KR101484782B1 - Aqueous dispersion type pressure-sensitive adhesive composition and pressure-sensitive adhesive film - Google Patents

Aqueous dispersion type pressure-sensitive adhesive composition and pressure-sensitive adhesive film Download PDF

Info

Publication number
KR101484782B1
KR101484782B1 KR20080041317A KR20080041317A KR101484782B1 KR 101484782 B1 KR101484782 B1 KR 101484782B1 KR 20080041317 A KR20080041317 A KR 20080041317A KR 20080041317 A KR20080041317 A KR 20080041317A KR 101484782 B1 KR101484782 B1 KR 101484782B1
Authority
KR
South Korea
Prior art keywords
sensitive adhesive
pressure
meth
adhesive composition
aqueous dispersion
Prior art date
Application number
KR20080041317A
Other languages
Korean (ko)
Other versions
KR20080097948A (en
Inventor
도시타카 다카하시
겐이치 오카다
요우스케 마키하타
구니아키 이누이
다이키 시모구리
미카 오카다
나미코 무라야마
Original Assignee
닛토덴코 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2007163931A external-priority patent/JP2009001673A/en
Priority claimed from JP2008101755A external-priority patent/JP5250292B2/en
Application filed by 닛토덴코 가부시키가이샤 filed Critical 닛토덴코 가부시키가이샤
Publication of KR20080097948A publication Critical patent/KR20080097948A/en
Application granted granted Critical
Publication of KR101484782B1 publication Critical patent/KR101484782B1/en

Abstract

본 발명에 따른 수분산형 점착제 조성물은 탄소수가 4 내지 18이고 직쇄상 또는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터, (메트)아크릴산, 인산기 함유 바이닐 모노머 및 알콕시 실릴기 함유 바이닐 모노머를 함유하는 반응 성분을 반응시킴으로써 얻어지는 수분산형 공중합체 및 카복실기와의 반응성을 갖는 가교제를 포함한다. 상기 수분산형 점착제 조성물에서는 가교제의 배합 비율이 수분산형 공중합체 100중량부에 대하여 0.07 내지 4중량부이며, 수분산형 점착제 조성물로 이루어지는 점착제층은 90℃에서의 신장도가 200% 이하다. The water dispersion type pressure-sensitive adhesive composition according to the present invention is a pressure-sensitive adhesive composition comprising a (meth) acrylic acid alkyl ester having 4 to 18 carbon atoms and a linear or branched alkyl group, a (meth) acrylic acid, a vinyl monomer containing a phosphoric acid group and a vinyl monomer containing an alkoxysilyl group And a cross-linking agent having reactivity with the carboxyl group. In the above water dispersion type pressure-sensitive adhesive composition, the blending ratio of the crosslinking agent is 0.07 to 4 parts by weight based on 100 parts by weight of the water dispersion type copolymer, and the pressure-sensitive adhesive layer comprising the water dispersion type pressure-sensitive adhesive composition has an elongation at 90 ° C of 200% or less.

점착제, 조성물, 수분산형, 신장도 Adhesive, composition, water dispersion type, elongation degree

Description

수분산형 점착제 조성물 및 점착 필름{AQUEOUS DISPERSION TYPE PRESSURE-SENSITIVE ADHESIVE COMPOSITION AND PRESSURE-SENSITIVE ADHESIVE FILM}AQUEOUS DISPERSION TYPE PRESSURE-SENSITIVE ADHESIVE COMPOSITION AND PRESSURE-SENSITIVE ADHESIVE FILM < RTI ID = 0.0 >

본 발명은 수분산형 점착제 조성물 및 점착 필름에 관한 것이다. The present invention relates to an aqueous dispersion type pressure-sensitive adhesive composition and an adhesive film.

종래부터 편광 필름, 위상차 필름, 휘도 향상 필름, 시야각 확대 필름 등의 광학 필름이 각종 산업 용도로 사용되고 있으며, 예컨대, 액정 디스플레이, 유기 전기 발광 장치(유기 EL 표시 장치), 플라즈마 디스플레이 패널(PDP) 등의 화상 표시 장치에 접착되어 사용되고 있다. Conventionally, optical films such as a polarizing film, a retardation film, a luminance enhancement film, and a viewing angle enlarging film have been used for various industrial applications. For example, a liquid crystal display, an organic electroluminescence device (organic EL display device), a plasma display panel And is used by being adhered to an image display apparatus of the present invention.

이러한 광학 필름으로서 광학 필름에 점착제를 적층한 점착형 광학 필름이 알려져 있다. As such an optical film, a pressure-sensitive adhesive optical film obtained by laminating an adhesive on an optical film is known.

또한, 최근, 환경 부하의 관점에서 유기 용제의 사용을 저감하는 것이 요구되고 있고, 용매로서 유기 용제를 사용하는 용제형 점착제에서 분산매로서 물을 사용하는 수분산형 점착제로의 전환이 요구되고 있다. In recent years, it has been required to reduce the use of an organic solvent from the viewpoint of environmental load. In the solvent type pressure-sensitive adhesive using an organic solvent as a solvent, conversion to an aqueous dispersion type pressure-sensitive adhesive using water as a dispersion medium is required.

이러한 수분산형 점착제로서, 예컨대 공중합체 에멀젼을 포함하는 감압 접착제 조성물로서, 공중합체가 공중합체 전체에 대하여 10 내지 50중량%의 메타크릴산2-에틸헥실이 공중합되어 있고, 또한，공중합체의 유리 전이 온도가 -25℃ 이하인 감압성 접착제 조성물이 제안되어 있다(예컨대, 일본 특허 공개 2001-254063호 공보 참조). As such an aqueous dispersion type pressure-sensitive adhesive, for example, a pressure-sensitive adhesive composition comprising a copolymer emulsion, wherein the copolymer is copolymerized with 10 to 50% by weight of 2-ethylhexyl methacrylate based on the whole copolymer, A pressure-sensitive adhesive composition having a transition temperature of -25 占 폚 or lower has been proposed (for example, see Japanese Patent Laid-Open No. 2001-254063).

그러나, 상기와 같은 일본 특허 공개 2001-254063호 공보를 포함하는 종래의 수분산형 점착제는 폴리올레핀 등의 소수성 피착체에 대한 접착성은 개선된 것이지만, 유리 등의 친수성 피착체에 대한 접착성이 특히 낮아서, 화상 표시 장치에 사용되는 유리 기판에 강고하게 접착하기가 어렵다. However, the conventional aqueous dispersion type pressure-sensitive adhesive containing the above-described Japanese Patent Application Laid-Open No. 2001-254063 has improved adhesion to a hydrophobic adherend such as polyolefin, but the adhesiveness to a hydrophilic adherend such as glass is particularly low, It is difficult to firmly adhere to a glass substrate used in an image display apparatus.

또한, 광학 필름에 적층되는 수분산형 점착제에는 가혹한 가열이나 가습 등에 의해서도 밀착성 등이 저하되지 않는 높은 내열성이나 내습성이 요구된다. In addition, the water-dispersible pressure-sensitive adhesive laminated on the optical film is required to have high heat resistance and moisture resistance that do not deteriorate adhesiveness even by severe heating or humidification.

그러나, 상기한 수분산형 점착제에서는 가혹한 가열이나 가습 등에 의해서, 기포나 변형이 발생하여 광학 특성이 저하된다고 하는 불량이 있다. However, in the above-mentioned water dispersion type pressure-sensitive adhesive, bubbles or deformation are caused by severe heating or humidification, and there is a problem that the optical characteristics are deteriorated.

본 발명의 목적은 기판과의 접착성이 높고, 높은 내열성 및 내습성을 갖는 수분산형 점착제 조성물 및 그 수분산형 점착제 조성물로 이루어지는 점착제층을 구비한 점착 필름을 제공하는 것에 있다. An object of the present invention is to provide a pressure-sensitive adhesive film comprising a water-dispersible pressure-sensitive adhesive composition having high adhesiveness to a substrate, high heat resistance and moisture resistance, and a pressure-sensitive adhesive layer comprising the water-dispersible pressure-sensitive adhesive composition.

본 발명의 수분산형 점착제 조성물은, 탄소수가 4 내지 18이고 직쇄상 또는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터, (메트)아크릴산, 인산기 함유 바이닐 모노머 및 알콕시실릴기 함유 바이닐 모노머를 함유하는 반응 성분을 반응시킴으로써 얻어지는 수분산형 공중합체, 및 카복실기와의 반응성을 갖는 가교제를 포함하는 수분산형 점착제 조성물로서, 상기 가교제의 배합 비율이 상기 수분산형 공중합체 100중량부에 대하여 0.07 내지 4중량부이고, 상기 수분산형 점착제 조성 물로 이루어지는 점착제층은 하기 시험에 의한 90℃에서의 신장도가 200% 이하인 것을 특징으로 하고 있다. The water dispersion type pressure-sensitive adhesive composition of the present invention is a pressure-sensitive adhesive composition comprising a (meth) acrylic acid alkyl ester having 4 to 18 carbon atoms and a linear or branched alkyl group, a (meth) acrylic acid, a vinyl monomer containing a phosphoric acid group and a vinyl monomer containing an alkoxysilyl group And a crosslinking agent having reactivity with a carboxyl group, wherein the blending ratio of the crosslinking agent is 0.07 to 4 parts by weight based on 100 parts by weight of the aqueous dispersion copolymer, The pressure-sensitive adhesive layer comprising the aqueous dispersion type pressure-sensitive adhesive composition is characterized by an elongation at 90 ° C of 200% or less by the following test.

시험 : 수분산형 점착제 조성물을 가열하여 점착제층을 조제하고, 이것을 단면적 4.6mm2, 길이 30mm의 원주 형상으로 성형하여 시험편을 제작한다. 이어서, 시험편을 90℃에서 1시간 방치한 후, 초기 시험편의 길이 L0를 측정한다. 그 후, 시험편의 한쪽 끝을 고정하고, 시험편의 다른 끝에 12g의 추를 달아 시험편을 90℃에서 2시간 늘어뜨리고, 2시간 늘어뜨린 후의 시험편의 길이 L1(mm)을 측정하여, 다음 수학식 1에 의해 신장도를 산출한다. Test: The pressure-sensitive adhesive layer is prepared by heating the aqueous dispersion type pressure-sensitive adhesive composition, and the pressure-sensitive adhesive layer is molded into a cylindrical shape having a cross-sectional area of 4.6 mm 2 and a length of 30 mm. Then, the specimen is measured after left for one hour at 90 ℃, the length L 0 of the initial test pieces. Thereafter, one end of the test piece was fixed and the weight of 12 g was placed on the other end of the test piece. The test piece was hanged at 90 캜 for 2 hours, and the length L 1 (mm) of the test piece after hanging for 2 hours was measured. 1 < / RTI >

[수학식 1][Equation 1]

신장도(%)=(L1-L0)/L0×100Elongation (%) = (L 1 -L 0 ) / L 0 × 100

또한, 본 발명의 수분산형 점착제 조성물에서는, 상기 가교제가 카보다이이미드기를 갖는 화합물인 것이 적합하다. Further, in the aqueous dispersion type pressure-sensitive adhesive composition of the present invention, it is preferable that the crosslinking agent is a compound having a carbodiimide group.

또한, 본 발명의 수분산형 점착제 조성물에서는, 상기 가교제가 옥사졸린기를 갖는 가교제이고, 상기 가교제의 배합 비율이 상기 수분산형 공중합체 100중량부에 대하여 0.07 내지 1.5중량부인 것이 적합하다. In the aqueous dispersion type pressure-sensitive adhesive composition of the present invention, it is preferable that the cross-linking agent is a cross-linking agent having an oxazoline group, and the mixing ratio of the cross-linking agent is 0.07 to 1.5 parts by weight based on 100 parts by weight of the water-

또한, 본 발명의 수분산형 점착제 조성물에서는, 상기 수분산형 점착제 조성물은 아세트산에틸에 침지했을 때의 겔분율이 80 내지 95중량%인 것이 적합하다. In the aqueous dispersion type pressure-sensitive adhesive composition of the present invention, it is preferable that the aqueous dispersion type pressure-sensitive adhesive composition has a gel fraction of 80 to 95% by weight when immersed in ethyl acetate.

또한, 본 발명의 점착 필름은 수분산형 점착제 조성물로 이루어지는 점착제층을 구비하고, 상기 수분산형 점착제 조성물은 탄소수가 4 내지 18이고 직쇄상 또 는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터, (메트)아크릴산, 인산기 함유 바이닐 모노머 및 알콕시실릴기 함유 바이닐 모노머를 함유하는 반응 성분을 반응시킴으로써 얻어지는 수분산형 공중합체 및 카복실기와의 반응성을 갖는 가교제를 포함하고, 상기 가교제의 배합 비율이 상기 수분산형 공중합체 100중량부에 대하여 007 내지 4중량부이며, 상기 점착제층은 하기 시험에 의한 90℃에서의 신장도가 200% 이하인 것을 특징으로 하고 있다. The pressure-sensitive adhesive film of the present invention comprises a pressure-sensitive adhesive layer comprising an aqueous dispersion type pressure-sensitive adhesive composition, wherein the water-dispersible pressure-sensitive adhesive composition is a (meth) acrylic acid alkyl ester having 4 to 18 carbon atoms and a linear or branched alkyl group, ) Acrylic acid, a phosphoric acid group-containing vinyl monomer and an alkoxysilyl group-containing vinyl monomer, and a cross-linking agent having reactivity with the carboxyl group, wherein the compounding ratio of the cross-linking agent is the same as that of the water- 007 to 4 parts by weight based on 100 parts by weight of the pressure-sensitive adhesive layer, and the pressure-sensitive adhesive layer has an elongation at 90 DEG C of 200% or less by the following test.

시험 : 수분산형 점착제 조성물을 가열하여 점착제층을 조제하고, 이것을 단면적 4.6mm2, 길이 30mm의 원주형상으로 성형하여 시험편을 제작한다. 이어서, 시험편을 90℃에서 1시간 방치한 후 초기 시험편의 길이 L0를 측정한다. 그 후, 시험편의 한쪽 끝을 고정하고, 시험편의 다른 끝에 12g의 추를 달아, 시험편을 90℃에서 2시간 늘어뜨리고, 2시간 늘어뜨린 후의 시험편의 길이 L1(mm)을 측정하고, 다음 수학식 1에 의해 신장도를 산출한다. Test: The pressure-sensitive adhesive layer is prepared by heating the aqueous dispersion type pressure-sensitive adhesive composition, and the pressure-sensitive adhesive layer is molded into a cylindrical shape having a cross-sectional area of 4.6 mm 2 and a length of 30 mm. Then, a test piece to measure the length L 0 of the was allowed to stand for 1 hour at 90 ℃ initial specimen. Thereafter, one end of the test piece was fixed, and a weight of 12 g was placed on the other end of the test piece. The test piece was hanged at 90 캜 for 2 hours, and the length L 1 (mm) of the test piece after hanging for 2 hours was measured. The elongation is calculated by Equation (1).

[수학식 1] [Equation 1]

신장도(%)=(L1-L0)/L0×100Elongation (%) = (L 1 -L 0 ) / L 0 × 100

또한, 본 발명의 점착 필름에서는, 상기 가교제가 카보다이이미드기를 갖는 화합물인 것이 적합하다. In the adhesive film of the present invention, it is preferable that the crosslinking agent is a compound having a carbodiimide group.

또한, 본 발명의 점착 필름에서는, 상기 가교제가 옥사졸린기를 갖는 가교제이고, 상기 가교제의 배합 비율이 상기 수분산형 공중합체 100중량부에 대하여 0.07 내지 1.5중량부인 것이 적합하다. In the adhesive film of the present invention, it is preferable that the crosslinking agent is a crosslinking agent having an oxazoline group, and the mixing ratio of the crosslinking agent is 0.07 to 1.5 parts by weight based on 100 parts by weight of the aqueous dispersion copolymer.

본 발명의 수분산형 점착제 조성물 및 그 수분산형 점착제 조성물로 이루어지는 점착제층을 구비한 점착 필름은, 기판과의 접착력이 높아서 강고한 접착을 달성할 수 있다. 또한, 높은 내열성 및 내습성을 갖기 때문에, 고온 고습 분위기하에서 우수한 내구성을 얻을 수 있다. The pressure-sensitive adhesive film comprising the pressure-sensitive adhesive layer comprising the aqueous dispersion type pressure-sensitive adhesive composition of the present invention and the water-dispersible pressure-sensitive adhesive composition of the present invention has high adhesive strength with the substrate and can achieve strong adhesion. In addition, since it has high heat resistance and moisture resistance, excellent durability can be obtained in a high temperature and high humidity atmosphere.

특히, 본 발명의 수분산형 점착제 조성물 및 그 수분산형 점착제 조성물로 이루어지는 점착제층을 구비한 점착 필름은 고온 및 고습에 있어서의 기포 및 변형의 발생을 유효하게 방지할 수 있다. 이 때문에, 광학 특성의 저하를 유효하게 방지할 수 있다.Particularly, the pressure-sensitive adhesive film comprising the pressure-sensitive adhesive layer comprising the aqueous dispersion type pressure-sensitive adhesive composition of the present invention and the aqueous dispersion type pressure-sensitive adhesive composition can effectively prevent the occurrence of bubbles and deformation at high temperature and high humidity. Therefore, deterioration of optical characteristics can be effectively prevented.

본 발명의 수분산형 점착제 조성물은 수분산형 공중합체와 가교제를 포함하고 있다. The water dispersion type pressure-sensitive adhesive composition of the present invention comprises a water-dispersible copolymer and a crosslinking agent.

상기 수분산형 공중합체는 (메트)아크릴산알킬에스터, (메트)아크릴산, 인산기 함유 바이닐 모노머 및 알콕시실릴기 함유 바이닐 모노머를 함유하는 반응 성분을 반응시킴으로써 얻어진다. The aqueous dispersion copolymer is obtained by reacting a reaction component containing a (meth) acrylic acid alkyl ester, (meth) acrylic acid, a phosphoric acid group-containing vinyl monomer and an alkoxysilyl group-containing vinyl monomer.

(메트)아크릴산알킬에스터는 탄소수가 4 내지 18이고 직쇄상 또는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터(메타크릴산알킬에스터 및/또는 아크릴산알킬에스터)이고, 예컨대, (메트)아크릴산뷰틸, (메트)아크릴산아이소뷰틸, (메트)아크릴산 sec-뷰틸, (메트)아크릴산 t-뷰틸, (메트)아크릴산펜틸, (메트)아크릴산네오펜틸, (메트)아크릴산아이소아밀, (메트)아크릴산헥실, (메트)아크릴산헵틸, (메트)아크릴산옥틸, (메트)아크릴산2-에틸헥실, (메트)아크릴산아이소옥틸, (메트)아크릴산노닐, (메트)아크릴산아이소노닐, (메트)아크릴산데실, (메트)아크릴산아이소데실, (메트)아크릴산운데실, (메트)아크릴산도데실, (메트)아크릴산트리데실, (메트)아크릴산테트라데실, (메트)아크릴산펜타데실, (메트)아크릴산헥사데실, (메트)아크릴산헵타데실, (메트)아크릴산옥타데실 등을 들 수 있다. 이들 (메트)아크릴산알킬에스터 중 바람직하게는 아크릴산뷰틸을 들 수 있다. 이들 (메트)아크릴산알킬에스터는 단독 사용 또는 병용할 수 있다. (Meth) acrylic acid alkyl ester is a (meth) acrylic acid alkyl ester (methacrylic acid alkyl ester and / or acrylic acid alkyl ester) having 4 to 18 carbon atoms and having a linear or branched alkyl group such as (meth) (Meth) acrylate, isoamyl (meth) acrylate, hexyl (meth) acrylate, (meth) acrylate, isobutyl (meth) acrylate, sec- (Meth) acrylate, isobutyl (meth) acrylate, octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl (Meth) acrylate, pentadecyl (meth) acrylate, hexadecyl (meth) acrylate, dodecyl (meth) acrylate, undecyl Heptadecyl acrylate, Octadecyl acrylate, and octadecyl acrylate. Among these (meth) acrylic acid alkyl esters, preferred is butyl acrylate. These (meth) acrylic acid alkyl esters can be used alone or in combination.

(메트)아크릴산알킬에스터의 배합 비율은 반응 성분 100중량부에 대하여, 예컨대, 60 내지 99중량부, 바람직하게는 80 내지 99중량부, 더 바람직하게는 80 내지 98중량부이다. (Meth) acrylic acid alkyl ester is, for example, 60 to 99 parts by weight, preferably 80 to 99 parts by weight, more preferably 80 to 98 parts by weight based on 100 parts by weight of the reaction component.

(메트)아크릴산으로서는 예컨대, 메타크릴산, 아크릴산을 들 수 있다. Examples of the (meth) acrylic acid include methacrylic acid and acrylic acid.

(메트)아크릴산은 단독 사용 또는 병용할 수 있다. (메트)아크릴산의 배합 비율은 반응 성분 100중량부에 대하여, 예컨대, 0.5 내지 15중량부, 바람직하게는 0.5 내지 10중량부, 더 바람직하게는 1 내지 10중량부이다. 상기 범위보다 적으면 수분산형 점착제 조성물의 응집력이 저하되는 경우가 있고, 상기 범위보다 많으면 유화 중합시의 안정성 및 수분산형 점착제 조성물의 내수성이 저하되는 경우가 있다. (Meth) acrylic acid may be used alone or in combination. (Meth) acrylic acid is, for example, 0.5 to 15 parts by weight, preferably 0.5 to 10 parts by weight, more preferably 1 to 10 parts by weight based on 100 parts by weight of the reaction component. When the amount is less than the above range, the cohesive strength of the aqueous dispersion type pressure-sensitive adhesive composition may be lowered, and if it is more than the above range, stability during emulsion polymerization and water resistance of the water dispersion type pressure-sensitive adhesive composition may be deteriorated.

인산기 함유 바이닐 모노머는 예컨대, 하기 화학식 1로 표시되는 폴리알킬렌옥사이드(메트)아크릴레이트인산에스터이고, The vinyl monomer containing a phosphoric acid group is, for example, a polyalkylene oxide (meth) acrylate phosphate ester represented by the following formula (1)

Figure 112008031822378-pat00001
Figure 112008031822378-pat00001

(화학식 1 중, R1은 수소 원자 또는 메틸기이고, R2는 폴리옥시알킬렌기이며를, X는 인산기 또는 그 염을 나타낸다.)Wherein R 1 is a hydrogen atom or a methyl group, R 2 is a polyoxyalkylene group, and X is a phosphate group or a salt thereof.

R2로 표시되는 폴리옥시알킬렌기로서는 하기 화학식 2로 표시되며, The polyoxyalkylene group represented by R 2 is represented by the following general formula (2)

Figure 112008031822378-pat00002
Figure 112008031822378-pat00002

(화학식 2 중, n은 1 내지 4의 정수, m은 2 이상의 정수를 나타낸다.)(In the general formula (2), n represents an integer of 1 to 4, and m represents an integer of 2 or more.)

예컨대, 폴리옥시에틸렌기(화학식 2 중, n=2에 상당.), 폴리옥시프로필렌기(화학식 2 중, n=3에 상당.) 및 이들의 랜덤, 블록 또는 그래프트 유닛 등을 들 수 있으며, 이들 옥시알킬렌기의 중합도, 즉 화학식 2 중 m은 바람직하게는 4 이상, 통상 40 이하다. Examples thereof include polyoxyethylene groups (corresponding to n = 2 in the formula (2)), polyoxypropylene groups (corresponding to n = 3 in the formula (2)) and random, block or graft units thereof, The polymerization degree of these oxyalkylene groups, that is, m in formula (2) is preferably 4 or more, and usually 40 or less.

옥시알킬렌기의 중합도가 높을수록 인산기를 갖는 측쇄의 운동성이 높아 유리와 신속히 상호 작용하기 때문에, 수분산형 점착제 조성물의 유리 기판에의 접착성이 향상된다. The higher the degree of polymerization of the oxyalkylene group is, the higher the mobility of the side chain having a phosphoric group is, and the faster the interaction with the glass, the better the adhesion of the aqueous dispersion type pressure-sensitive adhesive composition to the glass substrate.

또한, X로 표시되는 인산기 또는 그 염은 하기 화학식 3으로 표시되며, The phosphoric acid group represented by X or a salt thereof is represented by the following general formula (3)

Figure 112008031822378-pat00003
Figure 112008031822378-pat00003

(화학식 3 중, M1 및 M2는 각각 독립적으로, 수소 원자 또는 양이온을 나타낸다.)(In the formula (3), M 1 and M 2 each independently represent a hydrogen atom or a cation.)

양이온으로서는 특별히 제한되지 않으며, 예컨대 나트륨, 칼륨 등의 알칼리 금속, 예컨대 칼슘, 마그네슘 등의 알카리 토류 금속 등의 무기양이온, 예컨대, 4급 아민류 등의 유기양 이온 등을 들 수 있다. The cation is not particularly limited, and examples thereof include inorganic cations such as alkali metals such as sodium and potassium, and alkaline earth metals such as calcium and magnesium, and organic cation ions such as quaternary amines.

또한, 인산기 함유 바이닐 모노머는 일반적으로 시판되고 있는 것을 이용할 수 있으며, 예컨대, Sipomer PAM-100(로디어 닛카(주)제), Phosmer PE(유니케미컬(주)제), Phosmer PEH(유니케미컬(주)제), Phosmer PEDM(유니케미컬(주)제) 등의 모노[폴리(에틸렌옥사이드)메타크릴레이트]인산에스터, 예컨대 Sipomer PAM-200(로디어 닛카(주)제), Phosmer PP(유니케미컬(주)제), Phosmer PPH(유니케미컬(주)제), Phosmer PPDM(유니케미컬(주)제) 등의 모노[폴리(프로필렌옥사이드)메타크릴레이트] 인산에스터 등을 들 수 있다. The vinyl monomer containing a phosphoric acid group may be a commercially available one which is commercially available. Examples thereof include Sipomer PAM-100 (manufactured by Rhodia Nikka Co.), Phosmer PE (manufactured by UniChemical Co., Ltd.), Phosmer PEH (Ethylene oxide) methacrylate] phosphoric acid esters such as Sipomer PAM-200 (manufactured by Rodi Organics), Phosmer PP (manufactured by Nippon Kayaku Co., Ltd.) and Phosmer PEDM (Propylene oxide) methacrylate] phosphoric acid esters such as Phosmer PPH (manufactured by UniChemical Co., Ltd.) and Phosmer PPDM (manufactured by UniChemical Co., Ltd.).

이들 인산기 함유 바이닐 모노머는 단독 사용 또는 병용할 수 있다. These phosphoric acid group-containing vinyl monomers may be used alone or in combination.

인산기 함유 바이닐 모노머중 인산기 농도는 반응 성분 중, 예컨대, 0.01 내지 0.45밀리몰/g, 바람직하게는 0.02 내지 0.20밀리몰/g이다. 인산기 함유 바이닐 모노머중 인산기 농도를 상기 범위로 하기 위해서는 인산기 함유 바이닐 모노머의 분자량에도 따르지만, 인산기 함유 바이닐 모노머의 배합 비율을 반응 성분 100중량부에 대하여, 예컨대, 0.5 내지 20중량부, 바람직하게는 0.5 내지 10중량부, 더 바람직하게는 1 내지 5중량부로 설정한다. The phosphoric acid group concentration in the phosphoric acid group-containing vinyl monomer is, for example, 0.01 to 0.45 mmol / g, preferably 0.02 to 0.20 mmol / g in the reaction component. The concentration of the phosphoric acid group in the phosphoric acid group-containing vinyl monomer is in the above-mentioned range, but the mixing ratio of the phosphoric acid group-containing vinyl monomer is, for example, 0.5 to 20 parts by weight, preferably 0.5 To 10 parts by weight, more preferably from 1 to 5 parts by weight.

인산기 함유 바이닐 모노머의 인산기 농도 및 배합 비율이 상기 범위보다 적으면 유리 기판으로의 접착력 향상의 효과가 충분히 얻어지지 않는 경우가 있다. 인산기 함유 바이닐 모노머의 인산기 농도 및 배합 비율이 상기 범위보다 많으면, 유화 중합시의 안정성 및 수분산형 점착제 조성물의 내수성이 저하되는 경우가 있고, 또한 수분산형 점착제 조성물의 탄성율이 높아짐으로써 접착성이 저하되는 경우가 있다. When the phosphoric acid group concentration and the compounding ratio of the phosphoric acid group-containing vinyl monomer are less than the above range, the effect of improving the adhesion to the glass substrate may not be sufficiently obtained. When the phosphoric acid group concentration and the blending ratio of the phosphoric acid group-containing vinyl monomer are more than the above range, the stability in emulsion polymerization and the water resistance of the water dispersion type pressure-sensitive adhesive composition may be deteriorated. In addition, the adhesiveness is lowered by increasing the elastic modulus of the water- There is a case.

알콕시실릴기 함유 바이닐 모노머로서는 예컨대, 실리콘계(메트) 아크릴레이트 모노머나, 실리콘계 바이닐 모노머 등을 들 수 있다. Examples of the alkoxysilyl group-containing vinyl monomers include silicone-based (meth) acrylate monomers and silicone-based vinyl monomers.

실리콘계(메트)아크릴레이트 모노머로서는 예컨대, (메트)아크릴로일옥시메틸-트라이메톡시실란, (메트)아크릴로일옥시메틸-트라이에톡시실란, 2-(메트)아크릴로일옥시에틸-트라이메톡시실란, 2-(메트)아크릴로일옥시에틸-트라이에톡시실란, 3-(메트)아크릴로일옥시프로필-트라이메톡시실란, 3-(메트)아크릴로일옥시프로필-트라이에톡시실란, 3-(메트)아크릴로일옥시프로필-트라이프로폭시실란, 3-(메트)아크릴로일옥시프로필-트라이아이소프로폭시실란, 3-(메트)아크릴로일옥시프로필-트라이뷰톡시실란 등의 (메트)아크릴로일옥시알킬-트라이알콕시실란, 예컨대, (메트)아크릴로일옥시메틸-메틸다이메톡시실란, (메트)아크릴로일옥시메틸-메틸다이에톡시실란, 2-(메트)아크릴로일옥시에틸-메틸다이메톡시실란, 2-(메트)아크릴로일옥시 에틸-메틸다이에톡시실란, 3-(메트)아크릴로일옥시프로필-메틸다이메톡시실란, 3-(메트)아크릴로일옥시프로필-메틸다이에톡시실란, 3-(메트)아크릴로일옥시프로필-메틸다이프로폭시실란, 3-(메트)아크릴로일옥시프로필-메틸다이아이소프로폭시실란, 3-(메트)아크릴로일옥시프로필-메틸다이부톡시실란, 3-(메트)아크릴로일옥시프로필-에틸다이메톡시실란, 3-(메트)아크릴로일옥시프로필-에틸다이에톡시실란, 3-(메트)아크릴로일옥시프로필-에틸다이프로폭시실란, 3-(메트)아크릴로일옥시프로필-에틸다이아이소프로폭시실란, 3-(메트)아크릴로일옥시프로필-에틸다이부톡시시란, 3-(메트)아크릴로일옥시프로필-프로필다이메톡시실란, 3-(메트)아크릴로일옥시프로필-프로필다이에톡시실란 등의 (메트)아크릴로일옥시알킬-알킬다이알콕시실란이나, 이들에 대응하는 (메트)아크릴로일옥시알킬-다이알킬(모노)알콕시실란 등을 들 수 있다. Examples of the silicone-based (meth) acrylate monomer include (meth) acryloyloxymethyl-trimethoxysilane, (meth) acryloyloxymethyl-triethoxysilane, 2- (meth) acryloyloxyethyl-tri (Meth) acryloyloxypropyltriethoxysilane, 3- (meth) acryloyloxypropyltrimethoxysilane, 3- (meth) acryloyloxypropyltriethoxy silane, 2- Silane, 3- (meth) acryloyloxypropyltripropoxysilane, 3- (meth) acryloyloxypropyl-triisopropoxysilane, 3- (meth) acryloyloxypropyl- (Meth) acryloyloxymethyl-methyldiethoxysilane, 2- ((meth) acryloyloxymethyl-methyldiethoxysilane, (Meth) acryloyloxyethyl-methyl dimethoxysilane, 2- (meth) acryloyloxyethyl-methyl di (Meth) acryloyloxypropyl-methyldimethoxysilane, 3- (meth) acryloyloxypropyl-methyldiethoxysilane, 3- (meth) (Meth) acryloyloxypropyl-methyldiisopropoxysilane, 3- (meth) acryloyloxypropyl-methyldibutoxysilane, 3- (meth) acryloyloxypropyl- (Meth) acryloyloxypropyl-ethyldiethoxysilane, 3- (meth) acryloyloxypropyl-ethyldipropoxysilane, 3- (meth) acryloyloxypropyl- (Meth) acryloyloxypropyl-propyldimethoxysilane, 3- (meth) acryloyloxypropyl-ethyldibutoxysilane, 3- (Meth) acryloyloxyalkyl-alkyldialkoxysilane such as diethyl (meth) acrylate, di (meth) acrylate, One oxyalkylene a krill-and the like can be mentioned dialkyl (mono) alkoxysilanes.

또한, 실리콘계 바이닐 모노머로서는 예컨대, 바이닐트라이메톡시실란, 바이닐트라이에톡시실란, 바이닐트라이프로폭시실란, 바이닐트라이아이소프로폭시실란, 바이닐트라이뷰톡시실란 등의 바이닐트라이알콕시실란 외에, 이들에 대응하는 바이닐알킬다이알콕시실란이나 바이닐다이알킬알콕시실란, 예컨대, 바이닐메틸트라이메톡시실란, 바이닐메틸트라이에톡시실란, β-바이닐에틸트라이메톡시실란, β-바이닐에틸트라이에톡시실란, γ-바이닐프로필트라이메톡시실란, γ-바이닐프로필트라이에톡시실란, γ-바이닐프로필트라이프로폭시실란, γ-바이닐프로필트라이아이소프로폭시실란, γ-바이닐프로필트라이뷰톡시실란 등의 바이닐알킬트라이알콕시실란 외에, 이들에 대응하는 (바이닐알킬)알킬다이알콕시실란이나 (바이닐알킬)다이알 킬(모노)알콕시실란 등을 들 수 있다. Examples of the silicon-based vinyl monomers include vinyltrialkoxysilanes such as vinyltrimethoxysilane, vinyltriethoxysilane, vinyltripropoxysilane, vinyltriisopropoxysilane and vinyltri butoxysilane, as well as vinyltrialkoxysilane corresponding to them Vinyl alkyl dialkoxy silane or vinyl dialkyl alkoxy silane such as vinyl methyl trimethoxy silane, vinyl methyl triethoxy silane, beta-vinyl ethyl trimethoxy silane, beta-vinyl ethyl triethoxy silane, gamma -vinyl propyl silane, In addition to vinylalkyltrialkoxysilanes such as trimethoxysilane,? -Vinylpropyltriethoxysilane,? -Vinylpropyltripropoxysilane,? -Vinylpropyltriisopropoxysilane and? -Vinylpropyltributoxysilane, The corresponding (vinylalkyl) alkyldialkoxysilane or (vinylalkyl) dialkyl (mono) And alkoxysilane.

이들 알콕시실릴기 함유 바이닐 모노머 중, 바람직하게는 실리콘계(메트)아크릴레이트 모노머를 들 수 있고, 더 바람직하게는 3-메타크릴로일옥시프로필-트라이메톡시실란을 들 수 있다. Of these alkoxysilyl group-containing vinyl monomers, silicone-based (meth) acrylate monomers are preferable, and 3-methacryloyloxypropyl-trimethoxysilane is more preferable.

이들 알콕시실릴기 함유 바이닐 모노머는 단독 사용 또는 병용할 수 있다. These alkoxysilyl group-containing vinyl monomers may be used alone or in combination.

알콕시실릴기 함유 바이닐 모노머의 배합 비율은 반응 성분 100중량부에 대하여, 예컨대, 0.001 내지 1중량부, 바람직하게는 0.01 내지 0.1중량부이다. 상기 범위보다 적으면, 알콕시실릴기에 의한 가교가 부족하여, 수분산형 점착제 조성물의 응집력 저하를 초래하거나, 수분산형 접착제 조성물과 유리 기판과의 접착성의 향상이 얻어지지 않고, 상기 범위보다 많으면 유화 중합시의 안정성 저하나 접착성의 저하를 초래하는 경우가 있다. The blending ratio of the alkoxysilyl group-containing vinyl monomer is, for example, 0.001 to 1 part by weight, preferably 0.01 to 0.1 part by weight based on 100 parts by weight of the reaction component. When the amount is less than the above range, crosslinking due to an alkoxysilyl group is insufficient to cause deterioration of the cohesive strength of the aqueous dispersion type pressure-sensitive adhesive composition or improvement in adhesion between the aqueous dispersion type adhesive composition and the glass substrate. The stability of the thermosetting resin may deteriorate and the adhesiveness may be deteriorated.

또한, 반응 성분은 (메트)아크릴산알킬에스터와 공중합 가능한 공중합성 바이닐 모노머를 또한 함유할 수도 있다. In addition, the reaction component may also contain a copolymerizable vinyl monomer copolymerizable with the (meth) acrylic acid alkyl ester.

이와 같은 공중합성 바이닐 모노머로서는 예컨대, (메트)아크릴산 사이클로헥실, (메트)아크릴산보르닐, (메트)아크릴산아이소보르닐 등의, 탄소수가 6이상인 지환식 탄화수소기를 갖는 (메트)아크릴산 지환식 탄화수소 에스터, 예컨대, 스타이렌 등의 방향족계 바이닐 모노머, 예컨대, (메트)아크릴산메틸, (메트)아크릴산에틸, (메트)아크릴산프로필, (메트)아크릴산아이소프로필 등의, 탄소수가 1 내지 3이고 직쇄상 또는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터, 예컨대, (메트)아크릴산페닐 등의 (메트)아크릴산아릴에스터, 예컨대, (메트)아크릴산메톡 시에틸, (메트)아크릴산에톡시에틸 등의 알콕시기 함유 불포화 모노머, 예컨대, 에틸렌, 프로필렌, 아이소프렌, 뷰타다이엔, 아이소뷰틸렌 등의 올레핀계 모노머, 예컨대, 바이닐에터 등의 바이닐에터계 모노머, 예컨대, 염화바이닐 등의 할로겐 원자 함유 불포화 모노머, 기타, 예컨대, N-바이닐피롤리돈, N-(1-메틸바이닐)피롤리돈, N-바이닐피리딘, N-바이닐피페리돈, N-바이닐피리미딘, N-바이닐피페라진, N-바이닐피라진, N-바이닐피롤, N-바이닐이미다졸, N-바이닐옥사졸, N-바이닐모폴린, (메트)아크릴산테트라하이드로퍼푸릴 등의 바이닐기 함유 헤테로환 화합물, 예컨대 불소(메트)아크릴레이트 등의, 불소 원자 등의 할로겐 원자를 함유하는 아크릴산에스터계 모노머 등을 들 수 있다. Examples of such a copolymerizable vinyl monomer include (meth) acrylic acid alicyclic hydrocarbon esters having an alicyclic hydrocarbon group having 6 or more carbon atoms such as cyclohexyl (meth) acrylate, boron (meth) acrylate and isobornyl (Meth) acrylate such as methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate and isopropyl (meth) acrylate, and aromatic vinyl monomers such as styrene, (Meth) acrylic acid alkyl ester having a branched alkyl group such as a (meth) acrylic acid aryl ester such as a (meth) acrylic acid ester such as methoxyethyl (meth) acrylate and ethoxyethyl (meth) Unsaturated monomers such as olefinic monomers such as ethylene, propylene, isoprene, butadiene and isobutylene, for example, vinyl ethers, Unsaturated monomers such as vinyl chloride and the like, and other unsaturated monomers such as N-vinylpyrrolidone, N- (1-methylvinyl) pyrrolidone, N-vinylpyridine, N-vinylpiperidone , N-vinylpiperazine, N-vinylpyrazine, N-vinylpyrrole, N-vinylimidazole, N-vinyloxazole, N-vinylmorpholine, (meth) acrylate tetrahydroperfuryl And vinyl group-containing heterocyclic compounds such as fluorine (meth) acrylate, and the like, and acrylic acid ester monomers containing a halogen atom such as a fluorine atom.

또한, 공중합성 바이닐 모노머로서는 작용기를 함유하는 작용기 함유 바이닐 모노머를 들 수 있다. Examples of the copolymerizable vinyl monomer include a functional monomer containing a functional group.

이와 같은 작용기 함유 바이닐 모노머로서는 예컨대, 푸마르산, 말레산, 이타콘산, 크로톤산, 신남산 등의 불포화 카복실산이나, 무수이타콘산, 무수말레산, 무수푸마르산 등의 불포화 다이카복실산 무수물 등의 카복실기 함유 바이닐 모노머((메트)아크릴산을 제외한다.), 예컨대, 아세트산바이닐, 프로피온산바이닐 등의 카복실산바이닐에스터, 예컨대, 아크릴산2-하이드록시에틸, 아크릴산2-하이드록시프로필, 아크릴산2-하이드록시뷰틸 등의 하이드록실기 함유 바이닐 모노머, 예컨대, (메트)아크릴아마이드, N,N-다이메틸(메트)아크릴아마이드, N,N-다이에틸(메트)아크릴아마이드, N-아이소프로필(메트)아크릴아마이드, N-뷰틸(메트)아크릴아마이드, N-메톡시메틸(메트)아크릴아마이드, N-메틸올(메트)아크릴아마이드, N-메틸 올프로페인(메트)아크릴아마이드, N-바이닐카복실산아마이드 등의 아마이드기 함유 불포화 모노머, 예컨대, (메트)아크릴산글라이시딜, (메트)아크릴산메틸글라이시딜 등의 글라이시딜기 함유 불포화 모노머, 예컨대, 아크릴로나이트릴, 메타크릴로나이트릴 등의 사이아노기 함유 불포화 모노머, 예컨대, 2-메타크릴로일옥시에틸아이소사이아네이트 등의 아이소사이아네이트기 함유 불포화 모노머, 예컨대, 스타이렌설폰산, 알릴설폰산, 2-(메트)아크릴아마이드-2-메틸프로페인 설폰산, (메트)아크릴아마이드 프로페인 설폰산, 설포프로필 (메트)아크릴레이트, (메트)아크릴로일옥시나프탈렌설폰산 등의 설폰산기 함유 불포화 모노머, 예컨대, N-사이클로헥실 말레이미드, N-아이소프로필 말레이미드, N-라우릴 말레이미드, N-페닐 말레이미드 등의 말레이미드계 모노머, 예컨대 N-메틸 이타콘이미드, N-에틸 이타콘이미드, N-부틸 이타콘이미드, N-옥틸 이타콘이미드, N-2-에틸 헥실 이타콘이미드, N-사이클로헥실 이타콘이미드, N-라우릴 이타콘이미드 등의 이타콘이미드계 모노머, 예컨대, N-(메트)아크릴로일옥시 메틸렌 석신이미드, N-(메트)아크릴로일-6-옥시헥사메틸렌 석신이미드, N-(메트)아크릴로일-8-옥시옥타메틸렌 석신이미드 등의 석신이미드계 모노머, 예컨대, (메트)아크릴산 폴리에틸렌 글라이콜, (메트)아크릴산 폴리프로필렌 글라이콜, (메트)아크릴산 메톡시에틸렌 글라이콜, (메트)아크릴산 메톡시 폴리프로필렌 글라이콜 등의 글라이콜계 아크릴 에스터 모노머 등을 들 수 있다. Examples of such functional group-containing vinyl monomers include unsaturated carboxylic acids such as fumaric acid, maleic acid, itaconic acid, crotonic acid and cinnamic acid, and unsaturated dicarboxylic acid anhydrides such as itaconic anhydride, maleic anhydride and fumaric anhydride. Examples of the monomer (excluding (meth) acrylic acid) include carboxylic acid vinyl esters such as vinyl acetate and vinyl propionate such as 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, and 2-hydroxybutyl acrylate (Meth) acrylamide, N, N-dimethyl (meth) acrylamide, N, N-diethyl (meth) acrylamide, N- (Meth) acrylamide, N-methylol (meth) acrylamide, N-methylol propane (meth) acrylamide Unsaturated monomers containing an amide group such as N, N-dimethylacrylamide, N, N-vinylcarboxylic acid amide, and the like, unsaturated monomers containing glycidyl groups such as (meth) acrylic acid glycidyl and (meth) acrylic acid methyl glycidyl, Unsaturated monomers containing an isocyanate group such as 2-methacryloyloxyethyl isocyanate, such as styrene sulfonic acid, allyl sulfonic acid, 2- Containing unsaturated monomers such as (meth) acrylamide-2-methylpropanesulfonic acid, (meth) acrylamide propanesulfonic acid, sulfopropyl (meth) acrylate and (meth) acryloyloxynaphthalenesulfonic acid, Maleimide-based monomers such as N-cyclohexylmaleimide, N-isopropylmaleimide, N-laurylmaleimide and N-phenylmaleimide, N-butyl-2-ethylhexanoic acid, N-cyclohexylketanoic acid, N-cyclohexylketanoic acid, (Meth) acryloyloxymethylene succinimide, N- (meth) acryloyl-6-oxyhexamethylene succinimide, N- (meth) acryloyl- (Meth) acryloylmethyl succinimide, and the like, such as (meth) acrylic acid polyethylene glycol, (meth) acrylic acid polypropylene glycol, (meth) acrylic acid And glycol-based acrylic ester monomers such as methoxyethylene glycol and (meth) acrylic acid methoxypolypropylene glycol.

또한, 상기 작용기 함유 바이닐 모노머로서는 다작용성 모노머를 들 수 있다. The functional group-containing vinyl monomers include polyfunctional monomers.

다작용성 모노머로서는 예컨대, 에틸렌 글라이콜 다이(메트)아크릴레이트, 다이에틸렌 글라이콜 다이(메트)아크릴레이트, 트라이에틸렌 글라이콜 다이(메트)아크릴레이트, 트라이메틸올 프로페인 트라이(메트)아크릴레이트, 테트라에틸렌 글라이콜 다이(메트)아크릴레이트 등의 (모노 또는 폴리)에틸렌글라이콜 다이(메트)아크릴레이트나, 프로필렌글라이콜 다이(메트)아크릴레이트 등의 (모노 또는 폴리)프로필렌글라이콜 다이(메트)아크릴레이트 등의 (모노 또는 폴리) 알킬렌글라이콜 다이(메트)아크릴레이트 외에, 네오펜틸글라이콜 다이(메트)아크릴레이트, 1,6-헥세인다이올 다이(메트)아크릴레이트, 펜타에리트리톨 다이(메트)아크릴레이트, 트라이메틸올프로페인 트라이(메트)아크릴레이트, 펜타에리트리톨 트라이(메트)아크릴레이트, 다이펜타에리트리톨 헥사(메트)아크릴레이트, 다이바이닐벤젠 등을 들 수 있다. 또한, 다작용성 모노머로서, 에폭시 아크릴레이트, 폴리에스터 아크릴레이트, 우레탄 아크릴레이트 등도 들 수 있다. Examples of the polyfunctional monomer include ethylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, triethylene glycol di (meth) acrylate, trimethylol propane tri (meth) (Mono or poly) ethylene glycol di (meth) acrylate such as tetraethylene glycol di (meth) acrylate and propylene glycol di (meth) acrylate; (Meth) acrylate such as neopentyl glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, neopentyl glycol di (Meth) acrylate, pentaerythritol tri (meth) acrylate, trimethylol propane tri (meth) acrylate, pentaerythritol tri (meth) (Meth) acrylate, divinylbenzene, and the like. Further, examples of the polyfunctional monomer include epoxy acrylate, polyester acrylate, and urethane acrylate.

공중합성 바이닐 모노머는 단독 사용 또는 병용할 수 있다. The copolymerizable vinyl monomer may be used alone or in combination.

이들 공중합성 바이닐 모노머 중 바람직하게는 탄소수가 6 이상인 지환식 탄화수소기를 갖는 (메트)아크릴산 지환식 탄화수소에스터를 들 수 있고, 더 바람직하게는 메타크릴산 사이클로 헥실을 들 수 있다. Among these copolymerized vinyl monomers, a (meth) acrylic acid alicyclic hydrocarbon ester having an alicyclic hydrocarbon group preferably having 6 or more carbon atoms is preferable, and cyclohexyl methacrylate is more preferable.

공중합성 바이닐 모노머는 반응 성분에 임의적으로 배합되고, 그 배합 비율은 반응 성분 100중량부에 대하여, 예컨대, 39중량부 이하, 바람직하게는 19중량부 이하, 더 바람직하게는 18중량부 이하다. The copolymerizable vinyl monomer is arbitrarily compounded in the reaction component and the blend ratio thereof is, for example, not more than 39 parts by weight, preferably not more than 19 parts by weight, more preferably not more than 18 parts by weight based on 100 parts by weight of the reaction component.

이들 공중합성 바이닐 모노머를 반응 성분에 배합시킴으로써, 수분산형 점착 제 조성물의 접착성을 향상시킬 수 있다. By blending these copolymerizable vinyl monomers with the reaction components, the adhesiveness of the aqueous dispersion type pressure sensitive adhesive composition can be improved.

수분산형 공중합체를 얻기 위해서는 상기 반응 성분을 예컨대, 유화 중합 등의 중합 방법에 의해 공중합한다. In order to obtain a water-dispersible copolymer, the above reaction components are copolymerized by a polymerization method such as emulsion polymerization.

유화 중합으로서는 예컨대, 상기 반응 성분과 함께, 중합개시제, 유화제, 필요에 따라 연쇄 이동제 등을 수중에서 적절히 배합하여 공중합한다. 보다 구체적으로는 예컨대, 일괄투입법(일괄중합법), 모노머 적하법, 모노머 에멀젼 적하법 등의 공지의 유화 중합법을 채용할 수 있다. 한편, 모노머 적하법으로서는 연속 적하 또는 분할 적하가 적절하게 선택된다. 반응 조건 등은 적절하게 선택되지만, 중합 온도는 예컨대, 20 내지 100℃이다.As the emulsion polymerization, for example, a polymerization initiator, an emulsifier and, if necessary, a chain transfer agent, etc., together with the above-mentioned reaction components, are appropriately compounded in water and copolymerized. More specifically, for example, known emulsion polymerization methods such as a batch addition method (batchwise polymerization), a monomer dropping method, and a monomer emulsion dropping method can be employed. On the other hand, as the monomer dropping method, continuous dropping or division dropping is appropriately selected. The reaction conditions and the like are appropriately selected, but the polymerization temperature is, for example, 20 to 100 占 폚.

중합개시제로서는 특별히 제한되지 않고, 유화 중합에 통상 사용되는 중합개시제가 사용된다. 예컨대, 2,2'-아조비스아이소뷰티로나이트릴, 2,2'-아조비스(2-메틸프로피온아미딘)2황산염, 2,2'-아조비스(2-메틸프로피온아미딘)2염산염, 2,2'-아조비스(2-아미디노프로페인)2염산염, 2,2'-아조비스[N-(2-카복시에틸)-2-메틸프로피온아미딘]수화물, 2,2'-아조비스(N,N'-다이메틸렌아이소뷰틸아미딘), 2,2'-아조비스[2-(2-이미다졸린-2-일)프로페인]2염산염 등의 아조계 개시제, 예컨대, 과황산칼륨, 과황산암모늄 등의 과황산염계 개시제, 예컨대 벤조일퍼옥사이드, t-뷰틸하이드로퍼옥사이드, 과산화수소 등의 과산화물계 개시제, 예컨대, 페닐 치환에탄 등의 치환에탄계 개시제, 예컨대, 방향족 카보닐화합물 등의 카보닐계 개시제, 예컨대, 과황산염과 아황산수소나트륨과의 조합, 과산화물과 아스코르브산나트륨과의 조합 등의 레독스계 개시제 등을 들 수 있다. The polymerization initiator is not particularly limited, and a polymerization initiator usually used in emulsion polymerization is used. Azo compounds such as 2,2'-azobisisobutyronitrile, 2,2'-azobis (2-methylpropionamidine) bisulfate, 2,2'-azobis (2-methylpropionamidine) dihydrochloride , 2,2'-azobis [N- (2-carboxyethyl) -2-methylpropionamidine] hydrate, 2,2'-azobis Azo initiators such as azobis (N, N'-dimethyleneisobutylamidine) and 2,2'-azobis [2- (2-imidazolin-2-yl) propane] dihydrochloride, Persulfate-based initiators such as potassium persulfate and ammonium persulfate such as peroxide initiators such as benzoyl peroxide, t-butyl hydroperoxide and hydrogen peroxide, and substituted initiators such as phenyl substituted ethanes, such as aromatic carbonyl And a redox initiator such as a combination of a persulfate and sodium hydrogen sulfite, a combination of a peroxide and sodium ascorbate, and the like.

이들 중합개시제는 단독 사용 또는 병용할 수 있다. These polymerization initiators may be used alone or in combination.

이들 중합개시제 중 바람직하게는 과황산염계 개시제, 더 바람직하게는 과황산암모늄이 사용된다. Among these polymerization initiators, a persulfate-based initiator, more preferably ammonium persulfate, is used.

중합개시제의 배합 비율은 적절히 선택되지만, 반응 성분 100중량부에 대하여, 예컨대, 0.001 내지 1중량부이다. The blending ratio of the polymerization initiator is appropriately selected, but is, for example, 0.001 to 1 part by weight per 100 parts by weight of the reaction component.

한편, 상기 반응 성분으로의 중합개시제의 배합전에, 또는 배합하면서, 또는 배합후에, 질소 치환에 의해서, 반응 성분 용액 중의 용존 산소 농도를 저감할 수도 있다. On the other hand, the concentration of dissolved oxygen in the reaction component solution may be reduced by nitrogen substitution before, during or after the addition of the polymerization initiator to the reaction component.

유화제로서는 특별히 제한되지 않고, 유화 중합에 통상 사용되는 공지의 유화제를 사용할 수 있다. 예컨대, 라우릴 황산나트륨, 라우릴 황산암모늄, 도데실벤젠설폰산나트륨, 폴리옥시에틸렌 라우릴황산나트륨, 폴리옥시에틸렌알킬에터황산나트륨, 폴리옥시에틸렌알킬페닐에터황산암모늄, 폴리옥시에틸렌알킬페닐에터황산나트륨, 폴리옥시에틸렌알킬설포석신산나트륨 등의 음이온계 유화제, 예컨대, 폴리옥시에틸렌알킬에터, 폴리옥시에틸렌알킬페닐에터, 폴리옥시에틸렌지방산에스터, 폴리옥시에틸렌 폴리옥시프로필렌블록 폴리머 등의 비이온계 유화제 등을 들 수 있다. The emulsifier is not particularly limited, and known emulsifiers commonly used in emulsion polymerization can be used. Examples thereof include sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzenesulfonate, sodium polyoxyethylene laurylsulfate, sodium polyoxyethylene alkylether sulfate, ammonium polyoxyethylene alkylphenylether sulfate, polyoxyethylene alkylphenylether Anionic emulsifiers such as sodium sulfate, polyoxyethylene alkylsulfosuccinic acid sodium and the like, for example, polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene fatty acid esters and polyoxyethylene polyoxypropylene block polymers Ionic emulsifiers and the like.

또한, 이들 음이온계 유화제나 비이온계 유화제에, 프로펜일기나 알릴에터기 등의 라디칼 중합성 작용기(반응성기)가 도입된 라디칼 중합성(반응성) 유화제(예컨대, HS-10(다이이치 공업 제약(주)제)) 등을 들 수 있다. Further, a radically polymerizable (reactive) emulsifier (for example, HS-10 (manufactured by Dai-ichi Kogyo Seiyaku Kogyo Co., Ltd.) having a radically polymerizable functional group (reactive group) such as a propenyl group or an allyl ether group is introduced into these anionic emulsifiers or nonionic emulsifiers Ltd.)) and the like.

이들 유화제는 단독 사용 또는 병용할 수 있다. 또한, 유화제의 배합 비율 은 반응 성분 100중량부에 대하여, 예컨대, 0.2 내지 10중량부, 바람직하게는 0.5 내지 5중량부이다. These emulsifiers may be used alone or in combination. The mixing ratio of the emulsifier is, for example, 0.2 to 10 parts by weight, preferably 0.5 to 5 parts by weight, based on 100 parts by weight of the reaction component.

연쇄 이동제는 필요에 따라, 수분산형 공중합체의 분자량을 조절하는 것으로서, 유화 중합에 통상 사용되는 연쇄 이동제를 사용할 수 있다. 예컨대, 1-도데칸싸이올, 머캅토아세트산, 2-머캅토에탄올, 싸이오글리콜산2-에틸헥실, 2,3-다이메틸카프토-1-프로판올 등의 머캅탄류 등을 들 수 있다. The chain transfer agent is used to adjust the molecular weight of the water-dispersible copolymer as required, and chain transfer agents usually used in emulsion polymerization can be used. Examples thereof include mercaptans such as 1-dodecanethiol, mercaptoacetic acid, 2-mercaptoethanol, 2-ethylhexyl thioglycolate, and 2,3-dimethylcapto-1-propanol.

이들 연쇄 이동제는 단독 사용 또는 병용할 수 있다. 또한, 연쇄 이동제의 배합 비율은 반응 성분 100중량부에 대하여, 예컨대, 0.001 내지 0.5중량부이다.These chain transfer agents may be used alone or in combination. The blending ratio of the chain transfer agent is, for example, 0.001 to 0.5 part by weight with respect to 100 parts by weight of the reaction component.

그리고, 이러한 유화 중합에 의해서, 얻어지는 수분산형 공중합체를 에멀젼(수분산액)으로서 조제할 수 있다. The obtained water-dispersible copolymer can be prepared as an emulsion (aqueous dispersion) by such emulsion polymerization.

한편, 수분산형 공중합체는 예컨대, 상기 반응 성분을 유화 중합 이외의 유기 용제를 사용하지 않는 방법에 의해서 중합한 후에 상기 유화제에 의해 물에 분산시켜 조제할 수도 있다. On the other hand, the water-dispersible copolymer may be prepared by, for example, polymerizing the above-mentioned reaction components by a method not using an organic solvent other than emulsion polymerization, and then dispersing it in water with the emulsifier.

또한, 수분산형 공중합체는 에멀젼의 안정성을 향상시킬 목적으로, 예컨대 암모니아수 등에 의해, 예컨대, pH 7 내지 9, 바람직하게는 pH 7 내지 8로 조정된다. For the purpose of improving the stability of the emulsion, the aqueous dispersion type copolymer is adjusted to pH 7 to 9, preferably pH 7 to 8, for example, by ammonia water or the like.

그리고, 상기에 의해 수득된 수분산형 공중합체와 가교제를 배합함으로써 본 발명의 수분산형 점착제 조성물을 얻는다. Then, the aqueous dispersion type pressure-sensitive adhesive composition of the present invention is obtained by blending the aqueous dispersion type copolymer obtained above with a crosslinking agent.

가교제로서는 카복실기(주로, (메트)아크릴산이 갖는 카복실기)와의 반응성을 갖는 가교제로서, 예컨대 카보다이이미드계 가교제, 아이소사이아네이트계 가교 제, 에폭시계 가교제, 옥사졸린계 가교제, 아지리딘계 가교제, 금속킬레이트계 가교제 등을 들 수 있다. 가교제로서는 바람직하게는 카보다이이미드계 가교제, 옥사졸린계 가교제를 들 수 있다. As the cross-linking agent, a cross-linking agent having reactivity with a carboxyl group (mainly a carboxyl group having (meth) acrylic acid)) can be used. Examples of the cross-linking agent include carbodiimide type crosslinking agents, isocyanate type crosslinking agents, epoxy type crosslinking agents, oxazoline type crosslinking agents, , Metal chelating crosslinking agents, and the like. The crosslinking agent is preferably a carbodiimide crosslinking agent or an oxazoline crosslinking agent.

또한, 가교제는 예컨대, 유용성 또는 수용성의 가교제 등을 사용할 수 있고, 혹은 수분산형(에멀젼 타입)으로서 조제된 가교제도 사용할 수 있다. 가교제(구체적으로는 옥사졸린계 가교제)로서, 바람직하게는 수분산형의 가교제, 더 바람직하게는 수분산형의 카보다이이미드계 가교제를 사용할 수 있다. The cross-linking agent may be, for example, an oil-soluble or water-soluble cross-linking agent, or a cross-linking agent prepared as an aqueous dispersion type (emulsion type). As the crosslinking agent (concretely, the oxazoline crosslinking agent), a water dispersible crosslinking agent, more preferably an aqueous dispersion type carbodiimide crosslinking agent, can be used.

수분산형 카보다이이미드계 가교제를 수분산형 공중합체의 카복실기와 반응성을 갖는 가교제로서 이용함으로써, 가교제의 배합후의 코팅액의 물리적 특성, 구체적으로는 점도에 있어서 변화가 일어나기 어렵고, 제조 공정에 있어서의 수분산형 점착제 조성물의 취급이 용이하게 된다. The use of the water dispersible carbodiimide crosslinking agent as a crosslinking agent having reactivity with the carboxyl group of the water dispersible copolymer makes it difficult to change the physical properties, specifically the viscosity, of the coating solution after the crosslinking agent is blended, The handling of the pressure-sensitive adhesive composition becomes easy.

카보다이이미드계 가교제는 카보다이이미드기를 갖는 화합물이다. 카보다이이미드기는 카보다이이미드(HN=C=NH)로부터 수소 원자가 하나 빠진 작용기(-N=C=NH) 또는 수소원자가 2개 빠진 작용기(-N=C=N-)이다. 이 카보다이이미드기는 카복실기와 반응할 수 있다. The carbodiimide crosslinking agent is a compound having a carbodiimide group. The carbodiimide group is a functional group (-N = C = NH) in which one hydrogen atom is missing from carbodiimide (HN = C = NH) or a functional group in which two hydrogen atoms are missing (-N = C = N-). This carbodiimide group can react with a carboxyl group.

보다 구체적으로는, 카보다이이미드계 가교제로서는 예컨대, 카보다이이미드기를 2개 이상 갖는 저분자 화합물 또는 고분자 화합물을 들 수 있다. More specifically, examples of the carbodiimide-based crosslinking agent include a low molecular weight compound or a high molecular weight compound having two or more carbodiimide groups.

카보다이이미드기를 갖는 저분자 화합물은 예컨대, 하기 화학식 a로 표시된다. The low molecular weight compound having a carbodiimide group is represented by, for example, the following formula (a).

[화학식 a](A)

R1-N=C=N-R2-N=C=N-R3 R 1 -N = C = NR 2 -N = C = NR 3

(상기 식에서, R1, R2 및 R3은 서로 상이하며, 탄화수소기를 나타낸다.)(Wherein R 1 , R 2 and R 3 are different from each other and represent a hydrocarbon group.)

카보다이이미드기를 갖는 고분자 화합물은 폴리카보다이이미드이고, 바람직하게는 물과의 친화성이 우수한 부위, 예컨대, 에틸렌옥사이드(-CH2-CH2-O-) 부위를 갖는 고분자 화합물을 들 수 있다. The polymer compound having a carbodiimide group is a polycarbodiimide, and preferably a polymer compound having a site having excellent affinity with water, for example, an ethylene oxide (-CH 2 -CH 2 -O-) site .

상기 카보다이이미드기를 갖는 고분자 화합물은 예컨대, 일반적으로 시판되고 있는 것을 이용할 수 있고, 예컨대, 수용성 카보다이라이트 V 시리즈(상품명:카보다이라이트 V-02, 카보다이라이트 V-02-L2, 카보다이라이트 V-04. 이상, 닛신보(주)제.), 예컨대, 에멀젼 타입(수분산형)의 카보다이라이트 E 시리즈(상품명: 카보다이라이트 E-01, 카보다이라이트 E-02, 카보다이라이트 E-04. 이상, 닛신보(주)제.) 등을 들 수 있다. Examples of the polymer compound having a carbodiimide group include commercially available products such as water-soluble carbodialite V series (trade name: carbodialite V-02, carbodialite V-02-L2, (Trade name: CARBODILITE E-01, CARBODILITE E-02, CARBODYLITE E-02, manufactured by Nisshinbo K.K.), for example, emulsion type E-04 or later, manufactured by Nisshinbo K.K.).

이들 카보다이이미드계 가교제는 단독 사용 또는 병용할 수 있다. These carbodiimide-based crosslinking agents may be used alone or in combination.

이들 카보다이이미드계 가교제 중, 바람직하게는 카보다이이미드기를 갖는 고분자 화합물을 들 수 있다. Of these carbodiimide-based crosslinking agents, preferred are polymer compounds having a carbodiimide group.

옥사졸린계 가교제는 옥사졸린기를 갖는 가교제로서, 예컨대, 아크릴 골격 또는 스타이렌 골격으로 이루어지는 주쇄를 포함하여, 그 주쇄의 측쇄에 옥사졸린기를 갖고 있는 것으로, 바람직하게는 아크릴 골격으로 이루어지는 주쇄를 포함하여, 그 주쇄의 측쇄에 옥사졸린기를 갖고 있는 옥사졸린기 함유 아크릴계 폴리머를 들 수 있다. The oxazoline crosslinking agent is a crosslinking agent having an oxazoline group and includes, for example, an acrylic skeleton or a styrene skeleton and an oxazoline group in the side chain of the main chain, preferably a main chain comprising an acrylic skeleton , And an oxazoline group-containing acrylic polymer having an oxazoline group in the side chain of the main chain thereof.

옥사졸린기로서는 예컨대, 2-옥사졸린기, 3-옥사졸린기, 4-옥사졸린기 등을 들 수 있고, 바람직하게는 2-옥사졸린기를 들 수 있다. Examples of the oxazoline group include a 2-oxazoline group, a 3-oxazoline group and a 4-oxazoline group, and a 2-oxazoline group is preferable.

2-옥사졸린기로서는 일반적으로, 하기 화학식 4로 표시된다. The 2-oxazoline group is generally represented by the following formula (4).

Figure 112008031822378-pat00004
Figure 112008031822378-pat00004

(화학식 4 중, R12, R13, R14 및 R15는 각각 독립적으로 수소 원자, 할로겐 원자, 알킬기, 아르알킬기, 페닐기 또는 치환페닐기를 나타낸다.)(Wherein R 12 , R 13 , R 14 and R 15 each independently represent a hydrogen atom, a halogen atom, an alkyl group, an aralkyl group, a phenyl group or a substituted phenyl group)

또한, 옥사졸린기 함유 폴리머는 물에 유화제를 이용하여 유화되어 있는 에멀젼 타입이나, 물에 용해되어 있는 수용액 타입으로서 사용될 수 있다. Further, the oxazoline group-containing polymer can be used as an emulsion type emulsified in water using an emulsifier or an aqueous solution type dissolved in water.

옥사졸린기 함유 폴리머는 통상의 일반 시판품을 사용할 수 있고, 구체적으로는 수용액 타입으로서, 에포크로스(EPOCROS) WS-500(고형분 40%, 주쇄: 아크릴계, pH 7 내지 9, 옥사졸린가 220g solid/eq., 니혼 쇼쿠바이사 제품), 에포크로스 WS-700(고형분 25%, 주쇄 : 아크릴계, pH 7 내지 9, 옥사졸린가 220g solid/eq., 니혼 쇼쿠바이사 제품) 등의 옥사졸린기 함유 아크릴계 폴리머를 들 수 있고, 예컨대, 에멀젼 타입으로서, 에포크로스 K-1000 시리즈(고형분 40%, 주쇄 : 스타이렌/아크릴계, 옥사졸린가 1100g solid/eq., pH 7 내지 9, 니혼 쇼쿠바이사 제품), 에 포크로스 K-2000 시리즈(고형분 40%, 주쇄 : 스타이렌/아크릴계, pH7 내지 9, 옥사졸린가 550g solid/eq., 니혼 쇼쿠바이사 제품) 등의 옥사졸린기 함유 아크릴/스타이렌계 폴리머 등을 들 수 있다. EPOCROS WS-500 (solid content: 40%, main chain: acrylic type, pH 7 to 9, oxazolidine value: 220 g solid / eq) as an aqueous solution type can be used as the oxazoline group- Containing acrylic polymer such as Epocross WS-700 (solid content 25%, main chain: acrylic, pH 7 to 9, 220 g solid / eq. Of oxazoline, solid / eq., Manufactured by Nihon Shokubai Co., Ltd.) (Main component: styrene / acrylic system, oxazoline 1100 g solid / eq., PH 7 to 9, manufactured by Nippon Shokubai Co., Ltd.) as an emulsion type, Oxazoline group-containing acrylic / styrene polymers such as Pocross K-2000 series (solid content 40%, main chain: styrene / acrylic, pH 7 to 9, oxazolidine 550 g solid / eq., Manufactured by Nippon Shokubai Co.) .

이들 옥사졸린계 가교제는 단독 또는 2종 이상 병용할 수 있다. These oxazoline crosslinking agents may be used alone or in combination of two or more.

이러한 옥사졸린계 가교제가 수분산형 점착제 조성물에 포함되면, 옥사졸린기가 주로 작용기(주로, (메트)아크릴산의 카복실기 등) 등과 비교적 저온에서 반응하기 때문에, 강고한 점착제층을 형성할 수 있다. When such an oxazoline crosslinking agent is included in the water dispersion type pressure-sensitive adhesive composition, the oxazoline group mainly reacts at a relatively low temperature with a functional group (mainly, a carboxyl group of (meth) acrylic acid) or the like, so that a strong pressure-sensitive adhesive layer can be formed.

가교제(카보다이이미드계 가교제)의 배합 비율은 수분산형 공중합체(즉, 수분산액의 고형분) 100중량부에 대하여 0.07 내지 4중량부, 바람직하게는 0.08 내지 3중량부, 더 바람직하게는 0.1 내지 2중량부이다. 또한, 가교제가 옥사졸린계 가교제인 경우에는 그 배합 비율은 수분산형 공중합체(즉, 수분산액의 고형분) 100중량부에 대하여, 예컨대, 0.07 내지 1.5중량부, 바람직하게는 0.1 내지 1중량부, 더 바람직하게는 0.1 내지 0.3중량부이다. The blending ratio of the crosslinking agent (carbodiimide type crosslinking agent) is 0.07 to 4 parts by weight, preferably 0.08 to 3 parts by weight, more preferably 0.1 to 3 parts by weight, relative to 100 parts by weight of the water dispersion type copolymer (i.e., solid content of the aqueous dispersion) 2 parts by weight. When the cross-linking agent is an oxazoline-based cross-linking agent, the mixing ratio thereof is, for example, 0.07 to 1.5 parts by weight, preferably 0.1 to 1 part by weight, more preferably 0.1 to 1 part by weight, based on 100 parts by weight of the aqueous dispersion copolymer (that is, More preferably 0.1 to 0.3 parts by weight.

상기 범위보다 적으면 고온 분위기 하에서의 점착제층의 발포를 억제할 수 없고, 한편, 상기 범위보다 많으면, 수분산형 점착제 조성물의 접착성(점착성), 특히 가열 및 가습시의 유리 기판으로의 접착력이 저하된다. 한편, 가열 및 가습시의 접착력(90°박리 접착력 : 박리속도[10mm/min])은 2.0N/25mm 이상이 바람직하다. If the amount is less than the above range, foaming of the pressure-sensitive adhesive layer in a high-temperature atmosphere can not be suppressed. If the amount is larger than the above range, the adhesiveness (tackiness) of the aqueous dispersion type pressure-sensitive adhesive composition, particularly, . On the other hand, the adhesive force (90 deg. Peeling adhesion: peeling speed [10 mm / min]) during heating and humidification is preferably 2.0 N / 25 mm or more.

이 수분산형 공중합체와 가교제의 배합에 의해 수분산형 공중합체가 가교된다. 보다 구체적으로는 가교제가 카보다이이미드계 가교제인 경우에는 수분산형 공중합체의 카복실기가, 카보다이이미드계 가교제의 카보다이이미드기와 반응하여, 수분산형 공중합체가 가교된다. 또한, 가교제가 옥사졸린계 가교제인 경우에는 수분산형 공중합체의 카복실기가, 옥사졸린계 가교제의 옥사졸린기와 반응하여 수분산형 공중합체가 가교된다. The water dispersible copolymer is crosslinked by the combination of the water dispersible copolymer and the crosslinking agent. More specifically, in the case where the cross-linking agent is a carbodiimide-based cross-linking agent, the carboxyl group of the water-dispersible copolymer reacts with the carbodiimide group of the carbodiimide-based cross-linking agent to crosslink the water-dispersed copolymer. When the crosslinking agent is an oxazoline crosslinking agent, the carboxyl group of the water dispersible copolymer reacts with the oxazoline group of the oxazoline crosslinking agent to crosslink the water dispersible copolymer.

한편, 수분산형 공중합체와 가교제를 배합한 후에, 가교 반응을 촉진시키기 위해서, 예컨대, 80 내지 150℃, 바람직하게는 80 내지 120℃에서, 예컨대, 1 내지 10분간 가열할 수도 있다. 한편, 이 가열은 후술하는 점착제층의 형성시의 건조에 의한 가열을 이용할 수도 있다. On the other hand, after the water dispersion type copolymer and the crosslinking agent are mixed, heating may be performed at 80 to 150 ° C, preferably 80 to 120 ° C, for example, for 1 to 10 minutes in order to accelerate the crosslinking reaction. On the other hand, this heating may be performed by drying by drying at the time of forming a pressure-sensitive adhesive layer described later.

또한, 획득된 수분산형 점착제 조성물에는 필요에 따라, 점도 조정제, 박리 조정제, 가소제, 연화제, 충전제, 착색제(안료, 염료 등), 노화 방지제, 계면 활성제 등, 수분산형 점착제 조성물에 통상 첨가되는 첨가제를 적절히 첨가할 수도 있다. 이들 첨가제의 배합 비율은 특별히 제한되지 않고, 적절히, 선택할 수 있다. The obtained aqueous dispersion type pressure-sensitive adhesive composition may further contain additives usually added to the aqueous dispersion type pressure-sensitive adhesive composition, such as a viscosity adjusting agent, a peeling agent, a plasticizer, a softening agent, a filler, a coloring agent (pigment, dye, etc.), an anti- May be appropriately added. The compounding ratio of these additives is not particularly limited and can be appropriately selected.

이와 같이 조제된 수분산형 점착제 조성물(고형분)의 겔분율은 예컨대, 80 내지 95중량%, 바람직하게는 80 내지 93중량%이다. 겔분율이 상기 값보다 낮으면, 이 수분산형 점착제 조성물을 점착형 광학 필름에 적용하여 고온 분위기 하에서 사용했을 때에 발포가 생기는 경우가 있다. 또한, 겔분율이 상기 값보다 높으면, 수분산형 점착제 조성물의 접착력이 저하되는 경우가 있다. The gel fraction of the aqueous dispersion type pressure-sensitive adhesive composition (solid content) thus prepared is, for example, 80 to 95% by weight, preferably 80 to 93% by weight. When the gel fraction is lower than the above-mentioned value, the aqueous dispersion type pressure-sensitive adhesive composition is applied to a pressure-sensitive adhesive optical film and foaming may occur when used in a high temperature atmosphere. If the gel fraction is higher than the above value, the adhesive strength of the aqueous dispersion type pressure-sensitive adhesive composition may be lowered.

또한, 겔분율은 수분산형 점착제 조성물을 테플론 시트(등록 상표)에 피복하고, 이것을 아세트산 에틸에 7일간 침지했을 때에, 다음 수학식 2로 산출할 수 있 다. The gel fraction can be calculated from the following formula (2) when the aqueous dispersion type pressure-sensitive adhesive composition is coated on a Teflon sheet (registered trademark) and immersed in ethyl acetate for 7 days.

[수학식 2]&Quot; (2) "

겔분율(중량%)=(침지후의 테플론 시트(등록 상표)에 부착하는 수분산형 점착제 조성물의 중량/침지전의 수분산형 점착제 조성물의 중량)×100 Gel fraction (% by weight) = (weight of water dispersion type pressure-sensitive adhesive composition attached to Teflon sheet (registered trademark) after immersion / weight of water dispersion type pressure-sensitive adhesive composition before immersion) 占 100

이하, 도 1을 참조하여 본 발명의 점착 필름의 일 실시 형태인 점착형 광학 필름의 제조 방법에 대하여 설명한다. Hereinafter, a method of manufacturing a pressure-sensitive adhesive optical film as an embodiment of the pressure-sensitive adhesive film of the present invention will be described with reference to Fig.

점착형 광학 필름을 얻기 위해서는 우선, 광학 필름(1)을 준비한다. In order to obtain an adhesive optical film, first, an optical film (1) is prepared.

광학 필름(1)으로서는 광학 특성을 가지며, 액정 디스플레이 등에 접착되는 필름이면 특별히 제한되지 않으며, 예컨대 편광 필름, 위상차 필름, 휘도 향상 필름, 시야각 확대 필름 등을 들 수 있다. The optical film (1) is not particularly limited as long as it has optical properties and is adhered to a liquid crystal display or the like, and examples thereof include a polarizing film, a retardation film, a luminance improving film and a viewing angle enlarging film.

편광 필름으로서는 편광자의 한면 또는 양면에, 투명 보호 필름이 마련된 것을 사용할 수 있다. As the polarizing film, those having a transparent protective film provided on one or both sides of the polarizer can be used.

편광자로서는 특별히 제한되지 않으며, 예컨대 폴리바이닐알코올계 필름, 부분 포르말화 폴리바이닐알코올계 필름, 에틸렌·아세트산바이닐공중합체계 부분 비누화필름 등의 친수성 고분자 필름에, 요오드나 2색성 염료 등의 2색성 물질로 염색하여 1축 연신한 것이나, 폴리바이닐알코올의 탈수 처리물이나 폴리염화바이닐의 탈염산 처리물 등 폴리엔계 배향 필름 등을 들 수 있다. 바람직하게는 폴리바이닐알코올계필름을 요오드로 염색하여 1축연신한 편광자를 들 수 있다. The polarizer is not particularly limited. For example, a hydrophilic polymer film such as a polyvinyl alcohol film, a partially porous polyvinyl alcohol film, or an ethylene / vinyl acetate copolymerization system partially saponified film may be coated with a dichroic material such as iodine or a dichromatic dye And polyene oriented films such as dehydrated products of polyvinyl alcohol and dehydrochlorinated products of polyvinyl chloride, and the like. Preferably, the polarizer is a monoaxially stretched polarizer obtained by dyeing a polyvinyl alcohol-based film with iodine.

투명 보호 필름으로서는 예컨대, 폴리에틸렌테레프탈레이트나 폴리에틸렌나프탈레이트 등의 폴리에스터계 폴리머 필름, 다이아세틸 셀룰로스나 트라이아세틸 셀룰로스 등의 셀룰로스계 폴리머 필름, 폴리메틸메타크릴레이트 등의 아크릴계 폴리머 필름, 폴리스타이렌이나 아크릴로나이트릴·스타이렌공중합체(AS 수지) 등의 스타이렌계 폴리머 필름, 폴리카보네이트계 폴리머 필름 등을 들 수 있다. 또한, 폴리에틸렌, 폴리프로필렌, 사이클로 또는 노르보르넨 구조를 갖는 폴리올레핀, 에틸렌·프로필렌 공중합체 등의 폴리올레핀계 폴리머 필름, 염화바이닐계 폴리머 필름, 나일론, 방향족 폴리아마이드 등의 아마이드계 폴리머 필름, 이미드계 폴리머 필름, 설폰계 폴리머 필름, 폴리에터설폰계 폴리머 필름, 폴리에터에터케톤계 폴리머 필름, 폴리페닐렌설파이드계 폴리머 필름, 바이닐알코올계 폴리머 필름, 염화바이닐리덴계 폴리머 필름, 바이닐뷰티랄계 폴리머 필름, 아릴레이트계 폴리머 필름, 폴리옥시메틸렌계 폴리머 필름, 에폭시계 폴리머 필름, 또는 상기 폴리머의 블렌드물의 필름 등도 들 수 있다. Examples of the transparent protective film include polyester-based polymer films such as polyethylene terephthalate and polyethylene naphthalate, cellulose-based polymer films such as diacetyl cellulose and triacetyl cellulose, acrylic polymer films such as polymethyl methacrylate, Styrene-based polymer films such as nitrile-styrene copolymer (AS resin), and polycarbonate-based polymer films. Examples of the amide-based polymer film include polyolefin-based polymer films such as polyethylene, polypropylene, cyclo- or norbornene-based polyolefins, ethylene-propylene copolymers and the like, chlorinated vinyl polymer films, nylon and aromatic polyamides, Film, a sulfonated polymer film, a polyether sulfone type polymer film, a polyetheretherketone type polymer film, a polyphenylene sulfide type polymer film, a vinyl alcohol type polymer film, a chlorinated vinylidene type polymer film, a vinyl butyral type polymer film , An arylate-based polymer film, a polyoxymethylene-based polymer film, an epoxy-based polymer film, or a film of a blend of the above-mentioned polymers.

투명 보호 필름은 아크릴계, 우레탄계, 아크릴 우레탄계, 에폭시계, 실리콘계 등의 열경화형, 자외선경화형의 수지의 경화층으로서 형성할 수도 있다. The transparent protective film may be formed as a cured layer of a thermosetting or ultraviolet curing resin such as acrylic, urethane, acrylic urethane, epoxy or silicone.

투명 보호 필름으로서는 바람직하게는 셀룰로스계 폴리머를 들 수 있다. 투명 보호 필름의 두께는 특별히 제한되지 않고, 예컨대, 500㎛ 이하, 바람직하게는 1 내지 300㎛, 더 바람직하게는 5 내지 200㎛이다. The transparent protective film is preferably a cellulose-based polymer. The thickness of the transparent protective film is not particularly limited, and is, for example, 500 탆 or less, preferably 1 to 300 탆, and more preferably 5 to 200 탆.

편광자와 투명 보호 필름을 접착 처리하기 위해서는 예컨대, 아이소사이아네이트계 접착제, 폴리바이닐알코올계 접착제, 젤라틴계 접착제, 바이닐계 접착제, 라텍스계 접착제, 수계 폴리에스터 접착제 등을 이용하여 접착한다. In order to bond the polarizer and the transparent protective film to each other, for example, an isocyanate-based adhesive, a polyvinyl alcohol-based adhesive, a gelatin-based adhesive, a vinyl-based adhesive, a latex-based adhesive, or a water-based polyester adhesive is used.

위상차 필름으로서는 고분자 소재를 1축 또는 2축 연신 처리하여 이루어지는 복굴절성 필름, 액정 폴리머의 배향 필름, 액정 폴리머의 배향층을 필름으로 하여 지지한 것 등을 들 수 있다. 위상차 필름의 두께는 특별히 제한되지 않고, 예컨대, 20 내지 150㎛이다. Examples of the retardation film include a birefringent film obtained by uniaxially or biaxially stretching a polymer material, an orientation film of a liquid crystal polymer, and a film supported with an orientation layer of a liquid crystal polymer as a film. The thickness of the retardation film is not particularly limited, and is, for example, 20 to 150 mu m.

고분자 소재로서는 예컨대, 폴리바이닐알코올, 폴리바이닐뷰티랄, 폴리메틸바이닐에터, 폴리하이드록시에틸아크릴레이트, 하이드록시에틸 셀룰로스, 하이드록시프로필 셀룰로스, 메틸 셀룰로스, 폴리카보네이트, 폴리아릴레이트, 폴리설폰, 폴리에틸렌테레프탈레이트, 폴리에틸렌나프탈레이트, 폴리에터설폰, 폴리페닐렌 설파이드, 폴리페닐렌 옥사이드, 폴리알릴설폰, 폴리바이닐알코올, 폴리아마이드, 폴리이미드, 폴리올레핀, 폴리염화바이닐, 셀룰로스계 중합체, 또는 이들의 2원계, 3원계 각종 공중합체, 그래프트 공중합체, 블렌드물 등을 들 수 있다. 이들 고분자소재는 연신 등에 의해 배향물(연신 필름)이 된다. Examples of the polymer material include polyvinyl alcohol, polyvinyl butyral, polymethyl vinyl ether, polyhydroxyethyl acrylate, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, polycarbonate, polyarylate, polysulfone, There may be mentioned polyolefins such as polyethylene terephthalate, polyethylene naphthalate, polyethersulfone, polyphenylene sulfide, polyphenylene oxide, polyallylsulfone, polyvinyl alcohol, polyamide, polyimide, polyolefin, polyvinyl chloride, Ternary system, various ternary copolymers, graft copolymers, and blended materials. These polymer materials become oriented products (stretched films) by stretching or the like.

액정성 폴리머로서는 예컨대, 액정 배향성을 부여하는 공액성의 직선상 원자단(메소겐)이 폴리머의 주쇄나 측쇄에 도입된 주쇄형이나 측쇄형의 각종의 것 등을 들 수 있다. 주쇄형의 액정성 폴리머로서는 예컨대, 굴곡성을 부여하는 스페이서부에서 메소겐기를 결합한 구조로, 구체적으로는 네마틱 배향성의 폴리에스터계 액정성 폴리머, 디스코틱 폴리머나 콜레스테릭 폴리머 등을 들 수 있다. 측쇄형의 액정성 폴리머로서는 예컨대, 폴리실록산, 폴리아크릴레이트, 폴리메타크릴레이트 또는 폴리말로네이트를 주쇄 골격으로 하고, 측쇄로서 공액성의 원자단으로 이루어지는 스페이서부를 통해서 네마틱 배향 부여성의 파라 치환 환상 화합물 단위로 이루어지는 메소겐부를 갖는 것 등을 들 수 있다. 이들 액정성 폴리머는 예컨대, 유 리판 위에 형성한 폴리이미드나 폴리바이닐 알코올 등의 박막의 표면을 러빙 처리한 것, 산화 규소를 사방(斜方) 증착한 것 등의 배향 처리면 상에 액정성 폴리머의 용액을 전개하여 열 처리함으로써 얻어진다. Examples of the liquid crystalline polymer include various types of main chain type and side chain type in which conjugated straight-chain atomic groups (mesogens) for imparting liquid crystal alignability are introduced into the main chain or side chain of the polymer. As the main chain type liquid crystalline polymer, for example, a structure in which a mesogen group is bonded at a spacer portion imparting flexibility, specifically, a nematic-oriented polyester-based liquid crystalline polymer, a discotic polymer or a cholesteric polymer . Examples of the side chain type liquid crystalline polymer include polysaccharides such as polysiloxane, polyacrylate, polymethacrylate or polymalonate as the main chain skeleton and spacer moieties having conjugated atomic groups as side chains, , And the like. These liquid crystalline polymers can be obtained, for example, by subjecting a surface of a thin film such as polyimide or polyvinyl alcohol formed on a glass plate to rubbing treatment, a liquid crystal polymer on the oriented surface such as silicon oxide obliquely deposited, And then heat-treating the solution.

또한, 위상차 필름은 예컨대, 각종 파장 필름이나 액정층의 복굴절에 의한 착색이나 시야각 등의 확대를 목적으로 한 것, 기타 사용 목적에 따라서, 적절히, 위상차를 갖는 것이면 되고, 2종 이상의 위상차 필름을 적층하여 위상차 등의 광학 특성을 제어한 것 등이여도 된다. The retardation film may be any one having a phase difference suitably depending on the purpose of use, for example, for the purpose of increasing the coloration or the viewing angle by various birefringence of the liquid crystal layer or various wavelength films, And controlling the optical characteristics such as the phase difference.

휘도 향상 필름으로서는 예컨대, 유전체의 다층 박막이나 굴절률 이방성이 상이한 박막 필름의 다층 적층체 등, 소정 편광축의 직선 편광은 투과하고 다른 광은 반사하는 특성을 나타내는 것, 콜레스테릭 액정 폴리머의 배향 필름이나 그 배향 액정층을 필름 기재 상에 지지한 것 등, 좌회전 또는 우회전 중 어느하나의 원편광은 반사하고 다른 광은 투과하는 특성을 나타내는 것 등을 들 수 있다. As the brightness enhancement film, for example, a multilayer laminate of a dielectric multilayer or a multilayer laminate of a thin film having a different refractive index anisotropy may be used. Examples of the brightness enhancement film include those that transmit linearly polarized light of a predetermined polarization axis and reflect other light, A material in which the alignment liquid crystal layer is supported on a film base material, and a material in which one of the left-handed circularly polarized light and the right-handed circularly polarized light is reflected and the other light is transmitted.

시야각 확대 필름은 액정 디스플레이의 화면을 화면에 수직이 아닌 약간 기울어진 방향에서 본 경우에도, 화상이 비교적 선명하게 보이도록 시야각을 넓히기 위한 필름으로, 예컨대, 위상차 필름, 액정 폴리머 등의 배향 필름이나 투명 기재상에 액정 폴리머 등의 배향층을 지지한 것 등을 들 수 있다. 시야각 확대 필름으로서 사용되는 위상차 필름에는 면 방향으로 2축으로 연신된 복굴절을 갖는 폴리머 필름이나, 면 방향으로 1축으로 연신되고 두께 방향으로도 연신된 두께 방향의 굴절률을 제어한 복굴절을 갖는 폴리머나 경사 배향 필름 같은 2 방향 연신 필름 등이 사용된다. The viewing angle expanding film is a film for widening the viewing angle so that the image can be seen relatively clearly even when the screen of the liquid crystal display is viewed in a slightly tilted direction rather than in a vertical direction on the screen. Examples thereof include an orientation film such as a retardation film, And those in which an alignment layer such as a liquid crystal polymer is supported on a substrate. A retardation film to be used as the viewing angle expanding film includes a polymer film having birefringence stretched biaxially in the surface direction or a polymer film stretched uniaxially in the surface direction and stretched in the thickness direction and having a birefringence controlled in the refractive index in the thickness direction A two-direction stretched film such as an oblique oriented film, or the like is used.

그리고, 광학 필름(1)의 한 면에, 수분산형 점착제 조성물로 이루어지는 점착제층(2)을 마련한다. On one side of the optical film (1), a pressure-sensitive adhesive layer (2) comprising an aqueous dispersion type pressure-sensitive adhesive composition is provided.

점착제층(2)을 마련하기 위해서는 예컨대, 상기 광학 필름(1)에, 점착제층(2)이 형성된 이형 시트(3)로부터 점착제층(2)을 전사한다. 점착제층(2)이 형성된 이형 시트(3)는, 이형 시트(3)에 나이프 코팅법 등의 공지의 코팅 방법에 의해 수분산형 점착제 조성물을 직접 코팅한다. 그 후, 이것을 예컨대, 80 내지 150℃에서, 1 내지 10분간 가열하여 건조함으로써 점착제층(2)을 이형 시트(3)의 위에 마련한다. 또한, 점착제층(2)을 전사하기 위해서는 점착제층(2)이 형성된 이형 시트(3)를 광학 필름(1)에 접합한 후, 점착제층(2)으로부터 이형 시트(3)를 박리한다. In order to provide the pressure-sensitive adhesive layer 2, for example, the pressure-sensitive adhesive layer 2 is transferred to the optical film 1 from the release sheet 3 on which the pressure-sensitive adhesive layer 2 is formed. The release sheet 3 on which the pressure-sensitive adhesive layer 2 is formed is directly coated with the water-dispersible pressure-sensitive adhesive composition on the release sheet 3 by a known coating method such as a knife coating method. Thereafter, this is heated and dried, for example, at 80 to 150 DEG C for 1 to 10 minutes to provide the pressure-sensitive adhesive layer 2 on the release sheet 3. [ In order to transfer the pressure-sensitive adhesive layer 2, the release sheet 3 having the pressure-sensitive adhesive layer 2 formed thereon is bonded to the optical film 1, and then the release sheet 3 is peeled from the pressure-sensitive adhesive layer 2.

또한, 점착제층(2)을 마련하기 위해서는 예컨대, 광학 필름(1)에 수분산형 점착제 조성물을 나이프 코팅법 등의 공지의 코팅 방법에 의해, 직접 코팅하고, 그 후, 이것을 예컨대, 80 내지 150℃에서, 1 내지 10분간 가열하여, 건조하도록 할 수도 있다. In order to prepare the pressure-sensitive adhesive layer 2, for example, an aqueous dispersion type pressure-sensitive adhesive composition is directly coated on the optical film 1 by a known coating method such as a knife coating method, For 1 to 10 minutes, and then dried.

또한, 도 2에 나타낸 바와 같이, 광학 필름(1)에는 점착제층(2)과의 접착력(투묘력)을 향상시키기 위해서, 미리 적절히 하도층(4)을 마련하는 등의 하도 처리를 실시할 수 있다. 2, the optical film 1 may be subjected to a priming treatment such as the provision of a primer layer 4 in advance in order to improve the adhesive force (tearing force) with the pressure-sensitive adhesive layer 2 have.

하도층(4)은 예컨대, 수지를 포함하며, 이러한 수지로서는 예컨대, 폴리아크릴 수지, 폴리우레탄 수지, 폴리에스터 수지 등을 들 수 있고, 바람직하게는 이들 수지를 반응성 작용기로 변성한 수지 등을 들 수 있다. Examples of the resin include a polyacrylic resin, a polyurethane resin, and a polyester resin. Preferably, the resin layer 4 is modified with a reactive functional group. .

반응성 작용기로서는 예컨대, 옥사졸린기, 카복실기, 하이드록실기, 아미노기를 들 수 있고, 바람직하게는 옥사졸린기를 들 수 있다. Examples of the reactive functional group include an oxazoline group, a carboxyl group, a hydroxyl group and an amino group, and preferably an oxazoline group.

옥사졸린기로서는 상기와 동일한 것을 들 수 있다. The oxazoline group may be the same as described above.

반응성 작용기로 변성한 수지로서, 보다 구체적으로는 예컨대, 반응성 작용기가 옥사졸린기인 경우에는 아크릴 골격 또는 스타이렌 골격으로 이루어지는 주쇄를 포함하며, 그 주쇄의 측쇄에 옥사졸린기를 갖고 있는 것으로서, 바람직하게는 상기와 동일한 옥사졸린기 함유 아크릴계 폴리머를 들 수 있다. More specifically, for example, when the reactive functional group is an oxazoline group, the resin includes a main chain composed of an acrylic skeleton or a styrene skeleton, and has an oxazoline group in the side chain of the main chain, And the same oxazoline group-containing acrylic polymer as mentioned above.

옥사졸린기 함유 아크릴계 폴리머는 그 수 평균 분자량이, 예컨대, 5000 이상, 바람직하게는 10000 이상이며, 통상, 1000000 이하가 바람직하다. 수평균 분자량이 5000보다 낮으면, 하도층의 강도가 부족해서 응집 파괴를 일으켜, 투묘력을 향상할 수 없는 경우가 있다. 수평균 분자량이 1000000보다 높으면, 작업성이 뒤떨어지는 경우가 있다. 또한, 옥사졸린기 함유 아크릴계 폴리머는 그 옥사졸린가가, 예컨대, 1500g solid/eq. 이하, 바람직하게는 1200g solid/eq. 이하다. 옥사졸린가가 1500g solid/eq. 보다 크면, 분자 중에 포함되는 옥사졸린기의 양이 적어져서, 투묘력을 향상할 수 없는 경우가 있다. The number average molecular weight of the oxazoline group-containing acrylic polymer is, for example, 5000 or more, preferably 10000 or more, and usually 1000000 or less. If the number average molecular weight is lower than 5,000, the strength of the undercoating layer is insufficient, causing cohesive failure, and the anchoring force may not be improved. If the number average molecular weight is higher than 1,000,000, the workability may be poor. Further, the oxazoline group-containing acrylic polymer has an oxazoline value of, for example, 1500 g solid / eq. Preferably 1200 g solid / eq. Respectively. Oxazolidine is 1500 g solid / eq. , The amount of the oxazoline group contained in the molecule is decreased, and the anchoring power may not be improved in some cases.

이와 같은 수지는 단독 또는 병용하여 사용된다. 이와 같은 수지는 통상, 그 고형분의 배합 비율이 0.01 내지 15중량%, 바람직하게는 0.05 내지 5 중량%가 되도록, 유기용제나 물 등에 용해 또는 분산되어 조제되어 있다. Such a resin is used alone or in combination. Such a resin is usually prepared by dissolving or dispersing in an organic solvent or water such that the blending ratio of the solid content is 0.01 to 15% by weight, preferably 0.05 to 5% by weight.

하도층(4)을 마련하기 위해서는 예컨대, 광학 필름(1)에 수지를 포함하는 하도액(용액 또는 분산액)을 코팅법, 디핑법, 스프레이법 등의 공지의 도포 방법에 의해, 직접 도포하여 건조하는 방법을 들 수 있다. In order to prepare the undercoat layer 4, for example, the undercoating liquid (solution or dispersion) containing a resin is directly applied to the optical film 1 by a known coating method such as coating method, dipping method, .

하도층(4)의 두께는 건조전의 두께가 예컨대, 1 내지 500㎛, 바람직하게는 10 내지 100㎛, 더 바람직하게는 20 내지 50㎛이고, 건조후의 두께가 예컨대, 1 내지 1000nm, 바람직하게는 10 내지 500nm, 더 바람직하게는 20 내지 400nm이 되도록 설정한다. The thickness of the undercoat layer 4 is preferably 1 to 500 占 퐉, preferably 10 to 100 占 퐉, more preferably 20 to 50 占 퐉, and the thickness after drying is, for example, 1 to 1000 nm, 10 to 500 nm, and more preferably 20 to 400 nm.

이형 시트(3)로서는 종이, 폴리에틸렌, 폴리프로필렌, 폴리에틸렌테레프탈레이트 등의 합성 수지 필름, 예컨대, 고무시트, 천, 부직포, 네트, 발포 시트나 금속 박, 또는 이들 적층 시트체 등을 들 수 있다. 이형 시트(3)의 표면에는 점착제층(2)으로부터의 박리성을 높이기 위해서, 필요에 따라 실리콘 처리, 장쇄 알킬 처리, 불소 처리 등의 처리(박리 처리)가 이루어져도 된다. Examples of the release sheet 3 include synthetic resin films such as paper, polyethylene, polypropylene and polyethylene terephthalate such as rubber sheets, cloths, nonwoven fabrics, nets, foam sheets and metal foils, and these laminated sheet bodies. The surface of the release sheet 3 may be subjected to a treatment such as a silicone treatment, a long-chain alkyl treatment or a fluorine treatment (peeling treatment) if necessary in order to improve the peeling property from the pressure-sensitive adhesive layer 2.

점착제층(2)의 두께(건조후 두께)는 예컨대, 1 내지 100㎛, 바람직하게는 5 내지 50㎛, 더 바람직하게는 10 내지 30㎛의 범위로 설정된다. The thickness (thickness after drying) of the pressure-sensitive adhesive layer 2 is set in the range of, for example, 1 to 100 占 퐉, preferably 5 to 50 占 퐉, more preferably 10 to 30 占 퐉.

상기 수분산형 점착제 조성물로 이루어지는 점착제층(2)은 하기 시험에 의한 90℃에서의 신장도가, 200% 이하, 바람직하게는 180% 이하, 더 바람직하게는 150% 이하, 특히 바람직하게는 100% 이하, 가장 바람직하게는 50% 이하, 통상, 0% 이상이다. The pressure-sensitive adhesive layer (2) comprising the aqueous dispersion type pressure-sensitive adhesive composition has an elongation at 90 DEG C of 200% or less, preferably 180% or less, more preferably 150% or less, particularly preferably 100% , Most preferably not more than 50%, usually not less than 0%.

90℃에서의 신장도 시험 : 수분산형 점착제 조성물을 가열하여 점착제층을 조제하고, 이것을 단면적 4.6mm2, 길이 30mm의 원주 형상으로 성형하여, 시험편을 제작한다. 이어서, 시험편을 90℃에서 1 시간 방치한 후, 초기 시험편의 길이 L0를 측정한다. 그 후, 시험편의 한쪽 끝을 고정하고, 시험편의 다른 끝에 12g의 추를 달아 시험편을 90℃에서 2시간 늘어뜨리고, 2시간 늘어뜨린 후의 시험편의 길이 L1(mm)을 측정하여, 다음 수학식 1에 의해 신장도를 산출한다. Elongation test at 90 캜: The pressure-sensitive adhesive layer composition is prepared by heating the aqueous dispersion type pressure-sensitive adhesive composition, and the pressure-sensitive adhesive layer is molded into a cylindrical shape having a cross-sectional area of 4.6 mm 2 and a length of 30 mm. Then, the specimen is measured after left for one hour at 90 ℃, the length L 0 of the initial test pieces. Thereafter, one end of the test piece was fixed and the weight of 12 g was placed on the other end of the test piece. The test piece was hanged at 90 캜 for 2 hours, and the length L 1 (mm) of the test piece after hanging for 2 hours was measured. 1 < / RTI >

[수학식 1][Equation 1]

신장도(%)=(L1-L0)/L0×100Elongation (%) = (L 1 -L 0 ) / L 0 × 100

90℃에서의 신장도가 상기한 범위를 초과하면 고온분위기 하에 있어서의 점착제층(2)의 내발포성이 저하되어 발포를 억제할 수 없다. If the extensibility at 90 캜 exceeds the above-mentioned range, the foamability of the pressure-sensitive adhesive layer (2) under a high-temperature atmosphere is lowered and foaming can not be suppressed.

또한, 점착제층(2)은 23℃에서의 신장도가, 예컨대, 150% 이하, 바람직하게는 130% 이하, 더 바람직하게는 100% 이하, 특히 바람직하게는 80% 이하, 가장 바람직하게는 50% 이하, 통상, 0% 이상이다. The pressure-sensitive adhesive layer (2) has an elongation at 23 ° C of, for example, not more than 150%, preferably not more than 130%, more preferably not more than 100%, particularly preferably not more than 80% %, Usually at least 0%.

한편, 23℃에서의 신장도는 상기 90℃에서의 신장 시험에 있어서, 90℃를 23℃로 변경한 외에는 상기 90℃에서의 신장 시험과 동일하게 하여, 신장도를 산출할 수 있다. On the other hand, the elongation at 23 ° C can be calculated in the same manner as in the elongation test at 90 ° C except that the 90 ° C is changed to 23 ° C in the elongation test at 90 ° C.

이와 같이, 광학 필름(1)의 한 면에, 수분산형 점착제 조성물로 이루어지는 점착제층(2)을 마련함으로써, 점착형 광학 필름을 얻을 수 있다. As described above, the pressure-sensitive adhesive layer (2) comprising an aqueous dispersion type pressure-sensitive adhesive composition is provided on one side of the optical film (1) to obtain a pressure-sensitive adhesive optical film.

이렇게 하여 얻어지는 점착형 광학 필름은 편광 필름, 위상차 필름, 휘도 향상 필름, 시야각 확대 필름 등의 점착형 광학 필름 등으로서, 각종 산업 용도에 적합하게 사용된다. The adhesive optical film thus obtained is used as a polarizing film, a retardation film, a luminance improving film, an adhesive optical film such as a viewing angle enlarging film, etc., and is suitably used in various industrial applications.

본 발명의 수분산형 점착제 조성물은 유리 기판에 접착하는 경우에도, 높은 접착성을 갖기 때문에, 유리 기판에 점착형 광학 필름을 강고하게 접착할 수 있다. INDUSTRIAL APPLICABILITY Since the water dispersible pressure-sensitive adhesive composition of the present invention has high adhesiveness even when adhered to a glass substrate, the adhesive optical film can be firmly adhered to the glass substrate.

또한, 이 점착형 광학 필름은 높은 내열성이나 내습성을 갖고 있기 때문에, 고온 고습 분위기에서도 우수한 내구성을 얻을 수 있다. Further, since this adhesive optical film has high heat resistance and moisture resistance, excellent durability can be obtained even in a high temperature and high humidity atmosphere.

특히, 본 발명의 수분산형 점착제 조성물 및 그 수분산형 점착제 조성물로 이루어지는 점착제층을 구비한 점착형 광학 필름은 고온 및 고습에 있어서의 기포 및 변형의 발생을 유효하게 방지할 수 있다. 이 때문에, 광학 특성의 저하를 유효하게 방지할 수 있다. In particular, the pressure-sensitive adhesive optical film comprising the pressure-sensitive adhesive layer comprising the aqueous dispersion type pressure-sensitive adhesive composition of the present invention and the aqueous dispersion type pressure-sensitive adhesive composition can effectively prevent the occurrence of bubbles and deformation at high temperature and high humidity. Therefore, deterioration of optical characteristics can be effectively prevented.

한편, 상기 설명에서는 본 발명의 점착 필름을, 점착형 광학 필름을 예시하여 설명했지만, 광학 필름 이외의 피착체에 접착되는 점착 필름으로서 이용할 수도 있다. 또한, 본 발명의 점착 필름은 예컨대, 점착 시트, 점착 테이프 등으로서도 이용된다. In the above description, the adhesive film of the present invention is described as an adhesive optical film, but it can also be used as an adhesive film to be adhered to an adherend other than an optical film. The adhesive film of the present invention is also used as an adhesive sheet, an adhesive tape, and the like.

한편, 상기 설명에 있어서, 점착제층(2) 및 필요에 따라 마련되는 하도층(4)을 광학 필름(1)의 한면에 설치했지만, 광학 필름(1)의 양면에 설치할 수도 있다. In the above description, the pressure-sensitive adhesive layer (2) and the undercoat layer (4) as required are provided on one side of the optical film (1), but may be provided on both sides of the optical film (1).

한편, 통상의 수분산형 점착제 조성물로서는 피착체로의 밀착성을 높이기 위해서는 로진계 수지, 엘라스토머 등의 점착 부여 수지 등을 첨가하지만, 본 발명의 수분산형 점착제 조성물은 수분산형이면서도, 그와 같은 점착 부여 수지를 첨가하지 않고도 밀착성을 높일 수 있기 때문에, 저비용으로 밀착성이 높은 수분산형 점착제 조성물 및 이러한 수분산형 점착제 조성물로 이루어지는 점착제층을 구비하고 있는 점착 필름을 얻을 수 있다. On the other hand, as a conventional aqueous dispersion type pressure-sensitive adhesive composition, a pressure-sensitive adhesive resin such as a rosin-based resin or an elastomer is added in order to enhance the adhesion to an adherend. However, the aqueous dispersion type pressure-sensitive adhesive composition of the present invention is an aqueous dispersion type, It is possible to obtain a pressure-sensitive adhesive film comprising a water-dispersible pressure-sensitive adhesive composition having high adhesiveness at low cost and a pressure-sensitive adhesive layer comprising such an aqueous dispersion type pressure-sensitive adhesive composition.

실시예Example

이하에 실시예 및 비교예를 들어, 본 발명을 보다 구체적으로 설명한다. 단, 본 발명은 이하의 실시예 및 비교예에 조금도 제한되지 않는다. 한편, 이하의 설명에 있어서, 「부」 및 「%」는 특별히 명기하지 않는 한 중량 기준이다. Hereinafter, the present invention will be described in more detail by way of examples and comparative examples. However, the present invention is not limited to the following Examples and Comparative Examples at all. In the following description, " part " and "% " are by weight unless otherwise specified.

실시예 1 Example 1

(모노머프리에멀젼의 조제)(Preparation of monomer-free emulsion)

용기에 아크릴산뷰틸 92부, 메타크릴산 6부, 모노[폴리(프로필렌옥사이드)메타크릴레이트]인산에스터(프로필렌옥사이드의 평균 중합도 약 5.0) 2부 및 3-메타크릴로일옥시프로필-트라이메톡시실란(KBM-503, 신에츠화학(주)제) 0.03부를 가하고 혼합하여 반응 성분의 혼합물을 조제했다. 이어서, 조제한 반응 성분의 혼합물 388g에 반응성 유화제 아크아론 HS-10(다이이치 공업 제약(주)) 46.6g 및 이온 교환수 346g을 가하고 호모게나이저(토쿠슈기카(주)제)를 이용하여, 5분간, 5000(1/min)로 교반하여 강제 유화하여, 모노머프리에멀젼을 조제했다. The vessel was charged with 92 parts of butyl acrylate, 6 parts of methacrylic acid, 2 parts of mono [poly (propylene oxide) methacrylate] phosphoric acid ester (average degree of polymerization of propylene oxide about 5.0) and 3 parts of 3-methacryloyloxypropyl-trimethoxy 0.03 part of silane (KBM-503, Shin-Etsu Chemical Co., Ltd.) was added and mixed to prepare a mixture of reaction components. Subsequently, 466 g of reactive emulsifier Arkaron HS-10 (manufactured by Daiichi Kogyo Pharmaceutical Co., Ltd.) and 346 g of ion-exchanged water were added to 388 g of the prepared mixture of reaction components, and using homogenizer (manufactured by Tokushu Kika Kogyo Co., Ltd.) The mixture was stirred for 5 minutes at 5000 (1 / min), and forced emulsification was carried out to prepare a monomer-free emulsion.

(수분산형 공중합체의 에멀젼의 조제) (Preparation of Emulsion of Water-dispersible Copolymer)

냉각관, 질소도입관, 온도계 및 교반기를 구비한 반응 용기에 상기에서 조제한 모노머 프리에멀젼 중의 156g 및 이온 교환수 219g을 투입하고, 이어서 반응 용기를 질소치환하고, 과황산 암모늄 0.023g(투입된 모노머프리 에멀젼의 고형분 100부에 대하여, 0.03부)를 첨가하여, 65℃에서, 2.5시간 중합했다. 이어서, 잔부의 모노머프리에멀젼 625g에 과황산암모늄 0.217g(잔부의 모노머프리에멀젼의 고형분 100부에 대하여 0.07부)를 첨가하고, 이것을 반응 용기에 3시간에 걸쳐 적하하며, 그 후 질소 치환하면서 70℃에서 3 시간 중합하여, 고형분 40%의 수분산형 공중합 체의 에멀젼(수분산액)을 획득했다 156 g of the monomer-free emulsion prepared above and 219 g of ion-exchanged water were introduced into a reaction vessel equipped with a condenser, a nitrogen inlet tube, a thermometer and a stirrer. Subsequently, the reaction vessel was purged with nitrogen and 0.023 g of ammonium persulfate 0.03 part based on 100 parts of the solid content of the emulsion) was added and the mixture was polymerized at 65 占 폚 for 2.5 hours. Subsequently, 0.217 g of ammonium persulfate (0.07 part with respect to 100 parts of the solid content of the monomer pre-emulsion) was added to 625 g of the remaining monomer-free emulsion, and this was dropped into the reaction vessel over 3 hours, ° C for 3 hours to obtain an emulsion (aqueous dispersion) of an aqueous dispersion copolymer having a solid content of 40%

(수분산형 점착제 조성물의 조제)(Preparation of water dispersion type pressure-sensitive adhesive composition)

획득된 에멀젼을 실온까지 냉각하고, 10% 암모니아수를 첨가하여 pH를 8로 조정하고, 카보다이이미드계 가교제(카보다이라이트 V-04, 수용성 타입, 닛신보(주)제)를 또한 에멀젼의 고형분(수분산형 공중합체) 100부에 대하여 0.1부 첨가하여, 수분산형 점착제 조성물을 조제했다. The obtained emulsion was cooled to room temperature, and the pH was adjusted to 8 by adding 10% ammonia water. Then, a carbodiimide type crosslinking agent (carbodialite V-04, water-soluble type, manufactured by Nisshinbo) (Water dispersion type copolymer) in an amount of 0.1 part based on 100 parts of the aqueous dispersion type pressure-sensitive adhesive composition.

(점착형 광학 필름의 제작)(Production of adhesive optical film)

조제한 수분산형 점착제 조성물을, 박리제로 처리한 폴리에스터 필름으로 이루어진 이형 시트에 코팅하고, 100℃에서 2분간 가열하여 건조함으로써 두께 23㎛의 점착제층을 형성했다. The prepared aqueous dispersion type pressure-sensitive adhesive composition was coated on a release sheet composed of a polyester film treated with a release agent, heated at 100 캜 for 2 minutes and dried to form a pressure-sensitive adhesive layer having a thickness of 23 탆.

또한, 미리 하도 처리한 편광 필름을 준비했다. 하도 처리로서는 우선, 옥사졸린기 함유 아크릴계 폴리머(에포크로스 WS-700, (주)니혼쇼쿠바이제)를, 물과 에탄올의 혼합 용매(용량비로 1:1)에서 고형분이 0.25중량%이 되도록 희석한 하도제 용액을 조제했다. 이어서, 이 하도제 용액을 와이어 바 #5를 이용하여 편광 필름의 한 면에 도포하고, 40℃에서 2분간 가열하여 건조함으로써 하도층을 마련했다. Further, a polarizing film prepared in advance was prepared. First, as an undercoat treatment, an oxazoline group-containing acrylic polymer (Epochros WS-700, Nippon Shokubai Co., Ltd.) was diluted to a solid content of 0.25% by weight in a mixed solvent of water and ethanol To prepare a base stock solution. Subsequently, this undercoating solution was coated on one side of the polarizing film by using a wire bar # 5, heated at 40 占 폚 for 2 minutes, and dried to provide a subbing layer.

또한, 상기 편광 필름은 폴리바이닐알코올 필름을 요오드 수용액 중에서 연신하고, 건조후, 이 편광자 양측에 투명 보호 필름으로서 트라이아세틸셀룰로스 필름을 접착함으로써 제작했다. The polarizing film was produced by stretching a polyvinyl alcohol film in an aqueous iodine solution, drying the film, and then attaching a triacetylcellulose film as a transparent protective film to both sides of the polarizer.

이어서, 이 편광 필름을 위상차 필름(NAZ-# 195-0.3, 닛토덴코(주)제)의 위 에, 하도층이 마련되어 있지 않은 면과 위상차 필름이 접합되도록 적층했다. 이로써, 하도층이 마련된 편광 필름과 위상차 필름이 적층된 광학 필름을 제작했다. Subsequently, the polarizing film was laminated on a retardation film (NAZ- # 195-0.3, manufactured by Nitto Denko Corporation) such that a surface not provided with a primer layer and a retardation film were bonded to each other. Thus, an optical film having a polarizing film and a retardation film laminated with a primer layer was produced.

이어서, 점착제층을 광학 필름의 하도층 위에 적층하여, 점착형 광학 필름을 제작했다(도 2 참조). Subsequently, a pressure-sensitive adhesive layer was laminated on the undercoat layer of the optical film to produce a pressure-sensitive optical film (see Fig. 2).

실시예 2 Example 2

실시예 1에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.1부 대신에, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.3부를 첨가한 이외에는 실시예 1과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. 0.3 part of a carbodiimide type crosslinking agent (Carbodialite V-04) was added in place of 0.1 part of a carbodiimide type crosslinking agent (Carbodialite V-04) in the preparation of the aqueous dispersion type pressure- Except that a dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 1, and then a pressure-sensitive adhesive optical film was produced.

실시예 3Example 3

(모노머프리에멀젼의 조제)(Preparation of monomer-free emulsion)

용기에, 아크릴산뷰틸 88부, 아크릴산 5부, 메타크릴산 사이클로헥실 5부, 모노[폴리(프로필렌옥사이드)메타크릴레이트]인산에스터(프로필렌옥사이드의 평균 중합도 약 5.0) 2부 및 3-메타크릴로일옥시프로필-트라이메톡시실란(KBM-503, 신에츠화학(주)제) 0.03부를 가하고 혼합하여, 반응 성분의 혼합물을 조제했다. 이어서, 조제한 반응 성분의 혼합물 388g에 반응성 유화제 아크아론 HS-10(다이이치 공업 제약(주)) 46.6g 및 이온 교환수 346g을 가하고, 호모게나이저(토쿠슈기카(주)제)를 이용하여, 5분간, 5000(1/min)로 교반하여 강제 유화하여, 모노머프리에멀젼 을 조제했다. To the vessel were added 88 parts of butyl acrylate, 5 parts of acrylic acid, 5 parts of cyclohexyl methacrylate, 2 parts of mono [poly (propylene oxide) methacrylate] phosphoric acid ester (average degree of polymerization of propylene oxide: about 5.0) (KBM-503, Shin-Etsu Chemical Co., Ltd.) 0.03 part were added and mixed to prepare a mixture of reaction components. Subsequently, 466 g of a reactive emulsifier Arkaron HS-10 (manufactured by Daiichi Kogyo Pharmaceutical Co., Ltd.) and 346 g of ion-exchanged water were added to 388 g of the prepared mixture of reaction components, and the mixture was homogenized using a homogenizer (manufactured by Tokushu Kika Kogyo Co., , And stirred for 5 minutes at 5000 (1 / min) to perform forced emulsification to prepare a monomer-free emulsion.

(수분산형 공중합체의 에멀젼의 조제) (Preparation of Emulsion of Water-dispersible Copolymer)

냉각관, 질소도입관, 온도계 및 교반기를 갖춘 반응 용기에, 상기에서 조제한 모노머프리에멀젼중의 78g 및 이온 교환수 219g을 투입하고, 이어서, 반응 용기를 질소치환하고, 과황산 암모늄 0.004g(투입된 모노머프리 에멀젼의 고형분 100부에 대하여 0.01부)를 첨가하여, 65℃에서 2.5시간 중합했다. 이어서, 잔부의 모노머프리에멀젼의 702.5g에 과황산암모늄 0.244g(잔부의 모노머프리에멀젼의 고형분 100부에 대하여, 0.07부)을 첨가하고, 이것을 반응 용기에 3시간에 걸쳐 적하하며, 그 후, 질소 치환하면서, 75℃에서 3 시간 중합하여, 고형분 40%의 수분산형 공중합체의 에멀젼(수분산액)을 획득했다. 78 g of the monomer-free emulsion prepared above and 219 g of ion-exchanged water were charged into a reaction vessel equipped with a stirrer, a cooling tube, a nitrogen inlet tube, a thermometer and a stirrer. Subsequently, the reaction vessel was purged with nitrogen and 0.004 g 0.01 part based on 100 parts of the solid content of the monomer-free emulsion) was added, and the mixture was polymerized at 65 DEG C for 2.5 hours. Subsequently, 0.244 g of ammonium persulfate (0.07 part based on 100 parts of the solid content of the monomer pre-emulsion) was added to 702.5 g of the remaining monomer-free emulsion, and this was dropped into the reaction vessel over 3 hours, And polymerization was carried out at 75 캜 for 3 hours while replacing nitrogen to obtain an emulsion (aqueous dispersion) of a water-dispersed copolymer having a solid content of 40%.

(수분산형 점착제 조성물의 조제)(Preparation of water dispersion type pressure-sensitive adhesive composition)

획득된 에멀젼을 실온까지 냉각하고, 10% 암모니아수를 첨가하여 pH를 8로 조정하고, 카보다이이미드계 가교제(카보다이라이트 V-04)를 또한 에멀젼의 고형분(수분산형 공중합체) 100부에 대하여 0.5부 첨가하여, 수분산형 점착제 조성물을 조제했다. The obtained emulsion was cooled to room temperature, and the pH was adjusted to 8 by adding 10% ammonia water. Then, a carbodiimide crosslinking agent (carbodialite V-04) was added to 100 parts of the solid content of the emulsion 0.5 part were added to prepare an aqueous dispersion type pressure-sensitive adhesive composition.

(점착형 광학 필름의 제작)(Production of adhesive optical film)

조제한 수분산형 점착제 조성물을, 박리제로 처리한 폴리에스터 필름으로 이루어지는 이형 시트에 코팅하고 100℃에서 2분간 가열 처리하여, 두께 23㎛의 점착제층을 형성했다. The prepared aqueous dispersion type pressure-sensitive adhesive composition was coated on a release sheet comprising a polyester film treated with a release agent and heat-treated at 100 占 폚 for 2 minutes to form a pressure-sensitive adhesive layer having a thickness of 23 占 퐉.

이어서, 점착제층을 실시예 1과 동일한 광학 필름의 하도층에 적층하여, 점 착형 광학 필름을 제작했다(도 2 참조). Subsequently, a pressure-sensitive adhesive layer was laminated on the undercoat layer of the same optical film as in Example 1 to produce a viscous-type optical film (see Fig. 2).

실시예 4 Example 4

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 V-04) 1부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Except that 1 part of a carbodiimide-based crosslinking agent (Carbodialite V-04) was added instead of 0.5 part of a carbodiimide crosslinking agent (Carbodialite V-04) in the preparation of the aqueous dispersion type pressure- , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and then a pressure-sensitive adhesive optical film was produced.

실시예 5 Example 5

실시예 3에 있어서의 수분산형 공중합체의 에멀젼의 조제에 있어서, 적하 중합에 있어서의 과황산 암모늄 0.244g(잔부의 모노머프리에멀젼의 고형분 100부에 대하여, 0.07부) 대신에, 과황산암모늄 0.175g(잔부의 모노머프리에멀젼의 고형분 100부에 대하여, 0.05부)을 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 공중합체의 에멀젼(수분산액)을 조제하고, 이어서 수분산형 점착제 조성물을 조제하며, 이어서 점착형 광학 필름을 제작했다. In the preparation of the emulsion of the water dispersion type copolymer in Example 3, an aqueous solution of ammonium persulfate 0.175 (0.07 part by mass based on 100 parts by mass of the solid content of the remaining monomer pre-emulsion) (aqueous dispersion) was prepared in the same manner as in Example 3, except that 0.05 part by mass of the monomer (s) (the remaining part of the solid content of the monomer-free emulsion was added in an amount of 0.05 part) And then an adhesive optical film was produced.

실시예 6Example 6

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 V-04) 1부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착 제 조성물을 조제하고, 계속해서 점착형 광학 필름을 제작했다. Except that 1 part of a carbodiimide-based crosslinking agent (Carbodialite V-04) was added instead of 0.5 part of a carbodiimide crosslinking agent (Carbodialite V-04) in the preparation of the aqueous dispersion type pressure- , An aqueous adhesive composition was prepared in the same manner as in Example 3, and a pressure-sensitive adhesive optical film was produced.

실시예 7Example 7

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 V-04) 2부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Except that 2 parts of a carbodiimide type crosslinking agent (carbodialite V-04) was added instead of 0.5 part of a carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure-sensitive adhesive composition of Example 3 , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and then a pressure-sensitive adhesive optical film was produced.

실시예 8Example 8

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 V-04) 3부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Except that 3 parts of a carbodiimide type crosslinking agent (carbodialite V-04) was added instead of 0.5 part of a carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure-sensitive adhesive composition of Example 3 , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and then a pressure-sensitive adhesive optical film was produced.

실시예 9Example 9

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 E-04, 에멀젼 타입, 닛신보(주)제) 1부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. (Carbodialite E-04, emulsion type, Nisshinbo) was used in place of 0.5 part of the carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure- (1) was added to the dispersion, and then an aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3. Subsequently, a pressure-sensitive optical film was produced.

실시예 10Example 10

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 E-04, 에멀젼 타입, 닛신보(주)제) 0.5부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. (Carbodialite E-04, emulsion type, Nisshinbo) was used in place of 0.5 part of the carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure- (Manufactured by Nippon Kayaku Co., Ltd.), 0.5 part was added, followed by preparing a pressure-sensitive adhesive optical film by the same method as in Example 3.

실시예 11Example 11

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신, 카보다이이미드계 가교제(카보다이라이트 E-04, 에멀젼 타입, 닛신보(주)제) 2부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. (Carbodialite E-04, emulsion type, Nisshinbo) was used in place of 0.5 part of the carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure- (Manufactured by Mitsubishi Kagaku Kogyo K.K.), 2 parts were added, and a dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and then a pressure-sensitive adhesive optical film was produced.

비교예 1 Comparative Example 1

실시예 1에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제를 첨가하지 않은 것 외에는, 실시예 1과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서 점착형 광학 필름을 제작했다. A dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 1 except that no carbodiimide type crosslinking agent was added in preparation of the aqueous dispersion type pressure-sensitive adhesive composition of Example 1, and then an adhesive optical film was produced did.

비교예 2 Comparative Example 2

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제를 첨가하지 않은 것 외에는 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서 점착형 광학 필름을 제작했다. A dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3 except that no carbodiimide-based crosslinking agent was added in the preparation of the aqueous dispersion type pressure-sensitive adhesive composition in Example 3, and a pressure-sensitive adhesive optical film was subsequently prepared .

비교예 3Comparative Example 3

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.1부 대신, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.0005부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Except that 0.0005 part of a carbodiimide type crosslinking agent (carbodialite V-04) was added instead of 0.1 part of a carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure-sensitive adhesive composition of Example 3 , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and then a pressure-sensitive adhesive optical film was produced.

비교예 4Comparative Example 4

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신에, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.001부를 첨가한 외에는 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. 0.001 part of a carbodiimide crosslinking agent (carbodiaryl V-04) was added in place of 0.5 part of a carbodiimide crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure- , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and subsequently, a pressure-sensitive optical film was produced.

비교예 5Comparative Example 5

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신에, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.05부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서 점착형 광학 필름을 제작했다. 0.05 part of a carbodiimide type crosslinking agent (carbodialite V-04) was added in place of 0.5 part of a carbodiimide type crosslinking agent (carbodialite V-04) in the preparation of the aqueous dispersion type pressure- , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and a pressure-sensitive adhesive optical film was subsequently produced.

비교예 6Comparative Example 6

실시예 3에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 카보다이이미드계 가교제(카보다이라이트 V-04) 0.5부 대신에, 카보다이이미드계 가교제(카보다이라이트 V-04) 5부를 첨가한 외에는, 실시예 3과 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. 5 parts of a carbodiimide type crosslinking agent (Carbodialite V-04) was added in place of 0.5 part of a carbodiimide type crosslinking agent (Carbodialite V-04) in the preparation of the aqueous dispersion type pressure- , An aqueous dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 3, and subsequently, a pressure-sensitive adhesive optical film was produced.

(평가)(evaluation)

1) 점착제층의 신장도 1) Elongation degree of the pressure-sensitive adhesive layer

실시예 1 내지 11 및 비교예 1 내지 6에 있어서의 수분산형 점착제 조성물을 100℃에서 2분간 가열함으로써 두께 23㎛의 점착제층을 각각 조제했다. 점착제층을 냉각한 후, 주걱으로 200mm×30mm의 평면 직사각형 시트 형상으로 성형했다. 다음으로, 이것을 손으로 권회함으로써 단면적 4.6mm2, 길이 30mm의 원주 형상으로 성형하여 시험편을 제작했다. 이어서, 시험편의 길이 방향 양쪽 끝의 10mm의 부분을 클립으로 각각 끼었다. 그리고, 23℃(실온) 및 90℃의 분위기 하에서, 1시간 방치하여, 시험편을 양생시켰다. Sensitive adhesive compositions of Examples 1 to 11 and Comparative Examples 1 to 6 were heated at 100 占 폚 for 2 minutes to prepare pressure sensitive adhesive layers each having a thickness of 23 占 퐉. After the pressure-sensitive adhesive layer was cooled, it was formed into a flat rectangular sheet of 200 mm x 30 mm with a spatula. Next, this was manually rolled into a cylindrical shape having a cross-sectional area of 4.6 mm 2 and a length of 30 mm to prepare a test piece. Then, 10 mm portions at both ends in the longitudinal direction of the test piece were each clipped. Then, the test piece was allowed to stand for 1 hour in an atmosphere of 23 占 폚 (room temperature) and 90 占 폚 to cure the test piece.

그 후, 시험편에 있어서의 클립으로 끼워져 있지 않은 길이 방향 중간의 길이(초기의 길이) L0(mm)를 미리 자로 측정했다. 이어서, 시험편의 한쪽 끝의 클립 을 고정하고, 시험편의 다른 끝의 클립에 12g의 추를 달아 23℃(실온) 및 90℃의 분위기 하에서, 시험편을 2시간 늘어뜨렸다. 2시간 늘어뜨린 후에 있어서의, 시험편에 있어서의 클립으로 고정되어 있지 않은 길이 방향 중간의 길이 L1(mm)을 자로 각각 측정했다. 한편, 초기의 길이 L0는 약 10mm이다. Thereafter, the length (initial length) L 0 (mm) in the longitudinal direction of the test piece not sandwiched by the clip was measured in advance. Then, a clip at one end of the test piece was fixed, and 12 g of weight was attached to the clip at the other end of the test piece, and the test piece was suspended for 2 hours under the atmosphere of 23 캜 (room temperature) and 90 캜. The length L 1 (mm) in the longitudinal direction of the test piece after being stuck for 2 hours, which is not fixed by the clip, was measured as a letter. On the other hand, the initial length L 0 is about 10 mm.

그리고, 다음 수학식 1로부터 23℃에서의 2시간의 신장도 및 90℃에서의 2시간의 신장도를 각각 산출했다. 그 결과를 표 1에 나타낸다. From the following equation (1), the degree of elongation at 23 DEG C for 2 hours and the degree of elongation at 90 DEG C for 2 hours were respectively calculated. The results are shown in Table 1.

[수학식 1][Equation 1]

신장도(%)=(L1-L0)/L0×100Elongation (%) = (L 1 -L 0 ) / L 0 × 100

2) 겔분율 2) Gel fraction

실시예 1 내지 11 및 비교예 1 내지 6의 수분산형 점착제 조성물(약 100mg)을, 우선 미리 중량 측정한 테플론 시트(등록 상표 품번 : NTF-1122) 및 연사(12cm)로 감싸고, 이 감싼 꾸러미를 중량 측정했다. 이어서, 50ml 유리병에 이 꾸러미를 넣고, 이어서 아세트산 에틸을 충분히 가하고 유리병을 밀봉하여, 실온에서 7일간 침지했다. 그 후, 침지한 꾸러미를 꺼내서, 테플론 시트(등록 상표)에 부착된 아세트산 에틸을 닦아낸 후, 이 꾸러미를 130℃에서 2시간, 건조기로 건조했다. 그 후, 건조 후의 꾸러미를 중량 측정했다. 그리고, 하기의 수학식 3에 의해, 겔분율을 산출했다. (About 100 mg) of Examples 1 to 11 and Comparative Examples 1 to 6 were first wrapped in a pre-weighed Teflon sheet (registered trademark part number: NTF-1122) and twisted yarn (12 cm), and the wrapped package And weighed. Then, the package was put in a 50 ml glass bottle, followed by sufficiently adding ethyl acetate, sealing the glass bottle, and dipping at room temperature for 7 days. Thereafter, the dipped package was taken out and the ethyl acetate adhered to the Teflon sheet (registered trademark) was wiped off, and the package was dried in a dryer at 130 DEG C for 2 hours. Thereafter, the package after drying was weighed. Then, the gel fraction was calculated by the following equation (3).

[수학식 3]&Quot; (3) "

겔분율(중량%)={(C-A)/(B-A)}×100Gel fraction (% by weight) = {(C-A) / (BA)} 100

한편, 식 중의 기호의 상세에 대해서는 이하와 같다. Details of symbols in the formula are as follows.

A(g) : 테플론 시트(등록 상표) 및 연사의 총 중량(겉포장의 중량) A (g): Teflon sheet (registered trademark) and the total weight of the twist yarn (weight of the outer package)

B(g) : 테플론 시트(등록 상표) 및 연사와, 수분산형 점착제 조성물과의 아세트산 에틸 침지, 건조 전의 총 중량 B (g): the total weight of the Teflon sheet (registered trademark) and the twisted yarn before and after the immersion of the ethyl acetate with the aqueous dispersion type pressure-

C(g) : 테플론 시트(등록 상표) 및 연사와, 수분산형 점착제 조성물의 아세트산 에틸 침지, 건조 후의 총 중량C (g): Teflon sheet (registered trademark) and twist yarn, the total weight of the aqueous dispersion type pressure-sensitive adhesive composition after immersion in ethyl acetate and drying

그 결과를 표 1에 나타낸다. The results are shown in Table 1.

3) 유리 접착성 3) Glass adhesion

실시예 1 내지 11 및 비교예 1 내지 6에 의해 획득된 점착형 광학 필름을 폭 25mm로 절단하고, 이것을 유리판(코닝 #1737, 코닝(주)제)에 접착하여 2kg의 고무 롤러를 1 왕복시켜 압착하고, 50℃, 0.5MPa의 오토클레이브 중에 15분간 방치하고, 이어서, 25℃로 냉각하여, 90°박리 접착력(박리속도 10mm/min)을 측정했다(초기 접착력). The adhesive optical films obtained in Examples 1 to 11 and Comparative Examples 1 to 6 were cut into a width of 25 mm and adhered to a glass plate (Corning # 1737, manufactured by Corning Incorporated), and a 2-kg rubber roller was reciprocated one time Pressed and allowed to stand in an autoclave at 50 ° C and 0.5 MPa for 15 minutes and then cooled to 25 ° C to measure a 90 ° peeling adhesive force (peeling rate 10 mm / min) (initial adhesive force).

또한, 오토클레이브 중에 방치한 후, 또한, 60℃ 및 60℃/90% RH의 분위기 하에서, 40시간 각각 방치하고, 이어서, 25℃로 냉각하여, 90°박리 접착력(박리 속도 10mm/min)을 각각 측정했다. 그 결과를, 표 1에 나타낸다. Further, after being left in an autoclave, it was allowed to stand for 40 hours in an atmosphere of 60 DEG C and 60 DEG C / 90% RH, and then cooled to 25 DEG C to obtain a 90 DEG peel adhesion force (peel rate 10 mm / min) Respectively. The results are shown in Table 1.

한편, 유리 접착성은 박리 접착력의 값이 높을수록 양호한 것을 나타낸다. On the other hand, the higher the value of the peel adhesion force, the better the glass adhesion.

4) 점착형 광학 필름의 가열 발포성4) Heat foaming of adhesive optical film

실시예 1 내지 11 및 비교예 1 내지 6의 점착형 광학 필름을 폭 235mm×길이 310mm의 크기로 절단하고, 이것을 두께 0.7mm의 유리판(코닝#1737, 코닝(주)제)에 접착했다. 그 후, 50℃, 0.5MPa의 오토클레이브 중에 15분간 방치한 후, 90℃로 가열한 분위기 하에서, 500시간 방치했다. 그 후, 점착형 광학 필름의 발포의 유무를 육안에 의해 관찰했다. The adhesive optical films of Examples 1 to 11 and Comparative Examples 1 to 6 were cut into a size of 235 mm in width × 310 mm in length and adhered to a glass plate (Corning # 1737, Corning) having a thickness of 0.7 mm. Thereafter, the mixture was allowed to stand in an autoclave at 50 DEG C and 0.5 MPa for 15 minutes, and then left in an atmosphere heated to 90 DEG C for 500 hours. Thereafter, the presence or absence of foaming of the adhesive optical film was visually observed.

한편, 점착형 광학 필름에 있어서의 발포의 유무를 하기의 기준으로 관찰했다. On the other hand, the presence or absence of foaming in the adhesive optical film was observed based on the following criteria.

○ : 발포가 발견되지 않았다 ○: No foaming was found

△ : 발포가 약간 발견되었다 ?: Some foaming was found

× : 발포가 발견되었다X: Foaming was found

Figure 112008031822378-pat00005
Figure 112008031822378-pat00005

표 1 중의 약자를 이하에 나타낸다. Abbreviations in Table 1 are shown below.

PAM-200 : Sipomer PAM-200(모노[폴리(프로필렌옥사이드)메타크릴레이트]인산에스터(프로필렌옥사이드의 평균중합도 약 5.0), 로디어 닛카(주)제) PAM-200: Sipomer PAM-200 (mono [poly (propylene oxide) methacrylate] phosphoric acid ester (average degree of polymerization of propylene oxide: about 5.0)

KBM-503 : 3-메타크릴로일옥시프로필-트라이메톡시실란(신에츠화학(주)제) KBM-503: 3-methacryloyloxypropyl-trimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.)

HS-10 : 반응성 유화제 아크아론 HS-10(다이이치 공업 제약(주)) HS-10: Reactive emulsifier Ark Aaron HS-10 (Daiichi Kogyo Pharmaceutical Co., Ltd.)

V-04 : 카보다이이미드계 가교제(카보다이라이트 V-04, 수용성 타입, 닛신보(주)제) V-04: Carbodiimide type crosslinking agent (Carbodialite V-04, water-soluble type, manufactured by Nisshinbo K.K.)

E-04 : 카보다이이미드계 가교제(카보다이라이트 E-04, 에멀젼 타입, 닛신보(주)제)E-04: Carbodiimide type crosslinking agent (carbodialite E-04, emulsion type, manufactured by Nisshinbo)

실시예 12Example 12

(모노머프리에멀젼의 조제)(Preparation of monomer-free emulsion)

용기에, 아크릴산 뷰틸 88부, 아크릴산 5부, 메타크릴산 사이클로헥실 5부, 모노[폴리(프로필렌옥사이드)메타크릴레이트]인산에스터(프로필렌옥사이드의 평균중합도 약 5.0, Sipomer PAM-200, 로디어 닛카사 제품) 2부 및 3-메타크릴로일옥시프로필-트라이메톡시실란(KBM-503, 신에츠화학사 제품) 0.03부를 가하고 혼합하여, 반응 성분을 조제했다. 이어서, 조제한 반응 성분 388g에 반응성 유화제 아크아론 HS-10(다이이치 공업 제약사) 46.6g 및 이온 교환수 109g을 가하고, 호모게나이저(토쿠슈기카(주)제)를 이용하여, 5분간, 5000(1/min)로 교반하고 강제 유화하여, 모노머프리에멀젼을 조제했다. To the vessel were added 88 parts of butyl acrylate, 5 parts of acrylic acid, 5 parts of cyclohexyl methacrylate, a mono [poly (propylene oxide) methacrylate] phosphoric acid ester (average degree of polymerization of propylene oxide: about 5.0, Sipomer PAM- 2 parts) and 0.03 parts of 3-methacryloyloxypropyl-trimethoxysilane (KBM-503, Shin-Etsu Chemical Co., Ltd.) were added and mixed to prepare a reaction component. Subsequently, 46.6 g of the reactive emulsifier ARKALON HS-10 (manufactured by Daiichi Kogyo Pharmaceutical Co., Ltd.) and 109 g of ion-exchanged water were added to 388 g of the prepared reaction component, (1 / min) and forced emulsification to prepare a monomer-free emulsion.

(수분산형 공중합체의 에멀젼의 조제) (Preparation of Emulsion of Water-dispersible Copolymer)

냉각관, 질소 도입관, 온도계 및 교반기를 구비한 반응 용기에, 상기에서 조제한 모노머 프리에멀젼 중의 54g, 이온 교환수 456g을 투입하고, 이어서 반응 용기를 질소 치환하고, 과황산 암모늄 0.3g을 첨가하여 65℃에서, 2.5시간 중합했다. 이어서, 잔부의 모노머 프리에멀젼의 489.6g을 반응 용기에서 3시간에 걸쳐 적하하고, 그 후 3시간 중합시켰다. 그 후, 질소 치환하면서, 75℃에서 3시간 더 중합하여, 고형분 40%의 수분산형 공중합체의 에멀젼(수분산액)을 획득했다. 54 g of ion-exchanged water and 45 g of ion-exchanged water were charged into a reaction vessel equipped with a condenser, a nitrogen inlet tube, a thermometer and a stirrer, and then the reaction vessel was purged with nitrogen. 0.3 g of ammonium persulfate was added At 65 ° C for 2.5 hours. Then, 489.6 g of the remaining monomer-free emulsion was dropped in the reaction vessel over 3 hours, and then polymerized for 3 hours. Thereafter, the mixture was further polymerized at 75 캜 for 3 hours while replacing nitrogen to obtain an emulsion (aqueous dispersion) of a water-dispersed copolymer having a solid content of 40%.

(수분산형 점착제 조성물의 조제)(Preparation of water dispersion type pressure-sensitive adhesive composition)

획득된 에멀젼을 실온까지 냉각하고, 10% 암모니아수를 첨가하여 pH를 8로 조정하고, 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼쇼쿠바이사 제품)를 또한 에멀젼의 고형분(수분산형 공중합체) 100부에 대하여 0.1부 첨가하여 수분산형 점착제 조성물을 조제했다. The obtained emulsion was cooled to room temperature, and the pH was adjusted to 8 by adding 10% ammonia water. An oxazoline crosslinking agent (Epochros WS-700, an acryl-based polymer containing oxazoline group, aqueous solution type, manufactured by Nihon Shokubai Co., Ltd.) Further, 0.1 part was added to 100 parts of the solid content of the emulsion (water dispersion type copolymer) to prepare an aqueous dispersion type pressure-sensitive adhesive composition.

(점착형 광학 필름의 제작)(Production of adhesive optical film)

조제한 수분산형 점착제 조성물을, 박리제로 처리한 폴리에스터 필름으로 이루어진 이형 시트에 코팅하고, 100℃에서 2분간 가열하여 건조함으로써 두께 23㎛의 점착제층을 형성했다.The prepared aqueous dispersion type pressure-sensitive adhesive composition was coated on a release sheet composed of a polyester film treated with a release agent, heated at 100 캜 for 2 minutes and dried to form a pressure-sensitive adhesive layer having a thickness of 23 탆.

또한, 미리 하도 처리한 편광 필름을 준비했다. 하도 처리로서는 우선, 옥사졸린기 함유 아크릴계 폴리머(에포크로스 WS-700, 니혼쇼쿠바이사 제품)를 물과에탄올의 혼합 용매(용량비로 1:1)에서 고형분이 2중량%이 되도록 희석한 하도제 용액을 조제했다. 이어서, 이 하도제 용액을 와이어 바 #5를 이용하여 편광 필름의 한 면에 도포하고, 40℃에서 2분간 가열하여 건조함으로써 하도층을 마련했다. Further, a polarizing film prepared in advance was prepared. As the undercoat treatment, an oxazoline group-containing acrylic polymer (Epochros WS-700, manufactured by Nippon Shokubai Co., Ltd.) was diluted with a mixed solvent of water and ethanol (1: 1 by volume) so that the solid content became 2 wt% Solution. Subsequently, this undercoating solution was coated on one side of the polarizing film by using a wire bar # 5, heated at 40 占 폚 for 2 minutes, and dried to provide a subbing layer.

한편, 상기 편광 필름은 폴리바이닐 알코올 필름을 요오드 수용액 속에서 연신하고, 건조후, 이 편광자 양측에 투명 보호 필름으로서 트라이아세틸셀룰로스 필름을 접착함으로써 제작했다. On the other hand, the polarizing film was produced by stretching a polyvinyl alcohol film in an aqueous iodine solution, drying it, and then attaching a triacetyl cellulose film as a transparent protective film to both sides of the polarizer.

이어서, 이 편광 필름을 위상차 필름(NAZ-# 195-0.3, 닛토덴코사 제품) 위에, 하도층이 마련되어 있지 않은 면과 위상차 필름이 접합되도록 적층했다. 이로써 하도층이 마련된 편광 필름과 위상차 필름이 적층된 광학 필름을 제작했다. Then, this polarizing film was laminated on a retardation film (NAZ- # 195-0.3, manufactured by Nitto Denko) so that a surface not provided with a primer layer and a retardation film were bonded. As a result, an optical film having a polarizing film and a retardation film laminated with a primer layer was produced.

이어서, 점착제층을 광학 필름의 하도층 위에 적층하여 점착형 광학 필름을 제작했다(도 2 참조). Subsequently, a pressure-sensitive adhesive layer was laminated on the undercoating layer of the optical film to produce a pressure-sensitive adhesive optical film (see Fig. 2).

실시예 13Example 13

실시예 12에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.1부 대신에 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.3부를 첨가한 것 외에는, 실시예 12와 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Sensitive adhesive composition of Example 12 was prepared in the same manner as in Example 12 except that 0.1 part of an oxazoline crosslinking agent (Epochros WS-700, an acryl-based polymer containing an oxazoline group, aqueous solution type, manufactured by Nippon Shokubai Co., Ltd.) Dispersed pressure-sensitive adhesive composition was prepared in the same manner as in Example 12 except that 0.3 part of an acrylic pressure-sensitive adhesive (Epochros WS-700, an oxazoline group-containing acrylic polymer, aqueous solution type, manufactured by Nippon Shokubai Co., An optical film was produced.

실시예 14Example 14

실시예 12에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.1부 대신에 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 1부를 첨가한 것 외에는, 실시예 12와 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Sensitive adhesive composition of Example 12 was prepared in the same manner as in Example 12 except that 0.1 part of an oxazoline crosslinking agent (Epochros WS-700, an acryl-based polymer containing an oxazoline group, aqueous solution type, manufactured by Nippon Shokubai Co., Ltd.) Dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 12, except that 1 part of a pressure-sensitive adhesive (Epochros WS-700, an oxazoline group-containing acrylic polymer, aqueous solution type, manufactured by Nippon Shokubai Co., An optical film was produced.

비교예 7Comparative Example 7

실시예 12에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.1부 대신에 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.001부를 첨가한 것 외에는, 실시예 12와 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Sensitive adhesive composition of Example 12 was prepared in the same manner as in Example 12 except that 0.1 part of an oxazoline crosslinking agent (Epochros WS-700, an acryl-based polymer containing an oxazoline group, aqueous solution type, manufactured by Nippon Shokubai Co., Ltd.) Dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 12, except that 0.001 part of an acrylic pressure-sensitive adhesive (Epochros WS-700, an oxazoline group-containing acrylic polymer, aqueous solution type, manufactured by Nippon Shokubai Co., An optical film was produced.

비교예 8Comparative Example 8

실시예 12에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.1부 대신에 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.05부를 첨가한 것 외에는, 실시예 12와 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Sensitive adhesive composition of Example 12 was prepared in the same manner as in Example 12 except that 0.1 part of an oxazoline crosslinking agent (Epochros WS-700, an acryl-based polymer containing an oxazoline group, aqueous solution type, manufactured by Nippon Shokubai Co., Ltd.) Sensitive adhesive composition was prepared in the same manner as in Example 12, except that 0.05 part of an acrylic pressure-sensitive adhesive (Epochros WS-700, an oxazoline group-containing acrylic polymer, aqueous solution type, manufactured by Nippon Shokubai Co., An optical film was produced.

비교예 9Comparative Example 9

실시예 12에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 옥사졸린계 가교제(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품) 0.1부 대신에 옥사졸린계 가교제 2부(에포크로스 WS-700, 옥사졸린기 함유 아크릴계 폴리머, 수용액 타입, 니혼 쇼쿠바이사 제품)를 첨가한 것 외에는, 실시예 12와 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. Sensitive adhesive composition of Example 12 was prepared in the same manner as in Example 12 except that 0.1 part of an oxazoline crosslinking agent (Epochros WS-700, an acryl-based polymer containing an oxazoline group, aqueous solution type, manufactured by Nippon Shokubai Co., Ltd.) Sensitive adhesive composition was prepared in the same manner as in Example 12 except that 2 parts (Epochros WS-700, an oxazoline group-containing acrylic polymer, aqueous solution type, manufactured by Nihon Shokubai Co., Ltd.) Type optical film.

비교예 10Comparative Example 10

실시예 12에 있어서의 수분산형 점착제 조성물의 조제에 있어서, 옥사졸린계 가교제를 첨가하지 않은 것 외에는 실시예 12와 동일한 방법으로 수분산형 점착제 조성물을 조제하고, 계속해서, 점착형 광학 필름을 제작했다. A dispersion type pressure-sensitive adhesive composition was prepared in the same manner as in Example 12 except that no oxazoline crosslinking agent was added in preparation of the aqueous dispersion type pressure-sensitive adhesive composition of Example 12, and then a pressure-sensitive adhesive optical film was produced .

(평가)(evaluation)

5) 점착제층의 신장도 5) Elongation degree of the pressure-sensitive adhesive layer

실시예 12 내지 14 및 비교예 7 내지 10에 있어서의 수분산형 점착제 조성물에 대하여, 상기와 동일한 방법으로 23℃에서의 2시간의 신장도, 및 90℃에서의 2시간의 신장도를 각각 산출했다. 그 결과를 표 2에 나타낸다. The extensional elongation at 23 ° C for 2 hours and the elongation at 90 ° C for 2 hours were respectively calculated for the aqueous dispersion type pressure-sensitive adhesive compositions of Examples 12 to 14 and Comparative Examples 7 to 10 . The results are shown in Table 2.

6) 겔분율6) Gel fraction

실시예 12 내지 14 및 비교예 7 내지 10의 수분산형 점착제 조성물의 겔분율을 상기와 같은 방법에 의해 산출했다. 그 결과를 표 2에 나타낸다. The gel fraction of the aqueous dispersion type pressure-sensitive adhesive compositions of Examples 12 to 14 and Comparative Examples 7 to 10 was calculated by the above-mentioned method. The results are shown in Table 2.

7) 유리 접착성 7) Glass adhesion

실시예 12 내지 14 및 비교예 7 내지 10에 의해 수득된 점착형 광학 필름에 대하여, 상기와 같은 방법에 의해 90°박리 접착력(박리 속도 10mm/min)을 각각 측정했다. 그 결과를 표 2에 나타낸다. The 90 ° peeling adhesive force (peeling rate: 10 mm / min) was measured for each of the adhesive optical films obtained in Examples 12 to 14 and Comparative Examples 7 to 10 by the same method as described above. The results are shown in Table 2.

8) 점착형 광학 필름의 가열 발포성 8) Heat foaming of adhesive optical film

실시예 12 내지 14 및 비교예 7 내지 10의 점착형 광학 필름에 대하여, 상기와 같은 방법에 의해 발포의 유무를 관찰했다. With respect to the pressure-sensitive optical films of Examples 12 to 14 and Comparative Examples 7 to 10, the presence or absence of foaming was observed by the same method as described above.

Figure 112008031822378-pat00006
Figure 112008031822378-pat00006

표 2 중의 약호를 이하에 나타낸다. The abbreviations in Table 2 are shown below.

PAM-200 : Sipomer PAM-200(모노[폴리(프로필렌옥사이드)메타크릴레이트]인산에스터(프로필렌옥사이드의 평균 중합도 약 5.0), 로디어 닛카사 제품) PAM-200: Sipomer PAM-200 (mono [poly (propylene oxide) methacrylate] phosphoric acid ester (average degree of polymerization of propylene oxide: about 5.0)

KBM-503 : 3-메타크릴로일옥시프로필-트라이메톡시실란(신에츠화학사제)KBM-503: 3-methacryloyloxypropyl-trimethoxysilane (Shin-Etsu Chemical Co., Ltd.)

에포크로스 WS-700 : 옥사졸린기 함유 아크릴계 폴리머(수용액 타입, 고형분 25%, 주쇄: 아크릴계, pH7 내지 9, 옥사졸린가 220g solid/eq., 니혼쇼쿠바이사 제품)Epocross WS-700: oxazoline group-containing acrylic polymer (aqueous solution type, solid content 25%, main chain: acrylic, pH 7-9, oxazoline 220 g solid / eq., Product of Nihon Shokubai Co., Ltd.)

한편, 상기 설명은 본 발명의 예시의 실시 형태로서 제공했지만, 이것은 단순한 예시에 지나지 않으며, 한정적으로 해석해서는 안된다. 상기 기술 분야의 당업자에 의해서 분명한 본 발명의 변형예는 후기의 특허 청구의 범위에 포함되는 것이다.While the above description has been provided as an example of the present invention, this is merely an example, and should not be construed as limiting. Variations of the invention which will be apparent to those skilled in the art are intended to be within the scope of the following claims.

도 1은 본 발명의 점착 필름의 일 실시 형태인 점착형 광학 필름의 확대 단면도,1 is an enlarged cross-sectional view of a pressure-sensitive adhesive optical film as an embodiment of the pressure-sensitive adhesive film of the present invention,

도 2는 본 발명의 점착 필름의 다른 실시 형태인 점착형 광학 필름의 확대 단면도.2 is an enlarged cross-sectional view of a pressure-sensitive adhesive optical film as another embodiment of the pressure-sensitive adhesive film of the present invention.

Claims (7)

수분산형 점착제 조성물로 이루어지는 점착제층을 구비하고,A pressure-sensitive adhesive layer comprising a water-dispersible pressure-sensitive adhesive composition, 상기 수분산형 점착제 조성물은, The aqueous dispersion type pressure- 탄소수가 4 내지 18이고 직쇄상 또는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터, (메트)아크릴산, 인산기 함유 바이닐 모노머 및 알콕시실릴기 함유 바이닐 모노머를 함유하는 반응 성분을 반응시킴으로써 얻어지는 수분산형 공중합체; 및 (Meth) acrylic acid, a vinyl monomer containing a phosphoric acid group, and a vinyl monomer containing an alkoxysilyl group, with an alkyl (meth) acrylate having a carbon number of 4 to 18 and a linear or branched alkyl group ; And 카복실기와의 반응성을 갖는 가교제를 포함하는 수분산형 점착제 조성물이며, Sensitive adhesive composition comprising a cross-linking agent having reactivity with a carboxyl group, 상기 가교제가 카보다이이미드기를 갖는 화합물이고, Wherein the crosslinking agent is a compound having a carbodiimide group, 상기 가교제의 배합 비율이 상기 수분산형 공중합체 100중량부에 대하여 0.07 내지 4중량부이고, The blending ratio of the crosslinking agent is 0.07 to 4 parts by weight based on 100 parts by weight of the aqueous dispersion copolymer, 상기 점착제층은 하기 시험에 의한 90℃에서의 신장도가 200% 이하인 것을 특징으로 하는 점착형 광학 필름. Wherein the pressure-sensitive adhesive layer has an elongation at 90 DEG C of 200% or less by the following test. 시험 : 수분산형 점착제 조성물을 가열하여 점착제층을 조제하고, 이것을 단면적 4.6mm2, 길이 30mm의 원주 형상으로 성형하여 시험편을 제작한다. 이어서, 시험편을 90℃에서 1시간 방치한 후, 초기 시험편의 길이 L0를 측정한다. 그 후, 시험편의 한쪽 끝을 고정하고, 시험편의 다른 끝에 12g의 추를 달아 시험편을 90℃에서 2시간 늘어뜨리고, 2시간 늘어뜨린 후의 시험편의 길이 L1(mm)을 측정하여, 다음 수학식 1에 의해 신장도를 산출한다. Test: The pressure-sensitive adhesive layer is prepared by heating the aqueous dispersion type pressure-sensitive adhesive composition, and the pressure-sensitive adhesive layer is molded into a cylindrical shape having a cross-sectional area of 4.6 mm 2 and a length of 30 mm. Then, the specimen is measured after left for one hour at 90 ℃, the length L 0 of the initial test pieces. Thereafter, one end of the test piece was fixed and the weight of 12 g was placed on the other end of the test piece. The test piece was hanged at 90 캜 for 2 hours, and the length L 1 (mm) of the test piece after hanging for 2 hours was measured. 1 < / RTI > [수학식 1][Equation 1] 신장도(%)=(L1-L0)/L0×100Elongation (%) = (L 1 -L 0 ) / L 0 × 100 삭제delete 수분산형 점착제 조성물로 이루어지는 점착제층을 구비하고,A pressure-sensitive adhesive layer comprising a water-dispersible pressure-sensitive adhesive composition, 상기 수분산형 점착제 조성물은, The aqueous dispersion type pressure- 탄소수가 4 내지 18이고 직쇄상 또는 분지상인 알킬기를 갖는 (메트)아크릴산알킬에스터, (메트)아크릴산, 인산기 함유 바이닐 모노머 및 알콕시실릴기 함유 바이닐 모노머를 함유하는 반응 성분을 반응시킴으로써 얻어지는 수분산형 공중합체; 및 (Meth) acrylic acid, a vinyl monomer containing a phosphoric acid group, and a vinyl monomer containing an alkoxysilyl group, with an alkyl (meth) acrylate having a carbon number of 4 to 18 and a linear or branched alkyl group ; And 카복실기와의 반응성을 갖는 가교제를 포함하는 수분산형 점착제 조성물이며, Sensitive adhesive composition comprising a cross-linking agent having reactivity with a carboxyl group, 상기 가교제가 옥사졸린기를 갖는 가교제이고, Wherein the crosslinking agent is a crosslinking agent having an oxazoline group, 상기 가교제의 배합 비율이 상기 수분산형 공중합체 100중량부에 대하여 0.07 내지 0.3중량부이고, The blending ratio of the crosslinking agent is 0.07 to 0.3 parts by weight based on 100 parts by weight of the aqueous dispersion copolymer, 상기 점착제층은 하기 시험에 의한 90℃에서의 신장도가 200% 이하인 것을 특징으로 하는 점착형 광학 필름. Wherein the pressure-sensitive adhesive layer has an elongation at 90 DEG C of 200% or less by the following test. 시험 : 수분산형 점착제 조성물을 가열하여 점착제층을 조제하고, 이것을 단면적 4.6mm2, 길이 30mm의 원주 형상으로 성형하여 시험편을 제작한다. 이어서, 시험편을 90℃에서 1시간 방치한 후, 초기 시험편의 길이 L0를 측정한다. 그 후, 시험편의 한쪽 끝을 고정하고, 시험편의 다른 끝에 12g의 추를 달아 시험편을 90℃에서 2시간 늘어뜨리고, 2시간 늘어뜨린 후의 시험편의 길이 L1(mm)을 측정하여, 다음 수학식 1에 의해 신장도를 산출한다. Test: The pressure-sensitive adhesive layer is prepared by heating the aqueous dispersion type pressure-sensitive adhesive composition, and the pressure-sensitive adhesive layer is molded into a cylindrical shape having a cross-sectional area of 4.6 mm 2 and a length of 30 mm. Then, the specimen is measured after left for one hour at 90 ℃, the length L 0 of the initial test pieces. Thereafter, one end of the test piece was fixed and the weight of 12 g was placed on the other end of the test piece. The test piece was hanged at 90 캜 for 2 hours, and the length L 1 (mm) of the test piece after hanging for 2 hours was measured. 1 < / RTI > [수학식 1][Equation 1] 신장도(%)=(L1-L0)/L0×100Elongation (%) = (L 1 -L 0 ) / L 0 × 100 제 1 항 또는 제 3 항에 있어서, The method according to claim 1 or 3, 상기 수분산형 점착제 조성물은 아세트산에틸에 침지했을 때의 겔분율이 80 내지 95중량%인 것을 특징으로 하는 점착형 광학 필름. Wherein the aqueous dispersion type pressure-sensitive adhesive composition has a gel fraction of 80 to 95% by weight when immersed in ethyl acetate. 삭제delete 삭제delete 삭제delete
KR20080041317A 2007-05-02 2008-05-02 Aqueous dispersion type pressure-sensitive adhesive composition and pressure-sensitive adhesive film KR101484782B1 (en)