KR101335524B1 - UV curable fluorinated copolymer with improved adhesion property and a composition containing same, and their films containing same - Google Patents

UV curable fluorinated copolymer with improved adhesion property and a composition containing same, and their films containing same Download PDF

Info

Publication number
KR101335524B1
KR101335524B1 KR1020110035645A KR20110035645A KR101335524B1 KR 101335524 B1 KR101335524 B1 KR 101335524B1 KR 1020110035645 A KR1020110035645 A KR 1020110035645A KR 20110035645 A KR20110035645 A KR 20110035645A KR 101335524 B1 KR101335524 B1 KR 101335524B1
Authority
KR
South Korea
Prior art keywords
thin film
transparent
formula
industry
benzophenone
Prior art date
Application number
KR1020110035645A
Other languages
Korean (ko)
Other versions
KR20120118208A (en
Inventor
이수복
박인준
하종욱
김수한
이광원
이명숙
이종철
Original Assignee
한국화학연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국화학연구원 filed Critical 한국화학연구원
Priority to KR1020110035645A priority Critical patent/KR101335524B1/en
Publication of KR20120118208A publication Critical patent/KR20120118208A/en
Application granted granted Critical
Publication of KR101335524B1 publication Critical patent/KR101335524B1/en

Abstract

본 발명은 접착성이 향상된 자외선 경화 불소계 공중합체와 이를 포함하는 코팅조성물 및 이를 포함하는 막에 관한 것으로, 상세하게는 화학식 1로 표시되는 과불소 폴리에테르 변성 화합물 중 1종과 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체 1종 이상을 공중합한 공중합체를 제공한다. 본 발명에 따른 접착성이 향상된 자외선 경화 불소계 공중합체는 자외선 경화형 투명 코팅제로 사용 가능하고, 투명성, 저굴절율 및 방오성이 요구되는 각종 부품의 표면 가공 시 유용하게 사용될 수 있으며, 섬유 산업, 도료 산업, 접착제 산업, 정밀 화학 산업, 생물, 생화학 산업, 전기 전자 산업, 자동차 산업 및 금속 산업 등에서 다양한 용도로 활용 가능하다.The present invention relates to an ultraviolet curable fluorine-based copolymer with improved adhesion, a coating composition comprising the same, and a film including the same, and specifically, one of the perfluorinated polyether-modified compounds represented by Formula 1 and represented by Formula 2 Provided is a copolymer obtained by copolymerizing at least one benzophenone acrylate monomer. The UV curable fluorine-based copolymer having improved adhesion according to the present invention can be used as an ultraviolet curable transparent coating agent, and can be usefully used for the surface processing of various components requiring transparency, low refractive index and antifouling property, and the textile industry, paint industry, It can be used for various purposes in the adhesive industry, fine chemical industry, biological, biochemical industry, electric and electronic industry, automobile industry and metal industry.

Description

접착성이 향상된 자외선 경화 불소계 공중합체와 이를 포함하는 코팅조성물 및 이를 포함하는 막{UV curable fluorinated copolymer with improved adhesion property and a composition containing same, and their films containing same}UV curable fluorinated copolymer with improved adhesion property and a composition containing same, and their films containing same}

본 발명은 접착성이 향상된 자외선 경화 불소계 공중합체와 이를 포함하는 코팅조성물 및 이를 포함하는 막에 관한 것이다.
The present invention relates to an ultraviolet curable fluorine-based copolymer with improved adhesion, a coating composition comprising the same, and a film including the same.

불소계 기능성 코팅제는 저 굴절율, 고 투광성, 극히 낮은 마찰계수, 우수한 내식성 등 타 소재가 발휘할 수 없는 매우 우수한 특성을 다양하게 보유하기 때문에 반도체, 광통신, 컴퓨터 분야 등 첨단산업 분야뿐만 아니라, 가전기기, 광기억 매체 등 일상생활에 필요한 다양한 응용분야에서 차세대 핵심 소재 기술의 하나로 주목받고 있다. 최근에는 전 세계적으로 연간 수십 억대 규모인 디스플레이 산업에서 적용 및 응용이 확대되고 있고, 디스플레이를 구성하는 프레임(frame)과 전면의 화면에 대한 적용되고 있다. 특히 디스플레이 프레임에 불소계 기능성 코팅제를 적용하여 디스플레이 프레임의 사출 가공시 표면이 매우 미려한 제품들을 국내 가전업체에서 출시하여 전 세계적으로 큰 호평을 받고 있다. 반면, 광택이 우수하고 지나치게 깨끗한 표면은 지문 등의 외부 오염에 의해 훼손되면, 오히려 시각적 거부감을 주는 문제가 있다. 따라서 프레임(frame) 자체의 색상, 미려함 등은 훼손하지 않으며 시각적으로 광간섭을 일으키지 않는 수십 nm 두께인 불소계 투명 박막 코팅 소재의 개발과 적용기술이 시급히 요구되고 있다.
Since the fluorine-based functional coatings have various properties that can not be exhibited by other materials such as low refractive index, high light transmittance, extremely low friction coefficient and excellent corrosion resistance, they are used not only in high-tech industrial fields such as semiconductor, optical communication and computer, And it is attracting attention as one of the next generation core materials technology in various application fields required for daily life such as storage medium. Recently, applications and applications are expanding in the display industry, which is annually billions of years worldwide, and has been applied to the frames and front screens of the display. In particular, by applying a fluorine-based functional coating to the display frame, products with a very beautiful surface during the injection processing of the display frame are released by domestic home appliance manufacturers, and have been highly popular all over the world. On the other hand, if a surface with excellent gloss and an excessively clean surface is damaged by external pollution such as a fingerprint, there is a problem of giving a visual rejection. Accordingly, development and application of a fluorine transparent thin film coating material having a thickness of several tens of nanometers which does not damage the color and the beauty of the frame itself and which does not cause visual interference with light are urgently required.

또한 디스플레이 전면에 불소계 기능성 코팅제를 활용하는 경우의 예로써 가장 대표적으로 반사방지 코팅을 들 수 있다. 구동방식이 다른 LED, LCD, PDP, OLED와 같은 모든 디스플레이는 최종적으로 인간의 눈에 의해 감지되며, 일차적으로 기기에서 발생하는 빛은 외부의 광원인 태양 혹은 실내등과 같은 외부광원에 의해 디스플레이 표면에서 반사 혹은 간섭을 일으켜 최종적으로는 복합된 광선이 인간의 눈에 감지되게 된다. 따라서 급속히 발전하는 디스플레이의 구동방식에 관계없이 디스플레이 표면의 외부광원에 대한 반사방지층 소재 및 적용기술은 디스플레이의 좀 더 나은 화질과 시야를 확보함으로써 디스플레이의 부가가치를 높이기 위해 반드시 필요하다.
Also, as an example of the case where a fluorine functional coating agent is used on the front surface of a display, antireflection coating is most representative. All displays such as LEDs, LCDs, PDPs, and OLEDs with different driving methods are finally detected by the human eye, and the light emitted from the device is first displayed on the display surface by an external light source such as the sun or an indoor light. It causes reflection or interference, and finally the combined rays are perceived by the human eye. Thus, anti-reflective layer materials and application techniques for external light sources of the display surface, regardless of how rapidly the display is driven, are essential to increase the value of the display by ensuring a better picture quality and field of view of the display.

디스플레이에 있어서 반사방지층은 통상적으로 디스플레이 디바이스(Device) 외곽에 위치하며, 폴리에스테르(PET), 트리아세테이트셀룰로스(TAC) 등과 같은 투명한 베이스 필름(base film), 액정을 보호하고 평판화하기 위한 10 ~ 20 μm 두께의 하드코팅층, 외부 광간섭을 상쇄시켜 선명한 화질을 제공하기 위한 각각 λ/4 두께 (약 100 nm)의 저 굴절율/고 굴절율 복합층 또는 저 굴절율 단일 반사방지층 및 최외곽에 광반사 및 간섭을 최소화하고 오염을 방지하기 위한 10~20 nm 두께의 오염방지층(방오층)으로 구성하는 것이 일반적이다. 이때, 굴절율이 1.40 이하인 저 굴절율 층과 최외곽 표면의 오염방지층의 경우 타 소재로 대체가 불가능하여 기능성 불소화합물을 사용하여 제조되고 있다. 또한 반사방지층의 성능을 좌우하는 주요인자로는 외부로부터 추가적인 오염박막을 형성하지 않고, 형성된 오염층도 쉽게 제거할 수 있는 특성이 중요하다. 즉, 투명한 광학 반사방지층에 있어서 표면의 오염방지 및 제거기능은 제품의 외관 및 성능을 좌우하는 중요한 인자로써, 이를 해결·개선하려는 산업적 요구가 매우 크다.
In the display, the antireflection layer is typically located outside the display device and includes a transparent base film such as polyester (PET), triacetate cellulose (TAC), etc., a protective film for protecting and flattening the liquid crystal, A hard coating layer having a thickness of 20 占 퐉, a low refractive index / high refractive index composite layer or a low refractive index single antireflection layer of? / 4 thickness (about 100 nm) to provide clear image quality by canceling external light interference, It is common to construct a 10-20 nm thick antifouling layer (antifouling layer) to minimize interference and prevent contamination. In this case, the low refractive index layer having a refractive index of 1.40 or less and the antifouling layer on the outermost surface are not replaceable with other materials, and are manufactured using a functional fluorine compound. It is also important that the characteristic of the antireflection layer that can easily remove the contaminant layer formed without forming an additional contaminated thin film from the outside is the important factor that determines the performance of the antireflection layer. That is, in the transparent optical anti-reflection layer, contamination prevention and removal of the surface are important factors that influence the appearance and performance of the product, and there is a great industrial demand for solving and improving this.

불소는 전자밀도가 높고 수소원자 다음으로 원자 반경이 작으며 또한 강한 전기 음성도를 갖고 있으므로 견고한 탄소-불소 결합을 형성한다. 이러한 불화탄소 화합물의 특성 때문에 과불소 알킬기를 포함하는 단량체는 임계표면장력이 6-8 dynes/cm 정도이고, 이와 같이 매우 낮은 표면에너지로 인하여 물과 기름에 매우 큰 접촉각을 나타낸다. 이에 따라 불소계 화합물은 비교적 고가임에도 불구하고 화학적 안정성, 내열성, 내후성 등이 탁월하여 고부가 가치의 수지 및 필름, 윤활제, 도료 등에 사용하고 있으며, 비 점착성, 낮은 표면에너지, 발수성, 낮은 굴절률 등의 특성이 필요한 오염방지제, 광학소재, 기능성 염료, 전자 소재 등으로 사용 영역이 확대되고 있다.
Fluorine forms a strong carbon-fluorine bond because it has a high electron density, a small atomic radius next to hydrogen atoms, and strong electronegativity. Due to the characteristics of the fluorocarbon compound, the monomer containing a perfluorinated alkyl group has a critical surface tension of about 6-8 dynes / cm, and thus has a very large contact angle with water and oil due to the very low surface energy. Accordingly, the fluorine-based compounds are excellent in chemical stability, heat resistance and weather resistance, and are used for resins, films, lubricants, and paints of high added value, and have properties such as non-tackiness, low surface energy, water repellency and low refractive index The use area is expanding as required antifouling agents, optical materials, functional dyes, and electronic materials.

하지만 대표적인 저 굴절율 및 저에너지 표면을 형성하는 물질인 과불소알킬 화합물에서 유래되는 코팅제는 초기 오염방지성은 우수하나 오염제거성이 불량하고, 과불소알킬 화합물을 활용한 대표적인 아크릴레이트인 F(CF2)7CH2CH=CH2 단중합체 및 F(CF2)5CH2CH=CH2 단중합체의 경우 각각 1.3390와 1.3560 정도인 비교적 낮은 굴절율을 나타내지만, 측쇄에 의한 결정구조 때문에 빛에 대한 투광성이 좋지 않다. 또한 과불소화합물의 경우 자체의 표면에너지가 낮고, 표면이 비활성을 띠기 때문에 금속, 무기물 또는 플라스틱과 같이 기재를 이루는 물질과의 접착력이 좋지 않기 때문에 우수한 물성을 보유함에도 불구하고 표면 코팅제로써 그 사용이 제한적이었다.
However, the coating agent derived from the perfluoroalkyl compound, which is a material that forms a low refractive index and a low energy surface, is excellent in initial contamination prevention but poor in decontamination, and is a representative acrylate using a perfluoroalkyl compound, F (CF 2 ) 7 CH 2 CH = CH 2 homopolymers and F (CF 2 ) 5 CH 2 CH = CH 2 homopolymers have relatively low refractive indices of about 1.3390 and 1.3560, respectively, but the light-transmitting property is due to the crystal structure of the side chains. Not good. In addition, the perfluorocompounds have low surface energy and have ineffective surface. Therefore, the perfluorocompound is used as a surface coating agent even though it possesses good physical properties because it has poor adhesion to materials such as metals, minerals or plastics. It was limited.

이러한 표면오염 제거성 및 광학물성 면에서 과불소알킬 화합물의 단점을 극복할 수 있는 대체 가능성이 큰 화합물로써 과불소폴리에테르 화합물을 들 수 있다. 과불소폴리에테르 화합물은 과불소알킬 화합물의 저 표면에너지 표면 특성에 더해서 탁월한 유연성, 오염방지성 및 윤활성에서 유래되는 오염제거성을 보유한다. 또한 박막형성시 비결정성 특성을 가지며 투명성, 저 굴절율 특성 [poly(hexafluoro- propylene oxide), n D = 1.3010, T300 ~800 nm > 95 %] 등 매우 우수한 광학물성을 보유한다. 반면에 물리적 특성 면에서는 거의 전 분자량 영역에서 액상을 유지하기 때문에 고상박막을 형성하고 활용하기 어려운 문제가 있다.
In view of such surface decontamination properties and optical properties, a perfluoropolyether compound is a compound having a high possibility of overcoming the disadvantages of the perfluoroalkyl compound. Perfluoropolyether compounds possess decontamination properties derived from superior flexibility, anti-fouling and lubricity in addition to the low surface energy surface properties of perfluoroalkyl compounds. In addition, it possesses amorphous properties when forming a thin film and possesses excellent optical properties such as transparency and low refractive index [poly (hexafluoropropylene oxide), n D = 1.3010, T 300 to 800 nm > 95%]. On the other hand, in terms of physical properties, there is a problem that it is difficult to form and utilize a solid-phase thin film because it maintains a liquid phase in an almost whole molecular weight region.

이에 본 발명자들은 박막형성이 용이하고, 낮은 굴절율 및 내오염성을 나타내는 박막을 제조하는 방법을 연구하던 중, 과불소 폴리에테르계 아크릴레이트 단량체와 자외선 경화가 가능한 벤조페논계 단량체를 공중합하여 접착성이 향상된 자외선 경화 불소계 공중합체를 개발하고, 본 발명을 완성하였다.
The inventors of the present invention, while studying a method for producing a thin film that is easy to form a thin film and exhibits a low refractive index and fouling resistance, the copolymerization of the perfluorinated polyether acrylate monomer and the benzophenone monomer capable of UV curing adhesiveness An improved ultraviolet curing fluorine-based copolymer was developed and the present invention was completed.

본 발명의 목적은 접착성이 향상된 자외선 경화 불소계 공중합체와 이를 포함하는 코팅조성물 및 이를 포함하는 막을 제공하는 데 있다.SUMMARY OF THE INVENTION An object of the present invention is to provide a UV-curable fluorine-based copolymer with improved adhesion, a coating composition including the same, and a film including the same.

상기 목적을 달성하기 위하여, 본 발명은 하기 화학식 1로 표시되는 과불소 폴리에테르 변성 화합물 중 1종과 하기 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체 1종 이상을 공중합한 공중합체를 제공한다;
In order to achieve the above object, the present invention provides a copolymer obtained by copolymerizing one or more of the perfluoropolyether-modified compound represented by the following formula (1) and at least one benzophenone-based acrylate monomer represented by the following formula (2);

<화학식 1>&Lt; Formula 1 >

CF3CF2CF2-O-CF(CF3)-X-Y-X-CZ=CH2, CF3CF2CF2-O-CF(CF3)-Y-X-CZ=CH2 CF 3 CF 2 CF 2 -O-CF (CF 3 ) -XYX-CZ = CH 2 , CF 3 CF 2 CF 2 CF 2 -O-CF (CF 3 ) -YX-CZ = CH 2

(상기 화학식 1에서 X는 에스테르, 우레탄, 에테르 또는 아미드 연결기를 나타내고, Y는 탄소수 0~5의 알킬기를 나타내며, Z는 수소, 염소, 불소 또는 탄소수 1~5의 알킬기를 나타낸다)
(In Formula 1, X represents an ester, urethane, ether or amide linking group, Y represents an alkyl group having 0 to 5 carbon atoms, and Z represents hydrogen, chlorine, fluorine or an alkyl group having 1 to 5 carbon atoms.)

<화학식 2>(2)

Figure 112011028477655-pat00001
Figure 112011028477655-pat00001

(상기 화학식 2에서 X는 할로겐, 수소 또는 탄소수 1~4의 알킬기를 나타내고, Y는 에스테르 연결기, 아미드 연결기, 또는 우레탄 연결기를 나타내며, Z는 탄소수 1 ~ 10의 알킬기를 나타내고, A는 하기 구조식 1로 표시되는 UV 경화가 가능한 벤조페논계 단위체(unit) 중 1종을 나타낸다)
(In Formula 2, X represents a halogen, hydrogen, or an alkyl group having 1 to 4 carbon atoms, Y represents an ester linking group, an amide linking group, or a urethane linking group, Z represents an alkyl group having 1 to 10 carbon atoms, and A represents the following structural formula 1 Represents one kind of benzophenone-based units capable of UV curing represented by

<구조식 1><Structure 1>

Figure 112011028477655-pat00002
,
Figure 112011028477655-pat00003
,
Figure 112011028477655-pat00004
,
Figure 112011028477655-pat00005
,
Figure 112011028477655-pat00006
.
Figure 112011028477655-pat00002
,
Figure 112011028477655-pat00003
,
Figure 112011028477655-pat00004
,
Figure 112011028477655-pat00005
,
Figure 112011028477655-pat00006
.

본 발명에 따른 접착성이 향상된 자외선 경화 불소계 공중합체는 자외선 경화형 투명 코팅제로 사용 가능하고, 투명성, 저굴절율 및 방오성이 요구되는 각종 부품의 표면 가공 시 유용하게 사용될 수 있으며, 섬유 산업, 도료 산업, 접착제 산업, 정밀 화학 산업, 생물, 생화학 산업, 전기 전자 산업, 자동차 산업 및 금속 산업 등에서 다양한 용도로 활용 가능하다.
The UV curable fluorine-based copolymer having improved adhesion according to the present invention can be used as an ultraviolet curable transparent coating agent, and can be usefully used for the surface processing of various components requiring transparency, low refractive index and antifouling property, and the textile industry, paint industry, It can be used for various purposes in the adhesive industry, fine chemical industry, biological, biochemical industry, electric and electronic industry, automobile industry and metal industry.

도 1은 본 발명에 따른 투명 박막의 투명도를 측정한 그래프이고;
도 2는 본 발명에 따른 투명 박막의 반사율을 측정한 그래프이다.1 is a graph measuring the transparency of a transparent thin film according to the present invention;
Figure 2 is a graph measuring the reflectance of the transparent thin film according to the present invention.

본 발명은 하기 화학식 1로 표시되는 과불소 폴리에테르 변성 화합물 중 1종과 하기 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체 1종 이상을 공중합한 공중합체를 제공한다;
The present invention provides a copolymer obtained by copolymerizing one or more of the perfluoropolyether-modified compound represented by the following Chemical Formula 1 with one or more benzophenone acrylate monomers represented by the following Chemical Formula 2;

<화학식 1>&Lt; Formula 1 >

CF3CF2CF2-O-CF(CF3)-X-Y-X-CZ=CH2, CF3CF2CF2-O-CF(CF3)-Y-X-CZ=CH2 CF 3 CF 2 CF 2 -O-CF (CF 3 ) -XYX-CZ = CH 2 , CF 3 CF 2 CF 2 CF 2 -O-CF (CF 3 ) -YX-CZ = CH 2

(상기 화학식 1에서 X는 에스테르, 우레탄, 에테르 또는 아미드 연결기를 나타내고, Y는 탄소수 0~5의 알킬기를 나타내며, Z는 수소, 염소, 불소 또는 탄소수 1~5의 알킬기를 나타낸다)
(In Formula 1, X represents an ester, urethane, ether or amide linking group, Y represents an alkyl group having 0 to 5 carbon atoms, and Z represents hydrogen, chlorine, fluorine or an alkyl group having 1 to 5 carbon atoms.)

<화학식 2>(2)

Figure 112011028477655-pat00007
Figure 112011028477655-pat00007

(상기 화학식 2에서 X는 할로겐, 수소 또는 탄소수 1~4의 알킬기를 나타내고, Y는 에스테르 연결기, 아미드 연결기, 또는 우레탄 연결기를 나타내며, Z는 탄소수 1 ~ 10의 알킬기를 나타내고, A는 하기 구조식 1로 표시되는 UV 경화가 가능한 벤조페논계 단위체(unit) 중 1종을 나타낸다)
(In Formula 2, X represents a halogen, hydrogen, or an alkyl group having 1 to 4 carbon atoms, Y represents an ester linking group, an amide linking group, or a urethane linking group, Z represents an alkyl group having 1 to 10 carbon atoms, and A represents the following structural formula 1 Represents one kind of benzophenone-based units capable of UV curing represented by

<구조식 1><Structure 1>

Figure 112011028477655-pat00008
,
Figure 112011028477655-pat00009
,
Figure 112011028477655-pat00010
,
Figure 112011028477655-pat00011
,
Figure 112011028477655-pat00012
.
Figure 112011028477655-pat00008
,
Figure 112011028477655-pat00009
,
Figure 112011028477655-pat00010
,
Figure 112011028477655-pat00011
,
Figure 112011028477655-pat00012
.

이하, 본 발명을 상세히 설명한다.
Hereinafter, the present invention will be described in detail.

본 발명은 상기 화학식 1로 표시되는 과불소 폴리에테르 변성 아크릴레이트 중 1종과 상기 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체의 공중합체를 제공한다. 본 발명에 따른 상기 혼합물은 기재(substrate)에 코팅 후 UV 경화하여 투명 박막을 형성할 수 있고, 제조된 투명 박막은 저 굴절율, 방오, 발수, 발유 및 우수한 오염제거성을 나타낼 수 있으며, 기재 본래의 색상 및 경도와 같은 특성 훼손이 발생하지 않는다. The present invention provides a copolymer of one of the perfluorinated polyether modified acrylates represented by Formula 1 and the benzophenone-based acrylate monomers represented by Formula 2. The mixture according to the present invention may be coated on a substrate (substrate) and then UV cured to form a transparent thin film, the prepared transparent thin film may exhibit low refractive index, antifouling, water repellent, oil repellent and excellent decontamination properties, No deterioration of properties such as the color and hardness of the.

본 발명에 따른 상기 공중합체는 상기 화학식 1로 표시되는 과불소 폴리에테르 변성 아크릴레이트와 상기 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체의 물질 및 조성을 적절히 조정하여 형성되는 투명 박막의 굴절율을 조절할 수 있다.The copolymer according to the present invention can adjust the refractive index of the transparent thin film formed by appropriately adjusting the material and composition of the perfluorinated polyether modified acrylate represented by Formula 1 and the benzophenone-based acrylate monomer represented by Formula 2 have.

본 발명에 따른 상기 공중합체에 있어서, 상기 화학식 1로 표시되는 과불소 폴리에테르 변성 화합물은 박막에 발수, 발유, 방오성, 오염제거성 등을 부여할 수 있고, 사용용도에 따라 상기 화학식 1의 과불소 폴리에테르 변성 화합물의 화합물 및 분자량을 선택하여 합성할 수 있다. In the copolymer according to the present invention, the perfluorinated polyether-modified compound represented by Chemical Formula 1 may impart water repellency, oil repellency, antifouling property, decontamination property, etc. to the thin film. The compound and molecular weight of the small polyether-modified compound can be selected and synthesized.

과불소 폴리에테르 화합물의 합성은 하기와 같은 공지된 방법으로 수행될 수 있다 [JAMES T. HILL, J. Macromol. Sci. Chem. , A8, (3), p499 (1974)]. 즉, 헥사 플루오르 프로필렌 옥사이드(HFPO)와 세슘 플루오라이드를 용매에 넣어 혼합한다. 이때, 상기 용매는 당 분야에서 일반적으로 사용되는 것으로 특별히 한정하지 않으나, 예를 들어, 트리글리메, 테트라글리메, 부틸디글리메, 에틸디글리메 등의 용매 중 1종 이상을 선택하여 사용할 수 있다. 상기 방법으로 합성된 과불소 폴리에테르 화합물의 중합도(분자량)는 HFPO의 주입 속도, HFPO 주입량 및 세슘 플루오라이드의 비, 그리고 반응 온도에 의해서 제어될 수 있다. Synthesis of the perfluorinated polyether compound can be carried out by a known method as described in JAMES T. HILL, J. Macromol. Sci. Chem. , A8, (3), p 499 (1974)]. That is, hexa fluoro propylene oxide (HFPO) and cesium fluoride are mixed in a solvent. In this case, the solvent is generally used in the art, and is not particularly limited. For example, one or more solvents such as triglyme, tetraglyme, butyl diglyme, and ethyl diglyme may be selected and used. have. The degree of polymerization (molecular weight) of the perfluorinated polyether compound synthesized by the above method can be controlled by the injection rate of HFPO, the HFPO injection amount and the ratio of cesium fluoride, and the reaction temperature.

또한 상기 방법으로 합성된 과불소 폴리에테르 화합물은 말단기를 변환시킴으로써 아크릴레이트로 변환될 수 있고, 예를 들어 과불소폴리에테르 화합물과 2-하이드록시 에틸 메타아크릴레이트(2-hydroxy ethyl methacrylate)의 축합반응에 의해 상기 화학식 1의 과불소 폴리에테르 변성화합물을 합성할 수 있다. 이때, 상기 과불소 폴리에테르 화합물의 변환방법은 이에 제한되는 것은 아니고, 공지된 방법 중 적절한 방법을 택하여 수행될 수 있다.In addition, the perfluorinated polyether compound synthesized by the above method may be converted into an acrylate by converting an end group, for example, of the perfluoropolyether compound and 2-hydroxy ethyl methacrylate. By the condensation reaction, the perfluorinated polyether-modified compound of Chemical Formula 1 may be synthesized. In this case, the method of converting the perfluorinated polyether compound is not limited thereto, and may be performed by selecting an appropriate method from among known methods.

본 발명에 따른 상기 공중합체에 있어서, 상기 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체는 UV조사를 통한 광 경화에 의해 경화될 수 있어, 상기 화학식 1의 과불소 폴리에테르 변성 화합물과 공중합함으로써 본 발명에 따른 상기 공중합체가 광경화에 의해 경화될 수 있게 한다. 이때, 상기 벤조페논계 아크릴레이트 단량체 1종 또는 2종 이상이 화학식 1의 과불소 폴리에테르 변성 화합물과 공중합될 수 있으며, 상기 과불소 폴리에테르 변성 아크릴레이트와 벤조페논계 단량체의 공중합체 합성시 벤조페논계 아크릴레이트 단량체의 조성은 0.01 ~ 15 중량%의 비율로 혼합·반응시키는 것이 바람직하다. 상기 벤조페논계 아크릴레이트 단량체의 조성이 상기 범위를 벗어나는 경우에는 본 발명에 따른 공중합체가 높은 굴절율을 나타내는 문제가 있고, 내오염성이 저하되는 문제가 있다.
In the copolymer according to the present invention, the benzophenone-based acrylate monomer represented by Chemical Formula 2 may be cured by photocuring through UV irradiation, and may be copolymerized with the perfluorinated polyether-modified compound of Chemical Formula 1 The copolymer according to the invention allows to be cured by photocuring. In this case, one or two or more of the benzophenone acrylate monomers may be copolymerized with the perfluorinated polyether modified compound of Formula 1, and benzo when synthesizing a copolymer of the perfluorinated polyether modified acrylate and the benzophenone monomer It is preferable to mix and react the composition of a phenone acrylate monomer in the ratio of 0.01-15 weight%. When the composition of the benzophenone acrylate monomer is out of the above range, there is a problem that the copolymer according to the present invention exhibits a high refractive index, and the pollution resistance is lowered.

본 발명에 따른 상기 공중합체는 투명하고 통상적인 저 굴절율 화합물의 기준인 1.40 미만의 굴절율을 나타내고, 일례로 하기 화학식 3으로 표시되는 과불소폴리에테르 변성 아크릴레이트 화합물과 벤조페논계 아크릴레이트 단량체를 공중합시켜 제조될 수 있다.
The copolymer according to the present invention exhibits a refractive index of less than 1.40, which is a standard for transparent and conventional low refractive index compounds, and copolymerizes a perfluoropolyether-modified acrylate compound and a benzophenone-based acrylate monomer represented by Formula 3, for example. Can be prepared.

<화합물 3><Compound 3>

CF3CF2CF2-O-CF(CF3)-COO-CH2CH2-COO-CH(CH3)=CH2
CF 3 CF 2 CF 2 -O-CF (CF 3 ) -COO-CH 2 CH 2 -COO-CH (CH 3 ) = CH 2

본 발명에 따른 상기 공중합체의 공중합 반응은 일반적인 고분자 라디칼 반응인 벌크 중합, 용액중합, 에멀젼 중합 기술 등을 이용하여 수행될 수 있으며, 제조된 공중합체의 분자량은 무게평균 분자량으로 500 ~ 500,000의 범위로 제조된다. 본 발명에 따른 공중합체의 분자량이 무게평균 분자량으로 500 미만인 경우에는 코팅시 점도가 낮아 100 nm 이하의 균일한 박막을 제조하기 어려운 문제가 있고, 이에 따라 투명성, 저굴절율, 방오성 등의 특성이 발현되지 않는 문제가 있다. 또한 본 발명에 따른 공중합체의 분자량이 무게평균 분자량으로 500,000을 초과하는 경우에는 용매로의 용해가 어렵고, 점도가 지나치게 높아 표면 물성을 제어하기 어려워 방소성 특성을 발현하는 박막을 제조할 수 없는 문제가 있다.
Copolymerization of the copolymer according to the present invention can be carried out using a common polymer radical reaction, bulk polymerization, solution polymerization, emulsion polymerization technology, the molecular weight of the prepared copolymer is a weight average molecular weight in the range of 500 ~ 500,000 Is manufactured. When the molecular weight of the copolymer according to the present invention has a weight average molecular weight of less than 500, there is a problem in that it is difficult to produce a uniform thin film having a thickness of 100 nm or less due to low viscosity at the time of coating. There is no problem. In addition, when the molecular weight of the copolymer according to the present invention exceeds the weight average molecular weight of 500,000, it is difficult to dissolve in a solvent, the viscosity is too high to control the surface properties, it is difficult to produce a thin film that exhibits anti-fogging properties There is.

본 발명에 따른 상기 공중합체는 코팅 경화시 표면이행성이 탁월하여 저에너지 표면개질 효과가 우수하고, 오염방지성과 오염물질의 제거가 용이한 박막을 제조할 수 있다. 또한 제조된 박막이 투명하고 저 굴절율을 나타낼 수 있게 한다. 특히, 본 발명에 따른 상기 공중합체는 UV 경화에 의해 가교 결합기를 조절하여 경화될 수 있어 기재와의 밀착력이 우수하고, 저 굴절율을 유지할 수 있으며, 방오, 발수, 발유 및 오염제거 성능이 우수하고 투명도가 매우 높은 박막을 제조할 수 있다.
The copolymer according to the present invention can produce a thin film that is excellent in low energy surface modification effect and excellent in anti-pollution and easy to remove contaminants due to excellent surface migration during coating curing. Further, the produced thin film is transparent and can exhibit a low refractive index. In particular, the copolymer according to the present invention can be cured by adjusting the cross-linking group by UV curing, excellent adhesion to the substrate, can maintain a low refractive index, excellent antifouling, water repellent, oil repellent and decontamination performance It is possible to produce thin films with very high transparency.

또한, 본 발명은 상기 과불소 폴리에테르 변성 아크릴레이트와 벤조페논계 아크릴레이트 단량체의 공중합체 및 용제를 포함하는 투명 코팅제 조성물을 제공한다. 상기 투명 코팅제 조성물은 용제를 포함함으로써 용액공정을 통한 코팅이 용이하고, 이에 따라 박막으로의 제조가 간단한 장점이 있다.The present invention also provides a transparent coating composition comprising a copolymer and a solvent of the perfluorinated polyether-modified acrylate and the benzophenone acrylate monomer. The transparent coating composition is easy to coat through a solution process by including a solvent, accordingly has the advantage of simple manufacturing to a thin film.

이때, 상기 용제는 과불소 헵탄, 과불소 헥산, m-키시렌헥사 플로오라이드, 벤조트리플루오라이드, 메틸 과불소 부틸 에테르, 에틸 과불소 부틸 에테르, 과불소(2－부틸 테트라 하이드로 퓨란), 석유 벤젠, 미네랄 스피리츠, 이소 파라핀, 톨루엔, 크실렌, 아세톤, 메틸 에틸 케톤, 메틸 이소 부틸 케톤 및 시클로헥사논으로 이루어진 군으로부터 선택되는 1종 또는 2종 이상의 혼합물인 것이 바람직하나, 이에 제한되는 것은 아니다.
At this time, the solvent is perfluoro heptane, perfluoro hexane, m-xylene hexafluoride, benzotrifluoride, methyl perfluorine butyl ether, ethyl perfluorine butyl ether, perfluorine (2-butyl tetrahydrofuran), It is preferably, but not limited to, one or more mixtures selected from the group consisting of petroleum benzene, mineral spirits, isoparaffin, toluene, xylene, acetone, methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone. .

본 발명은 상기 투명 코팅제 조성물을 기판 상부로 코팅한 후 이를 경화시켜 제조되는 투명 박막을 제공한다. The present invention provides a transparent thin film prepared by coating the transparent coating composition on the substrate and then curing it.

본 발명에 따른 상기 투명 박막은 저 굴절율 및 발수, 발유, 오염제거성 등의 특성이 우수하고, 이때, 상기 투명 박막은 스핀 코팅, 침적 코팅, 커텐 코팅, 스프레이 코팅에 의해 코팅되어 제조될 수 있으나, 이에 제한되는 것은 아니다.The transparent thin film according to the present invention has excellent properties such as low refractive index and water repellency, oil repellency, decontamination property, and at this time, the transparent thin film may be prepared by coating by spin coating, dip coating, curtain coating, spray coating, However, the present invention is not limited thereto.

또한, 본 발명에 따른 상기 투명 박막의 두께는 5 내지 2000 nm 인 것이 바람직하다. 만약 상기 투명 박막의 두께가 5 nm 미만인 경우에는 물 또는 기름에 대한 방오성이 발현되지 않는 문제가 있고, 상기 투명 박막의 두께가 2000 nm를 초과하는 경우에는 경화 시 충분한 경화가 일어나지 않아 박막의 기계적 강도가 저하되고, 불균일한 코팅에 의한 간섭무늬가 발생되는 문제가 있다.In addition, the thickness of the transparent thin film according to the present invention is preferably 5 to 2000 nm. If the thickness of the transparent thin film is less than 5 nm, there is a problem in that antifouling properties against water or oil are not expressed. If the thickness of the transparent thin film exceeds 2000 nm, sufficient curing does not occur during curing, and thus the mechanical strength of the thin film is reduced. Is lowered, and there is a problem that interference fringes are generated due to uneven coating.

본 발명에 따른 상기 투명 박막은 투명한 유리 제품 또는 플라스틱 제품의 표면에 투명성을 유지함과 동시에 방오성, 오염제거성, 반사방지성 등을 부여할 수 있어, 디스플레이의 프레임, 렌즈, 유리창, 액정 또는 평판표시소자(PDP), 유기발광소자(EL) 및 전계방출디스플레이(FED)를 포함하는 평판 디스플레이의 오염방지 및 반사방지 투명막 또는 이들의 광학 필터로 이용될 수 있으며, 일반 가정용 유리, 산업용 유리, 건축 외장재, 미술용품 등 다양한 분야에 적용할 수 있다.
The transparent thin film according to the present invention can impart antifouling property, decontamination property, antireflection property, etc. while maintaining transparency on the surface of a transparent glass product or a plastic product, and can display a frame, a lens, a glass window, a liquid crystal display, or a flat panel display. It can be used as anti-pollution and anti-reflection transparent film or optical filter thereof for flat panel display including element (PDP), organic light emitting element (EL) and field emission display (FED), and can be used for general household glass, industrial glass, construction It can be applied to various fields such as exterior materials and art supplies.

이하, 본 발명을 실시예를 통해 보다 구체적으로 설명한다. 그러나, 하기 실시예는 본 발명을 설명하기 위한 것일 뿐, 하기 실시예에 의하여 본 발명의 권리범위가 한정되는 것은 아니다.
Hereinafter, the present invention will be described more specifically by way of examples. However, the following examples are intended to illustrate the present invention, but the scope of the present invention is not limited by the following examples.

<제조예 1> 과불소 폴리에테르 변성 화합물의 제조Preparation Example 1 Preparation of Perfluorinated Polyether Modified Compound

단계 1: 교반기, 냉각 자켓, 온도계, 압력계가 달린 스테인레스제 고압반응기에 테트라글리메 2.49 g, 불화세슘 1.69 g, 헥사플루오르 프로필렌(HFP) 87.75 g 및 헥사플루오르 프로필렌 옥사이드 420 g을 투입하고, 5 ℃의 온도에서 반응시켜 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머를 얻었다. 이때, 총 반응 시간은 8시간이었다.
Step 1: A stainless high pressure reactor with a stirrer, a cooling jacket, a thermometer and a pressure gauge was charged with 2.49 g of tetraglyme, 1.69 g of cesium fluoride, 87.75 g of hexafluoropropylene (HFP), and 420 g of hexafluoropropylene oxide, followed by 5 ° C. The reaction was carried out at a temperature of to obtain a hexafluoro propylene oxide (HFPO) oligomer. At this time, the total reaction time was 8 hours.

단계 2: 상기 단계 1에서 제조된 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머를 내경 4 cm, 길이 80 cm의 초자 증류탑을 이용해 상압증류하여 과불소 폴리에테르-COF 이량체(dimer)를 제조하였고, 이때의 증류온도는 52 ~ 54 ℃였다.
Step 2: The hexafluoro propylene oxide (HFPO) oligomer prepared in step 1 was distilled under atmospheric pressure using a vitreous distillation column having an inner diameter of 4 cm and a length of 80 cm to prepare a perfluorinated polyether-COF dimer. Distillation temperature was 52 ~ 54 ℃.

단계 3: 마그네틱 바(Magnetic bar), 버블트랩(bubble trap)이 장착된 3-neck 플라스크에 상기 단계 2에서 제조된 과불소 폴리에테르-COF 이량체(dimer) 100.0 g(0.30 mol)을 넣은 후 상온에서 교반하며 2-하이드록시 에틸 메타아크릴레이트(2-hydroxy ethyl methacrylate, HEMA) 46.99 g(0.36 mol)를 서서히 투입하였다. 이때, 기체 발생 여부를 버블트랩(bubble trap)을 통해 확인하였고, 용액의 색이 2-하이드록시 에틸 메타아크릴레이트가 투입된 후 점차 반투명한 흰색을 나타내는 것을 확인하였다. 이후 24시간 동안 교반을 수행하여 반응을 완료시켰고, 반응액에 냉매(Freon-113)를 추가하였으며, 이때 pH 시험지를 통해 반응액이 pH 3 ~ 4 정도의 산성임을 확인하였다. 또한, 미 반응물과 배출되지 않은 불산(HF)을 제거하기 위해 탄산수소나트륨(NaHCO3) 포화용액을 반응액의 pH가 7이 될 때까지 투입하고 교반하였다. 교반을 수행한 후 반응액이 층 분리되는 것을 확인하였고, 하부의 아크릴레이트 변형 단량체를 분리하였다. 분리된 아크릴레이트 변형 단량체에 증류수를 추가하고, 층 분리작업을 3회 반복하여 불순물을 제거하였고, 아크릴레이트 변형 단량체의 수분제거를 위하여 황산마그네슘(MgSO4)을 다량 첨가한 후 필터링하였다. 나아가, 최종 반응물에 잔존하는 휘발성 물질을 제거하기 위해 마그네틱 바를 넣고 교반하면서 5 ~ 10 분 감압시켰고, 최종 합성된 과불소 폴리에테르 변성 아크릴레이트는 투명한 액상으로 제조되었다.
Step 3: 100.0 g (0.30 mol) of the perfluorinated polyether-COF dimer prepared in Step 2 was added to a 3-neck flask equipped with a magnetic bar and a bubble trap. While stirring at room temperature, 46.99 g (0.36 mol) of 2-hydroxy ethyl methacrylate (HEMA) was slowly added thereto. At this time, it was confirmed whether the gas is generated through a bubble trap (bubble trap), the color of the solution was confirmed that after the addition of 2-hydroxy ethyl methacrylate gradually appeared translucent white. After the reaction was completed for 24 hours to complete the reaction, the refrigerant (Freon-113) was added to the reaction solution, at this time it was confirmed by the pH test paper that the reaction solution pH 3 ~ 4 acidic. In addition, a saturated sodium bicarbonate (NaHCO 3 ) solution was added and stirred until the pH of the reaction solution was reached to remove unreacted material and hydrofluoric acid (HF). After performing stirring, it was confirmed that the reaction solution was separated into layers, and the lower acrylate-modified monomer was separated. Distilled water was added to the separated acrylate-modified monomer, and the layer separation was repeated three times to remove impurities, and then filtered after adding a large amount of magnesium sulfate (MgSO 4 ) to remove water from the acrylate-modified monomer. Furthermore, to remove the volatiles remaining in the final reactant, a magnetic bar was added thereto, and the pressure was reduced for 5 to 10 minutes while stirring. The final synthesized perfluorinated polyether modified acrylate was prepared in a transparent liquid phase.

<제조예 2> 벤조페논계 아크릴레이트 단량체의 제조 1Preparation Example 2 Preparation of Benzophenone Acrylate Monomer 1

건조 질소 분위기 하에서 빙점조(ice bath)로 냉각하며 4-하이드록시벤조페논(4-hydroxybenzophenone) 19.8 g(0.1 mol), 트리에틸아민(triethylamine) 11.1 g (0.11 mol) , CH2Cl2 용액 100 mL로 아크릴로일 클로라이드(acryloyl chloride) 7.85 g(0.1 mol) 및 CH2Cl2 용액 50 mL를 첨가하였다. 이 후 혼합물을 상온까지 승온시킨후 24 시간 동안 교반하여 반응시켰다. 반응이 완료된 후 반응물을 1/2 포화 탄산수소나트륨(NaHCO3)용액, 1N 염산(HCl) 및 물을 이용하여 각각 3회 세정한 후 황산마그네슘(MgSO4)으로 건조하고 여과하여 용매 및 수분을 제거하여 N-(4-벤조일-페닐)-아크릴에스테르(N-(4-benzoyl-phenyl)-acrylester, BPA)를 제조하였다. 이때의 수율은 약 19.1 g(76%)이었다.
Cooled in an ice bath under a dry nitrogen atmosphere, 19.8 g (0.1 mol) of 4-hydroxybenzophenone, 11.1 g (0.11 mol) of triethylamine, CH 2 Cl 2 solution 100 To the mL was added 7.85 g (0.1 mol) of acryloyl chloride and 50 mL of CH 2 Cl 2 solution. Thereafter, the mixture was heated to room temperature and reacted for 24 hours with stirring. After the reaction was completed, the reaction product was washed three times with 1/2 saturated sodium hydrogen carbonate (NaHCO 3 ) solution, 1N hydrochloric acid (HCl) and water, dried over magnesium sulfate (MgSO 4 ), filtered, and the solvent and water were washed. N- (4-benzoyl-phenyl) -acrylester (BPA) was prepared by removal. The yield was about 19.1 g (76%).

<실시예 1> 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴레이트 단량체의 공중합체 제조Example 1 Preparation of Copolymer of Perfluorinated Polyether Modified Compound with Benzophenone-Based Acrylate Monomer

상기 제조예 1에서 제조된 과불소 폴리에테르 변성 화합물 10.55 g(0.024 mol), 상기 제조예 2에서 제조된 벤조페논계 아크릴레이트 단량체 0.3g (1.19x10-3mol), n-옥탄티올(n-octanethiol) 0.1095 g(7.5x10-4mol) 및 라디칼 개시제인 아조비스이소부틸로나이트릴(Azobisisobutyronitrile, AIBN) 0.1085 g(6.16x10-4mol)을 43.39 g의 트리플루오로 톨루엔으로 첨가하여 용해시켰다. 상기 혼합물로 동결/해동 싸이클(freeze-thaw cycle)을 3회 반복하여 수행한 후 60 ℃의 온도에서 15시간 동안 반응시켰다. 반응이 완료된 후 반응물을 상온으로 냉각하였고, 과량의 메탄올과 아세톤 혼합용액을 이용하여 석출시킴으로써 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴레이트 단량체의 공중합체를 제조하였다.
10.55 g (0.024 mol) of the perfluorinated polyether modified compound prepared in Preparation Example 1, 0.3 g (1.19 × 10 −3 mol) of the benzophenone-based acrylate monomer prepared in Preparation Example 2, n-octanethiol (n- octanethiol) 0.1095 g (7.5x10 -4 mol) and the radical initiator Azobisisobutyronitrile (AIBN) 0.1085 g (6.16x10 -4 mol) were dissolved by adding 43.39 g of trifluoro toluene. The freeze-thaw cycle was repeated three times with the mixture, followed by reaction at a temperature of 60 ° C. for 15 hours. After the reaction was completed, the reaction was cooled to room temperature, and a copolymer of a perfluorinated polyether-modified compound and a benzophenone-based acrylate monomer was prepared by precipitation using an excess methanol and acetone mixed solution.

<실시예 2> 투명 박막의 제조Example 2 Preparation of Transparent Thin Film

상기 실시예 1에서 제조된 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴레이트 단량체의 공중합체를 2,2,3,3-테트라플루오르-1-프로판올(2,2,3,3-tetrafluoro-1-propanol)에 2.5 중량%의 비율로 용해시켰고, 이를 슬라이드 그라스 상부에 300 μL 떨어뜨린 후 스핀 코팅(2000 rpm, 20 sec)를 통해 코팅하였다. 코팅이 수행된 후 진공오븐에서 760 mmHg, 80 ℃의 조건으로 30분간 건조시켰고, 약 0.65 μW/cm2의 광량인 UV 조사기를 이용하여 UV를 30분간 조사하여 경화시킴으로써 투명 박막을 제조하였다.
The copolymer of the perfluorinated polyether modified compound prepared in Example 1 and the benzophenone-based acrylate monomer was prepared as 2,2,3,3-tetrafluoro-1-propanol (2,2,3,3-tetrafluoro-1 -propanol) was dissolved at a rate of 2.5% by weight, which was dropped by 300 μL on top of the slide glass, and then coated through spin coating (2000 rpm, 20 sec). After the coating was carried out, the vacuum oven was dried for 30 minutes under conditions of 760 mmHg and 80 ° C., and a transparent thin film was prepared by irradiating and curing UV for 30 minutes using a UV irradiator having a light quantity of about 0.65 μW / cm 2 .

분석analysis

(1) 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머의 분석(1) Analysis of hexafluoro propylene oxide (HFPO) oligomer

상기 제조예 1의 단계 1에서 제조된 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머를 겔침투크로마토그래피(gel permeation chromatography) 및 19F-NMR 핵자기공명(CDCL3, 300 MHz) 분석을 하였고, 그 결과를 하기 표 1에 나타내었다.
Hexafluoro propylene oxide (HFPO) oligomer prepared in step 1 of Preparation Example 1 was subjected to gel permeation chromatography (gel permeation chromatography) and 19 F-NMR nuclear magnetic resonance (CDCL 3 , 300 MHz) analysis, the results It is shown in Table 1 below.

구조rescue 스펙트럼 (PPM)Spectrum (PPM) 3F, s, CF 3CF2CF2 3F, s, C F 3 CF 2 CF 2 83.883.8 2F, m, CF3CF 2CF2 2F, m, CF 3 C F 2 CF 2 131.3131.3 [(2F, m, CF3CF2CF 2), (3F, s, CF(CF 3)COF)][(2F, m, CF 3 CF 2 C F 2 ), (3F, s, CF (C F 3 ) COF)] 83.283.2 1F, t, OCFCF3CF2 1 F , t, OC F CF 3 CF 2 146.2146.2 [(3F, m, OCF(CF 3)CF2), (m, 2F, OCF(CF3)CF 2)][(3F, m, OCF ( C F 3) CF 2), (m, 2F, OCF (CF 3) C F 2)] 81.681.6 1F, t, CFCOF1F, t, C F COF 132.0132.0

상기 표 1에 나타낸 바와 같이, 상기 제조예 1의 단계 1에서 제조된 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머를 19F-NMR 핵자기공명 분석한 결과 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머의 83.8 PPM 및 131.3PPM에서 CF3CF2의 불소 피크를, 146.2 PPM에서 OCF(CF3)CF2의 불소피크를 확인할 수 있다. 또한, 겔침투크로마토그래피(gel permeation chromatography) 분석 결과 상기 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머의 분자량이 4400인 것을 확인하였다. 이를 통하여 헥사플루오르 프로필렌 옥사이드(HFPO) 올리고머의 제조가 제대로 수행되었음을 확인할 수 있었다.
As shown in Table 1, 83.8 PPM and 131.3 of the hexafluoro propylene oxide (HFPO) oligomer as a result of 19 F-NMR nuclear magnetic resonance analysis of the hexafluoro propylene oxide (HFPO) oligomer prepared in Step 1 of Preparation Example 1 CF 3 CF 2 in PPM Fluorine peak, 146.2 PPM shows fluorine peaks of OC F (CF 3 ) CF 2 . In addition, gel permeation chromatography analysis confirmed that the molecular weight of the hexafluoro propylene oxide (HFPO) oligomer was 4400. Through this, it was confirmed that the production of hexafluoropropylene oxide (HFPO) oligomer was successfully performed.

(2) 벤조페논계 아크릴레이트 단량체의 분석(2) Analysis of benzophenone acrylate monomer

상기 제조예 2에서 제조된 벤조페논계 아크릴레이트 단량체를 1H-NMR 핵자기공명(CDCL3, 300 MHz) 분석하였고, 그 결과를 하기 표 2에 나타내었다.
The benzophenone-based acrylate monomer prepared in Preparation Example 2 was analyzed by 1 H-NMR nuclear magnetic resonance (CDCL 3 , 300 MHz), and the results are shown in Table 2 below.

구조rescue 스펙트럼 (PPM)Spectrum (PPM) 2s, 2H, CH2=2s, 2H, CH 2 = 5.7-6.3 5.7-6.3 various m, 9H, C-Haromvarious m, 9H, C-Harom 7.2-7.9 7.2-7.9

상기 표 2에 나타낸 바와 같이, 상기 제조예 2에서 제조된 벤조페논계 아크릴레이트 단량체를 1H-NMR 핵자기공명 분석한 결과 벤조페논계 아크릴레이트 단량체의 5.7 ~ 6.3 PPM 및 7.2 ~ 7.9 PPM에서 CH2=피크 및 C-Harom(벤젠의 C-H 피크) 피크를 확인할 수 있다. 이를 통하여 벤조페논계 아크릴레이트 단량체의 제조가 제대로 수행되었음을 확인할 수 있었다.
In, 5.7 ~ of the benzophenone-based acrylate monomer, a first analysis of H-NMR nuclear magnetic resonance benzophenone acrylate monomer prepared in Preparative Example 2 6.3 PPM and 7.2 ~ 7.9 PPM As shown in Table 2 CH 2 = peak and C-Harom (CH peak of benzene) peaks can be seen. Through this, it was confirmed that the preparation of the benzophenone-based acrylate monomer was properly performed.

<실험예 1> 핵자기공명분석(NMR)Experimental Example 1 Nuclear Magnetic Resonance Analysis (NMR)

본 발명에 따른 실시예 1의 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴레이트 단량체의 공중합체를 19F-NMR(CDCL3, 300 MHz) 및 1H-NMR (CDCL3, 300 MHz)핵자기공명분석하였고, 그 결과를 하기 표 3 및 표 4에 나타내었다.
The copolymer of the perfluorinated polyether modified compound of Example 1 and the benzophenone-based acrylate monomer according to the present invention was prepared using 19 F-NMR (CDCL 3 , 300 MHz) and 1 H-NMR (CDCL 3 , 300 MHz). Resonance analysis, the results are shown in Table 3 and Table 4.

19F-NMR 분석결과 19 F-NMR analysis results 구조rescue 스펙트럼 (PPM)Spectrum (PPM) 3F, s, CF 3CF2CF2 3F, s, C F 3 CF 2 CF 2 83.883.8 2F, m, CF3CF 2CF2 2F, m, CF 3 C F 2 CF 2 131.3131.3 [(2F, m, CF3CF2CF 2), (3F, s, CF(CF 3)COO)][(2F, m, CF 3 CF 2 C F 2 ), (3F, s, CF (C F 3 ) COO)] 83.283.2 1F, t, CF(CF3)COO1F, t, C F (CF 3 ) COO 132.0132.0

1H-NMR 분석결과 1 H-NMR analysis result 구조rescue 스펙트럼 (PPM)Spectrum (PPM) (-CH2-CH-)(-CH 2 -CH-) 1.4 / 2.01.4 / 2.0 C-HaromC-Harom 7.4 ~ 8.07.4-8.0

상기 표 3 및 표 4에 나타낸 바와 같이, 실시예 1의 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴레이트 단량체의 공중합체는19F-NMR 핵자기공명 분석결과 83.8 PPM 및 131.3PPM에서 CF3CF2피크를, 132.0 PPM에서 CF(CF3)피크와 같은 불소기를 확인할 수 있었고, 1H-NMR 핵자기공명 분석한 결과 1.4 PPM 및 2.0 PPM에서 (-CH2-CH-) 피크를 확인할 수 있었으며, 7.4 ~ 8.0 PPM에서 C-Harom 피크를 확인할 수 있었다. 이를 통해, 본 발명에 따른 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴레이트 단량체의 공중합체가 공중합반응을 통해 제조되었음을 확인할 수 있었다.
As shown in Table 3 and Table 4, the copolymer of the perfluorinated polyether modified compound of Example 1 and the benzophenone-based acrylate monomer was CF 3 CF at 83.8 PPM and 131.3 PPM as a result of 19 F-NMR nuclear magnetic resonance analysis 2 peaks, Fluorine groups such as C F (CF 3 ) peaks were identified at 132.0 PPM, and (-CH 2 -CH-) peaks were identified at 1.4 PPM and 2.0 PPM from 1 H-NMR nuclear magnetic resonance analysis. C-Harom peak was confirmed at 8.0 PPM. Through this, it was confirmed that the copolymer of the perfluorinated polyether modified compound and the benzophenone-based acrylate monomer according to the present invention was produced through the copolymerization reaction.

<실험예 2> 투명 박막의 특성 분석Experimental Example 2 Characterization of the Transparent Thin Film

본 발명에 따른 실시예 2의 투명 박막의 두께(Essential Macleod Simulation에 의하여), 굴절율(Essential Macleod Simulation에 의하여), 투명도(UV spectrometer Jasco V-650, λ =550 nm), 반사율(UV spectrometer Jasco V-650, λ =550 nm), 접촉각(접촉각 측정기, Kruss DSA-100) 및 표면에너지(기하평균법에 의하여) 분석하였고, 그 결과를 하기 표 5, 도 1 및 도 2에 나타내었다.
Thickness of the transparent thin film of Example 2 according to the present invention (by Essential Macleod Simulation), refractive index (by Essential Macleod Simulation), transparency (UV spectrometer Jasco V-650, λ = 550 nm), reflectance (UV spectrometer Jasco V -650, λ = 550 nm), contact angle (contact angle meter, Kruss DSA-100) and surface energy (by geometric mean method) were analyzed and the results are shown in Table 5, FIGS. 1 and 2 below.

두께
(nm)thickness
(nm) 굴절율
(at 25 ℃)
Refractive index
(at 25 ℃)

투명도
transparency

반사율
reflectivity 접촉각
(°)Contact angle
(°) 표면에너지
(dyn/cm)Surface energy
(dyn / cm) 물water CH2I2 CH 2 I 2 HDHD 실시예1Example 1 120120 1.3951.395 93%93% 2.0%2.0% 107107 9393 7070 13.1913.19

(상기 표면에너지는 하기 수학식을 이용한 기하평균법으로 계산)(The surface energy is calculated by the geometric mean method using the following equation.)

<수학식>&Lt; Equation &

Figure 112011028477655-pat00013
Figure 112011028477655-pat00013

Figure 112011028477655-pat00014

Figure 112011028477655-pat00014

표 5, 도 2 및 도 3에 나타낸 바와 같이, 실시예 2의 투명 박막의 두께는 120 nm로 박막으로의 코팅이 성공적으로 수행된 것을 알 수 있었고, 일반적인 저 굴절율 화합물·혼합물의 기준인 굴절율 1.40을 넘지 않는 굴절율을 나타낸 것을 확인하였다. 이를 통하여 과불소 폴리에테르 변성 화합물과 탄화수소계 다 관능기 아크릴레이트 혼합물이 저 굴절율인 것을 확인할 수 있었다. 또한, 실시예 2의 투명 박막은 93%의 투명도를 나타내고, 2%의 반사율을 나타내었다. 나아가, 실시예 2의 투명 박막은 물, 다이아이오도메탄(CH2I2) 및 헥사데칸(hexadecane)에 대하여 각각 107°, 93°및 70°인 접촉각을 나타내었고, 표면에너지는 13.19 (dyn/cm)으로 나타났다. 이를 통하여, 본 발명에 따른 투명박막은 높은 접촉각 및 낮은 표면에너지를 가지는 것을 확인하였고, 투명도가 매우 높은 것을 알 수 있었다.As shown in Table 5, FIG. 2 and FIG. 3, it was found that the thickness of the transparent thin film of Example 2 was 120 nm and the coating on the thin film was successfully performed. It was confirmed that the refractive index was not exceeded. Through this, it was confirmed that the perfluorinated polyether modified compound and the hydrocarbon-based polyfunctional acrylate mixture had a low refractive index. In addition, the transparent thin film of Example 2 exhibited a transparency of 93% and a reflectance of 2%. Furthermore, the transparent thin film of Example 2 exhibited contact angles of 107 °, 93 ° and 70 ° for water, diiodomethane (CH 2 I 2 ) and hexadecane, respectively, and the surface energy was 13.19 (dyn). / cm). Through this, the transparent thin film according to the present invention was confirmed to have a high contact angle and low surface energy, it was found that the transparency is very high.

Claims (8)

하기 화학식 1로 표시되는 과불소 폴리에테르 변성 화합물 중 1종과 하기 화학식 2로 표시되는 벤조페논계 아크릴레이트 단량체 1종 이상을 공중합한 공중합체;

<화학식 1>
CF3CF2CF2-O-CF(CF3)-X-Y-X-CZ=CH2
(상기 화학식 1에서 X는 에스테르 연결기를 나타내고, Y는 탄소수 1~5의 알킬렌을 나타내며, Z는 수소 또는 탄소수 1 ~ 5의 알킬기를 나타낸다)

<화학식 2>
Figure 112013078706826-pat00015

(상기 화학식 2에서 X는 수소를 나타내고, Y는 에스테르 연결기를 나타내며, Z는 단일결합을 나타내고, A는 하기 구조식 1로 표시되는 UV 경화가 가능한 벤조페논계 단위체(unit)를 나타낸다)

<구조식 1>
Figure 112013078706826-pat00016
.
A copolymer obtained by copolymerizing one or more of the perfluoropolyether-modified compound represented by the following Chemical Formula 1 with one or more benzophenone-based acrylate monomers represented by the following Chemical Formula 2;

&Lt; Formula 1 >
CF 3 CF 2 CF 2 -O-CF (CF 3 ) -XYX-CZ = CH 2
(In Formula 1, X represents an ester linking group, Y represents alkylene having 1 to 5 carbon atoms, and Z represents hydrogen or an alkyl group having 1 to 5 carbon atoms.)

(2)
Figure 112013078706826-pat00015

(In Formula 2, X represents hydrogen, Y represents an ester linkage group, Z represents a single bond, and A represents a benzophenone-based unit capable of UV curing represented by Structural Formula 1 below.)

<Structure 1>
Figure 112013078706826-pat00016
.
제1항에 있어서, 상기 과불소 폴리에테르 변성 화합물과 벤조페논계 아크릴 단량체의 공중합체는 벤조페논계 아크릴 단량체의 조성이 0.01 ~ 15 중량%인 것을 특징으로 하는 공중합체.
The copolymer of claim 1, wherein the copolymer of the perfluorinated polyether-modified compound and the benzophenone-based acrylic monomer has a composition of 0.01 to 15% by weight of the benzophenone-based acrylic monomer.
제1항의 공중합체 및 용제를 포함하는 접착성이 향상된 투명 코팅제 조성물.
A transparent coating composition with improved adhesion comprising the copolymer of claim 1 and a solvent.
제3항에 있어서, 상기 용제는 과불소 헵탄, 과불소 헥산, m-키시렌헥사 플로오라이드, 벤조트리플루오라이드, 메틸 과불소 부틸 에테르, 에틸 과불소 부틸 에테르 및 과불소(2－부틸 테트라 하이드로 퓨란)으로 이루어지는 군으로부터 선택되는 1종 또는 2종 이상의 혼합물인 것을 특징으로 하는 접착성이 향상된 투명 코팅제 조성물.
The method of claim 3, wherein the solvent is perfluoro heptane, perfluorine hexane, m-xylene hexafluoride, benzotrifluoride, methyl perfluorine butyl ether, ethyl perfluorine butyl ether and perfluorine (2-butyl tetra Hydrofuran), a transparent coating composition with improved adhesion, characterized in that one or a mixture of two or more selected from the group consisting of.
제3항에 있어서, 상기 투명 코팅제 조성물은 광경화되는 것을 특징으로 하는 접착성이 향상된 투명 코팅제 조성물.
The transparent coating composition of claim 3, wherein the transparent coating composition is photocured.
제3항의 투명 코팅제 조성물을 기판 상부로 코팅한 후 경화시켜 제조되는 투명 박막.
A transparent thin film prepared by coating the transparent coating composition of claim 3 on a substrate and then curing.
제6항에 있어서, 상기 박막의 두께는 5 내지 2000 nm인 것을 특징으로 하는 투명 박막.
The transparent thin film according to claim 6, wherein the thin film has a thickness of 5 to 2000 nm.
제6항에 있어서, 상기 투명 박막은 디스플레이의 프레임, 렌즈, 유리창, 액정 또는 평판표시소자(PDP), 유기발광소자(EL) 및 전계방출디스플레이(FED)를 포함하는 평판 디스플레이의 오염방지 및 반사방지 투명막 또는 이들의 광학 필터로 이용되는 것을 특징으로 하는 투명 박막.The method of claim 6, wherein the transparent thin film includes a frame, a lens, a glass window, a liquid crystal or a flat panel display device (PDP), an organic light emitting device (EL), and a field emission display (FED) of the display. A transparent thin film, which is used as an anti-transparent film or an optical filter thereof.
KR1020110035645A 2011-04-18 2011-04-18 UV curable fluorinated copolymer with improved adhesion property and a composition containing same, and their films containing same KR101335524B1 (en)