An Antibacterial Composition Comprising Sodium hypochlorite and Deodorization and Constructing Methods Using Thereof Download PDFInfo
- Publication number
- KR101678398B1 KR101678398B1 KR1020160073695A KR20160073695A KR101678398B1 KR 101678398 B1 KR101678398 B1 KR 101678398B1 KR 1020160073695 A KR1020160073695 A KR 1020160073695A KR 20160073695 A KR20160073695 A KR 20160073695A KR 101678398 B1 KR101678398 B1 KR 101678398B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- polymer resin
- resin
- composition
- Prior art date
Abstract
Description
본 발명은 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물 및 이를 이용한 시공방법에 관한 것으로서, 보다 상세하기는 살균 기능을 갖는 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물 및 이를 이용한 시공방법에 관한 것이다.
The present invention relates to a fungicide composition containing sodium hypochlorite and a method of using the same, and more particularly, to a fungicide composition containing sodium hypochlorite having a sterilizing function and a method of using the same.
미생물은 우리 주변에서 항상 공존하고 있는 생명체이며, 이러한 미생물들은 인간에게 도움을 주는 유익한 종류도 있는 반면에 세균과 곰팡이 및 바이러스 등 질병을 유발하거나 악취를 발생시키는 등 인체에 해를 끼지는 병원성 미생물도 다수 존재한다.Microorganisms are living organisms that always coexist in our surroundings. These microorganisms are beneficial to humans, while pathogenic microorganisms that cause harm to humans, such as bacteria, fungi, and viruses, There are many.
특히, 우리는 일생 생활에서 대장균과 같이 인체에 유해한 세균 및 곰팡이와 같은 미생물에 노출되어 있어 그 피해가 빈번히 발생하고 있다. In particular, we are exposed to microorganisms such as bacteria and fungi which are harmful to the human body such as E. coli in their lifetime, and the damage is frequently occurred.
상기 미생물에 의한 피해는 섬유, 목재, 유리뿐만 아니라 플라스틱도 미생물에 대해 안전하지 않다는 인식의 확산으로 위생제품에 대한 소비자의 욕구가 점증됨에 따라 항균기능을 가진 제품이 다양하게 개발되고 있다.As the consumer's desire for hygiene products is increasing due to the spread of the awareness that the damage caused by the microorganisms is not safe for fibers, wood, glass and plastic microorganisms, various products having antibacterial function are being developed.
따라서 유해한 미생물로 인한 비위생적 환경을 개선코자 하는 다양한 위생관리용품이 개발되는 동시에 이에 대한 관심이 높아지는 추세이다. 특히 2000년대 이후 SARS, 조류독감, 신종플루 등 여러 유행성 전염병이 창궐하면서 이러한 유행성 전염병들로부터 예방을 위한 위생관리용품들이 많은 관심을 받고 있는 상황이다.Therefore, a variety of sanitary ware products have been developed to improve the unsanitary environment caused by harmful microorganisms, and there is an increasing interest in this. Especially since 2000, many pandemic infectious diseases such as SARS, avian influenza and swine flu have been emerging, and hygiene products for prevention from these pandemic infectious diseases are attracting much attention.
한편, 일반주택이나 공동주택 등 건축물에서는 다양한 형태의 시멘트 제품이 사용되고 있다. 시멘트 제품의 종류로는 석고보드, 시멘트 보드, 경량시멘트 패널, 등이 가장 많이 사용되고 있다. 이들 제품은 그 형태로서 표면의 마감이 끝나는 것이 아니고 다시 제품의 표면 위에 벽지를 바르거나 페인트, 또는 페인트와 유사한 형태의 표면 마감재를 사용한다. On the other hand, various types of cement products are used in buildings such as general houses and apartment buildings. The most common types of cement products are gypsum board, cement board, and lightweight cement panel. These products are not the end of the surface finish, but they are used again on the surface of the product, or use a paint or paint-like surface finish.
이러한 표면 마감재를 사용할 경우 건축물의 내/외부의 온도차에 의한 결로 현상으로 인하여 곰팡이 등이 발생하여 심각한 환경문제를 야기 시키고 있다. When such surface finishing materials are used, condensation due to temperature difference between the inside and outside of the building causes mold and causes serious environmental problems.
또한, 페인트와 유사한 마감용 코팅제의 경우 사용되는 원료에 휘발성 유기 화합물이 다량 함유되어 있어 코팅 작업 시 작업자에게 심각한 위해를 가하고 있다. 또한 이들 함유된 유기 화합물은 작업이 완료된 후에도 쉽게 분해되지 않아 인체에 심각한 피해를 기도 한다.In the case of paint-like finish coating agents, volatile organic compounds are contained in a large amount in the raw materials to be used, which poses a serious risk to the operator during the coating operation. Further, these organic compounds are not easily decomposed even after the work is completed, and they seriously damage the human body.
더욱이, 건축물의 내부 단열 벽체로 이용되는 석고판 등은 습기에 약하여 곰팡이가 빈번히 발생되어 잦은 도배와 거주자의 불편이 증가하고 있다.Furthermore, gypsum boards and the like used as the internal insulating walls of the buildings are weak in moisture, and molds are frequently generated, and frequent drainage and inconveniences of residents are increasing.
전술한 문제점을 극복하기 위하여 여러 가지 세라믹재료를 활용하는 방안이 검토되고 있으며, 일부 검증되지 않은 재료도 사용되고 있는 실정이다.In order to overcome the above-mentioned problems, various ceramic materials have been studied and some unexamined materials have been used.
특히, 곰팡이 및 세균은 적당한 온도와 습기, 그리고 옷감이나, 벽지, 도료, 등에서의 영양분 공급, PH 4.5에서 6.5 정도의 약산성 환경에서 잘 서식한다. 이러한 특징 때문에 온도 습도를 조절할 수 있는 재료를 사용하거나 오존 등의 재료를 사용하기도 한다.In particular, fungi and bacteria live well in moderate temperature and humidity, nutrient supply from cloth, wallpaper, paint, etc., and in a slightly acidic environment of pH 4.5 to 6.5. Because of these features, materials that can control temperature and humidity are used, or materials such as ozone are used.
이러한 재료들은 가격이 고가이며, 그 충분한 기능을 만족하기 위해서는 상당한 량의 재료를 사용해야 함은 물론 부착성능 및 벽체에의 흡수성능 등을 만족하기 위해서는 또 다른 유기 접착제를 사용해야 하는 부담이 있다. 유기 접착제를 사용함으로서 오히려 악취 발생을 유발하는 효과가 발생하기도 한다.These materials are expensive, and in order to satisfy their sufficient functions, it is necessary to use a considerable amount of materials, as well as to use another organic adhesive in order to satisfy the adhesion performance and the absorption performance to the wall. The use of an organic adhesive may cause an effect of causing a malodor.
이러한 종래 기술의 문제점의 해결방안으로 대한민국 공개특허공보 특 2003- 0032633호에는 원적외선 방사기능, 항균성 및 탈취기능 등 특수기능을 갖는 견운모 분말 및 황토를 주성분으로 하고 여기에 팽창성 시멘트, 석회, 마이크로실리카, 변성아크릴수지, 고화제 및 경화제를 첨가한 수경화성 바름재 조성물에 관한 기술이 개시되어 있다. 그러나, 이때 구성되는 견운모 및 황토의 량이 전체의 45 내지 65 wt%로서 재료 자체의 경화특성이 부족하여 CSA 시멘트나 석회만으로는 부착성능을 만족할 수 없으며, 더구나 부착성능을 위하여 변성 아크릴 모노머 등 유기화합물을 사용하고 있는데, 이를 사용함으로 오히려 유기물에 의한 탈취효과가 저감될 수 있는 문제점이 있다.
As a solution to the problems of the prior art, Korean Patent Laid-Open Publication No. 2003- 0032633 discloses a cement mortar composition comprising mainly a sericite powder and loess having a special function such as a far-infrared ray radiation function, an antibacterial property and a deodorization function and containing therein extensible cement, lime, Discloses a technique relating to a water-curable pressure-sensitive adhesive composition to which a modified acrylic resin, a solidifying agent and a curing agent are added. However, since the amount of the sericite and the loess constituted at this time is 45 to 65 wt% of the whole, the curing property of the material itself is insufficient, so that the CSA cement or lime alone can not satisfy the adhesion performance. In addition, However, the use of the organic deodorizing agent reduces the deodorizing effect due to organic substances.
본 발명은 상기와 같은 문제점을 해결하기 위해 도출된 것으로서, 도포 대상면, 특정적으로 건축물, 예를 들면 벽면, 바닥, 천정 또는 단열 벽체로 이용되는 석고판 등에 도포됨으로써, 대상표면에서 손상을 야기하는 박테리아와 곰팡이 등의 생육이 억제되어 건축물의 내구성을 향상시킬 수 있을 뿐만 아니라, 건축물의 마감에 사용되는 건축 마감자재의 손상을 방지하고, 악취 발생을 차단하도록 한다.
SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems, and it is an object of the present invention to provide a gypsum board which is coated on a surface to be coated, specifically a building such as a wall, floor, ceiling or gypsum board, It is possible not only to improve the durability of the building but also to prevent damage to the building finish material used for finishing the building and to prevent the generation of odor.
본 발명은
고분자 수지 100중량부 기준으로,
차아염소산나트륨 3 내지 20중량부;
탄산나트륨 1 내지 10중량부;
증점제 5 내지 10중량부;
나노세라믹입자 5 내지 10중량부;
항균성 물질 5 내지 20중량부;
계면활성제 2 내지 10중량부;
바인더 1 내지 15중량부;
재유화형 폴리머 분말 0.1 내지 10중량부;
용매 30 내지 150중량부; 및
변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물에,
아미노 함유 실록산을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고,
옥틸트리에톡시실란을 고분자 수지 100중량부를 기준으로 3 내지 15중량부로 더 포함하며,
왁스를 고분자 수지 100중량부를 기준으로 2 내지 5중량부로 더 포함하고,
마그네슘 실리케이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
테트라에틸렌펜타민을 고분자 수지 100중량부를 기준으로 1 내지 10중량부로 더 포함하고,
알긴산 나트륨을 고분자 수지 100중량부를 기준으로 5 내지 10중량부로 더 포함하며,
폴리비닐알콜을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고,
글리세린을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
오일을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하고,
부틸셀루솔브를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,The present invention
On the basis of 100 parts by weight of the polymer resin,
3 to 20 parts by weight of sodium hypochlorite;
1 to 10 parts by weight of sodium carbonate;
5 to 10 parts by weight of a thickener;
5 to 10 parts by weight of nano-ceramic particles;
5 to 20 parts by weight of an antibacterial substance;
2 to 10 parts by weight of a surfactant;
1 to 15 parts by weight of a binder;
0.1 to 10 parts by weight of a re-forming type polymer powder;
30 to 150 parts by weight of a solvent; And
To 3 to 10 parts by weight of a modified silane silicate composition,
Further comprising 2 to 10 parts by weight of an amino-containing siloxane based on 100 parts by weight of the polymer resin,
Further comprising 3 to 15 parts by weight of octyltriethoxysilane based on 100 parts by weight of the polymer resin,
The wax is further contained in an amount of 2 to 5 parts by weight based on 100 parts by weight of the polymer resin,
Further comprising 1 to 5 parts by weight of magnesium silicate based on 100 parts by weight of the polymer resin,
Further comprising 1 to 10 parts by weight of tetraethylene pentamine based on 100 parts by weight of the polymer resin,
Further comprising 5 to 10 parts by weight of sodium alginate based on 100 parts by weight of the polymer resin,
Further comprising 2 to 10 parts by weight of polyvinyl alcohol based on 100 parts by weight of the polymer resin,
Further comprising 1 to 5 parts by weight of glycerin based on 100 parts by weight of the polymer resin,
Wherein the oil further comprises 1 to 5 parts by weight based on 100 parts by weight of the polymer resin,
1 to 5 parts by weight of butyl cellosolve based on 100 parts by weight of the polymer resin,
소디윰스테아레이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 곰팡이 방지제 조성물을 제공한다.
And 1 to 5 parts by weight of sodium dodecyl stearate based on 100 parts by weight of the polymer resin.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
또한, 본 발명은
대상표면의 이물질을 제거하여 청결하게 하는 청결단계;
상기 청결단계가 종료된 후 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부, 탄산나트륨 1 내지 10중량부, 증점제 5 내지 10중량부, 나노세라믹입자 5 내지 10중량부, 항균성 물질 5 내지 20중량부, 계면활성제 2 내지 10중량부, 바인더 1 내지 15중량부, 재유화형 폴리머 분말 0.1 내지 10중량부, 용매 30 내지 150중량부, 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물에, 아미노 함유 실록산을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고, 옥틸트리에톡시실란을 고분자 수지 100중량부를 기준으로 3 내지 15중량부로 더 포함하며, 왁스를 고분자 수지 100중량부를 기준으로 2 내지 5중량부로 더 포함하고, 마그네슘 실리케이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 테트라에틸렌펜타민을 고분자 수지 100중량부를 기준으로 1 내지 10중량부로 더 포함하고, 알긴산 나트륨을 고분자 수지 100중량부를 기준으로 5 내지 10중량부로 더 포함하며, 폴리비닐알콜을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고, 글리세린을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 오일을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하고, 부틸셀루솔브를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 소디윰스테아레이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 곰팡이 방지제 조성물을 1 내지 3회 도포하는 조성물 도포단계; 및In addition,
A cleaning step of removing foreign matter on the surface of the object to be cleaned;
After completion of the cleaning step, 3 to 20 parts by weight of sodium hypochlorite, 1 to 10 parts by weight of sodium carbonate, 5 to 10 parts by weight of a thickener, 5 to 10 parts by weight of nanoceramic particles, 5 parts by weight of an antimicrobial substance 5 To 20 parts by weight of a surfactant, 2 to 10 parts by weight of a surfactant, 1 to 15 parts by weight of a binder, 0.1 to 10 parts by weight of a re-lubrication type polymer powder, 30 to 150 parts by weight of a solvent and 3 to 10 parts by weight of a modified silane silicate compound Wherein the amino resin composition further comprises 2 to 10 parts by weight of an amino-containing siloxane based on 100 parts by weight of the polymer resin and 3 to 15 parts by weight of octyltriethoxysilane based on 100 parts by weight of the polymer resin, Based on 100 parts by weight of the polymeric resin, 1 to 5 parts by weight of the magnesium silicate, based on 100 parts by weight of the polymeric resin, And 1 to 10 parts by weight of tetraethylenepentamine based on 100 parts by weight of the polymer resin, and further comprising sodium alginate in an amount of 5 to 10 parts by weight based on 100 parts by weight of the polymer resin, wherein the polyvinyl alcohol is mixed with 100 parts by weight of the polymer resin Based on 100 parts by weight of the polymer resin, the oil further comprises 1 to 5 parts by weight based on 100 parts by weight of the polymer resin, and the butyl cellosolve Wherein the composition further comprises 1 to 5 parts by weight based on 100 parts by weight of the polymer resin and 1 to 5 parts by weight of sodium dodecyl stearate based on 100 parts by weight of the polymer resin, ; And
상기 곰팡이 방지제 조성물 도포단계가 종료된 후 건조시키는 건조단계를 포함하는 곰팡이 방지제 조성물 시공방법을 제공한다.
And a drying step of drying after the application of the fungicide composition composition is completed.
삭제delete
삭제delete
본 발명에 따른 곰팡이 방지제 조성물, 특정적으로 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물은 건축물, 예를 들면 벽면, 바닥, 천정 또는 단열 벽체로 이용되는 석고판 등에 도포됨으로써, 대상표면에서 손상을 야기하는 박테리아와 곰팡이 등의 생육이 억제되어 건축물의 내구성을 향상시킬 수 있을 뿐만 아니라, 건축물의 마감에 사용되는 건축 마감자재의 손상을 방지하고, 악취 발생을 차단하는 효과가 있다.
The fungicide composition according to the present invention, particularly the antifungal composition comprising sodium hypochlorite, is applied to a gypsum board used as a building, such as a wall, a floor, a ceiling or a heat insulating wall, It is possible to improve the durability of the building by inhibiting the growth of bacteria and fungi, as well as to prevent damage to the building finish material used for finishing the building, and to prevent the generation of odor.
이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.
한 가지 관점에서, 본 발명은 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부; 탄산나트륨 1 내지 10중량부; 증점제 5 내지 10중량부; 나노세라믹입자 5 내지 10중량부; 항균성 물질 5 내지 20중량부; 계면활성제 2 내지 10중량부; 바인더 1 내지 15중량부; 재유화형 폴리머 분말 0.1 내지 10중량부; 용매 30 내지 150중량부; 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물을 제공한다.In one aspect, the present invention relates to a polymeric resin composition comprising, based on 100 parts by weight of a polymer resin, 3 to 20 parts by weight of sodium hypochlorite; 1 to 10 parts by weight of sodium carbonate; 5 to 10 parts by weight of a thickener; 5 to 10 parts by weight of nano-ceramic particles; 5 to 20 parts by weight of an antibacterial substance; 2 to 10 parts by weight of a surfactant; 1 to 15 parts by weight of a binder; 0.1 to 10 parts by weight of a re-forming type polymer powder; 30 to 150 parts by weight of a solvent; And 3 to 10 parts by weight of a modified silane silicate compound.
다른 관점에서, 본 발명은 대상표면의 이물질을 제거하여 청결하게 하는 청결단계; 상기 청결단계가 종료된 후 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부, 탄산나트륨 1 내지 10중량부, 증점제 5 내지 10중량부, 나노세라믹입자 5 내지 10중량부, 항균성 물질 5 내지 20중량부, 계면활성제 2 내지 10중량부, 바인더 1 내지 15중량부, 재유화형 폴리머 분말 0.1 내지 10중량부, 용매 30 내지 150중량부, 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물을 1 내지 3회 도포하는 조성물 도포단계; 및 상기 곰팡이 방지제 조성물 도포단계가 종료된 후 건조시키는 건조단계를 포함하는 곰팡이 방지제 조성물 시공방법을 제공한다.
According to another aspect of the present invention, there is provided a cleaning method comprising the steps of: After completion of the cleaning step, 3 to 20 parts by weight of sodium hypochlorite, 1 to 10 parts by weight of sodium carbonate, 5 to 10 parts by weight of a thickener, 5 to 10 parts by weight of nanoceramic particles, 5 parts by weight of an antimicrobial substance 5 To 20 parts by weight of a surfactant, 2 to 10 parts by weight of a surfactant, 1 to 15 parts by weight of a binder, 0.1 to 10 parts by weight of a re-lubrication type polymer powder, 30 to 150 parts by weight of a solvent and 3 to 10 parts by weight of a modified silane silicate compound Applying the composition for applying the inhibitor composition one to three times; And a drying step of drying after the application of the fungicide composition composition is completed.
본 발명에 따른 곰팡이 방지제 조성물, 특정적으로 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물은 건축물, 예를 들면 건축물의 벽면, 바닥, 천정 또는 단열 벽체로 이용되는 석고판 등에 도포됨으로써, 대상표면에서 손상을 야기하는 박테리아와 곰팡이 등의 생육이 억제시켜 건축물의 내구성을 향상시킬 수 있는 것이라면 어떠한 것을 사용하여도 무방하다.The anti-fungal composition according to the present invention, particularly the anti-fungal composition containing sodium hypochlorite, is applied to a building, for example, a gypsum board used as a wall, a floor, a ceiling or a heat insulating wall of a building, Anything can be used as long as it can inhibit the growth of bacteria and fungi that may cause it to improve the durability of the building.
본 발명에 따른 고분자 수지는 곰팡이 방지제 조성물에 포함되어 보호하고자 하는 보호 대상표면이 외부에 노출되지 않도록 하는 동시에, 곰팡이 방지제 조성물의 구성성분이 대상표면에 용이하게 도포되도록 하기 위한 것으로서, 이러한 목적을 위해 통상적으로 사용하는 고분자 수지라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 수용성아크릴수지, 에틸렌 초산 비닐(EVA), 스틸렌-부타디엔고무(SBR), 스티렌 부타디엔 스티렌(stylene butadiene stylene; SBS) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.The polymer resin according to the present invention is contained in a fungicide composition so that the surface to be protected is not exposed to the outside and the constituent components of the fungicide composition are easily applied to the surface of the object. For this purpose, Any resin may be used as long as it is a commonly used polymer resin, but water-soluble acrylic resin, ethylene-vinyl acetate (EVA), styrene-butadiene rubber (SBR), styrene butadiene styrene (SBS) It is preferable to use at least one selected mixture.
여기서, 상기 수용성아크릴수지는 산 및/또는 염기에 강하고, 자외선에 의한 변색이나 구조노화를 방지하는 내후성을 제공하는 동시에 표면 광택을 부가할 수 있다.Here, the water-soluble acrylic resin is resistant to acid and / or base, and can provide surface gloss and weather resistance to prevent discoloration and aging due to ultraviolet rays.
또한, 상기 고분자 수지는 곰팡이 방지제 조성물에 포함되어 보호 도포막을 형성하고자 하는 시공표면에 용이하게 접착할 수 있도록 하는 접착력을 제공할 수 있다.In addition, the polymer resin may be included in the antifungal composition to provide an adhesive force to easily adhere to a construction surface on which a protective coating film is to be formed.
본 발명에 따른 곰팡이 방지제 조성물, 특정적으로 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물의 고분자 수지 외 나머지 성분들의 함량은 고분자 수지 100중량부를 기준으로 한다.The content of the components other than the polymer resin of the fungicide composition according to the present invention, specifically the antifungal agent composition containing sodium hypochlorite, is based on 100 parts by weight of the polymer resin.
본 발명에 따른 차아염소산나트륨은 아염소산염의 하나로서, 통상 수산화나트륨 용액에 염소 가스를 흡수시켜 얻어지며, 식품첨가물로 사용 가능하여 식품의 부패균이나 병원균을 사멸하기 위한 살균제로서, 이러한 용도로 당업계에서 통상적으로 사용되는 차아염소산나트륨이라면 어떠한 것을 사용하여도 무방한다.The sodium hypochlorite according to the present invention is one of chlorites, which is obtained by absorbing chlorine gas into a sodium hydroxide solution, and is a disinfectant for killing spoilage and pathogenic bacteria in food, which can be used as a food additive. Any sodium hypochlorite conventionally used in the art may be used.
바람직한 차아염소산나트륨은 고분자 수지 100중량부 기준으로 3 내지 20중량부를 사용하는 것을 추천한다.It is recommended that the preferable sodium hypochlorite be used in an amount of 3 to 20 parts by weight based on 100 parts by weight of the polymer resin.
본 발명에 따른 탄산나트륨은 탄산의 나트륨염으로 보통 소다 또는 탄산소다라고도 지칭되며, 흡수성이 강하다.The sodium carbonate according to the present invention is a sodium salt of carbonic acid, which is also referred to as soda or carbonate, and has a high water absorption.
바람직한 탄산나트륨의 사용량은 고분자 수지 100중량부 기준으로 1 내지 10중량부인 것이 좋다.The amount of sodium carbonate to be used is preferably 1 to 10 parts by weight based on 100 parts by weight of the polymer resin.
본 발명에 따른 증점제는 곰팡이 방지제 조성물의 점도를 조절하여 조성물의 사용을 용이하게 하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 증점제라면 특별히 한정되지 않지만, 바람직하게는 폴리아크릴산, 하이드록시 에틸 셀룰로오즈(HydroxyEthyl Cellulose), 소수성 우레탄변성계 증점제 또는 이들의 혼합물을 사용하는 것을 추천한다.The thickening agent according to the present invention is for controlling the viscosity of the antifungal agent composition to facilitate the use of the composition. For this purpose, the thickening agent conventionally used in the art is not particularly limited, but polyacrylic acid, hydroxy It is recommended to use ethyl cellulose (HydroxyEthyl Cellulose), a hydrophobic urethane modifier thickener or a mixture thereof.
상기 증점제의 사용량은 고분자 수지 100중량부를 기준으로 5 내지 10중량부인 것이 바람직하다.The amount of the thickener to be used is preferably 5 to 10 parts by weight based on 100 parts by weight of the polymer resin.
여기서, 상기 증점제로 사용되는 하이드록시 에틸 셀룰로오즈는 보수성을 가질 수 있다.Here, the hydroxyethyl cellulose used as the thickener may have water retention property.
본 발명에 따른 나노세라믹 입자는 곰팡이 방지제 조성물의 도포시 그 표면으로 부상하여 치밀하고 경도가 높은 표면을 형성하기 때문에, 수증기와 기타 기체, 액체의 투과를 방지함은 물론, 내습성, 내구성, 내후성, 내충격성, 내약품성이 향상된다.The nanoceramic particles according to the present invention float on the surface of the antifungal agent composition when applied to form a dense and hard surface, thereby preventing permeation of water vapor and other gases and liquids, and also preventing moisture, durability, , Impact resistance and chemical resistance are improved.
상기 나노세라믹 입자의 사용량은 고분자 수지 100중량부를 기준으로 5 내지 10중량부인 것이 좋다.The amount of the nanoceramic particles used is preferably 5 to 10 parts by weight based on 100 parts by weight of the polymer resin.
바람직한 나노세라믹 입자는 실리콘카바이드, 알루미나, 실리카, 지르코니아-실리카, ZnO, TiO2 및/또는 CaCO3가 포함된다. Preferred nanoceramic particles include silicon carbide, alumina, silica, zirconia-silica, ZnO, TiO 2 and / or CaCO 3 .
이들 세라믹입자는 평균 입경이 나노 범위인 것이 바람직한데, 구체적으로 상기 실리콘카바이드의 평균 입경은 300 내지 500nm, 상기 알루미나의 평균 입경은 500 내지 1000nm, 상기 실리카의 평균 입경은 700 내지 1500nm, 상기 지르코니아-실리카의 평균 입경은 500 내지 1000nm, 상기 ZnO의 평균 입경은 500 내지 1000nm, 상기 TiO2의 평균 입경은 100 내지 300nm, 그리고 CaCO3의 평균 입경은 500 내지 1000nm인 것이 바람직하다.Preferably, the average particle size of the ceramic particles is in the range of 300 to 500 nm, the average particle size of the alumina is 500 to 1000 nm, the average particle size of the silica is 700 to 1500 nm, the zirconia- It is preferable that the average particle size of silica is 500 to 1000 nm, the average particle size of ZnO is 500 to 1000 nm, the average particle size of TiO 2 is 100 to 300 nm, and the average particle size of CaCO 3 is 500 to 1000 nm.
이 중에서도 실리콘카바이드는 천연광물로 존재하지 않으므로 인공적으로 합성하며, 고온에서의 화학적 안정성 및 내식성이 뛰어나고 높은 경도를 갖는다.Among them, silicon carbide does not exist as natural minerals, so it is synthesized artificially, has excellent chemical stability and corrosion resistance at high temperature, and has high hardness.
본 발명에 따른 항균성 물질은 항균 및/또는 항취 성능을 갖는 당업계에서 통상적으로 사용하는 항균성 물질이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 무기계 및/또는 유기계 항균성 물질을 사용하는 것이 좋고, 그 사용량은 고분자 수지 100중량부 기준으로 5 내지 20중량부인 것을 추천한다.The antimicrobial substance according to the present invention may be any antibacterial substance commonly used in the art having antimicrobial and / or anti-inflammatory properties. Preferably, inorganic and / or organic antimicrobial substances are used. The amount to be used is preferably 5 to 20 parts by weight based on 100 parts by weight of the polymer resin.
상기 항균성 물질로서 사용 가능한 무기계 항균성 물질로는 은, 구리, 아연 등의 금속 또는 상기 은, 구리, 아연 등의 금속을 무기질 재료에 담지한 무기계 항균성 물질을 사용할 수 있다.Examples of the inorganic antimicrobial substance usable as the antimicrobial substance include inorganic antimicrobial substances containing a metal such as silver, copper and zinc or a metal such as silver, copper and zinc on an inorganic material.
상기 항균성 물질로서 사용 가능한 유기계 항균성 물질은 CAS(Chemical Abstracts Service) 및 EPA(Environmental Protection Agency)에 등록된 화학물질 중 2-피리디오티올-1-옥사이드 소듐염(2-Pyridiothiol-1-oxide sodium salt), N,N-디메틸-N'-페닐-(N'-플로로-디클로로메틸-티올)-설포마이드(N,N-dimethyl-N'-phenyl-(N'-fluoro-dichloromethyl-thio)-sulfoamide), 디오도메틸-P-토릴 설폰(Diiodomethyl-P-tolyl Sulfone), 이소프로필메틸페놀(Isopropylmethylphenol), 메틸이소시아졸리논(Methylisothiazolinone) 또는 메틸디브로모 글루타로니트릴(Methyldibromo Glutaronitrile) 등의 화합물을 단독 또는 둘 이상 혼합하여 사용한다. Organic antimicrobial agents that can be used as the antimicrobial agent include 2-pyridothiol-1-oxide sodium salt (2-pyridothiol-1-oxide sodium salt) among chemicals registered in Chemical Abstracts Service (CAS) ), N, N-dimethyl-N'-phenyl- (N'-fluoro-dichloromethyl-thio) Diethylmethyl-P-tolyl Sulfone, Isopropylmethylphenol, Methylisothiazolinone, Methyldibromo Glutaronitrile, and the like. Are used singly or in combination of two or more.
한편. 상기 항균성 물질은 천연 프로폴리스, 피톤치드 등의 천연에서 추출된 항균 물질을 사용할 수도 있다.Meanwhile. The antimicrobial substance may be an antimicrobial substance extracted from a natural source such as natural propolis or phytoncide.
특정 양태로서, 본 발명에 따른 항균성 물질은 곰팡이 방지제 조성물, 특정적으로 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물에 용이하게 적용되기 위해 분말 형태, 추천하기로는 초미립자 분말 형태로 구성될 수 있다.In a particular embodiment, the antimicrobial material according to the present invention may be in powder form, preferably in the form of ultrafine powder, for easy application to anti-fungal compositions, especially anti-fungal compositions comprising sodium hypochlorite.
여기서, 상기 초미립자 분말로 이루어진 항균성 물질, 특정적으로 항균성 초미립자 분말은 항균성 물질, 특정적으로 유기계 항균성 물질을 금속 및/또는 금속산화물계 무기물 입자에 커플링하여 제조할 수 있다.Here, the antimicrobial substance composed of the ultrafine particle powder, specifically, the antimicrobial ultrafine particle powder can be produced by coupling an antimicrobial substance, specifically an organic antimicrobial substance, with a metal and / or a metal oxide based inorganic particle.
상기 금속 및/또는 금속산화물계 무기물의 평균입도는 커플링되어 제조되는 항균성 초미립자 분말의 크기를 고려하여 볼 때, 5 내지 15nm, 바람직하게는 8 내지 12nm인 것이 좋다.The average particle size of the metal and / or metal oxide based inorganic material is preferably 5 to 15 nm, and more preferably 8 to 12 nm in view of the size of the antibacterial ultrafine particle powder produced by coupling.
이때, 상기 금속 및/또는 금속산화물계 무기물은 통상적으로 사용되는 금속산화물계 무기물이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 광촉매 반응을 유도하는 물질 예를 들면, TiO2, ZnO2, ZnO, SrTiO3, CdS, GaP, InP, GaAs, BaTiO3, KNbO3, ZrPO4, Fe2O3, Ta2O5, WO3, SnO2, Bi2O3, NiO, Cu2O, SiO, SiO2, MoS2, InPb, RuO2, CeO2 등을 단독 또는 둘 이상 혼합하여 사용할 수 있고, 내광부식성, 유해성, 광촉매활성 등을 고려하여 볼 때, 인체에 무해하고 광촉매활성이 탁월하며, 내광부식성이 우수할 뿐만 아니라 가격 또한 저렴한 이산화티탄이 좋다. The metal and / or metal oxide-based inorganic material may be any metal oxide-based inorganic material conventionally used. Preferably, the metal and / or metal oxide-based inorganic material is a material that induces a photocatalytic reaction such as TiO 2 , ZnO 2 , ZnO, SrTiO 3, CdS, GaP, InP , GaAs, BaTiO 3, KNbO 3, ZrPO 4, Fe 2 O 3, Ta 2 O 5, WO 3, SnO 2, Bi2O 3, NiO, Cu 2 O, SiO, SiO 2, MoS 2 , InPb, RuO 2 and CeO 2 can be used singly or in combination of two or more. In view of corrosion resistance, harmfulness and photocatalytic activity, it is harmless to human body, excellent in photocatalytic activity, Not only is titanium dioxide cheap in price, but also good.
이때, 상기 이산화티탄은 아나타제 형태와 루틸 형태의 두 가지 결정구조를 가지고 있는데, 상기 루틸 형태의 경우 비활성으로서 항균 효과가 부족하다. 그러므로 더욱 바람직하게는 아나타제형의 이산화티탄 결정을 사용하는 것이 좋다.At this time, the titanium dioxide has two crystal structures of an anatase form and a rutile form. In the case of the rutile form, the inactive form is insufficient in antibacterial effect. Therefore, it is more preferable to use anatase-type titanium dioxide crystals.
한편, 상기 이산화티탄은 388㎚ 이하의 자외선을 흡수하여 반응함으로써 전자(전도대)와 정공(가전자대)이 생성되며, 상기 반응에서 생성된 전자와 정공은 10-12 내지 10-9 초 만에 재결합하지만, 재결합하기 전에 오염물질 등이 표면에 흡착하게 되면 상기 전자와 정공에 의해 분해된다.On the other hand, the titanium dioxide absorbs ultraviolet rays of 388 nm or less and reacts to generate electrons (conduction band) and holes (valence band), and electrons and holes generated in the reaction are recombined in 10-12 to 10-9 seconds However, when a contaminant or the like is adsorbed on the surface before recombination, it is decomposed by the electrons and holes.
본 발명에 따른 항균성 유기물과 금속 및/또는 금속산화물계 무기물을 커플링하여 복합화하는데 사용되는 커플링제로는 실라놀 화합물을 쉽게 형성하는 실란계 커플링제 예를 들면, 3-글리시독시프로필 트리메톡시실란, (3,4 에폭시사이크로헥실)-에틸트리메톡시실란, 메틸트리메톡시실란, 테트라에톡시실란 또는 메틸트리에톡시실란 등을 선택하여 사용한다. 항균성 유기물과 금속 및/또는 금속산화물계 무기물을 실란계 커플링제로 커플링시킬 경우에는 발열반응이 발생하므로 계속하여 가수 분해와 탈수축합 반응이 연속적으로 일어나고 이에 따라 물과 알코올이 생성된다.As the coupling agent used for coupling and combining the antimicrobial organic material according to the present invention with the metal and / or metal oxide based inorganic material, a silane coupling agent that easily forms a silanol compound such as 3-glycidoxypropyltrimethoxysilane (3,4 epoxycyclohexyl) -ethyltrimethoxysilane, methyltrimethoxysilane, tetraethoxysilane, methyltriethoxysilane or the like may be selected and used. When an antibacterial organic substance and a metal and / or a metal oxide-based inorganic substance are coupled by a silane coupling agent, an exothermic reaction occurs, and therefore hydrolysis and dehydration condensation reaction are continuously performed, and water and alcohol are produced.
또한, 본 발명에 따른 금속 및/또는 금속산화물계 무기물은 광촉매 활성 무기물로서 항균작용 이외에 주위의 유기물을 분해시키는 성질이 있는데, 이러한 문제는 항균성 초미립자 분말을 제조하는 과정에서 상기 광촉매 활성을 갖는 금속 및/또는 금속산화물계 무기물의 활성점들을 커플링제로 도포하여 스크리닝함으로써 해결할 수 있다.In addition, the metal and / or metal oxide based inorganic material according to the present invention is a photocatalytically active inorganic substance and has a property of decomposing the surrounding organic substances in addition to the antibacterial action. Such a problem is caused by the fact that in the course of producing the antibacterial ultrafine particle powder, / ≪ / RTI > or metal oxide-based inorganic active materials with a coupling agent and screening them.
특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물을 구성하는 항균성 물질은 마이크로캡슐 형태로 제조되어 항균성 물질이 외부의 충격으로부터 보호되며 장시간 동안 서서히 캡슐의 외부로 용출될 수 있도록 구성할 수 있다.As a specific aspect, the antimicrobial substance constituting the fungicide composition according to the present invention may be prepared in the form of microcapsules so that the antimicrobial substance is protected from external impact and can be gradually released to the outside of the capsule for a long time.
여기서, 상기 항균성 물질을 마이크로캡슐 형태로 제조하기 위해서는 상기 항균성 물질을 코어로 하고, 그 외벽면에 멜라민 수지, 요소 수지, 아크릴 수지 또는 이들의 혼합물이 도포되도록 형성시켜 최종적인 캡슐 형태의 항균성 물질을 구성할 수 있다. In order to produce the antimicrobial substance in a microcapsule form, the antimicrobial substance is used as a core and melamine resin, urea resin, acrylic resin or a mixture thereof is coated on the outer wall surface to form a final capsule-like antimicrobial substance Can be configured.
이때, 상기 항균성 물질이 마이크로캡슐 형태로 구성되는 경우, 이를 본 발명에서는 항균성 마이크로캡슐로 지칭하기로 하며, 상기 항균성 마이크로캡슐이 곰팡이 방지제 조성물에 포함되면, 상기 항균성 마이크로캡슐의 사용량은 항균성 물질을 단독으로 사용하는 것 보다 증가시켜야 만족할 수 있는 항균 및/또는 항취 효과를 얻을 수 있다.When the antibacterial microcapsule is included in the antifungal composition, the amount of the antibacterial microcapsule may be used alone or in combination with the antibacterial microcapsule. In this case, It is possible to obtain an antibacterial and / or anti-inflammatory effect that can be satisfactorily increased.
바람직한 항균성 마이크로캡슐의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 고분자 수지 100중량부 기준으로 20 내지 30중량부인 것이 좋다.The amount of the antimicrobial microcapsule to be used may be changed according to the user's choice, but it is preferably 20 to 30 parts by weight based on 100 parts by weight of the polymer resin.
본 발명에 따른 계면활성제는 당업계의 통상적인 계면활성제라면 어떠한 것을 사용하여도 무방하지만, 바람직한 계면활성제는 이온성계면활성제(음이온, 양이온, 양성) 비이온성계면활성제를 사용하고, 음이온계면활성제로서 술폰 에스테르(Sulfuric ester), 술폰산(sulfonic acid), 포스포릭 에스테르(phosphoric ester); 양이온계면활성제로서 2차 아민염(Secondary amine salt), 3차 아민염(tertiary amine salt); 양이온성계면활성제로서 아미노산 타입(amino acid type), 베타인 타입(betaine type); 비이온성계면활성제로서 폴리에틸렌글리콜 타입(polyethyleneglycol type), 폴리하이드록시알코올 타입(polyhydroxyalcohol type) 또는 이들의 혼합물을 사용할 수 있다.The surfactant according to the present invention may be any conventional surfactant in the art, but preferred surfactants are nonionic surfactants such as ionic surfactants (anionic, cationic, amphoteric), anionic surfactants Sulfuric esters, sulfonic acids, phosphoric esters; As the cationic surfactant, a secondary amine salt, a tertiary amine salt; As cationic surfactants there may be mentioned amino acid type, betaine type; As the nonionic surfactant, a polyethylene glycol type, a polyhydroxyalcohol type, or a mixture thereof may be used.
바람직한 계면활성제는 사용자의 선택에 따라 변경 가능하지만, 고분자 수지 100중량부 기준으로 2 내지 10중량부인 것을 추천한다.The preferred surfactant can be varied depending on the user's choice, but it is recommended that the surfactant be 2 to 10 parts by weight based on 100 parts by weight of the polymer resin.
본 발명에 따른 바인더는 상기 곰팡이 방지제 조성물의 도포시 차아염소산나트륨, 탄산나트륨, 항균성 물질, 특정적으로 항균성 초미립자 분말 또는 항균성 마이크로캡슐이 도포 대상면에 용이하게 도포되도록 하는 것으로서, 이러한 용도로 사용되는 당업계의 통상적인 바인더라면 어떠한 것을 사용하여도 무방하다.The binder according to the present invention allows easy application of sodium hypochlorite, sodium carbonate, an antimicrobial substance, an antimicrobial ultrafine particle powder or an antimicrobial microcapsule on a surface to be coated upon application of the antifungal agent composition, Any conventional binder in the industry may be used.
바림직한 바인더로는 열가소성수지, 열경화형수지, 광경화형수지, 실란컴파운드, 티타늄컴파운드, 고분자 공중합체, 자기조립형수지 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용할 수 있지만, 보다 구체적으로 멜라민 수지, 알키드 수지, 불포화 폴리에스테르 수지, 폴리우레탄 수지, 페놀 수지, 에폭시 수지, 실리콘 수지 또는 이들로부터 선택되는 적어도 하나 이상의 혼합물을 사용할 수도 있다.The binder to be applied may be a thermoplastic resin, a thermosetting resin, a photocurable resin, a silane compound, a titanium compound, a polymer copolymer, a self-assembled resin or a mixture of at least one selected from the foregoing. More specifically, A resin, an unsaturated polyester resin, a polyurethane resin, a phenol resin, an epoxy resin, a silicone resin, or a mixture of at least one selected from these may be used.
본 발명에 따른 재유화형 폴리머 분말(Redispersible Polymer Powder)은 곰팡이 방지제 조성물 내부에 필름을 형성하여 휨 및 부착강도를 향상시키며, 보수성이 개선되어 중성화, 염화물 이온 침투, 동결융해 등의 내구성을 향상시킬 수 있다.The redispersible polymer powder according to the present invention improves the warpage and adhesion strength by forming a film inside the antifungal agent composition and improves the water retention, thereby improving durability such as neutralization, chloride ion penetration, freezing and thawing have.
바람직한 재유화형 폴리머 분말은 에틸렌 초산 비닐(EVA) 또는 초산비닐/비닐바사테이트(Va/VeoVa) 중 선택된 어느 하나 이상으로 구성되는데, 겉보기 비중은 475ㅁg/l, 입도는 max,2%>400㎛이고, 물에 재분산 시 0.3 내지 9㎛의 입도분포를 나타내며, 그 사용량은 고분자 수지 100중량부 기준으로 0.1 내지 10중량부인 것이 좋다.The preferred re-firing polymer powder is composed of at least one selected from ethylene vinyl acetate (EVA) or vinyl acetate / vinyl valerate (Va / VeoVa), wherein the apparent specific gravity is 475? G / Mu m and exhibits a particle size distribution of 0.3 to 9 mu m when redispersed in water, and the amount of use is preferably 0.1 to 10 parts by weight based on 100 parts by weight of the polymer resin.
본 발명에 따른 용매는 당업계에서 통상적으로 사용하는 용매라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 물, 아세톤, 메틸에틸케톤, 메틸알콜, 에틸알콜, 이소프로필알콜, 부틸알콜, 에틸렌글라이콜, 폴리에틸렌글라이콜, 테트라하이드로푸란, 디메틸포름아미드, 디메틸아세트아마이드, N-메틸-2-피롤리돈, 헥산, 사이클로헥사논, 톨루엔, 클로로포름, 증류수, 디클로로벤젠, 디메틸벤젠, 트리메틸벤젠, 피리딘, 메틸나프탈렌, 니트로메탄, 아크릴로니트릴, 옥타데실아민, 아닐린, 디메틸설폭사이드로 이루어진 군으로부터 하나 이상 선택하여 사용하는 것을 추천하며, 그 사용량은 고분자 수지 100중량부 기준으로 30 내지 150중량부를 사용하는 것이 좋다.The solvent according to the present invention may be any solvent conventionally used in the art, but it is preferably water, acetone, methyl ethyl ketone, methyl alcohol, ethyl alcohol, isopropyl alcohol, butyl alcohol, ethylene glycol A solvent such as methanol, ethanol, isopropanol, n-butanol, isopropanol, n-butanol, isopropanol, n-butanol, It is recommended to use at least one selected from the group consisting of pyridine, methylnaphthalene, nitromethane, acrylonitrile, octadecylamine, aniline, and dimethylsulfoxide, and the amount thereof is 30 to 150 parts by weight based on 100 parts by weight of the polymer resin It is good to use.
본 발명에 따른 변성실란실리케이트 합성물은 곰팡이 방지제 조성물로 도포되는 도포면의 내크랙성, 내수성, 내오염성, 내마모성 및/또는 내부착성 등을 향상시키기 위한 것이다.The modified silane silicate composition according to the present invention is intended to improve the crack resistance, water resistance, stain resistance, abrasion resistance, and / or adhesion resistance of a coated surface coated with a fungicide composition.
상기 변성실란실리케이트 합성물은 실리케이트와 실란을 혼합하여 제조할 수 있다.The modified silane silicate compound can be prepared by mixing silicate and silane.
바람직한 실리케이트는 당업계에서 통상적으로 사용하는 실리케이트라면 어떠한 것을 사용하여도 무방하지만, 보다 바람직하게는 알칼리 실리케이트, 특히 바람직하게는 리튬실리케이트, 순수포타슘실리케이트, 전처리된 포타슘실리케이트, 합성실리케이트(리튬, 소디윰, 포타슘), 콜로이드실리카 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다. 그러나 이에 한정되는 것은 아니다.The preferred silicate may be any silicate commonly used in the art, but more preferably an alkali silicate, particularly preferably a lithium silicate, a pure potassium silicate, a pre-treated potassium silicate, a synthetic silicate (lithium, , Potassium), colloidal silica, or a mixture of at least one selected from these. However, the present invention is not limited thereto.
바람직한 실란은 당업계에서 통상적으로 사용되는 실란이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 아미노실란, 비닐실란, 에폭시 실란, 메타크릴실란, 유황, 알킬실란, 페닐실란, 클로로실란 중 비닐트리클로로실란, 노르말헥실트리에톡시실란, 아미노에칠아미노프로필실란, 페닐트리메톡시실란, 비닐벤질아미노에틸아미노프로필트리메톡시실란, 메틸디메톡시실란, 메타크릴록시프로필트리메톡시실란, 아미노에틸아미노프로필트리메톡시실란, 비닐트리메톡시실란, 테트라에톡시실란(TEOS), 3글리시독시프로필트리메톡시실란, 아미노프로필트리메톡시실란 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다. 하지만, 이에 한정되는 것은 아니다.The preferred silane may be any silane commonly used in the art, but it may be any one selected from aminosilane, vinylsilane, epoxysilane, methacrylsilane, sulfur, alkylsilane, phenylsilane, vinyltrichloro Silane, n-hexyltriethoxysilane, aminoethylaminopropylsilane, phenyltrimethoxysilane, vinylbenzylaminoethylaminopropyltrimethoxysilane, methyldimethoxysilane, methacryloxypropyltrimethoxysilane, aminoethylamino It is preferable to use at least one selected from the group consisting of propyltrimethoxysilane, vinyltrimethoxysilane, tetraethoxysilane (TEOS), 3 glycidoxypropyltrimethoxysilane, aminopropyltrimethoxysilane, and mixtures thereof. However, the present invention is not limited thereto.
한편, 상기 실리케이트 및 실란을 서로 혼합하여 변성실란실리케이트 합성물을 제조하는 방법은 특별히 한정되는 것은 아니지만, 추천하기로는 실리케이트 100중량부를 기준으로, 실리케이트에 실란 0.1 내지 2중량부를 95 내지 110℃의 온도범위에서 희석하여 200 내지 400rpm의 속도로 1 내지 2시간 동안 교반하는 것을 포함한다.The method for preparing the modified silane silicate compound by mixing the silicate and the silane is not particularly limited but preferably 0.1 to 2 parts by weight of silane is added to the silicate at a temperature ranging from 95 to 110 ° C And stirring for 1 to 2 hours at a speed of 200 to 400 rpm.
바람직한 변성실란실리케이트 합성물의 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 고분자 수지 100중량부 기준으로 5 내지 20중량부를 사용하는 것이 좋다.The amount of the modified silane silicate compound to be used is not particularly limited, but it is recommended to use 5 to 20 parts by weight based on 100 parts by weight of the polymer resin.
특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물, 특정적으로 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물은 조성물을 자외선으로부터 보호하여 안정성을 제공하기 위하여 고분자 수지 100중량부 기준으로 2 내지 10중량부의 안정제를 더 포함할 수 있다.In a specific embodiment, the fungicide composition according to the present invention, specifically the fungicide composition comprising sodium hypochlorite, may contain 2 to 10 parts by weight of a stabilizer based on 100 parts by weight of the polymeric resin in order to protect the composition against ultraviolet rays to provide stability .
바람직한 안정제로는 아크릴 폴리올 수지, 무황변 폴리 우레아수지, 폴리이소시아네이트 또는 이들의 혼합물을 사용하는 것이 좋다.Preferred stabilizers are acrylic polyol resins, non-yellowing polyurea resins, polyisocyanates or mixtures thereof.
다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 실온에서 효과적으로 경화하고 내열성, 저온 성능, 내화학성, 내용매성 및 내유성과 같은 개선된 특성을 제공하기 위하여 아미노 함유 실록산(Aminofunctional siloxan)을 더 포함할 수 있다.In another specific embodiment, the antifungal composition according to the present invention further comprises an aminofunctional siloxane to effectively cure at room temperature and to provide improved properties such as heat resistance, low temperature performance, chemical resistance, solvent resistance and oil resistance .
상기 아미노 함유 실록산은 특별히 제한되는 것은 아니며, 일례로서 아미노메틸폴리디메틸실록산을 들 수 있고, 그 사용량은 고분자 수지 100중량부를 기준으로 2 내지 10중량부인 것을 추천한다.The amino-containing siloxane is not particularly limited, and for example, aminomethylpolydimethylsiloxane is exemplified, and its amount to be used is preferably 2 to 10 parts by weight based on 100 parts by weight of the polymer resin.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 접착성 및 부착강도를 향상시키기 위하여 고분자 수지 100중량부 기준으로 3 내지 15중량부의 옥틸트리에톡시실란을 더 포함할 수 있다.In another specific embodiment, the antifungal agent composition according to the present invention may further contain 3 to 15 parts by weight of octyltriethoxysilane based on 100 parts by weight of the polymer resin to improve adhesion and adhesion strength.
바람직한 옥틸트리에톡시실란은 단량체 형태로 사용가능하며, 상기 단량체의 분자량은 특별히 한정되는 것은 아니지만, 바람직하게는 150 내지 450Da인 것이 좋다.The preferred octyltriethoxysilane can be used in the form of a monomer, and the molecular weight of the monomer is not particularly limited, but is preferably 150 to 450 Da.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 건조층의 표면 택키(tacky)를 방지하여 표면오염을 방지하기 위한 왁스를 고분자 수지 100중량부 기준으로 2 내지 5중량부 더 포함할 수 있다.In another specific embodiment, the fungicide composition according to the present invention may further contain 2 to 5 parts by weight of a wax for preventing surface tackiness of the dried layer and preventing surface contamination based on 100 parts by weight of the polymer resin .
바람직한 왁스로는 폴리에틸렌 왁스 또는 폴리프로필렌 왁스 또는 이들의 혼합물을 사용하는 것이 좋다.As the preferable wax, polyethylene wax or polypropylene wax or a mixture thereof is preferably used.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 조성물의 수명 연장을 위하여 마그네슘 실리케이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the fungicide composition according to the present invention may further comprise magnesium silicate in an amount of 1 to 5 parts by weight based on 100 parts by weight of the polymeric resin for extending the life of the composition.
상기, 마그네슘 실리케이트는 내화학성 및 내약품성과 풍화 저항성이 우수한 물성을 갖고 있으므로 곰팡이 방지제 조성물에 포함되면 상기와 같은 특성에 의해 수명이 연장되는 것이다.Since magnesium silicate has excellent chemical resistance, chemical resistance and weathering resistance, if it is included in the fungicide composition, the lifespan is extended due to the above characteristics.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 점도 조절 및 강도증진을 위하여 테트라에틸렌펜타민(Tetraethylenepentamine; TEPA)을 고분자 수지 100중량부 기준으로 1 내지 10중량부 더 포함할 수 있는데, 테트라에틸렌펜타민이 1중량부 미만이면 그 효과가 미미하며, 10중량부를 초과하면 그 양이 과다하여 곰팡이 방지제 조성물의 물성에 좋지 않은 영향을 줄 수 있다.In another specific embodiment, the fungicide composition according to the present invention may further comprise 1 to 10 parts by weight of tetraethylenepentamine (TEPA) based on 100 parts by weight of the polymer resin for controlling viscosity and strength, When the amount of ethylene pentamine is less than 1 part by weight, the effect is insignificant. When the amount is more than 10 parts by weight, the amount thereof is excessive, which may adversely affect the physical properties of the antifungal agent composition.
또 다른 특정 양태로서, 본 발명에 곰팡이 방지제 조성물은 점도증진 및 부착력 강화를 위하여 고분자 수지 100중량부를 기준으로 5 내지 10중량부의 알긴산 나트륨을 더 포함할 수 있는데, 상기 고분자 수지 100중량부에 대하여 함량이 5중량부 미만이면 소수성이 저하되고, 함량이 10중량부를 초과하면 과도하게 점도가 상승되어 좋지 않다.In another specific embodiment, the fungicide composition according to the present invention may further comprise 5 to 10 parts by weight of sodium alginate based on 100 parts by weight of the polymer resin for the purpose of enhancing viscosity and enhancing adhesion. In 100 parts by weight of the polymer resin, When the amount is less than 5 parts by weight, the hydrophobicity decreases. When the content exceeds 10 parts by weight, the viscosity is excessively increased.
상기 알긴산 나트륨은(C6H8O6)n으로 표시되는 다당류의 하나로서 카르복실기를 가지고 있으며, 다시마류를 소다회 처리하여 만들 수 있는데, 알긴산 나트륨 자체에 점성을 갖고 있어 이를 곰팡이 방지제 조성물에 혼입되면 점도증진 및 부착력을 강화하게 된다.The sodium alginate is one of the polysaccharides represented by (C 6 H 8 O 6 ) n and has a carboxyl group. The sodium alginate itself can be made by soda ash treatment. The sodium alginate itself has a viscosity, and when it is incorporated into the antifungal composition Thereby enhancing viscosity and adhesion.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 초기 접착력을 강화하기 위하여 폴리비닐알콜을 더 포함할 수 있는데, 폴리비닐알콜은 곰팡이 방지제 조성물의 구성성분의 분산성을 좋게 할 뿐만 아니라, 초기의 끈적임 정도(tacky property)도 증가되어 초기접착력을 개선하여 들뜸 현상, 뒤틀림 등의 불량률을 감소시킬 수 있다.In another specific embodiment, the fungicide composition according to the present invention may further comprise polyvinyl alcohol in order to enhance the initial adhesive strength. The polyvinyl alcohol not only improves the dispersibility of the components of the fungicide composition, The tacky property of the adhesive is also increased to improve the initial adhesive force, thereby reducing the defective rate such as floating phenomenon and warping.
상기 폴리비닐알콜의 사용량은 고분자 수지 100중량부를 기준으로 2 내지 10중량부인데, 폴리비닐알콜이 2중량부 이하 일 때는 그 효과가 미미하며, 10중량부 이상일 경우에는 그 양이 과도하여 경제적이지 못할 뿐만 아니라, 곰팡이 방지제 조성물의 내후성 등에 나쁜 영향을 미칠 수 있어 바람직하지 않다.The amount of the polyvinyl alcohol used is 2 to 10 parts by weight based on 100 parts by weight of the polymer resin. When the amount of the polyvinyl alcohol is 2 parts by weight or less, the effect is insignificant. When the amount is 10 parts by weight or more, But also the weather resistance and the like of the antifungal agent composition may be adversely affected.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 고분자 수지 100중량부를 기준으로 1 내지 5중량부의 글리세린을 더 포함할 수 있다. In another specific embodiment, the fungicide composition according to the present invention may further comprise 1 to 5 parts by weight of glycerin based on 100 parts by weight of the polymer resin.
상기 글리세린은 곰방이 방지제 조성물 도포 후 발생할 수 있는 백화현상을 방지하는 역할을 한다.The glycerin serves to prevent bleaching phenomenon that may occur after application of the antifouling composition.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 고분자 수지 100중량부를 기준으로 1 내지 5중량부의 파라핀 오일, 아마인유 또는 테레핀유에서 선택되는 하나 이상의 오일을 더 포함할 수 있는데, 상기 오일은 곰팡이 방지제 조성물이 도포되는 코팅층의 표면의 광택을 증가 시키고 표면을 매끄럽게 하는 역할을 한다.In another specific embodiment, the antifungal composition according to the present invention may further comprise 1 to 5 parts by weight of at least one oil selected from paraffin oil, linseed oil or terphene oil based on 100 parts by weight of the polymer resin, The antifungal agent composition serves to increase the gloss of the surface of the coating layer to which the antifungal agent composition is applied and smooth the surface.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 고분자 수지 100중량부를 기준으로 1 내지 5중량부의 부틸셀루솔브를 더 포함할 수 있다.In another specific embodiment, the antifungal composition according to the present invention may further comprise 1 to 5 parts by weight of butyl cellosolve based on 100 parts by weight of the polymer resin.
상기 부틸셀루솔부(butyl cellosolve)는 곰팡이 방지제 조성물의 건조속도를 지연시킴으로써 작업성을 향상시킬 수 있는데, 즉, 곰팡이 방지제 조성물의 코팅 형성시 건조속도의 차이에 의해 건조시간이 상이해져 표면 상태가 불균일하게 되는 것을 미연에 방지하는 역할을 하는 것이다. The butyl cellosolve can improve the workability by delaying the drying speed of the antifungal agent composition. That is, the drying time is different due to the difference in the drying speed during the formation of the antifungal agent composition, It is the role of preventing it from being done beforehand.
또 다른 특정 양태로서, 본 발명에 따른 곰팡이 방지제 조성물은 고분자 수지 100중량부를 기준으로 1 내지 5중량부의 소디윰스테아레이트를 더 포함할 수 있다.In another specific embodiment, the fungicide composition according to the present invention may further comprise 1 to 5 parts by weight of sodium dodecyl stearate based on 100 parts by weight of the polymer resin.
상기 소디윰스테아레이트는 곰방이 방지제 조성물의 표면에 대한 수분침투를 방지하면서 통기성을 확보하는 역할도 하는데, 1중량부 미만이면 목적한 침투방지기능을 얻을 수 없으며, 5중량부를 초과하면 곰팡이 방지제 조성물의 강도 저하현상을 나타내어 좋지 않다.
When the amount of the antifungal agent is less than 1 part by weight, the intended antifouling function can not be obtained. When the amount of the antifungal agent exceeds 5 parts by weight, Which is not preferable.
전술한 구성을 갖는 본 발명에 따른 곰팡이 방지제 조성물, 특정적으로 차아염소산나트륨을 포함하는 곰팡이 방지제 조성물의 시공방법은 당업계의 통상적인 시공방법이라면 특별히 한정되지 않는다.The fungicide composition according to the present invention having the above-mentioned constitution, specifically the antifungal agent composition containing sodium hypochlorite, is not particularly limited as long as it is a conventional method in the art.
이러한 일례로서, 본 발명에 따른 곰팡이 방지제 조성물의 시공방법은 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부, 탄산나트륨 1 내지 10중량부, 증점제 5 내지 10중량부, 나노세라믹입자 5 내지 10중량부, 항균성 물질 5 내지 20중량부, 계면활성제 2 내지 10중량부, 바인더 1 내지 15중량부, 재유화형 폴리머 분말 0.1 내지 10중량부, 용매 30 내지 150중량부, 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물을 건물의 외벽 또는 내벽에 포설하는 것을 포함할 수 있다. As an example, the antifungal agent composition according to the present invention may comprise 3 to 20 parts by weight of sodium hypochlorite, 1 to 10 parts by weight of sodium carbonate, 5 to 10 parts by weight of a thickener, 5 to 10 parts by weight of a nanoceramic particle 5 10 to 10 parts by weight of an anti-bacterial material, 2 to 10 parts by weight of a surfactant, 1 to 15 parts by weight of a binder, 0.1 to 10 parts by weight of a re-applied polymer powder, 30 to 150 parts by weight of a solvent, And 3 to 10 parts by weight of a fungicide composition on the outer wall or the inner wall of the building.
다른 일례로서, 본 발명에 따른 곰팡이 방지제 조성물의 시공방법은 대상표면의 이물질을 제거하여 청결하게 하는 청결단계; 상기 청결단계가 종료된 후 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부, 탄산나트륨 1 내지 10중량부, 증점제 5 내지 10중량부, 나노세라믹입자 5 내지 10중량부, 항균성 물질 5 내지 20중량부, 계면활성제 2 내지 10중량부, 바인더 1 내지 15중량부, 재유화형 폴리머 분말 0.1 내지 10중량부, 용매 30 내지 150중량부, 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물을 1 내지 3회 도포하는 조성물 도포단계; 및 상기 곰팡이 방지제 조성물 도포단계가 종료된 후 건조시키는 건조단계를 포함한다.As another example, the method of applying the antifungal agent composition according to the present invention may include a cleaning step of removing foreign matters on the surface of the object to be cleaned; After completion of the cleaning step, 3 to 20 parts by weight of sodium hypochlorite, 1 to 10 parts by weight of sodium carbonate, 5 to 10 parts by weight of a thickener, 5 to 10 parts by weight of nanoceramic particles, 5 parts by weight of an antimicrobial substance 5 To 20 parts by weight of a surfactant, 2 to 10 parts by weight of a surfactant, 1 to 15 parts by weight of a binder, 0.1 to 10 parts by weight of a re-lubrication type polymer powder, 30 to 150 parts by weight of a solvent and 3 to 10 parts by weight of a modified silane silicate compound Applying the composition for applying the inhibitor composition one to three times; And a drying step of drying after the application of the antifungal agent composition is completed.
또 다른 일례로서, 본 발명에 따른 곰팡이 방지제 조성물의 시공방법은 건축물의 내부 단열 벽체로 이용되는 석고판이 습기에 약하여 곰팡이가 빈번히 발생되는 것을 방지하기 위하여 석고판 또는 벽체 등의 마감재에 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부, 탄산나트륨 1 내지 10중량부, 증점제 5 내지 10중량부, 나노세라믹입자 5 내지 10중량부, 항균성 물질 5 내지 20중량부, 계면활성제 2 내지 10중량부, 바인더 1 내지 15중량부, 재유화형 폴리머 분말 0.1 내지 10중량부, 용매 30 내지 150중량부, 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물을 포설 후 도배 또는 도색 작업을 하는 것을 포함한다.
As another example, the method of applying the antifungal agent composition according to the present invention is a method in which a gypsum board used as an inner heat insulating wall of a building is weak in moisture and prevents molds from frequently occurring, 3 to 20 parts by weight of sodium hypochlorite, 1 to 10 parts by weight of sodium carbonate, 5 to 10 parts by weight of a thickener, 5 to 10 parts by weight of nanoceramics, 5 to 20 parts by weight of an antimicrobial substance, 2 to 10 parts by weight of a surfactant A binder, 1 to 15 parts by weight of a binder, 0.1 to 10 parts by weight of a re-fired polymer powder, 30 to 150 parts by weight of a solvent, and 3 to 10 parts by weight of a modified silane silicate composition. .
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
[실시예 1][Example 1]
수용성아크릴수지 100g, 차아염소산나트륨 10g, 탄산나트륨 5g, 폴리아크릴산 7g, 평균입경이 400nm인 실리콘카바이드 8g, 2-피리디오티올-1-옥사이드 소듐염 10g, 술폰 에스테르 5g, 멜라민 수지 7g, 에틸렌 초산 비닐 5g, 물 60g, 및 리튬실리케이트와 에폭시 실란을 합성하여 제조한 변성실란실리케이트 합성물 5g을 혼합하여 곰팡이 방지제 조성물을 제조하였다.
100 g of water-soluble acrylic resin, 10 g of sodium hypochlorite, 5 g of sodium carbonate, 7 g of polyacrylic acid, 8 g of silicon carbide having an average particle diameter of 400 nm, 10 g of 2-pyridothiol-1-oxide sodium salt, 5 g of sulfone ester, 5 g of water, 60 g of water, and 5 g of a modified silane silicate composite prepared by synthesizing lithium silicate and epoxy silane were mixed to prepare a fungicide composition.
[실시예 2][Example 2]
실시예 1과 동일한 방법으로 실시하되, 항균성 물질인 2-피리디오티올-1-옥사이드 소듐염 10g 대신 2-피리디오티올-1-옥사이드 소듐염을 코어로 하여 외벽면에 멜라민 수지가 코팅된 항균성 마이크로캡슐 10g을 사용하여 실시하였다.
Except that 10 g of 2-pyridothiol-1-oxide sodium salt, which is an antimicrobial substance, was used instead of the antimicrobial substance, 2-pyridothiol-1-oxide sodium salt was used as a core, and antimicrobial activity And 10 g of microcapsules.
[실시예 3][Example 3]
실시예 1과 동일한 방법으로 실시하되, 항균성 물질인 2-피리디오티올-1-옥사이드 소듐염 10g 대신 금속알콕시드기를 가진 항균성 물질인 이소프로필메틸페놀 실리콘 알콕사이드가 이산화티타늄에 커플링된 항균성 초미립자 분말 10g을 사용하여 실시하였다.Except that 10 g of 2-pyridothiol-1-oxide sodium salt, which is an antimicrobial substance, was used instead of the antimicrobial ultrafine particle powder of isopropylmethylphenol silicon alkoxide, which is an antibacterial substance having a metal alkoxide group, 10 g.
이때, 상기 항균성 초미립자 분말의 평균 일차 입도는 50 내지 100nm이고, 이차 입도는 0.5 내지 1㎛였다.
At this time, the average primary particle size of the antibacterial ultrafine particle powder was 50 to 100 nm, and the secondary particle size was 0.5 to 1 占 퐉.
[실시예 4][Example 4]
실시예 1과 동일한 방법으로 실시하되, 아크릴 폴리올 수지 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of acrylic polyol resin was further added.
[실시예 5][Example 5]
실시예 1과 동일한 방법으로 실시하되, 아미노메틸폴리디메틸실록산 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of aminomethylpolydimethylsiloxane was further added.
[실시예 6][Example 6]
실시예 1과 동일한 방법으로 실시하되, 분자량 약 400Da의 옥틸트리에톡시실란 7g을 더 부가하여 실시하였다.
7 g of octyltriethoxysilane having a molecular weight of about 400 Da was further added in the same manner as in Example 1.
[실시예 7][Example 7]
실시예 1과 동일한 방법으로 실시하되, 폴리에틸렌 왁스 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of polyethylene wax was further added.
[실시예 8][Example 8]
실시예 1과 동일한 방법으로 실시하되, 마그네슘 실리케이트 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of magnesium silicate was further added.
[실시예 9][Example 9]
실시예 1과 동일한 방법으로 실시하되, 테트라에틸렌펜타민 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of tetraethylene pentamine was further added.
[실시예 10][Example 10]
실시예 1과 동일한 방법으로 실시하되, 알긴산 나트륨 7g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 7 g of sodium alginate was further added.
[실시예 11][Example 11]
실시예 1과 동일한 방법으로 실시하되, 폴리비닐알콜 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of polyvinyl alcohol was further added.
[실시예 12][Example 12]
실시예 1과 동일한 방법으로 실시하되, 글리세린 2g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 2 g of glycerin was added.
[실시예 13][Example 13]
실시예 1과 동일한 방법으로 실시하되, 파라핀 오일 4g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 4 g of paraffin oil was further added.
[실시예 14][Example 14]
실시예 1과 동일한 방법으로 실시하되, 부틸셀루솔부 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of butylcellulose was added.
[실시예 15][Example 15]
실시예 1과 동일한 방법으로 실시하되, 소디윰스테아레이트 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of sodium dodecyl stearate was further added.
[비교예 1][Comparative Example 1]
실시예 1과 동일한 방법으로 실시하되, 차아염소산나트륨 및 항균성 물질을 제외하고 실시하였다.
The same procedure as in Example 1 was carried out except that sodium hypochlorite and antimicrobial substances were excluded.
[비교예 2][Comparative Example 2]
실시예 1과 동일한 방법으로 실시하되, 차아염소산나트륨을 제외하고 실시하였다.
The procedure of Example 1 was repeated except that sodium hypochlorite was excluded.
[실험][Experiment]
실시예 및 비교예에 따라 제조된 곰팡이 방지제 조성물을 콘크리트로 이루어진 0.5m*0.5m 크기의 평면에 도포한 후 도포성, 항곰팡이성 및 항균성 실험을 실시하여 그 결과를 표 1로 나타냈다. The antifungal agent compositions prepared according to the examples and comparative examples were applied to a flat surface of 0.5 m * 0.5 m made of concrete and subjected to coating, antifungal and antimicrobial tests, and the results are shown in Table 1.
표 1에 나타난 바와 같이, 차아염소산나트륨 및 항균성 물질을 포함하는 실시예에 따른 곰팡이 방지제 조성물이 비교예 보다 높은 항곰팡이성 및 항균성을 나타내는 것으로 확인되었다.
As shown in Table 1, it was confirmed that the antifungal composition according to the Example including sodium hypochlorite and the antimicrobial substance showed higher antifungal and antimicrobial properties than the Comparative Example.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the spirit and scope of the present invention as defined by the appended claims and their equivalents.
Claims (5)
차아염소산나트륨 3 내지 20중량부;
탄산나트륨 1 내지 10중량부;
증점제 5 내지 10중량부;
나노세라믹입자 5 내지 10중량부;
항균성 물질 5 내지 20중량부;
계면활성제 2 내지 10중량부;
바인더 1 내지 15중량부;
재유화형 폴리머 분말 0.1 내지 10중량부;
용매 30 내지 150중량부; 및
변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물에,
아미노 함유 실록산을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고,
옥틸트리에톡시실란을 고분자 수지 100중량부를 기준으로 3 내지 15중량부로 더 포함하며,
왁스를 고분자 수지 100중량부를 기준으로 2 내지 5중량부로 더 포함하고,
마그네슘 실리케이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
테트라에틸렌펜타민을 고분자 수지 100중량부를 기준으로 1 내지 10중량부로 더 포함하고,
알긴산 나트륨을 고분자 수지 100중량부를 기준으로 5 내지 10중량부로 더 포함하며,
폴리비닐알콜을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고,
글리세린을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
오일을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하고,
부틸셀루솔브를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
소디윰스테아레이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 곰팡이 방지제 조성물.
On the basis of 100 parts by weight of the polymer resin,
3 to 20 parts by weight of sodium hypochlorite;
1 to 10 parts by weight of sodium carbonate;
5 to 10 parts by weight of a thickener;
5 to 10 parts by weight of nano-ceramic particles;
5 to 20 parts by weight of an antibacterial substance;
2 to 10 parts by weight of a surfactant;
1 to 15 parts by weight of a binder;
0.1 to 10 parts by weight of a re-forming type polymer powder;
30 to 150 parts by weight of a solvent; And
To 3 to 10 parts by weight of a modified silane silicate composition,
Further comprising 2 to 10 parts by weight of an amino-containing siloxane based on 100 parts by weight of the polymer resin,
Further comprising 3 to 15 parts by weight of octyltriethoxysilane based on 100 parts by weight of the polymer resin,
The wax is further contained in an amount of 2 to 5 parts by weight based on 100 parts by weight of the polymer resin,
Further comprising 1 to 5 parts by weight of magnesium silicate based on 100 parts by weight of the polymer resin,
Further comprising 1 to 10 parts by weight of tetraethylene pentamine based on 100 parts by weight of the polymer resin,
Further comprising 5 to 10 parts by weight of sodium alginate based on 100 parts by weight of the polymer resin,
Further comprising 2 to 10 parts by weight of polyvinyl alcohol based on 100 parts by weight of the polymer resin,
Further comprising 1 to 5 parts by weight of glycerin based on 100 parts by weight of the polymer resin,
Wherein the oil further comprises 1 to 5 parts by weight based on 100 parts by weight of the polymer resin,
1 to 5 parts by weight of butyl cellosolve based on 100 parts by weight of the polymer resin,
And 1 to 5 parts by weight of sodium dodecyl stearate based on 100 parts by weight of the polymer resin.
상기 청결단계가 종료된 후 고분자 수지 100중량부 기준으로, 차아염소산나트륨 3 내지 20중량부, 탄산나트륨 1 내지 10중량부, 증점제 5 내지 10중량부, 나노세라믹입자 5 내지 10중량부, 항균성 물질 5 내지 20중량부, 계면활성제 2 내지 10중량부, 바인더 1 내지 15중량부, 재유화형 폴리머 분말 0.1 내지 10중량부, 용매 30 내지 150중량부, 및 변성실란실리케이트 합성물 3 내지 10중량부를 포함하는 곰팡이 방지제 조성물에, 아미노 함유 실록산을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고, 옥틸트리에톡시실란을 고분자 수지 100중량부를 기준으로 3 내지 15중량부로 더 포함하며, 왁스를 고분자 수지 100중량부를 기준으로 2 내지 5중량부로 더 포함하고, 마그네슘 실리케이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 테트라에틸렌펜타민을 고분자 수지 100중량부를 기준으로 1 내지 10중량부로 더 포함하고, 알긴산 나트륨을 고분자 수지 100중량부를 기준으로 5 내지 10중량부로 더 포함하며, 폴리비닐알콜을 고분자 수지 100중량부를 기준으로 2 내지 10중량부로 더 포함하고, 글리세린을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 오일을 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하고, 부틸셀루솔브를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 소디윰스테아레이트를 고분자 수지 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 곰팡이 방지제 조성물을 1 내지 3회 도포하는 조성물 도포단계; 및
상기 곰팡이 방지제 조성물 도포단계가 종료된 후 건조시키는 건조단계를 포함하는 곰팡이 방지제 조성물 시공방법.
A cleaning step of removing foreign matter on the surface of the object to be cleaned;
After completion of the cleaning step, 3 to 20 parts by weight of sodium hypochlorite, 1 to 10 parts by weight of sodium carbonate, 5 to 10 parts by weight of a thickener, 5 to 10 parts by weight of nanoceramic particles, 5 parts by weight of an antimicrobial substance 5 To 20 parts by weight of a surfactant, 2 to 10 parts by weight of a surfactant, 1 to 15 parts by weight of a binder, 0.1 to 10 parts by weight of a re-lubrication type polymer powder, 30 to 150 parts by weight of a solvent and 3 to 10 parts by weight of a modified silane silicate compound Wherein the amino resin composition further comprises 2 to 10 parts by weight of an amino-containing siloxane based on 100 parts by weight of the polymer resin and 3 to 15 parts by weight of octyltriethoxysilane based on 100 parts by weight of the polymer resin, Based on 100 parts by weight of the polymeric resin, 1 to 5 parts by weight of the magnesium silicate, based on 100 parts by weight of the polymeric resin, And 1 to 10 parts by weight of tetraethylenepentamine based on 100 parts by weight of the polymer resin, and further comprising sodium alginate in an amount of 5 to 10 parts by weight based on 100 parts by weight of the polymer resin, wherein the polyvinyl alcohol is mixed with 100 parts by weight of the polymer resin Based on 100 parts by weight of the polymer resin, the oil further comprises 1 to 5 parts by weight based on 100 parts by weight of the polymer resin, and the butyl cellosolve Wherein the composition further comprises 1 to 5 parts by weight based on 100 parts by weight of the polymer resin and 1 to 5 parts by weight of sodium dodecyl stearate based on 100 parts by weight of the polymer resin, ; And
And a drying step of drying after the application of the fungicide composition composition is completed.