KR101461931B1 - Cosmetic hydrogel composition comprising tourmaline with high dispersion stability - Google Patents
Cosmetic hydrogel composition comprising tourmaline with high dispersion stability Download PDFInfo
- Publication number
- KR101461931B1 KR101461931B1 KR1020120131806A KR20120131806A KR101461931B1 KR 101461931 B1 KR101461931 B1 KR 101461931B1 KR 1020120131806 A KR1020120131806 A KR 1020120131806A KR 20120131806 A KR20120131806 A KR 20120131806A KR 101461931 B1 KR101461931 B1 KR 101461931B1
- Authority
- KR
- South Korea
- Prior art keywords
- tourmaline
- composition
- carrageenan
- present
- hydrogel composition
- Prior art date
Abstract
본 발명은 토르말린을 포함하는 미용 하이드로겔 조성물에 관한 것으로, 본 발명에 따라 토르말린, 카라기난(carrageenan) 및 양친매성 분산제를 포함하는 것을 특징으로 하는 토르말린 함유 미용 하이드로겔 조성물은 함유된 토르말린의 안정성 및 분산성이 우수할 뿐 아니라 원적외선 및 음이온 방사 효과가 뛰어나 피부에 적용시 피부 혈행을 현저히 개선시킴으로써 피부로의 수분 및 피부유효성분의 흡수를 극대화시킬 수 있으므로, 마스크 팩 등의 여러 화장품 개발 등에 광범위하게 활용될 수 있다.The present invention relates to a cosmetic hydrogel composition comprising tourmaline, characterized in that it comprises tourmaline, carrageenan and an amphipathic dispersant according to the present invention, wherein the stability of the contained tourmaline and the solubility of the amorphous It is excellent in acidity and is excellent in far infrared ray and negative ion radiation effect, and it can maximize the absorption of moisture and active ingredients of skin by improving the skin blood circulation when applied to skin, so that it is widely used for development of various cosmetics such as mask pack .
Description
본 발명은 토르말린을 포함하는 미용 하이드로겔 조성물에 관한 것으로, 보다 구체적으로 토르말린, 카라기난(carrageenan) 및 양친매성 분산제를 포함하는 것을 특징으로 하여 토르말린의 분산 안정성이 우수하며 원적외선 및 음이온 방사 효과가 뛰어나 피부 혈행을 현저히 개선시킬 수 있는 토르말린 함유 미용 하이드로겔 조성물에 관한 것이다.The present invention relates to a cosmetic hydrogel composition comprising tourmaline, and more specifically to a composition containing tourmaline, carrageenan and an amphipathic dispersant, which is excellent in dispersion stability of tourmaline and excellent in far-infrared ray and anion radiation effect, Containing amorphous hydrogel composition capable of remarkably improving blood circulation.
하이드로겔(hydrogel)은 정제수를 분산매체로 하는 삼차원 친수성 고분자 망상구조를 가진 물질로서, 다량의 수분을 함유하면서도 천연 조직과 같은 유연성을 나타내므로 상처드레싱, 콘텍트렌즈, 약제, 화장품, 보형물, 폐수처리제 등을 포함하는 여러 의약, 미용, 환경 산업 분야에서 활발히 연구 개발되고 있다. 최근에는 이러한 하이드로겔에 함유 성분 전달을 제어할 수 있는 지능형 방출특성(Controlled Release)이나, pH, 온도, 전기장 및 빛 등의 자극에 의해 팽창하거나 오그라드는 감응성의 특성을 부여하는 연구들이 이루어지고 있다.Hydrogel is a material having a three-dimensional hydrophilic polymer network structure using purified water as a dispersion medium. Since it exhibits flexibility such as natural tissue while containing a large amount of water, hydrogel is used as a wound dressing, contact lens, medicine, cosmetic, And has been actively researched and developed in various medical, cosmetic, and environmental industries. In recent years, studies have been made to provide controlled release properties capable of controlling the component transfer in the hydrogel, and sensitivity characteristics of expanding or shrinking due to stimulation such as pH, temperature, electric field, and light .
특히, 하이드로겔은 인체의 세포기질과 유사한 구조를 나타내어 불활성이면서 탄성이 우수하고 산소 및 영양분의 투과율이 뛰어나 우수한 생체 적합성을 나타내므로 의약 및 미용 산업에 더욱 관심을 모으고 있으며, 미용 분야의 경우 하이드로겔의 탄성, 피부 밀착성 및 부드러운 촉감을 이용하여 사용 성분의 종류 및 함량 조절을 통한 여러 보습 및 영양 공급 또는 각질 제거 효과를 강화시킬 수 있는 화장료 조성물들이 지속적으로 개발되고 있다.Particularly, hydrogels exhibit a structure similar to that of the human body and are inactive, excellent in elasticity, excellent in transmittance of oxygen and nutrients, and exhibit excellent biocompatibility. Therefore, the hydrogels are attracting more attention in the medical and cosmetic industries. Cosmetic compositions capable of enhancing various moisturizing, nutritional supply or exfoliation effects by controlling the kinds and contents of ingredients used by using elasticity, skin adhesion and soft touch of skin are continuously being developed.
한편, 토르말린(tourmaline, 전기석)은 붕소를 함유하는 규산염광물로서, 수분과 접촉하면 순간적으로 전기분해되어 １cc당 약 2000개 정도의 다량의 음이온을 발생하는 특징이 있다. 또한, 토르말린은 이러한 다량의 음이온뿐 아니라 원적외선을 방사하는 특징이 있으며, 생체 구성 물질인 나트륨, 마그네슘 등의 양이온 및 규소, 붕소, 마그네슘, 철 등의 미네랄을 풍부하게 함유한다. 따라서, 토르말린을 생체에 적용하는 경우 세포를 따뜻하게 하고 혈행을 개선하여 세포를 활성화시키므로, 세포 재생, 혈액 정화, 면역력 증진, 자율신경 조정 등의 여러 생체 유효 작용을 하는 것으로 알려져 있다. On the other hand, tourmaline (tourmaline) is a silicate mineral containing boron. When it comes into contact with water, tourmaline is instantly electrolyzed to generate about 2,000 anions per 1 cc. Tourmaline is characterized not only by a large amount of anions but also by emitting far infrared rays. It contains cations such as sodium and magnesium, which are biomaterials, and minerals such as silicon, boron, magnesium and iron in abundance. Therefore, when tourmaline is applied to a living body, the cell is warmed and blood circulation is improved to activate the cell. Therefore, it is known that it plays various bioactive functions such as cell regeneration, blood purification, immunity enhancement and autonomic nervous control.
따라서, 최근에는 이러한 유용한 토르말린을 함유하는 미용 하이드로겔 조성물에 대한 연구 및 개발이 활발히 이루어지고 있으나(대한민국 특허등록 제0471359호, 대한민국 특허공개 제2006-0081174호 및 제2005-0055332호 및 미국 특허등록 제6036965호 등), 상대적으로 비중이 높은 토르말린 입자의 안정성 및 분산성이 떨어지는 문제가 있어왔다. Therefore, in recent years, research and development have been actively conducted on beauty hydrogel compositions containing such useful tourmaline (Korea Patent No. 0471359, Korean Patent Publication No. 2006-0081174 and 2005-0055332, and US Patent No. 6036965, etc.), there has been a problem that stability and dispersibility of tourmaline particles having relatively high specific gravity are inferior.
이에 본 발명자들은 하이드로겔의 우수한 특성을 이용하면서 토르말린의 분산 안정성을 향상시킬 수 있는 화장료 조성물을 개발하기 위해 예의 연구한 결과, 토르말린, 천연고분자인 카라기난(carrageenan) 및 양친매성 분산제를 포함하는 것을 특징으로 하는 토르말린 함유 미용 하이드로겔 조성물이 토르말린의 분산 안정성을 향상시킬 뿐 아니라 원적외선 및 음이온 방사 효과가 뛰어나 피부에 적용시 피부 혈행을 현저히 개선시킬 수 있음을 발견하여 본 발명을 완성하였다. Accordingly, the present inventors have made intensive studies to develop a cosmetic composition that can improve the dispersion stability of tourmaline while taking advantage of the excellent properties of the hydrogel. As a result, they have found that they include tourmaline, carrageenan as a natural polymer and amphipathic dispersant Containing tourmaline hydrogel composition according to the present invention not only improves the dispersion stability of tourmaline but also has a far infrared ray and anion radiating effect and can significantly improve skin blood circulation upon application to the skin, thereby completing the present invention.
따라서, 본 발명의 목적은 토르말린의 분산 안정성이 우수하면서도 원적외선 및 음이온 방사 효과가 뛰어난 토르말린 함유 미용 하이드로겔 조성물을 제공하는 것이다.Accordingly, an object of the present invention is to provide a tourmaline-containing cosmetic hydrogel composition excellent in dispersion stability of tourmaline and excellent in far-infrared and anion radiative effects.
상기 목적에 따라, 본 발명은 토르말린, 카라기난(carrageenan) 및 양친매성 분산제를 포함하는 토르말린 함유 미용 하이드로겔 조성물을 제공한다.To this end, the present invention provides a tourmaline-containing cosmetic hydrogel composition comprising tourmaline, carrageenan and an amphipathic dispersant.
본 발명의 일실시예에 따르면, 상기 토르말린 함유 미용 하이드로겔 조성물은 총 중량 대비 0.05 내지 5 중량%의 토르말린, 0.5 내지 3 중량%의 카라기난(carrageenan) 및 0.05 내지 10 중량%의 양친매성 분산제를 포함할 수 있다.According to one embodiment of the present invention, the tourmaline-containing cosmetic hydrogel composition comprises from 0.05 to 5% by weight of tourmaline, from 0.5 to 3% by weight of carrageenan and from 0.05 to 10% by weight of an amphipathic dispersant, can do.
본 발명의 일실시예에 따르면, 상기 카라기난은 다른 천연고분자와의 혼합물로 포함될 수 있다.According to one embodiment of the present invention, the carrageenan may be included as a mixture with other natural polymers.
본 발명의 일실시예에 따르면, 상기 다른 천연고분자는 갈락토만난, 글루코만난, 구아껌, 로커스트 빈 껌, 아가, 알긴, 잔탄, 겔란, 젤라틴, 메틸셀룰로오스, 셀룰로오스, 카르복시메틸셀룰로오스 및 하이드록시에틸셀룰로오스를 포함하는 군으로부터 선택된 하나 이상일 수 있다.According to one embodiment of the present invention, the other natural polymer is selected from the group consisting of galactomannan, glucomannan, guar gum, locust bean gum, agar, algin, xanthan, gellan, gelatin, methylcellulose, cellulose, carboxymethylcellulose and hydroxyethylcellulose ≪ / RTI >
본 발명의 일실시예에 따르면, 상기 다른 천연고분자는 조성물 총 중량 대비 0.1 내지 3 중량%로 포함될 수 있다.According to an embodiment of the present invention, the other natural polymer may be included in an amount of 0.1 to 3% by weight based on the total weight of the composition.
본 발명의 일실시예에 따르면, 상기 양친매성 분산제는 부틸렌글라이콜디카프릴레이트/디카프레이트(butylene glycol dicaprylate/dicaprate), 피이지-60 하이드로제네이티드캐스터오일(PEG-60 hydrogenated castor oil), 피이지-10 디메티콘(PEG-10 dimethicone), 비스-에톡시디글라이콜사이클로헥산1,4-디카복실레이트(bis-ethoxydigly colcyclohexane 1,4-dicarboxylate) 및 이소스테아릭애씨드(isostearic acid)를 포함하는 군으로부터 선택된 하나 이상일 수 있다.According to one embodiment of the present invention, the amphipathic dispersant is selected from the group consisting of butylene glycol dicaprylate / dicaprate, PEG-60 hydrogenated castor oil, Bis-ethoxydigly colcyclohexane 1,4-dicarboxylate, and isostearic acid, as well as isophthalic acid, such as PEG-10 dimethicone, bis-ethoxydiglycolcyclohexane 1,4-dicarboxylate, And the like.
본 발명의 일실시예에 따르면, 상기 토르말린 함유 미용 하이드로겔 조성물은 다가 알코올을 추가로 포함할 수 있다.According to one embodiment of the present invention, the tourmaline-containing cosmetic hydrogel composition may further comprise a polyhydric alcohol.
본 발명의 일실시예에 따르면, 상기 다가 알코올은 글리세린, 에틸렌글리콜, 1,3-부틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜, 소르비톨, 및 자일리톨을 포함하는 군으로부터 선택된 하나 이상일 수 있다.According to one embodiment of the present invention, the polyhydric alcohol may be at least one selected from the group consisting of glycerin, ethylene glycol, 1,3-butylene glycol, propylene glycol, dipropylene glycol, sorbitol, and xylitol.
본 발명의 일실시예에 따르면, 상기 다가 알코올은 조성물 총 중량 대비 10 내지 30 중량%로 포함될 수 있다.According to an embodiment of the present invention, the polyhydric alcohol may be contained in an amount of 10 to 30% by weight based on the total weight of the composition.
본 발명에 따라 토르말린, 카라기난(carrageenan) 및 양친매성 분산제를 포함하는 것을 특징으로 하는 토르말린 함유 미용 하이드로겔 조성물은 함유된 토르말린의 분산 안정성이 우수할 뿐 아니라 원적외선 및 음이온 방사 효과가 뛰어나 피부에 적용시 피부 혈행을 현저히 개선시킴으로써 피부유효성분의 흡수율을 극대화시킬 수 있으므로, 마스크 팩 등의 여러 화장품 개발 등에 광범위하게 활용될 수 있다.The tourmaline-containing cosmetic hydrogel composition according to the present invention, which comprises tourmaline, carrageenan and an amphipathic dispersant, is excellent in the dispersion stability of tourmaline contained therein, and has excellent far-infrared and anion radiation effects. It is possible to maximize the absorption rate of the active ingredient of the skin by remarkably improving skin blood circulation, and thus it can be widely used for development of various cosmetics such as mask packs.
도 1의 A는 카라기난 및 양친매성 분산제를 포함하지 않는 비교예 3의 토르말린 함유 하이드로겔 조성물을 상온에서 방치하여 10분, 30분 및 1시간 후에 토르말린의 침전 정도를 육안으로 확인한 사진이며, B는 본 발명의 일실시예에 따른 실시예 3의 토르말린 함유 하이드로겔 조성물과 카라기난 및 양친매성 분산제를 포함하지 않는 비교예 3의 토르말린 함유 하이드로겔 조성물의 토르말린 분산 정도를 육안으로 비교 평가한 사진이다(토르말린 함유량 1%).
도 2는 본 발명의 일실시예에 따른 실시예 1 내지 3의 토르말린 함유 하이드로겔 조성물들과 양친매성 분산제를 포함하지 않거나(비교예 1 및 2) 조성물 총 중량 대비 0.01 중량%로 미량 포함하는(비교예 4) 비교예 1, 2 및 4의 토르말린 함유 하이드로겔 조성물들로부터 제조된 각각의 팩 제형의 토르말린 분산 정도를 육안으로 비교 평가한 사진이다.
도 3은 피험자 21 인을 대상으로 본 발명의 일실시예에 따른 실시예 1의 토르말린 함유 하이드로겔 마스크팩을 매일 사용하게 하여, 사용 전 그리고 매일 사용 후 7일째에 측정된 피부 혈행 정도의 평균값을 비교 분석한 결과이다.Fig. 1 (A) is a photograph showing visually the degree of precipitation of tourmaline after leaving the carrageenan and an amphipathic dispersant at room temperature for 10 minutes, 30 minutes, and 1 hour after leaving the tourmaline-containing hydrogel composition of Comparative Example 3, FIG. 6 is a photograph showing the comparative evaluation of the degree of tourmaline dispersion of the tourmaline-containing hydrogel composition of Example 3 according to one embodiment of the present invention and the tourmaline-containing hydrogel composition of Comparative Example 3 not including the carrageenan and amphipathic dispersant Content 1%).
Figure 2 is a graphical representation of the compositions of the present invention comprising tourmaline-containing hydrogel compositions of Examples 1 to 3 and amphipathic dispersants (Comparative Examples 1 and 2) Comparative Example 4: Visually comparative evaluation of the degree of dispersion of the tourmaline of each pack formulation prepared from the tourmaline-containing hydrogel compositions of Comparative Examples 1, 2 and 4.
FIG. 3 is a graph showing the average value of skin blood circulation measured before and after the daily use of the tourmaline-containing hydrogel mask pack of Example 1 according to an embodiment of the present invention, This is the result of comparative analysis.
이하, 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.
본 발명에 따른 토르말린 함유 미용 하이드로겔 조성물은 토르말린, 카라기난(carrageenan) 및 양친매성 분산제를 포함하며, 보다 구체적으로는 토르말린, 카라기난, 천연고분자, 다가알코올 및 용매(정제수)를 포함할 수 있다. 본 발명에 따른 토르말린 함유 미용 하이드로겔 조성물은 이러한 조성으로 인해 상대적으로 비중이 큰 토르말린 입자의 분산 안정성을 향상시켜 토르말린의 침전을 방지하므로 공장에서 대용량 스케일로 제조하는 경우에도 침전되기 쉬운 토르말린 입자를 균일하게 분산시켜 포함하는 하이드로겔 조성물을 수득할 수 있다. The tourmaline-containing cosmetic hydrogel composition according to the present invention comprises tourmaline, carrageenan and an amphipathic dispersant, more specifically tourmaline, carrageenan, natural polymers, polyhydric alcohols and solvents (purified water). The tourmaline-containing hair hydrogel composition according to the present invention improves the dispersion stability of relatively large specific gravity tourmaline particles and prevents sedimentation of tourmaline due to such a composition, so that tourmaline particles, which tend to precipitate even when they are produced in a large- To obtain a hydrogel composition.
본 발명에 포함되는 상기 토르말린은 토르말린 원석을 세척, 건조 및 분쇄시키는 전처리 공정에 의해 제조된 파우더 형태일 수 있다. 이때, 입자크기는 10 내지 1000 nm 범위인 것이 바람직하며, 상기 건조공정은 350 내지 500℃ 범위의 온도에서 열처리하여 수행될 수 있다. 또한, 본 발명에 포함되는 상기 토르말린의 함량은 조성물 총 중량 대비 0.05 내지 5 중량%일 수 있다.The tourmaline contained in the present invention may be in the form of a powder prepared by a pretreatment process of washing, drying and pulverizing tourmaline ore. In this case, the particle size is preferably in the range of 10 to 1000 nm, and the drying process may be performed by heat treatment at a temperature in the range of 350 to 500 ° C. In addition, the content of the tourmaline contained in the present invention may be 0.05 to 5% by weight based on the total weight of the composition.
본 발명에서, 상기 카라기난은 분산된 토르말린을 그물망 구조에 고정시켜 안정화시키는 역할을 한다. 상기 카라기난은 조성물 총 중량 대비 0.5 내지 3 중량%로 포함될 수 있으며, 이때 카라기난의 함량이 0.5 중량% 미만인 경우에는 토르말린을 충분히 분산시키기에 미흡할 수 있고, 3 중량% 초과인 경우에는 점성이 너무 높아져 유동성이 떨어져 하이드로겔의 형태 구현이 어려워질 수 있다. In the present invention, the carrageenan serves to fix and stabilize dispersed tourmaline in a network structure. The carrageenan may be contained in an amount of 0.5 to 3% by weight based on the total weight of the composition. If the content of carrageenan is less than 0.5% by weight, it may be insufficient for sufficiently dispersing tourmaline. When the content exceeds 3% by weight, The flowability may be deteriorated and the shape of the hydrogel may become difficult to implement.
본 발명에서 사용되는 카라기난은 대표적으로 캐퍼피커스 알바레지(Kappaphycus alvarezii), 콘드러스 크리스피스(Chondrus crispus), 쥐갈티나 라듈라(Gigartina radula), 쥐갈티나 스텔라타(Gigartina stellata), 유케우마 덴티큘래텀(Eucheuma denticulatum) 계통의 해조류 성분에서 정제, 추출 가능한 물질로서, α１→３, 또는 β１→４ 글리코시드 결합을 통해 갈락토스 단위의 결합을 반복함으로써 겔 형성을 유도하며, 황산화 과정을 통해 발생하는 황산화기의 정도 및 위치에 따라 그 특성이 발현된다. The carrageenans used in the present invention are typically Kappaphycus alvarezii , Chondrus crispus , Gigartina radula ), Gigartina stellata , Eucheuma denticulatum ), which induces gel formation by repeating the binding of galactose units through α1 → 3, or β1 → 4 glycosidic linkages, and the formation of sulfate groups The characteristics are expressed according to the degree and position.
보다 구체적으로 카라기난은 카파-카라기난(Kappa-Carrageenan)과 아이오타-카라기난(Iota-Carrageenan)으로 분류될 수 있으며, 카파-카라기난(Kappa-Carrageenan)은 D-갈락토스-4-설페이트-3,6-언하이드로-D-갈락토스의 반복단위를 형성하는 반면, 아이오타-카라기난(Iota-Carrageenan)은 D-갈락토스-4-설페이트-3,6-언하이드로-D-갈락토스-2-설페이트의 반복구조를 갖는다. 본 발명에서 "카라기난"이라는 용어는 카파-카라기난(Kappa-Carrageenan)을 필수 성분으로 하여 필요에 따라 아이오타-카라기난(Iota-Carrageenan)을 혼합한 혼합물을 의미하는 것으로 사용된다.More specifically, carrageenan can be classified as Kappa-Carrageenan and Iota-Carrageenan, and Kappa-Carrageenan is classified as D-galactose-4-sulfate-3,6- D-galactose while Iota-carrageenan forms a repeating unit of D-galactose-4-sulfate-3,6-anhydro-D-galactose-2-sulfate . In the present invention, the term "carrageenan" is used to mean a mixture of Kota-carrageenan as an essential ingredient and optionally Iota-carrageenan.
또한, 본 발명에서 천연고분자로서 포함되는 상기 카라기난은 다른 천연 고분자들과의 혼합물로서 포함될 수 있다. 이러한 천연고분자로는 통상적으로 사용되는 천연고분자라면 어느 것이든 사용 가능하며, 예를 들면 갈락토만난, 글루코만난, 구아껌, 로커스트 빈 껌, 아가, 알긴, 잔탄, 겔란, 젤라틴, 메틸셀룰로오스, 셀룰로오스, 카르복시메틸셀룰로오스 및 하이드록시에틸셀룰로오스 등을 하나 이상 선택하여 사용할 수 있다. 또한, 상기 카라기난과 함께 포함되는 천연고분자의 함량은 조성물 총 중량 대비 0.1 내지 3 중량%일 수 있으나, 이에 제한되는 것은 아니다. In addition, the carrageenan contained as a natural polymer in the present invention may be included as a mixture with other natural polymers. Examples of such natural polymers include natural polymers such as galactomannan, glucomannan, guar gum, locust bean gum, agar, algin, xanthan, gellan, gelatin, methylcellulose, cellulose, Carboxymethylcellulose, hydroxyethylcellulose, and the like may be selected and used. In addition, the content of the natural polymer included with the carrageenan may be 0.1 to 3% by weight based on the total weight of the composition, but is not limited thereto.
본 발명의 토르말린 함유 미용 하이드로겔 조성물에서, 상기 양친매성 분산제는 토르말린의 표면장력을 낮추어줌으로써 토르말린 입자의 응집을 저해하고 분산성을 향상시키는 역할을 한다. 이러한 양친매성 분산제로는 당 분야에 통상적으로 사용되는 양친매성 물질이라면 어느 것이든 사용될 수 있으며, 예를 들면 부틸렌글라이콜디카프릴레이트/디카프레이트(butylene glycol dicaprylate/dicaprate), 피이지-60 하이드로제네이티드캐스터오일(PEG-60 hydrogenated castor oil), 피이지-10 디메티콘(PEG-10 dimethicone), 비스-에톡시디글라이콜사이클로헥산1,4-디카복실레이트(bis-ethoxydigly colcyclohexane 1,4-dicarboxylate) 및 이소스테아릭애씨드(isostearic acid) 등을 단독으로 또는 둘 이상의 혼합물로 사용할 수 있다. 상기 양친매성 분산제는 조성물 총 중량 대비 0.05 내지 10 중량%로 포함될 수 있으며, 이때 양친매성 분산제의 함량이 0.05 중량% 미만인 경우에는 토르말린 입자가 서로 응집되어 고르게 분산시킬 수 없고, 10 중량% 초과인 경우에는 피부에 자극이 되거나 제형 안정성이 떨어질 수 있다.In the tourmaline-containing cosmetic hydrogel composition of the present invention, the amphipathic dispersant serves to inhibit agglomeration of tourmaline particles and improve dispersibility by lowering the surface tension of tourmaline. As the amphipathic dispersant, any of amphipathic substances commonly used in the art can be used, and examples thereof include butylene glycol dicaprylate / dicaprate, PEG-10 hydrogenated castor oil, PEG-10 dimethicone, bis-ethoxydiglycolcyclohexane 1,4 (bis-ethoxydiglycolcyclohexane 1,4) -dicarboxylate and isostearic acid may be used singly or in a mixture of two or more thereof. The amphipathic dispersant may be included in an amount of 0.05 to 10% by weight based on the total weight of the composition. When the content of the amphipathic dispersant is less than 0.05% by weight, the tourmaline particles can not be dispersed uniformly, May be irritating to the skin or may reduce formulation stability.
본 발명의 미용 하이드로겔 조성물은 상기 토르말린, 카라기난 및 양친매성 분산제 외에 다가알코올 및 용매 등을 포함할 수 있다. 이때 상기 용매는 당 분야에 통상적으로 사용되는 정제수 또는 유기용매 등을 단독으로 또는 둘 이상의 혼합물로 사용할 수 있다. 또한, 상기 다가알코올로는 당 분야에 통상적으로 사용되는 다가알코올류라면 어느 것이든 사용될 수 있으며, 예를 들면 글리세린, 에틸렌글리콜, 1,3-부틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜, 소르비톨 및 자일리톨 등을 단독으로 또는 둘 이상의 혼합물로 사용할 수 있고, 바람직하게는 글리세린을 사용할 수 있다. 상기 다가알코올은 조성물 총 중량 대비 10 내지 30 중량%로 포함될 수 있으며, 이때 다가알코올의 함량이 10 중량% 미만인 경우에는 수분의 휘산이 발생될 수 있을 뿐 아니라 천연 고분자의 분산이 저해될 수 있고, 30 중량% 초과인 경우에는 점성이 증가하며 원료단가의 상승으로 인해 비경제적인 문제가 있다. In addition to the tourmaline, carrageenan and amphipathic dispersant, the cosmetic hydrogel composition of the present invention may contain a polyhydric alcohol, a solvent, and the like. In this case, the solvent may be purified water or an organic solvent commonly used in the art, either singly or as a mixture of two or more thereof. As the polyhydric alcohol, polyhydric alcohols conventionally used in the art can be used. Examples of the polyhydric alcohol include glycerin, ethylene glycol, 1,3-butylene glycol, propylene glycol, dipropylene glycol, sorbitol, Xylitol and the like can be used alone or in a mixture of two or more thereof, and glycerin can be preferably used. The polyhydric alcohol may be contained in an amount of 10 to 30% by weight based on the total weight of the composition. If the content of the polyhydric alcohol is less than 10% by weight, water vaporization may occur, dispersion of the natural polymer may be inhibited, When the content is more than 30% by weight, the viscosity increases and there is an uneconomical problem due to an increase in raw material cost.
본 발명에 따른 토르말린 함유 미용 하이드로겔 조성물은 상기 성분들 외에도 필요에 따라 당 분야에 통상적으로 사용되는 피부유효성분, pH조절제, 보존제, 향료, 색소, 살균제 또는 산화안정화제 등을 적절히 선택하여 추가로 포함할 수 있다. The tourmaline-containing cosmetic hydrogel composition according to the present invention may further comprise, as appropriate, a skin active ingredient, a pH adjusting agent, a preservative, a flavoring, a coloring agent, a bactericide or an oxidative stabilizer, which are conventionally used in the art, .
또한, 본 발명에 따른 토르말린 함유 미용 하이드로겔 조성물은 당 분야의 통상적인 방법에 따라 각 성분들을 혼합하여 제조될 수 있으며, 본 발명의 바람직한 일실시예에 따르면, 토르말린 및 양친매성 분산제를 다가알코올에 용해시킨 후, 여기에 60 내지 80℃에서 가열 혼합시켜 수득한 카라기난 등의 천연고분자 혼합물과 기타 다가알코올, 미용성분 및 보존제 성분 등을 첨가 및 혼합하여 제조될 수 있으나, 이에 제한되는 것은 아니다.
In addition, the tourmaline-containing cosmetic hydrogel composition according to the present invention can be prepared by mixing the respective components according to a conventional method in the art. According to a preferred embodiment of the present invention, the tourmaline and amphiphilic dispersant are mixed with a polyhydric alcohol And then adding and mixing natural polymer mixture such as carrageenan obtained by heating and mixing at 60 to 80 ° C, other polyhydric alcohol, cosmetic ingredient, preservative ingredient, etc., but the present invention is not limited thereto.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 예시하기 위한 것으로서, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지 않는 것은 당 업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.
Hereinafter, the present invention will be described in more detail with reference to Examples. It is to be understood by those skilled in the art that these embodiments are merely illustrative of the present invention and that the scope of the present invention is not construed as being limited by these embodiments.
실시예Example 1 내지 5 1 to 5
하기 표 1의 성분들을 다음과 같이 혼합하여 본 발명에 따른 실시예 1 내지 5의 미용 하이드로겔 조성물을 제조하였다.The components of the following Table 1 were mixed as follows to prepare the cosmetic hydrogel compositions of Examples 1 to 5 according to the present invention.
우선, 하기 표 1에서의 1 및 2의 성분을 글리세린에 용해시킨 후, 여기에 3의 천연고분자 성분들을 60 내지 80℃의 온도에서 혼합시켜 수득한 혼합물로서 첨가하였으며, 이후 다가알코올, 미용성분 및 보존제 성분을 첨가하여 혼합시켜 하이드로겔 조성물을 제조하였다. 이를 PET 필름상에 코팅한 다음, 원하는 모양으로 성형하여 실시예 1 내지 5의 하이드로겔 마스크팩을 제조하였다. First, components 1 and 2 in the following Table 1 were dissolved in glycerin, and then the natural polymer components of 3 were added thereto as a mixture obtained by mixing at a temperature of 60 to 80 DEG C, and then the polyhydric alcohol, A preservative component was added and mixed to prepare a hydrogel composition. This was coated on a PET film, and then molded into a desired shape to prepare the hydrogel mask packs of Examples 1 to 5.
분산제Amphipathic
Dispersant
성분Beauty
ingredient
비교예Comparative Example 1 내지 4 1 to 4
하기 표 2에서 볼 수 있는 바와 같이, 상기 실시예들에서 사용된 양친매성 분산제를 사용하지 않거나(비교예 1 및 2), 카라기난 및 양친매성 분산제를 둘 다 사용하지 않거나(비교예 3), 또는 2의 양친매성 분산제 성분인 PEG-60 하이드로제네이티드캐스터오일을 0.01 g으로 미량 사용하는 것(비교예 4)을 제외하고, 상기 실시예 1 내지 5에서와 동일한 방법으로 하기 표 2에 제시된 성분들을 혼합하여 비교예 1 내지 4의 하이드로겔 조성물을 제조하였으며, 이들을 각각 PET 필름상에 코팅한 다음 원하는 모양으로 성형하여 비교예 1 내지 4의 하이드로겔 마스크팩을 제조하였다.As can be seen in the following Table 2, either the amphipathic dispersant used in the above examples was not used (Comparative Examples 1 and 2), neither the carrageenan nor the amphipathic dispersant was used (Comparative Example 3), or 2 < / RTI > amphipathic dispersant component PEG-60 The components shown in the following Table 2 were mixed in the same manner as in Examples 1 to 5 except that a small amount of hydrogenated castor oil was used in an amount of 0.01 g (Comparative Example 4), and hydrogels of Comparative Examples 1 to 4 The compositions were each coated on a PET film and then molded into a desired shape to prepare hydrogel mask packs of Comparative Examples 1 to 4.
분산제Amphipathic
Dispersant
성분Beauty
ingredient
시험예Test Example
1)One) 하이드로겔Hydrogel 조성물 내Within the composition 토르말린의Tourmaline 분산 안정성 확인 Confirm dispersion stability
상기 실시예 1 내지 5 및 비교예 1 내지 4의 하이드로겔 조성물 내 토르말린의 분산 안정성을 확인하기 위해, 제조된 조성물들을 상온에서 1시간 동안 방치하여 토르말린 침전여부를 육안으로 확인하였으며, 그 일부 결과를 도 1에 나타내었다. In order to confirm the dispersion stability of the tourmaline in the hydrogel compositions of Examples 1 to 5 and Comparative Examples 1 to 4, the prepared compositions were allowed to stand at room temperature for 1 hour to visually confirm the precipitation of tourmaline. 1.
그 결과, 도 1의 A에서 볼 수 있는 바와 같이, 카라기난 및/또는 양친매성 분산제를 포함하지 않거나 미량 포함하는 비교예 3을 비롯한 비교예 1 내지 4의 조성물들은 방치 10분 후부터 1 시간 이내에 토르말린 입자의 침전이 서서히 일어난 반면, 도 1의 B에서 볼 수 있는 바와 같이, 실시예 3을 비롯한 실시예 1 내지 5의 조성물들은 1 시간 이상 방치하여도 우수한 분산 안정성으로 인해 토르말린의 침전이 거의 일어나지 않는 것을 확인하였다. As a result, as can be seen from Fig. 1A, the compositions of Comparative Examples 1 to 4, which did not contain or contain trace amounts of carrageenan and / or amphipathic dispersing agent, contained tourmaline particles 1, the compositions of Examples 1 to 5, including Example 3, showed that precipitation of tourmaline hardly occurred due to excellent dispersion stability even after being left for 1 hour or more Respectively.
또한, 이들 혼합물들을 각각 PET 필름상에 코팅한 다음, 원하는 모양으로 성형하여 제조된 실시예 1 내지 5 및 비교예 1 내지 4의 하이드로겔 마스크팩 제형의 토르말린 분산도를 전자현미경으로 확인하여, 그 일부 결과를 도 2에 나타내었다.Further, the dispersions of the hydrogel mask packs of Examples 1 to 5 and Comparative Examples 1 to 4, which were prepared by coating these mixtures on a PET film and then molding them into a desired shape, were examined by an electron microscope, Some results are shown in Fig.
그 결과, 도 2에서 볼 수 있는 바와 같이, 양친매성 분산제가 포함되지 않거나 미량 포함된 비교예 1 내지 4의 하이드로겔 제형들은 토르말린 입자가 고르게 분산되지 못하고 뭉쳐있는 것을 확인한 반면, 실시예 1 내지 5의 하이드로겔 제형들은 토르말린 입자의 응집이 거의 발견되지 않는 것을 확인하였다.As a result, as can be seen from Fig. 2, the hydrogel formulations of Comparative Examples 1 to 4 in which the amphipathic dispersant was not included or contained a small amount, confirmed that the tourmaline particles were not uniformly dispersed and clumped, whereas Examples 1 to 5 Of the hydrogel formulations showed little aggregation of the tourmaline particles.
이로써, 본 발명에 따라 토르말린을 카라기난 및 양친매성 분산제와 함께 포함하는 하이드로겔 조성물은 우수한 토르말린 분산 안정성을 나타냄을 알 수 있다.
Thus, it can be seen that hydrogel compositions containing tourmaline in combination with carageenan and amphipathic dispersants according to the present invention exhibit excellent stability of tourmaline dispersion.
2) 2) 하이드로겔Hydrogel 마스크팩Mask Pack 제형의 구간별 음이온 방출량 측정 Measurement of anion emission by section of formulation
각 하이드로겔 조성물을 제형화하는 경우 피부에 유익한 음이온 방출이 제형 전체적으로 고르게 이루어지는지를 확인하기 위해 다음과 같이 구간별 음이온 방출량을 측정하였다.When each hydrogel composition was formulated, the amount of anion emission of each section was measured as follows to confirm whether or not the anion release which is beneficial to the skin is evenly distributed throughout the formulation.
먼저 조성물 총 중량 대비 1 중량%의 토르말린을 함유하는 실시예 3 및 비교예 3의 하이드로겔 조성물을 각각 PET 필름상에 넓게 코팅하여 하이드로겔 제형을 제조하였으며, 이를 5 개 구간으로 나누었다. 각 구간의 음이온량을 실내온도 26℃, 습도 32% 및 대기중 음이온수 102/cc 조건 하에 전하입자 측정 장치(기기명 COM3600, COMSYSTEM 니코(일본) 제조)를 이용하여 측정하였으며, 각 구간에서의 방출 음이온량을 단위체적(cc)당 음이온수로 산출하여 하기 표 3에 나타내었다.First, hydrogel compositions of Example 3 and Comparative Example 3 containing 1 wt% of tourmaline based on the total weight of the composition were coated on a PET film to prepare a hydrogel formulation, which was divided into 5 sections. The amount of negative ions in each section was measured using a charge particle measuring device (COM3600, manufactured by COMSYSTEM NIKO (Japan)) under the conditions of room temperature of 26 ° C, humidity of 32% and number of anions in the air of 102 / cc. The amount of negative ions is calculated as the number of negative ions per unit volume (cc) and is shown in Table 3 below.
(음이온 ion/cc)Example 3
(Anion ion / cc)
(음이온 ion/cc)Comparative Example 3
(Anion ion / cc)
그 결과, 상기 표 3에서 볼 수 있는 바와 같이, 실시예 3의 하이드로겔 제형의 경우 구간에 따른 음이온 방출량의 차이가 크지 않고 균일한 반면, 비교예 3의 하이드로겔 제형의 경우 구간별로 음이온 방출량의 차이가 크고 균일하지 못한 것을 확인하였다.
As a result, as shown in Table 3, in the case of the hydrogel formulation of Example 3, the difference in the amount of anion emission according to the interval was not large and uniform, while in the case of the hydrogel formulation of Comparative Example 3, It was confirmed that the difference was large and not uniform.
3) 원적외선 혈행촉진효과3) Effect of promoting far infrared blood circulation
본 발명에 따른 하이드로겔 조성물 내 포함된 토르말린의 원적외선 방출에 의한 피부 혈행 촉진 효과를 확인하기 위해 다음과 같이 시험하였다.The following tests were conducted to confirm the effect of promoting skin blood circulation by far-infrared emission of tourmaline contained in the hydrogel composition according to the present invention.
먼저 피험자 21 인을 대상으로 상기에서 제조된 실시예 1의 하이드로겔 마스크팩을 7일 동안 매일 사용하게 하여, 마스크팩 사용 전 및 매일 사용 후 7일째에 각 피험자의 마스크팩 적용 부위의 피부 혈행 정도를 체열 측정기(thermography, PeriScan PIM 3 System-Laser Doppler Blood Perfusion Imager, PERIMED 사)를 사용하여 측정하였다. 측정된 각 피험자의 결과를 하기 표 4에 나열하였으며, 이를 근거로 개선율의 평균값(43.84%)을 산출하여 비교 분석한 결과를 도 3에 나타내었다.First, the hydrogel mask pack of Example 1 prepared above was used for 7 days for 21 days, and the skin blood circulation level of each subject's mask pack before and after 7 days of daily use Was measured using a thermography (PeriScan PIM 3 System-Laser Doppler Blood Perfusion Imager, PERIMED). The results of each subject measured The results are shown in Table 4, and the average value (43.84%) of the improvement ratio was calculated based on the results.
그 결과, 상기 표 4 및 도 3에서 볼 수 있는 바와 같이, 본 발명에 따른 토르말린 함유 하이드로겔 마스크팩을 매일 사용한 경우, 사용 후 7일째의 평균 피부 혈행 정도가 사용 전과 비교하여 현저히 개선되는 것을 확인하였다.
As a result, as can be seen from Table 4 and FIG. 3, when the tourmaline-containing hydrogel mask pack according to the present invention was used daily, the average degree of skin blood circulation on the seventh day after use was remarkably improved Respectively.
이제까지 본 발명에 대하여 그 바람직한 실시예들을 중심으로 살펴보았다. 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자는 본 발명이 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 변형된 형태로 구현될 수 있음을 이해할 수 있을 것이다. 그러므로 개시된 실시예들은 한정적인 관점이 아니라 설명적인 관점에서 고려되어야 한다. 본 발명의 범위는 전술한 설명이 아니라 특허청구범위에 나타나 있으며, 그와 동등한 범위 내에 있는 모든 차이점은 본 발명에 포함된 것으로 해석되어야 할 것이다.The present invention has been described with reference to the preferred embodiments. It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. Therefore, the disclosed embodiments should be considered in an illustrative rather than a restrictive sense. The scope of the present invention is defined by the appended claims rather than by the foregoing description, and all differences within the scope of equivalents thereof should be construed as being included in the present invention.
Claims (9)
상기 카라기난은 다른 천연고분자와의 혼합물로 포함되는 것을 특징으로 하는, 토르말린 함유 미용 하이드로겔 조성물.The method according to claim 1,
Wherein said carrageenan is comprised in admixture with other natural polymers.
상기 다른 천연고분자는 갈락토만난, 글루코만난, 구아껌, 로커스트 빈 껌, 아가, 알긴, 잔탄, 겔란, 젤라틴, 메틸셀룰로오스, 셀룰로오스, 카르복시메틸셀룰로오스 및 하이드록시에틸셀룰로오스를 포함하는 군으로부터 선택된 하나 이상인 것을 특징으로 하는, 토르말린 함유 미용 하이드로겔 조성물.The method of claim 3,
The other natural polymer is at least one selected from the group consisting of galactomannan, glucomannan, guar gum, locust bean gum, agar, algin, xanthan, gellan, gelatin, methylcellulose, cellulose, carboxymethylcellulose and hydroxyethylcellulose ≪ / RTI > characterized in that the tourmaline-containing cosmetic hydrogel composition is a cosmetic composition.
상기 다른 천연고분자는 조성물 총 중량 대비 0.1 내지 3 중량%로 포함되는 것을 특징으로 하는, 토르말린 함유 미용 하이드로겔 조성물.The method of claim 3,
Wherein the other natural polymer is included in an amount of 0.1 to 3% by weight based on the total weight of the composition.
상기 양친매성 분산제는 부틸렌글라이콜디카프릴레이트/디카프레이트(butylene glycol dicaprylate/dicaprate), 피이지-60 하이드로제네이티드캐스터오일(PEG-60 hydrogenated castor oil), 피이지-10 디메티콘(PEG-10 dimethicone), 비스-에톡시디글라이콜사이클로헥산1,4-디카복실레이트(bis-ethoxydigly colcyclohexane 1,4-dicarboxylate) 및 이소스테아릭애씨드(isostearic acid)를 포함하는 군으로부터 선택된 하나 이상인 것을 특징으로 하는, 토르말린 함유 미용 하이드로겔 조성물.The method according to claim 1,
The amphipathic dispersant is selected from the group consisting of butylene glycol dicaprylate / dicaprate, PEG-60 hydrogenated castor oil, PEG-10 dimethicone (PEG- 10 dimethicone, bis-ethoxydiglycolcyclohexane 1,4-dicarboxylate, and isostearic acid. The isocyanate compound is preferably at least one selected from the group consisting of bis-ethoxydiglycolcyclohexane 1,4-dicarboxylate and isostearic acid. By weight, based on the total weight of the composition.
상기 토르말린 함유 미용 하이드로겔 조성물은 다가 알코올을 추가로 포함하는 것을 특징으로 하는 토르말린 함유 미용 하이드로겔 조성물.The method according to claim 1,
Wherein the tourmaline-containing cosmetic hydrogel composition further comprises a polyhydric alcohol.
상기 다가 알코올은 글리세린, 에틸렌글리콜, 1,3-부틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜, 소르비톨, 및 자일리톨을 포함하는 군으로부터 선택된 하나 이상인 것을 특징으로 하는 토르말린 함유 미용 하이드로겔 조성물.8. The method of claim 7,
Wherein the polyhydric alcohol is at least one selected from the group consisting of glycerin, ethylene glycol, 1,3-butylene glycol, propylene glycol, dipropylene glycol, sorbitol, and xylitol.
상기 다가 알코올은 조성물 총 중량 대비 10 내지 30 중량%로 포함되는 것을 특징으로 하는, 토르말린 함유 미용 하이드로겔 조성물.8. The method of claim 7,
Wherein the polyhydric alcohol is present in an amount of 10 to 30% by weight based on the total weight of the composition.