JPWO2019087856A1 - Odor control methods, compositions, wipers, and sprays - Google Patents

Odor control methods, compositions, wipers, and sprays Download PDF

Info

Publication number
JPWO2019087856A1
JPWO2019087856A1 JP2019551146A JP2019551146A JPWO2019087856A1 JP WO2019087856 A1 JPWO2019087856 A1 JP WO2019087856A1 JP 2019551146 A JP2019551146 A JP 2019551146A JP 2019551146 A JP2019551146 A JP 2019551146A JP WO2019087856 A1 JPWO2019087856 A1 JP WO2019087856A1
Authority
JP
Japan
Prior art keywords
metal
inorganic
composition
group
odor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
JP2019551146A
Other languages
Japanese (ja)
Inventor
光正 ▲濱▼野
光正 ▲濱▼野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujifilm Corp
Original Assignee
Fujifilm Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujifilm Corp filed Critical Fujifilm Corp
Publication of JPWO2019087856A1 publication Critical patent/JPWO2019087856A1/en
Abandoned legal-status Critical Current

Abstract

本発明は、被消臭物の臭気を抑制できる臭気抑制方法を提供する。また、組成物、ワイパー、及び、スプレーを提供する。本発明の臭気抑制方法は、第１の金属を含有する無機物、並びに、第１の金属とは異なる第２の金属を含有する無機物、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する組成物と、クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌を含有する被消臭物と、を接触させて、細菌に由来する臭気を抑制する。The present invention provides an odor suppressing method capable of suppressing the odor of an object to be deodorized. Also provided are compositions, wipers, and sprays. The odor control method of the present invention is selected from the group consisting of an inorganic substance containing a first metal, an inorganic substance containing a second metal different from the first metal, and an organic substance containing a second metal. Contains at least one bacterium selected from the group consisting of Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. The deodorant is brought into contact with the deodorant to suppress the odor derived from bacteria.

Description

本発明は、臭気抑制方法、組成物、ワイパー、及び、スプレーに関する。 The present invention relates to odor control methods, compositions, wipers, and sprays.

銀を含有し、抗菌性を有する組成物が知られている。例えば、特許文献１には、「銀イオン及び銀コロイド粒子からなる群から選ばれる少なくとも１つを含む銀成分と、添着剤とを含むスプレー用組成物」が記載されている。 Compositions containing silver and having antibacterial properties are known. For example, Patent Document 1 describes "a composition for spraying containing a silver component containing at least one selected from the group consisting of silver ions and silver colloidal particles, and an adhering agent".

特開２００６−２８２６２９号公報Japanese Unexamined Patent Publication No. 2006-228629

本発明者らは、様々な臭気を有する被消臭物に対して、特許文献１に記載された組成物を適用して、臭気の抑制を試みた。ところが、被消臭物によっては、上記組成物を用いても十分に臭気が抑制できないことを知見した。そこで、本発明は、被消臭物の臭気を抑制できる臭気抑制方法を提供することを課題とする。また、本発明は、組成物、ワイパー、及び、スプレーを提供することも課題とする。 The present inventors tried to suppress the odor by applying the composition described in Patent Document 1 to the deodorant having various odors. However, it has been found that the odor cannot be sufficiently suppressed even if the above composition is used, depending on the deodorant. Therefore, an object of the present invention is to provide an odor suppressing method capable of suppressing the odor of a deodorized product. It is also an object of the present invention to provide a composition, a wiper, and a spray.

本発明者らは、上記課題を解決すべく鋭意検討した結果、以下の構成により上記課題が解決されるのを見出した。 As a result of diligent studies to solve the above problems, the present inventors have found that the above problems can be solved by the following configuration.

［１］ 第１の金属を含有する無機物、並びに、第１の金属とは異なる第２の金属を含有する無機物、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する組成物と、クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌を含有する被消臭物と、を接触させて、細菌に由来する臭気を抑制する臭気抑制方法。
［２］ 第１の金属を含有する無機物が、第１の金属の単体、第１の金属の酸化物、及び、無機担体と無機担体に担持された第１の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、［１］に記載の臭気抑制方法。
［３］ 第２の金属を含有する無機物が、第２の金属の単体、第２の金属の酸化物、及び、無機担体と無機担体に担持された第２の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、［１］又は［２］に記載の臭気抑制方法。
［４］ 組成物が、第２の金属を含有する無機物を含有し、第１の金属が銀であり、第２の金属が銅である、［１］〜［３］のいずれかに記載の臭気抑制方法。
［５］ 組成物が、更に、水、及び、アルコールからなる群から選択される少なくとも１種を含有する、［１］〜［４］のいずれかに記載の臭気抑制方法。
［６］ 組成物が、第２の金属を含有する無機物を含有し、第１の金属を含有する無機物は、第１の無機担体と第１の無機担体に担持された銀とを有する金属担持無機担体であり、第２の金属を含有する無機物は、第２の無機担体と第２の無機担体に担持された銅とを有する金属担持無機担体である、［１］〜［５］のいずれかに記載の臭気抑制方法。
［７］ 組成物が、更に、第１の金属、及び、第２の金属のいずれとも異なる第３の金属を含有する無機物を含有する、［１］〜［６］のいずれかに記載の臭気抑制方法。
［８］ 第３の金属を含有する無機物が、リン原子を含有する、［７］に記載の臭気抑制方法。
［９］ 組成物のｐＨが６．５以下である、［１］〜［８］のいずれかに記載の臭気抑制方法。
［１０］ 組成物が、更に、親水性バインダー前駆体、及び、親水性バインダーからなる群から選択される親水性成分を含有する、［１］〜［９］のいずれかに記載の臭気抑制方法。
［１１］ 親水性成分が、シリケート系化合物、親水性基を有するモノマー、及び、親水性基を有するポリマーからなる群より選ばれる少なくとも１種を含有する、［１０］に記載の臭気抑制方法。
［１２］ 組成物が、更に、ノニオン系分散剤、及び、アニオン系分散剤からなる群から少なくとも１種を含有する、［１］〜［１１］のいずれかに記載の臭気抑制方法。
［１３］ 基布と、基布に含浸させた組成物とを有するワイパーを用いて、被消臭物を拭いて、組成物と被消臭物とを接触させる、［１］〜［１２］のいずれかに記載の臭気抑制方法。
［１４］ スプレー容器と、スプレー容器に収納された組成物とを有するスプレーを用いて、被消臭物に組成物を噴霧して、被消臭物と組成物とを接触させる、［１］〜［１２］のいずれかに記載の臭気抑制方法。
［１５］ 第１の金属を含有する無機物、並びに、第１の金属とは異なる第２の金属を含有する無機物、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する膜と、クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌を含有する被消臭物と、を接触させて、細菌に由来する臭気を抑制する臭気抑制方法。
［１６］ 第１の金属を含有する無機物が、第１の金属の単体、第１の金属の酸化物、及び、無機担体と無機担体に担持された第１の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、［１５］に記載の臭気抑制方法。
［１７］ 第２の金属を含有する無機物が、第２の金属の単体、第２の金属の酸化物、及び、無機担体と無機担体に担持された第２の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、［１５］又は［１６］に記載の臭気抑制方法。
［１８］ 膜が、第２の金属を含有する無機物を含有し、第１の金属が銀であり、第２の金属が銅である、［１５］〜［１７］のいずれかに記載の臭気抑制方法。
［１９］ 膜が、第２の金属を含有する無機物を含有し、第１の金属を含有する無機物は、第１の無機担体と第１の無機担体に担持された銀とを有する金属担持無機担体であり、第２の金属を含有する無機物は、第２の無機担体と第２の無機担体に担持された銅とを有する金属担持無機担体である、［１５］〜［１８］のいずれかに記載の臭気抑制方法。
［２０］ 膜が、更に、第１の金属、及び、第２の金属のいずれとも異なる第３の金属を含有する無機物を含有する、［１５］〜［１９］のいずれかに記載の臭気抑制方法。
［２１］ 第３の金属を含有する無機物が、更に、リン原子を含有する、［２０］に記載の臭気抑制方法。
［２２］ 膜の膜面のｐＨが６．５以下である、［１５］〜［２１］のいずれかに記載の臭気抑制方法。
［２３］ 膜が、更に、親水性バインダーを含む、［１５］〜［２２］のいずれかに記載の臭気抑制方法。
［２４］ 膜が、更に、ノニオン系分散剤、及び、アニオン系分散剤からなる群から少なくとも１種を含有する、［１５］〜［２３］のいずれかに記載の臭気抑制方法。
［２５］ 第１の金属を含有する無機物、並びに、第１の金属とは異なる第２の金属を含有する無機物、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有し、クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌に由来する臭気の抑制に用いられる、組成物。
［２６］ 第１の金属を含有する無機物が、第１の金属の単体、第１の金属の酸化物、及び、無機担体と無機担体に担持された第１の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、［２５］に記載の組成物。
［２７］ 第２の金属を含有する無機物が、第２の金属の単体、第２の金属の酸化物、及び、無機担体と無機担体に担持された第２の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、［２５］又は［２６］に記載の組成物。
［２８］ 第２の金属を含有する無機物を含有し、第１の金属が銀であり、第２の金属が銅である、［２５］〜［２７］のいずれかに記載の組成物。
［２９］ 組成物が、更に、水、及び、アルコールからなる群から選択される少なくとも１種を含有する、［２５］〜［２８］のいずれかに記載の組成物。
［３０］ 第２の金属を含有する無機物を含有し、第１の金属を含有する無機物は、第１の無機担体と第１の無機担体に担持された銀とを有する金属担持無機担体であり、第２の金属を含有する無機物は、第２の無機担体と第２の無機担体に担持された銅とを有する金属担持無機担体である、［２５］〜［２９］のいずれかに記載の組成物。
［３１］ 組成物が、更に、第１の金属、及び、第２の金属のいずれとも異なる第３の金属を含有する無機物を含有する、［２５］〜［３０］のいずれかに記載の組成物。
［３２］ 第３の金属を含有する無機物が、更に、リン原子を含有する、［３１］に記載の組成物。
［３３］ ｐＨが６．５以下である、［２５］〜［３２］のいずれかに記載の組成物。
［３４］ 更に、親水性バインダー前駆体、及び、親水性バインダーからなる群から選択される親水性成分を含有する、［２５］〜［３３］のいずれかに記載の組成物。
［３５］ 膜が、更に、ノニオン系分散剤、及び、アニオン系分散剤からなる群から少なくとも１種を含有する、［２５］〜［３４］のいずれかに記載の組成物。
［３６］ スプレー容器と、スプレー容器に収納された［２５］〜［３５］のいずれかに記載の組成物とを有するスプレー。
［３７］ 基布と、基布に含浸された［２５］〜［３５］のいずれかに記載の組成物とを有するワイパー。[1] At least one selected from the group consisting of an inorganic substance containing a first metal, an inorganic substance containing a second metal different from the first metal, and an organic substance containing a second metal. Deodorant containing at least one bacterium selected from the group consisting of Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. An odor control method that suppresses odors derived from bacteria by contacting with and.
[2] A metal-supported inorganic carrier in which the inorganic substance containing the first metal has a simple substance of the first metal, an oxide of the first metal, and an inorganic carrier and a first metal supported on the inorganic carrier. The odor control method according to [1], which is at least one selected from the group consisting of.
[3] A metal-supported inorganic carrier in which the inorganic substance containing the second metal has a simple substance of the second metal, an oxide of the second metal, and an inorganic carrier and a second metal supported on the inorganic carrier. The odor control method according to [1] or [2], which is at least one selected from the group consisting of.
[4] The composition according to any one of [1] to [3], wherein the composition contains an inorganic substance containing a second metal, the first metal is silver, and the second metal is copper. Odor control method.
[5] The method for suppressing odor according to any one of [1] to [4], wherein the composition further contains at least one selected from the group consisting of water and alcohol.
[6] The composition contains an inorganic substance containing a second metal, and the inorganic substance containing the first metal is a metal-supported product having a first inorganic carrier and silver supported on the first inorganic carrier. The inorganic substance containing the second metal, which is an inorganic carrier, is any of [1] to [5], which is a metal-supported inorganic carrier having a second inorganic carrier and copper supported on the second inorganic carrier. The odor control method described in Crab.
[7] The odor according to any one of [1] to [6], wherein the composition further contains an inorganic substance containing a first metal and a third metal different from any of the second metals. Suppression method.
[8] The method for suppressing odor according to [7], wherein the inorganic substance containing a third metal contains a phosphorus atom.
[9] The method for suppressing odor according to any one of [1] to [8], wherein the pH of the composition is 6.5 or less.
[10] The method for suppressing odor according to any one of [1] to [9], wherein the composition further contains a hydrophilic binder precursor and a hydrophilic component selected from the group consisting of a hydrophilic binder. ..
[11] The method for suppressing odor according to [10], wherein the hydrophilic component contains at least one selected from the group consisting of a silicate-based compound, a monomer having a hydrophilic group, and a polymer having a hydrophilic group.
[12] The method for suppressing odor according to any one of [1] to [11], wherein the composition further contains at least one from the group consisting of a nonionic dispersant and an anionic dispersant.
[13] Using a wiper having a base cloth and a composition impregnated in the base cloth, the deodorant is wiped and the composition and the deodorant are brought into contact with each other [1] to [12]. The odor control method according to any one of.
[14] Using a spray having a spray container and a spray containing the composition contained in the spray container, the composition is sprayed on the deodorant to bring the deodorant into contact with the composition [1]. The odor suppressing method according to any one of [12].
[15] At least one selected from the group consisting of an inorganic substance containing a first metal, an inorganic substance containing a second metal different from the first metal, and an organic substance containing a second metal. And a deodorant containing at least one bacterium selected from the group consisting of Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. An odor control method that suppresses odors derived from bacteria by contacting.
[16] A metal-supported inorganic carrier in which the inorganic substance containing the first metal has a simple substance of the first metal, an oxide of the first metal, and an inorganic carrier and a first metal supported on the inorganic carrier. The odor control method according to [15], which is at least one selected from the group consisting of.
[17] A metal-supported inorganic carrier in which the inorganic substance containing the second metal has a simple substance of the second metal, an oxide of the second metal, and an inorganic carrier and a second metal supported on the inorganic carrier. The odor control method according to [15] or [16], which is at least one selected from the group consisting of.
[18] The odor according to any one of [15] to [17], wherein the film contains an inorganic substance containing a second metal, the first metal is silver, and the second metal is copper. Suppression method.
[19] The film contains an inorganic substance containing a second metal, and the inorganic substance containing the first metal is a metal-supported inorganic substance having a first inorganic carrier and silver supported on the first inorganic carrier. The carrier and the inorganic substance containing the second metal is any one of [15] to [18], which is a metal-supported inorganic carrier having a second inorganic carrier and copper supported on the second inorganic carrier. The odor control method described in 1.
[20] The odor suppression according to any one of [15] to [19], wherein the film further contains an inorganic substance containing a first metal and a third metal different from any of the second metals. Method.
[21] The method for suppressing odor according to [20], wherein the inorganic substance containing the third metal further contains a phosphorus atom.
[22] The method for suppressing odor according to any one of [15] to [21], wherein the pH of the film surface of the film is 6.5 or less.
[23] The method for suppressing odor according to any one of [15] to [22], wherein the film further contains a hydrophilic binder.
[24] The method for suppressing odor according to any one of [15] to [23], wherein the membrane further contains at least one from the group consisting of a nonionic dispersant and an anionic dispersant.
[25] At least one selected from the group consisting of an inorganic substance containing a first metal, an inorganic substance containing a second metal different from the first metal, and an organic substance containing a second metal. Is used to suppress odors derived from at least one bacterium selected from the group consisting of Klebsiella, Citrobacta, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. Composition.
[26] A metal-supported inorganic carrier in which the inorganic substance containing the first metal has a simple substance of the first metal, an oxide of the first metal, and an inorganic carrier and a first metal supported on the inorganic carrier. The composition according to [25], which is at least one selected from the group consisting of.
[27] A metal-supported inorganic carrier in which the inorganic substance containing the second metal has a simple substance of the second metal, an oxide of the second metal, and an inorganic carrier and a second metal supported on the inorganic carrier. The composition according to [25] or [26], which is at least one selected from the group consisting of.
[28] The composition according to any one of [25] to [27], which contains an inorganic substance containing a second metal, the first metal being silver and the second metal being copper.
[29] The composition according to any one of [25] to [28], wherein the composition further contains at least one selected from the group consisting of water and alcohol.
[30] The inorganic substance containing a second metal and containing the first metal is a metal-supported inorganic carrier having a first inorganic carrier and silver supported on the first inorganic carrier. The inorganic substance containing the second metal is a metal-supported inorganic carrier having a second inorganic carrier and copper supported on the second inorganic carrier, according to any one of [25] to [29]. Composition.
[31] The composition according to any one of [25] to [30], wherein the composition further contains an inorganic substance containing a first metal and a third metal different from any of the second metals. Stuff.
[32] The composition according to [31], wherein the inorganic substance containing a third metal further contains a phosphorus atom.
[33] The composition according to any one of [25] to [32], which has a pH of 6.5 or less.
[34] The composition according to any one of [25] to [33], further containing a hydrophilic binder precursor and a hydrophilic component selected from the group consisting of hydrophilic binders.
[35] The composition according to any one of [25] to [34], wherein the membrane further contains at least one of the group consisting of a nonionic dispersant and an anionic dispersant.
[36] A spray having a spray container and the composition according to any one of [25] to [35] contained in the spray container.
[37] A wiper having a base cloth and the composition according to any one of [25] to [35] impregnated in the base cloth.

本発明によれば、被消臭物の臭気を抑制できる臭気抑制方法を提供できる。また、本発明は、組成物、ワイパー、及び、スプレーを提供できる。 According to the present invention, it is possible to provide an odor suppressing method capable of suppressing the odor of a deodorized product. The present invention can also provide compositions, wipers, and sprays.

以下、本発明について詳細に説明する。
以下に記載する構成要件の説明は、本発明の代表的な実施態様に基づいてなされることがあるが、本発明はそのような実施態様に制限されるものではない。
なお、本明細書における基（原子群）の表記において、置換、及び無置換を記していない表記は、本発明の効果を損ねない範囲で、置換基を有さないものと共に置換基を有するものをも包含するものである。例えば、「アルキル基」とは、置換基を有さないアルキル基（無置換アルキル基）のみならず、置換基を有するアルキル基（置換アルキル基）をも包含するものである。このことは、各化合物についても同義である。
また、本明細書において、「（メタ）アクリレート」はアクリレート、及びメタクリレートの双方、又はいずれかを表し、「（メタ）アクリル」はアクリル、及びメタクリルの双方、又はいずれかを表し、「（メタ）アクリロイル」はアクリロイル、及びメタクリロイルの双方、又はいずれかを表す。
また、本明細書において、「〜」を用いて表される数値範囲は、「〜」の前後に記載される数値を下限値、及び上限値として含む範囲を意味する。Hereinafter, the present invention will be described in detail.
The description of the constituent elements described below may be based on typical embodiments of the present invention, but the present invention is not limited to such embodiments.
In the notation of groups (atomic groups) in the present specification, the notations that do not describe substitutions and non-substitutions are those having a substituent as well as those having no substituent within the range not impairing the effect of the present invention. Also includes. For example, the "alkyl group" includes not only an alkyl group having no substituent (unsubstituted alkyl group) but also an alkyl group having a substituent (substituted alkyl group). This is synonymous with each compound.
Further, in the present specification, "(meth) acrylate" represents both acrylate and methacrylate, or either, and "(meth) acrylic" represents both acrylic and methacrylic, or either. ) Acryloyl "represents both acryloyl and / or methacryloyl.
Further, in the present specification, the numerical range represented by using "~" means a range including the numerical values before and after "~" as the lower limit value and the upper limit value.

［臭気抑制方法の第１実施形態］
本発明の第１の実施形態に係る臭気抑制方法は、第１の金属を含有する無機物、並びに、第１の金属とは異なる第２の金属を含有する無機物、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する組成物と、クレブシエラ（Klebsiella）属、シトロバクター（Citrobacter）属、エンテロバクター（Enterobacter）属、プロテウス（Proteus）属、シュードモナス属（Pseudomonas）、セラチア（Serratia）属及び、モルガネラ（Morganella）属からなる群から選択される少なくとも１種類の細菌（以下、「特定細菌」ともいう。）を含有する被消臭物と、を接触させて、上記特定細菌に由来する臭気を抑制する臭気抑制方法である。[First Embodiment of Odor Control Method]
The odor control method according to the first embodiment of the present invention contains an inorganic substance containing a first metal, an inorganic substance containing a second metal different from the first metal, and a second metal. A composition containing at least one selected from the group consisting of organic substances, and the genus Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas. , A deodorant containing at least one type of bacterium (hereinafter, also referred to as "specific bacterium") selected from the group consisting of the genus Serratia and the genus Morganella, is brought into contact with the deodorant. This is an odor suppressing method for suppressing an odor derived from the specific bacterium.

本発明者らは特許文献１に記載された組成物を様々な被消臭物に適用して、臭気の抑制を試みたところ、特定細菌を含有する被消臭物では、その臭気が十分に抑制されないことを知見した。この理由は必ずしも明らかではないが、被消臭物に上記特定細菌が含有される場合、上記特定細菌に由来して（例えば、上記特定細菌の代謝によって）臭気が発生しこの臭気が十分に抑制されていないものと推測された。
本発明者は上記知見を元に、特定細菌に由来する臭気を抑制する方法を鋭意検討した結果、本発明の完成に至った。The present inventors tried to suppress the odor by applying the composition described in Patent Document 1 to various deodorants, and found that the odor was sufficiently present in the deodorant containing a specific bacterium. It was found that it was not suppressed. The reason for this is not always clear, but when the deodorant contains the specific bacterium, an odor is generated from the specific bacterium (for example, by metabolism of the specific bacterium) and this odor is sufficiently suppressed. It was speculated that it was not done.
Based on the above findings, the present inventor has diligently studied a method for suppressing an odor derived from a specific bacterium, and as a result, the present invention has been completed.

被消臭物に組成物を接触する方法としては特に制限されないが、例えば、以下の方法が挙げられる。
・基布と、基布に含浸させた組成物とを有するワイパーを用いて、被消臭物を拭いて、組成物と被消臭物とを接触させる方法（ワイプ法）
・スプレー容器と、スプレー容器に収納された組成物とを有するスプレーを用いて、被消臭物に組成物を噴霧して、被消臭物と組成物とを接触させる方法（スプレー法）The method of bringing the composition into contact with the deodorant is not particularly limited, and examples thereof include the following methods.
-A method in which a wiper having a base cloth and a composition impregnated in the base cloth is used to wipe the deodorant and bring the composition into contact with the deodorant (wiping method).
-A method of spraying a composition on a deodorant by using a spray having a spray container and a composition contained in the spray container to bring the deodorant into contact with the composition (spray method).

（ワイプ法）
ワイプ法では、後述する組成物を基布に含浸させたワイパーを用いる。ワイパーを用いて被消臭物（被消臭物の詳細は後述する）を拭く方法としては特に制限されず、公知の方法が使用できる。(Wipe method)
In the wipe method, a wiper in which the base cloth is impregnated with the composition described later is used. The method of wiping the deodorant (details of the deodorant will be described later) with a wiper is not particularly limited, and a known method can be used.

本方法で使用する基布としては、特に制限されず、天然繊維で形成されたものであっても、化学繊維で形成されたものであってもよい。
天然繊維としては、例えば、パルプ、綿、麻、亜麻、羊毛、キヤメル、カシミヤ、モヘヤ、及び絹等が挙げられる。
化学繊維の材料としては、レーヨン、ポリノジック、アセテート、トリアセテート、ナイロン、ポリエステル、ポリアクリロニトリル、ポリビニルアルコール、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリエチレン、ポリプロピレン、ポリウレタン、ポリアルキレンパラオキシベンゾエート、及びポリクラール等が挙げられる。The base cloth used in this method is not particularly limited, and may be one made of natural fibers or one made of chemical fibers.
Examples of natural fibers include pulp, cotton, hemp, flax, wool, camel, cashmere, mohair, silk and the like.
Examples of the material of the chemical fiber include rayon, polynosic, acetate, triacetate, nylon, polyester, polyacrylonitrile, polyvinyl alcohol, polyvinyl chloride, polyvinylidene chloride, polyethylene, polypropylene, polyurethane, polyalkylene paraoxybenzoate, and polyclaral. ..

なかでも、これらの基布のうち、組成物が含浸しやすい点で、親水性の基布が好ましい。親水性の基布とは、例えば、水酸基、アミノ基、カルボキシ基、アミド基、及びスルホニル基等の親水性基を有する繊維を含む基布である。親水性の基布としては、具体的には、植物性繊維、綿、パルプ、動物性繊維、レーヨン、ナイロン、ポリエステル、ポリアクリロニトリル、及びポリビニルアルコール等が挙げられる。
なかでも、基布としては、不織布、布、タオル、ガーゼ、及び脱脂綿等が挙げられ、なかでも不織布が好ましい。
また、基布の目付（単位面積当たりの質量）は、１００ｇ／ｍ２以下が好ましい。上記組成物を基布に含浸させる際の含浸量は、基布の質量に対して１倍以上の量が好ましい。Of these base fabrics, hydrophilic base fabrics are preferable because they are easily impregnated with the composition. The hydrophilic base cloth is a base cloth containing fibers having a hydrophilic group such as a hydroxyl group, an amino group, a carboxy group, an amide group, and a sulfonyl group. Specific examples of the hydrophilic base fabric include vegetable fibers, cotton, pulp, animal fibers, rayon, nylon, polyester, polyacrylonitrile, polyvinyl alcohol and the like.
Among them, examples of the base cloth include non-woven fabric, cloth, towel, gauze, absorbent cotton and the like, and non-woven fabric is preferable.
The basis weight (mass per unit area) of the base cloth is preferably 100 g / m 2 or less. The amount of impregnation when the base cloth is impregnated with the above composition is preferably 1 times or more the mass of the base cloth.

（スプレー法）
スプレー法では、スプレー容器と、スプレー容器に収納された組成物とを有するスプレーを用いる。スプレーを用いて、被消臭物に組成物を噴霧する方法としては特に制限されず、公知の方法が使用できる。
なお、典型的には、スプレーとしては、トリガー形態、ポンプ形態、及び、スプレー容器に組成物と噴射剤とが充填されたエアゾール形態等が挙げられる。噴射剤としては、特に制限されないが、例えば液化石油ガス等が挙げられる。(Spray method)
In the spray method, a spray having a spray container and a composition contained in the spray container is used. The method of spraying the composition on the deodorant by using a spray is not particularly limited, and a known method can be used.
Typically, examples of the spray include a trigger form, a pump form, and an aerosol form in which a spray container is filled with a composition and a propellant. The propellant is not particularly limited, and examples thereof include liquefied petroleum gas and the like.

〔被消臭物〕
上記被消臭物は、特定細菌を含有する。被消臭物が特定細菌を含有する形態としては特に制限されない。
被消臭物は、更に、基質を含有することが好ましい。基質としては、特に制限されないが、レシチン、メチオニン、尿素、及び、コリン等が挙げられる。すなわち、被消臭物は、特定細菌と基質とを含有することが好ましい。
被消臭物が特定細菌と基質とを含有する形態としては特に制限されない。基質は、典型的には、尿（ヒト及びヒト以外の動物の尿を意味し、特に、***症を罹患したヒト及びヒト以外の動物の尿が好ましい）、糞便、汗、喀痰、及び、食べかす等に含有されることが多く、基質が尿、又は、糞便に含有される場合に、本発明はより優れた効果を発揮し、特に尿に基質が含有される場合に、更に優れた効果を発揮する。
基質が尿に含有される場合を例に、被消臭物の形態について具体的に説明する。
被消臭物としては、基材に特定細菌を含有する尿が吸収、又は、吸着されたもの、基材上に特定細菌を含有する尿が配置されたもの、特定細菌を含有する尿自体等が挙げられる。この場合、基材としては、特に制限されないが、例えば、下着類を含む衣服、寝具、おむつ等の介護用品、便器、床、及び、壁等が挙げられる。[Deodorant]
The deodorant contains specific bacteria. The form in which the deodorant contains a specific bacterium is not particularly limited.
The deodorant preferably further contains a substrate. The substrate is not particularly limited, and examples thereof include lecithin, methionine, urea, and choline. That is, the deodorant preferably contains a specific bacterium and a substrate.
The form in which the deodorant contains a specific bacterium and a substrate is not particularly limited. The substrate typically refers to urine (meaning human and non-human animal urine, particularly preferably human and non-human animal urine with urinary tract infections), feces, sweat, sputum, and. The present invention exerts a more excellent effect when the substrate is contained in urine or feces, and is even more excellent especially when the substrate is contained in urine. It is effective.
The form of the deodorant will be specifically described by taking the case where the substrate is contained in urine as an example.
Deodorants include those in which urine containing specific bacteria is absorbed or adsorbed on the base material, those in which urine containing specific bacteria is arranged on the base material, urine itself containing specific bacteria, etc. Can be mentioned. In this case, the base material is not particularly limited, and examples thereof include clothes including underwear, bedding, nursing care products such as diapers, toilet bowls, floors, and walls.

被消臭物中では、特定細菌に由来して悪臭物質（臭気）が産生されると推測される。例えば、尿を含有する被消臭物中では、典型的には特定細菌が発現するウレアーゼによって、尿中の尿素（基質）が分解され、アンモニアが生ずる。このように、上記被消臭物からは、特定細菌に由来して、悪臭物質（臭気）が発生すると推測される。 It is presumed that a malodorous substance (odor) is produced from a specific bacterium in the deodorant. For example, in a deodorant containing urine, urea (substrate) in urine is typically decomposed by urease expressed by a specific bacterium to generate ammonia. As described above, it is presumed that a malodorous substance (odor) is generated from the deodorant substance due to the specific bacteria.

より具体的には、本方法は、Klebsiella oxytoca、Klebsiella pneumoniae、Citrobacter freundii、Citrobacter diversus、Enterobacter aerogenes、Enterobacter cloacae、Proteus mirabilis、Proteus vulgaris、Pseudomonas aeruginosa、Serratia marcescens、及び、Morganella morganii等の細菌を含有する被消臭物における、上記細菌に由来する臭気の抑制により優れた効果を有する。 More specifically, this method contains Klebsiella oxytoca, Klebsiella pneumoniae, Citrobacter freundii, Citrobacter diversus, Enterobacter aerogenes, Enterobacter cloacae, Proteus mirabilis, Proteus vulgaris, Pseudomonas aeruginosa, Serratia marcescens, etc. It has an excellent effect by suppressing the odor derived from the above bacteria in the deodorant.

〔組成物〕
上記組成物は、第１の金属を含有する無機物（以下「無機物（１）」又は「第１金属含有物」ともいう。）、並びに、第１の金属とは異なる第２の金属を含有する無機物（以下「無機物（２）」ともいう。）、及び、上記第２の金属を含有する有機物からなる群から選択される少なくとも１種（以下、「第２金属含有物」ともいう。）を含有する。
なお、本明細書において、単に「金属」という時は、金属単体（金属単体粒子）、金属イオン、及び、化合物中に含有される金属原子を含むものとする。〔Composition〕
The composition contains an inorganic substance containing a first metal (hereinafter, also referred to as "inorganic substance (1)" or "first metal-containing substance"), and a second metal different from the first metal. At least one selected from the group consisting of an inorganic substance (hereinafter, also referred to as "inorganic substance (2)") and an organic substance containing the second metal (hereinafter, also referred to as "second metal-containing substance"). contains.
In addition, in this specification, the term "metal" simply includes a metal simple substance (metal simple substance particles), a metal ion, and a metal atom contained in a compound.

＜無機物（１）＞
上記組成物は無機物（１）を含有する。組成物中における無機物（１）の含有量としては特に制限されないが、一般に、組成物の全固形分に対して、０．００１〜８０質量％が好ましい。無機物（１）は、１種を単独で用いても、２種以上を併用してもよい。２種以上の無機物（１）を併用する場合には、合計含有量が上記範囲内であることが好ましい。<Inorganic matter (1)>
The composition contains an inorganic substance (1). The content of the inorganic substance (1) in the composition is not particularly limited, but is generally preferably 0.001 to 80% by mass with respect to the total solid content of the composition. As the inorganic substance (1), one type may be used alone, or two or more types may be used in combination. When two or more kinds of inorganic substances (1) are used in combination, the total content is preferably within the above range.

無機物（１）は、固形物であっても、液状物であってもよいが、本発明の効果により優れる点で、無機物（１）は固形物が好ましく、固形物としては、粒子（組成物中で粒子として存在するもの）がより好ましい。 The inorganic substance (1) may be a solid substance or a liquid substance, but the inorganic substance (1) is preferably a solid substance in that it is superior to the effect of the present invention, and the solid substance is a particle (composition). Those existing as particles) are more preferable.

無機物（１）は第１の金属を含有する。無機物（１）の形態としては特に制限されず、第１の金属の単体（金属単体粒子）、第１の金属のイオン、及び、第１の金属を含有する無機化合物のいずれであってもよく、これらの混合物であってもよい。また、無機物（１）は、無機化合物と、第１の金属との複合体であってもよい。複合体としては、例えば、無機担体と、上記無機担体に担持された第１の金属（第１の金属の単体（金属単体粒子）、第１の金属のイオン、及び、第１の金属を含有する無機化合物のいずれであってもよい）とを有する金属担持担体（以下、「第１金属担持無機担体」ともいう。）が挙げられる。
なかでも、本発明の効果により優れる観点で、無機物（１）は、第１の金属の単体（粒子）、第１の金属のイオン、第１の金属の酸化物、及び、第１金属担持無機担体からなる群から選択される少なくとも１種が好ましく、第１金属担持無機担体がより好ましい。The inorganic substance (1) contains a first metal. The form of the inorganic substance (1) is not particularly limited, and may be any of a simple substance of the first metal (elemental metal particles), an ion of the first metal, and an inorganic compound containing the first metal. , These may be a mixture. Further, the inorganic substance (1) may be a composite of the inorganic compound and the first metal. The composite contains, for example, an inorganic carrier, a first metal supported on the inorganic carrier (a simple substance of the first metal (elemental metal particles), an ion of the first metal, and a first metal. Examples thereof include a metal-supporting carrier (hereinafter, also referred to as “first metal-supporting inorganic carrier”) having an inorganic compound (which may be any of the above-mentioned inorganic compounds).
Among them, from the viewpoint of being more excellent in the effect of the present invention, the inorganic substance (1) is a simple substance (particle) of the first metal, an ion of the first metal, an oxide of the first metal, and an inorganic substance carrying the first metal. At least one selected from the group consisting of carriers is preferable, and a first metal-supported inorganic carrier is more preferable.

第１の金属としては、特に制限されないが、銀、銅、亜鉛、水銀、鉄、鉛、ビスマス、チタン、錫、ジルコニウム、アルミニウム、及び、ニッケル等が挙げられ、なかでも、銀、銅、又は、亜鉛が好ましく、銀、又は、銅がより好ましく、銀が更に好ましい。
無機物（１）は、例えば、第１の金属の酸化物、窒化物、ハロゲン化物、シアン化物、セレン化物、硫化物、テルル化物、及び、第１の金属の塩等であってもよい。第１の金属の塩としては、例えば、ヒ酸塩、フッ化水素塩、臭素酸塩、塩素酸塩、クロム酸塩、シアン酸塩、ヘキサフルオロアンチモン酸塩、ヘキサフルオロヒ酸塩、ヘキサフルオロリン酸塩、ヨウ素酸塩、イソチオシアン酸塩、モリブデン酸塩、硝酸塩、亜硝酸塩、過塩素酸塩、過マンガン酸塩、過レニウム酸塩、リン酸塩、セレン酸塩、亜セレン酸塩、硫酸塩、亜硫酸塩、テトラフルオロほう酸塩、テトラタングステン酸塩、チオシアン酸塩、及び、バナジン酸塩等が挙げられる。The first metal is not particularly limited, and examples thereof include silver, copper, zinc, mercury, iron, lead, bismuth, titanium, tin, zirconium, aluminum, and nickel, and among them, silver, copper, or nickel. , Zinc is preferred, silver or copper is more preferred, and silver is even more preferred.
The inorganic substance (1) may be, for example, an oxide of the first metal, a nitride, a halide, a cyanide, a selenium compound, a sulfide, a telluride compound, a salt of the first metal, or the like. Examples of the salt of the first metal include hydride, hydrogen fluoride salt, bromine salt, chlorate, chromate, cyanate, hexafluoroantimonate, hexafluorohydrate, hexafluoro. Phosphate, iodate, isothiocyanate, molybdenate, nitrate, nitrite, perchlorate, permanganate, perlenate, phosphate, selenate, selenate, sulfate Examples thereof include salts, sulfites, tetrafluoroborates, tetratungstates, thiocyanates, vanazine salts and the like.

第１金属担持無機担体の無機担体としては特に制限されないが、無機酸化物（例えば、ゼオライト：結晶性アルミノケイ酸塩）、シリカゲル、及び、粘土鉱物等のケイ酸塩；ガラス（水溶性ガラスを含む）；リン酸ジルコニウム；リン酸カルシウム；活性炭；等が挙げられる。
なお、本明細書において、第１金属担持無機担体の無機担体を「第１の無機担体」という事がある。The inorganic carrier of the first metal-supported inorganic carrier is not particularly limited, but is an inorganic oxide (for example, zeolite: crystalline aluminosilicate), silica gel, and silicates such as clay minerals; glass (including water-soluble glass). ); Zirconium phosphate; Calcium phosphate; Activated charcoal; etc.
In the present specification, the inorganic carrier of the first metal-supported inorganic carrier may be referred to as "first inorganic carrier".

無機担体としてはより具体的には、リン酸亜鉛カルシウム、リン酸カルシウム、リン酸ジルコニウム、リン酸アルミニウム、ケイ酸カルシウム、活性炭、活性アルミナ、シリカゲル、ガラス（酸化ケイ素）、ゼオライト、アパタイト、ヒドロキシアパタイト、リン酸チタン、チタン酸カリウム、含水酸化ビスマス、含水酸化ジルコニウム、及びハイドロタルサイト等が挙げられる。
無機担体としては、結晶性であっても、非晶性（アモルファス）であってもよいが、非晶性であることが好ましい。言い換えると、無機担体としてはガラスが好ましい。
ガラスを構成し得る材料としては、例えば、ケイ酸塩、ホウケイ酸塩、及びリン酸塩等（言い換えると、ケイ酸塩ガラス、ホウケイ酸塩ガラス、及びリン酸塩ガラス等）が挙げられる。なかでも、ケイ酸塩が好ましい。
上記ケイ酸塩は、アルカリ金属及びアルカリ土類金属からなる群から選ばれる１種以上の原子を含んでいることが好ましく、ケイ酸アルミニウムがより好ましい。More specifically, the inorganic carrier includes calcium zinc phosphate, calcium phosphate, zirconium phosphate, aluminum phosphate, calcium silicate, activated charcoal, active alumina, silica gel, glass (silicon oxide), zeolite, apatite, hydroxyapatite, and phosphorus. Examples thereof include titanium phosphate, potassium titanate, bismuth-containing hydroxide, zirconium-containing zirconium, and hydrotalcite.
The inorganic carrier may be crystalline or amorphous, but is preferably amorphous. In other words, glass is preferable as the inorganic carrier.
Examples of the material that can constitute glass include silicate, borosilicate, phosphate and the like (in other words, silicate glass, borosilicate glass, phosphate glass and the like). Of these, silicate is preferable.
The silicate preferably contains one or more atoms selected from the group consisting of alkali metals and alkaline earth metals, and aluminum silicate is more preferable.

第１金属担持無機担体としては、第１の金属が担持された、金属担持ゼオライト、金属担持アパタイト、金属担持ガラス、金属担持リン酸ジルコニウム、又は、金属担持ケイ酸カルシウムが好ましく、金属担持アパタイト、又は、金属担持ガラスがより好ましく、金属担持ガラスが更に好ましい。 As the first metal-supported inorganic carrier, a metal-supported zeolite, a metal-supported apatite, a metal-supported glass, a metal-supported zirconium phosphate, or a metal-supported calcium silicate on which the first metal is supported is preferable, and the metal-supported apatite, Alternatively, metal-supported glass is more preferable, and metal-supported glass is even more preferable.

無機物（１）が粒子である場合、無機物（１）の粒子の平均粒径としては、特に制限されないが、一般に、０．０１μｍ以上が好ましく、０．０５μｍ以上がより好ましく、２０μｍ以下が好ましく、１５μｍ以下がより好ましい。
なお、無機物（１）の粒子の平均粒径は、電子顕微鏡を用いて観察することにより測定できる。具体的には、上記平均粒径は、無機物（１）の粒子について、一次粒子及び二次粒子（なお、「二次粒子」とは、一次粒子同士が融合あるいは接触して構成される集合体と定義する。）の直径を電子顕微鏡の画像から計測し、全粒子数の中の最も直径が小さい側の粒子数５％と、最も直径が大きい側の粒子数５％を除いた、９０％の範囲の粒子の直径を平均した値である。つまり、平均粒径は、一次粒子及び二次粒子から求められる値である。また、直径とは、粒子の外接円相当直径のことをいう。
なお、無機物（１）の粒子の粒子形状に大きく違いがない場合、堀場製作所社製のレーザー回折／散乱式粒度分布測定装置を用いて５０％体積累積径（Ｄ５０）を３回測定して、３回測定した値の平均値を平均粒径として代用してもよい。When the inorganic substance (1) is a particle, the average particle size of the particles of the inorganic substance (1) is not particularly limited, but is generally preferably 0.01 μm or more, more preferably 0.05 μm or more, and preferably 20 μm or less. More preferably, it is 15 μm or less.
The average particle size of the particles of the inorganic substance (1) can be measured by observing with an electron microscope. Specifically, the average particle size of the particles of the inorganic substance (1) is an aggregate composed of primary particles and secondary particles (note that "secondary particles" are formed by fusion or contact between primary particles. 90%, excluding 5% of the particles on the smallest diameter side and 5% of the particles on the largest diameter side of the total number of particles, measured from the image of the electron microscope. It is a value obtained by averaging the diameters of particles in the range of. That is, the average particle size is a value obtained from the primary particles and the secondary particles. Further, the diameter means the diameter corresponding to the circumscribed circle of the particles.
If there is no significant difference in the particle shape of the particles of the inorganic substance (1), the 50% volume cumulative diameter (D50) is measured three times using a laser diffraction / scattering particle size distribution measuring device manufactured by HORIBA, Ltd. The average value of the values measured three times may be substituted as the average particle size.

無機物（１）の粒子の平均粒径は、従来公知の方法により調節でき、例えば、乾式粉砕及び湿式粉砕等の方法を採用できる。乾式粉砕においては、例えば、乳鉢、ジェットミル、ハンマーミル、ピンミル、回転ミル、振動ミル、遊星ミル、及びビーズミル等が適宜用いられる。また、湿式粉砕においては、各種ボールミル、高速回転粉砕機、ジェットミル、ビーズミル、超音波ホモジナイザー、及び高圧ホモジナイザー等が適宜用いられる。
例えば、ビーズミルにおいては、メディアとなるビーズの径、種類、及び混合量等を調節することで平均粒径を制御できる。The average particle size of the particles of the inorganic substance (1) can be adjusted by a conventionally known method, and for example, methods such as dry pulverization and wet pulverization can be adopted. In the dry pulverization, for example, a mortar, a jet mill, a hammer mill, a pin mill, a rotary mill, a vibration mill, a planetary mill, a bead mill and the like are appropriately used. Further, in wet pulverization, various ball mills, high-speed rotary pulverizers, jet mills, bead mills, ultrasonic homogenizers, high-pressure homogenizers and the like are appropriately used.
For example, in a bead mill, the average particle size can be controlled by adjusting the diameter, type, mixing amount, and the like of beads as a medium.

＜第２金属含有物＞
上記組成物は、無機物（２）、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種（第２金属含有物）を含有する。組成物中における第２金属含有物の含有量としては特に制限されないが、一般に、組成物の全固形分に対して、０．００１〜８０質量％が好ましい。第２金属含有物は、１種を単独で用いても、２種以上を併用してもよい。２種以上の第２金属含有物を併用する場合には、合計含有量が上記範囲内であることが好ましい。<Second metal-containing material>
The above composition contains at least one selected from the group consisting of an inorganic substance (2) and an organic substance containing a second metal (second metal-containing substance). The content of the second metal-containing material in the composition is not particularly limited, but is generally preferably 0.001 to 80% by mass with respect to the total solid content of the composition. As the second metal-containing material, one type may be used alone, or two or more types may be used in combination. When two or more kinds of secondary metal-containing substances are used in combination, the total content is preferably within the above range.

第２の金属は、第１の金属とは異なる。ここで、「異なる」とは、金属元素の種類が異なることを意味する。
第２金属含有物の形態としては特に制限されず、第２の金属の単体（粒子）、第２金属のイオン、又は、第２の金属を含有する無機化合物（化合物の定義：化学変化によって2種又はそれ以上の元素の単体に分けることができる純粋物質をいう）若しくは有機物のいずれであってもよく、これらの混合物であってもよく、第２の金属の単体（粒子）、第２金属のイオン、及び、第２の金属を含有する無機物からなる群から選択される少なくとも１種が好ましい。第２金属含有物は、無機化合物及び／又は有機化合物と、第２の金属との複合体であってもよい。複合体としては、例えば、無機担体又は有機担体と、上記担体に担持された第２の金属とを有する金属担持担体、又は、第２の金属を含む無機化合物と上記無機化合物を覆うように配置された有機化合物とを含む有機無機複合体が好ましく、なかでも、無機担体と無機担体に担持された第２の金属とを有する金属担持無機担体がより好ましい。The second metal is different from the first metal. Here, "different" means that the types of metal elements are different.
The form of the second metal-containing substance is not particularly limited, and is an elemental substance (particle) of the second metal, an ion of the second metal, or an inorganic compound containing the second metal (compound definition: 2 due to chemical change). It may be either a pure substance that can be divided into simple substances of seeds or higher elements) or organic substances, and it may be a mixture of these, a simple substance (particle) of a second metal, a second metal. At least one selected from the group consisting of the above-mentioned ions and an inorganic substance containing a second metal is preferable. The second metal-containing substance may be a composite of an inorganic compound and / or an organic compound and the second metal. The composite is arranged so as to cover, for example, a metal-supporting carrier having an inorganic carrier or an organic carrier and a second metal supported on the carrier, or an inorganic compound containing the second metal and the inorganic compound. An organic-inorganic composite containing the above-mentioned organic compound is preferable, and a metal-supported inorganic carrier having an inorganic carrier and a second metal supported on the inorganic carrier is more preferable.

第２金属含有物は、固形物であっても、液状物であってもよいが、本発明の効果により優れる点で、第２金属含有物は固形物が好ましく、固形物としては、粒子（組成物中で粒子として存在するもの）が好ましい。 The second metal-containing material may be a solid material or a liquid material, but the second metal-containing material is preferably a solid material, and the solid material is particles ( Those present as particles in the composition) are preferred.

なかでも、本発明の効果がより優れる点で、第２金属含有物としては、無機物（２）が好ましい。無機物（２）は、上記無機物（１）における第１の金属の形態としては、上記のほか、無機物（１）の説明における第１の金属を第２の金属に置き換えたものも使用できる。 Among them, the inorganic substance (2) is preferable as the second metal-containing substance because the effect of the present invention is more excellent. As the inorganic substance (2), as the form of the first metal in the inorganic substance (1), in addition to the above, a substance in which the first metal in the description of the inorganic substance (1) is replaced with a second metal can also be used.

第２の金属としては、特に制限されないが、銀、銅、亜鉛、水銀、鉄、鉛、ビスマス、チタン、錫、ジルコニウム、アルミニウム、及び、ニッケル等が挙げられ、銀、銅、ジルコニウム、又は、亜鉛が好ましく、銀、銅、又は、亜鉛がより好ましく、銀、又は、銅が更に好ましい。
第２の金属を含有する有機物としては、例えば、第２の金属の塩が挙げられる。第２の金属の塩としては、酢酸塩、アセチルアセトン酸塩、金属アセチリド、（ｃｉｓ，ｃｉｓ−１，５−シクロオクタジエン）−１，１，１，５，５，５−ヘキサフルオロアセチルアセトン酸塩、ジエチルジチオカルバミン酸塩、７，７−ジメチル−１，１，１，２，２，３，３−ヘプタフルオロ−４，６−オクタンジオン酸塩、乳酸塩、シュウ酸塩、ペルフルオロ酪酸塩、ペルフルオロプロピオン酸塩、ピクリン酸塩、プロピオン酸塩、スルファジアジン塩、ｐ−トルエンスルホン酸塩、トリフルオロメタンスルホン酸塩、及び、トリフルオロ酢酸塩等が挙げられる。The second metal is not particularly limited, and examples thereof include silver, copper, zinc, mercury, iron, lead, bismuth, titanium, tin, zirconium, aluminum, and nickel, and silver, copper, zirconium, or Zinc is preferred, silver, copper or zinc is more preferred, silver or copper is even more preferred.
Examples of the organic substance containing the second metal include salts of the second metal. Examples of the second metal salt include acetate, acetylacetate, metal acetylide, (cis, cis-1,5-cyclooctadiene) -1,1,1,5,5,5-hexafluoroacetylacetoneate. , Diethyldithiocarbamate, 7,7-dimethyl-1,1,1,2,2,3,3-heptafluoro-4,6-octanedione, lactate, oxalate, perfluorobutyrate, perfluoro Examples thereof include propionate, picrate, propionate, sulfaziazine salt, p-toluenesulfonate, trifluoromethanesulfonate, trifluoroacetate and the like.

第２金属担持無機担体の無機担体としては、第１金属担持担体の無機担体として説明したものと同様のものが使用できる。なお、本明細書において、第２金属担持無機担体の無機担体を「第２の無機担体」という事がある。また、第２金属担持有機担体の有機担体としては、例えばポリマー粒子が挙げられる。
第２金属担持無機担体の具体例としては、第２金属が担持された、金属担持ゼオライト、金属担持アパタイト、金属担持ガラス、金属担持リン酸ジルコニウム、又は、金属担持ケイ酸カルシウムが好ましく、金属担持アパタイト、又は、金属担持ガラスがより好ましく、金属担持ガラスが更に好ましい。As the inorganic carrier of the second metal-supporting inorganic carrier, the same as those described as the inorganic carrier of the first metal-supporting carrier can be used. In the present specification, the inorganic carrier of the second metal-supported inorganic carrier may be referred to as "second inorganic carrier". Further, examples of the organic carrier of the second metal-supported organic carrier include polymer particles.
Specific examples of the second metal-supported inorganic carrier are metal-supported zeolite, metal-supported apatite, metal-supported glass, metal-supported zirconium phosphate, or metal-supported calcium silicate, preferably metal-supported. Apatite or metal-supported glass is more preferable, and metal-supported glass is even more preferable.

第２金属含有物が粒子である場合、第２金属含有物の平均粒径としては、特に制限されないが、一般に、０．０１μｍ以上が好ましく、０．０５μｍ以上がより好ましく、２０μｍ以下が好ましく、１５μｍ以下がより好ましい。
なお、第２金属含有粒子の平均粒径の測定及び調整は、既に説明した無機物（１）の粒子の平均粒径の測定及び調整方法を使用できる。When the second metal-containing material is particles, the average particle size of the second metal-containing material is not particularly limited, but is generally preferably 0.01 μm or more, more preferably 0.05 μm or more, and preferably 20 μm or less. More preferably, it is 15 μm or less.
For the measurement and adjustment of the average particle size of the second metal-containing particles, the method for measuring and adjusting the average particle size of the particles of the inorganic substance (1) already described can be used.

＜その他の成分＞
上記組成物は、無機物（１）及び第２金属含有物以外の成分を含有することが好ましい。無機物（１）及び第２金属含有物以外の成分としては、溶剤、リン化合物、及び、親水性成分が挙げられる。また、上記組成物は、酸性材料、重合開始剤、分散剤、触媒、界面活性剤、香料、造膜剤、及び、有機系抗菌剤等を含有してもよい。以下では、上記各成分について説明する。<Other ingredients>
The composition preferably contains components other than the inorganic substance (1) and the second metal-containing substance. Examples of the components other than the inorganic substance (1) and the second metal-containing substance include a solvent, a phosphorus compound, and a hydrophilic component. In addition, the above composition may contain an acidic material, a polymerization initiator, a dispersant, a catalyst, a surfactant, a fragrance, a film-forming agent, an organic antibacterial agent and the like. Hereinafter, each of the above components will be described.

（溶剤）
上記組成物は溶剤を含有することが好ましい。
溶剤としては特に制限されず、水及び／又は有機溶剤が挙げられる。有機溶剤としては、メタノール、エタノール、ｎ−プロパノール、イソプロパノール、ｎ−ブタノール、イソブタノール、ｓｅｃ−ブタノール、ｔｅｒｔ−ブタノール、ｎ−ペンタノール、イソペンタノール、フェニルエチルアルコール、カプリルアルコール、ラウリルアルコール、及びミリスチルアルコール等のアルコール系溶剤；メチルセロソルブ、エチルセロソルブ、エチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールジメチルエーテル、プロピレングリコールジエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノブチルエーテル、テトラエチレングリコールモノブチルエーテル、及びジプロピレングリコールモノブチルエーテル等のグリコールエーテル系溶剤；ベンゼン、トルエン、キシレン、及びエチルベンゼン等の芳香族炭化水素系溶剤；シクロペンタン、シクロヘキサン、メチルシクロヘキサン、及びエチルシクロヘキサン等の脂環族炭化水素系溶剤；テトラヒドロフラン、ジオキサン、ジイソプロピルエーテル、及びジ−ｎ−ブチルエーテル等のエーテル系溶剤；アセトン、メチルエチルケトン、及びメチルイソブチルケトン等のケトン系溶剤；酢酸メチル、酢酸エチル、酢酸ｎ−プロピル、酢酸イソプロピル、酢酸ｎ−ブチル、酢酸イソブチル、酢酸ｎ−アミル、酢酸イソアミル、酢酸ヘキシル、プロピオン酸エチル、及びプロピオン酸ブチル等のエステル系溶剤；１０％安息香酸デナトニウムアルコール溶液、ゲラニオール、八アセチル化ショ糖、ブルシン、リナロール、リナリールアセテート、及び酢酸等の親水性溶剤；が挙げられる。溶剤は１種を単独で用いても、２種以上を併用してもよい。(solvent)
The composition preferably contains a solvent.
The solvent is not particularly limited, and examples thereof include water and / or an organic solvent. Organic solvents include methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, sec-butanol, tert-butanol, n-pentanol, isopentanol, phenylethyl alcohol, capryl alcohol, lauryl alcohol, and Alcohol-based solvents such as myristyl alcohol; methyl cellosolve, ethyl cellosolve, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol dimethyl ether, propylene glycol diethyl ether, ethylene Glycol ether solvents such as glycol monobutyl ether, diethylene glycol monobutyl ether, triethylene glycol monobutyl ether, tetraethylene glycol monobutyl ether, and dipropylene glycol monobutyl ether; aromatic hydrocarbon solvents such as benzene, toluene, xylene, and ethylbenzene; Alicyclic hydrocarbon solvents such as cyclopentane, cyclohexane, methylcyclohexane, and ethylcyclohexane; ether solvents such as tetrahydrofuran, dioxane, diisopropyl ether, and di-n-butyl ether; acetone, methylethylketone, methylisobutylketone, etc. Ketone solvents; ester solvents such as methyl acetate, ethyl acetate, n-propyl acetate, isopropyl acetate, n-butyl acetate, isobutyl acetate, n-amyl acetate, isoamyl acetate, hexyl acetate, ethyl propionate, and butyl propionate. ; 10% denatonium benzoate alcohol solution, geraniol, octaacetylated sucrose, burcin, linalol, linaryl acetate, hydrophilic solvents such as acetic acid; One type of solvent may be used alone, or two or more types may be used in combination.

なかでも、本発明の効果により優れる観点から、組成物は、水、及び、アルコールからなる群から選択される少なくとも１種を含有することが好ましい。
組成物がアルコールを含有せず、水を含有する場合、組成物中の水の含有量としては特に制限されないが、組成物の全質量に対して、０．０１〜９９．９９９質量％が好ましい。
組成物が水を含有せず、アルコールを含有する場合、組成物中のアルコールの含有量としては特に制限されないが、組成物の全質量に対して、０．０１〜９９．９９９質量％が好ましい。
組成物が水とアルコールとを含有する場合、組成物中における水とアルコールの合計含有量としては特に制限されないが、組成物の全質量に対して、０．０１〜９９．９９９質量％が好ましい。この場合、水の含有量に対する、アルコールの含有量の含有質量比（アルコール／水）としては特に制限されないが１００〜０．０１が好ましい。Among them, from the viewpoint of being more excellent in the effect of the present invention, the composition preferably contains at least one selected from the group consisting of water and alcohol.
When the composition does not contain alcohol and contains water, the content of water in the composition is not particularly limited, but is preferably 0.01 to 99.999% by mass with respect to the total mass of the composition. ..
When the composition does not contain water and contains alcohol, the content of alcohol in the composition is not particularly limited, but is preferably 0.01 to 99.999% by mass with respect to the total mass of the composition. ..
When the composition contains water and alcohol, the total content of water and alcohol in the composition is not particularly limited, but is preferably 0.01 to 99.999% by mass with respect to the total mass of the composition. .. In this case, the content-mass ratio (alcohol / water) of the alcohol content to the water content is not particularly limited, but is preferably 100 to 0.01.

アルコールとしては上記で説明したものが使用できるが、溶剤へ第１の金属及び第２の金属がより溶出しにくく、結果として、より優れた本発明の効果が得られる点で、エタノール、又は、イソプロピルアルコールがより好ましい。 As the alcohol, those described above can be used, but ethanol or ethanol or alcohol can be used in that the first metal and the second metal are less likely to elute into the solvent, and as a result, more excellent effects of the present invention can be obtained. Isopropyl alcohol is more preferred.

上記組成物が溶剤を含有する場合、組成物の固形分としては、特に制限されないが、組成物全質量に対して、０．０００１〜５０質量％が好ましい。溶剤は１種を単独で用いても、２種以上を併用してもよい。２種以上の溶剤を併用する場合、合計含有量が上記範囲内であることが好ましい。 When the composition contains a solvent, the solid content of the composition is not particularly limited, but is preferably 0.0001 to 50% by mass with respect to the total mass of the composition. One type of solvent may be used alone, or two or more types may be used in combination. When two or more kinds of solvents are used in combination, the total content is preferably within the above range.

（第３の金属を含有する無機物）
組成物は、第３の金属を含有する無機物（以下、「無機物（３）」又は「第３金属含有物」ともいう。）を含有することが好ましい。組成物中における無機物（３）の含有量としては特に制限されないが、一般に、組成物の全固形分に対して、０．０００１〜３０質量％が好ましい。
無機物（３）に含有される第３の金属は、第１の金属、及び、第２の金属のいずれとも異なれば、特に制限されないが、例えば、銀、銅、亜鉛、水銀、鉄、鉛、ビスマス、チタン、錫、ジルコニウム、アルミニウム、及び、ニッケル等が挙げられ、ジルコニウム、アルミニウム、又は、チタンが好ましく、ジルコニウムがより好ましい。
なお、無機物（３）は、は１種を単独で用いても、２種以上を併用してもよい。２種以上のリン化合物を併用する場合には、合計含有量が上記範囲内であることが好ましい。(Inorganic substance containing a third metal)
The composition preferably contains an inorganic substance containing a third metal (hereinafter, also referred to as "inorganic substance (3)" or "third metal-containing substance"). The content of the inorganic substance (3) in the composition is not particularly limited, but is generally preferably 0.0001 to 30% by mass with respect to the total solid content of the composition.
The third metal contained in the inorganic substance (3) is not particularly limited as long as it is different from any of the first metal and the second metal, and is not particularly limited, but for example, silver, copper, zinc, mercury, iron, lead, and the like. Examples thereof include bismuth, titanium, tin, zirconium, aluminum, and nickel, with zirconium, aluminum, or titanium being preferred, and zirconium being more preferred.
As the inorganic substance (3), one type may be used alone, or two or more types may be used in combination. When two or more kinds of phosphorus compounds are used in combination, the total content is preferably within the above range.

無機物（３）は、リン原子を含有することが好ましい。リン原子を含有する無機物（３）としては特に制限されいが、アンモニア等の塩基性の悪臭物質をイオン交換して取り込み、より優れた本発明の効果が得られる点で、層状構造を有するリン酸金属塩が好ましい。層状構造を有するリン酸金属塩としては、例えば、リン酸ジルコニウム、リン酸チタン、及び、トリポリリン酸二水素アルミニウム等が挙げられる。すなわち、組成物は、リン酸ジルコニウム、リン酸チタン、及び、トリポリリン酸二水素アルミニウムからなる群から選択される少なくとも１種のリン化合物を含有することが好ましく、リン酸ジルコニウムを含有することがより好ましい。 The inorganic substance (3) preferably contains a phosphorus atom. The inorganic substance (3) containing a phosphorus atom is not particularly limited, but phosphorus having a layered structure is obtained in that a basic malodorous substance such as ammonia can be ion-exchanged and incorporated to obtain a better effect of the present invention. Acid metal salts are preferred. Examples of the metal phosphate having a layered structure include zirconium phosphate, titanium phosphate, and aluminum dihydrogen tripolyphosphate. That is, the composition preferably contains at least one phosphorus compound selected from the group consisting of zirconium phosphate, titanium phosphate, and aluminum dihydrogen tripolyphosphate, and more preferably contains zirconium phosphate. preferable.

（親水性成分）
上記組成物は、親水性バインダー前駆体及び親水性バインダーからなる群より選ばれる親水性成分を含むことが好ましい。
なお、親水性バインダー前駆体とは、縮合及び重合等の硬化反応により親水性バインダーを形成可能な材料を意味する。
また、親水性バインダーは、無機物（１）及び第２金属含有物を支持可能な親水性の膜を形成できる材料を意味する。親水性バインダーとしては、ガラス基板上に上記親水性バインダーからなる膜を形成した場合、例えば、水接触角が６０°以下となるもの好ましく、５０°以下となるものが好ましい。水接触角の下限は特に制限されないが、一般に５°以上が好ましい。
なお、水接触角は、ＪＩＳ Ｒ ３２５７：１９９９の静滴法に基づいて測定を行う。測定には、協和界面科学株式会社製ＦＡＭＭＳ ＤＭ−７０１を用いる。(Hydrophilic component)
The composition preferably contains a hydrophilic component selected from the group consisting of a hydrophilic binder precursor and a hydrophilic binder.
The hydrophilic binder precursor means a material capable of forming a hydrophilic binder by a curing reaction such as condensation and polymerization.
Further, the hydrophilic binder means a material capable of forming a hydrophilic film capable of supporting the inorganic substance (1) and the second metal-containing substance. As the hydrophilic binder, when a film made of the above hydrophilic binder is formed on a glass substrate, for example, a water contact angle of 60 ° or less is preferable, and a hydrophilic binder of 50 ° or less is preferable. The lower limit of the water contact angle is not particularly limited, but is generally preferably 5 ° or more.
The water contact angle is measured based on the static drip method of JIS R 3257: 1999. For the measurement, FAMMS DM-701 manufactured by Kyowa Interface Science Co., Ltd. is used.

親水性成分としては、なかでも、堅牢性により優れる点で、シリケート系化合物、親水性基を有するモノマー（以下、「親水性モノマー」ともいう。）、及び親水性基を有するポリマー（以下、「親水性ポリマー」ともいう。）からなる群から選択される少なくとも１種が好ましい。
なお、親水性基を有するモノマーとは、親水性基と重合性基とを有する化合物を意味する。親水性モノマーは、上記組成物が後述する重合開始剤を含む場合、重合して親水性ポリマーを形成する。
以下に、シリケート系化合物、親水性モノマー、及び、親水性ポリマーについて、それぞれ説明する。Among the hydrophilic components, a silicate-based compound, a monomer having a hydrophilic group (hereinafter, also referred to as “hydrophilic monomer”), and a polymer having a hydrophilic group (hereinafter, “”, are excellent in toughness. At least one selected from the group consisting of "hydrophilic polymers") is preferred.
The monomer having a hydrophilic group means a compound having a hydrophilic group and a polymerizable group. When the above composition contains a polymerization initiator described later, the hydrophilic monomer is polymerized to form a hydrophilic polymer.
The silicate-based compound, the hydrophilic monomer, and the hydrophilic polymer will be described below.

・シリケート系化合物
本明細書において、シリケート系化合物とは、ケイ素原子に加水分解性基が結合した化合物、その加水分解物、及びその加水分解縮合物からなる群から選択される化合物であり、例えば、下記式（１）で表される化合物、その加水分解物、及びその加水分解縮合物からなる群から選択される少なくとも１種が挙げられる。
式（１） Ｓｉ−（ＯＲ）４
上記式（１）中、Ｒは、炭素数１〜４のアルキル基を表し、同一でも異なっていてもよい。-Sylicate-based compound In the present specification, the silicate-based compound is a compound selected from the group consisting of a compound in which a hydrolyzable group is bonded to a silicon atom, a hydrolyzate thereof, and a hydrolyzable condensate thereof, for example. , At least one selected from the group consisting of a compound represented by the following formula (1), a hydrolyzate thereof, and a hydrolyzed condensate thereof.
Equation (1) Si- (OR) 4
In the above formula (1), R represents an alkyl group having 1 to 4 carbon atoms, and may be the same or different.

上記式（１）で表される化合物としては、テトラメチルシリケート、テトラエチルシリケート、テトラ−ｎ−プロピルシリケート、テトラ−ｉ−プロピルシリケート、テトラ−ｎ−ブチルシリケート、テトラ−ｉ−ブチルシリケート、テトラ−ｔ−ブチルシリケート、メチルエチルシリケート、メチルプロピルシリケート、メチルブチルシリケート、エチルプロピルシリケート、及びプロピルブチルシリケート等が挙げられる。 Examples of the compound represented by the above formula (1) include tetramethyl silicate, tetraethyl silicate, tetra-n-propyl silicate, tetra-i-propyl silicate, tetra-n-butyl silicate, tetra-i-butyl silicate, and tetra-. Examples thereof include t-butyl silicate, methyl ethyl silicate, methyl propyl silicate, methyl butyl silicate, ethyl propyl silicate, propyl butyl silicate and the like.

式（１）で表される化合物の加水分解物とは、式（１）で表される化合物中のＯＲ基が加水分解して得られる化合物を意図する。なお、上記加水分解物は、ＯＲ基のすべてが加水分解されているもの（完全加水分解物）であっても、ＯＲ基の一部が加水分解されているもの（部分加水分解物）であってもよい。つまり、上記加水分解物は、完全加水分解物、部分加水分解物、又は、これらの混合物であってもよい。
また、式（１）で表される化合物の加水分解縮合物とは、式（１）で表される化合物中のＯＲ基が加水分解し、得られた加水分解物を縮合して得られる化合物を意図する。なお、上記加水分解縮合物としては、すべてのＯＲ基が加水分解され、かつ、加水分解物がすべて縮合されているもの（完全加水分解縮合物）であっても、一部のＯＲ基が加水分解され、一部の加水分解物が縮合しているもの（部分加水分解縮合物）であってもよい。つまり、上記加水分解縮合物は、完全加水分解縮合物、部分加水分解縮合物、又は、これらの混合物であってもよい。
なお、加水分解縮合物の縮合度としては、１〜１００が好ましく、１〜２０がより好ましく、３〜１５が更に好ましい。The hydrolyzate of the compound represented by the formula (1) is intended to be a compound obtained by hydrolyzing the OR group in the compound represented by the formula (1). The hydrolyzate is a product in which all of the OR groups are hydrolyzed (complete hydrolyzate), but a part of the OR groups is hydrolyzed (partial hydrolyzate). You may. That is, the hydrolyzate may be a complete hydrolyzate, a partial hydrolyzate, or a mixture thereof.
The hydrolyzate of the compound represented by the formula (1) is a compound obtained by hydrolyzing the OR group in the compound represented by the formula (1) and condensing the obtained hydrolyzate. Intended. As the above-mentioned hydrolyzed condensate, even if all the OR groups are hydrolyzed and all the hydrolyzated products are condensed (completely hydrolyzed condensate), some OR groups are hydrolyzed. It may be decomposed and a part of the hydrolyzate is condensed (partially hydrolyzed condensate). That is, the hydrolyzed condensate may be a completely hydrolyzed condensate, a partially hydrolyzed condensate, or a mixture thereof.
The degree of condensation of the hydrolyzed condensate is preferably 1 to 100, more preferably 1 to 20, and even more preferably 3 to 15.

式（１）で表される化合物は、水成分とともに混合されることにより、少なくとも一部が加水分解された状態となる。式（１）で表される化合物の加水分解物は、式（１）で表される化合物を水成分と反応させ、ケイ素に結合したＯＲ基をヒドロキシ基に変化させることにより得られる。加水分解に際しては必ずしも全てのＯＲ基が反応する必要はないが、塗布後に親水性を発揮するためにはなるべく多くのＯＲ基が加水分解されることが好ましい。また、加水分解に際して最低限必要な水成分の量は式（１）で表される化合物のＯＲ基と等しいモル量となるが、反応を円滑に進めるには大過剰の量の水が存在することが好ましい。 The compound represented by the formula (1) is in a state of being hydrolyzed at least in part by being mixed with the water component. The hydrolyzate of the compound represented by the formula (1) can be obtained by reacting the compound represented by the formula (1) with a water component and changing the OR group bonded to silicon to a hydroxy group. It is not always necessary for all the OR groups to react during hydrolysis, but it is preferable that as many OR groups as possible are hydrolyzed in order to exhibit hydrophilicity after coating. The minimum amount of water component required for hydrolysis is the same molar amount as the OR group of the compound represented by the formula (1), but there is a large excess amount of water to facilitate the reaction. Is preferable.

なお、上記シリケート系化合物の加水分解反応は室温でも進行するが、反応促進のために加温してもよい。また反応時間は長い方がより反応が進むため好ましい。また、触媒の存在下であれば半日程度でも加水分解物を得ることが可能である。
なお、一般に加水分解反応は可逆反応であり、系から水が除かれると上記シリケート系化合物の加水分解物はヒドロキシ基間で縮合を開始してしまう。従って、上記シリケート系化合物に大過剰の水を反応させて加水分解物の水溶液を得た場合、そこから加水分解物を無理に単離せずに水溶液のまま用いることが好ましい。Although the hydrolysis reaction of the silicate-based compound proceeds even at room temperature, it may be heated to promote the reaction. Further, the longer the reaction time is, the more the reaction proceeds, which is preferable. Further, in the presence of a catalyst, it is possible to obtain a hydrolyzate in about half a day.
In general, the hydrolysis reaction is a reversible reaction, and when water is removed from the system, the hydrolyzate of the silicate-based compound starts condensation between hydroxy groups. Therefore, when a large excess of water is reacted with the silicate-based compound to obtain an aqueous solution of the hydrolyzate, it is preferable to use the hydrolyzate as it is without forcibly isolating it.

上記シリケート系化合物の好適態様としては、式（Ｘ）で表される化合物が挙げられる。 Preferable embodiments of the silicate-based compound include a compound represented by the formula (X).

ここで、式（Ｘ）中、Ｒ１〜Ｒ４はそれぞれ独立に炭素数１〜４のアルキル基を表す。また、ｎは２〜１００の整数を表す。
ｎは、３〜１５が好ましく、５〜１０がより好ましい。Here, in the formula (X), R 1 to R 4 independently represent alkyl groups having 1 to 4 carbon atoms. Further, n represents an integer of 2 to 100.
n is preferably 3 to 15, more preferably 5 to 10.

上記シリケート系化合物の市販品としては、例えば、コルコート社製「エチルシリケート４８」、及び三菱化学社製「ＭＫＣシリケート ＭＳ５１」等が挙げられる。
なお、シリケート系化合物は１種を単独で用いても、２種以上を併用してもよい。Examples of commercially available products of the silicate-based compound include "ethyl silicate 48" manufactured by Corcote and "MKC silicate MS51" manufactured by Mitsubishi Chemical Corporation.
The silicate-based compound may be used alone or in combination of two or more.

・親水性を有するモノマー（親水性モノマー）
親水性基としては特に制限されず、例えば、ポリオキシアルキレン基（例えば、ポリオキシエチレン基、ポリオキシプロピレン基、オキシエチレン基とオキシプロピレン基がブロック又はランダム結合したポリオキシアルキレン基）、アミノ基、カルボキシ基、カルボキシ基のアルカリ金属塩、ヒドロキシ基、アルコキシ基、アミド基、カルバモイル基、スルホンアミド基、スルファモイル基、スルホン酸基、及び、スルホン酸基のアルカリ金属塩等が挙げられる。親水性モノマー中における親水性基の数は特に制限されないが、得られる膜がより親水性を示す点より、２個以上が好ましく、２〜６個がより好ましく、２〜３個が更に好ましい。-Hydrophilic monomer (hydrophilic monomer)
The hydrophilic group is not particularly limited, and is, for example, a polyoxyalkylene group (for example, a polyoxyethylene group, a polyoxypropylene group, a polyoxyalkylene group in which an oxyethylene group and an oxypropylene group are blocked or randomly bonded), an amino group. , Carboxylic group, alkali metal salt of carboxy group, hydroxy group, alkoxy group, amide group, carbamoyl group, sulfonamide group, sulfamoyl group, sulfonic acid group, alkali metal salt of sulfonic acid group and the like. The number of hydrophilic groups in the hydrophilic monomer is not particularly limited, but 2 or more is preferable, 2 to 6 is more preferable, and 2 to 3 is more preferable from the viewpoint that the obtained film exhibits more hydrophilicity.

重合性基としては特に制限されず、例えば、ラジカル重合性基、カチオン重合性基、及びアニオン重合性基等が挙げられる。ラジカル重合性基としては、（メタ）アクリロイル基、アクリルアミド基、ビニル基、スチリル基、及び、アリル基等が挙げられる。カチオン重合性基としては、ビニルエーテル基、オキシラニル基、及び、オキセタニル基等が挙げられる。重合性基としては、なかでも、（メタ）アクリロイル基が好ましい。
親水性モノマー中における重合性基の数は特に制限されないが、得られる膜の機械的強度がより優れる点で、２個以上が好ましく、２〜６個がより好ましく、２〜３個が更に好ましい。The polymerizable group is not particularly limited, and examples thereof include a radical polymerizable group, a cationically polymerizable group, and an anionic polymerizable group. Examples of the radically polymerizable group include a (meth) acryloyl group, an acrylamide group, a vinyl group, a styryl group, an allyl group and the like. Examples of the cationically polymerizable group include a vinyl ether group, an oxylanyl group, an oxetanyl group and the like. As the polymerizable group, a (meth) acryloyl group is particularly preferable.
The number of polymerizable groups in the hydrophilic monomer is not particularly limited, but 2 or more are preferable, 2 to 6 are more preferable, and 2 to 3 are further preferable in terms of more excellent mechanical strength of the obtained membrane. ..

親水性モノマーの重合により形成される親水性ポリマーの主鎖の構造は特に制限されず、例えば、ポリウレタン、ポリ（メタ）アクリレート、ポリスチレン、ポリエステル、ポリアミド、ポリイミド、及び、ポリウレア等が挙げられる。
親水性モノマーは１種を単独で用いても、２種以上を併用してもよい。The structure of the main chain of the hydrophilic polymer formed by the polymerization of the hydrophilic monomer is not particularly limited, and examples thereof include polyurethane, poly (meth) acrylate, polystyrene, polyester, polyamide, polyimide, and polyurea.
One type of hydrophilic monomer may be used alone, or two or more types may be used in combination.

（親水性を有するポリマー（親水性ポリマー））
親水性ポリマーとしては特に制限されず、公知のものを使用できる。なお、親水性基の定義は、上述したとおりである。
親水性ポリマーとしては、上記親水性モノマーを重合して得られるポリマーが挙げられる。それ以外にも、例えば、セルロース系化合物が挙げられる。セルロース系化合物とは、セルロースを母核とする化合物を意図し、例えば、カルボキシメチルセルロースのほか、トリアセチルセルロースを原料とするナノファイバー等が挙げられる。
親水性ポリマーの重量平均分子量は特に制限されないが、溶解性等取扱い性がより優れる点で、１，０００〜１，０００，０００が好ましく、１０，０００〜５００，０００がより好ましい。なお、本明細書において、重量平均分子量は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）測定でのポリスチレン換算値として定義される。
親水性ポリマーは１種を単独で用いても、２種以上を併用してもよい。(Polymer with hydrophilicity (hydrophilic polymer))
The hydrophilic polymer is not particularly limited, and known ones can be used. The definition of the hydrophilic group is as described above.
Examples of the hydrophilic polymer include a polymer obtained by polymerizing the above hydrophilic monomer. Other examples include cellulosic compounds. The cellulosic compound is intended to be a compound having cellulose as a mother nucleus, and examples thereof include carboxymethyl cellulose and nanofibers made from triacetyl cellulose as a raw material.
The weight average molecular weight of the hydrophilic polymer is not particularly limited, but is preferably 1,000 to 1,000,000, more preferably 10,000 to 500,000 in terms of excellent handleability such as solubility. In the present specification, the weight average molecular weight is defined as a polystyrene-equivalent value in gel permeation chromatography (GPC) measurement.
One type of hydrophilic polymer may be used alone, or two or more types may be used in combination.

上記組成物中における親水性成分の含有量としては特に制限されないが、組成物の全固形分に対して、０．５〜９９．８質量％が好ましく、１〜９０質量％がより好ましく、１．５〜９９質量％が更に好ましい。
なお、親水性成分は１種を単独で用いても、２種以上を併用してもよい。２種以上の親水性成分を併用する場合、合計含有量が上記範囲内であることが好ましい。The content of the hydrophilic component in the above composition is not particularly limited, but is preferably 0.5 to 99.8% by mass, more preferably 1 to 90% by mass, based on the total solid content of the composition. .5 to 99% by mass is more preferable.
The hydrophilic component may be used alone or in combination of two or more. When two or more kinds of hydrophilic components are used in combination, the total content is preferably within the above range.

（酸性材料）
組成物は、酸性材料を含有してもよい。組成物中における酸性材料の含有量としては特に制限されないが、一般に、組成物の全質量に対して、０．０００１〜５０質量％が好ましい。酸性材料は１種を単独で用いても、２種以上を併用してもよい。２種以上の酸性材料を併用する場合には、合計含有量が上記範囲内であることが好ましい。(Acid material)
The composition may contain an acidic material. The content of the acidic material in the composition is not particularly limited, but is generally preferably 0.0001 to 50% by mass with respect to the total mass of the composition. One type of acidic material may be used alone, or two or more types may be used in combination. When two or more kinds of acidic materials are used in combination, the total content is preferably within the above range.

組成物が、酸性材料を含有すると、アンモニア等の塩基性の悪臭物質をより効率的に消臭できる。なかでも、組成物のｐＨが６．５以下となるよう、酸性材料の種類及び量が選択されることが好ましい。
酸性材料としては、リン酸、及び、硫酸等の無機酸；リンゴ酸、乳酸、酒石酸、サリチル酸、グルコン酸、アジピン酸、フィチン酸、フマル酸、コハク酸、アスコルビン酸、ソルビン酸、グリオキシル酸、メルドラム酸、グルタミン酸、ピクリン酸、アスパラギン酸、酢酸、ギ酸、及び、クエン酸等の有機酸；等が挙げられる。
なお、本明細書において、酸性材料は、上記リン化合物には含まれないものとする。When the composition contains an acidic material, basic malodorous substances such as ammonia can be deodorized more efficiently. Among them, it is preferable that the type and amount of the acidic material are selected so that the pH of the composition is 6.5 or less.
Acidic materials include phosphoric acid and inorganic acids such as sulfuric acid; malic acid, lactic acid, tartaric acid, salicylic acid, gluconic acid, adipic acid, phytic acid, fumaric acid, succinic acid, ascorbic acid, sorbic acid, glyoxylic acid, meldrum. Organic acids such as acids, glutamates, picric acids, aspartic acids, acetic acids, formic acids, and citric acids; and the like.
In addition, in this specification, an acidic material is not included in the said phosphorus compound.

（重合開始剤）
上記組成物が親水性モノマーを含有する場合、上記組成物は、重合開始剤を含有することが好ましい。
重合開始剤としては特に制限されず、公知の重合開始剤を用いることができる。
重合開始剤としては、例えば、熱重合開始剤、及び、光重合開始剤等が挙げられる。
重合開始剤としては、例えば、ベンゾフェノン、及び、フェニルフォスフィンオキシド等の芳香族ケトン類；α−ヒドロキシアルキルフェノン系化合物（ＢＡＳＦ社製、ＩＲＧＡＣＵＲＥ１８４、１２７、２９５９、及び、ＤＡＲＯＣＵＲ１１７３等）；フェニルフォスフィンオキシド系化合物（モノアシルフォスフィンオキサイド：ＢＡＳＦ社製 ＩＲＧＡＣＵＲＥ ＴＰＯ、ビスアシルフォスフィンオキサイド：ＢＡＳＦ社製 ＩＲＧＡＣＵＲＥ ８１９）；等が挙げられる。
なかでも、反応効率の観点で、光重合開始剤が好ましい。(Polymer initiator)
When the composition contains a hydrophilic monomer, the composition preferably contains a polymerization initiator.
The polymerization initiator is not particularly limited, and a known polymerization initiator can be used.
Examples of the polymerization initiator include thermal polymerization initiators and photopolymerization initiators.
Examples of the polymerization initiator include benzophenone and aromatic ketones such as phenylphosphine oxide; α-hydroxyalkylphenone compounds (manufactured by BASF, IRGACURE184, 127, 2959, and DAROCUR1173, etc.); phenylphosphine. Oxide compounds (monoacylphosphine oxide: IRGACURE TPO manufactured by BASF, bisacylphosphine oxide: IRGACURE 819 manufactured by BASF); and the like.
Of these, a photopolymerization initiator is preferable from the viewpoint of reaction efficiency.

上記組成物中における重合開始剤の含有量としては特に制限されないが、親水性モノマー１００質量部に対して、０．１〜１５質量部が好ましく、１〜６質量部がより好ましい。
なお、重合開始剤は、１種を単独で用いても、２種以上を併用してもよい。２種以上の重合開始剤を併用する場合、合計含有量が上記範囲内であることが好ましい。The content of the polymerization initiator in the above composition is not particularly limited, but is preferably 0.1 to 15 parts by mass, more preferably 1 to 6 parts by mass with respect to 100 parts by mass of the hydrophilic monomer.
The polymerization initiator may be used alone or in combination of two or more. When two or more kinds of polymerization initiators are used in combination, the total content is preferably within the above range.

（分散剤）
上記組成物は分散剤を含有するのが好ましい。
分散剤としては特に制限されず、公知の分散剤が使用できる。
組成物は、分散剤として、ノニオン系分散剤、及び、アニオン系分散剤からなる群から選択される少なくとも１種を含有するのが好ましい。無機物（１）及び第２金属含有物に対する親和性の観点から、カルボキシ基、リン酸基、及び、水酸基等のアニオン性の極性基を有する分散剤（アニオン系分散剤）がより好ましい。
アニオン系分散剤としては、市販品を使用できる。その具体例としては、ＢＹＫ社の商品名ＤＩＳＰＥＲＢＹＫ（登録商標）−１１０、−１１１、−１１６、−１４０、−１６１、−１６２、−１６３、−１６４、−１７０、−１７１、−１７４、−１８０、−２０１２、及び−２０１３等が好適に挙げられる。また、ＢＡＳＦ社の商品名ＥＦＫＡ−７７０１が挙げられる。
また、ノニオン系分散剤としてはＢＹＫ社の商品名ＤＩＳＰＥＲＢＹＫ−２０１０が挙げられる。(Dispersant)
The composition preferably contains a dispersant.
The dispersant is not particularly limited, and a known dispersant can be used.
The composition preferably contains at least one selected from the group consisting of a nonionic dispersant and an anionic dispersant as the dispersant. From the viewpoint of affinity for the inorganic substance (1) and the second metal-containing substance, a dispersant having an anionic polar group such as a carboxy group, a phosphoric acid group, and a hydroxyl group (anionic dispersant) is more preferable.
As the anionic dispersant, a commercially available product can be used. Specific examples thereof include BYK's trade name DISPERBYK (registered trademark) -110, -111, -116, -140, -161, -162, -163, -164, -170, -171, -174,-. 180, -2012, -2013 and the like are preferably mentioned. In addition, BASF's trade name EFKA-7701 can be mentioned.
Moreover, as a nonionic dispersant, the trade name DISPERBYK-2010 of BYK can be mentioned.

上記組成物中における分散剤の含有量としては特に制限されないが、組成物の全固形分に対して、２０質量％以下が好ましく、１０質量％以下がより好ましく、８質量％以下が更に好ましい。
分散剤は、１種を単独で用いても、２種以上を併用してもよい。２種以上の分散剤を併用する場合、合計含有量が上記範囲内であることが好ましい。The content of the dispersant in the composition is not particularly limited, but is preferably 20% by mass or less, more preferably 10% by mass or less, and further preferably 8% by mass or less, based on the total solid content of the composition.
The dispersant may be used alone or in combination of two or more. When two or more kinds of dispersants are used in combination, the total content is preferably within the above range.

（触媒）
上記組成物がシリケート系化合物を含む場合、組成物は、シリケート系化合物の縮合を促進する触媒（以下「反応触媒」ともいう。）を含有してもよい。(catalyst)
When the composition contains a silicate-based compound, the composition may contain a catalyst that promotes condensation of the silicate-based compound (hereinafter, also referred to as "reaction catalyst").

触媒は特に制限されないが、アルカリ触媒及び有機金属触媒等が挙げられる。
アルカリ触媒の例としては、水酸化ナトリウム、水酸化カリウム、及び、水酸化テトラメチルアンモニウム等が挙げられる。
有機金属触媒の例としては、アルミニウムビス（エチルアセトアセテート）モノ（アセチルアセトネート）、アルミニウムトリス（アセチルアセトネート）、及びアルミニウムエチルアセトアセテートジイソプロピレート等のアルミキレート化合物、ジルコニウムテトラキス（アセチルアセトネート）、及びジルコニウムビス（ブトキシ）ビス（アセチルアセトネート）等のジルコニウムキレート化合物、チタニウムテトラキス（アセチルアセトネート）、及びチタニウムビス（ブトキシ）ビス（アセチルアセトネート）等のチタンキレート化合物、並びに、ジブチルスズジアセテート、ジブチルスズジラウレート、及びジブチルスズジオクチエート等の有機スズ化合物等が挙げられる。
触媒の種類は特に制限されないが、有機金属触媒が好ましく、なかでも、アルミキレート化合物、チタンキレート化合物、又は、ジルコニウムキレート化合物がより好ましく、アルミキレート化合物が更に好ましい。The catalyst is not particularly limited, and examples thereof include an alkali catalyst and an organometallic catalyst.
Examples of the alkaline catalyst include sodium hydroxide, potassium hydroxide, tetramethylammonium hydroxide and the like.
Examples of organometallic catalysts include aluminum bis (ethylacetacetate) mono (acetylacetoneate), aluminumtris (acetylacetoneate), aluminum chelate compounds such as aluminum ethylacetate acetate diisopropirate, and zirconium tetrakis (acetylacetoneate). ), And zirconium chelate compounds such as zirconium bis (butoxy) bis (acetylacetone), titanium chelate compounds such as titanium tetrakis (acetylacetone), and titanium bis (butoxy) bis (acetylacetone), and dibutyltindi Examples thereof include organic tin compounds such as acetate, dibutyltin dilaurate, and dibutyltin dioctate.
The type of catalyst is not particularly limited, but an organic metal catalyst is preferable, and among them, an aluminum chelate compound, a titanium chelate compound, or a zirconium chelate compound is more preferable, and an aluminum chelate compound is further preferable.

触媒の含有量は、組成物の全固形分１００質量部に対して、０．０１〜２０質量部が好ましく、０．０２〜１５質量部がより好ましく、０．０３〜１０質量部が更に好ましい。
なお、触媒は１種を単独で用いても、２種以上を併用してもよい。２種以上の触媒を併用する場合、合計含有量が上記範囲内であることが好ましい。The content of the catalyst is preferably 0.01 to 20 parts by mass, more preferably 0.02 to 15 parts by mass, still more preferably 0.03 to 10 parts by mass, based on 100 parts by mass of the total solid content of the composition. ..
The catalyst may be used alone or in combination of two or more. When two or more kinds of catalysts are used in combination, the total content is preferably within the above range.

（界面活性剤）
上記組成物は、界面活性剤を含有してもよい。界面活性剤は組成物の塗布性を向上する作用を有する。
界面活性剤としては特に制限されず、例えば、ノニオン性界面活性剤、アニオン性界面活性剤、カチオン性界面活性剤、及び、両性型界面活性剤等が挙げられる。
界面活性剤の含有量としては、組成物の全固形分１００質量部に対して、０．００１質量部以上が好ましい。なお、界面活性剤の含有量の上限値は特に制限されないが、組成物の全固形分１００質量部に対して、１０質量部以下が好ましく、５質量部以下がより好ましく、４質量部以下が更に好ましい。
なお、界面活性剤は１種を単独で用いても、２種以上を併用してもよい。２種以上を併用する場合は、それらの合計含有量が上記範囲内であることが好ましい。(Surfactant)
The composition may contain a surfactant. Surfactants have the effect of improving the coatability of the composition.
The surfactant is not particularly limited, and examples thereof include a nonionic surfactant, an anionic surfactant, a cationic surfactant, and an amphoteric surfactant.
The content of the surfactant is preferably 0.001 part by mass or more with respect to 100 parts by mass of the total solid content of the composition. The upper limit of the content of the surfactant is not particularly limited, but is preferably 10 parts by mass or less, more preferably 5 parts by mass or less, and 4 parts by mass or less with respect to 100 parts by mass of the total solid content of the composition. More preferred.
The surfactant may be used alone or in combination of two or more. When two or more kinds are used in combination, the total content thereof is preferably within the above range.

ノニオン性界面活性剤としては、ポリエチレングリコールモノラウリルエーテル、ポリエチレングリコールモノステアリルエーテル、ポリエチレングリコールモノセチルエーテル、ポリエチレングリコールモノラウリルエステル、及び、ポリエチレングリコールモノステアリルエステル等が挙げられる。 Examples of the nonionic surfactant include polyethylene glycol monolauryl ether, polyethylene glycol monostearyl ether, polyethylene glycol monocetyl ether, polyethylene glycol monolauryl ester, and polyethylene glycol monostearyl ester.

イオン性界面活性剤としては、アルキル硫酸塩、アルキルベンゼンスルホン酸塩、及び、アルキルリン酸塩等のアニオン性界面活性剤；アルキルトリメチルアンモニウム塩、及び、ジアルキルジメチルアンモニウム塩等のカチオン性界面活性剤；アルキルカルボキシベタイン等の両性型界面活性剤が挙げられる。 Examples of the ionic surfactant include anionic surfactants such as alkyl sulfates, alkylbenzene sulfonates, and alkyl phosphates; cationic surfactants such as alkyltrimethylammonium salts and dialkyldimethylammonium salts; Amphoteric surfactants such as alkylcarboxybetaine can be mentioned.

（香料）
上記組成物は、香料を含有してもよい。
香料として、長谷川香料社製のフレーバーＨ−１、Ｈ−２、Ｈ−３、Ｈ−４、Ｈ−６、Ｈ−９、Ｈ−１０、Ｈ−１１、Ｈ−１２、Ｈ−１３、Ｈ−１４、高砂香料工業社製のフレーバーＴ−１００、Ｔ−１０１、Ｔ−１０２、Ｔ−１０３、Ｔ−１０４、Ｔ−１０５、Ｔ−１０６、Ｔ−１０７、ＥＤＡ−１７１、曽田香料社製フレーバーＳ−２０１、理研香料工業社製フレーバーＤＡ−４０等を含有してもよい。
香料の含有量は、組成物全質量に対して、例えば、０．０１〜５質量％が好ましい。(Fragrance)
The above composition may contain a fragrance.
As fragrances, flavors H-1, H-2, H-3, H-4, H-6, H-9, H-10, H-11, H-12, H-13, H manufactured by Hasegawa Fragrance Co., Ltd. -14, Takasago International Corporation flavors T-100, T-101, T-102, T-103, T-104, T-105, T-106, T-107, EDA-171, Soda Aromatic Co., Ltd. Flavor S-201, flavor DA-40 manufactured by Riken Fragrance Industry Co., Ltd. may be contained.
The content of the fragrance is preferably 0.01 to 5% by mass with respect to the total mass of the composition.

（造膜剤）
上記組成物は、造膜剤を含有してもよい。なお、本明細書において、造膜剤には、上述した、シリケート系化合物、親水性モノマー、及び、親水性ポリマーは含まれない。
造膜剤としては、熱可塑性樹脂が挙げられる。造膜剤は、例えば、後述する膜を形成した場合には、バインダーとして機能する。
熱可塑性樹脂としては、最低造膜温度が０〜３５℃の樹脂であることが好ましく、公知の熱可塑性樹脂が使用できる。熱可塑性樹脂としては、より具体的には、ポリウレタン樹脂、ポリエステル樹脂、（メタ）アクリル樹脂、ポリスチレン樹脂、フッ素樹脂、ポリイミド樹脂、フッ素化ポリイミド樹脂、ポリアミド樹脂、ポリアミドイミド樹脂、ポリエーテルイミド樹脂、セルロースアシレート樹脂、ポリウレタン樹脂、ポリエーテルエーテルケトン樹脂、ポリカーボネート樹脂、脂環式ポリオレフィン樹脂、ポリアリレート樹脂、ポリエーテルスルホン樹脂、ポリスルホン樹脂、シクロオレフィンコポリマーからなる樹脂、フルオレン環変性ポリカーボネート樹脂、脂環変性ポリカーボネート樹脂、及び、フルオレン環変性ポリエステル樹脂等が挙げられる。なかでも、（メタ）アクリル樹脂、又はウレタン樹脂が好ましい。
なお、熱可塑性樹脂は、１種を単独で用いても、２種以上を併用してもよい。
熱可塑性樹脂の含有量は、熱可塑性樹脂の種類等に応じて適宜調節すればよいが、例えば、組成物の全固形分量に対して、６０質量％以下が好ましく、５０質量％以下がより好ましい。(Film-forming agent)
The above composition may contain a film-forming agent. In the present specification, the film-forming agent does not include the above-mentioned silicate-based compound, hydrophilic monomer, and hydrophilic polymer.
Examples of the film-forming agent include thermoplastic resins. The film-forming agent functions as a binder, for example, when a film described later is formed.
As the thermoplastic resin, a resin having a minimum film forming temperature of 0 to 35 ° C. is preferable, and a known thermoplastic resin can be used. More specifically, the thermoplastic resin includes polyurethane resin, polyester resin, (meth) acrylic resin, polystyrene resin, fluororesin, polyimide resin, fluorinated polyimide resin, polyamide resin, polyamideimide resin, polyetherimide resin, and the like. Cellulose acylate resin, polyurethane resin, polyether ether ketone resin, polycarbonate resin, alicyclic polyolefin resin, polyarylate resin, polyether sulfone resin, polysulfone resin, resin composed of cycloolefin copolymer, fluorene ring-modified polycarbonate resin, alicyclic Examples thereof include a modified polycarbonate resin and a fluorene ring-modified polyester resin. Of these, (meth) acrylic resin or urethane resin is preferable.
The thermoplastic resin may be used alone or in combination of two or more.
The content of the thermoplastic resin may be appropriately adjusted according to the type of the thermoplastic resin and the like. For example, the content is preferably 60% by mass or less, more preferably 50% by mass or less, based on the total solid content of the composition. ..

なお、組成物は、上記以外にも、本発明の効果を奏する範囲内において、有機系抗菌剤、紫外線吸収剤、防腐剤、ｐＨ調整剤、消泡剤、光触媒性材料、充填剤、老化防止剤、帯電防止剤、難燃剤、接着性付与剤、酸化防止剤、レベリング剤、艶消し剤、光安定剤、染料、顔料、及び、分散安定剤等の公知の添加剤を含有してもよい。
なお、有機系抗菌剤としては、特に制限されないが、例えば、第４アンモニウム塩、フェノールエーテル誘導体、イミダゾール誘導体、スルホン誘導体、Ｎ−ハロアルキルチオ化合物、アニリド誘導体、ピロール誘導体、ピリジン系化合物、トリアジン系化合物、ベンゾイソチアゾリン系化合物、及び、イソチアゾリン系化合物等が挙げられる。In addition to the above, the composition may contain an organic antibacterial agent, an ultraviolet absorber, a preservative, a pH adjuster, an antifoaming agent, a photocatalytic material, a filler, and an antistatic agent within the range in which the effects of the present invention are exhibited. It may contain known additives such as agents, antistatic agents, flame retardants, adhesive imparting agents, antioxidants, leveling agents, matting agents, light stabilizers, dyes, pigments, and dispersion stabilizers. ..
The organic antibacterial agent is not particularly limited, but for example, a tetraammonium salt, a phenol ether derivative, an imidazole derivative, a sulfone derivative, an N-haloalkylthio compound, an anilide derivative, a pyrrole derivative, a pyridine compound, and a triazine compound. , Benzoisothiazolin-based compounds, isothiazoline-based compounds and the like.

＜組成物のｐＨ＞
上記組成物のｐＨは特に制限されないが、アンモニア等の塩基性の悪臭物質をより効率に除去できる観点で、６．５以下が好ましい。なお、ｐＨは、市販のｐＨ測定メータ（例えば、東亜ディーケーケー社製のｐＨメータ ＨＭ−３０Ｒ等）を用いて測定できる。<pH of composition>
The pH of the composition is not particularly limited, but is preferably 6.5 or less from the viewpoint of more efficiently removing basic malodorous substances such as ammonia. The pH can be measured using a commercially available pH measuring meter (for example, a pH meter HM-30R manufactured by DKK-TOA CORPORATION).

＜組成物の粘度＞
上記組成物の粘度は特に制限されず、用途に応じて調整すればよい。
例えば、塗布性又はスプレー等に適用する場合、組成物の２５℃における粘度は、３００ｃＰ（センチポアズ：１ｃｐ＝１ｍＰａ・ｓ）以下が好ましく、２００ｃＰ以下がより好ましく、０．１〜１５０ｃＰが更に好ましい。
また、抗菌性及び消臭性の効果を長時間持続させる場合は、組成物の２５℃における粘度は、２５０ｃＰ以上が好ましく、３００ｃＰ以上がより好ましく、４００ｃＰ以上が更に好ましい。なお、その上限は、例えば、５００ｃＰ以下である。
なお、粘度は、東機産業社製ＶＩＳＣＯＭＥＴＥＲ ＴＵＢ−１０、又は、セコニック社製ＳＥＫＯＮＩＣ ＶＩＳＣＯＭＥＴＥＲを用いて測定できる。<Viscosity of composition>
The viscosity of the above composition is not particularly limited and may be adjusted according to the intended use.
For example, when applied to coatability or spray, the viscosity of the composition at 25 ° C. is preferably 300 cP (centipores: 1 cp = 1 mPa · s) or less, more preferably 200 cP or less, still more preferably 0.1 to 150 cP.
When the antibacterial and deodorant effects are to be maintained for a long time, the viscosity of the composition at 25 ° C. is preferably 250 cP or more, more preferably 300 cP or more, still more preferably 400 cP or more. The upper limit is, for example, 500 cP or less.
The viscosity can be measured using VISCOMETER TUB-10 manufactured by Toki Sangyo Co., Ltd. or SEKONIC VISCOMETER manufactured by SEKONIC Corporation.

＜ゼータ電位＞
上記組成物のゼータ電位は、特に限定されないが、組成物中において、粒状物が適度に分散して耐沈降性により優れることを考慮すると、適切な範囲に調整することが好ましい。上記組成物のゼータ電位は、８０ｍＶ〜−８０ｍＶが好ましく、７０ｍＶ〜−７０ｍＶがより好ましく、６０ｍＶ〜−６０ｍＶが更に好ましい。
なお、ゼータ電位は、公知の方法を用いて測定することができ、分散液をガラス製の専用測定セルに所定量導入し、大塚電子社製 ＥＬＳＺ１ＥＡＳを用いて測定することができる。<Zeta potential>
The zeta potential of the composition is not particularly limited, but it is preferably adjusted to an appropriate range in consideration of the fact that the granules are appropriately dispersed in the composition and are more excellent in sedimentation resistance. The zeta potential of the composition is preferably 80 mV to −80 mV, more preferably 70 mV to −70 mV, and even more preferably 60 mV to −60 mV.
The zeta potential can be measured by using a known method, and a predetermined amount of the dispersion liquid can be introduced into a dedicated measurement cell made of glass and measured using ELSZ1EAS manufactured by Otsuka Electronics Co., Ltd.

＜組成物の製造方法＞
上記組成物は、上述した必須成分及び任意成分を、適宜混合することによって調製できる。なお、上記成分の混合の順番は特に制限されない。<Manufacturing method of composition>
The above composition can be prepared by appropriately mixing the above-mentioned essential components and optional components. The order of mixing the above components is not particularly limited.

［臭気抑制方法の第２実施形態］
本発明の第２の実施形態に係る臭気抑制方法は、無機物（１）、及び、第２金属含有物を含有する膜と、特定細菌を含有する被消臭物と、を接触させて、特定細菌に由来する臭気を抑制する臭気抑制方法である。[Second Embodiment of Odor Control Method]
In the odor control method according to the second embodiment of the present invention, a membrane containing an inorganic substance (1) and a second metal-containing substance and a deodorant containing a specific bacterium are brought into contact with each other to specify the substance. This is an odor control method that suppresses odors derived from bacteria.

上記膜に被消臭物を接触させる方法としては特に制限されないが、典型的には、基材と、基材上に形成された上記膜とを有する膜付き基材に、既に説明した被消臭物（例えば、尿等）を接触させる方法が挙げられる。
なお、上記基材として、既に説明したものの他、形状が、板状、フィルム状、シート状、チューブ状、繊維状、及び、粒子状等であって、金属、ガラス、セラミックス、及び、プラスチック（樹脂）等からなる基材も使用できる。The method of bringing the deodorant into contact with the film is not particularly limited, but typically, the substrate with a film having the base material and the film formed on the base material is subjected to the above-described erasure. Examples thereof include a method of contacting an odorous substance (for example, urine).
As the above-mentioned base material, in addition to those already described, the shapes are plate-like, film-like, sheet-like, tube-like, fibrous, particle-like and the like, and metal, glass, ceramics, and plastic ( A base material made of resin) or the like can also be used.

〔膜〕
上記膜は、無機物（１）、及び、第２金属含有物を含有する。これらは、既に説明した組成物中における無機物（１）、及び、第２金属含有物の形態と同様である。
上記膜は、上記以外の成分として、親水性バインダー、及び、リン化合物を含有することが好ましい。また、本発明の効果を奏する範囲内において、その他の成分を含有してもよい。なお、リン化合物、及び、その他の成分の形態は、組成物が含有するその他の成分として既に説明した形態と同様である。〔film〕
The film contains an inorganic substance (1) and a second metal-containing substance. These are the same as the forms of the inorganic substance (1) and the second metal-containing substance in the composition already described.
The membrane preferably contains a hydrophilic binder and a phosphorus compound as components other than the above. In addition, other components may be contained within the range in which the effects of the present invention are exhibited. The form of the phosphorus compound and other components is the same as the form already described as the other components contained in the composition.

＜親水性バインダー＞
膜は、親水性バインダーを含有することが好ましい。親水性バインダーとしては特に制限されないが、例えば、ケイ素原子に加水分解性基が結合した化合物の加水分解物、及びその加水分解縮合物；親水性基を有するポリマー等が挙げられ、ケイ素原子に加水分解性基が結合した化合物の加水分解物、及びその加水分解縮合物からなる群から選択される少なくとも１種が好ましい。
なお、ケイ素原子に加水分解性基が結合した化合物の好ましい形態、及び、親水性基を有するポリマーの好ましい形態は、既に説明したとおりである。<Hydrophilic binder>
The membrane preferably contains a hydrophilic binder. The hydrophilic binder is not particularly limited, and examples thereof include a hydrolyzate of a compound in which a hydrolyzable group is bonded to a silicon atom and a hydrolyzed condensate thereof; a polymer having a hydrophilic group, and the like, and water is added to the silicon atom. At least one selected from the group consisting of a hydrolyzate of a compound to which a degradable group is bonded and a hydrolyzed condensate thereof is preferable.
The preferred form of the compound in which the hydrolyzable group is bonded to the silicon atom and the preferable form of the polymer having the hydrophilic group are as described above.

＜膜の製造方法＞
膜は、典型的には、既に説明した組成物を乾燥又は硬化して得られる。なお、組成物が親水性成分として親水性バインダー前駆体を含有する場合、上記膜は、組成物の塗膜（組成物層）を硬化して得られる。言い換えると、上記膜は、上記組成物層の硬化処理によって、組成物層中の親水性バインダー前駆体を親水性バインダーとすることにより得られる。これに対して、上記組成物中の親水性成分が親水性バインダーである場合、組成物に対して硬化処理を実施する必要はない。<Membrane manufacturing method>
Membranes are typically obtained by drying or curing the compositions already described. When the composition contains a hydrophilic binder precursor as a hydrophilic component, the film is obtained by curing the coating film (composition layer) of the composition. In other words, the film is obtained by making the hydrophilic binder precursor in the composition layer a hydrophilic binder by the curing treatment of the composition layer. On the other hand, when the hydrophilic component in the composition is a hydrophilic binder, it is not necessary to carry out a curing treatment on the composition.

＜膜の膜厚＞
膜の膜厚としては特に制限されないが、０．００１〜５０μｍが好ましく、０．０１〜１０μｍがより好ましい。
なお、上記膜厚とは、膜のサンプル片を樹脂に包埋して、ミクロトームで断面を削り出し、削り出した断面を走査電子顕微鏡で観察し測定する。膜の任意の１０点の位置における厚みを測定し、それらを算術平均した値を意図する。<Film thickness>
The film thickness is not particularly limited, but is preferably 0.001 to 50 μm, more preferably 0.01 to 10 μm.
The film thickness is measured by embedding a sample piece of a film in a resin, cutting out a cross section with a microtome, and observing the cut out cross section with a scanning electron microscope. The thickness at any 10 points of the membrane is measured and the arithmetic mean of them is intended.

＜膜のｐＨ＞
膜の膜面ｐＨは、特に制限されないが、特にアンモニア及びトリメチルアミン等の悪臭物質（臭気）に対する消臭性により優れる点で、６．５以下が好ましく、５．０以下がより好ましく、４．５以下が更に好ましい。膜の膜面ｐＨの下限は、特に制限されないが、例えば、１．０以上である。
なお、本明細書において、膜の膜面ｐＨは、膜面に０．０２ｍＬの液滴（純水）を滴下し、１分間経過した後、その液滴のｐＨを、堀場製作所社製のｐＨメータ ＬＡＱＵＡ Ｆ−７２を用いて測定することにより求めたときの値である。<Membrane pH>
The film surface pH of the film is not particularly limited, but is preferably 6.5 or less, more preferably 5.0 or less, and more preferably 4.5 or less, in that it is particularly excellent in deodorizing properties against malodorous substances (odors) such as ammonia and trimethylamine. The following is more preferable. The lower limit of the film surface pH of the film is not particularly limited, but is, for example, 1.0 or more.
In the present specification, the pH of the membrane surface is determined by dropping 0.02 mL of droplets (pure water) onto the membrane surface, and after 1 minute has passed, the pH of the droplets is the pH manufactured by HORIBA, Ltd. It is a value obtained by measuring with a meter LAQUA F-72.

膜は、ｐＨが低いまま保存されると、膜中の抗菌剤が変質して抗菌作用が低下する場合がある。このため、例えば、膜は、オムツ等の用途に適用される場合、尿等の被消臭物が膜面に付着したときに膜面ｐＨが上記数値範囲（好ましくは膜面ｐＨ６．５以下）となるようにすることが好ましい。
具体的な方法としては、例えば、酸性材料を含有する膜において、酸性材料を有機酸とする方法が挙げられる。有機酸は揮発性が低いため、乾燥状態では親水性バインダーに固着して存在する。このため、膜が乾燥状態にあるときは、膜面ｐＨは中性付近で保持される。一方、被消臭物が膜面に付着すると、被消臭物の含有する水分により膜表面の有機酸が溶解し、膜の膜面ｐＨが所定値以下となる。
また、他の方法としては、水等に溶解する皮膜と、上記皮膜内に内包された酸性材料とからなるマイクロカプセルを使用する方法が挙げられる。上記マイクロカプセルを含む膜の膜面に被消臭物が付着すると、マイクロカプセルの皮膜が溶解して酸性材料が露出し、膜の膜面ｐＨが所定値以下となる。If the membrane is stored at a low pH, the antibacterial agent in the membrane may be altered to reduce the antibacterial action. Therefore, for example, when the membrane is applied to applications such as diapers, the membrane surface pH is in the above numerical range (preferably membrane surface pH 6.5 or less) when a deodorant such as urine adheres to the membrane surface. It is preferable that
As a specific method, for example, in a membrane containing an acidic material, a method of using the acidic material as an organic acid can be mentioned. Since organic acids have low volatility, they are attached to hydrophilic binders in a dry state. Therefore, when the film is in a dry state, the film surface pH is maintained near neutral. On the other hand, when the deodorant adheres to the film surface, the organic acid on the film surface is dissolved by the water contained in the deodorant, and the film surface pH of the film becomes a predetermined value or less.
Further, as another method, there is a method of using a microcapsule composed of a film that dissolves in water or the like and an acidic material contained in the film. When the deodorant adheres to the film surface of the film containing the microcapsules, the film of the microcapsules is dissolved and the acidic material is exposed, and the film surface pH of the film becomes a predetermined value or less.

以下に実施例に基づいて本発明を更に詳細に説明する。以下の実施例に示す材料、使用量、割合、処理内容、及び、処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す実施例により限定的に解釈されるべきものではない。 The present invention will be described in more detail below based on examples. The materials, amounts used, ratios, treatment contents, treatment procedures, etc. shown in the following examples can be appropriately changed without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be construed as limiting by the examples shown below.

［実施例１］
容器中でエタノール２７８ｇを攪拌しながら、純水１５２ｇ、シロキサン化合物であるバインダー（三菱化学社製「ＭＫＣ（登録商標）シリケート」ＭＳ５１」）９．５ｇ、アルミキレートＤ（アルミニウムビス（エチルアセトアセテート）モノ（アセチルアセトネート）、エタノール希釈：固形分濃度１質量％）１５ｇ、ノニオン性界面活性剤（日本エマルジョン社製「エマレックス７１５」、純水希釈：固形分濃度０．５質量％）４０ｇ、アニオン性界面活性剤（ジ（２−エチルヘキシル）スルホコハク酸ナトリウム、純水希釈：固形分濃度０．２質量％）１０ｇ、を順次加えた後、イソプロパノール１５ｇ、分散剤（ＢＹＫ社製「ＤＩＳＰＥＲＢＹＫ（登録商標）−１８０」）１ｇ、平均粒径を０．６μｍに制御した銀担持ガラス（富士ケミカル社製、エタノール希釈：固形分含有量３０質量％、銀担持ガラスは、第１の金属を含有する無機物に該当する。）１ｇを加え、銅担持ガラス（東亞合成製「ＮＳ-２０Ｃ」、固形分含有量１００質量％、銅担持ガラスは、第２の金属を含有する無機物に該当する。）３ｇ、リン酸ジルコニウム（東亞合成製「ＮＳ-１０」、固形分含有量１００質量％、リン化合物に該当する。）３ｇを加え、２０分間攪拌し、組成物Ａを得た。
なお、調製した組成物については、上記記載のｐＨメータを使用して、２５℃におけるｐＨを測定した。結果を表１に示した。[Example 1]
While stirring 278 g of ethanol in the container, 152 g of pure water, 9.5 g of binder (Mitsubishi Chemical's "MKC (registered trademark) Dilute" MS51 "), aluminum chelate D (aluminum bis (ethylacetoacetate)) Mono (acetylacetonate), ethanol dilution: solid content concentration 1% by mass) 15g, nonionic surfactant (Nippon Emulsion Co., Ltd. "Emarex 715", pure water dilution: solid content concentration 0.5% by mass) 40g, After sequentially adding 10 g of an anionic surfactant (di (2-ethylhexyl) sodium sulfosuccinate, dilution of pure water: solid content concentration 0.2% by mass), 15 g of isopropanol and a dispersant (BYK "DISPERBYK (registered)" Trademark) -180 ") 1 g, silver-supported glass with an average particle size controlled to 0.6 μm (manufactured by Fuji Chemical Co., Ltd., ethanol dilution: solid content 30% by mass, silver-supported glass contains a first metal. (Corresponding to an inorganic substance.) Add 1 g of copper-supported glass (“NS-20C” manufactured by Toa Synthetic, solid content 100% by mass, copper-supported glass corresponds to an inorganic substance containing a second metal) 3 g. , 3 g of zirconium phosphate (“NS-10” manufactured by Toa Synthetic, solid content 100% by mass, corresponding to a phosphorus compound) was added, and the mixture was stirred for 20 minutes to obtain Composition A.
For the prepared composition, the pH at 25 ° C. was measured using the pH meter described above. The results are shown in Table 1.

上記実施例と同様の方法により、表１に記載した成分を混合し、固形分含有量を実施例１の組成物と同様にして、各実施例及び各比較例に係る組成物を得た。また、ｐＨを測定した結果を表１に示した。なお、各組成物は、組成物中の水の含有量（質量％）、及び、アルコールの合計含有量（質量％）が表１に記載したとおりになるように、溶媒（希釈用の溶媒）の組成を変更した。
なお、表１中における各略号は、以下の内容を表す。
・酸化銅粒子：和光純薬工業製「酸化銅（ＩＩ）」の平均粒径１μｍに制御したもの
・銀粒子：和光純薬工業製「銀、粉末」の平均粒径１μｍに制御したもの
・酸化亜鉛粒子：（和光純薬工業製「酸化亜鉛」の平均粒径１μｍに制御したもの）
・銅粒子/表面有機層（ポリスチレン）粒子：和光純薬工業製「銅、粉末」（平均粒径１μｍに制御したもの）を、末端にチオール基を有するポリスチレンのＴＨＦ（テトラヒドロフラン）溶液に１５時間浸漬し、乾燥させて作製したもの
・銀粒子/表面有機層（ゼラチン）粒子：純水、硝酸銀水溶液、及び、亜硫酸ナトリウムを混合した液にゼラチン水溶液を混合した液を乾燥させたものを平均粒径０．３μｍに制御して作製したもの
・銅フタロシアニン：和光純薬工業製「フタロシアニン銅（ＩＩ）」の平均粒径１μｍに制御したもの
・「種別」欄の「Ａ」：金属を含有する無機物
・「種別」欄の「Ｂ」：金属を含有する有機物
・「−」：その化合物を用いなかったことを表す。The components shown in Table 1 were mixed by the same method as in the above Examples, and the solid content was the same as the composition in Example 1 to obtain a composition according to each Example and each Comparative Example. The results of pH measurement are shown in Table 1. Each composition has a solvent (solvent for dilution) so that the water content (mass%) in the composition and the total alcohol content (mass%) are as shown in Table 1. The composition of was changed.
In addition, each abbreviation in Table 1 represents the following contents.
-Copper oxide particles: controlled to an average particle size of "copper (II) oxide" manufactured by Wako Pure Chemical Industries, Ltd. to an average particle size of 1 μm. Zinc oxide particles: (controlled to an average particle size of 1 μm of "zinc oxide" manufactured by Wako Pure Chemical Industries, Ltd.)
-Copper particles / surface organic layer (polystyrene) particles: "Copper, powder" manufactured by Wako Pure Chemical Industries, Ltd. (controlled to an average particle size of 1 μm) is placed in a THF (tetra) solution of polystyrene having a thiol group at the terminal for 15 hours. Prepared by dipping and drying-Silver particles / surface organic layer (gelatin) particles: Average grains obtained by drying a mixture of pure water, silver nitrate aqueous solution, and sodium sulfite mixed with gelatin aqueous solution. Made by controlling the diameter to 0.3 μm ・ Copper phthalocyanine: Controlled to an average particle size of 1 μm of “Copper phthalocyanine copper (II)” manufactured by Wako Pure Chemical Industries, Ltd. ・ “A” in the “Type” column: Contains metal Inorganic substance ・ "B" in the "Type" column: Organic substance containing metal ・ "-": Indicates that the compound was not used.

＜消臭性評価＞
不織布を準備し、不織布１００ｃｍ２当たり、各実施例及び比較例の組成物が１ｇ付着するように、不織布に対して組成物を噴射した。次に、得られた組成物付き不織布を２５℃にて２日間乾燥し、膜付き基材を得た。また、ＰＥＴ（ポリエチレンテレフタレート）基材上の同様に噴射して得られた膜の膜面ｐＨを表１に示した。<Deodorant evaluation>
A non-woven fabric was prepared, and the composition was sprayed onto the non-woven fabric so that 1 g of the compositions of each Example and Comparative Example adhered to 100 cm 2 of the non-woven fabric. Next, the obtained non-woven fabric with a composition was dried at 25 ° C. for 2 days to obtain a substrate with a film. Table 1 shows the film surface pH of the film obtained by similarly spraying on a PET (polyethylene terephthalate) substrate.

次に、臭気「Ｅ」のアンモニア臭がする尿を上記膜付き基材に１０ｇ噴霧し、室温放置した。放置後、１０分後、及び、８時間後の検体並びに対照検体の臭いを、３人のパネラーに嗅がせ、各検体の臭気を以下の基準で評価させた。（３人のパネラー間で評価結果に差はなかった。）結果は、表１の「消臭性」欄に示した。
なお、尿中（とりわけ***症患者の尿）には複数の菌を含んでおり、代表的な菌である大腸菌、ブドウ球菌に加えて、クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、モルガネラ属、及び、セラチア属等の細菌が混在しており、本評価試験で採用した尿も同様に複数の菌が存在している。
従って、本評価において、１０分後の評価結果は、もともと尿中に含まれる悪臭物質に対する消臭効果の程度を表し、８時間後の評価結果は、尿中に存在する上記細菌に由来する悪臭物質に対する消臭効果の程度を表しているものと考えられる。Next, 10 g of urine having an ammonia odor of odor "E" was sprayed on the substrate with a film and left at room temperature. The odors of the samples and control samples 10 minutes and 8 hours after being left to stand were smelled by three panelists, and the odors of each sample were evaluated according to the following criteria. (There was no difference in the evaluation results among the three panelists.) The results are shown in the "Deodorant" column of Table 1.
In addition, urine (particularly the urine of patients with urinary tract infections) contains multiple bacteria, and in addition to the typical bacteria Escherichia coli and Staphylococcus, Klebsiella, Citrobacter, Enterobacter, and Proteus Bacteria such as genus, Pseudomonas, Morganella, and Serratia are mixed, and the urine used in this evaluation test also has a plurality of bacteria.
Therefore, in this evaluation, the evaluation result after 10 minutes indicates the degree of deodorizing effect on the malodorous substance originally contained in urine, and the evaluation result after 8 hours is the malodor derived from the above-mentioned bacteria existing in urine. It is considered to indicate the degree of deodorant effect on the substance.

・評価基準
「ＡＡ」：臭気を感じない。
「Ａ」：ほぼ臭気を感じない。
「Ｂ」：わずかに臭気を感じる。
「Ｃ」：やや臭気を感じる。
「Ｄ」：臭気を感じる。
「Ｅ」：強く臭気を感じる。-Evaluation criteria "AA": No odor is felt.
"A": Almost no odor is felt.
"B": A slight odor is felt.
"C": A slight odor is felt.
"D": I feel an odor.
"E": A strong odor is felt.

上記官能評価で使用したのとは別の、新たな膜付き基材について、ＪＩＳ Ｚ ２８０１：２０１２記載の評価方法に準拠し、大腸菌（Escherichia coli、表中は、「E.coli」と記載した。）、黄色ブドウ球菌(Staphylococcus aureus、表中は、「S.aureus」と記載した。）、及び、特定細菌（Klebsiella pneumoniae [K.pneumoniae]、Citrobacter freundii [C.freundii]、Proteus mirabilis [P.mirabilis]、Enterobacter cloacae [E.cloacae]、Morganella morganii [M.morganii]、Pseudomonas aeruginosa [P.aeruginosa]、Serratia marcescens [S.marcescens]）をそれぞれ培養して得た菌液への接触時間を８時間に変更して試験を実施した。試験後の抗菌活性値を測定し、以下の評価基準に基づいて評価した。細菌種ごとの結果を表１の「抗菌性」欄に示した。なお、表１において、各細菌の属名は頭文字のみ示している。 A new substrate with a film, which was different from the one used in the above sensory evaluation, was described as Escherichia coli (E. coli in the table) in accordance with the evaluation method described in JIS Z 2801: 2012. .), Staphylococcus aureus (indicated as "S. aureus" in the table), and specific bacteria (Klebsiella pneumoniae [K.pneumoniae], Citrobacter freundii [C.freundii], Proteus mirabilis [P .mirabilis], Enterobacter cloacae [E.cloacae], Morganella morganii [M.morganii], Pseudomonas aeruginosa [P.aeruginosa], Serratia marcescens [S.marcescens]) The test was carried out after changing to 8 hours. The antibacterial activity value after the test was measured and evaluated based on the following evaluation criteria. The results for each bacterial species are shown in the "Antibacterial" column of Table 1. In Table 1, only the acronyms are shown for the genus names of each bacterium.

・評価基準
「ＡＡ」：抗菌活性値が３．２以上だった。
「Ａ」：抗菌活性値が２．２以上、３．２未満だった。
「Ｂ」：抗菌活性値が１．５以上、２．２未満だった。
「Ｃ」：抗菌活性値が１．０以上、１．５未満だった。
「Ｄ」：抗菌活性値が１．０未満だった。-Evaluation criteria "AA": The antibacterial activity value was 3.2 or higher.
"A": The antibacterial activity value was 2.2 or more and less than 3.2.
"B": The antibacterial activity value was 1.5 or more and less than 2.2.
"C": The antibacterial activity value was 1.0 or more and less than 1.5.
"D": The antibacterial activity value was less than 1.0.

以下の表１は、表１（その１）〜表１（その３）の３つに分割されている。各組成物の成分及び試験結果は、表１（その１）〜表１（その３）の各行にわたって記載されている。具体的には、実施例１の組成物は、第１金属含有物として銀担持ガラス（第１金属がＡｇ（銀）であり、Ａ：金属を含有する無機物に該当する）を０．３ｇ含有し、第２金属含有物として、銅担持ガラス（第２金属がＣｕ（銅）であり、Ａ：金属を含有する無機物に該当する）を３ｇ含有し、第３金属含有物として、リン酸ジルコニウム（第３金属がＺｒ（ジルコニウム）であり、Ａ：金属を含有する無機物に該当する）を３ｇ含有し、組成物中における水の含有量が３８質量％であり、アルコールの合計含有量が５９質量％であり、組成物（液）のｐＨが６．２であり、膜面ｐＨが６．１であり、消臭性が、１０分後が「Ｂ」であり、８時間後が「ＡＡ」であり、抗菌性が、Klebsiella pneumoniae（肺炎桿菌）に対して「ＡＡ」、Citrobacter freundiiに対して「ＡＡ」、Proteus mirabilisに対して「ＡＡ」、Enterobacter cloacaeに対して「ＡＡ」、Pseudomonas aeruginosa（緑膿菌）に対して「ＡＡ」、Morganella morganiiに対して「ＡＡ」、Serratia marcescensに対して「ＡＡ」、Escherichia coli（大腸菌）に対して「ＡＡ」、及び、Staphylococcus aureus（黄色ブドウ球菌）に対して「ＡＡ」だったことを表している。 Table 1 below is divided into three parts, Table 1 (No. 1) to Table 1 (No. 3). The components and test results of each composition are described across the lines of Table 1 (No. 1) to Table 1 (No. 3). Specifically, the composition of Example 1 contains 0.3 g of silver-supported glass (the first metal is Ag (silver) and A: corresponds to an inorganic substance containing a metal) as the first metal-containing substance. However, as the second metal-containing substance, 3 g of copper-supported glass (the second metal is Cu (copper) and corresponds to A: an inorganic substance containing a metal) is contained, and as the third metal-containing substance, zirconium phosphate It contains 3 g (the third metal is Zr (zinc) and corresponds to A: an inorganic substance containing a metal), the content of water in the composition is 38% by mass, and the total content of alcohol is 59. It is mass%, the pH of the composition (liquid) is 6.2, the film surface pH is 6.1, the deodorant property is "B" after 10 minutes, and "AA" after 8 hours. The antibacterial properties are "AA" for Klebsiella pneumoniae (Pseudomonas aeruginosa), "AA" for Citrobacter freundii, "AA" for Proteus mirabilis, "AA" for Enterobacter cloacae, Pseudomonas aeruginosa. "AA" for (Pseudomonas aeruginosa), "AA" for Morganella morganii, "AA" for Serratia marcescens, "AA" for Escherichia coli (E. coli), and Staphylococcus aureus (yellow staphylococcus aureus) ) Indicates that it was "AA".

表１に示した結果から、実施例１〜実施例１５に示すとおり、第１の金属を含有する無機物、並びに、第１の金属とは異なる第２の金属を含有する無機物、及び、第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する組成物と、特定細菌を含有する被消臭物と、を接触させることで、特定細菌に由来する臭気を抑制することができることがわかった。
一方、比較例１〜５の方法では、本発明の効果が得られなかった。From the results shown in Table 1, as shown in Examples 1 to 15, an inorganic substance containing a first metal, an inorganic substance containing a second metal different from the first metal, and a second metal. By contacting a composition containing at least one selected from the group consisting of organic substances containing the same metal with a deodorant containing a specific bacterium, the odor derived from the specific bacterium is suppressed. I found that I could do it.
On the other hand, the effects of the present invention were not obtained by the methods of Comparative Examples 1 to 5.

また、組成物が無機担体と無機担体に担持された第２の金属とを有する金属担持無機担体を含有する、実施例１の方法は、実施例１５の方法と比較して、より優れた本発明の効果を有していた。
また、組成物が、第２の金属を含有する無機物を含有し、第１の金属が銀であり、第２の金属が銅である、実施例１の方法は、実施例１１の方法と比較して、より優れた本発明の効果を有していた。
また、組成物が、第２の金属を含有する無機物を含有し、第１の金属を含有する無機物として、第１の無機担体と第１の無機担体に担持された銀とを有する金属担持無機担体を含有して、第２の金属を含有する無機物として、第２の無機担体と第２の無機担体に担持された銅とを有する金属担持無機担体を含有する、実施例１の方法は、実施例１０の方法と比較して、より優れた本発明の効果を有していた。
また、組成物が、更に、第１の金属、及び、第２の金属のいずれとも異なる第３の金属を含有する無機物を含有し、上記無機物が、リン原子を含有する、実施例１の方法は、実施例２の方法と比較して、より優れた本発明の効果を有していた。Further, the method of Example 1 in which the composition contains a metal-supported inorganic carrier having an inorganic carrier and a second metal supported on the inorganic carrier is a better book than the method of Example 15. It had the effect of the invention.
Further, the method of Example 1 in which the composition contains an inorganic substance containing a second metal, the first metal is silver, and the second metal is copper is compared with the method of Example 11. Therefore, it had a better effect of the present invention.
Further, the composition contains an inorganic substance containing a second metal, and as the inorganic substance containing the first metal, a metal-supported inorganic substance having a first inorganic carrier and silver supported on the first inorganic carrier. The method of Example 1 comprises a carrier-containing, second metal-containing inorganic material containing a metal-supported inorganic carrier having a second inorganic carrier and copper supported on the second inorganic carrier. It had a better effect of the present invention as compared with the method of Example 10.
Further, the method of Example 1 in which the composition further contains an inorganic substance containing a first metal and a third metal different from any of the second metals, and the inorganic substance contains a phosphorus atom. Had a better effect of the present invention as compared with the method of Example 2.

Claims (37)

第１の金属を含有する無機物、並びに、
前記第１の金属とは異なる第２の金属を含有する無機物、及び、前記第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する組成物と、
クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌を含有する被消臭物と、を接触させて、前記細菌に由来する臭気を抑制する臭気抑制方法。Inorganic substances containing the first metal, as well as
A composition containing at least one selected from the group consisting of an inorganic substance containing a second metal different from the first metal and an organic substance containing the second metal.
Contact with a deodorant containing at least one bacterium selected from the group consisting of Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. An odor control method for suppressing an odor derived from the bacterium. 前記第１の金属を含有する無機物が、前記第１の金属の単体、前記第１の金属の酸化物、及び、無機担体と前記無機担体に担持された前記第１の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、請求項１に記載の臭気抑制方法。 A metal bearing in which the inorganic substance containing the first metal has a simple substance of the first metal, an oxide of the first metal, and an inorganic carrier and the first metal supported on the inorganic carrier. The odor control method according to claim 1, which is at least one selected from the group consisting of inorganic carriers. 前記第２の金属を含有する無機物が、前記第２の金属の単体、前記第２の金属の酸化物、及び、無機担体と前記無機担体に担持された前記第２の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、請求項１又は２に記載の臭気抑制方法。 A metal bearing in which the inorganic substance containing the second metal has a simple substance of the second metal, an oxide of the second metal, and an inorganic carrier and the second metal supported on the inorganic carrier. The odor control method according to claim 1 or 2, which is at least one selected from the group consisting of inorganic carriers. 前記組成物が、前記第２の金属を含有する無機物を含有し、
前記第１の金属が銀であり、前記第２の金属が銅である、請求項１〜３のいずれか一項に記載の臭気抑制方法。The composition contains an inorganic substance containing the second metal,
The odor suppressing method according to any one of claims 1 to 3, wherein the first metal is silver and the second metal is copper. 前記組成物が、更に、水、及び、アルコールからなる群から選択される少なくとも１種を含有する、請求項１〜４のいずれか一項に記載の臭気抑制方法。 The method for suppressing odor according to any one of claims 1 to 4, wherein the composition further contains at least one selected from the group consisting of water and alcohol. 前記組成物が、前記第２の金属を含有する無機物を含有し、
前記第１の金属を含有する無機物は、第１の無機担体と前記第１の無機担体に担持された銀とを有する金属担持無機担体であり、前記第２の金属を含有する無機物は、第２の無機担体と前記第２の無機担体に担持された銅とを有する金属担持無機担体である、請求項１〜５のいずれか一項に記載の臭気抑制方法。The composition contains an inorganic substance containing the second metal,
The first metal-containing inorganic substance is a metal-supported inorganic carrier having a first inorganic carrier and silver supported on the first inorganic carrier, and the second metal-containing inorganic substance is a first. The method for suppressing odor according to any one of claims 1 to 5, which is a metal-supported inorganic carrier having the inorganic carrier of 2 and the copper supported on the second inorganic carrier. 前記組成物が、更に、前記第１の金属、及び、前記第２の金属のいずれとも異なる第３の金属を含有する無機物を含有する、請求項１〜６のいずれか一項に記載の臭気抑制方法。 The odor according to any one of claims 1 to 6, wherein the composition further contains an inorganic substance containing the first metal and a third metal different from any of the second metals. Suppression method. 前記第３の金属を含有する無機物が、リン原子を含有する、請求項７に記載の臭気抑制方法。 The method for suppressing odor according to claim 7, wherein the inorganic substance containing the third metal contains a phosphorus atom. 前記組成物のｐＨが６．５以下である、請求項１〜８のいずれか一項に記載の臭気抑制方法。 The method for suppressing odor according to any one of claims 1 to 8, wherein the pH of the composition is 6.5 or less. 前記組成物が、更に、親水性バインダー前駆体、及び、親水性バインダーからなる群から選択される親水性成分を含有する、請求項１〜９のいずれか一項に記載の臭気抑制方法。 The method for suppressing odor according to any one of claims 1 to 9, wherein the composition further contains a hydrophilic binder precursor and a hydrophilic component selected from the group consisting of a hydrophilic binder. 前記親水性成分が、シリケート系化合物、親水性基を有するモノマー、及び、親水性基を有するポリマーからなる群より選ばれる少なくとも１種を含有する、請求項１０に記載の臭気抑制方法。 The odor control method according to claim 10, wherein the hydrophilic component contains at least one selected from the group consisting of a silicate-based compound, a monomer having a hydrophilic group, and a polymer having a hydrophilic group. 前記組成物が、更に、ノニオン系分散剤、及び、アニオン系分散剤からなる群から少なくとも１種を含有する、請求項１〜１１のいずれか一項に記載の臭気抑制方法。 The odor suppressing method according to any one of claims 1 to 11, wherein the composition further contains at least one from the group consisting of a nonionic dispersant and an anionic dispersant. 基布と、前記基布に含浸させた前記組成物とを有するワイパーを用いて、前記被消臭物を拭いて、前記組成物と前記被消臭物とを接触させる、請求項１〜１２のいずれか一項に記載の臭気抑制方法。 Claims 1 to 12 in which the deodorant is wiped with a wiper having the base cloth and the composition impregnated in the base cloth to bring the composition and the deodorant into contact with each other. The odor control method according to any one of the above. スプレー容器と、前記スプレー容器に収納された前記組成物とを有するスプレーを用いて、前記被消臭物に前記組成物を噴霧して、前記被消臭物と前記組成物とを接触させる、請求項１〜１２のいずれか一項に記載の臭気抑制方法。 Using a spray container and a spray having the composition contained in the spray container, the composition is sprayed on the deodorant to bring the deodorant into contact with the composition. The odor suppressing method according to any one of claims 1 to 12. 第１の金属を含有する無機物、並びに、
前記第１の金属とは異なる第２の金属を含有する無機物、及び、前記第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有する膜と、
クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌を含有する被消臭物と、を接触させて、前記細菌に由来する臭気を抑制する臭気抑制方法。Inorganic substances containing the first metal, as well as
A film containing at least one selected from the group consisting of an inorganic substance containing a second metal different from the first metal and an organic substance containing the second metal.
Contact with a deodorant containing at least one bacterium selected from the group consisting of Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. An odor control method for suppressing an odor derived from the bacterium. 前記第１の金属を含有する無機物が、前記第１の金属の単体、前記第１の金属の酸化物、及び、無機担体と前記無機担体に担持された前記第１の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、請求項１５に記載の臭気抑制方法。 A metal bearing in which the inorganic substance containing the first metal has a simple substance of the first metal, an oxide of the first metal, and an inorganic carrier and the first metal supported on the inorganic carrier. The odor control method according to claim 15, which is at least one selected from the group consisting of inorganic carriers. 前記第２の金属を含有する無機物が、前記第２の金属の単体、前記第２の金属の酸化物、及び、無機担体と前記無機担体に担持された前記第２の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、請求項１５又は１６に記載の臭気抑制方法。 A metal bearing in which the inorganic substance containing the second metal has a simple substance of the second metal, an oxide of the second metal, and an inorganic carrier and the second metal supported on the inorganic carrier. The odor control method according to claim 15 or 16, which is at least one selected from the group consisting of inorganic carriers. 前記膜が、前記第２の金属を含有する無機物を含有し、
前記第１の金属が銀であり、前記第２の金属が銅である、請求項１５〜１７のいずれか一項に記載の臭気抑制方法。The film contains an inorganic substance containing the second metal,
The odor suppressing method according to any one of claims 15 to 17, wherein the first metal is silver and the second metal is copper. 前記膜が、前記第２の金属を含有する無機物を含有し、
前記第１の金属を含有する無機物は、第１の無機担体と前記第１の無機担体に担持された銀とを有する金属担持無機担体であり、前記第２の金属を含有する無機物は、第２の無機担体と前記第２の無機担体に担持された銅とを有する金属担持無機担体である、請求項１５〜１８のいずれか一項に記載の臭気抑制方法。The film contains an inorganic substance containing the second metal,
The first metal-containing inorganic substance is a metal-supported inorganic carrier having a first inorganic carrier and silver supported on the first inorganic carrier, and the second metal-containing inorganic substance is a first. The odor suppression method according to any one of claims 15 to 18, which is a metal-supported inorganic carrier having the inorganic carrier of 2 and the copper supported on the second inorganic carrier. 前記膜が、更に、前記第１の金属、及び、前記第２の金属のいずれとも異なる第３の金属を含有する無機物を含有する、請求項１５〜１９のいずれか一項に記載の臭気抑制方法。 The odor suppression according to any one of claims 15 to 19, wherein the film further contains an inorganic substance containing the first metal and a third metal different from any of the second metals. Method. 前記第３の金属を含有する無機物が、更に、リン原子を含有する、請求項２０に記載の臭気抑制方法。 The method for suppressing odor according to claim 20, wherein the inorganic substance containing the third metal further contains a phosphorus atom. 前記膜の膜面のｐＨが６．５以下である、請求項１５〜２１のいずれか一項に記載の臭気抑制方法。 The method for suppressing odor according to any one of claims 15 to 21, wherein the pH of the film surface of the film is 6.5 or less. 前記膜が、更に、親水性バインダーを含む、請求項１５〜２２のいずれか一項に記載の臭気抑制方法。 The method for suppressing odor according to any one of claims 15 to 22, wherein the film further contains a hydrophilic binder. 前記膜が、更に、ノニオン系分散剤、及び、アニオン系分散剤からなる群から少なくとも１種を含有する、請求項１５〜２３のいずれか一項に記載の臭気抑制方法。 The odor suppressing method according to any one of claims 15 to 23, wherein the membrane further contains at least one of the group consisting of a nonionic dispersant and an anionic dispersant. 第１の金属を含有する無機物、並びに、
前記第１の金属とは異なる第２の金属を含有する無機物、及び、前記第２の金属を含有する有機物からなる群から選択される少なくとも１種を含有し、
クレブシエラ属、シトロバクター属、エンテロバクター属、プロテウス属、シュードモナス属、セラチア属、及び、モルガネラ属からなる群から選択される少なくとも１種類の細菌に由来する臭気の抑制に用いられる、組成物。Inorganic substances containing the first metal, as well as
It contains at least one selected from the group consisting of an inorganic substance containing a second metal different from the first metal and an organic substance containing the second metal.
A composition used to suppress odors derived from at least one bacterium selected from the group consisting of Klebsiella, Citrobacter, Enterobacter, Proteus, Pseudomonas, Serratia, and Morganella. 前記第１の金属を含有する無機物が、前記第１の金属の単体、前記第１の金属の酸化物、及び、無機担体と前記無機担体に担持された前記第１の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、請求項２５に記載の組成物。 A metal support in which the inorganic substance containing the first metal has a simple substance of the first metal, an oxide of the first metal, and an inorganic carrier and the first metal supported on the inorganic carrier. The composition according to claim 25, which is at least one selected from the group consisting of inorganic carriers. 前記第２の金属を含有する無機物が、前記第２の金属の単体、前記第２の金属の酸化物、及び、無機担体と前記無機担体に担持された前記第２の金属とを有する金属担持無機担体からなる群から選択される少なくとも１種である、請求項２５又は２６に記載の組成物。 A metal bearing in which the inorganic substance containing the second metal has a simple substance of the second metal, an oxide of the second metal, and an inorganic carrier and the second metal supported on the inorganic carrier. The composition according to claim 25 or 26, which is at least one selected from the group consisting of inorganic carriers. 前記第２の金属を含有する無機物を含有し、
前記第１の金属が銀であり、前記第２の金属が銅である、請求項２５〜２７のいずれか一項に記載の組成物。Contains an inorganic substance containing the second metal,
The composition according to any one of claims 25 to 27, wherein the first metal is silver and the second metal is copper. 前記組成物が、更に、水、及び、アルコールからなる群から選択される少なくとも１種を含有する、請求項２５〜２８のいずれか一項に記載の組成物。 The composition according to any one of claims 25 to 28, wherein the composition further contains at least one selected from the group consisting of water and alcohol. 前記第２の金属を含有する無機物を含有し、
前記第１の金属を含有する無機物は、第１の無機担体と前記第１の無機担体に担持された銀とを有する金属担持無機担体であり、前記第２の金属を含有する無機物は、第２の無機担体と前記第２の無機担体に担持された銅とを有する金属担持無機担体である、請求項２５〜２９のいずれか一項に記載の組成物。Contains an inorganic substance containing the second metal,
The first metal-containing inorganic substance is a metal-supported inorganic carrier having a first inorganic carrier and silver supported on the first inorganic carrier, and the second metal-containing inorganic substance is a first. The composition according to any one of claims 25 to 29, which is a metal-supported inorganic carrier having the inorganic carrier of 2 and the copper supported on the second inorganic carrier. 前記組成物が、更に、前記第１の金属、及び、前記第２の金属のいずれとも異なる第３の金属を含有する無機物を含有する、請求項２５〜３０のいずれか一項に記載の組成物。 The composition according to any one of claims 25 to 30, wherein the composition further contains an inorganic substance containing the first metal and a third metal different from any of the second metals. Stuff. 前記第３の金属を含有する無機物が、更に、リン原子を含有する、請求項３１に記載の組成物。 The composition according to claim 31, wherein the inorganic substance containing the third metal further contains a phosphorus atom. ｐＨが６．５以下である、請求項２５〜３２のいずれか一項に記載の組成物。 The composition according to any one of claims 25 to 32, which has a pH of 6.5 or less. 更に、親水性バインダー前駆体、及び、親水性バインダーからなる群から選択される親水性成分を含有する、請求項２５〜３３のいずれか一項に記載の組成物。 The composition according to any one of claims 25 to 33, further containing a hydrophilic binder precursor and a hydrophilic component selected from the group consisting of hydrophilic binders. 前記組成物が、更に、ノニオン系分散剤、及び、アニオン系分散剤からなる群から少なくとも１種を含有する、請求項２５〜３４のいずれか一項に記載の組成物。 The composition according to any one of claims 25 to 34, wherein the composition further contains at least one from the group consisting of a nonionic dispersant and an anionic dispersant. スプレー容器と、前記スプレー容器に収納された請求項２５〜３５のいずれか一項に記載の組成物とを有するスプレー。 A spray having a spray container and the composition according to any one of claims 25 to 35 contained in the spray container. 基布と、前記基布に含浸された請求項２５〜３５のいずれか一項に記載の組成物とを有するワイパー。 A wiper having a base cloth and the composition according to any one of claims 25 to 35 impregnated in the base cloth.
JP2019551146A 2017-10-31 2018-10-23 Odor control methods, compositions, wipers, and sprays Abandoned JPWO2019087856A1 (en)