KR100490884B1 - Release film for automatic labeller and preparing method thereof - Google Patents
Release film for automatic labeller and preparing method thereof Download PDFInfo
- Publication number
- KR100490884B1 KR100490884B1 KR10-2002-0033442A KR20020033442A KR100490884B1 KR 100490884 B1 KR100490884 B1 KR 100490884B1 KR 20020033442 A KR20020033442 A KR 20020033442A KR 100490884 B1 KR100490884 B1 KR 100490884B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- release film
- film
- automatic labeling
- release
- Prior art date
Abstract
본 발명은 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 기재필름의 상면에 실리콘 수지를 증착시킨 실리콘 이형층과 하면에 아크릴계 수지 45 내지 55중량%, 착색제 4 내지 8중량%, 첨가제 1 내지 5중량% 및 용제 35 내지 45중량%를 차례로 배합하여 이루어진 코팅액이 적용된 코팅층을 갖는 자동라벨기용 이형필름 및 이의 제조방법에 관한 것이다. 본 발명에 따라 제조된 자동라벨기용 이형필름은 종래의 통상적으로 사용되는 그라싱지(glassine) 또는 크라프트지(kraft) 등의 이형지와 비교하여 인장강도가 커서 자동라벨 공정 중에 끊어질 가능성이 낮을 뿐만 아니라, 자동라벨기에 적용된 후의 필름이 바코드, 인쇄, 프린터, 복사기, 팩스, 필기류 등의 모든 인쇄매체에 적용하는 것이 가능하여 재활용면에서 크게 기여할 것으로 기대된다. The present invention is a silicone release layer in which a silicone resin is deposited on an upper surface of a polypropylene or polyethylene terephthalate base film and 45 to 55% by weight of an acrylic resin, 4 to 8% by weight of a colorant, 1 to 5% by weight of an additive and a solvent 35 to It relates to a release film for an automatic labeling machine having a coating layer applied by sequentially mixing 45% by weight and a method for producing the same. The release film for an automatic labeling machine manufactured according to the present invention has a high tensile strength compared to a release paper such as glassine or kraft paper, which is conventionally used, and has a low possibility of breaking during the automatic labeling process. In addition, it is expected that the film after being applied to the automatic labeling machine can be applied to all print media such as barcode, printing, printer, copier, fax, writing paper, etc., and will greatly contribute in terms of recycling.
Description
본 발명은 자동라벨기용 이형필름 및 이의 제조방법에 관한 것으로, 좀 더 구체적으로는 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 기재 필름의 상면에 실리콘 수지를 증착시킨 다음, 필름의 하면에 특수 코팅액을 처리하여 얻어진 이형필름 및 이의 제조방법에 관한 것이다. The present invention relates to a release film for an automatic labeling machine and a method for manufacturing the same, more specifically, a release obtained by depositing a silicone resin on the upper surface of a polypropylene or polyethylene terephthalate base film, and then treating a special coating liquid on the lower surface of the film. It relates to a film and a method for producing the same.
이형지(release paper) 또는 이형필름은 점착테이프의 점착면을 보호하기 위해 뒷면에 붙이는 종이 또는 필름으로, 점착테이프, 감압접착지, 라벨, 실 등의 점착면에 접촉시켜 면을 보호하고, 사용시에는 벗겨내어 목적을 달성할 수 있도록 표면가공이 되어 있다.Release paper or release film is a paper or film that is attached to the back side to protect the adhesive side of the adhesive tape.It protects the surface by contacting the adhesive side such as adhesive tape, pressure-sensitive adhesive paper, labels, and seals. The surface is processed to peel off and achieve the purpose.
일반적으로 이형지로 사용되는 원지로는 그라싱지(glassine), 크라프트지(kraft), 필름 등이 있고, 박리처리제로는 실리콘이 사용되는 것이 일반적이다. Generally, a base paper used as a release paper includes glassine, kraft paper, a film, and the like, and silicon is generally used as a release treatment agent.
종래의 자동라벨기용 이형재로는 일반적으로 백색 또는 옥색의 그라싱지 또는 크라프트지를 기재로 하고, 그 상면에 실리콘으로 이형처리하여 사용한다. 그러나, 그라싱지는 국내 생산이 불가한 품목으로 전량 수입에 의존하고 있어 그 구매원가가 1톤당 200만원이상으로 매우 고가이고, 자동라벨기에 적용된 후에 남은 그라싱지는 전량 폐기처리되어 그 재생이 불가능하며, 인장강도면에서도 종이류의 한계를 벗어나지 못하므로 라벨기의 고인장에 의해 파열되는 경우가 빈번히 발생하고 있다. As a release material for a conventional automatic labeling machine, generally, a white or aqua colored grazing paper or kraft paper is used as a base material, and the upper surface thereof is used by release treatment with silicon. However, since the grazing paper is an item that cannot be produced domestically, it depends on the total imports, so the purchase cost is very expensive, more than 2 million won per ton, and the remaining grazing paper after the application of the automatic labeling machine is discarded and cannot be recycled. In addition, even in terms of tensile strength, it is frequently broken due to the high tension of the labeling machine.
또한, 크라프트지는 그 위에 직접 실리콘 코팅을 할 수 없고, 폴리라미(polylami) 또는 클레이(clay) 코팅을 한 후에 실리콘을 증착시키는 것이 가능하므로 비용면에서 경제적이지 못하며, 인장강도 또한 종이류의 한계를 벗어나지 못하여 자동라벨기를 통과시 파열되는 경우가 있다.In addition, kraft paper is not directly coated on it, and it is not economical in terms of cost because it is possible to deposit silicon after polylami or clay coating, and the tensile strength does not exceed the limits of paper. It may be broken when passing through automatic labeling machine.
한편, 자동라벨기에 적용되는 이형필름에 관한 종래기술을 살펴보면, 한국 공개특허 제1997-20424호에서는 2축연신 폴리프로필렌에 실리콘을 처리하여 폴리에틸렌테레프탈레이트나 그라싱지를 대체하여 이형재로 사용하는 것을 개시하고 있으나, 그 효과를 증명할 수 있는 데이터를 나타내지 않고 본 발명에서 사용한 바와 같은 특수 코팅액으로 코팅처리하여 재활용도 및 인장강도를 높이는 기술에 대한 기재는 없다. On the other hand, looking at the prior art related to the release film applied to the automatic labeling machine, Korean Unexamined Patent Publication No. 1997-20424 discloses the use of a release material by replacing polyethylene terephthalate or grasping paper by treating silicon with biaxially stretched polypropylene. However, there is no description of a technique for increasing the recyclability and tensile strength by coating with a special coating liquid as used in the present invention without showing data that can prove the effect.
이에 본 발명에서는 종래의 이형지 또는 이형필름과 비교하여 강도가 우수하고, 자동라벨기에 적용 후에도 재활용할 수 있는 이형필름에 대한 다양한 연구를 수행한 결과, 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 필름의 하면에 본 발명에 따른 특수코팅액을 적용함으로써 강도가 우수하고, 재활용이 가능한 자동라벨기용 이형필름을 얻을 수 있었고, 이를 기초로 하여 본 발명을 완성하였다. Therefore, in the present invention, as compared with the conventional release paper or release film, the strength of the excellent, and after various studies on the release film that can be recycled even after applying the automatic labeling machine, the present invention on the lower surface of the polypropylene or polyethylene terephthalate film By applying a special coating solution according to the excellent strength, was able to obtain a release film for automatic labeling can be recycled, based on this completed the present invention.
따라서, 본 발명의 목적은 인장강도가 우수하고, 재활용이 용이하며 저렴한 자동라벨기용 이형필름 및 이를 이용한 점착테이프를 제공하는데 있다. Accordingly, an object of the present invention is to provide a release film for an automatic labeling device having excellent tensile strength, easy recycling, and an adhesive tape using the same.
본 발명의 다른 목적은 상기 자동라벨기용 이형필름의 제조방법을 제공하는데 있다. Another object of the present invention to provide a method for manufacturing a release film for the automatic labeling machine.
본 발명의 또 다른 목적은 상기 이형필름을 점착제가 처리된 점착원지와 압동합지하여 자동라벨기용 점착테이프를 제공하는데 있다.Still another object of the present invention is to provide a pressure-sensitive adhesive tape for automatic labeling by releasing the release film with a pressure sensitive adhesive-treated adhesive base paper.
상기 목적을 달성하기 위하여, 본 발명의 자동라벨기용 이형필름은 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 기재필름의 상면에 실리콘 수지를 증착시킨 실리콘 이형층을 형성시키고, 하면에는 아크릴계 수지 45 내지 55중량%, 착색제 4 내지 8중량%, 첨가제 1 내지 5중량% 및 용제 35 내지 45중량%를 차례로 배합하여 얻어진 코팅액을 적용한 코팅층을 형성시키므로써 얻게 되며, 상기 이형필름을 점착제가 처리된 점착원지와 압동합지하여 점착테이프를 얻는다. In order to achieve the above object, the release film for automatic labeling of the present invention forms a silicone release layer in which a silicone resin is deposited on the upper surface of a polypropylene or polyethylene terephthalate base film, the lower surface of the acrylic resin 45 to 55% by weight, colorant 4 to 8% by weight, 1 to 5% by weight of additives and 35 to 45% by weight of a solvent are obtained by forming a coating layer to which the coating solution is applied. The release film is press-bonded with pressure-sensitive adhesive paper treated with pressure-sensitive adhesive. Get the tape.
상기 다른 목적을 달성하기 위하여, 본 발명의 자동라벨기용 이형필름의 제조방법은 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 기재필름 상면에 실리콘 이형층을 증착시키고, 상기 실리콘 이형층이 증착된 기재필름의 하면에 아크릴계 수지 45 내지 55중량%, 착색제 4 내지 8중량%, 첨가제 1 내지 5중량% 및 용제 35 내지 45중량%를 차례로 배합하여 이루어진 코팅액을 적용시키는 것으로 이루어진다. In order to achieve the above another object, the method of manufacturing a release film for an automatic labeling device of the present invention by depositing a silicon release layer on the upper surface of the polypropylene or polyethylene terephthalate base film, the acrylic film on the lower surface of the base film on which the silicon release layer is deposited It consists of applying the coating liquid which consists of 45-55 weight% of resin, 4-8 weight% of coloring agents, 1-5 weight% of additives, and 35-45 weight% of solvents in order.
이하 본 발명을 좀 더 구체적으로 살펴보면 다음과 같다. Looking at the present invention in more detail as follows.
전술한 바와 같이, 본 발명은 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 기재필름의 상면에 실리콘 수지를 증착시킨 실리콘 이형층과 하면에 아크릴계 수지 45 내지 55중량%, 착색제 4 내지 8중량%, 첨가제 1 내지 5중량% 및 용제 35 내지 45중량%를 차례로 배합하여 이루어진 코팅액이 적용된 코팅층을 갖는 자동라벨기용 이형필름 및 이의 제조방법에 관한 것이다.As described above, the present invention is 45 to 55% by weight, acrylic resin 4 to 8% by weight, colorant 4 to 8% by weight, additives 1 to 5 by the silicone release layer and the lower surface of the silicone release layer in which the silicone resin is deposited on the upper surface of the polypropylene or polyethylene terephthalate base film It relates to a release film for an automatic labeling machine having a coating layer to which the coating solution made by mixing the% and the solvent 35 to 45% by weight in order.
본 발명에서 이형필름의 기재로 사용되는 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 필름은 통상적인 방법에 따라 용융, 압출, 성형하고, 일축 또는 이축연신된 것이다. The polypropylene or polyethylene terephthalate film used as the substrate of the release film in the present invention is melted, extruded, molded, uniaxially or biaxially stretched according to a conventional method.
상기 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 필름 상면에 증착되는 실리콘 수지로는 용제형, 무용제형 또는 에멀젼 형태 등이 모두 가능하고, 박리 안정성이 우수하고, 저온 단시간 열처리로 경화가 가능하며, 코팅후 코팅된 이형제의 표면이동이 적은 특성을 갖는 실리콘 수지가 바람직하다.The silicone resin deposited on the upper surface of the polypropylene or polyethylene terephthalate film may be a solvent type, a solvent-free type, or an emulsion form, all have excellent peeling stability, and may be cured by low temperature and short time heat treatment, and are coated with a release agent after coating. The silicone resin which has the characteristic of little surface movement of is preferable.
본 발명에서 사용되는 코팅액은 아크릴계 수지 45 내지 55중량%, 착색제 4 내지 8중량%, 첨가제 1 내지 5중량% 및 용제 35 내지 45중량%를 상온에서 순차적으로 첨가하여 5 내지 10분간 교반시켜 얻어진다. The coating liquid used in the present invention is obtained by sequentially adding 45 to 55% by weight of acrylic resin, 4 to 8% by weight of colorant, 1 to 5% by weight of additive, and 35 to 45% by weight of solvent at room temperature and stirring for 5 to 10 minutes. .
상기 아크릴계 수지는 에멀젼형이고, 그 첨가량이 45중량% 미만이면 점착성이 약해지고, 55중량%를 초과하면 점착성이 너무 강해지는 문제점이 있고, 상기 착색제는 카본블랙, 아조 화합물, 파우더 안료로 이루어진 군으로부터 선택된 하나 이상으로, 그 사용량이 4중량% 미만이면 색상이 밝지 않고, 8중량%를 초과하면 색상이 너무 짙어지는 문제점이 있다. 상기 아크릴계 수지에 착색제를 배합한 후, 첨가되는 첨가제는 가소제, 산화방지제, 자외선차단제 등이고, 그 첨가량이 1중량% 미만이면 산화방지 및 자외선 차단 등의 효과가 없으며, 5중량%를 초과하면 갈라지는 현상이 발생되는 문제점이 있다. 상기 성분들을 용해시키기 위해 최종적으로 용제가 첨가되는데, 이는 캡톤, 폴리비닐알코올, 에틸비닐아세테이트 및 글리콜로 이루어진 군으로부터 선택된 하나 이상으로 그 첨가량이 35중량% 미만이면 다른 화학성분들과 융화되지 않으며, 45중량%를 초과하면 빠른 속도로 굳어지는 현상이 발생되는 문제점이 있다.The acrylic resin is an emulsion type, when the added amount is less than 45% by weight, the adhesiveness is weakened, when the amount exceeds 55% by weight, the adhesiveness is too strong, the colorant is from the group consisting of carbon black, azo compound, powder pigment At least one selected, if the amount is less than 4% by weight, the color is not bright, if more than 8% by weight there is a problem that the color is too dark. After the colorant is blended with the acrylic resin, the additives added are plasticizers, antioxidants, sunscreens, etc., and if the amount is less than 1% by weight, there is no effect of anti-oxidation and UV protection. There is a problem that occurs. Solvent is finally added to dissolve the components, which are at least one selected from the group consisting of Kapton, polyvinyl alcohol, ethylvinylacetate and glycol, and when the addition amount is less than 35% by weight, are not compatible with other chemical components. If the weight percentage is exceeded, there is a problem that the phenomenon of hardening at a high speed occurs.
한편, 상기 코팅액에 옥색 또는 백색의 색깔을 나타내도록 하기 위해 안료를 추가로 첨가하는 것이 가능하다. On the other hand, it is possible to further add a pigment to the color of the coating solution to give a turquoise or white color.
본 발명에 따르면, 상기 폴리프로필렌 또는 폴리에틸렌테레프탈레이트 필름을 기재로 하고, 그 상면에 상기 실리콘 수지를 코팅로울러를 이용하여 코팅하고, 가열·건조시켜 증착시키고, 상기 실리콘 수지가 증착된 기재의 하면에 상기 제조된 코팅액을 통상의 코팅 방법, 예컨대, 혼마, 리버스, 역회전, 그라비아 등으로 코팅하여 인장강도가 우수하고, 재활용이 용이한 자동라벨기용 이형필름을 얻었다. According to the present invention, the polypropylene or polyethylene terephthalate film is used as a substrate, and the upper surface of the silicone resin is coated using a coating roller, and heated and dried to deposit the lower surface of the substrate on which the silicone resin is deposited. The coating solution prepared above was coated with a conventional coating method, such as Honma, reverse, reverse rotation, gravure, etc., thereby obtaining a release film for automatic labeling device having excellent tensile strength and easy recycling.
상기 자동라벨기용 이형필름은 종래의 그라싱지 또는 크라프트지 등의 종이와 비교하여 인장강도가 우수할 뿐만 아니라, 그 하면에 특수코팅액이 처리되어 자동라벨기에 적용된 후에 바코드, 인쇄, 프린터, 복사기, 팩스 및 각종 필기류 등의 인쇄매체에 사용하여 재활용될 수 있다. The release film for the automatic labeling machine not only has excellent tensile strength as compared with conventional paper such as grasping paper or kraft paper, but also has a special coating liquid on the bottom thereof, and is applied to an automatic labeling machine, such as barcode, printing, printer, copier, It can be used for printing media such as fax and various writing papers.
이하 실시예를 통하여 본 발명을 좀 더 구체적으로 설명하지만, 하기 실시예에 본 발명의 범주가 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to the following Examples, but the scope of the present invention is not limited to the following Examples.
실시예 1Example 1
코팅액의 제조Preparation of Coating Liquid
1) 용제1) Solvent
캡톤 40중량%, 알코올 10중량%, 초산에스틸렌 35중량% 및 글리콜 15중량%의 비율로 배합.It is blended in the ratio of 40 weight% of Kapton, 10 weight% of alcohol, 35 weight% of styrene acetate, and 15 weight% of glycol.
2) 착색제2) colorant
카본블랙 20중량%, 아조 25중량% 및 지당 55중량%의 비율로 배합. Formulated in a proportion of 20% carbon black, 25% azo and 55% by weight per branch.
3) 수지3) resin
아크릴바인더 100중량%.100% by weight of acrylic binder.
4) 첨가제4) additive
가소제 30중량%, 산화방지제 35중량%, 자외선 차단제 35중량%의 비율로 배합. 30% by weight of plasticizer, 35% by weight of antioxidant, 35% by weight of sunscreen.
상기 준비된 4종의 배합물을 수지 51.6중량%, 착색제 6.5중량%, 첨가제 3.2중량%, 용제 38.7중량%의 비율로 상온(1기압, 20℃)에서 순차적으로 첨가하여 5분간 교반시켜 코팅액을 얻었다. The four blends prepared above were added sequentially at room temperature (1 atm, 20 ° C.) at a ratio of 51.6% by weight of resin, 6.5% by weight of colorant, 3.2% by weight of additive, and 38.7% by weight of solvent to obtain a coating solution.
실시예 2Example 2
이형필름의 제조Manufacturing of Release Film
실리콘 수지(한국다우코닝 LS-203) 25중량%와 톨루엔 75중량%를 혼합하고, 백금촉매(한국다우코닝 SO-4000) 0.25중량%를 첨가, 5분간 교반하여 실리콘 수지 조성물을 얻었다. 두께가 30㎛인 폴리프로필렌 필름 위에 상기 실리콘 수지 조성물을 코팅 로울러를 이용하여 코팅한 후, 115℃의 건조닥트를 분당 50m의 속도로 진행하여 건조시켜 실리콘 이형층의 두께가 1㎛ 이하(0.2-0.3g/㎡)가 되도록 하였다. 25 weight% of silicone resin (Dow Corning LS-203) and 75 weight% of toluene were mixed, 0.25 weight% of platinum catalyst (Dow Corning SO-4000) was added, and it stirred for 5 minutes, and obtained the silicone resin composition. After coating the silicone resin composition on a polypropylene film having a thickness of 30 μm using a coating roller, a drying duct at 115 ° C. was carried out at a speed of 50 m per minute to be dried and the thickness of the silicone release layer was 1 μm or less (0.2− 0.3 g / m 2).
상기 실시예 1에서 얻어진 코팅액을 상기 실리콘 수지가 증착된 필름의 하면에 그라비아 코팅기, 헤리어 로울러 #100(원일기계)으로 2。 코팅을 실시하여 두께 10㎛의 코팅층을 갖는 이형필름을 얻었다. The coating solution obtained in Example 1 was coated on the lower surface of the film on which the silicone resin was deposited with a gravure coating machine and a Harrier Roller # 100 (one machine) to obtain a release film having a coating layer having a thickness of 10 μm.
실시예 3Example 3
이형필름의 제조Manufacturing of Release Film
실리콘 수지(한국다우코닝 LS-203) 25중량%와 톨루엔 75중량%를 혼합하고, 백금촉매(한국다우코닝 SO-4000) 0.25중량%를 첨가, 5분간 교반하여 실리콘 수지 조성물을 얻었다. 두께가 19㎛인 폴리에틸렌테레프탈레이트 필름 위에, 상기 실리콘 수지 조성물을 코팅 로울러를 이용하여 코팅한 후, 115℃의 건조닥트를 분당 40m의 속도로 진행하여 건조시켜 실리콘 이형층의 두께가 1㎛ 이하(0.2-0.3g/㎡)가 되도록 하였다. 25 weight% of silicone resin (Dow Corning LS-203) and 75 weight% of toluene were mixed, 0.25 weight% of platinum catalyst (Dow Corning SO-4000) was added, and it stirred for 5 minutes, and obtained the silicone resin composition. After coating the silicone resin composition on a polyethylene terephthalate film having a thickness of 19 μm using a coating roller, a 115 ° C. drying duct was carried out at a speed of 40 m per minute to be dried, and the thickness of the silicone release layer was 1 μm or less ( 0.2-0.3 g / m 2).
상기 실시예 1에서 얻어진 코팅액을 상기 실리콘 수지가 증착된 필름의 하면에 그라비아 코팅기, 헤리어 로울러 #100(원일기계)으로 2。 코팅을 실시하여 두께 10㎛의 코팅층을 갖는 이형필름을 얻었다. The coating solution obtained in Example 1 was coated on the lower surface of the film on which the silicone resin was deposited with a gravure coating machine and a Harrier Roller # 100 (one machine) to obtain a release film having a coating layer having a thickness of 10 μm.
실시예 4Example 4
점착코팅기(주식회사 흥일기계)를 이용하여 점착원지(PET 필름, 25㎛)를 코팅부에서 아크릴점착제를 도포한 후, 140℃의 건조닥트를 분당 35m의 속도로 통과시켜 건조한 후, 압동부의 압동로울러에서 실시예 2에 따라 제조된 이형필름과 압동합지하여 자동라벨기용 점착테이프를 제조하였다(도 2 참조). After applying the acrylic adhesive on the coating part using an adhesive coating machine (Hungil Machinery Co., Ltd.), and passing through the drying duct at 140 ° C at a speed of 35m per minute, the pressure of the pressure part Pressure-bonded with the release film prepared according to Example 2 in a roller to prepare an adhesive tape for an automatic labeling machine (see Fig. 2).
실시예 5Example 5
점착코팅기(주식회사 흥일기계)를 이용하여 점착원지(PET 필름, 25㎛)를 코팅부에서 아크릴점착제를 도포한 후, 140℃의 건조닥트를 분당 35m의 속도로 통과시켜 건조한 후, 압동부의 압동로울러에서 실시예 3에 따라 제조된 이형필름과 압동합지하여 자동라벨기용 점착테이프를 제조하였다(도 2 참조).After applying the acrylic adhesive on the coating part using an adhesive coating machine (Hungil Machinery Co., Ltd.), and passing through the drying duct at 140 ° C at a speed of 35m per minute, the pressure of the pressure part Pressure-bonded with the release film prepared according to Example 3 in a roller to prepare an adhesive tape for an automatic labeling machine (see Fig. 2).
전술한 바와 같이, 본 발명에 따라 제조된 자동라벨기용 이형필름은 종래의 그라싱지 또는 크라프트지 등과 비교하여 인장강도가 우수하여 작업 중 잘 끊어지지 않을 뿐만 아니라, 자동라벨기에 적용된 후에, 바코드, 인쇄, 프린터, 복사기, 팩스 및 각종 필기류 등의 인쇄매체에 사용함으로써 재활용될 수 있으며, 비용이 종래의 그라싱지에 비해 저렴하므로 경제적 효과도 볼 수 있는 장점이 있다. As described above, the release film for the automatic labeling machine manufactured according to the present invention has excellent tensile strength as compared to conventional grasping paper or kraft paper, and is not easily broken during the operation. It can be recycled by using in printing media such as printing, printers, copiers, faxes, and various writing materials, and the cost is cheaper than conventional grasping papers, so there is an advantage in that economic effects can be seen.
도 1은 본 발명에 따른 자동라벨기용 이형필름을 구비한 점착테이프의 단면도이다. 1 is a cross-sectional view of an adhesive tape having a release film for automatic labeling machine according to the present invention.
도 2는 본 발명에 따른 점착코팅기의 구성도이다.2 is a block diagram of an adhesive coating machine according to the present invention.
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 … 기재 필름 2 … 실리콘 이형층One … Base film 2. Silicon release layer
3 … 코팅액 4 … 점착제층3…. Coating liquid 4. Adhesive layer
5 … 점착원지 6 … 코팅로울러5... Adhesive base 6. Coating Roller
7 … 건조닥트 8 … 이형필름7. Dry doc 8. Release Film
9 … 압동로울러 10 … 점착테이프9. Pressure roller 10. Adhesive Tape
Claims (9)