그미분말, 라텍스, 폴리머, 조강혼합재료 중 어느 하나이거나 하나 이상 혼합하는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method according to claim 1 or 2, wherein the mixed material,
High-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete characterized by mixing one or more of silica fume, metakaolin, fly ash, blast furnace slag powder, latex, polymer, and crude steel mixture Manufacturing equipment.
청구항 5에 있어서,
상기 실리카퓸은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~15 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 5,
The silica fume is mixed in an amount of 5 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and a high-performance or fast-setting concrete manufacturing apparatus through shorting after mixing a fluid admixture and a mixed material into ordinary concrete.
청구항 5에 있어서,
상기 메타카올린은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 7~20 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 5,
The metakaolin is mixed in an amount of 7 to 20 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and a high-performance or fast-setting concrete manufacturing apparatus through shorting after mixing a fluid admixture and a mixed material into ordinary concrete.
청구항 5에 있어서,
상기 플라이애쉬와 고로슬래그미분말은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 5,
The fly ash and the blast furnace slag powder are mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.After mixing a fluid admixture and a mixed material into ordinary concrete, high-performance or fast-hardening concrete through shorting Manufacturing equipment.
청구항 5에 있어서,
상기 라텍스와 폴리머는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 3~15 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 5,
The latex and polymer are mixed in an amount of 3 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and a high-performance or fast-setting concrete manufacturing apparatus through shorting after mixing a fluid admixture and a mixed material into ordinary concrete.
청구항 5에 있어서, 상기 조강혼합재료는,
알루미나계 초속경클링커분말, 비정질알루미나계 초속경클링커분말, 아윈계 초속경클링커분말 중 어느 하나 또는 하나 이상 혼합하는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method according to claim 5, wherein the crude steel mixture material,
High-performance or fast-hardening through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized by mixing one or more of alumina-based ultra-fast hard clinker powder, amorphous alumina-based ultra-fast hard clinker powder, and Arwin-based ultra-fast hard clinker powder. Concrete manufacturing equipment.
청구항 10에 있어서,
조강콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~20 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 10,
In order to manufacture crude steel concrete, the crude steel mixture material is mixed in an amount of 5 to 20 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete. After mixing a fluid admixture and a mixed material into ordinary concrete, high performance or fast Hard concrete manufacturing equipment.
청구항 10에 있어서,
초조강콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 10,
In order to manufacture ultra-crude concrete, the crude steel mixture is mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.After mixing a fluid admixture and a mixed material into ordinary concrete, high performance through shorting or Rapid setting concrete manufacturing equipment.
청구항 10에 있어서,
초속경콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 25~40 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 10,
In order to manufacture ultra-fast-hard concrete, the crude steel mixture material is mixed in an amount of 25 to 40 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.After mixing a fluid admixture and a mixed material into ordinary concrete, high performance through shorting or Rapid setting concrete manufacturing equipment.
청구항 1 또는 청구항 2에 있어서,
상기 보통콘크리트에 유동혼화제와 혼합재료를 순차적으로 투입하는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method according to claim 1 or 2,
A high-performance or fast-hardening concrete manufacturing apparatus through shorting after mixing a fluid admixture and a mixed material into the ordinary concrete, characterized in that sequentially adding a fluid admixture and a mixed material to the ordinary concrete.
청구항 1 또는 청구항 2에 있어서, 상기 고성능 또는 속경성 콘크리트 숏팅부는,
상기 고성능 또는 속경성 콘크리트가 압축되어 배출되도록 내부가 관통된 양단부보다 중앙부의 직경이 작게 형성되어 고성능 또는 속경성 콘크리트 형성부에 착탈가능하게 장착되는 숏팅안내부재와;
상기 숏팅안내부재로 이동되는 고성능 또는 속경성 콘크리트에 포함된 유동혼화제를 소산시키기 위해 5기압 이상의 고압의 공기를 공급하도록 숏팅안내부재에 관통된 공기공급공을 포함하여 구비되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method according to claim 1 or 2, wherein the high-performance or fast-setting concrete shorting unit,
A shorting guide member having a diameter of a central portion smaller than both ends through which the high-performance or fast-setting concrete is compressed and discharged, and detachably mounted on the high-performance or fast-setting concrete forming portion;
Ordinary concrete, characterized in that it includes an air supply hole penetrating the shorting guide member to supply high-pressure air of 5 atm or higher in order to dissipate the fluid admixture contained in the high-performance or fast-setting concrete that is moved to the shorting guide member. High-performance or fast-hardening concrete manufacturing equipment through shorting after mixing fluid admixtures and mixed materials into
청구항 15에 있어서, 상기 공기공급공은,
상기 숏팅안내부재의 외주면에 방사상으로 경사지게 형성되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조장치.
The method of claim 15, wherein the air supply hole,
A high-performance or fast-hardening concrete manufacturing apparatus through shorting after mixing a fluid admixture and a mixed material into ordinary concrete, characterized in that it is formed to be inclined radially on the outer peripheral surface of the shorting guide member.
물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성단계와;
상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입단계와;
상기 보통콘크리트가 적재되는 레미콘트럭 내부에 형성되어 모터의 동력으로 회전하는 축이 구비되고, 상기 축에 적어도 1단 이상 방상으로 형성되어 보통콘크리트와 유동혼화제 및 혼합재료 투입부로부터 투입되는 유동혼화제 및 혼합재료를 혼합부재로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성단계와;
상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅단계를 포함하여 이루어지는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
Ordinary concrete forming step of forming ordinary concrete by mixing water, cement, and aggregate in a certain ratio;
A flow admixture and a mixed material input step of mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete;
It is formed inside the ready-mixed concrete truck in which the ordinary concrete is loaded and has a shaft that rotates with the power of a motor, and is formed in at least one stage on the shaft, and a fluid admixture that is introduced from the input unit of the common concrete and the fluid admixture and the mixed material, and A high-performance or fast-hardening concrete forming step of mixing the mixed material with a mixing member to form high-performance or fast-hardening concrete;
When discharging the high-performance or fast-setting concrete, the slump whose fluidity is increased due to the fluid admixture while the mixed material is dispersed through the scattering and impact of the material by shorting it with air of 5 atm or higher before the fluid admixture is mixed by the dissipation of the fluid admixture. High-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized in that it includes a high-performance or fast-hardening concrete shorting step that shortens high-performance or fast-hardening concrete reduced close to the slump range of concrete. Manufacturing method.
물, 시멘트, 골재를 일정비율로 배합하여 보통콘크리트를 형성하는 보통콘크리트 형성단계와;
상기 보통콘크리트의 슬럼프 증가 및 강도를 조절하도록 보통콘크리트에 유동혼화제 및 혼합재료를 혼입하는 유동혼화제 및 혼합재료 투입단계와;
상기 보통콘크리트와 유동혼화제 및 혼합재료를 공급받는 호퍼가 구비되고, 상기 호퍼로 공급되는 보통콘크리트와 유동혼화제 및 혼합재료 투입부로부터 투입되는 유동혼화제와 혼합재료를 스크류의 회전으로 혼합하여 고성능 또는 속경성 콘크리트를 형성하는 고성능 또는 속경성 콘크리트 형성단계와;
상기 고성능 또는 속경성 콘크리트를 배출할 때, 5기압 이상의 공기로 숏팅하여 재료의 비산과 충격으로 혼합재료를 분산시키면서 유동혼화제로 인해 유동성이 증가한 슬럼프를 유동혼화제의 소산으로 유동혼화제가 혼입되기 전의 보통콘크리트의 슬럼프 범위와 근접하게 감소시킨 고성능 또는 속경성 콘크리트를 숏팅하는 고성능 또는 속경성 콘크리트 숏팅단계를 포함하여 구성되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
Ordinary concrete forming step of forming ordinary concrete by mixing water, cement, and aggregate in a certain ratio;
A flow admixture and a mixed material input step of mixing a fluid admixture and a mixed material into the ordinary concrete to adjust the slump increase and strength of the ordinary concrete;
A hopper to receive the normal concrete, fluid admixture, and mixed material is provided, and the fluid admixture and the mixed material input from the input unit of the ordinary concrete, fluid admixture, and mixed material supplied to the hopper are mixed with rotation of a screw. High-performance or fast-setting concrete forming step of forming hard concrete;
When discharging the high-performance or fast-setting concrete, the slump whose fluidity is increased due to the fluid admixture while the mixed material is dispersed through the scattering and impact of the material by shorting it with air of 5 atm or higher before the fluid admixture is mixed by the dissipation of the fluid admixture. High-performance or fast-hardening through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized by comprising a high-performance or fast-setting concrete shorting step that shortens high-performance or fast-setting concrete that has been reduced close to the slump range of concrete. Concrete manufacturing method.
청구항 18에 있어서, 상기 유동혼화제는,
AE감수제, 감수제, 고성능감수제, 유동화제, 고유동화제 중 어느 하나이거나 하나 이상 혼합한 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 18, wherein the fluid admixture,
A method for producing high-performance or fast-setting concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized in that any one or more of an AE water reducing agent, water reducing agent, high performance water reducing agent, fluidizing agent, and high fluidizing agent is mixed.
청구항 18에 있어서, 상기 유동혼화제는,
상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5 중량부 이하로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 18, wherein the fluid admixture,
A method for producing high-performance or fast-hardening concrete through shorting after mixing a fluid admixture and a mixed material into ordinary concrete, characterized in that 5 parts by weight or less are mixed based on 100 parts by weight of cement forming the ordinary concrete.
청구항 18에 있어서, 상기 혼합재료는,
실리카퓸, 메타카올린, 플라이애쉬, 고로슬래그미분말, 라텍스, 폴리머, 조강혼합재료 중 어느 하나이거나 하나 이상 혼합하는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 18, wherein the mixed material,
High-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into ordinary concrete characterized by mixing one or more of silica fume, metakaolin, fly ash, blast furnace slag powder, latex, polymer, and crude steel mixture Manufacturing method.
청구항 21에 있어서,
상기 실리카퓸은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~15 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 21,
The silica fume is mixed in an amount of 5 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and a method for producing high-performance or fast-setting concrete through shorting after mixing a fluid admixture and a mixed material into ordinary concrete.
청구항 21에 있어서,
상기 메타카올린은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 7~20 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 21,
The metakaolin is mixed in an amount of 7 to 20 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and a method for producing high-performance or fast-setting concrete through shorting after mixing a fluid admixture and a mixed material into ordinary concrete.
청구항 21에 있어서,
상기 플라이애쉬와 고로슬래그미분말은, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 21,
The fly ash and the blast furnace slag fine powder are mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of cement forming the ordinary concrete.After mixing a fluid admixture and a mixed material into ordinary concrete, high-performance or fast-setting concrete through shorting Manufacturing method.
청구항 21에 있어서,
상기 라텍스와 폴리머는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 3~15 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 21,
The latex and polymer are mixed in an amount of 3 to 15 parts by weight based on 100 parts by weight of cement forming the ordinary concrete, and a high-performance or fast-setting concrete manufacturing method through shorting after mixing a fluid admixture and a mixed material into ordinary concrete.
청구항 21에 있어서, 상기 조강혼합재료는,
알루미나계 초속경클링커분말, 비정질알루미나계 초속경클링커분말, 아윈계 초속경클링커분말 중 어느 하나 또는 하나 이상 혼합하는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 21, wherein the crude steel mixture material,
High-performance or fast-hardening through shorting after mixing fluid admixtures and mixed materials into ordinary concrete, characterized by mixing one or more of alumina-based ultra-fast hard clinker powder, amorphous alumina-based ultra-fast hard clinker powder, and Arwin-based ultra-fast hard clinker powder. Concrete manufacturing method.
청구항 26에 있어서,
조강콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 5~20 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 26,
In order to manufacture crude steel concrete, the crude steel mixture material is mixed in an amount of 5 to 20 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete. After mixing a fluid admixture and a mixed material into ordinary concrete, high performance or fast Hard concrete manufacturing method.
청구항 26에 있어서,
초조강콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 15~25 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 26,
In order to manufacture ultra-crude concrete, the crude steel mixture is mixed in an amount of 15 to 25 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.After mixing a fluid admixture and a mixed material into ordinary concrete, high performance through shorting or Fast-hardening concrete manufacturing method.
청구항 26에 있어서,
초속경콘크리트를 제조하기 위해 상기 조강혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 25~40 중량부로 혼합되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 26,
In order to manufacture ultra-fast-hard concrete, the crude steel mixture material is mixed in an amount of 25 to 40 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.After mixing a fluid admixture and a mixed material into ordinary concrete, high performance through shorting or Fast-hardening concrete manufacturing method.
청구항 18 또는 청구항 19에 있어서,
상기 보통콘크리트에 유동혼화제와 혼합재료를 순차적으로 투입하는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 18 or 19,
A method for producing high-performance or fast-setting concrete through shorting after mixing a fluid admixture and a mixed material into the ordinary concrete, characterized in that the fluid admixture and the mixed material are sequentially added to the ordinary concrete.
청구항 18 또는 청구항 19에 있어서, 상기 고성능 또는 속경성 콘크리트 숏팅단계는,
상기 고성능 또는 속경성 콘크리트가 압축되어 배출되도록 내부가 관통된 양단부보다 중앙부의 직경이 작게 형성되어 고성능 또는 속경성 콘크리트 형성부에 착탈가능하게 장착되는 숏팅안내부재와;
상기 숏팅안내부재로 이동되는 고성능 또는 속경성 콘크리트에 포함된 유동혼화제를 소산시키기 위해 5기압 이상의 고압의 공기를 공급하도록 숏팅안내부재에 관통된 공기공급공을 포함하여 구비되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 18 or 19, wherein the high-performance or fast-setting concrete shorting step,
A shorting guide member having a diameter of a central portion smaller than both ends through which the high-performance or fast-setting concrete is compressed and discharged, and detachably mounted on the high-performance or fast-setting concrete forming portion;
Ordinary concrete, characterized in that it includes an air supply hole penetrating the shorting guide member to supply high-pressure air of 5 atm or higher in order to dissipate the fluid admixture contained in the high-performance or fast-setting concrete that is moved to the shorting guide member. A method for producing high-performance or fast-hardening concrete through shorting after mixing fluid admixtures and mixed materials into
청구항 31에 있어서, 상기 공기공급공은,
상기 숏팅안내부재의 외주면에 방사상으로 경사지게 형성되는 것을 특징으로 하는 보통콘크리트에 유동혼화제 및 혼합재료 혼입 후 숏팅을 통한 고성능 또는 속경성 콘크리트 제조방법.
The method of claim 31, wherein the air supply hole,
A method of producing high-performance or fast-hardening concrete through shorting after mixing a fluid admixture and a mixed material into ordinary concrete, characterized in that it is formed to be inclined radially on the outer peripheral surface of the shorting guide member.
KR1020140016537A 2014-02-13 2014-02-13 The high-performance or fast hardening concrete and manufacturing method thereof KR102155825B1 (en)