KR100472016B1 - Tile which be made by bonding and cementing artificial stone for construction - Google Patents
Tile which be made by bonding and cementing artificial stone for construction Download PDFInfo
- Publication number
- KR100472016B1 KR100472016B1 KR10-2002-0036021A KR20020036021A KR100472016B1 KR 100472016 B1 KR100472016 B1 KR 100472016B1 KR 20020036021 A KR20020036021 A KR 20020036021A KR 100472016 B1 KR100472016 B1 KR 100472016B1
- Authority
- KR
- South Korea
- Prior art keywords
- artificial stone
- tile
- epoxy adhesive
- stone
- artificial
- Prior art date
Abstract
본 발명은 자연석을 일정한 입자로 잘게 부숴 인조석을 얻고, 상기 인조석을 적량의 에폭시 접착제와 혼합하고, 상기 인조석을 이용하여 건축용 타일을 제조하되, 인조석과 에폭시 접착제의 혼입비율을 최적의 조건으로 하여 강도와 견고성이 우수한 타일을 얻게 함과 동시에 인조석의 입자를 용도에 맞게 적절한 입자의 크기로 선별사용케 하며, 또한 필요에 따라 타일에 형성되는 공극을 메워 이물질의 침투를 방지케 하여 사용중 악취발생의 원인을 제거케하고 타일의 테두리 혹은 배면에 보강테 혹은 보강재를 일체형으로 접합구성되게 하여 미려한 외관과 강도 및 견고성을 증진 시킨 양질의 건축용 타일을 제공받고자 하는 것이다.The present invention obtains the artificial stone finely crushed natural stone into a certain particle, the artificial stone is mixed with an appropriate amount of epoxy adhesive, and the building stone is manufactured using the artificial stone, the strength of the mixing ratio of artificial stone and epoxy adhesive as the optimum conditions In addition to obtaining tiles with excellent hardness and solidity, the particles of artificial stone can be selected and used in the appropriate size of particles according to the purpose, and the gap formed in the tiles can be filled as necessary to prevent the ingress of foreign substances, thereby causing odor during use. It is to be provided with a high quality building tile that improves the beautiful appearance, strength and robustness by removing the and to make the reinforcement frame or reinforcing material integrally bonded to the edge or back of the tile.
Description
본 발명은 자연석을 잘게 부순 인조석을 이용하여 건축용 내외장재로 사용되는 타일을 제조할 수 있도록 한 것으로서, 특히 제조된 타일의 강도를 견고히 하여 건축용 내외장재로 현실적으로 적용가능케 함과 동시에 타일 제조시 형성되는 내부의 공극을 차단하여 외부의 이물질이 침투되지 않게 하여 보다 이상적인 타일을 제조하고자 하는 것이다.The present invention is to enable the production of tiles used as interior and exterior materials for building using artificial stone finely crushed natural stone, in particular to strengthen the strength of the manufactured tiles to be practically applicable to the interior and exterior materials for building and at the same time formed during the manufacture of tiles By blocking the pores to prevent foreign matter from penetrating the outside is to produce a more ideal tile.
잘게 부순 자갈이나 모래와 같은 자연석 즉 인조석을 이용한 타일의 제조방법에 대하여서는 본 발명자가 "인조석을 이용한 타일의 제조방법"으로 선출원(특허출원제1998-6995호)한 것이있다.As for the method of producing a tile using natural stone, that is, artificial stone, such as finely crushed gravel or sand, the inventor has filed an application (patent application No. 1998-6995) as a "manufacturing method of tile using artificial stone".
즉 돌을 잘게 부수어 얻어진 인조석 18∼22kg에 에폭시 접착제 1∼2kg을 혼합하여 각종 보조형틀을 이용하여 원하는 규격과 형태로 가압성형한 뒤 경화시키는 방법으로 제조하는 인조석을 이용한 타일의 제조에 관한 것이다.That is, the present invention relates to the production of tiles using artificial stone, which is manufactured by a method of hardening after molding and molding a desired size and shape using various auxiliary molds by mixing 1 to 2 kg of epoxy adhesive with 18 to 22 kg of artificial stones obtained by crushing stones.
상기 본 발명자가 위와 같은 제조수단으로 타일을 제조하여 건축용 내외장재로 적용사용하여 본 바 여러가지 문제가 도출됨을 알 수 있었다.The inventors have found that various problems can be derived by using the tile as an interior and exterior building material by manufacturing tiles using the above manufacturing means.
즉 타일의 강도가 현저히 약하여 건축용 타일의 적용 사용시 쉽게 파손되는 문제가 있는 것이었고, 특히 내부에 무수한 기공 즉 공간이 형성되면서 건축용 내외장재로 사용시 타일에 형성된 공간부에 이물질이 침투되어 고인 후 부패되어 악취가 발생하게 되는 문제가 있었다.In other words, the strength of the tile was so weak that there was a problem that it is easily damaged when the application of the building tile is applied.In particular, when countless pores, that is, the space is formed inside, when the foreign matter penetrates into the space formed in the tile when used as interior and exterior materials for building, it decays and decays. There was a problem that occurred.
또한 제조된 타일의 크기가 대형일 뿐 아니라 무게가 너무 무거워 실제 사용하기가 곤란하며, 선출원에서는 이를 필요한 규격으로 절단사용한 다고 기재하고 있으나 이를 절단과정에서 타일의 파손현상이 많아 비경제적일뿐 아니라, 절단을 위하여 석재절단용 대형 절단설비가 필요하게 되며 그에 따른 시간과 인력이 낭비되는 등의 문제점이 있는 것이었다.In addition, the size of the manufactured tile is not only large, but too heavy, so it is difficult to use it practically, and the previous application states that it is used for cutting to the required standard, but it is uneconomical because there are many damages of the tile during the cutting process. For this purpose, a large cutting facility for stone cutting is required, which results in waste of time and manpower.
본 발명자는 이러한 문제점을 검토하여 본 바 강도에 대한 문제는 잘게 부순 인조석과 상기 인조석을 서로 접착시켜주는 에폭시 접착제의 혼합비율이 부적합하기 때문인 것으로 판단되어졌고, 사용시 타일을 구성하는 공극사이에 이물질이 침투, 부패하여 악취가 발생되는 것은 타일에 구성되는 공극을 차단시켜주지 못한 이유때문이며, 절단시 파손되는 문제와 별도의 절단기 구비는 원하는 크기의 타일로 제조하지 않고 한 번에 큰 타일을 제조한 다음 이를 필요한 크기로 절단사용한다는 것때문인 것으로 판단되어졌다.The present inventors have reviewed these problems, and it was determined that the problem with strength was due to the inadequate mixing ratio of finely crushed artificial stones and epoxy adhesives that bond the artificial stones to each other. Odor is generated due to penetration and decay due to the failure to block the voids formed in the tile. The problem of breakage during cutting and the provision of a separate cutter are not to make tiles of the desired size, It was judged that it was cut to the required size.
본 발명은 이러한 종래의 제반문제점을 시정하고자 잘게 부순 인조석과 에폭시 접착제의 혼합비율을 적절히 하여 충분한 강도를 갖는 타일을 제조함과 동시에 잘게 부순 인조석사이에 형성되는 공극에 이물질이 침투하는 것을 방지케 하며, 또한 필요한 크기로 규격화하여 절단없이 바로 사용할 수 있도록 한 것이다.The present invention prevents foreign matter from penetrating into the pores formed between finely crushed artificial stone while producing a tile having a sufficient strength by appropriately mixing the ratio of finely crushed artificial stone and epoxy adhesive to correct these problems. In addition, it is standardized to the required size so that it can be used immediately without cutting.
상기 목적을 달성하기 위하여 광석에서 채취한 자연석을 파쇄기를 이용하여 잘게 부순다음 잘게부순 인조석을 선별기를 통하여 규격별로 선별한다.In order to achieve the above object, the natural stone collected from the ore is finely crushed using a crusher, and then the finely crushed artificial stone is selected by the standard through a sorting machine.
이때 잘게부순 인조석의 경우 크기가 6∼10mm정도의 크기는 자갈 인조석의 용도로 사용하고 0.5∼1.5mm정도의 크기는 모래인조석의 용도로 사용한다. At this time, in the case of finely divided artificial stone, the size of 6 ~ 10mm is used for the gravel artificial stone and the size of 0.5 ~ 1.5mm is used for the sand artificial stone.
상기에서 잘게 부순 자갈 인조석과 에폭시 접착제의 혼합비율은 중량비로 자갈인조석 7∼9 : 에폭시 접착제 1의 비율로 혼합하고, 모래 인조석인 경우에는 모래 6∼8 : 에폭시 접착제 1의 비율로 혼합하는 것이 바람직하다.The mixing ratio of finely crushed gravel artificial stone and epoxy adhesive is mixed in the ratio of gravel artificial stone 7-9: epoxy adhesive 1 by weight ratio, and in the case of sand artificial stone, it is preferable to mix in the ratio of sand 6-8: epoxy adhesive 1. Do.
상기에서 잘게 부순 자갈이나 모래 인조석과 에폭시 접착제의 혼합비율은 제조된 타일의 사용용도(벽체, 바닥재)에 따라 조금씩 차이가 있다.The mixing ratio of finely crushed gravel or sand artificial stone and epoxy adhesive is slightly different depending on the use of the manufactured tile (wall, flooring).
상기한 혼합비율로 얻어진 소재를 이용하여 필요한 규격의 타일을 제조한 다음 타일의 표면을 에폭시 접착제로 코팅하여 도포막이 형성되게 하여 타일내에 이물질의 침투가 방지되게 하여서 된 것이다.By using the material obtained in the above mixing ratio to prepare a tile of the required standard and then coated the surface of the tile with an epoxy adhesive to form a coating film to prevent the penetration of foreign matter in the tile.
상기 본 발명에서 제공하고자 하는 타일을 제조함에 있어서 타일의 외면에 보강테두리를 구성하거나 타일의 배면에 목재판재나 그물망 등의 보강재를 일체형으로 구성하여 강도를 더욱 견고하게 하여 사용할 수도 있다.In the manufacture of the tile to be provided in the present invention may be used to configure the reinforcement border on the outer surface of the tile or to further strengthen the strength by integrally configuring the reinforcement such as wood plate or netting on the back of the tile.
이하 본 발명의 실시예를 첨부도면에 따라 상세히 설명하면 다음과 같다.Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings.
광산에서 채취한 자연석을 색깔별로 구분한 다음 파쇄기를 이용 파쇄하여 잘게 부순 자갈인조석과 모래인조석을 얻는다.The natural stones collected from the mine are classified by color and then crushed using a crusher to obtain finely crushed gravel and sand artificial stones.
상기에서 잘게 부순 자갈인조서의 경우에는 입자의 크기가 6∼10mm정도로 하고, 모래인조석의 경우에는 0.5∼1.5mm정도로 하며 이때 자갈인조석과 모래인조석의 선별은 통상의 선별기를 이용하여 필요한 입자의 인조석을 얻는다.In the case of the crushed gravel artificial stone, the particle size is about 6 to 10 mm, and in the case of the sand artificial stone, about 0.5 to 1.5 mm. At this time, the artificial stone of the granules and the sand artificial stone are required by using a conventional sorting machine. Get
상기에서 얻어진 자갈과 모래인조석(10)에 적량의 에폭시 접착제를 골고루 혼합한 다음 준비된 성형틀(20)을 이용하여 타일(30)을 제조하게 되며, 이때 타일의 사용 용도에 따라 인조석(10)과 에폭시 접착제의 투입량은 달라지게 된다.After mixing the appropriate amount of epoxy adhesive evenly in the gravel and sand artificial stone (10) obtained above to prepare a tile (30) using the prepared mold 20, the artificial stone (10) and according to the intended use of the tile The dosage of the epoxy adhesive will vary.
또한 상기 타일(30)을 제조함에 있어서 테두리에는 보강테(31)를 구성하거나 배면에 목재판이나 금속망과 같은 보강재(32)를 구성할 수 있다.In addition, in the manufacture of the tile 30 may be configured to the reinforcement frame 31 on the rim or to the reinforcement material 32, such as wooden boards or metal mesh on the back.
이하 실시예를 상세히 설명한다.Examples will be described in detail below.
실시예(1)Example (1)
실시예는 잘게 부순 자갈 및 모래인조석(10)를 이용하여 공원 산채로나 조경용 블럭용도로 사용하고자 하는 것이다.The embodiment is intended to be used as a park alive or as a block for landscaping using finely crushed gravel and sand artificial stone (10).
먼저 잘게부순 자갈인조석을 선별하되 입자를 6∼10mm정도의 인조석(10)을 선별기를 통하여 선별한다.First, the finely divided gravel artificial stone is selected, but the particles of the artificial stone 10 of about 6 ~ 10mm is selected through a sorting machine.
상기 선별된 인조석(10)을 에폭시 접착제와 골고루 교반하며, 이때 에폭시 접착제와 자갈인조석(10)의 혼합비율은 중량비율로 1 : 7∼7.5의 비율로 혼합하고, 혼합 즉시 준비된 성형틀(20)에 에폭시 접착제가 혼합된 인조석(10)을 채운다음 적절한 진동을 주어 충분히 다져지게 하고 상면을 가압, 경화, 탈형한다.The selected artificial stone 10 is evenly stirred with an epoxy adhesive, wherein the mixing ratio of the epoxy adhesive and the gravel artificial stone 10 is mixed in a ratio of 1: 7 to 7.5 by weight ratio, and ready to be mixed (20) After filling the artificial stone (10) mixed with epoxy adhesive to give a sufficient vibration to sufficiently compact and pressurize, harden, demolding the upper surface.
이때 가압수단은 가압롤러를 이용하거나 평판형 가압프레스를 이용할 수 있으며, 경화시간은 온도와 기상조건에 따라 달라지게 되나 통상적으로 상온에서 5∼6시간 정도이면 된다.In this case, the pressurizing means may use a press roller or a flat press press, and the curing time may vary depending on the temperature and the weather conditions, but usually 5 to 6 hours at room temperature.
그러나 경화에 많은 시간이 소요되므로 별도의 경화로를 설치사용하는 것이 바람직할 것으로 판단된다.However, since hardening takes a lot of time, it is judged that it is preferable to install and use a separate curing furnace.
상기에서 타일(30)의 강도와 견고성 향상을 위하여 테두리에 보강테(31)를 일체형으로 구성할 수 있으며, 또한 배면에 목재판이나 금속망과 같은 보강재(32)를 일체형으로 접착되게 할 수도 있다.The reinforcement frame 31 may be integrally formed on the rim to improve the strength and robustness of the tile 30, and the reinforcement material 32 such as a wooden board or a metal net may be integrally bonded to the back surface. .
보강테(31) 및 보강재(32)가 타일(30)과 일체형으로 구성되게 하기 위한 수단은 성형틀(20)내에 보강테(31)나 보강재(32)를 먼저 위치시킨 다음 그 위에 에폭시 접착제가 혼합된 인조석(10)을 채워 넣은 다음 가압경화하게 되며, 이때 보강테(31) 및 보강재(32)에는 에폭시 접착재를 도포하여 견고한 접착이 이루어지게 하는 것이 바람직하다.The means for allowing the reinforcement frame 31 and the reinforcement material 32 to be integrally formed with the tile 30 is to first place the reinforcement frame 31 or the reinforcement material 32 in the mold 20 and then epoxy adhesive thereon. Filling the artificial stone 10 is then hardened by pressure, at this time, it is preferable to make a strong adhesion by applying an epoxy adhesive to the reinforcing frame 31 and the reinforcing material (32).
상기에서 타일(30)의 테두리에 구성되는 보강테는 내구성 및 내부식성이 우수한 합성수지나 금속소재이면 만족하며, 바닥에 위치하는 보강재(32)는 목재판이나 합성수지판, 금속망, 섬유원단, 내구성이 우수한 종이 등을 사용할 수 있다.The reinforcing frame configured at the edge of the tile 30 is satisfied if it is a synthetic resin or a metal material with excellent durability and corrosion resistance, and the reinforcing material 32 located at the bottom is a wood board or a synthetic resin board, a metal net, a fabric of fabric, durability This excellent paper etc. can be used.
상기와 같은 조건으로 모래인조석 즉 입자가 0.5∼1.5mm정도의 인조석(10)을 이용하여 타일(30)을 제조한 다음 공원 산책로나 조경용 블럭으로 사용할 수도 있다.Under the same conditions as above, the tiles 30 may be manufactured using the artificial sand 10 having a particle size of about 0.5 to 1.5 mm and then used as a park walkway or a landscape block.
실시예(2)Example (2)
본 실시예는 벽체용으로 사용되는 타일(30)을 제조하고자 하는 것으로서, 자갈인조석과 모래인조석 2가지로 구분될 수 있으며, 이때 재료에 따른 차이는 에폭시 접차제의 혼입비율차이다.The present embodiment is intended to manufacture the tile 30 used for the wall, it can be divided into two kinds of gravel artificial stone and sand artificial stone, wherein the difference according to the material is the mixing ratio difference of the epoxy contact agent.
인조석(1)의 입자가 6∼10mm정도인 자갈인조석의 경우에는 에폭시 접착제와 인조석(10)의 혼합비율은 중량비로 1:8∼9의 비율로 혼합하고, 인조석(10)의 입자가 0.5∼1.5mm정도인 모래인조석의 경우에는 에폭시 접착제와 인조석의 혼합비율을 중량비로 1:7∼8의 비율로 혼합한다.In the case of gravel artificial stone having particles of artificial stone 1 of about 6 to 10 mm, the mixing ratio of epoxy adhesive and artificial stone 10 is mixed at a weight ratio of 1: 8 to 9, and the particles of artificial stone 10 are 0.5 to In the case of sand artificial stone of about 1.5mm, the mixing ratio of epoxy adhesive and artificial stone is mixed in a ratio of 1: 7 to 8 by weight.
상기와 같은 조건으로 에폭시 접착제와 혼합된 인조석(10)을 실시예(1)에서와 같이 성형틀(20)을 이용하여 타일(30)을 제조하게 되며 이때에도 타일(30)의 테두리 및 바닥에 보강테(31)나 보강재(32)가 일체형으로 구성되게 하여 강도와 견고성을 증진시킬 수 있다.In the above conditions, the artificial stone 10 mixed with the epoxy adhesive is manufactured in the tile 30 using the molding die 20, as in the embodiment (1), and at this time, the edge and the bottom of the tile 30 The reinforcing frame 31 or the reinforcing material 32 may be integrally formed to enhance strength and tightness.
위 제조과정에서 자갈인조석이 모래인조석 보다 많은 량의 에폭시 접착제를 필요로 하는 것은 자갈인조석이 모래인조석보다 많은 공극이 형성되므로 서로 접촉하면 표면적이 적기 때문에 보다 많은 량의 에폭시 접착제를 사용하게 된다.In the above manufacturing process, the gravel artificial stone requires more epoxy adhesive than the sand artificial stone, since the pores are formed more than the sand artificial stone, so the surface area is in contact with each other, so a larger amount of epoxy adhesive is used.
실시예(3)Example (3)
본 실시예는위에서 설명한 실시예에서와 같이 채취한 자연석을 잘게 부순 자갈인조석과 모래인조석을 이용하여 건물내부의 바닥용 타일로 제작사용하고자 하는 것이다.This embodiment is to produce and use as a floor tile in the building using the artificial stone and sand artificial stone crushed finely crushed as in the embodiment described above.
인조석(10의 입자가 6∼10mm정도인 자갈인조석을 이용한 타일(30)의 제조는 다음과 같다.Synthesis of the tile 30 using the artificial stone (grains of about 10 to 10 mm gravel artificial stone is as follows.
즉 에폭시 접착제와 자갈인조석의 배합비율을 1:7∼8의 중량비로 혼합한다.That is, the mixing ratio of the epoxy adhesive and the gravel artificial stone is mixed at a weight ratio of 1: 7 to 8.
또한 인조석(10)의 입자가 0.5∼1.5mm인 모래 인조석을 이용한 타일(30)의 제조는 에폭시 접착제와 모래인조석의 배합비율을 중량비로 1:6.5∼7.5의 혼합비로 하여 혼합한다.In addition, the manufacture of the tile 30 using the sand artificial stone whose particle | grains of the artificial stone 10 are 0.5-1.5 mm is mixed by mixing the compounding ratio of epoxy adhesive and sand artificial stone in the weight ratio of 1: 6.5-7.5.
상기에서와 같은 비율로 혼합된 인조석(10)을 실시예(1)에서와 같은 방법으로 준비된 성형틀(20)에 투입, 가압, 경화, 탈형하여 건물 바닥용 타일로 사용하게 되며 이때에 타일(30)의 테두리 및 바닥에는 보강테(31)나 보강재(32)를 일체형으로 접착구성되게 하여 사용할 수도 있다.The artificial stone 10 mixed in the same ratio as described above is put into a molding mold 20 prepared in the same manner as in Example 1, pressurized, cured, and demolded to be used as a tile for a building floor. 30 may be used to integrally bond the reinforcing frame 31 or the reinforcing material 32 to the edge and the bottom.
이때 건물 바닥용으로 사용되는 타일(30)의 경우에는 반드시 성형완료된 타일(30)의 표면에 이물질 침투방지를 위하여 에폭시 접착제를 도포하여 인조석(10)사이에 형성되는 공극을 메워주는 것이 바람직하며, 이는 사용시 인조석사이에 형성되는 공간부(공극)에 이물질이 침투. 부패하여 악취가 발생하는 현상을 방지함과 동시에 방수효과를 기대할 수 있도록 하는 것이다.In this case, in the case of the tile 30 used for the building floor, it is preferable to fill an air gap formed between the artificial stones 10 by applying an epoxy adhesive to prevent foreign matter from penetrating the surface of the finished tile 30. This foreign matter penetrates into the voids (voids) formed between artificial stones when used. It is to prevent the occurrence of bad smell due to corruption and at the same time can expect a waterproof effect.
실시예(4)Example (4)
본 실시예는 대리석(40)에 인조석(10)를 일체형으로 접합하여 사용할 수 있도록 한 것으로서 벽면이나 바닥에 인테리어용 마감재로 사용되는 대리석(40)에 특정한 무늬를 형성하거나 기능적으로 미끄럼방지용으로 사용할 수 있도록 한 것이다.This embodiment is to enable the artificial stone 10 to be integrally bonded to the marble 40 to form a specific pattern on the marble 40 used as interior finishing material on the wall or floor, or can be used for functionally slipping. It would be.
도5에서와 같이 내부마감재로 사용하는 대리석(40)에 표현하고자 하는 무늬나 문자등의 요입홈(41)을 구성하고, 상기 요입홈(41)에 잘게 부순 인조석(10)과 에폭시 접착제가 혼합된 인조석을 채운 다음 가압경화하여 대리석(40)에 인조석(10)으로 된 필요한 문양을 일체형으로 접합구성되게 할 수 있으며, 이때에는 다양한 색상의 인조석을 이용하여 보다 미려한 외관의 대리석 마감재를 얻을 수 가 있게 된다.As shown in FIG. 5, a concave groove 41 such as a pattern or a character to be expressed on the marble 40 used as the interior finishing material is formed, and the artificial stone 10 and the epoxy adhesive finely crushed in the concave groove 41 are mixed. Filled artificial stone and then pressure-cured to be integrally bonded to the required pattern of the artificial stone 10 to the marble 40, in this case, it is possible to obtain a marble finish of a more beautiful appearance by using artificial stone of various colors Will be.
도6은 계단으로 사용되는 대리석에 미끄럼방지용의 기능을 갖는 인조석(10)을 일체로 접착구성되게 하는 것이다.Fig. 6 is to integrally bond the artificial stone 10 having a function of anti-slip to marble used as stairs.
좀더 구체적으로 설명하면 계단으로 사용되는 대리석(40)의 선단부에 길이방향으로 길게 요입홈(41)을 구성하고 상기 요입홈(41)에 에폭시 접착제가 혼합된 인조석(10)을 채운다음 가압경화시키면 외관이 미려하면서 미끄럼방지수단이 우수한 계단용 대리석(40)을 제공받을 수 있게 된다.In more detail, when the concave groove 41 is formed in the longitudinal direction of the distal end of the marble 40 to be used as a stair, and the artificial groove 10 in which the epoxy adhesive is mixed into the concave groove 41 is pressed and cured. The appearance is beautiful and the non-slip means can be provided excellent marble marble 40.
상기에서 대리석(40)에 구성되는 요입홈(41)의 깊이는 최소한 6mm정도되는 것이 이상적이며 에폭시 접착제가 혼합된 인조석(10)을 일체로 접착되게 하는 수단도 먼저 요입홈(41)에 에폭시 접착제를 먼저 도포한 다음 인조석을 접합하면 보다 견고한 접합을 기대할 수 있게 된다.Ideally, the depth of the recessed groove 41 formed in the marble 40 is ideally at least about 6 mm, and means for integrally adhering the artificial stone 10 mixed with the epoxy adhesive is also first epoxy adhesive to the recessed groove 41. If you apply the first and then join the artificial stone, you can expect a more solid bonding.
또한 계단용 대리석(40)에 구성된 요입홈(41)에 접착되는 인조석(10)의 입자는 모래인조석 크기의 입자를 사용하는 것이 효과적이다.In addition, the particles of the artificial stone 10 adhered to the recessed grooves 41 formed in the marble for stairs 40, it is effective to use the size of the sand artificial stone.
실시예(5)Example (5)
본 실시예는 본 발명에서 제조하는 잘게 부숴진 인조석을 이용하여 타일(30)을 제조하고, 상기 타일(30)을 다른 외장재와 사용하면서 시각적으로 표출되게 하기 위하여 약간 돌출되게 하기 위한 타일(30)을 제조하기 위한 것이다.In this embodiment, the tile 30 is manufactured by using the finely crushed artificial stone manufactured in the present invention, and the tile 30 for slightly protruding to be visually expressed while using the tile 30 with other exterior materials is provided. It is for manufacturing.
즉 도7에서와 같이 먼저 필요한 문양으로 케이스(50)를 먼저 제작한 다음 상기 케이스(50)내에 에폭시 접착제가 혼합된 자갈인조석 혹은 모래인조석을 채워넣고 가압, 경화하고 다시 표면에 에폭시 접착제를 추가로 도포, 경화한 다음 탈형한다.That is, as shown in Figure 7, first, the case 50 is first made of the required pattern, and then the case 50 is filled with a gravel artificial stone or sand artificial stone mixed with an epoxy adhesive, pressurized and cured, and the epoxy adhesive is added to the surface again. Apply, harden and demold.
이때 케이스(50)로 사용되는 재질은 금속이 대부분이나 합성수지 혹은 모래를 사용할 수도 있다.In this case, the material used as the case 50 may be metal or synthetic resin or sand.
상기한 구성의 타일(30)을 다른 소재의 내부마감재(석재, 보도블럭, 마루판 등)와 함께 사용하면서 어느 한 부분만 본 발명에서 제공하고자 하는 타일을 사용하고자 할 때에 타일(30)배면에 목재판과 같은 소재의 마감재(51)를 일체형으로 접합하여 사용할 수 있다.When using the tile 30 having the above-described configuration together with the internal finishing material (stone, sidewalk block, floorboard, etc.) of another material, only one portion of the tile 30 is to be used when the tile to be provided by the present invention The finishing material 51 of the same material as the trial can be used by integrally bonding.
이상 설명한 바와 같이 본 발명은 채취한 자연석을 색상별로 구분한 다음 파쇄기를 이용하여 잘게부수고, 부서진 인조석을 선별기를 통하여 입자별로 구분 선별하여 자갈인조석과 모래인조석을 각각 얻고, 상기 인조석을 사용용도에 따라 적량의 에폭시 접착제와 혼합하고, 에폭시 접착제가 혼합된 인조석을 성형틀내에 채운다음 가압, 경화, 탈형하여 충분한 강도를 갖는 타일을 얻을 수 있게 되며 필요에 따라 테두리와 바닥에는 보강테와 보강재를 일체형으로 구성하고, 사용용도 즉 실내 바닥재로 사용될 경우에는 표면에 에폭시 접착제를 도포하여 공극을 메워 이물질의 침투를 방지케 하므로서 타일에 구성된 공극에 이물질이 유입, 부패되므로 인한 악취를 방지할 수 있게 된다.As described above, the present invention classifies the collected natural stone by color and then crushes finely using a crusher, and separates the broken artificial stone by particle through a sorting machine to obtain gravel artificial stone and sand artificial stone, and the artificial stone is used according to the intended use. After mixing with the appropriate amount of epoxy adhesive, the artificial stone mixed with epoxy adhesive is filled into the mold, and then pressed, hardened, and demolded to obtain a tile having sufficient strength. When the composition is used, that is, when used as an indoor flooring material, the epoxy adhesive is applied to the surface to fill the pores to prevent foreign substances from penetrating, thereby preventing odors due to the inflow and debris of the pores formed in the tile.
또한 경우에 따라 대리석에 요입부를 형성하고 상기 요입부에 에폭시 접착제가 혼합된 인조석을 일체형으로 채워넣어 장식용으로 사용하거나 기능성용도로 사용케 할 수가 있게 되는 등의 효과가 있는 것이다.In addition, in some cases, it is possible to form a recess in the marble and to integrally fill the recess with an artificial stone mixed with an epoxy adhesive to be used for decoration or to be used for functional purposes.
도 1 : 본 발명의 성형틀에 인조석을 투입하기 직전의 상태도.1: State diagram immediately before injecting artificial stone into the molding die of the present invention.
도 2 : 도1의 성형틀을 이용하여 성형한 타일의 사시도.FIG. 2: is a perspective view of the tile shape | molded using the shaping | molding die of FIG.
도 3 : 본 발명의 다른 실시에의 타일을 성형하기 위한 상태의 분해사시도.3: An exploded perspective view of a state for forming a tile in another embodiment of the present invention.
도 4 : 도3의 성형틀을 이용하여 성형한 타일의 사시도.4: perspective view of the tile shape | molded using the shaping | molding die of FIG.
도 5 : 본 발명의 다른 실시예로서 외장재로 사용되는 대리석에 인조석을 이용하여 문양을 형성하는 상태도.5 is a state of forming a pattern using artificial stone in the marble used as an exterior material as another embodiment of the present invention.
도 6 : 본 발명의 다른 실시예로서 계단용으로 사용되는 대리석에 인조석을 이용하여 미끄럼 방지부를 형성한 상태도.6 is a state in which a non-slip part is formed using artificial stone in marble used for stairs as another embodiment of the present invention.
도 7 : 본 발명 타일의 또 다른 실시예의 분해사시도.7 is an exploded perspective view of another embodiment of the present invention tile.
도 8 : 도7의 상태에서 타일에 보강재가 접합된 상태도.8 is a state in which the reinforcing material is bonded to the tile in the state of FIG.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
(10)--인조석 (20)--성형틀(10)-Artificial Stone (20)-Plastic Mold
(30)--타일 (31)--보강테(30)-tile (31)-reinforcement frame
(32)--보강재 (40)--대리석(32)-Reinforcements (40)-Marble
Claims (6)