KR101611676B1 - Positive electric charge- filter cartridge and Preparing method thereof - Google Patents

Positive electric charge- filter cartridge and Preparing method thereof Download PDF

Info

Publication number
KR101611676B1
KR101611676B1 KR1020130169204A KR20130169204A KR101611676B1 KR 101611676 B1 KR101611676 B1 KR 101611676B1 KR 1020130169204 A KR1020130169204 A KR 1020130169204A KR 20130169204 A KR20130169204 A KR 20130169204A KR 101611676 B1 KR101611676 B1 KR 101611676B1
Authority
KR
South Korea
Prior art keywords
nonwoven fabric
positive charge
epoxy resin
polysulfone
antiviral
Prior art date
Application number
KR1020130169204A
Other languages
Korean (ko)
Other versions
KR20150079160A (en
Inventor
김대훈
최원경
임수정
Original Assignee
도레이케미칼 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 도레이케미칼 주식회사 filed Critical 도레이케미칼 주식회사
Priority to KR1020130169204A priority Critical patent/KR101611676B1/en
Publication of KR20150079160A publication Critical patent/KR20150079160A/en
Application granted granted Critical
Publication of KR101611676B1 publication Critical patent/KR101611676B1/en

Abstract

본 발명은 양전하 필터 카트리지 및 이의 제조방법에 관한 것으로서, 기존의 유리섬유 기반의 항바이러스 부직포를 대체하면서도 우수한 수투과량을 갖고, 또한, 박테리아 제거성능 및 바이러스 제거성능을 우수한 친환경적인 양전하 필터 카트리지를 제공할 수 있는 발명에 관한 것이다.The present invention relates to a positive charge filter cartridge and a method of manufacturing the same, and more particularly, to an environmentally friendly positive charge filter cartridge having superior water permeation capacity and superior bacterial removal performance and virus removal performance while replacing existing glass fiber- The present invention relates to an image forming apparatus.

Description

양전하 필터 카트리지 및 이의 제조방법{Positive electric charge- filter cartridge and Preparing method thereof}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a positive charge filter cartridge and a manufacturing method thereof,

본 발명은 양전하 필터 카트리지 및 이의 제조방법에 관한 것으로써, 보다 상세하게는 박테리아 및 세균 등의 제거 효율을 가지면서도, 바이러스도 제거 가능한 항바이러스 및 제균이 우수한 필터 카트리지에 관한 것이다BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a positive charge filter cartridge and a method of manufacturing the same, and more particularly, to a filter cartridge having an anti-virus and a sterilizing effect capable of removing viruses while having efficiency of removing bacteria and bacteria

일반적으로 물 속에는 천연유기물질(Natural Organic Matter; NOM)을 비롯한 수많은 이온성 물질, 화학물질이 존재하며 상수처리 과정에서 제거되지 않고 새로운 오염물질을 발생시키는 원인물질로 작용한다. 또한, 최근에는 염소소독으로 제거되지 않은 병원성 미생물에 대한 존재여부가 논란이 되고 있다. 바이러스(Virus), 크립토스포리디움(Crytosphoridium), 자이알디아(Giardia) 등으로 분류되는 병원성 미생물은 인체 및 동물의 분변을 통해 환경 중으로 배출되어 하수뿐만 아니라 지표수와 지하수에도 존재한다. 바이러스는 0.02 ~ 0.09㎛, 박테리아는 길이 0.4 ~ 14㎛, 폭 0.2 ~ 1.2㎛의 크기를 갖으며 크립토스포리디움, 자이알디아 등 원생동물은 바이러스나 박테리아에 비해서는 비교적 큰 편이다. 바이러스의 경우 크기가 매우 작기 때문에 일반 여과에 의해서는 거의 처리되지 않으며 내성이 강한 낭종(Cyst)을 형성하여 물에서 수개월이상 안정적으로 살아있다. 현재 물 속의 미량오염물질을 제거하기 위하여 상수처리과정에서 고도응집처리 또는 활성탄 흡착, 막여과가 제시되고 있는데 최근 막을 사용한 정수처리 공정에 대한 국가단위의 대규모 연구가 진행 중이다.Generally, there are numerous ionic substances and chemicals, including natural organic matter (NOM), in water, and they are not removed in the process of water treatment but act as a cause of generating new pollutants. In addition, the presence of pathogenic microorganisms, which have not been removed by chlorine disinfection, has recently been controversial. Pathogenic microorganisms, such as viruses, crytosphoridium, and Giardia, are released into the environment through human and animal feces and are present in not only sewage but also surface and groundwater. The virus has a size of 0.02 to 0.09 μm, the bacteria have a length of 0.4 to 14 μm and a width of 0.2 to 1.2 μm, and the protozoan such as cryptosporidium and xylydia is relatively larger than viruses and bacteria. Because viruses are very small in size, they are hardly treated by general filtration. They form stable cysts and survive for several months in water. At present, in order to remove trace contaminants in water, advanced coagulation treatment, activated carbon adsorption and membrane filtration are proposed in the water treatment process. Recently, a large-scale study on the water treatment process using membranes is underway.

특히, 막 여과에 대해서는 최근에 많은 연구가 이루어져 고도정수처리 과정에서 실용화가 타진되고 있는데 아직까지도 경제적인 비용과 기술적인 문제로 인해 폭넓게 이용되지는 못하고 있다. 역삼투막(RO), 나노여과막(NF), 한외여과막(UF), 정밀여과막(MF)으로 분류되는 막을 비롯한 기존 필터들은 공경(pore, 기공)의 사이즈를 이용하여 물리적인 기작에 의거하여 물 중 오염물질을 제거하는 시스템이다.Particularly, membrane filtration has been recently studied and commercialized in advanced water treatment process. However, it is still not widely used due to economical cost and technical problems. Existing filters including membranes classified as reverse osmosis membrane (RO), nanofiltration membrane (NF), ultrafiltration membrane (UF), and microfiltration membrane (MF) It is a system for removing substances.

분리막의 오염물질제거에 대한 주된 메커니즘은 체분리(Sieve) 효과, 즉 입자크기에 의한 제거가 적용되어 물속에 부유하고 있는 박테리아, 바이러스, 유기 오염물 등을 제거하여 주는 것이다. 상기 입자크기에 의한 제거 외에도 분리막 표면 전하에 따른 정전기적 흡착에 의해서도 수중의 미생물 등을 걸러주며, 이 방법은 적은 운전압력 대비 높은 투수율 및 높은 입자제거 성능으로 각광 받으면서 연구되고 있다.The main mechanism for removing contaminants from the membrane is to remove bacteria, viruses and organic contaminants floating in the water by applying a sieve effect, ie removal by particle size. In addition to the removal by the particle size, electrostatic adsorption according to the surface charge of the separation membrane filters the microorganisms in the water, and this method has been studied for its high permeability and high particle removal performance compared to a small operating pressure.

종래의 수처리용으로 널리 사용되는 마이크로 섬유 필터는 여과 면적이 작고 정전기력이 없기 때문에 효율이 떨어진다는 단점이 있었으며, 멤브레인 필터는 여과 효율은 높으나 압력 손실이 크다는 단점이 있었다. 따라서, 마이크로 섬유 필터와 멤브레인 필터의 단점을 보완하기 위한 마이크로 사이즈의 공경을 가지는 섬유 필터에 정전기력을 부과함으로써 섬유 필터의 여과 효율을 증가시키고, 압력 손실을 감소시키는 연구가 진행되고 있다.The microfibre filter widely used for conventional water treatment has a disadvantage in that the efficiency is low because the filtration area is small and there is no electrostatic force. The membrane filter has a disadvantage in that the filtration efficiency is high but the pressure loss is large. Therefore, studies have been conducted to increase the filtration efficiency of the fiber filter and decrease the pressure loss by applying an electrostatic force to the microfibrillated fiber filter to compensate for the disadvantages of the microfibre filter and the membrane filter.

예를 들어, 종래기술에는 항바이러스 부직포 제조를 위해 유리섬유를 기본 여재로 두고, 유리섬유 제조시에 양전하를 띄는 무기화합물을 첨가하는 방식으로 제조하여 양전하 필터를 제조하고 이를 이용하여 바이러스를 흡착제거 하였다(대한민국 특허공개번호 10-2004-0301723, 미국 등록특허 7,601,262호 등). 그러나 이 기술은 유리섬유를 사용한다는 점에서 발암 등의 유해성 논란으로 수처리 공정의 적합성이 우려되는 문제점과 유리섬유를 사용하여 제조시 첨가되는 화합물에 의해 제품군에서 다양화가 되지 못한다는 문제점이 있었다.For example, in the prior art, a glass fiber is used as a basic filter material for producing an anti-virus nonwoven fabric, and a positive charge is prepared by adding an inorganic compound having a positive charge at the time of glass fiber production. (Korean Patent Publication No. 10-2004-0301723, U.S. Patent No. 7,601,262, etc.). However, since this technique uses glass fibers, there is a concern that the water treatment process may be suitably complicated due to the hazardousness of carcinogens and the like, and there is a problem in that the compound to be added during production using glass fiber can not be diversified in the product group.

다른 종래기술로는 유리섬유가 아닌 폴리프로필렌 여재를 사용하여 여재 안정성을 높였으며, 후처리 코팅 방식에 의해 양전하 필터 여재를 제조하였다(일본공개특허번호 1994-015167). 그러나, 이러한 기술은 바이러스만 제거가 가능할 뿐, 박테리아 및 세균 등을 제거하지 못하였을 뿐만 아니라, 유량 및 여과압력이 현저히 떨어진다는 문제점이 있었다.
In another prior art, a non-glass fiber polypropylene filter material was used to improve filter material stability, and a positive charge filter filter material was prepared by a post-treatment coating method (Japanese Patent Laid-Open No. 1994-015167). However, such a technique has a problem that not only the virus but also bacteria and bacteria can not be removed, but the flow rate and filtration pressure are significantly lowered.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은 박테리아 및 세균의 제거능은 유지하면서, 나노사이즈의 바이러스도 효과적으로 제거할 수 있는 양전하 필터 카트리지를 제공하는데 그 목적이 있다.It is an object of the present invention to provide a positive charge filter cartridge capable of effectively removing nano-sized virus while maintaining the ability to remove bacteria and bacteria.

상술한 과제를 해결하기 위하여 본 발명은 양전하 카트리지 필터에 관한 것으로서, 항바이러스 부직포 및 폴리술폰계 분리막을 포함하며, 필터링(filtering) 방향으로 상기 항바이러스 부직포의 일면에 상기 폴리술폰계 분리막이 적층된 것을 특징으로 할 수 있다.According to an aspect of the present invention, there is provided a positive charge cartridge filter comprising an antiviral nonwoven fabric and a polysulfone separating membrane, wherein the polysulfone separating membrane is laminated on one side of the antiviral nonwoven fabric in a filtering direction . ≪ / RTI >

본 발명의 바람직한 일실시예로서, 본 발명의 양전하 카트리지 필터에 있어서, 상기 항바이러스 부직포는 단층 또는 다층으로 적층된 형태인 것을 특징으로 할 수 있다.As a preferred embodiment of the present invention, in the positive charge cartridge filter of the present invention, the antiviral nonwoven fabric may be a monolayer or multilayer laminate.

본 발명의 바람직한 일실시예로서, 본 발명의 양전하 카트리지 필터에 있어서, 상기 항바이러스 부직포는 폴리프로필렌 섬유, 폴리에틸렌테레프탈레이트 섬유, 폴리에틸렌 섬유, 폴리에스테르 섬유, 나일론 섬유 및 셀룰로오스 섬유 중 선택된 1종 이상을 함유한 부직포; 및 상기 부직포의 내부 및 표면에 양전하 코팅층;이 형성되어 있는 것을 특징으로 할 수 있다.As a preferred embodiment of the present invention, in the positive charge cartridge filter of the present invention, the antiviral nonwoven fabric may comprise at least one selected from polypropylene fiber, polyethylene terephthalate fiber, polyethylene fiber, polyester fiber, nylon fiber and cellulose fiber Nonwoven fabrics containing; And a positive charge coating layer formed on the inside and the surface of the nonwoven fabric.

본 발명의 바람직한 일실시예로서, 본 발명의 양전하 카트리지 필터에 있어서, 상기 항바이러스 부직포의 양전하 코팅층은 코팅층은 비스페놀 A 에폭시 수지, 비스페놀 F 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 F 에폭시 수지, 난연성 에폭시(brominated epoxy) 수지, 및 노볼락형 에폭시 수지 중에서 선택된 1종 이상을 함유하는 가교제; 및 폴리에틸렌이민, 디에틸렌트리아민, 피페라진, 디메틸렌피페라진 및 디페닐아민 중에서 선택된 1종 이상을 함유하는 다관능성 아민 화합물;을 포함하는 것을 특징으로 할 수 있다.As a preferred embodiment of the present invention, in the positive charge cartridge filter of the present invention, the positively charged coating layer of the antiviral nonwoven fabric may comprise a coating layer comprising a bisphenol A epoxy resin, a bisphenol F epoxy resin, a hydrogenated bisphenol A epoxy resin, A crosslinking agent containing at least one selected from the group consisting of F epoxy resin, flame retardant epoxy resin, and novolak epoxy resin; And a polyfunctional amine compound containing at least one member selected from the group consisting of polyethyleneimine, diethylenetriamine, piperazine, dimethylenepiperazine and diphenylamine.

본 발명의 바람직한 일실시예로서, 상기 항바이러스 부직포의 양전하 코팅층은 상기 가교제 및 다관능성 아민 화합물를 1 : 0.5 ~ 10 당량비로 포함하는 것을 특징으로 할 수 있다.In one preferred embodiment of the present invention, the positive-acting coating layer of the antiviral nonwoven fabric may include the crosslinking agent and the polyfunctional amine compound in an equivalent ratio of 1: 0.5 to 10.

본 발명의 바람직한 다른 일실시예로서, 본 발명에 있어서, 상기 항바이러스 부직포의 부직포는 섬도가 평균직경 0.5 ~ 10㎛ 및 평균공경 1 ~ 30㎛인 것을 특징으로 할 수 있으며, 또한, 상기 부직포는 평균두께 0.1 ~ 2㎜ 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the nonwoven fabric of the antiviral nonwoven fabric may have an average fineness of 0.5 to 10 μm and an average pore size of 1 to 30 μm, And an average thickness of 0.1 to 2 mm.

본 발명의 바람직한 다른 일실시예로서, 본 발명에 있어서, 상기 항바이러스 부직포는 표면전하가 10 ~ 50 mV 인 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the antiviral nonwoven fabric may have a surface charge of 10 to 50 mV.

본 발명의 바람직한 또 다른 일실시예로서, 본 발명의 양전하 카트리지 필터에 있어서, 상기 폴리술폰계 분리막은 폴리에테르술폰, 폴리술폰, 폴리알릴에테르술폰, 폴리페닐설폰 및 폴리에테르에테르케톤 중에서 선택된 1종 이상을 함유한 폴리술폰계 중합체를 포함하는 것을 특징으로 할 수 있다.As another preferred embodiment of the present invention, in the positive charge cartridge filter of the present invention, the polysulfone type separator may be one selected from the group consisting of polyethersulfone, polysulfone, polyallyl ether sulfone, polyphenyl sulfone and polyether ether ketone Or more of a polysulfone-based polymer.

본 발명의 바람직한 또 다른 일실시예로서, 상기 폴리술폰계 분리막은 평균공경이 0.1 ~ 1㎛ 및 평균두께 100 ~ 180 ㎛인 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the polysulfone-based separator has an average pore size of 0.1 to 1 μm and an average thickness of 100 to 180 μm.

또한, 본 발명의 바람직한 일실시예로서, 본 발명의 양전하 카트리지 필터는 평균수투과량이 20 ~ 80 ㎖/cm2·min·bar인 것을 특징으로 할 수 있으며, 또한, 바이러스 제거성능이 2 log 이상이고, 박테리아 제거성능이 7 log 이상인 것을 특징으로 할 수 있다.
In addition, as a preferred embodiment of the present invention, the positive charge cartridge filter of the present invention may have an average water permeation rate of 20 to 80 ml / cm 2 · min · bar, , And the bacteria removal performance is 7 log or more.

본 발명의 다른 태양은 앞서 설명한 본 발명의 양전하 카트리지 필터를 제조하는 방법에 관한 것으로서, 폴리술폰계 분리막의 일면에 상기 항바이러스 부직포를 단층 또는 다층으로 적층 및 합지시켜서 제조할 수 있다.Another aspect of the present invention relates to a method of manufacturing the above-described positive charge cartridge filter of the present invention, wherein the antiviral nonwoven fabric is laminated and laminated on one surface of a polysulfone separator in a single layer or in multiple layers.

본 발명의 바람직한 일실시예로서, 상기 항바이러스 부직포는 양전하 코팅제에 부직포를 침전시켜서 부직포에 양전하 코팅제를 코팅시키는 단계; 및 양전하 코팅제가 코팅된 부직포를 열가교시켜서 양전하 코팅층을 형성시키는 단계;를 포함하는 공정을 수행하여 제조한 것을 특징으로 할 수 있다.According to a preferred embodiment of the present invention, the antiviral nonwoven fabric may be produced by: depositing a nonwoven fabric in a positive charge coating agent to coat a positive charge coating agent on the nonwoven fabric; And heat-crosslinking the nonwoven fabric coated with the positive charge coating agent to form a positive charge coating layer.

본 발명의 바람직한 일실시예로서, 상기 항바이러스 부직포 제조단계에 사용하는 상기 양전하 코팅제는 디메틸아세트아마이드, 디메틸포름아미드, N-메틸-2-피롤리돈, 에탄올, 이소프로필알콜, 아세톤 및 메탄올 중에서 선택된 1종 이상을 함유한 용매; 비스페놀 A 에폭시 수지, 비스페놀 F 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 F 에폭시 수지, 난연성 에폭시(brominated epoxy) 수지 및 노볼락형 에폭시 수지 중에서 선택된 1종 이상을 함유한 가교제; 및 폴리에틸렌이민, 디에틸렌트리아민, 피페라진, 디메틸렌피페라진 및 디페닐아민 중에서 선택된 1종 이상을 함유한 다관능성 아민 화합물;을 포함하는 것을 특징으로 할 수 있다.In a preferred embodiment of the present invention, the positive charge coating agent used in the step of preparing the antiviral nonwoven fabric is selected from the group consisting of dimethylacetamide, dimethylformamide, N-methyl-2-pyrrolidone, ethanol, isopropyl alcohol, acetone and methanol A solvent containing at least one selected; A crosslinking agent containing at least one selected from the group consisting of bisphenol A epoxy resin, bisphenol F epoxy resin, hydrogenated bisphenol A epoxy resin, hydrogenated bisphenol F epoxy resin, flame retardant epoxy resin and novolak epoxy resin; And a polyfunctional amine compound containing at least one selected from the group consisting of polyethyleneimine, diethylenetriamine, piperazine, dimethylenepiperazine and diphenylamine.

본 발명의 바람직한 다른 일실시예로서, 상기 양전하 코팅제는 상기 가교제 및 상기 다관능성 아민 화합물을 1 : 0.5 ~ 10 당량비로 포함하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, the positive charge coating agent comprises the cross-linking agent and the polyfunctional amine compound in an equivalent ratio of 1: 0.5 to 10.

본 발명의 바람직한 다른 일실시예로서, 상기 항바이러스 부직포의 제조단계에 있어서, 상기 침전은 15℃ ~ 40℃에서 5초 ~ 15시간 동안 수행하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, in the step of preparing the antiviral nonwoven fabric, the precipitation is performed at 15 ° C to 40 ° C for 5 seconds to 15 hours.

본 발명의 바람직한 다른 일실시예로서, 상기 항바이러스 부직포의 제조단계에 있어서, 열가교는 60℃ ~ 130℃ 하에서, 15초 ~ 8시간 동안 건조 및 가교를 수행하는 것을 특징으로 할 수 있다.In another preferred embodiment of the present invention, in the step of preparing the antiviral nonwoven fabric, the thermal crosslinking may be performed by drying and crosslinking at 60 ° C to 130 ° C for 15 seconds to 8 hours.

본 발명의 바람직한 또 다른 일실시예로서, 상기 항바이러스 부직포의 제조단계에 있어서, 상기 코팅시키는 단계의 침전 전의 부직포는 코로나, 플라즈마, 하이드로차징(hydro-charging), 스퍼터, 프라이머, 화염처리 및 산처리 중에서 선택된 1종 이상의 방법으로 부직포의 내부 및 표면을 전처리한 것을 특징으로 할 수 있다. In yet another preferred embodiment of the present invention, in the step of preparing the antiviral nonwoven fabric, the nonwoven fabric before the precipitation of the coating step may be a corona, a plasma, a hydro-charging, a sputter, a primer, The inner surface and the surface of the nonwoven fabric may be pretreated.

본 발명의 또 다른 태양은 비저장형 직수형 필터에 관한 것으로서, 앞서 설명한 다양한 형태의 양전하 카트리지 필터를 포함하는 것을 특징으로 할 수 있다.Still another aspect of the present invention relates to a non-storage linear filter, and may be characterized in that it includes various types of positive charge cartridge filters as described above.

본 발명의 양이온 필터 카트리지는 박테리아 및 세균 등에 대한 높은 미생물 제거능력을 가지면서도, 마이크로사이즈 및 나노사이즈의 바이러스에 대하여도 우수한 흡착 및 제거하는 성능을 갖을 뿐만 아니라, 본 발명의 양이온 필터 카트리지는 우수한 수투과유량을 갖을 수 있다.
The cationic filter cartridge of the present invention not only has a high microbial removal capability for bacteria and bacteria but also has excellent adsorption and removal performance against viruses of micro size and nano size, Permeate flow rate.

도 1은 본 발명의 항바이러스 부직포용 양전하 코팅제를 코팅시키기 전의 부직포 내부의 섬유에 대한 SEM 측정 사진이다.
도 2는 본 발명의 실시예 1에서 제조한 항바이러스 부직포의 부직포 내부의 섬유에 대한 SEM 측정 사진이다.
도 3 ~ 도 5는 본 발명의 바람직한 일구현예에 따른 양이온 필터 카트리지의 단면 개략도이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a SEM photograph of fibers in the nonwoven fabric before coating the positive charge coating agent for the antiviral nonwoven fabric of the present invention. FIG.
2 is a SEM photograph of the fibers in the nonwoven fabric of the antiviral nonwoven fabric prepared in Example 1 of the present invention.
3 to 5 are cross-sectional schematic views of a cation filter cartridge according to a preferred embodiment of the present invention.

본 발명의 필터링(filtering) 방향은 도 3 및 도4의 화살표 방향을 나타내며, 분리대상 물질이 유입되는 방향에서 유출되는 방향을 의미한다.The filtering direction of the present invention indicates the direction of arrows in FIGS. 3 and 4, and means a direction in which the separation target material flows out.

본 발명에서 폴리술폰계 분리막의 단면구조의 상층부와 하층부가 서로 다른 공경 크기를 갖을 때 비대칭구조라 명칭하고 상층부와 하층부의 기공들이 유사한 공경대를 가질 때 대칭구조라 정의한다. 그리고, 본 발명에서 사용하는 용어인 약비대칭은 상층부와 하층부의 공경 크기 차이가 크지 않으나, 비대칭 구조와 같이 다공성이 높고 유량이 높은 특성을 포함하는 것을 의미한다.
In the present invention, when the upper and lower portions of the cross-sectional structure of the polysulfone-based membrane have different pore sizes, they are referred to as asymmetric structures, and the pores of the upper and lower layers have a similar pore size. The term "weak asymmetry" used in the present invention means that the pore size difference between the upper layer portion and the lower layer portion is not large, but includes a high porosity and a high flow rate as in an asymmetric structure.

이하, 본 발명을 도면을 참조하여 보다 상세히 설명한다.Hereinafter, the present invention will be described in more detail with reference to the drawings.

본 발명의 한 측면에 따르면 항바이러스 부직포; 및 폴리술폰계 분리막;을 포함하며, 필터링(filtering) 방향으로 상기 항바이러스 부직포의 일면에 상기 폴리술폰계 분리막이 적층되고, 상기 항바이러스 부직포는 단층 또는 다층인 다공성 복합여재를 제공함으로써, 종래의 문제점을 해결할 뿐만 아니라, 항바이러스 및 제균능이 우수한 양전하 필터 카트리지를 제공한다.According to one aspect of the present invention there is provided an anti-viral nonwoven fabric; And the polysulfone separator is laminated on one side of the antiviral nonwoven fabric in a filtering direction and the antiviral nonwoven fabric is a single layer or a multilayer porous composite material, The present invention also provides a positive charge filter cartridge which is excellent in antiviral and disinfecting ability.

구체적으로 도 3은 본 발명의 바람직한 일구현예에 따른 양전하 필터 카트리지(300)의 단면 개략도로써, 항바이러스 부직포(302)의 한 측면에 폴리술폰계 분리막(301)이 적층 및 합지되어 있으며, 도4는 본 발명의 바람직한 다른 일구현예에 따른 양전하 필터 카트리지의 단면 개략도로써, 2층 구조의 항바이러스 부직포(302)의 한 측면에 폴리술폰계 분리막(301)이 합지되어 있는 형태로서, 항바이러스 부직포와 폴리술폰계 분리막은 필터링 방향으로 합지되어 있는 형태이다.
3 is a cross-sectional schematic view of a positive charge filter cartridge 300 according to a preferred embodiment of the present invention. The polysulfone-based separator 301 is laminated and bonded on one side of the antiviral nonwoven fabric 302, 4 is a schematic cross-sectional view of a positive charge filter cartridge according to another preferred embodiment of the present invention, in which a polysulfone separator 301 is laminated on one side of an antiviral nonwoven fabric 302 having a two- The nonwoven fabric and the polysulfone-based separator are laminated in the filtering direction.

먼저 항바이러스 부직포(302)에 대해 설명한다.First, the anti-virus nonwoven fabric 302 will be described.

본 발명의 상기 항바이러스 부직포는 바이러스를 흡착하여 제거하는 역할을 하며, 바람직하게는 5 ~ 90nm 크기인 바이러스를 흡착 제거할 수 있으며, 휴믹산 등 유기오염원을 흡착 제어하여 바이오 파울링을 제거할 수 있다.The antiviral nonwoven fabric of the present invention adsorbs and removes viruses, preferably adsorbs and removes viruses having a size of 5 to 90 nm, removes biofouling by adsorbing and controlling organic pollutants such as humic acid .

상술한 바와 같이 종래에는 유리섬유를 사용한다는 점에서 발암 등의 유해성 논란이 있으며 수처리 공정에 사용에 적합성이 우려되는 문제점과 유리섬유를 사용하여 제조시 첨가되는 화합물에 의한 제품군이 다양화되지 못하는 문제점이 있었는 바, 이에 본 발명자들은 유리섬유가 아닌 친환경적인 부직포를 이용한 항바이러스 부직포를 연구한 결과, 부직포가 높은 표면전하를 갖으면서도 부직포에 대한 접합성 및 상용성 등이 우수한 양전하 코팅제를 아래와 같이 개발하였다.
As described above, conventionally, there are controversial hazards of carcinogens and the like due to the use of glass fibers, and there is a concern that they are suitable for use in a water treatment process and problems in which a product group due to a compound added during production using glass fibers can not be diversified The inventors of the present invention have studied antiviral nonwoven fabric using environmentally friendly nonwoven fabric instead of glass fiber and have developed a positive charge coating agent having high surface charge and excellent bonding and compatibility to nonwoven fabric as follows .

상기 양전하 코팅제는 용매, 가교제 및 다관능성 아민 화합물을 포함할 수 있다.The positive charge coating agent may include a solvent, a cross-linking agent, and a polyfunctional amine compound.

본 발명에 있어서, 상기 용매는 디메틸아세트아마이드, 디메틸포름아미드, N-메틸-2-피롤리돈, 에탄올, 이소프로필알콜, 아세톤 및 메탄올 중에서 선택된 1종 및 2종 이상을, 바람직하게는 디메틸아세트아마이드 및 메탄올 중에서 선택된 1종 또는 2종을 포함할 수 있다.In the present invention, the solvent is preferably at least one selected from the group consisting of dimethylacetamide, dimethylformamide, N-methyl-2-pyrrolidone, ethanol, isopropyl alcohol, acetone and methanol, Amide, and methanol.

그리고, 본 발명에 있어서, 상기 가교제는 다관능성 아민 화합물 간의 가교제 역할 및 바인더 역할을 할 뿐만 아니라, 부직포와 코팅성분 간에 접착성을 향상시키는 역할을 하는 것으로서, 비스페놀 A 에폭시 수지, 비스페놀 F 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 F 에폭시 수지, 난연성 에폭시(brominated epoxy) 수지 및 노볼락형 에폭시 수지 중에서 선택된 1종을 또는 2종 이상을 혼합사용할 수 있으며, 바람직하게는 비스페놀 A 에폭시 수지, 비스페놀 F 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 F 에폭시 수지 및 노볼락형 에폭시 수지 중에서 선택된 1종 또는 2종 이상을, 더욱 바람직하게는 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 및 노볼락형 에폭시 수지 중에서 선택된 1종 또는 2종을 혼합하여 사용할 수 있다. 본 발명에 있어서, 상기 가교제의 사용량은 상기 용매 100 중량부에 대하여 상기 가교제를 0.5 ~ 8 중량부로, 바람직하게는 0.8 ~ 7 중량부로, 더욱 바람직하게는 1 ~ 6 중량부를 사용할 수 있으며, 이때, 가교제의 사용량이 0.5 중량부 미만이면 다관능성 아민 화합물이 부직포로부터 쉽게 떨어져 나갈 수 있고, 아민화합물의 수용양이 작아 바이러스 흡착이 원활하지 않은 문제가 있을 수 있고, 8 중량부를 초과하여 사용하면 양전하 코팅제의 점도가 너무 높아져서 부직포의 내부 즉, 부직포의 섬유를 충분하게 코팅시키지 못하여 여재 공경 크기 감소로 인한 투수량 감소의 문제가 있을 수 있다.In the present invention, the crosslinking agent serves not only to serve as a crosslinking agent and a binder between the polyfunctional amine compound, but also to improve the adhesion between the nonwoven fabric and the coating component. Examples of the crosslinking agent include bisphenol A epoxy resin, bisphenol F epoxy resin, Hydrogenated bisphenol A epoxy resin, hydrogenated bisphenol F epoxy resin, flame retardant epoxy resin and novolac epoxy resin, or a mixture of two or more selected from the group consisting of bisphenol A epoxy At least one selected from a resin, a bisphenol F epoxy resin, a hydrogenated bisphenol A epoxy resin, a hydrogenated bisphenol F epoxy resin and a novolak type epoxy resin, more preferably a bisphenol A epoxy resin, a hydrogenated bisphenol A epoxy resin, Bisphenol A epoxy resin, and novolak type epoxy resin. Or a mixture of two species. In the present invention, the amount of the crosslinking agent may be 0.5 to 8 parts by weight, preferably 0.8 to 7 parts by weight, more preferably 1 to 6 parts by weight, based on 100 parts by weight of the solvent. If the amount of the cross-linking agent is less than 0.5 parts by weight, the polyfunctional amine compound can easily be separated from the nonwoven fabric, the amount of the amine compound to be contained is small, and the virus adsorption may not be smooth. If the amount is more than 8 parts by weight, The viscosity of the nonwoven fabric may be too high to adequately coat the fibers of the nonwoven fabric, resulting in a reduction in the amount of permeability due to reduction in pore size.

또한, 본 발명에 있어서, 상기 다관능성 아민 화합물은 부직포의 내부 및 외부에 양전하를 나타내는 정전기적 성질을 부여하는 역할을 하며, 폴리에틸렌이민, 디에틸렌트리아민, 피페라진, 디메틸렌피페라진 및 디페닐아민 중에서 선택된 1종 또는 2종 이상을 혼합하여 사용할 수 있으며, 바람직하게는 디에틸렌트리아민 및 디페닐아민 중에서 선택된 1종 또는 2종 이상을 혼합하여 사용할 수 있다. 본 발명에 있어서, 상기 다관능성 아민 화합물의 사용량은 상기 용매 100 중량부에 대하여, 0.3 ~ 15 중량부로, 바람직하게는 0.5 ~ 13 중량부로, 더욱 바람직하게는 0.5 ~ 10 중량부를 사용할 수 있으며, 이때, 다관능성 아민 화합물의 사용량은 0.3 중량부 미만이면 본 발명의 양전하 카트리지 필터의 바이러스 제거능이 떨어지는 문제가 있을 수 있고, 15 중량부를 초과하여 사용하면 양전하 코팅제의 점도가 너무 높아져서 부직포의 내부 즉, 부직포의 섬유를 충분하게 코팅시키지 못하는 문제가 있을 수 있고, 미반응물이 용출되는 문제가 있을 수 있다.Also, in the present invention, the polyfunctional amine compound serves to impart electrostatic properties to the inside and the outside of the nonwoven fabric to exhibit a positive charge, and may include polyethyleneimine, diethylenetriamine, piperazine, dimethylenepiperazine, and diphenyl Amines, and mixtures thereof. One or more selected from diethylenetriamine and diphenylamine may be used in combination. In the present invention, the amount of the polyfunctional amine compound to be used may be 0.3 to 15 parts by weight, preferably 0.5 to 13 parts by weight, more preferably 0.5 to 10 parts by weight, based on 100 parts by weight of the solvent, If the amount of the polyfunctional amine compound is less than 0.3 part by weight, there may be a problem that the performance of the positive charge cartridge filter of the present invention is poor. When the amount of the polyfunctional amine compound is more than 15 parts by weight, the viscosity of the positive charge coating agent becomes too high, There is a problem that the fibers of the non-reacted material can not be sufficiently coated, and there may be a problem that unreacted materials are eluted.

상기 양전하 코팅제는 상기 가교제 및 상기 다관능성 아민 화합물을 1 : 0.5 ~ 10당량비로, 바람직하게는 1 : 0.8 ~ 9당량비로, 더욱 바람직하게는 1 : 1~8당량비로 사용하는 것이 좋은데, 이때, 다관능성 아민 화합물일 가교제 1 당량비에 대하여 0.5 당량비 미만이면 충분한 표면 전하를 여재에 제공할 수 없을 수 있으며, 10당량비를 초과하여 사용하면 상대적으로 가교제의 사용량이 너무 적어서 미 반응물 발생으로 코팅물이 용출되는 문제가 발생할 수 있다.The positive charge coating agent is preferably used in an amount of 1: 0.5 to 10 equivalents, preferably 1: 0.8 to 9 equivalents, more preferably 1: 1 to 8 equivalents, of the crosslinking agent and the polyfunctional amine compound. If the amount is less than 0.5 equivalents based on 1 equivalent of the polyfunctional amine compound mono-crosslinking agent, sufficient surface charge may not be provided in the filter material. When the amount is more than 10 equivalents, the amount of the crosslinking agent used is too small, There may be a problem.

앞서 설명한 본 발명의 상기 양전하 코팅제에 부직포를 코팅시켜서 본 발명의 양전하 필터 카트리지를 구성하는 항바이러스 부직포를 제조할 수 있으며, 이를 좀 더 구체적으로 설명하면 아래와 같다.An antiviral nonwoven fabric constituting the positive charge filter cartridge of the present invention can be manufactured by coating the nonwoven fabric with the positive charge coating agent of the present invention as described above.

앞서 설명한 다양한 형태의 양전하 코팅제에 부직포를 침전시켜서 부직포에 양전하 코팅제를 코팅시키는 단계; 및 양전하 코팅제가 코팅된 부직포를 열가교시켜서 양전하 코팅층을 형성시키는 단계;를 포함하는 공정을 거쳐서 본 발명의 항바이러스 부직포를 제조할 수 있으며, 이때, 상기 코팅시키는 단계의 침전 전의 부직포는 코로나, 플라즈마, 하이드로차징(hydro-charging), 스퍼터, 프라이머, 화염처리 및 산처리 중에서 선택된 1종 이상의 방법으로 부직포의 내부 및 표면을 전처리한 것일 수 있으며, 바람직하게는 코로나, 플라즈마, 하이드로차징 또는 산처리를 수행하여 전처리한 부직포를 사용함으로써, 양전하 코팅층와 부직포간의 접착력을 증대시킬 수 도 있다.Depositing a nonwoven fabric on the various types of positive charge coating agents described above to coat the nonwoven fabric with a positive charge coating agent; And a step of thermally crosslinking a nonwoven fabric coated with a positive charge coating agent to form a positive charge coating layer. The non-woven fabric of the present invention can be prepared by a process comprising the steps of: The inner surface and the surface of the nonwoven fabric may be pretreated by one or more methods selected from the group consisting of hydrothermal treatment, hydro-charging, sputtering, primer treatment, flame treatment and acid treatment, preferably corona, plasma, The adhesion between the positive charge transport layer and the nonwoven fabric can be increased.

항바이러스 부직포를 제조방법에서 사용하는 상기 양전하 코팅제의 종류, 특징, 성분 등은 앞서 설명한 바와 동일하다.The types, characteristics, components, etc. of the positive charge coating agent used in the production method of the antiviral nonwoven fabric are the same as those described above.

항바이러스 부직포의 제조방법에 있어서, 상기 부직포는 통상적으로 사용하는 것이면 적용가능하며, 바람직하게는 케미컬본딩부직포(Chemical Bonding), 써멀본딩부직포(Thermal Bonding), 에어레이부직포(Air Ray), 습식부직포(Wet Ray), 니들펀칭부직포(Needle Punching), 스판레스(수류결합법-Water zet), 스판본드(Spun Bond), 멜트블로운(Melt Blown) 및 스티치본드(Stitch Bond), 전기방사(electro spinning) 부직포 중에서 선택되는 어느 하나의 형태일 수 있다.In the process for producing an antiviral nonwoven fabric, the nonwoven fabric may be used as long as it is commonly used, and preferably a chemical bonding, a thermal bonding, an airlay, (Wet Ray), Needle Punching, Needle Punching, Spanless, Spun Bond, Melt Blown and Stitch Bond, Electro- spinning) non-woven fabric.

또한, 상기 항바이러스 부직포를 구성하는 섬유는 폴리프로필렌 섬유, 폴리에틸렌테레프탈레이트 섬유, 폴리에틸렌 섬유, 폴리에스테르 섬유, 나일론 섬유 및 셀룰로오스 섬유 중에서 선택된 1종 이상을, 바람직하게는 폴리프로필렌 섬유, 폴리에틸렌테레프탈레이트 섬유, 폴리에틸렌 섬유, 및 폴리에스테르 섬유 중에서 선택된 1종 또는 2종 이상을, 더욱 바람직하게는 폴리프로필렌 섬유 및 폴리에틸렌테레프탈레이트 섬유 중에서 선택된 1종 또는 2종을 포함할 수 있다.The fibers constituting the antiviral nonwoven fabric may be at least one selected from the group consisting of polypropylene fibers, polyethylene terephthalate fibers, polyethylene fibers, polyester fibers, nylon fibers and cellulose fibers, preferably polypropylene fibers, polyethylene terephthalate fibers , Polyethylene fibers, and polyester fibers, and more preferably one or two selected from polypropylene fibers and polyethylene terephthalate fibers.

그리고, 상기 부직포는 평균두께 0.1 ~ 2㎜ 인 것이, 바람직하게는 0.2 ~ 1㎜ 인 것이 좋으며, 이때, 평균두께 0.1 만약 평균두께가 0.1㎜미만이면, 바이러스 흡착 경로가 짧아서 제거효율이 감소한 문제가 있으며, 2㎜를 초과하면, 여과시 차압발생으로 유량이 감소한 문제가 있을 수 있다.The non-woven fabric preferably has an average thickness of 0.1 to 2 mm, preferably 0.2 to 1 mm, and an average thickness of 0.1. If the average thickness is less than 0.1 mm, If it exceeds 2 mm, there may be a problem that the flow rate is decreased due to the generation of differential pressure during filtration.

그리고, 상기 부직포를 구성하는 섬유의 섬도가 평균직경 0.5 ~ 10㎛ 및 평균공경 1 ~ 30㎛일 수 있으며, 바람직하게는 섬도가 평균직경 0.5 ~ 8㎛ 및 평균공경 2 ~ 10㎛ 일 수 있으며, 더욱 바람직하게는 섬도가 평균직경 1 ~ 5㎛ 및 평균공경 3 ~ 8㎛일 수 있다. 이때, 부직포를 구성하는 섬유의 섬도가 평균직경이 0.5㎛ 미만이면, 여과시 차압발생에 따른 유량 감소하는 문제가 있을 수 있고, 10㎛를 초과하면, 다공도가 떨어져 여과효율이 감소하는 문제가 있을 수 있다. 또한, 평균공경이 1㎛ 미만이면, 유량 감소한 문제가 있으며, 30㎛를 초과하면, 바이러스 제거성능이 감소하는 문제가 있을 수 있다. The fibers constituting the nonwoven fabric may have an average diameter of 0.5 to 10 mu m and an average pore diameter of 1 to 30 mu m, preferably a fineness of 0.5 to 8 mu m and an average pore diameter of 2 to 10 mu m, More preferably, the fineness may be an average diameter of 1 to 5 mu m and an average pore diameter of 3 to 8 mu m. If the fineness of the fibers constituting the nonwoven fabric is less than 0.5 mu m, there may be a problem that the flow rate decreases due to the generation of differential pressure during filtration. When the average diameter exceeds 10 mu m, the filtration efficiency decreases due to the decrease in porosity . If the average pore size is less than 1 占 퐉, there is a problem of decreasing the flow rate. If the average pore size exceeds 30 占 퐉, there may be a problem that the virus removal performance is decreased.

항바이러스 부직포의 제조방법에 있어서, 상기 양전하 코팅제를 코팅시키는 단계의 침전은 15℃ ~ 40℃에서 수행하는 것이, 바람직하게는 20℃ ~ 30℃ 에서 수행하는 것이 좋으며, 이때, 15℃ 미만에서 수행시 에폭시 점착력이 감소되는 문제가 있을 수 있고, 40℃를 초과하는 온도에서 수행시 용매 증기 발생에 의한 유해환경 및 폭발의 문제가 있을 수 있으므로 상기 온도 범위에서 침전을 수행하는 것이 좋다. 그리고, 침전시간은 5초 ~ 15시간 동안, 바람직하게는 20초 ~ 13시간 정도 수행하는 것이 좋다.In the method for producing the antiviral nonwoven fabric, the step of coating the positive charge coating agent is preferably carried out at 15 ° C to 40 ° C, preferably at 20 ° C to 30 ° C, There may be a problem that the epoxy adhesive strength is decreased, and there may be a problem of explosion due to the generation of solvent vapor when the temperature is higher than 40 DEG C, so it is preferable to perform the precipitation in the above temperature range. The precipitation time is preferably 5 seconds to 15 hours, preferably 20 seconds to 13 hours.

항바이러스 부직포의 제조방법에 있어서, 상기 열가교는 60℃ ~ 130℃ 하에서, 바람직하게는 70℃ ~ 110℃ 하에서, 더욱 바람직하게는 80℃ ~ 100℃에서 건조 및 가교를 수행하는 것이 좋은데, 이때, 열가교 온도가 60℃ 미만이면 가교제와 아민화합물의 가교반응이 충분히 이루어 지지 않아 물성 및 제조 공정의 효율이 감소되는 문제를 발생할 수 있으며, 130℃를 초과하면 부직포의 열변형을 가져와서 여재의 공경(기공)이 좁아져서 수투과량에 악영향을 줄 수 있으므로 상기 온도 범위 내에서 열가교를 수행하는 것이 좋다. 그리고, 열가교 시간은 열가교 온도에 따라 상대적으로 변하는 것으로서, 바람직하게는 15초 ~ 8시간 정도 수행하는 것이, 바람직하게는 30초 ~ 6시간 동안 수행하는 것이 좋다.
In the method for producing an antiviral nonwoven fabric, the thermal crosslinking is preferably carried out by drying and crosslinking at 60 ° C to 130 ° C, preferably at 70 ° C to 110 ° C, more preferably at 80 ° C to 100 ° C, If the thermal crosslinking temperature is less than 60 ° C, the crosslinking reaction between the crosslinking agent and the amine compound may not be sufficiently carried out, resulting in a decrease in the physical properties and efficiency of the manufacturing process. If the temperature exceeds 130 ° C, It is preferable to perform thermal crosslinking within the above-mentioned temperature range because pores (pores) become narrow to adversely affect water permeation amount. The heat crosslinking time varies depending on the heat crosslinking temperature. It is preferably carried out for 15 seconds to 8 hours, preferably 30 seconds to 6 hours.

본 발명에 있어서, 상기 항바이러스 부직포는 부직포의 내부 및 표면에 양전하 코팅층이 코팅되어 있는데, 상기 양전하 코팅층은 평균두께 0.01 ~ 3㎛을 갖도록 형성시키는 것이, 바람직하게는 평균두께 0.05 ~ 1㎛을 갖도록 하는 것이 좋으며, 이때, 코팅층의 평균두께가 0.01㎛ 미만이면 코팅 균일도 감소로 인한 물성편차 문제가 있을 수 있고, 3㎛를 초과하면 코팅층 내구성 감소로 용출문제 가 있을 수 있다.In the present invention, the antiviral nonwoven fabric is coated on the inside and the surface of the nonwoven fabric with a positive charge coating layer. The positive charge coating layer is preferably formed to have an average thickness of 0.01 to 3 μm, preferably 0.05 to 1 μm At this time, if the average thickness of the coating layer is less than 0.01 탆, there may be a problem of physical property deviation due to reduction in coating uniformity. If the average thickness exceeds 3 탆, coating layer durability may be decreased and there may be a problem of elution.

양전하 코팅층을 형성된 본 발명 항바이러스 부직포의 표면전하는10 ~ 50 mV 일 수 있으며, 바람직하게는 15 ~ 50 mV일 수 있다. 이는 부직포의 표면전하가 양전하를 나타냄으로써, 음전하를 갖는 바이러스를 흡착하여 포집할 수 있게 되는데, 만약 부직포의 표면전하가 10mV 미만이면, 바이러스 흡착능이 떨어지는 문제가 있을 수 있고, 50mV를 초과하여도 바이러스 흡착능은 유사하나 공정시 높은 표면전하를 나타내기 위한 반응시간 및 농도 증가에 의한 생산비용 증가한 문제가 있을 수 있다.The surface charge of the antiviral nonwoven fabric of the present invention having a positive charge coating layer may be 10 to 50 mV, preferably 15 to 50 mV. If the surface charge of the nonwoven fabric is less than 10 mV, there may be a problem that the virus adsorbing ability is poor. When the surface charge of the nonwoven fabric is more than 50 mV, Although the adsorption capacity is similar, there is a problem that the production cost is increased due to the increase of the reaction time and the concentration to show the high surface charge in the process.

그리고, 상기 표면전하는 Anton Parr 사의 Surpass 모델을 사용하여 흐름전위를 측정하여 하기 수학식 1에 의해 계산된 방법에 의거하여 측정할 수 있는데, 그러나, 본 발명이 이에 한정되는 것은 아니다.The surface electric charge can be measured based on a method calculated by the following Equation 1 by measuring the flow electric potential using a Surpass model manufactured by Anton Parr. However, the present invention is not limited thereto.

[수학식 1][Equation 1]

Figure 112013121324056-pat00001
Figure 112013121324056-pat00002

Figure 112013121324056-pat00001
Figure 112013121324056-pat00002

상기 수학식 1에서, ζ: 제타전위(mV), U : 흐름전위(streaming potential, p:압력(pressure), η: 전해질 점도, ε: 전해질의 기본유전율, ε0 : 전해질의 유전체상수, Kb : 전해질의 전기전도도
In Equation 1, ζ: Zeta potential (mV), U: streaming potential (streaming potential, p: pressure (pressure), η: viscosity of the electrolyte, ε: dielectric constant of the basic electrolyte, ε 0: The dielectric constant of the electrolyte, K b : Electrical conductivity of electrolyte

다음 폴리술폰계 분리막(301)에 대해 설명한다.The following polysulfone-based separator 301 will be described.

본 발명의 폴리술폰계 분리막은 박테리아 및 세균 등을 제거하는 역할 및 마이크로 크기를 가지를 입자를 제거하는 역할을 하며, 바람직하게는 0.2 ~ 20㎛의 미생물 등을 제거할 수 있다.The polysulfone-based separator of the present invention has the role of removing bacteria and bacteria, and has a function of removing microparticles having a micro size, and it is possible to remove microorganisms of 0.2 to 20 μm, preferably.

본 발명의 폴리술폰계 분리막은 통상적인 제조방법을 통해 제조된 폴리술폰계 분리막일 수 있으며, 그 제조방법 역시 통상적으로 당업자들이 제조할 수 있는 방법이라면 무관하다. 그리고 폴리술폰계 분리막의 두께는 100 ~ 180㎛, 바람직하게는 110 ~ 170㎛일 수 있다. 이때, 폴리술폰계 분리막의 두께가 평균두께가 100㎛ 미만이면, 사용주기 감소한 문제가 있으며, 평균두께가 180㎛를 초과하면, 차압발생에 의한 효율 감소하는 문제가 있을 수 있다.The polysulfone-based separator of the present invention may be a polysulfone-based separator prepared by a conventional method, and the method of manufacturing the polysulfone-based separator may be any method that can be manufactured by those skilled in the art. The thickness of the polysulfone type separator may be 100-180 탆, preferably 110-170 탆. If the average thickness of the polysulfone type separator is less than 100 탆, there is a problem that the use period is decreased. If the average thickness exceeds 180 탆, there is a problem that the efficiency due to the generation of the differential pressure is reduced.

또한, 분리막의 종류는 대칭막, 비대칭막, 약대칭막 등을 모두 포함할 수 있으며, 이뿐만 아니라 평막 또는 중공사도 포함될 수 있다.In addition, the type of the separator may include a symmetric membrane, an asymmetric membrane, a symmetric membrane, and the like, as well as a flat membrane or a hollow fiber membrane.

본 발명에 있어서, 상기 폴리술폰계 분리막은 폴리에테르술폰, 폴리술폰, 폴리알릴에테르술폰, 폴리페닐설폰 및 폴리에테르에테르케톤 중에서 선택된 1종 이상을 함유한 폴리술폰계 중합체를 포함할 수 있고, 바람직하게는 폴리에테르술폰, 폴리술폰 및 폴리알릴에테르술폰 중에서 선택된 1종 이상을 함유한 폴리술폰계 중합체를 포함할 수 있다.In the present invention, the polysulfone-based separator may comprise a polysulfone-based polymer containing at least one selected from the group consisting of polyethersulfone, polysulfone, polyallyl ether sulfone, polyphenyl sulfone and polyether ether ketone, May include a polysulfone-based polymer containing at least one selected from the group consisting of polyethersulfone, polysulfone, and polyallyl ether sulfone.

또한, 상기 폴리술폰계 분리막은 평균공경이 0.1㎛ ~ 1㎛일 수 있으며, 바람직하게는 0.1㎛ ~ 0.7㎛일 수 있다. 이때, 평균공경이 0.1㎛ 미만이면, 유량 감소한 문제가 있을 수 있고, 1㎛를 초과하면, 박테리아 및 세균 등을 제거성능이 미흡한 문제가 있을 수 있다.The polysulfone-based separator may have an average pore size of 0.1 to 1 탆, and preferably 0.1 to 0.7 탆. At this time, if the average pore size is less than 0.1 탆, there may be a problem that the flow rate is reduced. If the average pore size exceeds 1 탆, there is a problem that the ability to remove bacteria and bacteria is insufficient.

본 발명에서 사용하는 상기 폴리술폰계 분리막은 통상적인 제조방법을 통해 제조된 폴리술폰계 분리막일 수 있으며, 바람직하게는 다음의 방법대로 수행될 수 있다.The polysulfone-based separator used in the present invention may be a polysulfone-based separator prepared through a conventional method, and may be preferably carried out in the following manner.

본 발명의 풀리술폰계 분리막은 지지체 상에, 폴리술폰계 중합체, 친수성 공경조절제 및 잔량의 용매로 이루어진 고분자용액을 캐스팅하여 막을 형성하는 제1공정; 상기 형성된 막에 온도 20℃ ~ 60℃ 및 습도 30% ~ 99%로 유지된 공기분사에 의해 막의 상층부에 공경(또는 기공)을 형성하는 제2공정; 및 상기 제 2공정 이후, 응고조에 침지하여 상기 지지체로부터 막을 박리시키는 제3공정;을 포함하는 공정을 수행하여 제조할 수 있다. The pulley sulfone type separation membrane of the present invention comprises a first step of forming a film on a support by casting a polymer solution comprising a polysulfone polymer, a hydrophilic pore adjusting agent and a residual solvent; A second step of forming pores (or pores) in the upper layer of the film by air injection maintained at a temperature of 20 ° C to 60 ° C and a humidity of 30% to 99%; And a third step of immersing the film in the coagulation bath after the second step to peel the film from the support.

상기 제1공정에 사용되는 지지체는 금속소재 또는 폴리에틸렌 프탈레이트 필름이며, 상기 금속소재 특성상, 그 표면온도는 5℃ ~ 30℃일 수 있고, 지지체의 바람직한 일례로는 스테인리스 스틸, 알루미늄, 구리, 알루미늄합금 또는 구리합금 폴리에틸렌 프탈레이트 필름 등을 사용할 수 있다.The support used in the first step may be a metal material or a polyethylene phthalate film. The surface temperature of the metal material may be 5 ° C to 30 ° C, and preferred examples of the support include stainless steel, aluminum, Or a copper alloy polyethylene phthalate film.

그리고 상기 고분자용액은 폴리술폰계 중합체 8 ~ 40중량%, 친수성 공경 조절제 10 ~ 20중량% 및 잔량의 용매로 이루어질 수 있으며, 상기 고분자용액의 친수성 공경조절제는 내부 공경(또는 기공)을 형성하기 위하여 사용할 수 있다. 그리고 상기 친수성 공경조절제는 용매와 잘 혼합되는 것이라면 사용 가능하며, 바람직하게는 폴리비닐피롤리돈, 폴리에틸렌글리콜 및 실리카로 이루어진 군에서 선택되는 하나 이상을 사용할 수 있고, 더욱 바람직하게는 중량평균분자량 10,000 ~ 100,000의 범위를 가지는 폴리비닐피롤리돈을 친수성 공경조절제로서 사용할 수 있다.The polymer solution may be composed of 8 to 40% by weight of a polysulfone polymer, 10 to 20% by weight of a hydrophilic pore adjusting agent, and the remaining amount of the solvent. The hydrophilic pore adjusting agent of the polymer solution may be prepared to form an inner pore Can be used. The hydrophilic pore-controlling agent may be used as long as it is well mixed with a solvent, and preferably at least one selected from the group consisting of polyvinylpyrrolidone, polyethylene glycol and silica can be used, and more preferably, a weight average molecular weight of 10,000 Polyvinylpyrrolidone having a molecular weight of from about 100,000 to about 100,000 can be used as a hydrophilic pore size controlling agent.

상기 용매는 N-메틸-2-피롤리돈, 디메틸포름아마이드, 디메틸설폭사이드 및 디메틸아세트아마이드로 이루어진 군에서 선택되는 하나 이상이 사용되며, 이때, 용매의 함량은 전체 100 중량%에서 상기 조성함량을 제외한 잔량이 사용될 수 있다. 또한, 상기 고분자 용액에는 에틸렌글리콜 및 글리세롤을 포함하는 글리콜류; 에탄올 및 메탄올을 포함하는 알코올류; 및 아세톤을 포함하는 케톤류;로 이루어진 군에서 선택되는 어느 하나의 친수성 첨가제를 더 혼합할 수 있다.
The solvent may be at least one selected from the group consisting of N-methyl-2-pyrrolidone, dimethylformamide, dimethylsulfoxide and dimethylacetamide, wherein the solvent content is from 100% May be used. The polymer solution may contain glycols including ethylene glycol and glycerol; Alcohols including ethanol and methanol; And ketones including acetone; and a hydrophilic additive selected from the group consisting of:

다음 상기 제2공정은 형성된 막에 공경(또는 기공)을 형성하는 단계로서, 제2공정에서 형성되는 막 상층부의 평균공경크기는 0.01 ㎛~ 0.50 ㎛ 직경이며, 상기 상층부를 제외한 막의 하층부의 평균공경크기가 0.45 ㎛ ~ 20 ㎛ 직경일 수 있다.The second step is a step of forming pores (or pores) in the formed film, wherein the average pore size of the film upper layer formed in the second process is 0.01 to 0.50 탆 in diameter, and the average pore size And the size may be 0.45 mu m to 20 mu m in diameter.

구체적으로, 상층부에 공경을 형성하는 조건은 공기분사온도 20 ~ 60? 및 습도 30% ~ 99%로 유지된 조건하에서 0.01 ~ 5 m/min의 속도로 공기분사를 수행하여 공경을 형성할 수 있으며, 이때 공기 노출시간은 5초 ~ 10분 동안 수행될 수 있는데, 만약 상기 공기분사속도가 0.01 m/min 미만이면, 공정 컨트롤의 문제가 있고, 5 m/min를 초과하는 속도로 수행되면, 막 표면에 흠집을 발생하여 공경 형성에 영향을 주기 때문에 바람직하지 않다.Specifically, the conditions for forming the pores in the upper layer are the air injection temperature of 20 to 60? And air at a rate of 0.01 to 5 m / min under the condition that the humidity is maintained at 30% to 99% to form the pore, wherein the air exposure time can be performed for 5 seconds to 10 minutes If the air jetting rate is less than 0.01 m / min, there is a problem of process control. If the air jetting rate is more than 5 m / min, scratches are generated on the surface of the film to affect pore formation.

또한, 공기분사시의 공기 노출시간이 5초 미만이면, 표면의 공경 형성이 미흡하므로, 응고시키기 위한 체류시간을 충분하게 제어하도록 하는 것이 바람직하며, 공기노출시간이 10분을 초과하면, 막의 외관이 좋지 않아져 바람직하지 않다.When the air exposure time during air injection is less than 5 seconds, formation of pores on the surface is insufficient. Therefore, it is preferable to sufficiently control the residence time for coagulation. If the air exposure time exceeds 10 minutes, This is not preferable because it is not good.

상기 공기분사에 의해 형성되는 폴리술폰계 분리막 상층부의 공경크기는 0.01㎛ ~ 0.5㎛이며, 폴리술폰계 분리막 하층부의 공경크기 0.45㎛ ~ 20㎛일 수 있으며, 하층부의 공경형성은 지지체 상에 고분자용액을 캐스팅할 때, 지지지체와 고분자용액간의 온도차에 의해 공경이 형성될 수 있다. 이때, 지지체는 금속소재의 특성상 그 표면온도가 5℃ ~ 30℃이며, 이때, 지지체의 온도가 5℃ 미만으로 지나치게 낮으면, 접촉하는 고분자용액간의 온도차가 커져 균일한 도포가 어려워 막형성이 어려울 수 있으며, 반면에 30℃로 높게 유지되면, 고분자용액간의 온도차가 작아져 열유도상전이법에 의한 공경의 구조를 조절하기 비효율적이다. 따라서 상기 지지체 상에 캐스팅되는 고분자용액의 온도는 상기 지지체 온도보다 높은 온도로 유지하되, 바람직하게는 10℃ ~ 40℃를 유지하는 것이 좋다.The pore size of the upper part of the polysulfone separator formed by the air injection may be 0.01 탆 to 0.5 탆, the pore size of the lower part of the polysulfone separator may be 0.45 탆 to 20 탆, The pore size can be formed by the temperature difference between the support material and the polymer solution. At this time, if the surface temperature of the support is 5 ° C to 30 ° C due to the nature of the metal material, if the temperature of the support is too low, the temperature difference between the polymer solution to be contacted becomes large, On the other hand, if the temperature is kept as high as 30 ° C, the temperature difference between the polymer solution becomes small, and it is inefficient to control the structure of the pores by the heat induction phase transfer method. Therefore, the temperature of the polymer solution to be cast on the support is maintained at a temperature higher than the temperature of the support, preferably 10 ° C to 40 ° C.

즉, 본 발명의 바람직한 폴리술폰계 분리막 제조방법에 의해 상층부의 공경크기는 0.01㎛ ~ 0.50㎛이고, 하층부의 공경크기가 0.45㎛ ~ 20㎛인 비대칭구조의 폴리술폰계 막을 제공할 수 있다.
That is, the polysulfone-based membrane producing method according to the present invention can provide an asymmetric polysulfone-based membrane having an upper pore size of 0.01 to 0.50 μm and a lower pore size of 0.45 to 20 μm.

도 3 ~ 도 5에 나타낸 바와 같이, 본 발명의 양전하 필터 카트리지는 폴리술폰계 분리막의 일면에 본 발명의 항바이러스 부직포를 단층 또는 다층으로 적층시켜서 제조할 수 있으며, 또는 항바이러스 부직포 일면에 폴리술폰계 분리막을 적층시켜서 제조할 수 있다.As shown in Figs. 3 to 5, the positive charge filter cartridge of the present invention can be produced by laminating the antiviral nonwoven fabric of the present invention in a single layer or in multiple layers on one side of a polysulfone separation membrane, A polyester-based separator may be laminated.

본 발명에서 상기 적층시키는 방법으로는 통상적으로 사용가능한 방법으로 가능하며, 바람직하게는 크로스 적층(수평 적층) 및 버티컬적층(수직 적층) 중 선택되는 어느 하나 이상의 방법을 사용할 수 있다.In the present invention, the lamination can be carried out by a commonly used method, and preferably one or more of cross lamination (horizontal lamination) and vertical lamination (vertical lamination) can be used.

그리고 항바이러스 부직포는 단층 또는 다층으로 적층시킨 것을 사용할 수 있는데, 항바이러스 부직포를 다층 적층시키는 방법도 통상적으로 사용가능한 방법으로 가능하며, 바람직하게는 크로스 적층한 방법으로 수행할 수 있으며, 적층 후에는 압축하는 공정을 더 수행할 수 있다.
The antiviral nonwoven fabric may be laminated in a single layer or a multilayer. A method of laminating the antiviral nonwoven fabric in a multi-layered manner is also possible by a conventionally usable method, preferably by a cross lamination method. It is possible to further perform the compression process.

본 발명의 양전하 필터 카트리지는 전체 평균수투과량이 20 ~ 80 ㎖/cm2·min·bar로 높은 수투과량을 갖으면서도, 박테리아 제거성능이 7log 이상 및 바이러스 제거성 능2log 이상일 수 있으며, 바람직하게는 7.5log 이상 및 바이러스 제거성능 2.5log 이상일 수 있으며, 더욱 바람직하게는 8log 이상 및 바이러스 제거성능 3.0log 이상일 수 있다. The positive charge filter cartridge of the present invention has a high water permeation rate of 20 to 80 ml / cm 2 · min · bar as a total average water permeation amount, and can have a bacterial removal performance of 7 log or more and a virus removal capability of 2 log or more, log and virus removal performance of 2.5 log or more, more preferably 8 log or more and virus removal performance of 3.0 log or more.

이는 종래의 필터 카트리지는 박테리아만 제거가 가능하거나, 바이러스만을 제거가 가능한 필터 카트리지로써, 나노사이즈인 바이러스와 박테리아 등의 미생물을 동시에 제거할 수 없었으며, 또한, 동일한 유량에서 종래의 기술의 필터 카트리지로는 바이러스 및 박테리아를 제거하더라도 제거능에서 박테리아 제거성능 7log 이상 및 바이러스 제거성능 2log 이상을 동시에 만족시키지 못하였다. This is because the conventional filter cartridge can not only remove bacteria and microorganisms such as viruses and bacteria which are nano-sized at the same time as the filter cartridge which can remove only the virus, , It was not able to satisfy the bacterial removal performance of 7 log or more and the virus removal performance of 2 log or more at the same time even if the virus and the bacteria were removed.

본 발명의 양전하 필터 카트리지는 평균수과량도 20 ㎖/cm2·min·bar 이상을, 바람직하게는 20 ~ 80 ㎖/cm2·min·bar을, 더욱 바람직하게는 30 ~ 80 ㎖/cm2·min·bar을 갖을 수 있다.The positive charge filter cartridge of the present invention has an average excess amount of 20 ml / cm 2 · min · bar or more, preferably 20 to 80 ml / cm 2 · min · bar, more preferably 30 to 80 ml / cm 2 · min · bar.

하지만, 본 발명에서는 적정 유량을 유지함으로써, 사용수명도 증가하게 할 뿐만 아니라, 박테리아 및 바이러스를 동시에 제거할 수 있는 양전하 필터 카트리지를 제공할 수 있게 한다. However, in the present invention, it is possible to provide a positive charge filter cartridge capable of simultaneously removing bacteria and virus as well as increasing service life by maintaining a proper flow rate.

그리고, 본 발명의 양전하 필터 카트리지는 비저장 직수형 필터의 필터 카트리지로 사용하기에 적합하며, 특히, 제약용 비저장 직수형 필터 또는 가정용 비저장 직수형 정수기 필터로 사용하기에 적합하다.
And, the positive charge filter cartridge of the present invention is suitable for use as a filter cartridge of a non-storage linear filter, and is particularly suitable for use as a non-storage linear filter for pharmaceutical use or a non-storage linear water purifier filter for home use.

이하, 실시예를 통하여 본 발명을 더욱 구체적으로 설명하기로 하지만, 하기 실시예가 본 발명의 범위를 제한하는 것은 아니며, 이는 본 발명의 이해를 돕기 위한 것으로 해석되어야 할 것이다.Hereinafter, the present invention will be described in more detail with reference to the following examples. However, the following examples should not be construed as limiting the scope of the present invention, and should be construed to facilitate understanding of the present invention.

[[ 실시예Example ] ]

실시예Example 1 : 항바이러스 부직포의 제조 1: Preparation of antiviral nonwoven fabric

디메틸렌아세트아마이드 용매 100 중량부에 대하여, 노볼락형 에폭시 수지 4.5 중량부 및 폴리에틸렌이민 4.5 중량부를 혼합한 후, 25℃에서 30분간 교반하여 제조한 용액을 메탄올 용액에 20%로 희석하여 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 0.9 중량부를 포함하는 양전하 코팅제를 제조하였다. 4.5 parts by weight of a novolak type epoxy resin and 4.5 parts by weight of polyethyleneimine were mixed with 100 parts by weight of a dimethylene acetamide solvent, and the solution was stirred at 25 DEG C for 30 minutes to dilute the solution to 20% in a methanol solution, 0.9 parts by weight of the novolak type epoxy resin and 0.9 part by weight of the polyethyleneimine were prepared in 100 parts by weight.

다음으로, 평균공경 6㎛, 섬도가 평균직경 3㎛ 및 평균두께 703㎛를 갖는 폴리프로필렌 부직포를 상기 양전하 코팅제에 25℃에서 12시간 침적시킨 후, 이를 꺼내서, 80℃에서 6시간 동안 열 가교를 실시하여 부직포의 내부 및 표면에 평균두께 1㎛의 양전하 코팅층을 형성시켰다. Next, a polypropylene nonwoven fabric having an average pore diameter of 6 mu m, a fineness of an average diameter of 3 mu m and an average thickness of 703 mu m was immersed in the positive charge coating agent at 25 DEG C for 12 hours and then taken out of it to perform thermal crosslinking at 80 DEG C for 6 hours To form a positive charge coating layer having an average thickness of 1 mu m on the inside and the surface of the nonwoven fabric.

그리고, 양전하 코팅제로 침전, 열가교처리 전의 폴리프로필렌 부직포의 SEM 측정 사진을 도 1에 나타내었고, 열가교 처리 후의 폴리프로필렌 부직포의 SEM 측정 사진을 도 2에 나타내었다. 도 1과 도 2를 비교해보면, 폴리프로필렌 부직포의 내부 섬유에 양전하 코팅층이 잘 형성되어 있는 것을 확인할 수 있었다.
FIG. 1 shows a photograph of the SEM measurement of the polypropylene nonwoven fabric before the precipitation with the positive charge coating agent and the thermal crosslinking treatment, and FIG. 2 shows the SEM photograph of the polypropylene nonwoven fabric after the heat crosslinking treatment. Comparing FIG. 1 and FIG. 2, it can be confirmed that a positive charge coating layer is well formed on the internal fibers of the polypropylene nonwoven fabric.

실시예Example 2 2

침전 시간을 30초 동안만 수행한 것을 제외하고는 실시예 1과 동일하게 실시하여 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric was prepared in the same manner as in Example 1 except that the sedimentation time was only 30 seconds.

실시예Example 3 3

열가교 온도 및 시간을 100℃에서 5분간 열 가교를 실시한 것을 제외하고는 실시예 1과 동일하게 실시하여 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric was prepared in the same manner as in Example 1 except that the thermal crosslinking temperature and time were thermally crosslinked at 100 占 폚 for 5 minutes.

실시예Example 4 4

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 비스페놀 F형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 0.9 중량부를 포함하는 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric containing 0.9 part by weight of the bisphenol F type epoxy resin and 0.9 part by weight of the polyethyleneimine was prepared in the same manner as in Example 1 except that 100 parts by weight of the total solvent was used.

실시예Example 5 5

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 1.8 중량부를 포함하는 양전하 코팅제를 제조한 후, 이를 이용하여 항바이러스 부직포를 제조하였다.
Except that 0.9 parts by weight of the novolak type epoxy resin and 1.8 parts by weight of the polyethyleneimine were added to 100 parts by weight of the total solvent and the antiviral nonwoven fabric was prepared Respectively.

실시예Example 6 6

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 3.5 중량부를 포함하는 양전하 코팅제를 제조한 후, 이를 이용하여 항바이러스 부직포를 제조하였다.
Except that 0.9 parts by weight of the novolak type epoxy resin and 3.5 parts by weight of the polyethyleneimine were added to 100 parts by weight of the total solvent and the antiviral nonwoven fabric was prepared Respectively.

실시예Example 7 7

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 0.5 중량부를 포함하는 양전하 코팅제를 제조한 후, 이를 이용하여 항바이러스 부직포를 제조하였다.Except that 0.9 parts by weight of the novolak type epoxy resin and 0.5 part by weight of the polyethyleneimine were added to 100 parts by weight of the entire solvent and then an antiviral nonwoven fabric was prepared using the same Respectively.

실시예Example 8 8

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 디페닐아민 0.9 중량부를 포함하는 양전하 코팅제를 제조한 후, 이를 이용하여 항바이러스 부직포를 제조하였다.
Except that 0.9 parts by weight of the novolak type epoxy resin and 0.9 part by weight of the diphenylamine were added to 100 parts by weight of the total solvent, and then an antiviral nonwoven fabric was prepared using the same. .

실시예Example 9 9

상기 실시예 1과 동일하게 실시하되, 평균공경 15㎛, 섬도가 평균직경 7㎛ 및 평균두께 653㎛를 갖는 폴리프로필렌 부직포를 사용하여 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric was prepared in the same manner as in Example 1 except that polypropylene nonwoven fabric having an average pore size of 15 mu m, a fineness average diameter of 7 mu m and an average thickness of 653 mu m was used.

실시예Example 10 10

상기 실시예 1과 동일하게 실시하되, 코팅 용액을 메탄올 용액에 희석하지 않고 이를 이용한 항바이러스 부직포를 제조하였다.
The procedure of Example 1 was repeated except that the coating solution was not diluted in a methanol solution to prepare an antiviral nonwoven fabric.

비교예Comparative Example 1 One

실시예 1과 동일하게 실시하여 항바이러스 부직포를 제조하되, 폴리프로필렌 부직포로서, 평균공경 50㎛, 섬도가 평균직경 15㎛ 및 평균두께 996㎛를 갖는 폴리프로필렌 부직포를 사용한 것을 제외하고는 실시예 1과 동일하게 실시하여 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric was produced in the same manner as in Example 1 except that a polypropylene nonwoven fabric having an average pore size of 50 mu m, a fineness average diameter of 15 mu m and an average thickness of 996 mu m was used as the polypropylene nonwoven fabric, To prepare an antiviral nonwoven fabric.

비교예Comparative Example 2 2

열가교 온도 및 시간을 50℃에서 6 시간 동안 열가교를 실시한 것을 제외하고는 실시예 1과 동일하게 실시하여 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric was prepared in the same manner as in Example 1, except that the thermal crosslinking temperature and time were thermally crosslinked at 50 캜 for 6 hours.

비교예Comparative Example 3 3

열가교 온도 및 시간을 145℃에서 2 시간 동안 열가교를 실시한 것을 제외하고는 실시예 1과 동일하게 실시하여 항바이러스 부직포를 제조하였다.
An antiviral nonwoven fabric was prepared in the same manner as in Example 1 except that the thermal crosslinking temperature and time were thermally crosslinked at 145 占 폚 for 2 hours.

비교예Comparative Example 4 4

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 0.3 중량부를 포함하는 양전하 코팅제를 제조한 후, 이를 이용하여 항바이러스 부직포를 제조하였다.
Except that 0.9 parts by weight of the novolak type epoxy resin and 0.3 part by weight of the polyethyleneimine were added to 100 parts by weight of the total solvent and the antiviral nonwoven fabric was prepared Respectively.

비교예Comparative Example 5  5

상기 실시예 1과 동일하게 실시하되, 전체 용매 100 중량부에 대하여 상기 노볼락형 에폭시 수지 0.9 중량부 및 상기 폴리에틸렌이민 10 중량부를 포함하는 양전하 코팅제를 제조한 후, 이를 이용하여 항바이러스 부직포를 제조하였다.
Except that 0.9 parts by weight of the novolak type epoxy resin and 10 parts by weight of the polyethyleneimine were added to 100 parts by weight of the entire solvent and the antiviral nonwoven fabric was prepared Respectively.

실험예Experimental Example 1 One

상기 실시예 1 ~ 10, 비교예 1 ~ 5 에서 제조된 다공성 복합여재의 기본 물성을 파악하기 위해 분리막 기공 평가기(Maker:PMI, model: CFP-1200-AE) 기기를 사용하여 평균공경을 측정하였고, 평막 평가기((주)웅진케미칼 제작)를 이용하여 직경이 90mm인 샘플 홀더를 통해 일정한 압력(1bar)으로 단위면적 및 분당 유량을 측정하였다.The average pore size was measured by using a membrane porosimetric analyzer (PMI, model: CFP-1200-AE) to evaluate the basic properties of the porous composite media prepared in Examples 1 to 10 and Comparative Examples 1 to 5 And the flow rate per unit area and per minute was measured at a constant pressure (1 bar) through a sample holder having a diameter of 90 mm using a flat membrane evaluation machine (manufactured by Woongjin Chemical Co., Ltd.).

또한, 평막 평가기((주)웅진케미칼 제작)-직경이 90mm인 샘플 홀더를 통해 1bar의 정압에서 PFU/㎖(PFU: plaque formingunits)단위로 8×105/㎖로 희석한 바이러스(MS2 phage) 용액을 투과시켜 미생물 제거성능을 평가하였으며, 그 결과를 하기 표 1에 나타내었다.A virus (MS2 phage) diluted to 8 x 10 < 5 > / ml in PFU / ml (PFU: plaque forming units) at a constant pressure of 1 bar through a sample holder having a diameter of 90 mm was used for a flat membrane evaluator (manufactured by Woongjin Chemical Co., ) Solution was permeated to evaluate microbial removal performance. The results are shown in Table 1 below.

구분division 당량비
(에폭시 : PEI)Equivalence ratio
(Epoxy: PEI) 부직포
평균
두께(㎛)Non-woven
Average
Thickness (㎛) 여재
평균공경
(㎛)Filter media
Average pore size
(탆) 침전
온도
(℃)Sedimentation
Temperature
(° C) 침전
시간Sedimentation
time 열가교
온도
(℃)Thermal crosslinking
Temperature
(° C) 열가교
시간Thermal crosslinking
time 평균수투과량
(㎖/cm2·min·bar)Average permeability
(Ml / cm 2 .min.bar) 표면전하
(mV)Surface charge
(mV) 바이러스
제거성능(log)virus
Removal performance (log) 실시예 1Example 1 1:21: 2 703703 66 2525 12시간12 hours 8080 6시간6 hours 7373 3535 4.74.7 실시예 2Example 2 1:21: 2 701701 66 2525 30초30 seconds 8080 6시간6 hours 7070 3030 3.53.5 실시예 3Example 3 1:21: 2 704704 66 2525 12시간12 hours 100100 5 분5 minutes 6868 3030 2.62.6 실시예 4Example 4 1:21: 2 702702 66 2525 12시간12 hours 8080 6시간6 hours 6262 2828 3.83.8 실시예 5Example 5 1:41: 4 702702 66 2525 12시간12 hours 8080 6시간6 hours 7575 3636 4.94.9 실시예 6Example 6 1:81: 8 702702 66 2525 12시간12 hours 8080 6시간6 hours 7474 4242 5.15.1 실시예 7Example 7 1:11: 1 699699 66 2525 12시간12 hours 8080 6시간6 hours 7979 2323 3.03.0 실시예 8Example 8 1:11: 1 708708 66 2525 12시간12 hours 8080 6시간6 hours 5858 2626 3.43.4 실시예 9Example 9 1:21: 2 653653 1515 2525 12시간12 hours 100100 5 분5 minutes 6969 3535 4.44.4 실시예 10Example 10 1:21: 2 695695 66 2525 12시간12 hours 8080 6시간6 hours 6565 3333 4.54.5 비교예 1Comparative Example 1 1:21: 2 996996 5050 2525 12시간12 hours 8080 6시간6 hours 9292 2525 1.01.0 비교예 2Comparative Example 2 1:21: 2 702702 66 2525 12시간12 hours 5050 6시간6 hours 5353 55 0.60.6 비교예 3Comparative Example 3 1:21: 2 730730 66 2525 12시간12 hours 145145 2시간2 hours 1919 3737 4.94.9 비교예 4Comparative Example 4 1:0.31: 0.3 704704 66 2525 12시간12 hours 5050 6시간6 hours 3333 77 1.41.4 비교예 5Comparative Example 5 1:111:11 703703 66 2525 12시간12 hours 5050 6시간6 hours 3838 2727 1.61.6

상기 표 1에서 알 수 있듯이, 실시예 1 ~ 실시예 10의 항바이러스 부직포의 바이러스 제거 성능은 항바이러스 부직포 제조조건에 따라 2.0log 이상, 바람직하게는 2.6 ~ 4.7log로 매우 우수한 것을 확인할 수 있으며, 평균수투과량 또한 우수한 것을 확인할 수 있다. As can be seen from Table 1, the virus removal performance of the anti-viral nonwoven fabrics of Examples 1 to 10 was 2.0 log or more, preferably 2.6 to 4.7 log, And the average water permeation amount is also excellent.

그러나, 평균공경이 30㎛ 초과한 부직포를 사용한 비교예 1의 경우, 평균수투과량은 우수하나, 바이러스 제거성능이 미흡한 문제가 있었다. 그리고, 열가교 온도가 60℃ 미만이었던 비교예 2의 경우, 항바이러스 성능이 저조했는데, 이는 양전하 코팅제 성분이 부직포에 잘 가교되지 않았기 때문인 것으로 판단된다. 그리고, 열가교 온도가 130℃를 초과한 비교예 3의 경우, 바이러스 제거성능이 매우 우수했으나, 평균수투과량이 크게 떨어졌는데, 이는 부직포의 공경이 열변형이 일어나서 공경이 작아졌기 때문인 것으로 판단된다. However, in the case of Comparative Example 1 using nonwoven fabric having an average pore size exceeding 30 탆, there was a problem that the average water permeation amount was excellent but the virus removal performance was insufficient. In the case of Comparative Example 2 in which the thermal crosslinking temperature was less than 60 캜, the antiviral performance was poor because the positive charge coating agent component was not crosslinked well to the nonwoven fabric. In the case of Comparative Example 3 in which the thermal crosslinking temperature exceeded 130 캜, the virus removal performance was excellent, but the average water permeation amount was greatly decreased. This is because the pore size of the nonwoven fabric was affected by thermal deformation and decreased pore size.

또한, 다관능성 아민 화합물을 가교제 1 당량비에 대하여 0.5 당량비 미만으로 사용한 비교예 4의 경우, 바이러스 제거성능은 크게 감소하여 그 기능을 잃은 것을 확인할 수 있었다. 또한, 다관능성 아민 화합물을 가교제 1 당량비에 대하여 10 당량비를 초과하여 사용한 비교예 5의 경우, 실시예 6과 비교할 때 더이상의 바이러스 제거성능 향상이 없었으며, 오히려 평균수투과량이 감소하는 문제를 보였으며, 바이러스 제거성능도 감소했는데, 이는 미반응물이 용출되어 발생한 것으로 판단된다.
In addition, in the case of Comparative Example 4 in which the polyfunctional amine compound was used in an amount less than 0.5 equivalence ratio with respect to one equivalent ratio of the crosslinking agent, the virus removal performance was greatly reduced and it was confirmed that the function was lost. In Comparative Example 5, in which the polyfunctional amine compound was used in an amount of more than 10 equivalents based on one equivalent ratio of the crosslinking agent, there was no improvement in the virus removal performance, but rather the average water permeation amount was reduced , And the virus removal performance was also decreased, which is considered to be caused by the elution of unreacted materials.

제조예Manufacturing example 1 : 양전하 필터 카트리지의 제조 1: Manufacture of positive charge filter cartridge

상기 실시예 1에서 제조한 항바이러스 부직포의 일면에 평균공경 0.2㎛ 영역대 및 평균두께 125㎛의 폴리술폰막(웅진케미칼사 제품)을 적층하여 양전하 필터 카트리지를 제조하였다.
A polysulfone membrane (manufactured by Woongjin Chemical Co., Ltd.) having an average pore size of 0.2 탆 area and an average thickness of 125 탆 was laminated on one side of the antiviral nonwoven fabric prepared in Example 1 to prepare a positive charge filter cartridge.

제조예Manufacturing example 2 2

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 평균공경 0.45㎛ 영역대 및 및 평균두께 125㎛의 폴리술폰막(웅진케미칼사 제품)을 사용하여 양전하 필터 카트리지르 제조하였다.
A positive charge filter cartridge was prepared in the same manner as in Preparation Example 1 except that a polysulfone membrane having an average pore size of 0.45 μm and a mean thickness of 125 μm (manufactured by Woongjin Chemical Co., Ltd.) was used.

제조예Manufacturing example 3 3

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 도 4와 같은 형태인 2층으로 적층된 항바이러스 부직포를 사용하여 양전하 필터 카트리지를 제조하였다.
A positive charge filter cartridge was prepared in the same manner as in Preparation Example 1 except that the antiviral nonwoven fabric laminated with two layers as shown in FIG. 4 was used.

제조예Manufacturing example 4 4

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 도 5와 같은 형태인 3층으로 적층된 항바이러스 부직포를 사용하여 양전하 필터를 제조하였다.
A positive charge filter was prepared by using the antiviral nonwoven fabric laminated in three layers as shown in FIG. 5 by preparing a positive charge filter cartridge in the same manner as in Preparation Example 1.

제조예Manufacturing example 5 5

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 평균공경 0.90㎛ 영역대 및 및 평균두께 125㎛의 폴리술폰막(웅진케미칼사 제품)을 사용하여 양전하 필터 카트리지르 제조하였다.
A positive charge filter cartridge was prepared in the same manner as in Preparation Example 1 except that a polysulfone membrane (manufactured by Woongjin Chemical Co., Ltd.) having an average pore size of 0.90 mu m and a mean thickness of 125 mu m was used.

제조예Manufacturing example 6  6

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 평균공경 0.2㎛ 영역대 및 평균두께 145㎛의 폴리술폰막(웅진케미칼사 제품)을 사용하여 양전하 필터 카트리지르 제조하였다.
A positive charge filter cartridge was prepared in the same manner as in Preparation Example 1 except that a polysulfone membrane (manufactured by Woongjin Chemical Co., Ltd.) having an average pore size of 0.2 μm area band and an average thickness of 145 μm was used.

비교제조예Comparative Manufacturing Example 1 One

상기 실시예 1에서 제조한 항바이러스 부직포만으로 양전하 필터 카트리지로 사용하였다.
Only the antiviral nonwoven fabric prepared in Example 1 was used as a positive charge filter cartridge.

비교제조예Comparative Manufacturing Example 2 2

평균공경 0.2㎛ 영역대 및 평균두께 125㎛의 폴리술폰막(웅진케미칼사 제품)만을 양전하 필터 카트리지로 사용하였다.
A polysulfone membrane (manufactured by Woongjin Chemical) having an average pore size of 0.2 μm area and an average thickness of 125 μm was used as a positive charge filter cartridge.

비교제조예Comparative Manufacturing Example 3  3

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 평균공경 1.2 ㎛ 영역대 및 평균두께 120㎛의 폴리술폰막(웅진케미칼사 제품)을 사용하여 양전하 필터 카트리지를 제조하였다.
A positive charge filter cartridge was prepared using a polysulfone membrane (manufactured by Woongjin Chemical Co., Ltd.) having an average pore size of 1.2 탆 area area and an average thickness of 120 탆 in the same manner as in preparation example 1 above.

비교제조예Comparative Manufacturing Example 4  4

상기 제조예 1과 동일한 방법으로 양전하 필터 카트리지를 제조하되, 평균공경 0.2 ㎛ 영역대 및 평균두께 190㎛의 폴리술폰막(웅진케미칼사 제품)을 사용하여 양전하 필터 카트리지를 제조하였다.
A positive charge filter cartridge was manufactured using a polysulfone membrane (manufactured by Woongjin Chemical Co., Ltd.) having an average pore size of 0.2 탆 area area and an average thickness of 190 탆 in the same manner as in preparation example 1 above.

실험예Experimental Example 2 2

상기 제조예 1 ~ 6, 비교제조예 1 ~ 4 에서 제조된 양전하 필터 카트리지의 기본 물성을 파악하기 위해 분리막 기공 평가기(Maker:PMI, model: CFP-1200-AE) 기기를 사용하여 평균공경을 측정하였고, 평막 평가기((주)웅진케미칼 제작)를 이용하여 직경이 90mm인 샘플 홀더를 통해 일정한 압력(1bar)으로 단위면적 및 분당 유량을 측정하였다.In order to understand the basic properties of the positive charge filter cartridges prepared in Production Examples 1 to 6 and Comparative Production Examples 1 to 4, the average pore size was measured using a membrane porosity evaluation machine (PMI, model: CFP-1200-AE) And the flow rate per unit area and per minute was measured at a constant pressure (1 bar) through a sample holder having a diameter of 90 mm using a flat film evaluator (manufactured by Woongjin Chemical Co., Ltd.).

또한, 평막 평가기((주)웅진케미칼 제작)을 이용하여 직경이 90mm인 샘플 홀더를 통해 1bar의 정압에서 CFU/㎖(CFU: colony-forming units)단위로 8.2×107/㎖로 희석한 박테리아(Pseudomonasdiminuta) 용액을 투과시켜 미생물 제거성능을 평가하였다.The sample was diluted to 8.2 x 10 < 7 > / ml in CFU / ml (CFU: colony-forming units) at a constant pressure of 1 bar through a sample holder having a diameter of 90 mm using a flat membrane evaluator (manufactured by Woongjin Chemical) The bacterial (Pseudomonas diminuta) solution was permeated to evaluate microbial removal performance.

또한, 평막 평가기((주)웅진케미칼 제작)-직경이 90mm인 샘플 홀더를 통해 1bar의 정압에서 PFU/㎖(PFU: plaque formingunits)단위로 8×105/㎖로 희석한 바이러스(MS2 phage) 용액을 투과시켜 미생물 제거성능을 평가하였으며, 그 결과를 하기 표 2에 나타내었다.A virus (MS2 phage) diluted to 8 x 10 < 5 > / ml in PFU / ml (PFU: plaque forming units) at a constant pressure of 1 bar through a sample holder having a diameter of 90 mm was used for a flat membrane evaluator (manufactured by Woongjin Chemical Co., ) Solution was permeated to evaluate microbial removal performance. The results are shown in Table 2 below.

구분division 폴리술폰막
평균
두께(㎛)Polysulfone film
Average
Thickness (㎛) 폴리술폰막
평균공경(㎛)Polysulfone film
Average pore size (탆) 양전하 필터
카트리지의
평균수투과량
(㎖/cm2·min·bar)Positive charge filter
Of the cartridge
Average permeability
(Ml / cm 2 .min.bar) 바이러스
제거성능
(log)virus
Removal performance
(log) 박테리아
제거성능
(log)bacteria
Removal performance
(log) 제조예 1Production Example 1 125125 0.20.2 3636 4.7 4.7 9.3 9.3 제조예 2Production Example 2 125125 0.450.45 4747 4.54.5 9.19.1 제조예 3Production Example 3 125125 0.20.2 3232 5.05.0 9.19.1 제조예 4Production Example 4 125125 0.20.2 6464 5.35.3 9.29.2 제조예 5Production Example 5 125125 0.900.90 3434 2.72.7 7.57.5 제조예 6Production Example 6 145145 0.20.2 7373 4.84.8 9.59.5 비교제조예 1Comparative Preparation Example 1 -- -- 6161 4.5 4.5 0.30.3 비교제조예 2Comparative Production Example 2 125125 0.20.2 5454 0.1 0.1 8.9 8.9 비교제조예 3Comparative Production Example 3 120120 1.21.2 1919 4.54.5 5.85.8 비교제조예 4Comparative Production Example 4 190190 0.20.2 2828 4.84.8 9.89.8

상기 표 2의 실험결과를 살펴보면, 제조에 1 ~ 제조예 6의 경우, 바이러스 제거성능이 2log 이상으로, 바람직하게는 2.5log ~ 5.0log로 매우 우수했으며, 박테리아 제거성능 또한 7log 이상, 바람직하게는 7.5log 이상으로 매우 우수할 뿐만 아니라, 평균수과량도 20㎖/cm2·min·bar 이상으로 적정한 것을 확인할 수 있었다.As shown in the results of Table 2, the virus removal performance of Preparation 1 to Preparation Example 6 was excellent at 2 log or more, preferably 2.5 log to 5.0 log, and the bacterial removal performance was also 7 log or more, It was found that not only the water solubility was excellent not less than 7.5 log but also the average excess amount was more than 20 ml / cm 2 · min · bar.

그러나, 폴리술폰막을 사용하지 않은 비교제조예 1의 경우, 박테리아 제거효과가 거의 없었으며, 항바이러스 부직포를 사용하지 않은 비교제조예 2의 경우, 바이러스 제거 효과가 거의 없었다. However, Comparative Production Example 1, which did not use a polysulfone membrane, had almost no bacterial removal effect, and Comparative Production Example 2, which did not use an antiviral nonwoven fabric, showed almost no virus removal effect.

평균공경이 1㎛를 초과한 폴리술폰막을 사용한 비교제조예 3의 경우, 제조예 1과 비교할 때, 박테리아 제거성능이 크게 감소하는 문제가 있었다. 그리고, 평균두께가 190㎛를 초과한 폴리술폰막을 사용한 비교제조예 4의 경우, 제조예 1 및 제조예 6와 비교해 보면, 박테리아 제거성능이 상승했으나, 평균수투과량이 떨어지는 문제가 있었다.
In Comparative Preparation Example 3 using a polysulfone membrane having an average pore size exceeding 1 탆, there was a problem that the bacterial removal performance was greatly reduced as compared with Preparation Example 1. In Comparative Preparation Example 4 using a polysulfone membrane having an average thickness exceeding 190 占 퐉, there was a problem that the bacterial removal performance was increased but the average water permeation amount was lowered as compared with Production Example 1 and Production Example 6. [

상기 실시예 및 비교예를 통하여 본 발명의 양전하 필터 카트리지가 우수한 수투과량, 바이러스 제거성능 및 박테이라 제거성능을 갖는 것을 확인할 수 있었으며, 본 발명의 양전하 필터 카트리지는 기존의 유기섬유 기반의 항바이러스 부직포를 대체할 수 있는 친환경적인 필터 카트리지임을 확인할 수 있었다. 이러한, 본 발명의 필터 카트리지는 다양한 직수형 필터에 사용하기에 적합하며, 바람직하게는 비저장형 직수형 필터로서, 더욱 바람직하게는 제약용 비저장형 직수형 필터 등에 적용시킬 수 있다.
The positive charge filter cartridge of the present invention has excellent water permeation amount, virus removal performance, and bacteriophage removal performance through the above Examples and Comparative Examples, and the positive charge filter cartridge of the present invention can be applied to existing organic fiber- Friendly filter cartridge that can be used as a substitute for the filter cartridge. Such filter cartridges of the present invention are suitable for use in various linear filters, preferably non-storage linear filters, and more preferably non-storage linear filters for pharmaceutical use.

300 :양전하 필터 카트리지 301 : 폴리술폰계 분리막
302 : 항바이러스 부직포 300: Positive charge filter cartridge 301: Polysulfone-based membrane
302: Anti-virus nonwoven fabric

Claims (16)

항바이러스 부직포 및 폴리술폰계 분리막을 포함하며,
필터링(filtering) 방향으로 상기 항바이러스 부직포의 일면에 상기 폴리술폰계 분리막이 적층되고,
상기 항바이러스 부직포는 폴리프로필렌 섬유, 폴리에틸렌테레프탈레이트 섬유, 폴리에틸렌 섬유, 폴리에스테르 섬유, 나일론 섬유 및 셀룰로오스 섬유 중 선택된 1종 이상을 함유한 부직포; 및 상기 부직포의 내부 및 표면에 양전하 코팅층;이 형성되어 있으며,
상기 양전하 코팅층은 비스페놀 A 에폭시 수지, 비스페놀 F 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 F 에폭시 수지, 난연성 에폭시(brominated epoxy) 수지 및 노볼락형 에폭시 수지 중에서 선택된 1종 이상을 함유하는 가교제; 및
폴리에틸렌이민, 디에틸렌트리아민, 피페라진, 디메틸렌피페라진 및 디페닐아민 중에서 선택된 1종 이상을 함유하는 다관능성 아민 화합물;을 포함하는 것을 특징으로 하는 양전하 카트리지 필터.
An antiviral nonwoven fabric and a polysulfone-based membrane,
The polysulfone separator is laminated on one side of the antiviral nonwoven fabric in a filtering direction,
The antiviral nonwoven fabric may be a nonwoven fabric containing at least one selected from the group consisting of polypropylene fibers, polyethylene terephthalate fibers, polyethylene fibers, polyester fibers, nylon fibers and cellulose fibers; And a positive charge coating layer formed on the inside and the surface of the nonwoven fabric,
Wherein the positive charge coating layer contains at least one selected from the group consisting of bisphenol A epoxy resin, bisphenol F epoxy resin, hydrogenated bisphenol A epoxy resin, hydrogenated bisphenol F epoxy resin, flame retardant epoxy resin and novolac epoxy resin A crosslinking agent; And
A polyfunctional amine compound containing at least one member selected from the group consisting of polyethyleneimine, diethylenetriamine, piperazine, dimethylenepiperazine and diphenylamine.
삭제delete 제1항에 있어서, 상기 가교제 및 다관능성 아민 화합물를 1 : 0.5 ~ 10 당량비로 포함하는 것을 특징으로 하는 양전하 카트리지 필터.
The positive charge cartridge according to claim 1, wherein the cross-linking agent and the polyfunctional amine compound are contained in an amount of 1: 0.5 to 10 equivalents.
제1항에 있어서, 상기 부직포는 섬도가 평균직경 0.5 ~ 10㎛ 및 평균공경 1 ~ 30㎛인 것을 특징으로 하는 양전하 카트리지 필터.
2. The positive charge cartridge as claimed in claim 1, wherein the nonwoven fabric has an average diameter of 0.5 to 10 mu m and an average pore diameter of 1 to 30 mu m.
제 1항에 있어서, 상기 부직포는 평균두께 0.1 ~ 2㎜ 것을 특징으로 하는 양전하 카트리지 필터.
The positive charge cartridge according to claim 1, wherein the nonwoven fabric has an average thickness of 0.1 to 2 mm.
제 1항에 있어서, 항바이러스 부직포는 표면전하가 10 ~ 50 mV 인 것을 특징으로 하는 양전하 카트리지 필터.
The positive charge cartridge according to claim 1, wherein the antiviral nonwoven fabric has a surface charge of 10 to 50 mV.
제1항에 있어서, 상기 폴리술폰계 분리막은
폴리에테르술폰, 폴리술폰, 폴리알릴에테르술폰 및 폴리페닐설폰 중에서 선택된 1종 이상을 함유한 폴리술폰계 중합체를 포함하거나 또는
상기 폴리술폰계 중합체 및 폴리에테르에테르케톤을 포함하는 것을 특징으로 하는 양전하 카트리지 필터.
The method according to claim 1, wherein the polysulfone-
A polysulfone-based polymer containing at least one member selected from the group consisting of polyether sulfone, polysulfone, polyallyl ether sulfone, and polyphenyl sulfone;
Wherein the polysulfone-based polymer and the polyether ether ketone are contained.
제 1항에 있어서, 상기 폴리술폰계 분리막은
평균공경이 0.1 ~ 1㎛ 및 평균두께 100 ~ 180 ㎛인 것을 특징으로 하는 양전하 카트리지 필터.
The method according to claim 1, wherein the polysulfone-
Wherein the average pore diameter is 0.1 to 1 占 퐉 and the average thickness is 100 to 180 占 퐉.
제1항 및 제3항 내지 제8항 중에서 선택된 어느 한 항에 있어서, 평균수투과량이 20 ~ 80 ㎖/cm2·min·bar인 것을 특징으로 하는 양전하 카트리지 필터.
9. The positive charge cartridge as claimed in any one of claims 1 to 8, wherein the average water permeation amount is 20 to 80 ml / cm < 2 >
제9항에 있어서,
바이러스 제거성능이 2 log 이상이고, 박테리아 제거성능이 7 log 이상인 것을 특징으로 하는 양전하 카트리지 필터.
10. The method of claim 9,
Wherein the virus removal performance is 2 log or more and the bacteria removal performance is 7 log or more.
제1항 및 제3항 내지 제8항 중에서 선택된 어느 한 항의 양전하 카트리지 필터를 포함하는 것을 특징으로 하는 비저장형 직수형 필터.
9. A non-storage type linear filter, comprising a positive charge cartridge filter according to any one of claims 1 to 8.
폴리술폰계 분리막의 일면에 항바이러스 부직포를 단층 또는 다층으로 적층 및 합지시켜서 제조하며,
상기 항바이러스 부직포는 양전하 코팅제에 부직포를 침전시켜서 부직포에 양전하 코팅제를 코팅시키는 단계; 및 양전하 코팅제가 코팅된 부직포를 열가교시켜서 양전하 코팅층을 형성시키는 단계;를 포함하는 공정을 수행하여 제조한 것을 특징으로 하는 양전하 카트리지 필터의 제조방법.
The non-woven fabric is prepared by laminating and laminating an antiviral nonwoven fabric on one side of a polysulfone-based membrane as a single layer or multiple layers,
Wherein the antiviral nonwoven fabric is formed by depositing a nonwoven fabric in a positive charge coating agent and coating a positive charge coating agent on the nonwoven fabric; And thermally crosslinking the nonwoven fabric coated with the positive charge coating agent to form a positive charge coating layer.
제12항에 있어서, 상기 양전하 코팅제는
디메틸아세트아마이드, 디메틸포름아미드, N-메틸-2-피롤리돈, 에탄올, 이소프로필알콜, 아세톤 및 메탄올 중에서 선택된 1종 이상을 함유한 용매;
비스페놀 A 에폭시 수지, 비스페놀 F 에폭시 수지, 수소첨가된 비스페놀 A 에폭시 수지, 수소첨가된 비스페놀 F 에폭시 수지, 난연성 에폭시(brominated epoxy) 수지 및 노볼락형 에폭시 수지 중에서 선택된 1종 이상을 함유한 가교제; 및
폴리에틸렌이민, 디에틸렌트리아민, 피페라진, 디메틸렌피페라진 및 디페닐아민 중에서 선택된 1종 이상을 함유한 다관능성 아민 화합물;
을 포함하는 것을 특징으로 하는 양전하 카트리지 필터의 제조방법.
13. The method according to claim 12, wherein the positive charge coating agent
A solvent containing at least one selected from the group consisting of dimethylacetamide, dimethylformamide, N-methyl-2-pyrrolidone, ethanol, isopropyl alcohol, acetone and methanol;
A crosslinking agent containing at least one selected from the group consisting of bisphenol A epoxy resin, bisphenol F epoxy resin, hydrogenated bisphenol A epoxy resin, hydrogenated bisphenol F epoxy resin, flame retardant epoxy resin and novolak epoxy resin; And
A polyfunctional amine compound containing at least one member selected from the group consisting of polyethyleneimine, diethylenetriamine, piperazine, dimethylenepiperazine and diphenylamine;
Wherein the positive charge cartridge filter comprises:
제12항에 있어서, 상기 침전은 15℃ ~ 40℃에서 5초 ~ 15시간 동안 수행하는 것을 특징으로 하는 양전하 카트리지 필터의 제조방법.
[13] The method of claim 12, wherein the precipitation is performed at 15 [deg.] C to 40 [deg.] C for 5 seconds to 15 hours.
제12항에 있어서, 상기 열가교는 60℃ ~ 130℃ 하에서, 15초 ~ 8시간 동안 건조 및 가교를 수행하는 것을 특징으로 하는 양전하 카트리지 필터의 제조방법.
13. The method of claim 12, wherein the thermal crosslinking is performed at 60 DEG C to 130 DEG C for 15 seconds to 8 hours.
제12항에 있어서, 상기 코팅시키는 단계의 침전 전의 부직포는 코로나, 플라즈마, 하이드로차징(hydro-charging), 스퍼터, 프라이머, 화염처리 및 산처리 중에서 선택된 1종 이상의 방법으로 부직포의 내부 및 표면을 전처리한 것을 특징으로 하는 양전하 카트리지 필터의 제조방법.The nonwoven fabric according to claim 12, wherein the nonwoven fabric before the precipitation of the nonwoven fabric is subjected to a pretreatment such as a corona, a plasma, a hydro-charging, a sputter, a primer, Wherein the positive charge cartridge filter is made of a metal.
KR1020130169204A 2013-12-31 2013-12-31 Positive electric charge- filter cartridge and Preparing method thereof KR101611676B1 (en)