KR101883627B1 - Copper alloy and copper alloy casting expressing gold color - Google Patents
Copper alloy and copper alloy casting expressing gold color Download PDFInfo
- Publication number
- KR101883627B1 KR101883627B1 KR1020180066387A KR20180066387A KR101883627B1 KR 101883627 B1 KR101883627 B1 KR 101883627B1 KR 1020180066387 A KR1020180066387 A KR 1020180066387A KR 20180066387 A KR20180066387 A KR 20180066387A KR 101883627 B1 KR101883627 B1 KR 101883627B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- copper alloy
- larger
- less
- degree
- Prior art date
Abstract
본 발명은 동합금에 관한 것으로, 5 ~ 10 중량%의 알루미늄(Al), 3 ~ 7% 중량%의 철(Fe), 3 ~ 15% 중량%의 아연(Zn), 및 잔부의 구리(Cu)를 포함하고, 골드 칼라를 나타내는 것을 특징으로 한다. 상기 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함하는 것을 특징으로 한다.The present invention relates to a copper alloy, which comprises 5 to 10 wt% of aluminum (Al), 3 to 7 wt% of iron (Fe), 3 to 15 wt% of zinc (Zn) And a gold color. The copper alloy may contain up to 2% by weight of silicon (Si), up to 5% by weight of nickel (Ni), up to 2% by weight of tin (Sn), up to 3% by weight of magnesium (Mg) Cr), 10% or less of titanium (Ti), 3% or less of phosphorus (P), and 3% or less of boron (B)
Description
본 발명은 5 ~ 10 중량%의 알루미늄(Al), 3 ~ 7% 중량%의 철(Fe), 3 ~ 15% 중량%의 아연(Zn), 및 잔부의 구리(Cu)를 포함하고, 골드 칼라를 나타내는 것을 특징으로 하는 동합금에 관한 것이다.The present invention relates to an aluminum alloy comprising 5 to 10 wt% of aluminum (Al), 3 to 7 wt% of iron (Fe), 3 to 15 wt% of zinc (Zn), and the balance of copper (Cu) And a color of the copper alloy.
금(Au)은 화려한 색상을 가지고 있을 뿐만 아니라 그 색상이 변하지 않고 오랜 기간 동안 유지되므로 예로부터 장신구 등에 사용되어 왔다. 그러나 금은 고가의 재료인바 많은 양을 사용하여 일상용품 등을 제작하는데는 제한이 있었다. 이에 금 이외의 금속 성분을 혼합한 합금에 의해 금과 유사한 색상을 나타내려는 여러 시도가 있어 왔다.Gold (Au) has not only a brilliant color but also its color is kept unchanged for a long time. However, gold is a high-priced material, and there were limitations in making everyday goods using a large amount. There have been many attempts to produce a gold-like color by alloying a metal other than gold.
일본공개특허공보 소 60-152645호는 장식용 동합금에 관한 것으로, 중량비로 Al 2~15%, Ni 0.5 ~ 8%, Be 0.05 ~ 2%, 잔부 Cu를 포함하고 있다. 그러나 이 장식용 동합금에 포함된 베릴륨(Be)은 유해 물질로, 분진 상태로 공기 중에 2㎍/㎥ 이상 존재하면 만성폐질환, 작업성 피부질환, 급성 간질성 폐렴, 만성 베릴륨 중독증 등을 유발하는 문제점이 있다.Japanese Patent Application Laid-Open No. 60-152645 relates to a decorative copper alloy, which contains Al 2 to 15% by weight, Ni 0.5 to 8%, Be 0.05 to 2% by weight, and the balance Cu. However, beryllium (Be) contained in this decorative copper alloy is a harmful substance, and if it is present in the air in the air at a concentration of 2 μg / ㎥ or more, it causes problems such as chronic lung disease, workable skin disease, acute interstitial pneumonia, chronic beryllium poisoning .
본 발명은 상기한 문제점을 해결하기 위한 것으로, 5 ~ 10 중량%의 알루미늄(Al), 3 ~ 7% 중량%의 철(Fe), 3 ~ 15% 중량%의 아연(Zn), 및 잔부의 구리(Cu)를 포함하고, 골드 칼라를 나타내는 것을 특징으로 하는 동합금을 제공함으로써, 동합금에 의해 골드 칼라를 안정적으로 구현하는 것을 목적으로 한다.SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a method of manufacturing a honeycomb structure including 5 to 10 wt% aluminum, 3 to 7 wt% iron, 3 to 15 wt% The present invention provides a copper alloy containing copper (Cu) and exhibiting a gold color, thereby stably realizing gold color by a copper alloy.
상기 목적을 달성하기 위하여 본 발명은 5 ~ 10 중량%의 알루미늄(Al), 3 ~ 7% 중량%의 철(Fe), 3 ~ 15% 중량%의 아연(Zn), 및 잔부의 구리(Cu)를 포함하고, 골드 칼라를 나타내는 것을 특징으로 하는 동합금을 제공한다.In order to attain the above object, the present invention provides a method for producing a copper alloy comprising 5 to 10 wt% of aluminum (Al), 3 to 7 wt% of iron (Fe), 3 to 15 wt% of zinc (Zn) ), And exhibits a gold color.
상기 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함할 수 있다.The copper alloy may contain up to 2% by weight of silicon (Si), up to 5% by weight of nickel (Ni), up to 2% by weight of tin (Sn), up to 3% by weight of magnesium (Mg) Cr), 10 wt% or less of titanium (Ti), 3 wt% or less of phosphorus (P), and 3 wt% or less of boron (B).
상기 동합금은 색차 테스트에서 L*는 77.81, a*는 6.64, b*는 38.08의 값을 가지거나, L*는 82.60, a*는 3.13, b*는 26.16의 값을 가지거나, L*는 81.91, a*는 2.92, b*는 26.41의 값을 가지거나 또는 L*는 80.21, a*는 7.10, b*는 34.90의 값을 가질 수 있다. 여기서, L*는 명도로서 L*=100은 흰색, L*=0은 검은색에 해당되고, a*는 Red와 Green의 정도로 a*가 클수록 Red의 정도가 크고, b*는 Yellow와 Blue의 정도로 b*가 클수록 Yellow의 정도가 큰 것이다. The copper alloy has a value of L * of 77.81, a * of 6.64 and b * of 38.08 in the color difference test, L * of 82.60, a * of 3.13 and b * of 26.16 or L * of 81.91 , a * has a value of 2.92, b * has a value of 26.41, or L * has a value of 80.21, a * has a value of 7.10, and b * has a value of 34.90. Here, L * is lightness, L * = 100 is white, L * = 0 is black, a * is the degree of Red and Green, The greater the b *, the greater the degree of yellow.
상기 동합금은 제조과정 중에 발생하는 불가피한 불순물을 포함할 수 있다.The copper alloy may contain inevitable impurities generated during the manufacturing process.
상기 동합금으로 주조에 의해 동합금 주물을 제조하는 것을 특징으로 한다.And a copper alloy casting is produced by casting with the copper alloy.
본 발명에 따른 동합금 및 동합금 주물은 아래의 색차 테스트 결과에서 확인할 수 있듯이 골드 칼라에 가까운 색상을 안정적으로 구현할 수 있다. 또한, 본 발명에 따른 동합금은 유동성이 뛰어나 주조 제품을 제조하기에 적합하다. 따라서, 본 발명에 따른 동합금은 다이 캐스팅, 중력 주조 및 저압 주조 등의 주조(스퀴즈 캐스팅, 로스트 왁스 캐스팅, 틱소 캐스팅 등) 제품이나 분말 형태로 제조하여 코팅 분야나 3D 프린팅 분야에 적용 가능하다.The copper alloy and the copper alloy casting according to the present invention can stably realize a color close to gold color as can be seen from the color difference test results described below. Further, the copper alloy according to the present invention is excellent in fluidity and is suitable for producing a cast product. Accordingly, the copper alloy according to the present invention can be applied to casting (squeeze casting, roast wax casting, thixocasting or the like) such as die casting, gravity casting and low pressure casting, or in the form of powder and in the coating field or 3D printing field.
본 발명에 따른 동합금은 5 ~ 10 중량%의 알루미늄(Al), 3 ~ 7% 중량%의 철(Fe), 3 ~ 15% 중량%의 아연(Zn), 및 잔부의 구리(Cu)를 포함하고, 골드 칼라를 나타낸다. 또한, 본 발명에 따른 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함할 수 있다.The copper alloy according to the present invention contains 5 to 10 wt% of aluminum (Al), 3 to 7 wt% of iron (Fe), 3 to 15 wt% of zinc (Zn), and the balance of copper (Cu) And a gold color. The copper alloy according to the present invention may contain not more than 2 wt% Si, not more than 5 wt% Ni, not more than 2 wt% tin, not more than 3 wt% magnesium, (P) of not more than 3% by weight, and boron (B) of not more than 3% by weight of chromium (Cr), not more than 10% .
본 발명에 따른 동합금에 포함된 구성 원소의 특징 및 기능에 대해 살펴본다.The characteristics and functions of the constituent elements included in the copper alloy according to the present invention will be described.
알루미늄(Al)은 그 β상이 단단하며, 인장강도와 인성이 높다. 따라서, 합금의 내마멸성, 내피로성, 내식성을 향상시키고, 연신율을 개선시킨다.Aluminum (Al) has a strong β-phase and high tensile strength and toughness. Therefore, it improves the abrasion resistance, fatigue resistance and corrosion resistance of the alloy and improves elongation.
철(Fe)은 니켈(Ni)과 함께 강도와 인성을 향상시키고, 고온 내식성/내산화성에 도움을 준다.Iron (Fe), together with nickel (Ni), improves strength and toughness and helps in high temperature corrosion resistance / oxidation resistance.
아연(Zn)은 합금의 융점을 저하시키고, 동합금의 칼라를 개선하여 골드 칼라를 나타내도록 한다.Zinc (Zn) lowers the melting point of the alloy and improves the color of the copper alloy to give a gold color.
규소(Si)는 합금의 주조성, 내식성, 강도 및 인성 등의 개선에 도움을 준다.Silicon (Si) helps improve the casting, corrosion resistance, strength and toughness of the alloy.
니켈(Ni)이 합금에 첨가되면 강도, 내산화성, 내식성이 증가하며, 전기 저항도를 증가시킨다.Nickel (Ni) is added to alloys to increase strength, oxidation resistance, corrosion resistance, and increase electrical resistance.
주석(Sn)은 합금의 주조성, 내식성, 강도 및 인성 등의 개선에 도움을 준다.Tin (Sn) helps improve the casting, corrosion resistance, strength and toughness of the alloy.
마그네슘(Mg)은 합금의 진동흡수성, 치수안정성을 개선하고, 절삭가공성, 주조성을 향상시킨다.Magnesium (Mg) improves the vibration absorbability and dimensional stability of the alloy, improves cutting workability and castability.
크롬(Cr)은 합금에 첨가되면 내마모성과 내식성을 향상시킨다.Chromium (Cr) improves abrasion resistance and corrosion resistance when added to alloys.
티타늄(Ti)은 다양한 온도에서의 높은 강도, 강성, 인성, 낮은 밀도, 좋은 내식성을 지니고, 따라서 합금의 강도, 강성, 인성을 개선하면서 무게를 감소시킬 수 있다.Titanium (Ti) has high strength, stiffness, toughness, low density and good corrosion resistance at various temperatures, thus reducing the weight while improving the strength, stiffness and toughness of the alloy.
인(P)은 합금의 주조성, 내식성, 강도 및 인성 등의 개선에 도움을 준다.Phosphorus (P) helps improve the casting, corrosion resistance, strength and toughness of the alloy.
붕소(B)는 합금의 인성과 내마모성을 향상시킨다.Boron (B) improves the toughness and abrasion resistance of the alloy.
본 발명에 따른 동합금은 유동성이 뛰어나 주조 제품을 제조하기에 적합하므로, 다이 캐스팅, 중력 주조 및 저압 주조 등의 주조(스퀴즈 캐스팅, 로스트 왁스 캐스팅, 틱소 캐스팅 등)에 의해 동합금 주물을 제조할 수 있다. 또한, 본 발명에 따른 동합금은 분말 형태로 제조하여 코팅 분야나 3D 프린팅 분야에 적용 가능하다.Since the copper alloy according to the present invention is excellent in fluidity and is suitable for producing cast products, copper alloy castings can be produced by casting (squeeze casting, roast wax casting, thixocasting, etc.) such as die casting, gravity casting and low pressure casting . In addition, the copper alloy according to the present invention can be manufactured in powder form and applied to the field of coating and 3D printing.
본 발명에 따른 동합금에 대해서 기계적 특성을 평가하기 위해 다음과 같이 강도 및 경도를 측정하였다. In order to evaluate the mechanical properties of the copper alloy according to the present invention, strength and hardness were measured as follows.
표 1은 본 발명에 따른 실시예 따른 동합금의 구성성분을 중량%로 나타낸 표이다. 시료 01 내지 19에 대해서는 강도를 측정하여 그 결과를 표 2에 나타내었고, 시료 20 내지 25에 대해서는 경도를 측정하여 그 결과를 표 3에 나타내었고, 시료 26 내지 29에 대해서는 색차 테스트를 실시하여 그 결과를 표 4에 나타내었다. 표 1에서 기타 원소는 Ti, P, B 중의 하나이다.Table 1 is a table showing the constituent components of the copper alloy according to the embodiment of the present invention in terms of% by weight. The strengths of the samples 01 to 19 were measured and the results are shown in Table 2. The hardness of the samples 20 to 25 was measured and the results are shown in Table 3. The samples 26 to 29 were subjected to a color difference test The results are shown in Table 4. In Table 1, the other element is one of Ti, P,
표 2는 본 발명에 따른 동합금의 실시예에 대한 강도를 측정한 결과를 나타낸다.Table 2 shows the results of measuring the strength of the copper alloy according to the embodiment of the present invention.
강도는 KS B 0801(2007)에 준하는 시험편(14호A 시험편)을 제작, 0.05m/min의 크로스 헤더 속도로 인장시험을 실시하여 측정하였다. 인장강도는 300MPa ~ 660MPa의 값을, 항복강도는 200MPa ~ 380MPa의 값을, 연신율 10% ~ 50%의 값을 가진다. The strength was measured by making a test piece according to KS B 0801 (2007) (No. 14 A test piece) and performing a tensile test at a crosshead speed of 0.05 m / min. The tensile strength is 300 MPa to 660 MPa, the yield strength is 200 MPa to 380 MPa, and the elongation is 10% to 50%.
표 3은 본 발명에 따른 동합금의 실시예에 대한 경도를 측정한 결과(경도 단위: Hv)를 나타낸다.Table 3 shows the results (hardness unit: Hv) of the hardness of the copper alloy according to the embodiment of the present invention.
경도는 비커스 경도계를 이용하여 하중 500g으로 3번 측정한 평균값으로, 220Hv ~ 460Hv의 값을 가진다.The hardness is an average value measured three times at a load of 500 g using a Vickers hardness tester and has a value of 220 Hv to 460 Hv.
표 4는 본 발명에 따른 동합금의 실시예에 대해 색차 테스트를 실시한 결과를 나타낸다.Table 4 shows the result of performing a color difference test on an embodiment of the copper alloy according to the present invention.
본 색차 테스트에 사용한 장비는 일본 미놀타사 CM-5와 CM-600d이다. 표 4에서 L*는 명도를 나타내는 뜻으로 L*=100은 흰색(흰색이라기 보다는 광원의 색에 가까움)이고 L*=0은 검은색에 해당된다. a*는 Red와 Green의 정도로, 예를 들어 a*=80은 a*=50보다 더 붉게 보인다라는 의미이다. b*는 Yellow와 Blue의 정도로, 예를 들어 b*=50은 b*=20보다 훨씬 Yellow가 많게 보인다라는 의미이다.The equipment used for this color difference test is CM-5 and CM-600d of Minolta Co., Japan. In Table 4, L * denotes brightness, where L * = 100 is white (closer to the color of the light source than white) and L * = 0 corresponds to black. a * is the degree of Red and Green, for example a * = 80 means more red than a * = 50. b * is the degree of Yellow and Blue. For example, b * = 50 means that Yellow is much more than b * = 20.
색차 테스트에 사용된 24K와 18K는 시중에서 거래되고 있는 제품으로 표 4에 표시한 결과는 3회 측정한 평균값이다. 본 발명에 따른 동합금의 실시예로 색차 테스트를 실시한 결과 시료 26, 29번은 24K와 유사한 결과를 얻었으며, 시편 27, 28번은 18K와 유사한 결과값을 얻었다.The 24K and 18K used in the chrominance test are commercially available products. The results shown in Table 4 are the average values measured three times. As a result of the color difference test in the embodiment of the copper alloy according to the present invention, samples 26 and 29 obtained similar results to 24K, and specimens 27 and 28 obtained similar results to 18K.
앞에서 설명된 본 발명의 실시예들은, 본 발명의 기술적 사상을 한정하는 것으로 해석되어서는 안된다. 본 발명의 보호범위는 청구범위에 기재된 사항에 의하여만 제한되고, 본 발명의 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상을 다양한 형태로 개량 변경하는 것이 가능하다. 따라서 이러한 개량 및 변경은 통상의 지식을 가진 자에게 자명한 것인 한 본 발명의 보호범위에 속하게 될 것이다.The embodiments of the present invention described above should not be construed as limiting the technical idea of the present invention. The scope of protection of the present invention is limited only by the matters described in the claims, and those skilled in the art will be able to modify the technical idea of the present invention in various forms. Accordingly, such improvements and modifications will fall within the scope of the present invention as long as they are obvious to those skilled in the art.
Claims (5)
상기 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함하고,
상기 동합금은 색차 테스트에서 L*는 77.81, a*는 6.64, b*는 38.08의 값을 가지고, L*는 명도로서 L*=100은 흰색, L*=0은 검은색에 해당되고, a*는 Red와 Green의 정도로 a*가 클수록 Red의 정도가 크고, b*는 Yellow와 Blue의 정도로 b*가 클수록 Yellow의 정도가 큰 것을 특징으로 하는 동합금.
(Al), 3 to 7% by weight of iron (Fe), 3 to 15% by weight of zinc (Zn), and the balance of copper (Cu) As the copper alloy,
The copper alloy may contain up to 2% by weight of silicon (Si), up to 5% by weight of nickel (Ni), up to 2% by weight of tin (Sn), up to 3% by weight of magnesium (Mg) Cr), 10% by weight or less of titanium (Ti), 3% by weight or less of phosphorus (P), and 3% by weight or less of boron (B)
L * = 100 is white, L * = 0 is black, L * is black, and a * and b * have a brightness of 77.81, 6.64 and 38.08, respectively, in the color difference test. Is a degree of red and green, and a degree of red is larger as a * is larger, and a degree of yellow is larger as b * is larger than that of yellow and blue.
상기 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함하고,
상기 동합금은 색차 테스트에서 L*는 82.60, a*는 3.13, b*는 26.16의 값을 가지고, L*는 명도로서 L*=100은 흰색, L*=0은 검은색에 해당되고, a*는 Red와 Green의 정도로 a*가 클수록 Red의 정도가 크고, b*는 Yellow와 Blue의 정도로 b*가 클수록 Yellow의 정도가 큰 것을 특징으로 하는 동합금.
(Al), 3 to 7% by weight of iron (Fe), 3 to 15% by weight of zinc (Zn), and the balance of copper (Cu) As the copper alloy,
The copper alloy may contain up to 2% by weight of silicon (Si), up to 5% by weight of nickel (Ni), up to 2% by weight of tin (Sn), up to 3% by weight of magnesium (Mg) Cr), 10% by weight or less of titanium (Ti), 3% by weight or less of phosphorus (P), and 3% by weight or less of boron (B)
L * = 100 is white, L * = 0 is black, and a * is a black color. In the color difference test, L * is 82.60, a * is 3.13, b * is 26.16, Is a degree of red and green, and a degree of red is larger as a * is larger, and a degree of yellow is larger as b * is larger than that of yellow and blue.
상기 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함하고,
상기 동합금은 색차 테스트에서 L*는 81.91, a*는 2.92, b*는 26.41의 값을 가지고, L*는 명도로서 L*=100은 흰색, L*=0은 검은색에 해당되고, a*는 Red와 Green의 정도로 a*가 클수록 Red의 정도가 크고, b*는 Yellow와 Blue의 정도로 b*가 클수록 Yellow의 정도가 큰 것을 특징으로 하는 동합금.
(Al), 3 to 7% by weight of iron (Fe), 3 to 15% by weight of zinc (Zn), and the balance of copper (Cu) As the copper alloy,
The copper alloy may contain up to 2% by weight of silicon (Si), up to 5% by weight of nickel (Ni), up to 2% by weight of tin (Sn), up to 3% by weight of magnesium (Mg) Cr), 10% by weight or less of titanium (Ti), 3% by weight or less of phosphorus (P), and 3% by weight or less of boron (B)
L * = 100 is white, L * = 0 is black, and a * is a black color. In the color difference test, L * is 81.91, a * is 2.92, b * is 26.41, Is a degree of red and green, and a degree of red is larger as a * is larger, and a degree of yellow is larger as b * is larger than that of yellow and blue.
상기 동합금은 2 중량% 이하의 규소(Si), 5 중량% 이하의 니켈(Ni), 2 중량% 이하의 주석(Sn), 3 중량% 이하의 마그네슘(Mg), 7 중량% 이하의 크롬(Cr), 10 중량% 이하의 티타늄(Ti), 3 중량% 이하의 인(P) 및 3 중량% 이하의 붕소(B)로 이루어진 군으로부터 선택된 하나 이상을 더 포함하고,
상기 동합금은 색차 테스트에서 L*는 80.21, a*는 7.10, b*는 34.90의 값을 가지고, L*는 명도로서 L*=100은 흰색, L*=0은 검은색에 해당되고, a*는 Red와 Green의 정도로 a*가 클수록 Red의 정도가 크고, b*는 Yellow와 Blue의 정도로 b*가 클수록 Yellow의 정도가 큰 것을 특징으로 하는 동합금.
(Al), 3 to 7% by weight of iron (Fe), 3 to 15% by weight of zinc (Zn), and the balance of copper (Cu) As the copper alloy,
The copper alloy may contain up to 2% by weight of silicon (Si), up to 5% by weight of nickel (Ni), up to 2% by weight of tin (Sn), up to 3% by weight of magnesium (Mg) Cr), 10% by weight or less of titanium (Ti), 3% by weight or less of phosphorus (P), and 3% by weight or less of boron (B)
L * = 100 is white, L * = 0 is black, and a * is a black color. In the color difference test, L * is 80.21, a * is 7.10, b * is 34.90, Is a degree of red and green, and a degree of red is larger as a * is larger, and a degree of yellow is larger as b * is larger than that of yellow and blue.