KR101669406B1 - A Ceramic Welding Contact Tip prevented burn back - Google Patents

A Ceramic Welding Contact Tip prevented burn back Download PDF

Info

Publication number
KR101669406B1
KR101669406B1 KR1020160007519A KR20160007519A KR101669406B1 KR 101669406 B1 KR101669406 B1 KR 101669406B1 KR 1020160007519 A KR1020160007519 A KR 1020160007519A KR 20160007519 A KR20160007519 A KR 20160007519A KR 101669406 B1 KR101669406 B1 KR 101669406B1
Authority
KR
South Korea
Prior art keywords
tip
welding
ceramic
connecting rod
front surface
Prior art date
Application number
KR1020160007519A
Other languages
Korean (ko)
Inventor
정래식
Original Assignee
정래식
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정래식 filed Critical 정래식
Priority to KR1020160007519A priority Critical patent/KR101669406B1/en
Application granted granted Critical
Publication of KR101669406B1 publication Critical patent/KR101669406B1/en

Abstract

The present invention relates to a copper contact tip mounted on a front end of a gas metal arc type welding device receiving wires at constant speeds and forming a molten pool with welding arc generated between base materials, and inducing the molten pool by transmitting a welding current to the wires. The copper contact tip comprises: a copper tip body having a screw on one side to be mounted in the welding device, and having a through-hole formed on a center to supply the wires through the center; a current flow connecting rod protruding from the front end of the tip body; a burn-back preventing unit protruding from a front surface of the current flow connection rod; and a ceramic reinforcing tip formed into a cylindrical shape to prevent an increase in diameter of a tip outlet and burn back due to the welding arcs. The copper contact tip is capable of preventing the increase in diameter of the tip outlet due to abrasions when welding or the burn back that welding scatters due to the arc generated when arc-welding are attached to a front surface of the welding tip by seating the burn-back preventing unit and the ceramic reinforcing tip of which the thermal deformation are prevented on a front surface of the tip body of the welding body, thereby remarkably improving durability of the welding tip and remarkably reducing expenses for purchasing a new welding tip due to damage to the welding tip. In addition, the welding tip is capable of being used for a long time by reinforcing a strength of the copper welding tip. Additionally, thermal deformation caused by heat is reduced by securing a fine space in the welding tip, thereby obtaining an effect of safely using the welding tip.

Description

번백방지 세라믹 용접팁{A Ceramic Welding Contact Tip prevented burn back }BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a ceramic-

본 발명은 수명이 향상되도록 부싱이 구비된 가스메탈아크용접용 콘택트팁에 관한 것으로, 상세하게는 아크용접시 발생되는 아크로 인한 용접스캐터가 용접팁의 전단에 부착되는 번백이나 용접시 마모로 인한 팁 출구 구경의 확장되는 것을 방지하여 용접팁의 수명을 대폭 향상시킬 수 있으며, 용접팁 손상으로 인한 구입비용을 대폭 절감할 수 있고, 용이하게 통전되어 안전하게 장시간 용접할 수 있으며, 구리재질의 용접팁의 강도가 보강되어 장시간 사용할 수 있는 번백방지 세라믹용접팁에 관한 것이다.The present invention relates to a contact tip for gas metal arc welding having a bushing for improving the service life thereof. More particularly, the present invention relates to a contact tip for arc welding, It is possible to significantly increase the lifetime of the welding tip by preventing the tip exit diameter from being enlarged, to significantly reduce the purchase cost due to the damage of the welding tip, to easily carry out the welding for a long time safely, Resistant ceramic welding tip that can be used for a long time.

일반적으로 와이어를 모재로 사용하는 가스메탈아크 용접은 공급되는 용접 와이어 선단과 모재 사이에서 발생되는 용접아크에 의하여 용융되는 용융풀을 이용하는 것이다. In general, gas metal arc welding using a wire as a base material uses a molten pool which is melted by a welding arc generated between the tip of a welding wire and a base material to be supplied.

이와 같은 가스메탈아크 용접에서 안정적인 용접이 진행되기 위하여 용접전원으로부터 공급되는 콘택트팁을 이용하여 와이어에 전달되어야 한다.In order to perform stable welding in such gas metal arc welding, it is required to be transferred to the wire using a contact tip supplied from a welding power source.

상기 콘텍트팁은 용접전류를 와이어에 전송하면서, 와이어를 용접하고자 하는 위치로 유도하는 것이다.The contact tip is to direct the wire to a position to be welded, while transferring the welding current to the wire.

그런데 상기 콘택트팁을 장시간 사용하게 되면 이러한 기능이 저하되어 팁을 교환하여야 하는바, 최근 용접산업계에서 생산성 향상을 위해 콘택트 팁의 수명을향상시키기 위한 노력이 절실히 요구된다.However, if the contact tip is used for a long period of time, such a function is deteriorated and the tip must be replaced. Recently, in order to improve the productivity in the welding industry, efforts to improve the life of the contact tip are urgently required.

상기 콘택트팁의 수명의 결정하는 주요 요인은 아크의 불안정으로 스페터가 팁출구에 융착이나 용융되는 번백(burn back)과 팁마모에 의한 팁 출구 구경의 확장이 있는데, 현재 이론적으로 접근한 연구가 보고되지 않고 있으바, 이는 팁의 수명을 정령화하기 위해서는 많은 노력과 시간이 소요되기 때문에 산업현장에서 수행하기 어렵게 되므로 이에 따른 많은 노력이 요구되고 있다.A major factor in determining the service life of the contact tip is the burn back in which the spatter is fused or melted at the tip outlet due to instability of the arc and the tip exit aperture is enlarged by tip wear. It is difficult to perform in the industrial field because it takes a lot of effort and time to adjust the lifetime of the tip.

상기와 같은 콘택트팁이 사용되는 가스메탈아크용접의 대표적으로 CO2 용접이 주로사용되고 있으며, CO2용접은 불활성 가스인 CO2 가스를 방출하여 용접부를 대기와 차단하고, 그 속에 용접 와이어를 이송시켜 이를 전극으로 하여 용접 모재와 방전 현상을 발생시켜 용접하는 용접방법이다.CO2 welding is mainly used for the gas metal arc welding using the contact tip as described above. CO2 welding releases CO 2 gas, which is an inert gas, to cut off the welding part from the atmosphere, transfer the welding wire into the electrode, Thereby generating a discharge phenomenon with the welding base material.

특히, 자동차부품의 용접은 대량으로 생산하는 특성상 로봇을 이용하여 자동화 시스템을 갖춘 CO2 용접이 주로사용된다.Especially, CO2 welding with automation system using robots is mainly used for the production of automobile parts in large quantities.

도 6은 일반적인 탄산가스 용접기의 전체 구성도로서, 용접의 아암(4) 선단에 용접 토치(2)가 장착되고, 상기 용접 토치(2)의 내부에는 와이어(3)를 공급받을 수 있도록 용접 팁(1)이 안착되며, 상기 용접 팁(1)과 용접 토치(2) 사이의 공간부(5)를 통하여 CO2 탱크로부터 공급되는 CO2 가스가 용접부(6)를 향하여 방출되도록 하여 용접부(6)를 대기와 차단시키게 되는 것이다.FIG. 6 is an overall configuration view of a general carbon dioxide gas welding machine in which a welding torch 2 is mounted on the tip of an arm 4 of a welding torch and a wire 3 is inserted into the welding torch 2, And the CO 2 gas supplied from the CO2 tank is discharged toward the welding portion 6 through the space portion 5 between the welding tip 1 and the welding torch 2 so that the welding portion 6 It is blocked by the atmosphere.

그러나 상기와 같은 종래의 탄산가스 용접기용 용접 팁(1)은, 통전이 되도록 일체형의 구리재질로 형성되는바, 일정시간이 경과되면 용접팁에 과열이 발생되어 번백이나 팁출구의 확장으로 인하여 자주 교체하여야 할 뿐만 아니라 교체로 인한 비용이 과다하게 발생되는 문제점이 있었다.However, since the conventional welding tip 1 for a carbon dioxide gas welding machine is formed of an integral copper material so as to be energized, overheating occurs in the welding tip after a lapse of a predetermined time, There is a problem that not only replacement but also excessive replacement cost is incurred.

상기 문제점을 해소하기 위하여 본 발명의 출원인은 "세라믹이 적용된 탄소 용접팁"을 개발하여 특허등록(등록번호 제10-1214902)을 하였다.In order to solve the above problem, the applicant of the present invention developed a patented "Carbon Welding Tip with Ceramic Application" (Registration No. 10-1214902).

그러나 상기 등록특허 "세라믹이 적용된 탄소용접팁"은 도 7에 도시된 바와 같이, 용접의 아암(4) 선단에 용접 토치(2)가 장착되고, 상기 용접 토치(2)의 내부에는 와이어(3)를 공급받을 수 있도록 용접 팁(1)이 안착되며, 용접팁(1)의 몸통(100)의 선단에 체결부(200)를 구비하고, 상기 체결부(200)에 세라믹제질의 세라믹팁(300)을 안착시켜 용접시 발생되는 고열로 용접팁이 변형되는 것을 미연에 방지할 수 있으나, 상기 용접팁(1)의 몸통(100)의 선단에 부착된 세라믹팁(300)과 구리재질의 용접팁(1)과의 통전이 불가능하여 용접 와이어(3)가 쇼트되어 용접이 불가능하게 되는 문제점이 있었다.7, the welding torch 2 is mounted on the tip of the arm 4 of the welding, and the wire 3 is inserted into the welding torch 2, And a fastening part 200 is provided at the tip of the body 100 of the welding tip 1. The ceramic tip of a ceramic material is attached to the fastening part 200 The ceramic tip 300 attached to the tip of the body 100 of the welding tip 1 may be welded with a copper material 300. In this case, The welding with the tip 1 can not be conducted, and the welding wire 3 is short-circuited, which makes welding impossible.

또한 종래의 세라믹이 적용된 탄소용접팁은 체결부(200)를 가공하는 시간이 장시간 소요되어 현장에 적용이 곤란하고, 세라믹팁(300)의 전면에 천공된 관통으로 용접 스케터가 유입되어 용접와이어의 공급이 곤란하게 되는 문제점도 있었다.In addition, since the carbon welding tip using the conventional ceramic is required to process the fastening part 200 for a long time, it is difficult to apply it to the field, and the welding skater is pierced through the front surface of the ceramic tip 300, It is difficult to supply the fuel.

발명은 상기와 같은 종래 기술의 문제점을 해결하기 위해 창작된 것으로 본 발명에 의한 번백방지 세라믹용접팁의 목적은, 용접팁의 팁몸통 전면에 열변형이 방지되는 세라믹보강팁을 안착시켜 아크용접시 발생되는 아크로 인한 용접스캐터가 용접팁의 전면에 부착되는 번백이나 용접시 마모로 인한 팁 출구 구경의 확장되는 것을 방지하여 용접팁의 수명을 대폭 향상시킬 수 있으며, 용접팁 손상으로 인한 구입비용을 대폭 절감할 수 있고, 상기 팁몸통의 전면에 번백방지돌출부를 구비하여 용이하게 통전되어 안전하게 장시간 용접할 수 있을 뿐만 아니라 용접스케터가 내측으로 유입되는 되는 것이 방지되어 장시간 안전하게 사용할 수 있고, 용접팁 사이에 미세한 공간이 확보되면서 열로 한인 열변형이 감소되어 안전하게 사용할 수 있는데 그 목적이 있다.SUMMARY OF THE INVENTION It is an object of the present invention to provide an anti-sparking ceramic welding tip, in which a ceramic reinforcing tip, which prevents thermal deformation, is placed on the entire tip body of a welding tip, It is possible to improve the life of the welding tip by preventing the welding spot caused by the generated arc from being spread on the front surface of the welding tip or expanding the tip exit diameter due to abrasion during welding, It is possible to safely use the welding torch for a long time and to prevent the welder from flowing into the inside, so that the welding torch can be safely used for a long time, As the minute space is ensured between heat and heat, There is.

본 발명은 상기한 목적을 달성하기 위한 수단으로, 본 발명에 따른 번백방지 세라믹용접팁은, 일정속도로 와이어가 공급되어 모재 사이에서 발생되는 용접아크에 의하여 용융풀을 형성하는 가스메탈아크식 용접기의 선단에 장착되며, 용접전류를 와이어에 전송하여 용융풀을 유도하는 구리재질의 콘택트팁에 있어서, 상기 용접기에 장착되도록 일측에 나사 형성되고, 중앙에 와이어가 공급되도록 천공된 관통공이 형성된 구리재질의 팁몸통과; 상기 팁몸통의 전면에 상기 팁몸통의 외주부보다 협관되어 통전되도록 일체로 연결되고, 중앙에 와이어가 공급되도록 중앙이 천공된 원형바 형상의 통전연결봉과; 상기 통전연결봉의 전면에 용접 아크로 인한 번백과 팁 출구 구경의 확장이 방지되도록 상기 통전연결봉의 외주부보다 협관되어 일체로 돌출된 번백방지돌출부와; 상기 통전연결봉의 외주부에 용접시 열변형이 방지되도록 상기 통전연결봉의 외주연을 감싸는 세라믹재질의 세라믹보강팁;으로 구성된 것을 특징으로 한다.In order to achieve the above object, according to the present invention, there is provided an anti-sparking ceramic welding tip, comprising: a gas metal arc welding machine for supplying a wire at a constant speed to form a molten pool by welding arc generated between the base metals; A contact tip of a copper material which is mounted on a tip of a welding wire and guides welding current to the wire to induce a molten pool. The contact tip is made of a copper material having a through hole formed at one side thereof to be mounted on the welding device, A tip body; A circular bar-shaped energizing connecting rod integrally connected to the front surface of the tip body so as to be energized more narrowly than the outer circumferential portion of the tip body; A protrusion protruding from the front surface of the power connection rod so as to protrude integrally from the outer circumference of the power connection rod so as to prevent the burr and the tip diameter of the tip from being enlarged due to the welding arc; And a ceramic reinforcing tip of ceramic material surrounding the outer periphery of the connection connecting rod so as to prevent thermal deformation during welding at the outer periphery of the connection connecting rod.

상기 세라믹보강팁은 내측으로 상기 통전연결봉에 삽입되어 안착되도록 일측이 개방된 캡형상의 세라믹본체와, 상기 세라믹본체의 전면에 상기 번백방지돌출부가 안착되도록 천공된 안착공과, 상기 세라믹본체의 전면에 용접 스캐터가 부착되는 것이 방지되도록 곡면으로 형성된 전면곡면부로 구성된 것을 특징으로 한다.The ceramic reinforced tip includes a cap-shaped ceramic body having one side opened to be inserted into the energizing connection rod inwardly, and a seating hole formed in the front surface of the ceramic body to perforate the anti- And a front curved portion formed in a curved surface so as to prevent the scatter from being attached.

상기 세라믹보강팁의 선단에는 강도가 보강되며 용접스캐터가 부착되는 것이 방지되도록 코팅된 보강코팅부가 형성된 것을 특징으로 한다.And a reinforcement coating portion coated on the tip of the ceramic reinforcing tip to prevent a weld spot from being attached to the tip of the ceramic reinforcing tip.

상기 통전연결봉과 세라믹보강팁의 사이에는 상기 세라믹보강팁이 통전연결봉에 고정되어 열변형이 방지되도록 세라믹 접착재가 구비된 것을 특징으로 한다.And a ceramic adhesive is provided between the energizing connecting rod and the ceramic reinforcing tip so that the ceramic reinforcing tip is fixed to the energizing connecting rod to prevent thermal deformation.

상기와 같은 구성을 가지는 본 발명인 번백방지 세라믹용접팁은 다음과 같은 효과가 있다.The anti-rebar ceramic welding tip of the present invention having the above-described structure has the following effects.

첫째, 용접팁의 팁몸통 전면에 일체로 돌출된 통전연결봉을 구비함으로써 용접 와이어가 통전기둥으로 용이하게 통전되어 안전하게 장시간 용접할 수 있으며,First, since the welding connecting rod is integrally projected on the entire tip body of the welding tip, the welding wire can be easily energized by the energizing column to securely weld for a long time,

둘째, 상기 통전연결봉의 선단에 일체로 돌출된 번백방지돌출부가 형성됨으로써 아크용접시 발생되는 아크로 인한 용접스캐터가 내측으로 유입되는 것이 방지되고 용접팁의 전면에 부착되는 것이 방지되어 번백으로 용접팁이 손상되는 것을 미연에 방지할 수 있고, 용접시 마모로 인한 팁 출구 구경의 확장되는 것을 방지하여 용접팁의 수명을 대폭 향상시킬 수 있고, Secondly, since the anti-rebound protrusion integrally protruded at the tip of the energizing connection rod is formed, it is prevented that the welding scatter due to the arc generated at the arc welding is prevented from flowing inward and is prevented from being attached to the front surface of the welding tip, Can be prevented from being damaged in advance and the tip diameter of the tip due to abrasion during welding can be prevented from being enlarged so that the life of the welding tip can be greatly improved,

셋째, 상기 통전연결봉의 외주부를 감싸는 세라믹재질의 세라믹보강팁을 구비함으로써 용접시 용접팁의 열변형과 아크로 인한 번백을 미연에 방지하여 용접팁의 수명을 대폭 향상시킬 수 있을 뿐만 아니라 용접팁 손상으로 인한 교체나 구입비용을 대폭 절감할 수 있고,Third, since the ceramic reinforced tip of the ceramic material that surrounds the periphery of the energizing connection rod is provided, thermal deformation of the welding tip during welding can be prevented and the lifetime of the welding tip can be remarkably improved, It is possible to greatly reduce the replacement cost and the purchase cost,

넷째, 상기 금속부시와 선단보강팁을 팀몸통에 접착재로 고정시킴으로써 그 사이에 미세한 공간이 확보되면서 열로 한인 열변형이 감소되어 안전하게 사용할 수 있는 효과가 있다. Fourth, since the metal bush and the tip end reinforcing tip are fixed to the team body with an adhesive, a minute space is secured therebetween, and thermal deformation of the terminal is reduced.

도 1은, 본 발명에 따른 세라믹용접팁을 나타낸 개요도.
도 2는, 본 발명에 따른 세라믹용접팁을 나타낸 사시도.
도 3은, 본 발명에 따른 세라믹용접팁의 분해사시도.
도 4는, 본 발명에 따른 세라믹용접팁의 단면도.
도 5는, 일반적인 CO2 용접기를 나타낸 개요도.
도 6은, 종래의 세라믹용접팁를 나타낸 개요도.1 is a schematic view of a ceramic welding tip according to the invention;
2 is a perspective view of a ceramic welding tip according to the present invention;
3 is an exploded perspective view of a ceramic welding tip according to the present invention;
4 is a cross-sectional view of a ceramic welding tip according to the present invention;
5 is a schematic view showing a typical CO2 welding machine;
6 is a schematic view showing a conventional ceramic welding tip;

이하에서는, 첨부도면을 참고하여 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명에 따른 번백방지 세라믹용접팁은 도 1 및 도 2에 도시된 바와 같이, 일정속도로 와이어(3)가 공급되어 모재(2) 사이에서 발생되는 용접아크에 의하여 용융풀을 형성하는 가스메탈아크식 용접기(1)의 선단에 장착되며, 용접전류를 와이어(3)에 전송하여 용융풀을 유도하는 구리재질의 콘택트팁(4)으로서, 구리재질의 팁몸통(10)과, 중앙이 천공된 원형바 형상의 통전연결봉(20)과, 상기 통전연결봉(20)의 외주부보다 협관되어 일체로 돌출된 번백방지돌출부(30)와, 세라믹재질의 세라믹보강팁(40)으로 구성된다.As shown in FIGS. 1 and 2, the anti-spark plug ceramic welding tip according to the present invention is a ceramic spark plug having a gas metal, which is supplied with a wire 3 at a constant speed and forms a molten pool by a welding arc generated between the base metals 2 A contact tip (4) made of copper and mounted on the tip of an arc welding machine (1) and guiding welding current to the wire (3) to induce a molten pool. The contact tip (4) comprises a copper tip body (10) And a ceramic reinforcing tip 40 made of a ceramic material, which are integrally protruded from the outer circumferential portion of the energizing connection rod 20, and protruding integrally.

즉, 상기 구리재질의 팁몸통(10)은 용접기(1)에 장착되도록 일측에 나사 형성되고, 중앙에 와이어가 공급되도록 천공된 관통공(11)이 형성된다.That is, the tip body 10 made of copper is screwed on one side to be mounted on the welder 1, and a through hole 11 is formed in the center so as to feed the wire.

상기 통전연결봉(20)은 팁몸통(10)의 전면에 상기 팁몸통(10)의 외주부보다 협관되어 통전되도록 일체로 연결되고, 중앙에 와이어(3)가 공급되도록 중앙이 천공된 원형바 형상으로 형성된다.The current connecting rod 20 is integrally connected to the front surface of the tip body 10 so as to be narrower than the outer circumferential portion of the tip body 10 and electrically connected to the tip body 10 and has a circular bar shape .

상기 번백방지돌출부(30)는 통전연결봉(20)의 전면에 용접 아크로 인한 번백(burn back)과 팁 출구 구경의 확장이 방지되도록 상기 통전연결봉(20)의 외주부보다 협관되어 일체로 돌출되고, 상기 번백방지돌출부(30)의 전면에는 상기 세라믹보강팁(40)의 선단보다 더 곡면으로 돌출되는 곡면돌출부(31)가 추가로 구성된다.The protruding protrusion 30 is integrally protruded from the outer circumferential portion of the energization connecting rod 20 so as to prevent a burn back of the welding arc and an extension of a tip outlet diameter from being formed on the front surface of the energizing connecting rod 20, The front surface of the rebound preventing protrusion 30 is further provided with a curved surface protruding portion 31 that protrudes more than the front end of the ceramic reinforcing tip 40.

상기 세라믹재질의 세라믹보강팁(40)은 통전연결봉(20)의 외주부에 용접시 열변형이 방지되도록 상기 통전연결봉(20)의 외주연을 감싸며, 세라믹재질이나 강화유리 등으로 형성된다.The ceramics reinforcing tip 40 of the ceramic material surrounds the outer circumference of the energizing connecting rod 20 so as to prevent thermal deformation when welding the outer circumferential portion of the energizing connecting rod 20 and is formed of a ceramic material or tempered glass.

그리고, 상기 세라믹보강팁(40)은 내측으로 상기 통전연결봉(20)에 삽입되어 안착되도록 일측이 개방된 캡형상의 세라믹본체(41)와, 상기 세라믹본체(41)의 전면에 상기 번백방지돌출부(30)가 안착되도록 천공된 안착공(42)과, 상기 세라믹본체(41)의 전면에 용접 스캐터가 부착되는 것이 방지되도록 곡면으로 형성된 전면곡면부(43)로 구성된다.The ceramic reinforcing tip 40 has a cap-shaped ceramic main body 41 having one side opened to be inserted into the energizing connecting rod 20 to be seated inwardly, And a front curved surface portion 43 formed as a curved surface so as to prevent a welding spot from being attached to the front surface of the ceramic main body 41. [

또한, 상기 세라믹보강팁(40)의 선단에는 강도가 보강되며 용접스캐터가 부착되는 것이 방지되도록 코팅된 보강코팅부(44)가 형성된다.Further, a reinforced coating portion 44 is formed on the tip of the ceramic reinforcing tip 40 so as to be reinforced in strength and prevented from adhering a welding spot.

한편, 상기 통전연결봉(20)과 세라믹보강팁(40)의 사이에는 상기 세라믹보강팁(40)이 통전연결봉(20)에 고정되어 열변형이 방지되도록 세라믹 접착재(45)로 접착되는 것도 바람직하다.It is also preferable that the ceramic reinforcing tip 40 is fixed to the energizing connecting rod 20 between the energizing connecting rod 20 and the ceramic reinforcing tip 40 and is bonded with a ceramic adhesive 45 so as to prevent thermal deformation .

상기와 같은 구성으로 이루어진 본 발명에 따른 번백방지 세라믹용접팁의 작용을 살펴보면 아래와 같다.The operation of the anti-rebound ceramic welding tip according to the present invention having the above-described structure will be described below.

본 발명에 따른 번백방지 세라믹용접팁은 도 1 및 도 2에 도시된 바와 같이, 용접기(1)에 용접토치의 선단에 장착되는 팁몸통(10)의 전면에 중앙이 천공된 원형바 형상의 통전연결봉(20)이 돌출되어 안전하게 통전되고, 상기 통전연결봉(20)의 외주부보다 협관된 번백방지돌출부(30)가 일체로 돌출되어 모재와 용이하게 통전되며, 상기 통전연결봉(20)와 번백방지돌출부(30)의 외주에 세라믹재질의 세라믹보강팁(40)이 감싸게 되어 용접시 아크로 인한 구리재질의 용접팁을 보호하게 된다.As shown in FIGS. 1 and 2, the anti-sparking ceramic welding tip according to the present invention has a circular bar-shaped energization (see FIG. 1) in which a center is perforated on the front surface of a tip body 10 mounted on a welding torch, The connecting rod 20 protrudes and is safely energized so that the whirling preventing protrusion 30 which is narrower than the outer circumferential portion of the energizing connecting rod 20 integrally protrudes to be easily energized with the base material so that the energizing connecting rod 20 and the non- The ceramic reinforcing tip 40 of ceramic material is wrapped around the outer periphery of the ceramic body 30 to protect the welding tip of the copper material due to the arc during welding.

즉, 상기 팁몸통(10)은 구리재질로 형성되어 용접전류가 와이어(3)에 전송되고, 일측에 일측에 나사 형성되어 용접기(1)에 연결되며, 중앙에 와이어가 공급되도록 관통공(11)이 천공된다.That is, the tip body 10 is formed of a copper material, and a welding current is transmitted to the wire 3, and a thread is formed on one side of the wire body 3 to be connected to the welding machine 1, ).

상기 통전연결봉(20)은 팁몸통(10)의 전면에 상기 팁몸통(10)의 외주부보다 협관되어 통전되도록 일체로 연결되고, 중앙에 와이어(3)가 공급되도록 중앙이 천공된 원형바 형상으로 형성된다.The current connecting rod 20 is integrally connected to the front surface of the tip body 10 so as to be narrower than the outer circumferential portion of the tip body 10 and electrically connected to the tip body 10 and has a circular bar shape .

상기 통전연결봉(20)은 팁몸통(10)의 전면에는 와이어(3)가 공급되도록 중앙이 천공되고, 상기 팁몸통(10)의 외주부보다 협관되어 통전되도록 팁몸통(10)과 일체로 원형바 형상으로 돌출됨으로써 모제와 와이어가 항시 통전되어 안정적으로 용접할 수 있게 된다.The power supply connection rod 20 is inserted into the tip body 10 so as to be integrally formed with the tip end of the tip body 10 so as to be narrower than the outer circumferential portion of the tip body 10, So that the mother substrate and the wire are constantly energized and can be stably welded.

상기 번백방지돌출부(30)는 중앙에 와이어(3)가 공급되도록 관통공이 천공되고, 상기 통전연결봉(20)의 외주부보다 협관되어 일체로 돌출되고 그 선단에 상기 세라믹보강팁(40)의 선단보다 더 곡면으로 돌출되는 곡면돌출부(31)가 추가로 돌출됨으로써 아크용접시 발생되는 아크로 인한 용접스캐터가 용접팁(1)의 전면에 부착되는 번백(Burn back)을 방지하여 용접팁의 수명을 대폭 향상시킬 수 있게 된다. The protruding protrusion 30 is formed with a through hole so as to be supplied with a wire 3 at the center thereof and is integrally protruded from the outer circumferential portion of the energizing connecting rod 20 so as to be integrally protruded, The curved protrusion 31 protruding further in the curved surface is further protruded so as to prevent the welding back due to the arc caused by the arc generated in the arc welding from being attached to the front surface of the welding tip 1, .

상기 세라믹재질의 세라믹보강팁(40)은 통전연결봉(20)의 외주부에 용접시 열변형이 방지되도록 상기 통전연결봉(20)의 외주연을 감싸며, 세라믹재질이나 강화유리 등으로 형성됨으로써 용접시 용접팁의 열변형과 아크로 인한 번백을 미연에 방지하여 용접팁의 수명을 대폭 향상시킬 수 있고, 용접시 마모로 인한 팁 출구 구경의 확장되는 것을 방지하여 용접팁의 수명을 대폭 향상시킬 수 있을 뿐 아니라 용접팁 손상으로 인한 교체나 구입비용을 대폭 절감할 수 있다. The ceramic reinforcing tip 40 of the ceramic material surrounds the outer periphery of the energizing connecting rod 20 so as to prevent thermal deformation when welding the outer circumferential portion of the energizing connecting rod 20 and is formed of a ceramic material or tempered glass, It is possible to significantly improve the life of the welding tip by preventing the thermal deformation of the tip and the back due to the arc so as to prevent the extension of the tip exit diameter due to abrasion at the welding, The cost of replacement or purchase due to damage to the welding tip can be greatly reduced.

그리고, 상기 세라믹보강팁(40)의 세라믹본체(41) 전면에 곡면으로 형성된 전면곡면부(43)가 형성됨으로써 용접 스캐터가 미끄러지면서 부착되는 것이 방지되어 장시간 안전하게 사용할 수 있게 된다.The front surface of the ceramic reinforcing tip 40 is formed with a curved front surface 43 on the front surface of the ceramic body 41 so that the welding scarf is prevented from being slipped and attached to the ceramic body 41 so that it can be safely used for a long time.

또한, 상기 세라믹보강팁(40)의 선단에는 그리스나 금속도금와 같은 보강코팅부(44)가 형성됨으로써 세라믹보강팁의 강도를 대폭 향상시킬 수 있고 용접스캐터가 부착되는 것이 방지할 수 있게 된다.Also, since the reinforcing coating portion 44 such as grease or metal plating is formed at the tip of the ceramic reinforcing tip 40, the strength of the ceramic reinforcing tip can be greatly improved and the welding scar can be prevented from being attached.

한편, 상기 통전연결봉(20)과 세라믹보강팁(40)의 사이에는 상기 세라믹보강팁(40)이 통전연결봉(20)에 고정되어 열변형이 방지되도록 세라믹 접착재(45)로 고정됨으로써 통전연결봉(20)에 완벽하게 고정되어 물리적인 충격에도 안전하게 사용할 수 있고, 세라믹보강팁(40)의 내측에 미세한 공간이 확보되어 열로 한인 열변형을 감소시킬 수 있다.The ceramic reinforcing tip 40 is fixed to the energizing connecting rod 20 between the energizing connecting rod 20 and the ceramic reinforcing tip 40 to be fixed with a ceramic adhesive 45 so as to prevent thermal deformation, 20, so that it can be safely used even in a physical impact, and a minute space can be secured inside the ceramic reinforcing tip 40, so that thermal deformation of the ceramic by the heat can be reduced.

본 발명은 상술한 특정의 바람직한 실시 예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위 내에 있게 된다.It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined in the appended claims and their equivalents. Of course, such modifications are within the scope of the claims.

1 ; 용접기 2 ; 모재
3 ; 와이어 4 ; 콘택트팁
10 ; 팁몸통 11 ; 관통공
12 ; 코팅보강부 20 ; 통전연결봉
30 ; 번백방지돌출부 40 ; 세라믹보강팁
41 ; 세라믹본체 42 ; 안착공
42 ; 전면곡면부 44 ; 보강코팅부
45 ; 세라믹 접착재One ; Welder 2; Base material
3; Wire 4; Contact tip
10; Tip body 11; Through-hole
12; Coating reinforcement 20; Energizing connecting rod
30; Back protrusion 40; Ceramic Reinforcement Tips
41; A ceramic body 42; An early start
42; A front curved surface portion 44; Reinforced coating portion
45; Ceramic adhesive

Claims (4)

일정속도로 와이어(3)가 공급되어 모재(2) 사이에서 발생되는 용접아크에 의하여 용융풀을 형성하는 가스메탈아크식 용접기(1)의 선단에 장착되며, 용접전류를 와이어(3)에 전송하여 용융풀을 유도하는 구리재질의 콘택트팁(4)에 있어서,
상기 용접기(1)에 장착되도록 일측에 나사 형성되고, 중앙에 와이어가 공급되도록 천공된 관통공(11)이 형성된 구리재질의 팁몸통(10)과;
상기 팁몸통(10)의 전면에 상기 팁몸통(10)의 외주부보다 협관되어 통전되도록 일체로 연결되고, 중앙에 와이어(3)가 공급되도록 중앙이 천공된 원형바 형상의 통전연결봉(20)와;
상기 통전연결봉(20)의 전면에 용접 아크로 인한 번백(burn back)과 팁 출구 구경의 확장이 방지되도록 상기 통전연결봉(20)의 외주부보다 협관되어 일체로 돌출된 번백방지돌출부(30)와;
상기 통전연결봉(20)의 외주부에 용접시 열변형이 방지되도록 상기 통전연결봉(20)의 외주연을 감싸는 세라믹재질의 세라믹보강팁(40);으로 구성되고,
상기 세라믹보강팁(40)은 내측으로 상기 통전연결봉(20)에 삽입되어 안착되도록 일측이 개방된 캡형상의 세라믹본체(41)와, 상기 세라믹본체(41)의 전면에 상기 번백방지돌출부(30)가 안착되도록 천공된 안착공(42)과, 상기 세라믹본체(41)의 전면에 용접 스캐터가 부착되는 것이 방지되도록 곡면으로 형성된 전면곡면부(43)로 구성되고,
상기 번백방지돌출부(30)의 전면에는 상기 세라믹보강팁(40)의 선단보다 더 곡면으로 돌출되는 곡면돌출부(31)가 추가로 구성된 것을 특징으로 하는 번백방지 세라믹용접팁.Is mounted on the tip of a gas metal arc welder (1) which is supplied with a wire (3) at a constant speed and forms a molten pool by a welding arc generated between the base metals (2) A contact tip (4) made of a copper material for inducing a molten pool,
A tip body 10 made of copper and having a through hole 11 formed at one side thereof so as to be mounted on the welder 1 and perforated so as to supply a wire to the center thereof;
A circular bar-shaped energizing connecting rod 20 which is integrally connected to the front surface of the tip body 10 so as to be energized more narrowly than the outer circumferential portion of the tip body 10 and is pierced so that the wire 3 is supplied to the center thereof, ;
A protrusion 30 protruding from the front surface of the current connecting rod 20 so as to protrude from the outer circumferential portion of the current connecting rod 20 so as to prevent burn back of the welding arc and enlargement of the tip outlet diameter;
And a ceramic reinforcing tip (40) of ceramic material surrounding the outer periphery of the energizing connecting rod (20) so as to prevent thermal deformation during welding at the outer circumference of the energizing connecting rod (20)
The ceramic reinforcing tip 40 has a cap-shaped ceramic main body 41 having one side opened to be inserted into the energizing connecting rod 20 to be seated inward, And a front curved surface portion 43 formed as a curved surface so as to prevent the welding scatter from being attached to the front surface of the ceramic main body 41,
And a curved protrusion (31) protruding further than a tip end of the ceramic reinforcing tip (40) is further formed on a front surface of the anti-reblocking protrusion (30). 삭제delete 제 1항에 있어서,
상기 통전연결봉(20)과 세라믹보강팁(40)의 사이에는 상기 세라믹보강팁(40)이 통전연결봉(20)에 고정되어 열변형이 방지되도록 세라믹 접착재(45)가 구비된 것을 특징으로 하는 번백방지 세라믹용접팁.
The method according to claim 1,
And a ceramic adhesive 45 is provided between the energizing connecting rod 20 and the ceramic reinforcing tip 40 so that the ceramic reinforcing tip 40 is fixed to the energizing connecting rod 20 to prevent thermal deformation. Prevent ceramic welding tips.
삭제delete
KR1020160007519A 2016-01-21 2016-01-21 A Ceramic Welding Contact Tip prevented burn back KR101669406B1 (en)