JPWO2020137941A1 - Metallised film - Google Patents
Metallised film Download PDFInfo
- Publication number
- JPWO2020137941A1 JPWO2020137941A1 JP2020505517A JP2020505517A JPWO2020137941A1 JP WO2020137941 A1 JPWO2020137941 A1 JP WO2020137941A1 JP 2020505517 A JP2020505517 A JP 2020505517A JP 2020505517 A JP2020505517 A JP 2020505517A JP WO2020137941 A1 JPWO2020137941 A1 JP WO2020137941A1
- Authority
- JP
- Japan
- Prior art keywords
- intensity
- silicon compound
- compound layer
- film
- metallized film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本発明は、温度８５℃、湿度８５％ＲＨの過酷な環境に対して十分な耐湿性を発現し、フィルム搬送や後工程で加工不良を起こしにくく、耐湿性を維持することが可能な金属化フィルムを提供することを可能とする金属化フィルムに関する。本発明は、高分子基材（１）の少なくとも片面に、金属層（２）及びケイ素化合物層（３）がこの順に積層された金属化フィルムであって、前記ケイ素化合物層（３）は、ＦＴ-ＩＲ分析で得られる、波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ａと、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ａ／強度Ｂ）が、１．０以上である。INDUSTRIAL APPLICABILITY The present invention exhibits sufficient moisture resistance in a harsh environment with a temperature of 85 ° C. and a humidity of 85% RH, is less likely to cause processing defects in film transport and post-processes, and is metallized capable of maintaining moisture resistance. With respect to metallized films that make it possible to provide films. The present invention is a metallized film in which a metal layer (2) and a silicon compound layer (3) are laminated in this order on at least one surface of a polymer base material (1), wherein the silicon compound layer (3) is The intensity A of the peak having the maximum intensity in the range of 1030 cm-1 to 1130 cm-1 and the peak having the maximum intensity in the range of 1240 cm-1 to 1280 cm-1 obtained by FT-IR analysis. The strength ratio of strength B (strength A / strength B) is 1.0 or more.
Description
本発明は、極めて高い耐湿熱性に優れた金属層を有するコンデンサ用フィルムおよびそれを用いてなるコンデンサに関する。 The present invention relates to a film for a capacitor having a metal layer having extremely high moisture resistance and heat resistance, and a capacitor using the same.
近年のデジタル家電の急速な発達に伴い、機器内部の半導体基板に多数使用されるコンデンサの特性が重要視されるようになってきている。特に、薄型ディスプレイなどのデジタル機器においては、屋外や車載用途が増えつつあり、高温高湿の過酷な環境で耐圧性、保安性が求められている。 With the rapid development of digital home appliances in recent years, the characteristics of capacitors used in many semiconductor substrates inside equipment have become more important. In particular, in digital devices such as thin displays, outdoor and in-vehicle applications are increasing, and pressure resistance and safety are required in a harsh environment of high temperature and high humidity.
従来、コンデンサの耐電圧性を向上させる方法としては、フィルム上面に形成する金属薄膜を薄くして高膜抵抗とすることで、絶縁破壊時に流れる瞬時短絡電流により絶縁欠陥付近の金属薄膜を蒸発飛散させ絶縁を回復させる、いわゆる自己回復(セルフヒーリング)を機能しやすくする方法がある（特許文献１）。 Conventionally, as a method of improving the withstand voltage of a capacitor, the metal thin film formed on the upper surface of the film is thinned to have high film resistance, and the metal thin film near the insulation defect is evaporated and scattered by the instantaneous short-circuit current flowing at the time of dielectric breakdown. There is a method for facilitating the functioning of so-called self-healing (self-healing), which restores insulation.
ところで、従来技術のフィルム上面に金属薄膜を薄く形成する方法は、金属層の厚みが５ｎｍから３０ｎｍと薄いため、高温高湿の環境下では外気からの酸素や水によって、金属層が酸化あるいは水酸化して電極として機能しなくなり、容量低下、tanδの上昇を引き起こす問題がある。この問題点を改善する方法として、金属層を外気からの酸素や水から保護するために、金属層表面にアクリル樹脂を積層する技術が知られている（特許文献２）。 By the way, in the conventional method of forming a thin metal thin film on the upper surface of a film, the thickness of the metal layer is as thin as 5 nm to 30 nm, so that the metal layer is oxidized or watered by oxygen or water from the outside air in a high temperature and high humidity environment. There is a problem that it oxidizes and does not function as an electrode, causing a decrease in capacity and an increase in tan δ. As a method for improving this problem, a technique of laminating an acrylic resin on the surface of a metal layer is known in order to protect the metal layer from oxygen and water from the outside air (Patent Document 2).
また、別の改善する方法として、金属表面にＳｉ酸化物層を積層して水分から金属層を遮断する技術が知られている（特許文献３）。 Further, as another improvement method, a technique of laminating a Si oxide layer on a metal surface to block the metal layer from moisture is known (Patent Document 3).
しかしながら、特許文献２のように、アクリル樹脂を積層する方法は、例えば温度８５℃、湿度８５％ＲＨといった従来よりも過酷な高温高湿の環境下では、アクリル樹脂自体の酸素や水分の遮断性が不足し、金属層全体が酸化あるいは水酸化し、大きく容量低下する問題があった。また、特許文献３のように、金属表面にＳｉ酸化物層を積層する方法は、Ｓｉ酸化物層が硬く壊れやすい層であるため、コンデンサ素子作製時のフィルム搬送や巻き取り、プレス加工によって、Ｓｉ酸化物層にクラックや割れなどの欠点が発生し、欠点部から金属層が酸化あるいは水酸化し、容量低下する問題があった。 However, as in
本発明は、かかる従来技術の背景に鑑み、温度８５℃、湿度８５％ＲＨの過酷な環境に対して十分な耐湿性を発現し、フィルム搬送や後工程で加工不良を起こしにくく、耐湿性を維持することが可能な金属化フィルムを提供せんとするものである。 In view of the background of the prior art, the present invention exhibits sufficient moisture resistance in a harsh environment with a temperature of 85 ° C. and a humidity of 85% RH, is less likely to cause processing defects in film transport and subsequent processes, and has moisture resistance. It is intended to provide a metallized film that can be maintained.
本発明は、かかる課題を解決するために、次のような手段を採用する。すなわち、以下である。
（１） 高分子基材の少なくとも片面に、金属層及びケイ素化合物層がこの順に積層された金属化フィルムであって、
前記ケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ａと、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ａ／強度Ｂ）が、１．０以上であることを特徴とする、金属化フィルム。
（２） 高分子基材の少なくとも片面に、金属層及びケイ素化合物層がこの順に積層された金属化フィルムであって、
前記ケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｃと、１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ｃ／強度Ｂ）が、１．０以上であることを特徴とする、金属化フィルム。The present invention employs the following means in order to solve such a problem. That is, it is as follows.
(1) A metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material.
The silicon compound layer is obtained by FT-IR analysis, the intensity A of a peak having a maximum intensity that exist from the wave number 1030 cm -1 in the range of 1130 cm -1, present from the wave number 1240 cm -1 in the range of 1280 cm -1 A metallized film characterized in that the intensity ratio (intensity A / intensity B) of the intensity B of the peak having the maximum intensity is 1.0 or more.
(2) A metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material.
Maximum intensity the silicon compound layer is obtained by FT-IR analysis, present and strength C of a peak having a maximum intensity that exist from 870 cm -1 in the range of 940 cm -1, from 1240 cm -1 in the range of 1280 cm -1 A metallized film having a peak intensity B intensity ratio (intensity C / intensity B) of 1.0 or more.
本発明は、極めて高い耐湿性および耐酸化性に優れた金属化フィルムを提供することができる。 The present invention can provide a metallized film having extremely high moisture resistance and oxidation resistance.
［金属化フィルム］
本発明の金属化フィルムは、高分子基材の少なくとも片面に、金属層及びケイ素化合物層がこの順に積層された金属化フィルムであって、前記ケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ａと、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ａ／強度Ｂ）が、１．０以上であることを特徴とする、金属化フィルムである。以下、この態様の金属化フィルムを、本発明１という。[Metallised film]
The metallized film of the present invention is a metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material, and the silicon compound layer is obtained by FT-IR analysis. and intensity a of a peak having a maximum intensity that exist from the wave number 1030 cm -1 in the range of 1130 cm -1, the intensity ratio of the intensity B of a peak having a maximum intensity that exist from the wave number 1240 cm -1 in the range of 1280 cm -1 (intensity a / A metallized film having a strength B) of 1.0 or more. Hereinafter, the metallized film of this aspect is referred to as the present invention 1.
また別の態様の本発明の金属化フィルムは、高分子基材の少なくとも片面に、金属層及びケイ素化合物層がこの順に積層された金属化フィルムであって、前記ケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｃと、１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ｃ／強度Ｂ）が、１．０以上であることを特徴とする、金属化フィルムである。以下、この態様の金属化フィルムを、本発明２という。The metallized film of the present invention according to another aspect is a metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material, and the silicon compound layer is FT-IR. obtained in the analysis, and the intensity C of a peak having a maximum intensity that exist from 870 cm -1 in the range of 940 cm -1, the intensity ratio of the intensity B of a peak having a maximum intensity that exist from 1240 cm -1 in the range of 1280 cm -1 It is a metallized film characterized by having (strength C / strength B) of 1.0 or more. Hereinafter, the metallized film of this aspect is referred to as the
さらに本発明１と本発明２とを総称して、以下、本発明という。 Further, the present invention 1 and the
図１に本発明の金属化フィルムの一例の断面図と平面図を示す。本発明の金属化フィルムは、高分子基材１の片面に金属層２およびケイ素化合物層３がこの順に積層されている。図１の態様の本発明の金属化フィルムにおける金属層２の形成面には、長手方向の端部に連続した非蒸着マージン４が形成されている。一方、この態様の本発明の金属化フィルムにおける、非蒸着マージン４に対向する長手方向の端部は、金属層２が形成されている。ここで、長手方向とは高分子基材１の巻き取り方向のことであり、幅方向とは長手方向に直交する方向のことをいう。また、本明細書においては、非蒸着マージン４が施された側の端部を非蒸着マージン側端部５、金属層がある側の端部を電極側端部６と称する。 FIG. 1 shows a cross-sectional view and a plan view of an example of the metallized film of the present invention. In the metallized film of the present invention, the
本発明の金属化フィルムは、金層層の上にケイ素化合物層を積層することによって、ケイ素化合物層が金属層表面への水や酸素の付着を抑制するため、高度な耐湿性を有するものとなる。 The metallized film of the present invention has a high degree of moisture resistance because the silicon compound layer suppresses the adhesion of water and oxygen to the surface of the metal layer by laminating the silicon compound layer on the gold layer. Become.
本発明において、ＦＴ−ＩＲ分析とは、対象物に赤外線を照射し、透過また反射して得られる赤外吸収スペクトルから、分子の構造や官能基を把握することが可能な分析である。分析方法、手順の詳細は、実施例に示す通りである。 In the present invention, the FT-IR analysis is an analysis capable of grasping the structure and functional groups of a molecule from an infrared absorption spectrum obtained by irradiating an object with infrared rays and transmitting or reflecting it. Details of the analysis method and procedure are as shown in the examples.
本発明において、波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークとは、ケイ素化合物層に含まれるシロキサン結合（Ｓｉ−Ｏ−Ｓｉ結合）に帰属する吸収ピークである。さらに波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークとは、ケイ素化合物層に含まれるトリメチルシリル基（ＳｉＣＨ３）由来のＳｉ−Ｃ結合に帰属する吸収ピークである。すなわち、これら２つのピーク強度比の変化からケイ素化合物層の存在および結合状態を把握することができる。In the present invention, the peak having the maximum intensity existing in the wave number range of 1030 cm-1 to 1130 cm- 1 is an absorption peak attributed to the siloxane bond (Si—O—Si bond) contained in the silicon compound layer. Further, the peak having the maximum intensity existing in the wave number range of 1240 cm-1 to 1280 cm- 1 is an absorption peak attributed to the Si—C bond derived from the trimethylsilyl group (SiCH 3) contained in the silicon compound layer. That is, the existence and bonding state of the silicon compound layer can be grasped from the change in the ratio of these two peak intensities.
本発明１のケイ素化合物層は、ＦＴ−ＩＲ分析で得られる波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ａと、波数１２４０ｃｍ- １から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ａ／強度Ｂ）が、１．０以上である。ケイ素化合物層の強度比（強度Ａ／強度Ｂ）が１．０以上であることにより、ケイ素化合物層３にはＳｉ−Ｃ結合よりも結合エネルギーが高いＳｉ−Ｏ−Ｓｉ結合の含有比率が大きくなるため、金属層表面への水や酸素の付着を抑制でき、耐湿性を向上することができる。強度Ａ／強度Ｂが１．０未満である場合は、ケイ素化合物層全体の結合が弱くなるため、温度８５℃、湿度８５％ＲＨの過酷な環境下では層が破壊され、高度な耐湿性は得られない。また、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲にピークが存在しない場合は、有機成分であるＳｉＣＨ３を含有しないケイ素化合物層となるため、柔軟性が損なわれ、コンデンサ素子の作製中にクラックや割れなどの欠点が発生しやすく、耐湿性を悪化させる原因となる。なお、ケイ素化合物層に含まれるＳｉＣＨ３由来のＳｉ−Ｃ結合を完全に除去することは難しく、微量残留するため、強度Ａ／強度Ｂの上限は１０．０以下となる。従って、強度Ａ／強度Ｂは１．０以上であり、２．０以上が好ましく、また上限については特に限定はされないが、１０．０以下が好ましい。Silicon compound layer of the present invention 1, the intensity of the peak A having the maximum intensity that exist from the wave number 1030 cm -1 obtained by FT-IR analysis in the range of 1130 cm -1, wave number 1240 cm - 1 in the range of 1280 cm -1 The intensity ratio (intensity A / intensity B) of the intensity B of the peak having the maximum intensity existing is 1.0 or more. When the strength ratio (strength A / strength B) of the silicon compound layer is 1.0 or more, the content ratio of the Si—O—Si bond having a higher bond energy than the Si—C bond is large in the
ここで、ケイ素化合物層のＦＴ−ＩＲ分析で測定する位置に非蒸着マージンオイルを形成する際のフッ素オイルが付着している状態で、前述の強度Ａや強度Ｂ、後述する強度Ｃを測定する場合は、ケイ素化合物層と非蒸着マージン部のそれぞれについてＦＴ−ＩＲ分析で測定し、両者の差スペクトルを使用することで、前述の強度Ａや強度Ｂ、後述する強度Ｃを求めることができる。なお、ケイ素化合物層へのフッ素オイルの付着は、Ｘ線光電子分光法（ＸＰＳ）分析で判断することができる。ケイ素化合物層の表面からＸＰＳ分析を行い、得られた元素組成比において、フッ素原子が１．０％以上の場合にフッ素オイルが付着していると判断する。 Here, the above-mentioned strength A and strength B, and the strength C described later are measured in a state where the fluorine oil for forming the non-deposited margin oil is attached to the position measured by the FT-IR analysis of the silicon compound layer. In this case, each of the silicon compound layer and the non-deposited margin portion is measured by FT-IR analysis, and the difference spectrum between the two can be used to obtain the above-mentioned strength A and strength B, and the strength C described later. The adhesion of fluorine oil to the silicon compound layer can be determined by X-ray photoelectron spectroscopy (XPS) analysis. XPS analysis is performed from the surface of the silicon compound layer, and it is determined that fluorine oil is attached when the fluorine atom is 1.0% or more in the obtained element composition ratio.
本発明の金属化フィルムは、高分子基材の少なくとも片面に、金属層及びケイ素化合物層がこの順に積層された金属化フィルムである。そのため本発明の金属化フィルムは、高分子基材の片面のみまたは両面に金属層を設けることができ、ケイ素化合物層は、金属層を設けた高分子基材の片側のみまたは両側に設けても構わない。具体的な構成として、以下の（ｉ）〜（ｖ）のいずれでも構わない。
（ｉ）高分子基材／金属層／ケイ素化合物層
（ii）ケイ素化合物層／金属層／高分子基材／金属層
（iii）ケイ素化合物層／金属層／高分子基材／ケイ素化合物層
（iv）ケイ素化合物層／金属層／高分子基材／金属層／ケイ素化合物層
これらの中でも生産性の観点から（ｉ）の構成が好ましい。The metallized film of the present invention is a metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material. Therefore, the metallized film of the present invention can be provided with a metal layer on only one side or both sides of the polymer base material, and the silicon compound layer may be provided on only one side or both sides of the polymer base material provided with the metal layer. I do not care. As a specific configuration, any of the following (i) to (v) may be used.
(I) Polymer base material / metal layer / silicon compound layer (ii) Silicon compound layer / metal layer / polymer base material / metal layer (iii) Silicon compound layer / metal layer / polymer base material / silicon compound layer (ii) iv) Silicon compound layer / metal layer / polymer base material / metal layer / silicon compound layer Among these, the configuration of (i) is preferable from the viewpoint of productivity.
［高分子基材］
本発明に用いられる高分子基材は、金属層が蒸着などにより形成できるものであれば特に限定されないが、ポリエチレン、無延伸あるいは延伸ポリプロピレン、ポリメチルペンテン、シクロオレフィン系ポリマー、ノルボルネン系ポリマー、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリアミド、ポリアミドイミド、ポリフェニレンサルファイド、ポリエーテルイミド、ポリイミド、液晶ポリマーなどの単体、またはこれら２種以上の混合物並びにポリマーアロイからなる有機高分子フィルムが好ましく、コンデンサを形成した場合の耐電圧特性、誘電正接特性、絶縁抵抗特性に優れる点から、無延伸あるいは延伸のポリプロピレン系フィルムが特に好ましく用いられる。ポリプロピレン系フィルムは、ポリプロピレンのホモポリマーからなるフィルム以外に、プロピレンと他のαーオレフィン（例えばエチレン、ブテンなど）の共重合体からなるフィルムであっても、またポリプロピレンと他のα−オレフイン重合体（例えばポリエチレン、ポリブテンなど）とのブレンド品からなるフィルムであっても構わない。[Polymer substrate]
The polymer base material used in the present invention is not particularly limited as long as the metal layer can be formed by vapor deposition or the like, but is polyethylene, unstretched or stretched polypropylene, polymethylpentene, cycloolefin polymer, norbornene polymer, polyethylene. A single substance such as terephthalate, polyethylene naphthalate, polyamide, polyamideimide, polyphenylene sulfide, polyetherimide, polyimide, liquid crystal polymer, or a mixture of two or more of these, and an organic polymer film composed of a polymer alloy are preferable, and a capacitor is formed. A non-stretched or stretched polypropylene-based film is particularly preferably used because of its excellent withstand voltage characteristics, dielectric direct contact characteristics, and insulation resistance characteristics. The polypropylene-based film may be a film made of a copolymer of propylene and other α-olefins (for example, ethylene, butene, etc.) in addition to a film made of a polypropylene homopolymer, or a film made of polypropylene and another α-olephine polymer. It may be a film made of a blended product (for example, polyethylene, polybutene, etc.).
高分子基材には本発明の目的とする特性に支障を及ぼさない範囲で公知の添加剤として、滑剤や可塑剤などが含まれてもよい。また、高分子基材の表面はコロナ放電処理、火炎処理、プラズマ処理などの表面処理、或いは、接着剤のコーティング層、樹脂コーティング層、溶融押し出しによる樹脂層が積層されていても構わない。なお、高分子基材の表面に形成される接着剤のコーティング層、樹脂コーティング層、溶融押し出しによる樹脂層は、高分子基材に含まれる（高分子基材の一部である）。 The polymer substrate may contain a lubricant, a plasticizer, or the like as known additives as long as they do not interfere with the properties intended for the present invention. Further, the surface of the polymer base material may be surface-treated such as corona discharge treatment, flame treatment, plasma treatment, or may be laminated with an adhesive coating layer, a resin coating layer, and a resin layer by melt extrusion. The adhesive coating layer formed on the surface of the polymer base material, the resin coating layer, and the resin layer formed by melt extrusion are included in the polymer base material (a part of the polymer base material).
本発明で使用する高分子基材の厚みは、特に制限はなく、コンデンサを使用する用途に応じて適宜決定できるが、コンデンサの小型化、高容量化の観点から、０．１μｍ以上１０μｍ以下が良く、好ましくは１μｍ以上７μｍ以下である。 The thickness of the polymer base material used in the present invention is not particularly limited and can be appropriately determined depending on the application in which the capacitor is used. However, from the viewpoint of miniaturization and high capacity of the capacitor, the thickness is 0.1 μm or more and 10 μm or less. It is good, preferably 1 μm or more and 7 μm or less.
［金属層］
本発明の金属化フィルムに用いる事のできる金属層の材質としては、特に限定されないが、Ａｌ、Ｚｎ、Ｓｎ、Ｎｉ、Ｃｒ、Ｆｅ、Ｃｕ、Ｍｇ、Ｔｉ、Ｓｉ、及びこれら金属の合金からなる群より選ばれる少なくとも１つを含むものを用いることが好ましい。これらの中でも、均一で安定した導電性金属の蒸着膜を得る観点から、Ｚｎ単体、またはＺｎとＡｌの積層品、またはＺｎとＡｌの合金、Ａｌ単体を用いることが好ましい。[Metal layer]
The material of the metal layer that can be used for the metallized film of the present invention is not particularly limited, but is composed of Al, Zn, Sn, Ni, Cr, Fe, Cu, Mg, Ti, Si, and alloys of these metals. It is preferable to use one containing at least one selected from the group. Among these, from the viewpoint of obtaining a uniform and stable vapor-filmed film of a conductive metal, it is preferable to use a simple substance of Zn, a laminated product of Zn and Al, an alloy of Zn and Al, or a simple substance of Al.
金属層の厚みは電気特性、機械特性の観点から、１ｎｍ以上、５０ｎｍ以下が好ましい。導電性が十分に確保できる観点から金属層の厚みは１ｎｍ以上、５０ｎｍ以下が好ましく、さらには絶縁破壊時の自己回復性５ｎｍ以上３０ｎｍ以下がより好ましい。金属層の厚みは、通常は透過型電子顕微鏡（ＴＥＭ）による断面観察により測定することが可能である。 The thickness of the metal layer is preferably 1 nm or more and 50 nm or less from the viewpoint of electrical characteristics and mechanical characteristics. From the viewpoint of ensuring sufficient conductivity, the thickness of the metal layer is preferably 1 nm or more and 50 nm or less, and more preferably 5 nm or more and 30 nm or less for self-healing at the time of dielectric breakdown. The thickness of the metal layer can usually be measured by cross-sectional observation with a transmission electron microscope (TEM).
金属層の形成方法は、真空蒸着法やスパッタリング法、イオンプレーティング法等があるが、形成速度が速く、経済的に有利である観点から真空蒸着法が好ましい。真空蒸着法は、真空中で冷却ロールに密着した高分子基材に蒸着源から金属を蒸着させ、高分子基材表面に金属層を形成する方法である。この蒸着源には、抵抗加熱式のボート式や輻射あるいは高周波加熱によるルツボ形式や、電子ビーム加熱による方式などがあるが、特に限定されず、適宜選択すればよい。 As a method for forming the metal layer, there are a vacuum vapor deposition method, a sputtering method, an ion plating method and the like, but the vacuum vapor deposition method is preferable from the viewpoint of high formation speed and economical advantage. The vacuum vapor deposition method is a method in which a metal is vapor-deposited from a vapor deposition source on a polymer substrate that is in close contact with a cooling roll in a vacuum to form a metal layer on the surface of the polymer substrate. The vapor deposition source includes a resistance heating type boat type, a radiant or high frequency heating type, and an electron beam heating type, but the method is not particularly limited and may be appropriately selected.
［ケイ素化合物層］
次に、ケイ素化合物層について詳細を説明する。本発明におけるケイ素化合物層は、ケイ素化合物を含む層であり、ケイ素化合物を含みさえすれば、その層が他に何を含んでいてもかまわない。ケイ素化合物層中のケイ素化合物としては、ケイ素酸化物、ケイ素窒化物、ケイ素炭化物、ケイ素酸窒化物または、それらの混合物などをあげることができる。特に、ケイ素化合物層が、酸化ケイ素、炭化ケイ素、窒化ケイ素、及び酸窒化ケイ素からなる群より選択される少なくとも１つのケイ素化合物を含むことが好ましい。なお、ケイ素酸化物層に含まれる成分はケイ素（Ｓｉ）に限定されず、例えば、アルミニウム（Ａｌ）、チタン（Ｔｉ）、ジルコニウム(Ｚｒ）、スズ（Ｓｎ）、インジウム（Ｉｎ）、ニオブ（Ｎｂ）、モリブデン（Ｍｏ）、タンタル（Ｔａ）、パラジウム（Ｐｄ）等から形成された金属や金属酸化物を含んでも構わない。[Silicon compound layer]
Next, the silicon compound layer will be described in detail. The silicon compound layer in the present invention is a layer containing a silicon compound, and the layer may contain anything else as long as it contains a silicon compound. Examples of the silicon compound in the silicon compound layer include silicon oxide, silicon nitride, silicon carbide, silicon acid nitride, or a mixture thereof. In particular, it is preferable that the silicon compound layer contains at least one silicon compound selected from the group consisting of silicon oxide, silicon carbide, silicon nitride, and silicon oxynitride. The component contained in the silicon oxide layer is not limited to silicon (Si), and for example, aluminum (Al), titanium (Ti), zirconium (Zr), tin (Sn), indium (In), and niobium (Nb). ), Molybdenum (Mo), tantalum (Ta), palladium (Pd) and the like, and may contain a metal or a metal oxide.
本発明において、金属層の上にケイ素化合物層が形成されているかどうかは、以下の蛍光Ｘ線分析（ＸＲＦ分析）によるケイ素（Ｓｉ）原子の検出量から確認することができる。 In the present invention, whether or not the silicon compound layer is formed on the metal layer can be confirmed from the amount of silicon (Si) atoms detected by the following fluorescent X-ray analysis (XRF analysis).
本発明のケイ素化合物層は、金属層の耐湿性を向上させる観点から、ＸＲＦ分析で測定されるケイ素（Ｓｉ）原子の検出量が０．００５μｇ／ｃｍ２〜０．２μｇ／ｃｍ２であることが好ましく、さらにはケイ素（Ｓｉ）原子の検出量が０．０１μｇ／ｃｍ２〜０．１μｇ／ｃｍ２であることが好ましい。From the viewpoint of improving the moisture resistance of the metal layer, the silicon compound layer of the present invention has a detection amount of silicon (Si) atoms measured by XRF analysis of 0.005 μg / cm 2 to 0.2 μg / cm 2. it is preferred, and it is preferable that the detected amount of silicon (Si) atom is 0.01μg / cm 2 ~0.1μg / cm 2 .
また、本発明１のケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、波数８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｃと、強度Ｂの強度比（強度Ｃ／強度Ｂ）が、１．０以上であることが好ましい。さらに本発明２のケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、波数８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｃと、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ｃ／強度Ｂ）が、１．０以上である。ここで、波数８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークとは、金属層にアルミニウムが含有する場合において、金属層の表面に形成されるＡｌ−Ｏ結合に帰属する吸収ピークである。Further, the silicon compound layer of the present invention 1 is obtained by FT-IR analysis, and the intensity C of a peak having a maximum intensity that exist from the wave number 870 cm -1 in the range of 940 cm -1, the intensity ratio of the intensity B (intensity C / Strength B) is preferably 1.0 or more. Furthermore silicon compound layer of the
本発明品のケイ素化合物層は、強度Ｃと、強度Ｂの強度比（強度Ｃ／強度Ｂ）が、１．０以上であることにより、ケイ素化合物層に含まれるＳｉ−Ｃ結合よりも金属層の表面に形成されるＡｌ−Ｏ結合の存在比率が大きくなる。詳細は定かでは無いが、ケイ素化合物層を形成時のプラズマや熱によって、上述したＳｉ−Ｃ結合が減少し、Ｓｉ−Ｏ−Ｓｉ結合が増加する一方で、Ｓｉ−Ｏ−Ｓｉ結合の一部が切断され、金属層の表面に存在するＡｌ原子とＯ原子が結合し、Ａｌ−Ｏ結合やＡｌ−Ｏ−Ｓｉ結合を形成するため、金属層とケイ素化合物層との界面により強固な結合が形成されていると考えている。すなわち、金属層の表面にはＡｌ−Ｏ結合により不動態となる酸化アルミニウムの形成やＡｌ−Ｏ−Ｓｉ結合によるシリケートが形成され、金属層の表面が化学的に安定化するため、温度８５℃、湿度８５％ＲＨの過酷な環境に対しても酸化や水酸化の反応が起こりにくく、耐湿性を維持することが可能な金属化フィルムになると推測している。なお、ケイ素化合物層に含まれるＳｉＣＨ３由来のＳｉ−Ｃ結合を完全に除去することは難しく、微量残留するため、強度Ｃ／強度Ｂは１０．０以下となる。従って、強度Ｃ／強度Ｂは１．０以上であり、また上限については特に限定されないが、１０．０以下が好ましい。The silicon compound layer of the present invention is a metal layer rather than the Si—C bond contained in the silicon compound layer because the strength ratio (strength C / strength B) between the strength C and the strength B is 1.0 or more. The abundance ratio of Al—O bonds formed on the surface of the silicon increases. Although the details are not clear, the above-mentioned Si—C bond decreases and the Si—O—Si bond increases due to the plasma and heat during the formation of the silicon compound layer, while a part of the Si—O—Si bond. Is cleaved, and Al atoms and O atoms existing on the surface of the metal layer are bonded to form an Al—O bond or an Al—O—Si bond, so that a stronger bond is formed at the interface between the metal layer and the silicon compound layer. I think it has been formed. That is, the surface of the metal layer is formed of aluminum oxide that is passivated by the Al—O bond and silicate is formed by the Al—O—Si bond, and the surface of the metal layer is chemically stabilized. Therefore, the temperature is 85 ° C. It is presumed that it will be a metallized film that is less likely to undergo oxidation and hydroxylation reactions even in a harsh environment with a humidity of 85% RH and can maintain moisture resistance. Incidentally, the complete removal of Si-C bond derived from SiCH 3 contained in the silicon compound layer is difficult, because the trace amount of residual strength C / intensity B is 10.0 or less. Therefore, the strength C / strength B is 1.0 or more, and the upper limit is not particularly limited, but 10.0 or less is preferable.
本発明の金属化フィルムの製造方法について、以下に詳細を説明する。 The method for producing the metallized film of the present invention will be described in detail below.
本発明の金属化フィルムの製造方法は特に限定されないが、例えば、高分子基材上に長手方向に連続した非蒸着マージンを形成する工程と、金属層を設ける工程と、シリコーン組成物を加熱、蒸発させ、金属層上に塗布後、プラズマ放電処理をして強固なケイ素化合物層を形成する工程を経て作製される。これらの工程を一回のフィルム搬送で全て実施する方法として真空蒸着機を使用することが好ましい。 The method for producing the metallized film of the present invention is not particularly limited, and for example, a step of forming a continuous non-deposited margin in the longitudinal direction on a polymer base material, a step of providing a metal layer, and heating of a silicone composition are performed. It is produced by evaporating it, applying it on a metal layer, and then performing a plasma discharge treatment to form a strong silicon compound layer. It is preferable to use a vacuum vapor deposition machine as a method for carrying out all of these steps in one film transfer.
高分子基材上に長手方向に連続した非蒸着マージンを形成する工程は、シリコーン系オイル、フッ素系オイル、流動パラフィンなどのオイルを用いる方法がある。この他の方法として、テープ、レーザーを用いる方法があるが、いずれの方法でも所定の幅で非蒸着部分が長手方向連続的に形成されれば良く、特に方法に限定されない。これらの中でも高速かつ簡便に非蒸着マージンを形成する方法として、フッ素オイルを用いる方法が好ましい。オイル蒸発機の中にフッ素オイルを入れて、加熱、蒸発させ、オイル蒸発器上部に設けられたスリットを通して、フィルム基材に長手方向の非蒸着マージンを形成することができる。 As a step of forming a continuous non-deposited margin in the longitudinal direction on the polymer base material, there is a method of using an oil such as a silicone-based oil, a fluorine-based oil, or liquid paraffin. As another method, there is a method using a tape or a laser, but in any of the methods, the non-deposited portion may be continuously formed in the longitudinal direction with a predetermined width, and the method is not particularly limited. Among these, a method using fluorine oil is preferable as a method for forming a non-deposited margin quickly and easily. Fluorine oil can be placed in an oil evaporator, heated and evaporated, and a longitudinal non-deposited margin can be formed on the film substrate through a slit provided in the upper part of the oil evaporator.
金属層を設ける工程は、例えば、亜鉛とアルミニウムの合金膜を形成する場合、高分子基材を真空蒸着機内の巻出軸から巻出して高分子基材を冷却ドラム上で冷却しながら、亜鉛とアルミニウムがそれぞれ入った蒸着源から誘導加熱法もしくは抵抗加熱法、電子ビーム法などにより加熱・溶融させ、両金属を同時に蒸着することで形成できる。それぞれの蒸着源の温度を調整することで形成される金属層の組成を制御することができる。また、厚みはフィルム搬送速度により所望の厚みになるよう調整できる。 In the step of providing the metal layer, for example, when forming an alloy film of zinc and aluminum, zinc is wound while the polymer base material is unwound from the unwinding shaft in the vacuum vapor deposition machine and the polymer base material is cooled on a cooling drum. It can be formed by heating and melting from a vapor deposition source containing aluminum and aluminum by an induction heating method, a resistance heating method, an electron beam method, etc., and vapor deposition of both metals at the same time. The composition of the metal layer formed by adjusting the temperature of each vapor deposition source can be controlled. Further, the thickness can be adjusted to a desired thickness depending on the film transport speed.
ケイ素化合物層を形成する工程は、シリコーン組成物を含む塗料を乾燥後の厚みが所望の厚みになるように溶媒で固形分濃度を調整しリバースコート法、グラビアコート法、ロッドコート法、バーコート法、ダイコート法、スプレーコート法、スピンコート法などにより塗布し、加熱、蒸発させる方法や真空中において点状もしくは細いスリット状のノズルから加熱したシリコーン組成物を噴霧し、プラズマ放電処理をして形成する方法などがある。真空蒸着機で金属層を形成する場合、同じ蒸着機内でケイ素化合物層を形成でき、生産性や均一性に優れる観点から、後者方法である点状もしくは細いスリット状のノズルから加熱したシリコーン組成物を噴霧し、プラズマ放電処理をして強固なケイ素化合物層を形成する方法が好ましい。 In the step of forming the silicon compound layer, the solid content concentration is adjusted with a solvent so that the thickness of the paint containing the silicone composition after drying becomes a desired thickness, and the reverse coating method, gravure coating method, rod coating method, and bar coating are performed. A method of applying by a method, a die coating method, a spray coating method, a spin coating method, etc., heating and evaporating, or spraying a silicone composition heated from a punctate or fine slit-shaped nozzle in a vacuum and performing a plasma discharge treatment. There is a method of forming. When forming a metal layer with a vacuum vapor deposition machine, a silicon compound layer can be formed in the same vapor deposition machine, and from the viewpoint of excellent productivity and uniformity, the latter method is a silicone composition heated from a punctate or fine slit-shaped nozzle. Is preferable, and a method of spraying the silicon compound layer by plasma discharge treatment to form a strong silicon compound layer is preferable.
本発明のシリコーン組成物とは、シリコーンを７０重量％以上、好ましくは８５重量％以上含む樹脂組成物のことを言う。本発明に用いられるシリコーン組成物は、金属層上に噴霧されたシリコーン組成物をプラズマ放電処理でＳｉ−Ｃ結合を切断し、Ｓｉ−Ｏ−Ｓｉ結合の形成を促進させる観点から、主鎖にシロキサン結合（Ｓｉ−Ｏ−Ｓｉ）、側鎖にメチル基を有するジメチルポリシロキサンまたは側鎖にフェニル基を有するメチルフェニルシリコーンが好ましく、耐湿性の観点からフェニルメチルジメチルポリシロキサンがより好ましい。また、プラズマ放電処理でＳｉ−Ｏ−Ｓｉ結合の形成が促進するようにメチル基の一部を有機官能基に置き換えた有機変性シリコーンが好ましい。有機変性シリコーンには、側鎖の一部を有機官能基にした側鎖型や主鎖の両末端を有機官能基にした両末端型、側鎖と末端を有機官能基にした両末端側鎖型があるが、プラズマ放電処理による均一性の観点から両末端型が好ましい。シリコーン組成物としては、例えば、アミノ変性シリコーンやアルキル変性シリコーン、シラノール変性シリコーン、フェニル変性シリコーン、ポリエーテル変性シリコーンなどが好ましく、中でもシラノール変性シリコーンは、側鎖のＯＨ基がプラズマ放電処理で脱水縮合し、Ｓｉ−Ｏ−Ｓｉ結合の形成を促進させるためより好ましい。 The silicone composition of the present invention refers to a resin composition containing 70% by weight or more, preferably 85% by weight or more of silicone. The silicone composition used in the present invention has a main chain from the viewpoint of cleaving the Si—C bond by plasma discharge treatment of the silicone composition sprayed on the metal layer and promoting the formation of the Si—O—Si bond. A siloxane bond (Si—O—Si), dimethylpolysiloxane having a methyl group in the side chain, or methylphenylsilicone having a phenyl group in the side chain is preferable, and phenylmethyldimethylpolysiloxane is more preferable from the viewpoint of moisture resistance. Further, an organically modified silicone in which a part of the methyl group is replaced with an organic functional group is preferable so that the formation of the Si—O—Si bond is promoted by the plasma discharge treatment. Organically modified silicones include side chain type with a part of the side chain as an organic functional group, both end type with both ends of the main chain as organic functional groups, and both end side chains with side chains and ends as organic functional groups. There is a type, but the double-ended type is preferable from the viewpoint of uniformity due to plasma discharge treatment. As the silicone composition, for example, amino-modified silicone, alkyl-modified silicone, silanol-modified silicone, phenyl-modified silicone, polyether-modified silicone and the like are preferable. Among them, silanol-modified silicone has the OH group of the side chain dehydrated and condensed by plasma discharge treatment. It is more preferable because it promotes the formation of Si—O—Si bond.
金属層表面に噴霧されたシリコーン組成物をプラズマ放電処理する際に用いられるガス種は特に限定されないが、例えば、Ｏ２、Ａｒ、ＣＯ、ＣＯ２、Ｈ２などが挙げられる。特に好ましくはＯ２やＡｒ、あるいはこれらの１種以上を含む混合ガスである。プラズマ放電処理の電力密度は、１０Ｗ・ｍｉｎ／ｍ２以上にすることが好ましく、Ｓｉ−Ｏ−Ｓｉ結合の形成を促進させる観点から、３５Ｗ・ｍｉｎ／ｍ２以上がより好ましい。プラズマ放電電極には、異常放電が無く、安定放電が可能なターゲット材料として、ＣｕまたはＡｌ、あるいはステンレスを使用することが好ましい。The gas type used for plasma discharge treatment of the silicone composition sprayed on the surface of the metal layer is not particularly limited, and examples thereof include O 2 , Ar, CO, CO 2 , and H 2 . Particularly preferred is O 2 or Ar, or a mixed gas containing one or more of these. The power density of the plasma discharge treatment is preferably 10 W · min / m 2 or more, and more preferably 35 W · min / m 2 or more from the viewpoint of promoting the formation of Si—O—Si bonds. For the plasma discharge electrode, it is preferable to use Cu, Al, or stainless steel as a target material capable of stable discharge without abnormal discharge.
また、金属層表面に噴霧されたシリコーン組成物のプラズマ放電処理において、上述以外に効率良くＳｉ−Ｃ結合を切断し、Ｓｉ−Ｏ−Ｓｉ結合の形成を促進させる方法としては、高分子基材の両面から同時にプラズマ放電処理する方法や高分子基材の金属層を形成しない面側から４０℃以上のヒーターで加熱処理しながらシリコーン組成物をプラズマ放電処理する方法などがある。また、金属層表面にＡｌ−Ｏ結合やＡｌ−Ｏ−Ｓｉ結合を形成する方法としては、シリコーン組成物を噴霧する前の金属層表面をプラズマ放電処理する方法がある。この場合、プラズマ放電電極に使用するターゲット材料として、ＣｕまたはＡｌ、あるいはステンレスを使用することが好ましく、Ａｌ−Ｏ結合を促進させる観点からＡｌがより好ましい。 In addition to the above, in the plasma discharge treatment of the silicone composition sprayed on the surface of the metal layer, as a method of efficiently breaking the Si—C bond and promoting the formation of the Si—O—Si bond, a polymer base material is used. There are a method of performing plasma discharge treatment at the same time from both sides of the above, and a method of plasma discharge treatment of the silicone composition while heat-treating with a heater of 40 ° C. or higher from the surface side where the metal layer of the polymer base material is not formed. Further, as a method of forming an Al—O bond or an Al—O—Si bond on the surface of the metal layer, there is a method of plasma discharge treating the surface of the metal layer before spraying the silicone composition. In this case, Cu or Al or stainless steel is preferably used as the target material used for the plasma discharge electrode, and Al is more preferable from the viewpoint of promoting Al—O bond.
本発明の金属化フィルム中のケイ素化合物層は、その表面の水接触角が７０°以上９５°以下であることが好ましい。シリコーン組成物がプラズマ放電で十分に処理され、Ｓｉ−Ｏ−Ｓｉ結合を促進することにより、ケイ素化合物層の表面の水接触角を７０°以上、９５°以下とすることが可能である。ケイ素化合物層の表面の水接触角が９５°より大きい場合、プラズマ放電処理が不十分であるため、水や酸素がケイ素化合物層を透過しやすく、金属層が酸化や水酸化し、十分な耐湿性は得られない。ケイ素化合物層の表面の水接触角が７０°未満になると、ケイ素化合物層の表面に水や酸素が吸着しやすくなり、結果的に耐湿性は悪化する。すなわち、ケイ素化合物層の表面の水接触角は７０°以上、９５°以下が好ましく、処理の均一性が良い範囲として、水接触角は８５°以上、９５°以下がより好ましい。 The surface of the silicon compound layer in the metallized film of the present invention preferably has a water contact angle of 70 ° or more and 95 ° or less. The silicone composition is sufficiently treated by plasma discharge to promote the Si—O—Si bond, so that the water contact angle on the surface of the silicon compound layer can be 70 ° or more and 95 ° or less. When the water contact angle of the surface of the silicon compound layer is larger than 95 °, the plasma discharge treatment is insufficient, so that water and oxygen easily permeate the silicon compound layer, the metal layer is oxidized and hydroxylated, and sufficient moisture resistance is obtained. No sex can be obtained. When the water contact angle on the surface of the silicon compound layer is less than 70 °, water and oxygen are easily adsorbed on the surface of the silicon compound layer, and as a result, the moisture resistance is deteriorated. That is, the water contact angle on the surface of the silicon compound layer is preferably 70 ° or more and 95 ° or less, and the water contact angle is more preferably 85 ° or more and 95 ° or less as a range in which the treatment uniformity is good.
このようにして得られた金属化フィルムはコンデンサ用フィルムとして好ましく用いることが出来、公知の方法で積層もしくは巻回してコンデンサを得ることができる。 The metallized film thus obtained can be preferably used as a film for a capacitor, and a capacitor can be obtained by laminating or winding by a known method.
例えば、巻回型フィルムコンデンサの場合を例示する。幅方向に金属層と非蒸着マージンを有する金属化フィルムのロールにおいて、各金属層の中央部と各非蒸着マージンの中央部をスリットし、左側もしくは右側に非蒸着マージンを有する巻取リールを作製する。次に、左側に非蒸着マージンを有するリールと、右側に非蒸着マージンを有するリールを使用し、金属層端部を非蒸着マージンより外側にずらして重ね合わせ、巻回する。こうして得られた巻回体をプレスし、両端面にメタリコンを溶射して外部電極とし、メタリコンにリード線を溶接して巻回型コンデンサ素子を得ることができる。さらに外装ケース入りのコンデンサ素子の場合は、コンデンサ素子をエポキシ樹脂などの耐熱性、難燃性を有する樹脂製外装ケースに入れ、２液性注型エポキシ樹脂を充填、加熱、硬化して作製することができる。 For example, the case of a wound film capacitor will be illustrated. In a roll of a metallized film having a metal layer and a non-deposited margin in the width direction, the central part of each metal layer and the central part of each non-deposited margin are slit to produce a take-up reel having a non-deposited margin on the left side or the right side. do. Next, a reel having a non-deposited margin on the left side and a reel having a non-deposited margin on the right side are used, and the end of the metal layer is shifted outward from the non-deposited margin, overlapped, and wound. The wound body thus obtained is pressed, and metallicon is sprayed on both end faces to form an external electrode, and a lead wire is welded to the metallicon to obtain a wound capacitor element. Furthermore, in the case of a capacitor element in an outer case, the capacitor element is placed in a heat-resistant and flame-retardant resin outer case such as epoxy resin, filled with a two-component cast epoxy resin, heated, and cured. be able to.
本発明の金属化フィルムを用いて構成されるコンデンサは、外装コンデンサ、無外装コンデンサ、あるいは無含浸（乾式）コンデンサ、として使用され、例えば、一般家電や自動車や電車の電装用及びエンジン、モーター制御用コンデンサなどに用いられ、過酷環境に使用されるコンデンサにも適用される。 The capacitor constructed by using the metallized film of the present invention is used as an exterior capacitor, a non-exterior capacitor, or a non-impregnated (dry) capacitor, for example, for general household appliances, electric components of automobiles and trains, and engine and motor control. It is used for capacitors for harsh environments, and is also applied to capacitors used in harsh environments.
以下、本発明を実施例に基づき具体的に説明する。ただし、本発明は下記実施例に限定されるものではない。 Hereinafter, the present invention will be specifically described based on examples. However, the present invention is not limited to the following examples.
［評価方法］
次に、本発明に用いる測定法及び評価法について説明する。[Evaluation method]
Next, the measurement method and the evaluation method used in the present invention will be described.
（１）膜抵抗の測定方法
ヘビーエッジ部（非蒸着マージンに対向する長手方向の端部側の金属層が厚い部分のことを、ヘビーエッジ部という）の膜抵抗を測定する場合は、非蒸着マージンに対向する長手方向の金属層端部から幅方向に３ｍｍ、長手方向に２５０ｍｍを切り出し、測定サンプルとした。ヘビーエッジ部以外の膜抵抗を測定する場合は、長手方向の非蒸着マージンと金属膜の界面から幅方向に５ｍｍ、長手方向に２５０ｍｍを切り出し、測定サンプルとした。(1) Method for measuring film resistance When measuring the film resistance of a heavy edge portion (a portion where the metal layer on the end side in the longitudinal direction facing the non-deposited margin is called a heavy edge portion), non-deposited film resistance is measured. 3 mm in the width direction and 250 mm in the longitudinal direction were cut out from the end of the metal layer in the longitudinal direction facing the margin to prepare a measurement sample. When measuring the film resistance other than the heavy edge portion, 5 mm in the width direction and 250 mm in the longitudinal direction were cut out from the interface between the non-deposited margin in the longitudinal direction and the metal film and used as a measurement sample.
４端子法により、１００ｍｍの電極間の金属膜抵抗を測定し、測定値に（測定幅／電極間距離）を掛けて、幅１０ｍｍ、電極間距離１０ｍｍ当たりの膜抵抗を算出した。単位はΩ／□と表示する。 The metal film resistance between electrodes of 100 mm was measured by the 4-terminal method, and the measured value was multiplied by (measurement width / distance between electrodes) to calculate the film resistance per width of 10 mm and distance between electrodes of 10 mm. The unit is displayed as Ω / □.
（２）金属層のＺｎ量、Ａｌ量およびケイ素化合物層のＳｉ量
理学電気工業（株）製の自動蛍光Ｘ線分析装置（ＲＩＸ３０００）を用いて試料板の上にフィルムをのせ、１０ｍｍφの測定面積でＺｎ、Ａｌ、Ｓｉ元素のそれぞれの含有量を測定した。(2) Zn amount and Al amount of metal layer and Si amount of silicon compound layer Place a film on a sample plate using an automatic fluorescent X-ray analyzer (RIX3000) manufactured by Rigaku Denki Kogyo Co., Ltd. and measure 10 mmφ. The contents of Zn, Al, and Si elements were measured by area.
（３）水接触角測定
温度２３℃、相対湿度６５％の条件下で、接触角計ＣＡ−Ｄ型（協和界面科学（株）製）にて、金属層またはケイ素化合物層上での水の接触角を測定した。測定には、５個の平均値を用いた。(3) Water contact angle measurement Water on a metal layer or silicon compound layer with a contact angle meter CA-D type (manufactured by Kyowa Interface Science Co., Ltd.) under the conditions of a temperature of 23 ° C and a relative humidity of 65%. The contact angle was measured. The average value of 5 pieces was used for the measurement.
（４）ＦＴ−ＩＲ測定
ケイ素化合物層のＦＴ−ＩＲ測定は、ＡＴＲ（Ａｔｔｅｎｕａｔｅｄ Ｔｏｔａｌ Ｒｅｆｒｅｃｔｉｏｎ）法を用いた。(4) FT-IR measurement For the FT-IR measurement of the silicon compound layer, an ATR (Attached Total Reflection) method was used.
まずサンプルが無い状態で圧力０．１ＭＰａ以下まで測定セル内をポンプで排気し、以下の測定条件でベースライン測定を行った。次に、各水準サンプルのケイ素化合物層をＡＴＲ結晶に圧着し、圧力０．１ＭＰａ以下まで測定セル内をポンプで排気後、以下の測定条件で吸収スペクトルを測定した。各水準サンプルについて、ｎ＝２回ずつ測定を実施した。 First, in the absence of a sample, the inside of the measurement cell was exhausted with a pump to a pressure of 0.1 MPa or less, and baseline measurement was performed under the following measurement conditions. Next, the silicon compound layer of each level sample was pressure-bonded to the ATR crystal, the inside of the measurement cell was exhausted with a pump to a pressure of 0.1 MPa or less, and then the absorption spectrum was measured under the following measurement conditions. For each level sample, n = 2 measurements were performed.
得られた吸収スペクトルから、解析ソフトを使用して、波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ａと、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂ、波数８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｃをそれぞれ得た。各水準サンプルの強度Ａ／強度Ｂおよび強度Ｃ／強度Ｂの強度比の平均値を表１に示す。From the obtained absorption spectrum, using the analysis software, and the intensity of peak A having the maximum intensity that exist from the wave number 1030 cm -1 in the range of 1130 cm -1, present from the wave number 1240 cm -1 in the range of 1280 cm -1 The intensity B of the peak having the maximum intensity and the intensity C of the peak having the maximum intensity existing in the range of wave number 870 cm -1 to 940 cm -1 were obtained, respectively. Table 1 shows the average value of the intensity ratios of intensity A / intensity B and intensity C / intensity B of each level sample.
測定条件
・装置 ：ＦＴ／ＩＲ−６１００（日本分光株式会社製）
・光源 ：高輝度セラミック
・検知器 ：ＴＧＳ
・パージ ：窒素ガス
・分解能 ：４ｃｍ−１
・積算回数：３２回
・測定方法：減衰全反射（Ａｔｔｅｎｕａｔｅｄ Ｔｏｔａｌ Ｒｅｆｒｅｃｔｉｏｎ，ＡＴＲ）法
・測定波長：４，０００ｃｍ−１〜６００ｃｍ−１
・付属装置：ＡＴＲ ＰＲＯ４５０−Ｓ
・ＡＴＲ結晶：Ｇｅプリズム
・入射角度 ：４５度
・解析ソフト：Ｓｐｅｃｔｒａ Ｍａｎａｇｅｒ Ｖｅｒｓｉｏｎ２（日本分光（株）製）。Measurement conditions / equipment: FT / IR-6100 (manufactured by JASCO Corporation)
・ Light source: High-brightness ceramic ・ Detector: TGS
・ Purge: Nitrogen gas ・ Resolution: 4 cm -1
・ Number of integrations: 32 times ・ Measurement method: Attenuated total reflection (ATR) method ・ Measurement wavelength: 4,000 cm -1 to 600 cm -1
・ Attached device: ATR PRO450-S
-ATR crystal: Ge prism-incident angle: 45 degrees-Analysis software: Spectra Manager Version 2 (manufactured by JASCO Corporation).
（５）耐湿性評価
各水準の蒸着フィルムから作製されたコンデンサ素子各１０個を、温度８５℃、相対湿度８５%の雰囲気下で、電圧３１０ＶＡＣとなるように交流電圧を印加し、１０００時間経過後の静電容量変化率ΔＣ／Ｃ×１００（％）を測定した。(5) Moisture resistance evaluation An AC voltage was applied to each of 10 capacitor elements made from thin-film vapor deposition films of each level in an atmosphere with a temperature of 85 ° C and a relative humidity of 85% so that the voltage was 310 VAC, and 1000 hours passed. Later, the rate of change in capacitance ΔC / C × 100 (%) was measured.
ここで、Ｃ（μＦ）は耐湿性試験前の静電容量、ΔＣ（μＦ）は耐湿性試験後の静電容量変化量（＝耐湿性試験後の静電容量（μＦ）−耐湿性試験前の静電容量（μＦ））であり、静電容量変化率ΔＣ／Ｃ×１００は増加方向を＋、減少方向を−で表した。１０個の素子の測定値の平均を算出し、静電容量変化率が−１０〜＋１０％のものを良好と判断した。 Here, C (μF) is the capacitance before the moisture resistance test, and ΔC (μF) is the amount of change in the capacitance after the moisture resistance test (= capacitance after the moisture resistance test (μF) -before the moisture resistance test. Capacitance (μF)), and the capacitance change rate ΔC / C × 100 is represented by + in the increasing direction and − in the decreasing direction. The average of the measured values of the 10 elements was calculated, and the one having a capacitance change rate of -10 to + 10% was judged to be good.
（６）静電容量測定方法
（５）耐湿性評価におけるコンデンサ素子の静電容量は、安藤電気株式会社製ＴＹＰＥ
ＡＧ−４３１１ ＬＣＲＭＥＴＥＲを用いて、１ＶＡＣ×１ｋＨｚを荷電して測定した。(6) Capacitance measurement method (5) The capacitance of the capacitor element in the moisture resistance evaluation is TYPE manufactured by Ando Electric Co., Ltd.
Using AG-4311 LCRMETER, 1VAC × 1kHz was charged and measured.
（実施例１）
高分子基材として幅６４０ｍｍ、厚み６．０μｍの２軸延伸ポリプロピレンフィルム（東レ（株）製：トレファン（登録商標）２１７２）を用いた。まず真空蒸着機上室内を減圧し、予めオイル蒸発器の中に供給しておいたフッ素系オイルを９０℃以上に加熱し、オイル蒸発器上部に設けられたスリットを通して、高分子基材の長手方向に幅３．０ｍｍの非蒸着マージンを形成した。(Example 1)
A biaxially stretched polypropylene film (manufactured by Toray Industries, Inc .: Trefan (registered trademark) 2172) having a width of 640 mm and a thickness of 6.0 μm was used as the polymer base material. First, the pressure in the upper chamber of the vacuum vapor deposition machine is reduced, the fluorooil previously supplied into the oil evaporator is heated to 90 ° C. or higher, and the length of the polymer base material is passed through the slit provided in the upper part of the oil evaporator. A non-evaporated margin with a width of 3.0 mm was formed in the direction.
次いで、減圧された真空蒸着機下室に位置する冷却ロール下部で、アルミニウム、亜鉛の順にスリットを通して加熱蒸着し、膜抵抗がヘビーエッジ部で２〜３Ω／□、アクティブ部で８〜１０Ω／□となるようにスリットを通して蒸着し、アルミニウムと亜鉛の混合金属層を形成した。なお、アルミニウムと亜鉛の含有比率は、重量比３：９７になるように各金属の蒸着源の温度を調整した。 Next, in the lower part of the cooling roll located in the lower chamber of the vacuum vapor deposition machine where the pressure was reduced, aluminum and zinc were heated and vapor-deposited through slits in this order, and the film resistance was 2-3Ω / □ at the heavy edge part and 8-10Ω / □ at the active part. A mixed metal layer of aluminum and zinc was formed by thin-film deposition through a slit so as to be. The temperature of the vapor deposition source of each metal was adjusted so that the content ratio of aluminum and zinc was 3:97 by weight.
次いで、同一蒸着機内でアルミニウムと亜鉛の混合金属層上に、フェニルメチルジメチルポリシロキサン（ 東レダウコーニング株式会社製ＳＨ７０２）を加熱蒸着してケイ素化合物層を形成し、続けて高分子基材両面に、酸素ガスを微量供給しながら２５０ｋＨｚ、５．０ｋＷのパルスＤＣ電源を用いて、片面の処理電力密度Ｅ＝２５．５Ｗ・ｍｉｎ／ｍ２でプラズマ放電処理を施し、これを巻取軸で巻き取りアルミニウム、亜鉛の合金の金属化フィルムを得た。なお、ケイ素化合物層は、含有するＳｉ量が０．０３５〜０．０４５μｇ／ｃｍ２の範囲になるように、シロキサンの加熱温度を調整した。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。Next, phenylmethyldimethylpolysiloxane (SH702 manufactured by Toray Dow Corning Co., Ltd.) was heat-deposited on the mixed metal layer of aluminum and zinc in the same vapor deposition machine to form a silicon compound layer, and subsequently on both sides of the polymer substrate. Using a pulsed DC power supply of 250 kHz and 5.0 kW while supplying a small amount of oxygen gas , plasma discharge processing is performed at a processing power density of E = 25.5 W · min / m 2 on one side, and this is wound by a take-up shaft. A metallized film of an alloy of aluminum and zinc was obtained. The heating temperature of the siloxane of the silicon compound layer was adjusted so that the amount of Si contained in the silicon compound layer was in the range of 0.035 to 0.045 μg / cm 2. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムをフィルム幅１４ｍｍ、非蒸着マージン幅１．５ｍｍになるように裁断し、リールを作製した。得られたリール２つを互いに非蒸着マージンが反対面になるよう重ね、ずらし幅を１．０ｍｍとして巻回し、素子を作製した。ここで、作製後のフィルムコンデンサの静電容量は５００ＰＦになるように巻回長さを調整した。次に、得られた素子を圧力２５ｋｇ／ｃｍ２、温度１０５℃、プレス時間５分の条件でプレスして素子を扁平型にし、メタリコン処理、電極端子のはんだ付けを行い、フィルムコンデンサを作製した。得られたフィルムコンデンサ素子をエポキシ樹脂製外装ケースに入れ、２液性注型エポキシ樹脂を充填して温度１００℃で２時間加熱、硬化して、外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。Next, the obtained metallized film was cut so as to have a film width of 14 mm and a non-deposited margin width of 1.5 mm to prepare a reel. The two obtained reels were overlapped with each other so that the non-deposited margins were opposite to each other, and wound with a shift width of 1.0 mm to manufacture an element. Here, the winding length was adjusted so that the capacitance of the film capacitor after production was 500 PF. Next, the obtained element was pressed under the conditions of a pressure of 25 kg / cm 2 , a temperature of 105 ° C., and a press time of 5 minutes to flatten the element, and metallikon treatment and soldering of the electrode terminals were performed to prepare a film capacitor. .. The obtained film capacitor element was placed in an epoxy resin outer case, filled with a two-component cast epoxy resin, heated at a temperature of 100 ° C. for 2 hours, and cured to prepare a film capacitor element in the outer case. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例２）
実施例１のケイ素化合物層の形成において、高分子基材両面のプラズマ放電処理を片面の処理電力密度Ｅ＝４５．５Ｗ・ｍｉｎ／ｍ２とする以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 2)
In the formation of the silicon compound layer of Example 1, metallization is carried out in the same manner as in Example 1 except that the plasma discharge treatment on both sides of the polymer base material has a processing power density E = 45.5 W · min / m 2 on one side. I got a film. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例３）
実施例１のケイ素化合物層の形成において、フェニルメチルジメチルポリシロキサンの替わりに、ジメチルポリシロキサン（東レダウコーニング株式会社製ＳＨ２００、１０ｃｓ）を用いる以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 3)
In the formation of the silicon compound layer of Example 1, a metallized film was prepared in the same manner as in Example 1 except that dimethylpolysiloxane (SH200, 10cs manufactured by Dow Corning Co., Ltd.) was used instead of phenylmethyldimethylpolysiloxane. Obtained. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例４）
実施例１のケイ素化合物層の形成において、フェニルメチルジメチルポリシロキサンの替わりに、ジメチルポリシロキサン（東レダウコーニング株式会社製ＳＨ２００、１０ｃｓ）を用い、さらに高分子基材両面のプラズマ放電処理を片面の処理電力密度Ｅ＝４５．５Ｗ・ｍｉｎ／ｍ２とする以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 4)
In the formation of the silicon compound layer of Example 1, dimethylpolysiloxane (SH200, 10cs manufactured by Dow Corning Co., Ltd.) was used instead of phenylmethyldimethylpolysiloxane, and plasma discharge treatment on both sides of the polymer substrate was performed on one side. A metallized film was obtained in the same manner as in Example 1 except that the processing power density E was 45.5 W · min / m 2. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例５）
実施例１のケイ素化合物層の形成において、フェニルメチルジメチルポリシロキサンの替わりに、主鎖の両末端をＯＨ基にした両末端型のシラノール変性シリコーン（信越化学工業株式会社製Ｘ−２１−５８４１）を用いる以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 5)
In the formation of the silicon compound layer of Example 1, instead of phenylmethyldimethylpolysiloxane, a double-ended silanol-modified silicone having both ends of the main chain as OH groups (X-21-5841 manufactured by Shin-Etsu Chemical Industry Co., Ltd.) A metallized film was obtained in the same manner as in Example 1 except that the above was used. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例６）
実施例１のケイ素化合物層の形成において、フェニルメチルジメチルポリシロキサンの替わりに、主鎖の両末端をＯＨ基にした両末端型のシラノール変性シリコーン（信越化学工業株式会社製Ｘ−２１−５８４１）を用い、さらに高分子基材両面の片面のプラズマ放電処理を処理電力密度Ｅ＝４５．５Ｗ・ｍｉｎ／ｍ２とする以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 6)
In the formation of the silicon compound layer of Example 1, instead of phenylmethyldimethylpolysiloxane, a double-ended silanol-modified silicone having both ends of the main chain as OH groups (X-21-5841 manufactured by Shin-Etsu Chemical Industry Co., Ltd.) A metallized film was obtained in the same manner as in Example 1 except that the plasma discharge treatment on one side of both sides of the polymer substrate was set to a processing power density of E = 45.5 W · min / m 2. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例７）
実施例１のケイ素化合物層の形成において、フェニルメチルジメチルポリシロキサンの替わりに、アルキル変性シリコーン（東レダウコーニング株式会社製ＢＹ１６−８４６）を用いる以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 7)
In the formation of the silicon compound layer of Example 1, a metallized film was prepared in the same manner as in Example 1 except that an alkyl-modified silicone (BY16-846 manufactured by Dow Corning Co., Ltd.) was used instead of phenylmethyldimethylpolysiloxane. Obtained. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（実施例８）
実施例１のケイ素化合物層の形成において、フェニルメチルジメチルポリシロキサンの替わりに、アルキル変性シリコーン（東レダウコーニング株式会社製ＢＹ１６−８４６）を用い、さらに高分子基材両面のプラズマ放電処理を片面の処理電力密度Ｅ＝４５．５Ｗ・ｍｉｎ／ｍ２とする以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Example 8)
In the formation of the silicon compound layer of Example 1, an alkyl-modified silicone (BY16-846 manufactured by Toray Dow Corning Co., Ltd.) was used instead of phenylmethyldimethylpolysiloxane, and plasma discharge treatment on both sides of the polymer substrate was performed on one side. A metallized film was obtained in the same manner as in Example 1 except that the processing power density E was 45.5 W · min / m 2. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（比較例１）
実施例１のケイ素化合物層の形成しない以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Comparative Example 1)
A metallized film was obtained in the same manner as in Example 1 except that the silicon compound layer of Example 1 was not formed. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（比較例２）
実施例１のケイ素化合物層の形成において、高分子基材両面のプラズマ放電処理を施さない以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Comparative Example 2)
A metallized film was obtained in the same manner as in Example 1 except that the plasma discharge treatment on both sides of the polymer substrate was not performed in the formation of the silicon compound layer of Example 1. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（比較例３）
実施例３のケイ素化合物層の形成において、高分子基材両面のプラズマ放電処理を施さない以外は、実施例３と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Comparative Example 3)
A metallized film was obtained in the same manner as in Example 3 except that the plasma discharge treatment on both sides of the polymer substrate was not performed in the formation of the silicon compound layer of Example 3. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
（比較例４）
実施例１のケイ素化合物層の形成において、高分子基材のフェニルメチルジメチルポリシロキサン表面を処理電力密度Ｅ＝６．５Ｗ・ｍｉｎ／ｍ２でプラズマ放電処理を施し、フェニルメチルジメチルポリシロキサンを形成しない側の高分子基材表面にプラズマ放電処理を施さない以外は、実施例１と同様にして金属化フィルムを得た。得られた金属化フィルムについて、上述した（１）〜（４）の評価を行った。結果を表１に示す。(Comparative Example 4)
In the formation of the silicon compound layer of Example 1, the surface of the phenylmethyldimethylpolysiloxane of the polymer base material was subjected to plasma discharge treatment at a processing power density of E = 6.5 W · min / m 2 to form phenylmethyldimethylpolysiloxane. A metallized film was obtained in the same manner as in Example 1 except that the surface of the polymer base material on the non-side was not subjected to plasma discharge treatment. The obtained metallized film was evaluated in the above-mentioned (1) to (4). The results are shown in Table 1.
次いで、得られた金属化フィルムを使用し実施例１と同様にして外装ケース入りのフィルムコンデンサ素子を作製した。得られた外装ケース入りのフィルムコンデンサ素子について、（５）、（６）の評価を行った。結果を表１に示す。 Next, using the obtained metallized film, a film capacitor element in an outer case was produced in the same manner as in Example 1. The obtained film capacitor elements in the outer case were evaluated in (5) and (6). The results are shown in Table 1.
本発明の金属化フィルムは、高温、高湿環境に対する耐湿性に優れているので、例えば、過酷な環境で使用される自動車や電車の電装用及びエンジン、モーターの制御用やインバータ平滑コンデンサ、照明用などに好適に用いられる。 Since the metallized film of the present invention has excellent moisture resistance to high temperature and high humidity environments, for example, it is used for electrical equipment and engines of automobiles and trains used in harsh environments, for controlling motors, inverter smoothing capacitors, and lighting. It is suitably used for applications.
１ 高分子基材
２ 金属層
３ ケイ素化合物層
４ 非蒸着マージン
５ 非蒸着マージン側端部
６ 電極側端部1
Claims (5)
前記ケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、波数１０３０ｃｍ-１から１１３０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ａと、波数１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ａ／強度Ｂ）が、１．０以上であることを特徴とする、金属化フィルム。A metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material.
The silicon compound layer is obtained by FT-IR analysis, the intensity A of a peak having a maximum intensity that exist from the wave number 1030 cm -1 in the range of 1130 cm -1, present from the wave number 1240 cm -1 in the range of 1280 cm -1 A metallized film characterized in that the intensity ratio (intensity A / intensity B) of the intensity B of the peak having the maximum intensity is 1.0 or more.
前記ケイ素化合物層は、ＦＴ−ＩＲ分析で得られる、８７０ｃｍ-１から９４０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｃと、１２４０ｃｍ-１から１２８０ｃｍ-１の範囲に存在する最大強度を有するピークの強度Ｂの強度比（強度Ｃ／強度Ｂ）が、１．０以上であることを特徴とする、金属化フィルム。A metallized film in which a metal layer and a silicon compound layer are laminated in this order on at least one surface of a polymer base material.
Maximum intensity the silicon compound layer is obtained by FT-IR analysis, present and strength C of a peak having a maximum intensity that exist from 870 cm -1 in the range of 940 cm -1, from 1240 cm -1 in the range of 1280 cm -1 A metallized film having a peak intensity B intensity ratio (intensity C / intensity B) of 1.0 or more.