KR100463377B1 - Finish coat using serpentine-jade stones and construction method thereof - Google Patents
Finish coat using serpentine-jade stones and construction method thereof Download PDFInfo
- Publication number
- KR100463377B1 KR100463377B1 KR1020040042624A KR20040042624A KR100463377B1 KR 100463377 B1 KR100463377 B1 KR 100463377B1 KR 1020040042624 A KR1020040042624 A KR 1020040042624A KR 20040042624 A KR20040042624 A KR 20040042624A KR 100463377 B1 KR100463377 B1 KR 100463377B1
- Authority
- KR
- South Korea
- Prior art keywords
- finishing material
- cement
- weight
- parts
- serpentine
- Prior art date
Abstract
Description
본 발명은 사문옥석을 이용한 마감재에 관한 것으로, 더 상세하게는 사문옥석과 시멘트를 일정 비율로 혼합한 마감재와 이를 이용하여 건물의 바닥, 벽, 천장 등에 마감공사를하여 음이온과 원적외선 등의 유익한 성분이 다량 방출 가능하게 하는 사문옥석을 이용한 마감재 및 이를 이용한 건물시공방법에 관한 것이다.The present invention relates to a finishing material using serpentine stone, and more particularly, a finishing material in which a serpentine stone and cement are mixed at a predetermined ratio, and using the same, to finish a construction work on a floor, a wall, a ceiling, etc., and thus beneficial components such as anion and far infrared rays. The present invention relates to a finishing material using a serpentine jade stone and a building construction method using the same.
일반적으로 음이온은 원적외선과 마찬가지로 인체에 유익한 성분이라는 널리 알려져 왔다. 따라서, 이러한 유익한 성분인 음이온을 생활에 직접 접목하기 위해 공기청전제, 헤어드라이 등 각종 가전제품에 접목하여 사용되고 있다.In general, negative ions have been widely known as beneficial components to the human body, as well as far infrared rays. Therefore, in order to directly grafting an anion, which is such a beneficial component, into life, it is used in various household appliances such as an air cleaner and a hair dryer.
그러나, 상기 방법은 특정장소 일부분에 대해 임시적인 효과만 얻을 수 있는 것으로 일반인들의 주생활지인 주택 사무실 등의 건물 자체내에서 방출되는 유해물질에 대해서는 대체방안이 없는 실정이다.However, the method can only obtain a temporary effect on a part of a specific place, and there is no alternative for harmful substances emitted in the building itself, such as a residential office, which is the main residence of the general public.
즉, 기존의 주거용 건물 건설에 있어서 바닥은 콘크리트골조 위에 난방을 위한 온수파이프를 배관하고 온수파이프 주위를 모래나 자갈등으로 채운 다음, 시멘트를 이용하여 미장하고, 장판이나 비닐장판을 도배하는 방법으로 시공되며, 벽은 벽돌을 적층하여 형성하거나, 콘크리트골조에 시멘트를 타설한 후 벽지나 페인트로 도배하여 형성한다.In other words, in the construction of existing residential buildings, the floors are piped with hot water pipes for heating on concrete frameworks, filled with sand or gravel around the hot pipes, and then plastered with cement and plated with floor coverings or vinyl flooring. It is constructed, and the wall is formed by stacking bricks or by pouring cement on concrete frames and then painting them with wallpaper or paint.
이와같이 상기 건물 시공에는 시멘트가 필수적으로 사용되고 있어 시멘트에서 방출되는 다량의 양이온으로 인해 인체의 균형이 깨트려 질 수 있으며, 각종 미장재를 붙이기 위한 접착재로 인한 인체에 유해한 화학성분의 다량방출로 거주자의 건강을 해 할 수 있는 문제점이 있다.As such, cement is essential for the building construction, and the balance of the human body may be broken due to the large amount of cations emitted from the cement, and due to the large amount of chemicals harmful to the human body due to the adhesive for attaching various plastering materials, There are problems that can harm your health.
따라서, 본 발명은 상기 종래의 문제점을 해소하기 위해 안출된 것으로,Accordingly, the present invention has been made to solve the above conventional problems,
건물의 바닥, 벽, 천장 등의 마감재에 천연광물의 혼합물인 사문옥석을 혼합 또는 상기 마감재의 재료인 시멘트를 양이온 발생량이 적은 백시멘트로 하고 이에 사문옥석을 혼합하여 사용함으로서, 건물에서 방출되는 양이온의 량을 저하시키고, 음이온의 방출량을 증가시키며, 원적외선의 다량방출로 열효율을 향상시킬 수 있는 사문옥석을 이용한 마감재 및 이를 이용한 건물시공방법을 제공하는데 있다.The cation released from the building by mixing serpentine stone, which is a mixture of natural minerals, with cement, which is a material of the finishing material, with a low amount of cation generation, and by mixing serpentine stone in the cement, which is a material of the finishing material. The present invention provides a finishing material using serpentine gemstones and a building construction method using the same, which can lower the amount, increase the amount of negative ions, and improve thermal efficiency by emitting large amounts of far infrared rays.
도 1은 본 발명의 마감재를 이용한 건물시공방법에 따른 일실시예로 주택바닥시공상태를 도시한 단면도이고,1 is a cross-sectional view showing a home floor construction state as an embodiment according to the building construction method using the finishing material of the present invention,
도 2는 본 발명의 마감재를 이용한 건물시공방법에 따른 다른 실시예로 주택 바닥시공상태를 도시한 단면도이고,Figure 2 is a cross-sectional view showing a house floor construction in another embodiment according to the building construction method using the finishing material of the present invention,
도 3은 본 발명의 마감재를 이용한 건물시공방법에 따른 일실시예로 사무실 바닥시공상태를 도시한 단면도이고,3 is a cross-sectional view showing an office floor construction in one embodiment according to the building construction method using the finishing material of the present invention,
도 4는 본 발명의 마감재를 이용한 건물시공방법에 따른 일실시예로 벽시공상태를 도시한 단면도이다.Figure 4 is a cross-sectional view showing a wall construction in one embodiment according to the building construction method using the finishing material of the present invention.
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>
10 : 골조(바닥보, 벽보) 20 : 단열재10: frame (floor beam, wall beam) 20: insulation
30 : 온수파이프 40 : 발포콘크리트30: hot water pipe 40: foamed concrete
50 : 마감재 60 : 방음재50: finishing material 60: sound insulation
70 : 벽지70: wallpaper
상기 과제를 달성하기 위한 본 발명의 사문옥석을 이용한 마감재는,Finishing material using the serpentine stone of the present invention for achieving the above object,
건물시공에 사용되는 마감재에 있어서, 시멘트 50중량부에 대해 입경이 0.1 ~ 20mm이하인 미분된 사문옥석 20 ~ 120 중량부, 모래 1 ~ 100 중량부로 구성됨을 특징으로 한다.Finishing material used in building construction, characterized in that it consists of 20 ~ 120 parts by weight of finely divided serpentine stone having a particle diameter of 0.1 ~ 20mm or less, and 1 ~ 100 parts by weight with respect to 50 parts by weight of cement.
상기 시멘트는 토목건축용으로 사용되고 포틀랜트시멘트가 대표적인 수경성(水硬性)시멘트; 소석회(消石灰;수산화칼슘)·석고·마그네시아시멘트 등과 같은 기경성(氣硬性)시멘트; 고로(高爐)시멘트·실리카시멘트·플라이애시시멘트와 같은혼합시멘트; 알루미나시멘트·콜로이드시멘트·오일웰시멘트·지열시멘트·내산(耐酸)시멘트 등과 같은 특수시멘트등이 사용될 수 있다.The cement is used for civil construction and portland cement is typical hydraulic cement; Rigid cements such as calcium hydroxide, gypsum and magnesia cement; Mixed cements such as blast furnace cement, silica cement and fly ash cement; Special cements such as alumina cement, colloid cement, oil well cement, geothermal cement, acid resistant cement and the like can be used.
또한, 시멘트를 제조하는 데 있어 원료의 철분을 제거하고, 소성할 때는 매연이 적은 석유 연료를 사용하며, 분쇄는 철구(鐵球) 대신 경질석재 또는 자기(瓷器)를 사용하는 등, 시멘트색의 원인이 되는 것을 제거해서 만들어진 백시멘트(백색포틀랜드시멘트)를 이용할 수 있다. 이러한 백시멘트는 양이온의 방출량이 적어서 후기에 혼합되는 사문옥석의 음이온 효과를 더욱 증대시킬 수 있는 것이다.In addition, in the manufacture of cement, iron powder of raw material is removed, and petroleum fuel with less soot is used for calcination, and grinding is made of cement color such as hard stone or porcelain instead of iron ball. A white cement (white portland cement) made by removing the cause can be used. Such a back cement is able to further increase the anion effect of serpentine stones mixed later due to the small amount of cation released.
그리고, 상기 사문옥석은, 사문석, 경옥, 연옥을 분쇄하여 혼합한 것으로, 인체에 유익한 성분인 원적외선, 음이온의 방출과 항균 및 탈취효과가 있으며, 혈액순환, 기(氣)순환을 원활히 하고 인체에 노폐물을 제거하는 등 생체활성화를 돕는다.In addition, the serpentine, which is a mixture of pulverized serpentine, jadeite, purgatory, has the beneficial effect of far-infrared rays, anions and antibacterial and deodorizing effect to the human body, and facilitates blood circulation, Ki circulation and the human body Helps vitalize the body by removing waste products.
상기 마감재에는 충전재인 모래를 혼합하여 사문옥석 투입량을 조절할 수 있다. 이는 고가인 사문옥석의 량을 조절함으로서 시공비를 절감할 수 있는 것인데, 이 때 사문옥석의 량을 사문옥석을 20중량부 이하로 혼합할 경우에는 사문옥석의 효과가 미비하게 되며, 120중량부 이상으로 혼합될 경우에는 시멘트 응고력의 한계를 초과하여 마감재로의 역할을 수행 할 수 없게 됨으로, 가장 바람직하게는 사문옥석을 20 ~ 120중량부 범위 내 즉, 시멘트를 50중량부에 대해 사문옥석과 모래의 혼합량을 120중량부로 혼합하는 것이다.The finish can be mixed with the serpentine stone by mixing the filler sand. This can reduce the construction cost by adjusting the amount of expensive serpentine stone, when the serpentine stone is mixed with the serpentine stone to 20 parts by weight or less, the serpentine stone effect is insufficient, more than 120 parts by weight When mixed with, it is impossible to play a role as a finishing material exceeding the limit of cement coagulation power, most preferably in the range of 20 to 120 parts by weight of serpentine, that is, cement with 50 parts by weight of serpentine The amount of sand is mixed at 120 parts by weight.
또한, 상기 마감재에는 원적외선 및 음이온의 방출량을 증대시키기 위해 귀양석 0.2 ~ 20 중량부를 더 포함시킬 수 있다.In addition, the finishing material may further include 0.2 to 20 parts by weight of jewels in order to increase the amount of far infrared rays and anions.
상기 귀양석은, 약 6,500만년전의 지각변동에 의한 고온열수작용에 의해 형성되어지며, 2000년 3월 워터사이언스 연구회의 발표에 의하면, 국내,외의 기능소재 25가지중에서 "귀양석[E-STONE]"이 마이너스이온 발생량이 최대(개/cc)9,451이며, 원적선방사율이 평균 96%로 최고의 수치를 나타내어 일약 각광을 받고 있는 자연계의 에너지를 하나로 응축한 특수광물이다. 이러한 귀양석은 석영을 중심으로 Al2O3/ K2O/ Fe2O3/ CaO/ Na2O/ MgO/ TiO2/ IgIoss 등의 성분이 혼합되어 구성된다.The earstone is formed by high temperature hydrothermal action due to earthquake fluctuations about 65 million years ago. The amount of negative ions generated is 9,451 (cc / cc), and the average radiation emission rate is 96%, which is the highest value. Such a gemstone is composed of a mixture of components such as Al 2 O 3 / K 2 O / Fe 2 O 3 / CaO / Na 2 O / MgO / TiO 2 / IgIoss around the quartz.
또한, 상기 마감재에는 상기 귀양석 이외에 황토에서 유익한 성분만을 취득한 황토미분, 맥반석등의 유익한 광물 또는 수맥을 차단하는 동(Cu)등의 기능성물질을 첨가할 수 있으며, 모래를 제외한 시멘트, 사문옥석, 귀양석등을 일정크기의 kg단위로 포장하여 판매하거나, 레미콘 등과 같은 이동식 믹서장치 또는 고정식 믹서장치를 이용하여 현장에 직접 제공할 수 있다.In addition, the finishing material may be added to the minerals, such as loess fine powder obtained by only the beneficial ingredients in loess, elvan, or functional materials such as copper (Cu) to block the vein, in addition to the precious stone, cement, serpentine, The ear canal is packaged and sold in a unit of kg of a certain size, or it can be provided directly to the site using a mobile mixer or a fixed mixer such as ready mixed concrete.
상기한 바와같이 제조된 사문옥석을 이용한 마감재는 건물 내외장의 마감처리에 이용되는 것으로 건물의 바닥면과 벽에 마감처리하거나, 벽돌제조에 이용되는 등 건설분야의 다양한 부분에 사용 가능하다.Finishing material using the serpentine jade stone manufactured as described above is used to finish the interior and exterior of the building can be used in various parts of the construction field, such as finishing the floor and walls of the building, or used in the manufacture of bricks.
일예로 바닥면을 형성하기 위한 마감재를 이용한 시공방법은, 건물의 내·외장면을 마감처리하는 시공방법에 있어서, 시멘트 50중량부에 대해 입경이 0.1 ~ 20mm이하인 미분된 사문옥석 20 ~ 120 중량부, 모래 1 ~ 80 중량부로 구성된 마감재를 5 ~ 20mm 두께로 미장처리하여 이루어진다.For example, the construction method using the finishing material for forming the floor surface, in the construction method for finishing the interior and exterior surfaces of the building, 20 to 120 weight of finely divided serpentine stone having a particle size of 0.1 ~ 20mm or less with respect to 50 parts by weight of cement Part, sand is made by plastering the finishing material consisting of 1 to 80 parts by weight to a thickness of 5 to 20mm.
즉, 골조 위에 단열제를 설치하고 단열제 위에 온수파이프를 배관한 다음, 온수파이프 주변을 발포콘크리트로 채우고, 상술한 마감재를 이용하여 소정의 두께로 미장작업을 하여 바닥을 형성하는 것이다.That is, the insulation is installed on the framework and the hot water pipes are piped on the insulation, then filled with foamed concrete around the hot water pipes, and plastered to a predetermined thickness using the above-described finishing material to form a floor.
상기 마감재의 두께가 5mm이하일 경우에는 충분한 강도를 유지할 수 없고, 방출되는 음이온 및 원적외선의 량이 현저하게 적다. 그리고, 20mm이상으로 형성할 경우에는 재료비가 과다하게 소요되고, 음이온 및 원적외선의 방출량의 증가가 둔화되며, 온수파이프에 의한 난방의 효과가 절감되는 문제점이 있기 때문에 5 ~ 20mm의 범위내로 시공하는 것이 바람직하다.When the thickness of the finishing material is 5 mm or less, sufficient strength cannot be maintained, and the amount of negative ions and far infrared rays emitted is remarkably small. In the case of forming more than 20mm, the material cost is excessive, the increase in the amount of anion and far-infrared emission is slowed down, and the effect of heating by hot water pipe is reduced. desirable.
또한, 상기 시공방법에서 귀양석 0.2 ~ 20 중량부가 더 포함된 마감재를 이용하여 바닥면을 형성할 수 있다. 상기 귀양석이 포함된 마감재로 바닥면을 형성할 경우에는 음이온과 원적외선의 방출량을 더욱 증대시킬 수 있으며, 동(Cu)이 혼합된 마감재를 사용하여 수맥차단기능을 겸한 바닥면의 제공이 가능하다.In addition, the floor surface may be formed by using a finishing material containing 0.2 to 20 parts by weight of the jewels in the construction method. When the bottom surface is formed of the finish containing the mutton, it is possible to further increase the emission amount of negative ions and far infrared rays, it is possible to provide a bottom surface combined with water vein blocking function by using a finish mixed with copper (Cu).
이하, 도면을 참조하여 본 발명의 사문옥석을 이용한 마감재 및 이를 이용한 건물시공방법을 상세히 설명한다.Hereinafter, with reference to the drawings will be described in detail the finishing material using a serpentine stone of the present invention and a building construction method using the same.
도 1은 본 발명의 마감재를 이용한 건물시공방법에 따른 일실시예로 주택 바닥시공상태를 도시한 단면도이고, 도 2는 본 발명의 마감재를 이용한 건물시공방법에 따른 다른 실시예로 주택 바닥시공상태를 도시한 단면도이고, 도 3은 본 발명의 마감재를 이용한 건물시공방법에 따른 일실시예로 사무실 바닥시공상태를 도시한 단면도이고, 도 4는 본 발명의 마감재를 이용한 건물시공방법에 따른 일실시예로벽시공상태를 도시한 단면도이다.1 is a cross-sectional view showing a building floor construction state in one embodiment according to the building construction method using the finishing material of the present invention, Figure 2 is a floor construction state in a house according to another embodiment according to the building construction method using the finishing material of the present invention Figure 3 is a cross-sectional view, Figure 3 is a cross-sectional view showing an office floor construction state as an embodiment according to the building construction method using the finishing material of the present invention, Figure 4 is an embodiment according to the building construction method using the finishing material of the present invention For example, it is sectional drawing which shows the wall construction state.
도 1에 도시된 바와같이 본 발명의 마감재를 이용한 건물시공방법은, 주택건물의 바닥면 시공방법에 있어서, 골조인 바닥보(10)를 형성하는 과정과; 상기 바닥보의 상층에 열을 차단하기 위한 단열재(20)를 형성하는 과정과; 상기 단열재의 상층에 온수파이프(30)를 배관하는 과정과; 시멘트 50중량부에 대해 입경이 0.1 ~ 20mm이하인 미분된 사문옥석 20 ~ 120 중량부, 모래 1 ~ 100 중량부로 구성된 마감재를 이용하여 상기 온수파이프를 내포하여 타설하되, 상기 온수파이프의 상층으로 5 ~ 20mm 두께가 더 형성되게 타설하여 마감재층(50)을 형성하는 미장과정을 포함하여 구성된다.Building construction method using the finishing material of the present invention as shown in Figure 1, in the floor construction method of the house building, the process of forming a floor beam 10 frame; Forming a heat insulator 20 for blocking heat on the upper layer of the floor beam; Piping a hot water pipe (30) on the upper layer of the heat insulating material; The hot water pipe is poured by using a finishing material composed of 20 to 120 parts by weight of finely divided serpentine stone having a particle diameter of 0.1 to 20 mm or less and 1 to 100 parts by weight of sand, based on 50 parts by weight of cement. It is configured to include a plastering process to form a finish layer 50 by pouring 20mm thickness is formed more.
상기 골조(10)는 콘크리트골조로 이루어진 보를 의미하는 것으로, 대형건물 시공시에는 철근빔을 사용한 철근콘크리트보이고, 소형건물에서는 원형철근을 사용한 철근콘크리트보를 의미하며, 전술한 바닥보와 후술되는 벽보를 통칭하는 것이다.The frame 10 refers to a beam consisting of a concrete frame, the reinforced concrete beam using a reinforcement beam when constructing a large building, the reinforced concrete beam using a circular reinforcement in a small building, the above-described floor beam and the wall beam described below Collectively.
상기 골조(10), 단열재(20) 및 온수파이프(30) 배관과정은 일반적인 주택시공에 사용되는 것이다. 통상적으로는 온수파이프(30) 부분에는 일반 콘크리트 또는 발포콘크리트를 이용한 타설이 이루어지고 이 상층에 미장작업이 행하여 지는데, 본 실시예에서는 원적외선의 방사 또는 음이온을 방출하는 사문옥석을 이용한 미장재(50)를 이용하여 온수파이프부분을 타설하고 온수파이프를 보호하기 위해 온수파이프의 상층에 일정두께를 더 형성하는 방법으로 바닥면을 형성한다.The frame 10, the heat insulating material 20 and the hot water pipe 30 piping process is to be used in general housing construction. Typically, the hot water pipe 30 is made of ordinary concrete or foamed concrete, and plastering is performed on the upper layer. In this embodiment, plastering material using serpentine stone that emits far-infrared radiation or anions. )) The bottom surface is formed by placing a hot water pipe part and forming a certain thickness on the upper layer of the hot water pipe to protect the hot water pipe.
이와같은 방법으로 형성된 바닥면은 온수파이프(30)에서 공급된 열이 사문옥석을 이용한 마감재(50)에 즉시 전달되기 때문에, 마감재에서는 전달받은 열에 의해 원적외선 및 음이온의 방사량이 증폭되어 열효율을 극대화시킬 수 있다.Since the bottom surface formed in this way is immediately transferred to the finishing material 50 using the serpentine gemstone, the heat supplied from the hot water pipe 30 is amplified by the received heat from the far infrared rays and negative ions to maximize the thermal efficiency Can be.
또한, 도 2에 도시된 바와같이 본 발명의 마감재를 이용한 건물시공방법은, 골조인 바닥보(10) 위에 단열재(20)를 설치하고, 단열재 위에 온수파이프(30)를 배관한 후 온수파이프 주변에 발포콘크리트(40)를 타설한 다음 사문옥석을 이용한 마감재(50)로 미장작업을 하여 바닥면을 형성한다.In addition, the building construction method using the finishing material of the present invention, as shown in Figure 2, after installing the heat insulating material 20 on the frame beam 10, the hot water pipe 30 on the heat insulating pipe surrounding the hot water pipe Plastering the foamed concrete (40) to the plastering work with a finishing material 50 using serpentine stone to form the bottom surface.
마감재의 재료중 시멘트를 백시멘트로 사용할 경우 상기 과정으로 제조된 바닥면에 연마작업을 추가로 행하여 외관을 미려하게 할 수 있다. 즉, 장판이 깔리지 않는 부분에 한해 연마작업을 실시하여 대리석으로 시공한 것과 같은 고급스럽운 미감을 제공할 수 있는 것이다.When cement is used as the back cement in the material of the finishing material, the bottom surface manufactured by the above process may be additionally polished to make the appearance beautiful. In other words, only the part where the flooring is not laid can be polished to provide a luxurious aesthetic like marble.
이와같은 재질 및 과정으로 시공한 바닥은 온수파이프(30)에서 발생된 열이 마감재(50)를 통해 바닥상면에 전달되는데, 이 때 마감재(50)에 전달된 열은 마감재의 성분인 사문옥석 및 귀양석을 자극하여 내재되어 있는 원적외선의 방출을 극대화시킴으로 최종적으로 방출되는 열은 증대되는 것이다. 또한, 마감재의 한 성분인 백색시멘트는 철성분이 제거되어 있기 때문에 이를 이용한 콘크리트에서 방출되는 양이온의 량이 감소되고, 다른 성분인 사문옥석 및 귀양석에서는 음이온이 대량으로 방출됨으로, 하부 바닥보(10)에서 방출되는 양이온을 상쇄시키고 소비자에게 음이온을 제공하여 건강을 도모하게 할 수 있다.The floor constructed by such a material and process is the heat generated from the hot water pipe 30 is transferred to the bottom surface through the finishing material 50, wherein the heat transferred to the finishing material 50 is serpentine stone and a component of the finishing material Ultimately, the heat released is increased by stimulating guinea pigs and maximizing the emission of intrinsic infrared rays. In addition, the white cement, which is a component of the finishing material, reduces the amount of cations released from concrete because iron is removed, and the anion is released in large quantities from the serpentine and noble stones, which are different components. The cations released from) can be offset and provide anion to the consumer to promote health.
다음으로 본 발명의 마감재를 이용한 건물시공방법은, 사무실건물에 적용하여 시공할 수 있다.Next, the building construction method using the finishing material of the present invention can be applied to the office building.
도 3에 도시된 바와같이 본 발명에 의해 제조된 사무실건물의 바닥구조는 골조인 바닥보(10) 위에 방음재(60)를 설치하고, 방음재 위에 사문옥석을 이용한 마감재(50)로 미장작업을 하여 바닥면을 형성한다. 상기 방음재는 선택적인 사항으로 시공에서 제외하여도 무방하다.As shown in FIG. 3, the floor structure of the office building manufactured by the present invention is installed on the floor beam 10, which is framed, with soundproofing material 60, and plastered with a finishing material 50 using serpentine stone on the soundproofing material. Form the bottom surface. The sound insulation material is optional and may be excluded from construction.
이러한 구조의 바닥은 상술한 연마작업을 추가로 실시할 수 있는 것으로 상술한 예에서는 부분적으로 사용하나 본 예에서는 바닥 전면에 연마작업을 실시하여 대리석으로 시공한 것과 유사한 고풍격의 건조물을 제공할 수 있다. 이와같이 마감재(50)가 사무실 바닥구성에 적용되는 것은, 건물자체에서 방출되는 양이온의 량을 감소시키고, 음이온의 방출량을 증대시킴으로 최종적으로 방출되는 이온이 균등하게 하기 위함이다.The bottom of such a structure can be additionally subjected to the above-described polishing, but in the above-described example, the floor may be partially used, but in this example, the floor may be polished to provide a high-winding structure similar to that of marble. . In this way, the finishing material 50 is applied to the office floor configuration, in order to reduce the amount of cations emitted from the building itself, and to increase the amount of negative ions released in order to equalize the finally released ions.
마지막으로 본 발명의 마감재를 이용한 건물시공방법은, 벽체 구조에 적용이 가능하다. 도 4에 도시된 바와같이 본 발명에 의해 제조된 벽 구조는, 골조인 벽보(10)에 본 발명의 마감재(50)로 미장작업한 후 벽지(70)를 도배하여 형성된다. 상기 벽보(10)와 마감재(50)층 사이에는 열을 차단하기 위한 단열재(20) 또는 음을 차단하기 위한 방음재(60)를 더 형성할 수 있다.Finally, the building construction method using the finishing material of the present invention is applicable to the wall structure. As illustrated in FIG. 4, the wall structure manufactured by the present invention is formed by plastering the wall covering 10 that is framed with the finishing material 50 of the present invention and then wallpapering the wallpaper 70. Between the wall 10 and the finisher 50 layer, a heat insulating material 20 for blocking heat or a soundproof material 60 for blocking sound may be further formed.
이러한 벽의 구조는, 골조인 벽보(10)와 벽지(70)를 부착하기 위해 사용한 접착재에서 방출되는 양이온과 유해물질을 마감재에서 방출되는 음이온에 의해 상쇄됨으로 최적의 실내환경의 제공이 가능하게 된다. 또한, 도시하지 않았지만 본 발명의 마감재를 이용하여 벽돌 등의 건축자재를 생산하여 사용할 수도 있다.Such a wall structure can provide an optimal indoor environment by canceling the cations and toxic substances released from the adhesive used to attach the frame 10 and the wallpaper 70 by the anions released from the finishing material. . In addition, although not shown, it is also possible to produce and use building materials such as brick using the finishing material of the present invention.
상기 건물시공에 사용되는 마감재를 이용하여 유해물질(환경호르몬) 함유여부를 측정하였다.Using the finishing material used in the building construction was measured whether or not containing harmful substances (environmental hormone).
시험기관 - 한국원사직물시험연구원(접수번호 : 41-41-04-07738)Testing institution-Korea Yarn Textile Testing Institute (Reception number: 41-41-04-07738)
시험대상 - 사문옥석과 백시멘트가 혼합된 마감재.Test Subject-Finished material mixed with serpentine stone and back cement.
시험방법 - 마감재 시편을 n-헥산으로 속슬렛추출기(Soxhlet's extractor) 추출한 후 GC/MSD로 분석(검출한계=1.0mg/kg) 및 편광현미경법(석면함유여부)으로 측정함.Test method-Finished specimens were extracted by Soxhlet's extractor with n-hexane and analyzed by GC / MSD (detection limit = 1.0mg / kg) and polarization microscope (with or without asbestos).
상기 시험결과 본 발명의 마감재에서는 환경호르몬으로 알려진 다수의 물질이 검출되지 않음을 알수 있고, 석면이 극미량이 검출되었지만 이는 허용한도 이내의 값으로서 근래에 대두되는 새집증후근을 유발하는 물질의 배출량을 최소한으로 감소시킬 수 있다.As a result of the test, it can be seen that a large number of substances known as environmental hormones were not detected in the finishing material of the present invention, but asbestos was detected in a small amount, which is a value within the allowable limit, and at least the amount of the substance that causes sick house syndrome is emerging. Can be reduced.
한편, 상기 서술한 예는, 본 발명을 설명하고자하는 예일 뿐이다. 따라서 본 발명이 속하는 기술분야의 통상적인 전문가가 본 상세한 설명을 참조하여 부분변경 사용한 것도 본 발명의 범위에 속하는 것은 당연한 것이다.In addition, the above-mentioned example is only an example to demonstrate this invention. Therefore, it is obvious that the ordinary skilled in the art to which the present invention pertains uses the partial change with reference to the detailed description.
이상에서 살펴본 바와 같이, 본 발명의 사문옥석을 이용한 마감재 및 이를 이용한 건물시공방법는,As described above, the finishing material using the serpentine stone of the present invention and the building construction method using the same,
건물의 바닥, 벽, 천장 등의 마감재로 양이온의 발생량이 적은 백시멘트 또는 일반시멘트와 천연광물의 혼합물인 사문옥석 및 귀양석을 혼합하여 사용함으로, 건물에서 방출되는 양이온의 량을 저하시키고, 음이온의 방출량을 증가시키며, 원적외선의 다량방출로 열효율을 향상시킬 수 있는 유용한 제품 및 시공방법의 제공이 가능하게 되었다.As a finishing material for building floors, walls, ceilings, etc., it is used by mixing serpentine and precious stones, which are mixtures of white cement or general cement and natural minerals with low cations, thereby reducing the amount of cations emitted from the building. It is possible to provide useful products and construction methods that can increase the amount of emitted and improve the thermal efficiency by the large emission of far infrared rays.
Claims (7)