KR100658713B1 - Metal plate for preparing case for high power secondary battery, metal case for high power secondary battery, and high power secondary battery comprising the same - Google Patents
Metal plate for preparing case for high power secondary battery, metal case for high power secondary battery, and high power secondary battery comprising the same Download PDFInfo
- Publication number
- KR100658713B1 KR100658713B1 KR1020050024097A KR20050024097A KR100658713B1 KR 100658713 B1 KR100658713 B1 KR 100658713B1 KR 1020050024097 A KR1020050024097 A KR 1020050024097A KR 20050024097 A KR20050024097 A KR 20050024097A KR 100658713 B1 KR100658713 B1 KR 100658713B1
- Authority
- KR
- South Korea
- Prior art keywords
- case
- secondary battery
- high power
- metal
- metal plate
- Prior art date
Abstract
본 발명은 고출력 이차전지의 케이스 제조용 금속판, 고출력 이차전지용 금속 케이스, 및 이를 포함하는 고출력 이차전지에 관한 것으로서, 보다 상세하게는 알루미늄을 주성분으로 하며, 실리콘, 철, 구리, 망간, 마그네슘, 크롬, 및 알루미늄 잔부를 포함하는 고출력 이차전지의 케이스 제조용 금속판, 이를 사용하여 제조된 고출력 이차전지용 금속 케이스, 및 이를 포함하는 고출력 이차전지에 관한 것이다. The present invention relates to a metal plate for manufacturing a case of a high output secondary battery, a metal case for a high output secondary battery, and a high output secondary battery including the same. More specifically, the main component is aluminum, silicon, iron, copper, manganese, magnesium, chromium, And a metal plate for manufacturing a case of a high power secondary battery including an aluminum balance, a metal case for a high power secondary battery manufactured using the same, and a high power secondary battery including the same.
본 발명의 고출력 이차전지의 케이스 제조용 금속판, 고출력 이차전지용 금속 케이스, 및 이를 포함하는 고출력 이차전지는 기계적 강도가 우수하여 고출력 이차전지의 스웰링을 억제하고, 쉽게 변형되지 않으며, 가공성이 우수한 장점을 가지는 것이다. A metal plate for manufacturing a case of the high output secondary battery of the present invention, a metal case for a high output secondary battery, and a high output secondary battery including the same are excellent in mechanical strength to suppress swelling of the high output secondary battery, not easily deformed, and have excellent workability. It is.
고출력 이차전지, 케이스, 금속판, 스웰링, 가공성 High power secondary battery, case, metal plate, swelling, processability
Description
도 1은 본 발명의 고출력 이차전지용 금속 케이스를 사용하여 제조된 고출력 이차전지의 일 예를 도시한 단면도.1 is a cross-sectional view showing an example of a high output secondary battery manufactured using the metal case for high output secondary battery of the present invention.
[산업상 이용분야][Industrial use]
본 발명은 고출력 이차전지의 케이스 제조용 금속판, 고출력 이차전지용 금속 케이스, 및 이를 포함하는 고출력 이차전지에 관한 것으로서, 보다 상세하게는 고출력 이차전지의 스웰링을 억제하는 고출력 이차전지의 케이스 제조용 금속판, 고출력 이차전지용 금속 케이스, 및 이를 포함하는 고출력 이차전지에 관한 것이다.The present invention relates to a metal plate for manufacturing a case of a high output secondary battery, a metal case for a high output secondary battery, and a high output secondary battery including the same. It relates to a metal case for a secondary battery, and a high output secondary battery comprising the same.
[종래기술][Private Technology]
휴대전화 및 노트북 컴퓨터와 같은 휴대용 전자기기 시장이 확대되고 다양화 됨에 따라 재충전이 가능한 전원공급용 이차전지에 대한 수요도 확대되고 있다. 휴대용 전자기기의 소형화, 경량화, 고성능화 및 다기능화는 전력원으로 사용되는 이차전지에 대한 에너지 저장 밀도의 계속적인 향상을 요구하고 있다. As the market for portable electronic devices such as mobile phones and notebook computers expands and diversifies, the demand for rechargeable rechargeable batteries is increasing. Miniaturization, light weight, high performance, and multifunctionality of portable electronic devices require continuous improvement of energy storage density of secondary batteries used as power sources.
따라서, 이를 충족하기 위한 다년간의 연구결과, 현재의 리튬의 가역적인 삽입, 방출이 가능한 탄소음극과 리튬의 가역적인 삽입, 및 방출이 가능한 양극물질을 채용한 리튬이온 이차전지가 등장하였다. 이러한 리튬이온 이차전지는 기존의 니켈-카드뮴 및 니켈-수소와 같은 수용액계 이차전지보다 단위 무게, 부피당 에너지 밀도 및 충방전 수명이 상대적으로 크기 때문에 휴대용 전자기기의 새로운 에너지원으로써 급속히 기존 전지를 대체하고 있다. Accordingly, as a result of many years of research to satisfy this problem, a lithium ion secondary battery using a cathode material capable of reversible insertion and release of lithium and a reversible insertion and release of lithium have emerged. These lithium-ion secondary batteries rapidly replace existing batteries as new energy sources for portable electronic devices because of their relatively larger unit weight, energy density per charge, and charge / discharge lifetime than aqueous solution secondary batteries such as nickel-cadmium and nickel-hydrogen. Doing.
한편, 휴대 전화기 및 개인 휴대 정보 단말기들은 처리 및 표시 정보량의 증가로 인해 디스플레이의 크기가 증가 일로에 있으며, 이와 더불어 통신기능이 첨가되며 에너지 사용량도 급격히 증가하는 추세이다. 따라서, 통상의 6 mm 이하의 박형 리튬이온 이차전지를 채용하는 경우에는 충분한 구동시간을 얻기 힘든 실정이므로, 2개 이상의 전지를 연결하거나, 보다 두꺼운 전지를 채용해야 하는 것이 실정이다. On the other hand, mobile phones and personal digital assistants are increasing in size due to an increase in the amount of processing and display information. In addition, communication functions are added and energy consumption is rapidly increasing. Therefore, in the case of adopting a conventional thin lithium ion secondary battery of 6 mm or less, it is difficult to obtain sufficient driving time. Therefore, it is necessary to connect two or more batteries or employ a thicker battery.
이러한 리튬이온 이차전지의 외형은 크게 전해액 등이 삽입되는 케이스와, 케이스와 더불어 밀봉된 용기를 형성하는 캡으로 이루어진다. 그런데 리튬이온 이차전지의 넓이가 넓어지고 용량이 증가됨에 따라서, 리튬이온 이차전지를 사용하는 중에 자연적으로 발생하는 전극의 팽창 및 가스 발생에 따른 내압의 상승으로 케이스와 캡의 접촉 부위에서 전해액이 누액되는 상황이 종종 발생된다. 만일 이와 같 이 전해액이 누액되는 경우에는, 그 자체로 전지의 성능에 치명적인 영향을 미칠 뿐 만 아니라, 더욱 심각하게는 전지가 사용되고 있는 전자기기의 전자회로를 오염시켜 고가인 전자기기의 수명을 단축시키게 된다. The exterior of such a lithium ion secondary battery is largely composed of a case into which an electrolyte solution and the like are inserted, and a cap forming a sealed container together with the case. However, as the width of the lithium ion secondary battery becomes wider and the capacity thereof increases, the electrolyte leaks at the contact portion between the case and the cap due to an increase in the internal pressure due to the expansion of the electrode and gas generation that occur naturally during the use of the lithium ion secondary battery. Situations often arise. If the electrolyte leaks in this way, it not only has a fatal effect on the performance of the battery itself but, more seriously, contaminates the electronic circuit of the electronic device in which the battery is being used, which shortens the lifetime of expensive electronic equipment. Let's go.
또한, 최근에는 기존의 화석연료와 이차전지 또는 연료전지를 결합시킨 하이브리드 자동차에 대한 연구가 활발히 진행되면서, 짧은 시간 내에 고출력을 얻을 수 있는 리튬 이차 전지에 대한 요구가 증가하게 되었다. In addition, recently, as research on a hybrid vehicle combining an existing fossil fuel and a secondary battery or a fuel cell has been actively conducted, the demand for a lithium secondary battery capable of obtaining high output in a short time has increased.
통상적으로, 고출력 리튬 이차 전지는 종래의 휴대용 리튬 이차 전지에 비해 큰 부피와 중량을 가지며, 10년 이상의 장기간 동안 사용될 수 있어야 하므로, 종래의 휴대용 리튬 이차 전지용 케이스를 사용하기에는 부적합하며, 충분한 강도를 가지는 고출력 이차 전지용 케이스의 개발이 요구된다.In general, a high output lithium secondary battery has a larger volume and weight than a conventional portable lithium secondary battery, and should be able to be used for a long time of 10 years or more, so it is not suitable for using a case for a conventional portable lithium secondary battery and has sufficient strength. Development of a case for a high output secondary battery is required.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 장기간의 사용에 따른 고출력 이차전지의 스웰링을 억제하고, 자체의 하중을 견딜만한 강도를 가지면서, 가공성이 우수한 고출력 이차전지의 케이스 제조용 금속판을 제공하는 것이다. The present invention is to solve the above problems, an object of the present invention is to suppress the swelling of the high-output secondary battery according to the long-term use, having a strength to withstand its own load, high output secondary battery excellent in workability It is to provide a metal plate for the case production of.
본 발명의 다른 목적은 상기 금속판을 이용하여 제조된 고출력 이차전지용 금속 케이스를 제공하는 것이다.Another object of the present invention is to provide a metal case for a high output secondary battery manufactured using the metal plate.
본 발명의 또 다른 목적은 상기 금속케이스를 포함하는 고출력 이차전지를 제공하는 것이다.Still another object of the present invention is to provide a high output secondary battery including the metal case.
본 발명은 상기 목적을 달성하기 위하여, 알루미늄을 주성분으로 하며, 실리콘, 철, 구리, 망간, 마그네슘, 크롬, 및 알루미늄 잔부를 포함하는 고출력 이차전지의 케이스 제조용 금속판을 제공한다.In order to achieve the above object, the present invention provides a metal plate for manufacturing a case of a high-output secondary battery having aluminum as a main component and containing silicon, iron, copper, manganese, magnesium, chromium, and aluminum balance.
본 발명은 또한, 상기 고출력 이차전지의 케이스 제조용 금속판을 이용하여 제조된 고출력 이차전지용 금속 케이스를 제공한다.The present invention also provides a metal case for a high power secondary battery manufactured using a metal plate for manufacturing a case of the high power secondary battery.
본 발명은 또한, 양극판과 음극판이 세퍼레이터를 사이에 두고 위치하는 전극군; 전해액; 상기 전해액과 전극군을 수용할 수 있도록 일측 선단이 개방된 상기 고출력 이차전지용 금속 케이스; 상기 금속 케이스의 개구부 상단에 설치되고, 금속 케이스를 밀봉하는 캡 조립체; 상기 금속 케이스와 캡 조립체 사이에 위치하는 가스켓; 및 상기 전극군의 양극판과 전기적으로 연결되는 양극 집전판, 및 음극판과 전기적으로 연결되는 음극 집전판을 포함하는 고출력 이차전지를 제공한다.The present invention also provides an electrode group in which a positive electrode plate and a negative electrode plate are positioned with a separator interposed therebetween; Electrolyte solution; A metal case for the high output secondary battery whose one end is open to accommodate the electrolyte and the electrode group; A cap assembly installed at an upper end of the opening of the metal case and sealing the metal case; A gasket positioned between the metal case and the cap assembly; And a positive electrode current collector plate electrically connected to the positive electrode plate of the electrode group, and a negative electrode current collector plate electrically connected to the negative electrode plate.
이하, 본 발명을 보다 상세하게 설명한다. Hereinafter, the present invention will be described in more detail.
본 발명의 고출력 이차전지의 케이스 제조용 금속판은 알루미늄을 주성분으로 하며, 실리콘, 철, 구리, 망간, 마그네슘, 크롬, 및 알루미늄 잔부를 포함할 수 있다. The metal plate for manufacturing a case of the high output secondary battery of the present invention contains aluminum as a main component and may include silicon, iron, copper, manganese, magnesium, chromium, and aluminum balance.
상기 금속판에 포함되는 실리콘은 전체 금속판의 중량에 대하여 0.6 중량% 이하인 것이 바람직하며, 0.01 내지 0.6 중량%인 것이 더 바람직하다. The silicon contained in the metal plate is preferably 0.6% by weight or less, and more preferably 0.01 to 0.6% by weight based on the weight of the entire metal plate.
상기 금속판에 포함되는 철은 전체 금속판 중량에 대하여 0.7 중량% 이하인 것이 바람직하며, 0.01 내지 0.7 중량%인 것이 더 바람직하다. Iron contained in the metal plate is preferably 0.7% by weight or less, and more preferably 0.01 to 0.7% by weight relative to the total metal plate weight.
상기 금속판에 포함되는 구리는 전체 금속판 중량에 대하여 0.05 내지 0.2 중량%인 것이 바람직하다.Copper contained in the metal plate is preferably 0.05 to 0.2% by weight relative to the total metal plate weight.
상기 금속판에 포함되는 망간은 전체 금속판 중량에 대하여 0.01 내지 1.5 중량%인 것이 바람직하며, 0.01 내지 1.0 중량%인 것이 더 바람직하고, 0.01 내지 0.2 중량%인 것이 가장 바람직하다. The manganese contained in the metal plate is preferably 0.01 to 1.5% by weight, more preferably 0.01 to 1.0% by weight, and most preferably 0.01 to 0.2% by weight based on the total metal plate weight.
상기 실리콘, 철, 구리, 및 망간의 함량이 상기 범위를 초과하는 경우에는 고출력 이차전지의 케이스로서 인장강도 및 가공성이 나빠질 수 있다. When the content of silicon, iron, copper, and manganese exceeds the above range, tensile strength and workability may deteriorate as a case of a high output secondary battery.
상기 금속판에 포함되는 마그네슘은 전체 금속판 중량에 대하여 0.1 내지 5 중량%인 것이 바람직하다. 마그네슘의 함량이 0.1 중량% 미만인 경우에는 금속판의 강도가 충분하지 못하며, 5 중량%를 초과하는 경우에는 고출력 이차전지의 케이스의 가공이 어려워질 수 있다. Magnesium contained in the metal plate is preferably 0.1 to 5% by weight based on the total weight of the metal plate. If the magnesium content is less than 0.1% by weight, the strength of the metal plate is not sufficient, and if the content of more than 5% by weight, it may be difficult to process the case of the high power secondary battery.
또한, 상기 금속판에 포함되는 크롬은 전체 금속판 중량에 대하여 0.01 내지 5 중량%인 것이 바람직하고, 0.01 내지 1.0 중량%인 것이 더 바람직하며, 0.01 내지 0.4 중량%인 것이 가장 바람직하다. 크롬의 함량이 0.01 중량% 미만인 경우에는 금속판의 강도가 충분하지 못하며, 5 중량%를 초과하는 경우에는 고출력 이차전지의 케이스의 가공이 어려워질 수 있다. In addition, the chromium contained in the metal plate is preferably 0.01 to 5% by weight, more preferably 0.01 to 1.0% by weight, and most preferably 0.01 to 0.4% by weight based on the total metal plate weight. When the content of chromium is less than 0.01% by weight, the strength of the metal plate may not be sufficient, and when it exceeds 5% by weight, it may be difficult to process the case of the high power secondary battery.
또한, 상기 케이스용 금속판은 0.01 내지 0.3 중량%의 아연을 더 포함하는 것이 바람직하며, 0.01 내지 0.2 중량%의 티타늄을 더 포함하는 것이 더 바람직하다. 상기 아연 및 티타늄의 함량이 상기 범위 미만인 경우에는 첨가에 따른 효과가 미미하며, 상기 범위를 초과하는 경우에는 우수한 성능을 얻을 수 없다. In addition, the metal plate for the case preferably further comprises 0.01 to 0.3% by weight of zinc, more preferably 0.01 to 0.2% by weight of titanium. When the content of zinc and titanium is less than the above range, the effect of addition is insignificant, and when it exceeds the above range, excellent performance cannot be obtained.
본 발명의 고출력 이차전지의 케이스 제조용 금속판은 고출력 이차전지의 케이스의 제조에 사용되는 것으로서, 통상적인 이차전지의 케이스보다 강한 강도를 가져야 한다. 따라서, 상기 케이스용 금속판은 0.6 내지 3 mm의 두께를 가지는 것이 바람직하다. 상기 금속판의 두께가 0.6 mm 미만이 경우에는 장기간 사용에 따른 고출력 이차전지의 스웰링을 억제할 수 없게 되고, 자체의 하중이나 외부로부터의 충격을 견디기 어려우며, 3 mm를 초과하는 경우에는 가공이 어렵고, 고출력 이차전지 전체의 무게가 증가하게 된다. The metal plate for manufacturing a case of the high output secondary battery of the present invention is used to manufacture a case of a high output secondary battery, and should have a stronger strength than that of a conventional secondary battery. Therefore, the metal plate for the case preferably has a thickness of 0.6 to 3 mm. When the thickness of the metal plate is less than 0.6 mm, the swelling of the high output secondary battery due to long-term use cannot be suppressed, and it is difficult to withstand its own load or external shock, and when it exceeds 3 mm, it is difficult to process. As a result, the weight of the entire high-output secondary battery increases.
고출력 이차전지의 용도는 여러가지가 있을 수 있으나, 통상적으로 하이브리드 자동차의 전지로 사용되는 등, 외부환경의 변화가 심한 조건에서 사용될 가능성이 크다. The use of the high output secondary battery may be various, but it is generally used in a condition in which the external environment is severely changed, such as a battery of a hybrid vehicle.
따라서, 본 발명의 고출력 이차전지의 케이스 제조용 금속판은 20℃에서 측정한 인장강도가 12 내지 45 kgf/mm2인 것이 바람직하고, 20 내지 45 kgf/mm2인 것이 더 바람직하며, 30 내지 45 kgf/mm2인 것이 가장 바람직하다. 인장강도가 12 kgf/mm2미만인 경우에는 외력(外力)에 의한 변형이 일어날 수 있으며, 45 kgf/mm2를 초과하는 경우에는 케이스 형태로의 가공이 어려워진다. Therefore, the metal plate for manufacturing a case of the high output secondary battery of the present invention preferably has a tensile strength of 12 to 45 kgf / mm 2 measured at 20 ° C, more preferably 20 to 45 kgf / mm 2 , and 30 to 45 kgf. it is most preferred in / mm 2. If the tensile strength is less than 12 kgf / mm 2 , deformation due to external force may occur. If the tensile strength exceeds 45 kgf / mm 2 , it becomes difficult to process the case.
또한, 상기 금속판의 연신율은 1.6 mm 두께를 기준으로 25 % 이하인 것이 바람직하고, 1 내지 15% 인 것이 더 바람직하다. 연신율이 25%를 초과할 경우에는 전지의 가동 시에 발생하는 열과 외부의 충격에 의해 케이스의 변형이 일어날 수 있다.In addition, the elongation of the metal plate is preferably 25% or less, more preferably 1 to 15% based on 1.6 mm thickness. If the elongation exceeds 25%, deformation of the case may occur due to external heat shock and heat generated during operation of the battery.
본 발명의 고출력 이차전지의 케이스 제조용 금속판은 20℃에서 90o 의 절곡 조건으로 측정한 절곡강도가 1 톤 이상인 것이 바람직하며, 1톤 내지 2톤 인 것이 더 바람직하고, 1.5톤 내지 2톤인 것이 더 바람직하다. 절곡강도가 1 톤 미만인 경우에는 장기간 사용시 스웰링 현상이 발생할 수 있으며, 2톤을 초과하는 경우에는 케이스 형태로의 가공이 어려워진다. And case for manufacturing metal sheet of high-output secondary battery according to the present invention preferably has a bending strength measured at 20 ℃ the bent condition of 90 o 1 tone at 1 ton to two tons of it is more preferable, and 1.5 ton to about 2 tons to more desirable. If the bending strength is less than 1 ton, swelling may occur when used for a long period of time, and if it exceeds 2 tons, it becomes difficult to process the case.
상기 고출력 이차전지의 케이스 제조용 금속판은 일반적인 고출력 이차전지의 케이스의 제조에 모두 사용할 수 있으며, 바람직하게는 하이브리드 자동차용 고출력 이차전지의 케이스의 제조에 사용될 수 있고, 더 바람직하게는 하이브리드 자동차용 고출력 리튬이차전지의 케이스의 제조에 사용될 수 있다. The metal plate for manufacturing a case of the high output secondary battery may be used for manufacturing a case of a general high output secondary battery, and preferably may be used for manufacturing a case of a high output secondary battery for a hybrid vehicle, and more preferably a high output lithium for a hybrid vehicle. It can be used to manufacture a case of a secondary battery.
상기 고출력 이차전지의 케이스 제조용 금속판을 이용하여 제조된 고출력 이차전지용 금속 케이스는 특정한 케이스의 형태에 한정되지 아니하며, 필요에 따라 원통형, 각형 또는 기타 다른 형태로 제조될 수 있다. The metal case for a high output secondary battery manufactured using the metal plate for case manufacturing of the high output secondary battery is not limited to a specific case form, and may be manufactured in a cylindrical, rectangular or other form as necessary.
도 1은 본 발명의 고출력 이차전지용 금속 케이스를 사용하여 제조된 고출력 이차전지의 일 실시예를 도시한 단면도이다. 다만, 본 발명의 고출력 이차전지용 금속 케이스의 형태가 상기 도1의 형태로만 한정되는 것은 아니다.1 is a cross-sectional view showing an embodiment of a high output secondary battery manufactured using a metal case for a high output secondary battery of the present invention. However, the form of the metal case for a high output secondary battery of the present invention is not limited to the form of FIG.
상기한 도면을 참조하여 원통형의 이차 전지에 대해 살펴보면, 상기 이차 전지는 양극판(11)과 음극판(12)이 세퍼레이터(13)을 사이에 두고 위치하는 전극군(10)과, 전해액과 함께 전극군(10)을 수용할 수 있도록 일측 선단이 개방된 금속 케이스(20)과, 가스켓(31)을 매개로 상기 금속 케이스(20)의 개구부 상단에 설치되고 금속 케이스(20)를 밀봉하는 캡 조립체(30)와, 상기 전극군(10)의 양극판, 및 음극판(11,12)과 전기적으로 연결되는 양극, 음극 집전판(40,50)을 포함한다. Looking at the cylindrical secondary battery with reference to the above drawings, the secondary battery is the
또한, 상기 캡 조립체(30)는 외부 단자(32a)를 가지는 캡 플레이트(32)와, 케이스(20)와 캡 플레이트(32)를 절연시키는 가스켓(31)을 포함하며, 설정된 압력 조건에서 파손되어 가스를 방출함으로써 전지의 폭발을 방지하는 밴트 플레이트(33)를 더욱 포함할 수 있고, 상기 밴트 플레이트(33)는 리드(35)를 매개로 양극 집전판(40)과 전기적으로 연결된다. 상기 밴트 플레이트(33)는 설정된 압력 조건에서 상기 리드(35)을 통한 전극 조립체(10)와 외부 단자(32a)의 전기적 연결을 차단할 수 있는 구조이면 도시한 형상에 한정되지 않고 다양하게 변형되어 사용될 수 있다. In addition, the
이하, 본 발명의 바람직한 실시예를 기재한다. 다만, 하기의 실시예는 본 발명의 바람직한 일 실시예일 뿐, 본 발명이 하기 실시예에 의해 한정되는 것은 아니다.Hereinafter, preferred embodiments of the present invention are described. However, the following examples are only preferred embodiments of the present invention, and the present invention is not limited to the following examples.
[실시예]EXAMPLE
실시예 1Example 1
실리콘 0.3 중량%, 철 0.7 중량%, 구리 0.2 중량%, 망간 0.2 중량%, 마그네슘 1.1 중량%, 크롬 0.1 중량%, 아연 0.25 중량%, 불순물 0.05 중량%, 및 잔량의 알루미늄을 포함하며, 두께 1.6 mm인 금속판을 이용하여 도 1의 금속 케이스(20)와 동일한 형태의 케이스를 제조하였다. 0.3 wt% silicon, 0.7 wt% iron, 0.2 wt% copper, 0.2 wt% manganese, 1.1 wt% magnesium, 0.1 wt% chromium, 0.25 wt% zinc, 0.05 wt% impurity, and balance aluminum, and a thickness of 1.6 A case having the same shape as that of the
실시예 2Example 2
실리콘 0.25 중량%, 철 0.4 중량%, 구리 0.1 중량%, 망간 0.1 중량%, 마그네슘 2.8 중량%, 크롬 0.35 중량%, 아연 0.1 중량%, 불순물 0.05 중량%, 및 잔량의 알루미늄을 포함하며, 두께 1.6 mm인 금속판을 이용하여 도 1의 금속 케이스(20)와 동일한 형태의 케이스를 제조하였다.Contains 0.25 wt% silicon, 0.4 wt% iron, 0.1 wt% copper, 0.1 wt% manganese, 2.8 wt% magnesium, 0.35 wt% chromium, 0.1 wt% zinc, 0.05 wt% impurity, and balance aluminum, and a thickness of 1.6 A case having the same shape as that of the
실시예 3Example 3
실리콘 0.2 중량%, 철 0.35 중량%, 구리 0.15 중량%, 망간 0.15 중량%, 마그네슘 5 중량%, 크롬 0.15 중량%, 아연 0.25 중량%, 불순물 0.05 중량%, 및 잔량의 알루미늄을 포함하며, 두께 1.6 mm인 금속판을 이용하여 도 1의 금속 케이스(20)와 동일한 형태의 케이스를 제조하였다.Contains 0.2 wt% silicon, 0.35 wt% iron, 0.15 wt% copper, 0.15 wt% manganese, 5 wt% magnesium, 0.15 wt% chromium, 0.25 wt% zinc, 0.05 wt% impurity, and residual aluminum, thickness 1.6 A case having the same shape as that of the
실시예 1 내지 3에 따라 제조된 금속 케이스에 대하여 인장강도, 연신율, 및 절곡강도를 측정하였으며, 그 결과를 하기 표 1에 정리하였다. Tensile strength, elongation, and bending strength of the metal cases prepared according to Examples 1 to 3 were measured, and the results are summarized in Table 1 below.
[표 1]TABLE 1
상기 표 1에서 보는 것과 같이, 본 발명의 고출력 이차전지의 케이스 제조용 금속판을 이용한 케이스는 인장강도와 절곡강도가 우수하여 고출력 이차전지의 케이스로 적합한 것을 알 수 있다. As shown in Table 1, it can be seen that the case using the metal plate for manufacturing the case of the high output secondary battery of the present invention has excellent tensile strength and bending strength and is suitable as a case of the high output secondary battery.
본 발명의 고출력 이차전지의 케이스 제조용 금속판 및 이를 사용하여 제조된 고출력 이차전지용 금속 케이스는 기계적 강도가 우수하여 고출력 이차전지의 스웰링을 억제하고, 쉽게 변형되지 않으며, 가공성이 우수한 장점을 가진다. The metal plate for manufacturing a case of the high output secondary battery of the present invention and the metal case for a high output secondary battery manufactured using the same have excellent mechanical strength to suppress swelling of the high output secondary battery, not easily deformed, and have excellent workability.
Claims (9)