KR101965896B1 - Hard coating composition and scattering protecting film using the same - Google Patents

Hard coating composition and scattering protecting film using the same Download PDF

Info

Publication number
KR101965896B1
KR101965896B1 KR1020140111460A KR20140111460A KR101965896B1 KR 101965896 B1 KR101965896 B1 KR 101965896B1 KR 1020140111460 A KR1020140111460 A KR 1020140111460A KR 20140111460 A KR20140111460 A KR 20140111460A KR 101965896 B1 KR101965896 B1 KR 101965896B1
Authority
KR
South Korea
Prior art keywords
hard coating
solvent
weight
film
coating composition
Prior art date
Application number
KR1020140111460A
Other languages
Korean (ko)
Other versions
KR20160025119A (en
Inventor
홍주희
조홍관
김장순
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020140111460A priority Critical patent/KR101965896B1/en
Priority to PCT/KR2015/008765 priority patent/WO2016032173A1/en
Priority to TW104127944A priority patent/TW201615771A/en
Publication of KR20160025119A publication Critical patent/KR20160025119A/en
Application granted granted Critical
Publication of KR101965896B1 publication Critical patent/KR101965896B1/en

Abstract

본 발명은 자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함하고, 상기 혼합 용제는 케톤계 용제 및 알코올계 용제를 포함하는 것을 특징으로 하는 하드코팅 조성물 및 이를 이용한 비산 방지 필름에 관한 것이다.The present invention relates to an ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent, wherein the mixed solvent comprises a ketone-based solvent and an alcohol-based solvent, and a shatterproof film using the same.

Description

하드코팅 조성물 및 이를 이용한 비산 방지 필름{HARD COATING COMPOSITION AND SCATTERING PROTECTING FILM USING THE SAME}TECHNICAL FIELD [0001] The present invention relates to a hard coating composition and a shatterproof film using the coating composition,

본 발명은 하드코팅 조성물 및 이를 이용한 표면 경도 및 광학적 특성이 우수한 비산 방지 필름에 관한 것이다.
The present invention relates to a hard coating composition and a light-scattering film excellent in surface hardness and optical characteristics using the same.

휴대폰 등에 적용되는 터치 스크린 패널의 구조는 종래 다층형 구조에서 일체형 구조로 전환되는 추세에 있다. 이는 일체형 터치스크린 패널 구조는 원가 비중이 높은 투명전극(ITO) 필름을 사용하지 않아도 되는 점에 기인한다.The structure of a touch screen panel applied to a mobile phone or the like is shifting from a conventional multilayer structure to an integral structure. This is because the integrated touch screen panel structure does not require the use of a transparent electrode (ITO) film having a high cost ratio.

일체형 터치스크린 패널 구조를 통하여, 제품의 슬림화가 가능하며 가시광선 투과율을 높일 수 있다. 이 같은 장점에도 불구하고 낙하 충격 등에 의해 표시면측의 커버 유리가 깨지는 문제가 빈번히 발생하고 있다.Through the integrated touch screen panel structure, it is possible to make the product slimmer and to increase the visible light transmittance. Despite these advantages, the problem of breaking the cover glass on the display surface side frequently occurs due to the drop impact.

이에 따라, 휴대기기의 유리 파손시 발생하는 파편에 대한 안정성을 강화하기 위하여, 패널과 커버 유리 사이에 비산 방지 필름을 삽입하여 커버 유리의 비산을 방지하고 있다.Accordingly, in order to enhance the stability against fragments generated when the glass of the portable device is broken, a scattering prevention film is inserted between the panel and the cover glass to prevent scattering of the cover glass.

이러한 비산 방지 필름은 하드코팅층/기재/점착층의 구조를 포함하는 것이 일반적이며, 그 특성상 하드코팅층에 표면 경도 및 광학적 특성이 요구된다.
Such a shatterproof film generally includes a structure of a hard coat layer / substrate / adhesive layer, and the hard coat layer is required to have surface hardness and optical properties by its nature.

본 발명은 자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함하고, 상기 혼합 용제는 케톤계 용제 및 알코올계 용제를 포함하는 것을 특징으로 하는 하드코팅 조성물 및 이를 이용한 표면 경도 및 광학적 특성이 우수한 비산 방지 필름을 제공하고자 한다.The present invention relates to an ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent, wherein the mixed solvent comprises a ketone-based solvent and an alcohol-based solvent, and a shatterproof film excellent in surface hardness and optical characteristics using the same.

그러나, 본 발명이 이루고자 하는 기술적 과제는 이상에서 언급한 과제에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
However, the technical problem to be solved by the present invention is not limited to the above-mentioned problems, and other matters not mentioned can be clearly understood by those skilled in the art from the following description.

본 발명은 자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함하고, 상기 혼합 용제는 케톤계 용제 및 알코올계 용제를 포함하는 것을 특징으로 하는 하드코팅 조성물을 제공한다.The present invention relates to an ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent, wherein the mixed solvent comprises a ketone-based solvent and an alcohol-based solvent.

상기 혼합 용제의 극성도는 3 내지 5일 수 있다.The polarity of the mixed solvent may be 3 to 5.

상기 혼합 용제는 아마이드계 용제, 탄화수소계 용제, 에스테르계 용제, 에테르계 용제 및 글리콜계 용제로 이루어진 군으로부터 선택된 하나 이상의 기타 용제를 더 포함하는 것을 특징으로 할 수 있다.The mixed solvent may further include at least one other solvent selected from the group consisting of an amide-based solvent, a hydrocarbon-based solvent, an ester-based solvent, an ether-based solvent and a glycol-based solvent.

상기 혼합 용제는 케톤계 용제 60~80 중량%, 알코올계 용제 15~35 중량% 및 기타 용제 5~10 중량%를 포함하는 것을 특징으로 할 수 있다.The mixed solvent may include 60 to 80 wt% of a ketone solvent, 15 to 35 wt% of an alcohol solvent, and 5 to 10 wt% of another solvent.

상기 무기 나노입자의, 50% 누적질량 입자크기 분포 직경을 D50이라 할 때, 5nm<D50<20nm일 수 있다.When the 50% cumulative mass particle size distribution diameter of the inorganic nanoparticles is D50, 5 nm < D50 < 20 nm.

상기 조성물 총 100 중량부에 대하여, 자외선 경화형 아크릴레이트 수지 10~70 중량부; 무기 나노입자 1~30 중량부; 광개시제 1~15 중량부일 수 있다.10 to 70 parts by weight of an ultraviolet curing type acrylate resin, based on 100 parts by weight of the total composition; 1 to 30 parts by weight of inorganic nanoparticles; 1 to 15 parts by weight of a photoinitiator.

상기 조성물은 무기 나노입자에 의한 네트워크 구조를 형성할 수 있다.The composition can form a network structure with inorganic nanoparticles.

본 발명의 일 구현예로, 투명 필름; 및 상기 투명 필름의 상부에 형성된 하드코팅층을 포함하고, 상기 하드코팅층은 상기 하드코팅 조성물로 형성된 것인 비산 방지 필름을 제공한다.In one embodiment of the present invention, a transparent film; And a hard coating layer formed on the transparent film, wherein the hard coating layer is formed of the hard coating composition.

상기 하드코팅층의 두께는 0.1㎛ 내지 1㎛일 수 있다.The thickness of the hard coating layer may be 0.1 탆 to 1 탆.

상기 하드코팅층의 연필 경도는 1H 내지 9H일 수 있다.The pencil hardness of the hard coat layer may be from 1 H to 9H.

상기 하드코팅층의 투과율은 90% 내지 100%일 수 있다.The transmittance of the hard coating layer may be 90% to 100%.

상기 투명 필름의 하부에 형성된 점착층을 더 포함할 수 있다.And an adhesive layer formed on the lower portion of the transparent film.

상기 점착층의 하부에 형성된 이형 필름을 더 포함할 수 있다.
And a release film formed under the adhesive layer.

본 발명에 따른 하드코팅 조성물은 자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함하고, 상기 혼합 용제는 케톤계 용제 및 알코올계 용제를 포함하는 것을 특징으로 하는바, 무기 나노입자에 의한 네트워크 구조를 형성함으로써, 이로 형성된 하드코팅층은 얇은 두께를 가지더라도, 표면 경도 및 광학적 특성이 우수한 비산 방지 필름을 제조할 수 있다.
The hard coating composition according to the present invention comprises an ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent, wherein the mixed solvent comprises a ketone-based solvent and an alcohol-based solvent. By forming a network structure by the inorganic nanoparticles, the hard coating layer formed thereby has a thin thickness, It is possible to produce a shrink-preventive film excellent in hardness and optical characteristics.

도 1은 본 발명의 실시예 1 및 비교예 1에 따른 비산 방지 필름에서 하드코팅층의 주사전자현미경(SEM) 사진이다.
도 2는 본 발명의 일 구현예에 따른 비산 방지 필름을 개략적으로 나타낸 단면도이다.1 is a scanning electron microscope (SEM) photograph of a hard coat layer in the anti-scattering film according to Example 1 and Comparative Example 1 of the present invention.
2 is a cross-sectional view schematically showing a light-scattering film according to an embodiment of the present invention.

이하, 첨부한 도면을 참고로 하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings, which will be readily apparent to those skilled in the art to which the present invention pertains. The present invention may be embodied in many different forms and is not limited to the embodiments described herein.

본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조 부호를 붙이도록 한다.In order to clearly illustrate the present invention, parts not related to the description are omitted, and the same or similar components are denoted by the same reference numerals throughout the specification.

도면에서 여러 층 및 영역을 명확하게 표현하기 위하여 두께를 확대하여 나타내었다. 그리고 도면에서, 설명의 편의를 위해, 일부 층 및 영역의 두께를 과장되게 나타내었다.In the drawings, the thickness is enlarged to clearly represent the layers and regions. In the drawings, for the convenience of explanation, the thicknesses of some layers and regions are exaggerated.

이하에서 기재의 “상부 (또는 하부)”에 임의의 구성이 형성된다는 것은, 임의의 구성이 상기 기재의 상면 (또는 하면)에 접하여 형성되는 것을 의미할 뿐만 아니라, 상기 기재와 기재 상에 (또는 하에) 형성된 임의의 구성 사이에 다른 구성을 포함하지 않는 것으로 한정하는 것은 아니다.
Hereinafter, formation of an arbitrary structure in the "upper (or lower)" of the description means not only that an arbitrary structure is formed in contact with the upper surface (or lower surface) of the substrate, It is to be understood that the invention is not to be limited to the specific embodiments thereof.

하드코팅Hard coating 조성물 Composition

본 발명은 자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함하고, 상기 혼합 용제는 케톤계 용제 및 알코올계 용제를 포함하는 것을 특징으로 하는 하드코팅 조성물을 제공한다.The present invention relates to an ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent, wherein the mixed solvent comprises a ketone-based solvent and an alcohol-based solvent.

즉, 상기 하드코팅 조성물은 비산 방지 필름의 하드코팅층에 이용되기 위한 것으로, 자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함한다.That is, the hard coating composition for use in the hard coat layer of the anti-scattering film includes an ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent.

상기 하드코팅 조성물은 혼합 용제의 일정 극성도로 인하여 무기 나노입자에 의한 네트워크 구조를 형성하는 것을 특징으로 하는바, 이로 형성된 하드코팅층이 얇은 두께를 가지더라도 표면 경도가 우수하다.
The hard coating composition is characterized by forming a network structure of inorganic nanoparticles due to a certain polarity of the mixed solvent. The hard coating layer formed thereon is excellent in surface hardness even though it has a small thickness.

상기 자외선 경화형 아크릴레이트 수지는 적어도 2개 이상, 바람직하게 2~15개의 관능기를 포함하여 경도 향상 및 주름(Curl) 방지에 기여한다. 이때, 자외선 경화형 아크릴레이트 수지에 포함된 관능기의 수가 2개 미만이면 그 첨가 효과가 불충분할 수 있고, 반면에, 관능기의 수가 15개를 초과하면 주름 발생을 초래할 수 있다.The ultraviolet curing type acrylate resin contains at least two functional groups, preferably 2 to 15 functional groups, and contributes to hardness improvement and curl prevention. If the number of functional groups contained in the ultraviolet curable acrylate resin is less than 2, the effect of the addition may be insufficient. On the other hand, if the number of functional groups exceeds 15, wrinkles may be generated.

또한, 상기 자외선 경화형 아크릴레이트 수지는 조성물 총 100 중량부에 대하여 10~70 중량부로 첨가될 수 있다. 이때, 자외선 경화형 아크릴레이트 수지가 10 중량부 미만일 경우, 그 첨가 효과가 불충분할 수 있고, 자외선 경화형 아크릴레이트 수지가 70 중량부를 초과하는 경우, 코팅액이 가진 기능성이 부여되지 않을 수 있다.
The ultraviolet curable acrylate resin may be added in an amount of 10 to 70 parts by weight based on 100 parts by weight of the total composition. If the content of the ultraviolet curing type acrylate resin is less than 10 parts by weight, the effect of the addition may be insufficient, and if the amount of the ultraviolet curing type acrylate resin exceeds 70 parts by weight, the functionalities of the coating solution may not be imparted.

상기 무기 나노입자는 나노 크기의 무기 입자를 의미하는 것으로, 경도 및 주름(Curl)을 확보하기 위한 것이다. 상기 무기 나노입자는 실리카, 알루미나, 지르코니아, 제올라이트, 티타늄 산화물 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있고, 이 중 성능 및 비용적인 측면에서 실리카인 것이 더욱 바람직하나, 이에 한정되지 않는다. The inorganic nanoparticles mean nano-sized inorganic particles and are intended to secure hardness and curl. The inorganic nanoparticles may be at least one selected from the group consisting of silica, alumina, zirconia, zeolite, titanium oxide, and combinations thereof. Among them, silica is more preferable in view of performance and cost.

상기 무기 나노입자의, 상기 조성물 내 입자 분포에서 50% 누적질량 입자크기 분포 직경을 D50이라 할 때, 5nm<D50<20nm 일 수 있어, 무기 나노입자가 완전히 분산되지도 않고, 무기 나노입자가 분산되지 못하고 뭉치게 되지도 않는 채, 상기 조성물 내 네트워크 구조를 형성할 수 있다.When the 50% cumulative mass particle size distribution diameter of the inorganic nanoparticles in the particle distribution in the composition is defined as D50, 5 nm < D50 < 20 nm and the inorganic nanoparticles are not completely dispersed, The network structure in the composition can be formed without being aggregated or aggregated.

또한, 상기 무기 나노입자는 조성물 총 100 중량부에 대하여 1~30 중량부로 첨가될 수 있다. 이때, 무기 나노입자가 1 중량부 미만일 경우, 그 첨가 효과가 불충분할 수 있고, 무기 나노입자가 30 중량부를 초과하는 경우, 코팅액이 가진 기능성이 부여되지 않을 수 있다.
The inorganic nanoparticles may be added in an amount of 1 to 30 parts by weight based on 100 parts by weight of the total composition. If the amount of the inorganic nanoparticles is less than 1 part by weight, the effect of the addition may be insufficient. If the amount of the inorganic nanoparticles exceeds 30 parts by weight, the functionalities of the coating solution may not be imparted.

상기 광개시제는 자외선에 의해 여기되어 광중합을 개시하는 역할을 한다. 상기 광개시제로 공지의 광개시제를 사용할 수 있고, 벤조페논; 치환된 벤조페논; 아세토페논; 치환된 아세토페논; 벤조인; 벤조인 알킬 에스테르; 크산톤; 치환된 크산톤; 포스핀 옥시드; 디에톡시-아세토페논; 벤조인 메틸 에테르; 벤조인 에틸 에테르; 벤조인 이소프로필 에테르; 디에톡시크산톤; 클로로-티오-크산톤; N-메틸 디에탄올-아민-벤조페논; 2-히드록시-2-메틸-1-페닐-프로판-1-온; 2-벤질-2-(디메틸아미노)-1-[4-(4-모르폴리닐)페닐]-1-부탄온; 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상을 사용하는 것이 바람직하나, 이에 한정되지 않는다.The photoinitiator is excited by ultraviolet light to initiate photopolymerization. A known photoinitiator may be used as the photoinitiator, and benzophenone; Substituted benzophenones; Acetophenone; Substituted acetophenones; Benzoin; Benzoin alkyl esters; Xanthone; Substituted xanthones; Phosphine oxide; Diethoxy-acetophenone; Benzoin methyl ether; Benzoin ethyl ether; Benzoin isopropyl ether; Diethoxysilane; Chloro-thioxanthone; N-methyldiethanol-amine-benzophenone; 2-hydroxy-2-methyl-1-phenyl-propan-1-one; 2-Benzyl-2- (dimethylamino) -1- [4- (4-morpholinyl) phenyl] -1-butanone; And combinations thereof. However, the present invention is not limited thereto.

또한, 상기 광개시제는 조성물 총 100 중량부에 대하여 1~15 중량부로 첨가될 수 있다. 이때, 광개시제가 1 중량부 미만일 경우, 경화 반응 시간이 길어지는 문제점이 있고, 광개시제가 15 중량부를 초과하는 경우, 미반응 광개시제가 불순물로 잔존할 수 있는 문제점이 있다.
The photoinitiator may be added in an amount of 1 to 15 parts by weight based on 100 parts by weight of the composition. When the amount of the photoinitiator is less than 1 part by weight, the curing reaction time may become longer. When the amount of the photoinitiator exceeds 15 parts by weight, the unreacted photoinitiator may remain as an impurity.

상기 혼합 용제는 케톤계 용제 및 알코올계 용제를 포함하는 것을 특징으로 한다. 케톤계 용제로는 메틸에틸케톤, 메틸이소부틸케톤, 1-메틸-2-피롤리디논, 시클로헥사논 또는 아세톤 등이 있고, 알코올계 용제로는 프로필렌글리콜모노메틸에테르, 메탄올, 에탄올, 이소프로필알코올 또는 부틸알코올 등이 있다.The mixed solvent is characterized by containing a ketone-based solvent and an alcohol-based solvent. Examples of the ketone-based solvent include methyl ethyl ketone, methyl isobutyl ketone, 1-methyl-2-pyrrolidinone, cyclohexanone, and acetone. Examples of the alcoholic solvent include propylene glycol monomethyl ether, methanol, ethanol, isopropyl Alcohol or butyl alcohol.

상기 혼합 용제의 극성도(Polarity Index)는 3~5일 수 있다. 이때, 혼합 용제의 극성도가 3 미만인 경우, 극성이 너무 낮아 무기 나노입자가 완전히 분산되어 무기 나노입자에 의한 네트워크 구조를 형성하지 못하는 문제점이 있고, 혼합 용제의 극성도가 5를 초과하는 경우, 극성이 너무 높아 무기 나노입자가 분산되지 못하고 뭉치게 되는 문제점이 있다. The polarity index of the mixed solvent may be 3 to 5. At this time, when the polarity of the mixed solvent is less than 3, the polarity is too low to completely disperse the inorganic nanoparticles to form a network structure of inorganic nanoparticles. If the polarity of the mixed solvent exceeds 5, There is a problem that the inorganic nanoparticles are not dispersed and aggregated because the polarity is too high.

상기 혼합 용제는 아마이드계 용제, 탄화수소계 용제, 에스테르계 용제, 에테르계 용제 및 글리콜계 용제로 이루어진 군으로부터 선택된 하나 이상의 기타 용제를 더 포함할 수 있다. 아마이드계 용제로는 N,N-디메틸아세트아마이드, N,N-디메틸포름아마이드, 디메틸설폭사이드, N-메틸피롤리돈 또는 포름아마이드 등이 잇고, 탄화수소계 용제로는 헥산 또는 헵탄 등과 같은 지방족 탄화수소계 용제 및 아니솔, 메시틸렌 또는 자일렌 등과 같은 방향족 탄화수소계 용제가 있고, 에스테르계 용제로는 메틸 아세테이트, 에틸 아세테이트, 프로필 아세테이트, 메틸프로피오네이트, 에틸 프로피오네이트, γ-부티로락톤, γ-발레로락톤, γ-카프로락톤, δ-발레로락톤 또는 ε-카프로락톤 등이 있으며, 에테르계 용제로는 테트라하이드로퓨란, 2-메틸테트라하이드로퓨란 또는 디부틸에테르 등이 있다.The mixed solvent may further include at least one other solvent selected from the group consisting of an amide-based solvent, a hydrocarbon-based solvent, an ester-based solvent, an ether-based solvent and a glycol-based solvent. Examples of the amide-based solvent include N, N-dimethylacetamide, N, N-dimethylformamide, dimethylsulfoxide, N-methylpyrrolidone or formamide. Examples of the hydrocarbon-based solvent include aliphatic hydrocarbons such as hexane or heptane Based solvents, and aromatic hydrocarbon-based solvents such as anisole, mesitylene or xylene. Examples of the ester-based solvent include methyl acetate, ethyl acetate, propyl acetate, methyl propionate, ethyl propionate,? -Butyrolactone, gamma -valerolactone, gamma -caprolactone, delta -valerolactone, or epsilon -caprolactone, and ether-based solvents include tetrahydrofuran, 2-methyltetrahydrofuran or dibutyl ether.

상기 혼합 용제가 케톤계 용제, 알코올계 용제 및 기타 용제를 포함하는 경우, 상기 혼합 용제는 케톤계 용제 60~80 중량%, 알코올계 용제 15~35 중량% 및 기타 용제 5~10 중량%를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이와 같은 중량비를 유지함으로써, 상기 혼합 용제는 일정 극성도를 가짐으로써 무기 나노입자의 적절한 분산을 유도하여, 하드코팅 조성물 내 네트워크 구조를 형성할 수 있다.
When the mixed solvent includes a ketone solvent, an alcohol solvent, and other solvents, the mixed solvent includes 60 to 80 wt% of a ketone solvent, 15 to 35 wt% of an alcohol solvent, and 5 to 10 wt% of another solvent But is not limited thereto. By maintaining such a weight ratio, the mixed solvent has a certain degree of polarity, thereby inducing appropriate dispersion of the inorganic nanoparticles to form a network structure in the hard coating composition.

상기 하드코팅 조성물은 비산 방지 필름에서 하드코팅층으로 사용되기 위해 하드코팅성을 유지할 수 있는한, 첨가제를 더 추가할 수 있는데, 예를 들면, 염료, 충전제(필러(filler)), 보강제, 난연제, 가소제, 윤활제, 안정제(산화방지제, 자외선 흡수제, 열안정제 등), 이형제, 대전방지제, 계면활성제, 분산제, 유동 조정제, 레벨링(leveling)제, 소포제, 표면개질제, 저응력화제(실리콘 오일(silicone oil), 실리콘고무, 각종 플라스틱 분말 등), 내열성 개량제 등을 더 추가할 수 있다.
The hard coating composition may further contain additives as long as it can maintain hard coatability for use as a hard coat layer in a light-scattering film, for example, a dye, a filler (filler), a reinforcing agent, A surfactant, a dispersing agent, a flow regulator, a leveling agent, a defoaming agent, a surface modifier, a silicone oil (a silicone oil), a lubricant, a stabilizer (antioxidant, ultraviolet absorber, heat stabilizer, etc.) ), Silicone rubber, various kinds of plastic powders, etc.), a heat resistance improving agent, and the like.

비산arsenic acid 방지 필름 Prevention film

본 발명은 투명 필름; 및 상기 투명 필름의 상부에 형성된 하드코팅층을 포함하고, 상기 하드코팅층은 상기 하드코팅 조성물로 형성된 것인 비산 방지 필름을 제공한다.
The present invention relates to a transparent film; And a hard coating layer formed on the transparent film, wherein the hard coating layer is formed of the hard coating composition.

도 2는 본 발명의 일 구현예에 따른 비산 방지 필름을 개략적으로 나타낸 단면도이다.2 is a cross-sectional view schematically showing a light-scattering film according to an embodiment of the present invention.

도 2를 참조하면, 본 발명의 일 구현예에 따른 비산 방지 필름은 위로부터 형성된 하드코팅층(120) 및 투명 필름(110)을 포함하고, 상기 투명 필름(110) 하부에 차례로 형성된 점착층(130) 및 이형 필름(140)을 더 포함할 수 있다.
2, the anti-scattering film according to an exemplary embodiment of the present invention includes a hard coating layer 120 and a transparent film 110 formed from above, and an adhesive layer 130 And a release film 140. The release film 140 may be formed of a resin.

상기 투명 필름(110)은 터치 스크린 패널(touch screen panel)의 강화유리와 같은 유리의 비산을 방지할 수 있도록 강도가 우수하고, 아울러 광학적 특성을 저해하지 않도록 투과율이 적어도 90% 이상, 바람직하게는 90~100%인 투명성이 우수한 필름일 수 있다.The transparent film 110 is excellent in strength to prevent scattering of glass such as tempered glass of a touch screen panel and has a transmittance of not less than 90% It may be a film having excellent transparency of 90 to 100%.

이러한 투명 필름(110)으로, 폴리에틸렌 테레프탈레이트(polyethylene terephthalate; PET), 폴리에틸렌 나프탈레이트(polyethylene naphthalate; PEN), 폴리에테르설폰(polyethersulfone; PES), 폴리 카보네이트(Poly carbonate; PC), 폴리에틸렌(polyethylene; PE), 폴리 프로필렌(poly propylene; PP) 또는 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상을 사용하는 것이 바람직하고, 가시광선 투과율이 92%인 광학용 PET 필름을 사용하는 것이 보다 바람직하나, 이에 한정되지 않는다.
As such a transparent film 110, a transparent conductive film such as polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polyethersulfone (PES), polycarbonate (PC), polyethylene It is preferable to use at least one selected from the group consisting of polypropylene (PE), polypropylene (PP), or a combination thereof, and more preferably an optical PET film having a visible light transmittance of 92% It does not.

상기 하드코팅층(120)은 상기 투명 필름(110)의 상부에 형성된 것으로, 상기 하드코팅 조성물로 형성된 것을 특징으로 한다. 이때, 하드코팅 조성물에 대해서는 전술한 바와 같다.The hard coating layer 120 is formed on the transparent film 110 and is formed of the hard coating composition. Here, the hard coating composition is as described above.

즉, 상기 비산 방지 필름 조성물은 무기 나노입자에 의한 네트워크 구조를 형성함으로써, 이로 형성된 하드코팅층(120)은 얇은 두께를 가지더라도, 표면 경도 및 광학적 특성이 우수하다.That is, since the anti-scattering film composition forms a network structure by inorganic nanoparticles, the hard coating layer 120 formed thereon is excellent in surface hardness and optical characteristics even though it has a small thickness.

상기 하드코팅층(120)은 상기 하드코팅 조성물을 투명 필름 상부면에 코팅하여 형성하는데, 코팅 방법으로는 스핀 코팅(spin coating)법, 스프레이 코팅(spray coating)법, 캐스트(cast)법, 바 코팅(bar coating)법, 롤투롤 코팅(roll to roll coating)법, 그라비아 코팅(gravure coating)법, 디핑(dipping)법 등을 들 수 있다. 이들 방법 중 생산성 측면에서 롤투롤 코팅 법이 가장 바람직하나, 이에 한정되지 않는다.The hard coating layer 120 is formed by coating the hard coating composition on the upper surface of the transparent film. Examples of the coating method include a spin coating method, a spray coating method, a casting method, a bar coating method, a roll to roll coating method, a gravure coating method and a dipping method. Of these methods, the roll-to-roll coating method is most preferable in terms of productivity, but is not limited thereto.

상기 하드코팅층(120)의 두께는 0.1㎛ 내지 1㎛인 것이 바람직하고, 0.1㎛ 내지 0.8㎛인 것이 보다 바람직하고, 0.1㎛ 내지 0.7㎛인 것이 보다 더 바람직하나, 이에 한정되지 않는다. 상기 하드코팅층(120)은 상기와 같이 얇은 두께를 가지더라도, 무기 나노입자에 의한 네트워크 구조로 인하여 표면 경도 및 광학적 특성을 확보할 수 있다. 이때, 상기 하드코팅층(120)의 두께가 너무 얇은 경우, 하드코팅성에 문제점이 있고, 상기 하드코팅층(120)의 두께가 너무 두꺼운 경우, 하드코팅으로 인한 비용 상승의 문제점이 있다. The thickness of the hard coating layer 120 is preferably 0.1 탆 to 1 탆, more preferably 0.1 탆 to 0.8 탆, even more preferably 0.1 탆 to 0.7 탆, but is not limited thereto. Although the hard coating layer 120 has a thin thickness as described above, the hardness and optical characteristics of the hard coating layer 120 can be secured due to the network structure of the inorganic nanoparticles. If the thickness of the hard coating layer 120 is too thin, there is a problem in hard coating property. If the thickness of the hard coating layer 120 is too thick, there is a problem of cost increase due to hard coating.

상기 하드코팅층(120)의 연필 경도는 1H 내지 9H인 것일 수 있다. 상기 하드코팅층(120)이 상기 범위의 연필 경도를 가짐으로써 우수한 내마모성을 구현할 수 있다.The hard coat layer 120 may have a pencil hardness of 1H to 9H. The hard coat layer 120 has pencil hardness in the above range, so that excellent abrasion resistance can be realized.

또한, 상기 하드코팅층(120)의 투과율은 90% 내지 100%인 것일 수 있다. 상기 하드코팅층(120)이 상기 범위의 투과율을 가짐으로써 높은 수준의 투명성을 유지하여 우수한 광학적 특성을 구현할 수 있다.
Also, the hard coat layer 120 may have a transmittance of 90% to 100%. The hard coat layer 120 has a transmittance in the above range, thereby maintaining a high level of transparency and realizing excellent optical characteristics.

상기 점착층(120)은 상기 투명 필름(110)의 하부에 형성될 수 있는 것으로, 상기 점착층(120)은 피착면인 터치 스크린 패널 등에 부착을 위하여 추가로 형성될 수 있다.The adhesive layer 120 may be formed below the transparent film 110. The adhesive layer 120 may be additionally formed for attaching to a touch screen panel or the like.

구체적으로, 상기 점착층(130)은 상기 투명 필름(110)의 하부면에 직접 코팅되어 형성되거나, 상기 점착층(130)은 상기 이형 필름(140)의 상부면에 미리 코팅된 후 투명 필름(110)의 하부면에 이형 필름(140)을 합지함으로써 형성될 수 있다.The adhesive layer 130 may be coated directly on the lower surface of the transparent film 110 or the adhesive layer 130 may be coated on the upper surface of the release film 140, 110 by bonding the release film 140 to the lower surface.

이러한 점착층(130)은 아크릴계 점착제, 실리콘계 점착제, 무산(acid-free) 타입의 히드록실(hydroxyl) 함유 점착제 등 공지의 점착제를 제한없이 이용할 수 있다. 점착층(130)은 이들 중 선택된 1종 이상을 포함할 수 있다. 예를 들어, 무산 타입의 히드록실 함유 점착제는 2-에틸헥실아크릴레이트(2-ethylhexyl acrylate), 하이드록시에틸 아크릴레이트(Hydroxyethyl acrylate) 및 벤조페논 등의 공지된 광개시제를 포함할 수 있고, 첨가제를 더 포함할 수 있다. 첨가제는 점착제의 물성 향상을 위한 것으로, 공지의 경화 촉진제, 가소제, 분산제, 계면활성제, 대전 방지제, 소포제, 레벨링제 등을 제한없이 이용할 수 있다.
The pressure-sensitive adhesive layer 130 may be any known pressure-sensitive adhesive such as an acrylic pressure-sensitive adhesive, a silicone pressure-sensitive adhesive, and an acid-free type hydroxyl-containing pressure-sensitive adhesive. The adhesive layer 130 may include at least one selected from the above. For example, a hydroxyl-containing tackifier of the acid type may comprise a known photoinitiator such as 2-ethylhexyl acrylate, hydroxyethyl acrylate and benzophenone, . The additive is for improving the physical properties of the pressure-sensitive adhesive, and known curing accelerators, plasticizers, dispersants, surfactants, antistatic agents, antifoaming agents, leveling agents and the like can be used without limitation.

상기 이형 필름(140)은 상기 점착층(130)의 하부에 형성될 수 있는 것으로, 상기 점착층(130)을 보호하기 위한 것이다.The release film 140 may be formed under the adhesive layer 130 to protect the adhesive layer 130.

이러한 이형 필름(140)으로는 폴리에틸렌테레프탈레이트(Polyethylene terephthalate; PET) 필름 등 다양한 필름을 사용할 수 있고, 이형을 쉽게 할 수 있도록 이형력이 10g/in 정도인 이형용 PET 필름을 사용하는 것이 바람직하나, 이에 한정되지 않는다.
As the release film 140, various films such as a polyethylene terephthalate (PET) film can be used, and it is preferable to use a release PET film having a releasing force of about 10 g / in. But is not limited thereto.

이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시한다. 그러나 하기의 실시예는 본 발명을 보다 쉽게 이해하기 위하여 제공되는 것일 뿐, 하기 실시예에 의해 본 발명의 내용이 한정되는 것은 아니다.
Hereinafter, preferred embodiments of the present invention will be described in order to facilitate understanding of the present invention. However, the following examples are provided only for the purpose of easier understanding of the present invention, and the present invention is not limited by the following examples.

[[ 실시예Example ]]

실시예Example 1 One

케톤계 용제로서 메틸에틸케톤(MEK) 50 중량부, 알코올계 용제로서 프로필렌글리콜모노메틸에테르(PGME) 45 중량부 및 아마이드계 용제로서 N,N-디메틸아세트아마이드 5 중량부를 포함하는 혼합 용제를 준비하였다. 준비된 혼합 용제와, 조성물 총 100 중량부에 대하여, 자외선 경화형 아크릴레이트 수지 30 중량부, 약 10nm 크기의 실리카 20 중량부 및 벤조페논 10 중량부를 포함하여, 네트워크 구조를 형성하는 하드코팅 조성물을 제조하였다. 제조된 하드코팅 조성물을 롤투롤 코팅을 통해 PET 투명 필름 상부에 도포한 후, 건조 및 UV 경화하여 약 537.7~646.1nm 두께의 하드코팅층을 제조함으로써 비산 방지 필름을 제조하였다(도 1(a) 참조).
50 parts by weight of methyl ethyl ketone (MEK) as a ketone solvent, 45 parts by weight of propylene glycol monomethyl ether (PGME) as an alcohol solvent, and 5 parts by weight of N, N-dimethylacetamide as an amide solvent were prepared Respectively. A hard coating composition was prepared which comprised a prepared mixed solvent and 30 parts by weight of an ultraviolet curable acrylate resin, 20 parts by weight of silica having a size of about 10 nm and 10 parts by weight of benzophenone, based on 100 parts by weight of the total composition . The prepared hard coating composition was applied on top of a PET transparent film through a roll-to-roll coating, followed by drying and UV curing to produce a hard coat layer having a thickness of about 537.7 to 646.1 nm (see Fig. 1 (a) ).

비교예Comparative Example 1 One

혼합 용제 대신 케톤계 용제로서 메틸이소부틸케톤(MIBK)을 단독으로 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 하드코팅 조성물 및 약 1.5㎛ 두께의 하드코팅층을 포함하는 비산 방지 필름을 제조하였다(도 1(b) 참조).
A light-scattering film comprising a hard coating composition and a hard coating layer having a thickness of about 1.5 탆 was prepared in the same manner as in Example 1 except that methyl isobutyl ketone (MIBK) was used alone as a ketone solvent instead of the mixed solvent 1 (b)).

비교예Comparative Example 2 2

혼합 용제 대신 케톤계 용제로서 메틸이소부틸케톤(MIBK)을 단독으로 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 하드코팅 조성물 및 약 500nm 두께의 하드코팅층을 포함하는 비산 방지 필름을 제조하였다.
A light-scattering film comprising a hard coating composition and a hard coating layer having a thickness of about 500 nm was prepared in the same manner as in Example 1, except that methyl isobutyl ketone (MIBK) was used alone as a ketone solvent instead of the mixed solvent.

실험예Experimental Example : 물성 평가: Property evaluation

실시예 1 및 비교예 1~2에 따라 제조된 비산 방지 필름의 연필 경도 및 가시광선 투과율 광학적 특성 및 측정 결과는 하기 표 1에 나타내었다. The pencil hardness and visible light transmittance of the anti-scattering film prepared according to Example 1 and Comparative Examples 1 and 2 are shown in Table 1 below.

연필 경도는 JIS K5600-5-4에 의거하여 750g의 추를 사용하여 측정하였고, 가시광선 투과율은 JIS K7361-1에 의거하여 분광광도계(Konica Minolta社, CM-5)를 사용하여 측정하였다.The pencil hardness was measured using a weight of 750 g according to JIS K5600-5-4, and the visible light transmittance was measured using a spectrophotometer (Konica Minolta, CM-5) according to JIS K7361-1.

구 분division 연필 경도Pencil hardness 가시광선
투과율(%)Visible ray
Transmittance (%) 실시예 1Example 1 HH 9292 비교예 1Comparative Example 1 HH 9292 비교예 2Comparative Example 2 FF 9292

상기 표 1에서 보듯이, 실시예 1에 따른 하드코팅 조성물은 혼합 용제로 인하여 무기 나노입자에 의한 네트워크 구조를 형성함으로써, 이로 형성된 하드코팅층은 비교예 1에 비해 현저히 얇은 두께를 가지더라도, 연필 경도가 동등한 수준을 유지하면서도 가시광선 투과율이 우수함을 확인할 수 있었다. 한편, 비교예 2의 경우 연필 경도가 저하되어 비산 방지 필름으로서 적합하지 못함을 확인할 수 있었다.
As shown in Table 1, the hard coating composition according to Example 1 forms a network structure with inorganic nanoparticles due to a mixed solvent, so that the hard coating layer formed therefrom has a significantly thinner thickness than Comparative Example 1, And the visible light transmittance was excellent. On the other hand, in Comparative Example 2, it was confirmed that the pencil hardness was lowered and thus it was not suitable as a shatterproof film.

전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.
It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.

Claims (13)

자외선 경화형 아크릴레이트 수지; 무기 나노입자; 광개시제; 및 혼합 용제를 포함하고,
상기 혼합 용제는 케톤계 용제 50 중량% 이상 80 중량% 이하, 알코올계 용제 15 중량% 이상 45 중량% 이하 및 아마이드계 용제 5 중량% 이상 10 중량% 이하로 이루어지고, 극성도가 3 내지 5인 것을 특징으로 하는
하드코팅 조성물.
Ultraviolet curable acrylate resin; Inorganic nanoparticles; Photoinitiators; And a mixed solvent,
Wherein the mixed solvent comprises 50% by weight or more and 80% by weight or less of the ketone solvent, 15% by weight or more and 45% by weight or less of the alcoholic solvent and 5% Characterized by
Hard coating composition.
삭제delete 제1항에 있어서,
상기 혼합 용제는 탄화수소계 용제, 에스테르계 용제, 에테르계 용제 및 글리콜계 용제로 이루어진 군으로부터 선택된 하나 이상의 기타 용제를 더 포함하는 것을 특징으로 하는
하드코팅 조성물.
The method according to claim 1,
Wherein the mixed solvent further comprises at least one other solvent selected from the group consisting of a hydrocarbon-based solvent, an ester-based solvent, an ether-based solvent and a glycol-based solvent
Hard coating composition.
삭제delete 제1항에 있어서,
상기 무기 나노입자의, 50% 누적질량 입자크기 분포 직경을 D50이라 할 때, 5nm<D50<20nm인
하드코팅 조성물.
The method according to claim 1,
When the 50% cumulative mass particle size distribution diameter of the inorganic nanoparticles is D50, it is preferable that 5nm < D50 < 20nm
Hard coating composition.
제1항에 있어서,
상기 조성물 총 100 중량부에 대하여, 자외선 경화형 아크릴레이트 수지 1~70 중량부; 무기 나노입자 1~30 중량부; 광개시제 1~15 중량부인
하드코팅 조성물.
The method according to claim 1,
1 to 70 parts by weight of an ultraviolet curing type acrylate resin, based on 100 parts by weight of the total composition; 1 to 30 parts by weight of inorganic nanoparticles; 1 to 15 wt% of photoinitiator
Hard coating composition.
제1항에 있어서,
상기 조성물은 무기 나노입자에 의한 네트워크 구조를 형성하는
하드코팅 조성물.
The method according to claim 1,
The composition can be used to form a network structure by inorganic nanoparticles
Hard coating composition.
투명 필름; 및
상기 투명 필름의 상부에 형성된 하드코팅층을 포함하고,
상기 하드코팅층은 제1항, 제3항 및 제5항 내지 제7항 중 어느 한 항에 따른 하드코팅 조성물로 형성된 것인
비산 방지 필름.
Transparent film; And
And a hard coating layer formed on the transparent film,
Wherein the hard coat layer is formed from the hard coat composition according to any one of claims 1, 3 and 5 to 7,
Shatterproof film.
제8항에 있어서,
상기 하드코팅층의 두께는 0.1㎛ 내지 1㎛인
비산 방지 필름.
9. The method of claim 8,
The thickness of the hard coat layer is preferably from 0.1 mu m to 1 mu m
Shatterproof film.
제8항에 있어서,
상기 하드코팅층의 연필 경도는 1H 내지 9H인
비산 방지 필름.
9. The method of claim 8,
The pencil hardness of the hard coat layer is from 1H to 9H
Shatterproof film.
제8항에 있어서,
상기 하드코팅층의 투과율은 90% 내지 100%인
비산 방지 필름.
9. The method of claim 8,
The hard coat layer has a transmittance of 90% to 100%
Shatterproof film.
제8항에 있어서,
상기 투명 필름의 하부에 형성된 점착층을 더 포함하는
비산 방지 필름.
9. The method of claim 8,
And a pressure-sensitive adhesive layer formed on a lower portion of the transparent film
Shatterproof film.
제12항에 있어서,
상기 점착층의 하부에 형성된 이형 필름을 더 포함하는
비산 방지 필름.
13. The method of claim 12,
And a release film formed on a lower portion of the adhesive layer
Shatterproof film.
KR1020140111460A 2014-08-26 2014-08-26 Hard coating composition and scattering protecting film using the same KR101965896B1 (en)