KR101845632B1 - Fire stop sealant and preparing method thereof - Google Patents

Fire stop sealant and preparing method thereof Download PDF

Info

Publication number
KR101845632B1
KR101845632B1 KR1020160145092A KR20160145092A KR101845632B1 KR 101845632 B1 KR101845632 B1 KR 101845632B1 KR 1020160145092 A KR1020160145092 A KR 1020160145092A KR 20160145092 A KR20160145092 A KR 20160145092A KR 101845632 B1 KR101845632 B1 KR 101845632B1
Authority
KR
South Korea
Prior art keywords
mixture
sealant
fire
adhesive
mixing
Prior art date
Application number
KR1020160145092A
Other languages
Korean (ko)
Inventor
지근배
이인식
Original Assignee
지근배
이인식
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 지근배, 이인식 filed Critical 지근배
Priority to KR1020160145092A priority Critical patent/KR101845632B1/en
Application granted granted Critical
Publication of KR101845632B1 publication Critical patent/KR101845632B1/en

Abstract

The present invention relates to a fireproof sealant and a method of preparing the same. More specifically, the present invention provides a method of preparing a fireproof sealant, comprising the steps of: mixing expanded graphite with a fire-retardant material to prepare a first mixture; mixing a thermoplastic resin with an adhesive to prepare a second mixture; dispersing an adhesive in water containing phosphoric acid or a phosphate dissolved therein and mixing the same with one selected from carbon fiber chop, glass fiber chop, or wire chop to prepare a third mixture; combining the first mixture, the second mixture, and the third mixture prepared above and adding an adhesive thereto to adjust a viscosity of a sealant; and pushing and injecting the sealant with an adjusted viscosity into a container, inside a vacuum tank into which nitrogen gas is injected by means of air or a screw. The fireproof sealant according to the present invention can be expanded to seal the space to efficiently block fire or toxic gases, in case of fire in parts of a building penetrated by a piping installation and an electronic installation connecting between walls, ceilings, a floor and a wall, and the like. In addition, as flying ashes may cause secondary fire once fire breaks out, the fireproof sealant once expanded due to the fire allows ashes to remain in place, and thus may be applied to seal the parts penetrated by cables, pipes, and ducts, and gaps inside various buildings.

Description

방화용 실런트 및 이의 제조방법{Fire stop sealant and preparing method thereof}FIELD OF THE INVENTION The present invention relates to a fire sealant and a method of manufacturing the same,

본 발명은 방화용 실런트 및 이의 제조방법에 관한 것이다.The present invention relates to a fire sealant and a method of manufacturing the same.

고층 빌딩 등과 같은 밀폐된 공간 내의 화재, 연기 및 가스는 생명에 상당한 위험을 줄 수 있다. 화재가 구조물의 바닥과 천정 사이의 공간에서 발생하는 경우, 화재와 이로 인한 연기 및 가스는 빌딩 내 다른 개방 공간, 특히 화재의 발생 지점 보다 높은 개방 공간으로 빈번하게 확산되는 경향이 있다.Fire, smoke and gas in enclosed spaces such as high-rise buildings can pose a significant risk to life. When a fire occurs in the space between the floor of the structure and the ceiling, the fire and the resulting smoke and gas tend to spread frequently to other open spaces in the building, especially to open spaces higher than the point of fire occurrence.

화재 발생 시 2차 피해를 줄이기 위한 방안으로 화재 시 탄화막을 형성할 수 있는 팽창흑연을 사용한 방화용 실런트가 제안되었으나, 표면성질에 따라 접착력은 상이하며 상대습도가 85%이상인 경우, 또는 5℃ 이하의 낮은 기온 등에서는 정상적인 기능을 발휘하기 어려울 뿐만 아니라, 화재 발생 시 방화용 실런트의 팽창성이 떨어져 화염 또는 유독가스의 침투 차단성이 떨어진다는 문제점이 있다.In order to reduce the secondary damage in case of fire, fireproof sealant using expanded graphite capable of forming a carbonized film in case of fire has been proposed. However, when the relative humidity is more than 85% or less than 5 ℃ It is not only difficult to exhibit the normal function at low temperatures of the flame, but also has the problem that the infiltration of the flame or toxic gas is poor due to the inflating ability of the flame retardant sealant when a fire occurs.

따라서, 건축물 내부 등에서 화재 발생 시 개구부를 통해 화재로부터 확산되는 피해를 줄일 수 있고, 인명피해를 최소화 할 수 있는 방화용 실런트의 연구 개발이 시급한 상황이다.Therefore, it is urgent to research and develop fire-retardant sealant that can reduce the damage from the fire through the opening when a fire occurs inside the building, and minimize the damage to people.

중국공개특허 제105482742호Chinese Patent No. 105482742

본 발명의 목적은 건축물의 벽과 벽 사이에 개구부를 통해 화재로부터 확산되는 피해가 없도록 화염이나 유독가스 등을 차단하는 방화제품을 제공하는 데에 있다.It is an object of the present invention to provide an arsonized product that shields flames, toxic gases, and the like from being diffused from a fire through an opening between a wall and a wall of a building.

상기 목적을 달성하기 위하여, 본 발명은 전체 100 중량부에 대해, 팽창흑연 50 내지 55 중량부, 난연재 5 내지 10 중량부, 열가소성 수지 10 내지 15 중량부, 탄소섬유 촙 또는 와이어 촙 15 내지 20 중량부, 인산 또는 인산염 5 내지 6 중량부, 및 접착제 15 내지 20 중량부를 포함하는, 방화용 실런트 조성물을 제공한다.In order to achieve the above object, the present invention provides a thermoplastic resin composition comprising 50 to 55 parts by weight of expanded graphite, 5 to 10 parts by weight of a flame retardant, 10 to 15 parts by weight of a thermoplastic resin, 15 to 20 parts by weight of carbon fiber or wire, 5 to 6 parts by weight of phosphoric acid or phosphoric acid, and 15 to 20 parts by weight of an adhesive.

또한 본 발명은 팽창흑연과 난연재를 혼합하여 제1혼합물을 준비하는 단계; 열가소성 수지와 접착제를 혼합하여 제2혼합물을 준비하는 단계; 인산 또는 인산염 중 어느 하나를 용해시킨 물에 접착제를 분산시킨 후 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙 중 어느 하나를 혼합하여 제3혼합물을 준비하는 단계; 상기 준비된 제1혼합물, 제2혼합물, 및 제3혼합물을 혼합한 후 접착제를 첨가하여 실런트의 점성을 조절하는 단계; 및 상기 점성이 조절된 실런트를 질소 가스가 주입된 진공탱크에서 에어 또는 스크류로 밀어내어 용기에 주입하는 단계를 포함하는, 방화용 실런트 제조방법을 제공한다.The present invention also relates to a method for producing a flame retardant, comprising: preparing a first mixture by mixing expandable graphite and a flame retardant; Preparing a second mixture by mixing a thermoplastic resin and an adhesive; Dispersing an adhesive in water in which any one of phosphoric acid and phosphate is dissolved, and then preparing a third mixture by mixing any one of carbon fiber, glass fiber and wire; Mixing the prepared first mixture, second mixture, and third mixture, and then adding an adhesive to adjust the viscosity of the sealant; And pushing the viscous controlled sealant into air or a screw in a vacuum tank filled with nitrogen gas and injecting the sealant into the container.

또한 본 발명은 상기 제조방법에 의해 제조된 방화용 실런트를 제공한다.The present invention also provides a fire sealant manufactured by the above-described method.

본 발명에 따른 방화용 실런트는 건축물의 벽과 벽, 천장과 천장, 바닥과 벽 등을 이어주는 배관시설 및 전기 설비가 관통되는 부분에 화재 발생 시 팽창되어 공간을 밀폐시킬 수 있어 화염 또는 유독가스를 효율적으로 차단시킬 수 있다. 또한, 화재 발생 시 발화하면서 재가 날아다니면 2차 화재가 위험하므로 발화 후에 화재로부터 팽창 후에도 재가 그 자리에 유지 될 수 있어, 케이블, 파이프, 덕트 관통부위 밀폐 및 각종 건축물 내부의 틈새에 적용할 수 있다.The fire sealant according to the present invention can expand the fire or toxic gas when the fire occurs at a portion where the wall and the wall, the ceiling and the ceiling of the building, the ceiling, the floor, It can be effectively blocked. In addition, since fire is dangerous if the ash is blown while fire is generated in case of fire, ashes can stay in place after fire from fire after ignition, and it can be applied to sealing of penetrating parts of cables, pipes, ducts and gaps in various buildings .

도 1은 콘크리트 벽 또는 콘크리트 바닥을 통과하는 PVC 파이프, 스틸 파이프, 덕트, 또는 케이블 트레이를 콘크리트 몰탈과 방화용 실런트로 코킹하여 밀페시킨 단면도이다.1 is a sectional view of a PVC pipe, a steel pipe, a duct, or a cable tray passing through a concrete wall or a concrete floor by caulking with a concrete mortar and a fireproof sealant.

이하, 본 발명을 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.

본 발명의 발명자들은 탄소섬유 촙 또는 와이어 촙을 첨가하여 제조된 방화용 실런트를 건축물의 벽과 벽, 천장과 천장, 바닥과 벽 등을 이어주는 배관시설 및 전기 설비가 관통되는 연결 부분에 적용할 경우, 화재 발생 시 화염 또는 유독가스 차단성을 향상시킬 수 있음을 밝혀내어 본 발명을 완성하였다.The inventors of the present invention have found that when a fire sealant manufactured by adding carbon fiber or wire rope is applied to a connecting portion through which a piping facility for connecting walls and walls of a building, a ceiling and a ceiling, And it is possible to improve flame or toxic gas barrier property in the event of a fire, thereby completing the present invention.

본 발명은 전체 100 중량부에 대해, 팽창흑연 50 내지 55 중량부, 난연재 5 내지 10 중량부, 열가소성 수지 10 내지 15 중량부, 탄소섬유 촙 또는 와이어 촙 15 내지 20 중량부, 인산 또는 인산염 5 내지 6 중량부, 및 접착제 15 내지 20 중량부를 포함하는, 방화용 실런트 조성물을 제공한다.The present invention relates to a rubber composition comprising 50 to 55 parts by weight of expanded graphite, 5 to 10 parts by weight of a flame retardant, 10 to 15 parts by weight of a thermoplastic resin, 15 to 20 parts by weight of a carbon fiber or a wire, 6 parts by weight, and 15-20 parts by weight of an adhesive.

상기 팽창흑연은 50 메쉬 내지 250 메쉬의 크기를 가질 수 있으며, 이에 제한되는 것은 아니다.The expanded graphite may have a size of 50 mesh to 250 mesh, but is not limited thereto.

상기 팽창흑연이 50 메쉬 미만의 크기를 가질 경우 팽창저하의 문제점이 발생할 수 있으며, 또한 상기 팽창흑연이 250 메쉬를 초과하는 크기를 가질 경우 과 팽창후 날림현상과 같은 문제점을 야기할 수 있는 바, 상기 팽창흑연은 50 메쉬 내지 250 메쉬의 크기를 가지는 것이 바람직하며, 특히 화염 접촉을 고려하였을 때, 상기 팽창흑연은 80 메쉬 내지 150 메쉬의 크기를 가지는 것이 보다 바람직하다.If the expanded graphite has a size of less than 50 mesh, it may cause a problem of reduction in expansion. Further, if the expanded graphite has a size exceeding 250 mesh, it may cause problems such as expansion after expansion. The expanded graphite preferably has a size of 50 mesh to 250 mesh, and more preferably, the expanded graphite has a size of 80 mesh to 150 mesh, considering flame contact.

상기 난연재는 수산화알루미늄, 수산화마그네슘, 및 인계난연재로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The flame retardant may be any one selected from the group consisting of aluminum hydroxide, magnesium hydroxide, and phosphorus flame retardant, but is not limited thereto.

상기 인계난연재는 트리스-2-클로로에틸포스페이트, 트리스-2-클로로프로필포스페이트, 이소프로필페닐디페닐포스페이트, 트리크레실포스페이트, 트리페닐포스페이트, 트리에틸포스페이트, 멜라민포스페이트 및 암모늄포스페이트로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The phosphorus flame retardant is selected from the group consisting of tris-2-chloroethyl phosphate, tris-2-chloropropyl phosphate, isopropylphenyl diphenyl phosphate, tricresyl phosphate, triphenyl phosphate, triethyl phosphate, melamine phosphate and ammonium phosphate But the present invention is not limited thereto.

상기 열가소성 수지는 분말형(Powder type) 또는 과립형(Granule type) 중 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The thermoplastic resin may be either a powder type or a granule type, but is not limited thereto.

상기 열가소성 수지는 핫멜트 수지로서, 열에 녹아서 접착제가 되는 특성을 포함한다.The thermoplastic resin is a hot-melt resin, and includes properties of being melted to become an adhesive.

상기 열가소성 수지는 폴리에틸렌(Polyethylene; 이하 'PE'), 에틸렌초산비닐(Ethylene-vinyl acetate; 이하 'EVA'), 폴리프로필렌(Polypropylene; 이하 'PP'), 폴리아마이드(Polyamide; 이하 'PA'), 및 폴리에스터(Polyester)로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The thermoplastic resin may be selected from the group consisting of polyethylene (PE), ethylene-vinyl acetate (EVA), polypropylene (PP), polyamide (PA) , And polyester (polyester), but the present invention is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 폴리프로필렌(Polypropylene), 폴리부틸렌테레프탈렌(polybutylene-terephthalate), 폴리아마이드(Polyamide), 석고(gypsum) 및 나일론(Nylon)으로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The carbon fiber, glass fiber or wire can be selected from the group consisting of polypropylene, polybutylene-terephthalate, polyamide, gypsum and nylon. But is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 1 내지 15 mm의 평균 길이를 가질 수 있으며, 이에 제한되는 것은 아니다.The carbon fiber, glass fiber or wire can have an average length of 1 to 15 mm, but is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙이 1 mm 미만의 평균 길이를 가질 경우 재가 날리는 문제점이 발생할 수 있으며, 또한 상기 탄소섬유 촙 또는 와이어 촙이 15 mm를 초과하는 평균 길이를 가질 경우 생산과정에서 분산이 안되는 문제점을 야기할 수 있는 바, 상기 탄소섬유 촙 또는 와이어 촙은 1 내지 15 mm의 평균 길이를 가지는 것이 바람직하며, 특히 방화용 실런트의 밀폐성을 고려하였을 때, 상기 탄소섬유 촙 또는 와이어 촙은 7 내지 12 mm의 평균 길이를 가지는 것이 보다 바람직하다.If the carbon fibers, glass fibers or wire rods have an average length of less than 1 mm, there may be a problem of ash flying, and if the carbon fiber rods or wire rods have an average length exceeding 15 mm, It is preferable that the carbon fiber wire or the wire wire has an average length of 1 to 15 mm. In particular, when considering the hermeticity of the sealant for the fire, the carbon fiber wire or the wire wire, It is more preferable that the average length has a length of 7 to 12 mm.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 5 내지 30 ㎛의 평균 두께를 가질 수 있으며, 이에 제한되는 것은 아니다.The carbon fiber, glass fiber or wire can have an average thickness of 5 to 30 mu m, but is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙이 5 ㎛ 미만의 평균 두께를 가질 경우 고열에 연소되는 문제점이 발생할 수 있으며, 또한 상기 탄소섬유, 유리섬유 촙 촙 또는 와이어 촙이 30 ㎛를 초과하는 평균 두께를 가질 경우 생산성 저하 및 불규칙 배합과 같은 문제점을 야기할 수 있는 바, 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 5 내지 30 ㎛의 평균 두께를 가지는 것이 바람직하며, 특히 생산성 및 방화용 밀폐성을 고려하였을 때, 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 10 내지 25 ㎛의 평균 두께를 가지는 것이 보다 바람직하다.If the carbon fiber, glass fiber or wire fiber has an average thickness of less than 5 탆, it may cause a problem of burning due to high temperature, and the carbon fiber, glass fiber fiber or wire fiber may have an average It is preferable that the carbon fiber glass, the glass fiber glass or the wire glass have an average thickness of 5 to 30 탆. In particular, the glass fiber glass or the wire glass preferably has a productivity and an air tightness It is more preferable that the carbon fiber glass, glass fiber glass or wire glass have an average thickness of 10 to 25 탆.

상기 인산염은 트리크레실 포스페이트(Tricresyl phosphate), 트리메틸 포스페이트(Trimethyl phosphate), 트리에틸 포스페이트(Triethyl phosphate), 트리페닐 포스페이트(Triphenyl phosphate), 및 트리크실레닐 포스페이트(Trixylenyl phosphate)로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The phosphate is selected from the group consisting of Tricresyl phosphate, Trimethyl phosphate, Triethyl phosphate, Triphenyl phosphate, and Trixylenyl phosphate. But the present invention is not limited thereto.

상기 접착제는 실리콘 접착제, 아크릴 접착제, 및 폴리우레탄 접착제로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The adhesive may be any one selected from the group consisting of a silicone adhesive, an acrylic adhesive, and a polyurethane adhesive, but is not limited thereto.

또한 본 발명은 팽창흑연과 난연재를 혼합하여 제1혼합물을 준비하는 단계; 열가소성 수지와 접착제를 혼합하여 제2혼합물을 준비하는 단계; 인산 또는 인산염 중 어느 하나를 용해시킨 물에 접착제를 분산시킨 후 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙 중 어느 하나를 혼합하여 제3혼합물을 준비하는 단계; 상기 준비된 제1혼합물, 제2혼합물, 및 제3혼합물을 혼합한 후 접착제를 첨가하여 실런트의 점성을 조절하는 단계; 및 상기 점성이 조절된 실런트를 질소 가스가 주입된 진공탱크에서 에어 또는 스크류로 밀어내어 용기에 주입하는 단계를 포함하는, 방화용 실런트 제조방법을 제공한다.The present invention also relates to a method for producing a flame retardant, comprising: preparing a first mixture by mixing expandable graphite and a flame retardant; Preparing a second mixture by mixing a thermoplastic resin and an adhesive; Dispersing an adhesive in water in which any one of phosphoric acid and phosphate is dissolved, and then preparing a third mixture by mixing any one of carbon fiber, glass fiber and wire; Mixing the prepared first mixture, second mixture, and third mixture, and then adding an adhesive to adjust the viscosity of the sealant; And pushing the viscous controlled sealant into air or a screw in a vacuum tank filled with nitrogen gas and injecting the sealant into the container.

상기 제1혼합물을 준비하는 단계는 팽창흑연과 난연재를 10 : 3의 중량비로 혼합할 수 있으며, 이에 제한되는 것은 아니다.The step of preparing the first mixture may include mixing the expanded graphite and the flame retardant at a weight ratio of 10: 3, but is not limited thereto.

상기 팽창흑연과 난연재를 10 : 3 미만의 중량비로 혼합할 경우, 흑연과 흑연 사이의 공간이 커서 접착제가 많으면 밀폐성이 저하될 수 있으며, 또한 팽창흑연과 난연재를 10 : 3을 초과하는 중량비로 혼합할 경우 팽창 둔화를 야기할 수 있는 바, 화재 시 화염 번짐을 고려하였을 때, 팽창흑연과 난연재를 10 : 3 중량비로 혼합하는 것이 바람직하다.When the expanded graphite and the flame retardant are mixed at a weight ratio of less than 10: 3, the space between the graphite and the graphite is large, and if the amount of the adhesive is large, the airtightness may be deteriorated. It is preferable to mix the expanded graphite and the flame retardant in a weight ratio of 10: 3 when flame spreading is considered in a fire.

상기 제2혼합물을 준비하는 단계는 열가소성 수지와 접착제를 1 : 2의 중량비로 혼합할 수 있으며, 이에 제한되는 것은 아니다.The step of preparing the second mixture may be performed by mixing the thermoplastic resin and the adhesive in a weight ratio of 1: 2, but is not limited thereto.

상기 열가소성 수지와 접착제를 1 : 2 미만의 중량비로 혼합할 경우 접착성이 저하될 수 있으며, 또한 상기 열가소성 수지와 접착제를 1 : 2를 초과하는 중량비로 혼합할 경우 난연성이 저하 될 수 있는 바, 난연성을 고려하였을 때, 열가소성 수지와 접착제를 1 : 2의 중량비로 혼합하는 것이 바람직하다.When the thermoplastic resin and the adhesive are mixed at a weight ratio of less than 1: 2, the adhesiveness may be deteriorated. When the thermoplastic resin and the adhesive are mixed at a weight ratio exceeding 1: 2, the flame retardancy may be lowered. When the flame retardancy is taken into account, it is preferable to mix the thermoplastic resin and the adhesive in a weight ratio of 1: 2.

상기 접착제는 실리콘 접착제, 아크릴 접착제, 및 폴리우레탄 접착제로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The adhesive may be any one selected from the group consisting of a silicone adhesive, an acrylic adhesive, and a polyurethane adhesive, but is not limited thereto.

상기 팽창흑연은 50 메쉬 내지 250 메쉬의 크기를 가질 수 있으며, 이에 제한되는 것은 아니다.The expanded graphite may have a size of 50 mesh to 250 mesh, but is not limited thereto.

상기 팽창흑연이 50 메쉬 미만의 크기를 가질 경우 팽창저하의 문제점이 발생할 수 있으며, 또한 상기 팽창흑연이 250 메쉬를 초과하는 크기를 가질 경우 과 팽창후 날림현상과 같은 문제점을 야기할 수 있는 바, 상기 팽창흑연은 50 메쉬 내지 250 메쉬의 크기를 가지는 것이 바람직하며, 특히 화염 접촉을 고려하였을 때, 상기 팽창흑연은 80 메쉬 내지 150 메쉬의 크기를 가지는 것이 보다 바람직하다.If the expanded graphite has a size of less than 50 mesh, it may cause a problem of reduction in expansion. Further, if the expanded graphite has a size exceeding 250 mesh, it may cause problems such as expansion after expansion. The expanded graphite preferably has a size of 50 mesh to 250 mesh, and more preferably, the expanded graphite has a size of 80 mesh to 150 mesh, considering flame contact.

상기 난연재는 수산화알루미늄, 수산화마그네슘, 및 인계난연재로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The flame retardant may be any one selected from the group consisting of aluminum hydroxide, magnesium hydroxide, and phosphorus flame retardant, but is not limited thereto.

상기 인계난연재는 트리스-2-클로로에틸포스페이트, 트리스-2-클로로프로필포스페이트, 이소프로필페닐디페닐포스페이트, 트리크레실포스페이트, 트리페닐포스페이트, 트리에틸포스페이트, 멜라민포스페이트 및 암모늄포스페이트로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The phosphorus flame retardant is selected from the group consisting of tris-2-chloroethyl phosphate, tris-2-chloropropyl phosphate, isopropylphenyl diphenyl phosphate, tricresyl phosphate, triphenyl phosphate, triethyl phosphate, melamine phosphate and ammonium phosphate But the present invention is not limited thereto.

상기 열가소성 수지는 핫멜트 수지로서, 열에 녹아서 접착제가 되는 특성을 포함한다.The thermoplastic resin is a hot-melt resin, and includes properties of being melted to become an adhesive.

상기 열가소성 수지는 분말형(Powder type) 또는 과립형(Granule type) 중 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The thermoplastic resin may be either a powder type or a granule type, but is not limited thereto.

상기 열가소성 수지는 폴리에틸렌(Polyethylene), 에틸렌초산비닐(Ethylene-vinyl acetate), 폴리프로필렌(Polypropylene), 폴리아마이드(Polyamide), 및 폴리에스터(Polyester)로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The thermoplastic resin may be any one selected from the group consisting of polyethylene, ethylene-vinyl acetate, polypropylene, polyamide, and polyester. It is not.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 폴리프로필렌(Polypropylene), 폴리부틸렌테레프탈렌(polybutylene-terephthalate), 폴리아마이드(Polyamide), 및 나일론(Nylon)으로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The carbon fiber, glass fiber or wire can be any one selected from the group consisting of polypropylene, polybutylene-terephthalate, polyamide, and nylon. , But is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 1 내지 15 mm의 평균 길이를 가질 수 있으며, 이에 제한되는 것은 아니다.The carbon fiber, glass fiber or wire can have an average length of 1 to 15 mm, but is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙이 1 mm 미만의 평균 길이를 가질 경우 재가 날리는 문제점이 발생할 수 있으며, 또한 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙이 15 mm를 초과하는 평균 길이를 가질 경우 생산과정에서 분산이 안되는 문제점을 야기할 수 있는 바, 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 1 내지 15 mm의 평균 길이를 가지는 것이 바람직하며, 특히 방화용 실런트 테이프의 밀폐성을 고려하였을 때, 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 7 내지 12 mm의 평균 길이를 가지는 것이 보다 바람직하다.If the average length of the carbon fibers, glass fibers or wire rods is less than 1 mm, the carbon fibers, glass fibers or wire rods may have an average length exceeding 15 mm It is preferable that the carbon fiber glass, glass fiber glass or wire glass have an average length of 1 to 15 mm. In particular, considering the airtightness of the sealant tape for fireproofing, It is more preferable that the carbon fiber glass, glass fiber glass or wire glass has an average length of 7 to 12 mm.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 5 내지 30 ㎛의 평균 두께를 가질 수 있으며, 이에 제한되는 것은 아니다.The carbon fiber, glass fiber or wire can have an average thickness of 5 to 30 mu m, but is not limited thereto.

상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙이 5 ㎛ 미만의 평균 두께를 가질 경우 고열에 연소되는 문제점이 발생할 수 있으며, 또한 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙이 30 ㎛를 초과하는 평균 두께를 가질 경우 생산성 저하 및 불규칙 배합과 같은 문제점을 야기할 수 있는 바, 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 5 내지 30 ㎛의 평균 두께를 가지는 것이 바람직하며, 특히 생산성 및 방화용 밀폐성을 고려하였을 때, 상기 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 10 내지 25 ㎛의 평균 두께를 가지는 것이 보다 바람직하다.If the carbon fiber glass, glass fiber glass or wire glass has an average thickness of less than 5 탆, there may be a problem of burning due to high temperature, and the carbon fiber glass, glass fiber glass or wire glass may have an average It is preferable that the carbon fiber glass, the glass fiber glass or the wire glass have an average thickness of 5 to 30 탆. In particular, the glass fiber glass or the wire glass preferably has a productivity and an air tightness It is more preferable that the carbon fiber glass, glass fiber glass or wire glass have an average thickness of 10 to 25 탆.

상기 인산염은 트리크레실 포스페이트(Tricresyl phosphate), 트리메틸 포스페이트(Trimethyl phosphate), 트리에틸 포스페이트(Triethyl phosphate), 트리페닐 포스페이트(Triphenyl phosphate), 및 트리크실레닐 포스페이트(Trixylenyl phosphate)로 이루어진 군에서 선택된 어느 하나일 수 있으며, 이에 제한되는 것은 아니다.The phosphate is selected from the group consisting of Tricresyl phosphate, Trimethyl phosphate, Triethyl phosphate, Triphenyl phosphate, and Trixylenyl phosphate. But the present invention is not limited thereto.

상기 인산 또는 인산염 중 어느 하나를 용해시킨 물의 온도는 40℃ 내지 50℃일 수 있다.The temperature of the water in which the phosphoric acid or the phosphate is dissolved may be 40 to 50 ° C.

상기 물의 온도가 40℃ 내지 50℃일 경우, 인산 또는 인산염 중 어느 하나를 물에 용해시킬 때, 우수한 용해성을 나타낼 수 있으며, 접착력을 상승시킬 수 있는 효과가 있다.When the temperature of the water is in the range of 40 ° C to 50 ° C, when either of the phosphoric acid or the phosphate is dissolved in water, it can exhibit excellent solubility and increase the adhesive strength.

상기 실런트의 점성을 조절하는 단계는 준비된 제1혼합물, 제2혼합물, 및 제3혼합물을 6 : 1: 3의 중량비로 혼합한 후 전체 100 중량부에 대해 15 내지 20 중량부의 접착제를 첨가할 수 있으며, 이에 제한되는 것은 아니다.The viscosity of the sealant may be adjusted by mixing the prepared first mixture, second mixture, and third mixture in a weight ratio of 6: 1: 3 and then adding 15 to 20 parts by weight of adhesive to 100 parts by weight of the total mixture But is not limited thereto.

상기 실런트의 점성을 조절할 때 제1혼합물, 제2혼합물, 및 제3혼합물을 6 : 1: 3의 중량비를 벗어날 경우 밀폐성 저하와 같은 문제점이 발생할 수 있다.When the viscosity of the sealant is controlled, if the weight ratio of the first mixture, the second mixture, and the third mixture is out of the range of 6: 1: 3, problems such as lowering of air tightness may occur.

상기 전체 100 중량부에 대해 접착제가 15 내지 20 중량부의 범위를 벗어날 경우 접착력 저하와 같은 문제점이 발생할 수 있다.If the adhesive is out of the range of 15 to 20 parts by weight based on 100 parts by weight of the total amount, problems such as deterioration of adhesive strength may occur.

또한 본 발명은 상기 제조방법에 따라 제조된 것을 특징으로 하는, 방화용 실런트를 제공한다.Further, the present invention provides a fire sealant characterized in that it is produced according to the above-mentioned production method.

이하, 하기 실시예에 의해 본 발명을 보다 상세하게 설명한다. 다만, 이러한 실시예에 의해 본 발명이 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to the following examples. However, the present invention is not limited by these examples.

<실시예 1> 방화용 실런트 제조&Lt; Example 1 > Manufacture of fireproof sealant

1. 재료의 준비1. Preparation of materials

80 mesh의 팽창흑연(Expanding graphite)은 EVERGREEN INDUSTRY CO. LTD(중국)로부터 구입하였다.Expanding graphite of 80 mesh is available from EVERGREEN INDUSTRY CO. LTD (China).

열가소성 수지는 PA를 준비하였고, 탄소섬유 촙, 유리섬유 촙 또는 와이어 촙은 7 ~ 12 mm의 평균 길이, 및 7 ㎛ ~ 15 ㎛의 평균 두께를 갖는 GYBSOM(HEBEI YUNIU FIBERGLASS MANUFACTURING CO.LTD, 중국)을 준비하였다.GyBSOM (HEBEI YUNIU FIBERGLASS MANUFACTURING CO.LTD, China), which has an average length of 7 to 12 mm and an average thickness of 7 to 15 탆, is used as the thermoplastic resin, and the carbon fiber, glass fiber, Were prepared.

또한, 실리콘 접착제(KCC, 한국), 아크릴 접착제(노루페인트), 및 폴리우레탄 접착제(노루페인트)를 준비하였고, 인산염은 트리크레실 포스페이트를 준비하였다.In addition, a silicone adhesive (KCC, Korea), an acrylic adhesive (a hero paint), and a polyurethane adhesive (a herring paint) were prepared, and a phosphate tricresyl phosphate was prepared.

2. 방화용 실런트 제조2. Manufacture of fireproof sealants

상기 준비된 팽창흑연 40 g과 수산화알루미늄 12 g을 10 : 3의 중량비로 혼합하여 제1혼합물을 준비하였다.40 g of the prepared expanded graphite and 12 g of aluminum hydroxide were mixed at a weight ratio of 10: 3 to prepare a first mixture.

상기 준비된 열가소성수지(핫멜트)인 PA 10 g과 접착제 중에서 실리콘 접착제, 아크릴 접착제, 또는 폴리우레탄 접착제 중 어느 하나의 접착제 20 g을 1 : 2의 중량비로 혼합하여 제2혼합물을 준비하였다.A second mixture was prepared by mixing 10 g of the thermoplastic resin (hot melt) prepared above with 20 g of a silicone adhesive, acrylic adhesive, or polyurethane adhesive in a weight ratio of 1: 2 in an adhesive.

트리크레실 포스페이트 5 g을 40℃ 내지 50℃의 물에 용해시키고 실리콘 접착제, 아크릴 접착제, 또는 폴리우레탄 접착제 중 어느 하나의 접착제 17 g과 혼합하여 분산시킨 후, GYPSUM CHOP 15 g을 혼합시켜 제3혼합물을 준비하였다.5 g of tricresyl phosphate was dissolved in water at 40 ° C to 50 ° C and mixed with 17 g of any one of a silicone adhesive, an acrylic adhesive and a polyurethane adhesive and dispersed. Then, 15 g of GYPSUM CHOP was mixed to prepare a third The mixture was prepared.

상기 제1혼합물, 제2혼합물, 및 제3혼합물을 6 : 1 : 3의 중량비로 혼합한 후 전체 100 중량부에 대해 15 중량부의 실리콘 접착제, 아크릴 접착제, 또는 폴리우레탄 접착제 중 어느 하나의 접착제를 첨가하여 점성이 조절된 실런트를 제조하였다.The first mixture, the second mixture, and the third mixture were mixed at a weight ratio of 6: 1: 3, and then 15 parts by weight of an adhesive of silicone adhesive, acrylic adhesive, or polyurethane adhesive To prepare a viscous controlled sealant.

상기 점성이 조절된 실런트를 질소 가스가 주입된 진공탱크에서 에어 또는 스크류로 밀어내어 용기에 주입하여 방화용 실런트를 제조하였다.The viscous controlled sealant was pushed out of a vacuum tank filled with nitrogen gas into air or a screw and injected into a container to prepare a fire sealant.

<실시예 2> 방화용 실런트 제조&Lt; Example 2 > Production of fire retardant sealant

12 mm의 길이, 12 ㎛의 두께인 GYPSUM CHOP을 혼합시켜 제3혼합물을 준비한 것을 제외하고는, 상기 실시예 1과 동일한 조건이었다.Except that a third mixture was prepared by mixing GYPSUM CHOP having a length of 12 mm and a thickness of 12 탆.

<비교예 1> 방화용 실런트 제조&Lt; Comparative Example 1 > Production of fire retardant sealant

팽창흑연과 수산화알루미늄의 혼합비율이 7 : 1인 것을 제외하고는, 상기 실시예 1과 동일한 조건이었다.The same conditions as in Example 1 were obtained except that the mixing ratio of expanded graphite to aluminum hydroxide was 7: 1.

<비교예 2> 방화용 실런트 제조&Lt; Comparative Example 2 > Production of fire retardant sealant

1.5 mm의 길이, 200 ㎛의 두께인 GYPSUM CHOP을 혼합시켜 제3혼합물을 준비한 것을 제외하고는, 상기 실시예 1과 동일한 조건이었다.Except that the third mixture was prepared by mixing GYPSUM CHOP having a length of 1.5 mm and a thickness of 200 mu m to prepare a third mixture.

<비교예 3> 방화용 실런트 제조&Lt; Comparative Example 3 > Production of fire retardant sealant

탄소섬유 촙 또는 와이어 촙 대신에 아라미드 촙을 사용한 것을 제외하고는, 상기 실시예 1과 동일한 조건이었다.The same conditions as in Example 1 were used except that aramid fiber was used instead of carbon fiber fiber or wire fiber.

<실험예 1> 화염 및 유독가스 차단성 평가<Experimental Example 1> Evaluation of flame and toxic gas barrier property

상기 실시예 1 및 실시예 2에 의해 제조된 방화용 실런트와 비교예 1 내지 비교예 3에 의해 제조된 방화용 실런트의 화염 차단성을 평가하였다.The flame barrier properties of the fire sealant produced by the fire sealants prepared in Examples 1 and 2 and the fire sealants prepared in Comparative Examples 1 to 3 were evaluated.

각각 제조된 방화용 실런트를 케이블 트레이에 코킹한 후 100 ℃/min의 승온속도로 400℃까지 직접 연소시켰다.Each manufactured fire sealant was caulked to a cable tray and then directly burned to 400 ° C at a heating rate of 100 ° C / min.

구체적으로, 도 1을 참조하면, 콘크리트 벽 또는 콘크리트 바닥(2)을 통과하는 케이블 트레이(1)를 콘크리트 몰탈(4)과 방화용 실런트(3)로 코킹하여 밀페시켰다. 1, a cable tray 1 passing through a concrete wall or a concrete floor 2 is caulked and dumped by a concrete mortar 4 and a fire sealant 3.

상기 실시예 1 및 실시예 2에 의해 제조된 방화용 실런트를 케이블 트레이(1)에 적용할 경우, 실시예 1 및 실시예 2에 의해 제조된 방화용 실런트(3)가 팽창하여 공간을 팽창시킴으로써 화염 차단율 및 유독가스 침투율이 낮음을 확인하였다.When the fire sealant manufactured by the first and second embodiments is applied to the cable tray 1, the fire sealant 3 manufactured by the first and second embodiments expands and expands the space It was confirmed that the flame blocking rate and toxic gas permeability were low.

또한, 상기 비교예 1 내지 비교예 3에 의해 제조된 방화용 실런트를 케이블 트레이에 적용하여 화염 및 유독가스 차단성 평가를 수행하였다. 상기 비교예 1 내지 비교예 3에 의해 제조된 방화용 실런트(3)는 팽창하지 못하여 공간을 메꾸어 주지 못하는 문제점 때문에 플라스틱 또는 고무재질로 이루어진 케이블 트레이(1)에 화재가 발생하여 이로 인하여 유독가스가 배출됨을 확인하였다.In addition, by applying the fire-retardant sealant manufactured in Comparative Examples 1 to 3 to a cable tray, Evaluation was carried out. The fire sealant 3 produced by the comparative examples 1 to 3 can not inflate and can not fill the space, so that a fire is generated in the cable tray 1 made of plastic or rubber material, .

<실험예 2> <Experimental Example 2>

도 1을 참조하면, 상부층과 하부층을 연결하는 부위에 실시예 1 내지 실시예 3에 의해 제조된 방화용 실런트(3)를 처리할 경우, 방화용 실런트(3)가 팽창하여 공간을 밀폐시킴으로써 화염 차단율이 낮아 상부층에 연결되는 PVC 파이프(1)에 화재가 확산되지 않기 때문에 2차 피해의 발생정도가 크지 않았다. 반면, 상부층과 하부층을 연결하는 부위에 비교예 1 내지 비교예 3에 의해 제조된 방화용 실런트(3)를 처리할 경우, 상부층에 연결되는 PVC 파이프(1)는 화재 발생 후 연기와 더불어 유독가스가 배출됨을 확인하였다.Referring to FIG. 1, when the fire sealant 3 produced according to the first to third embodiments is treated at a portion connecting the upper layer and the lower layer, the fire sealant 3 expands to seal the space, Since the cut-off rate was low, the fire did not spread to the PVC pipe (1) connected to the upper layer, so the occurrence of secondary damage was not large. On the other hand, when the fire sealant 3 produced in Comparative Examples 1 to 3 is treated at a portion connecting the upper layer and the lower layer, the PVC pipe 1 connected to the upper layer is exposed to toxic gas .

이상과 같이, 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술 사상과 아래에 기재될 청구범위의 균등 범위 내에서 다양한 수정 및 변형이 가능함은 물론이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments. It is to be understood that various modifications and changes may be made without departing from the scope of the appended claims.

(1): PVC 파이프, 스틸 파이프, 덕트, 또는 케이블 트레이
(2): 콘크리트 벽 또는 콘크리트 바닥
(3): 방화용 실런트
(4): 콘크리트 몰탈(1): PVC pipe, steel pipe, duct, or cable tray
(2): Concrete wall or concrete floor
(3): Fire sealant
(4): Concrete mortar

Claims (14)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 팽창흑연과 난연재를 혼합하여 제1혼합물을 준비하는 단계;
열가소성 수지와 접착제를 혼합하여 제2혼합물을 준비하는 단계;
인산 또는 인산염 중 어느 하나를 용해시킨 물에 접착제를 분산시킨 후 7 내지 12 mm의 평균길이 및 10 내지 25 ㎛의 평균 두께를 갖는 석고(gypsum) 촙을 혼합하여 제3혼합물을 준비하는 단계;
상기 준비된 제1혼합물, 제2혼합물, 및 제3혼합물을 혼합한 후 접착제를 첨가하여 실런트의 점성을 조절하는 단계; 및
상기 점성이 조절된 실런트를 질소 가스가 주입된 진공탱크에서 에어 또는 스크류로 밀어내어 용기에 주입하는 단계를 포함하는, 방화용 실런트 제조방법.Mixing the expanded graphite and the flame retardant to prepare a first mixture;
Preparing a second mixture by mixing a thermoplastic resin and an adhesive;
Preparing a third mixture by dispersing the adhesive in water in which any one of phosphoric acid or phosphate is dissolved and then mixing a gypsum powder having an average length of 7 to 12 mm and an average thickness of 10 to 25 占 퐉;
Mixing the prepared first mixture, second mixture, and third mixture, and then adding an adhesive to adjust the viscosity of the sealant; And
And pushing the viscous controlled sealant from a vacuum tank filled with nitrogen gas to an air or a screw and injecting the sealant into the container. 청구항 10에 있어서,
상기 제1혼합물을 준비하는 단계는,
팽창흑연과 난연재를 10 : 3의 중량비로 혼합하는 것을 특징으로 하는, 방화용 실런트 제조방법. The method of claim 10,
Wherein preparing the first mixture comprises:
Wherein the expanded graphite and the flame retardant are mixed at a weight ratio of 10: 3. 청구항 10에 있어서,
상기 제2혼합물을 준비하는 단계는,
열가소성 수지와 접착제를 1 : 2의 중량비로 혼합하는 것을 특징으로 하는, 방화용 실런트 제조방법. The method of claim 10,
Wherein preparing the second mixture comprises:
Wherein the thermoplastic resin and the adhesive are mixed at a weight ratio of 1: 2. 청구항 10에 있어서,
상기 실런트의 점성을 조절하는 단계는,
준비된 제1혼합물, 제2혼합물, 및 제3혼합물을 6 : 1 : 3의 중량비로 혼합한 후 전체 100 중량부에 대해 15 내지 20 중량부의 접착제를 첨가하는 것을 특징으로 하는, 방화용 실런트 제조방법.The method of claim 10,
Wherein adjusting the viscosity of the sealant comprises:
Wherein the prepared first mixture, the second mixture, and the third mixture are mixed at a weight ratio of 6: 1: 3, and then 15 to 20 parts by weight of an adhesive is added to 100 parts by weight of the whole mixture . 청구항 10 내지 청구항 13 중 어느 한 항에 따라 제조된 것을 특징으로 하는, 방화용 실런트.A fire sealant manufactured according to any one of claims 10 to 13.
KR1020160145092A 2016-11-02 2016-11-02 Fire stop sealant and preparing method thereof KR101845632B1 (en)