KR101291584B1 - Coating Agent Containing Phytoncide and Manufacturing Method of The Same, and Fruit Cover and Film Cointaining The Coating Agent - Google Patents
Coating Agent Containing Phytoncide and Manufacturing Method of The Same, and Fruit Cover and Film Cointaining The Coating Agent Download PDFInfo
- Publication number
- KR101291584B1 KR101291584B1 KR1020110075796A KR20110075796A KR101291584B1 KR 101291584 B1 KR101291584 B1 KR 101291584B1 KR 1020110075796 A KR1020110075796 A KR 1020110075796A KR 20110075796 A KR20110075796 A KR 20110075796A KR 101291584 B1 KR101291584 B1 KR 101291584B1
- Authority
- KR
- South Korea
- Prior art keywords
- phytoncide
- solution
- photocatalyst
- thymol
- mixture
- Prior art date
Abstract
피톤치드와 티몰의 혼합물, 피톤치드와 스피아민트의 혼합물 및 피톤치드 중의 적어도 하나를 포함하는 천연 항균제, 그리고 광촉매 물질을 포함하는 코팅액.A coating solution comprising a natural antimicrobial agent comprising at least one of a mixture of phytoncide and thymol, a mixture of phytoncide and spearmint, and a phytoncide, and a photocatalytic material.
Description
본 발명은 피톤치드를 함유하는 코팅액과 그 제조 방법 및 그 코팅액을 함유하는 과일 봉지에 관한 것이다. The present invention relates to a coating liquid containing phytoncide, a method for producing the same, and a fruit bag containing the coating liquid.
농작물에 발생하는 병해충 방제는 주로 유기합성 농약을 사용하는데 이는 환경에 대한 부담이나 농산물에 대한 잔류성 및 토양 오염이 발생하므로 자연 생태계에 안전한 생물학적 방제 방법을 적용하기 위한 연구가 진행되고 있다. Pest control on crops mainly uses organic synthetic pesticides, which is a burden on the environment, residues on agricultural products, and soil pollution. Therefore, research is being conducted to apply safe biological control methods to natural ecosystems.
생물 농약 중에서도 환경 및 인체에 안전성이 높은 천연 물질을 이용한 병해충 방제제 개발이 활발하게 진행되고 있으나 항균력 등이 미흡하여 충분한 방제 효과를 내지 못하거나 천연 물질 자체의 강한 휘발성이나 분해성으로 인해 살포 후 단시간에 사라져 버리는 등의 문제가 있다.Among biological pesticides, the development of pest control agents using natural substances with high safety for the environment and human body is being actively conducted, but they do not have sufficient antibacterial effects due to insufficient antimicrobial activity or due to the strong volatility or degradability of natural substances themselves, There are problems such as disappearing.
잣나무 피톤치드는 향기 성분과 항균 활성이 우수하여 이미 치약, 껌, 화장품 원료 등으로 활용되고 있으며, 이 물질의 항균 활성을 극대화 한다면 신선 과채류에 발생하는 작물병의 방제에 최적의 천연 항균제로 사용될 수 있다. Pine tree phytoncide is already used for toothpaste, gum and cosmetics because it has excellent fragrance and antibacterial activity.If it maximizes the antimicrobial activity of this substance, it can be used as an optimal natural antibacterial agent for controlling crop diseases occurring in fresh fruits and vegetables. .
본 발명이 해결하고자 하는 과제는 피톤치드의 항균 활성을 향상하여 천연 항균제로 사용할 수 있도록 하는 것이다.The problem to be solved by the present invention is to improve the antibacterial activity of phytoncide to be used as a natural antibacterial agent.
본 발명이 해결하고자 하는 다른 과제는 피톤치드를 함유하며 항균 활성이 우수한 코팅액과 그 제조 방법을 제공하는 것이다.Another object of the present invention is to provide a coating solution containing phytoncide and excellent antimicrobial activity, and a method for producing the same.
본 발명의 과제들은 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problems of the present invention are not limited to the above-mentioned problems, and other problems not mentioned can be clearly understood by those skilled in the art from the following description.
본 발명의 일 실시예에 따른 코팅액은 피톤치드와 티몰의 혼합물, 피톤치드와 스피아민트의 혼합물 및 피톤치드 중의 적어도 하나를 포함하는 천연 항균제, 그리고 광촉매 물질을 포함한다.The coating solution according to an embodiment of the present invention includes a natural antimicrobial agent comprising at least one of a mixture of phytoncide and thymol, a mixture of phytoncide and spiramine, and a phytoncide, and a photocatalytic material.
상기 광촉매 물질은 이산화 티타늄일 수 있고, 코팅액은 바인더를 더 포함할 수 있다. 상기 바인더는 폴리 우레탄, 피브이비 셀룰로오스, 유기 실란 중의 어느 하나이거나 조합으로 이루어질 수 있고, 발수제로써 실리콘제를 더 포함할 수 있다.The photocatalyst material may be titanium dioxide, and the coating solution may further include a binder. The binder may be made of any one of polyurethane, fibbi cellulose, organic silane, or a combination thereof, and may further include a silicone agent as a water repellent.
본 발명의 다른 실시예에 따르면, 피톤치드와 티몰의 혼합물, 피톤치드와 스피아민트의 혼합물 및 피톤치드 중의 적어도 하나를 포함하는 천연 항균제와 광촉매 물질을 포함하는 코팅액을 함유하는 과일 봉지를 제공한다.According to another embodiment of the present invention, there is provided a fruit bag containing a coating solution comprising a natural antimicrobial agent and a photocatalyst material comprising at least one of a mixture of phytoncide and thymol, a mixture of phytoncide and spearmint, and a phytoncide.
상기 광촉매 물질은 이산화 티타늄일 수 있고, 코팅액은 발수제로써 실리콘제가 코팅되어 있을 수 있다.The photocatalyst material may be titanium dioxide, and the coating solution may be coated with silicone as a water repellent.
본 발명의 다른 실시예에 따르면, 나노 콜로이달 이산화 티타늄을 제조하는 단계, 피톤치드와 티몰의 혼합액 또는 피톤치드와 스피아민트의 혼합액 또는 피톤치드 용액을 상기 나노 콜로이달 이산화 티타늄과 혼합하여 광촉매 용액을 제조하는 단계, 그리고 바인더를 혼합하는 단계를 포함하는 코팅액의 제조 방법을 제공한다.According to another embodiment of the present invention, preparing a nano-colloidal titanium dioxide, a step of preparing a photocatalyst solution by mixing a mixture of phytoncide and thymol or a mixture of phytoncide and spearmint or phytoncide solution with the nano-colloidal titanium dioxide And it provides a method for producing a coating solution comprising the step of mixing the binder.
상기 바인더를 혼합하는 단계는 상기 광촉매 용액을 에틸 알콜로 희석하는 단계, 폴리우레탄 고형분을 에틸 알콜에 희석하는 단계, 상기 에틸 알콜로 희석된 광촉매 용액과 에틸 알콜에 희석된 폴리 우레탄 고형분을 분산기를 사용하여 혼합하는 단계를 포함할 수 있다.The mixing of the binder may include diluting the photocatalyst solution with ethyl alcohol, diluting the polyurethane solid with ethyl alcohol, and using a disperser for the photocatalyst solution diluted with ethyl alcohol and the polyurethane solid diluted in ethyl alcohol. And mixing the same.
잣나무 구과에서 추출한 피톤치드에 티몰 또는 스피아민트를 적정량 혼합함으로써 항균력을 극대화하여 천연 항균제로 사용할 수 있고, 생분해성 전분 등의 담체에 혼합함으로써 서방성을 확보하여 과실의 신선도 유지 소재로 사용할 수 있다.It can be used as a natural antimicrobial agent by maximizing the antimicrobial power by mixing an appropriate amount of thymol or spearmint in the phytoncide extracted from the pine conifer tree, and by using a carrier such as biodegradable starch, it can be used as a material to maintain the freshness of the fruit.
이러한 피톤치드를 이산화 티타늄 등의 광촉매와 혼합하여 코팅액을 제조함으로써 항균 활성을 향상할 수 있고, 이를 과일 봉지에 적용함으로써 과일 보호력을 향상할 수 있다.By mixing such phytoncide with a photocatalyst such as titanium dioxide to prepare a coating solution, antibacterial activity can be improved, and by applying this to a fruit bag, fruit protection can be improved.
도 1은 본 발명의 일 실시예에 따른 피톤치드 추출 장치의 개략도이다.1 is a schematic diagram of a phytoncide extracting apparatus according to an embodiment of the present invention.
첨부한 도면을 참고로 하여 본 발명의 실시예에 대해 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 도면부호가 사용되었다. 또한 널리 알려져 있는 공지기술의 경우 그 구체적인 설명은 생략한다. BRIEF DESCRIPTION OF THE DRAWINGS The above and other features and advantages of the present invention will be more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which: FIG. The present invention may be embodied in many different forms and is not limited to the embodiments described herein. In order to clearly illustrate the present invention, parts not related to the description are omitted, and the same reference numerals are used for the same or similar components throughout the specification. In the case of publicly known technologies, a detailed description thereof will be omitted.
<실시예><Examples>
1) 잣나무 구과 피톤치드의 준비1) Preparation of Pine Coniferous and Phytoncide
도 1에 도시된 바와 같이, 증류조(1), 냉각 장치(2), 유수 분리기(3) 및 증기 발생기(4)를 포함하는 정유 추출 장치의 증류조(1)에 잣나무 구과를 투입하고, 증기 발생기(4)의 보일러를 가동하여 스증기를 발생시켜 증류조(1)에 들어 있는 구과를 통과시킨다. 이 때, 증류조 내의 온도는 섭씨 80~120도가 바람직하며, 압력은 대기압으로 설정하나 감압 또는 가압하는 것도 가능하다. 증류조를 통과하면서 정유 성분과 혼합된 스증기가 냉각 장치(2)를 거치면서 응축된다. 냉각 장치(2)에서 응축된 응축액은 유수 분리기(3)로 모이고 비중이 물보다 가벼운 정유가 위에 뜨므로 유수 분리기(3) 상단의 밸브(a)를 통하여 연한 황색의 피톤치드 정유를 얻을 수 있고, 유수 분리기(3) 하단의 밸브(b)를 통하여 하이드로졸을 얻는다.As shown in FIG. 1, pine conifers are introduced into a
이와 같이, 잣을 수확하고 남는 잣나무 구과를 사용하여 피톤치드를 추출하면 잣나무 줄기나 가지 또는 잎으로부터 피톤치드 정유를 추출하는 것에 비하여 산림을 훼손할 염려가 적고 우수한 성분의 피톤치드를 얻을 수 있다. 아래의 표 1은 잣나무 구과에서 추출한 피톤치즈와 잎 및 수지에서 추출한 피톤치드의 주요 성분을 비교한 것이다.As such, when the phytoncide is extracted using the pine nut conifer remaining after harvesting the pine tree, the phytoncide of the constituents is less likely to be damaged than the extract of the phytoncide essential oil from the pine stalks, branches or leaves. Table 1 below compares the main components of phyton cheese extracted from pine cones and phytoncide extracted from leaves and resin.
위의 표 1에서 알 수 있는 바와 같이, 잣나무의 구과는 잎과 수지와는 다른 성분을 함유하며, 여기서 추출한 피톤치드도 성분의 차이를 가진다. 이러한 성분 차이는 천연 항균제로서의 효능에도 영향을 미칠 수 있고, 잣나무의 구과로부터 피톤치드를 추출하는 것이 피톤치드 수급에 보다 용이하다.As can be seen in Table 1 above, the conifers of the pine tree contain different components from the leaves and resin, and the phytoncide extracted here also has a difference in components. This component difference can also affect the efficacy as a natural antimicrobial agent, it is easier to extract the phytoncide from the conifer of pine.
2) 티몰(thymol)의 준비2) Preparation of thymol
티몰은 페놀의 일종으로 '2-이소프로필-5-메틸페놀'이라고도 한다. 화학식은 C10H14O이고, 사향 초유와 비슷한 냄새가 나는 무색 결정이며, 물에는 거의 녹지 않으나, 에탄올, 에테르 등의 유기 용매에는 잘 녹는다. 티몰은 멘톨의 합성 원료, 방부제, 살균제로서 치약, 비누 등에 사용되는 것 외에 분석 시약으로서 티탄암모니아 등의 분석에 사용되고, 또한 의약품으로서 구충제 등에 사용된다. Timol is a type of phenol, also known as 2-isopropyl-5-methylphenol. The chemical formula is C 10 H 14 O, colorless crystals with a smell similar to musk colostrum, almost insoluble in water, but soluble in organic solvents such as ethanol and ether. The thymol is not only used as a synthetic raw material of menthol, as an antiseptic, as a fungicide, but also as a toothpaste, soap, etc., and used for analysis of titanium ammonia and the like as an analytical reagent, and also used as an insect repellent and the like.
이러한 티몰은 티몰을 함유하는 사향 초유 또는 꿀풀과 식물 정유 등을 초임계 추출법, 수증기 증류법, 유기 용매 추출법 등을 사용하여 추출할 수 있다. 티몰은 딜 (Dill), 라벤더 (Lavender), 레몬 밤 (Lemon balm), 로즈마리 (Rosemary), 민트 (Mint), 세이보리 (Savory), 세이지(Sage), 센티드제라늄 (Scentedgeranium), 셀프 힐 (Self hill), 스위트 바질 (Sweet Basil), 차빌 (Chervil), 타임(Thyme), 탄지 (Tansy), 시너몬 (Cinnamon), 클로브 (Clove), 유칼립투스 (Eucalyptus), 레몬 (Lemon), 페퍼민트(Peppermint) 및 티 트리 (Tea tree) 등의 식물 정유 성분으로서 위의 초임계 추출법, 수증기 증류법, 유기 용매 추출법 등을 사용하여 식물로부터 추출할 수 있다. 본 실시예에서는 티몰은 일본의 순정 화학 주식회사가 시판 중인 티몰(순도 98.0% 녹는점 49~51˚C, 끓는점 232˚C, 비중 0.965)을 구입하여 사용하였다.Such thymol can be extracted by using a thymol-containing civet colostrum or nectar and plant essential oils, such as supercritical extraction, steam distillation, organic solvent extraction. Timols are Dill, Lavender, Lemon balm, Rosemary, Mint, Savory, Savory, Sage, Scentedgeranium, Self Heel hill, Sweet Basil, Chervil, Thyme, Tansy, Cinnamon, Clove, Eucalyptus, Lemon, Peppermint And a plant essential oil component such as Tea tree can be extracted from the plant using the above supercritical extraction method, steam distillation method, organic solvent extraction method and the like. In this example, thymol was purchased from Japan's Pure Chemical Co., Ltd., thymol (purity 98.0% melting point 49 ~ 51 ° C, boiling point 232 ° C, specific gravity 0.965) was used.
3) 스피아민트(spearmint)의 준비3) preparation of spearmint
스피아민트는 꿀풀과의 여러해살이 풀로서, 달콤하고 강한 상쾌한 향기를 내며, 살균소독, 건위강장, 진정 및 진통의 효과가 있다고 알려져 있다. 스피아민트 오일은 흔히 잎이나 꽃이 핀 선단부에 함유되어 있는데, 수증기 증류 추출, 초임계 추출 등의 방법으로 추출할 수 있다. 본 실시예에서 사용된 스피아민트 오일은 주식회사 서울 향료에서 구입하여 사용하였다.Spearmint is a perennial herb of Lamiaceae, which has a sweet and strong refreshing scent and is known to have antiseptic disinfection, healthy tonic, soothing and analgesic effects. Spearmint oil is often contained at the tip of leaves or flowers, and can be extracted by steam distillation, supercritical extraction, and the like. Spearmint oil used in this example was purchased from Seoul Inc.
스피아민트는 불포화 카본, 리모넨 등이 함유되어 있어서 진정, 진통, 피부 조직의 이완 효과 등이 있다. 스피아민트 오일은 피보보호제, 구토 방지제, 신경안정제, 소화제로 오래 전부터 사용되어 왔으며, 비누와 치약, 껌, 캔디, 음료수 등의 향기 성분으로 사용되어 왔으며, 따라서 환경에 안전하다고 알려져 있다.Spearmint contains unsaturated carbon, limonene, and the like and has soothing, analgesic, and skin tissue relaxation effects. Spearmint oil has been used for a long time as a pivoprotectant, an anti-emetic agent, a neuro stabilizer, and a digestive agent, and has been used as a fragrance ingredient in soaps, toothpastes, gums, candies, and beverages, and thus is known to be safe for the environment.
스피아민트 오일을 GC(Gas Chromatography)와 GC/MS(Mass Spectroscopy)로 분석한 결과, 주요 구성성분은 리모넨(limonene) 16.1%, 감마 테르핀(γ-terpinene) 13.8%, 피 시멘(p-cymene) 5.8%, 3-옥타놀(3-octanol) 6.9%, 카르본(carvone) 40.9%로 나타났다.Analysis of spearmint oil by Gas Chromatography (GC) and Mass Spectroscopy (GC / MS) showed that the main components were 16.1% of limonene, 13.8% of gamma-terpinene, and p-cymene. ) 5.8%, 3-octanol 6.9%, carvone 40.9%.
4) 피톤치드와 티몰 혼합물4) Phytoncide and thymol mixtures
잣나무 구과에서 추출한 피톤치드와 티몰의 혼합물을 제조하였고, 이 물질의 항균력을 측정하기 위하여 여러 균주에 혼합물을 투입하고 7일이 지난 후 균주별 생육 억제 정도를 측정하였다. 피톤치드와 티몰의 다양한 혼합에 따른 항균력을 비교하기 위하여 티몰 원액, 티몰과 순수를 혼합하여 1/10로 희석된 티몰 희석액, 피톤치드 원액(95%)과 티몰 원액(5%)을 혼합한 혼합 원액, 피톤치드 원액(95%)과 1/10로 희석된 티몰 희석액(5%)를 혼합한 혼합 희석액, 피톤치드 원액, 피톤치드와 순수를 혼합하여 1/10로 희석된 피톤치드 희석액을 각각 준비하여 시험을 진행하였고, 그에 따른 결과가 아래 표 2이다.A mixture of phytoncide and thymol extracted from pine cones was prepared. In order to measure the antimicrobial activity of the substance, the mixture was added to various strains and the growth inhibition of each strain was measured after 7 days. To compare the antimicrobial activity of various phytoncide and thymol mixtures, thymol stock solution, thymol and pure water, thymol dilution diluted 1/10, phytoncide stock solution (95%) and thymol stock solution (5%), The test was performed by preparing a mixed dilution solution containing a phytoncide stock solution (95%) and a thymol dilution solution (5%) diluted in 1/10, a phytoncide stock solution, a phytoncide solution and pure water, and diluting a 1/10 diluted phytoncide solution. The results are shown in Table 2 below.
여기서, B.cin은 보트리티스 시네리아(Botrytis cinerea), A.alt는 알타나리아 알타나타(Altenaria alternata), C.acu는 탄저병균(Colletotricum acutatum), F.oxy는 구근 부패 병균(Fusarium oxysporum), S.S는 균핵병균(Sclerotinia sclerotiorum), R.sol은 잘록병균(Rhizotonia solani)를 의미한다.Here, B.cin is Botrytis cinerea, A.alt is Altanaria alternata, C.acu is an anthrax (Colletotricum acutatum), and F.oxy is a bulbous rot fungus (Fusarium) oxysporum), SS means Sclerotinia sclerotiorum, and R.sol means Rhizotonia solani.
위의 표 2에서 알 수 있는 바와 같이, 피톤치드 원액과 티몰 원액을 혼합한 혼합물이 A.alt, C.acu, F.oxy 등의 생육을 70% 가까이 또는 그 이상으로 억제하며, B.cin과 R.sol의 생육도 어느정도 억제하여, 가장 우수한 항균력을 나타냈다.As can be seen in Table 2 above, the mixture of the phytoncide stock solution and the thymol stock solution inhibits the growth of A.alt, C.acu, F.oxy and the like to about 70% or more, and B.cin and It also inhibited the growth of R. sol to some extent, showing the best antibacterial activity.
이러한 피톤치드와 티몰 혼합물의 항균력은 피톤치드 원액 70~96%와 티몰 원액 4~30%를 혼합한 범위에서 어느 정도 효과를 유지하는 것으로 나타났고, 피톤치드 원액 94~96%와 티몰 원액 4~6%를 혼합한 범위에서 가장 우수한 항균력을 나타냈다.The antimicrobial activity of the phytoncide and thymol mixture was maintained to some extent in the range of 70 to 96% of the phytoncide stock solution and 4 to 30% of the thymol stock solution, and 94 to 96% of the phytoncide stock solution and 4 to 6% thymol solution. It showed the best antibacterial activity in the mixed range.
5) 피톤치드와 스피아민트 혼합물5) Phytoncide and Spearmint Mixture
잣나무 구과에서 추출한 피톤치드와 스피아민트의 혼합물을 제조하였고, 이 물질의 항균력을 측정하기 위하여 여러 균주에 혼합물을 투입하고 7일이 지난 후 균주별 생육 억제 정도를 측정하였다. 피톤치드와 스피아민트의 다양한 혼합에 따른 항균력을 비교하기 위하여 스피아민트 원액, 스피아민트와 순수를 혼합하여 1/10로 희석한 스피아민트 희석액, 스피아민트 원액(5%)과 티몰 원액(95%)의 혼합 원액, 스피아민트 원액(5%)과 티몰에 순수를 혼합하여 1/10로 희석한 스피아민트 희석액(95%)의 혼합액, 피톤치드 원액(95%)과 스피아민트 원액(5%)을 혼합한 혼합 원액, 1/10로 희석된 피톤치드 희석액(95%)과 스피아민트 원액(5%)을 혼합한 혼합 희석액을 각각 준비하여 시험을 진행하였고, 그에 따른 결과가 아래 표 3이다.A mixture of phytoncide and spearmint extracted from pine cones was prepared. In order to measure the antimicrobial activity of the substance, the mixture was added to various strains and the growth inhibition of each strain was measured after 7 days. In order to compare the antimicrobial activity of various phytoncide and spearmint mixtures, the spearmint stock solution, the spearmint dilution mixture (1%) and the spearmint stock solution (5%) and thymol stock solution (95%) Mixed stock, spearmint stock (5%) and thymol mixed with pure water diluted 1/10 dilute spearmint dilution (95%), phytoncide stock (95%) and spearmint stock (5%) The test mixture was prepared by mixing a mixed stock solution, a phytoncide dilution (95%) diluted with 1/10, and a mixed dilution solution containing spiamine stock solution (5%), respectively, and the results are shown in Table 3 below.
여기서, B.cin은 보트리티스 시네리아(Botrytis cinerea), A.alt는 알타나리아 알타나타(Altenaria alternata), C.acu는 탄저병균(Colletotricum acutatum), F.oxy는 구근 부패 병균(Fusarium oxysporum), S.S는 균핵병균(Sclerotinia sclerotiorum), R.sol은 잘록병균(Rhizotonia solani), KC08는 페니실린 익스팬슘(Penicillin expansum), JW81는 Penicillin expansum, Pi는 페니실린 이탈리쿰(Penicillin italicum)을 의미한다.Here, B.cin is Botrytis cinerea, A.alt is Altanaria alternata, C.acu is an anthrax (Colletotricum acutatum), and F.oxy is a bulbous rot fungus (Fusarium) oxysporum), SS stands for Sclerotinia sclerotiorum, R.sol stands for Rhizotonia solani, KC08 stands for penicillin expansum, JW81 stands for Penicillin expansum, and Pi stands for penicillin italicum. .
위의 표 3에서 알 수 있는 바와 같이, 피톤치드 원액과 스피아민트 원액을 혼합한 혼합물이 B.cin, F.oxy, A.alt, C.acu 등의 생육을 40% 이상 억제하고, KC08, JW81, Pi 및 R.sol의 생육도 어느정도 억제하여, 가장 우수한 항균력을 나타냈다.As can be seen in Table 3 above, the mixture of the phytoncide stock solution and the spearmint stock solution inhibits the growth of B.cin, F.oxy, A.alt, C.acu and the like by more than 40%, and KC08, JW81 The growth of, Pi and R.sol was also inhibited to some extent, showing the best antibacterial activity.
이러한 피톤치드와 스피아민트 혼합물의 항균력은 피톤치드 원액 70~96%와 스피아민트 원액 4~30%를 혼합한 범위에서 어느 정도 효과를 유지하는 것으로 나타났고, 피톤치드 원액 94~96%와 스피아민트 원액 4~6%를 혼합한 범위에서 가장 우수한 항균력을 나타냈다.The antimicrobial activity of the phytoncide and spearmint mixture was found to maintain a certain effect in the range of 70 to 96% of the phytoncide stock solution and 4 to 30% of the phytide stock solution, and 94 to 96% of the phytoncide stock solution and 4 to It showed the best antibacterial activity in the range of 6%.
본 발명의 천연 항균제의 서방성(徐放性)을 확보하고 사용 가능한 형태를 마련하고자 아래의 사용예를 제시한다.In order to secure the sustained release (徐 放 性) of the natural antibacterial agent of the present invention and to provide a usable form, the following use example is presented.
<사용예><Use example>
1) 무기담체1) weapon carrier
서방성 농약 입제를 만들기 위해 배합할 수 있는 담체는 특별히 한정되지 않지만, 예를 들어 일반 흙, 벤토나이트, 탄산칼슘, 규조토, 제올라이트, 버미큘라이트, 산성백토, 경석, 화이트 카본 (친수성 실리카, 소수성 실리카), 산화티탄 등을 들수 있다. 본 발명의 서방성 농약 입제에 배합할 수 있는 결합제는 특별히 한정되지 않지만, 예를 들어 폴리비닐알코올, 덱스트린, 카르복시메틸셀룰로스, 폴리비닐피롤리돈, 알긴산나트륨, 리그닌술폰산칼슘 등을 들 수 있다. 본 발명의 서방성 농약 입제에 배합할 수 있는 안정화제로는, 예를 들어 페놀계 산화방지제, 아민계 산화방지제, 인계 산화방지제, 황계 산화방지제, 에폭시화 대두유, 에폭시화 아마인유, 에틸렌글리콜 등을 들 수 있다. 본 발명의 서방성 농약 입제에 배합할 수 있는 활택제로는, 예를 들어 탤크, 스테아르산칼슘, 유동파라핀, 폴리에틸렌글리콜 등을 들 수 있다.Carriers that can be blended to produce sustained-release pesticide granules are not particularly limited, but for example, general soil, bentonite, calcium carbonate, diatomaceous earth, zeolite, vermiculite, acid clay, pumice, white carbon (hydrophilic silica, hydrophobic silica), Titanium oxide and the like. Although the binder which can be mix | blended with the sustained-release pesticide granulation of this invention is not specifically limited, For example, polyvinyl alcohol, dextrin, carboxymethylcellulose, polyvinylpyrrolidone, sodium alginate, calcium lignin sulfonate, etc. are mentioned. Examples of stabilizers that can be incorporated into the sustained-release pesticide granules of the present invention include phenolic antioxidants, amine antioxidants, phosphorus antioxidants, sulfur antioxidants, epoxidized soybean oil, epoxidized linseed oil, ethylene glycol, and the like. Can be mentioned. Examples of the lubricant that can be blended into the sustained-release pesticide granules of the present invention include talc, calcium stearate, liquid paraffin, polyethylene glycol, and the like.
2) 유기캡슐2) Organic Capsule
피톤치드를 마이크로캡슐화하는 피막물질로 생분해성 전분을 사용할 수 있다. 생분해성 변성 전분 30% 수용액 100g에 피톤치드 10g을 넣고 호모게나이저로 7000rpm에서 10분간 교반하여 마이크로캡슐 슬러리액을 만든다. 이 슬러리액을 스프레이 건조기를 사용하여 노즐 부분의 온도 80℃, 노즐의 분무속도 8∼9㎖/min의 조건으로 분사하여 분말 상태의 마이크로캡슐화된 피톤치드를 얻는다.Biodegradable starch may be used as a coating material for microencapsulating phytoncide. 100 g of biodegradable modified starch 30% aqueous solution was added 10 g of phytoncide 교반 and stirred for 10 minutes at 7000 rpm with a homogenizer to prepare a microcapsule slurry solution. This slurry liquid is sprayed using the spray dryer on the conditions of the nozzle part temperature of 80 degreeC, and the nozzle spray rate of 8-9 mL / min, and the powdery microencapsulated phytoncide is obtained.
이러한 마리크로캡슐화된 피톤치드를 그대로 사용할 수도 있으나, 발수제 등에 혼합하여 사용하기 위하여 섭씨 160도 정도의 내열성이 있어야 할 경우는 피막질로 쿠마린 수지 또는 커들란으로 사용할 수 있다.Although such micro-encapsulated phytoncide may be used as it is, in order to be mixed with a water repellent or the like and have a heat resistance of about 160 degrees Celsius, it may be used as a coumarin resin or curdlan as a film.
본 발명의 천연 항균제의 사용 형태는 캡슐에 한정되는 것은 아니고, 필름, 유제, 유화제, 수화제, 수용제, 에어로졸, 펌프 스프레이, 현탁제, 입제, 분제, 미립제, 캡슐제, 비드제, 훈증제, 훈연제, 연막제 또는 소독제의 형태로도 할 수 있다. The form of use of the natural antimicrobial agent of the present invention is not limited to capsules, films, emulsions, emulsifiers, hydrating agents, water soluble agents, aerosols, pump sprays, suspensions, granules, powders, granules, capsules, beads, fumigants, It may also be in the form of smoke, smoke or disinfectant.
이러한 천연 항균제는 다수확성, 항균성, 탈취성, 신선도 유지, 농도에 따른 생육 조절 기능 등의 기능성을 지니고 있어 농업용, 포장용, 보관용 용기 등의 제조에 유용하게 사용될 수 있으며 병충해 방지를 위해 노지에 적용하는 과일 봉지에 적용하기 위해 발수제와 함께 코팅 또는 발수제 코팅 후 스프레이 코팅 등의 방법으로 적용 할 수 있고, 저장고에 분무 등의 방법으로 적용할 수 있다.These natural antimicrobial agents have many functions such as multiplicity, antimicrobial, deodorant, freshness maintenance, growth control function according to concentration, and can be useful for manufacturing agricultural, packaging and storage containers. In order to apply to the fruit bag to be coated with a water repellent or after the water repellent coating can be applied by a method such as spray coating, it can be applied to the storage by spraying or the like.
3) 필름3) film
본 발명에 따른 천연 항균제를 실리카에 함유시켜 만든 실리카 분말 또는 제올라이트 분말을 방담제 등의 기타의 첨가제와 함께 넣어 필름을 제조하여 사용할 수 있다.Silica powder or zeolite powder made by containing the natural antimicrobial agent according to the present invention can be added together with other additives such as an antifoaming agent to produce a film.
농업용 필름의 제조에 사용될 경우에 천연 항균제인 피톤치드와 티몰 혼합액 또는 피톤치드와 스페어민트 혼합액을 실리카에 함유시켜 만든 실리카 분말 또는 제올라이트 분말은 수지 100 중량%에 대해 1 내지 70 중량%로 첨가되는 것이 바람직하다. 1 중량% 미만이 포함될 경우 위의 기능성을 충분히 나타낼 수 없으며, 70 중량%를 초과하는 범위에서는 농업용 필름으로서 요구되는 투광성이나 기계적 강도를 유지할 수 없기 때문이다. 농업용 필름으로 제조되는 경우라면, 수지로서 폴리에틸렌, 에틸렌/아세트산비닐 공중합체 등이 예시될 수 있다.When used in the manufacture of agricultural films, silica powder or zeolite powder made by containing a natural antimicrobial phytoncide and thymol mixture or phytoncide and sparemint mixture in silica is preferably added in an amount of 1 to 70% by weight based on 100% by weight of the resin. . If less than 1% by weight can not exhibit the above functionality sufficiently, in the range exceeding 70% by weight it is not possible to maintain the light transmittance or mechanical strength required as an agricultural film. If it is made of an agricultural film, polyethylene, ethylene / vinyl acetate copolymer and the like can be exemplified as the resin.
또한 본 발명이 포장용 또는 식품 저장용 필름으로 제조되는 경우라면 그러한 수지로서 폴리에틸렌(LLPE, LDPE 등), 폴리프로필렌, 에틸렌/비닐알콜 공중합체, 에틸렌/비닐아세테이트 공중합체 등이 예시될 수 있다.In addition, when the present invention is made of a film for packaging or food storage, such resin may include polyethylene (LLPE, LDPE, etc.), polypropylene, ethylene / vinyl alcohol copolymer, ethylene / vinylacetate copolymer, and the like.
본 발명에 따른 천연 항균제를 필름에 코팅하여 적용할 경우에는 윤활 및 발수의 기능을 부가하기 위하여 스테아르산, 올레산, 팔미트산 등의 지방산류, 이들의 금속염, 지방산 유래의 지방산 아미드, 폴리에틸렌왁스 등의 왁스류, 유동 파라핀, 글리세린지방산 에스테르 등의 에스테르류, 고급 알콜 등을 첨가 할 수 있다.When the natural antimicrobial agent according to the present invention is coated and applied to the film, in order to add lubrication and water repellency, fatty acids such as methylene stearic acid, oleic acid and palmitic acid, metal salts thereof, fatty acid amides derived from fatty acids, polyethylene wax, etc. Waxes, esters such as liquid paraffin, glycerin fatty acid esters, higher alcohols and the like can be added.
4) 코팅액4) Coating solution
가. 광촉매 혼합 코팅액end. Photocatalyst Mixed Coating Liquid
광촉매란 빛과 촉매의 합성어로 빛에 의하여 활성화되는 촉매를 말한다. 나노 크기의 입자가 빛을 받으면 입자 표면에서 강력한 산화 물질을 발생하여 공기 중의 유해한 물질을 무해한 물질로 분해한다. 광산화 분해 반응은 유기화합물 이외에도 불완전 질소 산화물이나 황화물 등을 산화분해 할 수 있으며, 유지나 담배 진처럼 분자량이 큰 유기물도 분해할 수 있고, 세균 등을 산화 분해하기도 한다. 기존의 항균제들이 살균만 하여 균들의 부패물이 축적되는 문제를 가진 반면, 광촉매는 살균된 균들도 분해하기 때문에 기술적으로 우위에 있다 하겠다. 이러한 광촉매의 산화력은 수처리에 사용되는 염소나 오존보다 강한 반응성을 보이며, 자신이 반응에 직접 참여하지 않기 때문에 반영구적으로 효과를 나타낼 수 있다는 장점을 가지고 있다. 또한 광촉매는 식물의 광합성 작용을 증진하는 효과도 나타낼 수 있다.The photocatalyst is a compound word of light and a catalyst, and refers to a catalyst activated by light. When nano-sized particles receive light, they generate powerful oxidants at the surface of the particles, breaking down harmful substances in the air into harmless substances. In addition to organic compounds, the photooxidative decomposition reaction can oxidatively decompose incomplete nitrogen oxides and sulfides, and also decompose organic substances having a high molecular weight, such as fats and oils, and oxidatively decompose bacteria. Existing antimicrobial agents have the problem of accumulating bacteria decay only by sterilization, while photocatalysts are technically superior because they decompose sterilized bacteria. The oxidizing power of the photocatalyst has a stronger reactivity than chlorine or ozone used in water treatment, and has the advantage of being semi-permanent since it does not directly participate in the reaction. Photocatalysts may also have the effect of enhancing photosynthetic activity of plants.
이러한 광촉매로는 반도체성 금속 산화물이나 황화합물이 이용된다. 현재 광촉매로 연구되고 있는 물질은 이산화 티타늄 이외에도 셀렌화 카드늄, 산화 아연, 황화 카드늄, 티탄산 스트롬튬, 이오브산 칼륨 등 여러 가지 물질이 있지만, 그 자체가 물에 쉽게 녹아 없어져 버리는 수용성 물질이거나 중금속 물질이므로 인체에 유해하고 물리 화학적으로 불안정하기 때문에 사용상 많은 제약 조건이 있다. 하지만 이산화 티타늄은 식품 첨가제로 사용할 만큼 인체에 무해하며, 화학 물리적으로 안정한 물질이고, 광활성도가 다른 화합물에 비해 우수하다. 광촉매 이산화 티타늄은 자외선을 에너지원으로 하여 공기 중의 산소나 물로부터 활성 산소 및 OH 라디칼을 생성한다. 이 활성 산소와 OH 라디칼은 강한 산화 환원력을 가지고 있어서 표면에 부착된 여러 가지 유기물을 분해하고, 살균을 하며, 악취 물질을 분해하는 작용이 있다. 따라서 이산화 티타늄을 코팅하여 항균, 탈취, 방오 기능을 부여할 수 있다. 이러한 광촉매의 산화 환원 작용 이외에 이산화 티타늄 표면에 지외선 빛을 조사하면 표면의 물과의 접촉각이 10 이하로 되는 친수성 특성도 알려져 있다. 이산화 티타늄은 백색도와 착색력이 뛰어난 고품질 재료로써 페인트, 잉크, 플라스틱, 제지, 고무와 섬유의 광택도 조절과 화학 섬유 및 합성 섬유의 내구성 향상을 위해 그리고 화장품에서 자외선 차단제 등으로 사용되어 왔다. 이산 화티타늄에는 아나타제(Anatase), 부루킷(Brookite), 루틸(Rutile) 등 3가지 결정형이 있는데 열역학적으로 루틸이 전체 온도 범위에서 안정한 상이면 나머지는 준안정상이다. 부루킷은 매우 불안정하며 순수한 결정을 합성하기도 어렵다. 이들 중에서 광촉매로서의 이산화 티타늄은 일반적으로 아나타제의 결정 구조를 가지고 있다. As such a photocatalyst, a semiconducting metal oxide or a sulfur compound is used. In addition to titanium dioxide, materials currently being studied as photocatalysts include various materials such as cadmium selenide, zinc oxide, cadmium sulfide, strontium titanate, and potassium iodide, but are themselves water-soluble or heavy metal substances that easily dissolve in water. There are many constraints on use because they are harmful to the human body and unstable physically and chemically. However, titanium dioxide is harmless to the human body as a food additive, is a chemically physically stable material, and has excellent photoactivity compared to other compounds. Photocatalyst titanium dioxide uses ultraviolet light as an energy source to generate free radicals and OH radicals from oxygen or water in the air. The active oxygen and OH radicals have a strong redox ability to decompose, sterilize, and decompose odorous substances. Therefore, by coating titanium dioxide can be given antibacterial, deodorant, antifouling function. In addition to the redox effect of such a photocatalyst, hydrophilic properties are also known in which the contact angle with water on the surface of the titanium dioxide surface is 10 or less when irradiated with ultraviolet light. Titanium dioxide is a high-quality material with excellent whiteness and colorability, and has been used to control the glossiness of paints, inks, plastics, paper, rubber and fibers, to improve the durability of chemical fibers and synthetic fibers, and as a sunscreen in cosmetics. Titanium dioxide has three crystalline forms: anatase, brookite, and rutile. Thermodynamically, if rutile is a stable phase over the entire temperature range, the rest is metastable. Burukits are very unstable and difficult to synthesize pure crystals. Among them, titanium dioxide as a photocatalyst generally has a crystal structure of anatase.
따라서 이하에서는 이산화 티타늄(TiO2)을 광촉매로 사용하는 코팅액을 중심으로 하여 설명한다.Therefore, hereinafter, the description will be made based on a coating liquid using titanium dioxide (TiO 2 ) as a photocatalyst.
이산화 티타늄을 광촉매로 사용하는 광촉매 혼합 코팅액은 아래와 같은 방법으로 제조한다.Photocatalyst mixed coating solution using titanium dioxide as a photocatalyst is prepared by the following method.
먼저, 나노 콜로이달(colloidal) 이산화 티타늄을 마련한다. 20~30nm의 입자 사이즈의 이산화 티타늄 고형분 10%가 물(H2O)과 2-Methoxy E-OH에 분산된 나노 콜로이달 이산화 티타늄을 준비한다.First, nano colloidal titanium dioxide is prepared. Prepare a nano colloidal titanium dioxide in which 10% titanium dioxide solids of 20-30 nm particle size are dispersed in water (H 2 O) and 2-Methoxy E-OH.
다음, 피톤치드와 티몰의 혼합액 또는 피톤치드와 스피아민트의 혼합액 또는 피톤치드 용액(이하 '피톤치드 용액 등'이라고 한다.)을 나노 콜로이달 이산화 티타늄과 혼합한다. 위에서 준비한 나노 콜로이달 이산화 티타늄과 피톤치드 용액 등을 고속 믹서기로 혼합하여 피톤치드 용액 등이 혼합된 광촉매 용액을 제조하였다Next, a mixed solution of phytoncide and thymol or a mixed solution of phytoncide and spearmint or a phytoncide solution (hereinafter referred to as a phytoncide solution and the like) is mixed with nano colloidal titanium dioxide. The nano-colloidal titanium dioxide and the phytoncide solution prepared above were mixed with a high speed mixer to prepare a photocatalyst solution in which the phytoncide solution and the like were mixed.
다음, 광촉매 용액에 바인더를 혼합한다. 바인더로는 고형분 10%인 폴리우레탄(Polyuretane)을 사용하였다. 광촉매 용액과 바인더의 혼합은 우선, 고형분 10%의 나노 콜로이달 이산화 티타늄과 피톤치드 용액 등이 혼합된 광촉매 용액을 99.9%의 에틸 알콜(Ethyl Alcohol)로 희석하여 3%(v/v)~5%(v/v)의 농도로 제조하였고, 바인더 또한 에틸 알콜로 희석하여 3%(v/v)~5%(v/v)의 농도로 제조하였다. 제조된 광촉매 용액 희석액과 바인더 희석액을 100ml씩 혼합하여 입자 분산기를 사용하여 700rpm에서 1시간 동안 분산하여 광촉매 혼합 코팅액을 제조하였다. 바인더의 농도가 5% 이상이 되면 응집 현상이 발생할 수 있다. Next, the binder is mixed with the photocatalyst solution. Polyurethane (Polyuretane) having a solid content of 10% was used as the binder. First of all, the photocatalyst solution and binder were mixed with 3% (v / v) to 5% by diluting the photocatalyst solution containing 10% of solid nanocolloidal titanium dioxide and phytoncide solution with 99.9% of ethyl alcohol. (v / v) was prepared, and the binder was also diluted with ethyl alcohol to prepare a concentration of 3% (v / v) to 5% (v / v). The photocatalyst solution diluent and the binder diluent were mixed 100 ml each, and dispersed at 700 rpm for 1 hour using a particle disperser to prepare a photocatalyst mixed coating solution. When the concentration of the binder is 5% or more, aggregation may occur.
또한, 상기 광촉매 혼합 코팅액의 제조 단계 중 어느 하나에서 선택적으로 바인더를 혼합할 수 있다. 바인더로는 폴리우레탄 이외에도 피브이비 셀룰로오스[PVB(Polyvinyl butyralc)-Cellulose]를 사용하거나 유기 실란(silane) 화합물을 단독으로 또는 혼합물을 첨가하여 사용할 수 있고, 상온 내지 60℃에서 1시간 내지 6시간 교반하여 광촉매 용액과 혼합한다. 유기 실란 화합물 바인더는 메틸트리메톡시실란, 메틸트리에톡시실란, 비닐트리메톡시실란, 비닐트리에톡시실란 등 이미 공지된 실란계 화합물을 말하며, 바인더로는 실리콘계 화합물 등 점착 특성을 갖는 것을 다양하게 사용할 수 있고 상기 물질에 국한되는 것은 아니다.In addition, the binder may be selectively mixed in any one of the steps of preparing the photocatalyst mixed coating solution. As a binder, in addition to polyurethane, fibbi cellulose [PVB (Polyvinyl butyralc) -Cellulose] may be used, or an organic silane compound may be used alone or by adding a mixture, and may be used at room temperature to 60 ° C. for 1 hour to 6 hours. Stir and mix with photocatalyst solution. The organosilane compound binder refers to a known silane compound such as methyltrimethoxysilane, methyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, and the like. It is possible to use it, but is not limited to the material.
이러한 광촉매 혼합 코팅액은 과일 봉지 등을 제조할 때, 원지에 발수제와 함께 코팅 또는 발수제 코팅 후 스프레이 코팅 등의 방법으로 적용할 수 있다. 좀더 구체적으로는 발수액 코팅 시 광촉매 혼합 코팅액을 혼합해서 코팅하는 방법과 별도의 과일 봉지를 재단하는 공정 중에 스프레이하는 방법, 과일 봉지 재단 공정 중에 회전 롤의 돌출 부분에 혼합액이 묻혀 지면서 과일 봉지에 묻혀 지는 방법 등이 있다. Such a photocatalyst mixed coating liquid may be applied by a method such as spray coating after coating with a water repellent or coating with a water repellent when preparing a fruit bag or the like. More specifically, the coating method of mixing and coating the photocatalyst mixed coating liquid for water repellent coating and spraying during the process of cutting a separate fruit bag, and the fruit bag being buried in the fruit bag while the mixed solution is buried in the protrusion of the rotating roll during the fruit bag cutting process. There are ways to lose.
여기서 발수제로 실리콘제를 사용하면 발수도는 물론 과일 봉지의 통기성도 우수한 친환경 제품을 제작할 수 있다.If silicone is used as a water repellent, it is possible to produce an eco-friendly product having excellent water repellency as well as breathability of a fruit bag.
이와 같이, 과일 봉지 등에 이산화 티타늄 등의 광촉매와 피톤치드 등을 함유한 광촉매 혼합 코팅액을 코팅할 경우 세균 등의 박멸 효과가 크게 증가한다. 그러나 이산화 티타늄이 과다하게 포함될 경우 자외선 차단 효과가 발생하므로 일조량을 감안하여 자외선 흡수 기능이 있는 활성탄의 양을 가감하여 조절한다.As described above, when the photocatalyst mixed coating liquid containing a photocatalyst such as titanium dioxide and phytoncide is coated on a fruit bag or the like, the eradication effect of bacteria or the like is greatly increased. However, when too much titanium dioxide is included, the sunscreen effect is generated, so that the amount of activated carbon with ultraviolet absorbing function is adjusted in consideration of the amount of sunshine.
이러한 광촉매 혼합 코팅액은 농업용 필름, 포장용 필름, 식품 저장용 필름 등을 제조할 때, 원 필름에 코팅하거나 원 필름 제작시 재료에 혼합하는 등의 방법으로 적용할 수 있다. 이 때에도 활성탄의 양을 가감하여 자외선 흡수율을 조절할 수 있다.Such a photocatalyst mixed coating liquid may be applied by a method such as coating on the original film or mixing the material in the production of the original film when manufacturing an agricultural film, a packaging film, a food storage film, and the like. In this case as well, the amount of activated carbon can be adjusted to adjust the ultraviolet absorbance.
나. 서방성 물질 혼합 코팅액I. Sustained release mixed solution
이산화 티타늄과 같은 광촉매 물질뿐만 아니라, 활성탄, 실리카, 일라이트, 제올라이트 등의 다공성 물질에 피톤치드 등을 혼합하여 과일 봉지 코팅액을 제조할 수도 있다. 이들 다공성 물질은 피톤치드 등을 흡수하여 서서히 방출하므로써 살균 효과가 오래도록 지속하도록 한다.In addition to a photocatalyst material such as titanium dioxide, a phytoncide may be mixed with a porous material such as activated carbon, silica, elite, zeolite, or the like to prepare a fruit encapsulation coating solution. These porous materials absorb phytoncide and the like and release them slowly, so that the sterilizing effect lasts for a long time.
이상에서는 잣나무 구과에서 추출한 피톤치드에 이산화 티타늄과 같은 광촉매를 혼합하거나 활성탄 등의 다공성 물질을 혼합하여 코팅액을 제조하는 것을 예시하였으나, 잣나무 추출 피톤치드 이외에도 편백 나무, 화백 나무, 소나무, 전나무 등 칩엽수로부터 추출한 피톤치드도 이산화 티타늄과 같은 광촉매를 혼합하거나 활성탄 등의 다공성 물질을 혼합하여 코팅액을 제조할 수도 있고, 이 경우에도 광촉매 작용으로 인한 항균 활성의 증대 효과나 서방성 향상의 효과가 있다.In the above example, the coating solution was prepared by mixing a photocatalyst, such as titanium dioxide, or a porous material such as activated carbon, with phytoncide extracted from a pine tree conifer, but extracted from chipwood such as cypress, birches, pine, fir, etc. Phytoncide may also be prepared by mixing a photocatalyst such as titanium dioxide or by mixing a porous material such as activated carbon, and in this case, also has an effect of increasing antibacterial activity or improving sustained release due to the photocatalytic action.
이상 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허청구범위의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the invention as defined in the appended claims. You will understand.
1 증류조
2 냉각 장치
3 유수 분리기
4 증기 발생기1 distillation tank
2 cooling system
3 oil-water separator
4 steam generator
Claims (14)
상기 광촉매 물질은 이산화 티타늄인 과일 봉지.In claim 7,
The photocatalyst material is titanium dioxide fruit bag.
상기 코팅액은 활성탄을 더 포함하는 과일 봉지.In claim 7,
The coating solution is a fruit bag further comprises activated carbon.
발수제로써 실리콘제가 코팅되어 있는 과일 봉지.The method according to any one of claims 7 to 9,
Fruit bag coated with silicone as a water repellent.
피톤치드와 티몰의 혼합액 또는 피톤치드와 스피아민트의 혼합액 또는 피톤치드 용액을 상기 나노 콜로이달 이산화 티타늄과 혼합하여 광촉매 용액을 제조하는 단계, 그리고
바인더를 혼합하는 단계
를 포함하는 코팅액의 제조 방법Preparing nano colloidal titanium dioxide,
Preparing a photocatalyst solution by mixing a phytoncide and thymol mixed solution or a phytoncide and spiramine mixed solution or phytoncide solution with the nano colloidal titanium dioxide; and
Mixing binder
Method for producing a coating liquid containing
상기 바인더를 혼합하는 단계는
상기 광촉매 용액을 에틸 알콜로 희석하는 단계,
폴리우레탄 고형분을 에틸 알콜에 희석하는 단계,
상기 에틸 알콜로 희석된 광촉매 용액과 에틸 알콜에 희석된 폴리 우레탄 고형분을 분산기를 사용하여 혼합하는 단계
를 포함하는 코팅액의 제조 방법.
The method of claim 12,
Mixing the binder
Diluting the photocatalyst solution with ethyl alcohol,
Diluting the polyurethane solids with ethyl alcohol,
Mixing the photocatalyst solution diluted with ethyl alcohol and the polyurethane solid diluted in ethyl alcohol using a disperser
Method of producing a coating liquid comprising a.
A method of spraying a coating solution comprising a natural antimicrobial agent comprising at least one of a mixture of phytoncide and thymol, a mixture of phytoncide and spearmint, and a phytoncide, and a photocatalytic material, directly onto a crop or tree.