KR100772483B1 - Block with water permeability and method of fabrication thereof - Google Patents

Block with water permeability and method of fabrication thereof Download PDF

Info

Publication number
KR100772483B1
KR100772483B1 KR1020070081367A KR20070081367A KR100772483B1 KR 100772483 B1 KR100772483 B1 KR 100772483B1 KR 1020070081367 A KR1020070081367 A KR 1020070081367A KR 20070081367 A KR20070081367 A KR 20070081367A KR 100772483 B1 KR100772483 B1 KR 100772483B1
Authority
KR
South Korea
Prior art keywords
water
permeable block
block
glass powder
weight
Prior art date
Application number
KR1020070081367A
Other languages
Korean (ko)
Inventor
한성필
조청휘
Original Assignee
한림로덱스(주)
한림에코텍 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한림로덱스(주), 한림에코텍 주식회사 filed Critical 한림로덱스(주)
Priority to KR1020070081367A priority Critical patent/KR100772483B1/en
Application granted granted Critical
Publication of KR100772483B1 publication Critical patent/KR100772483B1/en

Abstract

A permeable block and a method of manufacturing the same are provided to preclude the permeable block from being expanded due to a gelation reaction between silica in glass powder and alkali in cement by using a lithium composition, thereby increasing the use of the glass material such as wasted glass. A permeable block includes cement, glass powder, and aggregate. The block includes a lithium composition having LiNO2, LiNO3, and LiOH. The lithium composition includes 1:0.01:0.01 to 1:0.1:0.1 parts by weight of LiNO2, LiNO3, and LiOH. The permeable block is formed with a passivating film of insolubilized LiO2 and SiO2 on the surface of the glass powder. The block includes 150 to 300 parts by weight of glass powder, 40 to 60 parts by weight of aggregate, and 1 to 30 parts by weight of lithium composition for the 100 parts by weight of cement.

Description

투수성 블록 및 이의 제조방법{BLOCK WITH WATER PERMEABILITY AND METHOD OF FABRICATION THEREOF}Permeable block and its manufacturing method {BLOCK WITH WATER PERMEABILITY AND METHOD OF FABRICATION THEREOF}

본 발명은 투수성 블록 및 이의 제조방법에 관한 것으로, 더욱 상세하게는 종래 유리 분말을 사용하는 투수성 블록에서 유리 분말 내 실리카와 시멘트 내 알칼리의 겔화 반응에 의해 블록이 팽창되는 문제를 해소하며 회전 교반에 의해 모서리 부분이 완전히 제거된 것을 사용하여 폐유리의 사용량을 증가시키고, 외관 및 야간 시인성이 개선함에 따라 보도, 자전거 도로, 건축물 주변, 산책로, 주차장, 소형차도, 인테리어 구조물 장식용 등 다양한 분야에 적용 가능한 투수성 블록 및 이의 제조방법에 관한 것이다.The present invention relates to a water-permeable block and a method for manufacturing the same, and more particularly, in a water-permeable block using a conventional glass powder, the block is expanded by solving a gel expansion reaction of silica in a glass powder and alkali in a cement. The use of completely removed edges by agitation increases the use of waste glass and improves the appearance and visibility at night, and is therefore suitable for various fields such as sidewalks, bicycle paths, surrounding buildings, walkways, parking lots, small driveways, and interior structures. Applicable permeable block and method for manufacturing the same.

보도나 산책로에 시공된 투수성 블록은 골재와 골재 사이의 공극(void)이 있어 비 등에 의한 물을 지반으로 투수시켜 보도나 산책로 또는 도시 하천 등에 물이 유입되는 것을 지연 또는 방지한다.The permeable block constructed on the sidewalk or walkway has a void between the aggregate and the aggregate to permeate water due to rain and so on to delay or prevent water from entering the sidewalk, the walkway or urban rivers.

투수성 블록은 시멘트 및 골재를 혼합하여 사용하고, 상기 기본 성분에 필요에 따라 블록을 다층으로 형성하는 방법, 콘크리트 블록을 표면 처리하는 방법, 다공성 콘크리트 블록의 제조, 세라믹 입자 등의 무기물을 첨가, 폐타이어칩 첨가, 유리 섬유 보강재 첨가, 에폭시 등의 폴리머 수지를 첨가하는 등 다양한 방법이 사용되고 있다.The water-permeable block is used by mixing cement and aggregate, the method of forming a multi-layer block as needed, the method of surface treatment of concrete blocks, the production of porous concrete blocks, addition of inorganic materials such as ceramic particles, Various methods are used, such as waste tire chip addition, glass fiber reinforcement material addition, and polymer resins such as epoxy.

한국 공개특허 제93-23423호, 한국 공개특허 제94-6738호는 투수성 블록에 탄성을 부여하여 장시간 걷더라도 피곤하지 않도록, 폐타이어칩 또는 폐고무칩 등을 첨가하여 투수성 블록을 제조하는 방법이 제안되었다. Korean Patent Publication No. 93-23423 and Korean Patent Publication No. 94-6738 provide elasticity to a permeable block so as not to be tired even when walking for a long time, to manufacture a permeable block by adding waste tire chips or waste rubber chips. The method has been proposed.

한국 공개실용신안 제98-65372호는 고경도의 상층부와 저경도의 하층부를 갖는 2층 단면 구조를 가지며, 하층부의 저면에 소형 돌기가 형성된 탄성 블록을 제안하고 있다.Korean Utility Model Publication No. 98-65372 has a two-layered cross-sectional structure having a high hardness upper layer and a low hardness lower layer, and proposes an elastic block having a small protrusion on the bottom of the lower layer.

그러나 투수성 블록은 주위 환경에 의해 쉽게 마모 및 변형될 뿐만 아니라 그 재질적인 특성으로 인해 알칼리성 조건 하에서 불안정한 문제가 발생하였다. 즉, 비 등에 의해 투수성 블록 내부로 물이 확산되는 경우 쉽게 팽창되어 개보수가 요구된다.However, the permeable block is not only easily worn and deformed by the surrounding environment but also has an unstable problem under alkaline conditions due to its material properties. That is, when water is diffused into the water permeable block due to rain or the like, it is easily expanded and requires renovation.

한편 투수성 블록의 외관성과 야간 시인성을 개선하기 위해 폐유리를 사용하고 있다.Meanwhile, waste glass is used to improve the appearance and visibility of the permeable block.

특히 투수성 블록의 재질로 사용하는 시멘트와 유리 간의 알칼리-실리카 반응에 의해 시멘트의 팽창에 의해 투수성 블록의 균열이 발생하였다. 상기 알칼리-실리카 반응은 수년간에 걸쳐 서서히 일어나고, 결국 도로나 산책로 등은 몇 년에 한 번씩의 전면적인 보수가 요구되었다.Particularly, cracks in the water-permeable block occurred due to the expansion of the cement due to the alkali-silica reaction between the cement and the glass used as the material of the water-permeable block. The alkali-silica reaction occurs slowly over the years, and eventually roads, trails, and the like require a full refurbishment every few years.

이에 알칼리-실리카 반응을 억제하도록, 저알칼리 시멘트가 제안되었으나 이는 비용 상승이라는 또 다른 문제를 가져왔다. In order to suppress the alkali-silica reaction, low alkali cements have been proposed, but this brings another problem of increased cost.

또한 알칼리-실리카 반응을 고려하여 골재의 약 10% 정도를 폐유리로 치환시켜 사용하여 있으나, 이 경우 투수성 블록의 외관과 시인성이 크게 개선되지 못하고 있다. In addition, in consideration of the alkali-silica reaction, about 10% of the aggregate is replaced with waste glass, but in this case, the appearance and visibility of the permeable block are not significantly improved.

알칼리-실리카 반응은 수분의 영향을 크게 받는데, 특히 시멘트 내부의 비표면적이 크고 물과 접하기 쉬운 투수성 블록의 경우 알칼리-실리카 반응이 일반 블록에 비해 더욱 쉽게 발생하기 때문에 유리 골재의 사용이 불가능하다.Alkali-silica reaction is highly influenced by water, especially in the case of permeable blocks with large specific surface inside cement and easy to contact with water, it is impossible to use glass aggregate because alkali-silica reaction occurs more easily than general blocks. Do.

한국 공개특허 제2006-93562호는 투수성 블록의 변형을 방지하기 위해 플라이 애쉬, 실리카 퓸, CSA(Calsium Sulfate Aluminum)계 팽창재 및 글리콜계 수축저감제를 소정의 혼합 비율로 혼합함으로써, 수화열을 감소시키고, 강도를 증진하여 투수성 블록의 수축 균열과 같은 변형이 저감되는 효과를 얻고 있다고 언급하고 있다.Korean Patent Laid-Open Publication No. 2006-93562 discloses a method of reducing heat of hydration by mixing fly ash, silica fume, Calsium Sulfate Aluminum (CSA) -based expander and glycol-based shrinkage reducing agent at a predetermined mixing ratio to prevent deformation of the permeable block. It is mentioned that the effect of reducing deformation such as shrinkage cracking of the permeable block is reduced by increasing the strength.

한국특허출원 제2007-20382호는 콘크리트에 콜로이드 실리카 수용액, 질산염, 알루미늄염, 지방족계 고분자 화합물의 내염해성 증진제를 사용하여 투수성 블록의 내염해성을 향상시킨다고 언급하고 있다.Korean Patent Application No. 2007-20382 mentions the use of colloidal silica aqueous solution, nitrate, aluminum salt and salt resistance enhancer of aliphatic polymer compound in concrete to improve salt resistance of permeable block.

상기 특허와 같이 투수성 블록의 수축 또는 팽창과 같은 변형을 방지하기 위해 여러 가지 첨가제를 사용함에 따라 비용이 상승하고, 공정이 복잡해지는 문제가 수반되었다.As described above, the use of various additives to prevent deformation such as shrinkage or expansion of the permeable block has caused a problem of increased cost and complicated process.

한편 투수성 블록의 원료로 맥주병, 유리창 등과 같은 폐유리를 사용하는 경우 파쇄기로 파쇄하여 '카렛트'라고 하는 유리 조각 형태로 사용하고 있다. 상기 카렛트는 모서리 부분이 매우 뾰족하고 날카로워 작업하기에 주의가 요구된다. 또 한 폐유리의 경우 재활용을 위해서 색, 품종의 선별 공정이 우선적으로 이루어지고 있어, 라벨 제거나 세척과 같은 공정을 거친 후 재활용 수 있기 때문에 카렛트의 가격이 유리 원자재와 비교하여 가격은 고가이고 품질이 낮은 단점이 있다.Meanwhile, in the case of using waste glass such as beer bottles and glass windows as raw materials of the permeable block, the glass is crushed by a crusher and used in the form of a piece of glass called 'carlet'. The caret is very sharp at the corners and needs attention to work sharply. In the case of waste glass, the sorting process of color and varieties is preferentially performed for recycling, and since it can be recycled after a process such as label removal or cleaning, the price of the carpet is higher than that of glass raw materials. The disadvantage is low quality.

최근에 새로운 재활용 기술로 유리 제품 이외의 용도에 도로의 포장용, 콘크리트의 골재, 보드의 재료 등에 카렛트를 사용하는 연구가 폭넓게 행해지고 있다. 그러나 일반적인 파쇄기의 이용만으로는 카렛트의 모서리의 제거가 불가능하여 그 활용 범위를 넓히고 있지 못하다.In recent years, research has been widely conducted on the use of carpets for paving of roads, aggregates of concrete, board materials and the like for applications other than glass products with new recycling technologies. However, it is not possible to remove the edges of the carpet by using a general crusher alone, and thus does not expand the scope of its use.

본 발명의 목적은 리튬 화합물을 사용하여 유리 분말을 사용하는 투수성 블록에서 유리 분말 내 실리카와 시멘트 내 알칼리의 겔화 반응에 의해 블록이 팽창되는 문제를 해소할 수 있을 뿐만 아니라, 폐유리와 같은 유리 재질의 사용량을 크게 증가시키고, 블록의 외관과 시인성을 향상시킬 수 있는 투수성 블록 및 이의 제조방법을 제공하는 것이다.The object of the present invention is not only to solve the problem of block expansion by gelation reaction of silica in glass powder and alkali in cement in permeable block using glass powder using lithium compound, but also glass such as waste glass. It is to provide a water-permeable block and a method of manufacturing the same that can significantly increase the amount of material used, and improve the appearance and visibility of the block.

본 발명은 시멘트, 유리 분말 및 골재를 포함하는 투수성 블록에서, The present invention is a permeable block comprising cement, glass powder and aggregate,

아초산리튬(LiNO2), 초산리튬(LiNO3), 및 수산화리튬(LiOH)이 함유된 리튬 화합물을 포함하는 투수성 블록을 제공한다.A water permeable block including a lithium compound containing lithium acetate (LiNO 2 ), lithium acetate (LiNO 3 ), and lithium hydroxide (LiOH) is provided.

상기 리튬 화합물은 아초산 리튬: 초산리튬: 수산화리튬을 1:0.01:0.01 ∼ 1:0.1:0.1의 중량비로 포함한다.The lithium compound includes lithium acetate: lithium acetate: lithium hydroxide in a weight ratio of 1: 0.01: 0.01 to 1: 0.1: 0.1.

상기 투수성 블록은 유리 분말의 표면에 불용화된 Li2Ox·SiO2(1≤x≤4)의 부동태 피막을 형성한다.The water-permeable block forms a passivation film of Li 2 O x .SiO 2 (1≤x≤4) on the surface of the glass powder.

상기 투수성 블록은 시멘트 100 중량부에 대해 유리 분말 150∼300 중량부, 골재 40∼60 중량부, 및 리튬 화합물 1∼30 중량부를 포함한다.The water permeable block includes 150 to 300 parts by weight of glass powder, 40 to 60 parts by weight of aggregate, and 1 to 30 parts by weight of lithium compound, based on 100 parts by weight of cement.

또한 본 발명은 In addition, the present invention

a) 시멘트, 유리 분말, 골재 및 물을 혼합하여 혼합물을 제조하는 단계,a) mixing cement, glass powder, aggregate and water to prepare a mixture,

b) 상기 혼합물에 아초산리튬, 초산리튬, 및 수산화리튬이 함유된 리튬 화합물을 포함하는 수용액을 첨가하는 단계,b) adding an aqueous solution containing a lithium compound containing lithium acetate, lithium acetate, and lithium hydroxide to the mixture,

c) 상기 얻어진 혼합물을 성형하여 성형 블록을 제조하는 단계, 및c) molding the obtained mixture to prepare a forming block, and

d) 상기 얻어진 성형 블록은 양생 및 연마하는 단계d) curing and polishing the obtained molding block

를 포함하는 투수성 블록의 제조방법을 제공한다. It provides a method of manufacturing a water-permeable block comprising a.

바람직하기로 상기 유리 분말은 유리 또는 폐유리 원료(카렛트)를 물과 함께 회전 드럼기에 주입하고 회전 교반에 의해 파쇄된 것을 사용한다.Preferably, the glass powder is used to inject glass or waste glass raw material (cart) with water into a rotating drum and crushed by rotary stirring.

본 발명에 따른 투수성 블록은 리튬 화합물에 의해 부동태 피막을 형성하여, 종래 유리 분말을 사용하는 투수성 블록에서 유리 분말 내 실리카와 시멘트 내 알칼리의 겔화 반응에 의해 블록이 팽창되는 문제를 해소하며 폐유리를 사용량을 증가시켜 외관 및 야간 시인성이 개선함에 따라 보도, 자전거 도로, 건축물 주변, 산 책로, 주차장, 소형차도, 인테리어 구조물 장식용 등 다양한 분야에 바람직하게 적용된다.The water-permeable block according to the present invention forms a passive film by the lithium compound, thereby eliminating the problem that the block is expanded by the gelation reaction of silica in the glass powder and alkali in the cement in the water-permeable block using the conventional glass powder, As the use of glass is increased to improve appearance and night visibility, it is preferably applied to various fields such as sidewalks, bicycle paths, buildings, walkways, parking lots, small roadways, and interior structures.

또한 원료로 사용되는 유리 분말로 폐유리의 사용이 가능하여 자원 재활용이 가능해진다. 이러한 폐유리는 회전 교반에 의해 파쇄하여 유리 분말의 모서리를 완전히 제거할 수 있고, 유리 분말 원료로서 유색 유리의 사용이 가능해진다.In addition, the use of waste glass as a glass powder used as a raw material can be recycled resources. Such waste glass can be crushed by rotary stirring to completely remove the edges of the glass powder, and the use of colored glass can be used as the glass powder raw material.

투수성 블록의 경우 시멘트, 유리 분말 및 골재를 사용하고 있으며, 필요한 경우 여러 가지 첨가제를 사용하여 제조하고 있다. 그러나 시멘트와 유리 분말을 사용하는 경우 투수성 블록에 균열이 발생한다.For permeable blocks, cement, glass powder and aggregate are used, and if necessary, various additives are used. However, when cement and glass powder are used, cracks occur in the permeable block.

도 1은 종래 투수성 블록 내 부동태 피막 형성을 보여주는 모식도이다. 도 1에 나타낸 바와 같이 시멘트의 알칼리 성분과 유리 분말의 실리카와의 반응하여 겔을 형성하고, 상기 겔이 흡수 팽창하여 결과적으로 투수성 블록에 균열을 발생시킨다.1 is a schematic diagram showing the formation of a passive film in a conventional permeable block. As shown in Fig. 1, the alkali component of the cement reacts with the silica of the glass powder to form a gel, and the gel absorbs and expands, resulting in cracking of the permeable block.

본 발명에 따른 투수성 블록은 시멘트, 유리 분말 및 골재를 포함하는 투수성 블록에 리튬 화합물을 사용한다. 상기 리튬 화합물을 사용함에 따라 실리카(SiO2)가 주성분인 유리 분말의 표면에 불용화된 Li2Ox·SiO2(1≤x≤4)의 부동태 피막을 형성한다. The water permeable block according to the present invention uses a lithium compound in the water permeable block including cement, glass powder and aggregate. By using the lithium compound, a passivation film of Li 2 O x .SiO 2 (1 ≦ x ≦ 4) is formed on the surface of the glass powder containing silica (SiO 2 ) as a main component.

도 2는 본 발명에 따른 투수성 블록 내 부동태 피막 형성을 보여주는 모식도이다. Figure 2 is a schematic diagram showing the formation of a passive film in a permeable block according to the present invention.

도 2를 참조하면, 투수성 블록 내 함유된 리튬에 의해 유리 분말의 표면에 형성된 부동태 피막이 형성되고, 상기 부동태 피막에 의해 상기 실리카와 시멘트 내 함유된 알칼리 성분인 K, Na 등과 반응이 원천적으로 차단됨을 알 수 있다.Referring to FIG. 2, a passivation film formed on the surface of the glass powder is formed by lithium contained in the permeable block, and the passivation film fundamentally blocks the reaction of K and Na, which are alkali components contained in the silica and cement. It can be seen.

또한 비나 눈에 의해 투수성 블록이 수분에 노출되는 경우 수분을 흡수하여 투수성 블록이 팽창되지 않고, 상기 부동태 피막에 의해 수분이 그대로 투과하여 투수성이 우수한 효과가 있다.In addition, when the water-permeable block is exposed to water by rain or snow, the water-absorbing block does not expand and water is permeated by the passivation film.

상기 리튬 화합물은 시멘트 100 중량부에 대해 1∼30 중량부, 바람직하기로, 2∼15 중량부가 되도록 한다. 만약, 리튬 화합물의 함량이 상기 범위 미만이면 전술한 바의 효과를 얻기 어렵고, 이와 반대로 상기 범위를 초과하는 경우 효과상의 큰 상승 효과가 없어 비경제적이므로, 상기 범위 내에서 적절히 사용한다.The lithium compound is 1 to 30 parts by weight, preferably 2 to 15 parts by weight based on 100 parts by weight of cement. If the content of the lithium compound is less than the above range, it is difficult to obtain the above-described effects. On the contrary, if the content of the lithium compound exceeds the above range, there is no significant synergistic effect, and thus it is uneconomical.

이때 리튬 화합물은 아초산리튬(LiNO2), 초산리튬(LiNO3), 및 수산화리튬(LiOH)이 함유된 것을 사용하며, 바람직하기로 아초산 리튬: 초산리튬: 수산화리튬을 1:0.01:0.01 ∼1:0.1:0.1의 중량비로 포함한다. 이러한 리튬 화합물의 조성은 유리 분말 주위에 부동태 피막을 충분히 형성할 수 있음을 고려하여 얻어진 수치로, 상기 범위를 벗어난 리튬 화합물을 사용하게 되면 전술한 바의 효과를 얻기 어렵다.In this case, the lithium compound contains lithium acetate (LiNO 2 ), lithium acetate (LiNO 3 ), and lithium hydroxide (LiOH). Preferably, the lithium acetate: lithium acetate: lithium hydroxide is 1: 0.01: 0.01. It includes in a weight ratio of -1: 0.1: 0.1. The composition of the lithium compound is a value obtained in consideration of being able to sufficiently form a passivation film around the glass powder, and when the lithium compound outside the above range is used, it is difficult to obtain the effects described above.

상기 리튬 화합물 외에 본 발명에 따른 투수성 블록은 시멘트, 유리 분말 및 골재를 포함한다.In addition to the lithium compound, the water-permeable block according to the present invention includes cement, glass powder, and aggregate.

상기 시멘트는 고로슬래그 시멘트, 초조강 시멘트, 백시멘트, 포틀랜드 시멘 트, 조강 시멘트, 속경 시멘트, 및 이들의 혼합물로 이루어진 군에서 선택된 1종이 가능하다.The cement may be one selected from the group consisting of blast furnace slag cement, rough steel cement, back cement, Portland cement, crude steel cement, fast cement, and mixtures thereof.

유리 분말은 시멘트나 골재와 혼합을 용이하게 할 수 있도록 입자 크기를 조절하여 사용하는 것이 바람직하다. 구체적으로, 상기 유리 분말은 입자 크기가 ㎛ 수준인 미세한 입자에서부터 mm 수준의 거대 입자를 혼합하여 사용하고, 바람직하기로 200 ㎛∼15 mm, 더욱 바람직하기로 2.5 mm∼10 mm인 것을 이용한다.The glass powder is preferably used by adjusting the particle size to facilitate mixing with the cement or aggregate. Specifically, the glass powder is used by mixing a large particle of the mm level from the fine particles having a particle size of the micrometer level, preferably 200 ㎛ to 15 mm, more preferably 2.5 mm to 10 mm.

상기 유리 분말은 공지된 방법에 의해 분쇄를 통해 분쇄하여 사용하거나 시판되는 것을 구입하여 사용하며, 비용 저감을 위해 폐유리를 재활용한 것을 사용한다.The glass powder is used by pulverizing through a known method or a commercially available one, and recycled waste glass for cost reduction.

상기 폐유리를 재활용한 유리 분말로는 카렛트(파쇄된 폐유리)를 회전 교반기에 물과 함께 주입하여 상기 카렛트의 모서리를 완전히 제거한다.As the glass powder which recycled the waste glass, a carpet (crushed waste glass) is injected into a rotary stirrer together with water to completely remove the edge of the carpet.

상기 회전 교반기는 그 구조를 본 발명에서 특별히 한정하지 않으며, 일예로 다수의 교반 날개가 구비된 회전 드럼 형태의 교반기를 사용한다. 이때 회전 교반기의 작동에 의해 카렛트가 위 아래로 회전되며, 교반 날개에 충돌이 되고 마찰이 일어나 카렛트의 모서리 부분을 마모시켜 둥글게 만들어 준다.The rotary stirrer is not particularly limited in the structure of the present invention, for example, using a stirrer in the form of a rotating drum provided with a plurality of stirring blades. At this time, the carette is rotated up and down by the operation of the rotary stirrer, and the collision to the stirring blades and friction occurs to wear the corner portion of the carette to make it round.

상기 회전 교반기의 일측에 배수구를 설치하여 회전 교반시 사용된 물을 제거하고, 상기 물의 제거와 함께 카렛트에 부착된 종이 라벨지 등이 제거 및 배출된다.By installing a drain on one side of the rotary stirrer to remove the water used during the rotary stirring, and with the removal of the water, the paper label attached to the carpet is removed and discharged.

그 결과 유리 분말의 원료로 사용되는 카렛트의 모서리를 완전히 제거할 수 있어 작업성을 높인다. 또한 유리 분말 원료의 활용 범위가 높아져 유색 유리의 사용이 가능해진다.As a result, the edge of the carpet used as a raw material of glass powder can be removed completely, and workability is improved. Moreover, the utilization range of a glass powder raw material becomes high, and it becomes possible to use colored glass.

특히 본 발명에 따른 투수성 블록 제조시 상기 물의 배출 후 회전 교반기에 시멘트, 골재 및 리튬 화합물을 첨가하여 제조할 수 있어, 투수성 블록의 제조를 위해 별도의 장치 사용이 불필요해진다.In particular, when manufacturing the water-permeable block according to the present invention can be prepared by adding cement, aggregate and lithium compound to the rotary stirrer after the discharge of the water, it is unnecessary to use a separate device for the production of the water-permeable block.

바람직하기로, 본 발명에서는 유리 분말을 시멘트 100 중량부에 대해 150∼300 중량부, 바람직하기로 200∼280 중량부의 범위로 사용한다. 만약 유리 분말의 함량이 상기 범위를 벗어나게 되면 투수성 블록의 물성 등이 저하될 우려가 있으므로, 상기 범위 내에서 적절히 사용한다.Preferably, in the present invention, the glass powder is used in the range of 150 to 300 parts by weight, preferably 200 to 280 parts by weight based on 100 parts by weight of cement. If the content of the glass powder is out of the above range, there is a possibility that the physical properties of the water permeable block, etc. may be lowered, so that it is suitably used within the above range.

상기 골재는 파쇄석, 자갈, 모래, 쇄석 골재, 제강 슬래그 골재, 폐콘크리트 골재, 백운석 골재, 바텀 애쉬 골재, 및 이들의 혼합물로 이루어진 군에서 선택된 1종이 가능하다.The aggregate may be one selected from the group consisting of crushed stone, gravel, sand, crushed aggregate, steelmaking slag aggregate, waste concrete aggregate, dolomite aggregate, bottom ash aggregate, and mixtures thereof.

상기 골재의 혼합 사용은 골재의 재활용 측면과 제품 표면 연마시의 골재 단면 색상, 질감 등의 효과를 고려하여 선별한다. 일예로 연마 후 폐유리 골재는 백색, 청색, 갈색, 또는 혼합색을, 백운석 골재는 백색, 적색 또는 회색을, 바텀 애쉬 골재는 흑색, 또는 회색 등의 색상을 나타낸다.The mixed use of the aggregate is selected in consideration of the effects of the recycled side of the aggregate and the aggregate cross-section color, texture, etc. when polishing the surface of the product. For example, after grinding, the waste glass aggregate has a color of white, blue, brown, or mixed color, the dolomite aggregate has a color of white, red or gray, and the bottom ash aggregate has a color of black, or gray.

또한 상기 골재는 입도가 2∼15 mm, 바람직하기로 2∼7 mm 및 7∼15 mm의 서로 다른 크기를 가진 것을 혼합하여 사용함으로써, 투수성 블록에 충분한 공극과 강도를 부여한다. 또한 식물을 식생하는 경우 식물의 뿌리가 완성된 다공성 콘크리트 블록의 공극 사이를 통과하여 블록 하부의 토양속으로 용이하게 정착될 수 있다. In addition, the aggregate is used by mixing a particle having a different size of 2 to 15 mm, preferably 2 to 7 mm and 7 to 15 mm, thereby imparting sufficient voids and strength to the permeable block. In addition, when vegetation is planted, the roots of the plant can be easily settled into the soil beneath the block by passing between the pores of the completed porous concrete block.

이러한 골재와 시멘트는 투수성 블록이 하천의 호안 등 물가에 시공될 경우 폭우나 급류로 인하여 떠내려가지 않게 일정한 중량을 유지할 수 있도록, 콘크리트 블록의 공극률, 중량, 압축감 등을 고려하여 함량을 선정한다.These aggregates and cements are selected in consideration of the porosity, weight, and compression of the concrete block so that the permeable block can be maintained at a constant weight so as not to be floated due to heavy rain or rapids when it is installed on the shore, such as a river shore. .

본 발명에 따른 투수성 블록에서는 상기 골재를 시멘트 100 중량부에 대해 80∼200 중량부, 바람직하기로 100∼150 중량부의 범위로 사용한다. 만약 골재의 함량이 상기 범위를 벗어나게 되면 투수성 블록의 물성 등이 저하될 우려가 있으므로, 상기 범위 내에서 적절히 사용한다.In the permeable block according to the present invention, the aggregate is used in the range of 80 to 200 parts by weight, preferably 100 to 150 parts by weight, based on 100 parts by weight of cement. If the content of the aggregate is out of the above range because the physical properties of the water-permeable block may be lowered, it is appropriately used within the above range.

이때 추가로 필요에 따라 혼화제, 무기 안료, 감수제, 보강제 등의 각종 첨가제를 사용한다. At this time, if necessary, various additives such as admixtures, inorganic pigments, water reducing agents, and reinforcing agents are used.

상기 무기 안료는 심미적 효과를 부여하기 위한 것으로, 산화크롬, 산화철, 적산화철, 이산화티탄 및 이들의 혼합물이 가능하다. 상기 감수제는 발포성이 현저한 계면활성제로서 콘크리트 중에 미소한 독립된 기포를 고르게 발생시켜 블록의 내동결융해성, 내식성 등 내구성을 개선시킨다. 상기 보강제는 투수성 블록의 강도를 높이기 위한 것으로, 무기계 섬유, 유기계 섬유, 스크랩, 고탄력 고무강섬유, 유리섬유, 탄소섬유 등이 있고 유기계 섬유의 종류로는 아라미드섬유, 폴리프로필렌섬유, 비닐론섬유, 나일론 등이 사용된다. 또한 투수성 블록 내 알칼리 이온을 흡착하여 유리 분말 내 실리카와 시멘트 내 알칼리의 겔화 반응을 차단하여 리튬 화합물 첨가에 따른 효과를 보다 증가시킬 수 있도록 흡착제가 사용될 수 있으며, 이러한 흡착제로는 제올라이트가 가능하다. 이러한 첨가제의 함량은 통상적으로 사용되는 범위 내에서 사용되며, 일예로 시멘트 100 중량부에 대해 1∼5 중량부 내 외로 사용한다.The inorganic pigment is for imparting an aesthetic effect, and chromium oxide, iron oxide, red iron oxide, titanium dioxide, and mixtures thereof are possible. The water reducing agent is a surfactant having a remarkable foaming property to evenly generate minute independent bubbles in concrete to improve durability such as freeze-melting resistance and corrosion resistance of the block. The reinforcing agent is to increase the strength of the water-permeable block, and include inorganic fibers, organic fibers, scrap, high elastic rubber steel fibers, glass fibers, carbon fibers, and the like, aramid fibers, polypropylene fibers, vinylon fibers, nylon Etc. are used. In addition, an adsorbent may be used to adsorb the alkali ions in the permeable block to block the gelation reaction of silica in the glass powder and the alkali in the cement to increase the effect of the addition of the lithium compound. Zeolite may be used as such an adsorbent. . The content of such an additive is used within a range generally used, for example, 1 to 5 parts by weight based on 100 parts by weight of cement.

상기한 바의 투수성 블록은 The permeable block as described above

a) 시멘트, 유리 분말, 골재 및 물을 혼합하여 혼합물을 제조하는 단계,a) mixing cement, glass powder, aggregate and water to prepare a mixture,

b) 상기 혼합물에 아초산리튬, 초산리튬, 및 수산화리튬이 함유된 리튬 화합물을 포함하는 수용액을 첨가하는 단계,b) adding an aqueous solution containing a lithium compound containing lithium acetate, lithium acetate, and lithium hydroxide to the mixture,

c) 상기 얻어진 혼합물을 성형하여 성형 블록을 제조하는 단계, 및c) molding the obtained mixture to prepare a forming block, and

d) 상기 얻어진 성형 블록은 양생 및 연마하는 단계를 거쳐 제조된다.d) The obtained molding block is manufactured through curing and polishing.

먼저, 투수성 블록을 제조하기 위해 시멘트, 유리 분말, 골재 및 물을 각각 측량하여 혼합기에 투입하여 균일하게 혼합한다(단계 a).First, in order to produce a permeable block, cement, glass powder, aggregate, and water are respectively measured and added to the mixer and mixed uniformly (step a).

상기 혼합기는 통상적으로 사용되는 장치가 가능하며, 바람직하기로 교반 날개가 장착된 회전 교반기를 사용한다.The mixer can be a conventionally used device, preferably using a rotary stirrer equipped with stirring vanes.

바람직하기로, 상기 a) 단계 이전에 유리 분말을 제조하기 위해 카렛트를 회전 교반기에 물과 함께 주입한 후, 교반하여 카렛트의 모서리를 완전히 제거한다. 이후 회전 교반기 내 물을 배출한 후, 여기에 시멘트, 골재 및 물을 주입하여 단계 a)의 혼합물을 제조한다.Preferably, prior to step a), the carette is injected with water into a rotary stirrer to prepare the glass powder, followed by stirring to completely remove the edges of the carette. After discharging the water in the rotary stirrer, cement, aggregate and water are injected thereinto prepare a mixture of step a).

다음으로, 상기 혼합기에 리튬 화합물을 측량하여 첨가한 다음 균일하게 혼합한다(단계 b).Next, the lithium compound is measured and added to the mixer and then mixed uniformly (step b).

상기 첨가된 리튬 화합물은 수분산된 형태로 사용하며, 15∼30 중량%의 농도로 제조하여 사용한다. 이러한 리튬 화합물은 유리 분말의 표면에 형성된 부동태 피막을 형성한다.The added lithium compound is used in the form of water dispersion, prepared in a concentration of 15 to 30% by weight. This lithium compound forms a passivation film formed on the surface of the glass powder.

다음으로, 상기에서 얻어진 혼합물을 성형기에 투입하여 성형하여 성형 블록을 제조한다(단계 c).Next, the mixture obtained above is introduced into a molding machine and molded to prepare a molding block (step c).

이때, 상기 블록의 두께는 필요에 따라 적절하게 결정될 수 있는 것이므로 특별히 한정되지 않으며, 일예로 한국공업규격(KS)의 보차도용 블록의 기준에 따르는 것이 바람직하다.At this time, the thickness of the block is not particularly limited because it can be appropriately determined according to the need, for example, it is preferable to comply with the standard of the block for block diagram of the Korea Industrial Standard (KS).

상기 성형은 통상적으로 사용되는 성형 장치면 어느 것이든 가능하며, 이러한 성형 장치는 성형틀에 진동과 압력을 인가하는 진동 성형이 가능한 장치가 사용된다. 이때 성형틀의 형태에 따라 다양한 모양의 투수성 블록이 제조된다.The molding may be any molding apparatus that is commonly used, and the molding apparatus may be a vibrating molding apparatus that applies vibration and pressure to the molding die. In this case, permeable blocks of various shapes are manufactured according to the shape of the mold.

다음으로, 상기 제조된 성형 블록을 양생 후 연마하여 투수성 블록을 제조한다.Next, the prepared molded block is cured after curing to prepare a water permeable block.

상기 양생은 10∼80℃, 바람직하기로 20∼40℃에서 2∼4시간 동안 방치하여 수행한다.The curing is carried out by standing for 2 to 4 hours at 10 to 80 ℃, preferably 20 to 40 ℃.

상기 연마는 투수성 블록의 표면을 균일하게 하는 것으로, 통상적으로 사용되는 다축 마석 자동 연마기를 이용하여 수행한다.The polishing is to make the surface of the permeable block uniform, and is performed using a multi-axis manastone polishing machine that is commonly used.

이때 연마 이전에 투수성 블록의 표면 특성을 높이기 위해 표면 광택제를 더욱 사용할 수 있다. 이때, 상기 표면 광택제로는 실러코팅제를 사용할 수 있다. 상기 실러코팅제는 블록의 내마모성 및 강도 증진을 위하여 코팅하는 것으로서, 마감층의 유색 부위의 백화 현상 억제와 광택증진 등 최적의 조경성을 발휘하도록 하는 효과가 있다. 상기 실러코팅제는 컬러 콘크리트 포장공사의 마무리 공정에 주로 사용되는 UV 광택 실러 코팅제를 사용하는 것이 바람직하다.In this case, the surface polisher may be further used to increase the surface properties of the water permeable block before polishing. In this case, a sealer coating agent may be used as the surface polisher. The sealer coating agent is a coating for improving the abrasion resistance and strength of the block, there is an effect to exhibit the optimal landscaping, such as suppressing the whitening phenomenon of the colored portion of the finish layer and enhance the gloss. The sealer coating agent is preferably used a UV gloss sealer coating used mainly in the finishing process of color concrete pavement.

상기 단계를 거쳐 제조된 투수성 블록은 포장을 실시하고, 출하 전까지 양생 과정을 거친 후 적재하여 소비자에게 출하한다.The water-permeable block manufactured by the above steps is packaged, and after being cured before shipment, is loaded and shipped to the consumer.

본 발명에 따른 투수성 블록은 리튬 화합물을 첨가함에 따라 장시간 동안 사용하더라도 치수 변형율이 매우 적고, 투수율이 높아 보도, 자전거 도로, 건축물 주변, 산책로, 주차장, 소형차도, 인테리어 구조물 장식용 등 다양한 분야에 적용된다. The permeable block according to the present invention has a very small dimensional strain even when used for a long time due to the addition of a lithium compound, has a high permeability, and is applicable to various fields such as sidewalks, bicycle roads, buildings, walkways, parking lots, small roads, and interior structures. do.

또한 필요에 따라 투수성 블록 시공시 잔디나 풀씨 또는 작은 나무의 씨앗 등을 파종하는 경우 블록의 상면 및 측면 등 지표면 등으로 노출된 모든 면에 걸쳐서 식생이 이루어지게 되어 생태계의 보전에 크게 기여할 수 있는 친환경 블록으로 유용하게 사용될 수 있다.In addition, when sowing seeds of grass, grass, or small trees when constructing permeable blocks, vegetation occurs on all exposed surfaces such as the top and sides of the block, which can greatly contribute to the preservation of the ecosystem. It can be used as an eco-friendly block.

이하 본 발명을 하기 실시예를 통해 더욱 상세히 설명하겠는 바, 이러한 실시예는 본 발명을 설명하기 위한 일 예시일 뿐 이들에 의해 본 발명이 한정되는 것은 아니다. Hereinafter, the present invention will be described in more detail with reference to the following examples, which are illustrative only for explaining the present invention, and the present invention is not limited thereto.

실시예Example 1∼2,  1 to 2, 비교예Comparative example 1∼4 1 to 4

먼저, 하기 표 1의 조성을 계량한 다음, 자동 믹서기에 균일하게 혼합하였다. 이때 리튬 화합물로는 아초산 리튬:초산 리튬:수산화 리튬 =1:0.25:0.25 (중량비)가 20% 농도로 수분산 된 수용액을 사용하였다.First, the composition of Table 1 was measured, and then uniformly mixed in an automatic mixer. At this time, an aqueous solution in which lithium acetate: lithium acetate: lithium hydroxide = 1: 0.25: 0.25 (weight ratio) was dispersed at a concentration of 20% was used.

얻어진 혼합물을 컨베이어 벨트를 이용하여 성형기로 운반하고, 진동기를 작동시켜 진동시키면서 상기 혼합물이 성형기 구석구석 충분히 충진되도록 하였다. 성형 후 탈형하여 성형 블록을 제조한 다음, 양생실로 운반하여 상온에서 5시간 동안 양생 후 연마하였다. 연마된 성형 블록은 자연 상태에서 5일 동안 충분히 양생하여 투수성 블록(L300 ×W300 × H60 ·80mm)을 제조하였다.The resulting mixture was conveyed to a molding machine using a conveyor belt, and the vibrator was operated to vibrate so that the mixture was sufficiently filled in every corner of the molding machine. After molding, the mold was manufactured by demolding the mold, and then transported to a curing chamber for 5 hours at room temperature, followed by polishing. The polished molding block was sufficiently cured for 5 days in its natural state to produce a permeable block (L300 × W300 × H60 · 80 mm).

실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 포틀랜드 시멘트1 ) Portland cement 1 ) 60 kg60 kg 27 kg27 kg 60 kg60 kg 27 kg27 kg 30 kg30 kg 60 kg60 kg 고로 슬래그Blast furnace slag -- 33 kg33 kg -- 33 kg33 kg -- -- 유리 분말2 ) Glass Powder 2 ) 200 kg200 kg 280 kg280 kg 45 kg45 kg 45 kg3) 45 kg 3) 45 kg45 kg -- 모래sand 2.5 mm2.5 mm 15 kg15 kg 15 kg15 kg 15 kg15 kg 15 kg15 kg 15 kg15 kg -- 10 mm10 mm 30 kg30 kg 30 kg30 kg 30 kg30 kg 30 kg30 kg 30 kg30 kg -- 리튬 화합물Lithium compounds 12 kg12 kg 12 kg12 kg -- -- -- -- 물water 50 kg50 kg 50 kg50 kg 50 kg50 kg 50 kg50 kg 50 kg50 kg 50 kg50 kg 1) 포틀랜드 시멘트: 조성 내 Na2O 0.34 wt%, K2O 0.52 wt%를 포함하고, R2O(시멘트 중 전 알칼리)가 0.68 wt%인 함유한 시멘트. 2) 유리 분말: 입자 크기가 5 mm인 유리 분말. 3) 유리 분말: 입자 크기가 2.5∼5 mm인 혼합 유리 분말.1) Portland Cement: Cement containing 0.34 wt% Na 2 O, 0.52 wt% K 2 O in the composition, and 0.68 wt% R 2 O (all alkalis in cement). 2) Glass Powder: Glass powder with a particle size of 5 mm. 3) Glass Powder: A mixed glass powder having a particle size of 2.5 to 5 mm.

실험예Experimental Example 1: 길이 변화량 측정 1: Measurement of length variation

상기 실시예 및 비교예에서 제조된 투수성 블록의 길이 변화량을 JIS A 1804에 의거하여 측정하였으며, 얻어진 결과를 하기 표 2에 나타내었다. 이때 비교예 5의 투수성 블록은 시판되는 2층 구조의 인터로킹 블록을 구입하여 사용하였다.The change in length of the permeable block prepared in Examples and Comparative Examples was measured based on JIS A 1804, and the results obtained are shown in Table 2 below. At this time, the water-permeable block of Comparative Example 5 was purchased by using a commercially available two-layer interlocking block.

실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 길이 변화량(mm)Length change amount (mm) 0.0230.023 0.0300.030 0.5000.500 0.5500.550 0.0350.035 0.7100.710 0.4100.410 길이 변화율(%)Length change rate (%) 0.0140.014 0.0190.019 0.0310.031 0.0340.034 0.0220.022 0.0520.052 0.0290.029

상기 표 2를 참조하면, 본 발명에 의해 리튬 화합물을 첨가하여 제조된 투수성 블록의 경우, 비교예 1 내지 4의 투수성 블록과 비교하여 길이 변화가 거의 없음을 알 수 있다.Referring to Table 2, in the case of the water-permeable block prepared by adding the lithium compound according to the present invention, it can be seen that there is little change in length compared to the water-permeable block of Comparative Examples 1 to 4.

실험예 2: 치수 변화율 측정Experimental Example 2: Measurement of Dimensional Change Rate

상기 실시예 및 비교예에서 제조된 투수성 블록을 물을 채운 배트 안에 늘어놓고 40 ℃의 건조기에 넣어 고온다습한 환경으로 만들어 18개월 후 치수 변화율(초기 치수 대비)을 JIS A 1804 골재 알칼리 실리카 반응성 시험방법(신속법)에 의해 측정하였으며, 얻어진 결과를 하기 표 3에 나타내었다.The permeable blocks prepared in Examples and Comparative Examples were placed in a batter filled with water and placed in a dryer at 40 ° C. to a high temperature and high humidity environment. It measured by the test method (fast method), and the obtained results are shown in Table 3 below.

실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 1개월 후1 month later 0.05%0.05% 0.08%0.08% 0.10%0.10% 0.30%0.30% 0.03%0.03% 0.24%0.24% 0.15%0.15% 6개월 후6 months later 0.10%0.10% 0.13%0.13% 3.60%3.60% 1.50%1.50% 0.58%0.58% 3.70%3.70% 0.37%0.37% 12개월 후12 months later 0.80%0.80% 1.10%1.10% 9.54%9.54% 6.70%6.70% 1.80%1.80% 12.8%12.8% 5.25%5.25% 18개월 후18 months later 1.30%1.30% 1.45%1.45% 11.5%11.5% 8.40%8.40% 4.55%4.55% 25.9%25.9% 13.7%13.7%

상기 표 3을 참조하면, 본 발명에 따라 리튬 화합물이 첨가된 투수성 블록의 경우 18 개월 이후에서도 치수 변화가 거의 없었다. 이에 비하여 비교예 1 내지 5의 투수성 블록은 치수 변화가 나타났으며, 특히 비교예 1 및 비교예 5의 경우 심각한 치수 변화를 보였다.Referring to Table 3, there was almost no dimensional change even after 18 months in the case of the permeable block to which the lithium compound is added according to the present invention. On the other hand, the water permeable blocks of Comparative Examples 1 to 5 showed a dimensional change, especially in Comparative Example 1 and Comparative Example 5 showed a significant dimensional change.

실험예 3: 물성 측정Experimental Example 3: Measurement of Physical Properties

상기 실시예 및 비교예에서 제조된 투수성 블록의 물성을 하기에 의거하여 측정하고, 얻어진 결과를 하기 표 4에 나타내었다.Physical properties of the water-permeable block prepared in Examples and Comparative Examples were measured based on the following, and the obtained results are shown in Table 4 below.

A: 공극율 A: porosity

투수성 블록을 상부에서 물을 주입하여 완전히 포수시킨 중량과 공기 중에서 1일간 건조시킨 후의 중량을 측정하여 그 차이를 투수성 블록의 용적으로 나누어 공극률을 측정하였다.The water permeability of the permeable block was measured by pouring water from the top and the weight after drying in air for 1 day, and the difference was divided by the volume of the permeable block to measure the porosity.

B: 휨강도B: flexural strength

KS F2407 콘크리트의 휨강도 시험방법에 따라 측정하였다.It was measured according to the flexural strength test method of KS F2407 concrete.

C: 투수 계수C: Permeability Coefficient

KS F 2322에 의한 시험 방법에 따라 측정하였다.It was measured according to the test method according to KS F 2322.

D: 내화학성D: chemical resistance

투수성 블록을 1%의 황산 용액에 침지시켜 중량 변화율을 측정하여 평가하였다.The water permeable block was immersed in 1% sulfuric acid solution to measure the weight change rate.

E: 내충격성E: impact resistance

투수성 블록에 3kg의 강구를 낙하시켜 파괴시 낙하회수를 측정하여 평가하였다.3 kg of steel balls were dropped on the permeable block to evaluate the number of drop times upon breakdown.

실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 공극율(%)Porosity (%) 16.516.5 16.716.7 12.112.1 13.113.1 12.512.5 10.410.4 12.012.0 휨 강도(kg/cm3)Flexural strength (kg / cm 3 ) 258258 257257 239239 245245 234234 226226 224224 투수 계수(cm/sec)Permeability Factor (cm / sec) 0.198 0.198 0.1880.188 측정불가Not measurable 0.090.09 0.110.11 측정불가Not measurable 0.050.05 내화학성Chemical resistance 우수Great 우수Great 양호Good 양호Good 우수Great 양호Good 양호Good 내충격성Impact resistance 우수Great 우수Great 양호Good 양호Good 우수Great 양호Good 우수Great

상기 표 4를 참조하면, 본 발명에 의해 리튬 화합물이 함유된 투수성 블록은 공극율 및 투수 계수가 우수하고, 비교예 1 내지 5의 블록과 비교하여 전체적인 물성이 우수함을 알 수 있다.Referring to Table 4, the water-permeable block containing a lithium compound according to the present invention is excellent in porosity and permeability coefficient, it can be seen that the overall physical properties are superior to the blocks of Comparative Examples 1 to 5.

실험예 4: 외관 관찰Experimental Example 4: Observation of Appearance

상기 실시예 및 비교예에서 제조된 투수성 블록의 외관을 육안으로 관찰하여 하기 표 5에 나타내었다.The appearance of the permeable block prepared in Examples and Comparative Examples was visually observed and shown in Table 5 below.

실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 변형transform ◎◎ ◎◎ △△ △△ △△ ×× △△ 균열crack ◎◎ ◎◎ ×× ×× △△ ×× ×× 표면 상태Surface condition ◎◎ ◎◎ ×× ×× ×× ×× ×× 변형: ◎: 없음, ○: 양호, △: 약간의 변형, ×: 심각한 변형 균열: ◎: 없음, ○: 양호, △: 미미, ×: 심각, 표면 상태: ◎: 균열 발생 없음, ○: 양호, ×: 부적합Strain: ◎: None, ○: Good, △: Slight deformation, ×: Severe deformation Cracks: ◎: None, ○: Good, △: Insignificant, ×: Serious, Surface condition: ◎: No cracking, ○: Good , ×: Not suitable

상기 표 5를 참조하면, 본 발명에 의해 리튬 화합물이 함유된 투수성 블록은 변형이나 균열이 발생하지 않음을 알 수 있다. 이와 비교하여 비교예 1 내지 5의 투수성 블록의 경우 표면에 육안으로 관찰될 정도로 균형이 발생함을 확인하였다. 특히 비교예 4의 블록과 비교예 5의 2층 구조의 인터로킹 블록의 경우 표층과 기층의 팽창율 차이로 인해 균열이 심하게 발생하였다.Referring to Table 5, the permeable block containing a lithium compound according to the present invention can be seen that no deformation or cracking. In comparison with the water-permeable block of Comparative Examples 1 to 5 it was confirmed that the balance occurs to the visually observed. Particularly, in the case of the block of Comparative Example 4 and the interlocking block of the two-layer structure of Comparative Example 5, cracks were severely generated due to the difference in the expansion ratio between the surface layer and the base layer.

본 발명에 따른 투수성 블록은 보도, 자전거 도로, 건축물 주변, 산책로, 주차장, 소형차도, 인테리어 구조물 장식용 등 다양한 분야에 적용된다.The water-permeable block according to the present invention is applied to various fields such as sidewalks, bicycle paths, buildings, walkways, parking lots, small roads, and interior structures.

도 1은 종래 투수성 블록 내 부동태 피막 형성을 보여주는 모식도이다. 1 is a schematic diagram showing the formation of a passive film in a conventional permeable block.

도 2는 본 발명에 따른 투수성 블록 내 부동태 피막 형성을 보여주는 모식도이다. Figure 2 is a schematic diagram showing the formation of a passive film in a permeable block according to the present invention.

Claims (7)

시멘트, 유리 분말 및 골재를 포함하는 투수성 블록에서, 아초산리튬(LiNO2), 초산리튬(LiNO3), 및 수산화리튬(LiOH)이 함유된 리튬 화합물을 포함하는 투수성 블록.In a permeable block comprising cement, glass powder and aggregate, a permeable block comprising a lithium compound containing lithium acetate (LiNO 2 ), lithium acetate (LiNO 3 ), and lithium hydroxide (LiOH). 제1항에 있어서,The method of claim 1, 상기 리튬 화합물은 아초산 리튬: 초산리튬: 수산화리튬을 1:0.01:0.01 ∼1:0.1:0.1의 중량비로 포함하는 것인 투수성 블록.The lithium compound is a water permeable block containing lithium acetate: lithium acetate: lithium hydroxide in a weight ratio of 1: 0.01: 0.01 to 1: 0.1: 0.1. 제1항에 있어서,The method of claim 1, 상기 투수성 블록은 유리 분말의 표면에 불용화된 LiO2·SiO2의 부동태 피막이 형성된 것인 투수성 블록.The water-permeable block is a water-permeable block in which a passivation film of insoluble LiO 2 · SiO 2 is formed on the surface of the glass powder. 제1항에 있어서,The method of claim 1, 상기 투수성 블록은 시멘트 100 중량부에 대해 유리 분말 150∼300 중량부, 골재 40∼60 중량부, 및 리튬 화합물 1∼30 중량부를 포함하는 것인 투수성 블록.The water permeable block is a water permeable block containing 150 to 300 parts by weight of glass powder, 40 to 60 parts by weight of aggregate, and 1 to 30 parts by weight of a lithium compound, based on 100 parts by weight of cement. a) 시멘트, 유리 분말, 골재 및 물을 혼합하여 혼합물을 제조하는 단계,a) mixing cement, glass powder, aggregate and water to prepare a mixture, b) 상기 혼합물에 아초산리튬, 초산리튬, 및 수산화리튬이 함유된 리튬 화합물을 포함하는 수용액을 첨가하는 단계,b) adding an aqueous solution containing a lithium compound containing lithium acetate, lithium acetate, and lithium hydroxide to the mixture, c) 상기 얻어진 혼합물을 성형하여 성형 블록을 제조하는 단계, 및c) molding the obtained mixture to prepare a forming block, and d) 상기 얻어진 성형 블록은 양생 및 연마하는 단계d) curing and polishing the obtained molding block 를 포함하는 제1항의 투수성 블록의 제조방법.The method of manufacturing a water-permeable block of claim 1. 제5항에 있어서,The method of claim 5, 상기 리튬 화합물을 포함하는 수용액은 리튬 화합물이 15∼30 중량%의 농도로 수분산된 것인 투수성 블록의 제조방법.The aqueous solution containing the lithium compound is a method for producing a water-permeable block in which the lithium compound is dispersed at a concentration of 15 to 30% by weight. 제5항에 있어서,The method of claim 5, 상기 유리 분말은 다수의 교반 날개가 장착된 회전 교반기에 카렛트(파쇄된 유리) 및 물을 주입 후 교반하여 모서리 부분이 제거된 것을 사용하는 것인 투수성 블록의 제조방법.The glass powder is a method of producing a water-permeable block is used to remove the edge portion by injecting a caret (crushed glass) and water in a rotary stirrer equipped with a plurality of stirring blades.
KR1020070081367A 2007-08-13 2007-08-13 Block with water permeability and method of fabrication thereof KR100772483B1 (en)