KR101017223B1 - Elastic pavement excellent in elastic deformability and water permeability

Info

Publication number: KR101017223B1
Application number: KR1020100067147A
Authority: KR
Inventors: 김동현; 이태섭
Original assignee: 이태섭; 김동현
Priority date: 2010-07-13
Filing date: 2010-07-13
Publication date: 2011-02-28
Also published as: WO2012008646A1

Abstract

PURPOSE: An elastic paving material is provided to improve permeability by an air gap which remarkably grows larger. CONSTITUTION: An elastic paving material comprises an anchor mat and an elasticity chip(20). Fiber is made of a plastic material. The elasticity chip is combined on one side of the anchor mat with a binder. The elasticity chip covers the protruded part of the anchor mat and forms an elastic layer(21).

Description

탄성 변형성 및 투수성이 우수한 탄성포장재{ELASTIC PAVEMENT EXCELLENT IN ELASTIC DEFORMABILITY AND WATER PERMEABILITY}Elastic packaging material with excellent elastic deformation and permeability {ELASTIC PAVEMENT EXCELLENT IN ELASTIC DEFORMABILITY AND WATER PERMEABILITY}

본 발명은 탄성 변형성 및 투수성이 우수한 탄성포장재에 관한 것으로, 보다 상세하게는, 합성수지 섬유로 이루어진 앵커매트 상에 탄성칩을 접합함으로서 앵커매트 자체의 탄성 및 탄성층의 탄성을 이용하여 탄성 변형성이 증대되고, 앵커매트 자체의 공극과 앵커매트에 접착된 탄성칩 간의 공극으로 투수성이 향상된 탄성 변형성 및 투수성이 우수한 탄성포장재에 관한 것이다. The present invention relates to an elastic packaging material having excellent elastic deformation and water permeability, and more particularly, by bonding an elastic chip on an anchor mat made of synthetic resin fiber, elastic deformation of the anchor mat itself using elasticity and elasticity of the elastic layer. The present invention relates to an elastic packaging material having excellent elastic deformation and water permeability, which is increased and improved in water permeability by voids between the pores of the anchor mat itself and the elastic chips bonded to the anchor mat.

최근 여가 생활에 대한 비중이 높아짐에 따라 운동장 또는 경기장에 인조잔디를 조성하는 경우가 늘고 있다. 또한 산책 또는 운동을 위한 보도를 조성할 때에도 최근에는 탄성층으로 도포하는 경우가 늘고 있다.Recently, as the proportion of leisure life increases, artificial turf is being built on the playground or the stadium. In addition, when forming a walkway for walking or exercise in recent years has been increasingly applied as an elastic layer.

이러한 인조잔디 또는 탄성층을 포함한 포장도로는 상부로 유입되는 빗물이 지반으로 유입되도록 함으로서 지반에 수분공급 및 배수성능 향상을 달성하고 빗물의 저장을 통해 빗물을 활용할 수 있도록 빗물의 투수 및 저장 기능을 구비하도록 설계되고 있다.The pavement including artificial turf or elastic layer allows the rainwater flowing into the ground to improve the water supply and drainage performance of the ground, and the water permeation and storage function to utilize the rainwater through the storage of rainwater. It is designed to have.

그리고 인조잔디 또는 탄성층은 그 위에서 사람들이 다양한 신체활동을 할 때에 하중을 흡수하여 몸에 무리가 가지 않도록 해 주고, 장기간 사용시에도 평탄성을 유지하여 물고임이나 걸림을 방지하는 것이 중요하다.In addition, artificial turf or elastic layer absorbs loads when people perform various physical activities thereon so that the body does not overdo it, and it is important to maintain flatness even in long-term use to prevent bite or jam.

그런데 종래의 인조잔디의 하부에 설치되는 탄성포장재와 탄성층을 구성하는 탄성포장재는 고무칩과 바인더의 결합에 의해 이루어지는 것이 대부분이었다. 이러한 고무칩과 바인더에 의한 탄성포장재는 고무칩간의 결합에 의해 그 형태가 유지되므로 고무칩간의 결합력이 증대되도록 바인더의 투입량이 정해져야 하고 그로 인해 고무칩간에는 공극이 거의 없는 상태로 결합되게 된다. By the way, the elastic packaging material constituting the elastic packaging material and the elastic layer provided in the lower portion of the conventional artificial grass was mostly made by the combination of the rubber chip and the binder. Since the shape of the elastic packaging material by the rubber chip and the binder is maintained by the coupling between the rubber chips, the amount of the binder should be determined so as to increase the bonding force between the rubber chips, thereby causing the rubber chips to be bonded with little voids.

따라서 종래의 탄성포장재에서는, 고무칩간의 강인한 결합으로 인해 탄성포장재의 탄성 및 투수성이 저하되는 문제점이 있었다. 특히 바인더에 의해 결합된 고무칩의 외면의 변형이 제한되어 탄성 변형에 의한 하중 흡수능력이 저하되고, 하중을 지속적으로 받으면 고무칩간의 결합이 와해되면서 탄성포장재의 파손 또는 함몰을 초래하게 된다. Therefore, in the conventional elastic packaging material, there is a problem that the elasticity and permeability of the elastic packaging material is lowered due to the strong bonding between the rubber chips. In particular, the deformation of the outer surface of the rubber chip bonded by the binder is limited, the load absorbing capacity is reduced by the elastic deformation, and if the load is continuously received, the bond between the rubber chips is broken, causing breakage or depression of the elastic packaging material.

본 발명은 상기와 같은 문제점을 해소하기 위한 것으로, 본 발명의 목적은 횡방향 및 종방향으로 가해지는 하중에 대해 탄성 변형력이 증대되고 안정적으로 복원될 수 있는 탄성 변형성 및 투수성이 우수한 탄성포장재를 제공하는 데 있다.The present invention is to solve the above problems, the object of the present invention is to increase the elastic deformation force against the load applied in the transverse direction and longitudinal direction and excellent elastic deformation and permeability elastic packaging material that can be stably restored To provide.

본 발명의 다른 목적은, 전체 면적이 종래에 비해 현저히 커진 공극으로 인해 투수성이 현저히 향상된 탄성 변형성 및 투수성이 우수한 탄성포장재를 제공하는 데 있다. Another object of the present invention is to provide an elastic packaging material having excellent elastic deformation property and water permeability which is significantly improved in water permeability due to the voids of which the total area is significantly larger than in the related art.

상기한 바와 같은 목적을 달성하기 위한 본 발명의 특징에 따르면, 본 발명은, 탄성 변형성 및 투수성이 우수한 탄성포장재에 관한 것으로, 합성수지재의 다수개의 섬유가 부정형으로 얽혀서 격자형의 산과 골을 연속적으로 형성하는 앵커매트와, 상기 앵커매트의 일면 상에 바인더에 의해 결합되어 상기 앵커매트의 산을 덮어 탄성층을 형성하는 탄성칩을 포함하고, 상기 탄성칩은 2~10㎜의 입자크기를 갖는 고무칩이고, 상기 탄성층은, 상기 고무칩 75~85중량%와 바인더 15~20중량%를 혼합하여 이루어지거나, 상기 탄성칩은 5~8㎜의 입자크기를 갖는 코르크칩이고, 상기 탄성층은, 상기 코르크칩 40~50중량%와 바인더 50~60중량%를 혼합하여 이루어질 수 있다.According to a feature of the present invention for achieving the object as described above, the present invention relates to an elastic packaging material excellent in elastic deformation and water permeability, a plurality of fibers of the synthetic resin material is entangled in an irregular form to continuously form a grid of acid and bone Anchor mat to be formed, and an elastic chip coupled to one surface of the anchor mat by a binder to cover the acid of the anchor mat to form an elastic layer, the elastic chip is a rubber having a particle size of 2 ~ 10㎜ The elastic layer is made of a mixture of 75 to 85% by weight of the rubber chip and 15 to 20% by weight of the binder, or the elastic chip is a cork chip having a particle size of 5 ~ 8㎜, the elastic layer is It may be made by mixing 40 to 50% by weight of the cork chip and 50 to 60% by weight of the binder.

삭제delete

이러한 경우에, 상기 탄성포장재는 상기 탄성층 상에 적층되는 마감재를 더 포함하여 구성될 수도 있다.In this case, the elastic packaging material may further comprise a finishing material laminated on the elastic layer.

이때, 상기 마감재는 인조잔디일 수 있다.In this case, the finishing material may be artificial turf.

본 발명에 따른 탄성 변형성 및 투수성이 우수한 탄성포장재에 의하면, 앵커매트의 섬유에 탄성칩이 접착되므로 횡방향 하중뿐만 아니라 종방향 하중에 대해서도 앵커매트가 탄성칩을 지지하여 줌으로서 탄성포장재가 파손되거나 변형되지 않고, 탄성칩 자체의 탄성뿐만 아니라, 앵커매트 자체의 산과 골의 형상 및 그 형상으로 인해 앵커매트 저부에 형성되는 공간에 의해 앵커매트는 탄성을 발휘할 수 있으므로, 탄성도가 증대되고 탄성 변형된 상태에서 복원력도 현저히 향상되는 효과가 있다.According to the elastic packaging material having excellent elastic deformation and water permeability according to the present invention, since the elastic chip is bonded to the fibers of the anchor mat, the elastic mat member is damaged by supporting the elastic chip not only in the transverse load but also in the longitudinal load. The anchor mat can exhibit elasticity not only by elasticity of the elastic chip itself, but also by the space formed at the bottom of the anchor mat due to the shape and the shape of the peaks and valleys of the anchor mat itself, thereby increasing elasticity and elasticity. In the deformed state, the resilience is also significantly improved.

또한 본 발명에 따르면, 상기 탄성칩은 서로간에 밀착되게 접착되지 않아도 무방하므로 탄성칩 사이에는 전체 면적이 종래에 비해 현저히 커진 공극이 형성되어 상기 탄성칩 사이로의 배수가 원활한 장점이 있다. In addition, according to the present invention, since the elastic chips do not have to be adhered to each other in close contact with each other, there is an advantage that the gap between the elastic chips is significantly increased compared to the prior art, so that the drainage between the elastic chips is smooth.

도 1은 본 발명에 따른 탄성포장재의 사시도,
도 2는 본 발명에 따른 탄성포장재의 저면도,
도 3은 본 발명에 따른 앵커매트를 도시한 사시도,
도 4 및 도 5는 본 발명에 따른 탄성포장재의 작용을 도시한 단면도,
도 6은 본 발명에 따른 탄성포장재에 마감재가 추가된 상태를 도시한 단면도이다.1 is a perspective view of an elastic packaging material according to the present invention,
Figure 2 is a bottom view of the elastic packaging material according to the present invention,
Figure 3 is a perspective view of the anchor mat according to the present invention,
4 and 5 are cross-sectional views showing the action of the elastic packaging material according to the present invention,
Figure 6 is a cross-sectional view showing a state in which the finishing material is added to the elastic packaging material according to the present invention.

이하에서는 본 발명에 따른 탄성 변형성 및 투수성이 우수한 탄성포장재에 관하여 첨부되어진 도면과 더불어 설명하기로 한다.
Hereinafter will be described with reference to the accompanying drawings with respect to the elastic packaging material excellent in elastic deformation and water permeability.

도 1은 본 발명에 따른 탄성포장재의 사시도이고, 도 2는 본 발명에 따른 탄성포장재의 저면도이며, 도 3은 본 발명에 따른 앵커매트를 도시한 사시도이고, 도 4 및 도 5는 본 발명에 따른 탄성포장재의 작용을 도시한 단면도이다.1 is a perspective view of an elastic packaging material according to the invention, Figure 2 is a bottom view of the elastic packaging material according to the invention, Figure 3 is a perspective view showing an anchor mat according to the invention, Figures 4 and 5 the present invention Cross-sectional view showing the action of the elastic packaging material according to.

도시된 바와 같이, 본 실시예에 따른 탄성 변형성 및 투수성이 우수한 탄성포장재은, 앵커매트(10)와 탄성칩(20)으로 구성된다.As shown, the elastic packaging material excellent in elastic deformation and water permeability according to the present embodiment is composed of an anchor mat 10 and the elastic chip 20.

상기 앵커매트(10)는 강인하고 신축성이 좋은 입체구조를 지닌 합성수지 망으로서 95%의 빈 공간을 가진 자재이다. 다시 말하면, 상기 앵커매트(10)는 합성수지재로 이루어진 다수개의 섬유(11)가 일정한 형태 없는 부정형으로 얽혀서 격자형의 산(13)과 골(15)을 연속적으로 형성한다. 이때 앵커매트(10)에 사용되는 합성수지에는 특별한 한정은 없지만, 섬유(11)로 될 수 있는 성질이 우수한 나일론 6을 사용하는 것이 바람직하다.The anchor mat 10 is a synthetic resin network having a strong and flexible three-dimensional structure is a material having a void space of 95%. In other words, the anchor mat 10 is a plurality of fibers 11 made of a synthetic resin material is entangled in a non-formal irregular shape to form a continuous acid (13) and valleys 15 of the grid. At this time, the synthetic resin used in the anchor mat 10 is not particularly limited, it is preferable to use nylon 6 excellent in properties that can be made of fibers (11).

한편, 탄성칩(20)은 상기 앵커매트(10)의 일면 상에 바인더에 의해 결합되는 것으로, 상기 앵커매트(10)의 산(13)을 덮어 탄성층(21)을 형성한다. 다시 말해, 상기 탄성칩(20)은 상기 앵커매트(10)를 이루는 섬유(11)에 바인더를 통해 접착되고, 그렇게 접착되는 탄성층(21)이 쌓이면서 상기 앵커매트(10) 상으로 앵커매트(10)를 덮는 탄성층(21)을 형성하게 된다.On the other hand, the elastic chip 20 is bonded by a binder on one surface of the anchor mat 10, and covers the acid 13 of the anchor mat 10 to form an elastic layer 21. In other words, the elastic chip 20 is bonded to the fibers 11 constituting the anchor mat 10 through a binder, and the elastic layer 21 adhered to the anchor mat 10 is stacked on the anchor mat 10. The elastic layer 21 covering the 10 is formed.

이때 상기 탄성칩(20)은 앵커매트(10)의 섬유(11)에 접착되므로 탄성칩(20) 간에 밀착되지 않아도 횡방향 하중에도 파손되거나 변형되지 않을 뿐만 아니라, 앵커매트(10)에 지지된 상태로 자유롭게 휘어질 수 있다. 또한 상기 탄성칩(20)은 서로간에 밀착되게 접착되지 않아도 무방하므로 탄성칩(20) 사이에는 많은 공극이 형성되어 도 4에 도시된 바와 같이, 상기 탄성칩(20) 사이로의 배수가 원활하다. 아울러, 도 5에 도시된 바와 같이, 탄성칩(20) 자체의 탄성뿐만 아니라, 앵커매트(10) 자체의 산(13)과 골(15)의 형상 및 그 형상으로 인해 앵커매트(10) 저부에 형성되는 공간에 의해 앵커매트(10)는 탄성을 발휘할 수 있으므로, 탄성도가 증대되고 탄성 변형된 상태에서 복원력도 현저히 향상된다.At this time, since the elastic chip 20 is bonded to the fibers 11 of the anchor mat 10, the elastic chip 20 may not be damaged or deformed even in the lateral load even if the elastic chips 20 are not in close contact with each other. It can be bent freely in a state. In addition, since the elastic chip 20 does not have to be closely adhered to each other, many voids are formed between the elastic chips 20, and as shown in FIG. 4, the drainage between the elastic chips 20 is smooth. In addition, as shown in FIG. 5, not only the elasticity of the elastic chip 20 itself, but also the shape of the peak 13 and the valley 15 of the anchor mat 10 itself and the shape of the anchor mat 10 may be lower. Since the anchor mat 10 can exhibit elasticity due to the space formed therein, the elasticity is increased and the restoring force is remarkably improved in the elastically deformed state.

이러한 탄성칩(20)은 고무칩 또는 코르크칩일 수 있다.The elastic chip 20 may be a rubber chip or a cork chip.

탄성칩(20)으로 고무칩을 사용하는 경우에는, 상기 고무칩은 2~10㎜의 입자크기를 갖고, 이때 상기 탄성층(21)은 상기 고무칩 75~85중량%와 바인더 15~25중량%를 혼합하여 이루어진다. When the rubber chip is used as the elastic chip 20, the rubber chip has a particle size of 2 ~ 10 mm, wherein the elastic layer 21 is 75 to 85% by weight of the rubber chip and 15 to 25 weight of the binder Made by mixing%.

그리고 상기 고무칩은 상기와 같은 입자크기 범위 내에서 2~4㎜의 입자크기를 갖는 형태, 및 5~10㎜의 입자크기를 갖는 형태로 분류할 수 있다.The rubber chip may be classified into a form having a particle size of 2 to 4 mm and a particle size of 5 to 10 mm within the particle size range as described above.

이는 이러한 입자크기의 차이에 따라 탄성층(21)에 형성되는 공극의 크기가 달라지게 되기 때문이다. 즉, 입자크기가 크면 공극의 크기는 커지고 입자크기가 작아지면 공극의 크기는 상대적으로 작아진다. 따라서 이러한 특성을 이용하여 탄성층(21)에 형성되는 공극의 크기를 조절할 수 있다.This is because the size of the voids formed in the elastic layer 21 is changed according to the difference in particle size. That is, the larger the particle size, the larger the size of the pores, and the smaller the particle size, the smaller the size of the pores. Therefore, the size of the voids formed in the elastic layer 21 can be adjusted by using these characteristics.

또한 상기 탄성칩(20)으로 코르크칩이 사용되는 경우에는, 상기 코르크칩은 5~8㎜의 입자크기를 갖고, 이때 탄성층(21)은 상기 코르크칩 40~50중량%와 바인더 50~60중량%를 혼합하여 이루어진다.In addition, when the cork chip is used as the elastic chip 20, the cork chip has a particle size of 5 ~ 8㎜, wherein the elastic layer 21 is 40 to 50% by weight of the cork chip and the binder 50 to 60 By weight percent mixing.

이와 같은 구성의 탄성포장재의 전체 두께에 대해서는 특별한 한정이 없고, 가령, 가해지는 하중에 따라 두께를 조절할 수 있으며, 예를 들면, 대략 10㎜, 18㎜, 20㎜, 30㎜, 50㎜ 등으로 할 수 있다.There is no particular limitation on the overall thickness of the elastic packaging material having such a configuration, for example, the thickness can be adjusted according to the applied load, for example, about 10 mm, 18 mm, 20 mm, 30 mm, 50 mm and the like. can do.

그리고 이와 같이 구성되는 탄성포장재는, 도 6에 도시된 바와 같이, 추가적으로 마감재를 더 포함할 수 있다. 상기 마감재는 지면에 노출되어 직접적인 하중을 받는 부분으로서, 다양한 재료, 예를 들면, 탄성포장층, 천연잔디, 규사층 등이 사용될 수 있으나, 본 실시예에서는 이러한 마감재로서 인조잔디(30)가 사용되는 것이 예시되어 있다. And the elastic packaging material configured as described above, as shown in Figure 6, may further include a finish. The finishing material is a portion exposed to the ground and subjected to a direct load, various materials, for example, elastic packaging layer, natural grass, silica sand layer, etc. may be used, but in this embodiment, artificial turf 30 is used as such a finishing material. Is illustrated.

상기 인조잔디(30)는 상기 탄성층(21) 상에서 유동이 방지되도록 하부의 매트(31)가 접착제에 의해 상기 탄성층(21)에 접착된다.The artificial grass 30 is adhered to the elastic layer 21 by an adhesive to the lower mat 31 to prevent flow on the elastic layer 21.

만일 규사층을 마감재로 활용하기 위해서는, 입자크기 5~7㎜의 규사 90~95중량%와 바인더 5~10중량%를 혼합하여 적층함으로서 규사층을 형성한다.
If the silica sand layer is to be used as a finishing material, a silica sand layer is formed by mixing 90 to 95% by weight of silica sand with a particle size of 5 to 7 mm and 5 to 10% by weight of a binder.

다음으로 본 발명에 따른 탄성 변형성 및 투수성이 우수한 탄성포장재의 제조방법에 대해 5~10㎜의 고무칩을 사용하는 경우를 토대로 설명한다.Next, a method of manufacturing an elastic packaging material having excellent elastic deformation and water permeability according to the present invention will be described based on the case of using a rubber chip of 5 to 10 mm.

먼저 고무칩 80~85중량%와 바인더 15~20중량%를 혼합하여 1~2분간 교반한 후 앵커매트(10) 상부에 포설한다. 포설된 고무칩과 바인더의 혼합물에 대해 면고르기를 한 후, 항온롤러를 이용하여 대략 100~150℃ 범위를 유지한 상태로 수회 다짐한다. 다짐이 마무리되면 양생하여 본 발명에 따른 탄성포장재를 완성한다.First, 80 to 85% by weight of the rubber chip and 15 to 20% by weight of the binder are mixed and stirred for 1 to 2 minutes, and then placed on the anchor mat 10. After the surface of the mixture of the rubber chip and the binder is placed, and compacted several times while maintaining a range of approximately 100 ~ 150 ℃ using a constant temperature roller. When the compaction is finished, curing is completed to complete the elastic packaging material according to the present invention.

본 실시예에서 설명되는 2~4㎜의 고무칩과 5~8㎜의 코르크칩에 대해서도 동일한 제조방법이 적용된다.
The same manufacturing method is applied also to the rubber chip of 2-4 mm and the cork chip of 5-8 mm demonstrated in this Example.

본 발명의 권리는 위에서 설명된 실시예에 한정되지 않고 청구범위에 기재된 바에 의해 정의되며, 본 발명의 분야에서 통상의 지식을 가진 자가 청구범위에 기재된 권리범위 내에서 다양한 변형과 개작을 할 수 있다는 것은 자명하다.The rights of the present invention are not limited to the embodiments described above, but are defined by the claims, and those skilled in the art can make various modifications and adaptations within the scope of the claims. It is self-evident.

10 : 앵커매트 20 : 탄성칩
21 : 탄성층 30 : 인조잔디10: anchor mat 20: elastic chip
21: elastic layer 30: artificial turf

Claims

합성수지재의 다수개의 섬유(11)가 부정형으로 얽혀서 격자형의 산(13)과 골(15)을 연속적으로 형성하는 앵커매트(10)와,
상기 앵커매트(10)의 일면 상에 바인더에 의해 결합되어 상기 앵커매트(10)의 산(13)을 덮어 탄성층(21)을 형성하는 탄성칩(20)을 포함하고,
상기 탄성칩(20)은 2~10㎜의 입자크기를 갖는 고무칩이고, 상기 탄성층(21)은, 상기 고무칩 75~85중량%와 바인더 15~25중량%를 혼합하여 이루어지나, 또는 상기 탄성칩(20)은 5~8㎜의 입자크기를 갖는 코르크칩이고, 상기 탄성층(21)은, 상기 코르크칩 40~50중량%와 바인더 50~60중량%를 혼합하여 이루어지는 것을 특징으로 하는 탄성 변형성 및 투수성이 우수한 탄성포장재.A plurality of fibers 11 of the synthetic resin material is entangled in an irregular shape to form an anchor mat (10) and valleys (15) continuously,
It includes an elastic chip 20 coupled to one surface of the anchor mat 10 by a binder to cover the acid 13 of the anchor mat 10 to form an elastic layer 21,
The elastic chip 20 is a rubber chip having a particle size of 2 ~ 10㎜, the elastic layer 21 is made by mixing 75 to 85% by weight of the rubber chip and 15 to 25% by weight of the binder, or The elastic chip 20 is a cork chip having a particle size of 5 ~ 8㎜, the elastic layer 21 is characterized in that the cork chip 40-50% by weight and the binder 50-60% by weight Elastic packaging material excellent in elastic deformation and water permeability.

삭제delete

제1항에 있어서,
상기 탄성층(21) 상에 적층되는 마감재를 더 포함하는 것을 특징으로 하는 탄성 변형성 및 투수성이 우수한 탄성포장재.The method of claim 1,
Elastic packing material excellent in elastic deformation and water permeability, characterized in that it further comprises a finish laminated on the elastic layer (21).

제5항에 있어서,
상기 마감재는 인조잔디(30)인 것을 특징으로 하는 탄성 변형성 및 투수성이 우수한 탄성포장재.The method of claim 5,
The finishing material is an elastic packaging material having excellent elastic deformation and water permeability, characterized in that the artificial turf (30).