KR101415891B1 - Slope reinforcement methode for using thr high performance shotcrete and reinforcement - Google Patents

Slope reinforcement methode for using thr high performance shotcrete and reinforcement Download PDF

Info

Publication number
KR101415891B1
KR101415891B1 KR1020130159102A KR20130159102A KR101415891B1 KR 101415891 B1 KR101415891 B1 KR 101415891B1 KR 1020130159102 A KR1020130159102 A KR 1020130159102A KR 20130159102 A KR20130159102 A KR 20130159102A KR 101415891 B1 KR101415891 B1 KR 101415891B1
Authority
KR
South Korea
Prior art keywords
concrete
shotcrete
mixed
mixing
slope
Prior art date
Application number
KR1020130159102A
Other languages
Korean (ko)
Inventor
윤경구
Original Assignee
강원대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강원대학교산학협력단 filed Critical 강원대학교산학협력단
Priority to KR1020130159102A priority Critical patent/KR101415891B1/en
Application granted granted Critical
Publication of KR101415891B1 publication Critical patent/KR101415891B1/en
Priority to CN201480069796.4A priority patent/CN105829612B/en
Priority to PCT/KR2014/011815 priority patent/WO2015093760A1/en

Abstract

The present invention relates to a combined type slope reinforcing method using high performance shotcrete and a reinforcing member comprising the steps of: producing normal concrete with compression strength of 21-30 MPa in a batcher plant and transferring the normal concrete to a field; increasing the fluidity of the normal concrete by introducing 20-40% of bubbles, based on the volume of the normal concrete, to the normal concrete; forming normal strength shotcrete by mixing the normal concrete with low grade mixing material, which is either of fly ash and slag fine powder or the mixture of the fly ash and the slag fine powder; forming high performance shotcrete by mixing the normal concrete with high grade mixing material which is either of silica fume and metakaolin or the mixture of the silica fume and the metakaolin; forming color shotcrete by mixing the normal concrete with a coloring agent such as iron oxide or carbon black; and successively forming an inner layer part, an outer layer part, and a surface layer part on a slope. Therefore, the present invention reduces construction costs and secures high strength and high durability of the slope. Moreover, maintenance for the slope can be easily performed.

Description

고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법{Slope reinforcement methode for using thr high performance shotcrete and reinforcement}Technical Field [0001] The present invention relates to a slope reinforcement method using a high-performance shotcrete and a reinforcing member,

본 발명은 사면 보강방법에 관한 것으로, 보다 상세하게는, 배처플랜트에서 압축강도 21~30MPa의 보통콘크리트를 생산하여 현장 이송 후, 체적 대비 20~40%의 기포를 혼입하여 유동성을 증가시킨 상태에서 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료를 혼입하여 보통강도 숏크리트를 형성하고, 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고급 혼합재료를 혼입하여 고성능 숏크리트를 형성하며, 산화철이나 카본블랙의 착색재료를 혼입하여 칼라 숏크리트를 각각 형성하여 사면에 각각 내층부, 외층부, 표층부를 순차적으로 시공함으로, 시공비용 절감 및 고강도와 고내구성을 확보하여 유지관리를 용이하게 할 수 있는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법에 관한 것이다.
The present invention relates to a slope reinforcement method, and more particularly, to a slope reinforcement method in which a concrete plant having a compressive strength of 21 to 30 MPa is produced in a plant plant, and 20 to 40% A fly ash or a slag fine powder, or a fly ash or a slag fine powder to form an ordinary strength shotcrete, and a high-grade mixed material comprising either silica fume or meta kaolin or silica fume and meta kaolin To form a high-performance shotcrete. By mixing coloring materials such as iron oxide and carbon black to form color shotcrete, the inner layer portion, the outer layer portion and the surface layer portion are successively formed on each slope, thereby reducing the construction cost and increasing the strength and durability And a high-performance shotcrete that can be easily maintained and maintained. If it directed to a reinforcement method.

일반적으로 숏크리트는, 고압의 공기를 이용해 콘크리트를 대상 구조물에 뿜어 붙이는 공법으로, 최근에는 습식 숏크리트가 주로 사용되는데, 이는 시멘트, 골재, 물 등을 반죽하여 습한 상태의 혼합된 재료를 펌프 또는 압축공기로 압송하여 노즐 부근에서 뿜어 붙이는 방식으로 거푸집설치가 필요 없으며, 접근이 어려운 비탈면 등에 적용성이 뛰어나다.In general, shotcrete is a method of spraying concrete onto a target structure using high-pressure air. In recent years, wet shotcrete is mainly used. This is a method of kneading cement, aggregate, water, , It is not necessary to install a mold in a way that it is sprayed near the nozzle, and it is excellent in applicability to a slope surface which is difficult to approach.

상기 숏크리트는, 재령 28일 압축강도가 21MPa 이상으로 규정하고 있는 보통강도 숏크리트와 재령 28일 압축강도가 35MPa 이상으로 규정하고 있는 고강도 숏크리트로 분류되며, 상기 고강도 숏크리트는 고내구성을 함께 지니고 있으므로 일반적으로 고성능 숏크리트로 불리기도 한다.The shotcrete is classified into ordinary shotcrete having a compression strength of 21 MPa or more at 28 days of age and high-strength shotcrete having a compression strength of 28 MPa or more at an age of 28 days. Since the high-strength shotcrete has high durability, It is also called high performance shotcrete.

국내에서는 보통강도 숏크리트가 적용되는 경우가 대부분으로 이는 낮은 강도와 낮은 내구성으로 조기에 파손되는 문제점이 있었다.In Korea, most of strength shotcrete is applied in most cases, which has a problem of early breakage due to low strength and low durability.

표 1은 한국도로공사에서 국내의 고속도로 상에 333개소에 이르는 비탈면에 숏크리트공이 시공되어 있는 것을 전수조사하여 발표한 것으로, 균열과 백화 등 보통 이하의 품질을 나타낸 비탈면이 17.4%, 58개소로 나타났다. 조사결과, 비탈면의 균열은 53%, 백화는 89%, 골재화는 74%에서 진행중인 것으로 조사되었다.Table 1 shows that a shotcrete ball was installed on slopes up to 333 on the Korean highway at Korea Highway Corporation, and 17.4% of the slopes exhibited normal quality such as cracks and whiteness, and 58 locations . As a result, it was found that slope cracks were 53%, whiteness 89%, and aggregate 74%.

숏크리트 품질조사 현황(한국도로공사 연구보고서, 2011)Shotcrete quality survey status (Korea Highway Corporation Research Report, 2011) 구분division 균열
(EA)crack
(EA) 박리
(EA)Exfoliation
(EA) 백화
(EA)all sorts of flowers
(EA) 공동
(EA)public
(EA) 용수출
(EA)Export
(EA) 골재화
면적(㎡)Aggregation
Area (㎡) 최대S/C
두께(mm)Maximum S / C
Thickness (mm) 최대S/C
두께(mm)Maximum S / C
Thickness (mm) 평균압축강도
(MPa)Average compressive strength
(MPa) 평균Average 3.313.31 0.770.77 5.035.03 0.140.14 4.174.17 176.1176.1 86.9886.98 46.1546.15 17.9317.93 표준편차Standard Deviation 4.834.83 1.561.56 4.724.72 0.430.43 6.216.21 395.9395.9 11.7511.75 11.2111.21 4.654.65

한편, 사면의 보호 및 보강을 목적으로 사면보호공법과 사면보강공법이 있는데, 상기 사면보강공법은 비탈면의 절취로 안전율을 확보하기 위하여 비탈면 구배를 완만하게 조정하거나, 숏크리트공, 옹벽공, 말뚝공, 앵커공의 저항력을 이용하는 공법이다.In the meantime, there are slope protection methods and slope reinforcement methods for the purpose of protection and reinforcement of slopes. In the slope reinforcement method, slope inclination is gently adjusted to secure a safety rate by cutting slopes, or shotcrete ball, retaining wall ball, , And anchor balls.

이들 공법은 비탈면의 용도, 토질 및 암반특성, 지반여건, 유지보수조건, 경관 등을 종합적으로 고려하여 선정하는 것이 일반적이나, 현재까지는 기능성만을 중요시하고 경관을 도외시하여 주변의 경관을 해치는 경우가 많았다.These methods are generally selected taking into account the use of slopes, soil and rock properties, ground conditions, maintenance conditions, and landscapes, but until now, only the functionality has been emphasized and the landscape has been neglected by overlooking the landscape .

상기 경관을 중요시하여 기존 구조물인 사면에 인공암을 제작 및 설치하나, 인공암은 사면 외부에 추가 부착하여 시공하는 것으로, 내측에 인공암과 연결 및 지지하는 지지부재를 가지고 시공되며, 인공암의 내측부에 접착제를 도포하고 프라이머를 사용하여 인공암패널을 형성하나, 이는 구조적인 성능은 지니지 못한다.The artificial arm is manufactured and installed on the slope, which is a conventional structure, with respect to the landscape. The artificial arm is installed by being attached to the outside of the slope. The artificial arm is installed with a supporting member for connecting and supporting the artificial arm on the inside, An adhesive is applied to the medial side and the primer is used to form an artificial arm panel, but this does not have structural performance.

또한, 인공암은 주로 에폭시나 폴리머를 주요 결합재로 사용함으로써, 자외선에 노출될 시, 취성이 강해져 내구성이 현저히 떨어지므로, 보통 3~4년을 사용연한으로 가지고 있어 주기적인 유지보수가 필요하므로 유지관리가 어려운 문제점이 있었다.
Since artificial rock is mainly used as an epoxy or a polymer as a main binder, when exposed to ultraviolet rays, brittleness is intensified and durability is significantly lowered. Therefore, it is necessary to periodically maintain maintenance for 3 to 4 years There was a problem that management was difficult.

대한민국 등록특허 제10-1157874호
Korean Patent No. 10-1157874

이에 본 발명은 상기와 같은 종래의 제반 문제점을 해결하기 위한 것으로, 본 발명의 목적은, 배처플랜트에서 압축강도 21~30MPa의 보통콘크리트를 생산하여 현장 이송 후, 체적 대비 20~40%의 기포를 혼입하여 유동성을 증가시킨 상태에서 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료를 혼입하여 보통강도 숏크리트를 형성하고, 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고급 혼합재료를 혼입하여 고성능 숏크리트를 형성하며, 산화철이나 카본블랙의 착색재료를 혼입하여 칼라 숏크리트를 각각 형성하여 사면에 각각 내층부, 외층부, 표층부를 순차적으로 시공하여 시공비용을 절감할 수 있는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법을 제공함에 있다.Accordingly, the present invention has been made to solve the above-mentioned conventional problems, and it is an object of the present invention to provide a concrete plant with a compressive strength of 21 to 30 MPa produced in a plant plant, Mixed fly ash or a slag fine powder mixed with fly ash or slag fine powder to form an ordinary strength shotcrete, and either one of silica fume and meta kaolin or silica fume High-performance shotcrete is formed by mixing high-quality mixed material mixed with meta-kaolin, coloring materials such as iron oxide and carbon black are mixed to form color shotcrete, and the inner layer portion, the outer layer portion and the surface layer portion are successively formed on the slope, The present invention provides a combined slope reinforcement method using a high-performance shotcrete and a reinforcing member capable of reducing There.

또한, 본 발명의 다른 목적은, 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료가 혼입된 보통 숏크리트로 옹벽의 내층부를 형성하여 경제성과 시공의 수월성을 제공하고, 외층부는 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고급 혼합재료가 혼입된 고성능 숏크리트로 타설하여 고강도 및 고내구성을 확보하며, 표층부는 칼라 숏크리트로 타설하여 아름답고 자연스러운 모양으로 마무리함으로써, 경관이 미려하면서도 유지관리가 용이한 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법을 제공함에 있다.Another object of the present invention is to provide an inner layer portion of a retaining wall made of ordinary shotcrete mixed with a fly ash or a slag fine powder or a mixture of fly ash and slag fine powder to provide economy and ease of construction, The outer layer is poured into a high-performance shotcrete containing either silica fume or meta kaolin or a high-quality mixed concrete mixed with silica fume and meta kaolin to ensure high strength and high durability. The surface layer is cast into a color shotcrete to form a beautiful and natural shape. The present invention provides a combined slope reinforcement method using a high-performance shotcrete and a reinforcing member that are easy to maintain while maintaining a beautiful view.

또한, 본 발명의 또 다른 목적은, 사면을 보강하여 안정성을 확보하기 위해 설치된 앵커와 고성능 숏크리트를 타설하여 일체화함으로써, 구조적 안정성과 경제성을 확보할 수 있는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법을 제공함에 있다.
It is another object of the present invention to provide a high performance shotcrete which can secure structural stability and economical efficiency by integrating anchors installed with high performance shotcrete in order to secure stability by reinforcing slopes, Method.

본 발명 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법은,The present invention provides a combined slope reinforcement method using a high-performance shotcrete and a reinforcing member,

내층부를 형성하기 전, 사면을 보강부재로 안정화하는 단계와;Stabilizing the slope with a reinforcing member before forming the inner layer portion;

물, 시멘트, 골재를 일정비율로 배합하여 압축강도가 21~30MPa의 보통콘크리트를 생산 및 현장 이송하는 단계와;Water, cement and aggregate at a predetermined ratio to produce and transport the ordinary concrete having a compressive strength of 21 to 30 MPa;

상기 보통콘크리트에 기포 및 저급 혼합재료를 혼합부로 혼합하여 형성된 보통강도 콘크리트가 숏팅안내부재를 통해 사면으로 배출되어 외층부보다 두꺼운 두께로 내층부를 형성하는 단계와;The ordinary strength concrete formed by mixing the bare cell and the low grade mixed material into the mixed concrete is discharged to the slope through the shorting guide member to form an inner layer with a thickness greater than that of the outer layer;

상기 보통콘크리트에 기포 및 고급 혼합재료를 혼합부로 혼합하여 형성된 고성능 콘크리트가 숏팅안내부재를 통해 내층부 상면으로 내층부의 두께보다 얇은 두께로 배출되어 외층부를 형성하는 단계와;The high-performance concrete formed by mixing the normal concrete with the bubbles and the high-grade mixed material in the mixing portion is discharged through the shorting guide member to a thickness smaller than the thickness of the inner layer portion to form an outer layer portion;

상기 보통콘크리트에 기포 및 착색재료를 혼합부로 혼합하여 형성된 칼라 콘크리트가 숏팅안내부재를 통해 외층부 상면으로 배출되어 표층부를 형성하는 단계와;The color concrete formed by mixing the bare cell and the coloring material into the mixture of the ordinary concrete is discharged to the upper surface of the outer layer through the shorting guide member to form a surface layer;

상기 숏팅안내부재로 각 콘크리트가 배출될 때, 5기압 이상의 고압의 공기를 뿜어 각 콘크리트에 포함된 기포를 소산시키면서 슬럼프가 감소되도록 하는 것을 특징으로 하는 것이다.
When the concrete is discharged by the shorting guide member, air of a high pressure of 5 atm or higher is blown to dissipate the bubbles contained in the concrete, thereby reducing the slump.

본 발명에 의하면, 배처플랜트에서 압축강도 21~30MPa의 보통콘크리트를 생산하여 현장 이송 후, 체적 대비 20~40%의 기포를 혼입하여 유동성을 증가시킨 상태에서 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료를 혼입하여 보통강도 숏크리트를 형성하고, 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고급 혼합재료를 혼입하여 고성능 숏크리트를 형성하며, 산화철이나 카본블랙의 착색재료를 혼입하여 칼라 숏크리트를 각각 형성하여 사면에 각각 내층부, 외층부, 표층부를 순차적으로 시공하여 고강도 숏크리트로 사면을 시공할 때보다 시공비용을 절감할 수 있으므로 경제성을 향상시킬 수 있는 이점을 가질 수 있는 것이다.According to the present invention, it is possible to produce ordinary concrete having a compressive strength of 21 to 30 MPa in a batch plant, and after the site is transferred, 20 to 40% of bubbles are mixed with the mixture to increase fluidity, A high-performance shotcrete is formed by mixing a low-grade mixed material obtained by mixing ash or slag fine powder and an advanced mixed material obtained by mixing either silica fume or meta kaolin or silica fume with meta kaolin, And coloring materials of carbon black are mixed to form color shotcrete, and the inner layer, outer layer and surface layer are successively formed on the slope to reduce the construction cost compared with the case of constructing the slope with the high-strength shotcrete, thereby improving the economical efficiency It can have the advantage of being able to.

또한, 본 발명에 의하면, 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료가 혼입된 보통 숏크리트로 옹벽의 내층부를 형성하여 경제성과 시공의 수월성을 제공하고, 외층부는 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고성능 숏크리트로 타설하여 고강도 및 고내구성을 확보하며, 표층부는 칼라 숏크리트로 타설하여 아름답고 자연스러운 모양으로 마무리함으로써, 경관이 미려하면서도 유지관리를 용이하게 할 수 있는 이점을 가질 수 있는 것이다.Further, according to the present invention, an inner layer portion of a retaining wall is formed by a normal shotcrete mixed with a fly ash or a slag fine powder or a mixture of fly ash and slag fine powder to provide economy and ease of construction, High performance shotcrete with silica fume and meta kaolin mixed with silica fume and meta kaolin is installed to ensure high strength and high durability. The surface part is put into a color shotcrete to finish in a beautiful and natural shape, It is possible to have an advantage that it can be facilitated.

또한, 본 발명에 의하면, 사면을 보강하여 안정성을 확보하기 위해 설치된 앵커와 고성능 숏크리트를 타설하여 일체화함으로써, 구조적 안정성과 경제성을 확보할 수 있는 이점을 가질 수 있는 것이다.
Further, according to the present invention, an anchor and a high-performance shotcrete, which are installed to reinforce the slope and secure stability, are integrated into one body, thereby having an advantage of securing structural stability and economical efficiency.

도 1은 본 발명의 흐름도이다.
도 2는 본 발명의 사면을 안정화하는 도면
도 3은 본 발명이 보통콘크리트를 형성하는 도면
도 4는 본 발명의 기포를 나타낸 도면
도 5 내지 도 6은 본 발명의 혼합부를 나타낸 도면
도 7 내지 도 12는 본 발명 보통콘크리트, 고성능 콘크리트 및 숏팅콘크리트의 슬럼프 사진
도 13 내지 도 15는 본 발명의 숏팅과정도
도 16은 본 발명에 착색재료를 혼합상태 도면
도 17 내지 도 18은 본 발명에 의해 사면이 보강된 상태를 나타낸 도면1 is a flow chart of the present invention.
2 is a view for stabilizing the slope of the present invention
Figure 3 is a cross-sectional view of an embodiment of the present invention,
4 is a view showing the bubble of the present invention
5 to 6 are views showing a mixing part of the present invention
FIGS. 7 to 12 show slump photographs of the conventional concrete, high-performance concrete, and shorting concrete according to the present invention.
Figs. 13 to 15 are diagrams showing the shortening process of the present invention
Fig. 16 is a graph showing the relationship between coloring materials
17 to 18 are views showing a state in which slopes are reinforced by the present invention

이하, 첨부된 도면에 의거하여 본 발명을 상세히 설명한다. 도 1은 본 발명의 흐름도이다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings. 1 is a flow chart of the present invention.

본 발명 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법은,The present invention provides a combined slope reinforcement method using a high-performance shotcrete and a reinforcing member,

내층부(200)를 형성하기 전, 사면(100)을 보강부재(20)로 안정화하는 단계와;Stabilizing the slope (100) with the stiffening member (20) before forming the inner layer portion (200);

물, 시멘트, 골재를 일정비율로 배합하여 압축강도가 21~30MPa의 보통콘크리트를 생산 및 현장 이송하는 단계와;Water, cement and aggregate at a predetermined ratio to produce and transport the ordinary concrete having a compressive strength of 21 to 30 MPa;

상기 보통콘크리트에 기포 및 저급 혼합재료를 혼합부(60)로 혼합하여 형성된 보통강도 콘크리트가 숏팅안내부재(70)를 통해 사면(100)으로 배출되어 외층부(300)보다 두꺼운 두께로 내층부(200)를 형성하는 단계와;The normal strength concrete formed by mixing the bubbles and the low-grade mixed material in the mixer 60 with the ordinary concrete is discharged to the slope 100 through the shorting guide member 70 to be formed into a thicker layer than the outer layer portion 300 200) < / RTI >

상기 보통콘크리트에 기포 및 고급 혼합재료를 혼합부(60)로 혼합하여 형성된 고성능 콘크리트가 숏팅안내부재(70)를 통해 내층부(200) 상면으로 내층부(200)의 두께보다 얇은 두께로 배출되어 외층부(300)를 형성하는 단계와;The high performance concrete formed by mixing the bare cell and the high-grade mixed material with the mixer 60 is discharged through the shorting guide member 70 to a thickness smaller than the thickness of the innerlayer 200 on the upper surface of the innerlayer 200 Forming an outer layer portion (300);

상기 보통콘크리트에 기포 및 착색재료를 혼합부(60)로 혼합하여 형성된 칼라 콘크리트가 숏팅안내부재(70)를 통해 외층부(300) 상면으로 배출되어 표층부(400)를 형성하는 단계와;Forming a surface layer (400) by discharging the color concrete formed by mixing bubbles and a coloring material in the mixer (60) with the ordinary concrete to the upper surface of the outer layer section (300) through the shorting guide member (70);

상기 숏팅안내부재(70)로 각 콘크리트가 배출될 때, 5기압 이상의 고압의 공기를 뿜어 각 콘크리트에 포함된 기포를 소산시키면서 슬럼프가 감소되도록 하는 것이다.
When the concrete is discharged by the shorting guide member 70, air having a pressure higher than 5 atmospheres is blown to dissipate the bubbles contained in the concrete, thereby reducing the slump.

다음은 상기와 같이 구성된 본 발명의 시공과정을 설명한다.Hereinafter, a construction process of the present invention will be described.

먼저, 도 2에 도시된 바와 같이, 사면(100)의 상태를 고려하여 사면(100)을 보강부재(20)로 보강하고, 이 보강부재(20)를 수용하여 부착성 및 결속력을 높이도록 사면(100)에 철근 및 와이어메쉬를 설치하는데, 상기 보강부재(20)는 어스앵커, 쏘일네일, 락볼트 중 어느 하나임이 바람직하다.2, the slope 100 is reinforced by the reinforcing member 20 in consideration of the condition of the slope 100, and the reinforcing member 20 is received in the slope 100, The reinforcement member 20 is preferably made of an earth anchor, a soil nail, or a rock bolt.

상기 어스앵커(Earth Anchor)는 구조물을 지반에 정착시키기 위하여 고강도의 강재로 연결하고 높은 긴장력을 도입하여 구조물에 횡방향의 구속력을 가하기 위한 것으로, 지반과 구조물을 하나의 집합체로 묶는 효과를 발휘하며, 강선과 시멘트, 그라우트로 구성된다.The Earth Anchor is to connect the structure with a high-strength steel to fix it on the ground and to apply a high tensional force to the structure so as to bind the structure in the transverse direction. The earth anchor exhibits an effect of tying the ground and the structure into one aggregate , Steel wire, cement, and grout.

상기 쏘일네일(Soil Nailing)은, 굴착면에 대한 원위치 보강공법으로 Nail 이라 불리우는 인장응력, 전단응력 및 휨모멘트에 저항할 수 있는 보강부재(20)를 프리스트레싱 없이 비교적 좁은 간격으로 삽입한 후, 유연한 전면판을 설치하여 원지반의 전체적인 전단강도 증대 및 발생변위를 가능한 억제하고 굴착공사 도중 및 완료 후에 예상되는 이완을 억제하는 공법이다.The Soil Nailing is a method of inserting a reinforcing member 20 capable of resisting a tensile stress, a shear stress and a bending moment called Nail at a relatively narrow interval without prestressing by an in-situ reinforcing method on the excavation surface, The front plate is installed to increase the overall shear strength of the paperboard as much as possible and to suppress the occurrence of displacement, and to suppress the expected relaxation during and after excavation work.

상기 락볼트(Rock Bolt)는 암반이 본래 가지고 있는 강도를 유지시키는데 목적이 있으며, 그 주요역할은 절취된 암반 노출면에 잔존해 있으면서 낙하 혹은 활동을 야기시킬 수 있는 부석의 변위억제, 암반의 균열과 절리를 따라 발생하는 활동방지 등의 역할을 한다.The rock bolt is intended to maintain the original strength of the rock, and its main role is to suppress the displacement of the pumice which may remain on the exposed surface of the rock and cause the fall or activity, And prevention of activities that occur along the joints.

또한, 도 3에 도시된 바와 같이, 압축강도가 21~30MPa이고, 슬럼프 60~80mm의 보통콘크리트를 형성할 수 있도록 배처플랜트(10)에서 각각 공급되는 물, 시멘트, 골재 등을 일정비율로 배합 및 혼합한 후, 레미콘 트럭(40)에 의해 시공현장으로 이송한다.3, water, cement, aggregate, and the like supplied from the plant 10 are mixed at a predetermined ratio so as to form a normal concrete having a compressive strength of 21 to 30 MPa and a slump of 60 to 80 mm, And mixed, and then transported to the construction site by the remicon truck 40.

여기서 최종 숏크리트의 강도를 위해 물-시멘트 비는 42% 이하로 생산하되, 숏크리트 타설 후, 흘러내림을 방지하기 위하여 슬럼프는 물-시멘트 비로 조정하지 않고, 감수제나 AE제를 사용하여 조정하는 것이 바람직하다.For the strength of the final shotcrete, the water-cement ratio should be less than 42%, but it is preferable to adjust the slump by using the water reducing agent or AE agent without adjusting the water-cement ratio in order to prevent the run- Do.

상기 레미콘 트럭(40)이 현장 이송되면, 레미콘 트럭(40)에 투입된 보통콘크리트는 이송중 슬럼프의 추가 손실로 펌핑성이 나빠 펌핑이 어려워지기 때문에 도 4에 도시된 바와 같이, 발포제 및 기포제 또는 기포발생기로부터 생산된 기포를 상기 레미콘 트럭(40)에 투입한다.When the ready-mixed concrete truck 40 is transported in the field, the ordinary concrete injected into the ready-mixed concrete truck 40 has a poor pumping property due to an additional loss of slump during transportation, which makes pumping difficult. Therefore, Bubbles produced from the generator are introduced into the remicon truck 40.

이때, 상기 레미콘 트럭(40)에 투입되는 기포량은, 보통콘크리트에 체적대비 30%의 기포를 혼입시키기 위해 1㎥의 보통콘크리트에 기포발생기를 약 60초 가동하여 생성된 240ℓ의 기포를 혼입하는 것이 바람직하나, 도 5 내지 도 6에 도시된 바와 같이, 상기 보통콘크리트에 기포를 전체 콘크리트 체적대비 20~40% 정도 추가하여 기포의 볼베어링 효과 및 혼합부(60)의 축(61)에 장착되어 회전하는 다수의 혼합부재(62)에 의해 균일하게 혼합되는 보통강도 콘크리트를 형성하고, 이를 도 7에 도시된 바와 같이, 펌프카(50)로 공급하여 압송관(51)에 착탈가능하게 장착된 숏팅안내부재(70)를 통해 사면(100)으로 배출되도록 한다.At this time, the amount of bubbles to be injected into the ready-mixed concrete truck 40 is such that a bubbler is operated for about 60 seconds in 1 m3 of ordinary concrete to mix 30% of bubbles with the volume of concrete, However, as shown in FIGS. 5 to 6, bubbles are added to the ordinary concrete by about 20 to 40% of the total concrete volume, and the bubbles are mounted on the shaft 61 of the mixing unit 60 As shown in Fig. 7, the concrete strength is uniformly mixed by the plurality of rotating mixing members 62, and is supplied to the pump car 50, And is discharged to the slope 100 through the guide member 70.

여기서, 도 8 내지 도 10에 도시된 바와 같이, 상기 보통강도 콘크리트가 숏팅안내부재(70)로 공급되면, 내부가 관통되면서 입/출구의 직경보다 중앙부의 직경이 작게 형성된 숏팅안내몸체(71)로 공급됨과 동시에 보통강도 콘크리트는 압축되면서 압력이 발생한다.8 to 10, when the ordinary strength concrete is supplied to the shorting guide member 70, a shorting guide body 71 having a diameter smaller than the diameter of the inlet / And the normal strength concrete is compressed and pressure is generated.

또한, 상기 숏팅안내몸체(71)의 중앙부를 경유하여 중앙부의 직경보다 큰 직경의 숏팅안내몸체(71) 출구로 보통강도 콘크리트가 배출될 때, 5기압 이상의 고압의 압축공기가 숏팅안내몸체(71)의 외주면에 방사상으로 경사지게 형성된 공기공급공(72)으로 공급되면서 숏팅안내몸체(71)의 출구로 와류되어 숏팅되는데, 상기 압축공기와 보통강도 콘크리트는 스프레이방식으로 펼쳐짐은 물론 스프레이방식으로 압축공기와 보통강도 콘크리트가 펼쳐질 때, 압축공기와 보통강도 콘크리트가 부딪히면서 보통강도 콘크리트에 포함된 다량의 기포가 소산되도록 하고, 기포의 소산으로 슬럼프가 줄어들어 사면(100)으로 배출되는 보통강도 숏크리트는 도 11 내지 도 12에 도시된 바와 같이, 보통강도 숏크리트가 내층부(200)을 형성하며, 붙임성이 좋음을 알 수 있다.When the ordinary strength concrete is discharged to the exit of the shorting guide body 71 having a diameter larger than the diameter of the center portion through the center of the shorting guide body 71, compressed air of high pressure of 5 atm or higher is discharged from the shorting guide body 71 And is then swirled and shorted to the outlet of the shorting guide body 71. The compressed air and the ordinary strength concrete are spread by the spraying method and sprayed by the compressed air And ordinary strength concrete is spread, a large amount of bubbles contained in the ordinary strength concrete are dispersed due to the collision between the compressed air and the ordinary strength concrete, and the ordinary strength shotcrete discharged from the slope 100 due to the reduction of slump due to the dissipation of bubbles, 12, it can be seen that the ordinary strength shotcrete forms the inner layer portion 200 and is well-adhered.

표 2는 배합강도 27MPa, 슬럼프 70~80mm의 보통콘크리트에 단위체적당 기포를 20%. 27%, 33% 혼입하고, 컴프레샤를 이용해 9기압으로 숏팅 한 실험결과를 보여주고 있다. 도 13 내지 도 15에 도시된 바와 같이, 기포량 20%를 추가할 경우, 슬럼프는 보통콘크리트에서 80mm 이었던 것이 기포혼입 후, 250mm로 증가하였으며, 숏팅 후에는 90mm로 감소하였다. 기포량 20%를 추가할 경우, 6.8kg/㎥의 물이 추가 되었으나, 최종 숏팅 후, 슬럼프가 감소하였는데, 이는 보통강도 콘크리트 숏팅 중 물 분자가 일부분 대기중으로 소산되기 때문이다. 기포량을 27%와 33% 혼입할 경우, 추가 단위수량이 많아 숏팅 후, 최종 슬럼프는 보통콘크리트의 슬럼프보다 크게 되나, 최종 공기량은 보통콘크리트의 공기량이나 추가 혼입공기량과는 상관없이 일정함을 알 수 있다.Table 2 shows that 20% of air bubbles per unit volume are applied to ordinary concrete with a compounding strength of 27 MPa and a slump of 70 to 80 mm. 27% and 33%, respectively, and the experiment results are shown in which the pressure is reduced to 9 atm using a compressor. As shown in FIGS. 13 to 15, when the amount of bubbles is increased by 20%, the slump was increased from 80 mm in the concrete to 250 mm in the case of bubbling, and decreased to 90 mm after the shorting. Adding 20% of bubble volume added 6.8 kg / m3 of water, but after the final shot, the slump decreased because the water molecules were partially dissipated into the atmosphere during normal strength concrete shorting. When the amount of air bubbles is 27% and 33%, the final slump is larger than the slump of the ordinary concrete after the shorting, but the final air amount is constant irrespective of the air amount of the ordinary concrete or the amount of additional mixed air .

또한, 상기와 같이 체적대비 20~33%의 기포 혼입으로 슬럼프가 커진 보통강도 콘크리트는 펌핑성이 좋아 용이하게 숏팅할 수 있을 뿐만 아니라 기포만을 혼입하고 숏팅할 경우 최종 슬럼프가 90~150mm 로 너무 커서 대상 사면에 숏팅할 경우, 붙어 있지 않고 흘러내리게 된다. 따라서 가격이 저렴하면서 혼입 시 점성을 지니는 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료를 분말형태로 슬럼프가 커진 보통강도 콘크리트에 추가 혼입하여 물-결합재비를 낮추어 숏팅 후, 최종 슬럼프를 줄임으로써 붙임성을 증대시킬 수 있는 것이다.In addition, as described above, the ordinary strength concrete having a large slump due to the mixing of bubbles of 20 to 33% by volume has a good pumping property and can not only be easily shortened, but also has a final slump of 90 to 150 mm When the shot is shot on the target slope, it is not attached but flows down. Therefore, it is necessary to add a low-grade mixed material containing either fly ash or slag fine powder having low viscosity and viscosity at the time of incorporation or fly ash or slag fine powder into powdered slag normal strength concrete to lower the water- After shortening, the final slump can be reduced to increase the fuzziness.

기포혼입량에 따른 슬럼프와 공기량 변화Change of slump and air volume according to bubble content 기포혼입량Bubble content 슬럼프(mm)Slump (mm) 공기량(%)Air volume (%) 기포량Bubble volume 추가단위수량
(kg/㎥)Additional unit quantity
(kg / m3) 보통
콘크리트usually
concrete 기포
혼입 후bubble
After incorporation 숏팅 후After the shorting 보통
콘크리트usually
concrete 기포
혼입 후bubble
After incorporation 숏팅 후After the shorting 20%20% 6.86.8 8080 250250 9090 77 2020 66 27%27% 9.19.1 7070 260260 100100 55 2727 77 33%33% 18.118.1 7070 275275 150150 55 3333 77

즉, 상기 보통콘크리트에 기포 및 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료를 혼입하여 펌핑성을 증가시킴은 물론 기포가 혼합된 보통강도 콘크리트는 고압의 압축공기와 부딪히면서 배출되므로 보통강도 콘크리트의 기포를 소산시켜 보통강도 숏크리트의 붙임성 증가 및 내구성을 확보할 수 있으며, 상기 내층부(200)은 배근된 철근을 수용할 수 있도록 사면(100)에 형성되어야 한다.That is, a low-grade mixed material containing air bubbles, fly ash, or slag fine powder mixed with fly ash or slag fine powder is added to the ordinary concrete to increase the pumping property. In addition, the ordinary strength concrete mixed with air bubbles, So that the strength of the ordinary strength shotcrete can be increased and durability can be ensured. The inner layer portion 200 should be formed on the slope 100 so as to accommodate the reinforced reinforced concrete.

여기서, 상기 플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합한 저급 혼합재료는 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 3~30 중량부로 혼합되는 것이 바람직하다.Here, it is preferable that the low-grade mixed material obtained by mixing any one of the fly ash and the slag fine powder or the fly ash or the slag fine powder is mixed in an amount of 3 to 30 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete.

상기의 과정으로 내층부(200)가 형성되면, 현장 이송된 레미콘 트럭(40)에 기포를 전체 콘크리트 체적대비 20~40% 정도 추가하여 기포의 볼베어링 효과 및 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고급 혼합재료를 투입하여 혼합부(60)의 축(61)에 장착되어 회전하는 다수의 혼합부재(62)에 의해 균일하게 혼합되는 고성능 콘크리트를 형성하고, 이를 펌프카(50)에 공급하여 압송관(51)에 착탈가능하게 장착된 숏팅안내부재(70)를 통해 내층부(200) 상면으로 배출되도록 한다.When the inner layer portion 200 is formed through the above process, bubbles are added to the field-transferred ready-mixed concrete truck 40 by about 20 to 40% of the total concrete volume so that the ball bearing effect of the bubbles and the effect of either the silica fume or the meta- High-performance concrete which is uniformly mixed by a plurality of mixing members 62 mounted on a shaft 61 of the mixing unit 60 and rotated is input into a high-performance concrete mixed with fume and meta kaolin, 50 to be discharged to the upper surface of the inner layer portion 200 through the shorting guide member 70 detachably mounted on the pressure feeding pipe 51.

여기서, 상기 실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합한 고급 혼합재료는, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 2~20 중량부로 혼합되는 것이 바람직하다. 이는 고급 혼합재료의 각 범위보다 작을 경우, 고강도, 고내구성이 떨어지고, 상기 범위를 초과할 경우, 고강도, 고내구성이 더 높게 나타나지 않으면서 시공원가가 상승하며, 슬럼프를 줄여 붙임성을 증가시키기 때문이다.Here, it is preferable that the high-grade mixed material obtained by mixing either silica fume or metakaolin or silica fume with meta kaolin is mixed in an amount of 2 to 20 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete. If it is smaller than the range of the high-grade mixed material, high strength and high durability are deteriorated. If it exceeds the above range, high strength and high durability do not appear higher, and the construction cost is increased and the slump is reduced .

상기 고성능 콘크리트가 숏팅안내부재(70)를 통해 내층부(200) 상면으로 배출될 때, 내부가 관통되면서 입/출구의 직경보다 중앙부의 직경이 작게 형성된 숏팅안내몸체(71)로 공급되어 고성능 콘크리트는 압축되면서 압력이 발생하고, 상기 숏팅안내몸체(71)의 중앙부를 경유하여 중앙부의 직경보다 큰 직경의 숏팅안내몸체(71) 출구로 고성능 콘크리트가 배출될 때, 5기압 이상의 고압의 압축공기가 숏팅안내몸체(71)의 외주면에 방사상으로 경사지게 형성된 공기공급공(72)으로 공급되면서 숏팅안내몸체(71)의 출구로 와류되어 숏팅되도록 한다.When the high performance concrete is discharged to the upper surface of the inner layer portion 200 through the shorting guide member 70, the high performance concrete is supplied to the shorting guide body 71 having a diameter smaller than the diameter of the inlet / Pressure high-pressure compressed air of 5 atm or more is discharged from the outlet of the shorting guide body 71 having a diameter larger than the diameter of the center portion through the center of the shorting guide body 71 Is supplied to the outer circumferential surface of the shorting guide body (71) through an air supply hole (72) formed radially and inclined to the outlet of the shorting guide body (71).

이때, 상기 압축공기와 고성능 콘크리트는 스프레이방식으로 펼쳐짐은 물론 스프레이방식으로 압축공기와 고성능 콘크리트가 펼쳐질 때, 압축공기와 고성능 콘크리트가 부딪히면서 고성능 콘크리트에 포함된 다량의 기포가 소산되도록 하고, 기포의 소산으로 슬럼프가 줄어들어 사면(100)으로 배출되는 고성능 숏크리트가 외층부(300)을 형성하는데, 상기 외층부(300)는 내층부(200)의 두께보다 얇게 형성하여도 고성능 콘크리트로 타설한 구조물과 동일한 고강도 및 고내구성을 확보할 수 있으므로, 사면(100) 전체를 고성능 콘크리트로 타설할 때보다 시공원가를 줄여 경제성을 확보할 수 있는 것이다.At this time, the compressed air and the high-performance concrete are spread by the spraying method, and when the compressed air and the high-performance concrete are unfolded by the spraying method, the compressed air and the high-performance concrete collide so that a large amount of bubbles contained in the high- A high performance shotcrete discharged to the slope 100 forms an outer layer portion 300. The outer layer portion 300 is formed to have the same thickness as that of the structure poured with high performance concrete even if it is thinner than the thickness of the inner layer portion 200 High strength and high durability can be ensured, so that it is possible to secure economical efficiency by reducing the construction cost as compared with the case where the entire slope 100 is laid with high performance concrete.

표 3은 배합강도 27MPa, 슬럼프 70~80mm의 보통콘크리트에 단위체적당 기포를 27% 혼입하여 실험한 결과를 보여주고 있다. 슬럼프는 보통콘크리트에서 70mm 이었던 것이 기포혼입 후, 260mm로 증가하였으며, 실리카퓸 분말을 시멘트 대비 8% 추가한 후 150mm로 감소하였으며, 숏팅 후에는 제로 슬럼프의 고성능 콘크리트가 되었다. 공기량은 보통콘크리트에서 5%이었던 것이, 기포혼입 후 27%로 증가하였으며, 실리카퓸 분말 추가한 후, 21%로 감소하고, 숏팅 후에는 5%로 됨을 알 수 있다.Table 3 shows the results of mixing 27% of air bubbles per unit volume in a concrete with a compounding strength of 27 MPa and a slump of 70 to 80 mm. The slump was increased from 70mm in concrete to 260mm after mixing with air bubbles. The silica fume powder was reduced to 150mm after adding 8% of cement, and became a zero-slump high-performance concrete after shortening. The amount of air was increased from 27% after mixing with air bubbles to 5% in concrete, to 21% after adding silica fume powder, and to 5% after shorting.

상기와 같이 체적대비 27%의 기포혼입으로 슬럼프가 커진 보통콘크리트에 분말형태의 실리카퓸을 추가로 투입하여 고성능 콘크리트를 형성하고, 분말의 실리카퓸 첨가로 물-결합재 비를 줄여 붙임성이 좋은 고성능 콘크리트를 형성하고, 이를 숏팅하여 고성능 숏크리트를 얻을 수 있는 것이다.As described above, the high-performance concrete is formed by addition of powdery silica fume to the ordinary concrete having a large slump by the mixing of the foam with 27% of the volume, and the water-binder ratio is reduced by adding the silica fume of the powder. And a high-performance shotcrete can be obtained by shorting the shotcrete.

기포와 실리카퓸을 혼입하고 숏팅한 결과Result of mixing bubble and silica fume and shorting 항목Item 보통콘크리트Plain concrete 기포 27% 혼입 후Bubbles 27% After mixing 실리카퓸 혼입 후After incorporation of silica fume 숏팅 후After the shorting 슬럼프(mm)Slump (mm) 7070 260260 150150 00 공기량(%)Air volume (%) 55 2727 2121 55

상기의 과정으로 외층부(300)가 형성되면, 현장 이송된 레미콘 트럭(40)에 기포를 전체 콘크리트 체적대비 20~40% 정도 추가하여 기포의 볼베어링 효과 및 산화철, 카본블랙의 착색재료를 투입하여 혼합부(60)의 축(61)에 장착되어 회전하는 다수의 혼합부재(62)에 의해 균일하게 혼합되는 칼라 콘크리트를 형성하고, 이를 펌프카(50)로 공급하여 압송관(51)에 착탈가능하게 장착된 숏팅안내부재(70)를 통해 외층부(300) 상면으로 배출되도록 한다.When the outer layer part 300 is formed by the above process, air bubbles of the bubbles and the coloring materials of iron oxide and carbon black are added to the ready-mixed remicon truck 40 by adding about 20 to 40% The color concrete which is uniformly mixed by the plurality of mixing members 62 mounted on the shaft 61 of the mixing section 60 and is rotated is supplied to the pump car 50 and is detachably attached to the transfer tube 51 And is discharged to the upper surface of the outer layer portion 300 through the shorting guide member 70 mounted to the outer layer portion 300.

여기서 상기 착색재료의 산화철 및 카본블랙은, 도 16에 도시된 바와 같이, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 1~8 중량부로 혼합하는데, 이는 안료의 종류에 따라 5~8%에서 발색의 포화점에 도달하게 되고, 1~3% 사이에서 발색 농도가 급격히 상승하기 때문이다. 상기 안료의 입경은 시멘트보다 작기 때문에 안료의 혼합에 의해 콘크리트의 수량을 증가시키게 되고, 결국 물-시멘트비가 커져서 강도가 저하하는 경향이 일반적이지만, 시멘트의 5~6% 정도까지는 콘크리트가 굳기 전후의 물성에 미치는 영향은 거의 없으므로 색상의 포화도가 5~8% 인점으로 볼 때, 경제성의 측면에서도 8% 이상 첨가하지 않는 것이 바람직하다.As shown in FIG. 16, the iron oxide and carbon black of the coloring material are mixed in an amount of 1 to 8 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete, The saturation point of color development is reached, and the color density increases sharply between 1 and 3%. Since the particle diameter of the pigment is smaller than that of the cement, the amount of the concrete is increased by the mixing of the pigments. As a result, the water-cement ratio is increased and the strength tends to decrease. However, until 5 ~ 6% of the cement, It is preferable not to add more than 8% from the viewpoint of economical efficiency in view of the saturation degree of color of 5 to 8%.

상기 칼라 콘크리트가 숏팅안내부재(70)를 통해 외층부(300) 상면으로 배출될 때, 내부가 관통되면서 입/출구의 직경보다 중앙부의 직경이 작게 형성된 숏팅안내몸체(71)로 공급되어 칼라 콘크리트는 압축되면서 압력이 발생하고, 상기 숏팅안내몸체(71)의 중앙부를 경유하여 중앙부의 직경보다 큰 직경의 숏팅안내몸체(71) 출구로 칼라 콘크리트가 배출될 때, 5기압 이상의 고압의 압축공기가 숏팅안내몸체(71)의 외주면에 방사상으로 경사지게 형성된 공기공급공(72)으로 공급되면서 숏팅안내몸체(71)의 출구로 와류되어 숏팅되도록 한다.When the color concrete is discharged to the upper surface of the outer layer portion 300 through the shorting guide member 70, the interior of the color concrete is supplied to the shorting guide body 71 having a diameter smaller than the diameter of the inlet / Pressure compressed air having a pressure higher than 5 atmospheres is discharged through the center of the shorting guide body 71 to the outlet of the shorting guide body 71 having a diameter larger than the diameter of the center portion Is supplied to the outer circumferential surface of the shorting guide body (71) through an air supply hole (72) formed radially and inclined to the outlet of the shorting guide body (71).

이때, 상기 압축공기와 칼라 콘크리트는 스프레이방식으로 펼쳐짐은 물론 스프레이방식으로 압축공기와 칼라 콘크리트가 펼쳐질 때, 압축공기와 칼라 콘크리트가 부딪히면서 칼라 콘크리트에 포함된 다량의 기포가 소산되도록 하고, 기포의 소산으로 슬럼프가 줄어들어 사면(100)으로 배출되는 칼라 숏크리트가 표층부(400)를 형성하는데, 상기 표층부(400)는 외층부(300)의 두께보다 얇게 형성하는 것이 바람직하다.At this time, when the compressed air and the color concrete are unfolded by the spray method as well as the unfolded by the spray method, the compressed air and the color concrete collide with each other, so that a large amount of bubbles contained in the color concrete are dispersed, And the color shotcrete discharged to the slope 100 forms a surface layer portion 400. The surface layer portion 400 is preferably formed to be thinner than the thickness of the outer layer portion 300. [

상기 내층부(200)과 외층부(300) 및 표층부(400)는 내층부(200)가 일반 콘크리트에서 14~28일 동안 양생된 후, 외층부(300)를 형성할 수 있으나, 숏크리트로 쇼팅되기 때문에 내층부(200)이 흘러내리지 않을 경우, 내층부(200)에 외층부(300)을 숏팅하여 형성할 수 있으므로 시공기간을 단축시킬 수 있는 것이다.The inner layer part 200, the outer layer part 300 and the surface layer part 400 can form the outer layer part 300 after the inner layer part 200 is cured for 14 to 28 days in the general concrete, The outer layer portion 300 can be formed by shorting the inner layer portion 200 when the inner layer portion 200 does not flow down. Thus, the construction time can be shortened.

또한, 도 17 내지 도 18에 도시된 바와 같이, 상기의 과정으로 내층부(200)과 외층부(300) 및 표층부(400)가 형성되면, 상기 표층부(400)로 돌출된 보강부재(20)를 고정할 두부(Anchor Head)가 사용되는데, 상기 두부는 보강부재(20)에 발휘되는 높은 하중을 고정하기 위해 필요하며, 일반적으로 쐐기(wedge) 정착구(30)로 정착하여 시공을 마무리하나, 외층부(300)를 형성한 후, 보강부재(20)를 정착구(30)로 정착한 상태에서 표층부(400)를 형성하여 시공을 마무리할 수도 있는 것이다.17 to 18, when the inner layer portion 200, the outer layer portion 300, and the surface layer portion 400 are formed as described above, the reinforcing member 20 protruding from the surface layer portion 400 is formed, An anchor head is used for fixing the load to the reinforcing member 20. The toe is required to fix a high load exerted on the reinforcing member 20 and is usually fixed with a wedge fixture 30 to finish the construction, After forming the outer layer portion 300, the surface layer portion 400 may be formed in a state where the reinforcing member 20 is fixed to the fixing port 30, thereby completing the construction.

본 발명에서 상기 실시형태는 하나의 예시로서 본 발명이 여기에 한정되는 것은 아니다. 본 발명의 특허청구범위에 기재된 기술적 사상과 실질적으로 동일한 구성을 갖고 동일한 작용효과를 이루는 것은 어떠한 것이라도 본 발명의 기술적 범위에 포함된다 할 것이다.
The present invention is not limited to the above-described embodiments. Anything having substantially the same constitution as the technical idea described in the claims of the present invention and achieving the same operational effect will be included in the technical scope of the present invention.

10: 배처플랜트 20: 보강부재
30: 정착구 40: 레미콘 트럭
50: 펌프카 60: 혼합부
70: 숏팅안내부재 100: 사면
200: 내층부 300: 외층부
400: 표층부10: Rooter plant 20: Reinforcing member
30: Fixing area 40: Remicon truck
50: pump car 60: mixing part
70: a shorting guide member 100:
200: inner layer portion 300: outer layer portion
400:

Claims (11)

물, 시멘트, 골재를 일정비율로 배합하여 압축강도가 21~30MPa의 보통콘크리트를 생산 및 현장 이송하는 단계와;
상기 보통콘크리트에 기포 및 저급 혼합재료를 혼합부로 혼합하여 형성된 보통강도 콘크리트가 숏팅안내부재를 통해 사면으로 배출되어 외층부보다 두꺼운 두께로 내층부를 형성하는 단계와;
상기 보통콘크리트에 기포 및 고급 혼합재료를 혼합부로 혼합하여 형성된 고성능 콘크리트가 숏팅안내부재를 통해 내층부 상면으로 내층부의 두께보다 얇은 두께로 배출되어 외층부를 형성하는 단계와;
상기 보통콘크리트에 기포 및 착색재료를 혼합부로 혼합하여 형성된 칼라 콘크리트가 숏팅안내부재를 통해 외층부 상면으로 배출되어 표층부를 형성하는 단계와;
상기 숏팅안내부재로 각 콘크리트가 배출될 때, 5기압 이상의 고압의 공기를 뿜어 각 콘크리트에 포함된 기포를 소산시키면서 슬럼프가 감소되도록 하는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
Water, cement and aggregate at a predetermined ratio to produce and transport the ordinary concrete having a compressive strength of 21 to 30 MPa;
The ordinary strength concrete formed by mixing the bare cell and the low grade mixed material into the mixed concrete is discharged to the slope through the shorting guide member to form an inner layer with a thickness greater than that of the outer layer;
The high-performance concrete formed by mixing the normal concrete with the bubbles and the high-grade mixed material in the mixing portion is discharged through the shorting guide member to a thickness smaller than the thickness of the inner layer portion to form an outer layer portion;
The color concrete formed by mixing the bare cell and the coloring material into the mixture of the ordinary concrete is discharged to the upper surface of the outer layer through the shorting guide member to form a surface layer;
Characterized in that when the concrete is discharged through the shorting guide member, high pressure air of 5 atm or higher is blown to dissipate the bubbles contained in each concrete to reduce the slump, and the combined slope reinforcement method using the high- .
청구항 1에 있어서, 상기 저급 혼합재료는,
플라이애쉬나 슬래그미분말 중 어느 하나 또는 플라이애쉬나 슬래그미분말을 혼합하는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The method according to claim 1, wherein the low-
Characterized in that either fly ash or slag fine powder or fly ash or slag fine powder is mixed with a high performance shotcrete and a reinforced member.
청구항 2에 있어서,
상기 저급 혼합재료는, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 3~30 중량부로 혼합되는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The method of claim 2,
Wherein the low-grade mixed material is mixed in an amount of 3 to 30 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete, and the composite slope reinforcement method using the high-performance shotcrete and the reinforcing member.
청구항 1에 있어서, 상기 고급 혼합재료는,
실리카퓸과 메타카올린 중 어느 하나 또는 실리카퓸과 메타카올린을 혼합하는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The method of claim 1,
Characterized in that either silica fume or meta kaolin or silica fume and meta kaolin are mixed, and a combined slope reinforcement method using a high performance shotcrete and a reinforcing member.
청구항 4에 있어서,
상기 고급 혼합재료는, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 2~20 중량부로 혼합되는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The method of claim 4,
Characterized in that the high-grade mixed material is mixed in an amount of 2 to 20 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete, and the composite slope reinforcement method using the high-performance shotcrete and the reinforcing member.
청구항 1에 있어서, 상기 착색재료는,
산화철이나 카본블랙 중 어느 하나 또는 산화철이나 카본블랙을 혼합하는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The coloring material according to claim 1,
A composite slope reinforcement method using a high-performance shotcrete and a reinforcing member, characterized in that any one of iron oxide and carbon black or iron oxide or carbon black is mixed.
청구항 6에 있어서,
상기 착색재료는, 상기 보통콘크리트를 형성하는 시멘트 100 중량부 기준으로 1~8 중량부로 혼합되는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The method of claim 6,
Wherein the coloring material is mixed in an amount of 1 to 8 parts by weight based on 100 parts by weight of the cement forming the ordinary concrete, and the composite color slope reinforcement method using the high-performance shotcrete and the reinforcing member.
청구항 1에 있어서, 상기 혼합부는,
상기 보통콘크리트가 투입되는 레미콘 트럭 내부에 모터의 동력으로 회전하는 축과;
상기 축에 적어도 1단 이상 방사상으로 형성되어 축의 회전방향으로 회전하면서 보통콘크리트와 기포, 혼합재료 및 착색재료를 혼합하는 혼합부재를 포함하여 구비되는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
[2] The apparatus according to claim 1,
A shaft for rotating with the power of the motor in the ready-mix truck into which the ordinary concrete is injected;
And a mixing member which is formed in at least one or more stages radially on the shaft and rotates in a rotating direction of the shaft, and mixes ordinary concrete with bubbles, a mixed material and a coloring material. Slope reinforcement method.
청구항 1에 있어서, 상기 숏팅안내부재는,
상기 보통강도 콘크리트와 고성능 콘크리트 및 칼라 콘크리트가 유입 및 압축되어 배출되도록 내부가 관통되면서 각 콘크리트가 유입/배출되는 입/출구의 직경보다 중앙부의 직경이 작게 형성되는 숏팅안내몸체와;
상기 숏팅안내몸체로 유입되는 각 콘크리트에 포함된 기포를 소산시키면서 공기량을 감소시키도록 5기압 이상의 고압의 공기를 공급하도록 숏팅안내부재에 관통된 공기공급공을 포함하여 구비되는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
[2] The apparatus according to claim 1,
The concrete structure of the present invention is characterized in that the interior of the concrete structure is formed with a diameter smaller than the diameter of the inlet / outlet of the concrete.
And an air supply hole penetrating the shorting guide member to supply high-pressure air of 5 atm or higher to reduce the amount of air while dissipating bubbles contained in each concrete introduced into the shorting guide body. And a reinforced member.
청구항 9에 있어서, 상기 공기공급공은,
상기 숏팅안내몸체의 외주면에 방사상으로 경사지게 형성되는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.
The air conditioner according to claim 9,
Wherein the fastening guide body is sloped radially on an outer circumferential surface of the shorting guide body.
청구항 1에 있어서,
상기 보강부재를 정착구로 정착하는 단계를 더 포함하여 이루어지는 것을 특징으로 하는 고성능 숏크리트와 보강부재를 이용한 합체식 사면 보강방법.The method according to claim 1,
Further comprising the step of fixing the reinforcing member to a fixation member. The method of claim 1, wherein the reinforcing member is formed of a high-performance shotcrete.
KR1020130159102A 2013-12-19 2013-12-19 Slope reinforcement methode for using thr high performance shotcrete and reinforcement KR101415891B1 (en)