KR101851430B1 - Retardation Film and Polarizing Plate Using the Same - Google Patents
Retardation Film and Polarizing Plate Using the Same Download PDFInfo
- Publication number
- KR101851430B1 KR101851430B1 KR1020150030516A KR20150030516A KR101851430B1 KR 101851430 B1 KR101851430 B1 KR 101851430B1 KR 1020150030516 A KR1020150030516 A KR 1020150030516A KR 20150030516 A KR20150030516 A KR 20150030516A KR 101851430 B1 KR101851430 B1 KR 101851430B1
- Authority
- KR
- South Korea
- Prior art keywords
- film
- peeling
- retardation
- quot
- retardation film
- Prior art date
Abstract
본 발명은 위상차층을 기재필름으로부터 박리 및 전사 시 부분 미박리(나끼와카레), 미박리 또는 기포 혼입 등의 문제가 없는 위상차 필름 및 박리된 위상차층이 편광자의 적어도 일면에 전사된 편광판을 제공한다.The present invention provides a polarizing plate in which a retardation film free from problems such as partial delamination (lapping and currying), undrawn or bubble inclusion, and a peeled retardation layer are transferred onto at least one surface of a polarizer when peeling and transferring the retardation layer from a base film do.
Description
본 발명은 위상차 필름 및 이를 이용한 편광판에 관한 것으로, 보다 상세하게는 위상차층을 기재필름으로부터 박리 및 전사 시 부분 미박리(나끼와카레), 미박리 또는 기포 혼입 등의 문제가 없는 위상차 필름 및 박리된 위상차층이 편광자의 적어도 일면에 전사된 편광판에 관한 것이다.The present invention relates to a retardation film and a polarizing plate using the retardation film, and more particularly, to a retardation film and a retardation film which are free from problems such as partial peeling (peeling and curling) at peeling and transferring from a base film, Wherein the retardation layer is transferred onto at least one surface of the polarizer.
위상차 필름은 다양한 용도로 사용된다. 구체적으로 액정표시장치에서는 화상 착색을 해소하거나 시야각을 확대하기 위해 사용되며, 유기발광소자에서는 반사 방지 또는 편광판의 색상 보정을 위해 사용된다. 또한 터치 패널에서는 외광 반사를 저감하여 시인성을 향상시키기 위해 사용된다. 이러한 위상차 필름은 투명기재 상에 광배향성 폴리머 및 반응성 액정 화합물로부터 형성된 위상차층이 적층된 구조일 수 있다.The retardation film is used for various purposes. Specifically, in a liquid crystal display device, it is used for eliminating image coloring or for enlarging a viewing angle, and in an organic light emitting device, it is used for reflection prevention or color correction of a polarizing plate. In addition, the touch panel is used for reducing visibility of external light to improve visibility. Such a retardation film may be a structure in which a retardation layer formed from a photo-orientable polymer and a reactive liquid crystal compound is laminated on a transparent substrate.
최근, 슬림형 대형 벽걸이 TV, 모바일 타입의 컴퓨터, 차량용 TV, 차량용 네비게이션 시스템의 디스플레이, 휴대전화 등과 같은 슬림화된 디스플레이에 대한 시장이 급격하게 확대됨에 따라, 위상차 필름도 박형화 및 경량화에 대한 요구가 있어 왔다.2. Description of the Related Art In recent years, there has been a demand for thinning and weight reduction of a retardation film as a market for a thin wall-hung TV, a mobile type computer, a car TV, a display for a car navigation system, .
이를 위해 위상차 필름의 투명기재로부터 위상차층을 박리하여 위상차층을 편광자에 전사하는 방식이 제안되었으나, 위상차층이 박리되지 않거나 기포가 혼입되는 문제점이 있었다. For this purpose, a method of peeling a retardation layer from a transparent substrate of a retardation film and transferring the retardation layer to a polarizer has been proposed. However, there is a problem that the retardation layer is not peeled off or bubbles are incorporated.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 본 발명의 한 목적은 위상차층을 기재필름으로부터 박리 및 전사 시 부분 미박리(나끼와카레), 미박리 또는 기포 혼입 등의 문제가 없는 위상차 필름을 제공하는 것이다.SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and an object of the present invention is to provide a retardation film which is free from problems such as partial peeling (fog and curry) .
본 발명의 다른 목적은 상기 위상차 필름으로부터 박리된 위상차층이 편광자의 적어도 일면에 전사된 편광판을 제공하는 것이다.Another object of the present invention is to provide a polarizing plate in which a retardation layer peeled from the retardation film is transferred onto at least one surface of the polarizer.
본 발명의 또 다른 목적은 상기 편광판을 포함하는 화상표시장치를 제공하는 것이다.It is still another object of the present invention to provide an image display device including the polarizing plate.
한편으로, 본 발명은 기재필름 상에 위상차층이 적층된 위상차 필름으로서, 하기 수학식 1 내지 5를 만족하는 위상차 필름을 제공한다.On the other hand, the present invention provides a retardation film laminated with a retardation layer on a base film, which satisfies the following formulas (1) to (5).
[수학식 1][Equation 1]
0.05N/25mm < a ≤ 0.15N/25mm0.05 N / 25 mm < a < 0.15 N / 25 mm
[수학식 2]&Quot; (2) "
b < 0.2N/25mmb < 0.2N / 25mm
[수학식 3]&Quot; (3) "
c < 0.15N/25mmc < 0.15 N / 25 mm
[수학식 4]&Quot; (4) "
a의 면내 박리력 편차 ≤ 0.05In-plane peeling force deviation of a ≤ 0.05
[수학식 5]&Quot; (5) "
a < c x 2
a <cx 2
상기 식에서,In this formula,
a는 박리속도 10m/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 고속박리력이고,a is the high-speed peeling force when peeling the phase difference layer from the base film at a peeling speed of 10 m / min and a peeling angle of 180 °,
b는 박리속도 30m/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 고속박리력이며,b is a high-speed peeling force when the phase difference layer is peeled off from the base film at a peeling speed of 30 m / min and a peeling angle of 180 °,
c는 박리속도 300mm/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 저속박리력이다.c is a low peeling force when the phase difference layer is peeled from the base film at a peeling speed of 300 mm / min and a peeling angle of 180 deg.
본 발명의 일 실시형태에서, 상기 위상차 필름은 λ/4 위상차 필름일 수 있다.In one embodiment of the present invention, the retardation film may be a lambda / 4 retardation film.
본 발명의 일 실시형태에서, 상기 위상차 필름은 기재필름 상에 배향막 형성 조성물을 도포하고 배향성을 부여하여 배향막층을 형성하고, 상기 배향막층 상에 액정 화합물을 포함하는 코팅층 형성 조성물을 도포하여 액정 코팅층을 형성함으로써 제조될 수 있다.
In an embodiment of the present invention, the retardation film is formed by applying an alignment film forming composition on a base film and applying an orientation property to form an orientation film layer, and applying a coating layer forming composition containing a liquid crystal compound onto the orientation film layer, ≪ / RTI >
다른 한편으로, 본 발명은 상기 위상차 필름으로부터 박리된 위상차층이 편광자의 적어도 일면에 전사된 편광판을 제공한다.On the other hand, the present invention provides a polarizing plate in which a retardation layer peeled from the retardation film is transferred onto at least one surface of the polarizer.
또 다른 한편으로, 본 발명은 상기 편광판을 포함하는 화상표시장치를 제공한다.On the other hand, the present invention provides an image display device including the polarizer.
본 발명의 위상차 필름은 위상차층을 기재필름으로부터 박리 및 전사 시 나끼와카레, 미박리 또는 기포 혼입 등의 문제가 없어 외관이 양호한 편광판을 제조하는데 유용하게 사용될 수 있다.The retardation film of the present invention can be advantageously used for producing a polarizing plate having good appearance due to no problem of peeling and transferring of the retardation layer from the base film and no problems such as curling, unpeeling, or air bubble incorporation.
이하, 본 발명을 보다 상세히 설명한다.
Hereinafter, the present invention will be described in more detail.
본 발명의 일 실시형태는 기재필름 상에 위상차층이 적층된 위상차 필름으로서, 하기 수학식 1 내지 5를 만족하는 위상차 필름에 관한 것이다.An embodiment of the present invention relates to a retardation film in which a retardation layer is laminated on a base film and satisfies the following equations (1) to (5).
[수학식 1][Equation 1]
0.05N/25mm < a ≤ 0.15N/25mm0.05 N / 25 mm < a < 0.15 N / 25 mm
[수학식 2]&Quot; (2) "
b < 0.2N/25mmb < 0.2N / 25mm
[수학식 3]&Quot; (3) "
c < 0.15N/25mmc < 0.15 N / 25 mm
[수학식 4]&Quot; (4) "
a의 면내 박리력 편차 ≤ 0.05In-plane peeling force deviation of a ≤ 0.05
[수학식 5]&Quot; (5) "
a < c x 2
a <cx 2
상기 식에서,In this formula,
a는 박리속도 10m/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 고속박리력이고,a is the high-speed peeling force when peeling the phase difference layer from the base film at a peeling speed of 10 m / min and a peeling angle of 180 °,
b는 박리속도 30m/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 고속박리력이며,b is a high-speed peeling force when the phase difference layer is peeled off from the base film at a peeling speed of 30 m / min and a peeling angle of 180 °,
c는 박리속도 300mm/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 저속박리력이다.
c is a low peeling force when the phase difference layer is peeled from the base film at a peeling speed of 300 mm / min and a peeling angle of 180 deg.
상기 박리력은 기재필름과 위상차층의 밀착성을 평가하는 지표로서, 본 발명에서 박리력을 측정하는 방법은 특별히 제한되지 않으며, 예를 들면 후술하는 실험예에 제시된 방법으로 측정할 수 있다.
The peeling force is an index for evaluating the adhesion between the base film and the retardation layer. The method for measuring the peeling force in the present invention is not particularly limited, and can be measured by, for example, the method described in Experimental Examples described later.
상기 a의 면내 박리력 편차는 위상차 필름의 폭방향 위치별로 측정한 a 값의 편차(최대값-최소값)을 의미한다.
The in-plane peeling force deviation of a means the deviation (maximum value-minimum value) of a value measured for each position in the width direction of the retardation film.
본 발명의 일 실시형태에서는, 고속박리력(a)를 0.05 초과 0.15N/25mm 이하로, 고속박리력(b)를 0.2N/25mm 미만으로, 저속박리력(c)를 0.15N/25mm미만으로 조절하고, 고속박리력(a)의 면내 박리력 편차를 0.05 이하로 조절하며, 고속박리력(a)가 저속박리력(c)에 2를 곱한 값보다 작도록 조절함으로써, 기재필름으로부터 위상차층을 박리 시 발생하는 부분 미박리(나끼와카레) 또는 미박리 문제를 해결할 수 있다.
(B) is less than 0.2 N / 25 mm and the low-speed peeling force (c) is less than 0.15 N / 25 mm , The in-plane peeling force deviation of the high-speed peeling force (a) is adjusted to 0.05 or less, and the retardation force (a) is adjusted to be smaller than the value obtained by multiplying the low- It is possible to solve the partial peeling (peeling and curling) or the peeling-off problem that occurs when the layer is peeled off.
상기 수학식 1 내지 5를 만족하는 위상차 필름은 후술하는 배향막층의 종류나 두께, 액정 코팅층의 종류나 두께, 기재필름의 종류나 두께, 표면처리 방법 등을 적절히 변경함으로써 용이하게 제조할 수 있다.
The retardation film satisfying the above formulas (1) to (5) can be easily produced by appropriately changing the kind and thickness of the orientation film layer, the kind and thickness of the liquid crystal coating layer, the type and thickness of the base film,
본 발명의 일 실시형태에 따른 위상차 필름은 λ/4 위상차 필름일 수 있다. The retardation film according to an embodiment of the present invention may be a lambda / 4 retardation film.
상기 λ/4 위상차 필름은 편광자를 통과하면서 편광된 선편광에 1/4 파장만큼 위상차를 부여하여 상기 선편광을 원편광으로 변화시키는 역할을 하는 필름을 의미한다.
The? / 4 retardation film means a film having a role of changing the linearly polarized light to circularly polarized light by applying a retardation of 1/4 wavelength to polarized linearly polarized light while passing through the polarizer.
본 발명의 일 실시형태에 따른 위상차 필름을 형성할 수 있는 재료로서는, 상기 특성을 획득할 수 있는 한 임의의 적합한 재료를 채택할 수 있다. 예를 들어, 상기 위상차 필름은 기재필름 상에 배향막 형성 조성물을 도포하고 배향성을 부여하여 배향막층을 형성하고, 상기 배향막층 상에 액정 화합물을 포함하는 코팅층 형성 조성물을 도포하여 액정 코팅층을 형성함으로써 제조할 수 있다.
As the material capable of forming the retardation film according to one embodiment of the present invention, any suitable material can be employed as long as the above characteristics can be obtained. For example, the retardation film can be produced by applying an alignment film forming composition on a base film, applying an orientation property to form an orientation film layer, and applying a coating layer forming composition containing a liquid crystal compound on the orientation film layer to form a liquid crystal coating layer can do.
상기 배향막 형성 조성물은 당해 분야에서 통상적으로 사용되는 배향제, 광중합 개시제 및 용제를 포함할 수 있다.The composition for forming an alignment film may include an alignment agent, a photopolymerization initiator and a solvent commonly used in the art.
상기 배향제로는 당해 분야에서 통상적으로 사용되는 배향제가 특별한 제한 없이 사용될 수 있다. 예를 들면, 폴리아크릴레이트계 고분자, 폴리아믹산, 폴리이미드계 고분자 또는 신나메이트기를 포함하는 고분자를 배향제로 사용할 수 있으며, 광배향을 적용하는 경우에는 신나메이트기를 포함하는 고분자를 사용하는 것이 바람직하다. 배향제로 사용되는 고분자는 중량평균 분자량이 10,000-500,000 정도일 수 있으나, 이에 한정되는 것은 아니다.
As the aligning agent, an aligning agent ordinarily used in the art can be used without any particular limitation. For example, a polyacrylate-based polymer, a polyamic acid, a polyimide-based polymer, or a polymer containing a cinnamate group can be used as an alignment agent, and in the case of applying light alignment, a polymer containing a cinnamate group is preferably used . The polymer used as the aligning agent may have a weight average molecular weight of about 10,000 to 500,000, but is not limited thereto.
상기 광중합 개시제로서는 당해 분야에서 통상적으로 사용되는 광중합 개시제가 특별한 제한 없이 사용될 수 있다. 예를 들면, 벤조인 화합물, 벤조페논 화합물, 알킬페논 화합물, 아실포스핀옥사이드 화합물, 트리아진 화합물, 요오드늄염 및 술포늄염을 들 수 있다. 광중합 개시제로서 시판품을 사용할 수도 있다. 구체적으로는, 일가큐어(Irgacure) 907, 일가큐어 184, 일가큐어 651, 일가큐어 819, 일가큐어 250, 일가큐어 369(이상, 전부 BASF 재팬(주) 제조), 세이크올 BZ, 세이크올 Z, 세이크올 BEE(이상, 전부 세이코카가쿠(주) 제조), 카야큐어(kayacure) BP100(니혼카야쿠(주) 제조), 사이라큐어(CYRACURE) UVI-6992(다우케미컬 제조), 아데카옵토머 SP-152, 아데카옵토머 SP-170(이상, 전부 (주)ADEKA 제조), TAZ-A, TAZ-PP(이상, DKSH 재팬 제조), TAZ-104(산와케미컬 제조) 등을 들 수 있다.
As the photopolymerization initiator, a photopolymerization initiator commonly used in the art can be used without any particular limitation. Examples thereof include benzoin compounds, benzophenone compounds, alkylphenone compounds, acylphosphine oxide compounds, triazine compounds, iodonium salts and sulfonium salts. Commercially available products can also be used as photopolymerization initiators. More specifically, Irgacure 907, Irgacure 184, Irgacure 651, Irgacure 819, Irgacure 250, Irgacure 369 (all manufactured by BASF Japan Ltd.), Sheikol BZ, Sheikol Z, (All manufactured by SEIKO KAGAKU CO., LTD.), Kayacure BP100 (manufactured by Nippon Kayaku Co., Ltd.), CYRACURE UVI-6992 (manufactured by DOW CHEMICAL CO., LTD.), Adeka Opto TAZ-PP (manufactured by DKSH Japan) and TAZ-104 (manufactured by Sanwa Chemical Co., Ltd.), and the like can be given. have.
상기 용제로서는 당해 분야에서 통상적으로 사용되는 용제가 특별한 제한 없이 사용될 수 있다. 예를 들면, 메탄올, 에탄올, 에틸렌글리콜, 이소프로필알코올, 프로필렌글리콜, 에틸렌글리콜메틸에테르, 에틸렌글리콜부틸에테르, 프로필렌글리콜모노메틸에테르, 페놀 등의 알코올 용제; 아세트산에틸, 아세트산부틸, 에틸렌글리콜메틸에테르아세테이트, γ-부티로락톤, 프로필렌글리콜메틸에테르아세테이트, 젖산에틸 등의 에스테르 용제; 아세톤, 메틸에틸케톤, 시클로펜타논, 시클로헥사논, 2-헵타논, 메틸이소부틸케톤 등의 케톤 용제; 펜탄, 헥산, 헵탄 등의 지방족 탄화수소 용제; 톨루엔, 크실렌 등의 방향족 탄화수소 용제, 아세토니트릴 등의 니트릴 용제; 테트라히드로푸란, 디메톡시에탄 등의 에테르 용제; 및 클로로포름, 클로로벤젠 등의 염소계 용제를 들 수 있다. 이들 용제는 단독으로 이용할 수도 있고, 복수를 조합하여 이용할 수도 있다.
As the solvent, a solvent commonly used in the art can be used without particular limitation. Examples thereof include alcohol solvents such as methanol, ethanol, ethylene glycol, isopropyl alcohol, propylene glycol, ethylene glycol methyl ether, ethylene glycol butyl ether, propylene glycol monomethyl ether and phenol; Ester solvents such as ethyl acetate, butyl acetate, ethylene glycol methyl ether acetate,? -Butyrolactone, propylene glycol methyl ether acetate and ethyl lactate; Ketone solvents such as acetone, methyl ethyl ketone, cyclopentanone, cyclohexanone, 2-heptanone, and methyl isobutyl ketone; Aliphatic hydrocarbon solvents such as pentane, hexane and heptane; Aromatic hydrocarbon solvents such as toluene and xylene; nitrile solvents such as acetonitrile; Ether solvents such as tetrahydrofuran and dimethoxyethane; And chlorinated solvents such as chloroform and chlorobenzene. These solvents may be used alone, or a plurality of solvents may be used in combination.
상기의 배향막 형성 조성물은 필요에 따라 충진제, 경화제, 레벨링제, 밀착촉진제, 산화 방지제, 자외선 흡수제, 응집 방지제, 연쇄 이동제 등의 첨가제를 더 포함할 수 있다.
The composition for forming an alignment film may further contain additives such as a filler, a curing agent, a leveling agent, an adhesion promoter, an antioxidant, an ultraviolet absorber, an aggregation inhibitor and a chain transfer agent.
상기 배향막 형성 조성물로 시판품을 사용하여도 좋고, 그 구체예로서는 Rolic사로부터 시판되고 있는 ROP-108 EXP115을 들 수 있다.
A commercially available product may be used as the alignment film forming composition, and specific examples thereof include ROP-108 EXP115 commercially available from Rolic.
상기 배향막 형성 조성물의 도포는 예를 들면 닥터 블레이드, 와이어 바, 다이 코터, 콤마 코터, 그라비아 코터, 롤 등 당해 분야에 알려진 통상적인 도공 방식을 제한 없이 사용할 수 있다.The application of the alignment film forming composition can be carried out by any conventional coating methods known in the art, such as doctor blade, wire bar, die coater, comma coater, gravure coater and roll.
상기 배향막 형성 조성물을 기재필름 상에 도포한 후에는 건조공정을 수행할 수 있다. 이 경우, 건조는 120℃ 이하, 바람직하게는 30 내지 120℃, 보다 바람직하게는 50 내지 120℃에서 수행될 수 있으나, 이에 한정되는 것은 아니다.After the composition for forming an alignment film is applied on a base film, a drying process can be performed. In this case, drying may be performed at 120 ° C or lower, preferably 30 to 120 ° C, more preferably 50 to 120 ° C, but is not limited thereto.
상기 배향막 형성 조성물이 도포 및 필요에 따라 건조된 후에는 배향처리를 한다. 상기 배향처리는 당해 분야에 알려진 다양한 방법을 제한 없이 채택할 수 있으며, 바람직하게는 광경화를 사용할 수 있다.
After the composition for forming an alignment film is applied and if necessary dried, alignment treatment is performed. The alignment treatment may be carried out by various methods known in the art without limitation, and preferably, photo-curing can be used.
상기 코팅층 형성 조성물은 광학 이방성을 가지고, 광 또는 열에 의한 가교성을 가지는 액정 화합물을 이용하여 제조할 수 있다. 상기 액정 화합물은 일례로 반응성 액정 화합물(RM)이 포함될 수 있다. 반응성 액정 화합물(RM)의 예로서는 인포메이션디스플레이 10권 1호(반응성 액정 단량체(RM)의 최신 연구 동향)에 기재된 것을 들 수 있다.The coating layer forming composition can be produced by using a liquid crystal compound having optical anisotropy and having a crosslinkability by light or heat. The liquid crystal compound may include, for example, a reactive liquid crystal compound (RM). Examples of the reactive liquid crystal compound (RM) include those described in Information Display Vol. 10, No. 1 (Recent Research Trend of Reactive Liquid Crystal Monomer (RM)).
상기 반응성 액정 화합물은 액정성을 발현할 수 있는 메조겐(mesogen)과 중합이 가능한 말단기를 포함하여 액정상을 갖게 되는 단량체 분자를 의미한다. 반응성 액정 화합물을 중합하게 되면 액정의 배열된 상을 유지하면서 가교된 고분자 네트워크를 얻을 수 있게 된다. 반응성 액정 화합물 분자는 투명점(clearing point)으로부터 냉각하게 되면 같은 구조의 액정 고분자를 사용하는 경우보다 액정상에서 상대적으로 낮은 점도에서 보다 잘 배향된 구조를 갖는 대면적의 도메인을 얻을 수 있다.The reactive liquid crystal compound means a monomer molecule having a liquid crystal phase including a mesogen capable of exhibiting liquid crystallinity and an end group capable of polymerization. When the reactive liquid crystal compound is polymerized, a crosslinked polymer network can be obtained while maintaining the aligned phase of the liquid crystal. When a reactive liquid crystal compound molecule is cooled from a clearing point, a domain having a well-oriented structure with a relatively low viscosity on a liquid crystal can be obtained, as compared with the case of using a liquid crystal polymer having the same structure.
이와 같이 형성된 대면적의 액정상 가교 네트워크 필름은 액정이 가지는 광학 이방성이나 유전율 등의 특성을 그대로 유지하면서도 고체상의 박막 형태를 가지고 있기 때문에 기계적이나 열적으로 안정하다.The large-area liquid crystalline crosslinked network film thus formed is stable in terms of mechanical and thermal properties because it has a solid thin film form while maintaining the optical anisotropy and dielectric constant of the liquid crystal.
상기 반응성 액정 화합물로 시판품을 사용하여도 좋고, 그 구체예로서는 BASF사로부터 시판되고 있는 파리오컬러 LC242를 들 수 있다. 이들 반응성 액정 화합물은 단독으로 이용할 수도 있고, 복수를 조합시켜 이용할 수도 있다.
A commercially available product may be used as the above-mentioned reactive liquid crystal compound, and a specific example thereof is Pario color LC242 commercially available from BASF. These reactive liquid crystal compounds may be used alone or in combination of two or more.
상기 코팅층 형성 조성물은 코팅 공정의 효율성 및 코팅층의 균일성을 확보하기 위하여 용매에 희석시켜 사용하며, 바람직하기로는 액정 화합물을 용해시킬 수 있는 용매에 용해되어 균일함을 갖는 것이 바람직하다.The composition for forming a coating layer is preferably diluted in a solvent to ensure the efficiency of the coating process and uniformity of the coating layer. Preferably, the composition is dissolved in a solvent capable of dissolving the liquid crystal compound and has uniformity.
또한, 반응성 액정 화합물은 이를 중합 및 가교시키기 위한 개시제를 포함하여 코팅층 형성 조성물을 제조한다. 개시제는 공지의 광중합 개시제 또는 열중합 개시제를 사용할 수 있으며, 광중합 개시제가 반응시간 및 제어가 용이하여 바람직하다. 개시제는 반응성 액정 화합물 전체 고형분에 대해서 10중량% 이하, 바람직하게는 0.1 내지 5중량%이다.In addition, the reactive liquid crystal compound includes an initiator for polymerization and crosslinking thereof to prepare a coating layer forming composition. As the initiator, a known photopolymerization initiator or a thermal polymerization initiator can be used, and a photopolymerization initiator is preferable because the reaction time and control are easy. The amount of the initiator is 10% by weight or less, preferably 0.1 to 5% by weight based on the total solid content of the reactive liquid crystal compound.
또한, 반응성 액정 화합물은 첨가제를 추가로 포함하여 코팅층 형성 조성물을 제조한다. 첨가제는 일례로 분산제, 결합제(예컨대, 유리 라디칼 중합성 및 양이온성 중합성 결합성분), 방부제(예컨대, 글루타르디알데히드, 테트라메틸올아세틸렌우레아), 실란커플링제, 레벨링제, 가교제, 산화방지제, 탈기제, 소포제, 점도조절제, 유동 개선제, 침강방지제, 광택개선제, 윤활제, 접착 촉진제, 항피부제, 메팅제, 유화제, 안정제, 소수성 제제, 광안정화 첨가제, 처리 개선제, 대전방지제 등이 사용될 수 있다.
Further, the reactive liquid crystal compound further comprises an additive to prepare a coating layer forming composition. Additives include, for example, dispersants, binders (e.g., free radically polymerizable and cationic polymerizable binding components), preservatives (e.g., glutaraldehyde, tetramethylolacetylene urea), silane coupling agents, leveling agents, A lubricant, an adhesion promoter, an anti-dermatological agent, a matrix agent, an emulsifier, a stabilizer, a hydrophobic agent, a photostabilizing additive, a treatment improving agent, an antistatic agent, and the like can be used as the antioxidant, antioxidant, antifoaming agent, antifoaming agent, viscosity adjusting agent, flow improver, have.
상기 코팅층 형성 조성물을 도포하는 방법은 특별히 한정하지는 않으나, 구체적으로 핀 코팅, 롤 코팅, 디스펜싱 코팅, 그라비아 코팅 등이 사용될 수 있다. 코팅 방법에 따라 용매의 종류 및 사용량을 결정하는 것이 바람직하다.The method of applying the coating layer forming composition is not particularly limited, but specifically, pin coating, roll coating, dispensing coating, gravure coating, and the like can be used. It is preferable to determine the type and amount of the solvent depending on the coating method.
상기 코팅층 형성 조성물에 함유된 용매는 건조 공정을 통하여 증발시키게 된다.The solvent contained in the coating layer forming composition is evaporated through a drying process.
건조는 특별히 한정하지 않으며, 통상 열풍 건조기나 원적외선 가열기를 이용하여 수행할 수 있으며, 건조온도는 통상 50 내지 150℃, 바람직하게는 70 내지 130℃이고, 건조시간은 통상 30 내지 600초, 바람직하게는 60 내지 300초이다. 또한, 건조는 동일한 온도 조건에서 수행하거나, 단계적으로 온도를 상승시키면서 수행할 수 있다.The drying temperature is usually 50 to 150 ° C, preferably 70 to 130 ° C, the drying time is usually 30 to 600 seconds, and preferably 50 to 150 ° C. The drying temperature is not particularly limited, Is 60 to 300 seconds. In addition, the drying can be carried out under the same temperature condition or while raising the temperature stepwise.
건조한 후 자외선 등의 광 조사에 의해 광경화시켜, 또는 가열기 등의 열 조사에 의해 열경화시켜 액정 코팅층을 형성한다.
Dried and then photo-cured by light irradiation such as ultraviolet rays or thermally cured by heat irradiation with a heater or the like to form a liquid crystal coating layer.
상기 광경화는 저압 수은등, 중압 수은등, 고압 수은등, 초고압 수은등, 케미컬 램프, 블랙 라이트 램프, 마이크로 웨이브 여기 수은등, 메탈할라이드 램프 등을 이용할 수 있으며, 램프의 경제성과 출력면을 고려할 때 고압 수은등과 메탈할라이드 램프의 이용이 바람직하다.The light curing can be performed using a low pressure mercury lamp, a medium pressure mercury lamp, a high pressure mercury lamp, an ultra high pressure mercury lamp, a chemical lamp, a black light lamp, a microwave excited mercury lamp and a metal halide lamp. Use of a halide lamp is preferred.
조도는 30 내지 300mW/㎠, 바람직하게는 30 내지 250mW/㎠, 보다 바람직하게는 30 내지 200mW/㎠의 범위일 수 있다. 상기 조도가 30mW/㎠ 미만이면 경화시간이 길어져 생산성이 떨어질 수 있으며, 300mW/㎠ 초과이면 높은 조도로 인해 필름에 열 손상을 가해 필름이 변형될 수 있다.The roughness may be in the range of 30 to 300 mW / cm 2, preferably 30 to 250 mW / cm 2, more preferably 30 to 200 mW / cm 2. If the illuminance is less than 30 mW / cm 2, the curing time may become longer and the productivity may be lowered. If the illuminance is more than 300 mW / cm 2, the film may be deformed due to thermal damage due to high illuminance.
상기 액정 코팅층의 막 두께는 1 ㎛ 내지 50 ㎛가 바람직하고, 1 ㎛ 내지 20 ㎛가 보다 바람직하다.
The film thickness of the liquid crystal coating layer is preferably 1 占 퐉 to 50 占 퐉, more preferably 1 占 퐉 to 20 占 퐉.
상기 기재필름은 투명성, 기계적 강도, 열안정성, 수분차폐성, 등방성 등에서 우수한 필름이 사용될 수 있다. 구체적인 예로는, 폴리에틸렌테레프탈레이트, 폴리에틸렌이소프탈레이트, 폴리에틸렌나프탈레이트, 폴리부틸렌테레프탈레이트 등의 폴리에스테르계 수지; 디아세틸셀룰로오스, 트리아세틸셀룰로오스 등의 셀룰로오스계 수지; 폴리카보네이트계 수지; 폴리메틸(메타)아크릴레이트, 폴리에틸(메타)아크릴레이트 등의 아크릴계 수지; 폴리스티렌, 아크릴로니트릴-스티렌 공중합체 등의 스티렌계 수지; 폴리에틸렌, 폴리프로필렌, 시클로계 또는 노보넨 구조를 갖는 폴리올레핀, 에틸렌-프로필렌 공중합체 등의 폴리올레핀계 수지; 염화비닐계 수지; 나일론, 방향족 폴리아미드 등의 아미드계 수지; 이미드계 수지; 폴리에테르술폰계 수지; 폴리에테르에테르케톤계 수지; 황화 폴리페닐렌계 수지; 비닐알코올계 수지; 염화비닐리덴계 수지; 비닐부티랄계 수지; 알릴레이트계 수지; 폴리옥시메틸렌계 수지; 에폭시계 수지 등과 같은 열가소성 수지로 구성된 필름을 들 수 있으며, 상기 열가소성 수지의 블렌드물로 구성된 필름도 사용할 수 있다. 또한, (메타)아크릴계, 우레탄계, 아크릴우레탄계, 에폭시계, 실리콘계 등의 열경화성 수지 또는 자외선 경화형 수지로 된 필름을 이용할 수도 있다.
The base film may be a film excellent in transparency, mechanical strength, thermal stability, moisture barrier properties, isotropy, and the like. Specific examples include polyester resins such as polyethylene terephthalate, polyethylene isophthalate, polyethylene naphthalate and polybutylene terephthalate; Cellulose-based resins such as diacetylcellulose and triacetylcellulose; Polycarbonate resin; Acrylic resins such as polymethyl (meth) acrylate and polyethyl (meth) acrylate; Styrene resins such as polystyrene and acrylonitrile-styrene copolymer; Polyolefin resins such as polyethylene, polypropylene, cyclo- or norbornene-structured polyolefins, ethylene-propylene copolymers; Vinyl chloride resin; Amide resins such as nylon and aromatic polyamide; Imide resin; Polyether sulfone type resin; Polyether ether ketone resin; A sulfided polyphenylene resin; Vinyl alcohol-based resin; Vinylidene chloride resins; Vinyl butyral resin; Allylate series resin; Polyoxymethylene type resin; Epoxy resin, and the like, and a film composed of the blend of the thermoplastic resin may also be used. Further, a film made of a thermosetting resin such as (meth) acrylic, urethane, acrylic urethane, epoxy, or silicone or a film made of an ultraviolet curable resin may be used.
본 발명의 일 실시형태에 따른 위상차 필름은 위상차층을 기재필름으로부터 박리하여 편광자에 전사할 수 있다. 따라서, 본 발명의 일 실시형태는 상기 위상차 필름으로부터 박리된 위상차층이 편광자의 적어도 일면에 전사된 편광판에 관한 것이다.The retardation film according to one embodiment of the present invention can peel off the retardation layer from the base film and transfer it to the polarizer. Accordingly, one embodiment of the present invention relates to a polarizing plate in which a retardation layer peeled from the retardation film is transferred onto at least one surface of the polarizer.
상기 편광자는 입사하는 자연광을 원하는 단일 편광상태(선편광 상태)로 바꿔주는 역할을 하는 광학필름으로서, 당해 분야에서 일반적으로 편광기능을 수행할 수 있는 것이면 특별히 한정하지는 않는다.The polarizer is an optical film that serves to convert incident natural light into a desired single polarization state (linear polarization state), and is not particularly limited as long as it can perform a polarization function in the art in general.
구체적으로, PVA(폴리비닐알코올) 필름에 요오드나 이색성 염료를 염색시키고, 이것을 일정방향으로 연신하여 제조된 편광자, 또는 투명기판 위에 편광기능을 가진 미세한 패턴의 전도성 격자들이 있고 격자의 골과 마루에 절연층이 코팅되어 있는 박판 편광판 등이 사용될 수 있다.Specifically, a polarizer produced by dyeing iodine or a dichroic dye to a PVA (polyvinyl alcohol) film, stretching the film in a certain direction, or a transparent substrate has a minute pattern of conductive gratings having a polarizing function, A thin plate polarizer in which an insulating layer is coated, or the like can be used.
또한, 편광판은 기계적으로 약한 편광자를 보호하기 위한 보호필름이 편광자의 일면 또는 양면에 추가될 수 있다. 보호필름은 수지의 종류에 따라 투습도가 다르며, 투명성, 기계적 강도, 열안정성, 수분차폐성, 등방성 등이 우수한 필름을 사용할 수 있다.Further, the polarizing plate may be added to one side or both sides of the polarizer with a protective film for protecting the mechanically weak polarizer. The protective film has a different moisture permeability depending on the type of resin, and a film excellent in transparency, mechanical strength, thermal stability, moisture barrier property, and isotropy can be used.
이외의 편광판의 구성 및 제조방법은 당해 분야에서 일반적으로 사용되는 것으로 특별히 한정하지는 않는다.
The configuration and manufacturing method of the other polarizing plate are not particularly limited as they are generally used in the related art.
본 발명에 따른 편광판은 액정표시장치, 유기발광소자 등의 화상표시장치에 적용 가능하다. 따라서, 본 발명의 일 실시형태는 상기 편광판을 포함하는 화상표시장치에 관한 것이다.
The polarizing plate according to the present invention is applicable to an image display apparatus such as a liquid crystal display apparatus and an organic light emitting element. Therefore, an embodiment of the present invention relates to an image display apparatus including the polarizer.
이하, 실시예, 비교예 및 실험예에 의해 본 발명을 보다 구체적으로 설명하고자 한다. 이들 실시예, 비교예 및 실험예는 오직 본 발명을 설명하기 위한 것으로, 본 발명의 범위가 이들에 국한되지 않는다는 것은 당업자에게 있어서 자명하다.
Hereinafter, the present invention will be described more specifically with reference to Examples, Comparative Examples and Experimental Examples. It should be apparent to those skilled in the art that these examples, comparative examples and experimental examples are only for illustrating the present invention, and the scope of the present invention is not limited thereto.
실시예 1: 위상차 필름의 제조 Example 1: Preparation of retardation film
약 100㎛의 폴리에틸렌테레프탈레이트(PET) 기재 상에 ROP-108 EXP115(Rolic사)을 1㎛ 두께로 도포한 후 노광(150mJ/cm2)하여 배향막층을 형성하였다. 그런 다음, LC242(BASF사)을 포함하는 코팅층 형성 조성물을 50㎛ 두께로 도포한 후 110℃에서 3분간 건조하여 용제를 제거한 후, 40㎽／㎠로 1분간 UV 조사에 의해 경화하여 위상차 필름을 제조하였다.
After applying the ROP-108 EXP115 (Rolic G) onto about 100㎛ of polyethylene terephthalate (PET) substrate with a thickness 1㎛ to form an alignment film layer exposed (150mJ / cm 2). Then, the composition for forming a coating layer containing LC242 (BASF) was applied to a thickness of 50 mu m and dried at 110 DEG C for 3 minutes to remove the solvent. The solution was cured by UV irradiation for 1 minute at 40 mW / .
실시예 2: 위상차 필름의 제조Example 2: Preparation of retardation film
실시예 1과 동일하게 실시하되, 배향막층을 500㎛ 두께로 도포하였다.
The alignment film layer was applied in the same manner as in Example 1, with a thickness of 500 mu m.
비교예 1: 위상차 필름의 제조Comparative Example 1: Production of retardation film
실시예 1과 동일하게 실시하되, 기재필름의 두께를 40㎛로 하여 위상차 필름을 제조하였다.
A retardation film was prepared in the same manner as in Example 1 except that the thickness of the base film was 40 占 퐉.
비교예 2: 위상차 필름의 제조Comparative Example 2: Production of retardation film
실시예 1과 동일하게 실시하되, 노광량을 200mW/cm2로 하여 위상차 필름을 제조하였다.
A retardation film was produced in the same manner as in Example 1 except that the exposure amount was 200 mW / cm 2 .
비교예 3: 위상차 필름의 제조Comparative Example 3: Production of retardation film
실시예 1과 동일하게 실시하되, 배향막층을 400nm 두께로 도포하고 노광량을 150mW/cm2로 하여 위상차 필름을 제조하였다.
A retardation film was prepared in the same manner as in Example 1 except that the orientation film layer was applied to a thickness of 400 nm and the exposure amount was set to 150 mW / cm 2 .
실험예 1: Experimental Example 1:
한 면에 보호필름을 포함한 편광자에 점착제를 접합한 후, 상기 실시예 및 비교예에서 수득한 위상차 필름을 액정 코팅층이 점착제 면을 마주보도록 접합하였다. 그런 다음 물성을 하기의 방법으로 측정하고, 그 결과를 하기 표 1에 나타내었다.
A pressure sensitive adhesive was bonded to a polarizer including a protective film on one side, and then the retardation film obtained in the above Examples and Comparative Examples was bonded such that the liquid crystal coating layer faced the pressure sensitive adhesive side. Then, physical properties were measured by the following method, and the results are shown in Table 1 below.
(1) 고속박리력 (1) High peel force
제조된 편광판을 25mm × 100mm의 크기로 절단하고, 만능인장시험기(UTM, Instron)를 사용하여 박리속도 10m/min 또는 30m/min, 박리각도 180˚로 위상차 면의 기재필름을 박리하여 고속박리력(a), (b)을 측정하였다(단위: N/25mm). 이때, 측정은 23℃, 50%RH의 조건 하에서 실시하였다.
The prepared polarizing plate was cut into a size of 25 mm x 100 mm and the base film of the retardation film was peeled off at a peeling speed of 10 m / min or 30 m / min using a universal tensile tester (UTM, Instron) (a) and (b) were measured (unit: N / 25 mm). At this time, measurement was carried out under conditions of 23 캜 and 50% RH.
(2) 저속박리력 (2) Low peel force
제조된 편광판을 25mm × 100mm의 크기로 절단하고, 만능인장시험기(UTM, Instron)를 사용하여 박리속도 300mm/min, 박리각도 180˚로 위상차 면의 기재필름을 박리하여 저속박리력(c)을 측정하였다(단위: N/25mm). 이때, 측정은 23℃, 50%RH의 조건 하에서 실시하였다.
The prepared polarizing plate was cut into a size of 25 mm x 100 mm and the base film of the phase difference plane was peeled off with a universal tensile tester (UTM, Instron) at a peeling speed of 300 mm / min and a peeling angle of 180 deg. (Unit: N / 25 mm). At this time, measurement was carried out under conditions of 23 캜 and 50% RH.
(3) a의 면내 박리력 편차 (3) The in-plane peeling force deviation of a
편광판의 왼쪽 끝, 중앙 및 오른쪽 끝에서 각각 고속박리력(a)를 측정한 후, 고속박리력(a)의 최대값(Max)과 최소값(Min)의 편차를 계산하였다.
The high-speed peeling force (a) was measured at the left end, the center and the right end of the polarizing plate, respectively, and then the deviation between the maximum value (Max) and the minimum value (Min) of the high-speed peeling force (a) was calculated.
(4) 박리불량 여부 (4) Poor detachment
편광판에서 기재필름을 박리하면서 박리불량 여부를 육안으로 확인하였다.
The peeling of the base film was peeled off from the polarizing plate to visually confirm the peeling failure.
300mm/minLow speed peel force (c)
300 mm / min
10m/minHigh-speed peel force (a)
10 m / min
30m/minHigh-speed peel force (b)
30 m / min
박리력 편차in-plane of a
Deviation of peeling force
(나끼와카레)Partial peeling
(Nabe and curry)
상기 표 1에서 보듯이, 상기 수학식 1 내지 5를 모두 만족하는 본 발명에 따른 실시예 1 내지 2의 위상차 필름은 박리불량 없이 박리가 잘 되었다. 반면, 상기 수학식 1 내지 5 중 어느 한 조건을 만족하지 않는 비교예 1 내지 3의 위상차 필름은 박리가 되지 않거나 부분 미박리되는 것을 확인하였다.
As shown in Table 1, the retardation films of Examples 1 and 2 according to the present invention satisfying all of the equations (1) to (5) were well peeled without peeling failure. On the other hand, it was confirmed that the retardation films of Comparative Examples 1 to 3 which did not satisfy any one of the above-mentioned expressions (1) to (5) did not peel off or partially peel off.
이상으로 본 발명의 특정한 부분을 상세히 기술하였는 바, 본 발명이 속한 기술분야에서 통상의 지식을 가진 자에게 있어서 이러한 구체적인 기술은 단지 바람직한 구현예일 뿐이며, 이에 본 발명의 범위가 제한되는 것이 아님은 명백하다. 본 발명이 속한 기술분야에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 본 발명의 범주 내에서 다양한 응용 및 변형을 행하는 것이 가능할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the invention. Do. It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims.
따라서, 본 발명의 실질적인 범위는 첨부된 특허청구범위와 그의 등가물에 의하여 정의된다고 할 것이다.Accordingly, the actual scope of the invention is defined by the appended claims and their equivalents.
Claims (5)
[수학식 1]
0.05N/25mm < a ≤ 0.15N/25mm
[수학식 2]
b < 0.2N/25mm
[수학식 3]
c < 0.15N/25mm
[수학식 4]
a의 면내 박리력 편차 ≤ 0.05
[수학식 5]
a < c x 2
상기 식에서,
a는 박리속도 10m/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 고속박리력이고,
b는 박리속도 30m/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 고속박리력이며,
c는 박리속도 300mm/min, 박리각도 180˚로 기재필름으로부터 위상차층을 박리할 때의 저속박리력이다.A retardation film comprising a retardation layer laminated on a base film, wherein the retardation film satisfies the following equations (1) to (5):
[Equation 1]
0.05 N / 25 mm < a < 0.15 N / 25 mm
&Quot; (2) "
b < 0.2N / 25mm
&Quot; (3) "
c < 0.15 N / 25 mm
&Quot; (4) "
In-plane peeling force deviation of a ≤ 0.05
&Quot; (5) "
a <cx 2
In this formula,
a is the high-speed peeling force when peeling the phase difference layer from the base film at a peeling speed of 10 m / min and a peeling angle of 180 °,
b is a high-speed peeling force when the phase difference layer is peeled off from the base film at a peeling speed of 30 m / min and a peeling angle of 180 °,
c is a low peeling force when the phase difference layer is peeled from the base film at a peeling speed of 300 mm / min and a peeling angle of 180 deg.