KR100998727B1 - Outside of concrete construction injection repair method for leaks of oils such as asphalt solution and others - Google Patents

Outside of concrete construction injection repair method for leaks of oils such as asphalt solution and others Download PDF

Info

Publication number
KR100998727B1
KR100998727B1 KR1020100030198A KR20100030198A KR100998727B1 KR 100998727 B1 KR100998727 B1 KR 100998727B1 KR 1020100030198 A KR1020100030198 A KR 1020100030198A KR 20100030198 A KR20100030198 A KR 20100030198A KR 100998727 B1 KR100998727 B1 KR 100998727B1
Authority
KR
South Korea
Prior art keywords
inorganic
injection
organic
concrete structure
solution
Prior art date
Application number
KR1020100030198A
Other languages
Korean (ko)
Inventor
송병창
송철호
Original Assignee
주식회사 아키벤
송병창
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 아키벤, 송병창 filed Critical 주식회사 아키벤
Priority to KR1020100030198A priority Critical patent/KR100998727B1/en
Application granted granted Critical
Publication of KR100998727B1 publication Critical patent/KR100998727B1/en

Abstract

PURPOSE: A method of injection-repairing the rear side of a concrete structure for preventing the inflow and outflow of asphalt solution is provided to prevent the inflow and outflow of asphalt solution inside the concrete structure, since an organic film and an inorganic film are separately formed on the rear side of the concrete structure. CONSTITUTION: A method of injection-repairing the rear side of a concrete structure for preventing the inflow and outflow of asphalt solution comprises following steps. An inorganic injection hole(30) is formed along both sides of cracked portions to pass through a concrete structure(10) or a waterproof layer(20). Inorganic injection material(40) is injected into the rear side gap of the concrete structure. An inorganic membrane(50) is formed of inorganic hardener. An organic membrane(80) is formed of organic elastic gel by the injection of organic injection material(70) into the outside of the inorganic material film.

Description

아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법{Outside of Concrete Construction Injection Repair Method for Leaks of Oils such as Asphalt Solution and Others}Outside of Concrete Construction Injection Repair Method for Leaks of Oils such as Asphalt Solution and Others}

본 발명은 아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법에 관한 것으로, 균열이 발생한 콘크리트 구조물 배면에 견고한 무기질 피막층과 겔 탄성에 의한 유연성을 가진 물 흡수성 유기질 피막층의 이중구조 층을 형성하여, 콘크리트 구조체 내부, 또는 외부로의 아스팔트 용해액 등 유지분 유입 및 배출을 근원적으로 차단하고 내구적으로 보수할 수 있는 아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법에 관한 것이다.
The present invention relates to a method of injecting and repairing the back of a concrete structure to prevent the inflow and outflow of oils from the asphalt solution. By forming a structural layer, concrete structure to prevent oil inflow and outflow of asphalt solution, which can fundamentally block oil inflow and outflow and discharge of asphalt solution, such as asphalt solution into or out of the concrete structure. The back injection repair method.

일반적으로 콘크리트 구조체로 형성된 아스팔트 용해액 등 유지분 저장고 또는, 건설 구조물에 발생한 균열 등을 통한 아스팔트 용해액 등 유지분의 유입 및 유출 결함을 보수하기 위해, 건설현장에서는 아스팔트 용해액 등 유지분의 유입 및 유출균열 틈새를 발포성 우레탄, 에폭시 수지 접착제, 수경성 시멘트를 주성분으로 하는 균열 충전재 등으로 채우거나, In general, in order to repair inflows and outflows of oils and fats such as asphalt melts formed from concrete structures or asphalt melts through cracks in construction structures, inflow of oils and fats from asphalt melts at construction sites Filling the cracks of the outflow cracks with a foam filler composed mainly of foamed urethane, epoxy resin adhesive, hydraulic cement, or the like,

또는 상기 균열 표면을 V 및 U 컷팅하여 수경성 시멘트를 주성분으로 하는 표면 보수재나 유기계 실링재 등으로 채우거나, 또는 수경성 시멘트를 주성분으로 하는 그라우트재, 물과 반응성을 가진 유기 합성 고분자 지수재나, 물과 반응하여 체적을 늘이는 특징을 가진 벤토나이트 광물을 주성분으로 하는 그라우트재, 발포성 유기 그라우트재, 물흡수성 폴리머 수용액 등을 콘크리트 구조체 배면 또는, 콘크리트 구조체 배면 구조체와의 틈새에 강제 주입하여 경화, 발포, 또는 팽윤시키는 방법들을 사용하여 보수하고 있다.
Or V and U cut the crack surface to fill it with a surface repair material or an organic sealing material mainly composed of hydraulic cement, or a grout material mainly composed of hydraulic cement, an organic synthetic polymer index material that is reactive with water, or reacts with water. Grout, foamed organic grout, water-absorbing polymer aqueous solution, etc., which are mainly composed of bentonite minerals, which increase their volume, by injecting them into the gap between the concrete structure back surface or the concrete structure back structure to harden, foam, or swell. The methods are being repaired.

그러나, 전기 균열 틈새를 발포성 우레탄, 에폭시 수지 접착제, 수경성 시멘트를 주성분으로 하는 균열 충전재 등으로 채우는 보수방법과 균열 표면을 V 및 U 컷팅하여 수경성 시멘트를 주성분으로 하는 표면 보수재나 유기계 실링재 등으로 채우는 방법은 시간이 경과하면서 아스팔트 용해액 등 유지분에 용해되거나 균열 주변부에 새로이 발생하는 균열을 통한 아스팔트 용해액 등 유지분의 유입 및 유출을 방지하지 못하는 문제점이 있었다. However, a repair method for filling the electric crack gap with a foamed urethane, an epoxy resin adhesive, and a hydraulic cement-based crack filler, and a method for filling a crack surface with V and U cut surfaces with a hydraulic cement-based surface repair material or organic sealing material, etc. As time went by, there was a problem in that it could not be prevented from inflow and outflow of oils and fats such as asphalt solution through the cracks newly generated at the periphery or cracks in the oils and fats.

또한, 수경성 시멘트를 주성분으로 하는 그라우트재를 콘크리트 구조체 배면이나 또는 콘크리트 구조체 배면 구조체와의 틈새에 강제 주입하여 경화시키는 방법은, 함께 혼합하여 주입한 물 중, 경화체 형성에 필요한 물을 제외한 잉여수가 보수범위 밖에서 생긴 균열이나 또는 새로이 발생하는 균열을 통하여 구조물 내부로 유입되어 아스팔트 용해액 등 유지분을 오염시키거나, 누수결함의 원인이 되는 문제점이 있었다. In addition, the method of hardening by grouting the grout material mainly composed of hydraulic cement into the back of the concrete structure or the gap with the back structure of the concrete structure is to repair the surplus water except the water required for forming the hardened body among the water mixed and injected together. Through the cracks generated outside the range or newly generated cracks introduced into the structure to contaminate the oil, such as asphalt dissolving solution, there was a problem that causes the leak.

또한, 물과 반응성을 가진 유기 합성 고분자 지수재나, 물과 반응하여 체적을 늘이는 특징을 가진 벤토나이트 광물을 주성분으로 하는 그라우트재, 발포성 유기 그라우트재, 물흡수성 폴리머 수용액 등과 같이 주로 물과 반응하는 특성을 가진 재료를 콘크리트 구조체 배면에 강제 주입하여 발포, 또는 팽윤시키는 방법은 균열을 통하여 유입 또는 유출된 친수성의 물과는 성질이 전혀 다른 소수성의 아스팔트 용해액 등 유지분에 의해 발포, 팽윤되지 않거나, 또는 저항성을 잃어버려 보수효과를 전혀 발휘하지 못하는 등 여러가지 문제점이 있었다.
In addition, organic synthetic polymer index materials that are reactive with water, or bentonite minerals that have a characteristic of increasing volume by reacting with water, such as grout materials, effervescent organic grout materials, and water-absorbing polymer aqueous solutions, etc. The method of forcibly foaming or swelling the excitation material by pouring it into the back of the concrete structure is not foamed or swelled by oil or fat such as hydrophobic asphalt solution, which is completely different from the hydrophilic water flowing in or out through the crack, or There were various problems, such as losing resistance and not having a conservative effect at all.

본 발명은 상기와 같은 문제점을 해소하기 위한 것으로, 그 목적은 콘크리트 구조체 배면에 견고한 무기질피막과 유기질피막의 이중구조 피막층을 분리형성하여, 아스팔트 용해액 등 유지분의 콘크리트 구조체 내부 유입 및 유출을 차단할 수 있는 콘크리트 구조체 배면 주입보수방법을 제공하는 것이다. The present invention is to solve the above problems, its purpose is to separate the dual-layer coating layer of the solid inorganic film and the organic film on the back of the concrete structure, to block the inflow and outflow of the concrete structure of oil and fat such as asphalt solution It is to provide an injection repair method for the back of the concrete structure.

본 발명의 또다른 목적은 무기질피막을 형성하는 무기주입재와, 유기질피막을 형성하는 유기주입재의 연계반응을 통해 아스팔트 용해액 등 유지분을 콘크리트 구조체로부터 유리 및 고착시키고, 수화반응 잉여수를 포용하여 차수성 유기질 피막을 형성하여, 균열부위를 통하여 아스팔트 용해액 등 유지분, 또는 빗물이나 지하수가 유입 또는 유출되는 결함을 근원적, 내구적 및 경제적으로 보수할 수 있는 콘크리트 구조체 배면 주입보수공법을 제공하는 것이다. It is another object of the present invention to freeze and fix oils and fats such as asphalt solution from a concrete structure through a linkage reaction between an inorganic injection material for forming an inorganic coating and an organic injection material for forming an organic coating. Forming a water-soluble organic film, providing a back surface injection repair method of the concrete structure that can fundamentally, durable and economically repair defects such as asphalt solution, rainwater or groundwater inflow or outflow through cracks will be.

본 발명의 또다른 목적은 무기주입재와 유기주입재를 목표로 하는 주입위치에 정확하게 주입하여, 콘크리트 구조체의 균열부위를 관통하여 유입되는 아스팔트 용해액 등 유지분이나 지하수나 빗물 등에 의한 오염이나 누수결함, 또는 저장고 내의 아스팔트 용해액 등 유지분의 유출에 따른 토양오염 등에 대한 보수작업을 신속하고 정확하게 할 수 있는 콘크리트 구조체 배면 주입보수공법을 제공하는 것이다.Still another object of the present invention is to accurately inject the inorganic injection material and the organic injection material into the injection position, and contamination or leakage defects due to oils, groundwater or rainwater, such as asphalt solution, which flows through the cracked portion of the concrete structure, Or it is to provide a back injection repair method for the concrete structure that can quickly and accurately repair work such as soil contamination due to the outflow of oil and fat such as asphalt solution in the storage.

본 발명의 또 다른 목적은 콘크리트 구조체의 균열부위를 아스팔트 용해액 등 유지분과 반응하지 않는 수성 실란트로 봉합하여, 콘크리트 구조체 균열 내부에 잔존하는 아스팔트 용해액 등 유지분이 유출되지 않도록 보수하는 콘크리트 구조체 배면 주입보수공법을 제공하는 것이다.
Another object of the present invention is to seal the cracked portion of the concrete structure with an aqueous sealant that does not react with the oil and the like, such as asphalt dissolving solution, and to repair the back of the concrete structure to repair the oil and fat such as asphalt solution remaining inside the crack of the concrete structure to prevent leakage It is to provide a method.

본 발명은 콘크리트 구조체 또는 방수층을 관통하도록 균열부위 양측을 따라 무기주입구멍을 개공하는 1차개공단계;The present invention comprises a primary opening step of opening the inorganic injection hole along both sides of the crack to penetrate the concrete structure or waterproof layer;

상기 무기주입구멍을 통해 콘크리트 구조체의 배면틈새에 무기 주입재를 강제주입하여 충전시키는 무기 주입재 주입단계;An inorganic injection material injection step of forcibly filling and filling an inorganic injection material into the rear gap of the concrete structure through the inorganic injection hole;

상기 무기주입재 주입단계 후 5시간 이상 방치하여 무기주입재에 의해 무기경화체로 이루어진 무기질피막을 형성시키는 경화단계;A curing step of leaving the inorganic injecting material in an inorganic hardened body by leaving the inorganic injecting material for at least 5 hours;

상기 경화단계 후, 콘크리트 구조체와 무기질피막 또는 콘크리트 구조체와 무기질피막 및 방수층을 관통하도록 무기주입구멍과 이에 인접하는 또다른 무기 주입구멍의 중간 위치에 유기주입구멍을 개공하는 2차개공단계;A secondary opening step of opening the organic injection hole at an intermediate position between the inorganic injection hole and another inorganic injection hole adjacent thereto so as to pass through the concrete structure and the inorganic coating or the concrete structure and the inorganic coating and the waterproofing layer after the curing step;

상기 유기주입구멍을 통해 유기주입재를 무기질피막 외부 측으로 강제 주입시켜 유기질 탄성 겔로 이루어진 유기질피막을 형성하는 유기주입재 주입단계;An organic injection material injection step of forcibly injecting an organic injection material into the outer side of the inorganic coating through the organic injection hole to form an organic film made of an organic elastic gel;

상기 유기주입구멍, 무기주입구멍 및 균열부위를 무기시멘트 모르타르 또는 수성 실란트로 봉합시키는 봉합단계;를 통해 콘크리트 구조체 배면틈새에 무기질피막과, 유기질피막의 분리된 이중구조의 피막층이 형성되도록 되어 있다.
The organic injection hole, the inorganic injection hole and the cracked portion is sealed with an inorganic cement mortar or an aqueous sealant; through the gap between the rear surface of the concrete structure, an inorganic coating layer and an organic coating layer are formed so that a separate double layer coating layer is formed.

이와 같이 본 발명은 콘크리트 구조체 배면틈새에 무기경화체로 이루어진 무기질 피막과 유기질 탄성 겔로 이루어진 유기질 피막을 구비하도록 하여, 콘크리트 구조물에서 발생하는 균열, 익스펜션 죠인트(ExP.J), 구조 죠인트(Construction J.)등과 같은 틈새를 통한 아스팔트 용해액 등 유지분의 유입 및 유출 결함을 근원적으로 보수할 수 있다. As described above, the present invention is provided with an inorganic coating made of an inorganic hardening body and an organic coating made of an organic elastic gel in the rear gap of the concrete structure, so that cracks, expansion joints (ExP.J), and structural joints generated in the concrete structure are provided. It is possible to fundamentally repair inflow and outflow defects of fats and oils such as asphalt solution through gaps.

또한, 본 발명은 주로 물과 혼합하여 사용하는 수경성 시멘트로 조성되는 무기주입재를 목표로 하는 주입위치에 정확하게, 또는 적정량 주입하여, 물의 소수성 상호작용에 의해 콘크리트 구조체 균열표면에 부착하고 있는 아스팔트 용해액 등 유지분을 해리, 또는 분리시키고, 경화체 형성을 통하여 고착시켜 유동성을 억제하고, 이를 통해 유지분의 내부유입 및 외부유출을 차단하도록 되어 있다. In addition, the present invention is precisely or appropriately injected to the target injection position of the inorganic injection material composed mainly of hydraulic cement used by mixing with water, the asphalt solution is attached to the crack surface of the concrete structure by hydrophobic interaction of water The fat or oil is separated or separated, and is fixed through the formation of a cured body to suppress fluidity, thereby blocking the inflow and outflow of the fat or oil.

또한, 본 발명은 유기주입재로 물흡수성 유기 폴리머 수용액을 목표로 하는 주입위치에 정확하게 또한 적정량 주입하여, 물과 함께 주입한 수경성 무기 주입재의 잉여수를 포용하고, 이를 통해 차수성 겔 탄성체를 형성시킴으로써, 빗물이나 지하수에 의한 아스팔트 용해액 등 유지분의 오염, 또는 누수 발생을 보수할 수 있다. In addition, the present invention is to accurately and appropriately inject the water-absorbing organic polymer aqueous solution into the target injection position as an organic injection material, to include the excess water of the hydraulic inorganic injection material injected with water, thereby forming a water-repellent gel elastomer In addition, it is possible to repair the contamination of oil or fat such as asphalt solution by rainwater or groundwater, or leakage.

또한, 본 발명은 콘크리트 구조체의 균열, 유기주입구멍 및 무기주입구멍을 아스팔트 용해액 등 유지분과 반응하지 않는 무기시멘트 모르타르 또는 수성 실란트로 균열을 봉합하여 콘크리트 구조체 균열 내부에 잔존하는 아스팔트 용해액 등 유지분이 유출되지 않는 등 많은 효과가 있다.
In addition, the present invention seals the cracks of the inorganic structure mortar or aqueous sealant that does not react the cracks, organic injection holes and inorganic injection holes of the concrete structure with the fat and oil, such as asphalt dissolving liquid to maintain the fat and oil such as asphalt solution remaining in the crack of the concrete structure. There are many effects such as not leaking.

도 1 은 본 발명에 따른 보수과정을 보인 예시도
도 2 는 본 발명에 따른 무기/유기 주입구멍의 개구상태를 보인 예시도
도 3 은 본 발명에 따른 무기/유기 주입구멍의 개구정도를 보인 예시도
도 4 는 본 발명에 따른 유기주입재의 반응과정을 보인 예시도
도 5 는 본 발명에 따른 시공과정을 보인 블록예시도
도 6 은 본 발명에 따른 무기주입재 및 유기주입재 주입과정을 보인 예시도
도 7 은 본 발명에 따른 무기질피막 및 유기질피막의 형성과정을 보인 예시도1 is an exemplary view showing a repair process according to the present invention
2 is an exemplary view showing an opening state of the inorganic / organic injection hole according to the present invention.
Figure 3 is an exemplary view showing the opening degree of the inorganic / organic injection hole according to the present invention
4 is an exemplary view showing a reaction process of an organic injection material according to the present invention
5 is an exemplary block diagram showing a construction process according to the present invention.
6 is an exemplary view showing a process of injecting inorganic and organic injecting materials according to the present invention
7 is an exemplary view showing a process of forming an inorganic coating and an organic coating according to the present invention.

도 1 은 본 발명에 따른 보수과정을 보인 예시도를, 도 2 는 본 발명에 따른 무기/유기주입구멍의 개구상태를 보인 예시도를, 도 3 은 본 발명에 따른 무기/유기주입구멍의 개구정도를 보인 예시도를, 도 4 는 본 발명에 따른 유기주입재의 반응과정을 보인 예시도를, 도 5 는 본 발명에 따른 시공과정을 보인 블록예시도를 도시한 것으로, 1 is an exemplary view showing a repair process according to the present invention, Figure 2 is an exemplary view showing the opening state of the inorganic / organic injection hole according to the present invention, Figure 3 is an opening of the inorganic / organic injection hole according to the present invention Exemplary view showing the degree, Figure 4 is an illustration showing a reaction process of the organic injection material according to the invention, Figure 5 is a block diagram showing a construction process according to the present invention,

본 발명은 콘크리트 구조체(10) 또는 방수층(20)을 관통하도록 균열부위(11) 양측을 따라 무기주입구멍(30)를 개공하는 1차개공단계; 상기 무기주입구멍(30)을 통해 콘크리트 구조체(10)의 배면틈새에 무기주입재(40)를 강제주입하여 충전시키는 무기주입재 주입단계; 상기 무기주입재 주입단계 후 5시간 이상 방치하여 무기주입재(40)에 의해 무기경화체로 이루어진 무기질피막(50)을 형성시키는 경화단계; 상기 경화단계 후, 콘크리트 구조체(10)와 무기질피막(50) 또는 콘크리트 구조체(10)와 무기질피막(50) 및 방수층(20)을 관통하도록 무기주입구멍(30)과 이에 인접하는 또다른 무기주입구멍(30)의 중간 위치에 유기주입구멍(60)을 개공하는 2차개공단계; 상기 유기주입구멍(60)을 통해 유기주입재(70)를 무기질피막(50) 외부측으로 강제 주입시켜 유기질 탄성 겔로 이루어진 유기질피막(80)을 형성하는 유기주입재 주입단계; 상기 유기주입구멍(70), 무기주입구멍(30) 및 균열부위(11)를 수성의 실란트(90)로 봉합시키는 봉합단계;를 통해 콘크리트 구조체 배면틈새에 무기질피막(50)과, 유기질 피막(80)의 분리된 이중구조의 피막층이 형성되도록 되어 있다.
The present invention includes a primary opening step of opening the inorganic injection hole 30 along both sides of the crack portion 11 to penetrate the concrete structure 10 or the waterproof layer 20; An inorganic injection material injection step of forcibly injecting and filling the inorganic injection material 40 into the rear gap of the concrete structure 10 through the inorganic injection hole 30; A curing step of leaving the inorganic injecting material left for 5 hours or more to form the inorganic coating 50 made of the inorganic hardener by the inorganic injecting material 40; After the curing step, the inorganic injection hole 30 and another inorganic injection adjacent thereto to penetrate the concrete structure 10 and the inorganic coating 50 or the concrete structure 10 and the inorganic coating 50 and the waterproof layer 20 A secondary opening step of opening the organic injection hole 60 at an intermediate position of the hole 30; An organic injection material injection step of forcibly injecting the organic injection material 70 to the outside of the inorganic coating 50 through the organic injection hole 60 to form an organic coating 80 made of an organic elastic gel; Sealing step of sealing the organic injection hole 70, the inorganic injection hole 30 and the crack portion 11 with an aqueous sealant 90; the inorganic coating 50 and the organic coating ( 80 is to form a separate double-layer coating layer.

상기 1차개공단계는 아스팔트 용해액 등 유지분 유입, 또는 유출 결함이 발생되고 있는 콘크리트 구조체의 균열, 틈새, 누유흔적 및 방수층의 유무에 따라 무기주입재(40)의 주입위치를 결정하고, 상기 주입위치 결정에 따라 콘크리트 구조체 배면틈새 즉, 콘크리트 구조체(10)와 방수층(20) 사이, 콘크리트 구조체의 방수층(20)과 보호누름층(110) 또는 지반층(100) 사이에 무기주입재(40)가 주입되도록 콘크리트 구조체의 방수층, 배면 구조층이나 지반층까지 관통하는 무기주입구멍(30)을 일렬로 개공한다.
The primary opening step is to determine the injection position of the inorganic injection material 40 according to the presence of cracks, gaps, leakage marks and waterproof layer of the concrete structure in which oil inflow or outflow defects such as asphalt melt solution is generated, and the injection According to the positioning, an inorganic injection material 40 is formed between the rear surface of the concrete structure, that is, between the concrete structure 10 and the waterproof layer 20, and between the waterproof layer 20 and the protective pressing layer 110 or the ground layer 100 of the concrete structure. In order to be injected, the inorganic injection hole 30 penetrating to the waterproof layer, the back structure layer, or the ground layer of the concrete structure in a row.

도 2 는 본 발명에 따른 무기주입구멍의 개구상태를 보인 예시도를 도시한 것으로, 아스팔트 용해액 등 유지분 유입 및 유출결함이 발생하고 있는 균열이나, 익스펜션 죠인트(ExP.J), 구조 죠인트(Construction J.)등과 같은 틈새, 또는 상기 아스팔트 용해액 등 유지분 누유흔적을 따라 0.5M∼2.0M 간격으로, 직경 5∼50㎜ 크기의 콘크리트 드릴 등을 사용하여, 콘크리트 구조체 배면의 방수층(20)이나, 지반층(100)까지 관통하는 무기주입구멍(30)을 일렬로 개공한다. Figure 2 shows an exemplary view showing the opening state of the inorganic injection hole according to the present invention, the cracks, oil expansion joints (ExP.J), structural joints that are caused by oil inflow and outflow defects, such as asphalt melt solution The waterproofing layer on the back of the concrete structure using a concrete drill having a diameter of 5 to 50 mm at intervals of 0.5 M to 2.0 M along the oil leakage such as the construction solution J. ) And the inorganic injection hole 30 penetrating to the ground layer 100 in a row.

즉, 상기 아스팔트 용해액 등 유지분 누유결함이 발생하고 있는 균열이나, 익스펜션 죠인트(ExP.J), 구조 죠인트(Construction J.)등과 같은 틈새, 또는 상기 아스팔트 용해액 등 유지분 누유흔적을 따라 누유량이 많을 경우 0.5M간격으로, 누유량이 적을 경우에는 2.0M 간격으로, 또한, 주입 깊이에 따라 직경 5∼50㎜ 크기의 콘크리트 드릴 등을 사용하여, 콘크리트 구조체 배면의 방수층(20)이나, 보호누름층(110) 또는 지반층(100)까지 관통하는 무기주입구멍(30)을 일렬로 개공한다.
That is, along the cracks in which oil-oil leakage defects, such as the said asphalt solution, generate | occur | produce oil, gaps, such as expansion joints (ExP.J) and construction joints (Construction J.), or oil-oil leakage traces, such as the asphalt solution, If there is a large amount of oil leakage, the gap is 0.5M, if the amount of oil leakage is 2.0M interval, and depending on the depth of injection using a concrete drill having a diameter of 5-50mm, etc., the waterproof layer 20 on the back of the concrete structure or protection The inorganic injection hole 30 penetrates to the pressing layer 110 or the ground layer 100 in a row.

이때, 상기 무기주입재의 주입위치는 콘크리트 구조물의 특성, 방수층의 유무나 종별에 따라 결정된다. 즉, 무기주입재(40)의 적정 주입위치를 결정함에 있어, 기존 방수층의 활용여부를 판단하는 것이 중요하며, 경년 15년 이내의 구조물 방수층은 일부 누수되는 부위를 제외하고는 거의 재활용이 가능한 상태이다. 예를 들어, 접착력이 다소 열악한 시트 방수재의 경우에는 방수층 하부에 주입재를 주입하는 것이, 접착력이 뛰어난 도막계 방수층의 경우에는 방수층 표면위에 주입재를 주입하는 것이 효과를 극대화 시킬 수 있다. 물론 기존 방수층이나 보호누름층이 없을 경우에는 구조체 배면과 지반 틈새에 주입재를 주입할 필요가 있다. 따라서, 무기주입재의 주입 위치선정은 보수효과의 극대화를 위해서는 필수적이며, 당연히 구조물의 특성, 방수층의 유무나 종별을 확인할 필요가 있으며, 이에 따라 도 2 및 도 3 에 도시된 바와 같이, 배면주입재의 주입위치가 결정된다.
At this time, the injection position of the inorganic injection material is determined according to the characteristics of the concrete structure, the presence or absence of the waterproof layer. That is, in determining the proper injection position of the inorganic injection material 40, it is important to determine whether the existing waterproof layer is utilized, and within 15 years of construction, the waterproof layer of the structure is almost recyclable except for some leaky parts. . For example, in the case of a sheet waterproofing material having a poor adhesive strength, injecting the injection material under the waterproofing layer may maximize the effect of injecting the injection material on the surface of the waterproofing layer in the case of a coating-based waterproofing layer having excellent adhesion. Of course, if there is no existing waterproof layer or protective pressing layer, it is necessary to inject the injection material into the back of the structure and ground clearance. Therefore, the injection position selection of the inorganic injection material is essential for maximizing the repair effect, and of course, it is necessary to check the characteristics of the structure, the presence or absence of the waterproof layer, and, accordingly, as shown in FIGS. 2 and 3, The injection position is determined.

도 3 은 본 발명에 따른 무기주입구멍의 개구정도를 보인 예시도를 도시한 것으로, 도 3 의 (a)는 기존 방수층(20) 하부에 무기주입재(40)가 주입되도록 무기주입구멍(30)을 개공한 것으로, 기존 방수층이 쉬트 방수층 등 접착력이 좋지 않을 경우 적용하고, 도 3 의 (b)는 기존 방수층(20) 상부로 무기주입재(40)가 주입되도록 무기주입구멍(30)을 개공한 것으로, 기존 방수층이 도막 방수층 등 접착력이 좋을 경우 적용하며, 도 3 의 (c)는 기존 방수층(20) 및 보호누름층(110)을 관통하여 지반면(60)으로 무기주입재(10)가 주입되도록 무기주입구멍을 개공한 것으로, 기존 방수층이 완전히 파괴되었거나 애당초 방수층이나 보호누름층이 없을 경우 적용할 수 있다.
Figure 3 shows an exemplary view showing the opening degree of the inorganic injection hole according to the present invention, Figure 3 (a) is the inorganic injection hole 30 so that the inorganic injection material 40 is injected into the lower portion of the existing waterproof layer (20). If the existing waterproof layer is not good adhesion, such as sheet waterproof layer is applied, Figure 3 (b) is the opening of the inorganic injection hole 30 so that the inorganic injection material 40 is injected into the upper portion of the existing waterproof layer (20). In this case, the existing waterproof layer is applied when the adhesive strength such as the coating waterproof layer is good, and (c) of FIG. 3 allows the inorganic injection material 10 to be injected into the ground surface 60 through the existing waterproof layer 20 and the protective pressing layer 110. Opening of the inorganic injection hole, it can be applied when the existing waterproof layer is completely destroyed or there is no waterproof layer or protective pressing layer in the first place.

상기 무기주입재 주입단계는 개공된 무기주입구멍(30)에 주입구(120)를 설치하고, 상기 주입구(120)를 통해 콘크리트 구조체와 배면 구조체 틈새에 무기주입재(40)를 펌프로 강제 주입한다. 이와 같이 주입되는 무기주입재는 콘크리트 구조체와 기존 방수층, 또는 지반과의 사이에 대부분 충전된다.
In the inorganic injection material injection step, the injection hole 120 is installed in the opened inorganic injection hole 30, and the inorganic injection material 40 is forcedly pumped into the gap between the concrete structure and the rear structure through the injection hole 120. The inorganic injection material injected in this way is mostly filled between the concrete structure and the existing waterproof layer, or the ground.

상기 주입구(120)는 개공한 무기주입구멍에 길이 10∼1,000 정도의 팩커나 파이프 등과 같은 단관 주입구를 망치 등으로 타격하거나 조여서 설치한다. 상기와 같은 주입구의 설치는 공지의 기술이므로, 이에 대한 상세한 설명은 생략한다.
The injection hole 120 is installed by hitting or tightening a short pipe injection hole, such as a packer or a pipe, having a length of about 10 to 1,000, into a opened weapon injection hole with a hammer or the like. Since the installation of the inlet as described above is a known technique, a detailed description thereof will be omitted.

상기 무기주입재(40)는 물과 무기분체가 약 1 : 0.5∼1: 3.0 의 중량비율로 혼합된 것으로, 상기 무기분체는 수경성 미립시멘트를 주성분으로 하는 무기분체이다.The inorganic filler 40 is a mixture of water and inorganic powder in a weight ratio of about 1: 0.5 to 1: 3.0. The inorganic powder is an inorganic powder mainly composed of hydraulic particulates.

상기 무기분체는 일예로, 비표면적 4,000~10,000㎠/g 정도의 포틀랜드 등과 같은 수경성 미립 시멘트 60~85wt%, 비표면적 4,000~6,000㎠/g 정도의 실리카 흄 1~10wt%, 비표면적 3,000~4,000㎠/g 정도의 고로 슬래그 1~15wt%, 비표면적 5,000㎠/g 이상인 칼슘설포알루미네이트 이온 교환성 무기 결합 유도체(에트링가이트 생성제) 0.1~6wt% 및, 비표면적 10,000㎠/g 이상의 석회석 미분말 1~10wt% 을 포함한다. The inorganic powder is, for example, 60 to 85 wt% of hydraulic particulate cement such as Portland having a specific surface area of 4,000 to 10,000 cm2 / g, 1 to 10 wt% of silica fume having a specific surface area of 4,000 to 6000 cm2 / g, and a specific surface area of 3,000 to 4,000. Blast furnace slag of 1 cm2 / g, 1-15 wt%, calcium sulfoaluminate ion-exchangeable inorganic binding derivative (Ethringite generator) having a specific surface area of 5,000 cm2 / g or more, and limestone of 10,000 cm2 / g or more in specific surface area It contains 1 to 10 wt% of fine powder.

또한, 상기 무기주입재(40)는 균열을 통하여 유입 또는 유출되는 아스팔트 용해액 및 유지분이 많을 경우에는 혼합하는 물의 량을 늘여 구조체 콘크리트 표면으로부터 더 많이 해리될 수 있도록 하나, 물과 무기분체의 혼합을 중량비로 1:3.0을 초과하면 무기 경화체 피막이 얇아 내구성에 문제가 있을 수 있으며, 반면 중량비가 1:0.5 미만이 되면 콘크리트 구조체 표면에 부착하고 있는 아스팔트 용해액 및 유지분의 해리량이 작아져 주입효과가 떨어진다.
In addition, the inorganic injection material 40 is to increase the amount of water to mix when there is a lot of asphalt solution and oil inflow or outflow through the crack so as to be more dissociated from the concrete surface of the structure, the mixture of water and inorganic powder If the weight ratio exceeds 1: 3.0, the inorganic cured film may be thin and there may be a problem in durability.However, if the weight ratio is less than 1: 0.5, the dissociation amount of the asphalt dissolving liquid and fat adhering to the surface of the concrete structure becomes small and the injection effect is reduced. Falls.

상기 경화단계는 무기주입재(40)의 주입후, 24시간 이상 방치하여 양생시키는 단계로, 무기주입재(40)의 주입후 부터 무기 분체(콜로이드 분체)가 중합/고결되어 24시간 이상 경과후에는 수화반응이 진행하여 무기경화체로 이루어지는 무기질피막(50)이 형성되게 된다. 즉, 무기주입구멍(30)을 통해 배면 주입위치에 무기주입재(40)가 주입되면, 물보다 비중이 무거운 무기분체는 침강하여 축합되고, 수화반응하여 무기경화체가 형성되면서 아스팔트 용해액 등 유지분(46)을 고착시킨다. 반면 무기분체와 분리된 물은 상승하면서 소수 상호작용에 의해 아스팔트 용해액 등 유지분을 해리시키고, 또한, 물보다 비중이 가벼운 아스팔트 용해액 등 유지분은 물의 상부로 상승하여 콘크리트 구조체로부터 완전히 분리되어지고, 또한 하부에 견고한 무기경화체의 무기질피막(50)이 형성되므로, 다시 콘크리트 구조체 표면에 부착되지 않게 된다. 이때, 상기 무기분체와 혼합하는 물에 세제 등을 첨가하면 더욱 효과적인 유지분의 해리 및 분리를 이룰 수 있다.
The curing step is a step of curing by injecting the inorganic injection material 40, left for at least 24 hours, the inorganic powder (colloid powder) is polymerized / solidified after the injection of the inorganic injection material 40, the hydration after 24 hours or more The reaction proceeds to form an inorganic coating 50 made of an inorganic hardener. That is, when the inorganic injection material 40 is injected into the rear injection position through the inorganic injection hole 30, the inorganic powder having a specific gravity greater than water is sedimented and condensed, and the inorganic powder such as asphalt solution is formed by the hydration reaction to form an inorganic hardened body. Fix (46). On the other hand, the water separated from the inorganic powder rises and dissociates oils and fats such as asphalt solution by hydrophobic interaction, and the oils and fats such as asphalt solution, which is lighter than water, rises to the top of the water and is completely separated from the concrete structure. In addition, since the inorganic coating 50 of the rigid inorganic hardening body is formed at the bottom, it is not attached to the surface of the concrete structure again. In this case, when detergent or the like is added to water mixed with the inorganic powder, more effective dissociation and separation of fats and oils can be achieved.

를 더욱 구체적으로 설명하면,In more detail,

도 6 은 본 발명에 따른 무기주입재 및 유기주입재 주입과정을 보인 예시도를, 도 7 은 본 발명에 따른 무기질피막 및 유기질피막의 형성과정을 보인 예시도를 도시한 것이다. 이때, 도 7 의 (a)는 무기주입재의 주입에 따른 무기분체 침강상태를, (b)는 무기분체 축합수화반응 개시상태를, (c)는 무기경화제(무기질피막)형성 상태를, (d)는 유기주입재의 주입에 따른 반용해겔 상태를, (e)는 물흡수 포용 팽윤상태를 각각 도시한 것이다.
6 is an exemplary view showing a process of injecting an inorganic injection material and an organic injection material according to the present invention, Figure 7 shows an exemplary view showing a process of forming an inorganic film and an organic film according to the present invention. In this case, Figure 7 (a) is the inorganic powder settled state according to the injection of the inorganic filler, (b) is the inorganic powder condensation hydration reaction start state, (c) is the inorganic hardener (inorganic coating) forming state, (d ) Shows the anti-dissolving gel state according to the injection of the organic injection material, and (e) shows the swelling state for water absorption.

콘크리트 구조체 상부표면과 기존 방수층(시트 방수층) 하부 사이에 무기주입재가 주입되면, 비중이 약 2.5 이상으로 큰 무기주입재의 입자는 하부로 침강하고, 반면 일반적으로 비중이 물보다 가볍고, 소수성이 있는 용해 아스팔트 표면층의 Oil 과 유기용제 및 용해된 아스팔트 미립분 등의 부유물(45)은 물의 소수상호작용에 의해 분리(일부 용제는 분해됨)되어져 물의 표면으로 부유한다.When the inorganic filler is injected between the upper surface of the concrete structure and the bottom of the existing waterproofing layer (sheet waterproofing layer), particles of the inorganic filler having a specific gravity of about 2.5 or more settle down, while the specific gravity is generally lighter than water and hydrophobic The oil 45 of the asphalt surface layer, the suspended solids 45 such as the organic solvent and dissolved asphalt fine powder are separated by hydrophobic interaction of water (some solvents are decomposed) and floated to the surface of the water.

또한, 침강한 무기 주입재의 입자(특히 C3S, alite) 사이에는 이온 교환성 무기 결합 유도체에 의한 상호 인력(정전상호작용)이 작용하여, 표면가수분해(O2-→OH-, SiO4 4-→HnSiO4 (n-4), Ca2+→Ca2+ aq)된 다음, 겔(Gel)화 반응(2C3S+6H2O→C3S2H3+3Ca(OH)2)을 개시하고, 한편으로는 용해 아스팔트 표면층의 소수성 Oil 과 유기용제 및 용해된 아스팔트 미립분 등은 계속 분리되어, 친수성의 아스팔트 고형분체만 남게 된다.Further, by mutual attraction between particle sedimentation of the inorganic juipjae (especially C 3 S, alite) is ion-exchangeable inorganic binding derivative (electrostatic interaction) to the surface hydrolysis action (O 2- → OH -, SiO 4 4- → H n SiO 4 (n-4) , Ca 2+ → Ca 2+ aq ), and then gelation reaction (2C 3 S + 6H 2 O → C 3 S 2 H 3 + 3Ca (OH 2 ), and on the other hand, the hydrophobic oil, the organic solvent and the dissolved asphalt fine powder of the dissolved asphalt surface layer are continuously separated, leaving only the hydrophilic asphalt solid powder.

또한, 무기주입재(콜로이드)는 표면의 물과 belite의 수화반응(2C2S+4H2O→C3S2H3+Ca(OH)2), 실리케이트 이온 중합(SiO4 4-→Si2O7 6-→[(SiO3)n]2n-), 간극질 수화반응(C3A-H2O계, C3A-Ca(OH)2-H2O계, C3A-CaSO4-H2O계 및 C4AF계)과정을 거쳐 에트링가이트(3CaOAl2O33CaSO432H2O), 모노설페이트 수화물(3CaOAl2O3CaSO412H2O), 알루민산칼슘 수화물(3CaOAl2O36H2O)등을 만들어 용해 아스팔트 고형분체 표면과 결합된 견고하고 수밀한 무기경화체가 형성되며, 이러한 무기경화체가 무기질피막(50)에 해당된다.
In addition, the inorganic injection material (colloid) is a hydration reaction of water and belite (2C 2 S + 4H 2 O → C 3 S 2 H 3 + Ca (OH) 2 ), silicate ion polymerization (SiO 4 4- → Si 2) O 7 6- → [(SiO 3 ) n ] 2n- ), interstitial hydration (C 3 AH 2 O system, C 3 A-Ca (OH) 2 -H 2 O system, C 3 A-CaSO 4- after the H 2 O-based and C 4 AF system) to process ettringite (3CaOAl 2 O 3 3CaSO 4 32H 2 O), mono-sulfate hydrate (3CaOAl 2 O 3 CaSO 4 12H 2 O), calcium aluminate hydrates (3CaOAl 2 O 3 6H 2 O) and the like to form a solid and dense inorganic hardened body combined with the surface of the dissolved asphalt solid powder, this inorganic hardened body corresponds to the inorganic coating (50).

상기 2차개공단계는 유기주입재(70)의 주입을 위해 유기주입구멍(60)을 형성하는 단계로, 상기 무기주입구멍(30)과 인접하는 또다른 무기주입구멍(30)과의 가운데를 콘크리트 구조체(10)와 무기질피막(50)을 관통하도록 개공하여 유기주입구멍(60)을 형성한다.
The secondary opening step is to form an organic injection hole 60 for the injection of the organic injection material 70, the concrete in the center of another inorganic injection hole 30 adjacent to the inorganic injection hole 30 The organic injection hole 60 is formed by opening through the structure 10 and the inorganic coating 50.

상기 유기주입재 주입단계는 상기 개공된 유기주입구멍(60)에 주입구를 설치하고, 주입구를 통하여 펌프에 의해 유기주입재(70)를 콘크리트 구조체(10)와 무기경화체로 이루어진 무기질피막(50) 외부측으로 강제 주입한다.
The organic injection material injection step is to install the injection hole in the opening of the organic injection hole 60, the organic injection material 70 by the pump through the injection hole to the outside of the inorganic coating 50 made of the concrete structure 10 and the inorganic hardening body Force injection

상기 유기주입재(70)는 물흡수성 유기 폴리머(super absorbent polymer) 수용액을 사용한다. 상기 물흡수성 유기 폴리머(super absorbent polymer) 수용액은 일예로,The organic injection material 70 uses a water absorbing organic polymer (super absorbent polymer) aqueous solution. The water absorbing organic polymer (super absorbent polymer) aqueous solution is an example,

a. 수산기(-OH) 약 80~100% 와 아미노기(-NH2)약 0~20% 정도의 반응성 측쇄를 가질 수 있도록 조정한, 폴리아크릴산 또는, 폴리아크릴산과 폴리비닐 알콜 모노머의 혼합액과;a. Polyacrylic acid or a mixture of polyacrylic acid and polyvinyl alcohol monomer, adjusted to have a reactive side chain of about 80 to 100% of hydroxyl group (-OH) and about 0 to 20% of amino group (-NH 2 );

b. 가교제로 상기 폴리아크릴산과 폴리비닐 알콜 모노머와의 비에 따라 조정된 N, N'-메틸렌비스아크릴아마이드 또는 에틸렌글리콜디메타크릴레이트와;b. N, N'-methylenebisacrylamide or ethylene glycol dimethacrylate adjusted according to the ratio of the said polyacrylic acid and a polyvinyl alcohol monomer as a crosslinking agent;

c. 라디칼 개시제로 R'-SO4등과 같은 과황산염화물;을 혼합하여 조성한 용액(A);c. A solution (A) formed by mixing a persulfate such as R'-SO 4 as a radical initiator;

과황산 암모니움(APS)과 테트라메틸에틸렌디아민(TEMED)을 혼합하여 조성한 중합용액(B); A polymerization solution (B) formed by mixing ammonium persulfate (APS) and tetramethylethylenediamine (TEMED);

상기 두 용액(A+B)를 혼합하여 형성한다.
The two solutions (A + B) are formed by mixing.

이와 같은 유기주입재(70)는 라디칼 부가중합반응에 의해, 약 10분 이내에 중합반응을 개시하여 수소결합과 소량의 전리기(-COO-)를 가진 이온결합에 의한 3차원 망상구조의 물 흡수성 탄성 겔(MAPTAC, 아크릴산과 메타크릴아미드프로필트리메틸암모니움클로라이드 공중합체)이 형성된다.
The organic injector 70 starts a polymerization reaction within about 10 minutes by a radical addition polymerization reaction, and has a water absorption elasticity of a three-dimensional network structure by a hydrogen bond and an ionic bond having a small amount of ionizer (-COO-). A gel (MAPTAC, acrylic acid and methacrylamidepropyltrimethylammonium chloride copolymer) is formed.

상기 물흡수성 유기 폴리머(super absorbent polymer) 수용액을 콘크리트 구조체(10) 하부에서 주입하면, 대부분 기존 방수층(20) 하부와 콘크리트 구조체 상부의 무기질피막(50)의 표면 사이에 충전된다. When the water-absorbing organic polymer (super absorbent polymer) aqueous solution is injected from the lower portion of the concrete structure 10, most of the water is filled between the existing waterproof layer 20 and the surface of the inorganic coating 50 of the upper portion of the concrete structure.

상기와 같이 주입되는 유기주입재(70)는 무기질피막(50)을 이루는 무기경화체의 형성에 따른 잉여수를 흡수하여 탄성 겔을 형성하게 된다.The organic injection material 70 injected as described above forms an elastic gel by absorbing excess water due to the formation of the inorganic hardener forming the inorganic coating 50.

즉, 콘크리트 구조체의 배면에 주입된 무기주입재가 견고한 무기경화체를 만드는 동안, 일부 물은 수화반응에 사용되지만 나머지 물은 잉여수로 남게 되어 누수의 원인이 되기도 하고, 또한 해리시킨 아스팔트 용해액 등 유지분 등을 포함하고 있으므로 나중에 다시 문제를 야기시킬 우려가 있다.  That is, while the inorganic injection material injected into the back of the concrete structure makes a strong inorganic hardening body, some water is used for the hydration reaction, but the remaining water remains as surplus water, causing leakage, and also maintaining the dissolved asphalt solution. It contains minutes, etc., and may cause problems later.

본 발명의 유기주입재(70)는 상기와 같은 문제점을 해소하기 위한 것으로, 폴리아크릴산과 폴리비닐 알콜 모노머의 수산기(-OH)나 아미노기(-NH2) 등 2관능기의 라디칼 부가중합가교에 의해 3차원 망상구조의 탄성 겔을 형성한 다음, 수소결합과 소량의 전리기(-COO-)에 의한 이온결합력에 의해 최초 탄성 겔 체적의 약 3배까지 물을 흡수할 수 있는 특성을 활용하여 잉여수를 흡수하여 누수결함을 방지하도록 되어 있다. The organic injection material 70 of the present invention is intended to solve the above problems, by radical addition polymerization of bifunctional groups such as hydroxyl groups (-OH) and amino groups (-NH 2 ) of polyacrylic acid and polyvinyl alcohol monomers. D form an elastic gel of the network structure, and then, combined with a small amount of hydrogen Rigi (-COO -) for the water to about three times the initial volume of the elastic gel by an ion bond can surplus utilizing the properties that can be absorbed by It is absorbed to prevent leakage defects.

이를 더욱 구체적으로 설명하면,In more detail,

도 6 은 본 발명에 따른 무기주입재 및 유기주입재 주입과정을 보인 예시도를 도 7 은 본 발명에 따른 무기질피막 및 유기질피막의 형성과정을 보인 예시도를 도시한 것으로, 6 is an exemplary view showing a process of injecting an inorganic injection material and an organic injection material according to the present invention, Figure 7 is an exemplary view showing a process of forming an inorganic film and an organic film according to the present invention,

콘크리트 슬래브 상부(무기경화체-무기피막)표면과 기존 방수층의 시트하부 사이에 유기주입재가 주입되면, 약 10분 이내에 라디칼 반응하여 도 4 에 도시된 바와 같이, 소량의 전리기(-COO-)를 가진 3차원 망상구조의 이온교환성 수지(MAPTAC, 아크릴산과 메타크릴아미드프로필트리메틸암모니움클로라이드 공중합체)를 만들어 물과, 물속에 부유하고 있는 용해 아스팔트 표면층의 Oil과 유기 용제 및 용해된 아스팔트 미립분 등을 고정시킨다. 도 4 의 (a)는 수용성 고분자 상태를, (b)는 반 용해 겔상태를, (c)는 팽윤 겔 상태를, (d)는 이온교환성수지 상태를 각각 도시한 것이다. An upper concrete slab (cured inorganic-inorganic film) surface and when the organic juipjae is injected between the bottom sheet of the existing waterproof layer, as described in about 10 minutes shown in Figure 4 by the radical reaction, small amount of Rigi (-COO) 3D networked ion exchange resin (MAPTAC, acrylic acid and methacrylamide propyltrimethylammonium chloride copolymer) was prepared to make water, oil of surface layer of dissolved asphalt suspended in water, organic solvent and dissolved asphalt fine powder Secure your back. 4 (a) shows a water-soluble polymer state, (b) shows a semi-dissolved gel state, (c) shows a swelling gel state, and (d) shows an ion exchangeable resin state, respectively.

또한, 생성된 이온교환성 수지의 가교력에 의해 유기주입재는 주변의 물을 최초 겔 체적의 약 3배까지 흡수하여 체적을 늘여, 기존 방수층(시트 방수층) 하부 사이를 충전시켜 누수결함을 방지하고 빗물의 침투를 막아주게 된다.
In addition, due to the crosslinking force of the produced ion-exchangeable resin, the organic filler absorbs the surrounding water up to about three times the volume of the original gel and increases the volume, filling the lower portion of the existing waterproof layer (sheet waterproof layer) to prevent leakage defects. It prevents the ingress of rainwater.

도 7 의 (a)는 무기주입재의 주입에 따른 무기분체 침강 및 유지분 부유상태를, (b)는 무기분체 축합수화반응 개시상태 및 유지분 부유상태(1시간경과후)를, (c)는 무기경화제(무기질피막)형성 상태(약5시간경과후)를, (d)는 유기주입재의 주입에 따른 반용해겔 상태를, (e)는 물흡수 포용 팽윤상태를 각각 도시한 것이다.
Figure 7 (a) is the inorganic powder sedimentation and fat floating state according to the injection of the inorganic filler, (b) is the inorganic powder condensation hydration reaction start state and fat suspension state (after 1 hour elapsed), (c) Is an inorganic hardening agent (inorganic coating) formation state (after about 5 hours), (d) is an anti-dissolving gel state according to the injection of the organic filler, (e) is a water absorption inclusion swelling state, respectively.

상기 본 발명에 따른 유기주입재(70)와 무기주입재(40)는 1㎩∼100㎫의 압력으로 각각의 펌프(도시없음)에 의해 압송하여 유기주입구멍(60) 및 무기주입구멍(30)에 설치된 주입구를 통해 각각 주입된다.
The organic injection material 70 and the inorganic injection material 40 according to the present invention are pumped by the respective pumps (not shown) at a pressure of 1 kPa to 100 MPa to the organic injection holes 60 and the inorganic injection holes 30. Each is injected through the installed inlet.

상기 봉합단계는 유기주입재(70)의 주입을 위한 주입구를 제거하고 아스팔트 용해액 등 유지분 유입, 또는 유출결함이 발생된 균열부위(11)를 아스팔트 용해액 등 유지분과 반응하지 않는 급결성 약액을 혼입한 무기시멘트 모르타르 또는 수성 실란트(90)로 균열을 봉합하여 콘크리트 구조체 균열 내부에 잔존하는 아스팔트 용해액 등 유지분이 유출되지 않도록 보수한다.
The sealing step is to remove the inlet for the injection of the organic injection material 70 and the fastening chemical liquid that does not react with the oil and the like, such as asphalt dissolving liquid cracks (11) in which oil inflow, such as asphalt solution, or outflow defects are generated The cracks are sealed with the mixed inorganic cement mortar or the aqueous sealant 90 to repair the oil and fat such as asphalt solution remaining inside the cracks of the concrete structure.

상기 수성실란트는 일반적인 유기화합물로 조성되어 유기용제와 반응하여 용해되는 실란트, 예를 들어 에폭시계열, 우레탄 계열의 실란트와는 달리 공기중의 산소와 반응하여 피막을 만드는 특징을 가지고 있으므로, 콘크리트 구조체 균열 내부에 잔존하는 아스팔트 용해액 등 유지분에 함유되어 있는 유기용제와 반응하지 않는다. 또한, 균열 봉합 후 도장 등과 같은 마감작업도 용이하다.
Since the aqueous sealant is formed of a general organic compound and reacts with an organic solvent to dissolve, for example, an epoxy-based or urethane-based sealant, the aqueous sealant has a characteristic of forming a film by reacting with oxygen in the air. It does not react with organic solvents contained in fats and oils such as asphalt solution remaining inside. In addition, it is easy to finish the finishing work such as painting after crack closure.

즉, 유기주입재의 주입이 끝난 다음, 균열틈새에 잔여하고 있는 유기용제를 함유하고 있는 아스팔트 용해(누유)물의 낙하방지를 위해, 유기용제에 잘 용해되지 않는 수성의 아크릴계 실링재를 사용하여, 균열표면을 마감처리한다.That is, after the injection of the organic filler, the surface of the crack is made of an aqueous acrylic sealing material that is insoluble in the organic solvent to prevent the fall of the asphalt melt (leak) containing the organic solvent remaining in the crack gap. Finish the process.

또한, 육안으로 확인이 불가능한, 또는 현재까지 누유되고 있지 않은 미세 균열내부에 충진되어 있는 기존 아스팔트 용해(누유)물은 구조체 거동에 따라 향후 누유될 가능성이 있으며, 이러한 경우에도 유기용제에 잘 용해되지 않는 수성의 아크릴계 실링재를 사용하여 균열표면을 마감처리한다.
In addition, existing asphalt melts (leakage) that are not visible to the naked eye or filled in the microcracks that have not been leaked up to now may leak in the future depending on the structure behavior. The surface of the crack is finished using an aqueous acrylic sealing material.

또한, 본 발명은 무기주입재 주입단계 이전에 아스팔트 용해액 등 유지분 유입, 또는 유출결함이 발생된 균열부위를 밀폐시키는 균열부위 밀폐단계를 더 포함한다.
In addition, the present invention further includes a crack site sealing step of closing a crack site in which an oil inflow or an outflow defect, such as an asphalt solution, or an outflow defect occurs, before the inorganic injection material injection step.

상기와 같이 이루어지는 본 발명은 콘크리트 구조체의 배면에 위치하는 배면 방수층이 무기경화체로 이루어진 무기질피막(50)과, 3차원 망상구조의 이온교환성 수지의 탄성 겔로 이루어진 유기질피막(80)의 이중구조를 구비하여, 아스팔트 용해액 등 유지분의 콘크리트 구조체 내부 유입 및 외부 유출을 근원적, 내구적으로 보수하도록 되어 있다.
The present invention made as described above has a dual structure of an organic coating (80) made of an inorganic coating (50) made of an inorganic hardening body and an inorganic coating (50) made of an inorganic hardening body on the rear surface of the concrete structure. In addition, the inflow and outflow of the concrete structure of the oil and fat such as asphalt dissolving liquid is to be repaired fundamentally and durable.

본 발명은 상술한 특정의 바람직한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위내에 있게 된다.
The present invention is not limited to the above-described specific preferred embodiments, and various modifications can be made by any person having ordinary skill in the art without departing from the gist of the present invention claimed in the claims. Of course, such changes will fall within the scope of the claims.

(10) : 콘크리트 구조체 (11) : 균열부위
(20) : 방수층 (30) : 무기주입구멍
(40) : 무기주입재 (50) : 무기질피막
(60) : 유기주입구멍 (70) : 유기주입재
(80) : 유기질피
(90) : 무기시멘트 모르타르 또는 수성 실란트
(100) : 지반층 (110) : 보호누름층(10): concrete structure (11): cracked portion
(20): waterproof layer (30): weapon injection hole
(40): inorganic injection material (50): inorganic coating
60: organic injection hole 70: organic injection material
(80): Organic Skin
(90): inorganic cement mortar or aqueous sealant
(100): ground layer (110): protective pressing layer

Claims (6)

아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법에 있어서;
콘크리트 구조체 또는 방수층을 관통하도록 균열부위 양측을 따라 무기주입구멍을 개공하는 1차개공단계;
상기 무기주입구멍을 통해 콘크리트 구조체의 배면틈새에 무기 주입재를 강제주입하여 충전시키는 무기 주입재 주입단계;
상기 무기주입재 주입단계 후 24시간 이상 방치하여 무기주입재에 의해 무기경화체로 이루어진 무기질피막을 형성시키는 경화단계;
상기 경화단계 후, 콘크리트 구조체와 무기질피막 또는 콘크리트 구조체와 무기질피막 및 방수층을 관통하도록 무기주입구멍과 이에 인접하는 또다른 무기주입구멍의 중간 위치에 유기주입구멍을 개공하는 2차개공단계;
상기 유기주입구멍을 통해 유기주입재를 무기질피막 외부 측으로 강제 주입시켜 유기질 탄성 겔로 이루어진 유기질피막을 형성하는 유기주입재 주입단계;
상기 유기주입구멍, 무기주입구멍 및 균열부위를 무기시멘트 모르타르 또는 수성 실란트로 봉합시키는 봉합단계;를 통해 콘크리트 구조체 배면틈새에 무기질피막과, 유기질피막의 분리된 이중구조의 피막층이 형성되되,
상기 무기주입재는 물과 무기분체가 1 : 0.5∼3.0의 중량비율로 혼합된 콜로이드 수용액이고, 상기 유기주입재는 물흡수성 유기 폴리머(super absorbent polymer) 수용액인 것을 특징으로 하는 아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법.
Claims [1] A method for injecting and repairing a concrete structure back surface to prevent oil inflow and outflow of asphalt solution;
A first opening step of opening the inorganic injection hole along both sides of the crack to penetrate the concrete structure or the waterproof layer;
An inorganic injection material injection step of forcibly filling and filling an inorganic injection material into the rear gap of the concrete structure through the inorganic injection hole;
A curing step of leaving the inorganic injection material in an ingot for 24 hours or more to form an inorganic film made of an inorganic hardener by the inorganic injection material;
A secondary opening step of opening the organic injection hole at an intermediate position between the inorganic injection hole and another inorganic injection hole adjacent thereto so as to pass through the concrete structure and the inorganic coating or the concrete structure and the inorganic coating and the waterproofing layer after the curing step;
An organic injection material injection step of forcibly injecting an organic injection material into the outer side of the inorganic coating through the organic injection hole to form an organic film made of an organic elastic gel;
Sealing step of sealing the organic injection hole, inorganic injection hole and cracks with an inorganic cement mortar or an aqueous sealant; through the gap between the back of the concrete structure, an inorganic coating layer and an organic coating of the separated double structure of the organic film is formed,
The inorganic injection material is a colloidal aqueous solution in which water and inorganic powder are mixed in a weight ratio of 1: 0.5 to 3.0, and the organic injection material is an oil-in-water inflow of the asphalt solution, characterized in that the water-absorbing organic polymer (super absorbent polymer) aqueous solution. And a method for injecting and repairing the back of the concrete structure to prevent leakage.
청구항 1 에 있어서;
무기주입재 주입단계 이전에 콘크리트 균열부위를 무기시멘트 모르타르 또는 수성의 실란트로 밀폐시키는 균열부위 밀폐단계를 더 포함하는 것을 특징으로 하는 아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법.
The method of claim 1,
Before the inorganic injection material injection step, the concrete structure back injection repair method for preventing the inflow and outflow of the oil and fat of the asphalt solution characterized in that it further comprises a crack site sealing step of sealing the concrete crack site with the inorganic cement mortar or aqueous sealant. .
삭제delete 청구항 1 에 있어서;
상기 무기분체는 비표면적 4,000~10,000㎠/g 수경성 미립 시멘트 60~85wt%, 비표면적 4,000~6,000㎠/g 실리카 흄 1~10wt%, 비표면적 3,000~4,000㎠/g 고로 슬래그 1~15wt%, 비표면적 5,000㎠/g 이상인 칼슘설포알루미네이트 0.1~6wt% 및, 비표면적 10,000㎠/g 이상의 석회석 미분말 1~10wt% 을 포함하는 것을 특징으로 하는 아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법.
The method of claim 1,
The inorganic powder has a specific surface area of 4,000 to 10,000 cm 2 / g hydraulic particulate cement 60 to 85 wt%, specific surface area of 4,000 to 6,000 cm 2 / g silica fume 1 to 10 wt%, specific surface area of 3,000 to 4,000 cm 2 / g blast furnace slag 1 to 15 wt%, 0.1 to 6 wt% of calcium sulfoaluminate having a specific surface area of 5,000 cm 2 / g or more, and 1 to 10 wt% of limestone fine powder of 10,000 cm 2 / g or more of specific surface area for preventing the inflow and outflow of fats and oils of the asphalt solution. Injection repair method for the back of concrete structure.
삭제delete 청구항 1 에 있어서;
상기 유기주입재는 용액(A)와 중합용액(B)를 혼합하여 형성하되,
상기 용액(A)는
a. 수산기(-OH) 약 80~100% 와 아미노기(-NH2)약 0~20% 정도의 반응성 측쇄를 가질 수 있도록 조정한, 폴리아크릴산 또는, 폴리아크릴산과 폴리비닐 알콜 모노머의 혼합액과;
b. 가교제로 상기 폴리아크릴산과 폴리비닐 알콜 모노머와의 비에 따라 조정된 N, N'-메틸렌비스아크릴아마이드 또는 에틸렌글리콜디메타크릴레이트와;
c. 라디칼 개시제로 R'-SO4등과 같은 과황산염화물;을 혼합하여 조성하고,
상기 중합용액(B)는 과황산 암모니움(APS)과 테트라메틸에틸렌디아민(TEMED)을 혼합하여 조성하는 것을 특징으로 하는 아스팔트 용해액의 유지분 유입 및 유출을 방지하기 위한 콘크리트 구조체 배면 주입보수방법.The method of claim 1,
The organic filler is formed by mixing the solution (A) and the polymerization solution (B),
The solution (A) is
a. Polyacrylic acid or a mixture of polyacrylic acid and polyvinyl alcohol monomer, adjusted to have a reactive side chain of about 80 to 100% of hydroxyl group (-OH) and about 0 to 20% of amino group (-NH 2 );
b. N, N'-methylenebisacrylamide or ethylene glycol dimethacrylate adjusted according to the ratio of the said polyacrylic acid and a polyvinyl alcohol monomer as a crosslinking agent;
c. A persulfate, such as R'-SO 4 , as a radical initiator;
The polymerization solution (B) is a concrete structure back injection repair method for preventing the inflow and outflow of the oil solution of the asphalt solution, characterized in that the composition is mixed by mixing ammonium persulfate (APS) and tetramethylethylenediamine (TEMED) .
KR1020100030198A 2010-04-02 2010-04-02 Outside of concrete construction injection repair method for leaks of oils such as asphalt solution and others KR100998727B1 (en)