KR100916627B1 - Manufacturing method of mulching sheet - Google Patents
Manufacturing method of mulching sheet Download PDFInfo
- Publication number
- KR100916627B1 KR100916627B1 KR1020090014031A KR20090014031A KR100916627B1 KR 100916627 B1 KR100916627 B1 KR 100916627B1 KR 1020090014031 A KR1020090014031 A KR 1020090014031A KR 20090014031 A KR20090014031 A KR 20090014031A KR 100916627 B1 KR100916627 B1 KR 100916627B1
- Authority
- KR
- South Korea
- Prior art keywords
- extruder
- mixture
- sheet
- polyethylene
- mulching sheet
- Prior art date
Abstract
Description
본 발명은 멀칭시트의 제조방법에 관한 것이다.The present invention relates to a method for producing a mulching sheet.
멀칭시트(mulching sheet)는 과수원 또는 원예용 및 논과 밭의 두렁에 펼쳐 깔고 양쪽을 흙으로 덮거나 고정구로 고정시키는 일정한 두께의 시트로서, 잡초의 생장을 방지 또는 억제하기 위한 농업용품으로서 거의 필수적으로 사용되고 있다.Mulching sheets (mulching sheets) are sheets of constant thickness for spreading in orchards, horticulture and paddy fields and fields, and covered with soil or fixed with fixtures, and are almost essential as agricultural supplies for preventing or suppressing weed growth. It is used.
멀칭시트의 사용방법은 용도 또는 작물재배 방법에 따라 약간씩 상이할 수 있으나, 대체적으로는 다음과 같은 방법이 사용되고 있다.The method of using the mulching sheet may be slightly different depending on the use or crop cultivation method, but the following method is generally used.
즉, 논두렁의 경우 폭에 맞는 것을 선택하여 그 길이에 맞게 멀칭시트를 펼쳐 깐후, 양쪽에 일정한 간격으로 고정구를 이용하여 토양에 고정시킨다.That is, in the case of paddy field, select the one suitable for the width, spread the mulching sheet according to its length, and fix it to the soil by using a fixture at regular intervals on both sides.
시트가 피복 되므로서 햇볕이 차단되어 잡초들이 생장하지 못하므로 농약을 사용하지 않고도 제초효과가 탁월하므로 널리 사용되고 있는 실정이다.As the sheet is coated, the sun is blocked and weeds do not grow, so the herbicidal effect is excellent without using pesticides.
하지만, 멀칭시트의 특성상 통기성 및 통수성이 원활하지 않아 장기간 피복된 토양의 경우 흙 속의 미생물 등이 생장할 수 없으며 밀폐로 인해 토양속에 있는 식물의 뿌리들이 괴사되어 토양의 강도가 약해져 붕괴되며, 제초제 사용 없이 체초 효과는 탁월하나 자연 상태를 보존한다는 의미에서 오히려 친환경적이지 못하다. 뿐만 아니라, 걸어 다니기 미끄럽고, 특히 이슬 또는 비가 내린 후에는 미끄러워 농촌의 고령화, 여성화로 인해 안전사고의 문제점이 더하고 있는 실정이다. However, due to the characteristics of the mulching sheet, it is not breathable and water-permeable, so in the case of soil coated for a long time, the microorganisms in the soil cannot grow, and the roots of plants in the soil are necrotic due to the sealing, which causes the strength of the soil to collapse and collapse. The herbicidal effect is excellent without use, but rather environmentally friendly in the sense of preserving the natural state. In addition, it is slippery to walk, especially slippery after the rain or rain, the situation of safety accidents due to the aging, feminization of the countryside is adding.
이에 본 발명은 통기성 및 통수성이 우수하면서 미끄럼 방지 기능을 가지는 멀칭시트의 제조방법을 제공하는데 그 목적이 있다. Accordingly, an object of the present invention is to provide a method for producing a mulching sheet having excellent breathability and water permeability, and having an anti-slip function.
상기의 목적을 달성하기 위하여 본 발명은 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 펠렛 형태의 원료; 발포제; 탄산칼슘;을 혼합하여 제조한 1차 혼합물을 제1압출기의 투입부로 투입하는 단계; 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 펠렛 형태의 원료; 탄산칼슘;을 혼합하여 제조한 2차 혼합물을 제2압출기의 투입부로 투입하는 단계; 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 펠렛 형태의 원료; 탄산칼슘;을 혼합하여 제조한 2차 혼합물을 제3압출기의 투입부로 투입하는 단계; 제1압출기로부터 배출되는 1차 혼합물과 제2압출기로부터 배출되는 2차 혼합물 및 제3압출기로부터 배출되는 2차 혼합물이 하나의 토출구를 통해 동시에 블로우 성형되어 성형물의 외측면에는 1차 혼합물 성분이 위치하고 중측면 및 내측면에는 제2압출기 및 제3압출기로부터 각각 배출되는 2차 혼합물이 차례로 위치하도록 성형하는 단계; 및, 상기 블로우 성형물의 종단면을 절단하여 절단된 블로우 성형물을 시트 형태로 각각 펴지도록 지관에 감는 단계;를 포함하는 것을 특징으로 하는 멀칭시트의 제조방법을 제공한다.In order to achieve the above object, the present invention is a raw material in the form of powder or pellets made of polyethylene or polypropylene material; blowing agent; Injecting the primary mixture prepared by mixing calcium carbonate into the inlet of the first extruder; Raw materials in powder or pellet form composed of polyethylene or polypropylene material; Injecting a secondary mixture prepared by mixing calcium carbonate into an input unit of a second extruder; Raw materials in powder or pellet form composed of polyethylene or polypropylene material; Injecting a secondary mixture prepared by mixing calcium carbonate into an input unit of a third extruder; The primary mixture discharged from the first extruder, the secondary mixture discharged from the second extruder, and the secondary mixture discharged from the third extruder are blow-molded at the same time through one discharge port so that the primary mixture component is located on the outer surface of the molding. Forming a secondary mixture discharged from the second extruder and the third extruder on the middle side and the inner side in order; And cutting the longitudinal section of the blow molding to wind the cut blow molding in the form of a sheet so as to be unfolded in a sheet form.
이하 본 발명의 과제 해결 수단을 단계별로 세분화하여 상세히 설명하고자 한다.Hereinafter will be described in detail by breaking down the problem solving means of the present invention step by step.
단계 1: 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 Step 1: powder made of polyethylene or polypropylene material or 펠렛Pellet 형태의 원료; 발포제; 탄산칼슘; 을 혼합하여 제조한 1차 혼합물을 제1압출기의 Raw materials in the form; blowing agent; Calcium carbonate; The primary mixture prepared by mixing the first extruder 투입부로As input 투입하는 단계 Committing step
본 단계 1은 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 펠렛 형태의 원료; 발포제; 탄산칼슘;을 혼합하여 제조한 1차 혼합물을 제1압출기의 투입부로 투입하는 단계이다. Step 1 is a raw material in the form of powder or pellets made of polyethylene or polypropylene material; blowing agent; A step of injecting the primary mixture prepared by mixing the calcium carbonate into the input unit of the first extruder.
한편, 본 발명은 농업용에 사용되는 멀칭시트에 있어서, 작물에 수분 및 공기를 원활하게 공급하면서, 논둑 및 밭둑 또는 과수원과 원예용에 사용시 미끄럼방지 기능이 있는 멀칭시트를 제조하기 위해 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 펠렛 형태의 원료; 펠렛 또는 분말 형태의 발포제; 탄산칼슘;을 혼합하여 1차 혼합물을 제조하는데, 1차 혼합물은 멀칭시트의 외측면에 위치하는 성분이다. 1차 혼합물로 이루어진 멀칭시트의 외측면은 토양에 수분 및 공기 공급에 있어서, 직접적으로 수분 및 공기와 닿는 부분으로 통기성 및 통수성이 우수하여야 하고, 논둑에 사용시에는 미끄러움을 방지할 수 있도록 성형되어야 하는 부분으로, 1차 혼합물은 반드시 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 펠렛 형태의 원료; 펠렛 또는 분말 형태의 발포제; 탄산칼슘;을 포함하여야 한다. On the other hand, the present invention, in the mulching sheet used for agriculture, while supplying moisture and air to the crop smoothly, while producing a mulching sheet having a non-slip function when used in rice fields and field banks or orchards and gardening, polyethylene or polypropylene Raw material in pellet form composed of material; Blowing agents in pellet or powder form; Mixing calcium carbonate; to prepare a primary mixture, the primary mixture is a component located on the outer surface of the mulching sheet. The outer surface of the mulching sheet composed of the primary mixture should be excellent in breathability and water permeability to directly contact with moisture and air in supplying water and air to the soil, and molded to prevent slippage when used in rice fields. In part, the primary mixture must be a raw material in pellet form composed of polyethylene or polypropylene material; Blowing agents in pellet or powder form; Calcium carbonate;
본 발명에서 사용하는 폴리에틸렌(Polyethylene)은 유연성이 좋으면서 내수성, 전기 절연성이 우수하고, 자외선과 산 또는 알카리에 대해 잘 견디며, 저온에 서도 유연성을 잃지 않을 뿐만 아니라, 충격에도 강하다. Polyethylene (polyethylene) used in the present invention is excellent in flexibility, excellent in water resistance and electrical insulation, and well resistant to ultraviolet rays, acids or alkalis, and does not lose flexibility even at low temperatures, and is also resistant to impact.
한편, 본 발명에서 사용한 폴리에틸렌 재질은 특정의 종류에 한정되는 것은 아니나, 바람직하게는 LDPE(Low Density Polyethylene) 20~80 중량%, LLDPE(Linear Low Density Polyethylene) 20~80 중량%로 조성된 것이 좋다. Meanwhile, the polyethylene material used in the present invention is not limited to a specific kind, but preferably, 20 to 80 wt% of LDPE (Low Density Polyethylene) and 20 to 80 wt% of LLDPE (Linear Low Density Polyethylene) is preferable. .
폴리프로필렌(Polypropylene)은 전기 절연성이 우수하고 충격에도 강하며 고 내열성이다. Polypropylene has excellent electrical insulation, resistance to shock and high heat resistance.
한편, 발포제는 본 발명의 멀칭시트를 제조하는데 있어서, 조밀하면서 미세한 셀을 형성하여, 통기성 및 통수성이 우수한 멀칭시트를 제조할 수 있도록 할 뿐만 아니라, 본 발명으로부터 제조된 멀칭시트의 표면에 마찰력을 부여하여 미끄럼방지 효과를 발휘하도록 한다. 본 발명에서 사용하는 발포제는 특정 종류에 한정되는 것은 아니나, 바람직하게는 아조디카본아미드(Azodicarbonamide)인 것이 좋다. On the other hand, in the manufacturing of the mulching sheet of the present invention, the foaming agent forms a dense and fine cell, thereby making it possible to produce a mulching sheet excellent in breathability and water permeability, as well as a frictional force on the surface of the mulching sheet produced from the present invention. To give an anti-slip effect. Although the blowing agent used in the present invention is not limited to a specific kind, it is preferable that it is azodicarbonamide.
한편, 탄산칼슘(CaCO3)은 1차 혼합물 각 성분 간의 응집력 및 결집력을 증대시키며 고분자에 무기물이 첨가되면서 통기성 및 통수성이 우수한 멀칭시트를 제조하는데 영향을 미친다.On the other hand, calcium carbonate (CaCO 3 ) increases the cohesion and cohesion between the components of the primary mixture, and as the inorganic material is added to the polymer affects the production of a mulching sheet excellent in breathability and water permeability.
한편, 1차 혼합물은 바람직하게 산화방지제를 추가로 포함할 수 있는데, 자외선과 열로 인해 산화되는 것을 방지할 수 있기 때문이다.On the other hand, the primary mixture may preferably further comprise an antioxidant, because it can prevent the oxidation due to ultraviolet rays and heat.
단계 2: 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 Step 2: powder made of polyethylene or polypropylene material or 펠렛Pellet 형태 의 원료; 탄산칼슘;을 혼합하여 제조한 2차 혼합물을 제2압출기의 Form of raw material; The secondary mixture prepared by mixing calcium carbonate; 투입부로As input 투입하Committing 는 단계Steps
본 단계 2는 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 펠렛 형태의 원료; 탄산칼슘;을 혼합하여 제조한 2차 혼합물을 제2압출기의 투입부로 투입하는 단계이다. Step 2 is a raw material in the form of powder or pellets made of polyethylene or polypropylene material; The secondary mixture prepared by mixing the calcium carbonate; is introduced into the input unit of the second extruder.
본 단계 2에서 제조하는 2차 혼합물은 상기 단계 1에서 제조된 1차 혼합물에 압착되는 성분으로, 2차 혼합물도 통기성 및 통수성이 우수하여야 하므로 반드시 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 펠렛 형태의 원료; 탄산칼슘;을 혼합하여 제조한다. The secondary mixture prepared in step 2 is a component that is pressed into the primary mixture prepared in step 1, the secondary mixture must also be excellent in breathability and water permeability, so the raw material in the form of pellets made of polyethylene or polypropylene material; Calcium carbonate; prepared by mixing.
한편, 본 발명에서 2차 혼합물의 구성성분인 폴리에틸렌 재질로 구성된 펠렛 형태의 원료; 탄산칼슘;에 대한 구체적인 설명은 상기 단계 1에서 설명한 것과 동일하다. On the other hand, in the present invention, the raw material in the form of pellets composed of a polyethylene material which is a component of the secondary mixture; Specific description of the calcium carbonate is the same as described in step 1.
한편, 2차 혼합물은 바람직하게 셀룰로우즈(Cellulose)를 추가로 포함하는 것이 좋다.On the other hand, the secondary mixture preferably further comprises cellulose (Cellulose).
한편, 2차 혼합물은 바람직하게 산화방지제를 추가로 포함할 수 있는데, 이에 대한 구체적인 설명은 상기 단계 1에서 설명한 것과 동일하다.On the other hand, the secondary mixture may preferably further comprise an antioxidant, the detailed description thereof is the same as described in step 1 above.
단계 3: 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 Step 3: powder consisting of polyethylene or polypropylene material or 펠렛Pellet 형태의 원료; 탄산칼슘;을 혼합하여 제조한 2차 혼합물을 제3압출기의 Raw materials in the form; The secondary mixture prepared by mixing calcium carbonate; 투입부로As input 투입하Committing 는 단계;The step;
본 단계 3은 폴리에틸렌 또는 폴리프로필렌 재질로 구성된 분말 또는 펠렛 형태의 원료; 탄산칼슘;을 혼합하여 제조한 2차 혼합물을 제3압출기의 투입부로 투입하는 단계;This step 3 is a raw material in the form of powder or pellets made of polyethylene or polypropylene material; Injecting a secondary mixture prepared by mixing calcium carbonate into an input unit of a third extruder;
본 발명은 통기성과 통수성 뿐만 아니라 강도도 우수한 멀칭시트를 제조하기 위해 상기 단계 2에서 제조된 동일한 2차 혼합물을 제3압출기의 투입부로 투입한다. In the present invention, the same secondary mixture prepared in step 2 is introduced into the third extruder to prepare a mulching sheet having excellent strength as well as breathability and water permeability.
한편, 본 발명으로부터 제조되는 멀칭시트는 제1압출기로부터 배출되는 1차 혼합물, 제2압출기 및 제3압출기로부터 각각 배출되는 2차 혼합물이 하나의 토출구를 통해 용출되어 성형되므로 동시에 압착되어 3겹으로 이루어지기 때문에 강도가 우수한 장점이 있으며 각 층의 혼합물 조성비를 달리하여 통기 및 통수기능의 양도 조절이 가능하다.On the other hand, the mulching sheet produced from the present invention is the primary mixture discharged from the first extruder, the second extruder and the second mixture discharged from each of the third extruder is eluted through a single discharge port is molded at the same time to be pressed in three layers Because it is made, the strength is excellent, and the amount of aeration and water permeation can be controlled by varying the composition ratio of each layer.
단계 4: 제1압출기로부터 배출되는 1차 혼합물과 제2압출기로부터 배출되는 2차 혼합물 및 제3압출기로부터 배출되는 2차 혼합물이 하나의 토출구를 통해 동시에 Step 4: The primary mixture discharged from the first extruder, the secondary mixture discharged from the second extruder, and the secondary mixture discharged from the third extruder simultaneously through one outlet 블로우Blow 성형되어Molded 성형물의 Molding 외측면에는On the outside 1차 혼합물 성분이 위치하고 The primary mixture is located 중측면Medial side 및 내측면에는 제2압출기 및 제3압출기로부터 각각 배출되는 2차 혼합물이 차례로 위치하도록 성형하는 단계 And forming a secondary mixture discharged from the second extruder and the third extruder, respectively, on the inner side thereof in order.
본 단계 4는 제1압출기로부터 배출되는 1차 혼합물과 제2압출기로부터 배출되는 2차 혼합물 및 제3압출기로부터 배출되는 2차 혼합물이 하나의 토출구를 통해 동시에 블로우 성형되어 성형물의 외측면에는 1차 혼합물 성분이 위치하고 중측면 및 내측면에는 제2압출기 및 제3압출기로부터 각각 배출되는 2차 혼합물이 차례로 위치하도록 성형하는 단계;이다.In this step 4, the primary mixture discharged from the first extruder, the secondary mixture discharged from the second extruder, and the secondary mixture discharged from the third extruder are blow-molded at the same time through one discharge port, so that the primary surface Forming a mixture component so that the secondary mixture discharged from the second extruder and the third extruder, respectively, is located in the middle side and the inner side.
블로우 성형이란 원료를 주입하여 압출기를 통해 원료가 용해되어 토출구를 통해 용출될 때 관의 내부로 콤프레서를 이용하여 공기를 공급함으로써 성형하는 방법이다. 본 발명은 제1압출기로부터 배출되는 1차 혼합물과 제2압출기 및 제3압출기로부터 배출되는 2차 혼합물들을 토출구를 통해 동시에 블로우 성형을 함으로써 성형물의 외측면에는 1차 혼합물이, 중측면 및 내측면에는 제2압출기 및 제3압출기로부터 각각 배출되는 2차 혼합물이 차례로 위치하도록 멀칭시트를 제조할 수 있다.Blow molding is a method of molding by injecting raw materials and supplying air using a compressor to the inside of the tube when the raw materials are dissolved and eluted through the discharge port through the extruder. In the present invention, the primary mixture is discharged from the first extruder and the secondary mixture discharged from the second extruder and the third extruder simultaneously blow molding through the discharge port, the primary mixture is on the outer side of the molding, the middle side and the inner side In the mulch sheet may be prepared so that the secondary mixture discharged from the second extruder and the third extruder are located in sequence.
단계 5: 상기 Step 5: above 블로우Blow 성형물의 종단면을 절단하여 절단된 Cut by cutting the end face of the molding 블로우Blow 성형물을 시트 형태로 각각 펴지도록 지관에 감는 단계 Winding the moldings to the branch pipes so as to unfold the sheets in the form of sheets
단계 5는 상기 블로우 성형물의 종단면을 절단하여 절단된 블로우 성형물을 시트 형태로 각각 펴지도록 지관에 감는 단계이다.Step 5 is a step of cutting the longitudinal section of the blow molding and winding the cut blow molding to each of the branch pipe to be unfolded in the form of a sheet.
상기 단계 4에서 생산된 블로우 성형물은 이어진 형태이기 때문에 멀칭시트로 사용하기에는 어려움이 있다. 이에 본 발명은 서로 이어진 형태인 성형물의 종단면을 절단함으로써 블로우 성형물을 시트 형태로 각각 펴지도록하여 운반과 보관에 용이하게 지관에 감는 것이다. 이렇게 만들어진 멀칭시트는 미세한 셀이 형성된 3겹의 비닐을 동시에 압착한 것으로 외관상 한겹의 일체식으로 되있으며 통기성 및 통수성과 강도가 우수하면서 미끄럼 방지 효과를 발휘한다.The blow molded product produced in step 4 is difficult to use as a mulching sheet because it is a continuous form. Accordingly, the present invention is to cut the longitudinal cross-section of the moldings that are connected to each other to unfold the blow moldings in the form of a sheet, respectively, to easily wind the paper pipe for transportation and storage. The mulching sheet thus made is a single-layered one-piece integral form that simultaneously compresses three-ply vinyl with fine cells, and has excellent breathability, water permeability and strength while preventing slipping.
상기에서 살펴본 바와 같이 본 발명의 제조방법으로부터 제조된 멀칭시트는 미세한 셀을 형성하여 통기성 및 통수성이 우수하기 때문에 토양에 수분 및 공기를 원활하게 공급할 수 있어 장기간 피복되어 밀폐된 토양에서 발생하는 부작용을 방지할 수 있다. 그리고 토양 속 미생물의 생육에 방해가 되지 않기 때문에 자연상태를 그대로 유지하면서 잡초를 방지할 수 있는 제초효과가 탁월하다.As described above, the mulching sheet manufactured from the manufacturing method of the present invention forms a fine cell, which is excellent in breathability and water permeability, so that water and air can be smoothly supplied to the soil, so that side effects occurring in a closed soil for a long time are covered. Can be prevented. And because it does not interfere with the growth of microorganisms in the soil, weeding effect that can prevent weeds while maintaining the natural state is excellent.
또한, 본 발명으로부터 제조된 멀칭시트는 미끄럼방지 기능이 우수하여 폴리에틸렌 재질로 구성된 기존 시트의 문제점을 해결할 수 있는 효과를 발휘한다. In addition, the mulching sheet produced from the present invention is excellent in the anti-slip function to exhibit the effect of solving the problem of the existing sheet consisting of a polyethylene material.
또한, 폴리에틸렌 또는 폴리프로필렌 재질을 기본으로 구성된 혼합물들을 3겹으로 압착하였기 때문에 강도가 우수한 장점도 있고 각 층의 혼합물 조성비를 달리하여 생산할 수 있으므로 통기 및 통수량과 제품의 내구성도 조절할 수가 있다. In addition, since the mixture composed of polyethylene or polypropylene material is crimped in three layers, the strength is excellent and the mixture composition of each layer can be produced by varying the ratio of ventilation and water flow rate and the durability of the product.
이하, 본 발명의 내용에 대해 하기 실시예에서 더욱 상세히 설명하지만, 본 발명의 권리범위가 하기 실시예에만 한정되는 것은 아니고, 이와 등가의 기술적 사상의 변형까지를 포함한다. Hereinafter, the content of the present invention will be described in more detail in the following examples, but the scope of the present invention is not limited only to the following examples, and includes modifications of equivalent technical ideas.
실시예Example 1: One: 멀칭시트Mulching Sheet 제조 Produce
폴리에틸렌 재질로 구성된 펠렛 형태의 원료; 펠렛 또는 분말 형태의 발포 제; 탄산칼슘; 산화방지제를 혼합하여 제조한 1차 폴리에틸렌 혼합물을 제1압출기의 투입부로, 폴리에틸렌 재질로 펠렛 형태의 원료; 탄산칼슘; 산화방지제를 혼합하여 제조한 2차 폴리에틸렌 혼합물을 제2압출기 투입부와 제3압출기 투입부로 각각 투입한 후, 블로우 성형을 통해 제1압출기로부터 배출되는 1차 폴리에틸렌 혼합물은 외측면에, 제2압출기로부터 배출되는 2차 폴리에칠렌 혼합물을 중측면에, 제3압출기로부터 배출되는 2차 폴리에틸렌 혼합물은 내측면에 차례로 위치하도록 하나의 토출구를 통해 동시에 블로우 성형하였다. 상기 블로우 성형물의 종단면을 절단하여 절단된 성형물을 시트 형태로 각각 펴지도록하여 지관에 감아 보관 및 운반에 용이하도록 멀칭시트를 제조하였다. Raw material in pellet form composed of polyethylene material; Blowing agents in pellet or powder form; Calcium carbonate; A primary polyethylene mixture prepared by mixing an antioxidant as an input unit of a first extruder, a raw material in pellet form of polyethylene; Calcium carbonate; After the second polyethylene mixture prepared by mixing the antioxidant is introduced into the second extruder and the third extruder, respectively, the primary polyethylene mixture discharged from the first extruder through blow molding is disposed on the outer side and the second extruder. The secondary polyethylene mixture exiting from the blow molding was simultaneously blown through one outlet so that the secondary polyethylene mixture exiting from the third extruder was in turn located on the inner side. The mulching sheet was prepared by cutting the longitudinal cross-section of the blow molding product so that the cut moldings were unfolded in the form of sheets, respectively, and wound around the branch pipe to facilitate storage and transportation.
실험예Experimental Example 1: 미끄러짐 각도 측정 1: slip angle measurement
실시예 1에서 제조된 멀칭시트와 일반시트를 일정크기의 유리판에 씌운 후, 아크릴판을 사용하여 경사판의 각도를 올려 추가 미끄러지기 시작할 때의 경사각을 측정하였다.After covering the mulching sheet and the general sheet prepared in Example 1 on a glass plate of a certain size, the angle of the inclined plate was measured by raising the angle of the inclined plate using an acrylic plate.
미끄러짐 각도를 측정한 결과(표 1), 멀칭시트가 일반시트보다 높은 각도를 나타냈다. As a result of measuring the slip angle (Table 1), the mulching sheet showed a higher angle than the general sheet.
상기의 결과로부터 본 발명으로부터 제조된 멀칭시트는 미끄럼 방지 기능이 우수하여 일반 시트의 문제점을 해결할 수 있다는 사실을 확인할 수 있었다.From the above results, the mulching sheet manufactured from the present invention was confirmed that the problem of the general sheet can be solved by excellent anti-slip function.
실험예Experimental Example 2: 2: 투습도Breathable 측정 Measure
본 실험예 2에서는 상기 실시예 1에서 제조된 멀칭시트를 ASTM E 96-63에 준하여 투습도(g/㎡ 24hr)를 측정하였다(온도 : 37.8℃ 습도 90% R.H.)In Experimental Example 2, the moisture permeability (g / m 2 24hr) of the mulching sheet prepared in Example 1 was measured according to ASTM E 96-63 (temperature: 37.8 ° C humidity 90% R.H.)
투습도를 측정한 결과(표 2), 본 발명으로부터 제조된 실시예 1의 투습도가 일반 멀칭시트에 비해 우수한 것을 확인할 수 있었다. As a result of measuring the water vapor transmission rate (Table 2), it was confirmed that the water vapor transmission rate of Example 1 prepared from the present invention is superior to the general mulching sheet.
실험예Experimental Example 3: 제조된 3: manufactured 멀칭시트의Of mulching sheet 표면 확대 Surface magnification
전자현미경을 이용하여 실시예 1에서 제조된 멀칭시트 표면을 50배율과 80배율로 확대하여 관찰하였다.Using an electron microscope, the mulching sheet surface prepared in Example 1 was observed at 50 magnification and 80 magnification.
전자현미경으로 50배율(도 1) 및 80배율(도 2)로 확대하여 멀칭시트를 확대하여 관찰한 결과, 멀칭시트 표면에 조밀하면서 미세한 셀이 형성된 것을 확인할 수 있었다. As a result of enlarging the mulching sheet at 50 magnification (FIG. 1) and 80 magnification (FIG. 2) with an electron microscope, it was confirmed that dense and fine cells were formed on the surface of the mulching sheet.
도 1은 실시예 1에서 제조된 멀칭시트를 전자현미경으로 50배율 확대한 도이다.1 is an enlarged 50 times magnification of a mulching sheet prepared in Example 1 with an electron microscope.
도 2는 실시예 1에서 제조된 멀칭시트를 전자현미경으로 80배율 확대한 도이다.Figure 2 is an enlarged 80 times magnification of the mulching sheet prepared in Example 1 with an electron microscope.
Claims (6)