KR20110006071U - Structure of composite artificial turf for a football field - Google Patents

Structure of composite artificial turf for a football field Download PDF

Info

Publication number
KR20110006071U
KR20110006071U KR2020110003041U KR20110003041U KR20110006071U KR 20110006071 U KR20110006071 U KR 20110006071U KR 2020110003041 U KR2020110003041 U KR 2020110003041U KR 20110003041 U KR20110003041 U KR 20110003041U KR 20110006071 U KR20110006071 U KR 20110006071U
Authority
KR
South Korea
Prior art keywords
artificial turf
layer
elastic pad
thickness
football field
Prior art date
Application number
KR2020110003041U
Other languages
Korean (ko)
Inventor
김종필
권영훈
Original Assignee
코오롱글로텍주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코오롱글로텍주식회사 filed Critical 코오롱글로텍주식회사
Priority to KR2020110003041U priority Critical patent/KR20110006071U/en
Publication of KR20110006071U publication Critical patent/KR20110006071U/en

Abstract

본 고안은 축구장용 인조잔디 구조체에 관한 것으로, 보다 상세하게는 축구장용 인조잔디 구조체에 있어서, 기초지반층, 상기 기초지반층상에 원단이 2 내지 20㎜의 두께로 형성된 원단층, 상기 원단층상에 탄성패드가 10 내지 25㎜의 두께로 형성된 탄성패드층(또는 상기 기초지반층상에 탄성패드가 10 내지 25㎜의 두께로 형성된 탄성패드층, 상기 탄성패드층 상에 원단이 2 내지 20㎜의 두께로 형성된 원단층) 및 상기 탄성패드층상에(또는 원단층상에) 상기 인조잔디 파일을 고정시키는 지조직층과 인조잔디 파일을 포함하되, 상기 인조잔디 파일의 길이가 30 내지 65㎜임을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다The present invention relates to an artificial turf structure for a soccer field, and more particularly, in an artificial turf structure for a soccer field, a base layer, a fabric layer having a thickness of 2 to 20 mm on the base layer, and the fabric layer An elastic pad layer having an elastic pad having a thickness of 10 to 25 mm (or an elastic pad layer having an elastic pad having a thickness of 10 to 25 mm on the base ground layer, and a fabric having a thickness of 2 to 20 mm on the elastic pad layer) And an artificial turf layer for fixing the artificial turf file on the elastic pad layer (or the distal layer), wherein the length of the artificial turf file is 30 to 65 mm. Provide artificial turf structure for

Description

축구장용 인조잔디 구조체{Structure of composite artificial turf for a football field}Artificial turf structure for soccer field {Structure of composite artificial turf for a football field}

본 고안은 축구장용 인조잔디 구조체에 관한 것으로서, 보다 상세하게는 경기성 및 충격흡수성을 유지하면서 표면경화를 최소화 할 수 있는 축구장용 인조잔디 구조체에 관한 것이다.
The present invention relates to an artificial turf structure for a soccer field, and more particularly, to an artificial turf structure for a soccer field which can minimize surface hardening while maintaining playability and shock absorption.

인조잔디는 특별하게 사용하는 조경재료의 하나로서, 잔디의 형태를 갖추어 인공적으로 만든 잔디의 대용품이다. 미국에서 처음 제작된 이래 주로 스포츠 구장에 사용되었고 잔디의 생육이 불가능한 옥내 정원이나 일조시간이 극히 제한된 고층건물의 북쪽에 접한 옥외지역과 같은 곳에서 사용할 수 있다. 이러한 인조잔디는 항상 푸르름을 유지하고 환경조건의 제한을 받지 않아 시공 후 관리가 용이하다. 인조잔디가 시공된 인조잔디 구장은 일반 천연잔디에 비해 초기 시공비가 많이 들지만, 반영구적 사용이 가능하고 유지관리의 편의성, 운동하기에 적합하도록 표면이 고른 점 등으로 인해 선호도가 높다. 스포츠용 인조잔디에 있어서는 선수의 충격을 흡수하고, 공구름성, 공튀김성, 공이 지면에 바운드 되고난 이후의 공의 속도 변화 등 일련의 적정 경기성으로 확보하기 위한 수단으로 인조잔디가 활용되었다.Artificial turf is one of the specially used landscaping materials, and it is a substitute for artificial grass in the form of grass. Since it was first manufactured in the United States, it has been used primarily in sports grounds, and can be used in indoor gardens where grass cannot grow, or in outdoor areas just north of high-rise buildings with very limited sunshine hours. Such artificial turf is always green and is not restricted by environmental conditions, so it is easy to manage after construction. Artificial turf ball with artificial turf has higher initial construction cost than general natural turf, but it is highly preferred due to its semi-permanent use, ease of maintenance, and smooth surface for exercise. In artificial turf for sports, artificial turf was used as a means to absorb the impact of athletes and to secure a series of appropriate performances, such as tooling, splashing, and speed change after the ball was bound to the ground. .

이러한 인조잔디는 고객의 요구 및 소재 기술의 발달과 더불어 여러 단계를 거치면서 발전해 왔다. 특히 축구장용 인조잔디의 경우 1990년 이후 ‘FIFA 퀄리티 컨셉’이라고 하는 인조잔디에의 품질 인증 시스템인 FIFA 규격이 도입되면서 규격화된 경기성에 대한 욕구가 높아졌고, 이를 충족시키기 위한 여러 종류의 제품개발이 시도되고 있다. Such artificial turf has evolved through several stages with the development of customer's requirements and material technology. Especially, in the case of artificial turf for soccer field, since the introduction of the FIFA standard, which is a quality certification system of artificial turf called 'FIFA quality concept', since 1990, the desire for standardized gameability has increased, and various kinds of products development have been It is trying.

기존의 인조잔디 제품 동향은 파일의 길이가 약 55 ~ 70 mm의 장(長)파일류 타입이며 이러한 파일들 사이에 작은 알갱이의 탄성체를 충전시켜 넣어주므로써, FIFA가 정하는 충격흡수성 및 수직변형률, 공의 구름성(Ball Roll)이나 볼 리바운드성 등의 수치를 만족시키고 있다. 그러나, 이러한 타입의 인조잔디 구조체는 충전재 유실의 위험이 있고, 잔디 표면에 가해지는 반복적인 정적 및 동적 하중에 의해 구장 표면이 쉽게 딱딱해지는 현상(답압현상)이 발생되어 초기의 경기성을 지속적으로 유지시키지 못한다는 단점이 있었다. 구장 표면이 딱딱해지면 공이 구르는 길이는 더 멀어질 것이고, 경기 중 선수의 부상방지에 효율적이지 못하였다.The existing trend of artificial turf products is long pile type with file length of about 55 to 70 mm, and small piles of elastic material are filled between these piles, so that the shock absorbency and vertical strain rate defined by FIFA, It satisfies numerical values such as ball roll and ball rebound. However, this type of artificial turf structure has a risk of filling loss, and the surface of the turf is easily hardened by repeated static and dynamic loads applied to the grass surface. The disadvantage was that it could not be maintained. The harder the surface, the longer the ball will roll and the less effective it is to prevent injury to players during the game.

또한 기존의 인조잔디의 경우 볼 리바운드와 충격흡수성을 동시에 만족하지 못하였다. 충격흡수성이 만족되는 경우, 잔디 표면에 하중 및 마찰 자극 후(After Stimulation) 행해지는 볼 리바운드에 있어서는 표면 경화로 인해 기대치보다 높게 튀어오르는 현상을 볼 수 있다. In addition, the existing artificial turf did not satisfy the ball rebound and shock absorbency at the same time. If the shock absorbency is satisfied, the ball rebounding after the load and friction stimulation (After Stimulation) on the turf surface can be seen to spring higher than expected due to the surface hardening.

대한민국등록실용신안 제413557호는 잔디 파일을 3가지 다른 특성 및 형태를 갖는 섬유를 조합 또는 혼합하여 직조함으로써 3중 또는 4중 구조로 하여 인조잔디가 갈라지는 특성을 보안하여 쾌적하고 안전하게 경기할 수 있도록 하여 천연잔디와 흡사한 경기성, 복원력, 내구성을 가지는 인조잔디 구조체를 제안하고 있다. 그러나, 이와 같은 인조잔디는 잔디 파일의 높이를 55 내지 70㎜의 장(長)파일을 사용하며 지속적으로 사용시 표면이 경화되는 문제점이 있다.Republic of Korea Utility Model No. 413557 is a three- or four-layer structure by weaving or mixing the grass pile with fibers having three different characteristics and forms, so that the artificial turf cracking characteristics can be played comfortably and safely Therefore, artificial turf structure having similar playability, resilience and durability to natural grass is proposed. However, such artificial turf uses a long pile of 55 to 70 mm in height of the grass pile and has a problem that the surface is hardened when used continuously.

상기와 문제점으로 인하여 인조잔디 표면에 하중이 가해진 후 표면이 경화되는 것을 방지하여 공에 대한 반발력을 줄여줄 수 있는 축구장용 인조잔디 구조체가 요구되어져 왔다.
Due to the above problems and the artificial turf structure for the football field has been required that can prevent the surface hardening after the load is applied to the artificial turf surface to reduce the repulsive force on the ball.

상기와 같은 문제점을 해결하기 위해서 본 고안의 목적은 인조잔디 형성 초기상태의 볼리바운드성 및 충격흡수성을 유지하면서 경기성을 지속적으로 유지할 수 있는 축구장용 인조잔디 구조체를 제공하는 데 있다.In order to solve the above problems, an object of the present invention is to provide an artificial turf structure for a football field that can continuously maintain the game while maintaining the ball bounce and shock absorbency of the initial state of artificial turf formation.

또한 본 고안은 제품 생산시 원가를 절감할 수 있는 축구장용 인조잔디 구조체를 제공하는 데 목적이 있다.In addition, the present invention has an object to provide an artificial turf structure for a football field that can reduce the cost of production.

또한 본 고안은 시간 경과에 따른 표면 경화현상을 최소화 할 수 있는 축구장용 인조잔디 구조체를 제공하는 데 목적이 있다.
In addition, the present invention has an object to provide an artificial turf structure for a football field that can minimize the surface hardening phenomenon over time.

상기 목적을 달성하기 위해 본 고안은 축구장용 인조잔디 구조체에 있어서, 기초지반층, 상기 기초지반층상에 원단이 2 내지 20㎜의 두께로 형성된 원단층, 상기 원단층상에 탄성패드가 10 내지 25㎜의 두께로 형성된 탄성패드층(또는 상기 기초지반층상에 탄성패드가 10 내지 25㎜의 두께로 형성된 탄성패드층, 상기 탄성패드층 상에 원단이 2 내지 20㎜의 두께로 형성된 원단층) 및 상기 탄성패드층상에(또는 원단층상에) 상기 인조잔디 파일을 고정시키는 지조직층과 인조잔디 파일을 포함하되, 상기 인조잔디 파일의 길이가 30 내지 65㎜임을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다.In order to achieve the above object of the present invention, in the artificial turf structure for a soccer field, a base ground layer, a fabric layer formed with a thickness of 2 to 20 mm on the base ground layer, and an elastic pad on the fabric layer 10 to 25 mm An elastic pad layer (or an elastic pad layer having a thickness of 10 to 25 mm on the base ground layer, a fabric layer having a thickness of 2 to 20 mm on the elastic pad layer) formed on the base ground layer, and the The artificial turf layer for fixing the artificial turf file on the elastic pad layer (or the fabric layer) and the artificial turf file, the length of the artificial turf file provides an artificial turf structure for a football field characterized in that the length of 30 to 65mm. .

또한 본 고안은 상기 형성된 인조잔디 파일들 사이에는 충전재가 형성된 충전재층을 더 포함하는 축구장용 인조잔디 구조체를 제공한다.In addition, the present invention provides an artificial turf structure for a football field further comprising a filler layer having a filler formed therebetween the formed artificial turf files.

또한 본 고안은 상기 원단층이 부직포로 이루어짐을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다.In addition, the present invention provides an artificial turf structure for a football field, characterized in that the fabric layer is made of a nonwoven fabric.

또한 본 고안은 상기 탄성패드층이 EPP(expanded poly propylene), SBR(styrene-butadiene rubber), PVC(polyvinyl chloride) 및 PU(polyurethane)으로 이루어진 군에서 1이상 선택되는 것을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다.In addition, the present invention is the artificial turf for the football field, characterized in that the elastic pad layer is selected from the group consisting of expanded polypropylene (EPP), styrene-butadiene rubber (SBR), polyvinyl chloride (PVC) and PU (polyurethane) Provide a structure.

또한 본 고안은 상기 인조잔디 파일을 터프트하는 터프트수가 1㎡당 20,000 내지 30,000 인 것을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다.In another aspect, the present invention provides an artificial turf structure for a football field, characterized in that the number of tufts tufted the artificial turf file is 20,000 to 30,000 per square meter.

또한 본 고안은 상기 인조잔디 파일을 터프트하는 터프트수가 1㎡당 12,000 내지 19,000 인 것을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다.In another aspect, the present invention provides an artificial turf structure for a football field, characterized in that the number of tufts tufted the artificial turf file is 12,000 to 19,000 per square meter.

또한 본 고안은 상기 충전재층이 2개층(합성고무류 상에 규사 형성) 또는 3개층(합성고무류 상에 규사가 형성되고, 상기 규사상에 천연소재가 형성)으로 이루어진 것을 특징으로 하는 축구장용 인조잔디 구조체를 제공한다.
In addition, the present invention is artificial turf for the football field, characterized in that the filler layer is composed of two layers (silica sand formed on the synthetic rubber) or three layers (silica sand is formed on the synthetic rubber, a natural material is formed on the silica rubber). Provide a structure.

상기 본 고안에 따른 축구장용 인조잔디 구조체는 형성 초기상태의 볼 리바운드성 및 충격흡수성을 유지하면서 형성 초기의 경기성을 지속적으로 유지할 수 있다.The artificial turf structure for a soccer field according to the present invention can continuously maintain the playability of the initial formation while maintaining the ball rebound and shock absorbency of the initial formation state.

또한 본 고안에 따른 축구장용 인조잔디 구조체는 충전재 의존도를 감소시켜 제품 생산시 원가를 절감할 수 있으며, 시간 경과에 따른 표면 경화(답압)현상을 최소화 할 수 있다.
In addition, the artificial turf structure for the soccer field according to the present invention can reduce the dependence of the filler material to reduce the cost of production, and can minimize the surface hardening (resistance) phenomenon over time.

도 1은 본 고안의 바람직한 일실시예에 따른 충전재가 형성되지 않은 축구장용 인조잔디 구조체에 대한 단면도.
도 2는 본 고안의 바람직한 다른 일실시예에 따른 충전재가 형성된 축구장용 인조잔디 구조체에 대한 단면도.1 is a cross-sectional view of the artificial turf structure for the football field is not formed with a filler according to an embodiment of the present invention.
Figure 2 is a cross-sectional view of the artificial turf structure for the football field formed with a filler according to another embodiment of the present invention.

이하 본 고안에 첨부된 도면을 참조하여 고안을 실시하기 위한 구체적인 내용에서는 본 고안의 바람직한 일실시예를 상세히 설명하기로 한다. 우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 고안을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 고안의 요지를 모호하지 않게 하기 위하여 생략한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings of the present invention. First, it should be noted that in the drawings, the same components or parts denote the same reference numerals as much as possible. In describing the present invention, detailed descriptions of related well-known functions or configurations are omitted so as not to obscure the subject matter of the present invention.

본 명세서에서 사용되는 정도의 용어 “약”, “실질적으로” 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 고안의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.As used herein, the terms “about”, “substantially”, etc., are used at, or in close proximity to, numerical values when manufacturing and material tolerances inherent in the meanings indicated are intended to aid understanding of the subject innovation. Accurate or absolute figures are used to assist in the prevention of unfair use by unscrupulous infringers.

본 고안에서 "원단"이라 함은 제직 또는 편직에 의해 제조되는 물품, 부직포 및 섬유상 원단 등을 모두 포함하는 의미로 사용한다.In the present invention, "fabric" is used to mean all articles, non-woven fabrics and fibrous fabrics produced by weaving or knitting.

도 1은 본 고안의 바람직한 일실시예에 따른 축구장용 인조잔디 구조체에 대한 개략도이다.1 is a schematic diagram of an artificial turf structure for a soccer field according to an embodiment of the present invention.

본 고안에 따른 축구장용 인조잔디 구조체는 기초지반층(110), 원단층(120), 탄성패드층(130), 지조직층(140)을 포함한다. 본 고안의 상기 기초지반층(110)은 투수아스콘, 쇄석, 아스콘크리트 등으로 형성된다.The artificial turf structure for a soccer field according to the present invention includes a base ground layer 110, a fabric layer 120, an elastic pad layer 130, and a ground tissue layer 140. The base ground layer 110 of the present invention is formed of pitched ascon, crushed stone, asconcrete, and the like.

상기 기초지반층(110)상에 원단층(120)이 형성되며, 상기 원단의 두께는 2 내지 20㎜가 바람직하며, 3 내지 10㎜인 것이 더 바람직하다. 상기 범위로 원단층을 형성함으로써 볼 리바운드성과 충격흡수성이 동시에 만족될 수 있는데, 상기 원단층을 형성하지 않은 경우 양호한 충격흡수성을 얻을 수 있으나, 잔디 표면에 가해지는 하중 및 마찰 자극 후(After Stimulation) 행해지는 볼 리바운드에 있어서는 표면 변화로 인해 기대치보다 높게 튀어오르는 현상을 볼 수 있다. 따라서, 본 고안에 따른 원단층(120)을 형성함으로써 볼 리바운드성과 충격흡수성을 동시에 만족시킬 수 있게 된다.The fabric layer 120 is formed on the base ground layer 110, the thickness of the fabric is preferably 2 to 20mm, more preferably 3 to 10mm. By forming the fabric layer in the above range, the ball rebound and the shock absorbency can be satisfied at the same time. If the fabric layer is not formed, good shock absorbency can be obtained, but after the load and frictional stimulus applied to the grass surface (After Stimulation) In the ball rebound performed, a phenomenon that bounces higher than expected due to the surface change can be seen. Therefore, by forming the far-end layer 120 according to the present invention it is possible to satisfy the ball rebound and shock absorbency at the same time.

상기 원단층(120)은 부직포로 형성되는 것이 바람직하나, 이에 한정되는 것은 아니다. 상기 부직포를 사용함으로써 표면경화(답압)현상을 극복하는 데 현저한 효과가 있으며, 그 결과 경기성이 지속적으로 유지될 수 있으며, 선수의 부상방지에도 효과적이다. 상기 원단층(120)은 직물 또는 편물로도 형성될 수 있다.The fabric layer 120 is preferably formed of a nonwoven fabric, but is not limited thereto. By using the non-woven fabric has a remarkable effect in overcoming the surface hardening (pressing pressure) phenomenon, as a result can maintain the playability, effective for preventing the injury of the athlete. The fabric layer 120 may be formed of a woven or knitted fabric.

상기 원단층(120)의 상부에는 탄성패드층이 형성된다. 상기 탄성패드층(130)의 탄성패드 물질은 EPP(expanded poly propylene), SBR(styrene-butadiene rubber), PVC(polyvinyl chloride), PU(polyurethane) 등이 사용될 수 있으며, 상기 탄성패드층(130)의 높이는 10 내지 25㎜인 것이 바람직하다. 상기범위 미만의 경우 충격흡수성이 낮아지고 볼리바운드성은 높아지며, 상기범위를 초과하는 경우 충격흡수성이 높아지고 볼리바운드성은 낮아진다.An elastic pad layer is formed on the top of the distal layer 120. The elastic pad material of the elastic pad layer 130 may be expanded polypropylene (EPP), styrene-butadiene rubber (SBR), polyvinyl chloride (PVC), polyurethane (PU), or the like, and the elastic pad layer 130 may be used. It is preferable that the height of is 10-25 mm. If it is less than the above range, the shock absorbency is lowered, and the balliboundity is higher, and if it exceeds the above range, the shock absorbency is increased and the balliboundity is lowered.

본 고안에 있어서, 상기 원단층(120)과 탄성패드층(130)은 그 적층순서가 제한되는 것은 아니다.In the present invention, the fabric layer 120 and the elastic pad layer 130 is not limited in the stacking order.

상기 탄성패드층(130)의 상부에는 인조잔디 파일을 고정시키는 지조직(140)이 있어 인조잔디 파일의 밑부분을 고정시키는 역할을 한다.The upper portion of the elastic pad layer 130 has a paper tissue 140 for fixing the artificial turf file serves to fix the bottom of the artificial turf file.

상기 지조직(140)에 고정된 인조잔디 파일은 단(短)파일 일 수 있다. 상기 인조잔디 파일의 길이는 30 내지 65㎜이며 바람직하며 40 내지 50 mm 가 더 바람직하다. 상기 파일이 단(短)파일 일수록 원가절감 및 충전재의 소요량이 줄어드는 장점이 있지만 파일길이가 상기범위 미만일 경우에는 볼구름성(Ball Roll)이 커지게 된다. 반대로 상기 범위를 초과할 경우 충전재 없이 인조잔디가 식재되어 있을 경우 형태 불안정으로 인하여 파일이 뽑히는 문제점이 있다.The artificial turf file fixed to the branch tissue 140 may be a single file. The length of the artificial turf pile is 30 to 65 mm is preferred, 40 to 50 mm is more preferred. Although the file is a short file, there is an advantage of reducing the cost and the required amount of filler, but when the file length is less than the above range, the ball roll becomes large. On the contrary, when the artificial grass is planted without the filler when the range is exceeded, there is a problem in that the file is pulled out due to shape instability.

본 고안에 식재되는 인조잔디 파일수는 충전재의 유무에 따라서 달라질 수 있다. 충전재가 형성되어 있지 않은 경우 충격흡수 역할을 대체할 수단이 요구된다. 즉 인조잔디 파일수를 늘려 충격흡수 역할을 해야 한다. 반복 실험결과 조건에 맞는 인조잔디를 만들기 위해서는 충전재가 형성되어 있지 않을 경우 터프트수는 1㎡당 20,000 내지 30,000으로 식재하는 것이 바람직하며, 충전재가 형성되어 있는 경우 1㎡당 12,000 내지 19,000으로 식재하는 것이 바람직하다. 상기 범위 내로 파일을 식재할 경우 충격흡수성 및 볼리바운드성을 동시에 만족한다.
The number of artificial turf piles planted in the present invention may vary depending on the presence or absence of fillers. Means are required to replace the shock absorbing role if no filler is formed. That is, the number of artificial turf piles should be increased to act as a shock absorber. In order to make artificial turf that meets the repetition test results, when no filler is formed, the number of tufts is preferably planted at 20,000 to 30,000 per 1 m 2, and when the filler is formed, it is to be planted at 12,000 to 19,000 per 1 m 2. desirable. When planting the file within the above range satisfies the shock absorbing and bollibound simultaneously.

도 2는 본 고안의 바람직한 다른 일실시예에 따른 충전재가 형성된 축구장용 인조잔디 구조체에 대한 단면도이다.Figure 2 is a cross-sectional view of the artificial turf structure for the football field formed with a filler according to another embodiment of the present invention.

본 고안에 있어서 파일들 사이의 형태안정을 부여하고 충격을 흡수하는 역할을 하는 충전재(150)는 선택적 적용이 가능하다. 즉, 충전재(150)가 충전되어 있지 않은 인조잔디의 경우라도 파일의 길이가 단(短)파일인 특성으로 인하여 파일들의 형태 안정성을 유지할 수 있다. 반대로 상기 충전재(150)가 충전되는 경우 충전재(150)는 규사를 사용하는 것이 바람직하다. 또한 상기 본 고안의 충전재(150)는 3개의 층으로 형성될 수 있는데, 식물성 또는 광물성으로 이루어진 천연소재, 규사 및 합성고무류로 구성될 수 있다. 또한 상기 충전재는 합성고무류 및 규사의 2개의 층으로 이루어질 수도 있다. 적층 순서는 2개층일 경우에는 합성고무류 상에 규사가 형성되며, 3개층일 경우에는 합성고무류 상에 규사가 형성되고 상기 규사 상에 천연소재가 형성된다. 2개 층으로 형성될 경우 사용되는 양은 1㎡당 규사 10 내지 14㎏ 및 합성고무류 3 내지 4㎏을 사용하는 것이 바람직하며, 3개의 층으로 형성될 경우에는 1㎡ 당 천연소재 2.5 내지 3.5㎏, 규사 8 내지 12㎏ 및 합성고무류 3 내지 4㎏을 사용하는 것이 바람직하다.In the present invention, the filler 150, which provides shape stability between the piles and absorbs shock, may be selectively applied. That is, even in the case of the artificial turf in which the filler 150 is not filled, the shape stability of the files may be maintained due to the characteristic that the length of the file is a short file. On the contrary, when the filler 150 is filled, the filler 150 may preferably use silica sand. In addition, the filler 150 of the present invention may be formed of three layers, it may be composed of natural materials, silica, and synthetic rubber made of vegetable or mineral. The filler may also consist of two layers of synthetic rubber and silica. In the case of two layers, the silica sand is formed on the synthetic rubber in the case of two layers, and the silica sand is formed on the synthetic rubber in the case of three layers, and a natural material is formed on the silica sand. In the case of forming two layers, it is preferable to use 10 to 14 kg of silica sand per 1 m 2 and 3 to 4 kg of synthetic rubber, and when it is formed of three layers, 2.5 to 3.5 kg of natural material per 1 m 2, Preference is given to using 8 to 12 kg of silica sand and 3 to 4 kg of synthetic rubbers.

상기 식물성 천연소재 예로는 코르크, 광물성 천연소재의 예로는 질석이 바람직하다. 또한, 상기 합성고무류의 예로는 SBR(styrene-butadiene rubber), EPDM(ethylene propylene diene monomer), SEBS(styrene ethylene butylene styrene)를 사용하는 것이 바람직하다.
Cork, an example of natural mineral material is vermiculite is preferred as the vegetable natural material. In addition, examples of the synthetic rubbers include styrene-butadiene rubber (SBR), ethylene propylene diene monomer (EPDM), and styrene ethylene butylene styrene (SEBS).

이하, 본 고안의 실시예에 대하여 상세히 설명한다.Hereinafter, embodiments of the present invention will be described in detail.

하기 [표 1]은 FIFA에서 적절한 규격 및 허용치를 나타낸 수치이다.[Table 1] is a numerical value showing the appropriate specification and tolerance in FIFA.

측정항목
Metric
규 격
standard
요구사항Requirements 비 교
compare
FIFA-1FIFA-1 FIFA-2FIFA-2 볼리바운드
(Ball Rebound)Bollibound
(Ball Rebound) FIFA 01FIFA 01 60∼100 ㎝60-100 cm 60∼85 ㎝60 to 85 cm 앵글볼리바운드(Angled Ball Rebound)Angled Ball Rebound FIFA 02FIFA 02 45∼70%45 to 70% 45∼60%45 to 60% Dry Field 기준Dry Field Standard 볼롤
(Ball ROLL)Ball roll
(Ball ROLL) FIFA 03FIFA 03 4∼10m4-10m 4∼8m4-8m 충격흡수성(Shock Absorption)Shock Absorption FIFA 04FIFA 04 55∼70%55 to 70% 60∼70%60 to 70% 수직변형률(Vertical Deformation)Vertical Deformation FIFA 05FIFA 05 4∼9㎜4 to 9 mm 4∼8㎜4 to 8 mm 회전저항(Rotational Resistance)Rotational Resistance FIFA 06FIFA 06 25∼50Nm25-50 Nm 30∼45Nm30 to 45 Nm 선형마찰-SDV
(Linear Friction - Stud Deceleration Value)Linear Friction-SDV
(Linear Friction-Stud Deceleration Value) FIFA 07FIFA 07 3.0∼6.0g3.0-6.0 g 3.0∼5.5g3.0 to 5.5 g 선형마찰-SSV
(Linear Friction - Stud Slide Value) Linear Friction-SSV
(Linear Friction-Stud Slide Value) FIFA 08FIFA 08 120∼220120-220 130∼210130-210 배수성
(Water permeability Drainage
(Water permeability EN 12616EN 12616 ＞180㎜/h＞ 180mm / h ＞180㎜/h＞ 180mm / h 평탄성
(Surface regularity of Playing Surface)Flatness
(Surface regularity of playing surface) EN 13036
3M straightedge EN 13036
3M straightedge ＜ 10㎜<10 mm ＜ 10㎜<10 mm 구배
(Slope) gradient
(Slope) Surveyor Level Surveyor Level ≤2% in any place≤2% in any place ≤2% in any place≤2% in any place

이하 실험이 상기 표의 FIFA 규격에 만족하는지를 검토해 보도록 한다.Examine whether the experiment satisfies the FIFA standard of the above table.

실시예Example 1 One

원단층의 두께에 따른 결과를 확인하기 위한 방법으로 기초지반층으로는 투수아스콘으로 설치하였으며, 원단층은 2㎜의 두께로 부직포를 포설하고, 탄성패드층(130)은 15㎜의 두께로 SBR(styrene-butadiene rubber)의 탄성패드를 포설하고, 인조잔디 파일의 터프트수는 1㎡ 당 14,800개를 45㎜의 길이로 식재한다. 또한, 충전재로는 규사량은 10 ㎏/㎡, 그외 충전재로는 코르크 3.0 ㎏/㎡의 식물성 천연소재 및 SEBS(styrene ethylene butylene styrene) 3.5 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
As a method for confirming the results according to the thickness of the fabric layer, the foundation layer was installed with a permeable ascon, and the fabric layer laid a nonwoven fabric with a thickness of 2 mm, and the elastic pad layer 130 with a thickness of 15 mm SBR. Elastic pads of styrene-butadiene rubber are installed, and the number of tufts of artificial turf piles is planted to 14,800 pieces per 1㎡ with a length of 45㎜. In addition, as a filler, 10 kg / m2 of siliceous sand is mixed, and 3.0 kg / m2 of cork plant material and synthetic rubber of 3.5 kg / m2 of styrene ethylene butylene styrene (SEBS) are mixed. Prepared.

실시예Example 2 및 3 2 and 3

실시예 1과 동일하게 실시하되, 원단층의 부직포의 두께를 각각 10㎜, 20㎜로 하여 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 1, but the artificial turf structure for the football field was prepared by the thickness of the nonwoven fabric of the fabric layer to 10mm, 20mm, respectively.

실시예Example 4 4

탄성패드층의 두께에 따른 결과를 확인하기 위한 방법으로 기초지반층으로는 투수아스콘으로 설치하였으며, 원단층은 2㎜의 두께로 부직포를 포설하고, 탄성패드층은 10㎜의 두께로 SBR(styrene-butadiene rubber)의 탄성패드를 포설하고, 인조잔디 파일의 터프트수는 1㎡ 당 14,800개를 45㎜의 길이로 식재한다. 또한, 충전재로는 규사량은 10 ㎏/㎡, 그외 충전재로는 코르크 3.0 ㎏/㎡의 식물성 천연소재 및 SEBS(styrene ethylene butylene styrene) 3.5 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
As a method for confirming the results according to the thickness of the elastic pad layer, the base ground layer was installed with a permeable ascon, the fabric layer laid a nonwoven fabric with a thickness of 2 mm, and the elastic pad layer with a thickness of 10 mm SBR (styrene). -The elastic pad of butadiene rubber) is installed, and the number of tufts of artificial turf pile is planted 14,800 pieces per 1㎡ with a length of 45㎜. In addition, as a filler, 10 kg / m2 of siliceous sand is mixed, and 3.0 kg / m2 of cork plant material and synthetic rubber of 3.5 kg / m2 of styrene ethylene butylene styrene (SEBS) are mixed. Prepared.

실시예Example 5 내지 7 5 to 7

실시예 4와 동일하게 실시하되, 탄성패드층 탄성패드의 두께를 각각 15㎜, 20㎜, 25㎜로 하여 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 4, but the thickness of the elastic pad layer of the elastic pad was 15 mm, 20 mm, 25 mm, respectively, to prepare an artificial turf structure for a football field.

실시예Example 8 8

인조잔디의 길이에 따른 결과를 확인하기 위한 방법으로 기초지반층으로는 투수아스콘으로 설치하였으며, 원단층은 2㎜의 두께로 부직포를 포설하고, 탄성패드층은 15㎜의 두께로 SBR(styrene-butadiene rubber)의 탄성패드를 포설하고, 인조잔디 파일의 터프트수는 1㎡ 당 14,800개를 30㎜의 길이로 식재한다. 또한, 충전재로는 규사량은 10 ㎏/㎡, 그외 충전재로는 코르크 3.0 ㎏/㎡의 식물성 천연소재 및 SEBS(styrene ethylene butylene styrene) 3.5 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
As a method to check the results according to the length of the artificial turf, a permeable ascon was installed as the foundation ground layer, the fabric layer was laid with a non-woven fabric with a thickness of 2 mm, and the elastic pad layer with a thickness of 15 mm with SBR (styrene- Butadiene rubber) is installed and the number of tufts of artificial turf pile is planted 14,800 pieces per 1㎡ in length of 30㎜. In addition, as a filler, 10 kg / m2 of siliceous sand is mixed, and 3.0 kg / m2 of cork plant material and synthetic rubber of 3.5 kg / m2 of styrene ethylene butylene styrene (SEBS) are mixed. Prepared.

실시예Example 9 및 10 9 and 10

실시예 8과 동일하게 실시하되, 인조잔디 파일의 길이를 각각 50㎜, 65㎜로 하여 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 8, but the artificial turf piles were made 50 mm and 65 mm, respectively, to prepare an artificial turf structure for a football field.

실시예Example 11 11

충전재에 따른 결과를 확인하기 위한 방법으로 기초지반층으로는 투수아스콘으로 설치하였으며, 원단층은 3㎜의 두께로 부직포를 포설하고, 탄성패드층은 15㎜의 두께로 SBR(styrene-butadiene rubber)의 탄성패드를 포설하고, 인조잔디 파일의 터프트수는 1㎡ 당 20,000개를 45㎜의 길이로 식재하였으며, 충전재의 포설없이 축구장용 인조잔디 구조체를 제조하였다.
As a method for checking the results according to the filler, a permeable ascon was installed as the base ground layer, and the fabric layer was laid with a non-woven fabric with a thickness of 3 mm, and the elastic pad layer with a thickness of 15 mm with SBR (styrene-butadiene rubber). The elastic pads were installed, and the number of tufts of artificial turf piles was planted to 20,000 pieces per 1 m 2 in a length of 45 mm, and artificial turf structures for soccer fields were prepared without laying fillers.

실시예Example 12 12

실시예 11과 동일하게 실시하되, 인조잔디 파일의 터프트수는 1㎡ 당 14,800개를 식재하였으며, 충전재는 규사 10 ㎏/㎡ 및 SEBS(styrene ethylene butylene styrene) 3.5 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
The same procedure as in Example 11 was carried out, but the number of tufts of artificial turf pile was planted 14,800 per m 2, and the filler was mixed with 10 kg of silica sand and 3.5 kg / m 2 of synthetic rubber of SEBS (styrene ethylene butylene styrene). Artificial turf structure for a football field was prepared.

실시예Example 13 13

실시예 11과 동일하게 실시하되, 인조잔디 파일의 터프트수는 1㎡ 당 14,800개를 식재하였으며, 충전재는 규사 10 ㎏/㎡ 및 그외 충전재로 코르크 3.0 ㎏/㎡의 식물성 천연소재 및 SEBS(styrene ethylene butylene styrene) 3.5 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
The same procedure as in Example 11 was carried out, but the number of tufts of artificial turf pile was planted 14,800 per m 2, and the filling material was 10 kg / m 2 of silica sand and other fillers including 3.0 kg / m 2 of vegetable natural material and SEBS (styrene ethylene). butylene styrene) artificial grass structure for soccer field was prepared by mixing 3.5 kg / ㎡ of synthetic rubber.

비교예Comparative example 1 One

실시예 1과 동일하게 실시하되, 원단층의 부직포는 포설하지 않고 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 1, but the non-woven fabric of the fabric layer was prepared artificial turf structure for the football field.

비교예Comparative example 2 2

실시예 1과 동일하게 실시하되, 원단층의 부직포의 두께를 각각 25㎜로 하여 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 1, but the artificial turf structure for the football field was prepared with a nonwoven fabric thickness of 25 mm respectively.

비교예Comparative example 3 및 4 3 and 4

실시예 4와 동일하게 실시하되, 탄성패드층 탄성패드의 두께를 각각 5㎜, 30㎜로 하여 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 4, but the thickness of the elastic pad layer of the elastic pad was 5mm, 30mm, respectively, to prepare an artificial turf structure for a football field.

비교예Comparative example 5 및 6 5 and 6

실시예 8과 동일하게 실시하되, 인조잔디의 길이를 각각 25㎜, 70㎜로 하여 축구장용 인조잔디 구조체를 제조하였다.
In the same manner as in Example 8, the artificial turf structure for the football field was prepared by setting the length of the artificial turf to 25 mm and 70 mm, respectively.


구분
division

원단층
(㎜)
Fabric layer
(Mm)
탄성패드층
(㎜)
Elastic pad layer
(Mm) 인조잔디Artificial turf 충전재filling 테스트 결과Test results

비고

Remarks 길이
(㎜)Length
(Mm) 단위면적(1㎡)당터프트수Number of tufts per unit area (1㎡) 규사량
(㎏/㎡)Silica weight
(Kg / ㎡) 그 외 충전재(㎏/㎡)Other fillers (㎏ / ㎡) 충격흡수
(%)Shock absorption
(%) 수직변형
(-㎜)Vertical deformation
(-Mm) 볼리바운드
(㎝)Bollibound
(Cm) 볼롤
(m)Ball roll
(m) 선형마찰-SDV
(g)Linear Friction-SDV
(g) 선형마찰-SSVLinear Friction-SSV 실시예1Example 1 22 1515 4545 14,80014,800 1010 6.56.5 60.860.8 4.64.6 7575 실시예2Example 2 1010 1515 4545 14,80014,800 1010 6.56.5 61.461.4 4.94.9 7272 실시예3Example 3 2020 1515 4545 14,80014,800 1010 6.56.5 63.463.4 4.94.9 7070 실시예4Example 4 22 1010 4545 14,80014,800 1010 6.56.5 58.858.8 4.34.3 8080 실시예5Example 5 22 1515 4545 14,80014,800 1010 6.56.5 61.561.5 4.84.8 7575 실시예6Example 6 22 2020 4545 14,80014,800 1010 6.56.5 67.867.8 5.85.8 7272 실시예7Example 7 22 2525 4545 14,80014,800 1010 6.56.5 69.869.8 7.87.8 6565 실시예8Example 8 22 1515 3030 14,80014,800 1010 6.56.5 62.562.5 6.26.2 6262 9.59.5 3.63.6 160160 실시예9Example 9 22 1515 5050 14,80014,800 1010 6.56.5 62.862.8 5.85.8 6868 7.07.0 3.33.3 140140 실시예10Example 10 22 1515 6565 14,80014,800 1010 6.56.5 61.861.8 5.35.3 6666 4.04.0 3.13.1 120120 실시예11Example 11 33 1515 4545 20,00020,000 -- -- 60.860.8 4.14.1 7272 9.59.5 3.03.0 120120 실시예12Example 12 33 1515 4545 14,80014,800 1010 3.53.5 61.661.6 4.64.6 6969 8.68.6 3.33.3 135135 실시예13Example 13 33 1515 4545 14,80014,800 1010 6.56.5 62.862.8 4.84.8 6565 7.07.0 3.53.5 145145 비교예1Comparative Example 1 -- 1515 4545 14,80014,800 1010 6.56.5 63.263.2 4.94.9 110110 불합격fail 비교예2Comparative Example 2 2525 1515 4545 14,80014,800 1010 6.56.5 7272 5.15.1 5555 불합격fail 비교예3Comparative Example 3 22 55 4545 14,80014,800 1010 6.56.5 53.253.2 4.64.6 105105 불합격fail 비교예4Comparative Example 4 22 3030 4545 14,80014,800 1010 6.56.5 7474 8.78.7 5858 불합격fail 비교예5Comparative Example 5 22 1515 2525 14,80014,800 1010 6.56.5 62.862.8 8.28.2 5555 12.512.5 5.95.9 220220 불합격fail 비교예6Comparative Example 6 22 1515 7070 14,80014,800 1010 6.56.5 63.963.9 4.34.3 6868 3.83.8 2.52.5 9090 불합격fail

상기 [표 2]의 데이타는 잔디 구조체를 실제 경기장과 똑같이 재현시킨 후 FIFA 규격에 의거하여 진행되었고, 잔디 구조체에의 자극(하중, 마찰)을 부여한 후 실험한 결과치이다.The data in [Table 2] is based on the FIFA standard after the grass structure is reproduced in the same manner as the actual stadium, and is a result of experimenting after imparting a stimulus (load, friction) to the grass structure.

충격흡수성 및 수직변형률 수치 계산 방법은 총 3회를 측정한 후 처음 1회 수치를 무시하고, 2회 및 3회 수치를 평균하여 계산하였으며, 이를 총 10회 진행하여 이들의 평균을 계산하였다. 이는 반복적 하중에 의한 잔디 구조체의 경시 변화를 예측하기 위함이다.
The method of calculating shock absorbency and vertical strain values was calculated by ignoring the first one and averaging two and three times after measuring three times in total, and calculating the average of these two times. This is to predict the change over time of the turf structure due to the repetitive load.

실시예Example 14 14

시간 경과에 따른 결과를 확인하기 위한 방법으로 기초지반층으로는 투수아스콘으로 설치하였으며, 원단층은 5㎜의 두께로 부직포를 포설하고, 탄성패드층은 15㎜의 두께로 SBR(styrene-butadiene rubber)의 탄성패드를 포설하고, 인조잔디 파일의 터프트수는 1㎡ 당 14,800개를 45㎜의 길이로 식재한다. 또한, 충전재로는 규사량은 10 ㎏/㎡, 그외 충전재로는 코르크 3.0 ㎏/㎡의 식물성 천연소재 및 SEBS(styrene ethylene butylene styrene) 3.5 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
As a method for checking the results over time, the foundation layer was installed with a permeable ascon, the fabric layer laid a nonwoven fabric with a thickness of 5 mm, and the elastic pad layer with a thickness of 15 mm SBR (styrene-butadiene rubber). ) Elastic pads are installed, and the number of tufts of artificial turf piles is planted with 14,800 pieces per 1 m 2 in a length of 45 mm. In addition, as a filler, 10 kg / m2 of siliceous sand is mixed, and 3.0 kg / m2 of cork plant material and synthetic rubber of 3.5 kg / m2 of styrene ethylene butylene styrene (SEBS) are mixed. Prepared.

실시예Example 15 내지 18 15 to 18

실시예 14와 동일하게 제조한 축구장용 인조잔디 구조체를 이용하여 각각 3개월후, 6개월후, 9개월후, 12개월후에 FIFA 규격에 따른 테스트를 측정하였다.
Using the artificial turf structure for the soccer field prepared in the same manner as in Example 14, the test according to the FIFA standard was measured after 3 months, 6 months, 9 months, and 12 months, respectively.

비교예Comparative example 7 7

원단층 및 탄성패드층의 포설없이 인조잔디는 70㎜의 장파일을 사용하였으며, 터프트수는 1㎡ 당 8,700개를 식재하였다. 또한 충전재로 규사량은 21 ㎏/㎡, 그외 충전재로는 SBR(styrene-butadiene rubber) 15 ㎏/㎡의 합성고무를 혼합하여 축구장용 인조잔디 구조체를 제조하였다.
The artificial turf used a 70mm long pile without laying the fabric layer and the elastic pad layer, and 8,700 tufts were planted per 1m2. In addition, the artificial turf structure for the soccer field was prepared by mixing the synthetic silica of 21 kg / m 2 as the filler and 15 kg / m 2 of styrene-butadiene rubber as the filler.

비교예Comparative example 8 내지 11 8 to 11

비교예 7과 동일하게 제조한 축구장용 인조잔디 구조체를 이용하여 각각 3개월후, 6개월후, 9개월후, 12개월후에 FIFA 규격에 따른 테스트를 측정하였다.
Using the artificial turf structure for the soccer field manufactured in the same manner as in Comparative Example 7, the test according to the FIFA standard was measured after 3 months, 6 months, 9 months, and 12 months, respectively.


구분
division

원단층
(㎜)
Fabric layer
(Mm)
탄성패드층
(㎜)
Elastic pad layer
(Mm) 인조잔디Artificial turf 충전재filling 테스트 결과Test results

비고

Remarks 길이
(㎜)Length
(Mm) 단위면적(1㎡)당 터프트수Number of tufts per unit area (1㎡) 규사량
(㎏/㎡)Silica weight
(Kg / ㎡) 그 외 충전재(㎏/㎡)Other fillers (㎏ / ㎡) 충격흡수
(%)Shock absorption
(%) 수직변형
(-㎜)Vertical deformation
(-Mm) 볼리바운드
(㎝)Bollibound
(Cm) 볼롤
(m)Ball roll
(m) 선형마찰-SDV
(g)Linear Friction-SDV
(g) 선형마찰-SSVLinear Friction-SSV 실시예14Example 14 55 1515 4545 14,80014,800 1010 6.56.5 6565 6.06.0 6565 5.05.0 3.33.3 170170 포설초기Initial installation 실시예15Example 15 55 1515 4545 14,80014,800 1010 6.56.5 6565 5.55.5 6565 5.55.5 3.33.3 168168 3개월후3 months later 실시예16Example 16 55 1515 4545 14,80014,800 1010 6.56.5 6464 5.25.2 6262 6.26.2 3.23.2 165165 6개월후6 months later 실시예17Example 17 55 1515 4545 14,80014,800 1010 6.56.5 6262 4.94.9 6464 6.56.5 3.13.1 162162 9개월후9 months later 실시예18Example 18 55 1515 4545 14,80014,800 1010 6.56.5 6262 4.54.5 6565 7.87.8 3.13.1 152152 12개월후12 months later 비교예7Comparative Example 7 -- -- 7070 8,7008,700 2121 1515 5959 8.08.0 8585 7.57.5 4.04.0 160160 포설
초기Laying
Early 비교예8Comparative Example 8 -- -- 7070 8,7008,700 2121 1515 5757 7.77.7 9090 9.09.0 3.53.5 140140 3개
월후Three
After 비교예9Comparative Example 9 -- -- 7070 8,7008,700 2121 1515 5656 7.27.2 9292 1010 3.53.5 138138 6개
월후6
After 비교예10Comparative Example 10 -- -- 7070 8,7008,700 2121 1515 5555 5.25.2 105105 11.011.0 3.23.2 135135 9개
월후Nine
After 비교예11Comparative Example 11 -- -- 7070 8,7008,700 2121 1515 5555 4.24.2 110110 12.012.0 3.83.8 135135 12개
월후12
After

상기 [표 3]에서 나타난 실험결과 본 고안의 일실시예에 따른 축구장용 인조잔디 구조체는 시간이 지나더라도 표면 경화현상이 거의 일어나지 않아 충격흡수성, 볼리바운드성 등의 FIFA 규격을 유지하고 있다는 결과를 얻어낼 수 있다.
As a result of the experiment shown in [Table 3], the artificial turf structure for the soccer field according to an embodiment of the present invention hardly occurs surface hardening even after time, and thus maintains the FIFA standard such as shock absorbency and ballibound property. You can get it.

이상에서 설명한 본 고안은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 고안의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 고안이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.
The present invention described above is not limited to the above-described embodiments and the accompanying drawings, and various substitutions, modifications, and changes are possible within the scope without departing from the technical spirit of the present invention. It will be evident to those who have knowledge of.

Claims (7)

축구장용 인조잔디 구조체에 있어서,
기초지반층, 상기 기초지반층상에 원단이 2 내지 20㎜의 두께로 형성된 원단층, 상기 원단층상에 탄성패드가 10 내지 25㎜의 두께로 형성된 탄성패드층(또는 상기 기초지반층상에 탄성패드가 10 내지 25㎜의 두께로 형성된 탄성패드층, 상기 탄성패드층 상에 원단이 2 내지 20㎜의 두께로 형성된 원단층) 및 상기 탄성패드층상에(또는 원단층상에) 상기 인조잔디 파일을 고정시키는 지조직층과 인조잔디 파일을 포함하되,
상기 인조잔디 파일의 길이가 30 내지 65㎜임을 특징으로 하는 축구장용 인조잔디 구조체.In artificial turf structure for soccer field,
A base layer, a fabric layer having a thickness of 2 to 20 mm on the foundation layer, and an elastic pad layer having a thickness of 10 to 25 mm on the fabric layer (or an elastic pad on the foundation layer) Elastic pad layer having a thickness of 10 to 25 mm, a fabric layer having a thickness of 2 to 20 mm on the elastic pad layer) and fixing the artificial grass pile on the elastic pad layer (or on the fabric layer) Including strata and artificial turf files,
Artificial turf structure for a football field, characterized in that the length of the artificial turf pile is 30 to 65mm. 제1항에 있어서,
상기 형성된 인조잔디 파일들 사이에는 충전재가 형성된 충전재층을 더 포함하는 축구장용 인조잔디 구조체.The method of claim 1,
Artificial turf structure for a football field further comprising a filler layer formed between the artificial turf piles formed. 제1항 또는 제2항에 있어서,
상기 원단층은 부직포로 이루어짐을 특징으로 하는 축구장용 인조잔디 구조체.The method according to claim 1 or 2,
The fabric layer is artificial turf structure for a football field, characterized in that made of a non-woven fabric. 제1항 또는 제2항에 있어서,
상기 탄성패드층은 EPP(expanded poly propylene), SBR(styrene-butadiene rubber), PVC(polyvinyl chloride) 및 PU(polyurethane)으로 이루어진 군에서 1이상 선택되는 것을 특징으로 하는 축구장용 인조잔디 구조체.The method according to claim 1 or 2,
The elastic pad layer EPP (expanded poly propylene), SBR (styrene-butadiene rubber), PVC (polyvinyl chloride) and PU (polyurethane) artificial turf structure for a football field, characterized in that at least one selected from the group consisting of. 제1항에 있어서,
상기 인조잔디 파일을 터프트하는 터프트수는 1㎡당 20,000 내지 30,000 인 것을 특징으로 하는 축구장용 인조잔디 구조체.The method of claim 1,
Tufts for tufting the artificial turf pile artificial turf structure for a football field, characterized in that 20,000 to 30,000 per square meter. 제2항에 있어서,
상기 인조잔디 파일을 터프트하는 터프트수는 1㎡당 12,000 내지 19,000 인 것을 특징으로 하는 축구장용 인조잔디 구조체.The method of claim 2,
Tuft for tufting the artificial turf pile artificial turf structure for a football field, characterized in that 12,000 to 19,000 per square meter. 제2항에 있어서,
상기 충전재층은 2개층(합성고무류 상에 규사 형성) 또는 3개층(합성고무류 상에 규사가 형성되고, 상기 규사상에 천연소재가 형성)으로 이루어진 것을 특징으로 하는 축구장용 인조잔디 구조체.
The method of claim 2,
The filler layer is artificial turf structure for a soccer field, characterized in that consisting of two layers (silica sand formed on the synthetic rubber) or three layers (silica sand is formed on the synthetic rubber, a natural material is formed on the silica rubber).
KR2020110003041U 2011-04-11 2011-04-11 Structure of composite artificial turf for a football field KR20110006071U (en)