KR101551389B1 - Processing method for reusing of fly ash using BM consortium - Google Patents
Processing method for reusing of fly ash using BM consortium Download PDFInfo
- Publication number
- KR101551389B1 KR101551389B1 KR1020130119727A KR20130119727A KR101551389B1 KR 101551389 B1 KR101551389 B1 KR 101551389B1 KR 1020130119727 A KR1020130119727 A KR 1020130119727A KR 20130119727 A KR20130119727 A KR 20130119727A KR 101551389 B1 KR101551389 B1 KR 101551389B1
- Authority
- KR
- South Korea
- Prior art keywords
- coal ash
- solid body
- weight
- hours
- power plant
- Prior art date
Abstract
본 발명은 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법에 관한 것으로, 더욱 상세하게는 화력발전소에서 발생하는 석탄재를 일정한 크기를 가지는 펠릿 형태로 성형한 후 ＢＭ균과 결합시켜 수처리장치의 여재, 양식장 및 양어장의 수질개선제, 음식물쓰레기의 분해촉진제 및 악취제거제, 토양의 산성화방지제 및 비료대체제, 물밑의 오염원제거제 등으로 재사용할 수 있도록 가공하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법에 관한 것이다.
이러한 본 발명은, 화력발전소에서 발생하는 분말 상태의 석탄재에 결합제를 첨가하여 일정 메쉬 크기를 가지는 펠릿 형태의 초기 고형체를 형성하는 제1단계; 상기 초기 고형체를 액상의 ＢＭ균에 12~36시간 동안 함침시켜 ＢＭ균을 함유한 중간 고형체를 형성하는 제2단계; 및 상기 중간 고형체를 12~36시간 동안 자연 건조시켜 최종 고형체를 형성하여 완료하는 제3단계;를 포함하여 구성됨을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법을 기술적 요지로 한다.
또한, 본 발명은, 화력발전소에서 발생하는 분말 상태의 석탄재를 액상의 ＢＭ균에 12~36시간 동안 함침시켜 ＢＭ균을 함유한 분말체를 형성하는 제1단계; 상기 분말체에 결합제를 첨가하여 일정 메쉬 크기를 가지는 펠릿 형태의 중간 고형체를 형성하는 제2단계; 및 상기 중간 고형체를 12~36시간 동안 자연 건조시켜 최종 고형체를 형성하여 완료하는 제3단계;를 포함하여 구성됨을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법도 기술적 요지로 한다. The present invention relates to a method for reusing coal ash using a fungus, and more particularly, to a method for recovering coal ash from a thermal power plant by forming BM as a pellet having a predetermined size, Processing method for the re-use of coal ash for thermal power plant using BM bacteria that can be re-used as water quality improvement agent for farms and fish farms, degradation promoter and odor removing agent for food waste, acidification inhibitor for soil, substitute for fertilizer, .
According to the present invention, there is provided a method for producing a pellet-shaped initial solid body having a predetermined mesh size by adding a binder to powdery coal ash generated in a thermal power plant; A second step of impregnating the initial solid body with BM bacteria in a liquid state for 12 to 36 hours to form a solid body containing BM bacteria; And a third step of naturally drying the intermediate solid for 12 to 36 hours to form and complete a final solid body. The method for processing coal ash of a thermal power plant using the BM microorganism according to claim 1, .
In addition, the present invention provides a method for producing BM bacteria, comprising: a first step of impregnating a liquid coalaceous material generated from a thermal power plant into BM bacteria of a liquid phase for 12 to 36 hours to form a powder containing BM bacteria; A second step of adding a binder to the powder to form a pellet-shaped intermediate solid having a predetermined mesh size; And a third step of naturally drying the intermediate solid for 12 to 36 hours to form and complete a final solid body. The method for reusing coal ash using a BM fungus is also provided. .
Description
본 발명은 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법에 관한 것으로, 더욱 상세하게는 화력발전소에서 발생하는 석탄재를 일정한 크기를 가지는 펠릿 형태로 성형한 후 ＢＭ균과 결합시켜 수처리장치의 여재, 양식장 및 양어장의 수질개선제, 음식물쓰레기의 분해촉진제 및 악취제거제, 토양의 산성화방지제 및 비료대체제, 물밑의 오염원제거제 등으로 재사용할 수 있도록 가공하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법에 관한 것이다.
The present invention relates to a method for reusing coal ash using a fungus, and more particularly, to a method for recovering coal ash from a thermal power plant by forming BM as a pellet having a predetermined size, Processing method for the re-use of coal ash for thermal power plant using BM bacteria that can be re-used as water quality improvement agent for farms and fish farms, degradation promoter and odor removing agent for food waste, acidification inhibitor for soil, substitute for fertilizer, .
일반적으로 석탄을 연료로 사용하는 화력발전소에서는 석탄을 태우고 남은 석탄재(또는 석탄회)가 발생하게 된다. 이러한 석탄재는 일부 시멘트 원료로 재사용하기도 하지만 대부분 매립 처리하고 있다. Generally, in coal-fired thermal power plants, coal ash (or fly ash) is left after burning coal. Such coal ash is reused as some cement raw material, but most of it is landfilled.
그러나 화력발전소는 계속해서 사용할 수밖에 없으므로 화력발전소의 사용으로 인해 계속해서 발생하는 석탄재를 매립 처리하는 비용이 엄청나게 소요될 뿐만 아니라 석탄재를 매립하기 위한 매립지를 선정하는데도 많은 어려움이 있는 문제점이 있었다. However, since thermal power plants are inevitable to continue to use, there is a problem that the use of thermal power plants is costly to continuously incinerate the coal ash, and there is a great difficulty in selecting a landfill for landfilling coal ash.
이러한 석탄재의 매립 비용 증가와 매립 선정의 어려움을 해소하기 위해서는 석탄재를 매립하지 않고 이를 가공하여 다른 다양한 분야에 재사용할 수 있는 가공방법들이 개발되고 있다. In order to overcome the difficulty of increasing the landfill cost of coal ash and selecting the landfill, processing methods are being developed that can be reused in various fields without processing coal ash.
그러나 석탄재를 재사용하기 위한 종래의 가공방법들은 공정이 매우 복잡하고 어려우므로 가공효율이 떨어질 뿐만 아니라 최종 가공물이 대부분 분말 형태이므로 사용 용도가 한 분야로 국한되는 문제점이 있다. However, the conventional processing methods for reusing coal ash are not only complicated and difficult because of the complicated process, but also have a problem in that the processing efficiency is lowered and the finished product is mostly in the form of powder.
따라서 석탄재를 더욱 간편하게 가공하여 최종 가공물로 재생할 수 있고 사용 용도도 다양한 분야로 확대할 수 있는 가공 기술에 대한 연구 개발이 절실히 요구되고 있는 실정이다.
Therefore, there is an urgent need for research and development of processing technology that can recycle the coal as a final processed product more easily and can expand its use to various fields.
본 발명은 상기한 문제점을 해소하기 위해 발명된 것으로서, 석탄재의 매립 비용의 과다 발생과 매립지 선정의 어려움을 일거에 해소할 수 있고 간편하고 효율적인 방법으로 가공하여 다양한 용도로 재사용할 수 있도록 하기 위하여, 석탄재를 적절한 메쉬 크기의 펠릿 형태로 가공한 후 ＢＭ균과 결합시켜 수처리여재, 수질개선제, 음식물쓰레기 분해촉진 및 악취제거제, 농토의 산성화방지제, 비료대체제, 물밑 오염원의 제거제 등으로 재사용할 수 있도록 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법을 제공하는데 그 목적이 있다. Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a method and apparatus for recovering coal ash, The coal ash is processed into pellets of appropriate mesh size and then combined with BM bacteria to be reused as a water treatment filter material, water quality improvement agent, food waste decomposition promotion and odor removing agent, agricultural soil acidifying agent, fertilizer substitute agent, The present invention provides a processing method for reusing coal ash using a BM.
본 발명의 목적은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 명확하게 이해될 수 있을 것이다.
The objects of the present invention are not limited to the above-mentioned objects, and other objects not mentioned can be clearly understood from the following description.
상기 목적을 달성하기 위한 본 발명에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법은, 화력발전소에서 발생하는 분말 상태의 석탄재에 결합제를 첨가하여 일정 메쉬 크기를 가지는 펠릿 형태의 초기 고형체를 형성하는 제1단계; 상기 초기 고형체를 액상의 ＢＭ균에 12~36시간 동안 함침시켜 ＢＭ균을 함유한 중간 고형체를 형성하는 제2단계; 및 상기 중간 고형체를 12~36시간 동안 자연 건조시켜 최종 고형체를 형성하여 완료하는 제3단계;를 포함하여 구성됨을 특징으로 한다. In order to accomplish the above object, the present invention provides a method for reusing coal ash using a fungus, comprising adding a binder to powdery coal ash produced in a thermal power plant to produce a pellet- A first step of forming a first electrode; A second step of impregnating the initial solid body with BM bacteria in a liquid state for 12 to 36 hours to form a solid body containing BM bacteria; And a third step of naturally drying the intermediate solid for 12 to 36 hours to form and complete a final solid body.
상기 제1단계는, 석탄재 60~70중량%와, 석회 모르타르로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출 성형한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of coal ash and 30 to 40% by weight of binder composed of lime mortar are mixed and extruded into pellets, followed by naturally drying for 12 to 36 hours to form the initial solid .
상기 제1단계는, 석탄재 60~70중량%와, 시멘트 모르타르로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출 성형한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of coal ash and 30 to 40% by weight of binder composed of cement mortar are mixed and extruded in the form of pellets, followed by naturally drying for 12 to 36 hours to form the initial solid .
상기 제1단계는, 상기 석탄재 60~70중량%와, 전분 수용액으로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출 성형한 후 20~40℃에서 12~36시간 동안 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of an aqueous starch solution are mixed and extruded in the form of pellets, followed by drying at 20 to 40 ° C for 12 to 36 hours, Thereby forming a shape.
상기 제1단계는, 상기 석탄재 60~70중량%와, 규산나트륨 수용액으로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of an aqueous sodium silicate solution are mixed and extruded into pellets, followed by naturally drying for 12 to 36 hours to form the initial solid .
상기 제1단계는, 상기 석탄재 60~70중량%와, 이온교환수지로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of an ion exchange resin are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid .
상기 제1단계는, 상기 석탄재 60~70중량%와, 아교로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder as a glue are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid .
상기 제1단계는, 상기 석탄재 60~70중량%와, 벤토나이트와 당밀로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 한다. In the first step, 60 to 70% by weight of the coal ash is mixed with 30 to 40% by weight of a binder composed of bentonite and molasses as a pellet, and the mixture is naturally dried for 12 to 36 hours to form the initial solid .
상기 최종 고형체는, 사용 용도에 따라 상기 제1단계에서 펠릿 형태의 메쉬 크기가 결정되는 것으로, 수처리장치의 여재로 사용되는 경우에는 4~9 메쉬 크기로 구성되고, 양식장 및 양어장의 수질개선제로 사용되는 경우에는 5~10 메쉬 크기로 구성되며, 음식물쓰레기의 분해촉진제 및 악취제거제로 사용되는 경우에는 5~10 메쉬 크기로 구성되고, 농토의 산성화방지제 및 비료대체제로 사용되는 경우에는 10~15메쉬 크기로 구성되며, 물밑 오염원의 제거제로 사용되는 경우에는 5~10 메쉬 크기로 구성되는 것을 특징으로 한다. The final solid body has a pellet-shaped mesh size determined in the first step, depending on the intended use. When the filter is used as a filter material of a water treatment apparatus, the final solid body has a size of 4 to 9 mesh, When it is used, it is composed of 5 ~ 10 mesh size. When it is used as a decomposition accelerator for food waste and a malodor removing agent, it is composed of 5 ~ 10 mesh size. When it is used as an acidifying agent and fertilizer substitute for agricultural land, Mesh size, and when it is used as a remover for underwater pollutants, it is composed of 5 to 10 mesh size.
상기 제1단계 이전에는, 상기 석탄재의 오염상태에 따라 상기 석탄재에 포함되어 있는 오염물질을 제거하는 전처리단계를 더 포함하는 구성되는 것을 특징으로 한다. The method may further include a pretreatment step of removing contaminants contained in the coal ash in accordance with the contamination state of the coal ash before the first step.
또한, 본 발명에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법은, 화력발전소에서 발생하는 분말 상태의 석탄재를 액상의 ＢＭ균에 12~36시간 동안 함침시켜 ＢＭ균을 함유한 분말체를 형성하는 제1단계; 상기 분말체에 결합제를 첨가하여 일정 메쉬 크기를 가지는 펠릿 형태의 고형체를 형성하는 제2단계; 및 상기 고형체를 12~36시간 동안 자연 건조시켜 최종 고형체를 형성하여 완료하는 제3단계;를 포함하여 구성되는 것도 특징으로 한다. In addition, the method for reusing coal ash using thermal fungus according to the present invention is characterized in that powdery coal ash produced in a thermal power plant is impregnated with BM fungi in liquid form for 12 to 36 hours, A first step of forming a first electrode; A second step of adding a binder to the powder to form a pellet-like solid having a mesh size; And a third step of naturally drying the solid body for 12 to 36 hours to form and complete a final solid body.
상기 제1단계 이전에는, 상기 석탄재의 오염 상태에 따라 상기 석탄재에 포함되어 있는 오염물질을 제거하는 전처리단계를 더 포함하는 구성되는 것을 특징으로 한다.
The method may further include a pretreatment step of removing contaminants contained in the coal ash in accordance with the contamination state of the coal ash before the first step.
상기한 구성에 의한 본 발명은, 화력발전소에서 발생하는 석탄재를 ＢＭ균과 결합시켜 펠릿 형태의 고형체로 형성시켜 수처리여재, 수질개선제, 음식물쓰레기 분해촉진 및 악취제거제, 농토의 산성화방지제, 비료대체제, 물밑 오염원의 제거제 등의 다양한 용도로 재사용할 수 있도록 함으로써, 석탄재에 대한 매립 비용의 과다 발생과 매립지 선정의 어려움을 일거에 해소할 수 있는 효과가 있다. The present invention based on the above-mentioned constitution is characterized in that coal ash generated in a thermal power plant is combined with BM bacteria to form a pellet-shaped solid body to form a water treatment filter medium, a water quality improving agent, a food waste disposal decomposition accelerator and a malodor removing agent, It is possible to eliminate the inconvenience of the incineration cost of the coal ash and the difficulty of the selection of the landfill as a whole.
본 발명에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법은, 매립 비용과 매립지 선정에 어려움이 많은 화력발전소에서 발생하는 석탄재를 매립 처리하지 않고 재사용 가능하도록 한 것이다. The method for reusing coal ash using coal fired power plant using BM according to the present invention enables reusable coal ash that is generated in a thermal power plant having many difficulties in landfill cost and selection of landfill.
특히, 본 발명에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법은, 상기 석탄재를 더욱 간편하게 가공하여 최종 가공물로 재생할 수 있고 이렇게 재생한 최종 가공물을 다양한 용도로 사용할 수 있는 것이 특징이다. Particularly, the processing method for reusing coal ash using coal fired power plant using BM bacteria according to the present invention is characterized in that the coal ash can be more easily processed and regenerated as a final processed product, and the thus-regenerated final processed product can be used for various purposes.
이러한 특징은, 분말 상태의 석탄재를 펠릿 형태로 가공한 후 액상의 ＢＭ균에 함침시킨 다음 건조하는 공정을 통해 ＢＭ균을 함유한 펠릿 형태의 최종 고형체를 제조하거나, 분말 상태의 석탄재를 액상의 ＢＭ균에 함침시켜 건조한 후 펠릿 형태로 가공한 다음 재차 건조하는 공정을 통해 ＢＭ균을 함유한 펠릿 형태의 최종 고형체를 제조함으로써 달성된다. This feature can be achieved by preparing a final solid body in the form of a pellet containing BM bacteria by processing the powdery coal as a pellet, impregnating the BM in the liquid phase and then drying it, By impregnating BM microorganism, drying it, then processing it into a pellet form, and then drying it again, thereby producing a final solid body in the form of pellets containing BM bacteria.
이렇게 제조 완료된 최종 고형체는 공기가 차단된 상태로 보관하고 있다가 수처리장치의 여재, 양식장 및 양어장의 수질개선제, 음식물쓰레기의 분해촉진제 및 악취제거제, 토양의 산성화방지제 및 비료대체제, 물밑의 오염원제거제 등으로 사용하게 되는 것이다.
The final solid body thus manufactured is kept in an air-blocked state, and is used as a filter medium for a water treatment apparatus, a water quality improvement agent for farms and fish farms, a degradation promoter and a malodor removing agent for food waste, an acidifying agent and a fertilizer substitute for soil, And so on.
이하 본 발명의 바람직한 제1실시예에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용방법을 단계적으로 상세하게 설명하면 다음과 같다. Hereinafter, a method for reusing coal ash from a thermal power plant using BM bacteria according to a first preferred embodiment of the present invention will be described in detail.
먼저, 제1단계는 화력발전소에 발생하는 분말 상태의 석탄재에 결합제를 첨가하여 펠릿 형태의 초기 고형체를 형성하는 단계이다. First, the first step is to form a pellet-shaped initial solid by adding a binder to powdery coal ash generated in a thermal power plant.
즉, 석탄재를 상기한 용도에 맞도록 펠릿 형태로 만드는 공정으로서, 석탄재 단독으로는 펠릿 형태로 성형이 불가능하므로 석탄재를 상호 결합시키는 기능을 하는 결합제를 별도로 첨가하여 초기 고형체를 형성하는 것이다. That is, the process of making the coal ash into a pellet form suitable for the above-mentioned use, since the coal ash alone can not be formed into a pellet form, the binder which functions to bind the coal ash is separately added to form an initial solid.
단, 석탄재를 펠릿 형태로 형성한 후에는 그 형태가 유지되도록 일정시간 동안 건조해야 한다.However, after the coal ash is formed into pellets, it must be dried for a certain period of time so as to maintain its shape.
이때 결합제는 석탄재를 상호 결합시켜 압출시 펠릿 형태로 성형 가능하면서도 사용 용도에 맞는 재질이면 가능한데, 결합제의 종류에 따라 아래에 제시된 방법들 중의 하나를 선택하면 된다. At this time, the binder can be formed into a pellet form when the coal materials are combined with each other by extrusion, but it is possible to use a material suitable for the use purpose. Depending on the type of binder, one of the following methods may be selected.
(1) 첫 번째 방법은, 석탄재 60~70중량%와, 석회와 물을 2:1로 혼합한 석회 모르타르로 이루어지는 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 12~36시간 동안 자연 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (1) In the first method, 60 to 70% by weight of coal ash and 30 to 40% by weight of binder composed of lime mortar mixed with 2: 1 of lime and water are mixed with a mixer and extruded at a high temperature through an extruder to form pellets And then dried naturally for 12 to 36 hours to form an initial solid body in the form of pellets.
(2) 두 번째 방법은, 석탄재 60~70중량%와, 시멘트와 물을 2:1로 혼합한 시멘트 모르타르로 이루어지는 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 12~36시간 동안 자연 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (2) In the second method, 30 to 40% by weight of binder composed of 60 to 70% by weight of coal ash and cement mortar mixed with 2: 1 of cement and water are mixed with a mixer and extruded at a high temperature through an extruder to form pellets And then dried naturally for 12 to 36 hours to form an initial solid body in the form of pellets.
(3) 세 번째 방법은, 석탄재 60~70중량%와 전분과 물을 2:1로 혼합한 전분 수용액으로 이루어지는 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 20~40℃에서 12~36시간 동안 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (3) In the third method, 30 to 40% by weight of a binder consisting of 60 to 70% by weight of coal ash and 2 to 1% of starch and water as a starch aqueous solution are mixed in a mixer and extruded at a high temperature through an extruder to form pellets Molded and then dried at 20 to 40 ° C for 12 to 36 hours to form an initial solid body in the form of pellets.
(4) 네 번째 방법은, 석탄재 60~70중량%와, 규산나트륨과 물이 2:1로 혼합한 규산나트륨 수용액으로 이루어지는 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 12~36시간 동안 자연 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (4) In the fourth method, 60 to 70% by weight of coal ash and 30 to 40% by weight of a binder composed of an aqueous solution of sodium silicate mixed with sodium silicate and water at a ratio of 2: 1 are mixed in a mixer and extruded at a high temperature through an extruder It is molded into pellets and dried naturally for 12 to 36 hours to form an initial solid body in the form of pellets.
(5) 다섯 번째 방법은, 석탄재 60~70중량%와, 이온교환수지로 이루어지는 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 12~36시간 동안 자연 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (5) In a fifth method, 60 to 70% by weight of coal ash and 30 to 40% by weight of binder composed of an ion exchange resin are mixed in a mixer, extruded at a high temperature through an extruder to form pellets, Followed by natural drying to form an initial solid body in the form of pellets.
(6) 여섯 번째 방법은, 석탄재 60~70중량%와, 아교로 이루어지는 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 12~36시간 동안 자연 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (6) In the sixth method, 60 to 70% by weight of coal ash and 30 to 40% by weight of binder as a glue are mixed in a mixer, extruded at a high temperature through an extruder to form pellets, To form an initial solid body in the form of pellets.
(7) 일곱 번째 방법은, 석탄재 60~70중량%와, 벤토나이트와 당밀로 이루어진 결합제 30~40중량%를 혼합기로 혼합하여 압출기를 통해 고온으로 압출하여 펠릿 형태로 성형한 후 12~36시간 동안 자연 건조시켜 펠릿 형태의 초기 고형체를 형성하는 방법이다. (7) In the seventh method, 60 to 70% by weight of coal ash and 30 to 40% by weight of binder composed of bentonite and molasses are mixed in a mixer, extruded at a high temperature through an extruder to form pellets, Followed by natural drying to form an initial solid body in the form of pellets.
그리고 초기 고형체는 사용 용도에 맞도록 그 크기가 메쉬 단위로 결정하면 된다. 즉, 수처리장치의 여재로 사용되는 경우에는 4~9 메쉬 크기로 결정하고, 양식장 및 양어장의 수질개선제로 사용되는 경우에는 5~10 메쉬 크기로 결정하면 된다. The size of the initial solids can be determined in mesh units to suit the application. That is, the size is determined to be 4 to 9 mesh when used as a filter medium of a water treatment apparatus, and 5 to 10 mesh size when it is used as a water quality improving agent for a farm and a fish farm.
또한, 음식물쓰레기의 분해촉진제 및 악취제거제로 사용되는 경우에는 5~10 메쉬 크기로 결정하고, 농토의 산성화방지제 및 비료대체제로 사용되는 경우에는 10~15메쉬 크기로 결정하며, 물밑 오염원의 제거제로 사용되는 경우에는 5~10 메쉬 크기로 결정하면 된다. When used as a degradation promoter and a malodor removing agent for food waste, it is determined to have a size of 5 to 10 mesh. When it is used as an acidification inhibitor for agricultural land and as a fertilizer substitute, it is determined to have a size of 10 to 15 mesh. If used, the size may be 5 to 10 mesh.
여기서, 석탄재가 화력발전소에서 배출되어 바닷물 속에 투입된 상태에서 건조되어 사용되는 경우에는 중금속 등의 오염물질이 자연스럽게 제거됨에 따라 오염물질을 제거하는 전처리 단계가 필요하지 않으나, 석탄재가 화력발전소에서 바로 배출된 상태인 경우에는 중금속 등의 오염물질이 포함된 상태임에 따라 오염물질을 제거하는 전처리 단계를 제1단계에서 앞서서 선행하는 것이 바람직하다. 중금속 등의 오염물질을 제거하는 방법은 이미 잘 알려진 기술로서 이에 대한 설명은 생략하기로 한다. In this case, when the coal ash is discharged from the thermal power plant and dried and used in the seawater, there is no need for a pretreatment step for removing contaminants as the contaminants such as heavy metals are removed naturally, but coal ash is discharged directly from the thermal power plant It is preferable that the pretreatment step for removing the contaminants is preceded by the preceding step in the first step since the contaminants such as heavy metals are contained. Methods for removing contaminants such as heavy metals are well known and will not be described here.
다음으로, 제2단계는 ＢＭ균을 함유한 펠릿 형태의 중간 고형체를 형성하는 단계이다. Next, the second step is a step of forming a pellet-like intermediate solid containing BM bacteria.
즉, 제2단계는 제1단계에서 형성한 초기 고형체에 ＢＭ균이 함유되도록 하는 공정으로서, 이는 펠릿 형태의 초기 고형체를 액상의 ＢＭ균에 함침시키는 것이다. That is, the second step is a step of causing BM bacteria to be contained in the initial solid formed in the first step, which is to impregnate the liquid solid BM bacteria with the initial solids in pellet form.
이때 초기 고형체에 ＢＭ균이 원활하게 함유되도록 초기 고형체를 액상의 ＢＭ균에 완전히 잠긴 상태로 함침시켜야 한다. 그리고 초기 고형체에 ＢＭ균이 원활하게 효과적으로 함유되도록 초기 고형체를 액상의 ＢＭ균에 12~36시간 동안 함침시켜야 한다. At this time, the initial solid body should be impregnated completely in the liquid BM bacterium so that the BM solid is smoothly contained in the initial solid body. The initial solids should be impregnated with liquid BM bacteria for 12 to 36 hours so that the initial solids contain the BM bacteria effectively and smoothly.
마지막으로, 제3단계는 ＢＭ균을 함유한 펠릿 형태의 최종 고형체를 형성하여 가공을 완료하는 단계이다. Finally, the third step is a step of forming a final solid body in the form of a pellet containing BM bacteria to complete processing.
즉, 제3단계는, 제2단계에서 ＢＭ균을 함유한 펠릿 형태의 중간 고형체를 수분이 제거되도록 12~36시간 동안 자연 건조하는 공정으로서, 이는 중간 고형체가 ＢＭ균에 함침시키는 공정에서 흡수하는 수분을 제거하기 위한 것이다. That is, the third step is a step of naturally drying the pellet-shaped intermediate solid containing BM bacteria in the second step for 12 to 36 hours to remove moisture, which is a step of immersing the intermediate solid in BM bacteria This is to remove moisture that is absorbed.
그러면 상기 사용 용도에 맞도록 수분이 완전히 제거된 ＢＭ균을 함유한 펠릿 형태의 최종 고형체의 제조를 완료할 수 있게 된다. 단, 상기 ＢＭ균을 함유한 펠릿 형태의 최종 고형체는 사용시 본래의 기능을 제대로 발휘할 수 있도록 그 속에 함유된 ＢＭ균이 공기와 반응하지 못하도록 공기가 차단되게 밀봉된 상태로 보관해야 한다.
Thus, it is possible to complete the production of the final solid body in the form of pellets containing BM bacteria whose moisture has been completely removed to suit the intended use. However, the final solid body in the form of a pellet containing the BM microorganisms should be kept sealed so as to prevent air from reacting with the BM microorganisms contained in the final solid body in order to properly exhibit its original function.
이하 본 발명의 바람직한 제2실시예에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용방법을 단계적으로 상세하게 설명하면 다음과 같다. Hereinafter, a method for reusing coal ash using coal fines according to a second preferred embodiment of the present invention will be described in detail.
먼저, 제1단계는, 화력발전소에서 발생하는 분말 상태의 석탄재를 액상의 ＢＭ균에 함침시켜 ＢＭ균을 함유한 분말체를 형성하는 단계이다. First, the first step is a step of impregnating BM bacteria in a liquid state with powdery coal ash generated in a thermal power plant to form a powder containing BM bacteria.
제1단계는 제1실시예의 제2단계와 동일하다. 다만, 제1실시예와 달리 펠릭 형태의 중간 고형체 아닌 분말 상태의 석탄재를 액상의 ＢＭ균에 함침시키는 것만 다르다. The first step is the same as the second step of the first embodiment. Unlike the first embodiment, however, it differs from the first embodiment only in that impregnated BM liquid in liquid form is impregnated with pulverized coal ash in the form of powder, which is not a middle solid.
단, 분말 상태의 석탄재에 ＢＭ균이 원활하게 함유되도록 액상의 ＢＭ균에 12~36시간 동안 함침시켜야 한다. 그리고 석탄재는 함침 후에는 다시 분말 상태가 되도록 12~36시간 동안 자연 건조하는 것이 바람직하다. However, it should be impregnated into liquid BM bacteria for 12 to 36 hours so that the BM bacteria are smoothly contained in the powdery coal ash. It is preferable that the coal ash is naturally dried for 12 to 36 hours so that it becomes powdery again after impregnation.
이때도 석탄재가 화력발전소에서 배출되어 바닷물 속에 투입된 상태에서 건조되어 사용되는 경우에는 중금속 등의 오염물질이 자연스럽게 제거됨에 따라 오염물질을 제거하는 전처리 단계가 필요하지 않지만, 석탄재가 화력발전소에서 바로 배출된 상태인 경우에는 중금속 등의 오염물질이 포함된 상태임에 따라 오염물질을 제거하는 전처리 단계를 제1단계에서 앞서서 선행하는 것이 바람직하다. 중금속 등의 오염물질을 제거하는 방법은 이미 잘 알려진 기술로서 이에 대한 설명은 생략한다. In this case, when the coal ash is discharged from the thermal power plant and dried and used in the seawater, there is no need of a pretreatment step for removing contaminants as the heavy metals and the like are naturally removed, but coal ash is discharged directly from the thermal power plant It is preferable that the pretreatment step for removing the contaminants is preceded by the preceding step in the first step since the contaminants such as heavy metals are contained. The method for removing contaminants such as heavy metals is well known and will not be described here.
다음으로, 제2단계는, 제1단계에서 ＢＭ균이 함유된 분말체에 결합제를 첨가하여 일정 메쉬 크기를 가지는 펠릿 형태의 중간 고형체를 형성하는 단계로서, 제1실시예의 제1단계와 동일하다. Next, in the second step, a binder is added to the powder containing BM bacteria in the first step to form a pellet-shaped intermediate solid having a predetermined mesh size, which is the same as the first step of the first embodiment Do.
마지막으로, 제3단계는, ＢＭ균을 함유한 펠릿 형태의 최종 고형체를 형성하여 가공을 완료하는 단계이다. 즉, 제1실시예의 제3단계와 동일하게 제2단계에서 형성된 최종 고형체를 12~36시간 동안 자연 건조시켜 최종 고형체를 형성하는 공정이다. Finally, the third step is a step of forming a final solid body in the form of pellets containing BM bacteria to complete processing. That is, as in the third step of the first embodiment, the final solid body formed in the second step is naturally dried for 12 to 36 hours to form a final solid body.
그러면 상기 사용 용도에 맞도록 수분이 완전히 제거된 ＢＭ균을 함유한 펠릿 형태의 최종 고형체의 제조를 완료할 수 있게 된다. 단, 상기 ＢＭ균을 함유한 펠릿 형태의 최종 고형체는 사용시 본래의 기능을 제대로 발휘할 수 있도록 그 속에 함유된 ＢＭ균이 공기와 반응하지 못하도록 공기가 차단되게 밀봉된 상태로 보관해야 한다.
Thus, it is possible to complete the production of the final solid body in the form of pellets containing BM bacteria whose moisture has been completely removed to suit the intended use. However, the final solid body in the form of a pellet containing the BM microorganisms should be kept sealed so as to prevent air from reacting with the BM microorganisms contained in the final solid body in order to properly exhibit its original function.
이상과 같이 본 발명에 따른 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법은, 화력발전소에서 발생하는 석탄재를 ＢＭ균과 결합시켜 펠릿 형태로 가공하여 수처리장치의 여재, 양식장 및 양어장의 수질개선제, 음식물쓰레기의 분해촉진제 및 악취제거제, 토양의 산성화방지제 및 비료대체제, 물밑의 오염원제거제 등으로 재사용할 수 있는 고형체를 제공함으로써 석탄재의 매립으로 인한 문제점들을 일거에 해소할 수 있게 된다.
As described above, the processing method for reusing coal ash using coal fired power plant according to the present invention is characterized in that the coal ash generated in a thermal power plant is combined with BM bacteria and processed into pellets to improve water quality of the water treatment apparatus, It is possible to solve the problems caused by landfill of coal ash by providing a solid body which can be reused as a decomposition promoter and a malodor removing agent for food waste, an acidification inhibitor for soil, a substitute for fertilizer and a pollutant remover for underwater.
상기한 실시예는 예시적인 것에 불과한 것으로, 당해 기술분야에 대한 통상의 지식을 가진 자라면 이로부터 다양하게 변형된 다른 실시예가 가능하다. The above-described embodiments are merely illustrative, and various modifications may be made by those skilled in the art without departing from the scope of the present invention.
따라서 본 발명의 진정한 기술적 보호범위에는 하기의 특허청구범위에 기재된 발명의 기술적 사상에 의해 상기의 실시예뿐만 아니라 다양하게 변형된 다른 실시예가 포함되어야 한다. Therefore, the true technical protection scope of the present invention should include not only the above embodiments but also various other modified embodiments according to the technical idea of the invention described in the following claims.
Claims (12)
상기 초기 고형체에 액상의 ＢＭ균이 원활하게 함유되도록 상기 초기 고형체를 상기 액상의 ＢＭ균에 12~36시간 동안 완전히 잠긴 상태로 함침시켜 ＢＭ균을 함유한 중간 고형체를 형성하는 제2단계; 및
상기 중간 고형체를 12~36시간 동안 자연 건조시켜 상기 중간 고형체를 상기 액상의 ＢＭ균에 함침시키는 과정에서 흡수한 수분이 제거된 최종 고형체를 형성하여 완료하는 제3단계;를 포함하여 구성되되,
상기 최종 고형체는,
사용 용도에 따라 상기 제1단계에서 펠릿 형태의 메쉬 크기가 결정되는 것으로, 수처리장치의 여재로 사용되는 경우에는 4~9 메쉬 크기로 구성되고 양식장 및 양어장의 수질개선제로 사용되는 경우에는 5~10 메쉬 크기로 구성되며 음식물쓰레기의 분해촉진제 및 악취제거제로 사용되는 경우에는 5~10 메쉬 크기로 구성되고 농토의 산성화방지제 및 비료대체제로 사용되는 경우에는 10~15메쉬 크기로 구성되며 물밑 오염원의 제거제로 사용되는 경우에는 5~10 메쉬 크기로 구성되고,
상기 제1단계 이전에는,
상기 석탄재의 오염상태에 따라 상기 석탄재에 포함되어 있는 중금속을 포함한 오염물질을 제거하는 전처리단계를 더 포함하는 구성되는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법. A first step of forming a pellet-shaped initial solid material having a predetermined mesh size by adding a binder to powdery coal material generated from a thermal power plant, and then drying the solid material for a predetermined period of time;
A second step of immersing the initial solid body in the liquid BM microorganism in a completely submerged state for 12 to 36 hours so as to smoothly contain the liquid BM microorganism in the initial solid body to form an intermediate solid body containing the BM microorganism ; And
And a third step of naturally drying the intermediate solid body for 12 to 36 hours to form a final solid body from which the absorbed moisture has been removed in the process of impregnating the intermediate solid body with the BM bacteria in the liquid phase, However,
The final solids,
The mesh size of the pellet is determined in the first step according to the purpose of use. When used as a filter material of the water treatment apparatus, the mesh size is 4 to 9 mesh. When used as a water quality improving agent for aquaculture farm and fish farm, It is composed of 5 ~ 10 mesh size when it is used as a disintegration promoter and odor remover for food waste. It is composed of 10 ~ 15 mesh size when it is used as an acidifying agent and fertilizer substitute for agricultural land. , It is composed of 5 to 10 mesh size,
Prior to the first step,
Further comprising a pretreatment step of removing contaminants including heavy metals contained in the coal ash according to the contamination state of the coal ash.
상기 제1단계는,
상기 석탄재 60~70중량%와, 석회 모르타르로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출 성형한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법. The method according to claim 1,
In the first step,
Wherein 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of lime mortar are mixed and extruded in the form of pellets, followed by naturally drying for 12 to 36 hours to form the initial solid body Processing Method for Reusing coal ash using thermal power plant.
상기 제1단계는,
상기 석탄재 60~70중량%와, 시멘트 모르타르로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출 성형한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법. The method according to claim 1,
In the first step,
Wherein 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of cement mortar are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid body Processing Method for Reusing coal ash using thermal power plant.
상기 제1단계는,
상기 석탄재 60~70중량%와, 전분 수용액으로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출 성형한 후 20~40℃에서 12~36시간 동안 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법. The method according to claim 1,
In the first step,
60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of an aqueous starch solution are mixed and extruded into pellets and dried at 20 to 40 ° C for 12 to 36 hours to form the initial solid body Processing Method for Reuse of Coal Ash for Thermal Power Plant Using BM Microorganism.
상기 제1단계는,
상기 석탄재 60~70중량%와, 규산나트륨 수용액으로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법. The method according to claim 1,
In the first step,
Wherein 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of an aqueous solution of sodium silicate are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid body Processing Method for Reusing coal ash using thermal power plant.
상기 제1단계는,
상기 석탄재 60~70중량%와, 이온교환수지로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법.The method according to claim 1,
In the first step,
Wherein 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of an ion exchange resin are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid body. Processing Method for Reusing coal ash using thermal power plant.
상기 제1단계는,
상기 석탄재 60~70중량%와, 아교로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법.The method according to claim 1,
In the first step,
60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder as a glue are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid body Processing method for reuse of coal ash in thermal power plant.
상기 제1단계는,
상기 석탄재 60~70중량%와, 벤토나이트와 당밀로 이루어진 결합제 30~40중량%를 혼합하여 펠릿 형태로 압출한 후 12~36시간 동안 자연 건조시켜 상기 초기 고형체를 형성하는 것을 특징으로 하는 ＢＭ균을 이용한 화력발전소 석탄재의 재사용을 위한 가공방법.The method according to claim 1,
In the first step,
Wherein 60 to 70% by weight of the coal ash and 30 to 40% by weight of a binder composed of bentonite and molasses are mixed and extruded into pellets, followed by natural drying for 12 to 36 hours to form the initial solid body. Processing Method for Reusing coal ash using thermal power plant.