KR101497924B1 - Composition for rainwater permeablel upper slab of rainwater storage tank, rainwater storage tank and conctruction method of the rainwater storage tank using the composition - Google Patents

Abstract

The present invention relates to a composition for a rainwater permeable-type upper slab of a rainwater storage tank, the rainwater storage tank using the same, and a construction method thereof. The rainwater storage tank includes: a rainwater permeable-type upper slab; a lower slab for storing the rainwater in the rainwater storage tank by forming the bottom surface of the rainwater storage tank so that the rainwater does not leak from the lower portion; a post fixed to the lower slab to support the rainwater permeable-type upper slab; and a lateral slab forming a wall along an outer edge of the lower slab to connect the lower slab and the rainwater permeable-type upper slab. First protrusions provided on four corners of the bottom surface of the rainwater permeable-type upper slab are inserted in the insertion groove formed on the upper portion of the post, and four first protrusions are inserted in the insertion groove formed on the upper portion of the post, so that four rainwater permeable-type upper slabs are engaged to one post. Therefore, the present invention solves a problem of an existing rainwater storage tank to be constructed on the spot, and since the post, the upper slabs and the lateral slabs are manufactured at a factory in a precast manner, and then are assembled on the spot, it is possible to secure the sufficient inner space. Also, the prevention invention reduces the number of parts, facilitates the assembly, reduces construction periods, and saves construction costs.

Description

우수저류조의 우수 침투형 상부 슬래브용 조성물, 상기 우수 침투형 상부 슬래브용 조성물을 이용한 우수저류조 및 상기 우수저류조의 시공방법{Composition for rainwater permeablel upper slab of rainwater storage tank, rainwater storage tank and conctruction method of the rainwater storage tank using the composition}Technical Field [0001] The present invention relates to a composition for an excellent permeable upper slab of an excellent storages tank, a superior storages tank using the composition for the storm permeable upper slab, and a method of constructing the storm reservoir of a rainwater storage tank rainwater storage tank using the composition}

본 발명은 우수 침투형 상부 슬래브용 조성물, 이를 이용한 프리캐스트 콘크리트(Precast Concrete; PC) 우수저류조 및 그 시공방법에 관한 것으로, 더욱 상세하게는 현장에서 타설되는 기존 우수저류조의 문제점을 해결하기 위한 것으로 기둥, 상부 슬래브 및 측벽 슬래브를 프리캐스트(precast) 방식으로 공장제품으로 제작하고 현장에서 조립함으로써 충분한 내부공간을 확보할 수 있고, 부품의 개수가 적고 조립이 용이하며, 시공이 간단하여 시공 기간이 적게 걸리고 시공 비용을 절약할 수 있는 우수저류조의 우수 침투형 상부 슬래브용 조성물, 상기 우수 침투형 상부 슬래브용 조성물을 이용한 우수저류조 및 상기 우수저류조의 시공방법에 관한 것이다.
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a composition for an excellent permeable upper slab, a precast concrete (PC) stormwater storage tank using the same, and a method of constructing the same. More particularly, It is possible to secure a sufficient internal space by assembling the columns, the upper slab and the slab of the side wall in a precast system as a factory product and assemble in the field, and the number of parts is small, the assembly is easy, The present invention relates to a composition for an excellent penetration type upper slab of an excellent storeroom which can reduce the construction cost and can reduce the construction cost, and a method of constructing the storeroom and the storeroom using the composition for the superior penetration type upper slab.

최근 지구온난화, 엘리뇨 및 라니냐 등 기후변화 영향으로 인해 강우의 지속시간은 짧아진 반면, 매우 높은 강도를 가진 강우 발생으로 인해 홍수 피해가 빈번하게 발생하고 있다. 특히 우리나라는 지형적 특성으로 인한 집중호우, 태풍과 같은 이상 강우로 인한 홍수피해의 발생이 매년 나타나고 있으며, 홍수 피해의 빈도와 강도는 증가하고 있는 추세이다. 또한 지역에 따라 가뭄 피해도 잦은 실정이다.Recently, the duration of rainfall has been shortened due to the effects of climate change such as global warming, El Niño and La Niña, but flood damage has occurred frequently due to extremely high intensity rainfall. In particular, the occurrence of flood damage caused by abnormal rainfall such as heavy rainfall and typhoon due to geographical characteristics is appeared every year in Korea, and frequency and intensity of flood damage are increasing. Drought damage is also frequent depending on the region.

빗물을 일단 저류조에 저류하여 하천으로의 유출량을 조정하는 기술이 개발되고 있다. 종래에는 현장에서 하부 슬래브를 타설하고, 측벽 슬래브를 타설한 후, 상부 슬래브를 타설하는 과정을 거쳐 우수저류조를 제작하였다. 이와 같이 현장에서 타설되는 기존 우수저류조는 시공 기간이 오래 걸리고, 시공 비용이 증가하는 등의 문제점이 있었다. Techniques for reserving rainwater once in the reservoir and adjusting the flow rate to the stream are being developed. Conventionally, an underground slab is laid on a site, a side wall slab is laid, and an upper slab is laid. In this way, the conventional stormwater pond installed in the field has a problem that the construction period is long and the construction cost is increased.

이러한 종래의 문제점를 개선하기 위한 우수저류조의 제작기술중 하나가 일본 공개특허공보 평6-27299에 개시되어 있다. 일본 공개특허공보 평6-27299에 개시된 발명은 블록 단체의 경량화를 위하여 저면 저면판부의 네 모서리 기둥의 상단 부분에 수평 들보가 설치되고, 전후좌우의 각 수평들보 사이에 상면 개구부를 형성한 본체부용 블록과, 측면판부의 양측 가장자리 부분에 상면판부와 저면판부의 단부 부분을 연결하는 슬리브 벽부를 설치한 자 형상의 주변부용 블록과, 측면판부의 하단 부분에 저면판부를 연결 설치하고 상단 부분에 상면판부를 연결 설치하는 모퉁이 벽부용 블록으로 구성되고, 본체부용 블록군의 측면 개구부가 주변부용 블록으로 폐쇄되며, 수평 들보에 탑재된 뚜껑판으로 본체부용 블록의 상면 개구부가 폐쇄된다. 그러나, 이러한 우수저류조는 각각의 블록 중량을 경량화하여 운반이나 취급이 용이한 이점은 있으나, 각각의 부분이 분리되어 있기 때문에 각 부분을 조립하여 설치하는데 많은 노동력과 조립 시간이 요구되어 시공 비용이 증가한다는 문제점이 있다.One of techniques for fabricating a storage tank for improving such conventional problems is disclosed in Japanese Patent Application Laid-Open No. 6-27299. Japanese Unexamined Patent Application Publication No. 6-27299 discloses a structure in which a horizontal beam is provided at an upper end portion of four corner columns of a bottom surface plate portion for weight reduction of a block unit and an upper surface opening is formed between front, A block having a shape and a peripheral wall portion provided with a sleeve wall portion for connecting the upper plate portion and the end portion of the bottom plate portion to both side edge portions of the side plate portion and a bottom plate portion connected to the lower end portion of the side plate portion, And the side opening of the block group for the main body is closed by the peripheral block, and the upper surface opening of the block for the main body is closed by the cover plate mounted on the horizontal beam. However, such an excellent storage tank is advantageous in that the weight of each block is lightened, thereby facilitating transportation and handling. However, since each part is separated, labor and assembly time are required to assemble and install each part, .

또한, 대한민국 특허등록번호 제10-0582121에서는 육면체의 측면에 각각 개구부가 형성되도록 상면판과 저면판의 각 모서리에 기둥이 형성되고, 각 기둥의 상부 및 하부에 다수의 너트 안치홈이 형성되고, 상면판의 적어도 하나의 변에는 단차부가 형성되고, 저면판에는 기초면과 일체로 거동하도록 결합부가 형성되는 저류블록; 및 사각형의 판형상을 갖고 끝단이 상기 저류블록의 상면판 단차부에 안착되어 상기 저류블록의 상면판과 동일평면을 이루는 상면블록;을 포함하고, 상기 저류블록은 다수개가 일직선상으로 반복적으로 배열되고, 상기 상면블록은 다수개가 일직선상의 저류블록들 사이에 결합되어 저류공간을 형성하는 우수저류조를 제시하였다. 대한민국 특허등록번호 10-0582121에 제시된 우수저류조는 기본구조로서 육면체형상을 갖기 때문에 우수저류조로 사용하기 위해서는 완성품을 현장으로 이동할 수 없어 현장에서 직접 우수처리조를 제작해야 단점과 함께 우수저류조의 설치를 위해서는 대형 기중기 등이 필요한 문제와 함께 설치시 미세 조절에서도 거대한 무게로 인하여 조절이 어려운 단점이 있다.
In Korean Patent Registration No. 10-0582121, pillars are formed on the respective corners of the upper plate and the lower plate so that openings are respectively formed on the side surfaces of the hexahedron, and a plurality of nut housing grooves are formed in the upper and lower portions of the pillars, A bottom block having a step formed on at least one side of the top plate, and a bottom block having a coupling part formed to be integral with the base; And a top block having a rectangular plate shape and having an end mounted on the top plate stepped portion of the storage block and coplanar with the top plate of the storage block, wherein a plurality of the storage blocks are arranged in a straight line And the upper surface block is coupled between a plurality of straight block storage blocks to form a retention space. Since the superior reservoir shown in Korean Patent Registration No. 10-0582121 has a hexahedral shape as a basic structure, it is not possible to move the finished product to the site for use as an excellent reservoir, so it is necessary to manufacture a superior treatment tank directly on site, In addition, there is a disadvantage that it is difficult to control due to the huge weight in the fine adjustment at the installation together with the problem that the large crane is necessary.

일본 공개특허번호 평6-27299Japanese Patent Laid-Open No. 6-27299 대한민국 특허등록번호 10-0582121Korea Patent Registration No. 10-0582121

본 발명이 해결하고자 하는 과제는 현장에서 타설되는 기존 우수저류조의 문제점을 해결하기 위한 것으로 기둥, 상부 슬래브 및 측벽 슬래브를 프리캐스트(precast) 방식으로 공장제품으로 제작하고 현장에서 조립함으로써 충분한 내부공간을 확보할 수 있고, 부품의 개수가 적고 조립이 용이하며, 시공이 간단하여 시공 기간이 적게 걸리고 시공 비용을 절약할 수 있는 우수 침투형 프리캐스트 콘크리트 우수저류조를 제공함에 있다. A problem to be solved by the present invention is to solve the problem of existing storm reservoir which is installed in the field, and it is possible to manufacture a column, an upper slab and a side wall slab by a precast method, The present invention is to provide an excellent stormwater precast concrete excellent stor- age tank which can be secured with a small number of parts, is easy to assemble, is simple in construction, takes a short construction period and can save construction cost.

본 발명이 해결하고자 하는 과제는 투수성, 강도, 내구성 등이 우수한 우수 침투형 상부 슬래브용 조성물에 의해 콘크리트 자체에서의 누수와 균열 등을 방지할 수 있는 우수 침투형 상부 슬래브용 조성물을 제공함에 있다. A problem to be solved by the present invention is to provide a composition for an excellent permeable upper slab capable of preventing water leakage and cracking in a concrete itself by a composition for an excellent permeable upper slab excellent in permeability, strength, durability and the like .

또한, 본 발명이 해결하고자 하는 과제는 프리스트레스력을 이용하여 현장에서 우수저류조를 조립하는데 소요되는 시공시간을 절약함과 동시에 연결부위를 최소화함으로써 누수에 대한 문제점을 해결할 수 있을 뿐만 아니라, 투수성, 강도, 내구성 등이 우수한 우수 침투형 상부 슬래브용 조성물에 의해 콘크리트 자체에서의 누수와 균열 등을 방지할 수 있는 프리캐스트 콘크리트 우수저류조의 시공방법을 제공함에 있다.
It is another object of the present invention to solve the problems of leakage by minimizing the connection time and the construction time required for assembling the storerooms in the field by using the prestress force, Which is excellent in strength, durability and the like, can be prevented from leaking and cracking in the concrete itself by the composition for an excellent permeable upper slab.

본 발명은, 우수 침투형 상부 슬래브와, 우수저류조의 바닥면을 형성하면서 우수가 하부로 빠져나가지 못하게 하여 우수를 우수저류조 내에 가두기 위한 하부 슬래브와, 상기 하부 슬래브와 결합되어 고정되어 있고 상기 우수 침투형 상부 슬래브를 지지하는 기둥과, 상기 하부 슬래브의 외곽 테두리를 따라 벽체를 형성하여 상기 하부 슬래브와 상기 우수 침투형 상부 슬래브를 연결하는 측벽 슬래브를 포함하며, 상기 우수 침투형 상부 슬래브 하면의 네 모퉁이에 구비된 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈으로 삽입되어 고정되어 있고, 상기 기둥 상부에 구비된 삽입홈에는 4개의 제1 돌출부가 삽입되고, 4개의 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈에 삽입됨에 따라 4개의 우수 침투형 상부 슬래브가 하나의 기둥에 결합되는 형태를 갖고, 상기 우수 침투형 상부 슬래브의 네 모퉁이에 제1 요홈부가 구비되어 있고, 상기 제1 요홈부로 둘러싸인 영역에 몰탈이 주입되어 서로 이웃하는 우수 침투형 상부 슬래브 및 상기 기둥이 결합되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조를 제공한다. The present invention relates to an excellent permeable upper slab, a lower slab for forming a bottom surface of the storm reservoir and preventing the storm from escaping to the lower part to confine the stormwater into the stormwater storage tank, And a sidewall slab connecting the lower slab and the superior penetrating upper slab by forming a wall along an outer rim of the lower slab, wherein four corners of the bottom of the superior penetrating upper slab The first protrusions provided in the upper portion of the column are inserted and fixed, the four first protrusions are inserted into the insertion groove provided in the upper portion of the column, and the four first protrusions are inserted into the upper portion of the column As a result of being inserted into the provided insertion groove, four excellent penetration type upper slabs are coupled to one column And a mortar is injected into a region surrounded by the first recessed portion so that neighboring storm permeable upper slabs and the pillars are coupled to each other. To provide an excellent reservoir of precast concrete.

상기 제1 요홈부는 상부에서 하부로 향하는 방향을 따라 상기 우수 침투형 상부 슬래브의 상면부터 상기 제1 돌출부의 저면까지 구비되어 있을 수 있다.The first recess may be provided from the upper surface of the superior permeable upper slab to the lower surface of the first protruding portion along a direction from the upper portion to the lower portion.

상기 우수 침투형 상부 슬래브는 제1 상부 슬래브와 제2 상부 슬래브를 포함할 수 있고, 상기 우수 침투형 상부 슬래브의 상면에는 제1 상부 슬래브와 제1 상부 슬래브 사이를 움직이지 않도록 결합하거나 제1 상부 슬래브와 제2 상부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비될 수 있으며, 제1 상부 슬래브와 제1 상부 슬래브가 서로 이웃하게 설치되고 제1 상부 슬래브와 제2 상부 슬래브가 서로 이웃하게 설치된 상태에서 제1 결합수단에 볼트, 강선, 강봉 또는 강관이 삽입되어 제1 상부 슬래브와 제1 상부 슬래브 사이가 결합되고 제1 상부 슬래브와 제2 상부 슬래브 사이가 결합되어 있을 수 있다. The superior permeable upper slab may include a first upper slab and a second upper slab, wherein the upper surface of the superior permeable upper slab is movably coupled between the first upper slab and the first upper slab, A first upper slab and a first upper slab are disposed adjacent to each other and a first upper slab and a second upper slab are adjacent to each other A bolt, a steel wire, a steel bar, or a steel pipe may be inserted into the first joining means in the installed state so that the first upper slab and the first upper slab are engaged and the first upper slab and the second upper slab are engaged.

상기 측벽 슬래브의 상부에서 돌출된 철근과 상기 우수 침투형 상부 슬래브에서 돌출된 철근이 서로 결합되어 있고 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브 사이에 결합된 철근에 몰탈이 채워져서 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브가 결합되어 있을 수 있다.Wherein the reinforcing bars protruding from the upper portion of the side wall slab and the reinforcing bars projecting from the superior penetrating upper slab are coupled to each other and the reinforcing bars coupled between the side wall slab and the superior penetrating upper slab are filled with mortar, An excellent permeable top slab may be combined.

상기 하부 슬래브 상면의 네 모퉁이에 구비된 제2 돌출부가 기둥의 지지대 하부에 구비된 삽입홈으로 삽입되어 고정되어 있을 수 있고, 상기 기둥의 지지대 하부에 구비된 삽입홈에는 4개의 제2 돌출부가 삽입되고, 4개의 제2 돌출부가 상기 기둥의 지지대 하부에 구비된 삽입홈에 삽입됨에 따라 4개의 하부 슬래브가 하나의 기둥에 결합되는 형태를 가질 수 있다.A second protrusion provided at four corners of the upper slab may be inserted and fixed in an insertion groove provided in a lower portion of the support of the column, and four second protrusions are inserted into the insertion groove provided under the support of the column And four fourth slabs are coupled to one column as four second projections are inserted into insertion grooves provided under the supports of the columns.

상기 기둥의 하부에 돌출된 철근과 상기 하부 슬래브에 돌출된 철근이 서로 결합되어 있을 수 있고, 상기 기둥과 상기 하부 슬래브 사이에 결합된 철근에 몰탈이 채워져서 상기 기둥과 상기 하부 슬래브가 결합되어 있을 수 있다.The reinforcing bars protruding from the lower portion of the column and the reinforcing bars projecting from the lower slab may be coupled to each other and the reinforcing bars coupled between the column and the lower slab may be filled with mortar so that the column and the lower slab are coupled .

상기 하부 슬래브는 우수저류조의 하부 중앙부에 설치되는 제1 하부 슬래브와 우수저류조의 하부 외측부에 설치되는 제2 하부 슬래브를 포함하고, Wherein the lower slab includes a first lower slab installed at a lower central portion of the upper storage tank and a second lower slab installed at a lower outer side of the upper storage tank,

상기 하부 슬래브의 상면에는 제1 하부 슬래브와 제1 하부 슬래브 사이를 움직이지 않도록 결합하거나 제1 하부 슬래브와 제2 하부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비될 수 있으며, 제1 하부 슬래브와 제1 하부 슬래브가 서로 이웃하게 설치되고 제1 하부 슬래브와 제2 하부 슬래브가 서로 이웃하게 설치된 상태에서 제2 결합수단에 볼트, 강선, 강봉 또는 강관이 삽입되어 제1 하부 슬래브와 제1 하부 슬래브 사이가 결합되고 제1 하부 슬래브와 제2 하부 슬래브 사이가 결합되어 있을 수 있다.The top surface of the lower slab may be provided with an engaging means for engaging the first lower slab and the first lower slab so as not to move or for engaging the first lower slab and the second lower slab so as not to move, A bolt, a steel wire, a steel bar or a steel pipe is inserted into the second joining means in a state where the slab and the first lower slab are disposed adjacent to each other and the first and second lower slabs are adjacent to each other, The lower slab may be coupled and the first lower slab and the second lower slab may be coupled.

상기 측벽 슬래브 하부의 일측에는 돌출된 받침대가 구비될 수 있고, 상기 측벽 슬래브의 받침대에 구비된 철근과 상기 하부 슬래브에 구비된 철근이 서로 결합되어 있고 상기 받침대와 하부 슬래브 사이에 결합된 철근에 몰탈이 채워져서 상기 측벽 슬래브와 상기 하부 슬래브가 결합되어 있을 수 있다. The reinforcing bar provided on the pedestal of the side wall slab and the reinforcing bars provided on the lower slab are coupled to each other, and the reinforcing bar coupled between the pedestal and the lower slab is provided with a mortar So that the side wall slab and the lower slab are coupled.

상기 측벽 슬래브의 측면에는 측벽 슬래브와 측벽 슬래브 사이를 움직이지 않도록 결합시키기 위한 제3 결합수단이 구비될 수 있으며, 측벽 슬래브와 측벽 슬래브가 서로 이웃하게 설치된 상태에서 제3 결합수단에 볼트, 강선, 강봉 또는 강관이 삽입되어 측벽 슬래브와 측벽 슬래브 사이가 결합되어 있을 수 있다.The side wall slab may include a third coupling means for coupling the side wall slab and the side wall slab so as not to move. When the side wall slab and the side wall slab are adjacent to each other, the bolts, A steel bar or a steel pipe may be inserted so that the side wall slab and the side wall slab are engaged.

또한, 본 발명은, 상기 프리캐스트 콘크리트 우수저류조의 우수 침투형 상부 슬래브를 형성하기 위한 조성물로서, 시멘트계 결합재 3∼40중량%, 보투수성 결합재 0.01∼15중량%, 잔골재 45∼90중량%, 굵은골재 5∼40중량% 및 물 0.1∼15중량%를 포함하며, 상기 보투수성 결합재는 폴리메타크릴산 2-히드록시에틸 60∼99중량%, 아크릴아미드 0.01∼25중량%, 폴리아크릴산나트륨 0.01∼25중량% 및 아세틸셀롤로오스 0.01∼15중량%를 포함하는 것을 특징으로 하는 우수 침투형 상부 슬래브용 조성물을 제공한다. The present invention also provides a composition for forming an excellent permeable upper slab of a precast concrete excellent storage tank, comprising 3 to 40% by weight of a cementitious binder, 0.01 to 15% by weight of a water-repellent binder, 45 to 90% 5 to 40% by weight of coarse aggregate and 0.1 to 15% by weight of water, wherein the water-repellent binder comprises 60 to 99% by weight of 2-hydroxyethyl methacrylate, 0.01 to 25% by weight of acrylamide, 0.01 to 25% by weight, and acetylcellulose 0.01 to 15% by weight, based on the total weight of the composition.

상기 시멘트계 결합재는 보통 포틀랜드 시멘트 30∼90중량%, 석고 0.1∼20중량%, 알루미나시멘트 0.1∼20중량%, 플라이애쉬 1∼20중량%, 메타카올린 1∼20중량% 및 고로슬래그 5∼30중량%를 포함할 수 있다.The cementitious binder is usually composed of 30 to 90 wt% of Portland cement, 0.1 to 20 wt% of gypsum, 0.1 to 20 wt% of alumina cement, 1 to 20 wt% of fly ash, 1 to 20 wt% of meta kaolin, %. ≪ / RTI >

상기 시멘트계 결합재는 시트릭산 0.01∼5중량%를 더 포함할 수 있다.The cement based binder may further contain 0.01 to 5% by weight of citric acid.

상기 시멘트계 결합재는 칼슘포메이트 0.01∼5중량%를 더 포함할 수 있다.The cement based binder may further contain 0.01 to 5% by weight of calcium formate.

상기 보투수성 결합재는 에틸렌프로필렌 고무 0.01∼5중량%를 더 포함할 수 있다.The water-repellent binder may further include 0.01 to 5% by weight of ethylene propylene rubber.

상기 보투수성 결합재는 폴리부타디엔 고무 0.01∼5중량%를 더 포함할 수 있다.The water-repellent bonding material may further include 0.01 to 5% by weight of a polybutadiene rubber.

또한, 본 발명은, 상기 프리캐스트 콘크리트 우수저류조를 시공하기 위한 방법으로서, 프리캐스트 콘크리트 우수저류조를 설치할 하부 기초를 형성하기 위하여 골재를 포설하고 다짐한 후, 상부에 모래를 포설하고 다짐하여 하부 기초를 준비하는 단계와, 상기 하부 기초 상부에 린콘크리트를 타설하는 단계와, 상기 린콘크리트가 타설된 상부에 우수저류조의 바닥면을 형성하면서 우수가 하부로 빠져나가지 못하게 하여 우수를 우수저류조 내에 가두기 위한 하부 슬래브를 설치하거나 현장에서 몰탈을 타설하여 하부 슬래브를 형성하는 단계와, 우수 침투형 상부 슬래브를 지지하기 위한 기둥을 설치하고 상기 하부 슬래브와 결합하여 고정하는 단계와, 상기 하부 슬래브의 외곽 테두리를 따라 벽체를 형성하는 측벽 슬래브를 설치하는 단계 및 상기 측벽 슬래브와 상기 기둥 상부에 우수 침투형 상부 슬래브를 설치하는 단계를 포함하며, 상기 우수 침투형 상부 슬래브 하면의 네 모퉁이에 구비된 제1 돌출부를 상기 기둥 상부에 구비된 삽입홈으로 삽입하여 고정하고, 상기 기둥 상부에 구비된 삽입홈에 4개의 제1 돌출부를 삽입하며, 상기 우수 침투형 상부 슬래브의 네 모퉁이에 제1 요홈부가 구비되게 하고, 상기 제1 요홈부로 둘러싸인 영역에 몰탈을 주입하여 서로 이웃하는 우수 침투형 상부 슬래브 및 상기 기둥을 결합하며, 4개의 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈에 삽입됨에 따라 4개의 우수 침투형 상부 슬래브가 하나의 기둥에 결합되는 형태를 갖는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법을 제공한다. The present invention also relates to a method for constructing a pre-cast concrete excellent storage tank, comprising the steps of placing an aggregate in order to form a lower foundation to be installed in a pre-cast concrete storage tank, A step of pouring lean concrete on top of the lower basement, a step of forming a bottom surface of the storm reservoir at an upper portion in which the lean concrete is laid, a lower portion for trapping stormwater into the stormwater storage tank A step of forming a lower slab by installing a slab or placing a mortar in the site, installing a column for supporting the superior penetration type upper slab and fixing the lower slab in combination with the lower slab, Providing a side wall slab to form a wall; And a step of installing an excellent permeable upper slab on the wall slab and an upper portion of the column, wherein a first projection provided at four corners of the bottom of the superior permeable upper slab is inserted and fixed into an insertion groove provided in the upper portion of the column Four first protrusions are inserted into the inserting grooves formed in the upper portion of the column, the first recesses are provided at four corners of the superior penetrating type upper slab, and mortar is injected into the region surrounded by the first grooves, And the four excellent penetration type upper slabs are coupled to one column as the four first projections are inserted into the insertion grooves formed in the upper portion of the column, The present invention provides a method of constructing a pre-cast concrete excellent storeroom.

상기 제1 요홈부는 상부에서 하부로 향하는 방향을 따라 상기 우수 침투형 상부 슬래브의 상면부터 상기 제1 돌출부의 저면까지 구비되게 하는 것이 바람직하다.The first recess may be formed to extend from the upper surface of the storm permeable upper slab to the lower surface of the first protruding portion along the direction from the upper portion to the lower portion.

상기 우수 침투형 상부 슬래브는 제1 상부 슬래브와 제2 상부 슬래브를 포함할 수 있고, 상기 우수 침투형 상부 슬래브의 상면에 제1 상부 슬래브와 제1 상부 슬래브 사이를 움직이지 않도록 결합하거나 제1 상부 슬래브와 제2 상부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비되게 하며, 제1 상부 슬래브와 제1 상부 슬래브를 서로 이웃하게 설치하고 제1 상부 슬래브와 제2 상부 슬래브를 서로 이웃하게 설치한 상태에서 제1 결합수단에 볼트, 강선, 강봉 또는 강관을 삽입하여 제1 상부 슬래브와 제1 상부 슬래브 사이가 결합되고 제1 상부 슬래브와 제2 상부 슬래브 사이가 결합되게 할 수 있다.The storm permeable upper slab may comprise a first upper slab and a second upper slab and may be movably coupled between the first upper slab and the first upper slab on the upper surface of the storm permeable upper slab, A first upper slab and a first upper slab are disposed adjacent to each other and a first upper slab and a second upper slab are installed adjacent to each other, A bolt, a steel wire, a steel bar, or a steel pipe may be inserted into the first coupling means to couple between the first upper slab and the first upper slab, and between the first upper slab and the second upper slab.

상기 측벽 슬래브의 상부에서 돌출된 철근과 상기 우수 침투형 상부 슬래브에서 돌출된 철근을 서로 결합시키고, 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브 사이에 결합된 철근에 몰탈을 채워 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브를 결합시킬 수 있다.And a reinforcing bar protruding from an upper portion of the side wall slab and a reinforcing bar protruding from the superior penetrating upper slab are coupled to each other to fill the reinforcing bars coupled between the side wall slab and the superior penetrating upper slab, The permeable top slab can be joined.

상기 하부 슬래브 상면의 네 모퉁이에 제2 돌출부가 구비되게 하고, 상기 제2 돌출부를 기둥의 지지대 하부에 구비된 삽입홈으로 삽입하여 고정하고, 상기 기둥의 지지대 하부에 구비된 삽입홈에 4개의 제2 돌출부를 삽입하며, 4개의 제2 돌출부가 상기 기둥의 지지대 하부에 구비된 삽입홈에 삽입됨에 따라 4개의 하부 슬래브가 하나의 기둥에 결합되는 형태를 가질 수 있다.A second projection is provided at four corners of the upper surface of the lower slab, and the second projection is inserted and fixed in an insertion groove provided in a lower portion of the support of the column, Two protrusions are inserted and four fourth protrusions are inserted into insertion grooves provided under the support of the column so that the four lower slabs are coupled to one column.

상기 기둥의 하부에 돌출된 철근과 상기 하부 슬래브에 돌출된 철근을 서로 결합시키고, 상기 기둥과 상기 하부 슬래브 사이에 결합된 철근에 몰탈을 채워 상기 기둥과 상기 하부 슬래브를 결합시킬 수 있다.The column and the lower slab may be coupled by bonding a reinforcing bar protruding from a lower portion of the column and a reinforcing bar protruding from the lower slab to each other and filling the reinforcing bars coupled between the column and the lower slab with mortar.

상기 하부 슬래브는 우수저류조의 하부 중앙부에 설치되는 제1 하부 슬래브와 우수저류조의 하부 외측부에 설치되는 제2 하부 슬래브를 포함할 수 있고, 상기 하부 슬래브의 상면에 제1 하부 슬래브와 제1 하부 슬래브 사이를 움직이지 않도록 결합하거나 제1 하부 슬래브와 제2 하부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비되게 할 수 있으며, 제1 하부 슬래브와 제1 하부 슬래브를 서로 이웃하게 설치하고 제1 하부 슬래브와 제2 하부 슬래브를 서로 이웃하게 설치한 상태에서 제2 결합수단에 볼트, 강선, 강봉 또는 강관을 삽입하여 제1 하부 슬래브와 제1 하부 슬래브 사이가 결합되게 하고 제1 하부 슬래브와 제2 하부 슬래브 사이가 결합되게 할 수 있다.The lower slab may include a first lower slab installed at a lower central portion of the upper storage vessel and a second lower slab installed at a lower outer portion of the upper storage vessel. The first lower slab and the first lower slab, And a coupling means for coupling the first and second lower slabs so as not to move between the first and second lower slabs may be provided, and the first and second lower slabs may be disposed adjacent to each other, A bolt, a steel wire, a steel bar or a steel pipe is inserted into the second joining means in a state in which the lower slab and the second lower slab are disposed adjacent to each other so that the first lower slab and the first lower slab are engaged, 2 can be joined between the lower slabs.

상기 측벽 슬래브 하부의 일측으로 돌출된 받침대가 구비되게 하고, 상기 측벽 슬래브의 받침대에 구비된 철근과 상기 하부 슬래브에 구비된 철근을 서로 결합시키고, 상기 받침대와 하부 슬래브 사이에 결합된 철근에 몰탈을 채워 상기 측벽 슬래브와 상기 하부 슬래브를 결합시킬 수 있다.And a reinforcing bar provided on a bottom of the side wall slab and a reinforcing bar provided on the lower slab are coupled to each other, And the side wall slab and the lower slab can be joined together.

상기 측벽 슬래브의 측면에 측벽 슬래브와 측벽 슬래브 사이를 움직이지 않도록 결합시키기 위한 제3 결합수단이 구비되게 하고, 측벽 슬래브와 측벽 슬래브를 서로 이웃하게 설치한 상태에서 제3 결합수단에 볼트, 강선, 강봉 또는 강관을 삽입하여 측벽 슬래브와 측벽 슬래브 사이를 결합시킬 수 있다.
And a third coupling means for coupling the side wall slab and the side wall slab so as not to move between the side wall slab and the side wall slab is provided on the side surface of the side wall slab. In the state where the side wall slab and the side wall slab are adjacent to each other, A steel rod or a steel pipe may be inserted to join the side wall slab and the side wall slab.

본 발명의 프리캐스트 콘크리트 우수저류조에 의하면, 현장에서 타설되는 기존 우수저류조의 문제점을 해결할 수 있고, 기둥, 상부 슬래브 및 측벽 슬래브를 프리캐스트(precast) 방식으로 공장제품으로 제작하고 현장에서 조립함으로써 충분한 내부공간을 확보할 수 있으며, 부품의 개수가 적고 조립이 용이하며, 시공이 간단하여 시공 기간이 적게 걸리고 시공 비용을 절약할 수 있다.According to the precast concrete stormwater storage tank of the present invention, it is possible to solve the problems of the existing stormwater storage tank installed in the field, and to manufacture the column, the upper slab, and the side wall slab precast The internal space can be secured, the number of parts is small, the assembly is easy, the construction is simple, the construction time is short, and the construction cost can be saved.

본 발명의 우수 침투형 상부 슬래브용 조성물에 의하면, 투수성, 강도, 내구성 등이 우수하여 콘크리트 자체에서의 누수와 균열 등을 방지할 수 있다. According to the composition for an excellent penetration type upper slab of the present invention, water permeability, strength, durability and the like are excellent, so that water leakage and cracking in the concrete itself can be prevented.

본 발명의 프리캐스트 콘크리트 우수저류조의 시공방법에 의하면, 프리스트레스력을 이용하여 슬래브 간을 일체화시켜 시공할 수 있어 현장에서 우수저류조를 타설하는데 소요되는 시공기간을 절약함과 동시에 연결부위를 최소화함으로써 누수에 대한 문제점을 해결할 수 있을 뿐만 아니라, 투수성, 강도, 내구성 등이 우수한 우수 침투형 상부 슬래브용 조성물에 의해 콘크리트 자체에서의 누수와 균열 등을 방지할 수 있다.
According to the method of the present invention, it is possible to integrate the slabs by using the prestressing force, thereby saving the construction time required for installing the excellent storages in the field and minimizing the connection area, And it is also possible to prevent water leakage and cracking in the concrete itself by the composition for an excellent permeable upper slab excellent in water permeability, strength, durability and the like.

도 1은 우수 침투형 상부 슬래브를 도시한 도면이다.
도 2는 제1 상부 슬래브를 도시한 도면이다.
도 3은 제2 상부 슬래브를 도시한 도면이다.
도 4는 하부 슬래브를 도시한 도면이다.
도 5는 일 예에 따른 제1 하부 슬래브를 도시한 도면이다.
도 6은 다른 예에 따른 제1 하부 슬래브를 도시한 도면이다.
도 7은 일 예에 따른 제2 하부 슬래브를 도시한 도면이다.
도 8은 다른 예에 따른 제2 하부 슬래브를 도시한 도면이다.
도 9는 일 예에 따른 기둥을 도시한 도면이다.
도 10은 다른 예에 따른 기둥을 도시한 도면이다.
도 11은 또 다른 예에 따른 기둥을 도시한 도면이다.
도 12는 또 다른 예에 따른 기둥을 도시한 도면이다.
도 13은 측벽 슬래브를 도시한 도면이다.
도 14는 4개의 제1 상부 슬래브가 결합된 모습을 보여주는 도면이다.
도 15는 제1 상부 슬래브와 제2 상부 슬래브가 결합된 모습을 보여주는 도면이다.
도 16은 2개의 제1 하부 슬래브가 결합된 모습을 보여주는 도면이다.
도 17은 제1 하부 슬래브와 제2 하부 슬래브가 결합된 모습을 보여주는 도면이다.
도 18은 일 예에 따른 프리캐스트 콘크리트 우수저류조를 보여주는 평면도이다.
도 19는 도 18의 Ⅰ-Ⅱ 단면의 일 예를 보여주는 단면도이다.
도 20은 도 19의 'A' 부분을 확대하여 나타낸 도면이다.
도 21은 도 18의 Ⅰ-Ⅱ 단면의 다른 예를 보여주는 단면도이다. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a view showing a storm permeable upper slab.
2 is a view showing a first upper slab.
3 is a view showing a second upper slab.
4 is a view showing a lower slab.
5 is a view showing a first lower slab according to an example.
6 is a view showing a first lower slab according to another example.
7 is a view showing a second lower slab according to an example.
8 is a view showing a second lower slab according to another example.
9 is a view showing a column according to an example.
10 is a view showing a column according to another example.
11 is a view showing a column according to another example.
12 is a view showing a column according to another example.
13 is a view showing a side wall slab.
14 is a view showing a state where four first upper slabs are combined.
15 is a view showing a state in which the first upper slab and the second upper slab are combined.
16 is a view showing a state where two first lower slabs are combined.
17 is a view showing a state where the first lower slab and the second lower slab are combined.
18 is a plan view showing a precast concrete excellent storage tank according to an example.
19 is a cross-sectional view showing an example of a cross section taken along the line I-II in FIG.
FIG. 20 is an enlarged view of the portion 'A' in FIG. 19; FIG.
Fig. 21 is a cross-sectional view showing another example of the section I-II in Fig. 18;

이하, 첨부된 도면을 참조하여 본 발명에 따른 바람직한 실시예를 상세하게 설명한다. 그러나, 이하의 실시예는 이 기술분야에서 통상적인 지식을 가진 자에게 본 발명이 충분히 이해되도록 제공되는 것으로서 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 다음에 기술되는 실시예에 한정되는 것은 아니다. 도면상에서 동일 부호는 동일한 요소를 지칭한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. However, it should be understood that the following embodiments are provided so that those skilled in the art will be able to fully understand the present invention, and that various modifications may be made without departing from the scope of the present invention. It is not. Wherein like reference numerals refer to like elements throughout.

본 발명은 프리캐스트 콘크리트(Precast Concrete; PC) 우수저류조, 상기 우수저류조의 우수 침투형 상부 슬래브 재료로 사용되는 우수 침투형 상부 슬래브용 조성물 조성물, 그리고 상기 우수저류조의 시공방법을 제시한다. The present invention provides a composition for an excellent permeable upper slab, which is used as a precast concrete (PC) storm reservoir, an excellent penetration type upper slab material of the storm reservoir, and a method of constructing the storm reservoir.

본 발명의 바람직한 실시예에 따른 프리캐스트 콘크리트 우수저류조는, 우수 침투형 상부 슬래브와, 우수저류조의 바닥면을 형성하면서 우수가 하부로 빠져나가지 못하게 하여 우수를 우수저류조 내에 가두기 위한 하부 슬래브와, 상기 하부 슬래브와 결합되어 고정되어 있고 상기 우수 침투형 상부 슬래브를 지지하는 기둥과, 상기 하부 슬래브의 외곽 테두리를 따라 벽체를 형성하여 상기 하부 슬래브와 상기 우수 침투형 상부 슬래브를 연결하는 측벽 슬래브를 포함하며, 상기 우수 침투형 상부 슬래브 하면의 네 모퉁이에 구비된 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈으로 삽입되어 고정되어 있고, 상기 기둥 상부에 구비된 삽입홈에는 4개의 제1 돌출부가 삽입되고, 4개의 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈에 삽입됨에 따라 4개의 우수 침투형 상부 슬래브가 하나의 기둥에 결합되는 형태를 갖고, 상기 우수 침투형 상부 슬래브의 네 모퉁이에 제1 요홈부가 구비되어 있고, 상기 제1 요홈부로 둘러싸인 영역에 몰탈이 주입되어 서로 이웃하는 우수 침투형 상부 슬래브 및 상기 기둥이 결합되어 있다.The present invention relates to a precast concrete excellent stor- age tank, comprising: an excellent permeable upper slab; a lower slab for forming a bottom surface of the stor- age stor- age tank while preventing the storm from escaping to the lower portion, And a sidewall slab connected to the lower slab and supporting the superior permeable upper slab and a wall formed along the outer rim of the lower slab to connect the lower slab and the superior penetrating upper slab, A first protrusion provided at four corners of the lower surface of the superior permeable upper slab is inserted and fixed into an insertion groove provided in the upper portion of the column, and four first protrusions are inserted into the insertion groove provided in the upper portion of the column , Four first projections are inserted into the insertion groove provided in the upper portion of the column, Wherein the first slab has a first recess formed at four corners of the slab, and the mortar is injected into a region surrounded by the first slab, The permeable upper slab and the column are coupled.

본 발명의 바람직한 실시예에 따른 우수 침투형 상부 슬래브용 조성물은, 상기 프리캐스트 콘크리트 우수저류조의 우수 침투형 상부 슬래브를 형성하기 위한 조성물로서, 시멘트계 결합재 3∼40중량%, 보투수성 결합재 0.01∼15중량%, 잔골재 45∼90중량%, 굵은골재 5∼40중량% 및 물 0.1∼15중량%를 포함하며, 상기 보투수성 결합재는 폴리메타크릴산 2-히드록시에틸 60∼99중량%, 아크릴아미드 0.01∼25중량%, 폴리아크릴산나트륨 0.01∼25중량% 및 아세틸셀롤로오스 0.01∼15중량%를 포함한다. The composition for the superior penetration type upper slab according to the preferred embodiment of the present invention is a composition for forming the superior permeation type upper slab of the precast concrete excellent storage trough wherein the cement based binder is 3 to 40 wt% 15 to 15 weight% of fine aggregate, 45 to 90 weight% of fine aggregate, 5 to 40 weight% of coarse aggregate, and 0.1 to 15 weight% of water, wherein said waterproof binder comprises 60 to 99% by weight of 2-hydroxyethyl methacrylate, 0.01 to 25% by weight of acrylamide, 0.01 to 25% by weight of sodium polyacrylate, and 0.01 to 15% by weight of acetyl celluloses.

본 발명의 바람직한 실시예에 따른 프리캐스트 콘크리트 우수저류조의 시공방법은, 상기 프리캐스트 콘크리트 우수저류조를 시공하기 위한 방법으로서, 프리캐스트 콘크리트 우수저류조를 설치할 하부 기초를 형성하기 위하여 골재를 포설하고 다짐한 후, 상부에 모래를 포설하고 다짐하여 하부 기초를 준비하는 단계와, 상기 하부 기초 상부에 린콘크리트를 타설하는 단계와, 상기 린콘크리트가 타설된 상부에 우수저류조의 바닥면을 형성하면서 우수가 하부로 빠져나가지 못하게 하여 우수를 우수저류조 내에 가두기 위한 하부 슬래브를 설치하거나 현장에서 몰탈을 타설하여 하부 슬래브를 형성하는 단계와, 우수 침투형 상부 슬래브를 지지하기 위한 기둥을 설치하고 상기 하부 슬래브와 결합하여 고정하는 단계와, 상기 하부 슬래브의 외곽 테두리를 따라 벽체를 형성하는 측벽 슬래브를 설치하는 단계 및 상기 측벽 슬래브와 상기 기둥 상부에 우수 침투형 상부 슬래브를 설치하는 단계를 포함하며, 상기 우수 침투형 상부 슬래브 하면의 네 모퉁이에 구비된 제1 돌출부를 상기 기둥 상부에 구비된 삽입홈으로 삽입하여 고정하고, 상기 기둥 상부에 구비된 삽입홈에 4개의 제1 돌출부를 삽입하며, 상기 우수 침투형 상부 슬래브의 네 모퉁이에 제1 요홈부가 구비되게 하고, 상기 제1 요홈부로 둘러싸인 영역에 몰탈을 주입하여 서로 이웃하는 우수 침투형 상부 슬래브 및 상기 기둥을 결합하며, 4개의 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈에 삽입됨에 따라 4개의 우수 침투형 상부 슬래브가 하나의 기둥에 결합되는 형태를 갖는다. The method for constructing the precast concrete excellent storeroom according to the preferred embodiment of the present invention is a method for constructing the precast concrete excellent storeroom by installing an aggregate in order to form a lower foundation for installing the precast concrete storm reservoir, The method of claim 1, further comprising the steps of: preparing a lower foundation by laying sand on the upper portion of the lower basement; placing lean concrete on the lower foundation; forming a bottom surface of the upper side of the lehr concrete, Forming a lower slab by placing a lower slab in the field to prevent the slab from escaping and placing the mortar in situ; placing a column for supporting the slab having superior penetration type and fixing it by engaging with the lower slab; A step of forming an outer edge of the lower slab And a step of installing a superior permeable upper slab on the sidewall slab and the upper portion of the column, wherein a first projection provided at four corners of the bottom of the superior permeable upper slab And four first protrusions are inserted into the inserting grooves formed in the upper portion of the column and the first recesses are provided at four corners of the superior penetrating type upper slab, The mortar is injected into an area surrounded by the first concave portion to join the adjacent superior penetrating type upper slab and the column and the four first protrusions are inserted into the insertion groove provided in the upper portion of the column, Shaped slab is coupled to one column.

이하에서, 본 발명의 바람직한 실시예에 따른 프리캐스트 콘크리트 우수저류조에 대하여 더욱 구체적으로 설명한다. Hereinafter, a precast concrete excellent stor- age tank according to a preferred embodiment of the present invention will be described in more detail.

도 1은 우수 침투형 상부 슬래브를 도시한 도면이다. 도 2는 제1 상부 슬래브를 도시한 도면이다. 도 3은 제2 상부 슬래브를 도시한 도면이다. 도 4는 하부 슬래브를 도시한 도면이다. 도 5는 일 예에 따른 제1 하부 슬래브를 도시한 도면이다. 도 6은 다른 예에 따른 제1 하부 슬래브를 도시한 도면이다. 도 7은 일 예에 따른 제2 하부 슬래브를 도시한 도면이다. 도 8은 다른 예에 따른 제2 하부 슬래브를 도시한 도면이다. 도 9는 일 예에 따른 기둥을 도시한 도면이다. 도 10은 다른 예에 따른 기둥을 도시한 도면이다. 도 11은 또 다른 예에 따른 기둥을 도시한 도면이다. 도 12는 또 다른 예에 따른 기둥을 도시한 도면이다. 도 13은 측벽 슬래브를 도시한 도면이다. 도 14는 4개의 제1 상부 슬래브가 결합된 모습을 보여주는 도면이다. 도 15는 제1 상부 슬래브와 제2 상부 슬래브가 결합된 모습을 보여주는 도면이다. 도 16은 2개의 제1 하부 슬래브가 결합된 모습을 보여주는 도면이다. 도 17은 제1 하부 슬래브와 제2 하부 슬래브가 결합된 모습을 보여주는 도면이다. 도 18은 일 예에 따른 프리캐스트 콘크리트 우수저류조를 보여주는 평면도이다. 도 19는 도 18의 Ⅰ-Ⅱ 단면의 일 예를 보여주는 단면도이다. 도 20은 도 19의 'A' 부분을 확대하여 나타낸 도면이다. 도 21은 도 18의 Ⅰ-Ⅱ 단면의 다른 예를 보여주는 단면도이다. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a view showing a storm permeable upper slab. 2 is a view showing a first upper slab. 3 is a view showing a second upper slab. 4 is a view showing a lower slab. 5 is a view showing a first lower slab according to an example. 6 is a view showing a first lower slab according to another example. 7 is a view showing a second lower slab according to an example. 8 is a view showing a second lower slab according to another example. 9 is a view showing a column according to an example. 10 is a view showing a column according to another example. 11 is a view showing a column according to another example. 12 is a view showing a column according to another example. 13 is a view showing a side wall slab. 14 is a view showing a state where four first upper slabs are combined. 15 is a view showing a state in which the first upper slab and the second upper slab are combined. 16 is a view showing a state where two first lower slabs are combined. 17 is a view showing a state where the first lower slab and the second lower slab are combined. 18 is a plan view showing a precast concrete excellent storage tank according to an example. 19 is a cross-sectional view showing an example of a cross section taken along the line I-II in FIG. FIG. 20 is an enlarged view of the portion 'A' in FIG. 19; FIG. Fig. 21 is a cross-sectional view showing another example of the section I-II in Fig. 18;

도 1 내지 도 21을 참조하면, 본 발명의 바람직한 실시예에 따른 프리캐스트 콘크리트 우수저류조는 우수 침투형 상부 슬래브(110), 하부 슬래브(130), 기둥(150) 및 측벽 슬래브(170)를 포함한다. 1 to 21, a precast concrete storage tank according to a preferred embodiment of the present invention includes an upper permeable upper slab 110, a lower slab 130, a column 150, and a side wall slab 170 do.

우수 침투형 상부 슬래브(110)는 우수가 침투할 수 있도록 하기 위하여 우수 침투형 상부 슬래브용 조성물을 이용하여 제작된다. 우수 침투형 상부 슬래브(110)는 우수저류조의 상부를 구성하는 부품으로서, 우수가 우수저류조 내로 침투될 수 있도록 하는 역할을 하고, 우수 이외의 불순물이 우수저류조로 유입되는 것을 방지하는 역할도 한다. The superior permeable top slab 110 is fabricated using a composition for the superior permeable top slab so that the storm can penetrate. The storm permeable upper slab 110 is a part constituting the upper part of the storm reservoir and plays a role of allowing the storm to be permeated into the stormwater storeroom and also preventing impurities other than the storm from flowing into the storm reservoir.

우수 침투형 상부 슬래브(110)의 하부에는 기둥(150)과 결합할 수 있도록 제1 돌출부(116)가 구비되어 있다. 상기 제1 돌출부(116)는 우수 침투형 상부 슬래브(110) 하면의 네 모퉁이에 구비되는 것이 바람직하다. A first protrusion 116 is provided at the lower portion of the superior permeable upper slab 110 to be able to engage with the column 150. The first projections 116 are preferably provided at four corners of the lower surface of the storm permeable upper slab 110.

우수 침투형 상부 슬래브(110)의 네 모퉁이에는 도 1 내지 도 3에 도시된 바와 같이 몰탈을 채울 수 있도록 제1 요홈부(118)가 구비될 수 있다. 제1 요홈부(118)는 우수 침투형 상부 슬래브(110)에서 상부에서 하부로 향하는 방향을 따라 구비되는데, 상면(120)부터 제1 돌출부(116)의 저면까지 구비되는 것이 바람직하다. 이에 따라 우수 침투형 상부 슬래브(110)가 서로 연결되면 제1 요홈부(118)에 의해 빈 공간이 형성되게 되며 단면이 원형, 사각형 등의 형태를 이루게 된다. 제1 요홈부(118)로 둘러싸인 영역에 몰탈을 주입하여 서로 이웃하는 우수 침투형 상부 슬래브(110)와 기둥(150)이 더욱 견고하게 결합될 수 있게 된다.At the four corners of the storm permeable upper slab 110, first recessed grooves 118 may be provided to fill the mortar as shown in FIGS. The first recessed portion 118 is provided along the direction from the top to the bottom in the storm permeable upper slab 110 and is preferably provided from the upper surface 120 to the bottom of the first protruding portion 116. Accordingly, when the penetration-type upper slabs 110 are connected to each other, an empty space is formed by the first recessed trenches 118, and a cross-sectional shape becomes circular or square. The molten metal is injected into the region surrounded by the first recessed trench 118 so that the neighboring super permeable upper slab 110 and the pillar 150 can be more firmly coupled.

우수 침투형 상부 슬래브(110)는 우수저류조의 상부 중앙부에 설치되는 제1 상부 슬래브(112)와, 우수저류조의 상부 외측부에 설치되는 제2 상부 슬래브(114)를 포함할 수 있다. The storm permeable upper slab 110 may include a first upper slab 112 installed at the upper central portion of the storm reservoir and a second upper slab 114 installed at the upper lateral portion of the storm reservoir.

도 1 내지 도 3에 도시된 바와 같이, 우수 침투형 상부 슬래브(110)의 상면(120)에는 제1 상부 슬래브(112)와 제1 상부 슬래브(112) 사이를 움직이지 않도록 결합하거나 제1 상부 슬래브(112)와 제2 상부 슬래브(114) 사이를 움직이지 않도록 결합시키기 위한 제1 결합수단(124)이 구비될 수 있다. 이에 따라 제1 상부 슬래브(112)와 제1 상부 슬래브(112)가 서로 이웃하게 설치되거나 제1 상부 슬래브(112)와 제2 상부 슬래브(114)가 서로 이웃하게 설치된 상태에서 제1 결합수단(124)에 볼트, 강선, 강봉, 강관 등을 삽입하여 고정하면 서로 견고하게 결합될 수 있다. 도 1 내지 도 3에서는 우수 침투형 상부 슬래브(110)의 상면(120)에서 2개의 모서리 부분에만 제1 결합수단(124)이 구비된 것으로 도시되었으나, 우수 침투형 상부 슬래브(110)의 상면(120)에서 1개의 모서리 부분이나 4개의 모서리 부분 모두에 제1 결합수단(124)이 구비될 수도 있다. 1 to 3, the upper surface 120 of the storm permeable upper slab 110 may be movably coupled between the first upper slab 112 and the first upper slab 112, A first coupling means 124 for coupling the slab 112 and the second upper slab 114 in a non-movable manner may be provided. The first upper slab 112 and the first upper slab 112 are adjacent to each other or the first upper slab 112 and the second upper slab 114 are adjacent to each other, 124, by inserting and fixing bolts, steel wires, steel rods, steel pipes, or the like. 1 to 3 show that the first joining means 124 is provided on only two corner portions of the upper surface 120 of the storm permeable upper slab 110, The first coupling means 124 may be provided on either one of the corner portions or the four corner portions.

제2 상부 슬래브(114)는 측벽 슬래브(170)와 견고하게 결합될 수 있도록 철근(126)이 돌출되어 있을 수 있다. 상기 철근(126)은 제2 상부 슬래브(114)에 나사 등으로 결합되거나, 제2 상부 슬래브(114)의 제작시 일체로 형성될 수 있다. The second upper slab 114 may protrude from the reinforcing bars 126 so that the second upper slab 114 can be firmly engaged with the side wall slabs 170. The reinforcing bars 126 may be coupled to the second upper slab 114 by screws or may be integrally formed when the second upper slab 114 is manufactured.

하부 슬래브(130)는 우수저류조의 하부를 구성하는 부품으로서, 우수가 하부로 빠져나가지 못하게 하고 우수저류조 내에 가두는 역할을 한다. The lower slab 130 is a part constituting the lower part of the stor- age tank, and serves to prevent the storm from escaping to the lower part and to keep it in the stor- age tank.

하부 슬래브(130)의 상부에는 기둥(150)과 결합할 수 있도록 제2 돌출부(136)가 구비되어 있을 수 있다. 상기 제2 돌출부(136)는 하부 슬래브(130) 상면의 네 모퉁이에 구비되는 것이 바람직하다. A second projection 136 may be provided on the upper portion of the lower slab 130 so as to engage with the column 150. The second protrusions 136 may be provided at four corners of the upper surface of the lower slab 130.

하부 슬래브(130)의 네 모퉁이에는 도 4 내지 도 8에 도시된 바와 같이 몰탈을 채울 수 있도록 제2 요홈부(138)가 구비될 수 있다. 제2 요홈부(138)는 하부 슬래브(130)에서 하부에서 상부로 향하는 방향을 따라 구비되는데, 하면(142)부터 제2 돌출부(136)의 상면까지 구비되는 것이 바람직하다. 이에 따라 하부 슬래브(130)가 서로 연결되면 제2 요홈부(138)에 의해 빈 공간이 형성되게 되며 단면이 원형, 사각형 등의 형태를 이루게 된다. 제2 요홈부(138)로 둘러싸인 영역에 몰탈을 주입하여 서로 이웃하는 하부 슬래브(130)가 더욱 견고하게 결합될 수 있게 된다.4 to 8 may be provided at the four corners of the lower slab 130 so as to fill the mortar. The second recessed portion 138 is provided along the direction from the lower portion to the upper portion of the lower slab 130 and is preferably provided from the lower surface 142 to the upper surface of the second projection 136. Accordingly, when the lower slabs 130 are connected to each other, a hollow space is formed by the second recessed grooves 138, and a cross section of the slabs 130 has a circular shape or a square shape. The mortar is injected into the region surrounded by the second recessed portion 138, so that the neighboring lower slabs 130 can be more firmly coupled.

하부 슬래브(130)는 우수저류조의 하부 중앙부에 설치되는 제1 하부 슬래브(132)와, 우수저류조의 하부 외측부에 설치되는 제2 하부 슬래브(134)를 포함할 수 있다.The lower slab 130 may include a first lower slab 132 installed at a lower central portion of the upper storage vessel and a second lower slab 134 installed at a lower outer side of the upper storage vessel.

도 5 및 도 7에 도시된 바와 같이, 하부 슬래브(130)의 상면(140)에는 제1 하부 슬래브(132)와 제1 하부 슬래브(132) 사이를 움직이지 않도록 결합하거나 제1 하부 슬래브(132)와 제2 하부 슬래브(134) 사이를 움직이지 않도록 결합시키기 위한 제2 결합수단(144)이 구비될 수 있다. 이에 따라 제1 하부 슬래브(132)와 제1 하부 슬래브(132)가 서로 이웃하게 설치되거나 제1 하부 슬래브(132)와 제2 하부 슬래브(134)가 서로 이웃하게 설치된 상태에서 제2 결합수단(144)에 볼트, 강선, 강봉, 강관 등을 삽입하여 고정하면 서로 견고하게 결합될 수 있다.5 and 7, the upper surface 140 of the lower slab 130 may be movably coupled between the first lower slab 132 and the first lower slab 132, And a second coupling means 144 for coupling the first lower slab 134 and the second lower slab 134 in a non-moving manner. The first lower slab 132 and the first lower slab 132 may be adjacent to each other or the second lower slab 132 and the second lower slab 134 may be adjacent to each other, 144, a bolt, a steel wire, a steel bar, a steel pipe, and the like are inserted and fixed and can be firmly coupled with each other.

제1 하부 슬래브(132)와 제1 하부 슬래브(132) 사이 또는 제1 하부 슬래브(132)와 제2 하부 슬래브(134) 사이를 결합하는 다른 방법으로서, 도 6 및 도 8에 도시된 바와 같이 서로 이웃하는 하부 슬래브(130) 사이를 철근(146a)으로 고정하고 그 사이에 몰탈을 채워 하부 슬래브(130)의 유동을 방지하면서 견고하게 결합시킬 수도 있다. 이를 위해 제1 하부 슬래브(132)에는 제1 하부 슬래브(132) 간의 결합을 견고하게 하기 위하여 철근(146a)이 돌출되어 있을 수 있으며, 상기 철근(146a)은 제1 하부 슬래브(132)에 나사 등으로 결합되거나, 제1 하부 슬래브(132)의 제작시 일체로 형성될 수 있다. 제1 하부 슬래브(132)에서 돌출된 철근(146a)은 다른 제1 하부 슬래브(132)에서 돌출된 철근(146a)과 연결될 수 있으며, 제1 하부 슬래브(132)와 제1 하부 슬래브(132) 사이에 몰탈로 채워 견고하게 고정될 수 있다. As another method of joining between the first lower slab 132 and the first lower slab 132 or between the first lower slab 132 and the second lower slab 134, as shown in FIGS. 6 and 8 The lower slab 130 may be firmly coupled while preventing the flow of the lower slab 130 by fixing the adjacent lower slabs 130 with the reinforcing bars 146a and filling the mortar therebetween. To this end, a reinforcing bar 146a may protrude from the first lower slab 132 to secure the connection between the first lower slab 132 and the reinforcing bars 146a may be screwed into the first lower slab 132 Or may be integrally formed when the first lower slab 132 is manufactured. The reinforcing bars 146a protruding from the first lower slab 132 may be connected to the reinforcing bars 146a protruding from the first lower slab 132 and the first lower slab 132 and the first lower slab 132 may be connected to each other. It can be firmly fixed with mortar.

제2 하부 슬래브(134)에는 측벽 슬래브(170)와 견고하게 결합될 수 있도록 철근(146b)이 돌출되어 있을 수 있다. 상기 철근(146b)은 제2 하부 슬래브(134)에 나사 등으로 결합되거나, 제2 하부 슬래브(134)의 제작시 일체로 형성될 수 있다. The second lower slab 134 may have a reinforcing bar 146b protruding therefrom so as to firmly engage the side wall slab 170. The reinforcing bars 146b may be coupled to the second lower slab 134 by screws or may be integrally formed when the second lower slab 134 is manufactured.

기둥(150)은 우수 침투형 상부 슬래브(110)를 지지하는 역할을 한다. 우수 침투형 상부 슬래브(110)와 하부 슬래브(130) 사이의 간격은 기둥(150)의 길이에 따라 달라지게 된다. 기둥(150)은 하부 슬래브(130)와 결합되어 고정되어 있다.The column 150 serves to support the storm permeable upper slab 110. The distance between the superior permeable upper slab 110 and the lower slab 130 depends on the length of the column 150. The column 150 is fixedly coupled to the lower slab 130.

기둥(150)은 몸체(152)와 지지대(154)를 포함할 수 있다. 몸체(152)의 상부에는 우수 침투형 상부 슬래브(110)의 제1 돌출부(116)를 삽입하여 고정하기 위한 삽입홈(156)이 구비되어 있다. 하나의 삽입홈(156)에는 4개의 제1 돌출부(116)가 삽입될 수 있고, 4개의 제1 돌출부(116)가 삽입홈(156)에 삽입되는 경우에 4개의 우수 침투형 상부 슬래브(110)가 하나의 기둥(150)에 지지되는 형태를 갖게 된다. The column 150 may include a body 152 and a support 154. The upper portion of the body 152 is provided with an insertion groove 156 for inserting and fixing the first protrusion 116 of the superior permeable upper slab 110. Four first protrusions 116 can be inserted into one insertion groove 156 and four superior penetration type upper slabs 110 can be inserted when four first protrusions 116 are inserted into the insertion groove 156. [ Are supported on one pillar 150.

삽입홈(156)에는 우수 침투형 상부 슬래브(110)를 더욱 견고하게 고정하기 위하여 도 10에 도시된 바와 같이 철근(158a)이 돌출되어 있을 수 있으며, 상기 철근(158a)은 기둥(150)의 몸체(152)에 나사 등으로 결합되거나, 기둥(150)의 몸체(152) 제작시 일체로 형성될 수 있다. 이 경우에 상기 철근(158a)은 우수 침투형 상부 슬래브(110)의 제1 요홈부(118)에 의해 형성되는 빈 공간에 위치되게 되고, 제1 요홈부(118)로 둘러싸인 영역에 몰탈을 주입함으로써 서로 이웃하는 우수 침투형 상부 슬래브(110)와 기둥(150) 사이가 더욱 견고하게 결합될 수 있게 된다.The reinforcing bars 158a may protrude from the insertion grooves 156 as shown in FIG. 10 in order to more firmly fix the superior permeable upper slab 110, May be integrally formed with the body 152 by screws or the like when the body 152 of the column 150 is manufactured. In this case, the reinforcing bars 158a are located in the empty spaces formed by the first recessed grooves 118 of the superior permeable upper slab 110, and the molten metal is injected into the region surrounded by the first recessed grooves 118 Thereby making it possible to more firmly couple the pillars 150 to each other between the neighboring storm permeable upper slabs 110.

기둥(150)의 지지대(154)는 기둥(150)을 지면에 견고하게 고정시키는 역할을 한다. 지지대(154)의 하부에도 하부 슬래브(110)의 제2 돌출부(136)를 삽입하여 고정하기 위한 삽입홈이 구비되어 있을 수 있다. 또한, 지지대(154)에 구비된 삽입홈에는 4개의 제2 돌출부(136)가 삽입될 수 있고, 4개의 제2 돌출부(136)가 지지대(154)에 구비된 삽입홈에 삽입되는 경우에 4개의 하부 슬래브(130)가 하나의 기둥(150)에 결합되는 형태를 갖게 된다. The support posts 154 of the posts 150 serve to securely fix the posts 150 to the ground. And an insertion groove for inserting and fixing the second protrusion 136 of the lower slab 110 may be provided in the lower part of the support base 154. [ Four second protrusions 136 can be inserted into the insertion groove provided in the support base 154. When four second protrusions 136 are inserted into the insertion groove provided in the support base 154, So that the lower slabs 130 are coupled to the single pillar 150.

기둥(150)에는 지지대가 구비되지 않고, 도 11 및 도 12에 도시된 바와 같이, 기둥(150)의 하부에 기둥(150)을 지지하거나 하부 슬래브(130)와 견고하게 결합될 수 있도록 철근(158b)이 돌출되어 있을 수 있다. 상기 철근(158b)은 기둥(150)에 나사 등으로 결합되거나 기둥(150) 제작시 일체로 형성될 수 있다. 기둥(150)의 하부에서 돌출된 철근(158b)은 하부 슬래브(130)에서 돌출된 철근(146a)과 연결될 수 있으며, 기둥(150)과 하부 슬래브(130) 사이에 몰탈로 채워 견고하게 고정될 수 있다. As shown in FIGS. 11 and 12, the pillars 150 are not provided with a support, and the pillars 150 may be supported at the lower portion of the pillars 150, 158b may protrude therefrom. The reinforcing bars 158b may be screwed to the column 150 or integrally formed when the column 150 is manufactured. The reinforcing bars 158b protruding from the lower portion of the column 150 can be connected to the reinforcing bars 146a protruded from the lower slab 130 and are firmly fixed by the mortar between the column 150 and the lower slab 130 .

측벽 슬래브(170)는 우수저류조의 벽면을 구성하는 부품으로서, 우수가 측면로 빠져나가지 못하게 하고 우수저류조 내에 가두는 역할을 한다. 측벽 슬래브(170)는 하부 슬래브(130)의 외곽 테두리를 따라 벽체를 형성하여 하부 슬래브(130)와 우수 침투형 상부 슬래브(110)를 연결한다.The sidewall slab 170 is a part constituting the wall surface of the storm sewer, and serves to prevent the storm from escaping to the side and to keep it in the storeroom. The sidewall slab 170 forms a wall along the outer rim of the lower slab 130 to connect the lower slab 130 to the superior penetrating upper slab 110.

측벽 슬래브(170) 하부의 일측에는 하부 슬래브(130)와 결합하기 위하여 돌출된 받침대(172)가 구비될 수 있다. At one side of the lower portion of the side wall slab 170, a pedestal 172 protruded to engage with the lower slab 130 may be provided.

도 13에 도시된 바와 같이, 받침대(172)에는 하부 슬래브(130)와 견고하게 결합될 수 있도록 철근(174a)이 돌출되어 있을 수 있으며, 상기 철근(174a)은 받침대(172)에 나사 등으로 결합되거나 측벽 슬래브(170)의 제작시 일체로 형성될 수 있다. 받침대(172)에 구비된 철근(174a)은 하부 슬래브(130)에서 돌출된 철근(146b)과 연결될 수 있으며, 받침대(172)와 하부 슬래브(130) 사이에 몰탈로 채워 견고하게 고정될 수 있다. 13, a reinforcing bar 174a may protrude from the pedestal 172 so as to firmly engage with the lower slab 130, and the reinforcing bars 174a may be screwed to the pedestal 172 Or may be integrally formed when fabricating side wall slabs 170. The reinforcing bars 174a provided on the pedestal 172 may be connected to the reinforcing bars 146b protruded from the lower slab 130 and may be firmly fixed with mortar between the pedestal 172 and the lower slab 130 .

측벽 슬래브(170)의 상부에는 우수 침투형 상부 슬래브(110)와의 결합을 견고하게 하기 위하여 몰탈을 치기 위한 걸림턱(176)이 구비될 수 있다. 측벽 슬래브(170)의 상부는 우수 침투형 상부 슬래브(110)와 견고하게 결합될 수 있도록 철근(174b)이 돌출되어 있을 수 있으며, 상기 철근(174b)은 측벽 슬래브(170)에 나사 등으로 결합되거나 측벽 슬래브(170)의 제작시 일체로 형성될 수 있다. 측벽 슬래브(170)의 상부에서 돌출된 철근(174b)은 우수 침투형 상부 슬래브(110)에서 돌출된 철근(126)과 연결될 수 있으며, 측벽 슬래브(170)와 우수 침투형 상부 슬래브(110) 사이에 몰탈로 채워 견고하게 고정될 수 있다. An upper portion of the sidewall slab 170 may be provided with a latching jaw 176 for engaging the mortar to secure the connection with the storm permeable upper slab 110. The upper portion of the sidewall slab 170 may protrude from the reinforcing bars 174b so that the upper portion of the sidewall slab 170 can be firmly coupled to the superior permeable upper slab 110. The reinforcing bars 174b are screwed into the side wall slabs 170 Or may be integrally formed when the side wall slab 170 is manufactured. The reinforcing bars 174b protruding from the upper portion of the side wall slabs 170 may be connected to the reinforcing bars 126 projecting from the superior penetrating upper slabs 110 and between the side wall slabs 170 and the superior penetrating upper slabs 110 And can be firmly fixed.

측벽 슬래브(170)의 측면(140)에는 측벽 슬래브(170)와 측벽 슬래브(170) 사이를 움직이지 않도록 결합시키기 위한 제3 결합수단(178)이 구비될 수 있다. 이에 따라 측벽 슬래브(170)와 측벽 슬래브(170)가 서로 이웃하게 설치된 상태에서 제3 결합수단(1478에 볼트, 강선, 강봉, 강관 등을 삽입하여 고정하면 서로 견고하게 결합될 수 있다.The side 140 of the sidewall slab 170 may be provided with a third coupling means 178 for matingly engaging the sidewall slab 170 and the sidewall slab 170. Accordingly, when the side wall slabs 170 and the side wall slabs 170 are installed adjacent to each other, bolts, steel wires, steel rods, steel pipes, and the like are fixedly inserted into the third coupling means 1478.

이하에서, 본 발명의 바람직한 실시예에 따른 프리캐스트 콘크리트 우수저류조의 시공방법을 설명한다. Hereinafter, a method of constructing a pre-cast concrete stormwater storage tank according to a preferred embodiment of the present invention will be described.

본 발명의 바람직한 실시예에 따른 프리캐스트 콘크리트 우수저류조를 설치할 하부 기초를 형성하기 위하여 골재(잡석)를 포설하고 다짐한 후, 상부에 모래를 포설하고 다짐하여 하부 기초를 준비한다. In order to form a lower foundation to be installed in the pre-cast concrete excellent storage tank according to the preferred embodiment of the present invention, aggregate (rubble) is installed, and sand is laid on the upper part to prepare a lower foundation.

상기 하부 기초 상부에 린콘크리트(버림콘크리트)를 타설한다. And lean concrete (abandoned concrete) is laid on the lower foundation.

상기 린콘크리트가 타설된 상부에 도 4 내지 도 7에 도시된 바와 같은 하부 슬래브(130)를 설치하거나, 도 21에 도시된 바와 같이 현장에서 몰탈을 타설하여 하부 슬래브를 형성할 수도 있다. 도 19는 도 4 내지 도 7에 도시된 하부 슬래브를 린콘크리트가 타설된 상부에 설치한 경우를 보여주고, 도 21은 린콘크리트가 타설된 상부에 몰탈을 현장 타설하여 하부 슬래브(130)를 형성한 경우를 보여준다. 하부 슬래브를 현장 타설하는 경우에 사용하는 몰탈은 내투수성이 우수한 일반 몰탈 조성물을 사용할 수 있으며, 내투수성이 우수하여 물이 하부로 빠져나가는 것을 방지할 수 있는 몰탈 조성물이면 그 사용에 제한이 있는 것은 아니다. 상기 몰탈을 채우기 이전에 지반의 부등침하, 프리스트레스력에 의한 응력집중으로 발생될 수 있는 파손, 누수, 방수 등을 완벽하게 처리할 수 있도록 인장강도 2MPa 이상, 신율 400% 이상 및 부착강도 2MPa 이상의 성능을 가지는 우레탄-실리콘계 폴리머 채움재를 이용하여 실링하는 것이 바람직하다.The lower slab 130 as shown in FIGS. 4 to 7 may be installed on the upper portion where the lean concrete is installed, or the lower slab may be formed by installing the mortar in the site as shown in FIG. Fig. 19 shows a case where the lower slab shown in Figs. 4 to 7 is installed on an upper part with lean concrete laid. Fig. 21 shows a state where a mortar is laid on the upper part where lean concrete is laid to form a lower slab 130 One case is shown. The mortar used for casting the lower slab in the field can use a general mortar composition having excellent water permeability and the use of a mortar composition capable of preventing water from escaping to the bottom due to excellent water permeability is limited There is not. A tensile strength of not less than 2 MPa, a elongation of not less than 400%, and an adhesion strength of not less than 2 MPa so as to completely treat breakage, water leakage and waterproofing which may be caused by uneven settlement of the ground and stress concentration by the prestress force before filling the mortar It is preferable to perform sealing by using a urethane-silicone-based polymer filler having a low melting point.

설치된 하부 슬래브(130) 간을 프리스트레스력을 이용하여 조립할 수도 있다. 도 5 및 도 7에 도시된 바와 같이, 하부 슬래브(130)의 상면(140)에 제1 하부 슬래브(132)와 제1 하부 슬래브(132) 사이를 움직이지 않도록 결합하거나 제1 하부 슬래브(132)와 제2 하부 슬래브(134) 사이를 움직이지 않도록 결합시키기 위한 제2 결합수단(144)이 구비되게 하고, 제1 하부 슬래브(132)와 제1 하부 슬래브(132)를 서로 이웃하게 설치하고 제1 하부 슬래브(132)와 제2 하부 슬래브(134)를 서로 이웃하게 설치한 상태에서 제2 결합수단(144)에 볼트, 강선, 강봉, 강관 등을 삽입하여 서로 견고하게 결합시킬 수 있다. 제1 하부 슬래브(132)와 제1 하부 슬래브(132) 사이 또는 제1 하부 슬래브(132)와 제2 하부 슬래브(134) 사이를 결합하는 다른 방법으로서, 서로 이웃하는 하부 슬래브(130) 사이를 도 6 및 도 8에 도시된 바와 같이 철근(146a)으로 고정하고 그 사이에 몰탈을 채워 하부 슬래브(130)의 유동을 방지하면서 견고하게 결합시킬 수도 있다. 상기 몰탈을 채우기 이전에 지반의 부등침하, 프리스트레스력에 의한 응력집중으로 발생될 수 있는 파손, 누수, 방수 등을 완벽하게 처리할 수 있도록 인장강도 2MPa 이상, 신율 400% 이상 및 부착강도 2MPa 이상의 성능을 가지는 우레탄-실리콘계 폴리머 채움재를 이용하여 실링하는 것이 바람직하다.The lower slabs 130 installed may be assembled using a prestressing force. As shown in Figures 5 and 7, the first lower slab 132 and the first lower slab 132 are movably coupled to the upper surface 140 of the lower slab 130, or the first lower slab 132 The first lower slab 132 and the first lower slab 132 are disposed adjacent to each other and the first lower slab 132 and the first lower slab 132 are disposed adjacent to each other, A bolt, a steel wire, a steel bar, a steel pipe, or the like may be inserted into the second joining means 144 in a state where the first lower slab 132 and the second lower slab 134 are adjacent to each other. As an alternative method of joining between the first lower slab 132 and the first lower slab 132 or between the first lower slab 132 and the second lower slab 134, As shown in FIGS. 6 and 8, it is also possible to securely connect the lower slab 130 while preventing the flow of the lower slab 130 by fixing the slab 146a with a mortar therebetween. A tensile strength of not less than 2 MPa, a elongation of not less than 400%, and an adhesion strength of not less than 2 MPa so as to completely treat breakage, water leakage and waterproofing which may be caused by uneven settlement of the ground and stress concentration by the prestress force before filling the mortar It is preferable to perform sealing by using a urethane-silicone-based polymer filler having a low melting point.

상기 하부 슬래브(130)와 결합되어 고정되고 상기 우수 침투형 상부 슬래브(110)를 지지하기 위한 기둥(150)을 설치한다. And a column 150 fixedly coupled to the lower slab 130 and supporting the superior permeable upper slab 110 is installed.

기둥(150)의 지지대(154)에 구비된 삽입홈을 하부 슬래브(130)의 제2 돌출부(136)에 끼워서 기둥(150)을 설치할 수 있다. 지지대(154)에 구비된 삽입홈에는 4개의 제2 돌출부(136)가 삽입될 수 있고, 4개의 제2 돌출부(136)가 지지대(154)에 구비된 삽입홈에 삽입되는 경우에 4개의 하부 슬래브(130)가 하나의 기둥(150)에 결합되는 형태를 갖게 된다. The column 150 can be installed by inserting the insertion groove provided in the support base 154 of the column 150 into the second projection 136 of the lower slab 130. [ Four second projections 136 can be inserted into the insertion groove provided in the support member 154 and four second projections 136 can be inserted into the insertion groove provided in the support member 154, So that the slab 130 is coupled to one column 150.

기둥(150)에 지지대(154)가 구비되지 않는 경에는, 도 11 및 도 12에 도시된 바와 같은 철근(158b)과 도 6 및 도 8에 도시된 바와 같은 하부 슬래브(130)의 철근(146a)을 서로 결합시키고, 기둥(150)과 하부 슬래브(130) 사이에 결합된 철근에 몰탈을 채워 기둥(150)과 하부 슬래브(130)를 견고하게 결합시킬 수도 있다. 상기 몰탈을 채우기 이전에 지반의 부등침하, 프리스트레스력에 의한 응력집중으로 발생될 수 있는 파손, 누수, 방수 등을 완벽하게 처리할 수 있도록 인장강도 2MPa 이상, 신율 400% 이상 및 부착강도 2MPa 이상의 성능을 가지는 우레탄-실리콘계 폴리머 채움재를 이용하여 실링하는 것이 바람직하다.In the case where the column 150 is not provided with the support rods 154, the reinforcement 158b as shown in Figs. 11 and 12 and the reinforcement 146a of the lower slab 130 as shown in Figs. 6 and 8 And the pillars 150 and the lower slab 130 may be firmly coupled to each other by filling the reinforcing bars coupled between the pillars 150 and the lower slab 130 with mortar. A tensile strength of not less than 2 MPa, a elongation of not less than 400%, and an adhesion strength of not less than 2 MPa so as to completely treat breakage, water leakage and waterproofing which may be caused by uneven settlement of the ground and stress concentration by the prestress force before filling the mortar It is preferable to perform sealing by using a urethane-silicone-based polymer filler having a low melting point.

하부 슬래브(130)의 외곽 테두리를 따라 벽체를 형성하는 측벽 슬래브(170)를 설치한다. 측벽 슬래브(170)의 받침대(172)에 구비된 철근(174a)과 하부 슬래브(130)에 구비된 철근(146b)을 서로 결합시키고, 받침대(172)와 하부 슬래브(130) 사이에 결합된 철근에 몰탈을 채워 측벽 슬래브(170)와 하부 슬래브(130)를 견고하게 결합시킬 수 있다. 상기 몰탈을 채우기 이전에 지반의 부등침하, 프리스트레스력에 의한 응력집중으로 발생될 수 있는 파손, 누수, 방수 등을 완벽하게 처리할 수 있도록 인장강도 2MPa 이상, 신율 400% 이상 및 부착강도 2MPa 이상의 성능을 가지는 우레탄-실리콘계 폴리머 채움재를 이용하여 실링하는 것이 바람직하다.A sidewall slab 170, which forms a wall along the outer rim of the lower slab 130, is installed. The reinforcing bars 174a provided on the pedestal 172 of the side wall slabs 170 and the reinforcing bars 146b provided on the lower slabs 130 are coupled to each other, The bottom wall slab 170 and the bottom slab 130 can be firmly coupled to each other. A tensile strength of not less than 2 MPa, a elongation of not less than 400%, and an adhesion strength of not less than 2 MPa so as to completely treat breakage, water leakage and waterproofing which may be caused by uneven settlement of the ground and stress concentration by the prestress force before filling the mortar It is preferable to perform sealing by using a urethane-silicone-based polymer filler having a low melting point.

측벽 슬래브(170)의 측면(140)에 측벽 슬래브(170)와 측벽 슬래브(170) 사이를 움직이지 않도록 결합시키기 위한 제3 결합수단(178)이 구비되게 하고, 측벽 슬래브(170)와 측벽 슬래브(170)를 서로 이웃하게 설치한 상태에서 제3 결합수단(1478에 볼트, 강선, 강봉, 강관 등을 삽입하여 서로 견고하게 결합시킬 수 있다.The side wall slab 170 and the side wall slab 170 are provided with a third coupling means 178 for movably coupling the side wall slab 170 and the side wall slab 170 to the side surface 140 of the side wall slab 170, A steel wire, a steel bar, a steel pipe, and the like may be inserted into the third coupling means 1478 in a state where the first and second coupling members 170 are disposed adjacent to each other.

상기 측벽 슬래브(170)와 상기 기둥(150) 상부에 우수 침투형 상부 슬래브(110)를 설치한다. 도 18은 일 예에 따른 프리캐스트 콘크리트 우수저류조를 보여주는 평면도이며, 우수 침투형 상부 슬래브(110)의 상면(120)에 구비되는 제1 결합수단(124)은 도시하지 않았다. 기둥(150)에 구비된 삽입홈(156)에 우수 침투형 상부 슬래브(110)의 제1 돌출부(116)를 끼워서 우수 침투형 상부 슬래브(110)를 설치한다. 기둥(150)에 구비된 삽입홈(156)에는 4개의 제1 돌출부(116)가 삽입될 수 있고, 4개의 제1 돌출부(116)가 삽입홈(156)에 삽입되는 경우에 4개의 우수 침투형 상부 슬래브(110)가 하나의 기둥(150)에 결합되는 형태를 갖게 된다. A superior permeable upper slab (110) is installed on the side wall slab (170) and the column (150). FIG. 18 is a plan view showing a precast concrete excellent stor- age tank according to an example, and the first joining means 124 provided on the upper surface 120 of the storm permeable upper slab 110 is not shown. The superior penetrating type upper slab 110 is installed by inserting the first protrusion 116 of the superior permeable upper slab 110 into the insertion groove 156 provided in the column 150. Four first protrusions 116 can be inserted into the insertion groove 156 provided in the column 150 and four first penetrations 116 can be inserted into the insertion groove 156 when four first protrusions 116 are inserted into the insertion groove 156. [ The upper slab 110 is coupled to the pillar 150.

우수 침투형 상부 슬래브(110)의 상면(120)에 제1 상부 슬래브(112)와 제1 상부 슬래브(112) 사이를 움직이지 않도록 결합하거나 제1 상부 슬래브(112)와 제2 상부 슬래브(114) 사이를 움직이지 않도록 결합시키기 위한 제1 결합수단(124)이 구비되게 하고, 제1 상부 슬래브(112)와 제1 상부 슬래브(112)를 서로 이웃하게 설치하고 제1 상부 슬래브(112)와 제2 상부 슬래브(114)를 서로 이웃하게 설치한 상태에서 제1 결합수단(124)에 볼트, 강선, 강봉, 강관 등을 삽입하여 서로 견고하게 결합시킬 수 있다. The first upper slab 112 and the second upper slab 112 are coupled to each other so that they do not move between the first upper slab 112 and the first upper slab 112 on the upper surface 120 of the permeable upper slab 110, The first upper slab 112 and the first upper slab 112 are disposed adjacent to each other and the first upper slab 112 and the first upper slab 112 are disposed adjacent to each other. A bolt, a steel wire, a steel bar, a steel pipe, or the like may be inserted into the first joining means 124 in a state where the second upper slabs 114 are adjacent to each other.

측벽 슬래브(170)의 상부에는 우수 침투형 상부 슬래브(110)와의 결합을 견고하게 하기 위하여 몰탈을 치기 위한 걸림턱(176)이 구비될 수 있는데, 측벽 슬래브(170)의 상부에서 돌출된 철근(174b)과 우수 침투형 상부 슬래브(110)에서 돌출된 철근(126)을 서로 결합시키고, 측벽 슬래브(170)와 우수 침투형 상부 슬래브(110) 사이에 결합된 철근에 몰탈을 채워 측벽 슬래브(170)와 우수 침투형 상부 슬래브(110)를 견고하게 결합시킬 수도 있다. 상기 몰탈을 채우기 이전에 지반의 부등침하, 프리스트레스력에 의한 응력집중으로 발생될 수 있는 파손, 누수, 방수 등을 완벽하게 처리할 수 있도록 인장강도 2MPa 이상, 신율 400% 이상 및 부착강도 2MPa 이상의 성능을 가지는 우레탄-실리콘계 폴리머 채움재를 이용하여 실링하는 것이 바람직하다.An upper portion of the sidewall slab 170 may be provided with a retaining jaw 176 for striking the mortar to secure engagement with the superior permeable upper slab 110, 174b and the reinforcing bars 126 protruding from the storm permeable upper slab 110 to each other and filling the reinforcing bars coupled between the side wall slabs 170 and the storm permeable upper slabs 110 to form side wall slabs 170 And the superior permeable upper slab 110 may be firmly coupled. A tensile strength of not less than 2 MPa, a elongation of not less than 400%, and an adhesion strength of not less than 2 MPa so as to completely treat breakage, water leakage and waterproofing which may be caused by uneven settlement of the ground and stress concentration by the prestress force before filling the mortar It is preferable to perform sealing by using a urethane-silicone-based polymer filler having a low melting point.

이하에서, 본 발명의 바람직한 실시예에 따른 우수 침투형 상부 슬래브용 조성물을 더욱 구체적으로 설명한다. Hereinafter, a composition for a superior permeation type upper slab according to a preferred embodiment of the present invention will be described in more detail.

본 발명의 바람직한 실시예에 따른 우수 침투형 상부 슬래브용 조성물은 시멘트계 결합재 3∼40중량%, 보투수성 결합재 0.01∼15중량%, 잔골재 45∼90중량%, 굵은골재 5∼40중량% 및 물 0.1∼15중량%를 포함한다.The composition for an upper penetration type upper slab according to a preferred embodiment of the present invention comprises 3 to 40% by weight of a cementitious binder, 0.01 to 15% by weight of a water repellent binder, 45 to 90% by weight of a fine aggregate, 5 to 40% 0.1 to 15% by weight.

골재는 잔골재와 굵은골재로 구분되며, 이하에서 잔골재는 입경이 5mm 이하인 골재이고, 굵은골재는 입경이 5mm 보다 큰 골재를 의미하는 것으로 사용한다. 상기 잔골재로는 입경이 5mm 이하인 모래 또는 쇄사를 사용한다. 또한, 상기 잔골재로는 입경이 5mm 이하인 모래와 버텀애쉬를 중량비 1:0.1∼0.6로 혼합하여 사용할 수도 있다.The aggregate is classified into a fine aggregate and a coarse aggregate. Hereinafter, the fine aggregate is an aggregate having a particle size of 5 mm or less, and the coarse aggregate means an aggregate having a particle size larger than 5 mm. As the fine aggregate, sand or fine sand having a grain size of 5 mm or less is used. As the fine aggregate, sand having a particle diameter of 5 mm or less and bottom ash may be mixed in a weight ratio of 1: 0.1 to 0.6.

상기 잔골재는 우수 침투형 상부 슬래브용 조성물에 45∼90중량% 함유되는 것이 바람직하다. 상기 굵은골재는 입경이 25mm 이하인 골재로서 상기 잔골재보다 입자의 크기가 굵은 골재를 사용한다. 상기 굵은골재는 우수 침투형 상부 슬래브용 조성물에 5∼40중량% 함유되는 것이 바람직하다. The fine aggregate is preferably contained in an amount of 45 to 90% by weight in the composition for an excellent penetration type upper slab. The coarse aggregate is an aggregate having a particle size of 25 mm or less and an aggregate having a larger particle size than the fine aggregate. The coarse aggregate is preferably contained in an amount of 5 to 40% by weight in the composition for the superior penetration type upper slab.

상기 보투수성 결합재는 조성물의 경화시간, 내구성, 투수성, 보수성, 보습성 등을 개선시키기 위하여 사용하는 것으로, 폴리메타크릴산 2-히드록시에틸, 아크릴아미드, 폴리아크릴산나트륨 및 아세틸셀롤로오스를 포함할 수 있다.The above-mentioned water-repellent binder is used for improving the curing time, durability, water permeability, water retention, moisturizing property, etc. of the composition, and includes 2-hydroxyethyl methacrylate, acrylamide, sodium polyacrylate and acetylcellulose . ≪ / RTI >

상기 보투수성 결합재는 상기 우수 침투형 상부 슬래브용 조성물에 0.01∼15중량% 함유되는 것이 바람직하다. 보투수성 결합재의 함량이 15중량%를 초과하면 우수 침투형 상부 슬래브용 조성물의 점도가 너무 높아져 작업성(슬럼프)이 떨어질 수 있고, 수화반응을 지연시켜 조기 강도 발현을 저하시킴과 동시에 가격경쟁력이 저하될 수 있으며, 상기 보투수성 결합재의 함량이 0.01중량% 미만이면 만족할만한 내구성, 투수성 등을 기대하기 어려울 수 있다.It is preferable that the water-repellent bonding material is contained in the composition for the superior penetration type upper slab in an amount of 0.01 to 15 wt%. If the content of the water-repellent binder exceeds 15% by weight, the viscosity of the composition for an excellent penetration-type upper slab becomes too high to lower the workability (slump), delay the hydration reaction and lower the early strength development, If the content of the water-repellent binding material is less than 0.01% by weight, satisfactory durability and water permeability may not be expected.

상기 보투수성 결합재는 폴리메타크릴산 2-히드록시에틸 60∼99중량%, 아크릴아미드 0.01∼25중량%, 폴리아크릴산나트륨 0.01∼25중량% 및 아세틸셀롤로오스 0.01∼15중량%를 포함할 수 있다. Wherein the water-repellent binder comprises 60-99% by weight of 2-hydroxyethyl methacrylate, 0.01-25% by weight of acrylamide, 0.01-25% by weight of sodium polyacrylate and 0.01-15% by weight of acetylcellulose .

상기 폴리메타크릴산 2-히드록시에틸은 감수 효과가 탁월하여 고강도의 성능발현, 레벨링성 개선 및 크렉 방지를 위하여 사용한다. 특히, 경화된 후의 접착강도 및 파괴강도를 증가시키며, 시멘트의 강도를 높여주고, 우수 침투형 상부 슬래브용 조성물의 주입 후의 탈착을 방지함과 동시에 내구성을 좋게 한다. 상기 폴리메타크릴산 2-히드록시에틸은 상기 보투수성 결합재에 60∼99중량% 함유되는 것이 바람직하다. 상기 폴리메타크릴산 2-히드록시에틸의 함량이 99중량%를 초과하면 성능은 우수하나 점도가 높아져 작업성 및 강도가 저하될 수 있고, 상기 폴리메타크릴산 2-히드록시에틸의 함량이 60중량% 미만이면 작업성은 좋으나 성능 개선 효과가 미흡할 수 있다.The polymethacrylic acid 2-hydroxyethyl is excellent in water reducing effect and is used for manifesting high strength performance, improving leveling property and preventing crick. In particular, the adhesive strength and fracture strength after curing are increased, the strength of the cement is increased, and the composition for the superior penetration type upper slab is prevented from being detached after injection, and at the same time, the durability is improved. The 2-hydroxyethyl polymethacrylate is preferably contained in the water-repellent binding material in an amount of 60 to 99% by weight. When the content of the 2-hydroxyethylmethacrylate exceeds 99% by weight, the performance is excellent, but the viscosity and the workability and strength may be lowered. When the content of the 2-hydroxyethylmethacrylate is 60 If it is less than 10% by weight, the workability is good, but the effect of improving the performance may be insufficient.

상기 아크릴아미드는 우수 침투형 상부 슬래브용 조성물의 점도를 개선하고 내수성을 개선하기 위하여 사용한다. 상기 아크릴아미드는 상기 보투수성 결합재에 0.01∼25중량% 함유되는 것이 바람직하다. 상기 아크릴아미드의 함량이 25중량%를 초과하면 성능은 우수하나 점도가 높아져 작업성이 저하될 수 있고, 상기 아크릴아미드의 함량이 0.01중량% 미만이면 작업성은 좋으나 성능 개선 효과가 미흡할 수 있다.The acrylamide is used for improving the viscosity and improving the water resistance of the composition for the superior penetration type upper slab. The acrylamide is preferably contained in the water-repellent binder in an amount of 0.01 to 25% by weight. If the content of acrylamide is more than 25% by weight, the performance may be improved but the viscosity may be increased and the workability may be deteriorated. If the content of acrylamide is less than 0.01% by weight, workability is good but performance improvement effect may be insufficient.

상기 폴리아크릴산나트륨이 포함되면 우수 침투형 상부 슬래브용 조성물의 점성이 커져 작업성이 우수하게 됨과 동시에 물의 흡수를 촉진하여 보수성이 개선된다. 상기 폴리아크릴산나트륨은 보투수성 결합재에 0.01∼25중량% 함유되는 것이 바람직하다. 상기 폴리아크릴산나트륨의 함량이 25중량%를 초과하면 우수 침투형 상부 슬래브용 조성물의 보수성은 개선되지만 안정성이 저하되어 우수 침투형 상부 슬래브용 조성물의 조기 강도 발현이 저하될 수 있으며, 상기 폴리아크릴산나트륨의 함량이 0.01중량% 미만이면 우수 침투형 상부 슬래브용 조성물의 보수성 개선 효과가 미약할 수 있다. When the sodium polyacrylate is included, the viscosity of the composition for an excellent permeation type upper slab is increased, so that workability is improved, and water absorption is promoted, thereby improving water retention. The sodium polyacrylate is preferably contained in the water-repellent binder in an amount of 0.01 to 25% by weight. If the content of the sodium polyacrylate exceeds 25% by weight, the water retentivity of the composition for the superior permeable upper slab is improved, but the stability is lowered, and the early strength development of the composition for the superior permeable upper slab may be deteriorated. Is less than 0.01% by weight, the effect of improving the water retentivity of the composition for superior penetration type upper slab may be weak.

상기 아세틸셀롤로오스는 연성 및 휨강도 개선을 위하여 사용한다. 상기 아세틸셀롤로오스는 상기 보투수성 결합재에 0.01∼15중량% 함유되는 것이 바람직하다. 상기 아세틸셀롤로오스의 함량이 15중량%를 초과하면 성능은 개선되지만 안정성이 저하되어 강도 발현이 저하될 수 있으며, 상기 아세틸셀롤로오스의 함량이 0.01중량% 미만이면 성능 개선 효과가 미흡할 수 있다. The acetylcellulose is used for improving ductility and flexural strength. The acetylcellulose is preferably contained in the water-repellent binding material in an amount of 0.01 to 15% by weight. If the content of acetylcellulose exceeds 15% by weight, the performance is improved but the stability is lowered and the strength development may be lowered. If the content of acetylcellulose is less than 0.01% by weight, the performance improvement effect may be insufficient have.

상기 보투수성 결합재는 내유성 및 내오존성을 개선하기 위하여 에틸렌프로필렌 고무를 더 포함할 수 있다. 상기 에틸렌프로필렌 고무는 상기 보투수성 결합재에 0.01∼5중량% 함유되는 것이 바람직하다. 상기 에틸렌프로필렌 고무의 함량이 5중량%를 초과하면 성능은 개선되지만 경제성이 저하될 수 있고, 상기 에틸렌프로필렌 고무의 함량이 0.01중량% 미만이면 내유성 및 내오존성능 개선 효과가 미흡할 수 있다. The water-repellent bonding material may further include ethylene propylene rubber to improve oil resistance and ozone resistance. The ethylene propylene rubber is preferably contained in an amount of 0.01 to 5% by weight based on the weight of the water repellent binder. If the content of the ethylene propylene rubber exceeds 5% by weight, the performance may be improved but the economical efficiency may be lowered. If the content of the ethylene propylene rubber is less than 0.01% by weight, the oil resistance and ozone performance improving effect may be insufficient.

상기 보투수성 결합재는 내굴곡성을 개선하기 위하여 폴리부타디엔 고무를 더 포함할 수 있다. 상기 폴리부타디엔 고무는 상기 보투수성 결합재에 0.01∼5중량% 함유되는 것이 바람직하다. 상기 폴리부타디엔 고무의 함량이 5중량%를 초과하면 내굴곡성은 개선되지만 점도가 높아져 작업성이 저하될 수 있고, 상기 폴리부타디엔 고무의 함량이 0.01중량% 미만이면 작업성은 좋아지나 내굴곡성 개선 효과가 미약할 수 있다. The water-repellent binding material may further include a polybutadiene rubber to improve the flexural resistance. The polybutadiene rubber is preferably contained in an amount of 0.01 to 5% by weight based on the weight of the water-repellent binding material. If the content of the polybutadiene rubber is more than 5% by weight, the bending resistance is improved but the viscosity is increased and the workability may be deteriorated. If the content of the polybutadiene rubber is less than 0.01% by weight, workability is improved but bending property is improved It can be weak.

상기 보투수성 결합재는 감수제 0.01∼5중량%를 더 포함할 수 있다. 상기 감수제는 우수 침투형 상부 슬래브용 조성물의 물-시멘트비를 감소시켜 강도 및 내구성을 개선한다. 감수제의 종류에는, 폴리카본산계, 멜라민계, 나프탈렌계 등이 있는데, 멜라민계 또는 나프탈렌계 감수제는 폴리카본산계 감수제에 비하여 강도 및 내구성의 개선 효과가 미약하고, 물-시멘트비의 저감 효과가 크지 않으며, 폴리머와의 혼화성이 나쁘다는 단점이 있다. 따라서, 본 발명의 우수 침투형 상부 슬래브용 조성물에는 폴리카본산계 감수제를 사용하는 것이 바람직하다. 상기 감수제는 상기 보투수성 결합재에 0.01∼5중량% 함유되는 것이 바람직하다.The water-repellent binder may further include 0.01 to 5% by weight of a water reducing agent. The water reducing agent improves the strength and durability by reducing the water-cement ratio of the composition for the superior penetration type upper slab. Examples of the water reducing agent include polycarboxylic acid type, melamine type, naphthalene type and the like. The melamine type or naphthalene type water reducing agent is less effective for improving the strength and durability than the polycarboxylic acid type water reducing agent, and the water- , There is a disadvantage in that the miscibility with the polymer is poor. Therefore, it is preferable to use a polycarboxylic acid-based water reducing agent in the composition for the superior penetration type upper slab of the present invention. The water reducing agent is preferably contained in the water repellent binding material in an amount of 0.01 to 5% by weight.

또한, 상기 보투수성 결합재는 소포제 0.01∼3중량%를 더 포함할 수 있다. 상기 소포제는 우수 침투형 상부 슬래브용 조성물의 연행공기의 발생으로 인한 공기량의 증가를 감소시키기 위하여 첨가되는 것으로, 알콜계 소포제, 실리콘계 소포제, 지방산계 소포제, 오일계 소포제, 에스테르계 소포제, 옥시알킬렌계 소포제 등을 단독으로 또는 혼합하여 사용할 수 있으나, 이에 제한되는 것은 아니며, 당 업계에서 통상적으로 사용되는 종류가 사용될 수도 있다. 상기 실리콘계 소포제로는 디메틸실리콘유, 폴리오가노실록산, 플루오로실리콘유 등을 사용할 수 있다. 상기 지방산계 소포제로는 스테아린산, 올레인산 등을 사용할 수 있다. 상기 오일계 소포제로는 등유, 동식물유, 피마자유 등을 사용할 수 있다. 상기 에스테르계 소포제로는 솔리톨트리올레이트, 글리세롤모노리시놀레이트 등을 사용할 수 있다. 상기 옥시알킬렌계 소포제로는 폴리옥시알킬렌, 아세틸렌에테르류, 폴리옥시알킬렌지방산에스테르, 폴리옥시알킬렌알킬아민 등을 사용할 수 있다. 상기 알콜계 소포제로는 글리콜(glycol) 등을 사용할 수 있다. 상기 소포제는 상기 보투수성 결합재에 0.01∼3중량% 함유되는 것이 바람직하다. In addition, the water-repellent binder may further include 0.01 to 3% by weight of an antifoaming agent. The antifoaming agent is added to reduce the increase in the amount of air due to the generation of entrained air of the composition for the superior permeation type upper slab. The antifoaming agent may be an alcohol type antifoaming agent, a silicone type antifoaming agent, a fatty acid type antifoaming agent, an oil type antifoaming agent, Antifoaming agents, and the like may be used alone or in combination, but the present invention is not limited thereto, and a kind commonly used in the art may be used. Examples of the silicone defoaming agent include dimethyl silicone oil, polyorganosiloxane, and fluorosilicone oil. Examples of the fatty acid defoaming agent include stearic acid and oleic acid. As the oil defoamer, kerosene, animal or plant oil, castor oil, etc. may be used. As the ester type antifoaming agent, solitol trioleate, glycerol monoricinolate and the like can be used. Examples of the oxyalkylene antifoaming agents include polyoxyalkylene, acetylene ethers, polyoxyalkylene dihalogen esters, polyoxyalkylene alkylamines, and the like. As the alcohol defoaming agent, glycol or the like may be used. It is preferable that the antifoaming agent is contained in an amount of 0.01 to 3% by weight in the water-repellent binder.

상기 시멘트계 결합재는 우수 침투형 상부 슬래브용 조성물에 3∼40중량% 함유되는 것이 바람직하다. 상기 시멘트계 결합재는 보통 포틀랜드 시멘트 30∼90중량%, 석고 0.1∼20중량%, 알루미나시멘트 0.1∼20중량%, 플라이애쉬 1∼20중량%, 메타카올린 1∼20중량% 및 고로슬래그 5∼30중량%를 포함할 수 있다. 상기 시멘트계 결합재는 투수성, 강도, 내구성 등이 우수하다.It is preferable that the cementitious binder is contained in the composition for superior penetration type upper slab in an amount of 3 to 40% by weight. The cementitious binder is usually composed of 30 to 90 wt% of Portland cement, 0.1 to 20 wt% of gypsum, 0.1 to 20 wt% of alumina cement, 1 to 20 wt% of fly ash, 1 to 20 wt% of meta kaolin, %. ≪ / RTI > The cementitious binder is excellent in water permeability, strength and durability.

상기 보통 포틀랜드 시멘트는 KS에 규정된 것을 사용하는 것이 바람직하다. 상기 보통 포틀랜드 시멘트는 상기 시멘트계 결합재에 30∼90중량% 함유되는 것이 바람직하다. 상기 보통 포틀랜드 시멘트 함량이 30중량% 미만일 경우 작업성, 강도 및 내구성은 개선되나 건조수축 및 경제성이 떨어질 수 있고, 상기 보통 포틀랜드 시멘트의 함량이 90중량%를 초과하는 경우에는 건조수축은 적어지나 강도 및 내구성이 저하될 수 있다. It is preferable to use the ordinary Portland cement specified in KS. The ordinary Portland cement is preferably contained in the cement based binder in an amount of 30 to 90% by weight. If the content of the ordinary Portland cement is less than 30% by weight, the workability, strength and durability are improved but drying shrinkage and economic efficiency may be deteriorated. When the content of the ordinary Portland cement is more than 90% by weight, And durability may be lowered.

상기 석고는 무수석고, 이수석고 및 반수석고 중에서 어떠한 것도 가능하나, 무수석고를 사용하는 것이 바람직하며, 무수석고가 초기응결시간이 짧아 조기강도 발현에 유리하기 때문이다. 상기 석고는 상기 시멘트계 결합재에 0.1∼20중량% 함유되는 것이 바람직하다. 상기 석고의 중량비가 증가하면 빠른 경화특성을 나타내며, 상기 석고의 함량이 0.1중량% 미만일 경우 조기 강도 발현이 미약할 수 있고, 상기 석고의 함량이 20중량%를 초과할 경우에는 빠른 경화 특성으로 인해 좋은 물성을 얻을 수 있으나 작업성이 떨어지고 내구성이 저하될 수 있다. The gypsum can be any of anhydrous gypsum, anthracite and semi-gypsum plaster, but it is preferable to use anhydrous gypsum because anhydrite gypsum has a short initial coagulation time and is advantageous in expressing early strength. The gypsum is preferably contained in the cement based binder in an amount of 0.1 to 20% by weight. When the weight ratio of the gypsum is increased, rapid curing characteristics are exhibited. If the content of the gypsum is less than 0.1 wt%, the early strength development may be insignificant. When the gypsum content exceeds 20 wt% Good physical properties can be obtained, but workability is poor and durability can be reduced.

상기 알루미나 시멘트는 보통 시멘트와 접촉시 생성되는 에트린가이트 수화물의 생성이 약 1∼3일 이내에 완료되어 안정화하므로 보통 시멘트에 일부 소량 첨가 시 시멘트 경화체의 수축을 보상하여 시멘트 경화체의 자기수축 및 건조수축으로 인하여 발생하는 균열과 내구성능 저하를 방지한다. 상기 알루미나 시멘트는 상기 시멘트계 결합재에 0.1∼20중량% 함유되는 것이 바람직하다. 상기 알루미나 시멘트의 중량비가 증가하면 빠른 경화특성을 나타내며, 상기 알루미나 시멘트의 함량이 0.1중량% 미만일 경우 강도를 개선하고 균열 발생을 억제하는 효과가 미약할 수 있고, 상기 알루미나 시멘트의 함량이 20중량%를 초과할 경우에는 빠른 경화 특성으로 인해 좋은 물성을 얻을 수 있으나 제조 원가가 높아져 경제적이지 못하다. Generally, the alumina cement is formed and stabilized within about 1 to 3 days after the formation of the ettringite hydrate, which is produced when the cement is contacted with the cement. Usually, when the cement is slightly added to the cement, the shrinkage of the cement- To prevent cracks and durability deterioration that may be caused. The alumina cement is preferably contained in the cement based binder in an amount of 0.1 to 20 wt%. If the content of the alumina cement is less than 0.1% by weight, the effect of improving the strength and suppressing cracking may be insignificant. If the content of the alumina cement is less than 20% by weight, , Good physical properties can be obtained due to fast curing characteristics, but the production cost is high and it is not economical.

상기 플라이애쉬는 잠재 수경성 특성, 장기 강도 발현 및 내구성 증진을 위하여 사용한다. 상기 플라이애쉬의 중량비가 증가하면 초기 강도는 저하되나, 장기 강도 발현 및 내구성이 증가한다. 상기 플라이애쉬는 상기 시멘트계 결합재에 1∼20중량% 함유되는 것이 바람직하다.The fly ash is used for improving latent hydraulic characteristics, long-term strength development and durability. When the weight ratio of the fly ash is increased, the initial strength is lowered, but the long-term strength development and durability are increased. The fly ash is preferably contained in the cement based binder in an amount of 1 to 20 wt%.

상기 메타카올린은 잠재 수경성 특성, 장기 강도 발현 및 내구성 증진을 위하여 사용한다. 상기 메타카올린의 중량비가 증가하면 초기 강도는 저하되나, 장기 강도 발현 및 내구성이 증가한다. 상기 메타카올린은 상기 시멘트계 결합재에 1∼20중량% 함유되는 것이 바람직하다.The meta kaolin is used for potential hydraulic properties, long-term strength development and durability enhancement. When the weight ratio of meta-kaolin is increased, initial strength is lowered, but long-term strength development and durability are increased. The meta kaolin is preferably contained in the cement based binder in an amount of 1 to 20% by weight.

상기 고로슬래그는 잠재 수경성 특성, 장기 강도 발현 및 내구성 증진을 위하여 사용한다. 상기 고로슬래그의 중량비가 증가하면 초기 강도는 저하되나, 장기 강도 발현 및 내구성이 증가한다. 상기 고로슬래그는 상기 시멘트계 결합재에 5∼30중량% 함유되는 것이 바람직하다.The blast furnace slag is used for improving latent hydraulic characteristics, long-term strength development and durability. When the weight ratio of the blast furnace slag is increased, the initial strength is lowered, but the long-term strength development and durability are increased. The blast furnace slag is preferably contained in the cement based binder in an amount of 5 to 30% by weight.

상기 시멘트계 결합재는 감수제 0.01∼5중량%를 더 포함할 수 있다. 상기 감수제는 우수 침투형 상부 슬래브용 조성물의 물-시멘트비를 감소시켜 강도 및 내구성을 개선한다. 감수제의 종류에는, 폴리카본산계, 멜라민계, 나프탈렌계 등이 있는데, 멜라민계 또는 나프탈렌계 감수제는 폴리카본산계 감수제에 비하여 강도 및 내구성의 개선 효과가 미약하고, 물-시멘트비의 저감 효과가 크지 않으며, 보투수성 결합재와의 혼화성이 나쁘다는 단점이 있다. 따라서, 본 발명에 의한 우수 침투형 상부 슬래브용 조성물에는 폴리카본산계 감수제를 사용하는 것이 바람직하다. 상기 감수제는 상기 시멘트계 결합재에 0.01∼5중량% 함유되는 것이 바람직하다. The cementitious binder may further include 0.01 to 5% by weight of a water reducing agent. The water reducing agent improves the strength and durability by reducing the water-cement ratio of the composition for the superior penetration type upper slab. Examples of the water reducing agent include polycarboxylic acid type, melamine type, naphthalene type and the like. The melamine type or naphthalene type water reducing agent is less effective for improving the strength and durability than the polycarboxylic acid type water reducing agent, and the water- , And poor compatibility with the water-repellent binder. Therefore, it is preferable to use a polycarboxylic acid-based water reducing agent in the composition for the superior penetration type upper slab of the present invention. The water reducing agent is preferably contained in the cement based binder in an amount of 0.01 to 5% by weight.

또한, 상기 시멘트계 결합재는 지연제 0.01∼5중량%를 더 포함할 수 있다. 상기 지연제는 우수 침투형 상부 슬래브용 조성물의 경화시간을 늦춰 작업성을 확보하기 위하여 사용한다. 상기 지연제로서는 시트릭산을 사용하는 것이 바람직하다. 상기 지연제는 상기 시멘트계 결합재에 0.01∼5중량% 함유되는 것이 바람직하다.In addition, the cement based binder may further contain 0.01 to 5% by weight of a retarder. The retarder is used to delay the curing time of the composition for the superior penetration type upper slab and ensure workability. As the retarder, it is preferable to use citric acid. The retarder is preferably contained in the cement based binder in an amount of 0.01 to 5% by weight.

또한, 상기 시멘트계 결합재는 촉진제 0.01∼5중량%를 더 포함할 수 있다. 상기 촉진제는 우수 침투형 상부 슬래브용 조성물의 초기 반응성을 높여 조기 강도 발현성을 개선하기 위하여 사용한다. 상기 촉진제로서는 칼슘포메이트를 사용하는 것이 바람직하다. 상기 촉진제는 상기 시멘트계 결합재에 0.01∼5중량% 함유되는 것이 바람직하다.In addition, the cement based binder may further include 0.01 to 5% by weight of an accelerator. The accelerator is used to improve early strength development by increasing the initial reactivity of the composition for superior penetration type upper slab. As the accelerator, it is preferable to use calcium formate. The accelerator is preferably contained in the cement based binder in an amount of 0.01 to 5% by weight.

상기 우수 침투형 상부 슬래브용 조성물은 상기 시멘트계 결합재, 상기 잔골재 및 상기 굵은골재가 혼합된 혼합물에 상기 물과 상기 보투수성 결합재를 혼합하여 1∼10분간 강제식 믹서로 교반하여 제조할 수 있다.
The composition for the superior permeation-type upper slab may be prepared by mixing the water and the water-repellent binding material in a mixture of the cementitious binder, the fine aggregate and the coarse aggregate, and stirring the mixture with a forced mixer for 1 to 10 minutes.

이하에서, 본 발명에 따른 실시예들을 더욱 구체적으로 제시하며, 다음에 제시하는 실시예들에 의하여 본 발명이 한정되는 것은 아니다. Hereinafter, embodiments according to the present invention will be described in more detail, but the present invention is not limited to the following embodiments.

<실시예 1>&Lt; Example 1 >

시멘트계 결합재 35중량%, 잔골재 50중량%, 굵은골재 10중량%를 강제 믹서에서 교반시킨 후, 물 1중량% 및 보투수성 결합재 4중량%를 더 혼합하고 3분간 교반하여 우수 침투형 상부 슬래브용 조성물을 제조하였다. 35% by weight of cementitious binder, 50% by weight of fine aggregate, 10% by weight of coarse aggregate were stirred in a forced mixer, and then 1% by weight of water and 4% by weight of water repellent binder were further mixed and stirred for 3 minutes, A composition was prepared.

상기 시멘트계 결합재는 보통 포틀랜드 시멘트 55중량%, 석고 5중량%, 알루미나시멘트 5중량%, 플라이애쉬 10중량%, 메타카올린 5중량%, 고로슬래그 19중량%, 지연제 0.3중량%, 감수제 0.5중량% 및 촉진제 0.2중량%를 혼합하여 사용하였다. 상기 지연제로는 시트릭산을 사용하였고, 상기 감수제로는 폴리카본산계 감수제를 사용하였으며, 상기 촉진제로는 칼슘포메이트를 사용하였다. The cementitious binder usually contains 55 wt% of Portland cement, 5 wt% of gypsum, 5 wt% of alumina cement, 10 wt% of fly ash, 5 wt% of meta kaolin, 19 wt% of blast furnace slag, 0.3 wt% And 0.2 wt% of a promoter were mixed and used. As the retarder, citric acid was used. As the water reducing agent, a polycarboxylic acid-based water reducing agent was used, and as the accelerator, calcium formate was used.

상기 보투수성 결합재로는 폴리메타크릴산 2-히드록시에틸 95중량%, 아크릴아미드 2중량%, 아세틸셀롤로오스 1중량%, 폴리아크릴산나트륨 1중량%, 감수제 0.5중량% 및 소포제 0.5중량%를 혼합하여 사용하였다. 상기 감수제로는 폴리카본산계 감수제를 사용하였고, 상기 소포제는 실리콘계 소포제를 사용하였다.
As the water-repellent binder, 95 wt% of 2-hydroxyethyl polymethacrylate, 2 wt% of acrylamide, 1 wt% of acetylcellulose, 1 wt% of sodium polyacrylate, 0.5 wt% of water reducing agent and 0.5 wt% Were mixed and used. A polycarbonate-based water reducing agent was used as the water reducing agent, and a silicone-based defoaming agent was used as the defoaming agent.

<실시예 2>&Lt; Example 2 >

시멘트계 결합재 35중량%, 잔골재 50중량%, 굵은골재 10중량%를 강제 믹서에서 교반시킨 후, 물 1중량% 및 보투수성 결합재 4.0중량%를 더 혼합하고 3분간 교반하여 우수 침투형 상부 슬래브용 조성물을 제조하였다. 35% by weight of cement based binder, 50% by weight of fine aggregate and 10% by weight of coarse aggregate were stirred in a forced mixer, and then 1% by weight of water and 4.0% by weight of water repellent binder were further mixed and stirred for 3 minutes, A composition was prepared.

상기 시멘트계 결합재는 보통 포틀랜드 시멘트 55중량%, 석고 5중량%, 알루미나시멘트 5중량%, 플라이애쉬 10중량%, 메타카올린 5중량%, 고로슬래그 19중량%, 지연제 0.3중량%, 감수제 0.5중량% 및 촉진제 0.2중량%를 혼합하여 사용하였다. 상기 지연제로는 시트릭산을 사용하였고, 상기 감수제로는 폴리카본산계 감수제를 사용하였으며, 상기 촉진제로는 칼슘포메이트를 사용하였다. The cementitious binder usually contains 55 wt% of Portland cement, 5 wt% of gypsum, 5 wt% of alumina cement, 10 wt% of fly ash, 5 wt% of meta kaolin, 19 wt% of blast furnace slag, 0.3 wt% And 0.2 wt% of a promoter were mixed and used. As the retarder, citric acid was used. As the water reducing agent, a polycarboxylic acid-based water reducing agent was used, and as the accelerator, calcium formate was used.

상기 보투수성 결합재로는 폴리메타크릴산 2-히드록시에틸 90중량%, 아크릴아미드 5중량%, 아세틸셀롤로오스 2중량%, 폴리아크릴산나트륨 2중량%, 감수제 0.5중량% 및 소포제 0.5중량%를 혼합하여 사용하였다. 상기 감수제로는 폴리카본산계 감수제를 사용하였고, 상기 소포제는 실리콘계 소포제를 사용하였다.
As the water-repellent binder, 90 wt% of 2-hydroxyethyl methacrylate, 5 wt% of acrylamide, 2 wt% of acetylcellulose, 2 wt% of sodium polyacrylate, 0.5 wt% of water reducing agent, and 0.5 wt% Were mixed and used. A polycarbonate-based water reducing agent was used as the water reducing agent, and a silicone-based defoaming agent was used as the defoaming agent.

<실시예 3>&Lt; Example 3 >

시멘트계 결합재 35중량%, 잔골재 50중량%, 굵은골재 10중량%를 강제 믹서에서 교반시킨 후, 물 1중량% 및 보투수성 결합재 4.0중량%를 더 혼합하고 3분간 교반하여 우수 침투형 상부 슬래브용 조성물을 제조하였다. 35% by weight of cement based binder, 50% by weight of fine aggregate and 10% by weight of coarse aggregate were stirred in a forced mixer. Then, 1% by weight of water and 4.0% by weight of water repellent binder were further mixed and stirred for 3 minutes, A composition was prepared.

상기 시멘트계 결합재는 보통 포틀랜드 시멘트 55중량%, 석고 5중량%, 알루미나시멘트 5중량%, 플라이애쉬 10중량%, 메타카올린 5중량%, 고로슬래그 19중량%, 지연제 0.3중량%, 감수제 0.5중량% 및 촉진제 0.2중량%를 혼합하여 사용하였다. 상기 지연제로는 시트릭산을 사용하였고, 상기 감수제로는 폴리카본산계 감수제를 사용하였으며, 상기 촉진제로는 칼슘포메이트를 사용하였다. The cementitious binder usually contains 55 wt% of Portland cement, 5 wt% of gypsum, 5 wt% of alumina cement, 10 wt% of fly ash, 5 wt% of meta kaolin, 19 wt% of blast furnace slag, 0.3 wt% And 0.2 wt% of a promoter were mixed and used. As the retarder, citric acid was used. As the water reducing agent, a polycarboxylic acid-based water reducing agent was used, and as the accelerator, calcium formate was used.

상기 보투수성 결합재로는 폴리메타크릴산 2-히드록시에틸 85중량%, 아크릴아미드 6중량%, 아세틸셀롤로오스 4중량%, 폴리아크릴산나트륨 4중량%, 감수제 0.5중량% 및 소포제 0.5중량%를 혼합하여 사용하였다. 상기 감수제로는 폴리카본산계 감수제를 사용하였고, 상기 소포제는 실리콘계 소포제를 사용하였다.
As the water-repellent binder, 85 wt% of 2-hydroxyethyl polymethacrylate, 6 wt% of acrylamide, 4 wt% of acetylcellulose, 4 wt% of sodium polyacrylate, 0.5 wt% of a water reducing agent, and 0.5 wt% Were mixed and used. A polycarbonate-based water reducing agent was used as the water reducing agent, and a silicone-based defoaming agent was used as the defoaming agent.

실시예 1 내지 실시예 3의 특성을 보다 용이하게 파악할 수 있도록 비교할 수 있는 비교예들을 제시한다. 후술하는 비교예 1 및 비교예 2는 실시예들의 특성과 단순히 비교하기 위하여 제시하는 것으로 본 발명의 선행기술이 아님을 밝혀둔다.Comparative examples that can be compared are provided to more easily grasp the characteristics of Examples 1 to 3. It is to be noted that Comparative Example 1 and Comparative Example 2, which will be described later, are presented merely for comparison with the characteristics of the embodiments, and are not the prior art of the present invention.

<비교예 1>&Lt; Comparative Example 1 &

시멘트계 결합재 35중량%, 잔골재 50중량%, 굵은골재 10중량%를 강제 믹서에서 교반시킨 후, 물 5중량%를 더 혼합하고 3분간 교반하여 보통 시멘트 콘크리트 조성물을 제조하였다.
35 wt% of the cementitious binder, 50 wt% of the fine aggregate, and 10 wt% of the coarse aggregate were stirred in a forced mixer, and then 5 wt% of water was further mixed and stirred for 3 minutes to prepare a normal cement concrete composition.

<비교예 2>&Lt; Comparative Example 2 &

시멘트계 결합재 35중량%, 잔골재 50중량%, 굵은골재 10중량%를 강제 믹서에서 교반시킨 후, 물 1.0중량% 및 폴리메타크릴산 2-히드록시에틸 4.0중량%를 더 혼합하고 3분간 교반하여 폴리머 시멘트 콘크리트 조성물을 제조하였다.
35% by weight of cement based binder, 50% by weight of fine aggregate, and 10% by weight of coarse aggregate were stirred in a forced mixer. Then, 1.0% by weight of water and 4.0% by weight of 2-hydroxyethylmethyl methacrylate were further mixed and stirred for 3 minutes, Cement concrete composition was prepared.

아래의 시험예들은 본 발명에 따른 실시예 1 내지 실시예 3의 특성을 보다 용이하게 파악할 수 있도록 본 발명에 따른 실시예들과 비교예 1 및 비교예 2의 특성을 비교한 시험결과들을 나타낸 것이다.The following test examples show test results comparing characteristics of the embodiments of the present invention with those of Comparative Example 1 and Comparative Example 2 in order to more easily grasp the characteristics of Embodiments 1 to 3 according to the present invention .

<시험예1>&Lt; Test Example 1 >

조성물들의 양생은 일반적인 증기양생 후 재령 7일의 물리적 특성을 비교하기 위하여, 실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물과 비교예 1 및 비교예 2에 따라 제조된 조성물들 각각의 강도를 시험하여 표 1과 같은 결과를 얻었다. 각각 KS F 2405, KS F 2408 및 KS F 2423에 규정한 방법에 따라 시험을 실시하였다. The curing of the compositions was carried out in the same manner as in Example 1 except that the composition for the superior permeable upper slab prepared according to Examples 1 to 3 and the composition prepared according to Comparative Example 1 and Comparative Example 2 The results are shown in Table 1. The test was carried out according to the methods specified in KS F 2405, KS F 2408 and KS F 2423, respectively.

구분division 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 휨강도(kgf/cm²)Bending strength (kgf / cm ² ) 6060 6363 6767 4040 5252 압축강도(kgf/cm²)Compressive strength (kgf / cm ² ) 410410 440440 449449 385385 395395 인장강도(kgf/cm²)Tensile strength (kgf / cm ² ) 3333 3535 3737 2222 2525

표 1에 나타난 바와 같이, 실시예 1, 실시예 2 및 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물의 휨, 압축 및 인장강도는 비교예 1 및 비교예 2에 따라 제조된 조성물보다 월등히 높았다. 본 발명에 따라 제조된 우수 침투형 상부 슬래브용 조성물이 비교예 1 및 비교예 2에 따라 제조된 조성물과 비교하여 강도 면에서 월등히 우수함을 확인할 수 있었다.
As shown in Table 1, the flexural, compressive and tensile strengths of the compositions for superior penetration type upper slabs prepared according to Examples 1, 2 and 3 were higher than those of the compositions prepared according to Comparative Example 1 and Comparative Example 2 Respectively. It was confirmed that the composition for the superior penetration type upper slab prepared according to the present invention is much superior in strength to the composition prepared according to Comparative Example 1 and Comparative Example 2.

<시험예 2>&Lt; Test Example 2 &

실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물과 비교예 1 및 비교예 2에 따라 제조된 조성물을 KS F 2424(콘크리트의 길이변화 시험방법)에 의하여 건조수축율을 측정하였으며, 그 결과를 하기 표 2에 나타내었다.The composition for the superior penetration type upper slab prepared according to Examples 1 to 3 and the composition prepared according to Comparative Example 1 and Comparative Example 2 were measured by KS F 2424 (length change test method for concrete) , And the results are shown in Table 2 below.

구분division 실시예1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 건조수축율(%)Dry shrinkage (%) 0.070.07 0.050.05 0.040.04 0.120.12 0.090.09

표 2에서와 같이, 실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물이 비교예 1 및 비교예 2에 따라 제조된 조성물에 비하여 건조수축량이 감소되어 수축 저감 효과가 있음을 확인할 수 있었다.
As shown in Table 2, the composition for the superior penetration type upper slab prepared according to Examples 1 to 3 had a shrinkage reduction effect due to a decrease in the amount of drying shrinkage as compared with the composition prepared according to Comparative Example 1 and Comparative Example 2 I could confirm.

<시험예 3>&Lt; Test Example 3 >

표 3은 실시예 1, 실시예 2 및 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물과 비교예 1 및 비교예 2에 따라 제조된 조성물에 대하여 JIS A 1171에 규정한 방법에 따라 염화물이온 침투깊이의 측정결과를 나타낸 것이다. Table 3 shows the compositions of the superior permeation type upper slabs prepared according to Examples 1, 2 and 3 and the compositions prepared according to Comparative Examples 1 and 2 according to the method defined in JIS A 1171, The results of measurement of the ion penetration depth are shown.

구분division 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 염화물이온 침투깊이(mm)Chloride ion penetration depth (mm) 1.01.0 0.90.9 0.70.7 1.91.9 1.51.5

위의 표 3에서와 같이, 실시예 1, 실시예 2 및 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물이 비교예 1 및 비교예 2에 따라 제조된 조성물보다 염화물 이온 침투 깊이가 적게 나타나 염해에 대한 저항성이 높음을 확인할 수 있었다.
As shown in the above Table 3, the compositions for storm permeability upper slabs prepared according to Examples 1, 2 and 3 had lower chloride ion penetration depths than the compositions prepared according to Comparative Examples 1 and 2 And it was confirmed that it is highly resistant to salt attack.

<시험예 4><Test Example 4>

실시예 1, 실시예 2 및 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물과 비교예 1 및 비교예 2에 따라 제조된 조성물의 시험체에 대하여 JIS A 1171(폴리머 시멘트 모르타르의 시험방법)에 규정한 방법에 따라 중성화 침투깊이의 측정결과를 표 4에 나타내었다.JIS A 1171 (Test Method of Polymer Cement Mortar) was applied to the test specimen of the composition for superior penetration type upper slab prepared in Example 1, Example 2 and Example 3 and the composition prepared in Comparative Example 1 and Comparative Example 2, Table 4 shows the measurement result of the depth of neutralization penetration according to the method specified in Table 4.

구분division 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 중성화 깊이(mm)Neutralization depth (mm) 0.40.4 0.30.3 0.20.2 1.01.0 0.70.7

위의 표 4에서와 같이, 실시예 1, 실시예 2 및 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물이 비교예 1 및 비교예 2에 따라 제조된 조성물보다 중성화 침투 깊이가 적게 나타나 중성화에 대한 저항성이 높음을 확인할 수 있었다.
As shown in Table 4 above, the composition for the superior permeation type upper slab prepared according to Examples 1, 2, and 3 showed less neutrality penetration depth than the composition prepared according to Comparative Example 1 and Comparative Example 2 It was confirmed that the resistance to neutralization was high.

<시험예 5>&Lt; Test Example 5 >

본 발명에 의한 우수 침투형 상부 슬래브용 조성물의 투수성능을 확인하기 위하여, 실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물과 비교예 1 및 비교예 2에 따라 제조된 조성물로 φ10×10cm의 콘크리트 공시체를 제작하였고, KS F 2322(흙의 정수위 투수시험방법)에 의하여 재령 28일에 투수계수를 측정하였으며, 그 결과를 하기 표 5에 나타내었다. In order to confirm the permeability of the composition for the superior penetration type upper slab according to the present invention, the composition for the superior permeation type upper slab prepared according to Examples 1 to 3 and the composition prepared according to Comparative Example 1 and Comparative Example 2 And the permeability coefficient was measured on the 28th day by KS F 2322 (method of pure water permeability test of soil). The results are shown in Table 5 below.

실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 투수계수(cm/sec)Permeability Coefficient (cm / sec) 0.300.30 0.310.31 0.320.32 0.150.15 0.180.18

표 5에서와 같이, 실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물이 비교예 1 및 비교예 2에 따라 제조된 조성물에 비하여 투수계수가 월등히 높음을 알 수 있다.
As shown in Table 5, it can be seen that the composition for the superior penetration type upper slab prepared according to Examples 1 to 3 is much higher than the composition prepared according to Comparative Example 1 and Comparative Example 2.

<시험예 6>&Lt; Test Example 6 >

표 6은 실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물과 비교예 1 내지 비교예 2에 따라 제조된 조성물에 대하여, KS F 2456에 규정한 방법에 따라 동결융해저항성 시험의 측정 결과를 나타낸 것이다. 동결융해는 콘크리트에 흡수된 수분이 결빙되고 녹는 것을 말하는 것으로, 동결융해가 반복되면 콘크리트 조직에 미세한 균열이 발생하게 되어 내구성이 저하되는 문제가 발생하게 된다.Table 6 shows the freeze-thaw resistance resistance test according to the method defined in KS F 2456 for the composition for the superior penetration type upper slab prepared according to Examples 1 to 3 and the composition prepared according to Comparative Examples 1 to 2 . Fig. Freezing and thawing means that the water absorbed in the concrete is frozen and melted. When freezing and thawing is repeated, fine cracks are generated in the concrete structure, and the durability is lowered.

표 6은 동결융해 저항성 시험에 따른 각각의 실시예들 및 비교예들의 내구성 지수를 표시한 것이다.Table 6 shows the durability indices of the respective examples and comparative examples according to the freeze-thaw resistance test.

구분division 실시예1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 내구성 지수Durability index 9090 9191 9292 6060 8686

표 6에서와 같이, 실시예 1 내지 실시예 3에 따라 제조된 우수 침투형 상부 슬래브용 조성물이 비교예 1 및 비교예 2에 따라 제조된 조성물에 비하여 내구성 지수가 월등히 높으므로, 내구성이 향상된 것을 알 수 있다.
As shown in Table 6, the durability of the composition for superior penetration type upper slabs prepared according to Examples 1 to 3 was much higher than that of the composition prepared according to Comparative Example 1 and Comparative Example 2, Able to know.

이상, 본 발명의 바람직한 실시예를 들어 상세하게 설명하였으나, 본 발명은 상기 실시예에 한정되는 것은 아니며, 본 발명의 기술적 사상의 범위 내에서 당 분야에서 통상의 지식을 가진 자에 의하여 여러 가지 변형이 가능하다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, This is possible.

110: 우수 침투형 상부 슬래브 112: 제1 상부 슬래브
114: 제2 상부 슬래브 116: 제1 돌출부
118: 제1 요홈부 120: 우수 침투형 상부 슬래브의 상면
122: 우수 침투형 상부 슬래브의 하면
124: 제1 결합수단
126, 146a, 146b, 158a, 158b, 174a, 174b: 철근
130: 하부 슬래브 132: 제1 하부 슬래브
134: 제2 하부 슬래브 136: 제2 돌출부
138: 제2 요홈부 140: 하부 슬래브의 상면
142: 하부 슬래브의 하면 144: 제2 결합수단
150: 기둥 152: 몸체
154: 지지대 156: 삽입홈
170: 측벽 슬래브 172: 받침대
176: 걸림턱 178: 제3 결합수단110: Excellent permeable upper slab 112: First upper slab
114: second upper slab 116: first protrusion
118: first recessed portion 120: upper surface of the superior penetrating type upper slab
122: bottom of the superior permeable upper slab
124: first engaging means
126, 146a, 146b, 158a, 158b, 174a, 174b:
130: lower slab 132: first lower slab
134: second lower slab 136: second projection
138: second recessed portion 140: upper surface of the lower slab
142: lower surface of the lower slab 144: second coupling means
150: column 152: body
154: support rod 156: insertion groove
170: side wall slab 172: pedestal
176: Retaining jaw 178: Third engaging means

Claims (27)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 프리캐스트 콘크리트 우수저류조의 우수 침투형 상부 슬래브를 형성하기 위한 조성물로서,
시멘트계 결합재 3∼40중량%, 보투수성 결합재 0.01∼15중량%, 잔골재 45∼90중량%, 굵은골재 5∼40중량% 및 물 0.1∼15중량%를 포함하며,
상기 보투수성 결합재는 폴리메타크릴산 2-히드록시에틸 60∼99중량%, 아크릴아미드 0.01∼25중량%, 폴리아크릴산나트륨 0.01∼25중량%, 에틸렌프로필렌 고무 0.01∼5중량%, 폴리부타디엔 고무 0.01∼5중량% 및 아세틸셀롤로오스 0.01∼15중량%를 포함하고,
상기 시멘트계 결합재는 보통 포틀랜드 시멘트 30∼90중량%, 석고 0.1∼20중량%, 알루미나시멘트 0.1∼20중량%, 플라이애쉬 1∼20중량%, 메타카올린 1∼20중량%, 시트릭산 0.01∼5중량%, 칼슘포메이트 0.01∼5중량% 및 고로슬래그 5∼30중량%를 포함하는 것을 특징으로 하는 우수 침투형 상부 슬래브용 조성물.
A composition for forming an excellent permeable top slab of a precast concrete well tank,
3 to 40 wt% of a cementitious binder, 0.01 to 15 wt% of a water-repellent binder, 45 to 90 wt% of a fine aggregate, 5 to 40 wt% of a coarse aggregate, and 0.1 to 15 wt%
Wherein the water-repellent binder is a mixture of 60-99 wt% of 2-hydroxyethyl methacrylate, 0.01-25 wt% of acrylamide, 0.01-25 wt% of sodium polyacrylate, 0.01-5 wt% of ethylene propylene rubber, 0.01 to 5% by weight and acetylcellulose 0.01 to 15% by weight,
The cementitious binder is usually composed of 30 to 90 wt% of Portland cement, 0.1 to 20 wt% of gypsum, 0.1 to 20 wt% of alumina cement, 1 to 20 wt% of fly ash, 1 to 20 wt% of meta kaolin, 0.01 to 5% by weight of calcium formate, and 5 to 30% by weight of blast furnace slag.
삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 프리캐스트 콘크리트 우수저류조를 시공하기 위한 방법으로서,
프리캐스트 콘크리트 우수저류조를 설치할 하부 기초를 형성하기 위하여 골재를 포설하고 다짐한 후, 상부에 모래를 포설하고 다짐하여 하부 기초를 준비하는 단계;
상기 하부 기초 상부에 린콘크리트를 타설하는 단계;
상기 린콘크리트가 타설된 상부에 우수저류조의 바닥면을 형성하면서 우수가 하부로 빠져나가지 못하게 하여 우수를 우수저류조 내에 가두기 위한 하부 슬래브를 설치하거나 현장에서 몰탈을 타설하여 하부 슬래브를 형성하는 단계;
우수 침투형 상부 슬래브를 지지하기 위한 기둥을 설치하고 상기 하부 슬래브와 결합하여 고정하는 단계;
상기 하부 슬래브의 외곽 테두리를 따라 벽체를 형성하는 측벽 슬래브를 설치하는 단계; 및
상기 측벽 슬래브와 상기 기둥 상부에 제8항에 기재된 우수 침투형 상부 슬래브용 조성물을 이용하여 형성한 우수 침투형 상부 슬래브를 설치하는 단계를 포함하며,
상기 우수 침투형 상부 슬래브 하면의 네 모퉁이에 구비된 제1 돌출부를 상기 기둥 상부에 구비된 삽입홈으로 삽입하여 고정하고,
상기 기둥 상부에 구비된 삽입홈에 4개의 제1 돌출부를 삽입하고,
상기 우수 침투형 상부 슬래브의 네 모퉁이에 제1 요홈부가 구비되게 하고, 상기 제1 요홈부로 둘러싸인 영역에 몰탈을 주입하여 서로 이웃하는 우수 침투형 상부 슬래브 및 상기 기둥을 결합하며,
4개의 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈에 삽입됨에 따라 4개의 우수 침투형 상부 슬래브가 하나의 기둥에 결합되는 형태를 갖는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.
A method for constructing a precast concrete excellent storeroom,
Precast concrete concrete pouring and aggregating the aggregate to form a bottom foundation to be installed in the storage pond, preparing and sanding the upper part to prepare a lower foundation;
Placing lean concrete over the lower foundation;
Forming a bottom slab on an upper portion in which the lean concrete is laid and a bottom slab to prevent the slab from escaping into the bottom of the bottom tank;
Installing a column for supporting the superior permeable upper slab and fixing it in combination with the lower slab;
Installing a side wall slab to form a wall along an outer rim of the lower slab; And
And a step of installing a superior permeable upper slab formed by using the composition for the superior permeable upper slab according to claim 8 on the side wall slab and the column upper part,
A first protrusion provided at four corners of the lower surface of the superior permeable upper slab is inserted and fixed in an insertion groove provided in the upper portion of the column,
Four first protrusions are inserted into the insertion groove provided in the upper portion of the column,
A first recess is formed at four corners of the storm permeable upper slab and a mortar is injected into a region surrounded by the first recess to join the adjacent storm permeable upper slab and the column,
And the four first protrusions are inserted into the insertion grooves formed in the upper portion of the column, so that four excellent penetration type upper slabs are coupled to one column.
제14항에 있어서, 상기 제1 요홈부는 상부에서 하부로 향하는 방향을 따라 상기 우수 침투형 상부 슬래브의 상면부터 상기 제1 돌출부의 저면까지 구비되게 하는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.
15. The method as claimed in claim 14, wherein the first concave portion is provided from the upper surface of the superior permeable upper slab to the lower surface of the first protruding portion along a direction from the upper portion to the lower portion .
제14항에 있어서, 상기 우수 침투형 상부 슬래브는 제1 상부 슬래브와 제2 상부 슬래브를 포함하고,
상기 우수 침투형 상부 슬래브의 상면에 제1 상부 슬래브와 제1 상부 슬래브 사이를 움직이지 않도록 결합하거나 제1 상부 슬래브와 제2 상부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비되게 하며,
제1 상부 슬래브와 제1 상부 슬래브를 서로 이웃하게 설치하고 제1 상부 슬래브와 제2 상부 슬래브를 서로 이웃하게 설치한 상태에서 제1 결합수단에 볼트, 강선, 강봉 또는 강관을 삽입하여 제1 상부 슬래브와 제1 상부 슬래브 사이가 결합되고 제1 상부 슬래브와 제2 상부 슬래브 사이가 결합되게 하며,
상기 측벽 슬래브의 상부에서 돌출된 철근과 상기 우수 침투형 상부 슬래브에서 돌출된 철근을 서로 결합시키고, 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브 사이에 결합된 철근에 몰탈을 채워 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브를 결합시키는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.
15. The method of claim 14, wherein the storm permeable upper slab comprises a first upper slab and a second upper slab,
A coupling means for coupling the first upper slab and the first upper slab so as not to move or engaging the first upper slab and the second upper slab so as not to move is provided on the upper surface of the storm permeable upper slab,
The first upper slab and the first upper slab are disposed adjacent to each other and the first upper slab and the second upper slab are disposed adjacent to each other, and a bolt, a steel wire, a steel bar or a steel pipe is inserted into the first joining means, The slab and the first upper slab are engaged and the first upper slab and the second upper slab are engaged,
And a reinforcing bar protruding from an upper portion of the side wall slab and a reinforcing bar protruding from the superior penetrating upper slab are coupled to each other to fill the reinforcing bars coupled between the side wall slab and the superior penetrating upper slab, Wherein the permeable upper slab is joined to the pre-cast concrete upper slab.
제14항에 있어서, 상기 하부 슬래브 상면의 네 모퉁이에 제2 돌출부가 구비되게 하고, 상기 제2 돌출부를 기둥의 지지대 하부에 구비된 삽입홈으로 삽입하여 고정하고,
상기 기둥의 지지대 하부에 구비된 삽입홈에 4개의 제2 돌출부를 삽입하며,
4개의 제2 돌출부가 상기 기둥의 지지대 하부에 구비된 삽입홈에 삽입됨에 따라 4개의 하부 슬래브가 하나의 기둥에 결합되는 형태를 갖는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.
15. The method of claim 14, further comprising: providing a second projection at four corners of the upper surface of the lower slab, inserting and fixing the second projection into an insertion groove provided below the support of the column,
Four second projections are inserted into an insertion groove provided in a lower portion of the support of the column,
And the four second projections are inserted into the insertion grooves formed in the lower portion of the support of the column so that the four lower slabs are coupled to the one column.
제14항에 있어서, 상기 기둥의 하부에 돌출된 철근과 상기 하부 슬래브에 돌출된 철근을 서로 결합시키고,
상기 기둥과 상기 하부 슬래브 사이에 결합된 철근에 몰탈을 채워 상기 기둥과 상기 하부 슬래브를 결합시키는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.
15. The method of claim 14, wherein the reinforcing bars projecting from the lower portion of the column and the reinforcing bars projecting from the lower slab are coupled to each other,
Wherein the mortar is inserted into the reinforcing bars coupled between the column and the lower slab, thereby joining the pillars to the lower slab.
제14항에 있어서, 상기 하부 슬래브는 우수저류조의 하부 중앙부에 설치되는 제1 하부 슬래브와 우수저류조의 하부 외측부에 설치되는 제2 하부 슬래브를 포함하고,
상기 하부 슬래브의 상면에 제1 하부 슬래브와 제1 하부 슬래브 사이를 움직이지 않도록 결합하거나 제1 하부 슬래브와 제2 하부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비되게 하며,
제1 하부 슬래브와 제1 하부 슬래브를 서로 이웃하게 설치하고 제1 하부 슬래브와 제2 하부 슬래브를 서로 이웃하게 설치한 상태에서 제2 결합수단에 볼트, 강선, 강봉 또는 강관을 삽입하여 제1 하부 슬래브와 제1 하부 슬래브 사이가 결합되게 하고 제1 하부 슬래브와 제2 하부 슬래브 사이가 결합되게 하는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.
15. The apparatus of claim 14, wherein the lower slab includes a first lower slab installed in a lower central portion of the upper storage tank and a second lower slab installed in a lower outer portion of the upper storage tank,
A coupling means for coupling the first lower slab and the first lower slab so as not to move or engaging the first lower slab and the second lower slab so as not to move is provided on the upper surface of the lower slab,
The first lower slab and the first lower slab are disposed adjacent to each other and the bolts, the steel wires, the steel rods, or the steel pipes are inserted into the second coupling means in a state where the first and second lower slabs are adjacent to each other, Wherein the slab and the first lower slab are engaged with each other so that the first lower slab and the second lower slab are engaged with each other.
제14항에 있어서, 상기 측벽 슬래브 하부의 일측으로 돌출된 받침대가 구비되게 하고,
상기 측벽 슬래브의 받침대에 구비된 철근과 상기 하부 슬래브에 구비된 철근을 서로 결합시키고, 상기 받침대와 하부 슬래브 사이에 결합된 철근에 몰탈을 채워 상기 측벽 슬래브와 상기 하부 슬래브를 결합시키며,
상기 측벽 슬래브의 측면에 측벽 슬래브와 측벽 슬래브 사이를 움직이지 않도록 결합시키기 위한 제3 결합수단이 구비되게 하고, 측벽 슬래브와 측벽 슬래브를 서로 이웃하게 설치한 상태에서 제3 결합수단에 볼트, 강선, 강봉 또는 강관을 삽입하여 측벽 슬래브와 측벽 슬래브 사이를 결합시키는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조의 시공방법.15. The apparatus of claim 14, further comprising a pedestal protruding from one side of the lower portion of the side wall slab,
A reinforcing bar provided on a pedestal of the side wall slab and a reinforcing bar provided on the lower slab are coupled to each other and a mortar is inserted into a reinforcing bar coupled between the pedestal and the lower slab to join the side wall slab and the lower slab,
And a third coupling means for coupling the side wall slab and the side wall slab so as not to move between the side wall slab and the side wall slab is provided on the side surface of the side wall slab. In the state where the side wall slab and the side wall slab are adjacent to each other, Wherein a steel bar or a steel pipe is inserted to join between the side wall slab and the side wall slab. 제8항에 기재된 우수 침투형 상부 슬래브용 조성물을 이용하여 형성한 우수 침투형 상부 슬래브;
우수저류조의 바닥면을 형성하면서 우수가 하부로 빠져나가지 못하게 하여 우수를 우수저류조 내에 가두기 위한 하부 슬래브;
상기 하부 슬래브와 결합되어 고정되어 있고 상기 우수 침투형 상부 슬래브를 지지하는 기둥; 및
상기 하부 슬래브의 외곽 테두리를 따라 벽체를 형성하여 상기 하부 슬래브와 상기 우수 침투형 상부 슬래브를 연결하는 측벽 슬래브를 포함하며,
상기 우수 침투형 상부 슬래브 하면의 네 모퉁이에 구비된 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈으로 삽입되어 고정되어 있고,
상기 기둥 상부에 구비된 삽입홈에는 4개의 제1 돌출부가 삽입되고, 4개의 제1 돌출부가 상기 기둥 상부에 구비된 삽입홈에 삽입됨에 따라 4개의 우수 침투형 상부 슬래브가 하나의 기둥에 결합되는 형태를 갖고,
상기 우수 침투형 상부 슬래브의 네 모퉁이에 제1 요홈부가 구비되어 있고, 상기 제1 요홈부로 둘러싸인 영역에 몰탈이 주입되어 서로 이웃하는 우수 침투형 상부 슬래브 및 상기 기둥이 결합되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.
An excellent penetration type upper slab formed by using the composition for superior penetration type upper slab according to claim 8;
A lower slab for forming a bottom surface of the stor- age tank and preventing the storm from escaping to the lower portion to confine the stor- age in the stor- age tank;
A column fixedly coupled to the lower slab and supporting the superior permeable upper slab; And
And a sidewall slab that forms a wall along an outer rim of the lower slab to connect the lower slab and the superior penetrating upper slab,
A first protrusion provided at four corners of the lower surface of the superior permeable upper slab is inserted and fixed into an insertion groove provided in the upper portion of the column,
Four first protrusions are inserted into the insertion grooves formed in the upper portion of the column, and four superior penetrating upper slabs are coupled to one column as the first protrusions are inserted into the insertion grooves formed in the upper portion of the column Shaped,
Characterized in that a first recess is provided at the four corners of the storm permeable upper slab and the mortar is injected into the region surrounded by the first recess to join the adjacent storm permeable upper slab and the pillars Cast concrete excellent storage tank.
제21항에 있어서, 상기 제1 요홈부는 상부에서 하부로 향하는 방향을 따라 상기 우수 침투형 상부 슬래브의 상면부터 상기 제1 돌출부의 저면까지 구비되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.
The precast concrete excellent storeroom according to claim 21, wherein the first concave portion is provided from an upper surface of the storm permeable upper slab to a lower surface of the first protruding portion along a direction from the upper portion to the lower portion.
제21항에 있어서, 상기 우수 침투형 상부 슬래브는 우수저류조의 상부 중앙부에 설치되는 제1 상부 슬래브와 우수저류조의 상부 외측부에 설치되는 제2 상부 슬래브를 포함하고,
상기 우수 침투형 상부 슬래브의 상면에는 제1 상부 슬래브와 제1 상부 슬래브 사이를 움직이지 않도록 결합하거나 제1 상부 슬래브와 제2 상부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비되며,
제1 상부 슬래브와 제1 상부 슬래브가 서로 이웃하게 설치되고 제1 상부 슬래브와 제2 상부 슬래브가 서로 이웃하게 설치된 상태에서 제1 결합수단에 볼트, 강선, 강봉 또는 강관이 삽입되어 제1 상부 슬래브와 제1 상부 슬래브 사이가 결합되고 제1 상부 슬래브와 제2 상부 슬래브 사이가 결합되어 있으며,
상기 측벽 슬래브의 상부에서 돌출된 철근과 상기 우수 침투형 상부 슬래브에서 돌출된 철근이 서로 결합되어 있고, 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브 사이에 결합된 철근에 몰탈이 채워져서 상기 측벽 슬래브와 상기 우수 침투형 상부 슬래브가 결합되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.
22. The method of claim 21, wherein the storm permeable upper slab includes a first upper slab installed at an upper central portion of an upper storey tank and a second upper slab installed at an upper outer side of the stor- age tank,
A top surface of the storm permeable upper slab is provided with engaging means for engaging the first upper slab and the first upper slab so as not to move or engaging the first upper slab and the second upper slab so as not to move,
A bolt, a steel wire, a steel bar or a steel pipe is inserted into the first joining means in a state where the first upper slab and the first upper slab are disposed adjacent to each other and the first upper slab and the second upper slab are adjacent to each other, Is coupled between the first upper slab and the first upper slab, and between the first upper slab and the second upper slab,
Wherein the reinforcing bars projecting from the upper portion of the side wall slab and the reinforcing bars projecting from the superior penetrating upper slab are coupled to each other and the reinforcing bars coupled between the side wall slab and the superior penetrating upper slab are filled with mortar, Characterized in that the excellent permeable upper slab is coupled to the upper surface of the pre-permeable upper slab.
제21항에 있어서, 상기 하부 슬래브 상면의 네 모퉁이에 구비된 제2 돌출부가 기둥의 지지대 하부에 구비된 삽입홈으로 삽입되어 고정되어 있고,
상기 기둥의 지지대 하부에 구비된 삽입홈에는 4개의 제2 돌출부가 삽입되고,
4개의 제2 돌출부가 상기 기둥의 지지대 하부에 구비된 삽입홈에 삽입됨에 따라 4개의 하부 슬래브가 하나의 기둥에 결합되는 형태를 갖는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.
[22] The apparatus of claim 21, wherein a second projection provided at four corners of the upper surface of the lower slab is inserted and fixed into an insertion groove provided in a lower portion of a support of the column,
Four second projections are inserted into the insertion groove provided at the lower portion of the support of the column,
Wherein the four second slabs are coupled to one column as the four second slabs are inserted into the insertion grooves provided at the lower portion of the support of the column.
제21항에 있어서, 상기 기둥의 하부에 돌출된 철근과 상기 하부 슬래브에 돌출된 철근이 서로 결합되어 있고,
상기 기둥과 상기 하부 슬래브 사이에 결합된 철근에 몰탈이 채워져서 상기 기둥과 상기 하부 슬래브가 결합되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.
[22] The method of claim 21, wherein the reinforcing bars protruding from the lower portion of the column and the reinforcing bars projecting from the lower slab are coupled to each other,
And a reinforcing bar coupled between the column and the lower slab is filled with mortar so that the column and the lower slab are coupled to each other.
제21항에 있어서, 상기 하부 슬래브는 우수저류조의 하부 중앙부에 설치되는 제1 하부 슬래브와 우수저류조의 하부 외측부에 설치되는 제2 하부 슬래브를 포함하고,
상기 하부 슬래브의 상면에는 제1 하부 슬래브와 제1 하부 슬래브 사이를 움직이지 않도록 결합하거나 제1 하부 슬래브와 제2 하부 슬래브 사이를 움직이지 않도록 결합시키기 위한 결합수단이 구비되며,
제1 하부 슬래브와 제1 하부 슬래브가 서로 이웃하게 설치되고 제1 하부 슬래브와 제2 하부 슬래브가 서로 이웃하게 설치된 상태에서 제2 결합수단에 볼트, 강선, 강봉 또는 강관이 삽입되어 제1 하부 슬래브와 제1 하부 슬래브 사이가 결합되고 제1 하부 슬래브와 제2 하부 슬래브 사이가 결합되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.
[22] The method of claim 21, wherein the lower slab includes a first lower slab installed at a lower central portion of the storeroom, and a second lower slab installed at a lower outer portion of the storeroom,
A coupling means for coupling the first lower slab and the first lower slab so as not to move or coupling the first lower slab and the second lower slab so that they do not move is provided on the upper surface of the lower slab,
A bolt, a steel wire, a steel bar or a steel pipe is inserted into the second joining means in a state where the first lower slab and the first lower slab are disposed adjacent to each other and the first and second lower slabs are adjacent to each other, And the first lower slab are coupled and the first lower slab and the second lower slab are coupled to each other.
제21항에 있어서, 상기 측벽 슬래브 하부의 일측에는 돌출된 받침대가 구비되고,
상기 측벽 슬래브의 받침대에 구비된 철근과 상기 하부 슬래브에 구비된 철근이 서로 결합되어 있고, 상기 받침대와 하부 슬래브 사이에 결합된 철근에 몰탈이 채워져서 상기 측벽 슬래브와 상기 하부 슬래브가 결합되어 있으며,
상기 측벽 슬래브의 측면에는 측벽 슬래브와 측벽 슬래브 사이를 움직이지 않도록 결합시키기 위한 제3 결합수단이 구비되며, 측벽 슬래브와 측벽 슬래브가 서로 이웃하게 설치된 상태에서 제3 결합수단에 볼트, 강선, 강봉 또는 강관이 삽입되어 측벽 슬래브와 측벽 슬래브 사이가 결합되어 있는 것을 특징으로 하는 프리캐스트 콘크리트 우수저류조.[22] The method of claim 21, further comprising a protruding pedestal on one side of the lower portion of the side wall slab,
Wherein a reinforcing bar provided on a support of the side wall slab and a reinforcing bar provided on the lower slab are coupled to each other and the reinforcing bars coupled between the support and the lower slab are filled with mortar to connect the side wall slab and the lower slab,
A third coupling means for coupling the side wall slab and the side wall slab so that they do not move between the side wall slab and the side wall slab are provided on the side surface of the side wall slab and the bolt, Wherein the steel pipe is inserted to connect the side wall slab and the side wall slab.