KR101204935B1 - Preheating burner apparatus for submerged entry nozzle and method for preheating submerged entry nozzle using the same - Google Patents

Preheating burner apparatus for submerged entry nozzle and method for preheating submerged entry nozzle using the same Download PDF

Info

Publication number
KR101204935B1
KR101204935B1 KR1020100028896A KR20100028896A KR101204935B1 KR 101204935 B1 KR101204935 B1 KR 101204935B1 KR 1020100028896 A KR1020100028896 A KR 1020100028896A KR 20100028896 A KR20100028896 A KR 20100028896A KR 101204935 B1 KR101204935 B1 KR 101204935B1
Authority
KR
South Korea
Prior art keywords
immersion nozzle
mold
preheating
molten steel
burner
Prior art date
Application number
KR1020100028896A
Other languages
Korean (ko)
Other versions
KR20110109252A (en
Inventor
유대경
Original Assignee
현대제철 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 현대제철 주식회사 filed Critical 현대제철 주식회사
Priority to KR1020100028896A priority Critical patent/KR101204935B1/en
Publication of KR20110109252A publication Critical patent/KR20110109252A/en
Application granted granted Critical
Publication of KR101204935B1 publication Critical patent/KR101204935B1/en

Abstract

본 발명은, 침지 노즐이 삽입될 수 있는 홀을 상부에 구비한, 적어도 하나의 하우징; 및 상기 하우징 내에 설치되며, 상기 침지 노즐을 예열 하기 위한 버너를 포함하는, 적어도 하나의 침지 노즐을 예열하는, 침지 노즐 예열 버너 장치 및 이를 이용한 침지 노즐 예열 방법에 관한 것이다.The present invention, at least one housing having a hole in which the immersion nozzle can be inserted; And a immersion nozzle preheat burner device and a immersion nozzle preheating method using the same, which are installed in the housing and include a burner for preheating the immersion nozzle.

Description

침지 노즐 예열 버너 장치 및 이를 이용한 침지 노즐 예열 방법{PREHEATING BURNER APPARATUS FOR SUBMERGED ENTRY NOZZLE AND METHOD FOR PREHEATING SUBMERGED ENTRY NOZZLE USING THE SAME}PREPARING BURNER APPARATUS FOR SUBMERGED ENTRY NOZZLE AND METHOD FOR PREHEATING SUBMERGED ENTRY NOZZLE USING THE SAME}

본 발명은, 침지 노즐의 내경에 이물질이 융착되는 것을 방지하기 위한, 침지 노즐 예열 버너 장치 및 이를 이용한 침지 노즐 예열 방법에 관한 것이다.
The present invention relates to an immersion nozzle preheat burner device and an immersion nozzle preheating method using the same for preventing foreign matter from being fused to the inner diameter of the immersion nozzle.

일반적으로, 연속 주조기는 제강로에서 생산되어 래들(ladle)로 이송된 용강을 턴디쉬(turndish)에 받았다가 연속 주조기용 주형로 공급하여 일정한 크기의 슬라브를 생산하는 설비이다.In general, a continuous casting machine is a facility for producing slabs of a constant size by receiving a molten steel produced in a steelmaking furnace and transferred to a ladle in a tundish and then supplying it as a mold for a continuous casting machine.

상기 연속 주조기는 용강을 저장하는 래들과, 턴디쉬 및 상기 턴디쉬에서 출강되는 용강을 최초 냉각시켜 소정의 형상을 가지는 주물으로 형성하는 연속 주조기용 주형와, 상기 주형에 연결되어 주형에서 형성된 주물을 이동시키는 다수의 핀치롤러를 포함한다.The continuous casting machine includes a ladle for storing molten steel, a continuous casting machine mold for cooling the tundish and the molten steel discharged from the tundish to form a casting having a predetermined shape, and the casting formed in the mold connected to the mold to move. It includes a plurality of pinch rollers.

다시 말해서, 상기 래들과 턴디쉬에서 출강된 용강은 주형에서 소정의 폭과 두께를 가지는 슬라브(Slab) 또는 블룸(Bloom), 빌렛(Billet) 등의 주물로 형성되어 핀치롤러를 통해 이송되는 것이다.
In other words, the molten steel tapping out of the ladle and tundish is formed of a slab (Slab) or bloom (Bloom), billet (Billet) having a predetermined width and thickness in the mold and is transferred through the pinch roller.

본 발명은, 침지 노즐을 미리 예열시켜, 연속 주조에 이용되는 침지 노즐의 내경에 용강이 응고되는 현상을 줄여, 조업 중단으로 인한 경제적 손실을 낮추고, 연속 주조의 생산효율을 높이기 위한 침지 노즐 예열 버너 장치 및 방법을 제공하기 위함이다.
The present invention is to preheat the immersion nozzle in advance, to reduce the phenomenon that the molten steel is solidified to the inner diameter of the immersion nozzle used for continuous casting, to reduce the economic loss due to the interruption of operation, to increase the production efficiency of continuous casting immersion nozzle burner To provide an apparatus and method.

상술한 과제를 해결하기 위해, 본 발명에 따른 침지 노즐 예열 버너 장치는, 침지 노즐이 삽입되는 홀, 및 연소 가스를 배출하는 배출구를 상부에 구비함과 아울러 내구성 증진을 위해 이중 구조로 설계되는 적어도 하나의 하우징; 상기 침지 노즐을 예열하기 위해 상기 하우징 내에 설치되며, 산소를 공급하기 위한 공기 공급부, 연소용 가스를 공급하기 위한 가스 공급부, 상기 산소를 이용하여 상기 가스를 점화시키기 위한 점화부를 구비하는 버너; 및 상기 침지 노즐의 예열 온도를 제어하기 위해 상기 버너를 제어하는 제어부;를 포함하며, 상기 제어부는, 상기 하우징들 중 외곽에 삽입된 상기 침지 노즐을 상대적으로 높은 온도로 예열하도록 상기 버너를 제어할 수 있다.
In order to solve the above problems, the immersion nozzle preheat burner device according to the present invention is provided with a hole in which the immersion nozzle is inserted, and the discharge port for discharging the combustion gas at the top and at least designed in a dual structure to increase durability One housing; A burner installed in the housing for preheating the immersion nozzle and having an air supply unit for supplying oxygen, a gas supply unit for supplying combustion gas, and an ignition unit for igniting the gas using the oxygen; And a control unit controlling the burner to control the preheating temperature of the immersion nozzle, wherein the control unit controls the burner to preheat the immersion nozzle inserted into the outer one of the housings to a relatively high temperature. Can be.

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

상술한 구성을 가진 본발명의 일실시예에 따르면, 연속주조를 위해 침지노즐을 교체하는 경우, 침지 노즐 내경에 발생되는 용강 응고 가능성을 낮출 수 있다.According to one embodiment of the present invention having the above-described configuration, when replacing the immersion nozzle for continuous casting, it is possible to lower the possibility of molten steel solidification generated in the immersion nozzle inner diameter.

본 발명의 일실시예에 따르면, 노즐 교체시 턴디쉬에서 주형 주입 용강의 프리징(freezing) 현상을 방지하여, 연속 주조의 조업 안정화에 기여할 수 있다.
According to one embodiment of the present invention, it is possible to prevent the freezing phenomenon of the injection molding molten steel in the tundish when replacing the nozzle, it can contribute to the operation stabilization of continuous casting.

도 1은 본 발명의 일 실시예와 관련된 연속주조기를 보인 측면도.
도 2는 용강(M)의 흐름을 중심으로 도 1의 연속주조기를 설명하기 위한 개념도.
도 3은 도 2의 주형(30) 및 그와 인접한 부분에서의 용강(M)의 분포 형태를 보인 개념도.
도 4는 본 발명의 일실시예인 침지 노즐 예열 버너 장치의 구성도.
도 5는 본 발명의 다른 실시예인 침지 노즐 예열 방법을 설명하기 위한 흐름도.1 is a side view showing a continuous casting machine according to an embodiment of the present invention.
Figure 2 is a conceptual diagram for explaining the continuous caster of Figure 1 centered on the flow of molten steel (M).
3 is a conceptual view showing a distribution form of molten steel M in the mold 30 and an adjacent portion of FIG. 2.
Figure 4 is a block diagram of an immersion nozzle preheat burner device of an embodiment of the present invention.
5 is a flowchart illustrating a immersion nozzle preheating method according to another embodiment of the present invention.

이하, 본 발명의 바람직한 실시예에 따른 침지 노즐 예열 버너 장치 및 이를 이용한 침지 노즐 예열 방법에 대하여 첨부한 도면을 참조하여 상세히 설명한다. 본 명세서에서는 서로 다른 실시예라도 동일?유사한 구성에 대해서는 동일?유사한 참조번호를 부여하고, 그 설명은 처음 설명으로 갈음한다.
Hereinafter, an immersion nozzle preheat burner device and a immersion nozzle preheating method using the same according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings. In the present specification, different embodiments are given the same or similar reference numerals for the same or similar configurations, and the description is replaced with the first description.

연속주조(連續鑄造, Continuous casting)는 용융금속을 바닥이 없는 주형(鑄型, Mold)에서 응고시키면서 연속적으로 주물 또는 강괴(鋼塊, steel ingot)를 뽑아내는 주조법이다. 연속주조는 정사각형?직사각형?원형 등 단순한 단면형의 긴 제품과 주로 압연용 소재인 슬래브?블룸?빌릿을 제조하는 데 이용된다. Continuous casting is a casting method in which a casting or steel ingot is continuously extracted while solidifying molten metal in a mold without a bottom. Continuous casting is used to manufacture simple products such as squares, rectangles, circles, and other simple cross-sections, and slab, bloom and billets, which are mainly for rolling.

연속주조기의 형태는 수직형?수직굴곡형?수직축차굴곡형?만곡형?수평형 등으로 분류된다. 도 1 및 도 2에서는 만곡형을 예시하고 있다.The type of continuous casting machine is classified into vertical type, vertical bending type, vertical axis difference bending type, curved type and horizontal type. 1 and 2 illustrate a curved shape.

도 1은 본 발명의 일 실시예와 관련된 연속주조기를 보인 측면도이다.1 is a side view showing a continuous casting machine related to an embodiment of the present invention.

본 도면을 참조하면, 연속주조기는 턴디쉬(20)와, 주형(30)과, 2차냉각대(60 및 65), 핀치롤(70), 그리고 절단기(90)를 포함할 수 있다.Referring to this drawing, the continuous casting machine may include a tundish 20, a mold 30, secondary cooling tables 60 and 65, a pinch roll 70, and a cutter 90.

턴디쉬(Tundish, 20)는 래들(Laddle, 10)로부터 용융금속을 받아 주형(Mold, 30)으로 용융금속을 공급하는 용기이다. 래들(10)은 한 쌍으로 구비되어, 교대로 용강을 받아서 턴디쉬(20)에 공급하게 된다. 턴디쉬(20)에서는 주형(30)으로 흘러드는 용융금속의 공급 속도조절, 각 주형(30)으로 용융금속 분배, 용융금속의 저장, 슬래그 및 비금속 개재물(介在物)의 분리 등이 이루어진다. The tundish 20 is a container that receives molten metal from the ladle 10 and supplies molten metal to the mold 30. Ladle 10 is provided in a pair, alternately receives molten steel to supply to the tundish 20. In the tundish 20, the molten metal supply rate is adjusted to the mold 30, the molten metal is distributed to each mold 30, the molten metal is stored, and the slag and the non-metallic inclusions are separated.

주형(30)은 통상적으로 수냉식 구리제이며, 수강된 용강이 1차 냉각되게 한다. 주형(30)은 구조적으로 마주보는 한 쌍의 면들이 개구된 형태로서 용강이 수용되는 중공부를 형성한다. 슬라브를 제조하는 경우에, 주형(30)은 한 쌍의 장벽과, 장벽들을 연결하는 한 쌍의 단벽을 포함한다. 여기서, 단벽은 장벽보다 작은 넓이를 가지게 된다. 주형(30)의 벽들, 주로는 단벽들은 서로에 대하여 멀어지거나 가까워지도록 회전되어 일정 수준의 테이퍼(Taper)를 가질 수 있다. 이러한 테이퍼는 주형(30) 내에서 용강(M)의 응고로 이한 수축을 보상하기 위해 설정한다. 용강(M)의 응고 정도는 강종에 따른 탄소 함량, 파우더의 종류(강냉형 Vs 완냉형), 주조 속도 등에 의해 달라지게 된다. The mold 30 is typically made of water-cooled copper and allows the molten steel to be primary cooled. The mold 30 forms a hollow portion in which molten steel is accommodated as a pair of structurally facing faces are opened. In manufacturing the slab, the mold 30 comprises a pair of barriers and a pair of end walls connecting the barriers. Here, the short wall has a smaller area than the barrier. The walls of the mold 30, mainly short walls, may be rotated to move away from or close to each other to have a certain level of taper. This taper is set to compensate for shrinkage caused by solidification of the molten steel M in the mold 30. The degree of solidification of the molten steel (M) will vary depending on the carbon content, the type of powder (steel cold Vs slow cooling), casting speed and the like depending on the steel type.

주형(30)은 주형(30)에서 뽑아낸 주물이 모양을 유지하고, 아직 응고가 덜 된 용융금속이 유출되지 않게 강한 응고각(凝固殼) 또는 응고쉘(Solidifying shell, 81, 도 2 참조)이 형성되도록 하는 역할을 한다. 수냉 구조에는 구리관을 이용하는 방식, 구리블록에 수냉홈을 뚫는 식, 수냉홈이 있는 구리관을 조립하는 방식 등이 있다. The mold 30 has a strong solidification angle or solidifying shell 81 (see FIG. 2) so that the casting extracted from the mold 30 maintains its shape and does not leak molten metal which is still less solidified. It serves to form. The water cooling structure includes a method of using a copper pipe, a method of drilling a water cooling groove in the copper block, and a method of assembling a copper pipe having a water cooling groove.

주형(30)은 용강이 주형의 벽면에 붙는 것을 방지하기 위하여 오실레이터(40)에 의해 오실레이션(oscillation, 왕복운동)된다. 오실레이션 시 주형(30)과 주물과의 마찰을 줄이고 타는 것을 방지하기 위해 윤활제가 이용된다. 윤활제로는 뿜어 칠하는 평지 기름과 주형(30) 내의 용융금속 표면에 첨가되는 파우더(Powder)가 있다. 파우더는 주형(30) 내의 용융금속에 첨가되어 슬래그가 되며, 주형(30)과 주물의 윤활뿐만 아니라 주형(30) 내 용융금속의 산화?질화 방지와 보온, 용융금속의 표면에 떠오른 비금속 개재물의 흡수의 기능도 수행한다. 파우더를 주형(30)에 투입하기 위하여, 파우더 공급기(50)가 설치된다. 파우더 공급기(50)의 파우더를 배출하는 부분은 주형(30)의 입구를 지향한다.The mold 30 is oscillated by the oscillator 40 to prevent the molten steel from sticking to the wall of the mold. Lubricants are used to reduce friction between the mold 30 and the casting during oscillation and to prevent burning. Lubricants include splattered flat oil and powder added to the molten metal surface in the mold 30. The powder is added to the molten metal in the mold 30 to become slag, as well as the lubrication of the mold 30 and the casting, as well as the oxidation and nitriding prevention and thermal insulation of the molten metal in the mold 30, and the non-metal inclusions on the surface of the molten metal. It also performs the function of absorption. In order to inject the powder into the mold 30, a powder feeder 50 is installed. The part for discharging the powder of the powder feeder 50 faces the inlet of the mold 30.

2차 냉각대(60 및 65)는 주형(30)에서 1차로 냉각된 용강을 추가로 냉각한다. 1차 냉각된 용강은 지지롤(60)에 의해 응고각이 변형되지 않도록 유지되면서, 물을 분사하는 스프레이(65)에 의해 직접 냉각된다. 주물 응고는 대부분 상기 2차 냉각에 의해 이루어진다. The secondary cooling zones 60 and 65 further cool the molten steel that has been primarily cooled in the mold 30. The primary cooled molten steel is directly cooled by the spray 65 spraying water while maintaining the solidification angle by the support roll 60 so as not to deform. Casting solidification is mostly achieved by the secondary cooling.

인발장치(引拔裝置)는 주물이 미끄러지지 않게 뽑아내도록 몇 조의 핀치롤(70)들을 이용하는 멀티드라이브방식 등을 채용하고 있다. 핀치롤(70)은 용강의 응고된 선단부를 주조 방향으로 잡아당김으로써, 주형(30)을 통과한 용강이 주조방향으로 연속적으로 이동할 수 있게 한다. The drawing device adopts a multidrive method using a plurality of sets of pinch rolls 70 and the like so that the casting can be taken out without slipping. The pinch roll 70 pulls the solidified tip of the molten steel in the casting direction, thereby allowing the molten steel passing through the mold 30 to continuously move in the casting direction.

절단기(90)는 연속적으로 생산되는 주물을 일정한 크기로 절단하도록 형성된다. 절단기(90)로는 가스토치나 유압전단기(油壓剪斷機) 등이 채용될 수 있다.The cutter 90 is formed to cut continuously produced castings to a constant size. As the cutter 90, a gas torch, a hydraulic shear, or the like can be employed.

도 2는 용강(M)의 흐름을 중심으로 도 1의 연속주조기를 설명하기 위한 개념도이다.FIG. 2 is a conceptual view illustrating the continuous casting machine of FIG. 1 based on the flow of molten steel M. Referring to FIG.

본 도면을 참조하면, 용강(M)은 래들(10)에 수용된 상태에서 턴디쉬(20)로 유동하게 된다. 이러한 유동을 위하여, 래들(10)에는 턴디쉬(20)를 향해 연장하는 슈라우드 노즐(Shroud nozzle, 15)이 설치된다. 슈라우드 노즐(15)은 용강(M)이 공기에 노출되어 산화?질화되지 않도록 턴디쉬(20) 내의 용강에 잠기도록 연장한다. 슈라우드 노즐(15)의 파손 등으로 용강(M)이 공기 중에 노출된 경우를 오픈 캐스팅(Open casting)이라 한다.Referring to this figure, the molten steel (M) is to flow to the tundish 20 in the state accommodated in the ladle (10). For this flow, the ladle 10 is provided with a shroud nozzle 15 extending toward the tundish 20. The shroud nozzle 15 extends to be immersed in the molten steel in the tundish 20 so that the molten steel M is not exposed to air and oxidized and nitrided. The case where molten steel M is exposed to air due to breakage of shroud nozzle 15 is called open casting.

턴디쉬(20) 내의 용강(M)은 주형(30) 내로 연장하는 침지 노즐(SEN, Submerged Entry Nozzle, 25)에 의해 주형(30) 내로 유동하게 된다. 침지 노즐(25)은 주형(30)의 중앙에 배치되어, 침지 노즐(25)의 양 토출구에서 토출되는 용강(M)의 유동이 대칭을 이룰 수 있도록 한다. 침지 노즐(25)을 통한 용강(M)의 토출의 시작, 토출 속도, 및 중단은 침지 노즐(25)에 대응하여 턴디쉬(20)에 설치되는 스톱퍼(stopper, 21)에 의해 결정된다. 구체적으로, 스톱퍼(21)는 침지 노즐(25)의 입구를 개폐하도록 침지 노즐(25)과 동일한 라인을 따라 수직 이동될 수 있다. 침지 노즐(25)을 통한 용강(M)의 유동에 대한 제어는, 스톱퍼 방식과 다른, 슬라이드 게이트(Slide gate) 방식을 이용할 수도 있다. 슬라이드 게이트는 판재가 턴디쉬(20) 내에서 수평 방향으로 슬라이드 이동하면서 침지 노즐(25)을 통한 용강(M)의 토출 유량을 제어하게 된다.The molten steel M in the tundish 20 flows into the mold 30 by a submerged entry nozzle 25 extending into the mold 30. The immersion nozzle 25 is disposed in the center of the mold 30 so that the flow of molten steel M discharged from both discharge ports of the immersion nozzle 25 can be symmetrical. The start, discharge speed, and stop of the discharge of the molten steel M through the immersion nozzle 25 are determined by a stopper 21 installed in the tundish 20 corresponding to the immersion nozzle 25. Specifically, the stopper 21 may be vertically moved along the same line as the immersion nozzle 25 to open and close the inlet of the immersion nozzle 25. Control of the flow of the molten steel M through the immersion nozzle 25 may use a slide gate method, which is different from the stopper method. The slide gate controls the discharge flow rate of the molten steel M through the immersion nozzle 25 while the sheet material slides in the horizontal direction in the tundish 20.

주형(30) 내의 용강(M)은 주형(30)을 이루는 벽면에 접한 부분부터 응고하기 시작한다. 이는 용강(M)의 중심보다는 주변부가 수냉되는 주형(30)에 의해 열을 잃기 쉽기 때문이다. 주변부가 먼저 응고되는 방식에 의해, 스트랜드(80)의 주조 방향을 따른 뒷부분은 미응고 용강(82)이 용강(M)이 응고된 응고쉘(81)에 감싸여진 형태를 이루게 된다.The molten steel M in the mold 30 starts to solidify from the part in contact with the wall surface of the mold 30. This is because heat is more likely to be lost by the mold 30 in which the periphery is cooled rather than the center of the molten steel M. The rear portion along the casting direction of the strand 80 is formed by the non-solidified molten steel 82 being wrapped around the solidified shell 81 in which the molten steel M is solidified by the method in which the peripheral portion first solidifies.

핀치롤(70, 도 1)이 완전히 응고된 스트랜드(80)의 선단부(83)를 잡아당김에 따라, 미응고 용강(82)은 응고쉘(81)과 함께 주조 방향으로 이동하게 된다. 미응공 용강(82)은 위 이동 과정에서 냉각수를 분사하는 스프레이(65)에 의해 냉각된다. 이는 스트랜드(80)에서 미응고 용강(82)이 차지하는 두께가 점차로 작아지게 한다. 스트랜드(80)가 일 지점(85)에 이르면, 스트랜드(80)는 전체 두께가 응고쉘(81)로 채워지게 된다. 응고가 완료된 스트랜드(80)는 절단 지점(91)에서 일정 크기로 절단되어 슬라브 등과 같은 제품(P)으로 나뉘어진다.As the pinch roll 70 (FIG. 1) pulls the tip portion 83 of the fully solidified strand 80, the unsolidified molten steel 82 moves together with the solidified shell 81 in the casting direction. Uncondensed molten steel 82 is cooled by a spray 65 for spraying cooling water in the course of the above movement. This causes the thickness of the uncooled steel (82) in the strand (80) to gradually decrease. When the strand 80 reaches a point 85, the strand 80 is filled with the solidification shell 81 in its entire thickness. The solidified strand 80 is cut to a predetermined size at the cutting point 91 and divided into a product P such as a slab.

주형(30) 및 그와 인접한 부분에서의 용강(M)의 형태에 대해서는 도 3을 참조하여 설명한다. 도 3은 도 2의 주형(30) 및 그와 인접한 부분에서의 용강(M)의 분포 형태를 보인 개념도이다.The form of the molten steel M in the mold 30 and the part adjacent to it is demonstrated with reference to FIG. FIG. 3 is a conceptual diagram illustrating a distribution form of molten steel M in the mold 30 and adjacent portions of FIG. 2.

도 3을 참조하면, 침지 노즐(25)의 단부 측에는 통상적으로 도면상 좌우에 한 쌍의 토출구(25a)들이 형성된다{주형(30) 및 침지 노즐(25) 등의 형태는 중심선(C)을 기준으로 대칭되는 것으로 가정하여, 본 도면에서는 좌측만을 표시한다}.Referring to FIG. 3, a pair of discharge ports 25a are typically formed at the end side of the immersion nozzle 25 on the left and right sides of the drawing (in the form of the mold 30 and the immersion nozzle 25, the center line C is formed). Assuming that the reference is symmetrical, only the left side is shown in this drawing}.

토출구(25a)에서 아르곤(Ar) 가스와 함께 토출되는 용강(M)은 화살표(A1, A2)로 표시된 바와 같이 상측을 향한 방향(A1)과 하측을 향한 방향(A2)으로 유동하는 궤적을 그리게 된다.The molten steel M discharged together with the argon (Ar) gas from the discharge port 25a draws a trajectory flowing in the upward direction A1 and downward direction A2 as indicated by arrows A1 and A2. do.

주형(30) 내부의 상부에는 파우더 공급기(50)로부터 공급된 파우더에 의해 파우더층(51)이 형성된다. 파우더층(51)은 파우더가 공급된 형태대로 존재하는 층과 용강(M)의 열에 의해 소결된 층{소결층이 미응고 용강(82)에 더 가깝게 형성됨}을 포함할 수 있다. 파우더층(51)의 하측에는 파우더가 용강(M)에 의해 녹아서 형성된 슬래그층 또는 액체 유동층(52)이 존재하게 된다. 액체 유동층(52)은 주형(30) 내의 용강(M)의 온도를 유지하고 이물질의 침투를 차단한다. 파우더층(51)의 일부는 주형(30)의 벽면에서 응고되어 윤활층(53)을 형성한다. 윤활층(53)은 응고쉘(81)이 주형(30)에 붙지 않도록 윤활하는 기능을 한다. The powder layer 51 is formed on the upper part of the mold 30 by the powder supplied from the powder supplier 50. The powder layer 51 may include a layer present in a form in which the powder is supplied and a layer sintered by the heat of the molten steel M (sintered layer is formed closer to the unsolidified molten steel 82). Below the powder layer 51, a slag layer or a liquid fluidized layer 52 formed by melting powder by molten steel M is present. The liquid fluidized bed 52 maintains the temperature of the molten steel M in the mold 30 and blocks the ingress of foreign matter. A portion of the powder layer 51 solidifies at the wall surface of the mold 30 to form a lubrication layer 53. The lubrication layer 53 functions to lubricate the solidified shell 81 so as not to stick to the mold 30.

응고쉘(81)의 두께는 주조 방향으로 따라 진행할수록 두꺼워진다. 응고쉘(81)의 주형(30) 위치한 부분은 두께가 얇으며, 주형(30)의 오실레이션에 따라 자국(Ocillation mark, 87)이 형성되기도 한다. 응고쉘(81)은 지지롤(60)에 의해 지지되며, 물을 분사하는 스프레이(65)에 의해 그 두께가 두꺼워진다. 응고쉘(81)은 두꺼워지다가 일 부분이 볼록하게 돌출하는 벌징(Bulging) 영역(88)이 형성되기도 한다.
The thickness of the solidification shell 81 becomes thicker as it progresses along the casting direction. The portion where the mold 30 of the solidification shell 81 is positioned is thin, and an oscillation mark 87 may be formed according to the oscillation of the mold 30. The solidification shell 81 is supported by the support roll 60, and the thickness thereof is thickened by the spray 65 for spraying water. The solidification shell 81 may be thickened, and a bulging region 88 may be formed in which a portion protrudes convexly.

이하에서는, 본 발명의 일실시예인 침지 노즐 예열 버너 장치 및 침지 노즐 예열 방법에 대하여 도 4 및 도 5를 참조하여, 상세하게 설명하도록 한다. Hereinafter, the immersion nozzle preheat burner device and the immersion nozzle preheating method which is an embodiment of the present invention will be described in detail with reference to FIGS. 4 and 5.

도 4는 본 발명의 일실시예인 침지 노즐 예열 버너 장치의 구성이 도시되어 있다.Figure 4 is a configuration of the immersion nozzle preheat burner device is an embodiment of the present invention.

도시된 바와 같이, 본 발명의 일실시예인 침지 노즐 예열 버너 장치(100)은 하우징(110, 110', 110")과, 가스 공급부(120), 산소 공급부(공기 공급부)(130), 점화부(140, 140', 140")를 포함하는 버너가 복수개 나열되어 있다.As shown, the immersion nozzle preheat burner apparatus 100 according to an embodiment of the present invention includes a housing 110, 110 ′, 110 ″, a gas supply unit 120, an oxygen supply unit (air supply unit) 130, and an ignition unit. A plurality of burners including 140, 140 ', 140 "are listed.

하우징(110)은 그 상부에 침지 노즐(25)이 삽입되기 위한 홀(112)이 구비되어 있으며, 또한, 연소가스가 배출되기 위한 배출구(111)을 포함하고 있다. 상기 하우징은 그 내구성을 증진하기 위해, 이중 구조로 설계될 수 있다. 그리고, 하우징의 하부에는 버너가 설치될 수 있다.The housing 110 is provided with a hole 112 through which the immersion nozzle 25 is inserted, and includes a discharge port 111 through which the combustion gas is discharged. The housing can be designed in a dual structure to enhance its durability. The burner may be installed at the lower portion of the housing.

상기 버너는 가스 공급부(120), 공기 공급부(130), 및 점화부(140)를 포함한다. The burner includes a gas supply unit 120, an air supply unit 130, and an ignition unit 140.

가스 공급부(120)는 액화 천연가스, 액화 프로판 가스등의 가스를 공급하기 위한 공급부로서, 펌핑 장치(도시되지 않음)를 통해, 하우징(110) 내에 설치된 점화부(120)까지 가스가 공급되게 된다.The gas supply unit 120 is a supply unit for supplying gas such as liquefied natural gas, liquefied propane gas, and the gas is supplied to the ignition unit 120 installed in the housing 110 through a pumping device (not shown).

공기 공급부(130)는, 상기 가스를 점화시키기 위해 필요한 산소를 상기 하우징(110) 내에 공급하기 위한 구성요소이다. 펌핑장치(도시되지 않음)에 의해, 상기 공기를 하우징(110) 내에 설치된 점화부(140)까지 공급하게 된다.The air supply unit 130 is a component for supplying oxygen necessary to ignite the gas into the housing 110. By the pumping device (not shown), the air is supplied to the ignition unit 140 installed in the housing 110.

점화부(140)는 상기 공기공급부(130) 및 상기 가스 공급부(120)로부터 공급되는 산소와 연료용 가스(액화 천연가스 및 액화 프로판가스 등)를 연소시켜, 상기 하우징(140)의 상부의 홀(112)로부터 삽입되는 침지노즐(25)에 대하여 예열을 실행하게 된다. 이 때, 예열 온도는 용강의 온도를 고려하여 대략 1100 도에서 1300도 까지 예열을 하게된다. 이 침지 노즐의 예열 온도를 제어하기 하기 위해 제어부가 더 포함될 수 있다. 즉, 제어부는 각각의 버너를 독립제어함으로써, 각 하우징내의 침지 노즐(25)을 별도의 온도로 예열할 수 있다.The ignition unit 140 burns oxygen and fuel gas (liquefied natural gas, liquefied propane gas, etc.) supplied from the air supply unit 130 and the gas supply unit 120 to form a hole in the upper portion of the housing 140. Preheating is performed on the immersion nozzle 25 inserted from 112. At this time, the preheating temperature is preheated from about 1100 to 1300 degrees in consideration of the temperature of the molten steel. The control unit may be further included to control the preheating temperature of the immersion nozzle. That is, the controller can preheat the immersion nozzle 25 in each housing to a separate temperature by independently controlling each burner.

도 4에 도시된 바와 같이, 하우징이 복수개 포함되는 경우, 상기 제어부는,상기 침지 노즐들 중 양측에 배치된 침지 노즐을 상대적으로 높은 온도로 예열하도록 상기 버너를 제어할 수 있다. 통상, 턴디쉬(20)에 있어서, 양측은 중앙에 비하여 온도가 다소 낮게 된다. 따라서, 양측에 배치된 침지노즐에서 용강의 응고 현상이 일어나기 쉽다. 따라서, 양측의 예열 온도를 더 높게 하여 침지 노즐(25)의 내경에 발생할 수 있는 용강 응고 현상을 방지하게 된다. 예를 들면, 중앙의 침지 노즐(25)은 대략 1150도로 예열하고, 양측의 침지 노즐은 1250도로 예열할 수 있다.
As shown in FIG. 4, when a plurality of housings are included, the controller may control the burner to preheat the immersion nozzles disposed at both sides of the immersion nozzles to a relatively high temperature. Usually, in the tundish 20, both sides become somewhat lower in temperature than the center. Therefore, solidification phenomenon of molten steel is likely to occur in the immersion nozzles disposed on both sides. Therefore, the preheating temperature of both sides is made higher to prevent the molten steel solidification phenomenon which may occur in the inner diameter of the immersion nozzle 25. For example, the central immersion nozzle 25 may be preheated at approximately 1150 degrees, and the immersion nozzles at both sides may be preheated at 1250 degrees.

이하에서는 상술한 침지 노즐 예열 버너 장치를 이용한 침지 노즐 예열 방법을 도 5를 참조하여 설명하도록 한다.Hereinafter, the immersion nozzle preheating method using the immersion nozzle preheat burner apparatus described above will be described with reference to FIG. 5.

도 5는 본 발명의 다른 실시예인 침지 노즐 예열 방법을 설명하기 위한 흐름도이다.5 is a flowchart illustrating a immersion nozzle preheating method according to another embodiment of the present invention.

우선 복수의 하우징(110,110',110")을 포함한 예열 버너 장치를 제공한다(S1). 각 하우징에는 도 4에 도시된 바와 같이 예열 버너가 제공된다. 그 다음, 상기 하우징의 상부에 형성된 홀(112)을 통해 침지 노즐이 상기 하우징 내로 삽입한다(S3). 그 다음 예열 버너를 점화시켜 하우징(110) 내에 삽입된 침지 노즐(25)을 예열한다(S5). 이 때, 상기 침지 노즐이 적어도 3개 예열 되는 경우, 양측에 배치된 침지노즐을 상대적으로 높은 온도로 예열하게 된다. 예열이 완료되면, 침지 노즐(25)을 턴디쉬(20)로 이동시킨다(S7).
First, a preheat burner device including a plurality of housings 110, 110 ', and 110 "is provided (S1). Each housing is provided with a preheat burner as shown in Fig. 4. Next, a hole formed in an upper portion of the housing ( The immersion nozzle is inserted into the housing through 112. Then, the preheat burner is ignited to preheat the immersion nozzle 25 inserted into the housing 110 (S5), wherein the immersion nozzle is at least In case of three preheating, the immersion nozzles disposed at both sides are preheated to a relatively high temperature, and when the preheating is completed, the immersion nozzle 25 is moved to the tundish 20 (S7).

본 상세한 설명에서는 가스를 이용하여 침지노즐을 예열하는 방식에 대하여 설명하고 있으나, 이는 일예에 불과하고, 전기를 이용하거나, 레이저를 이용한 방법 등 다양한 방식이 이용될 수 있음이 이해되어야 할 것이다.
In this detailed description, a method of preheating the immersion nozzle using a gas is described, but it is only an example, and it should be understood that various methods such as a method using electricity or a laser may be used.

상기와 같은 침지 노즐 예열 버너 장치 및 이를 이용한 침지 노즐 예열 방법은 위에서 설명된 실시예들의 구성과 작동 방식에 한정되는 것이 아니다. 상기 실시예들은 각 실시예들의 전부 또는 일부가 선택적으로 조합되어 다양한 변형이 이루어질 수 있도록 구성될 수도 있다.
The immersion nozzle preheat burner device and the immersion nozzle preheating method using the same are not limited to the configuration and operation of the above-described embodiments. The above embodiments may be configured such that various modifications may be made by selectively combining all or part of the embodiments.

10: 래들 15: 슈라우드 노즐
20: 턴디쉬 25: 침지 노즐
30: 주형 40: 주형 오실레이터
50: 파우더 공급기 51: 파우더층
52: 액체 유동층 53: 윤활층
60: 지지롤 65: 스프레이
70: 핀치롤 80: 스트랜드
81: 응고쉘 82: 미응고 용강
83: 선단부 85: 응고 완료점
87: 오실레이션 자국 88: 벌징 영역
100: 침지 노즐 예열 버너 장치 110: 하우징
120: 가스 공급부 130: 공기공급부
140: 점화부10: ladle 15: shroud nozzle
20: tundish 25: immersion nozzle
30: mold 40: mold oscillator
50: powder feeder 51: powder layer
52: liquid fluidized bed 53: lubricating layer
60: support roll 65: spray
70: pinch roll 80: strand
81: solidified shell 82: unsolidified molten steel
83: tip 85: solidification completion point
87: oscillation mark 88: bulging area
100: immersion nozzle preheat burner device 110: housing
120: gas supply unit 130: air supply unit
140: ignition unit

Claims (6)

침지 노즐이 삽입되는 홀, 및 연소 가스를 배출하는 배출구를 상부에 구비함과 아울러 내구성 증진을 위해 이중 구조로 설계되는 적어도 하나의 하우징;
상기 침지 노즐을 예열하기 위해 상기 하우징 내에 설치되며, 산소를 공급하기 위한 공기 공급부, 연소용 가스를 공급하기 위한 가스 공급부, 상기 산소를 이용하여 상기 가스를 점화시키기 위한 점화부를 구비하는 버너; 및
상기 침지 노즐의 예열 온도를 제어하기 위해 상기 버너를 제어하는 제어부;를 포함하며,
상기 제어부는,
상기 하우징들 중 외곽에 삽입된 상기 침지 노즐을 상대적으로 높은 온도로 예열하도록 상기 버너를 제어하는 침지 노즐 예열 버너 장치.
At least one housing having a hole into which the immersion nozzle is inserted and an outlet for discharging combustion gas, and having a double structure designed to increase durability;
A burner installed in the housing for preheating the immersion nozzle and having an air supply unit for supplying oxygen, a gas supply unit for supplying combustion gas, and an ignition unit for igniting the gas using the oxygen; And
And a control unit controlling the burner to control a preheating temperature of the immersion nozzle.
The control unit,
An immersion nozzle preheat burner device for controlling the burner to preheat the immersion nozzle inserted in the outer one of the housings to a relatively high temperature.
삭제delete 삭제delete 삭제delete 삭제delete 삭제delete
KR1020100028896A 2010-03-31 2010-03-31 Preheating burner apparatus for submerged entry nozzle and method for preheating submerged entry nozzle using the same KR101204935B1 (en)