KR100895061B1 - Reed manufacturing method in loom - Google Patents

Reed manufacturing method in loom Download PDF

Info

Publication number
KR100895061B1
KR100895061B1 KR1020020071176A KR20020071176A KR100895061B1 KR 100895061 B1 KR100895061 B1 KR 100895061B1 KR 1020020071176 A KR1020020071176 A KR 1020020071176A KR 20020071176 A KR20020071176 A KR 20020071176A KR 100895061 B1 KR100895061 B1 KR 100895061B1
Authority
KR
South Korea
Prior art keywords
flesh
thin film
body flesh
diamond
contact surface
Prior art date
Application number
KR1020020071176A
Other languages
Korean (ko)
Other versions
KR20040042615A (en
Inventor
송근철
김경운
조정환
Original Assignee
두산인프라코어 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 두산인프라코어 주식회사 filed Critical 두산인프라코어 주식회사
Priority to KR1020020071176A priority Critical patent/KR100895061B1/en
Publication of KR20040042615A publication Critical patent/KR20040042615A/en
Application granted granted Critical
Publication of KR100895061B1 publication Critical patent/KR100895061B1/en

Abstract

본 발명은 직기용 바디의 바디살 제조방법을 제공한다. 본 발명의 바디살 제조방법은 마찰접촉면을 갖는 바디살을 제조하는 단계와; 제조된 바디살의 마찰접촉면을 세정하는 단계와; 세정된 바디살의 마찰접촉면에 바디살의 마찰접촉면에 실레인가스와 메탄가스가 2 : 8의 비율로 혼합된 혼합가스로 실리콘박막을 대략 0.5㎛정도의 두께로 코팅하는 단계; 실리콘박막 위에 플라즈마 보강 기상증착에 의한 방법으로 0.5㎛ 내지 10㎛범위의 두께로 다이아몬드상 카본박막을 코팅하는 단계;를 포함하며, 플라즈마 보강 기상증착은 구동전압이 -300Ｖ이상이고 합성온도가 200 이하인 조건으로 진행되는 것을 특징으로 한다. 이러한 본 발명에 의하면, 바디살의 마찰접촉면에 다이아몬드상 카본박막을 코팅처리함으로써 높은 표면 경도를 갖게 되며, 따라서 원사와의 잦은 마찰접촉에도 쉽게 마모되지 않는다. 또한, 다이아몬드상 카본박막이 코팅된 바디살은 높은 평활성과 윤활성을 갖게 되며, 따라서 원사를 손상시키지 않으면서 안전하게 가이드 할 수 있게 된다. 아울러 다이아몬드상 카본박막은 플라즈마 보강 기상증착에 의한 방법으로 바디살에 코팅되며, 따라서 높은 부착력으로 바디살에 코팅되는 효과를 갖는다. The present invention provides a body meat manufacturing method of a loom body. Body body manufacturing method of the present invention comprises the steps of manufacturing a body flesh having a friction contact surface; Cleaning the frictional contact surface of the manufactured body meat; Coating a thin silicon film with a thickness of approximately 0.5 μm with a mixed gas of silane gas and methane gas mixed at a frictional contact surface of the body flesh with a ratio of 2: 8 on the frictional contact surface of the body flesh; Coating a diamond-like carbon thin film with a thickness in the range of 0.5 μm to 10 μm by a method of plasma-reinforced vapor deposition on the silicon thin film, wherein the plasma-reinforced vapor deposition comprises a driving voltage of -300 Ｖ or more and a synthesis temperature of 200 or less It is characterized by proceeding under the condition. According to the present invention, by coating a diamond-like carbon thin film on the frictional contact surface of the body flesh has a high surface hardness, and therefore does not easily wear even in frequent frictional contact with the yarn. In addition, the body flesh coated with the diamond-like carbon thin film has high smoothness and lubricity, and thus can be safely guided without damaging the yarn. In addition, the diamond-like carbon thin film is coated on the body flesh by a plasma enhanced vapor deposition method, and thus has the effect of coating on the body flesh with high adhesion.

Description

직기용 바디의 바디살 제조방법{REED MANUFACTURING METHOD IN LOOM}Method for manufacturing body meat of loom body {REED MANUFACTURING METHOD IN LOOM}

도 1은 본 발명에 따른 직기용 바디의 바디살의 구성을 나타내는 단면도,1 is a cross-sectional view showing the configuration of the body flesh of the loom body according to the invention,

도 2는 본 발명에 따른 직기용 바디의 바디살의 제조방법을 나타내는 블록도이다. Figure 2 is a block diagram showing a method of manufacturing a body flesh of the loom body according to the invention.

♣ 도면의 주요 부분에 대한 부호의 설명 ♣ ♣ Explanation of symbols for the main parts of the drawing ♣

10: 바디살 14: 마찰접촉면10: body flesh 14: frictional contact surface

20: 다이아몬드상 카본박막 30: 실린콘박막20: diamond-like carbon thin film 30: silicon thin film

본 발명은 직기용 바디의 바디살 제조방법에 관한 것으로, 보다 상세하게는 표면 평활성이 우수하고 낮은 마찰계수를 가짐은 물론 내마모성이 우수하여 수명이 긴 직기용 바디의 바디살 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a body loom of a loom body, and more particularly, to a method of manufacturing a body loom of a loom body having a long surface life with excellent surface smoothness and a low coefficient of friction as well as excellent wear resistance.

직기(織機)는 직물을 짜는 기계로서, 날실과 씨실을 정렬하고 눌러서 다져주는 바디를 갖추고 있다. 바디는 바디프레임과, 바디프레임에 좁은 간격을 두고 나란하게 배열되는 다수의 바디살로 구성된다. 특히, 바디살은 그 양단이 바디프레임에 고정되는 것으로, 두께가 얇고 폭이 좁은 스테인레스강판으로 구성된다. Looms are weaving machines that have a body that aligns and presses the warp and weft threads. The body is composed of a body frame and a plurality of body flesh arranged side by side with a narrow gap on the body frame. In particular, the body meat is fixed to both ends of the body frame, it is composed of a thin stainless steel plate with a narrow thickness.

한편, 이러한 바디살은 항상 섬유, 즉 원사(原絲)와 마찰접촉하는 바, 쉽게 마모되는 단점이 지적되고 있다. 특히, 최근에는 고강도의 신소재 섬유가 개발됨에 따라 바디살의 마모가 더욱 가속화되는 문제점이 있다. 이같은 문제점은 마모된 바디살을 자주 교체해주어야 하는 바, 바디살의 교체에 따른 많은 교체시간과 많은 교체비용이 소요되는 결과를 초래한다. 결국, 바디살의 교체시간과 교체비용이 증가함에 따라 생산효율이 떨어지고, 제조단가가 증가되는 등, 여러 가지 문제점을 발생시킨다. On the other hand, the body meat is always in friction contact with the fiber, that is, the yarn (barn), it is pointed out the disadvantage that it is easily worn. In particular, as the recent development of a new high-strength fiber has a problem that the wear of the body flesh is further accelerated. This problem requires frequent replacement of the worn body flesh, which results in a large replacement time and a large replacement cost according to the replacement of the body flesh. As a result, as the replacement time and replacement cost of the body meat increase, the production efficiency is lowered, and the manufacturing cost is increased.

이를 감안하여 최근에는 바디살의 표면에 경질크롬도금 또는 TiN, TiC 코팅을 시행하여 표면 경도를 증가시키는 방법이 다양하게 제안되고 있다. 그러나 이 방법은 성능개선효과가 크지 않은 것으로 나타났다. 즉, 바디살의 표면에 경질크롬 도금을 시행하는 경우는, 내마모성능이 크게 개선되지 않음은 물론 오히려 내식성이 떨어져 부식되기 쉽다는 단점이 있다. 또한, 바디살의 표면에 TiN, TiC 코팅을 시행하는 경우에는, 내마모성능은 우수하나 모재, 즉 바디살에 대한 TiN, TiC 코팅 박막의 부착력이 취약하여 상기 바디살로부터 TiN, TiC 코팅막이 쉽게 박리된다는 단점이 있다. 특히, 바디살에 대한 TiN, TiC 박막의 코팅조건이 500℃ 정도의 고온에서 이루어지는 바, 모재, 즉 바디살에 연화(軟化)현상이 일어나는 문제점이 지적되고 있다. In view of this, recently, various methods of increasing the surface hardness by applying hard chromium plating, TiN, or TiC coating on the surface of the body flesh have been proposed. However, this method does not show a significant performance improvement. That is, when hard chromium plating is applied to the surface of the body flesh, wear resistance is not greatly improved, but rather, corrosion resistance is poor and corrosion is easy. In addition, when TiN, TiC coating is applied to the surface of the body flesh, the wear resistance is excellent, but the adhesion of the TiN, TiC coating thin film to the base material, that is, the body flesh is weak, so that the TiN, TiC coating film is easily peeled from the body flesh. There are disadvantages. In particular, the coating condition of the TiN, TiC thin film on the body flesh is made at a high temperature of about 500 ℃, it is pointed out a problem that softening phenomenon occurs in the base material, that is, the body flesh.

따라서, 원사와의 마찰접촉으로 인한 마모를 최소화시킬 수 있도록 높은 표면 경도를 갖추고 있고, 박막의 코팅처리 과정시 모재의 연화현상을 방지할 수 있으며, 코팅처리된 박막이 모재로부터 박리되는 것을 방지하는 직기용 바디의 바디살 제조방법의 개발이 시급히 요구되는 것이다.Therefore, it has a high surface hardness to minimize wear due to frictional contact with the yarn, can prevent the softening of the base material during the coating process of the thin film, and prevents the coated thin film from being peeled from the base material Development of a method of manufacturing a body meat of a loom body is urgently required.

한편, 이와 같은 요구에 따라 본 발명자는 각고의 실험과 연구 끝에 높은 표면경도와 낮은 마찰계수의 물성을 갖는 비정질 결정구조의 다이아몬드상 카본박막을 모재에 저온으로 코팅처리함으로써 내마모성능이 향상될 뿐만 아니라 원사의 손상이 방지되도록 낮은 마찰계수를 갖고, 박막의 코팅처리시 모재의 연화현상을 방지하며, 상기 모재와 박막을 견고하게 결합시킬 수 있는 직기용 바디의 바디살 제조방법을 개발하였다. On the other hand, in accordance with such demands, the inventors of the present invention have not only improved wear resistance but also improved abrasion resistance by coating a diamond-like carbonaceous film of amorphous crystal structure having high surface hardness and low coefficient of friction on the base material at low temperature. In order to prevent the damage of the low friction coefficient, to prevent the softening phenomenon of the base material during the coating process of the thin film, and to develop a body meat manufacturing method of the body of the loom body that can firmly bond the base material and the thin film.

따라서, 본 발명의 목적은 다이아몬드상 카본박막을 모재에 저온으로 코팅처리함으로써 내마모성능이 향상되고, 낮은 마찰계수를 가지며, 박막의 코팅처리시 모재의 연화현상을 방지할 수 있음은 물론 모재와 박막을 견고하게 결합시킬 수 있는 직기용 바디의 바디살 제조방법을 제공하는 데 있다.Accordingly, an object of the present invention is to improve the wear resistance by coating the diamond-like carbon thin film on the base material at low temperature, to have a low coefficient of friction, and to prevent the softening of the base material during the coating process of the thin film. It is to provide a method of manufacturing a body meat of the loom body that can be firmly combined.

이와 같은 목적을 달성하기 위해 본 발명에 따른 직기용 바디의 바디살 제조방법은 원사를 정렬하고 눌러서 다져주는 직기용 바디의 바디살을 제조하는 방법에 있어서, 마찰접촉면을 갖는 바디살을 제조하는 단계와; 제조된 상기 바디살의 마찰접촉면을 세정하는 단계와; 세정된 상기 바디살의 마찰접촉면에 상기 바디살의 마찰접촉면에 실레인가스와 메탄가스가 2 : 8의 비율로 혼합된 혼합가스로 실리콘박막을 대략 0.5㎛정도의 두께로 코팅하는 단계; 상기 실리콘박막 위에 플라즈마 보강 기상증착에 의한 방법으로 0.5㎛ 내지 10㎛범위의 두께로 다이아몬드상 카본박막을 코팅하는 단계;를 포함하며, 상기 플라즈마 보강 기상증착은 구동전압이 -300Ｖ이상이고 합성온도가 200 이하인 조건으로 진행되는 것을 특징으로 한다.In order to achieve the above object, the method of manufacturing a body flesh of a loom body according to the present invention is a method of manufacturing a body flesh of a loom body that aligns and presses a yarn, manufacturing a body flesh having a friction contact surface. Wow; Cleaning the frictional contact surface of the manufactured body flesh; Coating a thin silicon film with a thickness of approximately 0.5 μm with a mixed gas in which a silane gas and methane gas are mixed in a ratio of 2: 8 to the frictional contact surface of the body flesh on the frictional contact surface of the body flesh; Coating a diamond-like carbon thin film with a thickness in the range of 0.5 μm to 10 μm on the silicon thin film by a plasma enhanced vapor deposition method, wherein the plasma enhanced vapor deposition includes a driving voltage of -300 Ｖ or more and a synthesis temperature Characterized in that the proceeds under the condition of 200 or less.

삭제delete

이하, 본 발명에 따른 직기용 바디의 바디살 제조방법의 바람직한 실시예를 첨부 도면에 의거하여 상세히 설명한다. Hereinafter, with reference to the accompanying drawings a preferred embodiment of the method for manufacturing a body meat of the body for a loom according to the present invention will be described in detail.

도 1은 본 발명에 따른 직기용 바디의 바디살의 구성을 나타내는 단면도이다. 이를 살펴보면, 본 발명의 바디살(10)은 비교적 길게 형성되는 것으로, 그 양단에는 바디프레임(도시하지 않음)에 지지되는 지지부(12)가 형성되어 있으며, 그 상면에는 원사와 마찰접촉하는 마찰접촉면(14)가 형성되어 있다. 이러한 바디살 (10)은 두께가 얇고 폭이 좁은 스테인레스강판으로 구성된다. 1 is a cross-sectional view showing the configuration of the body flesh of the loom body according to the invention. Looking at this, the body flesh 10 of the present invention is formed to be relatively long, both ends of the support portion 12 is supported on the body frame (not shown) is formed, the upper surface of the friction contact surface in friction contact with the yarn 14 is formed. The body flesh 10 is composed of a stainless steel sheet with a narrow thickness and narrow width.                     

한편, 바디살(10)의 마찰접촉면(14)에는 다이아몬드상 카본(diamond like carbon) 박막(20)이 코팅되어 있다. 다이아몬드상 카본 박막(20)은 잘 알려진 바와 같이 독특한 물성을 갖는 재료로서, 높은 경도를 가지면서도 표면 평활성과 자체 윤활성이 우수한 특성을 갖는다. 특히, 다이아몬드상 카본 박막(20)은 합성조건에 따라 흑연에 가까운 구조와 성질을 가져 낮은 마찰계수를 유지할 수 있을 뿐만 아니라 탄소결합의 화학적 안정성으로 인하여 산성물질을 포함한 각종 부식성물질에 대한 내식성을 갖추고 있다. On the other hand, a diamond-like carbon thin film 20 is coated on the frictional contact surface 14 of the body flesh 10. Diamond-like carbon thin film 20 is a material having a unique physical properties, as is well known, and has a high hardness, but also has excellent surface smoothness and self-lubricating properties. In particular, the diamond-like carbon thin film 20 has a structure and properties close to graphite, depending on the synthesis conditions can not only maintain a low coefficient of friction, but also due to the chemical stability of the carbon bonds have a corrosion resistance to various corrosive materials including acidic materials. have.

이와 같은 다이아몬드상 카본 박막(20)은 증착에 의한 방법으로 바디살(10)에 코팅되는데, 이때 다이아몬드상 카본 박막(20)은 대략 0.5㎛ 내지 10㎛정도의 두께로 코팅된다. 이러한 다이아몬드상 카본 박막(20)은 바디살(10)의 마찰접촉면 (14)에 높은 표면경도를 인가하여 내마모성을 증가시킴은 물론 평활성과 윤활성을 인가하여 낮은 마찰계수를 유지토록 함으로써 원사와 직접적인 접촉으로 인한 마모율을 최소화시킴과 아울러 원사의 손상을 방지하는 역할을 한다. 특히, 다이아몬드상 카본 박막(20)은 바디살(10)의 내식성을 증진시킴으로써 상기 바디살(10)이 쉽게 부식되지 않게 한다. The diamond-like carbon thin film 20 is coated on the body flesh 10 by the deposition method, wherein the diamond-like carbon thin film 20 is coated with a thickness of about 0.5㎛ 10㎛. The diamond-like carbon thin film 20 is directly in contact with the yarn by applying a high surface hardness to the frictional contact surface 14 of the body flesh 10 to increase the wear resistance as well as to maintain a low coefficient of friction by applying smoothness and lubricity. Minimizes the wear rate due to the damage and prevents damage to the yarn. In particular, the diamond-like carbon thin film 20 enhances the corrosion resistance of the body flesh 10 so that the body flesh 10 is not easily corroded.

결과적으로, 다이아몬드상 카본 박막(20)이 코팅된 바디살(10)은 우수한 내마모성과 높은 표면 평활성과 윤활성 그리고 내식성을 갖게 되어 그 수명이 연장될 수 있는 것이다. As a result, the body flesh 10 coated with the diamond-like carbon thin film 20 may have excellent wear resistance, high surface smoothness, lubricity, and corrosion resistance, thereby extending its lifespan.

이하에서는 이와 같은 구성을 갖는 바디살의 제조방법을 도 2를 참고로하여 상세하게 살펴보면 다음과 같다. 먼저, 본 발명의 제조방법은 바디살(10)을 제조하는 단계를 포함한다(S101). 물론, 바디살(10)에는 상면의 마찰접촉면(14)과 양단의 지지부(12)가 형성되어야 한다. 여기서, 바디살(10)은 마르텐사이트계 스테인레스강으로 이루어진다. Hereinafter, a method of manufacturing a body meat having such a configuration will be described in detail with reference to FIG. 2. First, the manufacturing method of the present invention includes the step of manufacturing the body flesh 10 (S101). Of course, the body flesh 10 should be formed with a frictional contact surface 14 of the upper surface and the support portion 12 of both ends. Here, the body flesh 10 is made of martensitic stainless steel.

그리고 바디살(10)을 제조하는 과정에서 바디살(10)의 표면은 각종 유기물과 먼지, 원자, 분자, 이온 등에 의해 오염될 수 있으므로 그 표면을 세정해 주어야만 하는데, 이때 상기 바디살(10)의 표면오염이 극소화될 수 있도록 1차(S103)와 2차 (S105)에 걸쳐 세정한다. 1차적인 세정(S103) 방법으로는 초음파세정을 이용한다. 초음파세정은 잘 알려진 바와 같이 세척액이 담겨 있는 세정조에 바디살(10)을 침지(浸漬)시키고, 침지된 바디살(10)에 초음파를 가하여 바디살(10)의 표면을 세정한다. 초음파세정에 대해서는 이미 공지된 것이므로 그에 대한 상세한 설명은 생략하기로 한다.In the process of manufacturing the body flesh 10, the surface of the body flesh 10 may be contaminated by various organic materials and dust, atoms, molecules, and ions, and thus the surface of the body flesh 10 should be cleaned. In this case, the body flesh 10 In order to minimize the surface contamination of the first (S103) and the second (S105) to wash over. Ultrasonic cleaning is used as the primary cleaning method (S103). As is well known, the ultrasonic cleaning is performed by immersing the body meat 10 in a cleaning tank containing a washing solution, and applying ultrasonic waves to the immersed body meat 10 to clean the surface of the body meat 10. Since ultrasonic cleaning is already known, a detailed description thereof will be omitted.

그리고 바디살(10)의 2차적인 세정(S105) 방법으로는 스퍼터링(sputtering)세정을 이용한다. 스퍼터링세정은 잘 알려진 바와 같이 진공조 내의 불활성 가스에 전압을 인가하여 플라즈마 상태로 만들고, 상기 플라즈마의 이온을 바디살(10)의 오염된 표면에 물리적으로 충돌시켜 표면 세정을 한다. 스퍼터링세정에 대해서는 이미 공지되어 있으므로 그에 대한 상세한 설명은 생략하기로 한다. 한편, 스퍼터링세정은 구동전압 -600Ｖ로 30분간 시행하며, 불활성 가스로는 아르곤(Ar)을 사용한다. And sputtering (sputtering) cleaning is used as a secondary cleaning method (S105) of the body flesh (10). As is well known, sputtering cleans a surface by applying a voltage to an inert gas in a vacuum chamber, and physically collides the ions of the plasma with the contaminated surface of the body flesh 10. Since sputtering cleaning is already known, a detailed description thereof will be omitted. On the other hand, sputtering cleaning is carried out for 30 minutes with a driving voltage of -600 kV, and argon (Ar) is used as an inert gas.

다음으로, 바디살(10)의 표면세정이 완료되면, 이어서 바디살(10)의 표면에 다이아몬드상 카본박막(20)을 코팅한다(S107). 다이아몬드상 카본박막(20)의 코팅 은 플라즈마 보강 기상증착(plasma enhanced CVD)에 의한 방법으로 시행한다. 플라즈마 보강 기상증착은 잘 알려진 바와 같이 진공조 내의 원료가스에 전압을 인가하여 플라즈마 상태로 만들고, 이온화된 원료가스들이 큰 에너지를 얻어 피처리물에 증착되는 방법으로서, 증착률이 좋고 두께가 균일한 박막(薄膜)을 얻을 수 있다는 장점을 갖는다. 특히, 플라즈마 보강 기상증착은 200℃이하에서의 저온 합성이 가능함에 따라 모재, 즉 바디살(10)의 연화를 방지하는 역할을 한다. 플라즈마 보강 기상증착법에 대해서는 이미 공지되어 있으므로 그에 대한 상세한 설명은 생략하기로 한다. Next, when the surface cleaning of the body flesh 10 is completed, the diamond-like carbon thin film 20 is then coated on the surface of the body flesh 10 (S107). Coating of the diamond-like carbon thin film 20 is carried out by a plasma enhanced CVD method. Plasma-reinforced vapor deposition is a method in which a plasma is applied by applying a voltage to a source gas in a vacuum chamber, and ionized source gases are deposited on an object by obtaining a large energy. The deposition rate is good and the thickness is uniform. It has the advantage that a thin film can be obtained. In particular, the plasma enhanced vapor deposition serves to prevent the softening of the base material, that is, the body flesh 10 as it is possible to synthesize a low temperature below 200 ℃. Since the plasma enhanced vapor deposition method is already known, a detailed description thereof will be omitted.

한편, 다이아몬드상 카본박막(20)을 코팅하기 위한 플라즈마 보강 기상증착은 메탄(CH4)을 원료가스로 하여 작동압력 200mTorr, 구동전압 -400Ｖ로 150분간 시행한다. 이는 구동전압이 -500Ｖ이상일 경우에는 플라즈마의 밀도가 높아짐에 따라 합성온도가 200℃이상이 되어 바디살(10)에 연화가 발생될 우려가 있기 때문이며, 구동전압이 -300Ｖ이하일 경우에는 박막의 합성속도가 현저히 감소되어 생산성이 낮아지기 때문이다. 아울러 다이아몬드상 카본박막(20)은 증착 시간에 따라 각기 다른 두께를 갖는 바, 증착 시간을 적절히 조절하여 박막(20)의 두께가 0.5㎛ 내지 10㎛범위가 되도록 증착한다. 0.5㎛ 내지 10㎛범위의 두께를 갖는 다이아몬드상 카본박막(20)은 최적의 부착력을 가지며 바디실(10)의 마찰접촉면(14)에 증착된다. Meanwhile, plasma-reinforced vapor deposition for coating the diamond-like carbon thin film 20 is performed for 150 minutes using methane (CH 4 ) as a working gas at an operating pressure of 200 mTorr and a driving voltage of -400 kPa. This is because when the driving voltage is higher than -500 mA, as the plasma density increases, the synthesis temperature may be 200 ° C. or higher, and softening may occur in the body flesh 10. This is because the speed is significantly reduced and productivity is lowered. In addition, since the diamond-like carbon thin film 20 has different thicknesses according to the deposition time, the deposition time is appropriately controlled so that the thickness of the thin film 20 is deposited to be in the range of 0.5 μm to 10 μm. The diamond-like carbon thin film 20 having a thickness in the range of 0.5 μm to 10 μm has an optimum adhesion and is deposited on the frictional contact surface 14 of the body seal 10.

증착결과에 의하면, 작동압력 200mTorr, 구동전압 -400Ｖ로 150분간 증착할 경우, 다이아몬드상 카본박막(20)이 대략 3㎛정도의 두께로 코팅되는 것으로 나타 났으며, 3㎛ 두께의 다이아몬드상 카본박막(20)을 갖는 바디살(10)은, 종래의 바디살보다 10배 이상의 내구성을 갖는 것으로 나타났다.According to the deposition results, when deposited for 150 minutes at an operating pressure of 200 mTorr and a driving voltage of -400 kPa, the diamond-like carbon thin film 20 was coated with a thickness of approximately 3 μm. The body flesh 10 having 20 has been shown to have 10 times or more durability than the conventional body flesh.

한편, 도 1과 도 2에 도시된 바와 같이 본 발명의 바디살 제조방법은 다이아몬드상 카본박막(20)을 바디살(10)에 코팅(S107)하기 전에, 상기 바디살(10)의 마찰접촉면(14)에 실리콘 박막(30)을 먼저 코팅하는 단계를 더 포함한다(S106). 이는 바디살(10)에 대한 다이아몬드상 카본박막(20)의 부착력을 높여주기 위한 것으로, 실레인(SiH4)가스와 수소가스가 2 : 8의 비율로 혼합된 혼합가스를 원료가스로하여 작동압력 200mTorr, 구동전압 -300Ｖ로 30분간 인가함으로써 실리콘 박막(30)을 대략 0.5㎛정도의 두께로 코팅한다. 이같은 실리콘 박막(30)은 바디살(10)에 대한 다이아몬드상 카본박막(20)의 부착력을 증가시켜줌에 따라 상기 바디살(10)로부터 다이아몬드상 카본박막(20)이 박리되는 것을 방지한다. Meanwhile, as shown in FIGS. 1 and 2, in the method of manufacturing the body flesh of the present invention, before the diamond-like carbon thin film 20 is coated on the body flesh 10 (S107), the frictional contact surface of the body flesh 10 is provided. (14) further comprises the step of first coating the silicon thin film 30 (S106). This is to increase the adhesion of the diamond-like carbon thin film 20 to the body flesh 10, the operating pressure 200mTorr using a mixed gas mixed with silane (SiH4) gas and hydrogen gas in a ratio of 2: 8 The silicon thin film 30 is coated to a thickness of about 0.5 μm by applying at a driving voltage of −300 mA for 30 minutes. Such silicon thin film 30 increases the adhesion of the diamond-like carbon thin film 20 to the body flesh 10 to prevent the diamond-like carbon thin film 20 from being peeled off from the body flesh 10.

실험결과에 의하면, 실리콘 박막(30)위에 코팅된 다이아몬드상 카본박막(20) 은 바디살(10)에 직접 코팅된 다이아몬드상 카본박막(20)보다 2배 이상의 부착력을 가지면서 상기 바디살(10)에 부착되는 것으로 나타났다. According to the test results, the diamond-like carbon thin film 20 coated on the silicon thin film 30 has an adhesive force more than twice that of the diamond-like carbon thin film 20 directly coated on the body flesh 10 and the body flesh 10 )).

다시, 도 2를 살펴보면, 바디살(10)의 표면에 다이아몬드상 카본박막(20)이 코팅되면, 최종적으로 바디살(10)을 가공 처리한다(S109). 바디살(10)의 가공 처리 단계(S109)는 다이아몬드상 카본박막(20)이 코팅된 바디살(10)의 외면을 가공 처리함으로써 정밀도를 높여 준다. Referring back to FIG. 2, when the diamond-like carbon thin film 20 is coated on the surface of the body flesh 10, the body flesh 10 is finally processed (S109). The processing step (S109) of the body flesh 10 increases the precision by processing the outer surface of the body flesh 10 coated with the diamond-like carbon thin film 20.

이상에서와 같이 여러 단계를 통하여 제조된 바디살(10)은 그 마찰접촉면 (14)에 다이아몬드상 카본박막(20)이 코팅되며, 이에 따라 상기 바디살(10)은 높은 내구성을 갖게 되어 그 수명이 연장된다. 특히, 다이아몬드상 카본박막(20)이 코팅되는 바디살(10)은 낮은 마찰계수를 갖게 됨에 따라 원사를 손상시키지 않으면서 가이드할 수 있게 되는 것이다. As described above, the body flesh 10 manufactured through the various steps is coated with the diamond-like carbon thin film 20 on the friction contact surface 14, and thus the body flesh 10 has high durability and its lifespan. This is extended. In particular, the body flesh 10 to which the diamond-like carbon thin film 20 is coated has a low coefficient of friction so that it can be guided without damaging the yarn.

이상에서는 본 발명의 바람직한 실시예를 예시적으로 설명하였으나, 본 발명의 범위는 이와 같은 특정 실시예에만 한정되는 것은 아니며, 특허청구범위에 기재된 범주내에서 적절하게 변경 가능한 것이다.Although the preferred embodiments of the present invention have been described above by way of example, the scope of the present invention is not limited to these specific embodiments, and may be appropriately changed within the scope of the claims.

이상에서 설명한 바와 같이 본 발명에 따른 직기용 바디의 바디살 제조방법은 바디살의 마찰접촉면에 다이아몬드상 카본박막을 코팅처리함으로써 높은 표면 경도를 갖게 되며, 따라서 원사와의 잦은 마찰접촉에도 쉽게 마모되지 않는다. 또한, 다이아몬드상 카본박막이 코팅된 바디살은 높은 평활성과 윤활성을 갖게 되며, 따라서 원사를 손상시키지 않으면서 안전하게 가이드 할 수 있게 된다. 아울러 다이아몬드상 카본박막은 플라즈마 보강 기상증착에 의한 방법으로 바디살에 코팅되며, 따라서 높은 부착력으로 바디살에 코팅되는 효과를 갖는다. As described above, the method of manufacturing the body flesh of the loom body according to the present invention has a high surface hardness by coating a diamond-like carbon thin film on the frictional contact surface of the body flesh, and thus does not easily wear even in frequent frictional contact with the yarn. . In addition, the body flesh coated with the diamond-like carbon thin film has high smoothness and lubricity, and thus can be safely guided without damaging the yarn. In addition, the diamond-like carbon thin film is coated on the body flesh by a plasma enhanced vapor deposition method, and thus has the effect of coating on the body flesh with high adhesion.

Claims (4)

삭제delete 원사를 정렬하고 눌러서 다져주는 직기용 바디의 바디살을 제조하는 방법에 있어서, In the method of manufacturing the body flesh of the loom body to align and press the chopped yarn, 마찰접촉면을 갖는 바디살을 제조하는 단계와;Manufacturing a body flesh having a frictional contact surface; 제조된 상기 바디살의 마찰접촉면을 세정하는 단계와;Cleaning the frictional contact surface of the manufactured body flesh; 세정된 상기 바디살의 마찰접촉면에 상기 바디살의 마찰접촉면에 실레인가스와 메탄가스가 2 : 8의 비율로 혼합된 혼합가스로 실리콘박막을 대략 0.5㎛정도의 두께로 코팅하는 단계;Coating a thin silicon film with a thickness of approximately 0.5 μm with a mixed gas in which a silane gas and methane gas are mixed in a ratio of 2: 8 to the frictional contact surface of the body flesh on the frictional contact surface of the body flesh; 상기 실리콘박막 위에 플라즈마 보강 기상증착에 의한 방법으로 0.5㎛ 내지 10㎛범위의 두께로 다이아몬드상 카본박막을 코팅하는 단계;를 포함하며, And coating a diamond-like carbon thin film on the silicon thin film in a thickness range of 0.5 μm to 10 μm by a plasma enhanced vapor deposition method. 상기 플라즈마 보강 기상증착은 구동전압이 -300Ｖ이상이고 합성온도가 200 이하인 조건으로 진행되는 것을 특징으로 하는 직기용 바디의 바디살 제조방법.The plasma-reinforced vapor deposition is a method of manufacturing a body meat of a loom body, characterized in that the drive voltage is -300Ｖ or more and the synthesis temperature is carried out under the condition of 200 or less. 제 2항에 있어서, 바디살을 세정하는 단계는, 상기 바디살을 1차로 세정하는 단계와 2차로 세정하는 단계로 구성되며, 상기 1차 세정은 초음파에 의한 방법으로 세정하며, 상기 2차 세정은 스퍼터링에 의한 방법으로 세정하고, 3. The method of claim 2, wherein the washing of the body flesh comprises: first washing the body flesh and second cleaning, wherein the first cleaning is performed by an ultrasonic method, and the second cleaning. Is cleaned by the method by sputtering, 상기 스퍼터링은 구동전압 -600Ｖ로 30분간 시행하며, 불활성 가스로는 아르곤(Ar)을 사용하는 것을 특징으로 하는 직기용 바디의 바디살 제조방법.The sputtering is carried out for 30 minutes at a driving voltage of -600 kW, and the method of manufacturing a body meat of a body for a loom, characterized in that argon (Ar) is used as an inert gas. 삭제delete
KR1020020071176A 2002-11-15 2002-11-15 Reed manufacturing method in loom KR100895061B1 (en)