JPWO2015107796A1 - Semiconductor element, manufacturing method thereof, and semiconductor device - Google Patents
Semiconductor element, manufacturing method thereof, and semiconductor device Download PDFInfo
- Publication number
- JPWO2015107796A1 JPWO2015107796A1 JP2015531361A JP2015531361A JPWO2015107796A1 JP WO2015107796 A1 JPWO2015107796 A1 JP WO2015107796A1 JP 2015531361 A JP2015531361 A JP 2015531361A JP 2015531361 A JP2015531361 A JP 2015531361A JP WO2015107796 A1 JPWO2015107796 A1 JP WO2015107796A1
- Authority
- JP
- Japan
- Prior art keywords
- film
- protective film
- semiconductor element
- electrode
- opening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
第1の主面(1A)を有し、第1の主面(1A)上に形成されている電極(5)と、電極(5)の表面上において開口部を有し、電極(5)の少なくとも端部を覆うように形成されている保護膜(6)と、開口部において電極(5)上に形成されている第1めっき膜(7)とを備え、保護膜(6)は、開口部の側壁から開口部内に向けて延びる側縁部(60)を含み、側縁部(60)は、第1めっき膜(7)と嵌合している嵌合部を有し、嵌合部は第1の主面(1A)に交差する方向に延びる表面部分(60A)を有し、表面部分(60A)が第1めっき膜(7)と接触することにより第1めっき膜(7)と嵌合している。An electrode (5) having a first main surface (1A) and formed on the first main surface (1A); and an opening on the surface of the electrode (5); A protective film (6) formed so as to cover at least the end of the first plating film (7) formed on the electrode (5) in the opening, the protective film (6), It includes a side edge (60) extending from the side wall of the opening toward the inside of the opening, and the side edge (60) has a fitting portion fitted to the first plating film (7) and is fitted. The portion has a surface portion (60A) extending in a direction crossing the first main surface (1A), and the surface portion (60A) comes into contact with the first plating film (7) to thereby form the first plating film (7). It is mated with.
Description
本発明は、半導体素子およびその製造方法、ならびに半導体装置に関し、特にめっき法により形成された電極構造を有する半導体素子およびその製造方法、ならびに半導体装置に関する。 The present invention relates to a semiconductor element, a manufacturing method thereof, and a semiconductor device, and more particularly to a semiconductor element having an electrode structure formed by plating, a manufacturing method thereof, and a semiconductor device.
半導体素子は、外部との電気的接続を担うリードフレームと共に、当該半導体素子を物理的および化学的に保護することを目的として、一般に樹脂封止される。このとき、半導体素子上には、リードフレームと接合されるための電極構造が形成されており、当該電極とリードフレームとは一般にはんだにより接合される。 A semiconductor element is generally sealed with a resin for the purpose of physically and chemically protecting the semiconductor element together with a lead frame that is responsible for electrical connection with the outside. At this time, an electrode structure to be joined to the lead frame is formed on the semiconductor element, and the electrode and the lead frame are generally joined by solder.
上記電極構造としては、半導体層上に形成されており、かつ端部がポリイミド等の保護膜により保護されているアルミニウム(Al)電極上に、無電解めっき液を用いてニッケル(Ni)膜、および金(Au)膜の積層膜が形成された構造が広く知られている。この場合、Al電極上に開口部を有する保護膜上にも上記積層膜が成長されるが、Ni膜を形成した後Au膜を形成する際に、電極構造に係る各材料(Al、Ni、ポリイミド等)の間での熱膨張係数の差異により、Ni膜と保護膜との界面に隙間が形成されるという問題があった。 As the electrode structure, a nickel (Ni) film using an electroless plating solution on an aluminum (Al) electrode formed on a semiconductor layer and having an end portion protected by a protective film such as polyimide, A structure in which a laminated film of gold (Au) films is formed is widely known. In this case, the laminated film is also grown on the protective film having an opening on the Al electrode. However, when forming the Au film after forming the Ni film, each material (Al, Ni, There is a problem that a gap is formed at the interface between the Ni film and the protective film due to a difference in thermal expansion coefficient between polyimide and the like.
具体的には、Ni膜のめっき成膜後であってAu膜のめっき成膜前に実施される水洗工程において、水洗に用いる水の温度(たとえば23℃)がNiめっき浴の温度(たとえば80℃以上85℃以下)よりも低いために上記電極構造に係る各材料が冷却される。この結果、これらの材料間での熱膨張係数の差異から上記隙間が形成されると考えられる。この場合、一旦隙間が形成されてしまうと上記界面は粗さを有しているため、Niめっき浴とほぼ同じ温度の金めっき浴に浸漬させたとしても、凹凸部が引っかかり元のように密着した状態には戻らない。また、Auめっき完了後にウエハが室温が室温に戻ったときにも同様の現象が生じて、Niめっき中のようにポリイミドと密着した状態ではなくなる。 Specifically, in the water washing step performed after the Ni film plating and before the Au film plating, the temperature of the water used for the water washing (for example, 23 ° C.) is the temperature of the Ni plating bath (for example, 80 ° C.). Each material according to the above electrode structure is cooled. As a result, it is considered that the gap is formed due to the difference in thermal expansion coefficient between these materials. In this case, once the gap is formed, the interface has roughness, so even if it is immersed in a gold plating bath at the same temperature as the Ni plating bath, the uneven part is caught and adheres as it is. It does not return to the state that was done. In addition, the same phenomenon occurs when the wafer temperature returns to room temperature after Au plating is completed, and the wafer is not in close contact with the polyimide as in Ni plating.
特開平10−125682号公報には、上記問題に対して、Ni膜のめっき成膜後であってAu膜のめっき成膜前に実施される水洗工程に用いる水温をNiめっき浴の温度と同等程度とすることでNi膜と保護膜との界面に隙間が生じることを抑制する、半導体素子の電極形成方法が記載されている。 In Japanese Patent Laid-Open No. 10-125682, for the above problem, the water temperature used for the water washing step after the Ni film plating and before the Au film plating is equal to the temperature of the Ni plating bath. A method for forming an electrode of a semiconductor element is described that suppresses the formation of a gap at the interface between the Ni film and the protective film.
また、半導体素子の裏面から表面の周縁に延びる補強材を半導体素子に装着させて、めっきにより積層膜を形成することにより、半導体素子に温度変動が加えられても半導体素子の変形を抑制することができ、Ni膜と保護膜との界面に隙間が生じることを抑制することができる半導体素子の電極形成方法が記載されている。 In addition, by attaching a reinforcing material extending from the back surface of the semiconductor element to the periphery of the front surface to the semiconductor element, and forming a laminated film by plating, the semiconductor element is prevented from being deformed even if temperature fluctuations are applied to the semiconductor element. A method for forming an electrode of a semiconductor element is described which can suppress the generation of a gap at the interface between the Ni film and the protective film.
しかしながら、水洗工程に用いる水温をNiめっき浴の温度と同等程度とした場合であっても、上記電極構造を有する半導体素子は、めっき浴から大気中に取り出されて水洗される際の温度変動によっても、Ni膜と保護膜との界面に隙間が生じ得る。これは、当該半導体素子においては、Ni膜と保護膜とは分子間力により密着している状態にあるため、小さな力が加えられただけでも密着状態が乱されてしまうためである。 However, even when the water temperature used in the water washing step is about the same as the temperature of the Ni plating bath, the semiconductor element having the electrode structure described above is subject to temperature fluctuations when taken out from the plating bath into the atmosphere and washed with water. However, a gap may be formed at the interface between the Ni film and the protective film. This is because in the semiconductor element, the Ni film and the protective film are in close contact with each other due to intermolecular force, and the close contact state is disturbed even if a small force is applied.
また、上記半導体素子の変形を抑制するための補強材により半導体素子を拘束した場合であっても、上記電極構造、すなわちめっき膜や保護膜等については拘束できない。そのため、これらの変位を十分に抑制することができず、電極構造を構成する材料の熱膨張係数の差異によってNi膜や保護膜が収縮してNi膜と保護膜との界面に隙間が生じることを十分に抑制することは困難である。 Even when the semiconductor element is restrained by a reinforcing material for suppressing deformation of the semiconductor element, the electrode structure, that is, the plating film, the protective film, and the like cannot be restrained. Therefore, these displacements cannot be sufficiently suppressed, and the Ni film or the protective film contracts due to the difference in thermal expansion coefficients of the materials constituting the electrode structure, resulting in a gap at the interface between the Ni film and the protective film. It is difficult to sufficiently suppress this.
この場合、上記電極構造においてその後に成膜する材料(たとえばAuめっきやはんだ)が上記隙間に侵入するため、Ni膜が自身の膜応力によりAl電極から剥離したり、実使用時の温度履歴によりAl電極にクラックが進展し、素子破壊が引き起こされるという問題があった。 In this case, since the material (for example, Au plating or solder) to be subsequently formed in the electrode structure enters the gap, the Ni film peels off from the Al electrode due to its own film stress, or due to the temperature history during actual use. There was a problem that cracks progressed in the Al electrode, causing device destruction.
本発明は上記のような課題を解決するためになされたものである。本発明の主たる目的は、めっき膜と保護膜との界面に隙間が生じることを十分に抑制することができる半導体素子およびその製造方法、ならびに半導体装置を提供することにある。 The present invention has been made to solve the above-described problems. A main object of the present invention is to provide a semiconductor element, a manufacturing method thereof, and a semiconductor device that can sufficiently prevent a gap from being generated at the interface between a plating film and a protective film.
本発明に係る半導体素子は、第1の主面を有し、第1の主面上に形成されている電極と、電極の表面上において開口部を有し、電極の少なくとも端部を覆うように形成されている保護膜と、開口部において電極上に形成されている第1めっき膜とを備え、保護膜は、開口部の側壁から開口部内に向けて延びる側縁部を含み、側縁部は、第1めっき膜と嵌合している嵌合部を有し、嵌合部は第1の主面に交差する方向に延びる表面部分を有し、表面部分が第1めっき膜と接触することにより第1めっき膜と嵌合している。 The semiconductor element according to the present invention has a first main surface, an electrode formed on the first main surface, an opening on the surface of the electrode, and covering at least an end of the electrode. And a first plating film formed on the electrode in the opening, the protective film including a side edge extending from the side wall of the opening toward the inside of the opening, and the side edge The portion has a fitting portion that is fitted to the first plating film, the fitting portion has a surface portion extending in a direction intersecting the first main surface, and the surface portion is in contact with the first plating film. By doing so, it is fitted to the first plating film.
本発明に係る半導体素子の製造方法は、第1の主面上に電極が形成されている半導体素子を準備する工程と、電極の表面上において開口部を有し、電極の少なくとも端部を覆う保護膜を形成する工程と、開口部において電極上に第1めっき膜を形成する工程とを備え、保護膜を形成する工程は、開口部の側壁から開口部内に向けて延びる側縁部を形成する工程を含み、側縁部を形成する工程では、第1の主面に交差する方向に延びる表面部分を有し、表面部分が第1めっき膜と接触することにより第1めっき膜と嵌合する嵌合部を形成する。 The method of manufacturing a semiconductor device according to the present invention includes a step of preparing a semiconductor device having an electrode formed on a first main surface, an opening on the surface of the electrode, and covering at least an end of the electrode A step of forming a protective film and a step of forming a first plating film on the electrode in the opening, and the step of forming the protective film forms a side edge extending from the side wall of the opening toward the inside of the opening. The step of forming the side edge portion includes a surface portion extending in a direction intersecting the first main surface, and the surface portion is brought into contact with the first plating film so as to be fitted with the first plating film. The fitting part to be formed is formed.
本発明によれば、めっき膜と保護膜との界面に隙間が生じることを十分に抑制することができる半導体素子およびその製造方法、ならびに半導体装置を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the semiconductor element which can fully suppress that a clearance gap produces in the interface of a plating film and a protective film, its manufacturing method, and a semiconductor device can be provided.
以下、図面に基づいて本発明の実施の形態を説明する。なお、以下の図面において、同一または相当する部分には同一の参照番号を付し、その説明は繰り返さない。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. In the following drawings, the same or corresponding parts are denoted by the same reference numerals, and the description thereof will not be repeated.
(実施の形態1)
以下、本発明の実施の形態1について説明する。まず、図1を参照して、実施の形態1に係る半導体素子10の構成を説明する。半導体素子10は、半導体基板1上に所定のデバイス構造が形成された半導体素子である。半導体素子10は、外部と熱的に接続されている熱拡散板2と、外部と電気的に接続されているリードフレーム3との間に挟まれるように配置されている。半導体基板1はリードフレーム3と対向する第1の主面1Aと、第1の主面1Aと反対側に位置して熱拡散板2と対向する第2の主面1Bとを有している。第1の主面1Aには電極5が形成されており、電極5はリードフレーム3とはんだ4等を介して接合されている。第2の主面2Bには裏面電極(図示しない)が形成されており、該裏面電極ははんだ4を介して熱拡散板2と接合されている。(Embodiment 1)
Embodiment 1 of the present invention will be described below. First, the configuration of the semiconductor element 10 according to the first embodiment will be described with reference to FIG. The semiconductor element 10 is a semiconductor element in which a predetermined device structure is formed on the semiconductor substrate 1. The semiconductor element 10 is disposed so as to be sandwiched between the heat diffusion plate 2 that is thermally connected to the outside and the lead frame 3 that is electrically connected to the outside. The semiconductor substrate 1 has a first main surface 1A that opposes the lead frame 3, and a second main surface 1B that opposes the heat diffusion plate 2 and is located on the opposite side of the first main surface 1A. . An electrode 5 is formed on the first main surface 1A, and the electrode 5 is joined to the lead frame 3 via solder 4 or the like. A back electrode (not shown) is formed on the second main surface 2 </ b> B, and the back electrode is joined to the heat diffusion plate 2 via the solder 4.
半導体基板1を構成する材料は、任意の半導体材料とすることができ、たとえば炭化珪素(SiC)である。電極5を構成する材料は、任意の導電材料とすることができ、たとえば純アルミニウム(Al)である。他に、電極5を構成する材料は、珪素(Si)や銅(Cu)を含むAl合金、Cuやニッケル(Ni)を主成分とする合金であってもよい。 The material constituting semiconductor substrate 1 can be any semiconductor material, for example, silicon carbide (SiC). The material constituting the electrode 5 can be any conductive material, for example, pure aluminum (Al). In addition, the material constituting the electrode 5 may be an Al alloy containing silicon (Si) or copper (Cu), or an alloy containing Cu or nickel (Ni) as a main component.
半導体基板1の第1の主面1A上には、電極5を含む電極構造が形成されている。具体的には、電極5の端部(第1の主面1Aと交差する電極5の端面および当該端面から一定距離だけ電極5の中央部側に位置する部分)を覆うように、保護膜6が形成されている。保護膜6は電極5の中央部上において開口部を有している。保護膜6は、一般的な任意の保護膜により構成されていればよく、たとえばポリイミド膜として構成されていてもよいし、無機膜の積層構造として構成されていてもよい。また、感光性を有している材料で構成されていてもよいし、有していない材料で構成されていてもよい。保護膜6の膜厚は、4μm以上10μm以下である。 An electrode structure including the electrode 5 is formed on the first main surface 1 </ b> A of the semiconductor substrate 1. Specifically, the protective film 6 covers the end portion of the electrode 5 (the end surface of the electrode 5 that intersects the first main surface 1A and the portion located on the central portion side of the electrode 5 by a certain distance from the end surface). Is formed. The protective film 6 has an opening on the central portion of the electrode 5. The protective film 6 only needs to be composed of a general arbitrary protective film, and may be composed of, for example, a polyimide film or a laminated structure of inorganic films. Moreover, it may be comprised with the material which has photosensitivity, and may be comprised with the material which does not have. The film thickness of the protective film 6 is 4 μm or more and 10 μm or less.
図2を参照して、保護膜6の開口部の側壁6Eには、開口部内に向けて延びる側縁部60が形成されている。側縁部60は、半導体基板1の第1の主面1Aと交差する方向に延びる表面部分60Aおよび側端部分60Bを有している。 Referring to FIG. 2, side edge 60 extending toward the inside of the opening is formed on side wall 6 </ b> E of the opening of protective film 6. The side edge 60 has a surface portion 60A and a side end portion 60B extending in a direction intersecting with the first main surface 1A of the semiconductor substrate 1.
表面部分60Aは、側端部分60Bと比べて側壁6E側に位置し、保護膜6の側壁6Eと連なるように形成されている。側端部分60Bは、保護膜6において表面部分60Aよりも開口部の内側に位置し、表面部分60Aと連なるように形成されている。表面部分60Aと側壁6Eとが成す角度は鋭角であり、表面部分60Aと側端部分60Bとが成す角度は鋭角である。言い換えると、表面部分60Aは第1の主面1Aに対して傾斜している。つまり、表面部分60Aと側端部分60Bとが連なる領域、すなわち開口部の内側に位置している部分の厚みが、表面部分60Aと側壁6Eとが連なる領域、すなわち開口部の側壁6E側に位置する部分の厚みよりも厚い。 60 A of surface parts are located in the side wall 6E side compared with the side edge part 60B, and are formed so that the side wall 6E of the protective film 6 may be continued. The side end portion 60B is located on the inner side of the opening in the protective film 6 than the surface portion 60A, and is formed to be continuous with the surface portion 60A. The angle formed by the surface portion 60A and the side wall 6E is an acute angle, and the angle formed by the surface portion 60A and the side end portion 60B is an acute angle. In other words, the surface portion 60A is inclined with respect to the first main surface 1A. That is, the thickness of the region where the surface portion 60A and the side end portion 60B are connected, that is, the portion located inside the opening, is located on the region where the surface portion 60A and the side wall 6E are connected, ie, the side wall 6E side of the opening. It is thicker than the thickness of the part to be.
表面部分60Aと側壁6Eとが連なる領域、すなわち開口部の側壁6E側に位置する部分の厚みはたとえば3μmであり、側縁部60の開口部の内側に位置している部分の厚みと側壁6E側に位置する部分の厚みとの差はたとえば0.01μm以上1μm以下であり、好ましくは0.1μm以上0.5μmである。半導体基板1の第1の主面1Aに沿った方向における側縁部60の幅、すなわち保護膜6の側壁6Eから最も開口部の内側に位置する部分までの距離は、たとえば1μm以上10μm以下であり、好ましくは3μm以上7μmである。 The thickness of the region where the surface portion 60A and the side wall 6E are connected, that is, the portion located on the side wall 6E side of the opening is, for example, 3 μm, and the thickness of the portion located inside the opening of the side edge 60 and the side wall 6E. The difference with the thickness of the part located in the side is 0.01 micrometer or more and 1 micrometer or less, for example, Preferably they are 0.1 micrometer or more and 0.5 micrometer. The width of the side edge portion 60 in the direction along the first main surface 1A of the semiconductor substrate 1, that is, the distance from the side wall 6E of the protective film 6 to the innermost portion of the opening is, for example, 1 μm or more and 10 μm or less. Yes, preferably 3 μm or more and 7 μm.
保護膜6の開口部内における電極5上、および保護膜6の側縁部60の表面部分60Aの少なくとも一部上にはNi膜7が形成されている。Ni膜7は、側縁部60の表面部分60A上において、表面部分60Aと側端部分60Bとが成す稜線から所定の距離だけ側壁6E側にせり出すように形成されている。このとき、側縁部60において表面部分60Aと側端部分60Bとが連なる領域の厚みが、表面部分60Aと側壁6Eとが連なる領域の厚みよりも厚いため、表面部分60Aと側端部分60Bとが連なる側縁部60上に位置するNi膜7よりも、表面部分60Aと側壁6Eとが連なる側縁部60上に位置するNi膜7は第1の主面1Aと垂直な方向において第1の主面1A側に突出するように形成されている。 The Ni film 7 is formed on the electrode 5 in the opening of the protective film 6 and on at least a part of the surface portion 60 </ b> A of the side edge 60 of the protective film 6. The Ni film 7 is formed on the surface portion 60A of the side edge 60 so as to protrude toward the side wall 6E by a predetermined distance from the ridge line formed by the surface portion 60A and the side end portion 60B. At this time, since the thickness of the region where the surface portion 60A and the side end portion 60B are continuous in the side edge portion 60 is thicker than the thickness of the region where the surface portion 60A and the sidewall 6E are continuous, the surface portion 60A and the side end portion 60B The Ni film 7 located on the side edge portion 60 where the surface portion 60A and the side wall 6E are continuous is more in the direction perpendicular to the first main surface 1A than the Ni film 7 located on the side edge portion 60 where the first main surface 1A is continuous. It is formed so as to protrude to the main surface 1A side.
つまり、側縁部60とNi膜7とは表面部分60Aの少なくとも一部において面接触しており、側縁部60とNi膜7とは表面部分60A上において嵌合している。保護膜6とNi膜7との界面は、表面部分60AとNi膜7との界面と、側端部分60BとNi膜7との界面を含んで形成されているが、そのうち少なくともNi膜7の表層側に位置する表面部分60Aとの界面には隙間が形成されてない。Ni膜7の膜厚は、1μm以上10μm以下であり、好ましくは3μm以上7μm以下である。 That is, the side edge portion 60 and the Ni film 7 are in surface contact with at least a part of the surface portion 60A, and the side edge portion 60 and the Ni film 7 are fitted on the surface portion 60A. The interface between the protective film 6 and the Ni film 7 includes the interface between the surface portion 60A and the Ni film 7 and the interface between the side end portion 60B and the Ni film 7, of which at least the Ni film 7 is formed. No gap is formed at the interface with the surface portion 60A located on the surface layer side. The film thickness of the Ni film 7 is not less than 1 μm and not more than 10 μm, preferably not less than 3 μm and not more than 7 μm.
Ni膜7の電極5と接する面と反対側に位置する面上にはAu膜8が形成されている。Au膜8の膜厚は0.01μm以上0.3μm以下である。Au膜8は、めっき法により成膜され得るが、保護膜6とNi膜7との上記界面には形成されていない。 An Au film 8 is formed on the surface of the Ni film 7 located on the side opposite to the surface in contact with the electrode 5. The film thickness of the Au film 8 is not less than 0.01 μm and not more than 0.3 μm. The Au film 8 can be formed by a plating method, but is not formed at the interface between the protective film 6 and the Ni film 7.
Au膜8上にははんだ4が形成されており、はんだ4を介してリードフレーム3とNi膜7とが接合されている(図1中では、Au膜8を便宜上記載したが、実際にはんだ接合するとAu膜8は完全にはんだ4内に拡散し、Ni膜7とはんだ4とが合金化して接合される)。 Solder 4 is formed on the Au film 8, and the lead frame 3 and the Ni film 7 are joined via the solder 4 (in FIG. 1, the Au film 8 is described for convenience. When bonded, the Au film 8 is completely diffused into the solder 4, and the Ni film 7 and the solder 4 are alloyed and bonded).
図1および図2(a)は半導体素子10の概略断面図を示しており、保護膜6の側縁部60は、平面状に形成されている表面部分60Aおよび側端部分60Bの2平面で規定されているが、これに限られるものではない。図2(b)を参照して、たとえば、表面部分60Aおよび側端部分60Bのうち少なくとも一方が曲面状に形成されていてもよい。また、側縁部60は、表面部分60Aよりも保護膜6の側壁6E側において表面部分60A以外の部分(たとえば第1の主面1Aと略平行な面で規定されている略平坦部分)を有していてもよい。 FIG. 1 and FIG. 2A are schematic cross-sectional views of the semiconductor element 10, and the side edge 60 of the protective film 6 has two planes of a surface portion 60 </ b> A and a side end portion 60 </ b> B that are formed in a planar shape. It is defined but not limited to this. Referring to FIG. 2B, for example, at least one of the surface portion 60A and the side end portion 60B may be formed in a curved shape. Further, the side edge portion 60 is a portion other than the surface portion 60A on the side of the side wall 6E of the protective film 6 relative to the surface portion 60A (for example, a substantially flat portion defined by a surface substantially parallel to the first main surface 1A). You may have.
次に、図3を参照して、実施の形態1に係る半導体素子の製造方法について説明する。なお、図3に示す各図は、図1と異なり、表面部分60Aおよび側端部分60Bが曲面状に形成されている場合において実施の形態1に係る半導体素子の製造方法を説明する概略断面図である。 Next, with reference to FIG. 3, the manufacturing method of the semiconductor device according to the first embodiment will be described. 3 is a schematic cross-sectional view for explaining the method of manufacturing the semiconductor device according to the first embodiment when the surface portion 60A and the side end portion 60B are formed in a curved shape, unlike FIG. It is.
実施の形態1に係る半導体素子の製造方法は、第1の主面1A上に電極5が形成されている半導体素子(半導体基板1)を準備する工程(S10)と、電極5の表面上において開口部を有し、電極5の少なくとも端部を覆う保護膜6を形成する工程(S20)と、開口部において電極5上に第1めっき膜としてのNi膜7を形成する工程(S30)とを備える。 In the method of manufacturing a semiconductor element according to the first embodiment, a step (S10) of preparing a semiconductor element (semiconductor substrate 1) in which an electrode 5 is formed on a first main surface 1A, and a surface of the electrode 5 are prepared. A step (S20) of forming a protective film 6 having an opening and covering at least an end of the electrode 5, and a step of forming a Ni film 7 as a first plating film on the electrode 5 in the opening (S30) Is provided.
まず、第1の主面1A上に電極5が形成されている半導体素子(半導体基板1)を準備する(工程(S10))。第1の主面1A上に電極5が形成されている半導体基板1は、任意の方法で準備すればよい。また、半導体基板1の第2の主面1B上には裏面電極が形成されている。 First, a semiconductor element (semiconductor substrate 1) having an electrode 5 formed on the first main surface 1A is prepared (step (S10)). The semiconductor substrate 1 on which the electrode 5 is formed on the first main surface 1A may be prepared by any method. A back electrode is formed on the second main surface 1B of the semiconductor substrate 1.
次に、電極5の表面上において開口部を有し、電極5の少なくとも端部を覆う保護膜6を形成する(工程(S20))。本工程(S20)では、保護膜6の開口部の側壁から開口部内に向けて延びる側縁部60を形成する工程を含む。また、本工程(S20)では、保護膜6を下層保護膜61bと上層保護膜62bの2層に分けて形成する。なお、以下、各保護膜について加熱処理(キュア)前のものに添え字a、キュア後のものに添え字bを付して標記する。 Next, the protective film 6 having an opening on the surface of the electrode 5 and covering at least the end of the electrode 5 is formed (step (S20)). This step (S20) includes a step of forming the side edge 60 extending from the side wall of the opening of the protective film 6 into the opening. In this step (S20), the protective film 6 is formed in two layers, a lower protective film 61b and an upper protective film 62b. In the following, each protective film is labeled with a suffix a before heating treatment (curing) and a suffix b after curing.
図3(a)を参照して、先の工程(S10)において準備した半導体基板1の第1の主面1A上に下層保護膜61aを形成する。下層保護膜61aを構成する材料はたとえばポリイミドである。具体的には、はじめにポリイミドをスピンコート法により電極5が形成されている第1の主面1A上に塗布する。次に、ホットプレートに半導体基板1を載置して、たとえば加熱温度120℃で加熱時間3分の加熱処理を行って下層保護膜61aを乾燥させる。次に、写真製版加工を利用して、電極5の表面上に開口部を有し、少なくとも電極5の端部が覆われているように下層保護膜61aをパターニングする。下層保護膜61aのパターニングは、次工程(加熱処理工程)を行って下層保護膜61bを形成したときにその開口端部が最終的に側縁部60となるように行われる。これにより図3(a)に示す半導体素子が形成される。 Referring to FIG. 3A, lower protective film 61a is formed on first main surface 1A of semiconductor substrate 1 prepared in the previous step (S10). The material constituting the lower protective film 61a is, for example, polyimide. Specifically, first, polyimide is applied onto the first main surface 1A on which the electrode 5 is formed by spin coating. Next, the semiconductor substrate 1 is placed on a hot plate and, for example, a heat treatment is performed at a heating temperature of 120 ° C. for a heating time of 3 minutes to dry the lower protective film 61a. Next, using the photoengraving process, the lower protective film 61a is patterned so that it has an opening on the surface of the electrode 5 and at least the end of the electrode 5 is covered. The patterning of the lower protective film 61a is performed such that the opening end portion finally becomes the side edge 60 when the lower protective film 61b is formed by performing the next process (heat treatment process). As a result, the semiconductor element shown in FIG.
次に、図3(b)を参照して、図3(a)に示す半導体素子を加熱処理して、下層保護膜61aを硬化させる。具体的には、たとえば加熱温度350℃で加熱時間1時間程度の加熱処理を行う。これにより、下層保護膜61aは大きく収縮してキュア後の下層保護膜61bとなるが、このときその開口端部は後退しつつ凸状となる。この結果、下層保護膜61bの開口端部には、第1の主面1Aと交差する方向に延びる少なくとも2つの面が形成される。凸状部分も含めて下層保護膜61bの膜厚は、後の工程において形成されるNi膜7の膜厚よりも薄くなるように設けられている。 Next, referring to FIG. 3B, the semiconductor element shown in FIG. 3A is heat-treated to cure the lower protective film 61a. Specifically, for example, heat treatment is performed at a heating temperature of 350 ° C. for a heating time of about 1 hour. As a result, the lower protective film 61a is greatly contracted to become a cured lower protective film 61b, and at this time, the opening end portion thereof becomes convex while being retracted. As a result, at least two surfaces extending in a direction intersecting with the first main surface 1A are formed at the opening end of the lower protective film 61b. The film thickness of the lower protective film 61b including the convex portion is provided so as to be thinner than the film thickness of the Ni film 7 formed in a later process.
次に、図3(c)を参照して、下層保護膜61b上に上層保護膜62aを形成する。上層保護膜62aは、上述した下層保護膜61aと同様の方法で形成することができる。上層保護膜62aは、下層保護膜61bの開口部よりも大きく、下層保護膜61bの開口端部よりも後退している開口端部を有するように形成される。 Next, referring to FIG. 3C, an upper protective film 62a is formed on the lower protective film 61b. The upper protective film 62a can be formed by the same method as the lower protective film 61a described above. The upper protective film 62a is formed to have an opening end that is larger than the opening of the lower protective film 61b and recedes from the opening end of the lower protective film 61b.
図3(d)を参照して、さらに上層保護膜62aは、所定の加熱処理がなされることにより硬化され、上層保護膜62bとなる。上層保護膜62bの膜厚は、半導体素子に求められる電気絶縁特性に応じて設けられていればよく、好ましくはNi膜7の膜厚よりも厚く設けられている。上層保護膜62bの開口部の内側に位置する端面62Eは、保護膜6の側壁6Eとなる。 Referring to FIG. 3D, the upper protective film 62a is further cured by a predetermined heat treatment to become an upper protective film 62b. The film thickness of the upper protective film 62b may be provided in accordance with the electrical insulation characteristics required for the semiconductor element, and is preferably thicker than the film thickness of the Ni film 7. The end face 62E located inside the opening of the upper protective film 62b becomes the side wall 6E of the protective film 6.
本実施の形態では、下層保護膜61a,61bと上層保護膜62a,62bとが同一の材料で構成されているが、これに限られるものではない。たとえば、下層保護膜61a,61bは比較的熱収縮率の高いポリイミド材料で、上層保護膜62a,62bは比較的熱収縮率の低い材料で構成されていてもよい。下層保護膜61a,61bは、収縮により表面部分60Aを有する側端部分60Bとして形成される必要があるため、熱収縮率の高い材料で構成されるのが好ましい。これに対し、上層保護膜62a,62bは、側端部分60Bのような凹凸が形成される必要がないため、熱収縮率の低い材料で構成されることができる。 In the present embodiment, the lower protective films 61a and 61b and the upper protective films 62a and 62b are made of the same material, but the present invention is not limited to this. For example, the lower protective films 61a and 61b may be made of a polyimide material having a relatively high heat shrinkage rate, and the upper protective films 62a and 62b may be made of a material having a relatively low heat shrinkage rate. Since the lower protective films 61a and 61b need to be formed as the side end portion 60B having the surface portion 60A by contraction, it is preferable that the lower layer protection films 61a and 61b are made of a material having a high thermal contraction rate. On the other hand, the upper protective films 62a and 62b do not need to be uneven as in the side end portion 60B, and can be made of a material having a low thermal shrinkage rate.
次に、保護膜6の開口部において電極5上にNi膜7を形成する(工程(S30))。Ni膜7は、一般的な無電解めっき法により形成することができる。これにより、先の工程(S20)において形成した側縁部60と嵌合するようにNi膜7を形成することができる。無電解Niめっきでの浴温度は80℃以上85℃以下である。Ni膜7を形成し終えた後、Niめっき浴から大気中に取りだし、純水により半導体素子を洗浄する。純水の温度は所定の温度であればよく、たとえば23℃程度であればよい。つまり、純水をNiめっき浴の温度と同程度にまで加熱処理する必要がない。このとき、Niめっき浴の温度と純水の温度との間の約60℃の温度差により、保護膜6やNi膜7が収縮しても、傾斜した表面部分60Aにおける側縁部60とNi膜7との界面にはそれぞれの部材が収縮することに起因する押圧力が発生するので、少なくとも表面部分60AとNi膜7との界面において隙間が生じることは抑制されている。 Next, the Ni film 7 is formed on the electrode 5 in the opening of the protective film 6 (step (S30)). The Ni film 7 can be formed by a general electroless plating method. Thereby, the Ni film 7 can be formed so as to be fitted to the side edge portion 60 formed in the previous step (S20). The bath temperature in electroless Ni plating is 80 ° C. or higher and 85 ° C. or lower. After completing the formation of the Ni film 7, the Ni film is taken out from the Ni plating bath and the semiconductor element is washed with pure water. The temperature of pure water should just be a predetermined temperature, for example, should just be about 23 degreeC. That is, it is not necessary to heat the pure water to the same level as the temperature of the Ni plating bath. At this time, even if the protective film 6 and the Ni film 7 contract due to a temperature difference of about 60 ° C. between the temperature of the Ni plating bath and the temperature of pure water, the side edge portion 60 and the Ni in the inclined surface portion 60A are contracted. Since a pressing force due to contraction of each member is generated at the interface with the film 7, the generation of a gap at least at the interface between the surface portion 60A and the Ni film 7 is suppressed.
つまり、表面部分60Aは第1の主面1Aと交差する方向に延びており、かつ、側縁部60において表面部分60Aと側端部分60Bとが連なる領域の厚みが表面部分60Aと側壁6Eとが連なる領域の厚みよりも厚く形成されていることにより、Ni膜7において表面部分60Aと側端部分60Bとが連なる側縁部60上に位置する部分よりも、表面部分60Aと側壁6Eとが連なる側縁部60上に位置する部分は第1の主面1Aと垂直な方向において第1の主面1A側に突出するように形成されている。そのため、Ni膜7が主に第1の主面1Aの沿った方向でかつ保護膜6の開口部の内側に向かう方向に収縮し、かつ、保護膜6がNi膜7とは反対方向に収縮しても、表面部分60AとNi膜7との界面は密着が保たれて隙間が生じない。なお、上記収縮において、側端部分60BとNi膜7との界面においては密着が保たれず、隙間が生じ得る。 That is, the surface portion 60A extends in a direction intersecting the first main surface 1A, and the thickness of the region where the surface portion 60A and the side end portion 60B are continuous at the side edge portion 60 is the surface portion 60A and the side wall 6E. Is formed to be thicker than the thickness of the continuous region, the surface portion 60A and the side wall 6E are formed in the Ni film 7 rather than the portion located on the side edge portion 60 where the surface portion 60A and the side end portion 60B are continuous. A portion located on the continuous side edge 60 is formed so as to protrude toward the first main surface 1A in a direction perpendicular to the first main surface 1A. Therefore, the Ni film 7 contracts mainly in the direction along the first main surface 1 </ b> A and toward the inside of the opening of the protective film 6, and the protective film 6 contracts in the direction opposite to the Ni film 7. Even so, the interface between the surface portion 60A and the Ni film 7 is kept in close contact, and no gap is generated. In the above contraction, close contact is not maintained at the interface between the side end portion 60B and the Ni film 7, and a gap may be generated.
次に、Ni膜7において電極5と接する面と反対側に位置する面上に、Au膜8を形成する。Au膜8は、一般的な無電解めっき法により形成することができる。上述のように、側縁部60の表面部分60AとNi膜7との界面には隙間が形成されていないため、Auめっき液が当該界面に侵入することを抑制することができる。その結果、当該界面に面したNi膜7の腐食を抑制し、かつ当該界面にAu膜が形成されることを防止することができる。この結果、Ni膜7の剥離や電極5にクラックが生じることを防止することができる。 Next, an Au film 8 is formed on the surface of the Ni film 7 that is opposite to the surface in contact with the electrode 5. The Au film 8 can be formed by a general electroless plating method. As described above, since no gap is formed at the interface between the surface portion 60A of the side edge portion 60 and the Ni film 7, it is possible to prevent the Au plating solution from entering the interface. As a result, corrosion of the Ni film 7 facing the interface can be suppressed, and an Au film can be prevented from being formed at the interface. As a result, it is possible to prevent the Ni film 7 from peeling and the electrode 5 from cracking.
また、図4を参照して、側端部分60BとNi膜7との界面においては密着が保たれず、隙間が生じ得るが、このような隙間が発生したとしても表面部分60AとNi膜7との界面の密着(嵌合)が保たれているため、当該隙間は外部空間と連通されておらず、Auめっき液が当該隙間に侵入することを防止することができる。 Further, referring to FIG. 4, close contact is not maintained at the interface between the side end portion 60B and the Ni film 7, and a gap may be formed. Even if such a gap occurs, the surface portion 60A and the Ni film 7 are formed. Therefore, the gap is not communicated with the external space, and the Au plating solution can be prevented from entering the gap.
無電解Auめっきでの浴温度は80℃程度である。Au膜8を形成した後、Auめっき浴から大気中に取りだし、純水により半導体素子を洗浄する。このときも、Ni膜7形成後と同様に、純水の温度は所定の温度であればよく、たとえば23℃程度であればよい。この場合にも、上述の理由により側縁部60の表面部分60AとNi膜7との界面には隙間が形成されない。 The bath temperature in electroless Au plating is about 80 ° C. After forming the Au film 8, it is taken out from the Au plating bath to the atmosphere, and the semiconductor element is washed with pure water. Also at this time, the temperature of pure water may be a predetermined temperature, for example, about 23 ° C., as in the case after the Ni film 7 is formed. Also in this case, no gap is formed at the interface between the surface portion 60A of the side edge portion 60 and the Ni film 7 for the reason described above.
なお、Ni膜7を形成する工程(S30)において第2の主面1B上に形成されている裏面電極を保護するために、第2の主面1B上には予め保護部材を貼り付けておくのが好ましい。保護部材には、たとえば主な構成材料が粘着材にアクリル系またはシリコン系接着剤、基材にPETやポリオレフィンなどの高分子樹脂である保護テープや、石英基板などを用いることができる。 In order to protect the back electrode formed on the second main surface 1B in the step of forming the Ni film 7 (S30), a protective member is pasted on the second main surface 1B in advance. Is preferred. As the protective member, for example, an acrylic or silicon adhesive as a main constituent material can be used as an adhesive material, and a protective tape made of a polymer resin such as PET or polyolefin as a base material, a quartz substrate, or the like can be used.
以上のようにして得られた半導体素子10を用いて、実施の形態1に係る半導体装置100を得ることができる。半導体素子10をはんだ4を介して熱拡散板2上に接合し、さらにAu膜8とリードフレーム3とをはんだ4を介して接合する。上述のように、側縁部60の表面部分60AとNi膜7との界面に隙間が生じていないため、当該隙間にはんだ4が侵入することを防止することができる。以上のようにして、実施の形態1に係る半導体装置100を得ることができる。 The semiconductor device 100 according to the first embodiment can be obtained using the semiconductor element 10 obtained as described above. The semiconductor element 10 is bonded onto the heat diffusion plate 2 via the solder 4, and the Au film 8 and the lead frame 3 are bonded via the solder 4. As described above, since no gap is generated at the interface between the surface portion 60A of the side edge portion 60 and the Ni film 7, it is possible to prevent the solder 4 from entering the gap. As described above, the semiconductor device 100 according to the first embodiment can be obtained.
次に、実施の形態1に係る半導体素子およびその製造方法の作用効果について説明する。実施の形態1に係る半導体素子10は、保護膜6の開口部の側壁から開口部内に向けて延びる側縁部60を備え、側縁部60は第1の主面1Aに交差する方向に延びる表面部分60Aを有している。側縁部60において表面部分60Aは、Ni膜7と接触することによりNi膜7と嵌合している嵌合部を形成している。 Next, functions and effects of the semiconductor device and the manufacturing method thereof according to the first embodiment will be described. The semiconductor element 10 according to the first embodiment includes a side edge 60 extending from the side wall of the opening of the protective film 6 toward the inside of the opening, and the side edge 60 extends in a direction intersecting the first main surface 1A. It has a surface portion 60A. The surface portion 60 </ b> A in the side edge portion 60 is in contact with the Ni film 7 to form a fitting portion that is fitted with the Ni film 7.
これにより、Ni膜7およびAu膜8をめっき法により成膜する場合であっても、めっき工程でのめっき浴の温度とめっき浴から取り出したときの大気の温度との差異、さらにはめっき工程でのめっき浴の温度とめっき後の水洗工程での純水の温度との差異に起因して半導体素子10を構成する各部材が収縮し、保護膜6の側縁部60における表面部分60AとNi膜7との界面に隙間が生じることを防止することができる。 Thereby, even when the Ni film 7 and the Au film 8 are formed by the plating method, the difference between the temperature of the plating bath in the plating process and the temperature of the atmosphere when taken out from the plating bath, and further the plating process Each member constituting the semiconductor element 10 is contracted due to the difference between the temperature of the plating bath in the substrate and the temperature of pure water in the washing step after plating, and the surface portion 60A in the side edge portion 60 of the protective film 6 It is possible to prevent a gap from occurring at the interface with the Ni film 7.
この結果、半導体素子10を用いて製造された半導体装置100では、保護膜6とNi膜7との界面にAu膜8やはんだ4等が析出することを抑制することができるため、半導体素子10の実使用時の温度履歴により、Ni膜7において保護膜6と接する部分で局部腐食が進行することを抑制することができる。 As a result, in the semiconductor device 100 manufactured using the semiconductor element 10, it is possible to prevent the Au film 8, the solder 4, and the like from being deposited at the interface between the protective film 6 and the Ni film 7. Due to the temperature history during actual use, it is possible to suppress the local corrosion from proceeding at the portion of the Ni film 7 that is in contact with the protective film 6.
Ni膜7の局部腐食は、Ni膜7上に置換型Auメッキ液を用いてAu膜8を形成する際に、保護膜6とNi膜7の界面に侵入したAuメッキ液中のAuイオンが、Ni膜7を溶出させることにより発生した電子を受け取り、Ni膜7上に析出することで発生する。このとき、Ni膜7の膜質が均一である場合には、Ni膜7において保護膜6との界面に位置する部分ではなく、主にNi膜7の表面(遮るものが無く表出している面)が溶出することにより当該表面にAuが析出する。しかし、Ni膜7の膜質が不均一である場合には、Ni金属として安定でない部分、すなわちNi膜7において保護膜6との界面に位置する部分の溶出速度が、Ni膜7の表面の溶出速度よりも速くなる。その結果、Ni膜7において保護膜6との界面に位置する部分で局部腐食が進行することとなる。 The local corrosion of the Ni film 7 is caused by Au ions in the Au plating solution that have entered the interface between the protective film 6 and the Ni film 7 when the Au film 8 is formed on the Ni film 7 using a substitutional Au plating solution. This occurs when electrons generated by elution of the Ni film 7 are received and deposited on the Ni film 7. At this time, when the film quality of the Ni film 7 is uniform, it is not the portion of the Ni film 7 located at the interface with the protective film 6 but mainly the surface of the Ni film 7 (the surface exposed without any obstruction). ) Elutes to deposit Au on the surface. However, when the film quality of the Ni film 7 is non-uniform, the elution rate of the part that is not stable as Ni metal, that is, the part located at the interface with the protective film 6 in the Ni film 7 is the elution rate of the surface of the Ni film 7. Be faster than speed. As a result, local corrosion proceeds at a portion of the Ni film 7 located at the interface with the protective film 6.
本実施の形態に係る半導体素子10では、保護膜6の表面部分60AとNi膜7との界面に隙間が生じることを防止することができるため、仮にNi膜7の膜質の均一性が低い場合にも、保護膜6との界面に位置する部分に反応性の高いAuメッキ液が多量に供給されることを防止することができるため、Ni膜7の局部腐食の進行を防止することができる。その結果、電極5にクラックが進展したり、電極5からNi膜7が剥離して素子破壊に至るといった問題の発生を十分に抑制することができる。 In the semiconductor element 10 according to the present embodiment, it is possible to prevent a gap from being generated at the interface between the surface portion 60A of the protective film 6 and the Ni film 7, and therefore the uniformity of the film quality of the Ni film 7 is low. In addition, since it is possible to prevent a large amount of highly reactive Au plating solution from being supplied to the portion located at the interface with the protective film 6, it is possible to prevent the local corrosion of the Ni film 7 from proceeding. . As a result, it is possible to sufficiently suppress the occurrence of problems such as cracks developing in the electrode 5 and the Ni film 7 being peeled off from the electrode 5 to cause element destruction.
また、実施の形態1に係る半導体素子の製造方法では、保護膜6を形成する工程において、保護膜6を2層の積層構造として形成することによりNi膜7の膜厚よりも薄い側縁部60を容易に形成することができる。さらに、側縁部60における表面部分60Aは、熱収縮によって容易に形成することができる。さらに、Ni膜7およびAu膜8を、いずれも一般的な無電解めっき法により形成し、かつ、水洗工程に用いる純水をめっき浴の温度程度にまで加熱しなくても、保護膜6とNi膜7との界面に隙間が生じることを抑制しながら半導体素子10を製造することができる。その結果、組み立て工数や製造コスト等を増加させることなく、容易に実施の形態1に係る半導体素子10を得ることができる。 Further, in the method of manufacturing a semiconductor element according to the first embodiment, in the step of forming the protective film 6, the side edge portion thinner than the thickness of the Ni film 7 is formed by forming the protective film 6 as a two-layer laminated structure. 60 can be formed easily. Furthermore, the surface portion 60A in the side edge portion 60 can be easily formed by heat shrinkage. Furthermore, the Ni film 7 and the Au film 8 are both formed by a general electroless plating method, and the protective film 6 can be formed without heating the pure water used in the washing step to the temperature of the plating bath. The semiconductor element 10 can be manufactured while suppressing the generation of a gap at the interface with the Ni film 7. As a result, the semiconductor element 10 according to the first embodiment can be easily obtained without increasing the number of assembly steps, manufacturing costs, and the like.
なお、図1および図2(a)に示すような側縁部60は、実施の形態1に係る半導体素子の製造方法を用いて以下のようにして形成することができる。たとえば保護膜6における下層保護膜61a,61bを構成する材料に熱収縮率の小さいポリイミド材料を用いること、および保護膜6に対するキュア温度を低温化することのうちの少なくとも一方を行うことによって、ポリイミドの収縮量を抑制することができる。その結果、図1および図2(a)に示すような側縁部60を形成することができる。 The side edge portion 60 as shown in FIGS. 1 and 2A can be formed as follows using the method for manufacturing a semiconductor element according to the first embodiment. For example, by using at least one of using a polyimide material having a low thermal shrinkage as a material constituting the lower protective films 61a and 61b in the protective film 6 and lowering the curing temperature for the protective film 6, polyimide is obtained. The amount of shrinkage can be suppressed. As a result, the side edge portion 60 as shown in FIGS. 1 and 2A can be formed.
実施の形態1に係る半導体素子では、図5を参照して、上述のように表面部分60Aおよび側端部分60Bが曲面状に形成されていてもよい。さらに、側縁部60は、表面部分60Aよりも保護膜6の側壁6E側において第1の主面1Aと略平行な面で規定されている略平坦部分を有していてもよい。このようにしても、表面部分60Aは保護膜6やNi膜7の収縮する方向に対して交差する方向に延びており、保護膜6の側縁部60における表面部分60AとNi膜7との界面に隙間が生じることを防止することができる。 In the semiconductor element according to the first embodiment, referring to FIG. 5, surface portion 60A and side end portion 60B may be formed in a curved shape as described above. Further, the side edge 60 may have a substantially flat portion defined by a surface substantially parallel to the first main surface 1A on the side wall 6E side of the protective film 6 relative to the surface portion 60A. Even in this case, the surface portion 60 </ b> A extends in a direction intersecting with the shrinking direction of the protective film 6 and the Ni film 7, and the surface portion 60 </ b> A and the Ni film 7 at the side edge 60 of the protective film 6. It is possible to prevent a gap from occurring at the interface.
なお、実施の形態1に係る半導体素子では、半導体基板1と熱拡散板2とを接合する材料、およびAu膜8とリードフレーム3とを接合する材料にはんだ4を用いているが、これに限られるものではない。これらを接合する材料には、たとえばナノ銀(Ag)ペーストを用いてもよい。また、実施の形態1に係る半導体素子では、Alからなる電極5上に、Ni膜7およびAu膜8が積層した電極構造を有しているが、これに限られるものではない。たとえば、Ni/パラジウム(Pd)/Au、Ni/Ag、またはNi/Pd/Agなどの積層膜が保護膜6の開口部上に積層されてなる電極構造に対しても、当該保護膜6に側縁部60を形成しておくことにより、実施の形態1に係る半導体素子およびその製造方法と同様の効果を奏することができる。 In the semiconductor element according to the first embodiment, the solder 4 is used as a material for bonding the semiconductor substrate 1 and the thermal diffusion plate 2 and a material for bonding the Au film 8 and the lead frame 3. It is not limited. For example, a nano silver (Ag) paste may be used as a material for bonding them. In addition, the semiconductor element according to the first embodiment has an electrode structure in which the Ni film 7 and the Au film 8 are stacked on the electrode 5 made of Al, but is not limited thereto. For example, an electrode structure in which a laminated film such as Ni / palladium (Pd) / Au, Ni / Ag, or Ni / Pd / Ag is laminated on the opening of the protective film 6 is also applied to the protective film 6. By forming the side edge portion 60, the same effects as those of the semiconductor element and the manufacturing method thereof according to the first embodiment can be obtained.
(実施の形態2)
次に、実施の形態2に係る半導体素子およびその製造方法について説明する。図6を参照して、実施の形態2に係る半導体素子は、基本的には実施の形態1に係る半導体素子と同様の構成を備えるが、表面部分60Aが側縁部60上に形成されている凸状部分60Cの1つの面として形成されている点で異なる。(Embodiment 2)
Next, a semiconductor element and a manufacturing method thereof according to the second embodiment will be described. Referring to FIG. 6, the semiconductor element according to the second embodiment basically has the same configuration as the semiconductor element according to the first embodiment, except that surface portion 60 </ b> A is formed on side edge portion 60. It differs in that it is formed as one surface of the convex portion 60C.
具体的には、図6を参照して、側縁部60は、保護膜6の側壁6E側において第1の主面1Aと略平行な面で規定されている略平坦部分60Dと、略平行部分60Dに対して第1の主面1Aと垂直な方向の上方に突出している凸状部分60Cとを有している。 Specifically, referring to FIG. 6, side edge portion 60 is substantially parallel to substantially flat portion 60 </ b> D defined by a surface substantially parallel to first main surface 1 </ b> A on side wall 6 </ b> E side of protective film 6. It has a convex portion 60C protruding upward in a direction perpendicular to the first main surface 1A with respect to the portion 60D.
表面部分60Aは、凸状部分60Cの一つの面として形成されている。当該凸状部分60Cでは、表面部分60Aと第1の主面1Aに沿う方向において反対側に位置する面が側端部分60Bとして規定されている。言い換えれば、凸状部分60Cは、側縁部60において保護膜6の開口部と隣接する端部に形成されている。 The surface portion 60A is formed as one surface of the convex portion 60C. In the convex portion 60C, a surface located on the opposite side in the direction along the surface portion 60A and the first main surface 1A is defined as the side end portion 60B. In other words, the convex portion 60 </ b> C is formed at an end portion adjacent to the opening portion of the protective film 6 at the side edge portion 60.
この場合、側縁部60の表面部分60AとNi膜7との界面は、第1の主面1Aと垂直な方向に延びている。さらに、側縁部60において表面部分60Aと側端部分60Bとにより規定される凸状部分60Cの厚みが略平坦部分60Dの厚みよりも厚く形成されていることにより、Ni膜7において側縁部60の凸状部分60C上に位置する部分よりも、略平坦部分60D上に位置する部分は第1の主面1Aと垂直な方向において第1の主面1A側に突出するように形成されている。そのため、上述のように第1の主面1Aに沿った方向において半導体素子10の各部材が収縮した場合であっても表面部分60AとNi膜7との界面に隙間が生じることを抑制することができる。なお、図6(b)を参照して、実施の形態2に係る半導体素子においても、たとえば、表面部分60Aおよび側端部分60Bのうち少なくとも一方が曲面状に形成されていてもよい。このようにしてもこれらが平面状に形成されている場合と同様の効果を奏することができる。 In this case, the interface between the surface portion 60A of the side edge 60 and the Ni film 7 extends in a direction perpendicular to the first main surface 1A. Further, in the side edge portion 60, the convex portion 60C defined by the surface portion 60A and the side end portion 60B is formed to be thicker than the thickness of the substantially flat portion 60D. The portion positioned on the substantially flat portion 60D is formed so as to protrude toward the first main surface 1A in the direction perpendicular to the first main surface 1A rather than the portion positioned on the convex portion 60C of 60. Yes. Therefore, even when each member of the semiconductor element 10 contracts in the direction along the first main surface 1A as described above, it is possible to suppress the generation of a gap at the interface between the surface portion 60A and the Ni film 7. Can do. 6B, also in the semiconductor element according to the second embodiment, at least one of surface portion 60A and side end portion 60B may be formed in a curved surface. Even if it does in this way, there can exist an effect similar to the case where these are formed in planar shape.
図7を参照して、実施の形態2に係る半導体素子の製造方法について説明する。実施の形態2に係る半導体素子の製造方法は、実施の形態1に係る半導体素子の製造方法と基本的には同様の構成を備えるが、保護膜6を形成する工程(S20)において表面部分60Aを形成する方法が異なる。 With reference to FIG. 7, a method of manufacturing a semiconductor element according to the second embodiment will be described. The method for manufacturing a semiconductor element according to the second embodiment has basically the same configuration as the method for manufacturing a semiconductor element according to the first embodiment, but the surface portion 60A is formed in the step of forming the protective film 6 (S20). The method of forming is different.
表面部分60Aの形成方法は、下層保護膜61bの開口端部に凸状部分60Cを形成することができる任意の方法を採用することができるが、図7を参照して、たとえば下層保護膜61bを部分的にエッチングすることにより表面部分60A(図6参照)を形成することができる。 The surface portion 60A can be formed by any method that can form the convex portion 60C at the opening end of the lower protective film 61b. For example, referring to FIG. 7, for example, the lower protective film 61b The surface portion 60A (see FIG. 6) can be formed by partially etching.
具体的には、まず、図7(a)を参照して、実施の形態1に係る半導体素子の製造方法と同様の方法により、半導体基板1の第1の主面1A上に下層保護膜61bを形成する。具体的には、はじめにポリイミドをスピンコート法により電極5が形成されている第1の主面1A上に塗布する。次に、ホットプレートに半導体基板1を載置して、たとえば加熱温度120℃で加熱時間3分の加熱処理を行って下層保護膜61aを乾燥させる。次に、写真製版加工を利用して、電極5の表面上に開口部を有し、少なくとも電極5の端部が覆われているように下層保護膜61aをパターニングする。半導体素子を加熱処理して、下層保護膜61aを硬化させる。具体的には、たとえば加熱温度350℃で加熱時間1時間程度の加熱処理を行う。これにより、下層保護膜61aは収縮してキュア後の下層保護膜61bとなる。このときの下層保護膜61bの膜厚は、Ni膜7の膜厚よりも薄く、たとえば1μm以上5μm以下である。 Specifically, referring to FIG. 7A, first, lower protective film 61b is formed on first main surface 1A of semiconductor substrate 1 by a method similar to the method for manufacturing a semiconductor element according to the first embodiment. Form. Specifically, first, polyimide is applied onto the first main surface 1A on which the electrode 5 is formed by spin coating. Next, the semiconductor substrate 1 is placed on a hot plate and, for example, a heat treatment is performed at a heating temperature of 120 ° C. for a heating time of 3 minutes to dry the lower protective film 61a. Next, using the photoengraving process, the lower protective film 61a is patterned so that it has an opening on the surface of the electrode 5 and at least the end of the electrode 5 is covered. The semiconductor element is heat-treated to cure the lower protective film 61a. Specifically, for example, heat treatment is performed at a heating temperature of 350 ° C. for a heating time of about 1 hour. Thereby, the lower protective film 61a contracts to become a cured lower protective film 61b. The film thickness of the lower protective film 61b at this time is thinner than the film thickness of the Ni film 7, for example, 1 μm or more and 5 μm or less.
次に、図7(b)を参照して、下層保護膜61bの開口端部にフォトレジストを用いてマスクパターン11を形成する。第1の主面1Aに沿う方向におけるマスクパターン11の幅は、たとえば2μm以上4μm以下である。また、マスクパターン11の膜厚は、たとえば2μm以上4μm以下である。次に、マスクパターン11をエッチングマスクとして、下層保護膜61bを減膜する。減膜する方法は、マスクパターン11と下層保護膜61bとで選択比を所定の値以上とすることのできる任意の方法を採用することができるが、たとえばアッシングにより実施され得る。下層保護膜61bにおいてマスクパターン11に保護されていない領域の膜厚は、アッシングによってたとえば1μm以上4μm以下に減じられる。アッシング後、マスクパターン11はアセトン等によって下層保護膜61bに対して選択的に除去される。これにより、図7(c)に示すような凸状部分60Cを有する下層保護膜61bが形成される。 Next, referring to FIG. 7B, a mask pattern 11 is formed using a photoresist at the opening end of the lower protective film 61b. The width of mask pattern 11 in the direction along first main surface 1A is, for example, not less than 2 μm and not more than 4 μm. Moreover, the film thickness of the mask pattern 11 is 2 micrometers or more and 4 micrometers or less, for example. Next, the lower protective film 61b is reduced using the mask pattern 11 as an etching mask. As a method of reducing the film thickness, any method that can make the selectivity between the mask pattern 11 and the lower protective film 61b be equal to or higher than a predetermined value can be adopted. However, for example, ashing can be performed. The film thickness of the region not protected by the mask pattern 11 in the lower protective film 61b is reduced to, for example, 1 μm or more and 4 μm or less by ashing. After ashing, the mask pattern 11 is selectively removed from the lower protective film 61b with acetone or the like. As a result, a lower protective film 61b having a convex portion 60C as shown in FIG. 7C is formed.
その後は、実施の形態1に係る半導体素子の製造方法と同様に処理することにより、実施の形態2に係る半導体素子をえることができる。つまり、実施の形態2に係る半導体素子の製造方法は、実施の形態1に係る半導体素子の製造方法と同様の効果を奏することができる。 Thereafter, the semiconductor element according to the second embodiment can be obtained by processing in the same manner as the method for manufacturing the semiconductor element according to the first embodiment. That is, the semiconductor element manufacturing method according to the second embodiment can achieve the same effects as the semiconductor element manufacturing method according to the first embodiment.
また、実施の形態2に係る半導体素子の製造方法において、マスクパターン11を形成する位置は下層保護膜61bの開口端部に限られるものではない。言い換えると、実施の形態2に係る半導体素子において、側縁部60に設けられている凸状部分60Cは、任意の箇所に設けられていても良い。図7(b)を参照して、たとえば、マスクパターン11を下層保護膜61bの開口端部から所定の距離だけ離れた位置に形成することにより、図8に示すように、凸状部分60Cが側端部分60Bから所定の距離だけ側壁6E側に形成される。この場合には、表面部分60Aも保護膜6の側壁6E側に形成されることになるため、Ni膜7を表面部分60Aよりも側壁6E側にさらに広く形成する必要があるが、実施の形態2に係る半導体素子と同等の効果を奏することができる。なお、図8(b)を参照して、この場合にも、たとえば、側端部分60Bが曲面状に形成されていてもよい。このようにしてもこれが平面上に形成されている場合と同様の効果を奏することができる。 In the method for manufacturing a semiconductor element according to the second embodiment, the position where the mask pattern 11 is formed is not limited to the opening end of the lower protective film 61b. In other words, in the semiconductor element according to the second embodiment, the convex portion 60C provided on the side edge portion 60 may be provided at an arbitrary location. Referring to FIG. 7B, for example, by forming the mask pattern 11 at a position away from the opening end of the lower protective film 61b by a predetermined distance, as shown in FIG. It is formed on the side wall 6E side by a predetermined distance from the side end portion 60B. In this case, since the surface portion 60A is also formed on the side wall 6E side of the protective film 6, it is necessary to form the Ni film 7 wider on the side wall 6E side than the surface portion 60A. The same effect as the semiconductor element according to 2 can be obtained. Referring to FIG. 8B, also in this case, for example, the side end portion 60B may be formed in a curved surface shape. Even if it does in this way, there can exist an effect similar to the case where this is formed on the plane.
また、実施の形態2に係る半導体素子の製造方法において、側縁部60の凸状部分60C(異なる観点から言えば表面部分60A)は、マスクパターン11を用いて下層保護膜61bを減膜することにより形成されるが、これに限られるものではない。図9を参照して、下層保護膜61b上にさらに保護膜12を形成することにより、凸状部分60Cが形成されてもよい。 In the method for manufacturing a semiconductor device according to the second embodiment, the convex portion 60C (surface portion 60A from a different point of view) of the side edge portion 60 uses the mask pattern 11 to reduce the thickness of the lower protective film 61b. However, the present invention is not limited to this. Referring to FIG. 9, convex portion 60 </ b> C may be formed by further forming protective film 12 on lower protective film 61 b.
たとえば図9(a)を参照して、図7(a)に示す下層保護膜61bを形成した後、下層保護膜61b上の所定の位置に、下層保護膜61bを構成するポリイミド12を追加塗布する。ポリイミド12は、たとえばディスペンサーを用いて一筆書きで塗布される。ポリイミド12は、たとえば熱収縮率の高いポリイミドである。 For example, referring to FIG. 9A, after forming the lower protective film 61b shown in FIG. 7A, the polyimide 12 constituting the lower protective film 61b is additionally applied at a predetermined position on the lower protective film 61b. To do. The polyimide 12 is applied with a single stroke using, for example, a dispenser. The polyimide 12 is, for example, a polyimide having a high heat shrinkage rate.
図9(b)を参照して、追加塗布がされた後に下層保護膜61bに対する加熱処理と同様の処理を行い、ポリイミド12を硬化して凸状部分60Cとする。その後は、実施の形態1に係る半導体素子の製造方法と同様に処理することにより、図8に示す実施の形態2に係る半導体素子を得ることができる。 Referring to FIG. 9B, after the additional application, a process similar to the heating process for the lower protective film 61b is performed to cure the polyimide 12 to form a convex portion 60C. Thereafter, the semiconductor element according to the second embodiment shown in FIG. 8 can be obtained by processing in the same manner as the method for manufacturing the semiconductor element according to the first embodiment.
なお、図8(a)に示す側縁部60は、実施の形態2に係る半導体素子の製造方法において、たとえばポリイミド12を構成する材料を熱収縮率の低いポリイミドを用いて形成された凸状部分60cを所定のレジストマスクで保護し、当該マスクの周囲をエッチングすることにより形成することができる。 In addition, the side edge part 60 shown to Fig.8 (a) is the convex shape formed in the manufacturing method of the semiconductor element which concerns on Embodiment 2 using the material which comprises the polyimide 12, for example using the polyimide with a low thermal contraction rate. The portion 60c can be formed by protecting the portion 60c with a predetermined resist mask and etching the periphery of the mask.
(実施の形態3)
次に、実施の形態3に係る半導体素子およびその製造方法について説明する。実施の形態3に係る半導体素子は、基本的には実施の形態1に係る半導体素子と同様の構成を備えるが、表面部分60Aが側縁部60上に形成されている凹状部分60Fの1つの面として形成されている点で異なる。(Embodiment 3)
Next, a semiconductor element and a manufacturing method thereof according to the third embodiment will be described. The semiconductor element according to the third embodiment basically has the same configuration as that of the semiconductor element according to the first embodiment. However, one of the concave portions 60F in which the surface portion 60A is formed on the side edge portion 60 is provided. It differs in that it is formed as a surface.
具体的には、図10を参照して、側縁部60は、保護膜6の側壁6E側において第1の主面1Aと略平行な面で規定されている略平坦部分60Dと、略平行部分60Dに対して第1の主面1Aと垂直な方向の下方に陥没している凹状部分60Fとを有している。表面部分60Aは、凹状部分60Fの一つの面として形成されている。つまり、側縁部60において凹状部分60Fよりも保護膜6の開口部の内側には、凹状部分60Fが形成されている領域の膜厚よりも厚みが厚く、表面部分60Aを有する部分が形成されている。 Specifically, referring to FIG. 10, the side edge 60 is substantially parallel to a substantially flat portion 60 </ b> D defined by a surface substantially parallel to the first main surface 1 </ b> A on the side wall 6 </ b> E side of the protective film 6. The first main surface 1A with respect to the portion 60D has a concave portion 60F that is recessed downward in a direction perpendicular to the first main surface 1A. The surface portion 60A is formed as one surface of the concave portion 60F. That is, a portion having a surface portion 60 </ b> A is formed inside the opening of the protective film 6 at the side edge portion 60 rather than the recessed portion 60 </ b> F than the region where the recessed portion 60 </ b> F is formed. ing.
この場合、側縁部60の表面部分60AとNi膜7との界面は、第1の主面1Aと垂直な方向に延びている。さらに凹状部分60Fに隣接し、かつ保護膜6の開口部の内側に位置する部分の厚みが凹状部分60Fの厚みよりも厚く形成されている。言い換えれば、凹状部分60Fよりも保護膜6の開口部の内側に位置する部分と凹状部分60Fとの関係は、実施の形態2における凸状部分60Cと略平行部分60Dとの関係と同等である。そのため、上述のように第1の主面1Aに沿った方向において半導体素子10の各部材が収縮した場合であっても表面部分60AとNi膜7との界面に隙間が生じることを抑制することができる。つまり、実施の形態1に係る半導体素子と同様の効果を奏することができる。なお、図10(b)を参照して、実施の形態3に係る半導体素子においても、たとえば、側端部分60Bが曲面状に形成されていてもよい。このようにしてもこれが平面上に形成されている場合と同様の効果を奏することができる。 In this case, the interface between the surface portion 60A of the side edge 60 and the Ni film 7 extends in a direction perpendicular to the first main surface 1A. Furthermore, the thickness of the part which adjoins the concave part 60F and is located inside the opening part of the protective film 6 is formed thicker than the thickness of the concave part 60F. In other words, the relationship between the portion located inside the opening of the protective film 6 relative to the concave portion 60F and the concave portion 60F is equivalent to the relationship between the convex portion 60C and the substantially parallel portion 60D in the second embodiment. . Therefore, even when each member of the semiconductor element 10 contracts in the direction along the first main surface 1A as described above, it is possible to suppress the generation of a gap at the interface between the surface portion 60A and the Ni film 7. Can do. That is, the same effect as the semiconductor element according to the first embodiment can be obtained. Referring to FIG. 10B, also in the semiconductor element according to the third embodiment, for example, side end portion 60B may be formed in a curved shape. Even if it does in this way, there can exist an effect similar to the case where this is formed on the plane.
図11を参照して、実施の形態3に係る半導体素子の製造方法について説明する。実施の形態3に係る半導体素子の製造方法は、実施の形態1に係る半導体素子の製造方法と基本的には同様の構成を備えるが、保護膜6を形成する工程(S20)において表面部分60Aの形成する方法が異なる。 With reference to FIG. 11, the manufacturing method of the semiconductor element which concerns on Embodiment 3 is demonstrated. The method for manufacturing a semiconductor element according to the third embodiment basically has the same configuration as the method for manufacturing a semiconductor element according to the first embodiment, but the surface portion 60A is formed in the step of forming the protective film 6 (S20). The method of forming is different.
具体的には、まず、図11(a)を参照して、実施の形態1に係る半導体素子の製造方法と同様の方法により、半導体基板1の第1の主面1A上に下層保護膜61aを形成する。具体的には、はじめにポリイミドをスピンコート法により電極5が形成されている第1の主面1A上に塗布する。次に、ホットプレートに半導体基板1を載置して、たとえば加熱温度120℃で加熱時間3分の加熱処理を行って下層保護膜61aを乾燥させる。次に、写真製版加工を利用して、電極5の表面上に開口部を有し、少なくとも電極5の端部が覆われているように下層保護膜61aをパターニングする。半導体素子を加熱処理して、下層保護膜61aを硬化させる。具体的には、たとえば加熱温度350℃で加熱時間1時間程度の加熱処理を行う。これにより、下層保護膜61aは収縮してキュア後の下層保護膜61bとなる。このときの下層保護膜61bの膜厚は、Ni膜7の膜厚よりも薄く、たとえば1μm以上5μm以下である。 Specifically, referring to FIG. 11A, first, lower protective film 61a is formed on first main surface 1A of semiconductor substrate 1 by the same method as the method for manufacturing a semiconductor element according to the first embodiment. Form. Specifically, first, polyimide is applied onto the first main surface 1A on which the electrode 5 is formed by spin coating. Next, the semiconductor substrate 1 is placed on a hot plate and, for example, a heat treatment is performed at a heating temperature of 120 ° C. for a heating time of 3 minutes to dry the lower protective film 61a. Next, using the photoengraving process, the lower protective film 61a is patterned so that it has an opening on the surface of the electrode 5 and at least the end of the electrode 5 is covered. The semiconductor element is heat-treated to cure the lower protective film 61a. Specifically, for example, heat treatment is performed at a heating temperature of 350 ° C. for a heating time of about 1 hour. Thereby, the lower protective film 61a contracts to become a cured lower protective film 61b. The film thickness of the lower protective film 61b at this time is thinner than the film thickness of the Ni film 7, and is, for example, 1 μm or more and 5 μm or less.
次に、図11(b)を参照して、下層保護膜61b上の所定の位置に開口部を有するマスクパターン13を形成する。マスクパターン13は、所定のエッチング方法において下層保護膜61bに対してマスク材料となり得る任意の材料とすればよいが、たとえば窒化珪素(SiNx)膜を用いることができる。SiNxは、任意の方法で成膜されていればよいが、たとえばスパッタ法や低温プラズマCVD法により成膜すればよい。なお、マスクパターン13を構成する材料は、SiNxに限られるものではなく、たとえば酸化珪素(SiOx)等であってもよい。 Next, referring to FIG. 11B, a mask pattern 13 having an opening at a predetermined position on the lower protective film 61b is formed. The mask pattern 13 may be any material that can serve as a mask material for the lower protective film 61b in a predetermined etching method. For example, a silicon nitride (SiNx) film can be used. SiNx may be formed by any method, but may be formed by sputtering or low-temperature plasma CVD, for example. The material constituting the mask pattern 13 is not limited to SiNx, and may be, for example, silicon oxide (SiOx).
第1の主面1Aに沿う方向におけるマスクパターン13の開口部の幅は、たとえば2μm以上4μm以下である。また、マスクパターン13の膜厚は、たとえば2μm以上4μm以下である。次に、マスクパターン13をマスクとして、開口部下に位置する下層保護膜61bを減膜する。減膜する方法は、マスクパターン13と下層保護膜61bとで選択比を所定の値以上とすることのできる任意の方法を採用することができるが、たとえばアッシングやエッチングにより実施され得る。下層保護膜61bにおいてマスクパターン13に保護されていない領域の膜厚は、アッシングによってたとえば0.1μm以上4.5μm以下に減じられる。図11(c)を参照して、アッシング後は、マスクパターン13を除去せずに、マスクパターン13上に上層保護膜62aを形成することができる。なお、マスクパターン13は、任意の方法で除去した後、上層保護膜62aを形成してもよい。 The width of the opening of the mask pattern 13 in the direction along the first main surface 1A is, for example, not less than 2 μm and not more than 4 μm. Moreover, the film thickness of the mask pattern 13 is 2 micrometers or more and 4 micrometers or less, for example. Next, using the mask pattern 13 as a mask, the lower protective film 61b located under the opening is reduced. As a method of reducing the film thickness, any method that can make the selectivity between the mask pattern 13 and the lower protective film 61b be equal to or higher than a predetermined value can be adopted. However, for example, ashing or etching can be used. The film thickness of the region not protected by the mask pattern 13 in the lower protective film 61b is reduced to, for example, 0.1 μm or more and 4.5 μm or less by ashing. Referring to FIG. 11C, after ashing, the upper protective film 62 a can be formed on the mask pattern 13 without removing the mask pattern 13. The mask pattern 13 may be removed by any method, and then the upper protective film 62a may be formed.
その後は、実施の形態1に係る半導体素子の製造方法と同様に処理することにより、実施の形態3に係る半導体素子をえることができる。つまり、実施の形態3に係る半導体素子の製造方法は、実施の形態1に係る半導体素子の製造方法と同様の効果を奏することができる。なお、図10(a)に示す側縁部60は、たとえば保護膜6における下層保護膜61a,61bを構成する材料に熱収縮率の小さいポリイミド材料を用いること、および保護膜6に対するキュア温度を低温化することのうちの少なくとも一方を行うことによって、形成することができる。 After that, the semiconductor element according to the third embodiment can be obtained by processing in the same manner as the semiconductor element manufacturing method according to the first embodiment. That is, the semiconductor element manufacturing method according to the third embodiment can achieve the same effects as the semiconductor element manufacturing method according to the first embodiment. 10A, for example, a polyimide material having a low thermal shrinkage is used as the material constituting the lower protective films 61a and 61b in the protective film 6, and the curing temperature for the protective film 6 is set. It can be formed by performing at least one of lowering the temperature.
なお、実施の形態1〜実施の形態3において、保護膜6は下層保護膜61と上層保護膜62の2層が積層した積層構造を有しているが、これに限られるものではなく、3層以上の保護膜が積層した積層構造を有していてもよい。 In the first to third embodiments, the protective film 6 has a laminated structure in which the lower protective film 61 and the upper protective film 62 are laminated. However, the present invention is not limited to this. You may have the laminated structure on which the protective film more than the layer laminated | stacked.
(実施の形態4)
次に、図12および図13を参照して、実施の形態4に係る半導体素子およびその製造方法について説明する。図12は、実施の形態4に係る半導体素子における保護膜6の開口端部の構成を示す断面図であり、図13は、図12中領域XIIIの部分拡大図である。実施の形態4に係る半導体素子は、基本的には実施の形態1に係る半導体素子と同様の構成を備えるが、保護膜6が無機膜の積層構造として構成されていておらず、無機膜の単層構造として形成されている点で異なる。すなわち、実施の形態4に係る半導体素子の製造方法は、基本的には実施の形態1に係る半導体素子の製造方法と同様の構成を備えるが、保護膜6を形成する工程(S20)において下層保護膜61a,61bに相当する保護膜6のみが形成される点で異なる。言い換えると、実施の形態4における保護膜6は、実施の形態1〜実施の形態3に係る側縁部60に相当するものとして形成される。(Embodiment 4)
Next, with reference to FIG. 12 and FIG. 13, the semiconductor element and the manufacturing method thereof according to the fourth embodiment will be described. FIG. 12 is a cross-sectional view showing a configuration of the opening end portion of the protective film 6 in the semiconductor element according to the fourth embodiment, and FIG. 13 is a partially enlarged view of a region XIII in FIG. The semiconductor element according to the fourth embodiment basically has the same configuration as that of the semiconductor element according to the first embodiment, but the protective film 6 is not configured as a laminated structure of inorganic films. It differs in that it is formed as a single layer structure. That is, the semiconductor element manufacturing method according to the fourth embodiment basically has the same configuration as the semiconductor element manufacturing method according to the first embodiment, but the lower layer is formed in the step of forming the protective film 6 (S20). The difference is that only the protective film 6 corresponding to the protective films 61a and 61b is formed. In other words, the protective film 6 in the fourth embodiment is formed to correspond to the side edge portion 60 according to the first to third embodiments.
保護膜6の開口端部には、半導体基板1の第1の主面1Aと交差する方向に延びる内周側傾斜部分60Gおよび外周側傾斜部分60Iが形成されている。内周側傾斜部分60Gは、実施の形態1〜実施の形態3における側端部分60Bに相当する。また、外周側傾斜部分60Iは実施の形態1〜実施の形態3における表面部分60Aに相当する。 An inner peripheral inclined portion 60G and an outer peripheral inclined portion 60I extending in a direction intersecting the first main surface 1A of the semiconductor substrate 1 are formed at the opening end of the protective film 6. The inner peripheral inclined portion 60G corresponds to the side end portion 60B in the first to third embodiments. The outer peripheral inclined portion 60I corresponds to the surface portion 60A in the first to third embodiments.
内周側傾斜部分60Gは、外周側傾斜部分60Iと比べて開口部の内側に位置し、保護膜6において膜厚が最も厚い部分である保護膜頂点部分60Hを挟んで外周側傾斜部分60Iと連なるように形成されている。外周側傾斜部分60Iは、外周側傾斜部分60Iよりも開口部の外側において、第1の主面1Aと平行な表面を有する平行部分60Jと接続されている。内周側傾斜部分60Gは、たとえば曲面として形成されていてもよいし、複数の平面を有するように形成されていてもよい。 The inner peripheral side inclined portion 60G is located on the inner side of the opening compared to the outer peripheral side inclined portion 60I, and the outer peripheral side inclined portion 60I with the protective film apex portion 60H being the thickest portion of the protective film 6 interposed therebetween. It is formed to be continuous. The outer peripheral inclined portion 60I is connected to a parallel portion 60J having a surface parallel to the first main surface 1A on the outer side of the opening than the outer peripheral inclined portion 60I. The inner peripheral inclined portion 60G may be formed as a curved surface, for example, or may be formed to have a plurality of planes.
図13を参照して、外周側傾斜部分60Iの幅(第1の主面1Aに沿った方向であって、保護膜6の開口端部が延びる方向に垂直な方向における保護膜頂点部分60Hと平行部分60Jとの距離)Wは、後述する実施例の結果から、たとえば2.5μmである。外周側傾斜部分60Iの高さ(第1の主面1Aに垂直な方向における保護膜頂点部分60Hと平行部分60Jとの距離)Hは、後述する実施例の結果から、たとえば0.6μmである。 Referring to FIG. 13, the width of outer peripheral inclined portion 60I (the protective film apex portion 60H in the direction along the first main surface 1A and perpendicular to the direction in which the opening end of the protective film 6 extends) The distance (W) from the parallel portion 60J is, for example, 2.5 μm from the results of the examples described later. The height (the distance between the protective film apex portion 60H and the parallel portion 60J in the direction perpendicular to the first main surface 1A) H of the outer peripheral inclined portion 60I is, for example, 0.6 μm from the results of Examples described later. .
内周側傾斜部分60Gと第1の主面1Aとの成す角度は、たとえば30度であってもよいし、90度であってもよい。好ましくは、内周側傾斜部分60Gと第1の主面1Aとの成す角度は、30度以上90度未満であり、より好ましくは45度以上60度以下である。 The angle formed by the inner peripheral inclined portion 60G and the first main surface 1A may be, for example, 30 degrees or 90 degrees. Preferably, the angle formed between the inner peripheral inclined portion 60G and the first main surface 1A is 30 degrees or more and less than 90 degrees, and more preferably 45 degrees or more and 60 degrees or less.
保護膜6の膜厚は、たとえば1μm以上6μm以下である。保護膜6の開口部内における電極5上、および保護膜6の内周側傾斜部分60G、保護膜頂点部分60H、外周側傾斜部分60I、および平行部分60Jの少なくとも一部上にはNi膜7が形成されている。このとき、保護膜頂点部分60Hにおける保護膜6の厚みが、内周側傾斜部分60Gと外周側傾斜部分60Iにおける保護膜6の厚みよりも厚い。そのため、保護膜頂点部分60H上に位置するNi膜7よりも、内周側傾斜部分60Gと外周側傾斜部分60I上に位置するNi膜7は、第1の主面1Aと垂直な方向において第1の主面1A側に突出するように形成されている。 The film thickness of the protective film 6 is, for example, not less than 1 μm and not more than 6 μm. The Ni film 7 is formed on the electrode 5 in the opening of the protective film 6 and on at least part of the inner peripheral inclined portion 60G, the protective film apex portion 60H, the outer peripheral inclined portion 60I, and the parallel portion 60J. Is formed. At this time, the thickness of the protective film 6 at the protective film apex portion 60H is thicker than the thickness of the protective film 6 at the inner peripheral inclined portion 60G and the outer peripheral inclined portion 60I. For this reason, the Ni film 7 positioned on the inner peripheral side inclined portion 60G and the outer peripheral side inclined portion 60I is closer to the first main surface 1A than the Ni film 7 positioned on the protective film apex portion 60H. 1 is formed so as to protrude toward the main surface 1A.
保護膜6とNi膜7とは外周側傾斜部分60Iの少なくとも一部において面接触しており、保護膜6とNi膜7とは外周側傾斜部分60I上において嵌合している。保護膜6とNi膜7との界面は、外周側傾斜部分60IとNi膜7との界面と、内周側傾斜部分60GとNi膜7との界面を含んで形成されているが、そのうち少なくともNi膜7の表層側に位置する外周側傾斜部分60Iとの界面には隙間が形成されてない。 The protective film 6 and the Ni film 7 are in surface contact with at least a part of the outer peripheral inclined portion 60I, and the protective film 6 and the Ni film 7 are fitted on the outer peripheral inclined portion 60I. The interface between the protective film 6 and the Ni film 7 includes the interface between the outer peripheral inclined portion 60I and the Ni film 7 and the interface between the inner peripheral inclined portion 60G and the Ni film 7. No gap is formed at the interface with the outer peripheral inclined portion 60I located on the surface layer side of the Ni film 7.
また、実施の形態4に係る半導体素子の製造方法は、たとえば以下のように実施し得る。実施の形態4に係る半導体素子の製造方法は、第1の主面1A上に電極5が形成されている半導体素子(半導体基板1)を準備する工程(S10)と、電極5の表面上において開口部を有し、電極5の少なくとも端部を覆う保護膜6を形成する工程(S20)と、開口部において電極5上に第1めっき膜および第2めっき膜としてのNi膜7/Au膜8を形成する工程(S30)とを備える。 In addition, the method for manufacturing a semiconductor element according to the fourth embodiment can be performed as follows, for example. In the method of manufacturing a semiconductor element according to the fourth embodiment, a step (S10) of preparing a semiconductor element (semiconductor substrate 1) in which an electrode 5 is formed on the first main surface 1A, and on the surface of the electrode 5 Step (S20) of forming protective film 6 having an opening and covering at least the end of electrode 5, and Ni film 7 / Au film as first plating film and second plating film on electrode 5 in the opening 8 (S30).
半導体基板1を準備する工程(S10)は、実施の形態1に係る半導体素子の製造方法における半導体基板1を準備する工程(S10)と同様に実施され得る。電極5は、たとえばスパッタ法により膜厚が2μm以上6μm以下の金属膜として第1の主面1A上に形成された後、当該金属膜上にスピンコート法により形成され膜厚が2μm以上8μm以下のフォトレジストをマスクとして該写真製版により加工される。フォトレジストマスクは加工後に有機溶剤等により除去される。 The step (S10) of preparing the semiconductor substrate 1 can be performed in the same manner as the step (S10) of preparing the semiconductor substrate 1 in the method of manufacturing a semiconductor element according to the first embodiment. The electrode 5 is formed on the first main surface 1A as a metal film having a film thickness of 2 μm or more and 6 μm or less, for example, by sputtering, and then formed on the metal film by a spin coating method, and the film thickness is 2 μm or more and 8 μm or less. The photo resist is used as a mask to process the photo resist. The photoresist mask is removed with an organic solvent after processing.
保護膜6を形成する工程(S20)は、たとえば以下のように実施し得る。
保護膜6を構成する材料は、たとえばポリイミドである。ポリイミドをスピンコート法により第1の主面1A上に塗布した後、たとえば加熱温度120℃で加熱時間3分の加熱処理を行って乾燥させる。その後、写真製版加工を利用して、電極5の表面上に開口部を有し、少なくとも電極5の端部が覆われているように保護膜をパターニングする。The step (S20) of forming the protective film 6 can be performed as follows, for example.
The material constituting the protective film 6 is, for example, polyimide. After the polyimide is applied onto the first main surface 1A by a spin coating method, for example, a heat treatment is performed at a heating temperature of 120 ° C. for 3 minutes and then dried. Thereafter, using a photoengraving process, the protective film is patterned so that it has an opening on the surface of the electrode 5 and at least the end of the electrode 5 is covered.
次に、半導体素子を加熱処理して保護膜を硬化させ、保護膜6を形成する。具体的には、たとえば加熱温度350℃で加熱時間1時間程度の加熱処理を行う。これにより、保護膜は大きく収縮してキュア後の保護膜6となるが、このときその開口端部は後退しつつ凸状となる。この結果、保護膜6の開口端部には、第1の主面1Aと交差する方向に延びる少なくとも2つの面が形成される。保護膜頂点部分60Hも含めて保護膜6の膜厚は、後の工程において形成されるNi膜7の膜厚よりも薄くなるように設けられており、たとえば1μm以上6μm以下である。 Next, the semiconductor element is heated to cure the protective film, and the protective film 6 is formed. Specifically, for example, heat treatment is performed at a heating temperature of 350 ° C. for a heating time of about 1 hour. As a result, the protective film is greatly shrunk to become the cured protective film 6, but at this time, the opening end portion is convex while being retracted. As a result, at least two surfaces extending in the direction intersecting the first main surface 1A are formed at the opening end of the protective film 6. The film thickness of the protective film 6 including the protective film apex portion 60H is provided so as to be thinner than the film thickness of the Ni film 7 to be formed in a later step, and is, for example, 1 μm or more and 6 μm or less.
Ni膜7を形成する工程(S30)は、実施の形態1に係る半導体素子の製造方法におけるNi膜7を形成する工程(S30)と同様に実施され得る。すなわち、Ni膜7を無電解めっき法により電極5上に形成し、その後当該Ni膜7表面を乾燥させずにNi膜7において電極5と接する面と反対側に位置する面上に、無電解めっき法によりAu膜8を形成する。 The step (S30) of forming the Ni film 7 can be performed in the same manner as the step (S30) of forming the Ni film 7 in the method of manufacturing a semiconductor device according to the first embodiment. That is, the Ni film 7 is formed on the electrode 5 by the electroless plating method, and then the surface of the Ni film 7 is electrolessly formed on the surface of the Ni film 7 opposite to the surface in contact with the electrode 5 without drying. An Au film 8 is formed by plating.
このとき、Ni膜7を形成する工程(S30)において第2の主面1B上に形成されている裏面電極を保護するために、保護部材としてたとえば保護テープを第2の主面1B上に貼りつけていてもよいが、この場合には保護テープの耐薬品性の観点からNi膜7の膜厚を10μm程度以下とする必要がある。一方で、保護部材として石英基板を用いた場合にはこの限りではなく、Ni膜7の膜厚をたとえば15μm以上20μm以下としても、することも可能である。 At this time, in order to protect the back electrode formed on the second main surface 1B in the step of forming the Ni film 7 (S30), for example, a protective tape is applied as a protective member on the second main surface 1B. In this case, the Ni film 7 needs to have a thickness of about 10 μm or less from the viewpoint of chemical resistance of the protective tape. On the other hand, when a quartz substrate is used as the protective member, the present invention is not limited to this, and the thickness of the Ni film 7 can be set to 15 μm or more and 20 μm or less, for example.
このようにしても、実施の形態4に係る半導体素子は、実施の形態1に係る半導体素子と同等の効果を奏することができる。すなわち、実施の形態4に係る半導体素子によれば、保護膜6の外周側傾斜部分60IとNi膜7との界面に隙間が生じることを防止することができる。この結果、実施の形態4に係る半導体素子を用いて製造された半導体装置では、保護膜6とNi膜7との界面にAu膜8やはんだ4等が析出することを抑制することができるため、半導体素子10の実使用時の温度履歴により電極5にクラックが進展したり、電極5からNi膜7が剥離して素子破壊に至るといった問題の発生を十分に抑制することができる。 Even in this case, the semiconductor element according to the fourth embodiment can achieve the same effects as the semiconductor element according to the first embodiment. That is, according to the semiconductor element according to the fourth embodiment, it is possible to prevent a gap from being generated at the interface between the outer peripheral inclined portion 60 </ b> I of the protective film 6 and the Ni film 7. As a result, in the semiconductor device manufactured using the semiconductor element according to the fourth embodiment, it is possible to suppress the deposition of the Au film 8, the solder 4, etc. at the interface between the protective film 6 and the Ni film 7. Further, it is possible to sufficiently suppress the occurrence of problems such as a crack that develops in the electrode 5 due to a temperature history during actual use of the semiconductor element 10 or the Ni film 7 is peeled off from the electrode 5 to cause element destruction.
実施の形態1〜実施の形態4に係る半導体素子の製造方法において、電極5は第1の主面1A上に形成されているが、これに限られるものではない。図14に、実施の形態4に係る半導体素子の変形例を示す。図14に示すように、電極5はたとえば半導体基板1に埋め込まれて形成されていてもよい。この場合、保護膜6は、第1の主面1A上において電極5と半導体基板1の界面上を覆うように形成されていればよい。また、実施の形態1〜実施の形態3に係る半導体素子においても同様の構成とすることができる。このようにしても、実施の形態1〜実施の形態4に係る半導体素子と同様の効果を奏することができる。 In the method for manufacturing a semiconductor element according to the first to fourth embodiments, the electrode 5 is formed on the first main surface 1A, but is not limited thereto. FIG. 14 shows a modification of the semiconductor element according to the fourth embodiment. As shown in FIG. 14, the electrode 5 may be formed, for example, embedded in the semiconductor substrate 1. In this case, the protective film 6 may be formed so as to cover the interface between the electrode 5 and the semiconductor substrate 1 on the first main surface 1A. In addition, the same configuration can be applied to the semiconductor elements according to the first to third embodiments. Even if it does in this way, there can exist an effect similar to the semiconductor element which concerns on Embodiment 1- Embodiment 4. FIG.
なお、実施の形態1〜実施の形態4に係る半導体素子の製造方法において、Ni膜7を形成する工程(S30)においてNi膜7をめっき成膜する前に、保護膜6の開口部内に露出した電極5表面に対して一般的な前処理(脱脂、エッチング、ダブルジンケートなど)を行ってもよい。 In the semiconductor element manufacturing method according to the first to fourth embodiments, the Ni film 7 is exposed in the opening of the protective film 6 before the Ni film 7 is formed by plating in the step of forming the Ni film 7 (S30). General pretreatment (degreasing, etching, double zincate, etc.) may be performed on the surface of the electrode 5.
次に、実施例について説明する。
実施の形態4に係る半導体素子について、Au膜8形成後にNi膜7の局部腐食の有無を評価した。Next, examples will be described.
For the semiconductor element according to the fourth embodiment, the presence or absence of local corrosion of the Ni film 7 was evaluated after the Au film 8 was formed.
具体的には、実施例として、膜厚が6μmの保護膜6と、膜厚が15μmのNi膜7とが形成されている実施の形態4に係る半導体素子を作製した。 Specifically, as an example, a semiconductor element according to Embodiment 4 in which a protective film 6 having a film thickness of 6 μm and a Ni film 7 having a film thickness of 15 μm were formed.
また、比較例として、膜厚が6μmの保護膜と、膜厚が10μmのNi膜とが形成されている半導体素子を作製した。該保護膜の開口端部には、実施の形態4に係る半導体素子と同様に内周側傾斜部分60Gおよび外周側傾斜部分60Iが形成されているが、外周側傾斜部分60I上にまでNi膜7が形成されていない点で、上記実施例に係る半導体素子と異なる。つまり、比較例に係る半導体素子は、保護膜とNi膜とが外周側傾斜部分上において嵌合していない。 Further, as a comparative example, a semiconductor element in which a protective film having a film thickness of 6 μm and a Ni film having a film thickness of 10 μm were formed. An inner peripheral side inclined portion 60G and an outer peripheral side inclined portion 60I are formed at the opening end of the protective film in the same manner as the semiconductor element according to the fourth embodiment, but the Ni film extends over the outer peripheral side inclined portion 60I. 7 is different from the semiconductor device according to the above example in that 7 is not formed. That is, in the semiconductor element according to the comparative example, the protective film and the Ni film are not fitted on the outer peripheral inclined portion.
このようにして作製した実施例および比較例に係る半導体素子について断面観察を行った。断面観察は、集束イオンビーム走査型イオン顕微鏡(FIB−SIM)を用いて行った。図15は実施例に係る半導体素子のFIB−SIM像である。図16は比較例に係る半導体素子のFIB−SIM像である。また、図15および図16は、いずれも半導体素子に形成した断面部を45度傾斜させて撮影した像である。 Cross-sectional observation was performed about the semiconductor element which concerns on the Example and comparative example which were produced in this way. Cross-sectional observation was performed using a focused ion beam scanning ion microscope (FIB-SIM). FIG. 15 is a FIB-SIM image of the semiconductor element according to the example. FIG. 16 is a FIB-SIM image of a semiconductor element according to a comparative example. FIG. 15 and FIG. 16 are images taken by tilting the cross section formed in the semiconductor element by 45 degrees.
図16に示す比較例に係る半導体素子では、保護膜においてその上部にNi膜が形成されている部分の表面は半導体基板の表面(第1の主面)に略平行となっていた。さらに、図16において点線で囲っている部分の保護膜との界面に位置するNi膜が局部腐食していることが確認された(Ni膜と比べて濃い色合いの部分が局部腐食している部分)。 In the semiconductor element according to the comparative example shown in FIG. 16, the surface of the protective film where the Ni film is formed thereon is substantially parallel to the surface (first main surface) of the semiconductor substrate. Furthermore, it was confirmed that the Ni film located at the interface with the protective film in the part surrounded by the dotted line in FIG. 16 was locally corroded (the part having a darker shade than the Ni film was locally corroded). ).
一方、図15に示す実施例に係る半導体素子では、保護膜とNi膜とが嵌合していることが確認された。さらに、図15において保護膜との界面に位置するNi膜は局部腐食していないことが確認された。 On the other hand, in the semiconductor element according to the example shown in FIG. 15, it was confirmed that the protective film and the Ni film were fitted. Furthermore, in FIG. 15, it was confirmed that the Ni film located at the interface with the protective film is not locally corroded.
この結果から、保護膜6とNi膜7とが嵌合するために必要な寸法条件を見積もることができる。図15,16から、Ni膜はめっき法により等方的に成膜されるため、外周側傾斜部分60Iの幅Wは、保護膜頂点部分60Hよりも上方(第1の主面1Aに垂直な方向において電極5と反対側)に形成されているNi膜7の厚みと同等となる。つまり、保護膜6とNi膜7とが嵌合し、Ni膜7と外周側傾斜部分60Iとが面接触する領域を広く確保する観点からは、Ni膜7の膜厚を保護膜6の膜厚よりも十分に厚くすることが好ましい。たとえば、開口外縁部から十分に離れた場所での保護膜6の膜厚が2.5μm、Ni膜7の膜厚が6μm、外周側傾斜部分60Iの幅Wが2.5μm、外周側傾斜部分60Iの高さHが0.6μm、内周側傾斜部分60Gと電極5との接点から保護膜頂点部分60Hまでの水平方向(第1の主面1Aに沿った方向であって、保護膜6の開口端部が延びる方向に垂直な方向)での距離(内周側傾斜部分60Gの幅)が2.5μm以下である実施例に係る半導体素子では、図16に示すようなNi膜7の局部腐食を防止することができると考えられる。 From this result, it is possible to estimate the dimensional conditions necessary for fitting the protective film 6 and the Ni film 7 together. 15 and 16, since the Ni film is formed isotropically by plating, the width W of the outer peripheral inclined portion 60I is higher than the protective film apex portion 60H (perpendicular to the first main surface 1A). This is equivalent to the thickness of the Ni film 7 formed on the side opposite to the electrode 5 in the direction. That is, from the viewpoint of securing a wide area where the protective film 6 and the Ni film 7 are fitted and the Ni film 7 and the outer peripheral inclined portion 60I are in surface contact, the thickness of the Ni film 7 is set to the film of the protective film 6. It is preferable to make it sufficiently thicker than the thickness. For example, the protective film 6 has a thickness of 2.5 μm, the Ni film 7 has a thickness of 6 μm, the width W of the outer peripheral inclined portion 60I is 2.5 μm, and the outer peripheral inclined portion at a position sufficiently away from the outer edge of the opening The height H of 60I is 0.6 μm, and the horizontal direction from the contact point between the inner peripheral inclined portion 60G and the electrode 5 to the protective film apex portion 60H (the direction along the first main surface 1A and the protective film 6 In the semiconductor element according to the example in which the distance (the width of the inner peripheral side inclined portion 60G) in the direction perpendicular to the direction in which the opening end of each of the electrodes extends is 2.5 μm or less, the Ni film 7 as shown in FIG. It is thought that local corrosion can be prevented.
Ni膜7の膜厚は、たとえば保護膜6において内周側傾斜部分60Gの内周側端部から保護膜頂点部分60Hまでの表面距離よりも厚い。異なる観点から言えば、第1の主面1Aに沿った方向における内周側傾斜部分60Gの内周側端部から保護膜頂点部分60Hまでの距離に応じて、保護膜6やNi膜7の膜厚の好適条件が異なる。 The film thickness of the Ni film 7 is greater than the surface distance from the inner peripheral side end of the inner peripheral inclined portion 60G to the protective film apex portion 60H in the protective film 6, for example. If it says from a different viewpoint, according to the distance from the inner peripheral side edge part of the inner peripheral side inclined part 60G to the protective film apex part 60H in the direction along the first main surface 1A, the protective film 6 and the Ni film 7 The preferred conditions for film thickness are different.
第1の主面1Aに沿った方向における内周側傾斜部分60Gの内周側端部から保護膜頂点部分60Hまでの距離が長く形成される場合には、保護膜6の膜厚を薄くすることにより、内周側傾斜部分60Gの内周側端部から保護膜頂点部分60Hまでの表面距離が長くなることを防止することができる。つまり、保護膜6の開口端部の形状や膜厚を制御することにより、Ni膜7の膜厚を厚くすることなく保護膜6とNi膜7とを十分に嵌合させることが可能となる。Ni膜7の膜厚を厚くすることなく保護膜6とNi膜7とを十分に嵌合させる観点から、内周側傾斜部分60Gと電極5との接点から保護膜頂点部分60Hまでの水平方向での距離は、開口外縁部から十分に離れた場所での保護膜6の膜厚と同等以下であるのが好ましい。異なる観点から言えば、Ni膜7の膜厚を厚くすることなく保護膜6とNi膜7とを十分に嵌合させる観点から、内周側傾斜部分60Gと電極5との接触角は45°以上であるのが好ましい。さらに異なる観点から言えば、Ni膜7の膜厚を厚くすることなく保護膜6とNi膜7とを十分に嵌合させる観点から、内周側傾斜部分60Gと電極5との接点と保護膜頂点部分60Hとを結ぶ線分と、第1の主面1Aとの成す角度が45°以上であるのが好ましい。なお、このようなことは実施の形態4に係る半導体素子に限られず、実施の形態1〜実施の形態3に係る半導体素子においても同様である。 When the distance from the inner peripheral side end of the inner peripheral inclined portion 60G to the protective film apex portion 60H in the direction along the first main surface 1A is long, the thickness of the protective film 6 is reduced. Accordingly, it is possible to prevent the surface distance from the inner peripheral side end portion of the inner peripheral side inclined portion 60G to the protective film apex portion 60H from becoming long. That is, by controlling the shape and film thickness of the opening end of the protective film 6, it is possible to sufficiently fit the protective film 6 and the Ni film 7 without increasing the film thickness of the Ni film 7. . From the viewpoint of sufficiently fitting the protective film 6 and the Ni film 7 without increasing the thickness of the Ni film 7, the horizontal direction from the contact point between the inner peripheral inclined portion 60G and the electrode 5 to the protective film apex portion 60H Is preferably equal to or less than the film thickness of the protective film 6 at a location sufficiently away from the outer edge of the opening. From a different point of view, the contact angle between the inner peripheral inclined portion 60G and the electrode 5 is 45 ° from the viewpoint of sufficiently fitting the protective film 6 and the Ni film 7 without increasing the thickness of the Ni film 7. The above is preferable. Further, from a different point of view, from the viewpoint of sufficiently fitting the protective film 6 and the Ni film 7 without increasing the thickness of the Ni film 7, the contact between the inner peripheral inclined portion 60G and the electrode 5 and the protective film It is preferable that an angle formed by a line segment connecting the apex portion 60H and the first main surface 1A is 45 ° or more. This is not limited to the semiconductor element according to the fourth embodiment, and the same applies to the semiconductor elements according to the first to third embodiments.
以上のように本発明の実施の形態について説明を行ったが、上述の実施の形態を様々に変形することも可能である。また、本発明の範囲は上述の実施の形態に限定されるものではない。本発明の範囲は、請求の範囲によって示され、請求の範囲と均等の意味および範囲内でのすべての変更を含むことが意図される。 Although the embodiment of the present invention has been described above, the above-described embodiment can be variously modified. The scope of the present invention is not limited to the above-described embodiment. The scope of the present invention is defined by the terms of the claims, and is intended to include any modifications within the scope and meaning equivalent to the terms of the claims.
本発明は、電極の表面上に保護膜による開口部が形成されており、かつ当該表面上にめっき法により積層電極構造が形成されている半導体素子に特に有利に適用される。 The present invention is particularly advantageously applied to a semiconductor element in which an opening made of a protective film is formed on the surface of an electrode and a laminated electrode structure is formed on the surface by a plating method.
1 半導体基板、1A 第1の主面、1B 第2の主面、2 熱拡散板、3 リードフレーム、4 はんだ、5 電極、6 保護膜、6E 側壁、7 Ni膜、8 Au膜、10 半導体素子、11,13 マスクパターン、12 保護膜、60 側縁部、60A 表面部分、60B 側端部分、60C 凸状部分、60D 略平坦部分、60F 凹状部分、60G 内周側傾斜部分、60H 保護膜頂点部分、60I 外周側傾斜部分、60J 平行部分、61a,61b 下層保護膜、62a,62b 上層保護膜、62E 端面。 DESCRIPTION OF SYMBOLS 1 Semiconductor substrate, 1A 1st main surface, 1B 2nd main surface, 2 Thermal diffusion plate, 3 Lead frame, 4 Solder, 5 Electrode, 6 Protective film, 6E Side wall, 7 Ni film, 8 Au film, 10 Semiconductor Element, 11, 13 Mask pattern, 12 Protective film, 60 side edge, 60A surface part, 60B side end part, 60C convex part, 60D substantially flat part, 60F concave part, 60G inner peripheral inclined part, 60H protective film Apex part, 60I outer peripheral side inclined part, 60J parallel part, 61a, 61b lower layer protective film, 62a, 62b upper layer protective film, 62E end face.
本発明に係る半導体素子は、第1の主面を有し、第1の主面上に形成されている電極と、電極の表面上において開口部を有し、電極の少なくとも端部を覆うように形成されている保護膜と、開口部において電極上に形成されている第1めっき膜とを備え、保護膜は、開口部の側壁から開口部内に向けて延びる側縁部を含み、側縁部は、第1めっき膜と嵌合している嵌合部を有し、嵌合部は第1の主面に対して垂直な方向に延びる表面部分を有し、表面部分が第1めっき膜において表面部分よりも側壁側に位置する部分と接触することにより第1めっき膜と嵌合している。 The semiconductor element according to the present invention has a first main surface, an electrode formed on the first main surface, an opening on the surface of the electrode, and covering at least an end of the electrode. And a first plating film formed on the electrode in the opening, the protective film including a side edge extending from the side wall of the opening toward the inside of the opening, and the side edge Department has a fitting portion which is fitted with the first plating layer, the fitting portion has a surface portion extending in a direction perpendicular against the first major surface, a surface portion first plating film In contact with the portion located on the side of the side wall with respect to the surface portion, the first plating film is fitted.
本発明に係る半導体素子の製造方法は、第1の主面上に電極が形成されている半導体素子を準備する工程と、電極の表面上において開口部を有し、電極の少なくとも端部を覆う保護膜を形成する工程と、開口部において電極上に第1めっき膜を形成する工程とを備え、保護膜を形成する工程は、開口部の側壁から開口部内に向けて延びる側縁部を形成する工程を含み、側縁部を形成する工程では、第1の主面に対して垂直な方向に延びる表面部分を有し、表面部分が第1めっき膜において表面部分よりも側壁側に位置する部分と接触することにより第1めっき膜と嵌合する嵌合部を形成する。 The method of manufacturing a semiconductor device according to the present invention includes a step of preparing a semiconductor device having an electrode formed on a first main surface, an opening on the surface of the electrode, and covering at least an end of the electrode A step of forming a protective film and a step of forming a first plating film on the electrode in the opening, and the step of forming the protective film forms a side edge extending from the side wall of the opening toward the inside of the opening. comprising the step of, in the step of forming the side edge portion has a surface portion extending in a direction perpendicular against the first major surface, the surface portion is positioned on the side wall side of the surface portion in the first plating film A fitting portion that fits with the first plating film is formed by contacting the portion .
本発明に係る半導体素子は、第1の主面を有し、第1の主面上に形成されている電極と、電極の表面上において開口部を有し、電極の少なくとも端部を覆うように形成されている保護膜と、開口部において電極上に形成されている第1めっき膜と、第1めっき膜の電極と接する面と反対側に位置する面上に形成されている第2めっき膜と、第2めっき膜上に形成されているはんだ層とを備え、保護膜は、開口部の側壁から開口部内に向けて延びる側縁部を含み、側縁部は、第1めっき膜と嵌合している嵌合部を有し、嵌合部は第1の主面に対して垂直な方向に延びる表面部分を有し、表面部分が第1めっき膜において表面部分よりも側壁側に位置する部分と接触することにより第1めっき膜と嵌合している。はんだ層は、側縁部と、側縁部上に形成されている第2めっき膜の外周面と、側壁とに接している。本発明の他の局面に従った半導体素子は、第1の主面を有し、第1の主面上に形成されている電極と、電極の表面上において開口部を有し、電極の少なくとも端部を覆うように形成されている保護膜と、開口部において電極上に形成されている第1めっき膜とを備える。保護膜は第1の主面と交差する方向に延びる内周側傾斜部分と外周側傾斜部分と、膜厚が最も厚い部分である保護膜頂点部分とを有する。内周側傾斜部分は、外周側傾斜部分と比べて開口部の内側に位置し、保護膜頂点部分を挟んで外周側傾斜部分と連なるように形成されている。保護膜は外周側傾斜部分の少なくとも一部において第1めっき膜と面接触することにより第1めっき膜と嵌合している。 The semiconductor element according to the present invention has a first main surface, an electrode formed on the first main surface, an opening on the surface of the electrode, and covering at least an end of the electrode. A first plating film formed on the electrode in the opening, and a second plating formed on a surface located on the opposite side of the surface in contact with the electrode of the first plating film. A protective layer including a side edge portion extending from the side wall of the opening portion into the opening portion, the side edge portion including the first plating film and the solder layer formed on the second plating film. The fitting portion has a fitting portion, the fitting portion has a surface portion extending in a direction perpendicular to the first main surface, and the surface portion is closer to the side wall than the surface portion in the first plating film. The first plating film is fitted by contacting with the positioned portion. The solder layer is in contact with the side edge, the outer peripheral surface of the second plating film formed on the side edge, and the side wall. A semiconductor device according to another aspect of the present invention has a first main surface, an electrode formed on the first main surface, an opening on the surface of the electrode, and at least the electrode A protective film formed so as to cover the end, and a first plating film formed on the electrode in the opening. The protective film has an inner peripheral inclined portion and an outer peripheral inclined portion that extend in a direction intersecting the first main surface, and a protective film apex portion that is the thickest portion. The inner peripheral side inclined portion is located inside the opening as compared with the outer peripheral side inclined portion, and is formed to be continuous with the outer peripheral side inclined portion with the protective film apex portion interposed therebetween. The protective film is fitted to the first plating film by being in surface contact with the first plating film in at least a part of the inclined portion on the outer peripheral side.
本発明の半導体素子の製造方法は、第1の主面上に電極が形成されている半導体素
子を準備する工程と、電極の表面上において開口部を有し、電極の少なくとも端部を覆う保護膜を形成する工程と、開口部において電極上に第1めっき膜を形成する工程と、第1めっき膜において電極と接する面と反対側に位置する面上に第2めっき膜を形成する工程と、第2めっき膜上にはんだ層を形成する工程とを備え、保護膜を形成する工程は、開口部の側壁から開口部内に向けて延びる側縁部を形成する工程を含み、側縁部を形成する工程では、第1の主面に対して垂直な方向に延びる表面部分を有し、表面部分が第1めっき膜において表面部分よりも側壁側に位置する部分と接触することにより第1めっき膜と嵌合する嵌合部を形成する。はんだ層を形成する工程では、側縁部と、側縁部上に形成されている第2めっき膜の外周面と、側壁とに接するはんだ層が形成される。
The method of manufacturing a semiconductor device according to the present invention includes a step of preparing a semiconductor device having an electrode formed on a first main surface, and a protection having an opening on the surface of the electrode and covering at least an end portion of the electrode A step of forming a film, a step of forming a first plating film on the electrode in the opening, and a step of forming a second plating film on a surface of the first plating film located on a side opposite to the surface in contact with the electrode; Forming a solder layer on the second plating film, and the step of forming the protective film includes a step of forming a side edge extending from the side wall of the opening toward the inside of the opening. In the forming step, the first plating is provided by having a surface portion extending in a direction perpendicular to the first main surface, and the surface portion is in contact with a portion located on the side of the side wall of the first plating film. A fitting portion for fitting with the membrane is formed. In the step of forming the solder layer, a solder layer in contact with the side edge, the outer peripheral surface of the second plating film formed on the side edge, and the side wall is formed.
Claims (12)
前記第1の主面上に形成されている電極と、
前記電極の表面上において開口部を有し、前記電極の少なくとも端部を覆うように形成されている保護膜と、
前記開口部において前記電極上に形成されている第1めっき膜とを備え、
前記保護膜は、前記開口部の側壁から前記開口部内に向けて延びる側縁部を含み、
前記側縁部は、前記第1めっき膜と嵌合している嵌合部を有し、
前記嵌合部は前記第1の主面に交差する方向に延びる表面部分を有し、前記表面部分が前記第1めっき膜と接触することにより前記第1めっき膜と嵌合している、半導体素子。Having a first main surface,
An electrode formed on the first main surface;
A protective film having an opening on the surface of the electrode and formed to cover at least an end of the electrode;
A first plating film formed on the electrode in the opening,
The protective film includes a side edge extending from the side wall of the opening into the opening,
The side edge portion has a fitting portion that is fitted with the first plating film,
The fitting portion has a surface portion extending in a direction intersecting the first main surface, and the surface portion is fitted with the first plating film by contacting the first plating film. element.
前記第2めっき膜上に形成されているはんだ層とをさらに備える、請求項1〜請求項4のいずれか1項に記載の半導体素子。A second plating film formed on the surface of the first plating film located on the opposite side of the surface in contact with the electrode;
The semiconductor element of any one of Claims 1-4 further provided with the solder layer currently formed on the said 2nd plating film.
前記第1めっき膜はニッケルを含み、
前記第2めっき膜は金を含む、請求項6または請求項7に記載の半導体素子。The electrode comprises aluminum;
The first plating film includes nickel;
The semiconductor element according to claim 6, wherein the second plating film includes gold.
前記電極の表面上において開口部を有し、前記電極の少なくとも端部を覆う保護膜を形成する工程と、
前記開口部において前記電極上に第1めっき膜を形成する工程とを備え、
前記保護膜を形成する工程は、前記開口部の側壁から前記開口部内に向けて延びる側縁部を形成する工程を含み、
前記側縁部を形成する工程では、前記第1の主面に交差する方向に延びる表面部分を有し、前記表面部分が前記第1めっき膜と接触することにより前記第1めっき膜と嵌合する嵌合部を形成する、半導体素子の製造方法。Preparing a semiconductor element having an electrode formed on the first main surface;
Forming a protective film having an opening on the surface of the electrode and covering at least an end of the electrode;
Forming a first plating film on the electrode in the opening,
The step of forming the protective film includes a step of forming a side edge extending from the side wall of the opening toward the inside of the opening,
The step of forming the side edge includes a surface portion extending in a direction intersecting the first main surface, and the surface portion is fitted with the first plating film by contacting the first plating film. A method for manufacturing a semiconductor element, wherein a fitting portion is formed.