KR101457938B1 - Transparent conducting film and touch panel and manufacture method thereof - Google Patents

Transparent conducting film and touch panel and manufacture method thereof Download PDF

Info

Publication number
KR101457938B1
KR101457938B1 KR1020080085381A KR20080085381A KR101457938B1 KR 101457938 B1 KR101457938 B1 KR 101457938B1 KR 1020080085381 A KR1020080085381 A KR 1020080085381A KR 20080085381 A KR20080085381 A KR 20080085381A KR 101457938 B1 KR101457938 B1 KR 101457938B1
Authority
KR
South Korea
Prior art keywords
film
transparent
transparent conductive
conductive film
resin layer
Prior art date
Application number
KR1020080085381A
Other languages
Korean (ko)
Other versions
KR20100026393A (en
Inventor
황웅
Original Assignee
엘지이노텍 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지이노텍 주식회사 filed Critical 엘지이노텍 주식회사
Priority to KR1020080085381A priority Critical patent/KR101457938B1/en
Publication of KR20100026393A publication Critical patent/KR20100026393A/en
Application granted granted Critical
Publication of KR101457938B1 publication Critical patent/KR101457938B1/en

Abstract

본 발명은 투명 전도성 필름 및 터치 패널 및 그 제조방법을 제공하기 위한 것으로, 제 1 투명 필름 기재(211)에 투명 수지층(212)을 이용하여 음각의 격벽을 형성하는 제 1 단계(ST1)와; 상기 투명 수지층(212)에 형성된 음각의 격벽에 흡수용 매질을 채워 흡수용 격벽(213)을 형성하는 제 2 단계(ST2);를 포함하여 구성함으로서, 투명 수지층에 흡수용 격벽을 형성하여 투명 전도성 필름에 입사된 빛의 반사를 막아 시인성을 향상시킬 수 있게 되는 것이다.The present invention provides a transparent conductive film, a touch panel, and a method of manufacturing the same, and includes a first step ST1 of forming an engraved barrier rib by using a transparent resin layer 212 on a first transparent film substrate 211, ; And a second step (ST2) of filling an absorbing medium with an engraved barrier rib formed on the transparent resin layer (212) to form an absorbing barrier rib (213), thereby forming an absorbing barrier rib on the transparent resin layer Reflection of light incident on the transparent conductive film can be prevented and visibility can be improved.

투명 전도성 필름, 터치 패널, 격벽, 시인성, 디스플레이 Transparent conductive film, touch panel, barrier rib, visibility, display

Description

투명 전도성 필름 및 터치 패널 및 그 제조방법{Transparent conducting film and touch panel and manufacture method thereof}TECHNICAL FIELD [0001] The present invention relates to a transparent conductive film and a touch panel,

본 발명은 투명 전도성 필름 및 터치 패널에 관한 것으로, 특히 투명 수지층에 흡수용 격벽을 형성하여 투명 전도성 필름에 입사된 빛의 반사를 막아 시인성을 향상시키기에 적당하도록 한 투명 전도성 필름 및 터치 패널 및 그 제조방법에 관한 것이다.The present invention relates to a transparent conductive film and a touch panel. More particularly, the present invention relates to a transparent conductive film and a touch panel suitable for enhancing visibility by preventing reflection of light incident on a transparent conductive film by forming an absorbing barrier rib on a transparent resin layer, And a manufacturing method thereof.

일반적으로 터치 패널은 컴퓨터, 이동통신 단말기, PDA(Personal Digital Assistant) 등에 사용되는 것으로, 디스플레이에 표시되어 있는 버튼을 손가락으로 접촉하는 것만으로 컴퓨터 등을 대화적, 직감적으로 조작함으로써 누구나 쉽게 사용할 수 있는 입력장치이다.Generally, a touch panel is used for a computer, a mobile communication terminal, a PDA (Personal Digital Assistant), etc., and can be easily used by anyone by operating a computer or the like interactively and intuitively only by touching a button displayed on a display with a finger Input device.

이러한 터치 패널에는 투명 도전성 필름이 사용되는데, 투명 도전성 필름은 투명 필름 기재와 투명 전도성 박막 등으로 구성된다.A transparent conductive film is used for such a touch panel. The transparent conductive film is composed of a transparent film base and a transparent conductive thin film.

도 1은 종래 투명 도전성 필름의 단면도로서, 대한민국특허청 공개번호 제 10-2007-0106704 호의 "투명 도전성 필름 및 터치 패널"에 개시된 내용이다.1 is a cross-sectional view of a conventional transparent conductive film, which is disclosed in Korean Patent Application Publication No. 10-2007-0106704 entitled " Transparent conductive film and touch panel ".

여기서 참조번호 1, 11a, 12a는 투명한 필름 기재이고, 11b는 점착제층이며, 2는 투명 도전성 박막이고, 3은 하드 코팅층이고, 4는 반사 방지층이다.Reference numerals 1, 11a and 12a denote transparent film substrates, 11b denotes a pressure-sensitive adhesive layer, 2 denotes a transparent conductive thin film, 3 denotes a hard coating layer, and 4 denotes an antireflection layer.

도 1에서 (a)는 투명한 필름 기재(1)가 1 매 사용되고 있다. 도 1에서 (b)는 (a)의 투명 도전성 필름에 있어서의 투명한 필름 기재(1) 대신에, 투명한 필름 기재(11a) 와 투명한 필름 기재(12a)가 점착제층(11b)을 개재하여 접합되어 있는 적층체(1)를 사용한 경우를 나타낸 것이다. 도 1에서 (c)는 (a)의 투명 도전성 필름의 하드 코팅층(3)에 추가로 반사 방지층(4)을 갖는 경우를 나타낸 것이다. 도 1에서 (d)는 (b)의 투명 도전성 필름의 하드 코팅층(3)에 추가로 반사 방지층(4)을 갖는 경우를 나타낸 것이다.In Fig. 1 (a), one transparent film substrate 1 is used. 1 (b), a transparent film substrate 11a and a transparent film substrate 12a are bonded to each other via a pressure-sensitive adhesive layer 11b in place of the transparent film substrate 1 in the transparent conductive film of (a) In the case of using the layered product (1). 1 (c) shows a case where the antireflection layer 4 is further provided on the hard coat layer 3 of the transparent conductive film of (a). 1 (d) shows a case where the antireflection layer 4 is further provided on the hard coat layer 3 of the transparent conductive film of (b).

그러나 이러한 종래기술은 단순히 투명층의 적층구조이기 때문에 필름의 어느 일방에서 입사된 빛이 어떤 방해 없이 필름을 투과하게 된다. 따라서 필름을 투과하는 빛은 필름의 여러 적층의 각 층마다에서 반사가 일어나며, 필름을 완전히 투과한 빛은 필름 하부에 형성된 구조물에 의해 반사된 빛이 다시 필름 쪽으로 입사하게 되어 최종적으로는 입사된 빛이 많은 부분이 반사되어 되돌아오게 된다.However, since such a conventional technique is simply a laminated structure of a transparent layer, light incident from one side of the film passes through the film without any interference. Therefore, the light transmitted through the film reflects from each layer of various layers of the film, and the light completely transmitted through the film causes the light reflected by the structure formed at the bottom of the film to enter the film again, Many of these parts are reflected and returned.

이와 같이 종래의 기술에 의한 필름은 많은 반사를 가지게 되어 디스플레이의 상부에 필름이 적용된 경우 사람의 시인성이 떨어지게 되는 문제점이 있다.As described above, the conventional film has many reflections, and when the film is applied to the upper part of the display, the visibility of the person is deteriorated.

도 2는 종래 감압성 양면 접착 시트의 단면도로서, 대한민국특허청 공개번호 제 10-2004-0030187 호의 "감압성 양면 점착 시트 및 표시장치에 대한 터치패널의 접착 고정 방법"에 개시된 내용이다.2 is a cross-sectional view of a conventional pressure-sensitive double-side adhesive sheet, which is disclosed in Korean Patent Application Publication No. 10-2004-0030187 entitled "Pressure-sensitive double-faced pressure-sensitive adhesive sheet and method for bonding and fixing a touch panel to a display device".

여기서 참조번호 21은 감압성 양면 점착 시트이고, 22는 투명 기재이며, 23은 터치패널측 투명 감압성 점착제층이고, 24는 표시장치측 투명 감압성 점착제층이다. 그래서 감압성 양면 점착 시트(21)는 터치패널측 투명 감압성 점착제층(23)이 투명 기재(22)의 한 면에 형성되어 있고, 표시장치측 투명 감압성 점착제층(24)이 투명 기재(22)의 다른 면에 형성되어 있는 방식으로 제공된다.Reference numeral 21 denotes a pressure-sensitive double-faced pressure-sensitive adhesive sheet, 22 denotes a transparent substrate, 23 denotes a pressure-sensitive transparent pressure-sensitive adhesive layer on the touch panel side, and 24 denotes a pressure- Thus, the pressure-sensitive double-side pressure-sensitive adhesive sheet 21 is obtained in such a manner that the pressure-sensitive adhesive layer 23 on the touch panel side is formed on one side of the transparent substrate 22 and the pressure-sensitive adhesive layer 24 on the display- 22 on the other side.

그러나 이러한 종래기술 또한 많은 반사를 가지게 되어 디스플레이의 상부에 적용된 경우 사람의 시인성이 떨어지게 되는 문제점이 있다.However, such a conventional technique also has a problem in that visibility of a human being is deteriorated when applied to an upper portion of a display due to a large amount of reflection.

이에 본 발명은 상기와 같은 종래의 제반 문제점을 해결하기 위해 제안된 것으로, 본 발명의 목적은 투명 수지층에 흡수용 격벽을 형성하여 투명 전도성 필름에 입사된 빛의 반사를 막아 시인성을 향상시킬 수 있는 투명 전도성 필름 및 터치 패널 및 그 제조방법을 제공하는데 있다.SUMMARY OF THE INVENTION The present invention has been made in order to solve the problems of the related art as described above, and it is an object of the present invention to provide a method of manufacturing a transparent conductive film by forming an absorbing barrier rib on a transparent resin layer to prevent reflection of light incident on the transparent conductive film, And a method of manufacturing the same.

도 3은 본 발명의 일 실시예에 의한 투명 전도성 필름 및 터치 패널의 제조방법을 보인 흐름도이다.3 is a flowchart illustrating a method of manufacturing a transparent conductive film and a touch panel according to an embodiment of the present invention.

그래서 본 발명 투명 전도성 필름의 제조방법은, 제 1 투명 필름 기재(211)에 투명 수지층(212)을 이용하여 음각의 격벽을 형성하는 제 1 단계(ST1)와; 상기 투명 수지층(212)에 형성된 음각의 격벽에 흡수용 매질을 채워 흡수용 격벽(213)을 형성하는 제 2 단계(ST2);를 포함하여 수행하는 것을 특징으로 한다.Thus, the method for manufacturing a transparent conductive film of the present invention comprises: a first step (ST1) of forming an engraved barrier rib by using a transparent resin layer (212) on a first transparent film substrate (211); And a second step (ST2) of forming an absorbing barrier 213 by filling an absorbing medium in a diagonal barrier rib formed in the transparent resin layer 212. [

상기 투명 전도성 필름의 제조방법은, 상기 흡수용 격벽(213)이 형성된 격벽 함유 필름(210)과 제 2 투명 필름 기재(230)를 점착제(220)를 이용하여 점착시키는 제 3 단계(ST3)와; 제 1 투명 전도성 박막(240)을 상기 제 1 투명 필름 기재(211) 또는 상기 제 2 투명 필름 기재(230)의 어느 일방에 형성하여 제 1 필름(200)을 형성하는 제 4 단계(ST4);를 더욱 포함하여 수행하는 것을 특징으로 한다.The method of manufacturing the transparent conductive film may further include a third step ST3 of adhering the barrier rib containing film 210 on which the absorption barrier ribs 213 are formed and the second transparent film base material 230 using the adhesive 220 ; A fourth step (ST4) of forming a first film (200) by forming a first transparent conductive thin film (240) on one of the first transparent film substrate (211) or the second transparent film substrate (230); And further comprising the steps of:

또한 본 발명 터치 패널의 제조방법은, 상기 제 4 단계 후 제 3 투명 필름 기재(310)에 제 2 투명 전도성 박막(320)이 형성된 제 2 필름(300)을 형성하는 제 5 단계(ST5)와; 상기 제 1 필름(200)과 상기 제 2 필름(300) 사이에 스페이서(400)를 두고 테두리 부분을 접착하여 터치 패널(100)을 제조하는 제 6 단계(ST6);를 포함하여 수행하는 것을 특징으로 한다.The method of manufacturing a touch panel of the present invention may further include a fifth step ST5 of forming a second film 300 having the second transparent conductive thin film 320 on the third transparent film substrate 310 after the fourth step ; And a sixth step (ST6) of manufacturing the touch panel 100 by attaching a spacer 400 between the first film 200 and the second film 300 by bonding the edges of the first film 200 and the second film 300 .

도 4는 본 발명의 일 실시예에 의한 투명 전도성 필름의 단면도이다.4 is a cross-sectional view of a transparent conductive film according to an embodiment of the present invention.

이에 도시된 바와 같이, 투명 도전성 박막이 형성된 투명 전도성 필름(200)에 있어서, 상기 투명 전도성 필름(200)은, 제 1 투명 필름 기재(211)의 일면에 형성된 투명 수지층(212)과; 상기 투명 수지층(212)의 음각에 채워져 형성된 흡수용 격벽(213);을 포함하여 구성된 것을 특징으로 한다.As shown in the figure, in the transparent conductive film 200 having the transparent conductive thin film formed thereon, the transparent conductive film 200 includes a transparent resin layer 212 formed on one surface of the first transparent film substrate 211; And an absorption barrier 213 formed on the transparent resin layer 212 so as to fill the depressions of the transparent resin layer 212.

상기 투명 전도성 필름(200)은, 상기 제 1 투명 필름 기재(211), 상기 투명 수지층(212), 상기 흡수용 격벽(213)을 구비한 격벽 함유 필름(210)의 하면에서 점착제(220)에 의해 점착된 제 2 투명 필름 기재(230)와; 상기 제 2 투명 필름 기 재(230)에 형성된 제 1 투명 전도성 박막(240);을 포함하여 구성된 것을 특징으로 한다.The transparent conductive film 200 is formed on the lower surface of the barrier rib containing film 210 having the first transparent film base 211, the transparent resin layer 212 and the absorption barrier ribs 213, A second transparent film substrate 230 adhered by the second transparent film substrate 230; And a first transparent conductive thin film (240) formed on the second transparent film substrate (230).

도 5는 본 발명의 다른 실시예에 의한 투명 전도성 필름의 단면도이다.5 is a cross-sectional view of a transparent conductive film according to another embodiment of the present invention.

이에 도시된 바와 같이, 상기 투명 전도성 필름(200)은, 상기 제 1 투명 필름 기재(211), 상기 투명 수지층(212), 상기 흡수용 격벽(213)을 구비한 격벽 함유 필름(210)의 상면에서 점착제(220)에 의해 점착된 제 2 투명 필름 기재(230)와; 상기 제 1 투명 필름 기재(211)에 형성된 제 1 투명 전도성 박막(240);을 포함하여 구성된 것을 특징으로 한다.As shown, the transparent conductive film 200 includes the first transparent film substrate 211, the transparent resin layer 212, and the barrier rib containing film 210 having the absorption barrier ribs 213 A second transparent film substrate (230) adhered on the upper surface by a pressure sensitive adhesive (220); And a first transparent conductive thin film (240) formed on the first transparent film substrate (211).

도 6은 본 발명의 일 실시예에 의한 터치 패널의 단면도이다.6 is a cross-sectional view of a touch panel according to an embodiment of the present invention.

이에 도시된 바와 같이, 상기 제 1 필름(200)의 일 측면에 형성되며, 제 2 투명 필름 기재(310)에 제 2 투명 전도성 박막이 형성되고, 상기 제 1 필름(200)과의 사이에 스페이서(400)가 위치하고 테두리 부분이 상기 제 1 필름(200)과 접착된 제 2 필름(300);을 포함하여 구성된 것을 특징으로 한다.As shown, a second transparent conductive thin film is formed on one side of the first film 200, and a second transparent conductive thin film is formed on the second transparent film substrate 310, And a second film (300) having a rim portion (400) and a rim portion bonded to the first film (200).

본 발명에 의한 투명 전도성 필름 및 터치 패널 및 그 제조방법은 투명 수지층에 흡수용 격벽을 형성하여 투명 전도성 필름에 입사된 빛의 반사를 막아 시인성을 향상시킬 수 있는 효과가 있게 된다.The transparent conductive film, the touch panel, and the method of manufacturing the same according to the present invention have the effect of improving the visibility by forming the absorption barrier in the transparent resin layer to prevent reflection of light incident on the transparent conductive film.

이에 따라 본 발명은 디스플레이의 전면에 적용하여 실외에서 태양빛의 반사에 의해 시인성이 떨어지는 영향에 대해 흡수용 격벽을 이용하여 시인성을 높여줄 수 있게 된다.Accordingly, the present invention can be applied to a front surface of a display, thereby enhancing visibility by using an absorption barrier for the influence of visible light due to reflection of sunlight outdoors.

이와 같이 구성된 본 발명에 의한 투명 전도성 필름 및 터치 패널 및 그 제조방법의 바람직한 실시예를 첨부한 도면에 의거하여 상세히 설명하면 다음과 같다. 하기에서 본 발명을 설명함에 있어 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다. 그리고 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서, 이는 사용자, 운용자의 의도 또는 판례 등에 따라 달라질 수 있으며, 이에 따라 각 용어의 의미는 본 명세서 전반에 걸친 내용을 토대로 해석되어야 할 것이다.Hereinafter, preferred embodiments of the transparent conductive film and the touch panel according to the present invention will be described in detail with reference to the accompanying drawings. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear. It is to be understood that the following terms are defined in consideration of the functions of the present invention, and may be changed according to the intention of the user, the operator, or the precedent, and the meaning of each term should be interpreted based on the contents will be.

먼저 본 발명은 투명 수지층에 흡수용 격벽을 형성하여 투명 전도성 필름에 입사된 빛의 반사를 막아 시인성을 향상시키고자 한 것이다.First, the present invention aims to improve the visibility by forming an absorption barrier on the transparent resin layer to prevent reflection of light incident on the transparent conductive film.

도 3은 본 발명의 일 실시예에 의한 투명 전도성 필름 및 터치 패널의 제조방법을 보인 흐름도이다.3 is a flowchart illustrating a method of manufacturing a transparent conductive film and a touch panel according to an embodiment of the present invention.

그래서 본 발명에서는 투명 전도성 필름 또는 터치 패널을 제조하기 위해 다음과 같이 수행한다.In order to manufacture a transparent conductive film or a touch panel, the present invention is performed as follows.

먼저 제 1 투명 필름 기재(211)에 투명 수지층(212)을 이용하여 음각의 격벽을 형성한다(ST1).First, the transparent resin layer 212 is formed on the first transparent film substrate 211 to form an engraved barrier rib (ST1).

그리고 투명 수지층(212)에 형성된 음각의 격벽에 흡수용 매질을 채워 흡수 용 격벽(213)을 형성한다(ST2).Then, an absorbing barrier 213 is formed by filling the absorbing medium in the diagonal barrier ribs formed in the transparent resin layer 212 (ST2).

그리고 흡수용 격벽(213)이 형성된 격벽 함유 필름(210)과 제 2 투명 필름 기재(230)를 점착제(220)를 이용하여 점착시킨다(ST3).The barrier rib containing film 210 having the absorption barrier ribs 213 is adhered to the second transparent film substrate 230 using the adhesive 220 (ST3).

또한 제 1 투명 전도성 박막(240)을 제 1 투명 필름 기재(211) 또는 제 2 투명 필름 기재(230)의 어느 일방에 형성하여 제 1 필름(200)을 형성한다(ST4).The first transparent conductive thin film 240 is formed on either the first transparent film substrate 211 or the second transparent film substrate 230 to form the first film 200 (ST4).

한편 제 3 투명 필름 기재(310)에 제 2 투명 전도성 박막(320)이 형성된 제 2 필름(300)을 형성한다(ST5).On the other hand, a second film 300 having a second transparent conductive thin film 320 formed on the third transparent film substrate 310 is formed (ST5).

그리고 제 1 필름(200)과 제 2 필름(300) 사이에 스페이서(400)를 두고 테두리 부분을 접착하여 터치 패널(100)을 제조한다(ST6).A spacer 400 is sandwiched between the first film 200 and the second film 300 and the edge of the first film 200 and the second film 300 are bonded together to manufacture the touch panel 100 (ST6).

도 4는 본 발명의 일 실시예에 의한 투명 전도성 필름의 단면도이고, 도 5는 본 발명의 다른 실시예에 의한 투명 전도성 필름의 단면도이다.FIG. 4 is a cross-sectional view of a transparent conductive film according to an embodiment of the present invention, and FIG. 5 is a cross-sectional view of a transparent conductive film according to another embodiment of the present invention.

그래서 도 4의 경우는 제 2 투명 필름 기재(230)를 점착제(220)에 의해 흡수용 격벽(213)이 형성된 투명 수지층(212)과 결합시키고, 제 2 투명 필름 기재(230)에 제 1 투명 전도성 박막(240)을 결합시킨 예를 보인 것이다. 또한 제 5의 경우는 격벽 함유 필름(210)의 제 1 투명 필름 기재(211)에 제 1 투명 전도성 박막(240)을 결합시킨 예를 보인 것이다.4, the second transparent film substrate 230 is bonded to the transparent resin layer 212 formed with the absorbing barrier 213 by the adhesive 220 and the first transparent film substrate 230 is bonded to the first transparent film substrate 230 And the transparent conductive thin film 240 is bonded. In the fifth case, the first transparent conductive thin film 240 is bonded to the first transparent film base material 211 of the barrier rib containing film 210.

도 6은 본 발명의 일 실시예에 의한 터치 패널의 단면도이다.6 is a cross-sectional view of a touch panel according to an embodiment of the present invention.

그래서 터치 패널(100)을 구현하기 위해서 제 2 투명 필름 기재(310)에 제 2 투명 전도성 박막을 형성하여 제 2 필름(300)을 제조한다.In order to realize the touch panel 100, a second transparent conductive thin film is formed on the second transparent film substrate 310 to produce the second film 300.

그리고 제 1 필름(200)과 제 2 필름(300) 사이에 스페이서(400)가 위치하도 록 하고, 제 1 필름(200)과 제 2 필름(300)의 테두리 부분이 접착되도록 하여 터치 패널(100)을 구현한다.The spacers 400 are positioned between the first film 200 and the second film 300 and the edge portions of the first film 200 and the second film 300 are adhered to each other so that the touch panel 100 ).

도 7은 본 발명에서 투명 수지층에 형성된 흡수용 격벽에 의해 시인성이 향상되는 예를 보인 개념도이다.7 is a conceptual diagram showing an example in which visibility is improved by the absorption barrier formed on the transparent resin layer in the present invention.

그래서 이렇게 제작된 필름은 도 7에서와 같이 상부에서 외부광이 입사하게 되었을 때 흡수용 격벽(213)이 없을 경우에는 빛이 투과/반사를 일으키게 되지만, 흡수용 격벽(213)이 있을 경우에 외부광은 흡수용 격벽(213)이 흡수하게 되어 외부광에 대한 반사를 줄여줄 수 있게 되기 때문에 실외에서의 시인성을 향상 시킬 수 있다.7, light is transmitted / reflected when there is no absorbing barrier 213 when external light is incident on the upper part as shown in FIG. 7. However, when there is an absorbing barrier 213, The light can be absorbed by the absorption barrier 213 to reduce the reflection to the external light, so that the visibility in the outdoor can be improved.

이처럼 본 발명은 투명 수지층에 흡수용 격벽을 형성하여 투명 전도성 필름에 입사된 빛의 반사를 막아 시인성을 향상시키게 되는 것이다.As described above, according to the present invention, the absorption barrier is formed in the transparent resin layer to prevent reflection of light incident on the transparent conductive film, thereby improving visibility.

이상에서 실시예를 들어 본 발명을 더욱 상세하게 설명하였으나, 본 발명은 반드시 이러한 실시예로 국한되는 것은 아니고, 본 발명의 기술사상을 벗어나지 않는 범위 내에서 다양하게 변형실시될 수 있다. 따라서 본 발명에 개시된 실시예들은 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술적 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호범위는 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술적 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not to be limited to the details thereof, and various changes and modifications may be made without departing from the spirit and scope of the invention. Therefore, the embodiments disclosed in the present invention are not intended to limit the technical spirit of the present invention, but are intended to illustrate and not limit the scope of the technical spirit of the present invention. The scope of protection of the present invention should be construed according to the claims, and all technical ideas which are within the scope of the same should be interpreted as being included in the scope of the present invention.

도 1은 종래 투명 도전성 필름의 단면도이다.1 is a cross-sectional view of a conventional transparent conductive film.

도 2는 종래 감압성 양면 접착 시트의 단면도이다.2 is a cross-sectional view of a conventional pressure-sensitive double-faced adhesive sheet.

도 3은 본 발명의 일 실시예에 의한 투명 전도성 필름 및 터치 패널의 제조방법을 보인 흐름도이다.3 is a flowchart illustrating a method of manufacturing a transparent conductive film and a touch panel according to an embodiment of the present invention.

도 4는 본 발명의 일 실시예에 의한 투명 전도성 필름의 단면도이다.4 is a cross-sectional view of a transparent conductive film according to an embodiment of the present invention.

도 5는 본 발명의 다른 실시예에 의한 투명 전도성 필름의 단면도이다.5 is a cross-sectional view of a transparent conductive film according to another embodiment of the present invention.

도 6은 본 발명의 일 실시예에 의한 터치 패널의 단면도이다.6 is a cross-sectional view of a touch panel according to an embodiment of the present invention.

도 7은 본 발명에서 투명 수지층에 형성된 흡수용 격벽에 의해 시인성이 향상되는 예를 보인 개념도이다.7 is a conceptual diagram showing an example in which visibility is improved by the absorption barrier formed on the transparent resin layer in the present invention.

* 도면의 주요 부분에 대한 부호의 설명 *Description of the Related Art [0002]

100 : 터치 패널100: Touch panel

200 : 제 1 필름(투명 전도성 필름)200: First film (transparent conductive film)

210 : 격벽 함유 필름210: barrier rib containing film

211 : 제 1 투명 필름 기재211: First transparent film substrate

212 : 투명 수지층212: transparent resin layer

213 : 흡수용 격벽213: absorption barrier

220 : 점착제220: Adhesive

230 : 제 2 투명 필름 기재230: second transparent film substrate

240 : 제 1 투명 전도성 박막240: first transparent conductive thin film

300 : 제 2 필름300: Second film

310 : 제 3 투명 필름 기재310: Third transparent film base

320 : 제 2 투명 전도성 박막320: second transparent conductive thin film

Claims (7)

제 1 투명 필름 기재(211)에 투명 수지층(212)을 이용하여 음각의 격벽을 형성하는 제 1 단계(ST1)와;A first step (ST1) of forming an engraved barrier rib on the first transparent film substrate (211) by using a transparent resin layer (212); 상기 투명 수지층(212)에 형성된 음각의 격벽에 흡수용 매질을 채워 흡수용 격벽(213)을 형성하는 제 2 단계(ST2);A second step (ST2) of forming an absorbing barrier 213 by filling an absorbing medium in the partition walls formed in the transparent resin layer 212; 를 포함하여 수행하는 것을 특징으로 하는 투명 전도성 필름의 제조방법.Wherein the step of forming the transparent conductive film comprises: 청구항 1에 있어서,The method according to claim 1, 상기 투명 전도성 필름의 제조방법은,The method for producing the transparent conductive film may further comprise: 상기 흡수용 격벽(213)이 형성된 격벽 함유 필름(210)과 제 2 투명 필름 기재(230)를 점착제(220)를 이용하여 점착시키는 제 3 단계(ST3)와;A third step (ST3) of adhering the barrier rib containing film (210) having the absorption barrier rib (213) and the second transparent film base material (230) using an adhesive (220); 제 1 투명 전도성 박막(240)을 상기 제 1 투명 필름 기재(211) 또는 상기 제 2 투명 필름 기재(230)의 어느 일방에 형성하여 제 1 필름(200)을 형성하는 제 4 단계(ST4);A fourth step (ST4) of forming a first film (200) by forming a first transparent conductive thin film (240) on one of the first transparent film substrate (211) or the second transparent film substrate (230); 를 더욱 포함하여 수행하는 것을 특징으로 하는 투명 전도성 필름의 제조방법.Wherein the step of forming the transparent conductive film further comprises: 청구항 2에 있어서,The method of claim 2, 상기 투명 전도성 필름의 제조방법은,The method for producing the transparent conductive film may further comprise: 상기 제 4 단계 후 제 3 투명 필름 기재(310)에 제 2 투명 전도성 박막(320)이 형성된 제 2 필름(300)을 형성하는 제 5 단계(ST5)와;A fifth step (ST5) of forming a second film (300) having a second transparent conductive thin film (320) on the third transparent film substrate (310) after the fourth step; 상기 제 1 필름(200)과 상기 제 2 필름(300) 사이에 스페이서(400)를 두고 테두리 부분을 접착하여 터치 패널(100)을 제조하는 제 6 단계(ST6);A sixth step (ST6) of manufacturing a touch panel (100) by bonding a rim with a spacer (400) between the first film (200) and the second film (300); 를 더욱 포함하여 수행하는 것을 특징으로 하는 투명 전도성 필름의 제조방법.Wherein the step of forming the transparent conductive film further comprises: 투명 도전성 박막이 형성된 투명 전도성 필름(200)에 있어서,In a transparent conductive film (200) having a transparent conductive thin film formed thereon, 상기 투명 전도성 필름(200)은,The transparent conductive film (200) 제 1 투명 필름 기재(211)의 일면에 형성된 투명 수지층(212)과;A transparent resin layer 212 formed on one surface of the first transparent film substrate 211; 상기 투명 수지층(212)의 음각에 채워져 형성된 흡수용 격벽(213);An absorption barrier 213 formed to fill an engraved surface of the transparent resin layer 212; 을 포함하는 것을 특징으로 하는 투명 전도성 필름.And a transparent conductive film. 청구항 4에 있어서,The method of claim 4, 상기 투명 전도성 필름(200)은,The transparent conductive film (200) 상기 제 1 투명 필름 기재(211), 상기 투명 수지층(212), 상기 흡수용 격벽(213)을 구비한 격벽 함유 필름(210)의 하면에서 점착제(220)에 의해 점착된 제 2 투명 필름 기재(230)와;The second transparent film substrate 210 adhered by the adhesive 220 on the lower surface of the partition wall containing film 210 having the first transparent film substrate 211, the transparent resin layer 212 and the absorption barrier 213, (230); 상기 제 2 투명 필름 기재(230)에 형성된 제 1 투명 전도성 박막(240);A first transparent conductive thin film 240 formed on the second transparent film substrate 230; 을 포함하는 것을 특징으로 하는 투명 전도성 필름.And a transparent conductive film. 청구항 4에 있어서,The method of claim 4, 상기 투명 전도성 필름(200)은,The transparent conductive film (200) 상기 제 1 투명 필름 기재(211), 상기 투명 수지층(212), 상기 흡수용 격벽(213)을 구비한 격벽 함유 필름(210)의 상면에서 점착제(220)에 의해 점착된 제 2 투명 필름 기재(230)와;The second transparent film substrate 210 adhered by the adhesive 220 on the upper surface of the partition wall containing film 210 having the first transparent film substrate 211, the transparent resin layer 212 and the absorption barrier 213, (230); 상기 격벽 함유 필름(210)과 점착제(220)에 의해 점착된 제 2 투명 필름 기재(230)와;A second transparent film substrate 230 adhered by the barrier rib containing film 210 and the adhesive 220; 상기 제 1 투명 필름 기재(211)에 형성된 제 1 투명 전도성 박막(240);A first transparent conductive thin film (240) formed on the first transparent film base (211); 을 포함하는 것을 특징으로 하는 투명 전도성 필름.And a transparent conductive film. 청구항 4 내지 6 중 어느 한 항의 투명 전도성 필름(200);A transparent conductive film (200) according to any one of claims 4 to 6; 상기 투명 전도성 필름(200)의 일 측면에 형성되며, 제 2 투명 필름 기재(310)에 제 2 투명 전도성 박막이 형성되고, 상기 투명 전도성 필름(200)과의 사이에 스페이서(400)가 위치하고 테두리 부분이 상기 투명 전도성 필름(200)과 접착된 제 2 필름(300);A second transparent conductive thin film is formed on the second transparent film substrate 310 and a spacer 400 is positioned between the transparent conductive film 200 and the edge of the transparent conductive film 200, A second film (300) having a portion bonded to the transparent conductive film (200); 을 포함하는 것을 특징으로 하는 터치 패널.And a touch panel.
KR1020080085381A 2008-08-29 2008-08-29 Transparent conducting film and touch panel and manufacture method thereof KR101457938B1 (en)