KR100651530B1 - Polyurethane insulating waterproof systems with hollow material - Google Patents

Polyurethane insulating waterproof systems with hollow material Download PDF

Info

Publication number
KR100651530B1
KR100651530B1 KR1020050091107A KR20050091107A KR100651530B1 KR 100651530 B1 KR100651530 B1 KR 100651530B1 KR 1020050091107 A KR1020050091107 A KR 1020050091107A KR 20050091107 A KR20050091107 A KR 20050091107A KR 100651530 B1 KR100651530 B1 KR 100651530B1
Authority
KR
South Korea
Prior art keywords
layer
porous
mixed
waterproof
polyurethane
Prior art date
Application number
KR1020050091107A
Other languages
Korean (ko)
Inventor
김용현
마영길
Original Assignee
(주)아해
이원홍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)아해, 이원홍 filed Critical (주)아해
Priority to KR1020050091107A priority Critical patent/KR100651530B1/en
Application granted granted Critical
Publication of KR100651530B1 publication Critical patent/KR100651530B1/en

Abstract

A polyurethane adiabatic and waterproof construction method using porous materials is provided to shorten a period of construction and to make economical profits by obtaining waterproof and adiabatic effects with one construction. A polyurethane adiabatic and waterproof construction method using porous materials comprises the steps of: constructing a foundation layer(1); attaching a non-woven fabric sheet layer(2) on the foundation layer using polyurethane waterproofing materials; placing a polyurethane waterproof coating layer(4) with or without powdered porous materials on the non-woven fabric sheet layer to improve adiabatic and waterproof effects; placing a porous mixture layer(3) containing porous silica and porous inorganic materials having the particle size of 0.1~5 millimeters on the waterproof coating layer to improve adiabatic effect; and forming a top coating layer(6) on the waterproof coating layer to reinforce the weathering resistance of the waterproof coating layer.

Description

다공성 재질을 이용한 폴리우레탄 단열 방수 공법{POLYURETHANE INSULATING WATERPROOF SYSTEMS WITH HOLLOW MATERIAL}Polyurethane insulation waterproof method using porous material {POLYURETHANE INSULATING WATERPROOF SYSTEMS WITH HOLLOW MATERIAL}

도 1a 및 도 1b는 부직포 시트층을 사용한 본 발명의 일 실시예에 따른 단열 방수 공법의 단면도이다(노출공법).1A and 1B are cross-sectional views of an adiabatic waterproofing method according to an embodiment of the present invention using a nonwoven sheet layer (exposure method).

도 2a 및 도 2b는 부직포 시트층을 사용하지 아니한 본 발명의 다른 실시예에 따른 단열 방수 공법의 단면도이다(노출공법). 2A and 2B are cross-sectional views of a heat insulation waterproofing method according to another embodiment of the present invention without using a nonwoven sheet layer (exposure method).

도 3은 부직포 시트층을 사용한 본 발명의 또 다른 실시예에 따른 단열 방수 공법의 단면도이다(비노출공법).3 is a cross-sectional view of a heat insulation waterproofing method according to another embodiment of the present invention using a nonwoven fabric sheet layer (non-exposed method).

도 4는 부직포 시트층을 사용하지 아니한 본 발명의 또 다른 실시예에 따른 단열 방수 공법의 단면도이다(비노출공법).Figure 4 is a cross-sectional view of the thermal insulation waterproofing method according to another embodiment of the present invention without using a non-woven sheet layer (non-exposure method).

* 도면의 주요 부분에 대한 부호 설명* Explanation of symbols on the main parts of the drawing

1 : 바탕층1: base layer

2 : 부직포 시트층2: nonwoven sheet layer

3 : 다공질 혼합층3: porous mixed layer

4 : 도막방수층4: coating film waterproofing layer

5 : 다공질층5: porous layer

6 : 탑코팅층6: top coating layer

7 : 프라이머층7: primer layer

8 : 보호층8: protective layer

본 발명은 단열방수 공법에 관한 것으로, 보다 상세하게는 한 번의 시공으로 방수성능과 단열성능을 함께 발휘하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법에 관한 것이다.The present invention relates to a heat insulation waterproof method, and more particularly, to a polyurethane heat insulation waterproof method using a porous material that exhibits both waterproof performance and heat insulation performance in a single construction.

지금까지 다양한 방수제를 이용한 시공방법이 공지된 바 있으나, 이들 모두는 방수성능을 보유하기 위한 방법이며 방수성능을 확보한 후에 단열성능을 보유하기 위해서는 별도의 단열 시공을 하여야만 하였다. 따라서 이들 종래의 시공 방법은 2중의 작업이 필요할 뿐 아니라 별도의 공사로 시행되기 때문에 공기나 경제적인 면에서 많은 한계를 가지고 있는 문제점이 있었다.Up to now, a construction method using various waterproofing agents has been known, but all of them are methods for retaining the waterproofing performance and have to be separately insulated for securing the insulating performance after securing the waterproofing performance. Therefore, these conventional construction methods require a double work as well as a separate construction, there was a problem that has a lot of limitations in terms of air and economics.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 바닥의 시공방법에 있어서 단일의 시공으로 방수성능과 단열성능을 함께 발휘하는 시공방법을 제공하는 것이다.The present invention has been made to solve the above problems, the object of the present invention is to provide a construction method that exhibits both waterproof and heat insulating performance in a single construction in the construction method of the floor.

상기와 같은 본 발명의 목적은, 콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공하는 단계; 상기 바탕층(1) 위에 부직포 시트층(2)을 접착하는 단계; 상기 부직포 시트층(2) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계; 상기 도막방수층(4) 위에 입자크기 0.1~5mm의 다공성 실리카 및 다공성 무기재료를 포함하는 다공질 혼합층(3)을 적층하는 단계; 상기 다공질 혼합층(3) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계; 및 상기 도막방수층(4) 위에 도막방수층의 내후성을 보강하기 위한 탑코팅층(6)을 적층하는 단계를 포함하는 것을 특징으로 하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법에 의하여 달성된다.An object of the present invention as described above, the step of constructing a base layer (1) to form a foundation floor comprising concrete; Adhering a nonwoven sheet layer (2) onto the base layer (1); Stacking a polyurethane coating film waterproof layer (4) on which the powder of the porous material is mixed or not mixed on the nonwoven sheet layer (2); Stacking a porous mixed layer 3 including porous silica and a porous inorganic material having a particle size of 0.1 to 5 mm on the waterproofing layer 4; Stacking a polyurethane coating film waterproof layer (4) on which the porous powder is mixed or not mixed on the porous mixed layer (3); And laminating a top coating layer 6 for reinforcing the weather resistance of the coating waterproof layer 4 on the coating waterproof layer 4.

본 발명에서는 노출 공법이나 비노출 공법 모두 적용 가능하며, 방수재 고유의 탄성과 신축률을 보유하여 건축물의 진동이나 크랙에 대항하여 지속적인 방수기능을 보유하면서도 동시에 단열성능을 보유하여 종래의 기술에서 단열기능을 위한 별도의 시공을 생략하고 단 한번의 시공으로 방수 및 단열 성능을 발휘하는 시공방법을 제공하고자 한다. In the present invention, both the exposure method and the non-exposure method can be applied, and possess the inherent elasticity and elasticity of the waterproofing material to maintain the waterproofing function against the vibration or the crack of the building while at the same time retaining the insulating performance in the prior art It is to provide a construction method that exhibits waterproof and insulation performance by only one construction by omitting a separate construction for.

본 발명의 그 밖의 목적, 특정한 장점 및 신규한 특징들은 첨부된 도면들과 연관되어지는 이하의 발명의 상세한 설명과 바람직한 실시예로부터 더욱 분명해질 것이다.Other objects, specific advantages, and novel features of the present invention will become more apparent from the following detailed description of the invention and the preferred embodiments in connection with the accompanying drawings.

이하, 본 발명에 따른 다공성 재질을 이용한 폴리우레탄 단열 방수 공법의 구성에 대하여 설명하기로 한다.Hereinafter, the configuration of the polyurethane thermal insulation waterproof method using a porous material according to the present invention will be described.

통상 건축물의 방수시공 방법에는 여러 지 방법이 있을 수 있으나 비교적 안정되고 우수한 방수 성능을 부여하는 방법이 도막 방수 공법으로 알려져 있다. 본 발명은 단열기능을 보유한 도막 방수 공법이다. 건축물의 소요 기능 중에 단열 기능 및 방수 기능은 매우 중요한 사항인 바, 본 발명은 이러한 단열기능과 방수 기능을 동시에 보유한 획기적인 방법이라고 할 수 있다.In general, there may be various methods of waterproof construction of a building, but a method of providing a relatively stable and excellent waterproof performance is known as a coating waterproofing method. The present invention is a coating film waterproofing method having a heat insulating function. Among the required functions of the building, the heat insulation function and the waterproof function are very important matters, and the present invention can be said to be a breakthrough method having both the heat insulation function and the waterproof function.

도 1a 및 도 1b는 노출공법을 도시한 것으로 부직포 시트층을 사용한 단열 방수 공법의 단면도이다.1A and 1B are cross-sectional views of a heat insulation waterproof method using a nonwoven fabric sheet layer, showing an exposure method.

먼저, 도 1a에 대하여 설명하면, 콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공한 후, 상기 바탕층(1) 위에 부직포 시트층(2)을 접착한다. 상기 부직포 시트는 개량고무화 아스팔트, EVA, EPDM, 폴리우레탄 등 방수 성능을 갖는 고무상 재질의 시트의 양면 혹은 상면에 부직포를 접착하여 구성된 것으로 바탕층(1) 위에 접착시 폴리우레탄 방수제를 사용하여 접착한다.First, with reference to Figure 1a, after the base layer (1) to form a foundation floor containing concrete, the non-woven fabric sheet layer (2) is bonded on the base layer (1). The nonwoven fabric sheet is formed by adhering the nonwoven fabric to both surfaces or the upper surface of a rubber-like sheet having waterproof performance such as improved rubberized asphalt, EVA, EPDM, polyurethane, etc. Glue.

상기 부직포 시트층(2) 위에는 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층한다. 다공성 재질의 분말을 사용할 경우 단열기능을 부여한다. 상기 도막방수층(4)은 폴리우레탄 도막 방수층으로서, 1액형 또는 2액형 액상 도막 방수재 중 어느 하나를 사용할 수 있다. 폴리우레탄 도막 방수제는 방수 성능을 부여하는 주 구성요소로서 우수한 탄성과 신율을 보유하 고 있어 뛰어난 방수 성능을 보유하며 다공성 재질을 함유시킬 경우 방수성능과 더불어 우수한 단열성능을 발휘할 수 있다.On the nonwoven fabric sheet layer 2 is laminated a polyurethane coating waterproof layer 4 is mixed or not mixed with a powder of a porous material. When using powder of porous material, it gives insulation function. The coating film waterproofing layer 4 is a polyurethane coating film waterproofing layer, any one of a one-component or two-component liquid coating film waterproofing material can be used. Polyurethane coating waterproofing agent is a main component that gives waterproof performance. It has excellent elasticity and elongation, so it has excellent waterproofing performance. When it contains porous material, it can exhibit excellent thermal insulation performance as well as waterproofing performance.

상기 도막방수층(4) 위에는 입자크기 0.1~5mm의 다공성 실리카 및 다공성 무기재료를 포함하는 다공질 혼합층(3)을 적층한다. 다공질 혼합층(3)은 단열성능을 향상시키기 위한 것이며 다공성 재질은 내부에 폐쇄성 공극이 있는 다공질 실리카, 다공성 알루미나 또는 다공성 알루미늄 실리케이트 등을 사용하여 단열성능을 부여하며 다공질 혼합층(3)은 이러한 다공성 재질을 우레탄 도포 후 살포하여 우레탄에 침적시키는 구조로 구성된다.On the coating layer 4, a porous mixed layer 3 including porous silica and a porous inorganic material having a particle size of 0.1 to 5 mm is laminated. The porous mixed layer 3 is for improving the thermal insulation performance, and the porous material gives the thermal insulation performance by using porous silica, porous alumina, or porous aluminum silicate having a closed void therein, and the porous mixed layer 3 provides such a porous material. It is composed of a structure that is sprayed after urethane coating and deposited on urethane.

상기 다공질 혼합층(3) 위에는 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층한다. 도막방수층(4)은 위에서 설명한 것과 동일하다. On the porous mixed layer 3 is laminated a polyurethane coating waterproof layer (4) is mixed or not mixed with a powder of a porous material. The coating film waterproofing layer 4 is the same as that described above.

상기 도막방수층(4) 위에는 도막방수층의 내후성을 보강하기 위한 탑코팅층(6)을 적층한다. 탑코팅제는 내후성이 우수한 아크릴 우레탄 제품을 사용하는 것이 바람직하다.The top coating layer 6 is laminated on the coating waterproof layer 4 to reinforce the weather resistance of the coating waterproof layer. It is preferable to use an acrylic urethane product having excellent weather resistance as the top coating agent.

도 1b에서는 상기 탑코팅층(6)과 도막방수층(4) 사이에 단열성능을 보강하기 위한 다공성 실리카 또는 다공성 무기재료를 포함하는 다공질층(5)이 더 적층되는 것을 제외하고는 상기 도 1a에서와 동일하다. In FIG. 1B, except that a porous layer 5 including porous silica or a porous inorganic material for reinforcing a thermal insulation performance is further laminated between the top coating layer 6 and the coating waterproof layer 4, as illustrated in FIG. 1A. same.

도 2a 및 도 2b는 노출공법을 도시한 것으로 부직포 시트층을 사용하지 아니한 단열 방수 공법의 단면도이다.Figures 2a and 2b is a cross-sectional view of the thermal insulation waterproof method showing the exposure method and not using a nonwoven sheet layer.

먼저, 도 2a에 대하여 설명하면, 콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공한 후, 상기 바탕층(1) 위에 프라이머를 도포하고, 상기 프라이머층(7) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층한다. 상기 프라이머는 우레탄 도막방수층(4)와 바탕층(1) 사이의 들뜸현상을 방지하고 접착력을 보강하며 기포발생을 억제하기 위한 것으로 우레탄 프라이머를 사용하는 것이 바람직하다. 상기 도막방수층(4) 위에는 다공질 혼합층(3)을 적층하는 바, 그 이후의 공정은 도 1a에서 설명한 바와 동일하다. First, referring to FIG. 2A, after constructing a base layer 1 to form a foundation floor including concrete, a primer is applied on the base layer 1, and a porous material is formed on the primer layer 7. The polyurethane coating waterproofing layer 4 with or without powder is laminated. The primer is to prevent the lifting phenomenon between the urethane coating film waterproof layer (4) and the base layer (1) to reinforce the adhesive force and to suppress the generation of bubbles it is preferable to use a urethane primer. The porous mixed layer 3 is laminated on the coating waterproof layer 4, and the subsequent steps are the same as those described with reference to FIG. 1A.

도 2b에서는 상기 탑코팅층(6)과 도막방수층(4) 사이에 단열성능을 보강하기 위한 다공성 실리카 또는 다공성 무기재료를 포함하는 다공질층(5)이 더 적층되는 것을 제외하고는 상기 도 2a에서와 동일하다. In FIG. 2B, a porous layer 5 including porous silica or a porous inorganic material for reinforcing a thermal insulation performance is further laminated between the top coating layer 6 and the coating waterproof layer 4. same.

도 3은 비노출공법을 도시한 것으로 부직포 시트층을 사용한 단열 방수 공법의 단면도이다. 도 3에서는 바탕층(1)을 시공한 후, 그 위에 순차적으로 부직포 시트층(2), 도막방수층(4), 다공질 혼합층(3), 도막방수층(4)을 적층하는 것은 도 1a에서와 동일하며, 단지 여기에서는 비노출공법이므로 상기 도막방수층(4) 위에 보호층(8)을 적층하는 것만 다를 뿐이다. 상기 보호층(8)에는 누름 몰탈 또는 콘크리트 등이 적층된다.3 is a cross-sectional view of a heat-insulating waterproof method using a nonwoven fabric sheet layer, showing a non-exposure method. In FIG. 3, after the base layer 1 is constructed, the nonwoven fabric sheet layer 2, the coating film waterproofing layer 4, the porous mixed layer 3, and the coating film waterproofing layer 4 are sequentially stacked thereon as in FIG. 1A. In this case, only the protective layer 8 is laminated on the coating waterproof layer 4 because it is a non-exposure method. Pressed mortar or concrete is laminated on the protective layer 8.

도 4는 비노출공법을 도시한 것으로 부직포 시트층을 사용하지 아니한 단열 방수 공법의 단면도이다. 도 4에서는 바탕층(1)을 시공한 후, 그 위에 순차적으로 프라이머층(7), 도막방수층(4), 다공질 혼합층(3), 도막방수층(4)을 적층하는 것은 도 2a에서와 동일하며, 단지 여기에서는 비노출공법이므로 상기 도막방수층(4) 위에 보호층(8)을 적층하는 것만 다를 뿐이다. 상기 보호층(8)에는 누름 몰탈 또는 콘크리트 등이 적층된다.4 is a cross-sectional view of a heat-insulating waterproof method showing a non-exposure method and not using a nonwoven sheet layer. In FIG. 4, after the base layer 1 is constructed, the primer layer 7, the coating waterproof layer 4, the porous mixed layer 3, and the coating waterproof layer 4 are sequentially stacked thereon, as in FIG. 2A. Since only the non-exposure method is used here, only the protective layer 8 is laminated on the waterproof layer 4. Pressed mortar or concrete is laminated on the protective layer 8.

상기 언급한 바와 같은 본 발명에 따른 다공성 재질을 이용한 폴리우레탄 단열 방수 공법에 의하면, 한번의 시공으로 방수성능과 단열성능을 함께 발휘하여 공기의 단축과 경제적인 이익을 창출할 수 있다. According to the polyurethane insulation waterproofing method using the porous material according to the present invention as mentioned above, it is possible to shorten the air and economic benefits by showing both waterproof and heat insulating performance in a single construction.

본 발명에서는 종래의 기술로는 한계가 있는 탄성 폴리우레탄 도막 방수제에 단열성을 부여하여 별도의 단열 시공이 필요치 않으면서도 신률과 강도가 우수한 단열 폴리우레탄 도막 방수제의 기능을 잘 살릴 수 있는 효과가 있다. 또한, 부직포 쉬트를 사용하여 통상적으로 우레탄 도막 방수제 시공시에 발생할 수 있는 도막 들뜸이나 표면 기포발생 문제 등을 근본적으로 해결할 수 있는 특징이 있다.In the present invention, by providing a thermal insulation to the elastic polyurethane coating waterproofing agent which is limited by the conventional technology, there is an effect that can effectively utilize the function of the insulating polyurethane coating waterproofing excellent in elongation and strength without the need for a separate thermal insulation. In addition, there is a feature that can fundamentally solve the problem of coating film lifting or surface bubble generation that can occur during the construction of the urethane coating film waterproofing agent using a nonwoven fabric sheet.

비록 본 발명에 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 변형을 하는 것이 가능하다. 따라서 첨부된 특허청구범위는 본 발명의 요지에 속하는 이러한 수정이나 변형을 포함한다.Although described in connection with the preferred embodiments mentioned above in the present invention, it is possible to make various modifications or variations without departing from the spirit and scope of the invention. Accordingly, the appended claims include such modifications and variations as fall within the spirit of the invention.

Claims (5)

콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공하는 단계;Constructing a base layer (1) forming a foundation floor comprising concrete; 상기 바탕층(1) 위에 부직포 시트층(2)을 접착하는 단계;Adhering a nonwoven sheet layer (2) onto the base layer (1); 상기 부직포 시트층(2) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계;Stacking a polyurethane coating film waterproof layer (4) on which the powder of the porous material is mixed or not mixed on the nonwoven sheet layer (2); 상기 도막방수층(4) 위에 입자크기 0.1~5mm의 다공성 실리카 및 다공성 무기재료를 포함하는 다공질 혼합층(3)을 적층하는 단계;Stacking a porous mixed layer 3 including porous silica and a porous inorganic material having a particle size of 0.1 to 5 mm on the waterproofing layer 4; 상기 다공질 혼합층(3) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계; 및Stacking a polyurethane coating film waterproof layer (4) on which the porous powder is mixed or not mixed on the porous mixed layer (3); And 상기 도막방수층(4) 위에 도막방수층의 내후성을 보강하기 위한 탑코팅층(6)을 적층하는 단계를 포함하는 것을 특징으로 하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법.Polyurethane insulation waterproofing method using a porous material comprising the step of laminating a top coating layer (6) for reinforcing the weather resistance of the coating film waterproof layer on the coating film waterproof layer (4). 콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공하는 단계;Constructing a base layer (1) forming a foundation floor comprising concrete; 상기 바탕층(1) 위에 접착력을 보강하고 기포발생을 억제하기 위한 프라이머층(7)을 도포하는 단계;Applying a primer layer (7) on the base layer (1) to reinforce adhesion and suppress bubble generation; 상기 프라이머층(7) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계;Stacking a polyurethane coating waterproof layer (4) on which the powder of the porous material is mixed or not mixed on the primer layer (7); 상기 도막방수층(4) 위에 입자크기 0.1~5mm의 다공성 실리카 및 다공성 무기재료를 포함하는 다공질 혼합층(3)을 적층하는 단계;Stacking a porous mixed layer 3 including porous silica and a porous inorganic material having a particle size of 0.1 to 5 mm on the waterproofing layer 4; 상기 다공질 혼합층(3) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계; 및Stacking a polyurethane coating film waterproof layer (4) on which the porous powder is mixed or not mixed on the porous mixed layer (3); And 상기 도막방수층(4) 위에 도막방수층의 내후성을 보강하기 위한 탑코팅층(6)을 적층하는 단계를 포함하는 것을 특징으로 하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법.Polyurethane insulation waterproofing method using a porous material comprising the step of laminating a top coating layer (6) for reinforcing the weather resistance of the coating film waterproof layer on the coating film waterproof layer (4). 제 1항 또는 제 2항에 있어서, 상기 탑코팅층(6)과 도막방수층(4) 사이에는 단열성능을 보강하기 위한 다공성 실리카 또는 다공성 무기재료를 포함하는 다공질층(5)이 적층되는 단계가 더 포함되는 것을 특징으로 하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법.The method according to claim 1 or 2, further comprising the step of laminating a porous layer 5 including porous silica or a porous inorganic material for reinforcing the thermal insulation performance between the top coating layer 6 and the coating film waterproofing layer 4. Polyurethane insulation waterproof method using a porous material, characterized in that included. 콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공하는 단계;Constructing a base layer (1) forming a foundation floor comprising concrete; 상기 바탕층(1) 위에 부직포 시트층(2)을 접착하는 단계;Adhering a nonwoven sheet layer (2) onto the base layer (1); 상기 부직포 시트층(2) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계;Stacking a polyurethane coating film waterproof layer (4) on which the powder of the porous material is mixed or not mixed on the nonwoven sheet layer (2); 상기 도막방수층(4) 위에 입자크기 0.1~5mm의 다공성 실리카 및 다공성 무기 재료를 포함하는 다공질 혼합층(3)을 적층하는 단계;Stacking a porous mixed layer 3 including porous silica and a porous inorganic material having a particle size of 0.1 to 5 mm on the coating waterproof layer 4; 상기 다공질 혼합층(3) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계; 및Stacking a polyurethane coating film waterproof layer (4) on which the porous powder is mixed or not mixed on the porous mixed layer (3); And 상기 도막방수층(4) 위에 보호 누름 몰탈 또는 보호 콘크리트를 포함하는 보호층(8)을 적층하는 단계를 포함하는 것을 특징으로 하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법.Polyurethane insulation waterproof method using a porous material, characterized in that it comprises the step of laminating a protective layer (8) comprising a protective pressing mortar or protective concrete on the coating waterproof layer (4). 콘크리트를 포함하는 기초바닥을 형성하는 바탕층(1)을 시공하는 단계;Constructing a base layer (1) forming a foundation floor comprising concrete; 상기 바탕층(1) 위에 접착력을 보강하고 기포발생을 억제하기 위한 프라이머층(7)을 도포하는 단계;Applying a primer layer (7) on the base layer (1) to reinforce adhesion and suppress bubble generation; 상기 프라이머층(7) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계;Stacking a polyurethane coating waterproof layer (4) on which the powder of the porous material is mixed or not mixed on the primer layer (7); 상기 도막방수층(4) 위에 입자크기 0.1~5mm의 다공성 실리카 및 다공성 무기재료를 포함하는 다공질 혼합층(3)을 적층하는 단계;Stacking a porous mixed layer 3 including porous silica and a porous inorganic material having a particle size of 0.1 to 5 mm on the waterproofing layer 4; 상기 다공질 혼합층(3) 위에 다공성 재질의 분말이 혼합되거나 혼합되지 아니한 폴리우레탄 도막방수층(4)을 적층하는 단계; 및Stacking a polyurethane coating film waterproof layer (4) on which the porous powder is mixed or not mixed on the porous mixed layer (3); And 상기 도막방수층(4) 위에 보호 누름 몰탈 또는 보호 콘크리트를 포함하는 보호층(8)을 적층하는 단계를 포함하는 것을 특징으로 하는 다공성 재질을 이용한 폴리우레탄 단열 방수 공법.Polyurethane insulation waterproof method using a porous material, characterized in that it comprises the step of laminating a protective layer (8) comprising a protective pressing mortar or protective concrete on the coating waterproof layer (4).
KR1020050091107A 2005-09-29 2005-09-29 Polyurethane insulating waterproof systems with hollow material KR100651530B1 (en)