KR101007642B1 - Tire tread rubber composition - Google Patents

Tire tread rubber composition Download PDF

Info

Publication number
KR101007642B1
KR101007642B1 KR1020080089848A KR20080089848A KR101007642B1 KR 101007642 B1 KR101007642 B1 KR 101007642B1 KR 1020080089848 A KR1020080089848 A KR 1020080089848A KR 20080089848 A KR20080089848 A KR 20080089848A KR 101007642 B1 KR101007642 B1 KR 101007642B1
Authority
KR
South Korea
Prior art keywords
rubber
weight
parts
tire tread
rubber composition
Prior art date
Application number
KR1020080089848A
Other languages
Korean (ko)
Other versions
KR20100030888A (en
Inventor
김부영
Original Assignee
금호타이어 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 금호타이어 주식회사 filed Critical 금호타이어 주식회사
Priority to KR1020080089848A priority Critical patent/KR101007642B1/en
Publication of KR20100030888A publication Critical patent/KR20100030888A/en
Application granted granted Critical
Publication of KR101007642B1 publication Critical patent/KR101007642B1/en

Abstract

본 발명은 타이어 트레드 고무조성물에 관한 것으로 보다 상세하게는 타이어 트레드 고무조성물에 있어서, 원료고무 이외에 첨가제로서 고분산성 카본블랙, 고분산성 실리카, 폴리에틸렌, 커플링제를 포함하도록 하여 내발열성 및 내마모성을 향상시킬 수 있는 타이어 트레드 고무조성물에 관한 것이다.The present invention relates to a tire tread rubber composition, and more particularly, to a tire tread rubber composition, in order to include high dispersible carbon black, highly dispersible silica, polyethylene, and a coupling agent in addition to the raw material rubber to improve heat resistance and wear resistance. The present invention relates to a tire tread rubber composition.

폴리에틸렌, 고무, 트레드, 타이어 Polyethylene, rubber, tread, tire

Description

타이어 트레드 고무조성물{Tire tread rubber composition}Tire tread rubber composition

본 발명은 타이어 트레드 고무조성물에 관한 것으로 보다 상세하게는 타이어 트레드 고무조성물에 있어서, 원료고무 이외에 첨가제로서 고분산성 카본블랙, 고분산성 실리카, 폴리에틸렌, 커플링제를 포함하도록 하여 내발열성 및 내마모성을 향상시킬 수 있는 타이어 트레드 고무조성물에 관한 것이다.The present invention relates to a tire tread rubber composition, and more particularly, to a tire tread rubber composition, in order to include high dispersible carbon black, highly dispersible silica, polyethylene, and a coupling agent in addition to the raw material rubber to improve heat resistance and wear resistance. The present invention relates to a tire tread rubber composition.

타이어 트레드의 내마모성은 지면과 접하는 트레드 표면층의 성질에 의해 결정되는데, 고속주행시 필연적으로 따르는 열발생은 물성하락 및 내마모특성 저하의 원인이 되고 있다. The wear resistance of the tire tread is determined by the nature of the tread surface layer in contact with the ground, and the heat generation inevitably caused at high speeds causes the deterioration of physical properties and wear resistance.

종래 타이어 트레드의 물성하락 및 내마모특성 저하의 원인을 해결하기 위하여 천연고무를 주로 하는 고무의 사용으로 고무의 유리전이온도를 낮추는 방법, 일반적으로 모듈러스 및 경도가 높을 때 내마모성이 향상됨에 따라 모듈러스를 증가시키기 위한 방편으로 카본블랙의 첨가량을 증가하는 방법, 입자경이 작은 카본블랙의 적용, 공정조제 및 오일의 함량을 줄이는 방법, 고무에 내열특성이 양호한 노 화방지제를 사용하거나, 고무를 혼용하여 사용하는 방법, 가교결합제를 다중 황결합(polysulfide bond) 보다는 단일 황결합(monosulfide bond)으로 변경시켜 열안정성을 개선시키는 방법이 행하여져 왔다.In order to solve the cause of deterioration of the properties of the tire tread and the wear resistance, the method of lowering the glass transition temperature of the rubber by using rubber mainly made of natural rubber, generally modulus as the wear resistance is improved when the modulus and hardness are high As a means to increase the method of increasing the addition amount of carbon black, the application of carbon black with a small particle size, the method of reducing the content of the process aid and oil, the use of an anti-aging agent with good heat resistance properties or a mixture of rubber The method of improving the thermal stability by changing the crosslinking agent to a single sulfur bond (monosulfide bond) rather than polysulfide bond (polysulfide bond).

그러나 카본블랙의 첨가량을 증가하거나, 입자경이 작은 카본블랙을 적용함으로써 고무 내의 내발열성을 증가시키는 경우 이러한 고무를 타이어에 적용시 타이어의 노화 내구력을 감소시키는 단점이 있다.However, when the amount of carbon black is increased or when the heat resistance in the rubber is increased by applying carbon black having a small particle size, there is a disadvantage in reducing the aging durability of the tire when the rubber is applied to the tire.

따라서 이러한 문제점을 해결하면서 타이어 트레드의 내마모성을 향상시키기 위하여 다양한 고무조성물의 개발이 행하여 지고 있다. Therefore, various rubber compositions have been developed to improve the wear resistance of tire treads while solving these problems.

본 발명은 내발열성 및 내마모성을 향상시킬 수 있는 타이어 트레드 고무조성물을 제공하고자 한다.The present invention is to provide a tire tread rubber composition that can improve the heat resistance and wear resistance.

본 발명은 타이어 트레드 고무조성물에 있어서, 원료고무 100중량부에 대하여 고분산성 카본블랙 20∼50중량부, 고분산성 실리카 5∼30중량부, 폴리에틸렌 10∼30중량부, 커플링제 0.5∼5중량부 포함하도록 내발열성 및 내마모성을 향상시킬 수 있는 타이어 트레드 고무조성물을 제공하고자 한다.In the tire tread rubber composition, 20 to 50 parts by weight of highly dispersible carbon black, 5 to 30 parts by weight of highly dispersible silica, 10 to 30 parts by weight of polyethylene, and 0.5 to 5 parts by weight of coupling agent in 100 parts by weight of the raw material rubber To provide a tire tread rubber composition that can improve the heat resistance and wear resistance to include.

본 발명은 내발열성 및 내마모성을 향상시킬 수 있는 타이어 트레드 고무조성물 및 동 공무조성물로 이루어진 고무를 포함하도록 하여 내발열성 및 내마모성이 향상된 타이어를 제공할 수 있다.The present invention can provide a tire having improved heat resistance and wear resistance by including a rubber made of a tire tread rubber composition and a copper aerosol composition capable of improving heat resistance and wear resistance.

본 발명의 타이어 트레드 고무조성물은 폴리에틸렌, 특히 재생 폴리에틸렌을 사용할 수 있어 자원 재활용을 통한 친환경적인 타이어 트레드 고무조성물을 제공할 수 있다.The tire tread rubber composition of the present invention can use polyethylene, in particular recycled polyethylene can provide an environmentally friendly tire tread rubber composition through resource recycling.

본 발명은 내발열성 및 내마모성을 향상시킬 수 있는 타이어 트레드 고무조성물을 나타낸다.The present invention represents a tire tread rubber composition capable of improving heat resistance and wear resistance.

본 발명은 타이어 트레드 고무조성물에 있어서, 원료고무 100중량부에 대하여 고분산성 카본블랙 20∼50중량부, 고분산성 실리카 5∼30중량부, 폴리에틸렌 10∼30중량부, 커플링제 0.5∼5중량부 포함하는 타이어 트레드 고무조성물을 나타낸다.In the tire tread rubber composition, 20 to 50 parts by weight of highly dispersible carbon black, 5 to 30 parts by weight of highly dispersible silica, 10 to 30 parts by weight of polyethylene, and 0.5 to 5 parts by weight of coupling agent in 100 parts by weight of the raw material rubber A tire tread rubber composition is included.

본 발명에서 원료고무는 천연고무를 사용할 수 있다.In the present invention, the raw rubber may be natural rubber.

본 발명에서 원료고무는 합성고무를 사용할 수 있다.In the present invention, the raw material rubber may use synthetic rubber.

본 발명에서 원료고무는 천연고무, 합성고무가 혼합된 혼합고무를 사용할 수 있다.In the present invention, the raw material rubber may be a mixture of natural rubber and synthetic rubber.

상기에서 합성고무는 스티렌 부타디엔 고무(SBR), 부타디엔 고무(BR), 부틸고무, 이소프렌 고무, 에피클로로 히드린고무, 니트릴고무, 수소화된 니트릴고무, 이소프렌부타디엔고무, 폴리우레탄고무, 불소고무, 실리콘고무, 에틸렌프로필렌고무, EPDM고무, 하이팔론고무, 클로로프렌고무, 에틸렌비닐아세테이트고무, 아크릴고무, 니트릴을 포함하는 스티렌 부타디엔 고무, 네오프렌 고무 중에서 선택된 어느 하나 이상을 사용할 수 있다.Synthetic rubber is styrene butadiene rubber (SBR), butadiene rubber (BR), butyl rubber, isoprene rubber, epichlorohydrin rubber, nitrile rubber, hydrogenated nitrile rubber, isoprenebutadiene rubber, polyurethane rubber, fluorine rubber, silicone One or more selected from rubber, ethylene propylene rubber, EPDM rubber, hypalon rubber, chloroprene rubber, ethylene vinyl acetate rubber, acrylic rubber, styrene butadiene rubber including nitrile, and neoprene rubber can be used.

상기에서 합성고무는 유화 중합 스티렌-부타디엔 공중합 고무, 결합 스티렌 5 내지 50 중량%이고 부타디엔 결합 단위 부분의 1,2-비닐 결합량 10 내지 80%인 용액 중합 랜덤 스티렌-부타디엔 공중합 고무, 부타디엔 결합 단위 부분의 1,4-트랜스 결합량이 70 내지 95%인 고트랜스 스티렌-부타디엔 공중합 고무, 저시스폴리 부타디엔 고무, 고시스폴리부타디엔 고무, 부타디엔 결합 단위 부분의 1,4-트랜스 결합량 70 내지 95%인 고트랜스폴리부타디엔 고무, 스티렌-이소프렌 공중합 고무, 부타디엔-이소프렌 공중합체 고무, 용액 중합 랜덤 스티렌-부타디엔-이소프렌 공중합 고무, 유화 중합 랜덤 스티렌-부타디엔-이소프렌 공중합 고무, 유화 중합 스티렌-아크릴로니트릴-부타디엔 공중합 고무, 아크릴로니트릴-부타디엔 공중합 고무, 고비닐 스티렌-부타디엔 공중합 고무-저비닐 스티렌-부타디엔 공중합 고무 블록 공중합 고무, 및 폴리스티렌-폴리부타디엔-폴리스티렌 블록 공중합체의 군으로부터 선택된 어느 하나 이상을 사용할 수 있다.In the above, the synthetic rubber is an emulsion-polymerized styrene-butadiene copolymer rubber, a solution-polymerized random styrene-butadiene copolymer rubber, butadiene-coupling unit, which is 5 to 50% by weight of bonded styrene and 10 to 80% of 1,2-vinyl bond amount of the butadiene-coupling unit. High trans styrene-butadiene rubber, low cispolybutadiene rubber, high cispolybutadiene rubber, butadiene coupling amount of 70 to 95% of 1,4-trans bonding amount of the part 70 to 95% Phosphorus high transpolybutadiene rubber, styrene-isoprene copolymer rubber, butadiene-isoprene copolymer rubber, solution polymerization random styrene-butadiene-isoprene copolymer rubber, emulsion polymerization random styrene-butadiene-isoprene copolymer rubber, emulsion polymerization styrene-acrylonitrile- Butadiene copolymer rubber, Acrylonitrile-butadiene copolymer rubber, High vinyl styrene-butadiene Polymerized rubber-it may be at least one selected from the group consisting of polystyrene block copolymer-low vinyl styrene-butadiene copolymer rubber block copolymer rubber, and polystyrene-polybutadiene.

본 발명의 타이어 트레드 고무조성물에서 내발열성 및 내마모성 향상을 위해 고분산성 카본블랙, 고분산성 실리카 및 폴리에틸렌(polyethylene)을 고무조성물에 첨가하는 첨가제로 사용할 수 있다. 이때 폴리에틸렌은 재생 폴리에틸렌을 사용할 수 있어 자원 재활용적인 측면에서 친환경적인 타이어 트레드 고무조성물을 제공할 수 있다.In the tire tread rubber composition of the present invention, highly dispersible carbon black, highly dispersible silica, and polyethylene may be used as an additive to the rubber composition to improve heat resistance and wear resistance. At this time, polyethylene can use recycled polyethylene can provide an environmentally friendly tire tread rubber composition in terms of resource recycling.

상기에서 고분산성 카본블랙, 고분산성 실리카 및 폴리에틸렌은 원료고무 100중량부에 대하여 고분산성 카본블랙 20∼50중량부, 고분산성 실리카 5∼30중량부, 폴리에틸렌 10∼30중량부를 사용할 수 있다.The highly dispersible carbon black, highly dispersible silica, and polyethylene may be used in an amount of 20 to 50 parts by weight, 5 to 30 parts by weight of highly dispersible silica, and 10 to 30 parts by weight of polyethylene, based on 100 parts by weight of the raw material rubber.

본 발명의 타이어 트레드 고무조성물에서 고분산성 카본블랙은 요오드 흡착가 110∼130mg/g, DBP 흡유량이 110∼120ml/100g인 것을 사용할 수 있다.In the tire tread rubber composition of the present invention, the highly dispersible carbon black may have an iodine adsorption of 110 to 130 mg / g and a DBP oil absorption of 110 to 120 ml / 100 g.

본 발명의 타이어 트레드 고무조성물에서 고분산성 카본블랙은 요오드 흡착 가 118∼126mg/g, DBP 흡유량이 112∼120ml/100g인 것을 사용할 수 있다.In the tire tread rubber composition of the present invention, the highly dispersible carbon black may have an iodine adsorption of 118 to 126 mg / g and a DBP oil absorption of 112 to 120 ml / 100 g.

본 발명의 타이어 트레드 고무조성물에서 고분산성 실리카는 BET 120∼140m2/g, DBP 흡유량이 120∼130ml/100g인 것을 사용할 수 있다.In the tire tread rubber composition of the present invention, the highly dispersible silica may be one having a BET 120 to 140 m 2 / g and a DBP oil absorption of 120 to 130 ml / 100 g.

본 발명의 타이어 트레드 고무조성물에서 폴리에틸렌은 중량평균분자량(weight averaged molecular weight, Mw)이 10,000∼50,000인 것을 사용할 수 있다.In the tire tread rubber composition of the present invention, polyethylene may be used having a weight average molecular weight (Mw) of 10,000 to 50,000.

본 발명의 타이어 트레드 고무조성물에서 폴리에틸렌은 중량평균분자량(Mw)이 25,000∼30,000인 것을 사용할 수 있다.In the tire tread rubber composition of the present invention, polyethylene having a weight average molecular weight (Mw) of 25,000 to 30,000 can be used.

본 발명의 타이어 트레드 고무조성물에서 폴리에틸렌은 중량평균분자량(Mw)이 10,000∼50,000인 재생 폴리에틸렌을 사용할 수 있다.In the tire tread rubber composition of the present invention, polyethylene may be a recycled polyethylene having a weight average molecular weight (Mw) of 10,000 to 50,000.

본 발명의 타이어 트레드 고무조성물에서 폴리에틸렌은 중량평균분자량(Mw)이 25,000∼30,000인 재생 폴리에틸렌을 사용할 수 있다.In the tire tread rubber composition of the present invention, polyethylene may be used a recycled polyethylene having a weight average molecular weight (Mw) of 25,000 to 30,000.

본 발명의 타이어 트레드 고무조성물은 실리카의 분산성 향상을 위해 커플링제를 원료고무 100중량부에 대하여 0.5∼5중량부를 사용할 수 있다. The tire tread rubber composition of the present invention may use 0.5 to 5 parts by weight of the coupling agent based on 100 parts by weight of the raw material rubber to improve the dispersibility of silica.

상기에서 커플링제는 하기 구조식(1)의 다이메틸 아미노 에탄올(Dimethyl amino ethanol, DMAE), 하기 구조식(2)의 헥사메틸다이실라잔(Hexamethyldisilazane, HMDZ) 중에서 선택된 어느 하나 이상을 사용할 수 있다.In the coupling agent, any one or more selected from dimethyl amino ethanol (DMAE) of the following structural formula (1) and hexamethyldisilazane (HMDZ) of the following structural formula (2) may be used.

(EtO)3-Si-CH2CH2CH2-S-CO(CH2)6CH3...구조식(1)(EtO) 3 -Si-CH 2 CH 2 CH 2 -S-CO (CH 2 ) 6 CH 3 ... Structural formula (1)

(CH3)3Si-HN-Si(CH3)3....구조식(2)(CH 3 ) 3 Si-HN-Si (CH 3 ) 3 .... Structure (2)

본 발명의 타이어 트레드 고무조성물은 내발열성 및 내마모성 향상을 위해 클레이(Clay), 탈크(Talc), 운모(mica), 일라이트(illite), 카올린(kaolin), 토르말린(tourmaline), 맥반석(elvan), 자수정(amethyst), 황토(yellow stone), 신디오탁틱-1,2-폴리부타디엔(syndiotactic-1,2-polybutadiene, SPB) 중에서 선택된 어느 하나 이상의 충전제를 추가로 더 포함할 수 있다.The tire tread rubber composition of the present invention is clay, talc, mica, illite, kaolin, tourmaline, elvan to improve heat resistance and abrasion resistance. It may further comprise any one or more fillers selected from amethyst, yellow stone, syndiotactic-1,2-polybutadiene (SPB).

상기에서 클레이, 탈크, 운모, 일라이트, 카올린, 토르말린(tourmaline), 맥반석, 자수정, 황토, 신디오탁틱-1,2-폴리부타디엔 중에서 선택된 어느 하나 이상의 충전제를 원료고무 100중량부에 대하여 10∼20중량부를 추가로 더 포함할 수 있다.10 to 100 parts by weight of at least one filler selected from clay, talc, mica, illite, kaolin, tourmaline, elvan, amethyst, ocher, syndiotactic-1,2-polybutadiene, based on 100 parts by weight of raw rubber 20 parts by weight may be further included.

상기에서 신디오탁틱-1,2-폴리부타디엔(SPB)은 직경 0.01∼0.1㎛이고, 비표면적이 80∼90m2/g인 단섬유상인 것을 사용할 수 있다.In the above, syndiotactic-1,2-polybutadiene (SPB) may be a single fiber having a diameter of 0.01 to 0.1 µm and a specific surface area of 80 to 90 m 2 / g.

상기에서 신디오탁틱-1,2-폴리부타디엔(SPB)은 직경 1∼10㎛이고, 비표면적이 100∼120m2/g인 단섬유상인 것을 사용할 수 있다.In the above, syndiotactic-1,2-polybutadiene (SPB) may be a single fiber having a diameter of 1 to 10 µm and a specific surface area of 100 to 120 m 2 / g.

본 발명의 타이어 트레드 고무조성물에 대하여 다양한 성분, 함량을 적용한바, 본 발명의 목적에 부합하는 타이어 트레드 고무조성물을 얻기 위해서는 상기에서 언급한 조건의 타이어 트레드 고무조성물이 바람직하다.Various components and contents are applied to the tire tread rubber composition of the present invention. In order to obtain a tire tread rubber composition meeting the object of the present invention, the tire tread rubber composition under the above-mentioned conditions is preferable.

본 발명은 상기에서 언급한 원료고무, 충전제, 폴리에틸렌, 커플링제 이외에 종래 타이어 트레드 고무조성물에 사용되는 충전제, 노화방지제, 활성제, 공정오일, 가류제, 가류촉진제와 같은 각종 첨가제를 필요에 따라 적의 선택하여 소정의 함량으로 사용할 수 있다. 그러나 이들은 종래 타이어 트레드 고무조성물에 사용되는 일반적인 성분으로서 본원발명의 필수 구성성분이 아니므로 이하 자세한 내용은 생략하기로 한다.According to the present invention, various additives such as fillers, anti-aging agents, activators, process oils, vulcanizing agents, and vulcanization accelerators, which are used in conventional tire tread rubber compositions, in addition to the above-mentioned raw rubbers, fillers, polyethylene, and coupling agents, are selected as necessary. It can be used in a predetermined content. However, these are general components used in conventional tire tread rubber compositions, and thus are not essential components of the present invention, and thus the detailed descriptions thereof will be omitted.

본 발명은 상기의 타이어 트레드 고무조성물로 이루어진 고무를 포함한다. The present invention includes a rubber consisting of the tire tread rubber composition.

본 발명은 상기의 타이어 트레드 고무조성물로 이루어진 고무를 함유하는 타이어를 포함한다. The present invention includes a tire containing a rubber composed of the tire tread rubber composition described above.

본 발명은 상기의 타이어 트레드 고무조성물로 이루어진 고무를 트레드로 함유하는 타이어를 포함한다. The present invention includes a tire containing the rubber made of the tire tread rubber composition as a tread.

상기에서 본 타이어 트레드 고무조성물로 이루어진 고무를 함유하는 타이어에 있어서, 타이어는 승용차용 타이어, 트럭용 타이어, 버스용 타이어, 오토바이용 타이어, 항공기용 타이어 중에서 선택된 어느 하나를 나타낸다.In the tire containing the rubber made of the tire tread rubber composition as described above, the tire represents any one selected from passenger car tires, truck tires, bus tires, motorcycle tires and aircraft tires.

이하 본 발명을 다음의 실시예, 비교예, 시험예에 의하여 보다 상세히 설명하고자 한다. 그러나 이들은 본 발명의 설명하기 위한 하나의 일예일 뿐 이들에 의해 본 발명의 권리범위가 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail by the following examples, comparative examples, and test examples. However, these are only one example for describing the present invention, and the scope of the present invention is not limited thereto.

<비교예>Comparative Example

천연고무로 원료고무를 하고, 상기 원료고무 100중량부에 대하여 착해제 0.1중량부, 산화아연(ZnO) 3중량부(Stearic acid), 스테아린산 2중량부, 공정오일 3중량부, 카본블랙 50중량부를 밴버리 믹서에 첨가하고 150℃에서 10분 동안 배합하여 미가류 고무시편을 제조하였다.The raw material rubber is made of natural rubber, and 0.1 parts by weight of a decanting agent, 3 parts by weight of zinc oxide (ZnO), stearic acid, 2 parts by weight of stearic acid, 3 parts by weight of process oil, and 50 parts by weight of carbon black based on 100 parts by weight of the raw material rubber. Part was added to the Banbury mixer and blended at 150 ° C. for 10 minutes to prepare an unvulcanized rubber specimen.

상기에서 카본블랙은 요오드 흡착가 85±5g/kg, DBP 흡착가 90±5ml/100g인 것을 사용하였다.In the above carbon iodine adsorption was used as 85 ± 5g / kg, DBP adsorption 90 ± 5ml / 100g.

하기 표 1에 비교예 고무성분의 조성을 정리하여 나타내었다.Table 1 shows the composition of the rubber composition of the comparative example.

<실시예 1>&Lt; Example 1 >

천연고무로 원료고무를 하고, 상기 원료고무 100중량부에 대하여 착해제 0.1중량부, 산화아연(ZnO) 3중량부(Stearic acid), 스테아린산 2중량부, 공정오일 3중량부, 카본블랙 20중량부, 실리카 10중량부, 재생 폴리에틸렌 30중량부, 커플링제 2중량부를 밴버리 믹서에 첨가하고 150℃에서 10분 동안 배합하여 미가류 고무시편을 제조하였다.The raw material rubber is made of natural rubber, and 0.1 parts by weight of a decanting agent, 3 parts by weight of zinc oxide (ZnO), stearic acid, 2 parts by weight of stearic acid, 3 parts by weight of process oil, and 20 parts by weight of carbon black based on 100 parts by weight of the raw material rubber. 10 parts by weight of silica, 30 parts by weight of regenerated polyethylene, and 2 parts by weight of coupling agent were added to a Banbury mixer, and blended at 150 ° C. for 10 minutes to prepare an unvulcanized rubber specimen.

상기에서 카본블랙은 요오드 흡착가 122±4mg/g, DBP 흡유량이 116±4ml/100g인 것을 사용하였고, 실리카는 BET 130±10m2/g, DBP 흡유량이 125±5ml/100g인 것을 사용하였고, 재생 폴리에틸렌은 중량평균분자량(Mw)이 27500± 2500인 것을 사용하였다.In the carbon black, iodine adsorption was used at 122 ± 4mg / g, DBP oil absorption 116 ± 4ml / 100g, silica was used BET 130 ± 10m 2 / g, DBP oil absorption 125 ± 5ml / 100g, regeneration Polyethylene had a weight average molecular weight (Mw) of 27500 ± 2500.

상기에서 커플링제는 하기 구조식(1)의 다이메틸 아미노 에탄올(Dimethyl amino ethanol, DMAE)을 사용하였다.In the coupling agent, dimethyl amino ethanol (DMAE) of the following structural formula (1) was used.

(EtO)3-Si-CH2CH2CH2-S-CO(CH2)6CH3...구조식(1)(EtO) 3 -Si-CH 2 CH 2 CH 2 -S-CO (CH 2 ) 6 CH 3 ... Structural formula (1)

하기 표 1에 실시예 고무성분의 조성을 정리하여 나타내었다.Table 1 below shows the composition of the rubber component.

<실시예 2><Example 2>

커플링제로서 구조식(1)의 다이메틸 아미노 에탄올(DMAE) 대신 하기 구조식(2)의 헥사메틸다이실라잔(Hexamethyldisilazane, HMDZ)을 사용하는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 미가류 고무시편을 제조하였다.Unvulcanized rubber in the same manner as in Example 1 except for using hexamethyldisilazane (HMDZ) of formula (2) instead of dimethyl amino ethanol (DMAE) of formula (1) as a coupling agent. Specimen was prepared.

(CH3)3Si-HN-Si(CH3)3....구조식(2)(CH 3 ) 3 Si-HN-Si (CH 3 ) 3 .... Structure (2)

표 1. 비교예 및 실시예의 고무조성(단위:중량부)Table 1. Rubber composition of comparative examples and examples (unit: parts by weight)

항목Item 비교예Comparative example 실시예 1Example 1 실시예 2Example 2 천연고무Natural rubber 100100 100100 100100 착해제Releasing 0.10.1 0.10.1 0.10.1 산화아연Zinc oxide 33 33 33 스테아린산Stearic acid 22 22 22 공정오일Process oil 33 33 33 카본블랙Carbon black 5050 2020 2020 실리카Silica -- 1010 1010 재생 폴리에틸렌Recycled polyethylene -- 2020 2020 커플링제Coupling agent -- 22 22

<시험예><Test Example>

상기 비교예 및 실시예에서 제조한 미가류 고무시편에 대해 ASTM 관련규정에 의해 점도, 인장물성(경도, 300% 모듈러스 인장강도, 신율), 내발열성(Heat Build-Up, H.B.U.), 블로우 아웃(Blow out), 내마모성(PICO), 내커팅성 및 내칩성(Cut&Chip) 등의 물성을 측정하고 그 결과를 아래의 표 2에 나타내었다.Viscosity, tensile properties (hardness, 300% modulus tensile strength, elongation), heat resistance (Heat Build-Up, HBU) and blow out (according to ASTM related regulations) for the unvulcanized rubber specimens prepared in Comparative Examples and Examples Blow out), abrasion resistance (PICO), cutting resistance and chip resistance (Cut & Chip) and the physical properties were measured and the results are shown in Table 2 below.

표 2. 비교예 및 실시예 고무시편의 물성Table 2. Comparative Examples and Examples Properties of Rubber Specimens

시험항목Test Items 비교예Comparative example 실시예 1Example 1 실시예 1Example 1 100℃점도(cP)100 ℃ viscosity (cP) 6868 6969 6868 경도(shore A)Hardness (shore A) 6666 6868 6969 300% 모듈러스(kg/cm2)300% modulus (kg / cm 2 ) 113113 117117 118118 인장강도(kg/cm2)Tensile Strength (kg / cm 2 ) 243243 250250 252252 신율(%)% Elongation 540540 526526 528528 H.B.U(△℃)H.B.U (△ ° C) 2828 2626 2525 Blow out(min.)Blow out (min.) 4.94.9 5.15.1 5.25.2 내마모성(PICO)Wear Resistance (PICO) 0.0310.031 0.0230.023 0.0220.022 Cut&ChipCut & Chip 2.8552.855 2.6752.675 2.6732.673

*내발열성(Heat Build-Up, H.B.U.) : 페리 기계사의 히스테리시스 시험기(hystetsis testing machine)를 이용하여 일정한 스트로크를 시편에 부여하여 상승된 온도를 측정하는 방법으로 수치가 적을수록 내발열 특성이 우수함을 나타낸다. * Heat Build-Up (HBU): A method of measuring the elevated temperature by applying a certain stroke to the specimen using a Hysteresis testing machine manufactured by Perry Machinery. Indicates.

*내마모성(PICO) : 비.에프.굿리치 마모시험기를 이용하여 칼날이, 회전하는 시편의 위쪽을 누르면서 시험하는 방법으로, 최초의 시편무게와 시험후의 시편무게와의 무게차가 적을수록, 즉 수치가 적을수록 내마모 성능이 우수함을 나타낸다.* Wear resistance (PICO): A test using a B.F. Goodrich wear tester while pressing the upper part of a rotating specimen.The smaller the weight difference between the original specimen weight and the specimen specimen after the test, The smaller the value, the better the wear resistance.

*내커팅성 및 내칩성(Cut&Chip) : 비.에프.굿리치 커트 및 칩 테스터(B.F. Goodrich cut chip tester)를 이용하여 날카로운 칼날이, 회전하는 시편을 일정한 속도로 내리치면서 시험하는 방법으로, 최초의 시편 무게와 시험후의 시편 무게와 의 무게차가 적을수록 즉 수치가 적을수록 내커팅성 및 내칩성 성능이 우수함을 나타낸다.* Cut & Chip: It is a method that the sharp blade is tested while lowering the rotating specimen at a constant speed by using BF Goodrich cut chip tester. The smaller the difference between the weight of the specimen and the weight of the specimen after testing, that is, the smaller the value, the better the cutting resistance and chip resistance performance.

상기 표 2에서 보는 바와 같이 본 발명의 고무조성물을 나타낸 실시예 1,2의 미가류 고무시편은 종래 고무조성물을 나타낸 비교예의 미가류 고무시편과 물성을 비교시 인장물성, 내발열성 및 내마모성에 대한 특성이 우수함을 알 수 있다.As shown in Table 2, the unvulcanized rubber specimens of Examples 1 and 2 showing the rubber composition of the present invention are compared with those of the unvulcanized rubber specimens of the comparative example showing the conventional rubber composition for tensile properties, heat resistance and abrasion resistance. It can be seen that the characteristics are excellent.

상술한 바와 같이, 본 발명의 바람직한 실시예를 참조하여 설명하였지만 해당 기술 분야의 숙련된 당업자라면 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. As described above, although described with reference to a preferred embodiment of the present invention, those skilled in the art will be variously modified and modified within the scope of the present invention without departing from the spirit and scope of the invention described in the claims below. It will be appreciated that it can be changed.

Claims (5)

타이어 트레드 고무조성물에 있어서,In the tire tread rubber composition, 원료고무 100중량부에 대하여 요오드 흡착가 110∼130mg/g, DBP 흡유량이 110∼120ml/100g인 고분산성 카본블랙 20∼50중량부; 20 to 50 parts by weight of highly dispersible carbon black having an iodine adsorption of 110 to 130 mg / g and a DBP oil absorption of 110 to 120 ml / 100 g based on 100 parts by weight of the raw material rubber; BET 120∼140m2/g, DBP 흡유량이 120∼130ml/100g인 고분산성 실리카 5∼30중량부;5 to 30 parts by weight of highly dispersible silica having a BET of 120 to 140 m 2 / g and a DBP oil absorption of 120 to 130 ml / 100 g; 중량평균분자량이 25,000∼30,000인 폴리에틸렌 10∼30중량부; 10 to 30 parts by weight of polyethylene having a weight average molecular weight of 25,000 to 30,000; 하기 구조식(1)의 다이메틸 아미노 에탄올(Dimethyl amino ethanol, DMAE), 하기 구조식(2)의 헥사메틸다이실라잔(Hexamethyldisilazane, HMDZ) 중에서 선택된 어느 하나 이상인 커플링제 0.5∼5중량부;0.5 to 5 parts by weight of any one or more selected from dimethyl amino ethanol (DMAE) of the following structural formula (1) and hexamethyldisilazane (HMDZ) of the following structural formula (2); 탈크(Talc), 일라이트(illite), 카올린(kaolin), 토르말린(tourmaline), 맥반석(elvan), 자수정(amethyst), 신디오탁틱-1,2-폴리부타디엔(syndiotactic-1,2-polybutadiene, SPB) 중에서 선택된 어느 하나 이상의 충전제 10∼20중량부;를 포함하는 것을 특징으로 하는 타이어 트레드 고무조성물.Talc, illite, kaolin, tourmaline, elvan, amethyst, syndiotactic-1,2-polybutadiene, 10-20 parts by weight of any one or more fillers selected from SPB) tire tread rubber composition comprising a. (EtO)3-Si-CH2CH2CH2-S-CO(CH2)6CH3...구조식(1)(EtO) 3 -Si-CH 2 CH 2 CH 2 -S-CO (CH 2 ) 6 CH 3 ... Structural formula (1) (CH3)3Si-HN-Si(CH3)3....구조식(2)(CH 3 ) 3 Si-HN-Si (CH 3 ) 3 .... Structure (2) 삭제delete 삭제delete 삭제delete 특허청구범위 제1항의 고무조성물로 이루어진 고무를 포함하는 타이어.A tire comprising a rubber comprising the rubber composition of claim 1.
KR1020080089848A 2008-09-11 2008-09-11 Tire tread rubber composition KR101007642B1 (en)