KR101345355B1 - Pattern formed architectural cement finish plates and method of manufacture - Google Patents

Pattern formed architectural cement finish plates and method of manufacture Download PDF

Info

Publication number
KR101345355B1
KR101345355B1 KR1020120100537A KR20120100537A KR101345355B1 KR 101345355 B1 KR101345355 B1 KR 101345355B1 KR 1020120100537 A KR1020120100537 A KR 1020120100537A KR 20120100537 A KR20120100537 A KR 20120100537A KR 101345355 B1 KR101345355 B1 KR 101345355B1
Authority
KR
South Korea
Prior art keywords
cement
bottom frame
manufacturing
filling
mold
Prior art date
Application number
KR1020120100537A
Other languages
Korean (ko)
Inventor
김종석
Original Assignee
김종석
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김종석 filed Critical 김종석
Priority to KR1020120100537A priority Critical patent/KR101345355B1/en
Application granted granted Critical
Publication of KR101345355B1 publication Critical patent/KR101345355B1/en

Abstract

The present invention relates to a manufacturing method of a finishing board for construction with patterns, wherein the method possibly forms three-dimensional and natural patterns in a simple manner by forming multi-layered wooden patterns with different textures and colors by filling the groove of a molding frame with cement and mortar and apply transparent resins on the outer cover of the cured finishing board after fixing natural materials including leaves or petals. [Reference numerals] (S10) Preparing a molding frame; (S20) Manufacturing a floor frame; (S30) Fixing the floor frame; (S40) Coating a release agent; (S50) Filling cement; (S60) Discharging the cement; (S70) Filling mortar; (S80) Separating the molding frame

Description

무늬가 형성된 건축용 마감판재 및 그 제조방법{Pattern formed architectural cement finish plates and method of manufacture}Patterned architectural cement finish plates and method of manufacture

본 발명은 무늬가 형성된 건축용 마감판재 및 그 제조방법에 관한 것으로서, 보다 상세하게는 성형틀의 요부에 시멘트를 충진하고 모르타르 풀을 채움으로써 목재의 무늬가 재질과 색감이 다른 복수층으로 형성되어 입체적이고 자연스러운 무늬를 용이하게 형성할 수 있으며, 나뭇잎 또는 꽃잎의 자연소재를 늘어놓아 고정하고 함께 양생된 마감판재의 외피에 투명한 수지재를 도포하여 이루어지는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재와 그 제조방법에 관한 것이다.
The present invention relates to a patterned building finishing plate and a method of manufacturing the same, and more specifically, by filling the mortar paste with cement and filling the recess of the molding frame, the pattern of the wood is formed of a plurality of layers different in material and color to be three-dimensional It is possible to form a natural and natural pattern easily, the patterned building finishing plate material and its manufacture, characterized in that the transparent resin material is applied to the outer surface of the cured finishing board material by lining and fixing the natural material of leaves or petals It is about a method.

일반적으로 콘크리트 건축물은 거푸집을 지어서 그 내부에 콘크리트를 타설한 후 양생하여 건축물의 골격을 형성한 다음에 콘크리트 외벽을 벽지, 나무판, 페인트 등의 마감 처리하여 미적으로 보기 좋게 처리한다.In general, concrete buildings are made of formwork, and concrete is poured into them to cure and form the skeleton of the building, and then the exterior walls of the concrete are treated with aesthetic finish by finishing with wallpaper, wooden boards, and paint.

그러나 최근에 건축 자재비, 인건비 등의 상승으로 콘크리트 건물의 내벽이나 외벽에 나무, 벽지, 페인트 등의 마감재를 덮지 않고 콘크리트 그 자체를 노출시켜서 콘크리트 질감을 느낄 수 있게 하는 건축마감양식이 사용되고 있다.Recently, however, building finishing styles have been used to expose concrete itself without covering finishes such as wood, wallpaper and paint on the inner and outer walls of concrete buildings due to rising building materials and labor costs.

이와 같은 마감양식은 건축비를 절감하고 노출된 콘크리트의 질감은 거푸집의 이음새나 거푸집의 표면이 그대로 전사된 무늬나 질감이 표현되므로 색다른 미적 표현이 가능하였다.Such finishing styles reduce construction costs and the exposed concrete texture can be expressed in different aesthetics because the pattern or texture of the seam of the formwork or the surface of the formwork is transferred as it is.

콘크리트 외벽의 마감재로는 인간 친화적인 목재 마감재가 가장 바람직하나 나무자원의 고갈로 목재값이 매우 비싸므로 일반적으로 비용 때문에 사용하기 곤란하였다.As the finish of the concrete exterior wall is a human-friendly wood finish is most preferred, but because of the depletion of wood resources, the price of wood is very expensive, it is generally difficult to use because of the cost.

따라서 최근에는 목재 이외의 인조 대리석, 플라스틱 등의 마감재가 연구 개발되어 시판되고 있다.Therefore, in recent years, finishing materials such as artificial marble, plastics, etc. other than wood have been researched and marketed.

그러나 인조 대리석은 목재 질감을 가진 마감재의 개발이 곤란하고 플라스틱 마감재는 나무결 무늬 형태나 입체감 또는 색감 등을 표현할 수 있으나 아직까지는 천연그대로의 자연스러운 나무결 입체질감을 표현하지 못하고 있다.
선행기술: 공개특허공보 제10-2009-0103433호However, the artificial marble is difficult to develop a finish with a wood texture, plastic finish can express the shape of the wood grain pattern, three-dimensional or color, but so far it does not express the natural wood grain texture as it is.
Prior Art: Publication No. 10-2009-0103433

따라서, 본 발명은 상기한 바와 같은 종래 기술의 문제점을 해결하고자 안출된 것으로서, 본 발명의 목적은 인공적인 느낌을 배제하고 자연스럽게 실제 목재를 모사하면서도 용이하게 성형 및 생산가능한 무늬가 형성된 건축용 마감판재 및 제조방법을 제공하는데 있다.
Accordingly, the present invention has been made to solve the problems of the prior art as described above, the object of the present invention is to remove the artificial feeling and to naturally form the actual wood, while the building finish plate formed with a pattern that can be easily molded and produced and It is to provide a manufacturing method.

상기한 바와 같은 목적을 달성하기 위하여, 성형틀을 바닥면과 측벽이 구비되도록 형성하여 준비하는 성형틀 준비단계와; 표면에 입체적으로 요철이 구비되어 무늬가 형성된 바닥틀을 제작하는 바닥틀 제작단계와; 상기 바닥틀을 요철이 상부를 향하도록 성형틀의 바닥면에 안착하여 고정하는 바닥틀 고정단계와; 상기 성형틀과 바닥틀의 내측 표면에 박리제를 도포하는 박리제 도포단계와; 상기 성형틀 내부의 요철이 형성된 바닥틀 상부에 시멘트를 충진하는 시멘트 충진단계와; 상기 바닥틀의 요철 내부에 충진된 시멘트가 남아있도록 바닥틀의 상부에 충진된 시멘트를 긁어서 배출하는 시멘트 배출단계와; 상기 요철에 시멘트가 남아있는 바닥틀 상부에 모르타르를 채우는 모르타르 충진단계와; 상기 성형틀과 바닥틀을 분리하는 단계;를 포함하여 이루어지는 무늬가 형성된 건축용 마감판재의 제조방법에 있어서,
상기 시멘트 충진단계와 시멘트 배출단계는, 상기 성형틀 내부의 요철이 형성된 바닥틀 상부에 시멘트를 충진한 후, 탄력성이 있는 주걱을 사용하여 시멘트를 긁어서 요철의 일부에는 시멘트가 남겨지고 다른 부분의 시멘트만 배출하도록 하고, 상기 요철에 남겨진 시멘트가 소정 시간 동안 양생된 후 상기 바닥틀 상부에 상기 요철의 일부에 남겨진 시멘트와는 상이한 색상을 갖는 시멘트를 충진한 후 주걱으로 상기 상이한 색상을 갖는 시멘트를 긁어 배출함으로써, 표면에 서로 다른 색상을 갖는 시멘트로 이루어진 무늬가 형성되도록 하는 것을 특징으로 한다.In order to achieve the object as described above, forming the mold to prepare the mold to be provided with a bottom surface and side walls; A bottom frame manufacturing step of manufacturing a bottom frame having a pattern formed by irregularities on a surface thereof; A bottom frame fixing step of fixing the bottom frame to the bottom surface of the mold so that the unevenness faces upward; A release agent applying step of applying a release agent to the inner surfaces of the mold and the bottom frame; A cement filling step of filling cement in the upper part of the mold having the unevenness inside the mold; A cement discharging step of scraping and discharging the cement filled in the upper part of the frame so that the cement filled in the concavities and convexities remains in the bottom frame; A mortar filling step of filling mortar on an upper portion of the bottom frame in which cement is left in the unevenness; In the manufacturing method of the patterned building finishing plate comprising a; forming the mold and the bottom frame;
In the cement filling step and the cement discharging step, after filling the cement in the upper part of the bottom frame formed with the irregularities inside the mold, scraping the cement using an elastic spatula, the cement remains in part of the unevenness and the cement of the other part Only the cement left in the unevenness is cured for a predetermined time, and after filling the cement having a color different from that left in some of the unevenness in the upper part of the bottom frame, scraping the cement having the different color with a spatula. By discharging, it is characterized in that to form a pattern made of cement having a different color on the surface.

또한, 상기 바닥틀 제작단계는, 생나무 판재를 준비하는 생나무판재 준비단계와, 준비된 생나무 판재의 표면을 태우는 탄화단계와, 상기 생나무 판재의 표면에 나무결 무늬를 입체적으로 형성하도록 탄화된 연질부를 제거하는 단계로 이루어지는 것이 바람직하다.
또한, 상기 탄력성이 있는 주걱은 단부에 톱니형상이 형성되어 있는 것을 사용하는 것을 특징으로 한다.In addition, the bottom frame manufacturing step, the step of preparing the green bark board, the carbonizing step of burning the surface of the prepared raw wood board, and removing the soft portion carbonized to form three-dimensional wood grain pattern on the surface of the raw wood board It is preferably made up of steps.
In addition, the elastic spatula is characterized in that it is used that the tooth shape is formed at the end.

삭제delete

또한, 상기 시멘트 충진단계 내지 모르타르 충진단계 중 적어도 어느 한 단계에서 상기 성형틀을 진동시키고 상부에서 압착시키는 것이 바람직하다.In addition, in at least one of the cement filling step to the mortar filling step, it is preferable to vibrate the mold and press the upper mold.

또한, 상기 바닥틀 제작단계는, 생나무 판재를 준비하는 생나무판재 준비단계와, 준비된 생나무 판재의 상부에 나뭇잎 또는 꽃잎의 자연소재를 늘어놓아 고정하는 자연소재 고정단계로 이루어지는 것이 바람직하다.In addition, the bottom frame manufacturing step, it is preferable that the natural wood plate preparation step for preparing the raw wood plate, and the natural material fixing step of fixing the natural material of the leaves or petals arranged on top of the prepared raw wood plate.

또한, 상기 성형틀 분리단계 이후에, 양생된 마감판재의 외피에 투명한 합성수지재를 도포하여 굳히는 합성수지재 도포단계를 더 포함하여 이루어지는 것이 바람직하다.In addition, after the molding die separation step, it is preferable to further comprise a synthetic resin coating step of applying a solid synthetic resin material to the outer surface of the cured finish plate material to solidify.

본 발명에 의하면, 현대적인 건축 재료인 모르타르콘크리트를 사용하여 한옥 등에 이용될 수 있는 인조 목재를 용이하게 생산할 수 있게 되는 효과가 있다. 뿐만 아니라 본 발명에 의하면, 목재의 무늬를 입체적으로 형성함에 있어서, 일반적인 회색 모르타르콘크리트를 사용하는 대신 색첨가제를 혼합하여 복수의 층으로 구비함으로써 재료 자체가 목재 색깔을 띠도록 함으로써, 완성된 인조 목재의 겉에 페인트 등으로 도색할 필요가 없도록 하여 미관상 유리한 효과 및 (시간 등에 따른) 손상 가능성의 최소화 효과를 얻을 수 있도록 해 줄 뿐만 아니라, 공정 단계를 한 단계 줄임으로써 생산성을 높일 수 있는 효과가 있다.According to the present invention, there is an effect that can easily produce artificial wood that can be used in hanok using mortar concrete, which is a modern building material. In addition, according to the present invention, in forming the pattern of the wood three-dimensionally, instead of using a general gray mortar concrete, by mixing the color additives to be provided in a plurality of layers, the material itself has a wood color, the finished artificial wood Not only does it need to be painted with paint on the outside, it not only helps to obtain aesthetically beneficial effects and minimizes the possibility of damage (over time), but also increases productivity by reducing the process step by one step. .

또한 종래의 인조 목재의 경우 시간이 흐르면 페인트 도색이 벗겨지는 문제점을 원천적으로 배제할 수 있게 되는 효과가 있다. 더불어 이와 같이 벗겨져 나온 도색 재료가 주변 환경에 누적되는 문제 또한 원천적으로 배제할 수 있어, 이에 따라 종래의 인조 목재에 비해 높은 친환경성을 갖게 되는 효과 또한 있다.In addition, in the case of the conventional artificial wood has the effect that can be ruled out the problem that the paint paint peels off over time. In addition, the problem that the peeled off paint material accumulates in the surrounding environment can also be ruled out at the source. Thus, there is also an effect of having high environmental friendliness compared to conventional artificial wood.

또한 준비된 생내무 판재의 상부에 나뭇잎 또는 꽃잎의 자연소재를 늘어놓아 고정하여 마감판재의 표면에 자연소재가 드러날 수 있도록 형성함으로써 인공적인 느낌을 배제한 자연스러운 느낌을 최대한 가질 수 있도록 함으로써 미관상 크게 유리한 효과가 있으며, 양생된 마감판재의 외피에 투명한 수지재를 도포하여 굳히는 과정을 통해 마감판재의 표면이 노후되는 것을 방지하고 더욱 견고하게 제작될 수 있도록 하는 효과가 있다.
In addition, by placing a natural material of leaves or petals on the top of the prepared inner sheet to fix the natural material on the surface of the finishing board, it can have a natural feeling without the artificial feeling as much as possible. In addition, it is effective to prevent the surface of the finish plate from aging and to make it more robust through the process of applying a transparent resin material to the shell of the cured finish plate to harden.

도 1은 본 발명에 따른 마감판재 제조방법의 단계를 나타낸 흐름도
도 2는 본 발명에 따른 바닥틀 제작과정의 단계를 나타낸 흐름도
도 3은 본 발명의 바닥틀 제작단계를 나타낸 상태도
도 4는 본 발명의 바닥틀 고정단계를 나타낸 상태도
도 5는 본 발명의 시멘트를 긁어 배출하는 단계를 나타낸 상태도
도 6은 본 발명에 따른 충진된 시멘트의 상부를 긁어 배출된 상태를 나타낸 종단면도
도 7은 도 6의 a부분을 확대한 부분확대도
도 8은 본 발명에 충진된 시멘트의 상부를 긁어 배출되는 과정을 2번 수행한 상태를 나타낸 개략도
도 9는 본 발명의 모르타르 충진단계를 나타낸 상태도
도 10은 본 발명의 제조방법에 따른 무늬가 형성된 건축용 시멘트 마감판재
도 11은 본 발명의 제2실시예에 따른 바닥틀 제작과정의 단계를 나타낸 흐름도
도 12는 본 발명의 제2실시예에 따른 자연소재 고정단계를 나타낸 상태도
도 13은 본 발명의 제2실시예의 제조방법에 따른 무늬가 형성된 건축용 시멘트 마감판재1 is a flow chart showing the steps of the method for manufacturing the finishing plate according to the invention
2 is a flow chart showing the steps of the manufacturing process of the bottom frame according to the present invention.
Figure 3 is a state diagram showing the manufacturing step of the bottom frame of the present invention
Figure 4 is a state diagram showing the bottom frame fixing step of the present invention
Figure 5 is a state diagram showing the step of scraping out the cement of the present invention
Figure 6 is a longitudinal cross-sectional view showing a state in which the scraped off the top of the filled cement according to the invention
7 is an enlarged partial view of a portion a of FIG. 6
8 is a schematic view showing a state in which the process of scraping the upper portion of the cement filled in the present invention is performed twice
9 is a state diagram showing the mortar filling step of the present invention
Figure 10 is a construction cement finish plate material is patterned according to the manufacturing method of the present invention
11 is a flowchart showing the steps of the manufacturing process of the bottom frame according to a second embodiment of the present invention.
12 is a state diagram showing a natural material fixing step according to a second embodiment of the present invention
Figure 13 is a construction cement finish plate material patterned according to the manufacturing method of the second embodiment of the present invention

이하, 상기한 바와 같은 구성을 가지는 본 발명에 의한 무늬가 형성된 건축용 시멘트 마감판재 및 제조방법을 첨부된 도면을 참고하여 상세하게 설명한다.
It will be described below in detail with reference to the accompanying drawings, a cement construction plate and a manufacturing method for a patterned building according to the present invention having the configuration as described above.

먼저, 본 발명은 도 1에 도시된 바와 같이, 본 발명은 성형틀(10)을 바닥면과 측벽이 구비되도록 형성하여 준비하는 성형틀 준비단계(S10)와, 표면에 입체적으로 요철(21)이 구비되어 무늬가 형성된 바닥틀(20)을 제작하는 바닥틀 제작단계(S20)와, 상기 바닥틀(20)을 요철(21)이 상부를 향하도록 성형틀의 바닥면에 안착하여 고정하는 바닥틀 고정단계(S30)와, 상기 성형틀과 바닥틀의 내측 표면에 박리제를 도포하는 박리제 도포단계(S40)와, 상기 성형틀 내부로 바닥틀의 요철에 시멘트(30)를 충진하는 시멘트 충진단계(S50)와, 주걱을 이용하여 바닥틀의 상부로 시멘트를 긁어 배출하는 시멘트 배출단계(S60)와, 성형틀 내부의 충진된 시멘트의 상부로 모르타르(40)를 채우는 모르타르 충진단계(S70)와, 성형틀(10)을 분리하는 단계(S80)를 포함하여 이루어지는 것을 특징으로 한다.
First, the present invention, as shown in Figure 1, the present invention is to form and prepare the molding die 10 so that the bottom surface and the side wall is provided with a molding die preparation step (S10) and the surface irregularities 21 in three dimensions Is provided with a bottom frame manufacturing step (S20) for producing a patterned bottom frame 20, the bottom seat 20 is fixed to the bottom surface of the molding frame so that the concave-convex (21) toward the top A mold fixing step (S30), a release agent applying step (S40) for applying a release agent to the inner surface of the mold and the bottom frame, and the cement filling step of filling the cement 30 in the irregularities of the bottom frame into the mold (S50), and the cement discharge step (S60) for scraping the cement to the top of the bottom frame using a spatula, and the mortar filling step (S70) for filling the mortar (40) to the top of the filled cement in the molding frame and , Characterized in that it comprises a step (S80) for separating the molding die 10 .

상기 성형틀 준비단계(S10)는 상부가 개방된 함체의 형상으로 제작하여 바닥면과 측벽이 구비되도록 틀을 형성하여 준비한다.The forming mold preparing step (S10) is prepared in the form of a frame so that the bottom surface and sidewalls are prepared by manufacturing the shape of the upper open housing.

상기 바닥틀 제작단계(S20)는 표면에 입체적으로 요철(21)이 구비되어 무늬가 형성된 바닥틀(20)을 제작한다.The bottom frame manufacturing step (S20) is provided with a concave-convex (21) three-dimensionally on the surface to produce a patterned bottom frame 20.

도 2와 3에 도시된 바와 같이, 상기 바닥틀 제작단계(S20)는, 생나무 판재(1)를 준비하는 생나무판재 준비단계(S21)와, 준비된 생나무 판재의 표면을 태우는 탄화단계(S22)와, 상기 생나무 판재의 표면에 나무결 무늬를 입체적으로 형성하도록 탄화된 연질부를 제거하는 단계(S23)로 이루어지는 것이 바람직하다.As shown in Figures 2 and 3, the bottom frame production step (S20), and preparing the green wood board (1) (S21) and the carbonizing step (S22) to burn the surface of the prepared green wood boards and Preferably, the step of removing the carbonized soft portion (S23) to form a three-dimensional wood grain pattern on the surface of the raw wood plate.

상기 탄화된 연질부 제거단계(S23)는 일반적으로 목재는 목재의 고유의 나이테 부분에 의해 강질부와 연질부로 구성되어 함께 탄화되어도 연질부는 쉽게 제거가 가능하여 브러쉬가 설치된 그라인더를 이용하여 표면을 마찰시켜 탄화된 연질부를 쉽게 분리하는 방법을 사용하며, 압축된 공기를 연마제인 금속가루와 함께 탄화된 목재의 표면에 분사함으로써 연질부를 갈아내는 방법을 사용하여도 무방하다.In the carbonized soft part removing step (S23), generally, the wood is composed of a hard part and a soft part by a unique ring part of wood. It is also possible to use a method of easily separating the carbonized soft part, and to grind the soft part by spraying the compressed air with the abrasive metal powder on the surface of the carbonized wood.

또한, 본 발명에서는 자연스러운 마감판재의 무늬를 얻기 위하여, 소나무 등과 같은 실제 원목 목재를 사용하도록 하고 있으나, 문양이 가공제작된 합성수지 또는 금속재로 형성된 금형을 사용하여도 무방하다.In addition, in the present invention, in order to obtain the pattern of the natural finish plate, the actual wood timber such as pine, etc. are used, but the mold may be formed of a synthetic resin or metal material processed pattern.

또한, 도 4에 도시된 바와 같이, 상기 바닥틀 고정단계(S30)는 요철(21)이 입체적으로 형성된 바닥틀(20)을 요철(21)이 상부를 향하도록 성형틀(10)의 바닥면에 안착하여 고정한다.In addition, as shown in Figure 4, the bottom frame fixing step (S30) is the bottom surface of the mold 10 so that the concave-convex surface 21 is formed three-dimensionally concave-convex 21 facing upwards. Secure it by seating on it.

상기 박리제 도포단계(S40)는 상기 성형틀과 바닥틀의 내측으로 수용되는 시멘트 및 모르타르가 성형틀과 바닥틀의 분리가 용이하도록 성형틀과 바닥틀의 내측 표면에 박리제를 도포한다.The release agent applying step (S40) is to apply the release agent to the inner surface of the mold and the base frame so that the cement and mortar accommodated inside the mold and the base frame to facilitate separation of the mold and the base frame.

도 5 내지 7에 도시된 바와 같이, 상기 시멘트 충진단계(S50)는 상기 성형틀 내부로 바닥틀의 요철에 시멘트(30)를 충진하며, 시멘트 배출단계(S60)는 주걱(2)을 이용하여 바닥틀의 상부로 시멘트를 긁어 배출한다.As shown in Figures 5 to 7, the cement filling step (S50) is filled with the cement 30 to the concavities and convexities of the bottom frame into the mold, the cement discharge step (S60) using a spatula (2) Scrape off the cement with the top of the floor frame.

상기 시멘트(30)는 토목, 건축 재료로 쓰이는 접합제로서 석회석을 가루로 만든 것으로 물과 혼합하여 사용하되, 색상이 혼합된 염료와 함께 사용하는 것이 바람직하다.The cement 30 is used as a binder used in civil engineering and building materials, and made of limestone as a powder, mixed with water, and preferably used with a dye mixed with color.

따라서, 상기 바닥틀(20)의 상부에 형성된 요철(21)의 내부에 시멘트(30)가 충분히 수용될 수 있도록 일정량의 시멘트(30)를 성형틀(10)의 상부에 부어 넣으며, 요철(21)에 수용되고 바닥틀(20)의 상부로 돌출된 잔여 시멘트를 주걱(2)으로 긁어서 배출한다.Therefore, a certain amount of cement 30 is poured into the upper part of the mold 10 so that the cement 30 is sufficiently accommodated in the unevenness 21 formed on the upper part of the bottom mold 20, and the unevenness 21 ) And the remaining cement projected to the top of the bottom frame 20 by scraping with a spatula (2).

이때, 바닥틀(20)의 상부면과 접촉하는 주걱(2)의 재질의 탄성에 따라 돌출된 잔여 시멘트가 제거되는 정도가 결정되며, 비탄력적인 나무로 형성된 주걱을 사용하는 때에는 잔여 시멘트를 배출하고 난 뒤의 상태는 도 7에 도시된 바와 같이 충진된 시멘트(30)의 상부면이 바닥틀(20)의 상부면과 나란하게 일치하게 된다. 그러나 탄력적인 합성수지재의 고무로 형성된 주걱을 사용하여 잔여 시멘트를 배출하고 난 뒤의 상태는 도 8에 도시된 바와 같이 요철(21)의 모서리부에 충진된 시멘트(30a)는 남겨지고 내부의 충진된 시멘트의 일부는 배출되며, 배출되는 시멘트의 정도는 고무로 형성된 주걱과 바닥틀(20)의 접촉되는 힘에 따라 결정된다. 따라서, 모서리부에 충진된 시멘트(30a)가 소정의 시간동안 양생된 후 요철(21)의 내부로 새로운 시멘트(30b)를 충진하고 배출됨으로써, 상기 요철(21)의 내부로 충진되는 시멘트가 서로 다른 색상을 갖는 부분으로 형성되는 것이 가능해진다.At this time, the extent to which the protruding residual cement is removed according to the elasticity of the material of the spatula 2 in contact with the upper surface of the bottom frame 20 is determined, and when using a spatula made of inelastic wood, the remaining cement is discharged As shown in FIG. 7, the upper surface of the filled cement 30 coincides with the upper surface of the bottom frame 20 as shown in FIG. 7. However, after discharging the remaining cement using a spatula formed of rubber of elastic synthetic resin material, as shown in FIG. 8, the cement 30a filled in the corners of the unevenness 21 is left and filled inside. Part of the cement is discharged, and the degree of cement discharged is determined by the contact force between the spatula formed of rubber and the bottom frame 20. Therefore, after the cement 30a filled in the corner portion is cured for a predetermined time, the new cement 30b is filled and discharged into the inside of the unevenness 21 so that the cement filled into the unevenness 21 is mutually different. It is possible to be formed with parts having different colors.

이렇게 색상이 상이한 복수의 시멘트를 구비하여, 첫 번째 색상의 시멘트를 충진하고 배출한 후, 첫 번째 시멘트와는 다른 색상을 갖는 시멘트를 충진하고 배출하는 단계를 적어도 두 번 이상 반복 수행함으로써 다양한 색상의 무늬를 형성하는 것이 바람직하다.By having a plurality of cements of different colors, filling and discharging the cement of the first color, and then filling and discharging the cement having a color different from the first cement at least two or more times. It is preferable to form a pattern.

한편, 주걱(2)을 이용하여 바닥틀(20)의 상부로 시멘트(30)를 긁어 배출하는 시멘트 배출단계(S60)에 있어서, 바닥틀(20)의 상부면과 접촉하는 주걱(2)의 단부의 형상이 평평한 절편의 형상으로 형성되는 것이 바람직하나, 톱니 형상 및 구름 형상으로 형성되거나 바닥틀(20)의 상부면과 접촉하는 주걱(2)의 움직임이 길이방향, 폭방향 및 나선방향 등으로 다양한 방향으로 움직임이 가능함으로써 자연스러운 무늬가 형성되도록 하는 것이 바람직하다.On the other hand, in the cement discharge step (S60) of scraping the cement 30 to the upper portion of the bottom frame 20 by using the spatula 2, of the spatula 2 in contact with the upper surface of the bottom frame 20 It is preferable that the shape of the end portion is formed in the shape of a flat section, but the movement of the spatula 2 formed in the shape of a sawtooth and a cloud or contacting the upper surface of the bottom frame 20 is longitudinal, width and helical. As it is possible to move in various directions, it is desirable to form a natural pattern.

또한, 상기 시멘트 충진단계(S50) 내지 모르타르 충진단계(S70) 중 적어도 어느 한 단계에서 상기 성형틀을 진동시키고 상부에서 압착시키는 것이 바람직하다.In addition, in at least one of the cement filling step (S50) to the mortar filling step (S70) it is preferable to vibrate the molding die and to be pressed from the top.

한편, 도 11 내지 13에서 도시된 바와 같이, 바닥틀 제작단계(S20')는, 생나무 판재를 준비하는 생나무판재 준비단계(S21)와, 준비된 생나무 판재의 상부에 나뭇잎 또는 꽃잎의 자연소재(3)를 늘어놓아 고정하는 자연소재 고정단계(S24)로 이루어지는 것이 바람직하다.On the other hand, as shown in Figures 11 to 13, the bottom frame production step (S20 '), the raw wood plate preparation step (S21) to prepare the green wood plate, and the natural material of the leaves or petals (3) on top of the prepared raw wood plate (3) ) Is preferably made of a natural material fixing step (S24) to line and secure.

상기 자연소재(3)는 은행잎과 같은 가로수 잎이나 강아지풀과 같은 들풀 및 꽃잎 등과 같은 식물소재를 사용함으로써 제작되는 마감판재가 건축물의 외형 또는 내부 벽체에 시공되어 환경친화적인 심미감을 가질 수 있는 효과가 있다.The natural material (3) has the effect that the finishing plate produced by using plant material such as roadside leaves such as ginkgo leaves or wild grass and petals such as dog grass can be installed on the exterior or inner wall of the building to have an environmentally friendly aesthetic effect. have.

한편, 상기 바닥틀 제작단계(S20)에 있어서, 성형틀(10) 내부에 소정의 높이로 시멘트를 충진하고, 상기 시멘트가 반 고체 상태로 양생된 후에 주걱으로 문양을 그려넣듯이 요철을 형성하여 양생하는 방법으로 바닥틀을 제작하여도 무방하다.On the other hand, in the bottom frame manufacturing step (S20), filling the cement to a predetermined height inside the mold 10, and after the cement is cured in a semi-solid state to form the irregularities as if drawing a pattern with a spatula It is also possible to manufacture the floor frame by curing method.

따라서, 상기 시멘트로 양생된 바닥틀의 요철부에 색상이 다른 시멘트를 추가로 충진하여 배출함으로써 다양한 색상을 가진 마감판재를 제작할 수 있게 된다.Therefore, by filling and discharging the cement having a different color to the concave-convex portion of the bottom frame cured with the cement it is possible to manufacture a finish plate having a variety of colors.

한편 도 14에서 도시된 바와 같이, 바닥틀 제작단계(S20")는, 성형틀 내부로 시멘트를 소정의 높이로 충진하고 상기 시멘트가 반 고체 상태로 양생된 후에 주걱으로 길이방향으로 작업자의 임의에 따라 요철을 형성하여 양생하여도 무방하다.On the other hand, as shown in Figure 14, the bottom frame manufacturing step (S20 "), filling the cement into the mold to a predetermined height, and after the cement is cured in a semi-solid state, the spatula in the lengthwise direction of the operator As a result, irregularities may be formed and cured.

상기 주걱(2)은 톱니형상으로 형성되어 복수의 요철을 일정간격으로 나란하게 형성하여도 무방하며, 단부의 재질이 고무 등의 합성수지재로 형성되어도 무방하며, 상기 주걱을 대체하여 철재 또는 합성수지재의 모가 나란하게 삽입되어 고정된 브러쉬를 사용하여 다양한 형상의 요철을 구비할 수 있도록 이루어지는 것이 바람직하다.The spatula 2 may be formed in a sawtooth shape to form a plurality of irregularities side by side at a predetermined interval, and may be formed of a synthetic resin material such as rubber at the end thereof, and replace the spatula to be made of iron or synthetic resin material. It is preferable that the hairs are inserted so that they can be provided with irregularities of various shapes using a fixed brush.

또한, 상기 성형틀 분리단계(S80) 이후에, 양생된 마감판재의 외피에 투명한 합성수지재를 도포하여 굳히는 합성수지재 도포단계(S90)를 더 포함하여 이루어짐으로써 제작된 마감판재의 표피를 보호하여 마감판재의 표면이 노후되는 것을 방지하고 더욱 견고하게 제작될 수 있도록 하는 효과가 있다.In addition, after the molding frame separation step (S80), by further comprising a synthetic resin material applying step (S90) to apply a hardened by applying a transparent synthetic resin material on the outer surface of the cured finish plate material to protect the finish of the finished plate material It is effective to prevent the surface of the plate from aging and to be manufactured more firmly.

본 발명은 상기한 실시예에 한정되지 아니하며, 적용범위가 다양함은 물론이고, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이다.
It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. It goes without saying that various modifications can be made.

S100: 무늬가 형성된 건축용 시멘트 마감판재의 제조방법
S10: 성형틀 준비단계
S20: 바닥틀 제작단계
S21: 생나무판재 준비단계
S30: 바닥틀 고정단계
S40: 박리제 도포단계
S50: 시멘트 충진단계
S60: 시멘트 배출단계
S70: 모르타르 충진단계
S80: 성형틀 분리단계
S90: 투명 합성수지재 도포단계
100: 무늬가 형성된 건축용 시멘트 마감판재
1: 생나무판재 2: 주걱
3: 자연소재 10: 성형틀
20: 바닥틀 30: 시멘트
40: 모르타르S100: Method of manufacturing a patterned building cement finish plate
S10: forming mold preparation step
S20: Step of making frame
S21: preparatory wood board preparation step
S30: bottom frame fixing step
S40: release agent applying step
S50: Cement Filling Step
S60: Cement Discharge Stage
S70: mortar filling stage
S80: forming mold separation step
S90: transparent synthetic resin coating step
100: patterned building cement finishing board
1: raw wood board 2: spatula
3: natural material 10: mold
20: frame 30: cement
40: mortar

Claims (7)

성형틀(10)을 바닥면과 측벽이 구비되도록 형성하여 준비하는 성형틀 준비단계(S10)와; 표면에 입체적으로 요철(21)이 구비되어 무늬가 형성된 바닥틀(20)을 제작하는 바닥틀 제작단계(S20)와; 상기 바닥틀(20)을 요철(21)이 상부를 향하도록 성형틀의 바닥면에 안착하여 고정하는 바닥틀 고정단계(S30)와; 상기 성형틀과 바닥틀의 내측 표면에 박리제를 도포하는 박리제 도포단계(S40)와; 상기 성형틀 내부의 요철이 형성된 바닥틀 상부에 시멘트(30)를 충진하는 시멘트 충진단계(S50)와; 상기 바닥틀의 요철 내부에 충진된 시멘트가 남아있도록 바닥틀의 상부에 충진된 시멘트를 긁어서 배출하는 시멘트 배출단계(S60)와; 상기 요철에 시멘트가 남아있는 바닥틀 상부에 모르타르(40)를 채우는 모르타르 충진단계(S70)와; 상기 성형틀(10)과 바닥틀을 분리하는 단계(S80);를 포함하여 이루어지는 무늬가 형성된 건축용 마감판재의 제조방법에 있어서,
상기 시멘트 충진단계와 시멘트 배출단계는,
상기 성형틀 내부의 요철이 형성된 바닥틀 상부에 시멘트(30)를 충진한 후, 탄력성이 있는 주걱을 사용하여 시멘트를 긁어서 요철(21)의 일부에는 시멘트(30a)가 남겨지고 다른 부분의 시멘트만 배출하도록 하고, 상기 요철에 남겨진 시멘트가 소정 시간 동안 양생된 후 상기 바닥틀 상부에 상기 요철(21)의 일부에 남겨진 시멘트(30a)와는 상이한 색상을 갖는 시멘트(30b)를 충진한 후 주걱으로 상기 상이한 색상을 갖는 시멘트를 긁어 배출함으로써, 표면에 서로 다른 색상을 갖는 시멘트로 이루어진 무늬가 형성되도록 하는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재의 제조방법.
Forming mold preparation step (S10) for forming and preparing the forming mold 10 so that the bottom surface and the side wall; The bottom frame manufacturing step (S20) for producing a patterned bottom frame 20 is provided with a concave-convex 21 on the surface; A bottom frame fixing step (S30) for seating and fixing the bottom frame 20 to the bottom surface of the mold so that the unevenness 21 faces upward; A release agent applying step (S40) of applying a release agent to the inner surfaces of the mold and the bottom frame; Cement filling step (S50) for filling the cement 30 on the bottom frame formed with the irregularities inside the mold; A cement discharge step (S60) of scraping and discharging the cement filled in the upper part of the bottom frame so that the cement filled in the unevenness of the bottom frame remains; Mortar filling step (S70) for filling the mortar (40) in the upper portion of the bottom frame in which cement is left in the uneven; In the method of manufacturing a patterned building finishing plate material comprising a; forming step (S80) for separating the mold 10 and the bottom frame,
The cement filling step and the cement discharge step,
After filling the cement 30 with the top of the bottom frame formed with the irregularities inside the mold, scraping the cement using an elastic spatula to leave some of the cement 30a in the uneven portion 21 and only cement of the other part. After the cement left in the unevenness is cured for a predetermined time, the cement 30b having a color different from that of the cement 30a left in a part of the unevenness 21 is filled in the upper part of the bottom frame, and then the spatula The method of manufacturing a patterned building finishing plate, characterized in that by scraping out the cement having a different color, a pattern made of cement having a different color on the surface.
제1항에 있어서, 상기 바닥틀 제작단계(S20)는,
생나무 판재(1)를 준비하는 생나무판재 준비단계(S21)와; 준비된 생나무 판재의 표면을 태우는 탄화단계(S22)와; 상기 생나무 판재의 표면에 나무결 무늬를 입체적으로 형성하도록 탄화된 연질부를 제거하는 단계(S23);로 이루어지는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재의 제조방법.
According to claim 1, The bottom frame manufacturing step (S20),
Raw wood plate preparation step (S21) for preparing the raw wood plate (1); Carbonization step (S22) for burning the surface of the prepared raw wood plate; Removing the soft carbonized portion to form a three-dimensional wood grain pattern on the surface of the raw wood plate (S23); The manufacturing method of the patterned building finish plate comprising a.
제1항에 있어서, 상기 탄력성이 있는 주걱은 단부에 톱니형상이 형성되어 있는 것을 사용하는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재의 제조방법.
The method of claim 1, wherein the elastic spatula is formed with a sawtooth shape formed at an end portion thereof.
제1항에 있어서, 상기 시멘트 충진단계(S50), 시멘트 배출단계(S60) 또는 모르타르 충진단계(S70) 중 적어도 어느 한 단계에서 상기 성형틀을 진동시키고 상부에서 압착시키는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재의 제조방법.
According to claim 1, wherein at least one of the cement filling step (S50), the cement discharge step (S60) or the mortar filling step (S70) of the pattern formed, characterized in that the vibrating mold and pressed from the top Method of manufacturing finishing boards for construction.
제1항에 있어서, 상기 바닥틀 제작단계(S20)는, 생나무 판재를 준비하는 생나무판재 준비단계(S21)와, 준비된 생나무 판재의 상부에 나뭇잎 또는 꽃잎의 자연소재를 늘어놓아 고정하는 자연소재 고정단계(S24)로 이루어지는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재의 제조방법.
The method of claim 1, wherein the production step (S20) of the bottom frame, the step of preparing the raw wood board (S21) and the natural material fixing to secure the lined natural material of leaves or petals on top of the prepared raw wood board Method of manufacturing a patterned building finish plate characterized in that the step (S24).
제1항에 있어서, 상기 성형틀 분리단계(S80) 이후에, 양생된 마감판재의 외피에 투명한 합성수지재를 도포하여 굳히는 합성수지재 도포단계(S90)를 더 포함하여 이루어지는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재의 제조방법.
According to claim 1, After the molding frame separation step (S80), the pattern is formed, characterized in that it further comprises a synthetic resin coating step (S90) of applying a solid synthetic resin material to the outer surface of the cured finishing plate material to harden Method of manufacturing finishing boards for construction.
제1항 내지 제6항 중 어느 한 항에 따른 무늬가 형성된 건축용 마감판재의 제조방법으로 만들어지는 것을 특징으로 하는 무늬가 형성된 건축용 마감판재.
A patterned building finishing plate material, characterized in that it is made by the method of manufacturing a patterned building finishing plate according to any one of claims 1 to 6.
KR1020120100537A 2012-09-11 2012-09-11 Pattern formed architectural cement finish plates and method of manufacture KR101345355B1 (en)