KR100618462B1 - Gelling agent and gel compositions - Google Patents

Gelling agent and gel compositions Download PDF

Info

Publication number
KR100618462B1
KR100618462B1 KR1019980710544A KR19980710544A KR100618462B1 KR 100618462 B1 KR100618462 B1 KR 100618462B1 KR 1019980710544 A KR1019980710544 A KR 1019980710544A KR 19980710544 A KR19980710544 A KR 19980710544A KR 100618462 B1 KR100618462 B1 KR 100618462B1
Authority
KR
South Korea
Prior art keywords
oil
water
gelling agent
acid
clay mineral
Prior art date
Application number
KR1019980710544A
Other languages
Korean (ko)
Other versions
KR20000022128A (en
Inventor
후미아키 마츠자키
도시오 야나키
Original Assignee
가부시키가이샤 시세이도
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 가부시키가이샤 시세이도 filed Critical 가부시키가이샤 시세이도
Priority to KR1019980710544A priority Critical patent/KR100618462B1/en
Publication of KR20000022128A publication Critical patent/KR20000022128A/en
Application granted granted Critical
Publication of KR100618462B1 publication Critical patent/KR100618462B1/en

Abstract

수팽윤성 점토광물과 4차 암모늄염형 양이온 계면활성제와 상온액체의 지방산 또는 고급알코올을 혼합하여 얻어지는 겔화제 또는 유화제, 및 이를 사용한 겔조성물 또는 유화조성물이다. 본 발명에 의하면 광범위한 유분에 첨가혼합하더라도 안정성, 안전성, 사용성에 우수한 겔조성물 또는 유화조성물을 제공할 수가 있다.A gelling agent or emulsifier obtained by mixing a water-swellable clay mineral with a quaternary ammonium salt type cationic surfactant and a fatty acid or a higher alcohol of a room temperature liquid, and a gel composition or emulsion composition using the same. According to the present invention, it is possible to provide a gel composition or an emulsion composition which is excellent in stability, safety and usability even if it is mixed with a wide range of oils.

본 발명의 겔화제 또는 유화제를 사용한 겔조성물 또는 유화조성물은, 예를들면, 화장품, 의약부외품등의 기제로서 바람직하게 사용된다.The gel composition or emulsion composition using the gelling or emulsifying agent of the present invention is preferably used as a base for cosmetics, quasi-drugs and the like.

또, 상기 유화조성물에, 자외선방어제분말을 배합한 피부가 햇볕에 타서 검게 되는 일을 방지하는 화장재료는, 살갗에의 밀착성이 좋고, 내수성에 우수하고, 땀 또는 바다나 풀에서의 활동에 동반하는 물과의 접촉에 의해서도, 자외선방어제 분말에 의한 흰색의 두드러짐이 없는 우수한 사용성을 갖는 것이다. 따라서, 흰색의 두드러짐을 마음에 두지 않고, 필요량의 자외선 방어제 분말을 배합할 수 있으므로, 특히 높은 자외선방어효과를 기대하는 경우에 유용하다.Moreover, the cosmetic material which prevents the skin which mix | blended the ultraviolet protection agent powder with the said emulsion composition from becoming black in the sun has good adhesiveness to skin, and is excellent in water resistance, and is excellent in sweat or activity in the sea or a pool By contact with the accompanying water, it has the outstanding usability without whiteness by the ultraviolet protective agent powder. Therefore, it is possible to mix | blend a required amount of ultraviolet protective agent powder without minding white outstandingness, and is especially useful when expecting a high ultraviolet protection effect.

Description

겔화제 및 겔조성물{GELLING AGENT AND GEL COMPOSITIONS}Gelling agent and gel composition {GELLING AGENT AND GEL COMPOSITIONS}

(1) 본 발명은 겔화제 및 겔 조성물에 관한 것이다. 더욱 상세하게는, 화장품, 의약부외품 등의 용도에 있어서, 광범한 유분에 첨가혼합함으로써 안정성, 안전성, 사용성에 우수한 유성겔을 생성할 수 있는 겔화제 및 겔 조성물에 관한 것이다.(1) The present invention relates to a gelling agent and a gel composition. More specifically, the present invention relates to a gelling agent and a gel composition capable of producing oily gel excellent in stability, safety and usability by adding and mixing to a wide range of oils in the use of cosmetics, quasi-drugs and the like.

(2) 본 발명은 유화제 및 유화조성물에 관한 것이다. 더욱 상세하게는, 종래의 비이온성 계면활성제를 사용하지 않고, 광범한 유분에 첨가혼합함으로써, 유중수형(이하, W/O형 이라고도함)에 유화할 수 있는 유화제, 및 이를 사용한 안정성, 안전성, 사용성에 우수한 유화조성물에 관한 것이다.(2) The present invention relates to an emulsifier and an emulsion composition. More specifically, an emulsifier which can be emulsified in a water-in-oil type (hereinafter also referred to as W / O type) by adding and mixing to a wide range of oils without using a conventional nonionic surfactant, and stability, safety, It relates to an emulsion composition excellent in usability.

(3) 본 발명은 피부가 햇볕에 타서 검게되는 일을 방지하는 화장재료에 관한 것이다. 더욱 상세하게는, 내수성에 우수하고, 물과 접촉하였을 경우에 자외선 방어제 분말의 흰색이 두드러지지 않는 것을 특징으로 하는 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료에 관한 것이다.(3) The present invention relates to a cosmetic material which prevents the skin from darkening in the sun. More specifically, the present invention relates to a cosmetic material which is excellent in water resistance and prevents skin from blacking in the sun, which is characterized in that the white color of the UV protective agent powder is not noticeable when in contact with water.

(1) 종래, 유팽윤성 겔화제로서는, 수팽윤성점토광물(이하, 단순히 점토광물이라함)의 층간에 개재하는 물이나 교환성 양이온을 4차 암모늄염형 유기양이온으로 양이온교환하여 얻어지는 유기변성점토광물에 특정의 비이온활성제를 혼합처리하는 것으로 사용성이 양호한 겔이 조제가능한 것이 알려져 있다. 또, 유기변성점토광물을 비이온활성제에 대신하여 복합지질로 처리한 겔화제를 사용하는 겔화방법도 이미 알려져 있다.(1) Conventionally, as an oil-swellable gelling agent, organic modified clay minerals obtained by cation-exchanging water or exchangeable cations between layers of water-swellable clay minerals (hereinafter simply referred to as clay minerals) with quaternary ammonium salt type organic cations. It is known that a gel having good usability can be prepared by mixing and treating a specific nonionic active agent. Moreover, the gelation method using the gelling agent which processed the organic modified clay mineral with the complex lipid instead of the nonionic active agent is also known.

그러나, 상기의 겔화제를 사용한 겔화방법에서는, 사용하는 유분의 차이에 의하여 얻어지는 겔의 구조가 크게 다르기 때문에, 안정성이나 사용성이 양호한 겔을 얻기 위해서는 사용하는 유분에 맞추어서 그때마다 비이온 활성제나 복합 지질의 종류를 선별할 필요가 있었다.However, in the gelation method using the gelling agent described above, since the structure of the gel is greatly different due to the difference in the oil content to be used, in order to obtain a gel having good stability and usability, a nonionic activator or a complex lipid is used every time according to the oil content to be used. It was necessary to select the type of.

또, 충분한 안정성을 유지할 수 있는 겔은, 도포시의「퍼짐」이 나쁘고 사용성에 뒤떨어지는 경향이 있었다.Moreover, the gel which can maintain sufficient stability tended to be bad in "spreading" at the time of application | coating and to be inferior to usability.

본 발명자등은, 상술의 문제점에 비추어 예의 연구를 거듭한 결과, 수팽윤성 점토광물을 4차 암모늄염형 양이온 계면활성제와 상온액체의 지방산으로 혼합처리함으로써 얻어지는 겔화제가 광범한 유분에 대하여 안정성, 안전성, 사용성에 우수한 유성겔을 생성할 수 있는 것을 발견하고, 본 발명을 완성하기에 이르렀다.The inventors have conducted extensive research in view of the above-mentioned problems, and as a result, the gelling agent obtained by mixing the water-swellable clay mineral with the quaternary ammonium salt type cationic surfactant and the fatty acid of normal temperature liquid is stable, safe, It has been found that an oily gel excellent in usability can be produced, and the present invention has been completed.

또한, 수팽윤성점토광물을 4차 암모늄염형 양이온계면활성제와 상온액체의 고급알코올로 혼합처리함으로써 얻어지는 겔화제가 광범한 유분에 대하여 안정성, 안전성, 사용성에 우수한 유성겔을 생성할 수 있는 것을 발견하고 본 발명을 완성하기에 이르렀다.In addition, the gelling agent obtained by mixing the water-swellable clay mineral with a quaternary ammonium salt type cationic surfactant and a higher alcohol of room temperature liquid was found to be able to produce oily gel having excellent stability, safety and usability against a wide range of oils. The invention has been completed.

본 발명은, 광범한 유분에 첨가혼합하더라도 안정성, 안전성, 사용성에 우수한 유성겔을 생성할 수 있는 겔화제 및 이를 사용한 겔조성물을 제공하는것을 목적으로 한다.An object of the present invention is to provide a gelling agent and a gel composition using the same, which can produce an oily gel excellent in stability, safety, and usability even when added to a wide range of oils.

(2) 종래, W/O형 유화조성물을 얻는데는 유화제로서 HLB치가 1∼12의 친유성계면 활성제, 예를들면, 글리세린지방산에스테르, 소르비탄 지방산에스테르등의 다가알코올 지방산 에스테르계 계면활성제가 사용되고 있었다.(2) Conventionally, in order to obtain a W / O type emulsion composition, a lipophilic surfactant having an HLB value of 1 to 12, for example, a polyhydric alcohol fatty acid ester surfactant such as glycerin fatty acid ester or sorbitan fatty acid ester is used as an emulsifier. there was.

또, 광범한 유분을 안정하게 유화할 수 있는 유화제로서는, 일본특개소 61-129033호 공보에 개시되는 바와같이 유기변성점토 광물과 비이온성 계면활성제로 이루어지는 유화제조성물이나, 유화가 어려운 실리콘오일을 안정하게 유화하는 유화제 조성물로서 일본특개소 61-212321 공보에 개시되는 바와같은 유기변성 점토광물과 폴리옥시알킬렌 변성 오르가노 폴리실록산의 조합 등이 알려져 있다.Moreover, as an emulsifier which can emulsify a wide range of oils stably, as disclosed in Japanese Patent Laid-Open No. 61-129033, an emulsified composition composed of an organic modified clay mineral and a nonionic surfactant, or a silicone oil which is difficult to emulsify, is stabilized. As the emulsifier composition which emulsifies easily, a combination of an organic modified clay mineral and a polyoxyalkylene-modified organopolysiloxane as disclosed in Japanese Patent Laid-Open No. 61-212321 is known.

그러나, 상기의 유화제에서는, 안정성이나 사용성이 양호한 유화조성물을 얻기 위해서는, 사용하는 유분에 맞추어서 그때마다 유화제의 종류를 선별할 필요가 있었다.However, in the above emulsifier, in order to obtain an emulsion composition having good stability and usability, it is necessary to select a kind of emulsifier each time according to the oil fraction to be used.

또, 다량의 극성유를 유화하는 경우에 있어서는, 다량의 유화제가 필요하게 되고, 다량의 유화제의 사용은 유화조성물의 안전성 및 사용성을 나쁘게 하는 경우가 있었다.In the case of emulsifying a large amount of polar oil, a large amount of emulsifier is required, and the use of a large amount of emulsifier may deteriorate the safety and usability of the emulsion composition.

본 발명자등은, 상술의 문제점에 비추어 예의 연구를 거듭한 결과, 수팽윤성 점토광물을 4차 암모늄염형 양이온 계면활성제와 상온액체의 지방산으로 혼합처리함으로서 얻어지는 유화제가, 광범한 유분에 대하여 안정성, 안전성, 사용성에 우수한 유화조성물을 생성할 수 있는 것을 발견하고, 본 발명을 완성하기에 이르렀다. The present inventors have conducted extensive research in view of the above-mentioned problems, and as a result, the emulsifier obtained by mixing and treating a water-swellable clay mineral with a quaternary ammonium salt type cationic surfactant and a fatty acid of a room temperature liquid is stable and safe to a wide range of oils. The inventors have found that an emulsion composition excellent in usability can be produced, and have completed the present invention.

더욱더, 수팽윤성점토광물을 4차 암모늄염형 양이온 계면활성제와 상온액체의 고급알코올로 혼합처리함으로써 얻어지는 유화제가 광범한 유분에 대하여 안정성, 안전성, 사용성에 우수한 유화조성물을 생성할 수 있는 것을 발견하고, 본 발명을 완성하기에 이르렀다.Furthermore, it has been found that the emulsifier obtained by mixing the water-swellable clay mineral with a quaternary ammonium salt type cationic surfactant and a higher alcohol of room temperature liquid can produce an emulsion composition excellent in stability, safety and usability for a wide range of oils. The present invention has been completed.

본 발명은, 광범한 유분에 첨가혼합하더라도, 안정성, 안전성, 사용성에 우수한 W/O형 유화조성물을 생성할 수 있는 유화제 및 이를 사용한 W/O형 유화조성물을 제공하는것을 목적으로 한다. An object of the present invention is to provide an emulsifier capable of producing a W / O type emulsion composition excellent in stability, safety, and usability even if added to a wide range of oils, and a W / O type emulsion composition using the same.

(3) 유중수형유화조성물(이하, W/O형 유화조성물 이라함)은, 기제로서 내수성이 양호하기 때문에 햇볕에 타서 검게되는일을 방지하는 화장재료에 사용되어 왔다.(3) Water-in-oil type emulsion composition (hereinafter referred to as W / O type emulsion composition) has been used in cosmetic materials for preventing blackening in the sun because of its good water resistance.

일반적으로, W/O형 유화조성물은 온도안정성, 사용성에 우수한 계가 얻기 어렵다라는 결점이 있고, 이 결점을 개량한 기술로서, 수팽윤성 점토광물을 4차 암모늄염형 양이온 계면활성제와, 비이온성계면활성제로 처리하여 얻어지는 유기변성점토광물로 유화한 W/O형 유화제 조성물이 알려져 있다(일본특개소 61-114721호 공보, 일본특개소 61-129033호 공보, 일본특개소 61-212321호 공보).Generally, the W / O type emulsion composition has a drawback that a system excellent in temperature stability and usability is hardly obtained. As a technique to improve the drawback, a water-swellable clay mineral is used as a quaternary ammonium salt type cationic surfactant and a nonionic surfactant. W / O-type emulsifier compositions emulsified with organic modified clay minerals obtained by treatment with ethylene are known (Japanese Patent Laid-Open No. 61-114721, Japanese Patent Laid-Open No. 61-129033, Japanese Patent Laid-Open No. 61-212321).

또, 이 기술을 사용한 W/O형 유화조성물에 자외선 방어제로서 산화티탄이나 산화아연을 배합한 햇볕에 타서 검게되는 일을 방지하는 화장재료, 또한, 자외선 방어제분말의 도포색을 두드러지지 않게 하는 기술로서, 소수화 방추상 산화티탄을 사용하는 기술(일본 특개평7-258055호 공보)이 알려져 있다.In addition, a cosmetic material which prevents blackening in the sun containing titanium oxide or zinc oxide as a UV protective agent in a W / O type emulsion composition using this technology, and also does not stand out the coating color of the ultraviolet protective powder. As a technique to be used, a technique using a hydrophobized fusiform titanium oxide (Japanese Patent Laid-Open No. 7-258055) is known.

그러나, 종래의 자외선 방어제 분말을 배합한 햇볕에 타서 검게되는 일을 방지하는 화장재료는, 땀이나 바다, 풀(pool)에서의 활동에 동반하는 물과의 접촉에 의하여, 자외선 방어제분말이 희게 떠오른다라는 문제가 있었다.However, the cosmetic material which prevents blacking by the sun which mix | blended the conventional sunscreen powder contains the sunscreen powder by contact with sweat, the sea, and water accompanying activity in a pool. There was a problem that emerged white.

본 발명자등은, 상술의 문제점에 비추어, 상기 유기변성점토광물을 사용한 W/O형 햇볕에 타서 검게 되는일을 방지하는 화장재료에 있어서, 물과 접촉하였을 경우의 흰색이 두드러지지 않는 햇볕에 타서 검게되는 일을 방지하는 화장재료를 얻기 위하여 예의 연구한 결과, 종래의 비이온성 계면활성제를 사용하지 않고, 상온액체의 지방산 또는 고급알코올을 배합하면 해결될 수 있음을 발견하고, 본 발명을 완성하기에 이르렀다.The present inventors, in view of the above-mentioned problems, in a cosmetic material which prevents the blackening of the W / O type sun using the organic modified clay mineral, in which the white color in contact with water does not stand out, As a result of intensive research to obtain a cosmetic material that prevents blackening, it is found that by combining a fatty acid or a higher alcohol of a room temperature liquid without using a conventional nonionic surfactant, it can be solved. Reached.

본 발명은 내수성에 우수하고, 물과 접촉하였을 경우에 자외선 방어제 분말의 흰색이 두드러지지 않는 것을 특징으로 하는 햇볕에 타서 검게되는 일을 방지하는 화장재료를 제공하는 것을 목적으로 한다.An object of the present invention is to provide a cosmetic material which is excellent in water resistance and prevents blackening in the sun, which is characterized in that the white color of the ultraviolet protective agent powder does not stand out when contacted with water.

[발명의 개시][Initiation of invention]

(1) 즉, 본 발명은, 수팽윤성점토광물과 4차 암모늄염형 양이온 계면활성제와 상온액체의 지방산을 혼합하여 얻어지는 것을 특징으로 하는 겔화제를 제공하는 것이다.(1) In other words, the present invention provides a gelling agent obtained by mixing a water-swellable clay mineral, a quaternary ammonium salt type cationic surfactant, and a fatty acid of a room temperature liquid.

또, 본 발명은, 상기 4차 암모늄염형 양이온 계면활성제의 혼합량이 상기 수팽윤성 점토광물 100g에 대하여, 60∼140밀리당량인것을 특징으로 하는 상기의 겔화제를 제공하는 것이다.The present invention also provides the above-mentioned gelling agent, characterized in that the mixed amount of the quaternary ammonium salt type cationic surfactant is 60 to 140 milliliter equivalents to 100 g of the water-swellable clay mineral.

더욱이, 본 발명은, 상기 상온액체의 지방산의 혼합량이 상기 수팽윤성 점토광물 100g에 대하여, 1∼500g인것을 특징으로 하는 상기의 겔화제를 제공하는 것이다.Furthermore, the present invention provides the above-mentioned gelling agent, characterized in that the mixing amount of the fatty acid of the room temperature liquid is 1 to 500 g with respect to 100 g of the water-swellable clay mineral.

또, 본 발명은, 상기의 겔화제와 유분을 함유하는 것을 특징으로 하는 겔조성물을 제공하는 것이다.The present invention also provides a gel composition comprising the above-mentioned gelling agent and an oil.

더욱이, 본 발명은, 수팽윤성 점토광물과 4차 암모늄염형 양이온 계면활성제와 상온액체의 고급알코올을 혼합하여 얻어지는 것을 특징으로 하는 겔화제를 제공하는 것이다.Furthermore, the present invention provides a gelling agent obtained by mixing a water-swellable clay mineral, a quaternary ammonium salt type cationic surfactant, and a higher alcohol of a room temperature liquid.

또, 본 발명은, 상기 4차 암모늄염형 양이온 계면활성제의 혼합량이 상기 수팽윤성 점토광물 100g에 대하여, 60∼140밀리당량인 것을 특징으로 하는 상기의 겔화제를 제공하는 것이다.Moreover, this invention provides the said gelling agent characterized in that the mixing amount of the said quaternary ammonium salt type | mold cationic surfactant is 60-140 mm equivalent with respect to 100 g of said water swellable clay minerals.

더욱이, 본 발명은, 상기 상온액체의 고급알코올의 혼합량이, 상기 수팽윤성 점토광물 100g에 대하여 1∼500g인 것을 특징으로 하는 상기의 겔화제를 제공하는 것이다.Further, the present invention provides the above-mentioned gelling agent, characterized in that the mixed amount of the higher alcohol of the room temperature liquid is 1 to 500 g with respect to 100 g of the water-swellable clay mineral.

또, 본 발명은, 상기의 겔화제와 유분을 함유하는 것을 특징으로 하는 겔조성물을 제공하는 것이다.The present invention also provides a gel composition comprising the above-mentioned gelling agent and an oil.

(2) 즉, 본 발명은, 수팽윤성 점토광물과 4차 암모늄염형 양이온 계면활성제와 상온 액체의 지방산을 혼합하여 얻어지는 것을 특징으로 하는 유화제를 제공하는 것이다.(2) That is, this invention provides the emulsifier characterized by mixing the water-swellable clay mineral, the quaternary ammonium salt type cationic surfactant, and the fatty acid of normal temperature liquid.

또, 본 발명은, 상기 4차 암모늄염형 양이온 계면활성제의 혼합량이 상기 수팽윤성 점토광물 100g에 대하여, 60∼140밀리당량인 것을 특징으로 하는 상기의 유화제를 제공하는 것이다.Moreover, this invention provides the said emulsifier characterized by the mixed amount of the said quaternary ammonium salt type | mold cationic surfactant with respect to 100 g of said water swellable clay minerals.

더욱이, 본 발명은, 상기 상온액체의 지방산의 혼합량이 상기 수팽윤성 점토광물 100g에 대하여, 1∼500g인 것을 특징으로 하는 상기의 유화제를 제공하는 것이다.Moreover, this invention provides the said emulsifier characterized in that the mixing amount of the fatty acid of the said normal-temperature liquid is 1-500g with respect to 100g of said water swellable clay minerals.

또, 본 발명은, 상기의 유화제와 유분과 물을 함유하는 것을 특징으로 하는 유화조성물을 제공하는 것이다. The present invention also provides an emulsified composition comprising the above emulsifier, oil and water.

더욱이, 본 발명은, 수팽윤성점토광물과 4차 암모늄염형 양이온 계면활성제와 상온액체의 고급알코올을 혼합하여 얻어지는 것을 특징으로 하는 유화제를 제공하는 것이다.Furthermore, the present invention provides an emulsifier, which is obtained by mixing a water-swellable clay mineral, a quaternary ammonium salt type cationic surfactant, and a higher alcohol of a room temperature liquid.

또, 본 발명은, 상기 4차 암모늄염형 양이온 계면활성제의 혼합량이 상기 수팽윤성점토광물 100g에 대하여, 60∼140밀리당량인 것을 특징으로 하는 상기의 유화제를 제공하는 것이다.Moreover, this invention provides the said emulsifier characterized by the mixed amount of the said quaternary ammonium salt type | mold cationic surfactant with respect to 100g of said water swellable clay minerals.

더욱이, 본 발명은, 상기 상온 액체의 고급알코올의 혼합량이 상기 수팽윤성점토광물 100g에 대하여, 1∼500g인 것을 특징으로 하는 상기의 유화제를 제공하는 것이다.Moreover, this invention provides the said emulsifier characterized in that the mixing amount of the higher alcohol of the said normal temperature liquid is 1-500g with respect to 100g of said water swellable clay minerals.

또, 본 발명은, 상기의 유화제와 유분과 물을 함유하는 것을 특징으로 하는 유화조성물을 제공하는 것이다.The present invention also provides an emulsified composition comprising the above emulsifier, oil and water.

(3) 즉, 본 발명은, 상기의 유화조성물이, 또한 자외선 방어제 분말을 함유하는 것을 특징으로 하는 피부가 햇볕에 타서 검게되는 일을 방지하는 화장재료를 제공하는 것이다.(3) In other words, the present invention provides a cosmetic material which prevents the skin from blacking in the sun, wherein the emulsion composition further contains a UV protective agent powder.

[발명을 실시하기위한 최량의 형태][Best form for carrying out the invention]

이하, 본 발명의 구성요건을 더욱 상세히 설명한다.Hereinafter, the configuration requirements of the present invention will be described in more detail.

[겔화제, 겔조성물, 유화제, 유화조성물][Gelating agent, gel composition, emulsifier, emulsion composition]

본 발명에 사용하는 수팽윤성 점토광물은, 3층구조를 갖는 콜로이드성 함수규산알루미늄의 일종으로, 하기 일반식The water-swellable clay mineral used in the present invention is a kind of colloidal hydrous aluminum silicate having a three-layer structure, and has the following general formula

(X, Y)2-3(Si, Al)4O10(OH)2Z1/3·nH2O(X, Y) 2-3 (Si, Al) 4 O 10 (OH) 2 Z 1 / 3nH 2 O

단, X = Al, Fe(III), Mn(III), Cr(III)Provided that X = Al, Fe (III), Mn (III), Cr (III)

Y = Mg, Fe(II), Ni, Zn, Li, Mn(II)    Y = Mg, Fe (II), Ni, Zn, Li, Mn (II)

Z = K, Na, 1/2Ca, 1/2Mg    Z = K, Na, 1 / 2Ca, 1 / 2Mg

로 표시되고, 구체적으로는, 예를들면, 몬모릴나이트, 사포나이트 및 헥토라이트 등의 천연 또는 합성(이경우, 식중의 (OH)기가 불소로 치환된것)의 몬모릴나이트군(시판품에서는 비검, 구니피아, 라포나이트등이 있음) 및 나트륨 실리릭 마이카나 나트륨 또는 리튬 테니오라이트의 이름으로 알려지는 합성운모(시판품에서는 다이모나이트: 토피공업(주) 등이 있다)등을 들 수 있다.And specifically, for example, montmorillonite group (non-gum in commercially available products) of natural or synthetic (in this case, (OH) group substituted with fluorine in the formula) such as montmorillonite, saponite and hectorite , Guineapia, laponite, etc.) and synthetic mica known in the name of sodium silicic mica or sodium or lithium teniolite (the commercially available products include dimonite: Toffee Co., Ltd.). .

본 발명에 사용하는 4차 암모늄염형 양이온 계면활성제는 하기 일반식The quaternary ammonium salt type cationic surfactant used for this invention is a following general formula

(식중 R1은 탄소수 10∼22의 알킬기 또는 벤질기, R2는 메틸기 또는 탄소수 10∼22의 알킬기, R3과 R4는 탄소수 1∼3의 알킬기 또는 히드록시 알킬기, X는 할로겐원자 또는 메틸술페이트 잔기를 나타낸다.)으로 표시되는 것이다.Wherein R 1 is an alkyl group or benzyl group having 10 to 22 carbon atoms, R 2 is a methyl group or an alkyl group having 10 to 22 carbon atoms, R 3 and R 4 are an alkyl group or hydroxy alkyl group having 1 to 3 carbon atoms, X is a halogen atom or methyl Sulfate residues).

구체적으로는 예를들면, 도데실트리메틸암모늄클로라이드, 미리스틸트리메틸암모늄클로라이드, 세틸트리메틸암모늄클로라이드, 스테아릴트리메틸암모늄클로라이드, 아라킬트리메틸암모늄클로라이드, 베헤닐트리메틸암모늄클로라이드, 미리스틸디메틸에틸암모늄클로라이드, 세틸디메틸에틸암모늄클로라이드, 스테아릴디메틸에틸암모늄클로라이드, 아라킬디메틸에틸암모늄클로라이드, 베헤닐디메틸에틸암모늄클로라이드, 미리스틸디에틸메틸암모늄클로라이드, 세틸디에틸메틸암모늄클로라이드, 스테아릴디에틸메틸암모늄클로라이드, 아라킬디에틸메틸암모늄클로라이드, 베헤닐디에틸메틸암모늄클로라이드, 벤질디에틸메틸암모늄클로라이드, 벤질디메틸세틸암모늄클로라이드, 벤질디메틸스테아릴암모늄클로라이드, 벤질디메틸베헤닐암모늄클로라이드, 벤질메틸에틸세틸암모늄클로라이드, 벤질메틸에틸스테아릴암모늄클로라이드, 디베헤닐디히드록시에틸암모늄클로라이드 및 상당하는 프로미드 등, 또한, 디팔미틸프로필에틸암모늄메틸술페이트 등을 들 수 있다. 본 발명의 실시에 임해서는, 이들중 1종 또는 2종 이상이 임의로 선택된다.Specifically, for example, dodecyltrimethylammonium chloride, myristyl trimethylammonium chloride, cetyltrimethylammonium chloride, stearyltrimethylammonium chloride, arachyltrimethylammonium chloride, behenyltrimethylammonium chloride, myristyldimethylethylammonium chloride, cetyl Dimethylethylammonium chloride, stearyldimethylethylammonium chloride, aralkyldimethylethylammonium chloride, behenyldimethylethylammonium chloride, myristyldiethylmethylammonium chloride, cetyldiethylmethylammonium chloride, stearyldiethylmethylammonium chloride, ara Kyldiethylmethylammonium chloride, behenyldiethylmethylammonium chloride, benzyldiethylmethylammonium chloride, benzyldimethylcetylammonium chloride, benzyldimethylstearylammonium chloride, benzyldimethylbehenyl ammonium chloride Chloride, benzyl methylethyl cetyl ammonium chloride, benzyl methylethyl stearyl ammonium chloride, di behe nildi hydroxyethyl ammonium chloride, and corresponding pro mid to the like, and, di-palmityl ethyl ammonium methyl sulfate and the like. In the practice of the present invention, one or two or more of these are arbitrarily selected.

본 발명에 사용하는 상온 액체의 지방산으로서는, 예를 들면, 올레산, 이소스테아르산, 리놀레산, 리놀렌산, 에이코사 펜타엔산, 도코사 헥사엔산 등을 들 수 있다. 본 발명의 실시에 임해서는 이들중 1종 또는 2종 이상이 임의로 선택된다.As a fatty acid of the normal temperature liquid used for this invention, oleic acid, isostearic acid, linoleic acid, linolenic acid, eicosapentaenoic acid, docosa hexaenoic acid, etc. are mentioned, for example. In the practice of the present invention, one or two or more of these are arbitrarily selected.

또, 본 발명에 사용하는 상온 액체의 고급알코올로서는, 올레일알코올, 이소스테아릴알코올, 옥틸도데카놀, 데실테트라데카놀, 호호바알코올 등을 들 수 있다. 본발명의 실시에 임해서는 이들중 1종 또는 2종 이상이 임의로 선택된다.Moreover, oleyl alcohol, isostearyl alcohol, octyl dodecanol, decyl tetradecanol, jojoba alcohol, etc. are mentioned as a higher alcohol of the normal temperature liquid used for this invention. In the practice of the present invention, one or two or more of these are arbitrarily selected.

본 발명의 겔화제 또는 유화제는, 상기의 필수성분을 단순히 혼합함으로써 제조할수가 있다. 구체적으로는, 예를 들면, 물, 아세톤 혹은 저급알코올 등의 저 비등점 용제중에서 점토광물과 4차 암모늄염형 양이온활성제와 상온액체의 지방산 또는 고급알코올을 분산교반처리하든가, 또는, 미리 점토광물과 제4차 암모늄 염형 양이온 계면활성제를 저비등점 용매중에서 처리하여 양이온 변성점토광물(이하, 유기변성점토광물 이라고도 함)을 얻은후, 상온 액체의 지방산 또는 고급알코올로 혼합처리하고, 뒤이어 저비등점 용제를 제거함으로써 얻어진다. 더욱이, 본 발명에 있어서는, 저비등점용제를 제거하지 않고 겔화제 또는 유화제로서 제공하는것도 가능하다.The gelling agent or emulsifier of the present invention can be produced by simply mixing the above essential ingredients. Specifically, for example, the clay mineral and the quaternary ammonium salt type cationic activator and the fatty acid or higher alcohol of normal temperature liquid are dispersed and stirred in a low boiling point solvent such as water, acetone or lower alcohol, or the clay mineral and agent The quaternary ammonium salt type cationic surfactant was treated in a low boiling point solvent to obtain a cationic modified clay mineral (hereinafter referred to as an organic modified clay mineral), followed by mixing with a fatty acid or a higher alcohol in a room temperature liquid, followed by removing a low boiling point solvent. It is obtained by. Moreover, in this invention, it is also possible to provide as a gelling agent or an emulsifier, without removing a low boiling point solvent.

4차 암모늄염형 양이온 계면활성제와 상온액체의 지방산 또는 고급알코올이 점토광물의 층간에 들어감으로써, 점토광물의 층간은 넓어진 상태로 되므로 X선 회절로 장면(長面)간격을 측정함으로써 4차 암모늄염형 양이온 계면활성제와 상온액체의 지방산 또는 고급알코올의 흡착의 유무를 확인할 수 있다.As the quaternary ammonium salt type cationic surfactant and the fatty acid or higher alcohol of the room temperature liquid enter the layers of the clay minerals, the layers of the clay minerals become widened, and thus the quaternary ammonium salt type is determined by measuring the scene interval by X-ray diffraction. Adsorption of fatty acids or higher alcohols between cationic surfactants and room temperature liquids can be confirmed.

본 발명의 겔화제 또는 유화제중의 4차 암모늄염형 양이온 계면활성제의 함유량은 점토광물 100g에 대하여, 60∼140밀리당량인 것이 바람직하다. 또, 본 겔화제 또는 유화제중의 상온액체의 지방산 또는 고급알코올 함유량은, 점토광물 100g에 대하여, 1∼500g이 바람직하고, 더욱 바람직하게는 5∼400g이다. 지방산 또는 고급알코올 함유량이 1g 미만에서는 점토광물의 층간이 충분히 넓어지지 않고 겔화능력이 불충분하게 되고, 500g을 초과하면, 겔이 시간이 경과하면서 안정성이 나빠지는 경우가 있다.It is preferable that content of the quaternary ammonium salt type | mold cationic surfactant in the gelling agent or emulsifier of this invention is 60-140 milliequivalents with respect to 100g of clay minerals. The fatty acid or higher alcohol content of the room temperature liquid in the gelling agent or the emulsifier is preferably 1 to 500 g, more preferably 5 to 400 g based on 100 g of the clay mineral. If the fatty acid or higher alcohol content is less than 1 g, the interlayer of the clay mineral does not become wide enough, and the gelling ability is insufficient. If the content exceeds 500 g, the gel may deteriorate in stability over time.

본 발명의 겔화제는, 광범위의 유분중에서 첨가할 수가 있고, 점토광물을 이용한 종래의 겔화제에 비교하여 안정성, 안전성, 사용성에 우수한 유성겔조성물을 생성할 수가 있다.The gelling agent of the present invention can be added in a wide range of oils, and can produce an oily gel composition which is superior in stability, safety and usability as compared with the conventional gelling agent using clay minerals.

본 발명의 유화제는, 광범위의 유분과 물에 첨가하여 W/O형으로 유화할수가 있고, 점토광물을 이용한 종래의 유화제에 비교하여, 안정성, 안전성, 사용성에 우수한 유화조성물을 생성할수가 있다.The emulsifier of the present invention can be added to a wide range of oil and water to emulsify in W / O type, and can produce an emulsion composition excellent in stability, safety, and usability as compared with conventional emulsifiers using clay minerals.

본 발명의 겔조성물 또는 유화조성물에 사용하는 유분은, 화장재료, 의약품 등에서 사용되는 일반적인 유분을 전부 사용할 수가 있고, 그 범위도 극성유로부터 비극성유까지 폭넓게 사용할수가 있다.As the oil component used in the gel composition or the emulsion composition of the present invention, all of the common oils used in cosmetic materials, pharmaceuticals, and the like can be used, and the range thereof can be widely used from polar oils to nonpolar oils.

본 발명에 사용하는 유분을, 구체적으로 예시하면, 액체유지로서는, 아보카도유, 동백기름, 터틀유, 마카데미아낫유, 옥수수유, 밍크유, 올리브유, 유채기름, 노른자유, 참기름, 퍼시크유, 밀배아유, 사잔카유, 피마자유, 아마인유, 홍화기름, 면실유, 들기름, 대두유, 낙화생유, 다실유, 비자나무유, 쌀겨기름, 지나오동나무유, 일본오동나무유, 호호바유, 배아유, 트리글리세린, 트리옥탄산글리세린, 트리이소팔미트산 글리세린등을 들 수 있다.Specific examples of the oil fraction used in the present invention include avocado oil, camellia oil, turtle oil, macadamia nut oil, corn oil, mink oil, olive oil, rapeseed oil, yolk oil, sesame oil, and persian oil. , Wheat germ oil, sazanca oil, castor oil, linseed oil, safflower oil, cottonseed oil, perilla oil, soybean oil, peanut oil, tea seed oil, non-tree oil, rice bran oil, paulownia oil, Japanese paulownia oil, jojoba oil, embryo Oil, triglycerine, glycerin trioctanoate, glycerin triisopalmitate, etc. are mentioned.

고체유지로서는, 카카오지, 야자유, 마지, 경화야자유, 팜유, 우지, 양지, 경화우지, 팜핵유, 돈지, 우골지, 목랍핵유, 경화유, 우각지, 목랍, 경화피마자유 등을 들 수 있다.Examples of the solid fats and oils include kakaoji, palm oil, marzipan, hardened palm oil, palm oil, tallow, sunny place, hardened fat, palm kernel oil, pork fat, beef bone, wax core oil, hardened oil, right angle paper, wax, hardened castor oil and the like.

납류로서는, 밀랍, 캉델라랍, 면랍, 카우나우바랍, 베이베리랍, 백랍, 고래랍, 몬탄랍, 쌀겨랍, 라놀린, 케이폭랍, 아세트산 라놀린, 액상라놀린, 사탕수수랍, 라놀린지방산이소프로필, 라우르산헥실, 환원라놀린, 호호바랍, 경질라놀린, 셀락랍, POE 라놀린알코올에테르, POE 라놀린알코올아세테이트, POE콜레스테롤에테르, 라놀린지방산폴리에틸렌글리콜, POE수소첨가라놀린알코올에테르 등을 들 수 있다.As lead, beeswax, candelalap, cottonseed, kaunaurabap, bayberrywab, pewter, whalewab, montanwab, rice wax, lanolin, kappa wax, lanolin acetate, liquid lanolin, sugarcane, lanolin fatty acid isopropyl, Hexyl lauric acid, reduced lanolin, jojoba barb, hard lanolin, shellac, POE lanolin alcohol ether, POE lanolin alcohol acetate, POE cholesterol ether, lanolin fatty acid polyethylene glycol, POE hydrogenated lanolin alcohol ether, etc. are mentioned.

탄화수소유로서는, 유동파라핀, 오조케라이트, 스쿠알란, 프리스탄, 파라핀, 세레신, 스쿠알란, 와셀린, 마이크로크리스탈린 왁스 등을 들 수 있다.Examples of hydrocarbon oils include liquid paraffin, ozokerite, squalane, pristane, paraffin, ceresin, squalane, waselin, microcrystalline wax and the like.

고급지방산으로서는, 예를들면, 라우르산, 미리스트산, 팔미트산, 스테아르산, 베헨(베헤닌)산, 12-히드록시 스테아르산, 운데실렌산, 톨루산 등을 들 수 있다. Examples of higher fatty acids include lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, 12-hydroxy stearic acid, undecylenic acid, toluic acid, and the like.

고급알코올로서는, 예를들면, 세틸알코올, 스테아릴알코올, 베헤닐알코올, 미리스틸알코올, 세토스테아릴알코올 등을 들 수 있다.Examples of the higher alcohols include cetyl alcohol, stearyl alcohol, behenyl alcohol, myristyl alcohol, cetostearyl alcohol, and the like.

합성에스테르유로서는, 미리스트산 이소프로필, 옥탄산세틸, 미리스트산옥틸도데실, 팔미트산이소프로필, 스테아르산부틸, 라우르산헥실, 미리스트산 미리스틸, 올레산데실, 디메틸옥탄산헥실데실, 락트산세틸, 락트산 미리스틸, 아세트산라놀린, 스테아르산 이소세틸, 이소스테아르산 이소세틸, 12-히드록시 스테아르산 콜레스테릴, 디-2-에틸헥실산 에틸렌글리콜, 디펜타에리스리톨지방산에스테르, 모노이소스테아르산 N-알킬글리콜, 디카프르산네오펜틸글리콜, 말산디이소스테아릴, 디-2-헵틸운데칸산글리세린, 트리-2-에틸헥실산트리메틸올프로판, 트리이소스테아르산 트리메틸올프로판, 테트라-2-에틸헥실산펜탄에리스리톨, 트리-2-에틸헥실산글리세린, 트리이소스테아르산 트리메틸올프로판, 세틸-2-에틸헥사노에이트, 2-에틸헥실팔미테이트, 트리미리스트산글리세린, 트리-2-헵틸운데칸산 글리세라이드, 피마자유지방산메틸에스테르, 올레산오일, 세토스테아릴알코올, 아세트글리세라이드, 팔미트산2-헵틸운데실, 아디프산디이소부틸, N-라우로일-L-글루타민산-2-옥틸 도데실 에스테르, 아디프산디-2-헵틸 운데실, 에틸라우레이트, 세바스산디-2-에틸헥실, 미리스트산 2-헥실데실, 팔미트산 2-헥실데실, 아디프산 2-헥실데실, 세바스산 디이소프로필, 숙신산 2-에틸헥실, 아세트산에틸, 아세트산부틸, 아세트산아밀, 시트르산 트리에틸등을 들 수 있다.Examples of the synthetic ester oils include isopropyl myristate, cetyl octanoate, octyl dodecyl myristic acid, isopropyl palmitate, butyl stearate, hexyl laurate, myristyl myristate, decyl oleate and hexyl dimethyl octanoate. Decyl, cetyl lactate, myristyl lactic acid, lanolin acetate, isocetyl stearate, isocetyl isostearate, cholesteryl 12-hydroxy stearate, ethylene glycol di-2-ethylhexyl acid, dipentaerythritol fatty acid ester, mono N-alkyl glycol isostearic acid, neopentyl glycol dicapric acid, diisostearyl malic acid, glycerin di-2-heptyl undecanoate, tri-2-ethylhexyl trimethylolpropane, trimethylolpropane triisostearate, tetra 2-ethylhexyl pentane erythritol, tri-2-ethylhexyl glycerine, triisostearic acid trimethylolpropane, cetyl-2-ethylhexanoate, 2-ethylhexyl palmitate, Glycerine Limiter, Tri-2-heptyl Undecanoic Acid Glyceride, Castor Oil Fatty Acid Methyl Ester, Oleic Acid Oil, Cetostearyl Alcohol, Acetglyceride, 2-Heptyl Undecyl Palmitic Acid, Diisobutyl Adipic Acid, N- Lauroyl-L-glutamic acid-2-octyl dodecyl ester, adipic di-2-heptyl undecyl, ethyllaurate, di-2-ethylhexyl sebacate, 2-hexyldecyl myristic acid, palmitic acid 2 -Hexyldecyl, adipic acid 2-hexyldecyl, diisopropyl sebacate, 2-ethylhexyl succinate, ethyl acetate, butyl acetate, amyl acetate, triethyl citrate, etc. are mentioned.

실리콘유로서는, 예를들면 디메틸폴리실록산, 메틸페닐폴리실록산, 메틸하이드로젠폴리실록산등의 쇄상 폴리실록산, 데카메틸폴리실록산, 도데카메틸폴리실록산, 테트라메틸테트라하이드로젠폴리실록산등의 환상 폴리실록산등을 들 수 있다. 본 발명에 있어서는, 이들중 1종 또는 2종이상이 임의로 선택된다.As silicone oil, cyclic polysiloxane, such as linear polysiloxane, such as dimethyl polysiloxane, methylphenyl polysiloxane, and methylhydrogen polysiloxane, decamethyl polysiloxane, dodecamethyl polysiloxane, and tetramethyl tetrahydrogen polysiloxane, etc. are mentioned, for example. In the present invention, one or two or more of these are arbitrarily selected.

본 발명의 겔조성물 전량중의 유분의 배합량은 20∼95중량%, 바람직하게는 30∼80중량%이다. 배합량이 20중량% 미만에서는, 사용성이 양호한 유성겔 조성물을 제조할 수 없고, 95중량%를 초과하면 시간 경과시 안정성이 나빠지는 경우가 있다.The compounding quantity of the oil component in the whole gel composition of this invention is 20 to 95 weight%, Preferably it is 30 to 80 weight%. If the blending amount is less than 20% by weight, the oil gel composition having good usability cannot be produced, and if it exceeds 95% by weight, the stability may deteriorate over time.

본 발명의 유화조성물 전량중의 유분의 배합량은 임의이지만, 통상, 유화조성물 전량에 대하여 20∼80중량%가 알맞다. 또, 물의 배합량은 임의이지만, 통상, 유화조성물 전량에 대하여 20∼80중량%가 알맞다. 또한, 유분과 물을 유화하기 위하여 필요한 상기 유화제의 배합량은, 유분 및 물의 배합량에 상응하여 안정한 유화조성물이 얻어지도록 적당히 결정된다.Although the compounding quantity of the oil content in the whole amount of the emulsion composition of this invention is arbitrary, 20-80 weight% is suitable for the whole amount of the emulsion composition normally. Moreover, although the compounding quantity of water is arbitrary, 20-80 weight% is suitable normally with respect to the emulsion composition whole quantity. In addition, the compounding quantity of the said emulsifier which is necessary in order to emulsify an oil component and water is suitably determined so that a stable emulsion composition may be obtained corresponding to the compounding quantity of an oil component and water.

또, 본 발명의 겔조성물 또는 유화조성물에는, 상기 필수성분외에, 본 발명의 목적을 손상하지 않을 정도로, 필요에 따라 통상 화장재료에 배합되는 다른 성분, 예를 들면, 산화방지제, 보습제, 자외선흡수제, 방부제, 향료, 안료, 약제등을 배합할 수 있다.In addition, the gel composition or the emulsion composition of the present invention, in addition to the above essential components, other ingredients usually blended into cosmetic materials as necessary, such as antioxidants, humectants, and ultraviolet absorbers, to the extent that they do not impair the object of the present invention. , Preservatives, fragrances, pigments, drugs and the like can be blended.

본 발명의 겔조성물 또는 유화조성물의 제조법은, 본 발명의 겔화제 또는 유화제와 유분(및 물) 또는 유분(과 물)을 포함하는 조성물을 직접 혼합함으로써 얻어진다. 혼합은, 수(手)교반과 같은 약한 혼합력으로 행할 수 있지만, 디스퍼, 호모지나이저, 롤러, TK밀, 후버마러, 니더, 볼밀 등의 범용의 혼합기를 사용하는 편이 바람직하다. 더욱이, 희석등을 행하지않고 화장재료나 의약부외품등의 목적으로 하는 유성겔조성물 또는 유화조성물을 직접적으로 얻으려고 하는 경우는, 디스퍼, 호모지나이저 등의 혼합기를, 또, 필요시에 적당히 희석하여, 목적으로 하는 유성겔 조성물 또는 유화조성물을 얻는 저장가능한 고점도의 유성겔조성물 또는 유화조성물을 얻으려고 하는 경우에는, 롤러등의 강한 혼합력을 갖는 혼합기를 사용하는것이 바람직하다.The gel composition or emulsion composition of the present invention is obtained by directly mixing the gelling agent or emulsifier of the present invention with a composition comprising oil (and water) or oil (and water). Although mixing can be performed by weak mixing force like hand stirring, it is preferable to use general-purpose mixers, such as a disper, a homogenizer, a roller, a TK mill, a hoover marl, a kneader, a ball mill. In addition, when directly obtaining an oily gel composition or an emulsion composition for the purpose of cosmetic materials or quasi-drugs without dilution or the like, a mixer such as a disper, homogenizer or the like is diluted as necessary. Therefore, in the case of obtaining a storageable high viscosity oil gel composition or emulsion composition to obtain the desired oil gel composition or emulsion composition, it is preferable to use a mixer having a strong mixing force such as a roller.

또, 본발명의 겔화제 또는 유화제는, 겔조성물 또는 유화조성물을 제조하는 경우에, 그의 구성성분인 수팽윤성 점토광물, 4차 암모늄염형 양이온 계면활성제 및 상온 액체의 지방산 또는 고급알코올의 각각을, 유분(과 물)을 함유하는 조성물중에 따로따로 첨가하여 혼합하여도 좋고, 유분(과 물) 및 기타의 성분과 함께 혼합하는 것도 가능하다. 또한, 미리 수팽윤성점토광물과 4차 암모늄염형 양이온 계면활성제를 혼합처리하여 얻어지는 유기변성점토광물과 상온액체의 지방산 또는 고급알코올을, 유분(과 물)을 포함하는 조성물에 첨가하여 혼합하든가, 혹은 유분(과 물) 및 기타의 성분과 함께 혼합하여 본발명의 겔조성물 또는 유화조성물을 제조하는 것도 가능하다.In addition, the gelling agent or emulsifier of the present invention, when producing a gel composition or emulsified composition, each of the components of the water-swellable clay mineral, quaternary ammonium salt type cationic surfactant and fatty acid or higher alcohol of room temperature liquid, The composition containing oil (and water) may be separately added and mixed, or may be mixed with oil (and water) and other components. In addition, the organic-modified clay mineral obtained by mixing the water-swellable clay mineral and the quaternary ammonium salt type cationic surfactant in advance and the fatty acid or higher alcohol of the room temperature liquid is added to the composition containing oil (and water), or mixed. It is also possible to prepare a gel composition or emulsion composition of the present invention by mixing with oil (and water) and other ingredients.

본 발명의 겔화제 또는 유화제를 사용한 겔조성물 또는 유화조성물은, 우수한 안정성 및 사용성을 가지므로, 예를들면 화장품, 의약부외품등의 분야에 있어서 바람직하게 사용된다.Since the gel composition or emulsion composition using the gelling agent or emulsifier of the present invention has excellent stability and usability, it is preferably used in the fields of cosmetics, quasi-drugs and the like.

[피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료][Materials to prevent skin from blacking in the sun]

본 발명의 피부가 햇볕에 타서 검게되는것을 방지하는 화장재료는, 상기의 유화조성물이, 더욱더 자외선방어제분말을 함유시킴으로써, 내수성에 우수하고, 물과 접촉하였을 경우에, 자외선방어제분말의 흰색이 두드러지지 않는 것을 특징으로 하는 것이다.The cosmetic material which prevents the skin of the present invention from blacking in the sun is excellent in water resistance because the above emulsified composition further contains an ultraviolet protective agent powder and, when contacted with water, white of the ultraviolet protective agent powder. This is not characterized.

본 발명에 사용하는 자외선 방어제분말은, 예를들면, 산화티탄, 미립자 산화티탄, 산화아연, 미립자 산화아연, 산화철, 미립자산화철등을 들 수 있다. 이들의 자외선 방어제분말은 필요에 따라 표면에 유지를 흡착시키거나, 수산기등의 관능기를 이용하여, 에스테르화나 에테르화를 일으켜, 분말을 친유적으로 하는 유(오일)처리법, 지방산의 아연염이나 마그네슘염을 사용하는 금속비누처리법, 디메틸폴리실록산 또는 메틸수소폴리실록산을 사용하는 실리콘처리법, 퍼플루오로알킬기를 갖는 불소화합물로 처리하는 불소처리법등의 표면처리에 의하여 소수성분말로서 유분에 분산배합할수도 있다. Examples of the ultraviolet protective powder to be used in the present invention include titanium oxide, fine particle titanium oxide, zinc oxide, fine particle zinc oxide, iron oxide, fine iron oxide, and the like. These UV protective powders are oil (oil) treatment methods that make the powders lipophilic by adsorbing fats and oils on the surface as necessary or by using functional groups such as hydroxyl groups to make the powder lipophilic, zinc salts of fatty acids, It may be dispersed and mixed in oil as a hydrophobic powder by surface treatment such as metal soap treatment using magnesium salt, silicon treatment using dimethyl polysiloxane or methyl hydrogen polysiloxane, and fluorination treatment with fluorine compound having perfluoroalkyl group. .

피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료중의 자외선 방어제분말의 배합량은, 통상 1∼50중량%이고, 1중량% 미만에서는 자외선방어효과가 부족하고, 50중량%를 초과하여 배합하면, 분말의 응집등이 생겨 사용성이 뒤떨어지는 경우가 있다.The blending amount of the ultraviolet protective agent powder in the cosmetic material which prevents the skin from blacking in the sun is usually 1 to 50% by weight, and when it is less than 1% by weight, the UV protection effect is insufficient and when it is blended in excess of 50% by weight. Agglomeration of powder may occur, and the usability may be inferior.

본 발명의 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료는, 수팽윤성 점토광물을, 제4차암모늄염형 양이온 계면활성제 및 상온액체의 지방산 또는 고급알코올로 처리함으로써 얻어지는 유기변성점토광물을 유화제로서 미리 조정하여 두고 유분을 혼합한 유상과, 친수성의 자외선 방어제 분말을 분산한 수상을 첨가하고, 통상의 방법에 의하여 유화처리하여 얻어진다. 친유성의 자외선 방어제분말을 사용하는 경우는 유상에 분말을 분산해두는 것이 바람직하다.The cosmetic material for preventing the skin of the present invention from blacking in the sun is an organic modified clay mineral obtained by treating a water-swellable clay mineral with a quaternary ammonium salt type cationic surfactant and a fatty acid or higher alcohol of normal temperature liquid as an emulsifier. The oil phase which adjusted previously, mixed oil components, and the water phase which disperse | distributed the hydrophilic ultraviolet-protective agent powder are added, and is obtained by emulsifying by a conventional method. When using a lipophilic ultraviolet protective powder, it is preferable to disperse powder in an oil phase.

또, 유화제로서 미리 조정하는것 없이 수팽윤성점토광물, 제4차암모늄염형 양이온 계면활성제, 상온액체의 지방산 또는 고급알코올, 자외선방어제분말을, 각각 처방중의 수상 또는 유상중에 배합하여 유화할수도 있다. 구체적으로는, 4차 암모늄염형 양이온 계면활성제, 상온액체의 지방산 또는 고급알코올, 유분을 배합한 유상에 자외선 방어제분말을 분산혼합하고, 다음에 수팽윤성 점토광물을 분산혼합한 수상을 첨가하고 혼합교반함으로써, 목적의 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료를 제조할수가 있다.In addition, water swellable clay minerals, quaternary ammonium salt type cationic surfactants, fatty acids or higher alcohols of ordinary temperature liquids, and ultraviolet protective powders may be formulated and emulsified in an aqueous phase or an oil phase, respectively, without prior adjustment as an emulsifier. . Specifically, the UV protective agent powder is dispersed and mixed in an oil phase containing a quaternary ammonium salt type cationic surfactant, a fatty acid or higher alcohol of normal temperature liquid, and an oil, followed by adding and mixing an aqueous phase in which water-swellable clay minerals are dispersed and mixed. By stirring, the cosmetic material which prevents the target skin from becoming black by sunburn can be manufactured.

또한, 미리, 수팽윤성점토광물을 4차 암모늄염형 양이온계면활성제로 처리한 유기변성점토광물을 조정하여두고, 유기변성점토광물, 상온액체의 지방산 또는 고급알코올, 자외선방어제분말을, 각각 처방중의 수상 또는 유상중에 배합하여 유화할수도 있다. 구체적으로는, 상온액체의 지방산 또는 고급알코올, 유분을 배합한 유상에, 이미 수팽윤성점토광물을 4차 암모늄염형 양이온 계면활성제로 처리제의 유기변성점토광물과 자외선방어제분말을 분산혼합하고, 다음에 수상을 첨가하고 혼합교반함으로써, 목적의 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료가 제조될 수 있다.In addition, the organic modified clay mineral which previously processed the water-swellable clay mineral with the quaternary ammonium salt type cationic surfactant was adjusted, and the organic modified clay mineral, fatty acid of normal temperature liquid, higher alcohol, or ultraviolet protective powder were prescribed, respectively. It can also be formulated and emulsified in the water or oil phase. Specifically, an oily swellable clay mineral is prepared by dispersing an organic modified clay mineral and a UV protective agent powder with a quaternary ammonium salt type cationic surfactant in an oil phase in which a fatty acid or a higher alcohol and an oil of a room temperature liquid are mixed. By adding an aqueous phase to the mixture and stirring it, a cosmetic material which prevents the desired skin from burning in the sun and blackening can be produced.

본 발명의 피부가 햇볕에 타서 검게되는 것을 방지하기위한 화장재료에는 필요에 따라 자외선흡수제를 적당히 배합할수가 있다. 자외선흡수제로서는, 예를 들면 파라아미노 벤조산(이하, PABA라 약칭함), PABA 모노글리세린에스테르, N,N-디프로폭시 PABA에틸에스테르, N,N-디에톡시 PABA에틸에스테르, N,N-디메틸 PABA에틸에스테르, N,N-디메틸 PABA부틸에스테르, N,N-디메틸PABA 에틸에스테르등의 벤조산계 자외선흡수제: 호모멘틸-N-아세틸 안트라닐레이트 등의 안트라닐산계 자외선흡수제; 아밀살리실레이트, 멘틸살리실레이트, 호모멘틸살리실레이트, 옥틸살리실레이트, 페닐살리실레이트, 벤질살리실레이트, p-이소프로판올페닐살리실레이트 등의 살리실산계 자외선흡수제; 옥틸신나메이트, 에틸-4-이소프로필신나메이트, 메틸-2,5-디이소프로필신나메이트, 에틸-2,4-디이소프로필신나메이트, 메틸-2,4-디이소프로필신나메이트, 프로필-p-메톡시신나메이트, 이소프로필-p-메톡시신나메이트, 이소아밀-p-메톡시신나메이트, 옥틸-p-메톡시신나메이트(2-에틸헥실-p-메톡시신나메이트), 2-에톡시에틸-p-메톡시신나메이트, 시클로헥실-p-메톡시신나메이트, 에틸-α-시아노-β-페닐신나메이트, 2-에틸헥실-α-시아노-β-페닐신나메이트, 글리세릴모노-2-에틸헥사노일-디파라메톡시신나메이트등의 계피산계 자외선흡수제; 2,4-디히드록시 벤조페논, 2,2'-디히드록시-4-메톡시벤조페논, 2,2'-디히드록시-4,4'-디메톡시벤조페논, 2,2',4,4'-테트라히드록시벤조페논, 2-히드록시-4-메톡시벤조페논, 2-히드록시-4-메톡시-4'-메틸벤조페논, 2-히드록시-4-메톡시벤조페논-5-술폰산염, 4-페닐벤조페논, 2-에틸헥실-4'-페닐-벤조페논-2-카르복실레이트, 2-히드록시-4-n-옥톡시벤조페논, 4-히드록시-3-카르복시벤조페논등의 벤조페논계 자외선흡수제; 3-(4'-메틸 벤질리덴)-d,ℓ-캄퍼, 3-벤지리덴-d,ℓ-캄퍼, 유로카닌산, 유로카닌산에틸에스테르, 2-페닐-5-메틸벤조키사졸, 2,2'-히드록시-5-메틸페닐벤조트리아졸, 2-(2'-히드록시-5'-t-옥틸페닐)벤조트리아졸, 2-(2'-히드록시-5'-메틸페닐벤조트리아졸, 디벤자라딘, 디아니소일메탄, 4-메톡시-4'-t-부틸디벤조일메탄, 5-(3,3-디메틸-2-노르보르니리덴)-3-펜탄-2-온등을 들 수 있다.The cosmetic material for preventing the skin of the present invention from blacking in the sun can be suitably blended with an ultraviolet absorbent if necessary. As a ultraviolet absorber, for example, paraamino benzoic acid (hereinafter abbreviated as PABA), PABA monoglycerine ester, N, N-dipropoxy PABA ethyl ester, N, N-diethoxy PABA ethyl ester, N, N-dimethyl Benzoic acid ultraviolet absorbers such as PABA ethyl ester, N, N-dimethyl PABA butyl ester and N, N-dimethyl PABA ethyl ester: anthranilic acid ultraviolet absorbers such as homomentyl-N-acetyl anthranilate; Salicylic acid ultraviolet absorbers such as amyl salicylate, menthyl salicylate, homomentyl salicylate, octyl salicylate, phenyl salicylate, benzyl salicylate and p-isopropanolphenyl salicylate; Octylcinnamate, ethyl-4-isopropylcinnamate, methyl-2,5-diisopropylcinnamate, ethyl-2,4-diisopropylcinnamate, methyl-2,4-diisopropylcinnamate, propyl -p-methoxycinnamate, isopropyl-p-methoxycinnamate, isoamyl-p-methoxycinnamate, octyl-p-methoxycinnamate (2-ethylhexyl-p-methoxycinnamate), 2-ethoxyethyl-p-methoxycinnamate, cyclohexyl-p-methoxycinnamate, ethyl-α-cyano-β-phenylcinnamate, 2-ethylhexyl-α-cyano-β-phenylcinna Cinnamic acid ultraviolet absorbers such as mate and glyceryl mono-2-ethylhexanoyl-diparamethoxycinnamate; 2,4-dihydroxy benzophenone, 2,2'-dihydroxy-4-methoxybenzophenone, 2,2'-dihydroxy-4,4'-dimethoxybenzophenone, 2,2 ', 4,4'-tetrahydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxy-4'-methylbenzophenone, 2-hydroxy-4-methoxybenzo Phenone-5-sulfonate, 4-phenylbenzophenone, 2-ethylhexyl-4'-phenyl-benzophenone-2-carboxylate, 2-hydroxy-4-n-octoxybenzophenone, 4-hydroxy Benzophenone-based ultraviolet absorbers such as 3-carboxybenzophenone; 3- (4'-methyl benzylidene) -d, l-camphor, 3-benzilidene-d, l-camphor, urocanoic acid, urocanoic acid ethyl ester, 2-phenyl-5-methylbenzokizazole, 2,2'-hydroxy-5-methylphenylbenzotriazole, 2- (2'-hydroxy-5'-t-octylphenyl) benzotriazole, 2- (2'-hydroxy-5'-methylphenylbenzo Triazole, dibenjaradine, dianisoylmethane, 4-methoxy-4'-t-butyldibenzoylmethane, 5- (3,3-dimethyl-2-norbornylidene) -3-pentane-2- Warmth.

더욱이 본발명의 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료에는, 필요에 따라 본 발명의 효과를 손상하지 않는 범위에서, 통상 화장재료에 배합되는 성분, 예를들면, 나일론파우더, 폴리메틸메타크릴레이트, 스티렌-디비닐벤젠공중합체, 폴리에틸렌분말, 다공성비닐계폴리머, 아크릴레이트코폴리머, 폴리메틸실세스퀴옥산분말등의 수지분말이나 소수화처리수지분말; 보습제; 증점제; 저급알코올; 다가알코올; 무코다당류; 방부제; 산화방지제; 금속이온 봉쇄제; pH조정제; 소염제; 비타민, 아미노산, 호르몬등의 약제; 생약; 수렴제; 안료; 분산제; 향료등을 적당히 배합할수가 있다.Moreover, the cosmetic material which prevents the skin of the present invention from blacking in the sun, if necessary, in the range that does not impair the effects of the present invention, a component usually blended in the cosmetic material, for example, nylon powder, polymethylmeth Resin powders and hydrophobized resin powders such as acrylate, styrene-divinylbenzene copolymer, polyethylene powder, porous vinyl polymer, acrylate copolymer, and polymethylsilsesquioxane powder; Humectants; Thickeners; Lower alcohol; Polyhydric alcohol; Mucopolysaccharides; antiseptic; Antioxidants; Metal ion sequestrants; pH adjuster; Anti-inflammatory agents; Drugs such as vitamins, amino acids, hormones; Herbal medicine; Astringents; Pigments; Dispersants; You can mix flavors.

이하, 실시예에 의하여 본 발명을 더욱더 상세히 설명한다. 또한, 본 발명은 이들의 실시예에만 한정되는 것은 아니다. 또 배합량은 특히 지정이 없는 한 중량%로 표시한다.Hereinafter, the present invention will be described in more detail with reference to Examples. In addition, this invention is not limited only to these Examples. In addition, the compounding quantity is expressed by weight% unless there is particular notice.

[실시예 1]Example 1

이소스테아르산 10g과 에탄올 100ml를 혼합한 용액에 유기변성점토광물인 벤톤 38(몬모릴로나이트 100g을 100밀리당량의 디스테아릴디메틸암모늄클로라이드로 처리한 유기변성점토광물인 미국 내셔날 레드사제) 100g을 라보호모지나이저로 충분히 분산 혼합하였다. 뒤이어, 증발기로 에탄올을 제거한후, 건조하여 목적의 겔화제 또는 유화제를 얻었다. 이소스테아르산의 흡착은 X선 회절로부터 평가하였다.100 g of Benton 38 (organic modified clay mineral 100 g of montmorillonite treated with 100 milliliters of distearyldimethylammonium chloride) was added to the solution of 10 g of isostearic acid and 100 ml of ethanol. The dispersion was mixed well by the moisturizer. Subsequently, the ethanol was removed by an evaporator and then dried to obtain the desired gelling or emulsifying agent. Adsorption of isostearic acid was evaluated from X-ray diffraction.

[실시예 2]Example 2

이소스테아르산 50g과 에탄올 100ml를 혼합한 용액에 유기변성점토광물인 벤톤 38(몬모릴로나이트 100g을 100밀리당량의 디스테아릴디메틸암모늄크롤라이드로 처리한 유기변성점토광물인 미국 내셔날 레드사제) 100g을 라보호모지나이저로 충분히 분산 혼합하였다. 뒤이어, 증발기로 에탄올을 제거한후, 건조하여 목적의 겔화제 또는 유화제를 얻었다. 이소스테아르산의 흡착은 X선 회절로부터 평가하였다.Into a solution of 50 g of isostearic acid and 100 ml of ethanol, 100 g of Benton 38 (organic modified clay mineral (manufactured by US National Red Co., Ltd., an organic modified clay mineral in which 100 g of montmorillonite was treated with 100 milliliters of distearyldimethylammonium chloride) was used. The dispersion was sufficiently dispersed and mixed with a protective mortarizer. Subsequently, the ethanol was removed by an evaporator and then dried to obtain the desired gelling or emulsifying agent. Adsorption of isostearic acid was evaluated from X-ray diffraction.

[실시예 3]Example 3

이소스테아르산 200g과 에탄올 100ml를 혼합한 용액에 유기변성점토광물인 벤톤 38(몬모릴로나이트 100g을 100밀리당량의 디스테아릴디메틸암모늄크롤라이드로 처리한 유기변성점토광물인 미국 내셔날 레드사제) 100g을 라보호모지나이저로 충분히 분산 혼합하였다. 뒤이어, 증발기로 에탄올을 제거한후, 건조하여 목적의 겔화제 또는 유화제를 얻었다. 이소스테아르산의 흡착은 X선 회절로부터 평가하였다.In a solution of 200 g of isostearic acid and 100 ml of ethanol, 100 g of Benton 38 (organic modified clay mineral (manufactured by US National Red Co., Ltd., an organic modified clay mineral obtained by treating 100 g of montmorillonite with 100 milliliters of distearyldimethylammonium chloride)) The dispersion was sufficiently dispersed and mixed with a protective mortarizer. Subsequently, the ethanol was removed by an evaporator and then dried to obtain the desired gelling or emulsifying agent. Adsorption of isostearic acid was evaluated from X-ray diffraction.

실시예 1∼3에서 얻어진 본발명의 겔화제 또는 유화제와 유기변성점토광물인 벤톤 38에 대하여, X선회절에 의한 층간격치를 「표 1」에 나타낸다.The layer spacing value by X-ray diffraction is shown in "Table 1" with respect to the gelling agent or emulsifier of this invention obtained in Examples 1-3, and Benton 38 which is an organic modified clay mineral.

(단위: 옹스트롬)(Unit: angstrom) 벤톤38 실시예1 실시예2 실시예3Benton 38 Example 1 Example 2 Example 3 X선회절에 의한 층간격치 26.5 32.5 40.3 45.0 Floor Spacing by X-ray Diffraction 26.5 32.5 40.3 45.0

「표 1」로부터, 유기변성점토광물(벤톤 38)은 이소스테아르산으로 처리함으로써, 또, 처리량의 증가와 동시에 층간격이 넓어짐을 알 수 있고, 이는 지방산의 결합에 의하여 생긴다고 고려된다. From Table 1, it is understood that the organic modified clay mineral (benton 38) is treated with isostearic acid, and the layer spacing is increased at the same time as the throughput is increased, which is considered to be caused by the binding of fatty acids.

[실시예 4]Example 4

실시예 1에 있어서, 이소스테아르산 대신에 이소스테아릴알코올을 사용한것 이외에는 완전히 동일하게하여 겔화제 또는 유화제를 얻었다. In Example 1, the gelation agent or the emulsifier was obtained in the same manner except that isostearyl alcohol was used instead of isostearic acid.

[실시예 5]Example 5

실시예 2에 있어서, 이소스테아르산 대신에 이소스테아릴알코올을 사용한것 이외에는 완전히 동일하게하여 겔화제 또는 유화제를 얻었다.In Example 2, the gelation agent or the emulsifier was obtained in the same manner except that isostearyl alcohol was used instead of isostearic acid.

[실시예 6]Example 6

실시예 3에 있어서, 이소스테아르산 대신에 이소스테아릴알코올을 사용한것 이외에는 완전히 동일하게하여 겔화제 또는 유화제를 얻었다.In Example 3, the gelation agent or the emulsifier was obtained in the same manner except that isostearyl alcohol was used instead of isostearic acid.

실시예 4∼6에서 얻어진 본발명의 겔화제 또는 유화제와 유기변성점토광물인 벤톤 38에 대하여, X선회절에 의한 층간격치를 「표 2」에 나타낸다.The layer spacing values by X-ray diffraction are shown in "Table 2" for the gelling agent or emulsifier of the present invention obtained in Examples 4 to 6 and Benton 38 which is an organic modified clay mineral.

(단위: 옹스트롬)(Unit: angstrom) 벤톤38 실시예4 실시예5 실시예6Benton 38 Example 4 Example 5 Example 6 X선회절에 의한 층간격치 26.5 29.0 39.7 44.1 Layer Spacing by X-ray Diffraction 26.5 29.0 39.7 44.1

「표 2」로부터, 유기변성점토광물(벤톤 38)은 이소스테아릴 알코올로 처리함으로써, 또, 처리량의 증가와 함께 층간격이 넓어짐을 알 수 있고, 이는 고급알코올의 결합에 의하여 생긴다고 고려된다.From Table 2, it is understood that the organic modified clay mineral (benton 38) is treated with isostearyl alcohol, and the layer spacing increases with increasing throughput, which is considered to be caused by the bonding of higher alcohols.

(1) 겔조성물의 실시예(1) Example of Gel Composition

[실시예 7]Example 7

실시예 2에서 얻은 겔화제 10부를 유동파라핀 90부와 함께 디스퍼로 분산, 혼합하여 유성겔조성물을 얻었다.10 parts of the gelling agent obtained in Example 2 were dispersed and mixed with 90 parts of the liquid paraffin, and mixed to obtain an oily gel composition.

[실시예 8]Example 8

실시예 2에서 얻은 겔화제 20부를 트리2-에틸헥산산 글리세릴 80부와 함께 디스퍼로 분산, 혼합하여 유성겔 조성물을 얻었다.20 parts of the gelling agents obtained in Example 2 were dispersed and mixed with 80 parts of glyceryl tri2-ethylhexanoate to obtain an oily gel composition.

[실시예 9]Example 9

실시예 2에서 얻은 겔화제 20부를 디올레산 에틸렌 글리콜 POE(12) 10부 및 트리2-에틸헥산산글리세릴 70부와 함께 디스퍼로 분산, 혼합하여 유성겔 조성물을 얻었다.20 parts of the gelling agent obtained in Example 2 were dispersed and mixed with 10 parts of ethylene glycol POE (12) dioleate and 70 parts of glyceryl tri2-ethylhexanoate to obtain an oily gel composition.

[비교예 1]Comparative Example 1

벤톤 38 10부를 유동파라핀 90부와 함께 디스퍼로 분산, 혼합하여 유성겔 조성물을 얻었다.10 parts of Benton 38 was dispersed and mixed with 90 parts of liquid paraffins, and mixed to obtain an oily gel composition.

[비교예 2]Comparative Example 2

벤톤 38 20부를 트리 2-에틸헥산산 글리세릴 80부와 함께 디스퍼로 분산, 혼합하여 유성겔 조성물을 얻었다.20 parts of Benton 38 was disperse | distributed and mixed with 80 parts of glyceryl 2-triethylhexanoate, and the oily gel composition was obtained.

[비교예 3]Comparative Example 3

벤톤 38 20부를 디올레산에틸렌글리콜 POE(12) 10부 및 트리2-에틸헥산산 글리세릴 70부와 함께 디스퍼로 분산, 혼합하여 유성겔 조성물을 얻었다.20 parts of Benton 38 was disperse | distributed and mixed with 10 parts of ethylene glycol dioleate POE (12), and 70 parts of glyceryl tri2-ethylhexanoate, and the oily gel composition was obtained.

실시예 7,8 및 9에서 얻은 유성겔 조성물과 비교예 1,2 및 3에서 얻은 유성겔 조성물을, 50℃에서 2주간 방치하고, 그의 안정성을 이하의 평가기준으로 평가하여 「표 3」에 나타낸다. 또 전문패널 10명에 의하여, 그의 사용성을 이하의 평가기준으로 관능 평가하고 「표 3」에 나타낸다.The oily gel compositions obtained in Examples 7, 8 and 9 and the oily gel compositions obtained in Comparative Examples 1,2 and 3 were left to stand at 50 ° C for 2 weeks, and their stability was evaluated according to the following evaluation criteria. Indicates. Moreover, by ten professional panels, the usability was sensory evaluated by the following evaluation criteria, and it shows in "Table 3".

[안정성 평가기준][Stability Evaluation Criteria]

◎: 분리가 전혀 인정되지 않는다.(Double-circle): Separation is not recognized at all.

△: 유분의 분리가 인정된다.(Triangle | delta): Separation of oil is recognized.

×: 현저한 유분의 분리가 인정된다.X: Remarkable separation of oil is recognized.

[사용성 평가 기준][Usability evaluation criteria]

◎: 10명중 8명이상이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.(Double-circle): More than 8 out of 10 replied that spreading was good and usability was good.

○: 10명중 6명이상 8명 미만이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.(Circle): More than 6 out of 10 people answered that spreading was good and usability was good.

△: 10명중 4명이상 6명 미만이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.(Triangle | delta): More than four out of ten responded that spread | diffusion was good and usability was favorable.

×: 10명중 4명 미만이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.X: Less than 4 out of 10 people answered that spreading was good and usability was good.

실시예 비교예                 EXAMPLES Comparative Example 7 8 9 1 2 37 8 9 1 2 3 안정성 ◎ ◎ ◎ △ × × Stability ◎ ◎ ◎ △ × × 사용성 ◎ ◎ ◎ △ ○ ○ Usability ◎ ◎ ◎ △ ○ ○

「표 3」으로부터 명백한 바와같이 본발명의 겔화제는 비극성유계 혹은 극성유계 어느것에 있어서도 온도안정성 및 사용성에 우수한 유성겔 조성물을 생성할 수가 있다. 한편, 비교예에서는 어느경우도 안정한 유성겔 조성물은 얻을 수 없고, 사용성에 대하여도 실시예에 비해 뒤떨어지고 있다.As apparent from Table 3, the gelling agent of the present invention can produce an oil gel composition excellent in temperature stability and usability in either a nonpolar oil type or a polar oil type. On the other hand, in any of the comparative examples, a stable oil gel composition cannot be obtained, and the usability is inferior to the examples.

이하, 본 발명의 겔화제를 사용하여 제조한 겔조성물의 다른 실시예를 나타낸다.Hereinafter, another Example of the gel composition manufactured using the gelling agent of this invention is shown.

[실시예 10: 선스크린]Example 10 Sunscreen

비검(미국 반더빌트사제 수팽윤성 점토광물) 2.0중량%Non-gum (water swellable clay mineral made by Vanderbilt, USA) 2.0 wt%

벤질디메틸 스테아릴 암모늄 클로라이드 1.0Benzyldimethyl stearyl ammonium chloride 1.0

이소스테아르산 1.0Isostearic acid 1.0

유동파라핀 나머지Floating paraffin rest

와셀린 10.0Waselin 10.0

데카메틸 시클로 펜타실록산 20.0Decamethyl Cyclopentasiloxane 20.0

소수화산화티탄 10.0Hydrophobized Titanium Oxide 10.0

옥틸 메톡시 신남산 5.0Octyl methoxy cinnamic acid 5.0

향료 적당량Fragrance

(제법)(quite)

비검을 에탄올에 분산하고, 벤질디메틸스테아릴 암모늄 클로라이드를 가하여, 50℃로 가온후, 디스퍼로 분산한다. 그후, 충분히 건조하여 에탄올을 제거하고 유기변성점토광물을 얻었다. 다음에 나머지 성분을 유기변성점토광물에 가하여 가압력 15kg/cm의 롤러로 2회 연합(練合; 골고루 섞이도록 개다)하여, 본발명의 겔조성물인 선스크린을 얻었다. 얻어진 선스크린은 온도안정성이 양호하고, 퍼짐이 좋고 우수한 사용성을 갖고 있었다.The gums are dispersed in ethanol, benzyldimethylstearyl ammonium chloride is added, warmed to 50 DEG C, and then dispersed in a disper. Thereafter, it was sufficiently dried to remove ethanol to obtain an organic modified clay mineral. Next, the remaining components were added to the organic modified clay mineral and combined twice with a roller of 15 kg / cm pressing force to obtain a sunscreen as a gel composition of the present invention. The obtained sunscreen had good temperature stability, had good spreading, and had excellent usability.

[실시예11: 유성연고]Example 11 Oily Ointment

유기변성점토광물(벤톤 38) 5.0중량%5.0% by weight of organic modified clay mineral (benton 38)

올레산 5.0Oleic acid 5.0

유동파라핀 나머지Floating paraffin rest

와셀린 5.0Waselin 5.0

마이크로크리스탈린 왁스 5.0Microcrystalline Wax 5.0

글리세린 2.0Glycerin 2.0

약제 적당량Pharmaceutical proper amount

(제법)(quite)

올레산, 유동파라핀, 와셀린, 마이크로크리스탈린 왁스, 글리세린을 70℃로 균일 용해하고, 이에 벤톤 38을 디스퍼 교반하에 첨가하고, 본 발명의 겔조성물인 유성연고를 얻었다. 얻어진 유성연고는 온도 안정성이 양호하고, 퍼짐이 좋고 우수한 사용성을 갖고 있었다.Oleic acid, liquid paraffin, waselin, microcrystalline wax, and glycerin were uniformly dissolved at 70 ° C., and Benton 38 was added thereto under disper stirring to obtain an oily ointment as a gel composition of the present invention. The obtained oil-based ointment had good temperature stability, good spreading, and excellent usability.

[실시예 12: 선스크린]Example 12 Sunscreen

비검(미국 반더빌트사제 수팽윤성점토광물) 2.0중량%Non-gum (water swellable clay mineral made by Vanderbilt, USA) 2.0 wt%

벤질디메틸스테아릴암모늄클로라이드 1.0Benzyldimethylstearylammonium chloride 1.0

이소스테아릴 알코올 2.0Isostearyl Alcohol 2.0

이소파라핀 나머지Isoparaffin rest

와셀린 10.0Waselin 10.0

데카메틸시클로펜타실록산 20.0Decamethylcyclopentasiloxane 20.0

소수화산화티탄 10.0Hydrophobized Titanium Oxide 10.0

옥틸메톡시신남산 5.0Octylmethoxycinnamic acid 5.0

향료 적당량Fragrance

(제법)(quite)

비검을 에탄올에 분산하고, 벤질디메틸스테아릴암모늄 클로라이드를 가하여, 50℃로 가온후, 디스퍼로 분산한다. 그후, 충분히 건조하여 에탄올을 제거하고, 유기변성점토광물을 얻었다. 다음에, 나머지 성분을 유기변성점토광물에 가하여, 가압력 15kg/cm의 롤러로 2회 연합하여 본발명의 겔조성물인 선스크린을 얻었다. 얻어진 선스크린은 온도안정성이 양호하고, 퍼짐이 좋고, 우수한 사용성을 갖고 있었다.The gum is dispersed in ethanol, benzyldimethylstearylammonium chloride is added, warmed to 50 ° C, and then dispersed in a disper. Thereafter, the mixture was sufficiently dried to remove ethanol to obtain an organic modified clay mineral. Next, the remaining components were added to the organic modified clay mineral and combined twice with a roller of an applied pressure of 15 kg / cm to obtain a sunscreen as a gel composition of the present invention. The obtained sunscreen had good temperature stability, good spreading, and had excellent usability.

[실시예 13: 유성연고]Example 13: Oily Ointment

유기변성점토광물(벤톤 38) 5.0중량%5.0% by weight of organic modified clay mineral (benton 38)

옥틸도데칸올 5.0Octyldodecanol 5.0

유동파라핀 나머지Floating paraffin rest

와셀린 5.0Waselin 5.0

마이크로크리스탈린 왁스 5.0Microcrystalline Wax 5.0

글리세린 2.0Glycerin 2.0

약제 적당량Pharmaceutical proper amount

(제법)(quite)

옥틸도데칸올, 유동파라핀, 와셀린, 마이크로크리스탈린 왁스, 글리세린을 70℃로 균일 용해하고, 이에 벤톤 38을 디스퍼 교반하에 첨가하고, 본 발명의 겔조성물인 유성연고를 얻었다. 얻어진 유성연고는 온도 안정성이 양호하고, 퍼짐이 좋고 우수한 사용성을 갖고 있었다.Octyldodecanol, liquid paraffin, waselin, microcrystalline wax, and glycerin were uniformly dissolved at 70 ° C., and Benton 38 was added thereto under disper stirring to obtain an oily ointment as a gel composition of the present invention. The obtained oil-based ointment had good temperature stability, good spreading, and excellent usability.

(2) 유화 조성물의 실시예(2) Example of Emulsifying Composition

[실시예 14]Example 14

실시예 2에서 얻은 유화제1부를 유동파라핀 30부와 함께 디스퍼로 분산, 혼합한후, 여기에 정제수 69부를 가하여, 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.After dispersing and mixing 1 part of the emulsifier obtained in Example 2 with 30 parts of fluidized paraffin by dispersing, 69 parts of purified water was added thereto, and the resultant was further disper mixed to obtain an emulsified composition.

[실시예 15]Example 15

실시예 2에서 얻은 유화제 2부를 트리 2-에틸헥산산 글리세릴 20부와 함께 디스퍼로 분산, 혼합한후, 여기에 정제수 78부를 가하여 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.After dispersing and mixing 2 parts of the emulsifier obtained in Example 2 with 20 parts of glyceryl 2-ethylethyl hexanoate, it was added 78 parts of purified water, and further disper-mixed to obtain an emulsified composition.

[실시예 16]Example 16

실시예 2에서 얻은 유화제 2부를 메틸페닐실록산 20부와 함께 디스퍼로 분산, 혼합한후, 여기에 정제수 78부를 가하여 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.After dispersing and mixing 2 parts of the emulsifier obtained in Example 2 with 20 parts of methylphenylsiloxane in a disper, 78 parts of purified water was added thereto, and further disper mixing was carried out to obtain an emulsified composition.

[비교예 4][Comparative Example 4]

벤톤 38 2부, 폴리옥시 알킬렌 변성오르가노 폴리실록산 1부를 유동파라핀 30부와 함께 디스퍼로 분산, 혼합한후, 여기에 정제수 67부를 가하여 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.2 parts of Benton 38 and 1 part of polyoxyalkylene-modified organopolysiloxane were dispersed and mixed with 30 parts of liquid paraffin by dispersing, and 67 parts of purified water was added to this to further disperse mixing to obtain an emulsified composition.

[비교예 5][Comparative Example 5]

벤톤 38 2부, 글리세롤 이소스테아레이트 1부를 메틸페닐실록산 20부와 함께 디스퍼로 분산, 혼합한 후, 여기에 정제수 77부를 가하여, 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.2 parts of Benton 38 and 1 part of glycerol isostearates were disperse | distributed and mixed with 20 parts of methylphenylsiloxanes, and 77 parts of purified water was added to this, and the emulsified composition was obtained by further disperse mixing.

[비교예 6]Comparative Example 6

벤톤 38 2부, 글리세롤 이소스테아레이트 1부를 트리2-에틸헥산산 글리세릴 20부와 함께 디스퍼로 분산, 혼합한후, 여기에 정제수 77부를 가하여 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.2 parts of Benton 38 and 1 part of glycerol isostearates were disperse | distributed and mixed with 20 parts of glyceryl tri 2-ethylhexanoic acid, and 77 parts of purified water was added to this, and the disperse mixing was further carried out, and the emulsion composition was obtained.

[비교예 7]Comparative Example 7

벤톤 38 2부, 글리세롤 이소스테아레이트 5부를 트리 2-에틸 헥산산 글리세롤 20부와 함께 디스퍼로 분산, 혼합한 후, 여기에 정제수 73부를 가하여, 더욱 디스퍼 혼합하는 것으로 유화조성물을 얻었다.After dispersing and mixing 2 parts of Benton 38 and 5 parts of glycerol isostearate with 20 parts of glycerol of tri 2-ethyl hexanoate, it added 73 parts of purified water to this, and further emulsified and obtained the emulsion composition.

실시예 14,15 및 16에서 얻은 유화조성물과 비교예 5,6,7 및 8에서 얻은 유화 조성물을, 50℃에서 2주간 방치하고, 그의 안정성을 이하의 평가기준으로 평가하여 「표 4」에 나타낸다. 또 전문패널 10명에 의하여, 그 사용성을 이하의 평가기준으로 관능 평가하고 「표 4」에 나타낸다.The emulsion compositions obtained in Examples 14, 15 and 16 and the emulsion compositions obtained in Comparative Examples 5, 6, 7, and 8 were left to stand at 50 ° C. for 2 weeks, and their stability was evaluated according to the following evaluation criteria. Indicates. In addition, by the ten expert panels, the usability was sensory evaluated by the following evaluation criteria, and it shows in "Table 4".

[안정성 평가기준][Stability Evaluation Criteria]

◎: 분리가 전혀 인정되지 않는다.(Double-circle): Separation is not recognized at all.

△: 유분의 분리가 인정된다.(Triangle | delta): Separation of oil is recognized.

×: 현저한 유분의 분리가 인정된다.X: Remarkable separation of oil is recognized.

[사용성 평가 기준][Usability evaluation criteria]

◎: 10명중 8명이상이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.(Double-circle): More than 8 out of 10 replied that spreading was good and usability was good.

○: 10명중 6명이상 8명 미만이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.(Circle): More than 6 out of 10 people answered that spreading was good and usability was good.

△: 10명중 4명이상 6명 미만이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.(Triangle | delta): More than four out of ten responded that spread | diffusion was good and usability was favorable.

×: 10명중 4명 미만이 퍼짐이 좋고 사용성이 양호하다고 회답하였다.X: Less than 4 out of 10 people answered that spreading was good and usability was good.

실시예 비교예                 EXAMPLES Comparative Example 14 15 16 4 5 6 714 15 16 4 5 6 7 안정성 ◎ ◎ ◎ × × △ ◎ Stability ◎ ◎ ◎ × × △ ◎ 사용성 ○ ◎ ◎ △ ○ ○ × Usability ○ ◎ ◎ △ ○ ○ ×

「표 4」로부터 명백한 바와같이, 본발명의 유화제 조성물은 비극성유계 혹은 극성유계 어느것에 있어서도 온도안정성 및 사용성에 우수한 유화 조성물을 조제할 수가 있다. 한편, 비교예 5,6,7에서는 안정한 유화조성물은 얻을 수 없고, 또, 안정성이 양호한 유화조성물이 얻어진 비교예 8에서는 사용성에 있어서 실시예에 비해 뒤떨어지고 있다.As is apparent from Table 4, the emulsifier composition of the present invention can prepare an emulsion composition excellent in temperature stability and usability in either the nonpolar oil type or the polar oil type. On the other hand, in Comparative Examples 5, 6 and 7, a stable emulsion composition was not obtained, and Comparative Example 8 in which an emulsion composition having good stability was obtained was inferior to the Examples in usability.

이하, 본 발명의 유화제를 사용하여 제조한 유화조성물의 다른 실시예를 표시한다.Hereinafter, another Example of the emulsion composition manufactured using the emulsifier of this invention is shown.

[실시예 17: 미백용 크림]Example 17 Whitening Cream

비검(미국 반더빌트사제 수팽윤성 점토광물) 2.0중량%Non-gum (water swellable clay mineral made by Vanderbilt, USA) 2.0 wt%

벤질디메틸스테아릴 암모늄 클로라이드 1.0Benzyldimethylstearyl ammonium chloride 1.0

이소스테아르산 1.0Isostearic acid 1.0

데카메틸시클로펜타실록산 25.0Decamethylcyclopentasiloxane 25.0

아스코르브산 글루코시드 1.0Ascorbic Acid Glucoside 1.0

카르복시메틸 셀룰로오스나트륨 1.0Carboxymethyl Cellulose Sodium 1.0

시트르산 0.05Citric Acid 0.05

시트르산나트륨 0.5Sodium Citrate 0.5

글리세린 5.0Glycerin 5.0

1,3부틸렌글리콜 5.01,3 butylene glycol 5.0

파라히드록시 벤조산 메틸 0.1Parahydroxy Methyl Benzoate 0.1

향료 0.05Spices 0.05

정제수 나머지Purified water rest

(제법)(quite)

비검을 에탄올에 분산하고, 벤질디메틸스테아릴암모늄 클로라이드를 가하여, 50℃로 가온후, 디스퍼로 분산한다. 그후, 충분히 건조하여 에탄올을 제거하고, 유기변성점토광물을 얻었다. 다음에, 이소스테아르산을 유기변성점토광물에 가하여, 가압력 15kg/cm의 롤러로 2회 연합하여 본발명의 유화제를 얻었다. 얻어진 유화제에 데카메틸시클로펜타실록산을 가하여 유상을 조제하고, 여기에 나머지의 수상을 디스퍼 호모지나이저 교반하에 서서히 첨가함으로써 미백용크림을 얻었다.The gum is dispersed in ethanol, benzyldimethylstearylammonium chloride is added, warmed to 50 ° C, and then dispersed in a disper. Thereafter, the mixture was sufficiently dried to remove ethanol to obtain an organic modified clay mineral. Next, isostearic acid was added to the organic modified clay mineral and combined twice with a roller of 15 kg / cm pressing force to obtain an emulsifier of the present invention. Decamethylcyclopentasiloxane was added to the obtained emulsifier to prepare an oil phase, and the whitening cream was obtained by gradually adding the remaining water phase under the disper homogenizer stirring.

[실시예 18: 핸드크림]Example 18 Hand Cream

유기변성점토광물(벤톤 38) 1.0중량%1.0% by weight of organic modified clay mineral (benton 38)

올레산 2.0Oleic acid 2.0

유동파라핀 10.0Liquid Paraffin 10.0

스쿠알란 5.0Squalane 5.0

와셀린 2.0Waselin 2.0

마이크로크리스탈린 왁스 1.0Microcrystalline Wax 1.0

세틸이소옥타노에이트 5.0Cetylisooctanoate 5.0

글리세린 10.0Glycerin 10.0

약제 적당량Pharmaceutical proper amount

파라히드록시벤조산에틸 0.1Ethyl parahydroxybenzoate 0.1

향료 0.05Spices 0.05

정제수 나머지Purified water rest

(제법)(quite)

올레산, 유동파라핀, 스쿠알란, 와셀린, 마이크로크리스탈린 왁스, 세틸이소옥타노에이트를 80℃에서 균일용해하고, 여기에 벤톤 38을 디스퍼 교반하에 첨가하고, 유상을 조제한후, 나머지 수상을 디스퍼호모지나이저 교반하에 서서히 첨가하는 것으로 핸드크림을 얻었다. 얻어진 핸드크림은 온도안정성이 양호하고, 퍼짐이 좋고, 우수한 사용성을 갖고 있었다.Dissolve oleic acid, liquid paraffin, squalane, waselin, microcrystalline wax and cetylisooctanoate at 80 ° C. uniformly at 80 ° C., add Benton 38 under disper agitation, prepare an oil phase, and then dissolve the remaining aqueous phase Hand cream was obtained by the slow addition of the agent under stirring. The obtained hand cream had good temperature stability, good spreading, and had excellent usability.

[실시예 19: 선스크린]Example 19 Sunscreen

유기변성점토광물(벤톤 38) 2.0중량%2.0% by weight of organic modified clay mineral (benton 38)

에탄올 5.0Ethanol 5.0

이소스테아르산 2.0Isostearic acid 2.0

옥틸메톡시신나메이트 10.0Octylmethoxycinnamate 10.0

4-tert-부틸-4'-메톡시디벤조일메탄 2.04-tert-butyl-4'-methoxydibenzoylmethane 2.0

숙신산 디옥틸 10.0Dioctyl succinate 10.0

데카메틸 시클로펜타실록산 10.0Decamethyl Cyclopentasiloxane 10.0

글리세린 10.0Glycerin 10.0

약제 적당량Pharmaceutical proper amount

파라히드록시 벤조산에틸 0.25Parahydroxyethyl benzoate 0.25

향료 0.05Spices 0.05

정제수 나머지Purified water rest

(제법)(quite)

벤톤 38을 에탄올에 분산하고, 더욱 이소스테아르산을 가하여, 가압력 15kg/cm의 롤러로 2회 연합하여 본 발명의 유화제를 얻었다. 얻어진 유화제에 옥틸메톡시 신나메이트, 4-tert-부틸-4'-메톡시 디벤조일 메탄, 숙신산디옥틸, 데카메틸시클로 펜타실록산을 가하여 유상을 조제하고, 여기에 나머지의 수상을 디스퍼 호모지나이저 교반하에 서서히 첨가함으로써 선스크린을 얻었다. 얻어진 선스크린은 온도안정성이 양호하고, 퍼짐이 좋고, 우수한 사용성을 갖고있고, 높은 선스크린 효과를 갖고 있었다.Benton 38 was dispersed in ethanol, and isostearic acid was further added, and fed twice with a roller of 15 kg / cm pressing force to obtain an emulsifier of the present invention. Octylmethoxy cinnamate, 4-tert-butyl-4'-methoxy dibenzoyl methane, dioctyl succinate and decamethylcyclo pentasiloxane were added to the obtained emulsifier to prepare an oil phase, and the remaining aqueous phase was used as a disper homozyme. Sunscreens were obtained by the slow addition under Niger stirring. The obtained sunscreen had good temperature stability, had good spreading, had excellent usability, and had a high sunscreen effect.

[실시예 20 : 미백용 크림]Example 20 Whitening Cream

비검(미국 반더빌트사제 수팽윤성 점토광물) 2.0중량%Non-gum (water swellable clay mineral made by Vanderbilt, USA) 2.0 wt%

벤질디메틸스테아릴 암모늄 클로라이드 1.0Benzyldimethylstearyl ammonium chloride 1.0

이소스테아릴알코올 1.0Isostearyl Alcohol 1.0

데카메틸시클로펜타실록산 25.0Decamethylcyclopentasiloxane 25.0

아스코르브산 글루코시드 1.0Ascorbic Acid Glucoside 1.0

카르복시메틸 셀룰로오스나트륨 1.0Carboxymethyl Cellulose Sodium 1.0

시트르산 0.05Citric Acid 0.05

시트르산나트륨 0.5Sodium Citrate 0.5

글리세린 5.0Glycerin 5.0

1,3부틸렌글리콜 5.01,3 butylene glycol 5.0

파라히드록시 벤조산 메틸 0.1Parahydroxy Methyl Benzoate 0.1

향료 0.05Spices 0.05

정제수 나머지Purified water rest

(제법)(quite)

비검을 에탄올에 분산하고, 벤질디메틸스테아릴암모늄 클로라이드를 가하여, 50℃로 가온후, 디스퍼로 분산한다. 그후, 충분히 건조하여 에탄올을 제거하고 유기변성점토광물을 얻었다. 다음에 이소스테아릴 알코올을 유기변성점토광물에 가하여, 가압력 15kg/cm의 롤러로 2회 연합하여 본 발명의 유화제를 얻었다. 얻어진 유화제에 데카메틸시클로펜타실록산을 가하여 유상을 조제하고, 여기에 나머지의 수상을 디스퍼호모지나이저 교반하에 서서히 첨가하는 것으로 미백용 크림을 얻었다.The gum is dispersed in ethanol, benzyldimethylstearylammonium chloride is added, warmed to 50 ° C, and then dispersed in a disper. Thereafter, it was sufficiently dried to remove ethanol to obtain an organic modified clay mineral. Next, isostearyl alcohol was added to the organic modified clay mineral, and it was combined twice with the roller of 15 kg / cm of pressing force, and the emulsifier of this invention was obtained. Decamethylcyclopentasiloxane was added to the obtained emulsifier to prepare an oil phase, and the whitening cream was obtained by gradually adding the remaining water phase to the disper homogenizer stirring here.

[실시예 21: 핸드크림]Example 21 Hand Cream

유기변성점토광물(벤톤 38) 1.0중량%1.0% by weight of organic modified clay mineral (benton 38)

올레일알코올 2.0Oleyl alcohol 2.0

유동파라핀 10.0Liquid Paraffin 10.0

스쿠알란 5.0Squalane 5.0

와셀린 2.0Waselin 2.0

마이크로크리스탈린 왁스 1.0Microcrystalline Wax 1.0

세틸이소옥타노에이트 5.0Cetylisooctanoate 5.0

글리세린 10.0Glycerin 10.0

약제 적당량Pharmaceutical proper amount

파라히드록시벤조산에틸 0.1Ethyl parahydroxybenzoate 0.1

향료 0.05Spices 0.05

정제수 나머지Purified water rest

(제법)(quite)

올레일알코올, 유동파라핀, 스쿠알란, 와셀린, 마이크로크리스탈린 왁스, 세틸이소옥타노에이트를 80℃에서 균일용해하고, 여기에 벤톤 38을 디스퍼 교반하에 첨가하고, 유상을 조제한후, 나머지 수상을 디스퍼호모지나이저 교반하에 서서히 첨가하는 것으로 핸드크림을 얻었다. 얻어진 핸드크림은 온도안정성이 양호하고, 퍼짐이 좋고, 우수한 사용성을 갖고 있었다.Dissolve oleyl alcohol, liquid paraffin, squalane, waselin, microcrystalline wax and cetylisooctanoate at 80 ° C. uniformly at 80 ° C., add Benton 38 under disper stirring, prepare an oil phase, and then dissolve the remaining aqueous phase. Hand cream was obtained by the slow addition of per homogenizer under stirring. The obtained hand cream had good temperature stability, good spreading, and had excellent usability.

[실시예 22: 선스크린]Example 22 Sunscreen

유기변성점토광물(벤톤 38) 2.0중량%2.0% by weight of organic modified clay mineral (benton 38)

에탄올 5.0Ethanol 5.0

옥틸도데칸올 1.0Octyldodecanol 1.0

옥틸메톡시신나메이트 10.0Octylmethoxycinnamate 10.0

4-tert-부틸-4'-메톡시디벤조일메탄 2.04-tert-butyl-4'-methoxydibenzoylmethane 2.0

숙신산 디옥틸 10.0Dioctyl succinate 10.0

데카메틸 시클로펜타실록산 10.0Decamethyl Cyclopentasiloxane 10.0

글리세린 10.0Glycerin 10.0

약제 적당량Pharmaceutical proper amount

파라히드록시 벤조산에틸 0.25Parahydroxyethyl benzoate 0.25

향료 0.05Spices 0.05

정제수 나머지Purified water rest

(제법)(quite)

벤톤 38을 에탄올에 분산하고, 또한 옥틸도데칸올을 가하여, 가압력 15kg/cm의 롤러로 2회 연합하여 본 발명의 유화제를 얻었다. 얻어진 유화제에 옥틸메톡시 신나메이트, 4-tert-부틸-4'-메톡시 디벤조일 메탄, 숙신산디옥틸, 데카메틸시클로 펜타실록산을 가하여 유상을 조제하고, 여기에 나머지의 수상을 디스퍼 호모지나이저 교반하에 서서히 첨가함으로써 선스크린을 얻었다. 얻어진 선스크린은 온도안정성이 양호하고, 퍼짐이 좋고, 우수한 사용성을 갖고 있고, 높은 선스크린 효과를 갖고 있었다.Benton 38 was dispersed in ethanol, and further, octyldodecanol was added, and fed twice with a roller of 15 kg / cm pressing force to obtain an emulsifier of the present invention. Octylmethoxy cinnamate, 4-tert-butyl-4'-methoxy dibenzoyl methane, dioctyl succinate and decamethylcyclo pentasiloxane were added to the obtained emulsifier to prepare an oil phase, and the remaining aqueous phase was used as a disper homozyme. Sunscreens were obtained by the slow addition under Niger stirring. The obtained sunscreen had good temperature stability, good spreading, excellent usability, and had a high sunscreen effect.

(3) 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료의 실시예(3) an embodiment of a cosmetic material which prevents the skin from blacking in the sun

[실시예 23: 피부가 햇볕에 타서 검게되는 것을 방지하는 크림]Example 23 Cream for Preventing Skin from Sunburn and Blacking

(1) 데카메틸시클로 펜타실록산 25.0중량%(1) 25.0% by weight of decamethylcyclo pentasiloxane

(2) 유동파라핀 5.0(2) floating paraffin 5.0

(3) 이소스테아르산 1.0(3) isostearic acid 1.0

(4) 디스테아릴디메틸암모늄클로라이드 0.6(4) distearyldimethylammonium chloride 0.6

(5) 옥틸메톡시신나메이트 5.0(5) Octylmethoxycinnamate 5.0

(6) 파라벤 적당량(6) appropriate amount of parabens

(7) 향료 적당량(7) appropriate amount of spices

(8) 소수화방추형산화티탄 10.0(8) Hydrophobized spindle type titanium oxide 10.0

(9) 이온교환수 나머지(9) rest of ion exchange water

(10)글리세린 10.0(10) Glycerin 10.0

(11)스멕톤 1.0(11) smecton 1.0

제법quite

(1)∼(7)을 70℃로 가열하고, 미리 유상을 조제하여 둔다. 다음에 (8)을 가하여, 디스퍼로 분산혼합한다. (9)∼(11)을 70℃로 분산 혼합한 다음 유상에 디스퍼로 교반하면서 서서히 가하여, 충분히 균일하게 혼합교반, 냉각하여 목적의 피부가 햇볕에 타서 검게되는것을 방지하는 크림을 얻었다.(1)-(7) are heated to 70 degreeC, and the oil phase is prepared previously. (8) is then added and dispersed and mixed with a disper. (9)-(11) were dispersed and mixed at 70 degreeC, and it added gradually, stirring with an oily disperse to an oil phase, and mixing and cooling them evenly enough, and obtained the cream which prevents the target skin from burning in the sun and blackening.

[비교예 8: 피부가 햇볕에 타서 검게되는 것을 방지하는 크림][Comparative Example 8: Cream that prevents skin from blacking in the sun]

실시예 23에 있어서, 이소스테아르산 대신에 폴리옥시알킬렌변성 오르가노폴리실록산을 사용하여, 실시예 23과 같은 제법으로 피부가 햇볕에 타서 검게되는 것을 방지하는 크림을 제조하였다. In Example 23, a polyoxyalkylene-modified organopolysiloxane instead of isostearic acid was used to prepare a cream that prevents the skin from blacking in the sun in the same manner as in Example 23.

[실시예 24: 피부가 햇볕에 타서 검게되는 것을 방지하는 크림][Example 24: Cream for Preventing Skin from Blacking by Sun]

(1) 데카메틸시클로 펜타실록산 20.0중량%(1) 20.0% by weight of decamethylcyclo pentasiloxane

(2) 유동파라핀 10.0(2) floating paraffin 10.0

(3) 데실테트라데칸올 2.0(3) decyl tetradecanol 2.0

(4) 디스테아릴디메틸암모늄클로라이드 0.6(4) distearyldimethylammonium chloride 0.6

(5) 옥틸메톡시신나메이트 5.0(5) Octylmethoxycinnamate 5.0

(6) 에탄올 2.0(6) Ethanol 2.0

(7) 파라벤 적당량(7) appropriate amount of parabens

(8) 향료 적당량(8) appropriate amount of spices

(9) 소수화 산화티탄 5.0(9) Hydrophobized Titanium Oxide 5.0

(10) 소수화 산화아연 5.0(10) Hydrophobized Zinc Oxide 5.0

(11) 이온교환수 나머지(11) rest of ion exchange water

(12)글리세린 5.0(12) Glycerin 5.0

(13)스멕톤 1.0(13) smecton 1.0

제법quite

(1)∼(8)을 70℃로 가열하고, 미리 유상을 조제하여 둔다. 다음에 (9),(10)을 가하여, 디스퍼로 분산혼합한다. (11)∼(13)을 70℃로 분산 혼합한 다음 유상 디스퍼로 교반하면서 서서히 가하여 충분히 균일하게 혼합교반, 냉각하여 목적의 피부가 햇볕에 타서 검게되는 것을 방지하는 크림을 얻었다.(1)-(8) are heated to 70 degreeC, and the oil phase is prepared previously. Next, (9) and (10) are added and dispersed and mixed with a disper. After dispersing and mixing (11)-(13) at 70 degreeC, it added gradually, stirring with an oily disper, stirring and cooling mixing uniformly enough, and obtained the cream which prevents the target skin from burning in the sun.

[실시예 25: 크림상 파운데이션]Example 25 Creamy Foundation

(1) 데카메틸시클로펜타실록산 30.0중량%(1) 30.0% by weight of decamethylcyclopentasiloxane

(2) 유동파라핀 10.0(2) floating paraffin 10.0

(3) 올레산 0.1(3) oleic acid 0.1

(4) 벤질디메틸 디스테아릴 암모늄 클로라이드 0.05(4) benzyldimethyl distearyl ammonium chloride 0.05

(5) 옥틸메톡시신나메이트 8.0(5) Octylmethoxycinnamate 8.0

(6) 파라벤 적당량(6) appropriate amount of parabens

(7) 향료 적당량(7) appropriate amount of spices

(8) 소수화산화티탄 5.0(8) Hydrogenated Titanium Oxide 5.0

(9) 소수화산화아연 5.0(9) Hydrogenated Zinc Oxide 5.0

(10) 활석 20.0(10) talc 20.0

(11) 착색안료 적당량(11) Suitable amount of pigment

(12) 이온교환수 나머지(12) rest of ion exchange water

(13) 글리세린 5.0(13) Glycerin 5.0

(14) 스멕톤 0.2(14) smecton 0.2

제법quite

(1)∼(7)을 70℃로 가열하고, 미리 유상을 제조하여둔다. 다음에 (8)로부터 (11)을 가하여 디스퍼로 분산혼합한다. (12)∼(14)를 70℃에서 분산혼합한후 유상에 디스퍼로 교반하면서 서서히 가하여, 충분히 균일하게 혼합교반, 냉각하여 목적의 크림상의 파운데이션을 얻었다.(1)-(7) are heated to 70 degreeC, and an oil phase is manufactured previously. Next, (8) to (11) are added and dispersed and mixed with a disper. (12)-(14) were dispersed and mixed at 70 ° C, and gradually added while stirring with a dispersible oil phase, and stirred and cooled sufficiently uniformly to obtain a target creamy foundation.

[실시예 26 : 피부가 햇볕에 타서 검게되는 것을 방지하는 크림]Example 26 Cream Preventing Skin from Blacking in the Sun

(1) 유동파라핀 20.0중량%(1) 20.0 wt% of liquid paraffin

(2) 트리옥탄산 글리세릴 5.0(2) glyceryl trioctanoate 5.0

(3) 이소스테아르산 2.0(3) isostearic acid 2.0

(4) 디스테아릴 디메틸암모늄클로라이드 0.05(4) distearyl dimethylammonium chloride 0.05

(5) 옥틸메톡시 신나메이트 5.0(5) Octylmethoxy cinnamate 5.0

(6) 2-히드록시-4-메톡시벤조페논 2.0(6) 2-hydroxy-4-methoxybenzophenone 2.0

(7) 파라벤 적당량(7) appropriate amount of parabens

(8) 향료 적당량(8) appropriate amount of spices

(9) 소수화 산화티탄 1.0(9) Hydrophobized Titanium Oxide 1.0

(10) 이온교환수 나머지(10) rest of ion exchange water

(11) 1,3-부틸렌 글리콜 5.0(11) 1,3-butylene glycol 5.0

(12) 비검 0.5(12) Sword 0.5

제법quite

(1)∼(8)을 70℃로 가열하고, 미리 유상을 조제하여둔다. 다음에 (9)를 가하여 디스퍼로 분산혼합한다. (10)∼(12)를 70℃에서 분산혼합한후 유상에 디스퍼로 교반하면서 서서히 가하여, 충분히 균일하게 혼합교반, 냉각하여 목적의 피부가 햇볕에 타서 검게되는 것을 방지하는 크림을 얻었다.(1)-(8) are heated to 70 degreeC, and the oil phase is prepared previously. Next, (9) is added and dispersed and mixed with a disper. After dispersing and mixing (10) to (12) at 70 ° C, the mixture was gradually added while stirring with a dispersible oil phase, and mixed and cooled sufficiently uniformly to obtain a cream that prevents the desired skin from burning in the sun.

[실시예 27: 피부가 햇볕에 타서 검게되는 것을 방지하는 크림]Example 27 Cream Preventing Skin Burning in the Sun

(1) 데카메틸시클로 펜타실록산 28.0중량%(1) 28.0% by weight of decamethylcyclo pentasiloxane

(2) 이소스테아릴 알코올 5.0(2) isostearyl alcohol 5.0

(3) 옥틸메톡시 신나메이트 10.0(3) octylmethoxy cinnamate 10.0

(4) 2-히드록시-4-메톡시벤조페논 0.5(4) 2-hydroxy-4-methoxybenzophenone 0.5

(5) 파라벤 적당량(5) appropriate amount of parabens

(6) 향료 적당량(6) appropriate amount of spices

(7) 벤톤 38 2.0(7) Benton 38 2.0

(8) 소수화방추형산화티탄 20.0 (8) Hydrophobized Titanium Oxide 20.0

(9) 소수화산화아연 3.0(9) Hydrogenated Zinc Oxide 3.0

(10) 폴리메틸실세스퀴옥산 5.0(10) polymethylsilsesquioxane 5.0

(11) 이온교환수 나머지(11) rest of ion exchange water

(12) 1,3 부틸렌글리콜 5.0(12) 1,3 butylene glycol 5.0

제법quite

(1)∼(6)을 70℃로 가열하고, 미리 유상을 조제하여 둔다. 다음에 (7)∼(9)를 가하여, 디스퍼로 분산혼합한다. (10)∼(12)를 70℃에서 분산혼합한 다음 유상에 디스퍼로 교반하면서 서서히 가하여, 충분히 균일하게 혼합교반, 냉각하여 목적의 피부가 햇볕에 타서 검게되는 것을 방지하는 크림을 얻었다. 또한, 소수화방추형산화티탄은 미립자 산화티탄 100-T(제국화공사제)를 사용하였다. 또, 벤톤 38이란 몬모릴로나이트 100g을 100m당량의 디스테아릴 디메틸 암모늄 클로라이드로 처리한 유기변성점토 광물이다(미국내셔널 레드사제).(1)-(6) are heated to 70 degreeC, and an oil phase is prepared previously. Next, (7) to (9) are added and dispersed and mixed with a disper. (10)-(12) were dispersed and mixed at 70 DEG C, and then gradually added while stirring with a dispersible oil phase, and mixed and cooled sufficiently uniformly to obtain a cream that prevents the desired skin from burning in the sun. As the hydrophobized titanium oxide, fine particle titanium oxide 100-T (manufactured by Imperialization Corporation) was used. Benton 38 is an organic modified clay mineral obtained by treating 100 g of montmorillonite with 100 m equivalent of distearyl dimethyl ammonium chloride (manufactured by National Red).

[비교예 9 : 피부가 햇볕에 타서 검게되는 것을 방지하는 크림][Comparative Example 9: Cream to prevent the skin from blacking in the sun]

실시예 27에 있어서, 이소스테아릴알코올 대신에 폴리옥시알킬렌변성오르가노 폴리실록산을 사용하고, 또한, 소수화방추형 산화티탄대신에 평균입경 0.03∼0.04미크론, 직경과 단경의 평균비율 1.3인 소수화산화티탄을 사용하여, 실시예 27과 같은 제법으로 피부가 햇볕에 타서 검게되는 것을 방지하는 크림을 제조하였다.In Example 27, polyoxyalkylene-modified organopolysiloxane was used in place of isostearyl alcohol, and instead of hydrophobized spindle type titanium oxide, hydrophobized titanium oxide having an average particle diameter of 0.03-0.04 microns and an average ratio of diameter and short diameter of 1.3. Using, to prepare a cream to prevent the skin from blacking in the sun in the same manner as in Example 27.

다음에, 상기에서 얻어진 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료에 대하여, 흰색의 두드러지기 어려움에 대하여 이하의 시험을 행하고, 그 효과를 「표 5」에 평가하였다.Next, with respect to the cosmetic material which prevents the skin obtained above from becoming black in the sun, the following test was done about the difficulty of outstanding whiteness, and the effect was evaluated in "Table 5".

(1) 흰색의 두드러짐 시험(1) whiteness test

평가전문패널 20명의 앞팔내측부(5×10cm)에 샘플(실시예 1∼5, 비교예 1∼2)을 도포하고, 30분간 방치후, 흰색의 두드러지는 상태를 평가하였다. (2) 수세후의 흰색의 두드러짐 시험.The sample (Examples 1-5, Comparative Examples 1-2) was apply | coated to the inner side part (5x10cm) of 20 professional panelists, and after standing for 30 minutes, the white outstanding state was evaluated. (2) White outstanding test after washing with water.

(1)에서, 흰색의 두드러지는 상태를 평가한후, 10분간 흐르는 물(30℃)로 도포부를 수세하고, 흰색의 두드러지는 상태를 평가하였다.In (1), after a white outstanding state was evaluated, the coating part was washed with running water (30 degreeC) for 10 minutes, and the white outstanding state was evaluated.

(1),(2)에 있어서 시험결과는 어느것이나 하기에 표시하는 평가기준에 따랐다.In (1) and (2), all the test results followed the evaluation criteria shown below.

(평가기준)(Evaluation standard)

20명중 16명 이상이 두드러짐이 없다고 평가하였다: ◎More than 16 out of 20 rated no appreciation:

20명중 12명 이상이 두드러짐이 없다고 평가하였다: ○More than 12 out of 20 respondents were not prominent:

20명중 6명 이상이 두드러짐이 없다고 평가하였다: △More than six out of twenty assessed no noticeable:

20명중 6명 미만이 두드러짐이 없다고 평가하였다: ×Fewer than six out of twenty assessed no appreciation: ×

실시예 비교예EXAMPLES Comparative Example 23 24 25 26 27 8 923 24 25 26 27 8 9 (1) 흰색의 두드러짐 시험 ○ ○ ○ ◎ ◎ ○ △(1) White stand out test ○ ○ ○ ◎ ◎ ○ △ (2) 수세후의 흰색의 두드러짐 시험 ○ ○ ○ ◎ ◎ × ×(2) White outstanding test after washing ○ ○ ○ ◎ ◎ × ×

「표 5」의 결과로부터 명백한 바와같이, 본발명의 실시예는, 수세후의 흰색이 두드러지지 않는 우수한, 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료 임을 알 수 있다.As is apparent from the results of Table 5, it can be seen that the embodiment of the present invention is a cosmetic material which prevents the skin from blacking in the sun, which is excellent in white after washing with water.

이상 설명한바와 같이, 본 발명에 의하면, 광범위한 유분에 첨가혼합하더라도, 안정성, 안전성, 사용성에 우수한 유성겔 조성물 또는 유화조성물을 생성할 수 있는 겔화제 또는 유화제, 및 이를 사용한 겔조성물 또는 유화조성물을 제공할 수 있다.As described above, the present invention provides a gelling agent or an emulsifying agent capable of producing an oily gel composition or an emulsion composition excellent in stability, safety, and usability even when added to a wide range of oils, and a gel composition or an emulsion composition using the same. can do.

본발명의 겔화제 또는 유화제를 사용한 겔 조성물 또는 유화조성물은, 예를들면, 화장품, 의약부외품 등의 기제로서 바람직하게 사용된다.The gel composition or emulsion composition using the gelling or emulsifying agent of the present invention is preferably used as a base for cosmetics, quasi-drugs and the like.

또, 본 발명에 의하면, 살갗에의 밀착성이 좋고, 내수성에 우수하고, 땀 또는 바다나 풀에서의 활동에 동반하는 물과의 접촉에 의해서도, 살갗에 도포한 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료가 희게 떠오르는 일이 없는 우수한 사용성을 갖는 피부가 햇볕에 타서 검게되는 것을 방지하는 화장재료를 제공할 수가 있다. 따라서, 흰색의 두드러짐을 마음에 둘 필요없이, 필요량의 자외선방어제 분말을 배합할 수 있으므로 특히 높은 자외선 방어효과를 기대하는 경우에 유용하다.Furthermore, according to the present invention, the adhesion to skin is good, the water resistance is excellent, and the skin applied to skin is prevented from burning in the sun even by contact with water accompanying sweat or activity in the sea or grass. It is possible to provide a cosmetic material which prevents the skin having excellent usability without causing the cosmetic material to be whitened from being sunburned and blackened. Therefore, since it is possible to mix the required amount of the ultraviolet protective agent powder without having to take notice of the whiteness, it is particularly useful when a high ultraviolet protective effect is expected.

Claims (6)

3층구조를 갖는 콜로이드성 함수 규산 알루미늄의 일종으로 하기 일반식The following general formula is a kind of colloidal aluminum silicate having a three-layer structure (X, Y)2-3(Si, Al)4O10(OH)2Z1/3·nH2O(X, Y) 2-3 (Si, Al) 4 O 10 (OH) 2 Z 1 / 3nH 2 O 단, X = Al, Fe(III), Mn(III), Cr(III)Provided that X = Al, Fe (III), Mn (III), Cr (III) Y = Mg, Fe(II), Ni, Zn, Li, Mn(II)    Y = Mg, Fe (II), Ni, Zn, Li, Mn (II) Z = K, Na, 1/2Ca, 1/2Mg 으로 나타내어지는 수팽윤성 점토광물과     Water swellable clay mineral represented by Z = K, Na, 1 / 2Ca, 1 / 2Mg 하기의 일반식General formula (식중 R1은 탄소수 10∼22의 알킬기 또는 벤질기, R2는 메틸기 또는 탄소수 10∼22의 알킬기, R3과 R4는 탄소수 1∼3의 알킬기 또는 히드록시 알킬기, X는 할로겐원자 또는 메틸술페이트 잔기를 나타낸다.)으로 나타내어지는 4차 암모늄염형 양이온 계면활성제와, 상온액체의 지방산을 혼합해서 얻어지는 것을 특징으로 하는 겔화제로서, 상기 4차 암모늄염형 양이온 계면활성제의 혼합량이 상기 수팽윤성 점토광물 100g에 대해서 60~140 밀리당량이고, 상기 상온액체의 지방산의 혼합량이 상기 수팽윤성점토광물 100g에 대해서 1~500g인 것을 특징으로 하는 겔화제.Wherein R 1 is an alkyl group or benzyl group having 10 to 22 carbon atoms, R 2 is a methyl group or an alkyl group having 10 to 22 carbon atoms, R 3 and R 4 are an alkyl group or hydroxy alkyl group having 1 to 3 carbon atoms, X is a halogen atom or methyl It is obtained by mixing the quaternary ammonium salt type | mold cationic surfactant shown to a sulfate residue, and the fatty acid of a normal-temperature liquid, and the mixing amount of the said quaternary ammonium salt type | mold cationic surfactant is said water-swellable clay. A gelling agent, characterized in that 60 to 140 milliliter equivalents with respect to 100 g of minerals, and 1 to 500 g with respect to 100 g of the water-swellable clay minerals. 제 1 항에 있어서, 상기 상온액체의 지방산이 이소스테아르산인 것을 특징으로 하는 겔화제.The gelling agent according to claim 1, wherein the fatty acid of the room temperature liquid is isostearic acid. 제 1항 또는 제 2항의 겔화제와 유분을 포함하는 것을 특징으로 하는 겔조성물로서, 상기 유분은 트리글리세린, 트리옥탄산글리세린, 트리이소팔미트산 글리세린, 라놀린지방산폴리에틸렌글리콜, 유동파라핀, 스쿠알란, 파라핀, 와셀린, 스테아르산, 12-히드록시 스테아르산, 스테아릴알코올, 세토스테아릴알코올, 트리-2-에틸헥실산글리세린, 올레산오일, 메틸페닐폴리실록산 및 데카메틸폴리실록산으로 이루어지는 군으로부터 선택되는 것을 특징으로 하는 겔 조성물.A gel composition comprising the gelling agent and oil of claim 1 or 2, wherein the oil is triglycerol, glycerin trioctanoate, glycerin triisopalmitate, lanolin fatty acid polyethylene glycol, liquid paraffin, squalane, paraffin. , Waselin, stearic acid, 12-hydroxy stearic acid, stearyl alcohol, cetostearyl alcohol, tri-2-ethylhexyl glycerol, oleic oil, methylphenylpolysiloxane and decamethylpolysiloxane, characterized in that Gel composition. 3층구조를 갖는 콜로이드성 함수 규산 알루미늄의 일종으로 하기 일반식The following general formula is a kind of colloidal aluminum silicate having a three-layer structure (X, Y)2-3(Si, Al)4O10(OH)2Z1/3·nH2O(X, Y) 2-3 (Si, Al) 4 O 10 (OH) 2 Z 1 / 3nH 2 O 단, X = Al, Fe(III), Mn(III), Cr(III)Provided that X = Al, Fe (III), Mn (III), Cr (III) Y = Mg, Fe(II), Ni, Zn, Li, Mn(II)    Y = Mg, Fe (II), Ni, Zn, Li, Mn (II) Z = K, Na, 1/2Ca, 1/2Mg으로 표시되어지는 수팽윤성점토광물과    Z = K, Na, 1 / 2Ca, 1 / 2Mg and the water swellable clay mineral 하기 일반식General formula (식중 R1은 탄소수 10∼22의 알킬기 또는 벤질기, R2는 메틸기 또는 탄소수 10∼22의 알킬기, R3과 R4는 탄소수 1∼3의 알킬기 또는 히드록시 알킬기, X는 할로겐원자 또는 메틸술페이트 잔기를 나타낸다.)으로 표시되어지는 4차 암모늄염형 양이온 계면활성제와 상온액체의 고급 알코올을 혼합해서 얻어지는 것을 특징으로 하는 겔화제로서, 상기 4차 암모늄염형 양이온 계면활성제의 혼합량이 상기 수팽윤성점토광물 100g에 대해서, 60~140밀리당량이고, 상기 상온액체의 고급 알코올의 혼합량이 상기 수팽윤성점토광물 100g에 대해서, 1~500g인 것을 특징으로 하는 겔화제.Wherein R 1 is an alkyl group or benzyl group having 10 to 22 carbon atoms, R 2 is a methyl group or an alkyl group having 10 to 22 carbon atoms, R 3 and R 4 are an alkyl group or hydroxy alkyl group having 1 to 3 carbon atoms, X is a halogen atom or methyl A gelation agent obtained by mixing a quaternary ammonium salt type cationic surfactant and a higher alcohol of a room temperature liquid, wherein the amount of the quaternary ammonium salt type cationic surfactant is mixed. It is 60-140 milliliter equivalents with respect to 100g of clay minerals, The gelling agent characterized by the mixed amount of the higher alcohol of the said normal-temperature liquid is 1-500g with respect to 100g of said water swellable clay minerals. 제 4항에 있어서, 상기 상온액체의 고급 알코올이 이소스테아릴알코올인 것을 특징으로 하는 겔화제.The gelling agent according to claim 4, wherein the higher alcohol of the room temperature liquid is isostearyl alcohol. 제 4항 또는 제 5항의 겔화제와 유분을 포함하는 것을 특징으로 하는 겔조성물로서, 상기 유분은 트리글리세린, 트리옥탄산글리세린, 트리이소팔미트산 글리세린, 라놀린지방산폴리에틸렌글리콜, 유동파라핀, 스쿠알란, 파라핀, 와셀린, 스테아르산, 12-히드록시 스테아르산, 스테아릴알코올, 세토스테아릴알코올, 트리-2-에틸헥실산글리세린, 올레산오일, 메틸페닐폴리실록산 및 데카메틸폴리실록산으로 이루어지는 군으로부터 선택되는 것을 특징으로 하는 겔 조성물.A gel composition comprising the gelling agent and oil of claim 4 or 5, wherein the oil is triglycerol, glycerin trioctanoate, glycerin triisopalmitate, lanolin fatty acid polyethylene glycol, liquid paraffin, squalane, paraffin. , Waselin, stearic acid, 12-hydroxy stearic acid, stearyl alcohol, cetostearyl alcohol, tri-2-ethylhexyl glycerol, oleic oil, methylphenylpolysiloxane and decamethylpolysiloxane, characterized in that Gel composition.
KR1019980710544A 1997-05-30 1998-05-28 Gelling agent and gel compositions KR100618462B1 (en)