KR101941445B1 - Position guiding apparatus for needle for ultrasonic operation - Google Patents

Position guiding apparatus for needle for ultrasonic operation Download PDF

Info

Publication number
KR101941445B1
KR101941445B1 KR1020110143791A KR20110143791A KR101941445B1 KR 101941445 B1 KR101941445 B1 KR 101941445B1 KR 1020110143791 A KR1020110143791 A KR 1020110143791A KR 20110143791 A KR20110143791 A KR 20110143791A KR 101941445 B1 KR101941445 B1 KR 101941445B1
Authority
KR
South Korea
Prior art keywords
silica
cover substrate
refractive index
hardness
air
Prior art date
Application number
KR1020110143791A
Other languages
Korean (ko)
Other versions
KR20130075428A (en
Inventor
김성희
채기성
김진욱
Original Assignee
엘지디스플레이 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지디스플레이 주식회사 filed Critical 엘지디스플레이 주식회사
Priority to KR1020110143791A priority Critical patent/KR101941445B1/en
Publication of KR20130075428A publication Critical patent/KR20130075428A/en
Application granted granted Critical
Publication of KR101941445B1 publication Critical patent/KR101941445B1/en

Abstract

본 발명은 저반사 고경도 코팅막 및 이를 이용한 표시 장치에 관한 것으로, 본 발명의 저반사 고경도 코팅막은 고경도를 위해 폴리실록산과 실리카 혼성으로 네트워크를 구성하며 다수의 미세기공을 포함하는 다공성 실리카 나노층 구조를 포함하고; 상기 다공성 실리카 나노층은 실리카 및 에어 부피비 조절을 통해 1.3 이하의 저굴절율을 갖는다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a low reflection hardness coating film and a display device using the same. The low reflection hardness coating film of the present invention comprises a porous silica nano-layer comprising a polysiloxane- Structure; The porous silica nano-layer has a low refractive index of 1.3 or less through adjustment of silica and air volume ratio.

Description

초음파 시술용 바늘의 위치 가이드 장치{Position guiding apparatus for needle for ultrasonic operation}[0001] The present invention relates to a position guiding apparatus for ultrasonic operation,

본 발명은 표시 장치용 커버 기판에 적용하기 위한 코팅막에 관한 것으로, 특히 커버 기판으로 적합한 고경도 특성을 유지하면서도 저반사 특징으로 야외 시인성을 향상시킬 수 있는 저반사 고경도 코팅막 및 이를 이용한 표시 장치에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coating film for use in a cover substrate for a display device, and more particularly, to a low reflection hardness coating film capable of improving outdoor visibility with a low reflection characteristic while maintaining a high hardness characteristic suitable as a cover substrate, .

최근 널리 사용되고 있는 모바일(Mobile) 전자기기는 영상을 표시하는 표시 장치를 포함한다. 모바일용 표시 장치로는 액정 표시 장치(Liquid Crystal Display; LCD)와 유기 발광 다이오드(Organic Light Emitting Diode; OLED) 표시 장치가 주로 이용된다. 액정 표시 장치는 굴절율 및 유전율 등의 이방성을 갖는 액정의 전기적 및 광학적 특성을 이용하여 화상을 표시하는 것으로, 각 화소가 데이터 신호에 따른 액정 배열 방향의 가변으로 편광판을 투과하는 광 투과율을 조절함으로써 계조를 구현한다. 유기 발광 다이오드 표시 장치는 전자와 정공의 재결합으로 유기 발광층을 발광시키는 자발광 소자로, 각 화소의 구동 회로가 데이터 신호에 따라 유기 발광 다이오드로 공급되는 전류를 조절함으로써 계조를 구현한다.Recently, mobile electronic devices widely used include a display device for displaying an image. As a mobile display device, a liquid crystal display (LCD) and an organic light emitting diode (OLED) display device are mainly used. The liquid crystal display device displays an image by using electrical and optical characteristics of liquid crystal having anisotropy such as refractive index and permittivity. By adjusting the light transmittance of each pixel through the polarizing plate in accordance with the data signal, . The organic light emitting diode display device is a self-light emitting device that emits an organic light emitting layer by recombination of electrons and holes. The driving circuit of each pixel implements a gray level by controlling a current supplied to the organic light emitting diode according to a data signal.

모바일 기기는 사용 환경상 실내에서 뿐만 아니라 야외에서도 충분한 시인성을 가져야 한다. 최근 모바일 기기에는 윈도우 글라스(Window Glass) 및 터치 스크린 패널의 적용이 일반화됨에 따라 야외 시인성 저하가 문제가 되고 있다. Mobile devices should have sufficient visibility both indoors and outdoors in their use environment. In recent years, application of window glass and touch screen panel has become common in mobile devices, so that outdoor visibility has become a problem.

터치 스크린 패널 상에 커버 기판으로 부착되는 윈도우 글라스로는 내구성이 강한 강화 유리를 주로 사용하고, 시인성 향상을 위하여 SVR(Super Viewing Resin)을 접착제로 이용하여 터치 스크린 패널 상에 커버 기판을 부착하고 있다. 그러나, SVR은 커버 기판의 내부나, 터치 스크린 패널 또는 액정 표시 장치의 내부에서 발생되는 반사를 감소시킬 수는 있으나, 커버 기판의 표면에서 발생하는 외부광 난반사를 방지할 수 없어서 시인성을 향상시키는데 한계가 있다. A durable tempered glass is mainly used as a window glass attached to a cover substrate on a touch screen panel and a cover substrate is attached on a touch screen panel using SVR (Super Viewing Resin) as an adhesive in order to improve visibility . However, although SVR can reduce the reflection generated in the interior of the cover substrate, the touch screen panel, or the liquid crystal display device, the SVR can not prevent the diffused external light generated on the surface of the cover substrate, .

본 발명은 종래의 문제점을 해결하기 위하여 안출된 것으로, 본 발명이 해결하고자 하는 과제는 저반사 특징으로 야외 시인성을 향상시킴과 아울러 고경도를 유지할 수 있는 저반사 고경도 코팅막 및 이를 이용한 표시 장치를 제공하는 것이다.DISCLOSURE Technical Problem The present invention has been made to solve the conventional problems, and it is an object of the present invention to provide a low reflection hardness coating film capable of improving outdoor visibility and maintaining high hardness, .

상기 과제를 해결하기 위하여, 본 발명의 실시예에 따른 저반사 고경도 코팅막은 고경도를 위해 폴리실록산과 실리카 혼성으로 네트워크를 구성하며 다수의 미세기공을 포함하는 다공성 실리카 나노층 구조를 포함하고; 상기 다공성 실리카 나노층은 실리카 및 에어 부피비 조절을 통해 1.3 이하의 저굴절율을 갖는다.In order to solve the above problems, a low reflection hardness coating film according to an embodiment of the present invention includes a porous silica nanorayer structure including a polysiloxane-silica hybrid network and a plurality of micropores for high hardness; The porous silica nano-layer has a low refractive index of 1.3 or less through adjustment of silica and air volume ratio.

상기 다공성 실리카 나노층에서 에어 분압 조절을 통해 상기 실리카의 부피비는 0.55~0.8의 범위를 포함하고, 상기 에어의 부피비는 0.2~0.45 범위를 포함한다.The volume ratio of the silica through controlling the partial pressure of air in the porous silica nano-layer includes the range of 0.55 to 0.8, and the volume ratio of the air includes the range of 0.2 to 0.45.

본 발명의 저반사 고경도 코팅막은 150℃ 이하의 저온 소성 특성을 갖는 알코올계 용매를 추가로 포함한다.The low reflection hard coat film of the present invention further comprises an alcoholic solvent having a low temperature baking property of 150 DEG C or less.

본 발명의 실시예에 따른 표시 장치는 터치 센서가 일체화된 표시 모듈과; 상기 표시 모듈 상에 부착되고, 상기 저반사 고경도 코팅막이 코팅된 커버 기판을 구비한다.A display device according to an embodiment of the present invention includes: a display module in which a touch sensor is integrated; And a cover substrate attached to the display module and coated with the low reflection hardness coating film.

본 발명에 따른 고경도 저반사 코팅막은 에어 분압 조절을 통해 나노층 구조가 제어된 다공성 실리카 나노층을 포함함으로써 고경도와 높은 투과율 및 저굴절 특성을 확보할 수 있다. The high hardness low reflection coating film according to the present invention can secure high hardness, high transmittance and low refractive index by including a porous silica nano-layer having a nano layer structure controlled by controlling the partial pressure of air.

따라서, 본 발명에 따른 고경도 저반사 코팅막을 이용한 표시 장치는 커버 기판의 표면에 다공성 실리카막을 포함하는 고경도 저반사 코팅막을 코팅함으로써 커버 기판 표면에서의 외부광 반사를 감소시켜 외부 시인성을 향상시킬 수 있음과 아울러 고경도를 유지할 수 있다.Therefore, in the display device using the high-hardness low reflection coating film according to the present invention, the high-hardness low reflection coating film including the porous silica film is coated on the surface of the cover substrate to reduce external light reflection on the cover substrate surface, And the hardness can be maintained.

도 1a 및 도 1b는 일반적인 실리카 나노 입자를 포함하는 모노층의 SEM 및 TEM 사진이다.
도 2a 내지도 2c는 본 발명에 따른 다공성 실리카 나노층의 SEM 및 TEM 사진이다.
도 3은 본 발명에 따른 저반사 고경도 코팅막의 파장에 대한 광반사율을 나타낸 그래프이다.
도 4는 본 발명의 실시예에 따른 저반사 고경도 코팅막이 적용된 터치 패널 일체형 표시 장치를 나타낸 단면도이다.FIGS. 1A and 1B are SEM and TEM photographs of a monolayer comprising common silica nanoparticles. FIG.
2A to 2C are SEM and TEM photographs of the porous silica nano-layer according to the present invention.
3 is a graph showing the light reflectance with respect to the wavelength of the low reflection hard coat film according to the present invention.
4 is a cross-sectional view illustrating a touch panel integrated type display device to which a low reflection hardness coating film according to an embodiment of the present invention is applied.

본 발명에서는 야외 시인성 향상을 위하여 커버 기판의 표면에 저반사(저굴절) 고경도 코팅막을 코팅함으로써 경도를 확보하면서도 커버 기판 표면에서의 외부광 반사를 감소시켜서 휘도 및 컨트라스트비를 향상시키고자 한다. In the present invention, it is desired to improve the outdoor visibility by coating a low reflection (low refractive index) hard coating film on the surface of the cover substrate to improve the brightness and contrast ratio by reducing external light reflection on the cover substrate surface while securing the hardness.

본 발명에 따른 저반사 고경도 코팅막은 굴절율이 낮고 경도가 높은 유리 계열의 실리카(SiO2)를 포함하는 바인더, 계면 활성제, 저온 소성 용매 및 기타 첨가제를 포함하며, 나노 세라믹 하이브리드 타입의 고투과 특성을 갖는다. The low reflection hardness coating film according to the present invention includes a binder including silica (SiO 2 ) having a low refractive index and high hardness, a surfactant, a low-temperature firing solvent, and other additives, and exhibits high transparency characteristics of a nanoceramic hybrid type .

예를 들면, 본 발명에 따른 저반사 고경도 코팅막은 고강도를 위해 폴리실록산과 실리카가 혼합되어 네트워크를 구성한 실록산 화합물을 포함한다. 특히, 본 발명에 따른 저반사 고경도 코팅막은 네트워크를 구성한 실리카막의 나노 구조 제어를 통해 높은 투과율과, 1.3 이하의 낮은 굴절율을 갖으면서도 연필경도 9H 이상의 높은 경도를 확보할 수 있다. 용매로는 커버 기판이 터치 패널 상에 부착되는 부가형(add-on type) 및 커버 기판이 터치 패널의 상부 기판으로 이용되는 변형 부가형(modified add-on type)에 모두 적용이 가능하도록 150℃ 정도의 저온 소성 특성을 갖는 알코올계 용매가 이용된다.For example, the low reflection hardness coating film according to the present invention includes a siloxane compound in which a polysiloxane and silica are mixed to constitute a network for high strength. Particularly, the low reflection hardness coating film according to the present invention has a high transmittance and a low refractive index of 1.3 or less through the control of the nanostructure of the silica film constituting the network, and can secure a high hardness of 9H or higher pencil hardness. As the solvent, it is preferable to use an add-on type in which a cover substrate is attached on a touch panel and a substrate in which the cover substrate is applied to a modified add-on type in which the cover substrate is used as an upper substrate of the touch panel. An alcohol-based solvent having low-temperature firing characteristics is used.

고강도 특성을 갖는 실리카의 굴절율은 통상 1.45이지만, 아래의 수학식 1과 같이 실리카와, 에어의 부피비 제어를 통해 실리카 나노층 구조를 제어하여 다공성(porous) 실리카막을 형성함으로써 실리카의 고경도 특성을 유지하면서도 1.3 보다 낮은 굴절율과 높은 투과율을 확보할 수 있다. The refractive index of silica having high strength characteristics is usually 1.45, but the silica nanowire structure is controlled by controlling the volume ratio of silica and air as shown in the following formula (1) to form a porous silica film, But a refractive index lower than 1.3 and a high transmittance can be secured.

Figure 112011104085532-pat00001
Figure 112011104085532-pat00001

상기 수학식 1에서 nSiO2는 실리카의 굴절율을, nair은 에어의 굴절율을, f는 실리카의 부피비를, (1-f)는 에어의 부피비를, neff는 저반사 고경도 코팅막의 굴절율을 나타낸다. 다공성 실리카막이 1.3 보다 낮은 굴절율을 갖기 위하여, 실리카의 부피비(f)는 0.55~0.8의 범위를 갖고, 에어의 부피비(1-f)는 0.2~0.45 범위의 부피비를 갖는 것이 바람직하다. 실리카의 부피비(f)가 0.55 보다 작으면 다공성 실리카막의 경도가 낮고, 0.8 보다 크면 다공성 실리카막의 굴절율이 증가한다.(1-f) is the volume fraction of air, and n eff is the refractive index of the low reflection hardness coating film. In the formula (1), n SiO2 represents the refractive index of silica, n air represents the refractive index of air, f represents the volume ratio of silica, . In order for the porous silica film to have a refractive index lower than 1.3, it is preferable that the volume ratio f of the silica is in the range of 0.55 to 0.8 and the volume ratio (1-f) of the air has the volume ratio in the range of 0.2 to 0.45. When the volume ratio (f) of silica is less than 0.55, the hardness of the porous silica film is low, and when it is more than 0.8, the refractive index of the porous silica film is increased.

도 1a 및 도 1b는 일반적인 구형 실리카 나노 입자 모노층의 주사전자 현미경(Scanning Electron Microscopy; SEM) 및 투사전자 현미경(Transmission Electron Microscopy; TEM)사진이고, 도 2a 내지 도 2c는 본 발명의 실시예에 따른 다공성 실리카 나노층 구조를 포함하는 고경도 저반사 코팅막의 SEM 및 TEM 사진이다. 1A and 1B are a scanning electron microscope (SEM) and a transmission electron microscopy (TEM) photographs of a general spherical silica nanoparticle monolayer, and FIGS. 2A to 2C are cross- SEM and TEM photographs of a high-hardness low reflection coating film including a porous silica nanorayer structure according to the present invention.

도 1a 및 도 1b에 도시된 바와 같이 일반적인 구형 실리카 나노 입자는 미세기공을 포함하는 균일한 구형 구조를 갖고 있음에 따라 굴절율이 1.5 이상으로 높은 반면에, 도 2a 내지 도 2c에 도시된 바와 같이 본 발명의 실시예에 따른 다공성 실리카 나노층은 기존과 같은 균일한 구형을 갖지 않으면서 다수의 미세기공이 존재함을 알 수 있다. 다수의 미세기공은 다공성 실리카 나노층 형성시 에어 분압을 조절함으로써 형성할 수 있고, 에어 분압 조절을 통해 미세기공의 부피비를 조절함으로써 굴절율을 감소시킬 수 있다. 도 2a는 200mTorr의 에어 분압을 이용한 경우이고, 도 2b는 250mTorr의 에어 분압을 이용한 경우로 에어 분압이 증가하면 미세기공, 즉 에어의 부피비가 증가함을 알 수 있다. 에어 분압은 전술한 바와 같이 실리카의 부피비(f)는 0.55~0.8의 범위를 갖고, 에어의 부피비(1-f)는 0.2~0.45 범위의 부피비를 갖도록 조절하는 것이 바람직하다. As shown in FIG. 1A and FIG. 1B, since the general spherical silica nanoparticles have a uniform spherical structure including micropores, the refractive index is as high as 1.5 or more. On the other hand, as shown in FIGS. 2A to 2C, It can be seen that the porous silica nano-layer according to the embodiment of the present invention has a plurality of fine pores without having a uniform spherical shape. A plurality of micropores can be formed by controlling the partial pressure of air when the porous silica nanolayers are formed, and the refractive index can be reduced by controlling the volume ratio of micropores through controlling the partial pressure of air. FIG. 2A shows a case where air partial pressure of 200 mTorr is used, and FIG. 2B shows a case where air partial pressure of 250 mTorr is used. As the air partial pressure increases, the volume ratio of fine pores, that is, air, increases. As described above, the partial pressure of air is preferably adjusted so that the volume ratio f of silica is in the range of 0.55 to 0.8 and the volume ratio of air 1-f is in the range of 0.2 to 0.45.

본 발명의 실시예에 따른 다공성 실리카 나노층을 제조하는 방법을 예를 들면 다음과 같다. A method for producing the porous silica nanorods according to an embodiment of the present invention will be described below.

먼저, TEOS(tetraethylorthosilicate; Si(OC2H5)4, C2H5OH, H2O를 최적의 몰비로 혼합하고 NH4OH를 첨가한 후 졸 용액(sol solution)을 제조한다. 그 다음, 제조된 졸 용액을 에어 분압을 조절하면서 기판 상에 형성함으로써 도 2a 내지 도 2c에 도시된 바와 같이 다공성 실리카 나노층을 형성할 수 있다. First, TEOS (tetraethylorthosilicate; Si (OC 2 H 5 ) 4 , C 2 H 5 OH, and H 2 O are mixed at an optimal molar ratio and NH 4 OH is added to prepare a sol solution. The prepared sol solution can be formed on a substrate while controlling the partial pressure of air to form a porous silica nano-layer as shown in Figs. 2A to 2C.

이와 같이, 본 발명에 따른 고경도 저반사 코팅막은 에어 분압 조절을 통해 에어 부피비가 조절된 다공성 실리카 나노층을 포함함으로써 1.3 이하의 저굴절율을 확보할 수 있음과 아울러 9PH 이상의 고경도를 확보할 수 있다. 또한, 본 발명의 고경도 저반사 코팅막은 나노 세라믹 하이브리드 타입의 고투과 특성을 갖는다. 본 발명에 따른 고경도 저반사 코팅막은 커버 기판의 표면에 코팅하여 이용한다.As described above, the high-hardness low reflection coating film according to the present invention can secure a low refractive index of 1.3 or lower and a high hardness of 9 PH or higher by including the porous silica nano- have. Further, the high hardness low reflection coating film of the present invention has a high transparency characteristic of a nanoceramic hybrid type. The low hardness low reflection coating film according to the present invention is coated on the surface of the cover substrate.

도 3을 참조하면, 본 발명에 따른 저반사 고경도 코팅막이 코팅된 기판(PET 필름)의 반사율이 저반사 고경도 코팅막이 코팅되지 않은 베어 기판(PET 필름) 보다 광반사율이 5% 미만으로 현저하게 낮음을 알 수 있다. 이에 따라, 고경도 코팅막을 표시 장치의 커버 기판에 적용한 경우 커버 기판의 고경도를 확보하면서도 커버 기판의 표면에서의 외부광 반사를 감소시킴으로써 시인성을 향상시킬 수 있다.Referring to FIG. 3, the reflectance of the substrate coated with the low reflection hard coat film according to the present invention (PET film) is lower than that of the bare substrate (PET film) not coated with the low reflection hard coat film, As shown in Fig. Accordingly, when the high hardness coating film is applied to the cover substrate of the display device, the visibility can be improved by reducing the external light reflection on the surface of the cover substrate, while securing the high hardness of the cover substrate.

도 4는 본 발명의 실시예에 따른 고경도 저반사 코팅제를 이용한 터치 패널 일체형 표시 장치를 나타낸 단면도이다.4 is a cross-sectional view of a touch panel integrated type display device using a high hardness low reflection coating agent according to an embodiment of the present invention.

도 4에 도시된 터치 패널 일체형 표시 장치는 표시 패널(10)과, 표시 패널(10) 상에 제1 점착층(20)에 의해 부착된 터치 패널(30)과, 터치 패널(30) 상에 제2 점착층(30)에 의해 부착된 커버 기판(50)을 구비한다.4 includes a display panel 10, a touch panel 30 attached on the display panel 10 by a first adhesive layer 20, and a touch panel 30 on the touch panel 30, And a cover substrate (50) attached by a second adhesive layer (30).

표시 패널(10)로는 액정 패널, 유기 발광 다이오드 표시 패널, 플라즈마 디스플레이 패널 등과 같은 평판 표시 패널이 이용된다. 예를 들어, 표시 패널(10)로 액정 패널을 이용하는 경우, 표시 패널(10)은 박막 트랜지스터 및 화소 전극을 포함하는 박막 트랜지스터 어레이가 형성된 하부 기판과, 블랙 매트릭스 및 컬러 필터를 포함하는 컬러 필터 어레이가 형성된 상부 기판과, 상하부 기판 사이에 형성된 액정층과, 상하부 기판의 외측면에 각각 부착된 상하부 편광판과, 하부 편광판 아래에 위치하는 백라이트 유닛을 구비한다. 공통 전극은 하부 기판 또는 상부 기판에 형성된다. 액정층은 TN(Twisted Nematic) 모드 또는 VA(Vertical Alignment) 모드와 같이 수직 전계에 의해 구동되거나, IPS(In-Plane Switching) 모드 또는 FFS(Fringe Field Switching) 모드와 같이 수평 전계에 의해 구동된다. As the display panel 10, a flat panel display panel such as a liquid crystal panel, an organic light emitting diode display panel, or a plasma display panel is used. For example, when a liquid crystal panel is used as the display panel 10, the display panel 10 includes a lower substrate on which a thin film transistor array including thin film transistors and pixel electrodes is formed, a color filter array including a black matrix and a color filter A liquid crystal layer formed between the upper and lower substrates, an upper and lower polarizer plates respectively attached to outer surfaces of the upper and lower substrates, and a backlight unit positioned below the lower polarizer. The common electrode is formed on the lower substrate or the upper substrate. The liquid crystal layer is driven by a vertical electric field such as a TN (Twisted Nematic) mode or VA (Vertical Alignment) mode, or by a horizontal electric field such as an IPS (In-Plane Switching) mode or an FFS (Fringe Field Switching) mode.

터치 패널(30)로는 포토 터치 센서, 저항막 방식 터치 센서, 또는 커패시티브 터치 센서를 이용할 수 있다. 포토 터치 센서는 포토 트랜지스터를 이용하여 광세기에 따라 터치를 인식한다. 커패시티브 터치 센서는 커패시티브 가변에 따라 터치를 인식한다. 저항막 터치 센서는 터치압에 의해 상하부 저항막이 컨택하여 발생되는 전압 변화에 따라 터치를 인식한다. As the touch panel 30, a photo touch sensor, a resistive touch sensor, or a capacitive touch sensor can be used. The photo touch sensor recognizes the touch according to the light intensity by using the phototransistor. The capacitive touch sensor recognizes the touch according to the capacitive variable. The resistive film touch sensor recognizes the touch according to the voltage change generated by the contact of the upper and lower resistive films by the touch pressure.

커버 기판(50)으로는 강화 유리나 투명 고분자 플라스틱이 이용된다. 또한, 커버 기판(50)의 표면에는 전술한 고경도 저반사 코팅막(52)이 코팅된다. 고경도 저반사 코팅막(52)은 고강도를 위해 폴리실록산과 네크워크를 구성한 실리카 나노층을 포함하고, 에어 분압 조절을 통해 실리카 나노층이 다수의 미세기공을 포함하는 다공성 실리카 나노층 구조를 갖음으로써 1.3 이하의 낮은 굴절율과 9H 이상의 높은 경도를 확보할 수 있다. 또한, 용매로는 커버 기판이 터치 패널 상에 부착되는 부가형(add-on type) 및 커버 기판이 터치 패널의 상부 기판으로 이용되는 변형 부가형(modified add-on type)에 모두 적용이 가능하도록 150℃ 정도의 저온 소성 특성을 갖는 알코올계 용매가 이용된다. 고경도 저반사 코팅막(52)은 나노 세라믹 하이브리드 타입의 고투과 특성을 갖는다. As the cover substrate 50, reinforced glass or transparent polymer plastic is used. Further, the surface of the cover substrate 50 is coated with the above-mentioned high-hardness low reflection coating film 52. The high hardness low reflection coating layer 52 includes a silica nanocrystal layer constituting a network with a polysiloxane for high strength and has a porous silica nanocrystal structure in which a silica nanocrystal layer includes a large number of micropores through control of air partial pressure, And a high hardness of 9H or more can be ensured. The solvent may be added to the add-on type in which the cover substrate is attached to the touch panel and the add-on type in which the cover substrate is used in the modified add-on type in which the cover substrate is used as the upper substrate of the touch panel. Alcoholic solvent having low-temperature baking property is used. The high hardness low reflection coating film 52 has a high transparency characteristic of a nanoceramic hybrid type.

터치 패널(30)은 표시 패널(10)의 전면에 도포된 제1 접착층(20)에 의해 표시 패널(10) 상에 부착된다. 커버 기판(50)은 터치 패널(30)의 전면에 도포된 제2 접착층(40)에 의해 터치 패널(30) 상에 부착된다. 제1 및 제2 접착층(20)으로는 광학 탄성 수지, 예를 들면 아크릴계 자외선 경화형 수지인 SVR(Super Viewing Resin)이 이용된다. SVR은 시인성을 향상시키고 내충격성을 갖는다. The touch panel 30 is attached on the display panel 10 by the first adhesive layer 20 applied to the front surface of the display panel 10. [ The cover substrate 50 is attached on the touch panel 30 by the second adhesive layer 40 applied to the front surface of the touch panel 30. [ As the first and second adhesive layers 20, SVR (Super Viewing Resin), which is an optical elastic resin such as acrylic ultraviolet curable resin, is used. SVR improves visibility and has impact resistance.

이와 같이, 본 발명은 커버 기판(50)에 에어 분압을 통해 에어 부피비가 조절된 다공성 실리카 나노층을 포함하는 고경도 저반사 코팅막(52)을 코팅함으로써 외부광 반사를 방지하여 야외 시인성을 향상시킬 수 있음과 아울러 고경도 및 고투과율을 확보할 수 있다.As described above, according to the present invention, the high-hardness low reflection coating film 52 including the porous silica nano-layer having the air volume ratio adjusted through the air partial pressure is coated on the cover substrate 50 to improve the outdoor visibility And high hardness and high transmittance can be ensured.

10: 표시 패널 20: 제1 접착층
30: 터치 패널 40: 제2 접착층
50: 커버 기판 52: 저반사 고경도 코팅막10: display panel 20: first adhesive layer
30: touch panel 40: second adhesive layer
50: cover substrate 52: low reflection hardness coating film

Claims (7)

삭제delete 삭제delete 삭제delete 표시 패널; 상기 표시 패널의 전면에 도포된 제1 접착층에 의해 상기 표시 패널에 부착되는 터치 패널; 및 상기 터치 패널 상에 커버 기판을 부착하기 위해 상기 터치 패널의 전면에 도포된 제2 접착층을 포함하여 터치 센서가 일체화된 표시 모듈과;
고경도를 위해 폴리실록산과 실리카 혼성으로 네트워크를 구성하며 다수의 미세기공을 포함하는 다공성 실리카 나노층 구조를 포함하고; 하기의 수식과 같이 상기 다공성 실리카 나노층에서 상기 실리카의 부피비는 0.55~0.8의 범위를 포함하고, 에어의 부피비는 0.2~0.45 범위를 포함하도록 실리카와 에어의 부피를 제어하며,
Figure 112019501011147-pat00010
상기 수식에서 neff는 저반사 고경도 코팅막의 굴절율을, nSiO2는 실리카의 굴절율을, f는 실리카의 부피비를, nair은 에어의 굴절율을, (1-f)는 에어의 부피비를 나타냄에 따라, 상기 다공성 실리카 나노층은 연필강도 9H 이상의 경도와 1.3 이하의 저굴절율을 갖도록 구성되는 저반사 고경도 코팅막이 코팅되어 상기 표시 모듈 상에 부착되는 커버 기판을 구비하는 것을 특징으로 하는 표시 장치.Display panel; A touch panel attached to the display panel by a first adhesive layer applied to the front surface of the display panel; And a second adhesive layer applied to the front surface of the touch panel for attaching the cover substrate on the touch panel.
Comprising a porous silica nanorayer structure comprising a network of polysiloxane and silica hybrid for high hardness and comprising a plurality of micropores; Wherein the volume ratio of the silica in the porous silica nanocrystal layer is in the range of 0.55 to 0.8 and the volume ratio of air is in the range of 0.2 to 0.45,
Figure 112019501011147-pat00010
In the above formula, n eff represents the refractive index of the low reflection hard coat film, n SiO2 represents the refractive index of silica, f represents the volume ratio of silica, n air represents the refractive index of air, and (1-f) represents the volume ratio of air Wherein the porous silica nano-layer comprises a cover substrate coated with a low-reflection hard coat layer having a hardness of not less than 9H and a low refractive index of not more than 1.3, and is attached to the display module. 삭제delete 제4항에 있어서,
상기 커버 기판이 상기 터치 패널 상에 부착되는 부가형(add-on type) 또는 상기 커버 기판이 상기 터치 패널의 상부 기판으로 이용되는 변형 부가형 (modified add-on type) 중 어느 하나의 타입인 것을 특징으로 하는 표시 장치.5. The method of claim 4,
Wherein the cover substrate is an add-on type in which the cover substrate is attached to the touch panel or a modified add-on type in which the cover substrate is used as an upper substrate of the touch panel. / RTI > 제4항에 있어서,
상기 저반사 고경도 코팅막은 나노 세라믹 하이브리드 타입의 고투과 특성을 갖는 것을 특징으로 하는 표시 장치.5. The method of claim 4,
Wherein the low reflection hardness coating film has a high transparency characteristic of a nanoceramic hybrid type.
KR1020110143791A 2011-12-27 2011-12-27 Position guiding apparatus for needle for ultrasonic operation KR101941445B1 (en)