KR100982330B1 - A composition for forming a electron emitter of flat panel display and an electron emitter prepared therefrom - Google Patents
A composition for forming a electron emitter of flat panel display and an electron emitter prepared therefrom Download PDFInfo
- Publication number
- KR100982330B1 KR100982330B1 KR1020030086090A KR20030086090A KR100982330B1 KR 100982330 B1 KR100982330 B1 KR 100982330B1 KR 1020030086090 A KR1020030086090 A KR 1020030086090A KR 20030086090 A KR20030086090 A KR 20030086090A KR 100982330 B1 KR100982330 B1 KR 100982330B1
- Authority
- KR
- South Korea
- Prior art keywords
- electron emission
- composition
- emission source
- reducing agent
- carbon
- Prior art date
Abstract
본 발명은 평판 표시소자의 전자 방출원 형성용 조성물 및 이로부터 제조되는 전자 방출원에 관한 것으로서, 보다 상세하게는 카본계 물질, 환원제 물질, 글래스 프릿, 바인더, 및 용매를 포함하는 전자 방출원 형성용 조성물과 이로부터 제조되는 전자 방출원 및 상기 전자 방출원을 포함하는 평판 표시 소자에 관한 것이다.The present invention relates to a composition for forming an electron emission source of a flat panel display device and an electron emission source prepared therefrom, and more particularly, to an electron emission source including a carbon-based material, a reducing agent material, a glass frit, a binder, and a solvent. The present invention relates to a composition for use, an electron emission source produced therefrom, and a flat panel display device including the electron emission source.
본 발명의 평판 표시소자의 전자 방출원은 전자 방출 효율을 증가시키기 위하여, 카본계 물질을 포함하며, 이와 함께 환원제 물질을 포함하여 전자 방출원의 소성시에 발생할 수 있는 카본계 물질의 산화를 방지함으로써, 전자 방출 효율이 극대화 되는 장점이 있다.The electron emission source of the flat panel display device of the present invention includes a carbon-based material in order to increase the electron emission efficiency, and together with the reducing agent material, prevents oxidation of the carbon-based material that may occur during firing of the electron emission source. By doing so, there is an advantage that the electron emission efficiency is maximized.
전계 방출 소자, 전자 방출원, 카본계 물질, 환원제 물질Field emitters, electron emitters, carbon materials, reducing agents
Description
도 1은 환원제 물질을 포함하지 않는 전자 방출원 형성용 조성물을 이용하여 형성된 전자 방출원의 단면을 모식적으로 나타낸 단면도이다.1 is a cross-sectional view schematically showing a cross section of an electron emission source formed using the composition for forming an electron emission source containing no reducing agent material.
도 2는 환원제 물질을 포함하는 전자 방출원 형성용 조성물을 이용하여 형성된 전자 방출원의 단면을 모식적으로 나타낸 단면도이다.2 is a cross-sectional view schematically showing a cross section of an electron emission source formed using the composition for forming an electron emission source containing a reducing agent material.
도 3은 실시예 1 및 비교예 1에 따라 제조된 전자 방출원의 전자 방출 특성을 보인 도면이다.3 is a view showing electron emission characteristics of the electron emission source prepared according to Example 1 and Comparative Example 1.
[산업상 이용분야][Industrial use]
본 발명은 평판 표시소자의 전자 방출원 형성용 조성물 및 그로부터 제조되는 전자 방출원에 관한 것으로서, 더욱 상세하게는 카본계 물질과 함께 환원제 물질을 포함하여 전자 방출원의 소성시에 발생할 수 있는 카본계 물질의 산화를 방지함으로써, 전자 방출 효율을 높일 수 있는 전자 방출원 형성용 조성물 및 그로부터 제조되는 전자 방출원에 관한 것이다.The present invention relates to a composition for forming an electron emission source of a flat panel display device and an electron emission source manufactured therefrom. More particularly, the present invention relates to a carbon-based material which may occur upon firing of an electron emission source including a reducing agent material together with a carbon-based material. The present invention relates to a composition for forming an electron emission source capable of increasing the electron emission efficiency by preventing oxidation of a substance, and an electron emission source produced therefrom.
[종래 기술][Prior art]
평면 표시 소자 중, 초기에 제안된 전계 방출 표시 소자(FED: Field Emission Display)는 전자 방출원으로서 몰리브덴이나 실리콘 등의 물질을 적층시켜 선단을 뾰족하게 구성한 스핀트(spindt) 타입을 사용하였으나, 상기 스핀트 타입의 전자 방출원은 초미세 구조로서 제조 방법이 복잡하고, 고정밀도의 제조 기술이 요구되어 전계 방출 표시 소자를 대면적화하여 제작하는 데 한계가 있다.Among the flat panel display devices, a field emission display (FED) proposed earlier uses a spindt type in which a tip is formed by stacking molybdenum or silicon as an electron emission source. The spin type electron emission source has an ultra-fine structure, a complicated manufacturing method, and a high precision manufacturing technique is required. Therefore, there are limitations in manufacturing a large-area field emission display device.
따라서, 최근에는 낮은 일함수(work function)를 갖는 탄소계 물질을 전자 방출원으로 적용하는 연구가 활발하게 진행되고 있으며, 상기 탄소계 물질 가운데 특히 높은 종횡비를 갖는 카본 나노 튜브(CNT: Carbon Nano Tube)는 끝단의 곡률 반경이 100 Å정도로 극히 미세하여 1 내지 3 V/㎛의 외부 전압에 의해서도 전자 방출을 원활하게 일으켜 이상적인 전자 방출원으로 기대되고 있다.Therefore, recently, studies are being actively conducted to apply a carbon-based material having a low work function as an electron emission source, and carbon nanotubes having a particularly high aspect ratio among the carbon-based materials (CNT: Carbon Nano Tube) ), The radius of curvature of the tip is extremely fine, such as 100 kPa, and is expected to be an ideal electron emission source by smoothly generating electrons even by an external voltage of 1 to 3 V / µm.
일반적으로 상기 카본 나노 튜브와 같은 카본계 물질은 용매 및 바인더 수지 등과 함께 페이스트 형태로 구비되어, 기판 사이에 스크린 인쇄된 후 열처리 과정을 거쳐 전자 방출원으로 형성된다. 이러한 카본 나노 튜브는 낮은 일함수 특성에 의해 저전압 구동이 가능하고, 제조가 용이하여 대면적 디스플레이 구현에 보다 유리한 장점을 갖는다.In general, a carbon-based material such as the carbon nanotubes is provided in the form of a paste together with a solvent, a binder resin, and the like, and is screen-printed between the substrates and then heat-treated to form an electron emission source. The carbon nanotubes can be driven at low voltage due to their low work function, and are easy to manufacture, which is more advantageous for large area display.
스크린 인쇄 방법에 의해 카본계 물질을 전자 방출원으로 형성되면, 카본계 물질이 페이스트의 고형분과 섞여 상기 고형분 내부에 불규칙적으로 분포하게 되므로, 대부분의 카본 나노 튜브는 그 끝단이 고형분 내부에 묻히게 된다. When the carbon-based material is formed as an electron emission source by the screen printing method, since the carbon-based material is mixed with the solid content of the paste and irregularly distributed in the solid content, most carbon nanotubes have their ends embedded in the solid content.
따라서, 지금까지 평판 표시소자의 전자 방출원에 대한 연구는 주로 상기 카본 나노 튜브의 끝단을 밖으로 노출시키는 방법에 대하여 진행되어 왔다.(일본 특허 공개 제2000-223004호, 일본 특허 공개 제2000-36243호) Thus, studies on the electron emission source of the flat panel display device have been mainly conducted on the method of exposing the ends of the carbon nanotubes to the outside. (Japanese Patent Laid-Open No. 2000-223004, Japanese Patent Laid-Open No. 2000-36243 number)
일반적으로 카본계 물질은 열처리(소성) 과정에서 공기 중에 존재하는 산소와 반응하여 CO2의 형태로 산화되기 쉽기 때문에, 상기 열처리 과정은 반드시 비산화 분위기에서 진행된다. 그러나, 이러한 경우라도, 일부 잔존하는 산소가스에 의해서 카본계 물질의 산화반응이 일어날 수 있고, 이러한 경우 전자 방출 효율이 떨어진다는 문제점이 있다.In general, the carbon-based material is easily oxidized in the form of CO 2 by reacting with the oxygen present in the air during the heat treatment (firing) process, the heat treatment process necessarily proceeds in a non-oxidizing atmosphere. However, even in this case, some residual oxygen gas may cause oxidation reaction of the carbon-based material, and in this case, there is a problem that the electron emission efficiency is lowered.
본 발명은 상술한 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 카본계 물질의 산화반응을 방지하여 전자 방출 효율이 우수한 평판 표시소자의 전자 방출원 형성용 조성물을 제공하는 것이다.SUMMARY OF THE INVENTION The present invention has been made to solve the above problems, and an object of the present invention is to provide a composition for forming an electron emission source of a flat panel display device having excellent electron emission efficiency by preventing oxidation reaction of a carbon-based material.
본 발명의 또 다른 목적은 상기 전자 방출원 형성용 조성물로부터 제조되는 전자 방출원을 제공하는 것이다.Still another object of the present invention is to provide an electron emission source prepared from the composition for forming an electron emission source.
본 발명의 또 다른 목적은 상기 전자 방출원을 포함하는 평판 표시 소자를 제공하는 것이다. Still another object of the present invention is to provide a flat panel display device including the electron emission source.
상기 목적을 달성하기 위하여, 본 발명은 카본계 물질, 환원제 물질, 글래스 프릿, 바인더, 및 용매를 포함하는 전자 방출원 형성용 조성물을 제공한다. In order to achieve the above object, the present invention provides a composition for forming an electron emission source comprising a carbon-based material, a reducing agent material, a glass frit, a binder, and a solvent.
본 발명은 또한, 상기 전자 방출원 형성용 조성물을 인쇄, 코팅하여 형성된 전자 방출원 및 이를 포함하는 평판 표시소자를 제공한다.The present invention also provides an electron emission source formed by printing and coating the composition for forming an electron emission source and a flat panel display device including the same.
이하, 본 발명을 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 전자 방출원 형성용 조성물은 카본계 물질, 환원제 물질, 글래스 프릿, 바인더, 및 용매를 포함한다. The composition for forming an electron emission source of the present invention includes a carbonaceous material, a reducing agent material, a glass frit, a binder, and a solvent.
상기 카본계 물질로는 종래에 평판 표시소자의 전자 방출원으로 사용되고 있는 카본계 물질이면 어느 것이든 사용될 수 있으며, 바람직한 예로는 카본 나노튜브, 그라파이트, 다이아몬드 다이아몬드상 카본(DLC:diamond like carbon), 플러렌 등이 있다.As the carbon-based material, any carbon-based material that is conventionally used as an electron emission source of a flat panel display device may be used. Examples of the carbon-based material include carbon nanotubes, graphite, diamond like carbon (DLC), Fullerene and the like.
본 발명의 전자 방출원 형성용 조성물은 상기 카본계 물질보다 쉽게 산화되는 환원제 물질을 포함하여, 비산화 분위기 하에서도 잔존할 수 있는 산소가스의 싱커(sinker)로 작용한다. The composition for forming an electron emission source of the present invention includes a reducing agent material that is more easily oxidized than the carbonaceous material, and functions as a sinker of oxygen gas that may remain even in a non-oxidizing atmosphere.
상기 환원제 물질의 예로는 산소 결핍구조를 가지는 비화학양론적 금속 산화물이 있으며, 바람직하게는 니켈, 몰리브덴, 구리, 텅스텐, 알루미늄, 티타늄, 바나듐, 크롬, 철, 코발트, 아연, 지르코늄, 니오븀, 루데늄, 팔라튬, 은, 카드뮴, 인디움, 주석, 하프늄, 탄탈늄, 오스뮴, 팔라티늄, 금, 안티몬, 이리듐, 실리콘, 베릴륨 등의 금속을 포함하는, 산소 결핍구조를 가지는 비화학양론적 금속 산화물이 있고, 더 바람직하게는 ZnO1-x(0 < x < 1), SnO2-x(0 < x < 2) 등과 같은 금속 산화물이 있고, 가장 바람직하게는 ZnO1-x(0 < x < 0.5), SnO2-x(0 < x < 1) 금속 산화 물이 있다. 상기 금속 산화물은 각각 단독으로 사용될 수 있으며, 둘 이상을 혼합하여 사용할 수도 있다. Examples of the reducing agent material are non-stoichiometric metal oxides having an oxygen deficient structure, preferably nickel, molybdenum, copper, tungsten, aluminum, titanium, vanadium, chromium, iron, cobalt, zinc, zirconium, niobium, ru Non-stoichiometric metals with oxygen deficient structures, including metals such as denium, palladium, silver, cadmium, indium, tin, hafnium, tantalum, osmium, palladium, gold, antimony, iridium, silicon, beryllium Oxides, more preferably metal oxides such as ZnO 1-x (0 <x <1), SnO 2-x (0 <x <2), etc., most preferably ZnO 1-x (0 <x <0.5), SnO 2-x (0 <x <1) metal oxides. The metal oxides may be used alone, or two or more may be used in combination.
또한, 상기 환원제 물질의 또 다른 예로는 H2S, SnCl2 등과 같이 전자친화력이 낮은 원소를 함유하는 물질이 있으며, 이들을 각각 단독으로 사용하거나, 혼합하여 사용할 수 있다.In addition, another example of the reducing agent material is a material containing an element having a low electron affinity such as H 2 S, SnCl 2 and the like, each of these may be used alone, or may be used in combination.
상기 환원제 물질의 크기는 1 nm 내지 50 ㎛인 것을 사용할 수 있고, 1 nm 내지 10 ㎛인 것이 바람직하며, 1 nm 내지 1 ㎛인 것이 더 바람직하다. 환원제 물질의 크기가 50 ㎛를 초과하는 경우에는 패터닝이 어렵게 되고, 1 nm 미만의 금속산화물은 현실적으로 얻기 어렵다.The reducing agent material may have a size of 1 nm to 50 μm, preferably 1 nm to 10 μm, and more preferably 1 nm to 1 μm. Patterning becomes difficult when the size of the reducing agent material exceeds 50 μm, and metal oxides of less than 1 nm are practically hard to obtain.
본 발명의 전자 방출원 형성용 조성물에 있어서, 상기 글래스 프릿은 상기 카본계 물질 10 중량부에 대하여 2.5 내지 700 중량부로 포함되는 것이 바람직하다.In the composition for forming an electron emission source of the present invention, the glass frit is preferably included in an amount of 2.5 to 700 parts by weight based on 10 parts by weight of the carbonaceous material.
또한, 상기 환원제 물질은 상기 카본계 물질 10 중량부에 대하여 5 내지 1200 중량부로 포함되는 것이 바람직하며, 5 내지 400 중량부로 포함되는 것이 더 바람직하다. 환원제 물질의 함량이 5 중량부 미만인 경우에는 충분한 환원효과를 얻을 수 없으며, 1200 중량부를 초과하는 경우에는 충분한 전자방출 효과를 얻을 수 없다.In addition, the reducing agent material is preferably included 5 to 1200 parts by weight, more preferably 5 to 400 parts by weight based on 10 parts by weight of the carbon-based material. When the content of the reducing agent material is less than 5 parts by weight, a sufficient reducing effect may not be obtained, and when it exceeds 1200 parts by weight, sufficient electron emission effect may not be obtained.
본 발명의 전자 방출원 형성용 조성물의 성분으로 사용되는 바인더 수지와 용매는 조성물의 인쇄가 용이하도록 도와주는 물질로서, 비이클(vehicle) 성분이라 고 한다. 이러한 비이클 성분은 조성물을 인쇄한 후, 소성공정을 거쳐 제거된다. 본 발명의 전자 방출원 형성용 조성물에서 비이클의 양은 주된 성분인 탄소계 물질과 환원제 물질, 글래스 프릿의 사용량에 따라 적절히 조절할 수 있으며, 특별히 제한되지 않는다. 다만, 전자 방출원 형성용 조성물의 인쇄가 용이하게 되도록 하기 위해서는 상기 카본계 물질의 함량이 전체 조성물에 대하여 0.5 내지 20 중량%로 포함되도록 조절하는 것이 바람직하다. 상기 카본계 물질의 함량이 0.5 중량% 미만이면 전류방출 특성과 수명이 저하될 수 있고, 20 중량%보다 많으면 코팅이 되지 않을 수 있다.The binder resin and the solvent used as the components of the composition for forming an electron emission source of the present invention are materials that facilitate printing of the composition, and are referred to as vehicle components. This vehicle component is removed after the composition has been printed and then calcined. The amount of the vehicle in the composition for forming an electron emission source of the present invention can be appropriately adjusted according to the amount of the carbon-based material, the reducing agent material, and the glass frit, which are the main components, and is not particularly limited. However, in order to facilitate printing of the composition for forming an electron emission source, it is preferable to adjust the content of the carbonaceous material to be included in an amount of 0.5 to 20 wt% based on the total composition. If the content of the carbon-based material is less than 0.5% by weight, the current dissipation characteristics and life may be lowered, and when more than 20% by weight, the coating may not be performed.
상기 바인더 수지와 용매는 통상적으로 평판 표시소자의 전자 방출원에 사용되고 있는 것이라면 어느 것이든 사용될 수 있으며, 상기 바인더 수지의 바람직한 예로는 아크릴계 수지, 에폭시계 수지, 에틸 셀룰로오스 또는 니트로 셀룰로오스와 같은 셀룰로오스계 수지 등이 사용 가능하고, 상기 용매의 바람직한 예로는 부틸 카르비톨(BC:butyl carbitol), 부틸 카르비톨 아세테이트(BCA:butyl carbitol acetate), 테르피테올(TP:terpineol), 텍사놀(texanol) 등의 유기용매가 사용 가능하다. The binder resin and the solvent may be used as long as they are typically used for the electron emission source of the flat panel display device, and a preferable example of the binder resin is a cellulose resin such as acrylic resin, epoxy resin, ethyl cellulose or nitro cellulose. And the like. Preferred examples of the solvent include butyl carbitol (BC), butyl carbitol acetate (BCA), terpineol (TP: terpineol), and texanol. Organic solvents can be used.
또한, 본 발명의 전자 방출원 형성용 조성물은 필요에 따라 광반응성 모노머와 광개시제, 폴리에스테르 아크릴레이트 등과 같은 감광성 수지, 또는 셀룰로오스, 아크릴레이트, 비닐계 고분자 등과 같은 비감광성 폴리머를 더 포함할 수 있다.In addition, the composition for forming an electron emission source of the present invention may further include a photosensitive resin such as a photoreactive monomer and a photoinitiator, polyester acrylate or the like, or a non-photosensitive polymer such as cellulose, acrylate, vinyl polymer, etc. .
상기 광반응성 모노머는 패턴의 분해 향상제로 첨가되며, 열분해성 아크릴레 이트 계열의 모노머, 벤조페논계 모노머, 아세트페논계 모노머, 또는 티오키산톤계 모노머 등이 있으며, 보다 구체적으로는 에폭시 아크릴레이트, 폴리에스테르 아크릴레이트, 2,4-디에틸옥산톤(2,4-diethyloxanthone), 또는 2,2-디메톡시-2-페닐아세토페논을 사용할 수 있다. The photoreactive monomer may be added as a decomposition enhancer of a pattern, and may include a thermally decomposable acrylate monomer, a benzophenone monomer, an acetphenone monomer, or a thioxanthone monomer, and more specifically, an epoxy acrylate, Polyester acrylate, 2,4-diethyloxanthone, or 2,2-dimethoxy-2-phenylacetophenone can be used.
본 발명의 전자 방출원 형성용 조성물은 5,000 내지 100,000 cps의 점도를 가지는 페이스트 상태의 조성물이다. The composition for forming an electron emission source of the present invention is a composition in a paste state having a viscosity of 5,000 to 100,000 cps.
페이스트 상태의 전자 방출원 형성용 조성물을 금속, 반도체, 절연체 등의 기판에 인쇄한 후 열처리하여 원하는 모양의 평판 표시 소자의 전자 방출원을 제조한다. 전자 방출원을 형성하기 위한 인쇄 공정은 스프레이, 스핀 코팅, 스크린 인쇄, 롤 코팅, 딥핑(dipping) 공정 등을 이용할 수 있다. 상기 열처리 공정은 300 내지 500℃의 진공 또는 가스 분위기에서 실시할 수 있으며, 상기 가스 분위기는 공기, N2 가스 또는 비활성 가스를 포함한다. 환원제 물질은 소성로 내에 존재하는 일부 산소와 카본계 물질이 반응을 일으키기 전에, 먼저 산소와 반응하게 되고, 이로써 산소로부터 카본계 물질을 보호하는 역할을 한다. The composition for forming an electron emission source in a paste state is printed on a substrate such as a metal, a semiconductor, an insulator, and the like, followed by heat treatment to produce an electron emission source of a flat panel display device having a desired shape. The printing process for forming the electron emission source may use a spray, spin coating, screen printing, roll coating, dipping process and the like. The heat treatment process may be carried out in a vacuum or gas atmosphere of 300 to 500 ℃, the gas atmosphere includes air, N 2 gas or inert gas. The reducing agent material first reacts with oxygen before the reaction of some oxygen present in the kiln with the carbonaceous material, thereby protecting the carbonaceous material from oxygen.
도 1에 카본계 물질, 바인더 수지, 글래스 프릿, 및 용매를 포함하는 페이스트 조성물을 이용하여 형성된 전자 방출원의 단면을 모식적으로 도시하였다. 도 1에서 캐소드 전극(10) 위에 형성된 전자 방출원은 카본계 물질(12)의 부착을 위해 첨가한 글래스 프릿(14)에 일부 부착된 구조를 가지며, 카본계 물질의 일부가 산화된 상태(20)로 존재하게 된다.
FIG. 1 schematically illustrates a cross section of an electron emission source formed using a paste composition including a carbonaceous material, a binder resin, a glass frit, and a solvent. In FIG. 1, the electron emission source formed on the
도 2는 본 발명의 카본계 물질, 환원제 물질, 글래스 프릿, 바인더 수지, 및 용매를 포함하는 페이스트 조성물을 이용하여 형성된 전자 방출원의 단면을 모식적으로 도시하였다. 도 2에서 캐소드 전극 위에 위치하는 환원제 물질(16)의 일부는 산소와 반응하여 산화물(18)의 형태로 존재하며, 카본계 물질(12)은 소성 후에도 안정한 상태로 유지된다. 2 schematically illustrates a cross section of an electron emission source formed using a paste composition comprising a carbonaceous material, a reducing agent material, a glass frit, a binder resin, and a solvent of the present invention. In FIG. 2, a part of the reducing
상기와 같이 제조된 본 발명의 전자 방출원은 평판 표시 소자의 음극에 사용될 수 있고, 바람직하게는 전계 방출 소자의 음극에 사용될 수 있다.The electron emission source of the present invention prepared as described above may be used for the cathode of the flat panel display device, preferably used for the cathode of the field emission device.
이하 본 발명의 바람직한 실시예 및 비교예를 기재한다. 하기 실시예는 본 발명을 보다 명확히 표현하기 위한 목적으로 기재될 뿐 본 발명의 내용은 하기 실시예에 한정되지 않는다.Hereinafter, preferred examples and comparative examples of the present invention are described. The following examples are described for the purpose of more clearly expressing the present invention, but the contents of the present invention are not limited to the following examples.
[비교예 1]Comparative Example 1
CNT 파우더와 글래스 프릿을 전체 조성물에 대하여 각각 20중량%씩 첨가하여 혼합한 후 볼밀링하였다. 그런 다음 상기 혼합물에 테르피네올(terpineol)에 에틸 셀룰로오스 수지를 녹인 비이클(vehicle)을 혼합하여 전체 100중량%가 되도록 한 후, 교반하여 페이스트 조성물을 제조하였다. 이 페이스트 조성물을 스크린 프린팅(Screen Printing)하고, N2 가스 존재 하에서 400 ℃로 열처리하여 도 1에 도시된 것과 같은 형태의 전자 방출원을 제조하였다. CNT powder and glass frit were added by 20% by weight based on the total composition, mixed, and ball milled. Then, a mixture of a vehicle in which ethyl cellulose resin was dissolved in terpineol (terpineol) was mixed to a total weight of 100% by weight, followed by stirring to prepare a paste composition. The paste composition was screen printed and heat-treated at 400 ° C. in the presence of N 2 gas to produce an electron emission source of the type as shown in FIG. 1.
[실시예 1]Example 1
CNT 파우더와 SnO, 글래스 프릿을 전체조성물에 대하여 각각 20중량%, 15중 량%, 20중량%로 혼합한 것을 제외하고는 비교예 1과 동일한 방법으로 도 2에 도시된 것과 같은 형태의 전자 방출원을 제조하였다.Emission of electrons in the form as shown in FIG. 2 in the same manner as in Comparative Example 1 except that CNT powder, SnO and glass frit were mixed at 20 wt%, 15 wt% and 20 wt%, respectively, based on the total composition The circle was prepared.
상기 실시예 1 및 비교예 1에 따라 제조된 전자 방출원에 대하여 전자방출 특성을 조사하여 그 결과를 도 3에 나타내었다. 도 3에서 보는 바와 같이 실시예 1에 의해 제조된 전자 방출원의 전자 방출 특성이 비교예 1에 의해 제조된 전자 방출원의 전자 방출 특성보다 우수한 것을 알 수 있다.The electron emission characteristics of the electron emission sources prepared according to Example 1 and Comparative Example 1 were investigated, and the results are shown in FIG. 3. As shown in FIG. 3, it can be seen that the electron emission characteristics of the electron emission source manufactured by Example 1 are superior to the electron emission characteristics of the electron emission source prepared by Comparative Example 1.
본 발명의 평판 표시소자의 전자 방출원은 전자 방출 효율을 증가시키기 위하여, 카본계 물질을 포함하며, 이와 함께 환원제 물질을 포함하여 전자 방출원의 소성시에 발생할 수 있는 카본계 물질의 산화를 방지함으로써, 전자 방출 효율이 극대화 되는 장점이 있다.The electron emission source of the flat panel display device of the present invention includes a carbon-based material in order to increase the electron emission efficiency, and together with the reducing agent material, prevents oxidation of the carbon-based material that may occur during firing of the electron emission source. By doing so, there is an advantage that the electron emission efficiency is maximized.
Claims (13)