JPWO2008081755A1 - Adhesive tape and fixing method using the same - Google Patents

Adhesive tape and fixing method using the same Download PDF

Info

Publication number
JPWO2008081755A1
JPWO2008081755A1 JP2008552102A JP2008552102A JPWO2008081755A1 JP WO2008081755 A1 JPWO2008081755 A1 JP WO2008081755A1 JP 2008552102 A JP2008552102 A JP 2008552102A JP 2008552102 A JP2008552102 A JP 2008552102A JP WO2008081755 A1 JPWO2008081755 A1 JP WO2008081755A1
Authority
JP
Japan
Prior art keywords
adhesive tape
adhesive
sensitive adhesive
weight
meth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2008552102A
Other languages
Japanese (ja)
Inventor
博之 岩見
博之 岩見
Original Assignee
日東電工Ｃｓシステム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工Ｃｓシステム株式会社 filed Critical 日東電工Ｃｓシステム株式会社
Publication of JPWO2008081755A1 publication Critical patent/JPWO2008081755A1/en
Pending legal-status Critical Current

Abstract

基材の片面に粘着剤層を有する、物品の仮止め固定用粘着テープにおいて、前記基材が、ポリエステル系フィルムであり、前記粘着剤層が、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有するアクリル系エマルション型粘着剤により形成されたものであり、前記基材と前記粘着剤層との間には、ベースポリマーとしての芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含む下塗り層を有することを特徴とする物品の仮止め固定用粘着テープ。In the adhesive tape for temporarily fixing and fixing an article having an adhesive layer on one side of the substrate, the substrate is a polyester film, and the adhesive layer is an alkyl having 4 to 12 carbon atoms in an alkyl group ( Formed with an acrylic copolymer emulsion obtained from a monomer mixture containing a meth) acrylate as a main component and a carboxyl group-containing monomer and an acrylic emulsion-type pressure-sensitive adhesive containing an oxazoline group-containing aqueous crosslinking agent A temporary fixing for fixing an article characterized by having an undercoat layer containing an aromatic polyester resin as a base polymer and an isocyanate-based crosslinking agent between the base material and the pressure-sensitive adhesive layer Adhesive tape.

Description

本発明は、物品を仮止め固定するために用いられる粘着テープに関する。また、本発明は、前記粘着テープにより、物品が、仮止め固定された、仮止め固定物品に関する。さらに、本発明は、前記粘着テープにより物品を仮止め固定する物品の仮止め固定方法に関する。なお、本発明の粘着テープは、テープ状またはシート状で用いられる。   The present invention relates to an adhesive tape used for temporarily fixing an article. In addition, the present invention relates to a temporarily fixed article in which the article is temporarily fixed by the adhesive tape. Furthermore, the present invention relates to an article temporary fixing method for temporarily fixing an article with the adhesive tape. The pressure-sensitive adhesive tape of the present invention is used in a tape shape or a sheet shape.

本発明の物品の仮止め固定用粘着テープは、たとえば、電化製品、ＯＡ機器等の物品を製品出荷する際に、被着体である前記物品を梱包するにあたり、当該物品の内部部品やドア等の被着部分（たとえば、印刷鋼板や樹脂板等）を仮止め固定するために、前記被着部分に貼り付けて用いられる。たとえば、物品が冷蔵庫の場合には、本発明の粘着テープは、冷蔵庫のドア等の仮止め固定に用いられる。   The adhesive tape for temporarily fixing and fixing the article of the present invention is, for example, when packing an article such as an electrical appliance or an OA device, when packing the article as an adherend, an internal part of the article, a door, or the like In order to temporarily fix and fix a part to be adhered (for example, a printed steel plate or a resin plate), it is used by being attached to the part to be adhered. For example, when the article is a refrigerator, the pressure-sensitive adhesive tape of the present invention is used for temporary fixing of a refrigerator door or the like.

電化製品、ＯＡ機器等の物品の仮止め固定に用いられ粘着テープに要求される特性としては、被着体である物品の内部部品やドア等の被着部分を確実に固定するために、粘着テープが被着部分に貼り付けられた状態において応力が発生しても剥がれないことが求められる。また、前記物品はその使用にあたり、不要になった粘着テープを最終的に被着部分から剥離するため、当該粘着テープには容易に剥離することが求められる。このように、仮止め固定用粘着テープには相反する特性が要求される。   The properties required for adhesive tapes used for temporarily fixing and fixing articles such as electrical appliances and OA equipment include adhesives to securely fix the internal parts of articles that are adherends and the parts to be attached such as doors. It is required that the tape does not peel even if stress is generated in a state where the tape is attached to the adherend portion. In addition, when the article is used, the adhesive tape that is no longer needed is finally peeled off from the adherend, and therefore the adhesive tape is required to be easily peeled off. Thus, the temporarily fixing adhesive tape is required to have contradictory characteristics.

従来より、仮止め固定用粘着テープとしては、支持体の片面または両面に粘着剤層を形成したものが知られている。仮止め固定用粘着テープは、できるだけ安価なものであることが要求されるため、通常、ダンボール箱封緘用粘着テープと同様のものが用いられている（たとえば、特許文献１参照）。たとえば、汎用の延伸ポリプロピレン（ＯＰＰ）フィルムからなる基材の一面に粘着剤層を、他面に離型剤層を形成した粘着テープが一般的に用いられてきた。また、近年、ＯＰＰフィルムに代わり、より基材強度の高いポリエチレンテレフタレート（ＰＥＴ）フィルムや縦一軸延伸ポリプロピレンフィルムを基材とした粘着テープも使用されてきている。   2. Description of the Related Art Conventionally, adhesive tapes for fixing temporarily are known in which an adhesive layer is formed on one side or both sides of a support. Since the temporarily fixing adhesive tape is required to be as inexpensive as possible, the same adhesive tape as the cardboard box sealing adhesive tape is usually used (see, for example, Patent Document 1). For example, a pressure-sensitive adhesive tape in which a pressure-sensitive adhesive layer is formed on one surface of a base material made of a general-purpose stretched polypropylene (OPP) film and a release agent layer is formed on the other surface has been generally used. In recent years, pressure-sensitive adhesive tapes based on a polyethylene terephthalate (PET) film or a longitudinally uniaxially stretched polypropylene film having higher substrate strength instead of the OPP film have been used.

一方、仮止め固定用粘着テープに使用される粘着剤としては、有機溶剤型粘着剤が使用されていたが、一般の粘着剤の場合と同様に、環境保護、省資源、安全衛生等に対する社会的な要請と規制強化から、有機溶剤型粘着剤に代わる粘着剤として、水系粘着剤が用いられるようになっている。水系粘着剤としてはアクリル系エマルション型粘着剤が、通常、用いられる。   On the other hand, organic solvent-type adhesives were used as adhesives used for temporarily fixing adhesive tapes. However, as with ordinary adhesives, social protection for environmental protection, resource conservation, health and safety, etc. Due to general demands and stricter regulations, water-based adhesives are being used as adhesives to replace organic solvent adhesives. As the water-based adhesive, an acrylic emulsion-type adhesive is usually used.

アクリル系エマルション型粘着剤を塗布して形成した粘着剤層は、家電製品等の物品の被着部分（たとえば印刷鋼板や樹脂板等）に対する接着力が高い。しかしながら、前記基材とアクリル系エマルション型粘着剤により形成された粘着剤層とは密着力が弱い。そのため、仮止め固定用粘着テープを被着体から剥離する際には、被着部分の印刷面がむしり取られたり、粘着剤層の層間破壊により、被着体に糊残りが生じたりする問題があった。   A pressure-sensitive adhesive layer formed by applying an acrylic emulsion-type pressure-sensitive adhesive has a high adhesive force with respect to a part to be adhered (for example, a printed steel plate or a resin plate) of an article such as a home appliance. However, the adhesive force between the base material and the pressure-sensitive adhesive layer formed from the acrylic emulsion-type pressure-sensitive adhesive is weak. For this reason, when the adhesive tape for temporarily fixing is peeled off from the adherend, there is a problem that the printed surface of the adherend portion is peeled off, or adhesive residue is generated on the adherend due to interlayer breakage of the adhesive layer. there were.

特に、家電製品の国内仕様では、流通段階における環境温度として−２０℃〜＋５０℃の範囲が想定されており、高温処理や高温低温のサイクル処理下などの過酷な処理後であっても、接着力の増加がなく、糊残り現象が抑制された粘着テープ類が求められつつある。また、メッキ鋼板などの表面処理加工された被着体部分にプラスチック被着体用の粘着テープを用いると糊残りが生じてしまうといった問題が判明した。   In particular, in domestic specifications for home appliances, the environmental temperature in the distribution stage is assumed to be in the range of −20 ° C. to + 50 ° C. Even after severe processing such as high-temperature processing or high-temperature / low-temperature cycle processing, adhesion is possible. There is a demand for pressure-sensitive adhesive tapes that do not increase in force and have reduced adhesive residue. Further, a problem has been found that when an adhesive tape for a plastic adherend is used on a surface-treated adherend portion such as a plated steel plate, adhesive residue is generated.

さらに、上記粘着テープでは水性樹脂を用いるため、顔料や色素を混入・分散させることが困難であり、着色や隠蔽機能の付与が困難であった。このため、材料メーカーが自社の製品の差別化や広告のためにテープ表面を意匠的、広告的に活用することの他、隠蔽処理や安全対策面からの着色などができなかった。   Further, since the above adhesive tape uses an aqueous resin, it is difficult to mix and disperse pigments and dyes, and it is difficult to impart coloring and hiding functions. For this reason, the material manufacturer cannot use the tape surface for design and advertisement in order to differentiate its products and to advertise, and it cannot be concealed or colored for safety measures.

特開昭６３−８６７８６号公報JP-A 63-86786

本発明は、このような事情に照らし、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、かつ、高温処理や高温低温のサイクル処理下などの過酷な処理後であっても、目的を達成した後、剥離する際には容易に剥がすことができ、かつ糊残りが生じにくい、物品の仮止め固定用粘着テープを提供することを目的とする。   In light of such circumstances, the present invention is difficult to peel off even when stress is generated in a state of being attached to an adherend portion of an article that is an adherend, and is harsh under high temperature treatment or high temperature / low temperature cycle treatment. It is an object of the present invention to provide an adhesive tape for temporarily fixing and fixing articles, which can be easily peeled off when it is peeled after achieving the purpose even after a proper treatment, and is less likely to have adhesive residue.

また、本発明は、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、かつ、目的を達成した後、剥離する際には容易に剥がすことができ、着色が容易であり、かつ糊残りが生じにくい、物品の仮止め固定用粘着テープを提供することを目的とする。   In addition, the present invention is difficult to peel off even if stress is generated in a state of being attached to an adherend part of an article that is an adherend, and can be easily peeled off when the purpose is achieved and then peeled off. An object of the present invention is to provide an adhesive tape for temporarily fixing and fixing an article, which is easy to be colored and hardly causes adhesive residue.

さらに、本発明は、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、かつ、目的を達成した後、剥離する際には容易に剥がすことができ、着色が容易であり、かつ糊残りが生じにくい、物品の仮止め固定方法を提供することを目的とする。   Furthermore, the present invention is difficult to peel off even when stress is generated in a state of being attached to an adherend part of an article that is an adherend, and can be easily peeled off when the purpose is achieved and then peeled off. An object of the present invention is to provide a method for temporarily fixing and fixing an article, which is easy to be colored and hardly causes adhesive residue.

本発明者らは、上記課題を達成すべく鋭意研究を重ねた結果、以下に示す粘着テープにより上記目的を達成できることを見出し、本発明を完成するに至った。   As a result of intensive studies to achieve the above-mentioned problems, the present inventors have found that the above object can be achieved by the adhesive tape shown below, and have completed the present invention.

すなわち、本発明の粘着テープは、基材の片面に粘着剤層を有する、物品の仮止め固定用に用いられるものであって、
前記基材が、ポリエステル系フィルムであり、
前記粘着剤層が、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有するアクリル系エマルション型粘着剤により形成されたものであり、
前記基材と前記粘着剤層との間には、芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含む下塗り層を有することを特徴とする。That is, the pressure-sensitive adhesive tape of the present invention has a pressure-sensitive adhesive layer on one side of a substrate, and is used for temporarily fixing an article,
The substrate is a polyester film,
An acrylic copolymer emulsion obtained from a monomer mixture in which the pressure-sensitive adhesive layer contains an alkyl (meth) acrylate having an alkyl group having 4 to 12 carbon atoms as a main component and a carboxyl group-containing monomer. And an acrylic emulsion-type pressure-sensitive adhesive containing an oxazoline group-containing aqueous crosslinking agent,
Between the said base material and the said adhesive layer, it has the undercoat layer containing an aromatic polyester resin and an isocyanate type crosslinking agent, It is characterized by the above-mentioned.

本発明の粘着テープは、前記アルキル（メタ）アクリレートが、アルキル基の炭素数が４〜６のアルキル（メタ）アクリレート、及び、アルキル基の炭素数が７〜１２のアルキル（メタ）アクリレートを含有するものであることが好ましい。   In the pressure-sensitive adhesive tape of the present invention, the alkyl (meth) acrylate contains an alkyl (meth) acrylate having 4 to 6 carbon atoms in the alkyl group and an alkyl (meth) acrylate having 7 to 12 carbon atoms in the alkyl group. It is preferable that

本発明の粘着テープは、更に、前記アクリル系共重合体エマルションが窒素原子含有単量体を含有することが好ましい。   In the pressure-sensitive adhesive tape of the present invention, it is preferable that the acrylic copolymer emulsion further contains a nitrogen atom-containing monomer.

本発明の粘着テープは、前記カルボキシル基含有単量体がメタクリル酸であることが好ましい。   In the pressure-sensitive adhesive tape of the present invention, the carboxyl group-containing monomer is preferably methacrylic acid.

また、本発明は、上記の物品の仮止め固定用粘着テープにより、物品が、仮止め固定されていることを特徴とする、仮止め固定物品、に関する。   The present invention also relates to a temporarily fixed article, wherein the article is temporarily fixed by the above-described temporary fixing fixing adhesive tape.

さらに、本発明は、上記の物品の仮止め固定用粘着テープを用いて物品を仮止めすることを特徴とする物品の仮止め固定方法、に関する。   Further, the present invention relates to a method for temporarily fixing an article, characterized in that the article is temporarily fixed using the adhesive tape for temporarily fixing the article.

本発明の仮止め固定用粘着テープは、粘着剤層の形成にアクリル系エマルション型粘着剤を用いており、高温処理や高温低温のサイクル処理下などの過酷な処理後であっても、物品の被着体（被着部分）に対する接着力が良好であり、被着部分に粘着テープを貼り付けた状態で応力が発生しても剥がれにくく、物品の仮止め固定を確実に行うことができる。   The adhesive tape for temporary fixing of the present invention uses an acrylic emulsion-type pressure-sensitive adhesive for forming a pressure-sensitive adhesive layer, and even after severe processing such as high-temperature processing or high-temperature low-temperature cycle processing, Adhesive strength to the adherend (adhered portion) is good, and even if stress is generated in a state where the adhesive tape is applied to the adherend portion, it is difficult to peel off, and the article can be securely fixed temporarily.

また、本発明では、基材として、機械的強度の良いポリエステル系フィルムを用い、粘着剤層の形成に用いるアクリル系エマルション型粘着剤には、架橋剤として、オキサゾリン基含有水系架橋剤を用い、かつ、前記基材と粘着剤層との間には、芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含む下塗り層を設けている。このように、本発明では、基材、粘着剤層の架橋剤、下塗り層の材料として、それぞれ、選択して用いることにより、基材と粘着剤層との密着性を向上させている。そのため、本発明の仮止め固定用粘着テープは、目的を達成した後、被着体からの剥離を容易に行うことができ、被着部分の印刷面の毟り取りや、糊残りを生じにくくしている。また、本発明の仮止め固定用粘着テープの粘着剤層は、高温処理や高温低温のサイクル処理下などの過酷な処理後であっても、接着力が良好である他、凝集力（保持力）も良好であり、かかる点からも被着部分の印刷面のむしり取りや糊残りを生じにくくしている。さらに、本発明の粘着テープは、従来の粘着テープに比して、メッキ鋼板などの表面処理加工された被着体に対して接着性や糊残り性などの特性に特に改善されたものである。   In the present invention, a polyester film having good mechanical strength is used as a base material, and an acrylic emulsion-type pressure-sensitive adhesive used for forming a pressure-sensitive adhesive layer uses an oxazoline group-containing water-based cross-linking agent as a cross-linking agent. In addition, an undercoat layer containing an aromatic polyester resin and an isocyanate-based crosslinking agent is provided between the substrate and the pressure-sensitive adhesive layer. Thus, in this invention, the adhesiveness of a base material and an adhesive layer is improved by selecting and using as a base material, the crosslinking agent of an adhesive layer, and the material of undercoat, respectively. Therefore, the adhesive tape for temporary fixing of the present invention can be easily peeled off from the adherend after achieving the purpose, making it difficult to scrape the printed surface of the adherend and to leave no adhesive residue. ing. In addition, the adhesive layer of the adhesive tape for temporary fixing of the present invention has good adhesive strength and cohesive strength (holding power) even after severe processing such as high temperature processing or high temperature low temperature cycle processing. ) Is also good, and from this point, the printed surface of the adherend is not easily peeled off or the adhesive residue is hardly generated. Furthermore, the pressure-sensitive adhesive tape of the present invention is particularly improved in properties such as adhesion and adhesive residue with respect to a surface-treated adherend such as a plated steel sheet, as compared with conventional pressure-sensitive adhesive tapes. .

このように、本発明の仮止め固定用粘着テープは、物品の被着部分の仮止め固定を確実に行うことができる接着力を有し、かつ、糊残りなく、容易に剥がすことができ、接着性と剥離性の相反する特性を満足することができる。仮止め固定用粘着テープが適用される物品として例示される、家電製品の国内仕様では、流通段階における環境温度として、−２０℃〜＋５０℃の範囲が想定されているが、かかる本発明の仮止め固定用粘着テープは、前記仕様において、特に好適に用いられる。   As described above, the adhesive tape for temporarily fixing and fixing the present invention has an adhesive force capable of securely fixing the temporarily attached portion of the article, and can be easily peeled off without any adhesive residue. It is possible to satisfy the conflicting properties of adhesiveness and peelability. In the domestic specification of household electrical appliances exemplified as an article to which the temporary fixing fixing adhesive tape is applied, the environmental temperature in the distribution stage is assumed to be in the range of -20 ° C to + 50 ° C. The fixing tape for fastening and fixing is particularly preferably used in the above specifications.

また、上記粘着テープを用いることにより、従来の着色等が困難な水性樹脂を用いることなく上記物性を発現することが可能となるため、上記下塗り層に着色、装飾および隠蔽処理等が可能となるものである。したがって、本発明の粘着テープは、材料メーカーが自社の製品の差別化や広告のためにテープ表面を意匠的、広告的に活用することの他、隠蔽処理や安全対策面からの着色などを低コストで可能とするものである。   In addition, by using the adhesive tape, the above physical properties can be expressed without using a conventional aqueous resin that is difficult to be colored, so that the undercoat layer can be colored, decorated, concealed, and the like. Is. Therefore, the pressure-sensitive adhesive tape of the present invention reduces the concealment treatment and coloring from safety measures, in addition to the fact that the material manufacturer uses the surface of the tape for design and advertisement for the differentiation and advertisement of its products. It is possible at cost.

さらに、本発明の物品の仮止め固定方法は、上述のような作用効果を有する上記粘着テープを用いるため、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、かつ、目的を達成した後、剥離する際には容易に剥がすことができ、着色が容易であり、かつ糊残りが生じにくい、物品の仮止め固定方法となる。   Furthermore, since the method for temporarily fixing and fixing the article of the present invention uses the above-mentioned adhesive tape having the above-described effects, even if stress is generated in a state where it is applied to the adherend part of the article that is the adherend. This is a method for temporarily fixing an article, which is difficult to peel off and can be easily peeled off after achieving the purpose and is easy to be colored, and is less likely to have adhesive residue.

以下、本発明の実施の形態について詳細に説明する。   Hereinafter, embodiments of the present invention will be described in detail.

本発明の粘着テープは、基材の片面に粘着剤層を有する、物品の仮止め固定用に用いられるものであって、
前記基材が、ポリエステル系フィルムであり、
前記粘着剤層が、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有するアクリル系エマルション型粘着剤により形成されたものであり、
前記基材と前記粘着剤層との間には、芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含む下塗り層を有することを特徴とする。The pressure-sensitive adhesive tape of the present invention has a pressure-sensitive adhesive layer on one side of a substrate, and is used for temporarily fixing an article,
The substrate is a polyester film,
An acrylic copolymer emulsion obtained from a monomer mixture in which the pressure-sensitive adhesive layer contains an alkyl (meth) acrylate having an alkyl group having 4 to 12 carbon atoms as a main component and a carboxyl group-containing monomer. And an acrylic emulsion-type pressure-sensitive adhesive containing an oxazoline group-containing aqueous crosslinking agent,
Between the said base material and the said adhesive layer, it has the undercoat layer containing an aromatic polyester resin and an isocyanate type crosslinking agent, It is characterized by the above-mentioned.

本発明の物品の仮止め固定用粘着テープは、基材として、ポリエステル系フィルムを用いる。   The adhesive tape for temporarily fixing and fixing the article of the present invention uses a polyester film as a base material.

ポリエステル系フィルムの具体例としては、たとえば、ポリエチレンテレフタレートフィルム、ポリブチレンテレフタレートフィルム、ポリナフチレンテレフタレートフィルム等があげられる。これらのなかでもポリエチレンテレフタレートフィルムが好ましい。ポリエステル系フィルムは、延伸フィルムを用いることができる。   Specific examples of the polyester film include a polyethylene terephthalate film, a polybutylene terephthalate film, a polynaphthylene terephthalate film, and the like. Among these, a polyethylene terephthalate film is preferable. A stretched film can be used as the polyester film.

ポリエステル系フィルムは、特に限定されるものではないが、機械的強度の点より、厚みが２５〜１００μｍの範囲のものを用いるのが、家電製品の部品等を確実に仮固定することができるので好ましい。なお、厚みが２５μｍ未満のポリエステル系フィルムでは切れ易く、家電製品の部品を確実に仮固定するのに強度が不足する場合がある。一方、厚みが１００μｍを超えると鋼性が高くて扱い難く、コストが高くなる場合がある。   The polyester film is not particularly limited, but from the viewpoint of mechanical strength, using a film with a thickness in the range of 25 to 100 μm can reliably temporarily fix parts of home appliances, etc. preferable. In addition, it is easy to cut | disconnect with the polyester-type film less than 25 micrometers in thickness, and intensity | strength may be insufficient in order to temporarily fix the components of household appliances reliably. On the other hand, if the thickness exceeds 100 μm, the steel property is high and difficult to handle, and the cost may increase.

上記ポリエステル系フィルム表面にはコロナ放電処理を設けておくのが好ましい。またポリエステル系フィルムには、必要に応じて印刷などを施すことができる。また、ポリエステル系フィルムの粘着剤層を設けない側には、粘着テープを巻回したときの剥離性を確保するために、長鏡アルキル系、シリコーン系の背面処理剤により背面処理層を設けることができる。   It is preferable to provide a corona discharge treatment on the surface of the polyester film. Moreover, printing etc. can be given to a polyester-type film as needed. In addition, on the side of the polyester film where the adhesive layer is not provided, a back treatment layer is provided with a long mirror alkyl type or silicone type back treatment agent in order to ensure releasability when the adhesive tape is wound. Can do.

本発明の仮止め固定用粘着テープにおいて、粘着剤層を形成するアクリル系エマルション型粘着剤は、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションを含有する。アルキル（メタ）アクリレートは、アルキルアクリレートおよび／またはアルキルメタクリレートを意味する。   The acrylic emulsion-type pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer in the temporary fixing fixing pressure-sensitive adhesive tape of the present invention is mainly composed of an alkyl (meth) acrylate having an alkyl group having 4 to 12 carbon atoms and a carboxyl group-containing single-piece. An acrylic copolymer emulsion obtained from a monomer mixture containing a monomer is contained. Alkyl (meth) acrylate means alkyl acrylate and / or alkyl methacrylate.

アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートとしては、ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、イソアミル（メタ）アクリレート、ヘキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、２-エチルヘキシル（メタ）アクリレート、イソオクチル（メタ）アクリレート、イソノニル（メタ）アクリレート、などがあげられ、これらの中からその１種または２種以上が用いられる。   Examples of the alkyl (meth) acrylate having 4 to 12 carbon atoms in the alkyl group include butyl (meth) acrylate, isobutyl (meth) acrylate, isoamyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, 2- Examples include ethylhexyl (meth) acrylate, isooctyl (meth) acrylate, and isononyl (meth) acrylate, and one or more of these are used.

これらアルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートは、アクリル系共重合体エマルションを構成する単量体の主成分として、全単量体中、５０〜９９．９重量％程度を含むことが好ましい。好ましくは８０重量％以上、さらに好ましくは９０重量％以上、さらには９３重量％以上の割合で用いられる。アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートの割合が少ないと、良好な接着性の粘着剤が得られにくい。   These alkyl (meth) acrylates having 4 to 12 carbon atoms in the alkyl group, as a main component of the monomer constituting the acrylic copolymer emulsion, account for about 50 to 99.9% by weight in all monomers. It is preferable to include. The ratio is preferably 80% by weight or more, more preferably 90% by weight or more, and further 93% by weight or more. When the proportion of the alkyl (meth) acrylate having 4 to 12 carbon atoms in the alkyl group is small, it is difficult to obtain a good adhesive pressure-sensitive adhesive.

また、前記アルキル（メタ）アクリレートが、アルキル基の炭素数が４〜６のアルキル（メタ）アクリレート、及び、アルキル基の炭素数が７〜１２のアルキル（メタ）アクリレートを含有する(併用する)ものであることが、より好ましい態様である。アルキル基の炭素数が小さい（炭素数が４〜６）のものと、炭素数が大きい（炭素数が７〜１２）のアルキル（メタ）アクリレートを併用する理由としては、炭素数が小さいものを含有することにより、凝集力を向上させることができ、炭素数が大きいものを含有することにより、タックや粘着力を向上させることができ、これらを併用することにより、アクリル系エマルション型粘着剤の特性のバランスを取ることができ、有用である。   Further, the alkyl (meth) acrylate contains (used in combination) an alkyl (meth) acrylate having 4 to 6 carbon atoms in the alkyl group and an alkyl (meth) acrylate having 7 to 12 carbon atoms in the alkyl group. It is a more preferable aspect that it is. The reason why the alkyl group having a small number of carbon atoms (4 to 6 carbon atoms) and the alkyl (meth) acrylate having a large number of carbon atoms (7 to 12 carbon atoms) is used in combination is that of a small number of carbon atoms. By containing, the cohesive force can be improved, and by containing those having a large number of carbon atoms, tack and adhesive strength can be improved. By using these together, the acrylic emulsion-type pressure-sensitive adhesive It is possible to balance the characteristics and is useful.

前記アルキル基の炭素数が４〜６のアルキル（メタ）アクリレートは、アクリル系共重合体エマルションを構成する単量体の主成分として、全単量体中、１〜９０重量％程度を含むことが好ましく、より好ましくは１０〜３０重量％である。また、アルキル基の炭素数が７〜１２のアルキル（メタ）アクリレートは、アクリル系共重合体エマルションを構成する単量体の主成分として、全単量体中、１〜９５重量％程度を含むことが好ましく、より好ましくは５０〜９０重量％である。前記範囲内に含まれる場合、特に良好な接着性の粘着剤が得られる。   The alkyl (meth) acrylate having 4 to 6 carbon atoms in the alkyl group contains about 1 to 90% by weight in all monomers as a main component of the monomer constituting the acrylic copolymer emulsion. Is more preferable, and more preferably 10 to 30% by weight. Moreover, the alkyl (meth) acrylate having 7 to 12 carbon atoms in the alkyl group contains about 1 to 95% by weight in the whole monomer as a main component of the monomer constituting the acrylic copolymer emulsion. It is preferably 50 to 90% by weight. When included in the above range, a particularly good adhesive pressure-sensitive adhesive can be obtained.

共重合体エマルションを構成する単量体は、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートのほかに、被着体への接着力を向上させること、架橋点を導入すること、粘着剤の凝集力を高めることを目的とし、カルボキシル基含有単量体を含有している。カルボキシル基含有単量体は、分子中に少なくとも１つのカルボキシル基を含有していればよい。カルボキシル基含有単量体としては、アクリル酸、メタクリル酸、イタコン酸、マレイン酸、クロトン酸などがあげられ、特に好ましくはメタクリル酸である。メタクリル酸を使用した粘着テープは、鋼板などの金属板に接着後、粘着テープを剥離する際に、金属板に対する粘着力の上昇及び糊残りを抑制でき、粘着性(接着性)と剥離性という、相反する特性を満足できる優れた効果を有する。従って、本発明のように物品の仮止め固定用粘着テープに使用する場合に、有用である。   In addition to the alkyl (meth) acrylate having 4 to 12 carbon atoms in the alkyl group, the monomer constituting the copolymer emulsion can improve adhesion to the adherend, introduce a crosslinking point, For the purpose of increasing the cohesive strength of the pressure-sensitive adhesive, it contains a carboxyl group-containing monomer. The carboxyl group-containing monomer only needs to contain at least one carboxyl group in the molecule. Examples of the carboxyl group-containing monomer include acrylic acid, methacrylic acid, itaconic acid, maleic acid, and crotonic acid, with methacrylic acid being particularly preferred. Adhesive tape using methacrylic acid can suppress an increase in adhesive strength and adhesive residue on the metal plate when peeling the adhesive tape after bonding to a metal plate such as a steel plate, and is called adhesive (adhesive) and peelability , It has an excellent effect of satisfying conflicting characteristics. Therefore, it is useful when used for an adhesive tape for temporarily fixing and fixing articles as in the present invention.

カルボキシル基含有単量体は、アクリル系共重合体エマルションを構成する全単量体中、０．１〜１０重量％程度、好ましくは０．５〜７重量％の割合で用いられる。カルボキシル基含有単量体が０．１重量％未満では、凝集力が低下し、基材に対する密着性が低下するおそれある。一方、１０重量％を超える場合には、粘着性が低下するおそれがある。なお、単量体として、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートおよびカルボキシル基含有単量体を用いる場合には、それらの合計量が１００重量％になるように調整する。   The carboxyl group-containing monomer is used in a proportion of about 0.1 to 10% by weight, preferably 0.5 to 7% by weight, based on all monomers constituting the acrylic copolymer emulsion. If the carboxyl group-containing monomer is less than 0.1% by weight, the cohesive force is lowered and the adhesion to the substrate may be lowered. On the other hand, if it exceeds 10% by weight, the adhesiveness may be lowered. In addition, when using the alkyl (meth) acrylate and carboxyl group-containing monomer whose carbon number of an alkyl group is 4-12 as a monomer, it adjusts so that those total amounts may be 100 weight%.

また、アクリル系共重合体エマルションには、本発明の特性に支障がない範囲で、前記以外の単量体を使用してもよい。これら他の単量体等は、アクリル系共重合体エマルションを構成する全単量体中、１０重量％以下の割合で使用するのが好ましい。   Moreover, you may use a monomer other than the above for an acrylic copolymer emulsion in the range which does not have trouble in the characteristic of this invention. These other monomers are preferably used in a proportion of 10% by weight or less in the total monomers constituting the acrylic copolymer emulsion.

上述の他の単量体としては、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート、２−ヒドロキシブチル（メタ）アクリレートなどの水酸基含有単量体；（メタ）アクリルアミド、Ｎ，Ｎ−ジメチル（メタ）アクリルアミド、Ｎ−メチロール（メタ）アクリルアミド、Ｎ−メトキシメチル（メタ）アクリルアミド、Ｎ−ブトキシメチル（メタ）アクリルアミドなどのアミド基含有単量体；２−（Ｎ，Ｎ−ジメチルアミノ）エチル（メタ）アクリレートなどのアミノ基含有単量体；グリシジル（メタ）アクリレートなどのグリシジル基含有単量体；プロピルトリメトキシシラン（メタ）アクリレート、プロピルジメトキシシラン（メタ）アクリレート、プロピルトリエトキシシラン（メタ）アクリレートなどのアルコキシシリル基含有単量体；（メタ）アクリロニトリル、Ｎ−（メタ）アクリロイルモルホリン、Ｎ−ビニル−２−ピロリドンなどがあげられる。また、メチル（メタ）アクリレート、エチル（メタ）アクリレート、イソプロピル（メタ）アクリレートなどのアルキル基の炭素数が１〜３のアルキル（メタ）アクリレート；トリデシル（メタ）アクリレート、ステアリル（メタ）アクリレートなどのアルキル基の炭素数が１３〜１８のアルキル（メタ）アクリレート、酢酸ビニル、スチレン、ビニルトルエンなどがあげられる。また、ネオペンチルグリコールジ（メタ）アクリレート、ヘキサンジオールジ（メタ）アクリレート、プロピレングリコールジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、テトラメチロールメタンテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート等の二つ以上の重合性官能基を有するものがあげられる。これら単量体はその１種を単独でまたは２種以上を使用できる。なお、他の単量体としては、前記アミド基含有単量体や、アミノ基含有単量体、（メタ）アクリロニトリルなどの窒素原子含有単量体を用いることがより好ましく、特に（メタ）アクリロニトリルを用いることが好ましい態様である。（メタ）アクリロニトリルを使用することにより、被着体表面が粗面の場合に、粗面に対するアクリル系エマルション型粘着剤の親和性(粘着性)が向上し、物品の被着部分への仮止めを確実に行うことができ、有用である。また、アクリル系エマルション型粘着剤中に窒素原子含有単量体とカルボキシル基含有単量体が共存すると、その相互作用により内部凝集力(保持力)が向上し、有用である。   Examples of other monomers mentioned above include hydroxyl group-containing monomers such as 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, and 2-hydroxybutyl (meth) acrylate; (meth) acrylamide, N Amide group-containing monomers such as N, N-dimethyl (meth) acrylamide, N-methylol (meth) acrylamide, N-methoxymethyl (meth) acrylamide, N-butoxymethyl (meth) acrylamide; Amino group-containing monomers such as dimethylamino) ethyl (meth) acrylate; glycidyl group-containing monomers such as glycidyl (meth) acrylate; propyltrimethoxysilane (meth) acrylate, propyldimethoxysilane (meth) acrylate, propyltri Ethoxysilane (meth) acrelane Alkoxysilyl group-containing monomers such as; (meth) acrylonitrile, N- (meth) acryloyl morpholine, N- vinyl-2-pyrrolidone. In addition, alkyl (meth) acrylates having 1 to 3 carbon atoms of alkyl groups such as methyl (meth) acrylate, ethyl (meth) acrylate, isopropyl (meth) acrylate, etc .; tridecyl (meth) acrylate, stearyl (meth) acrylate, etc. Examples thereof include alkyl (meth) acrylates having 13 to 18 carbon atoms in the alkyl group, vinyl acetate, styrene, and vinyl toluene. Also, neopentyl glycol di (meth) acrylate, hexanediol di (meth) acrylate, propylene glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, tetramethylolmethane tetra (meth) acrylate, dipentaerythritol hexa ( Examples thereof include those having two or more polymerizable functional groups such as (meth) acrylate. These monomers can be used alone or in combination of two or more. As the other monomer, it is more preferable to use a nitrogen atom-containing monomer such as the amide group-containing monomer, amino group-containing monomer, or (meth) acrylonitrile, and particularly (meth) acrylonitrile. It is a preferable aspect to use. By using (meth) acrylonitrile, when the adherend surface is rough, the affinity (adhesiveness) of the acrylic emulsion-type pressure-sensitive adhesive to the rough surface is improved, and temporarily fixed to the adherend part of the article Can be performed reliably and is useful. Further, when a nitrogen atom-containing monomer and a carboxyl group-containing monomer coexist in an acrylic emulsion-type pressure-sensitive adhesive, the internal cohesive force (holding force) is improved by the interaction, which is useful.

前記窒素原子含有単量体は、アクリル系共重合体エマルションを構成する全単量体中、０．１〜１５重量％程度が好ましく、より好ましくは２〜８重量％の割合で用いられる。カルボキシル基含有単量体が前記範囲内の場合、粘着性と凝集力(保持力)を向上することができ、有用である。   The nitrogen atom-containing monomer is preferably used in an amount of about 0.1 to 15% by weight, more preferably 2 to 8% by weight, based on all monomers constituting the acrylic copolymer emulsion. When the carboxyl group-containing monomer is within the above range, the adhesiveness and cohesion (retention force) can be improved, which is useful.

アクリル系共重合体エマルションは、前記単量体を、乳化剤の存在下に、適宜の重合開始剤を用いて、常法により乳化重合することにより得られる。乳化重合は、一般的な一括重合、連続滴下重合、分割滴下重合などにより行う。   The acrylic copolymer emulsion is obtained by subjecting the monomer to emulsion polymerization by a conventional method using an appropriate polymerization initiator in the presence of an emulsifier. Emulsion polymerization is performed by general batch polymerization, continuous dropping polymerization, divided dropping polymerization, or the like.

乳化剤としては、乳化重合において用いられるアニオン系乳化剤やノニオン系乳化剤を特に制限なく使用できる。たとえば、ラウリル硫酸ナトリウム、ラウリル硫酸アンモニウム、ドデシルベンゼンスルホン酸ナトリウム、ポリオキシエチレンアルキルエーテル硫酸ナトリウム、ポリオキシエチレンアルキルフェニルエーテル硫酸ナトリウムなどのアニオン系乳化剤、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテルなどのノニオン系乳化剤などがあげられる。その他、カチオン系乳化剤、両性乳化剤を用いることができる。乳化剤の使用量は、特に制限されないが、単量体（合計）１００重量部に対して、０．３〜５重量部程度とするのが好ましい。   As the emulsifier, anionic emulsifiers and nonionic emulsifiers used in emulsion polymerization can be used without particular limitation. For example, anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzene sulfonate, sodium polyoxyethylene alkyl ether sulfate, sodium polyoxyethylene alkyl phenyl ether sulfate, polyoxyethylene alkyl ether, polyoxyethylene alkyl phenyl ether, etc. Nonionic emulsifiers and the like. In addition, cationic emulsifiers and amphoteric emulsifiers can be used. Although the usage-amount of an emulsifier is not restrict | limited in particular, It is preferable to set it as about 0.3-5 weight part with respect to 100 weight part of monomers (total).

重合開始剤としては、たとえば、２，２′−アゾビスイソブチロニトリル、２，２′−アゾビス（２−アミジノプロパン）ジヒドロクロライド、２，２′−アゾビス（Ｎ，Ｎ′−ジメチレンイソブチルアミジン）などのアゾ系開始剤、過硫酸カリウム、過硫酸アンモニウムなどの過硫酸塩系開始剤、ベンゾイルパーオキサイド、ｔ−ブチルハイドロパ−オキサイドなどの過酸化物系開始剤や、過硫酸塩と亜硫酸水素ナトリウムなどのレドツクス系開始剤などがあげられる。また、乳化重合においては、得られる共重合体の分子量の調整のために、必要に応じて、メルカプタン類などに代表される適宜の連鎖移動剤を使用してもよい。   Examples of the polymerization initiator include 2,2′-azobisisobutyronitrile, 2,2′-azobis (2-amidinopropane) dihydrochloride, 2,2′-azobis (N, N′-dimethyleneisobutyl). Azo initiators such as amidine), persulfate initiators such as potassium persulfate and ammonium persulfate, peroxide initiators such as benzoyl peroxide and t-butyl hydroperoxide, and persulfates and sulfites. Examples thereof include redox initiators such as sodium hydrogen. In the emulsion polymerization, an appropriate chain transfer agent typified by mercaptans may be used as necessary to adjust the molecular weight of the resulting copolymer.

アクリル系共重合体エマルションは、重量平均分子量が１５万以上であることが好ましく、さらには２５万以上であることが好ましく、より好ましくは１００万以上であり、特に好ましくは１００万〜２００万である。重量平均分子量が１５万未満の場合には、アクリル系エマルション型粘着剤の凝集力が低下し、被着体（基材）に対する密着性も低下する傾向がある。重量平均分子量が大きく設定することにより、アクリル系エマルション型粘着剤の被着体に対する糊残り性を改善することができる。重量平均分子量は、テトラヒドロフラン可溶分をＧＰＣ（ゲルパーミエーションクロマトグラフィー）により測定した値である。   The acrylic copolymer emulsion preferably has a weight average molecular weight of 150,000 or more, more preferably 250,000 or more, more preferably 1,000,000 or more, particularly preferably 1,000,000 to 2,000,000. is there. When the weight average molecular weight is less than 150,000, the cohesive force of the acrylic emulsion-type pressure-sensitive adhesive is lowered, and the adhesion to the adherend (base material) tends to be lowered. By setting the weight average molecular weight large, it is possible to improve the adhesive residue on the adherend of the acrylic emulsion-type pressure-sensitive adhesive. The weight average molecular weight is a value obtained by measuring tetrahydrofuran-soluble content by GPC (gel permeation chromatography).

本発明のアクリル系エマルション型粘着剤は、上記アクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有する。   The acrylic emulsion-type pressure-sensitive adhesive of the present invention contains the above acrylic copolymer emulsion and an oxazoline group-containing aqueous crosslinking agent.

オキサゾリン基含有水系架橋剤としては、分子内にオキサゾリン基を有し、かつ水分散性または水溶性の水系架橋剤であれば、制限なく使用できる。たとえば、２−ビニル−２−オキサゾリン、２−ビニル−４−メチル−２−オキサゾリン、２−ビニル−５−メチル−２−オキサゾリン、２−イソプロペニル−２−オキサゾリン、２−イソプロペニル−４−メチル−２−オキサゾリン、２−イソプロペニル−５−エチル−２−オキサゾリン等の付加重合性オキサゾリンを１種又は２種以上用いて乳化重合等により得られた水系架橋剤が用いられる。具体的には、日本触媒社製の商品名「エポクロスＷＳ−５００」、「エポクロスＷＳ−７００」があげられる。   The oxazoline group-containing aqueous crosslinking agent can be used without limitation as long as it has an oxazoline group in the molecule and is water-dispersible or water-soluble. For example, 2-vinyl-2-oxazoline, 2-vinyl-4-methyl-2-oxazoline, 2-vinyl-5-methyl-2-oxazoline, 2-isopropenyl-2-oxazoline, 2-isopropenyl-4- An aqueous crosslinking agent obtained by emulsion polymerization or the like using one or more addition polymerizable oxazolines such as methyl-2-oxazoline and 2-isopropenyl-5-ethyl-2-oxazoline is used. Specifically, trade names “Epocross WS-500” and “Epocross WS-700” manufactured by Nippon Shokubai Co., Ltd. may be mentioned.

オキサゾリン基含有水系架橋剤（固形分）の配合量は、アクリル系共重合体エマルション１００重量部（固形分）に対して、０．０１〜１０重量部程度とするのが好ましい。同配合量が０．０１重量部未満の場合は、架橋剤としてのオキサゾリン基が少なくなるため、凝集力が低下し、基材に対する密着性も低下するおそれがある。一方、同配合量が１０重量部を超える場合は、接着力が低下する傾向がある。   The amount of the oxazoline group-containing aqueous crosslinking agent (solid content) is preferably about 0.01 to 10 parts by weight with respect to 100 parts by weight (solid content) of the acrylic copolymer emulsion. When the blending amount is less than 0.01 parts by weight, the oxazoline group as a crosslinking agent is reduced, so that the cohesive force is lowered and the adhesion to the substrate may be lowered. On the other hand, when the blending amount exceeds 10 parts by weight, the adhesive force tends to decrease.

さらに、本発明で用いられるアクリル系エマルション型粘着剤には、その特性を阻害しない範囲で各種添加剤、たとえば軟化剤、可塑剤、粘着付与剤、老化防止剤、着色剤を用いることができる。また、前記オキサゾリン基と前記アクリル系共重合体エマルション中のカルボキシル基の反応速度の調整剤として、カルボキシル基と塩を形成する水酸化ナトリウムなどの水酸化金属化合物、アンモニア、アルキルアミンなどの塩基性化合物を配合することができる。   Furthermore, various additives such as a softener, a plasticizer, a tackifier, an anti-aging agent, and a colorant can be used in the acrylic emulsion-type pressure-sensitive adhesive used in the present invention as long as the properties are not impaired. In addition, as a regulator of the reaction rate of the carboxyl group in the oxazoline group and the acrylic copolymer emulsion, a metal hydroxide compound such as sodium hydroxide that forms a salt with the carboxyl group, basic such as ammonia and alkylamine A compound can be blended.

なお、本発明の水性エマルション型粘着剤組成物は、ガラス転移温度が−１０〜−８０℃、さらに−２０〜−６０℃であることが望ましい。ガラス転移温度は、ＤＳＣ（示差熱分析）により測定した値である。   In addition, as for the water-based emulsion type adhesive composition of this invention, it is desirable that glass transition temperature is -10-80 degreeC, and also -20-20 degreeC. The glass transition temperature is a value measured by DSC (differential thermal analysis).

本発明の物品の仮止め固定用粘着テープは、前記基材と粘着剤層との間に、芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含む下塗り層を有する。   The pressure-sensitive adhesive tape for temporarily fixing an article of the present invention has an undercoat layer containing an aromatic polyester resin and an isocyanate-based crosslinking agent between the base material and the pressure-sensitive adhesive layer.

下塗り層を形成するために用いられる下塗り剤は、芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含むものが用いられるが、芳香族ポリエステル樹脂をベースポリマー（５０重量％以上の主成分、好ましくは６０重量％以上、より好ましくは７０重量％以上）として含むものであって本発明の目的を損なわない範囲であれば、他の樹脂を混合してもよい。   As the primer used for forming the primer layer, those containing an aromatic polyester resin and an isocyanate-based crosslinking agent are used. The aromatic polyester resin is used as a base polymer (main component of 50% by weight or more, preferably 60% by weight). % Or more, more preferably 70% by weight or more), and other resins may be mixed as long as the object of the present invention is not impaired.

本発明の芳香族ポリエステル樹脂とは、特に制限されないが、テレフタル酸、イソフタル酸、セバシン酸エチレングリコール、ジエチレングリコールなどを単量体成分として含むポリエステル樹脂があげられる。たとえば、ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート（ＰＢＴ）、ポリナフチレンテレフタレート、ポリアリレート系樹脂などがあげられる。これらのなかでもセバシン酸エチレングリコールを含むポリエチレンテレフタレート（ＰＥＴ）が好ましい。   The aromatic polyester resin of the present invention is not particularly limited, and examples thereof include polyester resins containing terephthalic acid, isophthalic acid, ethylene glycol sebacate, diethylene glycol and the like as monomer components. Examples thereof include polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polynaphthylene terephthalate, and polyarylate resin. Among these, polyethylene terephthalate (PET) containing ethylene glycol sebacate is preferable.

本発明におけるイソシアネート系架橋剤とは、２以上のイソシアネート基（イソシアネート基をブロック剤、数量体化などにより一時的に保護したイソシアネート再生型官能基を含む）を１分子中に有するイソシアネート化合物をいう。   The isocyanate-based crosslinking agent in the present invention refers to an isocyanate compound having two or more isocyanate groups (including isocyanate-regenerating functional groups in which isocyanate groups are temporarily protected by blocking agents, quantification, etc.) in one molecule. .

本発明のイソシアネート系架橋剤としては、トリレンジイソシアネート、キシレンジイソシアネートなどの芳香族イソシアネート、イソホロンジイソシアネートなどの脂環族イソシアネート、ヘキサメチレンジイソシアネートなどの脂肪族イソシアネートなどがあげられる。   Examples of the isocyanate-based crosslinking agent of the present invention include aromatic isocyanates such as tolylene diisocyanate and xylene diisocyanate, alicyclic isocyanates such as isophorone diisocyanate, and aliphatic isocyanates such as hexamethylene diisocyanate.

より具体的には、たとえば、ブチレンジイソシアネート、ヘキサメチレンジイソシアネートなどの低級脂肪族ポリイソシアネート類、シクロペンチレンジイソシアネート、シクロヘキシレンジイソシアネート、イソホロンジイソシアネートなどの脂環族イソシアネート類、２，４−トリレンジイソシアネート、４，４’−ジフェニルメタンジイソシアネート、キシリレンジイソシアネート、ポリメチレンポリフェニルイソシアネートなどの芳香族ジイソシアネート類、トリメチロールプロパン／トリレンジイソシアネート３量体付加物（日本ポリウレタン工業社製、商品名コロネートＬ）、トリメチロールプロパン／ヘキサメチレンジイソシアネート３量体付加物（日本ポリウレタン工業社製、商品名コロネートＨＬ）、ヘキサメチレンジイソシアネートのイソシアヌレート体（日本ポリウレタン工業社製、商品名コロネートＨＸ）などのイソシアネート付加物、ポリエーテルポリイソシアネート、ポリエステルポリイソシアネート、ならびにこれらと各種のポリオールとの付加物、イソシアヌレート結合、ビューレット結合、アロファネート結合などで多官能化したポリイソシアネートなどをあげることができる。   More specifically, for example, lower aliphatic polyisocyanates such as butylene diisocyanate and hexamethylene diisocyanate, alicyclic isocyanates such as cyclopentylene diisocyanate, cyclohexylene diisocyanate and isophorone diisocyanate, 2,4-tolylene diisocyanate, Aromatic diisocyanates such as 4,4′-diphenylmethane diisocyanate, xylylene diisocyanate, polymethylene polyphenyl isocyanate, trimethylolpropane / tolylene diisocyanate trimer adduct (trade name Coronate L manufactured by Nippon Polyurethane Industry Co., Ltd.), tri Methylolpropane / hexamethylene diisocyanate trimer adduct (trade name Coronate HL, manufactured by Nippon Polyurethane Industry Co., Ltd.), hexamethylene dii Isocyanurate of cyanate (product name: Coronate HX, manufactured by Nippon Polyurethane Industry Co., Ltd.), polyether polyisocyanate, polyester polyisocyanate, and adducts of these with various polyols, isocyanurate bond, burette bond And polyisocyanates polyfunctionalized with allophanate bonds.

上記イソシアネート系架橋剤は単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、下塗り層に含まれる上記芳香族ポリエステル樹脂１００重量部に対し、前記イソシアネート系架橋剤０．０１〜１０重量部含有することが好ましく、０．１〜５重量部含有することがより好ましく、０．５〜２重量部含有することがさらに好ましい。０．０１重量部未満では、密着性付与効果が不足する場合があり、一方、１０重量部を越えると、架橋形成が過多となり、粘着剤面への転写発生、外観不良(白化)などの問題が生じる場合がある。   The isocyanate-based crosslinking agent may be used alone or in combination of two or more, but the total content is 100 parts by weight of the aromatic polyester resin contained in the undercoat layer. On the other hand, it is preferable to contain 0.01-10 weight part of the said isocyanate type crosslinking agent, It is more preferable to contain 0.1-5 weight part, It is more preferable to contain 0.5-2 weight part. If it is less than 0.01 parts by weight, the effect of imparting adhesion may be insufficient. On the other hand, if it exceeds 10 parts by weight, excessive crosslinking will be formed, causing problems such as transfer to the pressure-sensitive adhesive surface and poor appearance (whitening). May occur.

下塗り層の形成は、通常、前記基材に、下塗り剤を塗工し、乾燥することにより行われる。下塗り層の厚み（乾燥後）は、通常、０．００１〜３μｍ程度、好ましくは０．０１〜２μｍであり、さらに好ましくは、０．０３〜２μｍである。かかる範囲の厚みであれば、基材と粘着剤層との密着性を十分向上させることができる。   The undercoat layer is usually formed by applying an undercoat agent to the substrate and drying it. The thickness of the undercoat layer (after drying) is usually about 0.001 to 3 μm, preferably 0.01 to 2 μm, and more preferably 0.03 to 2 μm. If it is the thickness of this range, the adhesiveness of a base material and an adhesive layer can fully be improved.

粘着剤層の形成は、上述のアクリル系エマルション型粘着剤を、下塗り層の表面に直接塗布し乾燥させることにより形成することができる。またセパレータ上に形成した粘着剤層を、下塗り層を有する基材上に転写することによっても粘着剤層を形成することができる。粘着剤層の厚み（乾燥後）は、通常、１０〜５０μｍ程度、好ましくは２０〜４０μｍである。   The pressure-sensitive adhesive layer can be formed by directly applying and drying the above-mentioned acrylic emulsion-type pressure-sensitive adhesive on the surface of the undercoat layer. The pressure-sensitive adhesive layer can also be formed by transferring the pressure-sensitive adhesive layer formed on the separator onto a substrate having an undercoat layer. The thickness (after drying) of the pressure-sensitive adhesive layer is usually about 10 to 50 μm, preferably 20 to 40 μm.

また、本発明の粘着テープは、メッキ鋼板などの表面処理加工された被着体に対して接着性や糊残り性などの特性に特に優れるものである。   The pressure-sensitive adhesive tape of the present invention is particularly excellent in properties such as adhesiveness and adhesive residue with respect to an adherend subjected to surface treatment such as a plated steel plate.

上記被着体としては、表面処理加工された亜鉛メッキ鋼板、電磁鋼板、アルミニウム板、亜鉛板、銅版、ステンレス板、トタン板、ガルバニウム板、ニッケル板、真鋳などがあげられる。   Examples of the adherend include surface-treated galvanized steel sheet, electromagnetic steel sheet, aluminum plate, zinc plate, copper plate, stainless steel plate, tin plate, galvanium plate, nickel plate, true casting and the like.

また、上記表面処理とは、クロムメッキ処理、アルミメッキ処理、クロムフリー無機処理、クロムフリー有機処理などをあげることができる。   Examples of the surface treatment include chrome plating treatment, aluminum plating treatment, chrome-free inorganic treatment, and chrome-free organic treatment.

また、本発明の粘着テープの被着体としては、上記被着体のほか、ポリカーボネート、ポリスチレン、ポリプロピレン、ポリエチレン、アクリロニトリルブタジエンスチレン、ハイインパクトポリスチレンなどのプラスチック類、またはその混合物等をあげることができる。   Examples of the adherend of the pressure-sensitive adhesive tape of the present invention include the above-mentioned adherend, plastics such as polycarbonate, polystyrene, polypropylene, polyethylene, acrylonitrile butadiene styrene, and high impact polystyrene, or a mixture thereof. .

本発明の物品の仮止め固定用粘着テープは、前記基材に、前記下塗り剤により形成された下塗り層を介して、粘着剤層が設けられている。   The pressure-sensitive adhesive tape for temporarily fixing an article of the present invention is provided with a pressure-sensitive adhesive layer on the base material via an undercoat layer formed of the undercoat agent.

以下、本発明の構成と効果を具体的に示す実施例等について説明する。   Examples and the like specifically showing the configuration and effects of the present invention will be described below.

〔実施例１〕
（基材）
厚さ３８μｍのポリエチレンテレフタレートフィルムを用いた。当該フィルムは、一方の面に、長鎖アルキル系背面処理剤（一方社油脂工業社製、ピーロイル１０１０）を溶剤（トルエン）に溶解した溶液を、乾燥厚みが、０．５μｍとなるように塗工した背面処理層を有する。[Example 1]
(Base material)
A polyethylene terephthalate film having a thickness of 38 μm was used. The film is coated on one surface with a solution obtained by dissolving a long-chain alkyl-based back-treating agent (manufactured by Oil and Fat Industries, Pyroyl 1010) in a solvent (toluene) so that the dry thickness is 0.5 μm. It has a processed back treatment layer.

（下塗り剤）
芳香族ポリエステルとイソシアネート系架橋剤からなる下塗り剤（ＡＳＡ ＣＯＬＯＲ社製、ＡＳＡ ＲＯＴＯ ＰＲＩＭＥＲ＃２、青色顔料入り）を１００重量部用いた。(Undercoat)
100 parts by weight of an undercoat made of an aromatic polyester and an isocyanate-based crosslinking agent (ASA COLOR, ASA ROTO PRIMER # 2, containing a blue pigment) was used.

（粘着剤）
アクリル系共重合体エマルション（ＤＯＷ社製、ＤＯＷ ＵＣＡＲ ＬＡＴＥＸ Ｒ−９８０１Ｍ）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。(Adhesive)
Oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) 2 parts by weight (solid content conversion) with respect to 100 parts of solid content of acrylic copolymer emulsion (DOW UCAR LATEX R-9801M, manufactured by DOW) ) To prepare an acrylic emulsion-type pressure-sensitive adhesive.

前記アクリル系共重合体エマルションは、ｎ−ブチルアクリレート９５重量部およびアクリル酸５重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、重量平均分子量は１５０万であった。また、アクリル系エマルション型粘着剤のガラス転移温度は−４５℃であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 95 parts by weight of n-butyl acrylate and 5 parts by weight of acrylic acid in the presence of an anionic emulsifier, and the weight average molecular weight was 1,500,000. there were. The glass transition temperature of the acrylic emulsion-type pressure-sensitive adhesive was −45 ° C.

（粘着テープの作製）
上記基材の片面（背面処理層を設けていない側、コロナ処理面）に、上記下塗り剤を乾燥後の厚さが１μｍになるように塗工して、１００℃で１分間乾燥し、下塗り層を形成した。さらに、下塗り層の上に、上記アクリル系エマルション型粘着剤を、乾燥後の厚さが３０μｍ厚みとなるように塗工して、１２０℃で３分間乾燥し、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
On one side of the substrate (the side where the back treatment layer is not provided, the corona-treated surface), the primer is applied so that the thickness after drying is 1 μm, and dried at 100 ° C. for 1 minute. A layer was formed. Furthermore, on the undercoat layer, the acrylic emulsion-type pressure-sensitive adhesive is applied so that the thickness after drying is 30 μm, and dried at 120 ° C. for 3 minutes to form a pressure-sensitive adhesive layer. An adhesive tape was obtained.

〔実施例２〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。[Example 2]
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、ｎ−ブチルアクリレート９４重量部およびメタクリル酸６重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 94 parts by weight of n-butyl acrylate and 6 parts by weight of methacrylic acid in the presence of an anionic emulsifier, and the sol molecular weight was about 300,000 ( Viscosity: 200 cps) (base 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例３〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 3
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、ｎ−ブチルアクリレート９８重量部およびアクリル酸２重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 98 parts by weight of n-butyl acrylate and 2 parts by weight of acrylic acid in the presence of an anionic emulsifier, and the sol molecular weight was about 300,000 ( Viscosity: 200 cps) (base 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例４〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 4
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、ｎ−ブチルアクリレート９６重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 96 parts by weight of n-butyl acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier, and the sol molecular weight was about 300,000 ( Viscosity: 200 cps) (base 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例５〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 5
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、ｎ−ブチルアクリレート９８重量部およびメタクリル酸２重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 98 parts by weight of n-butyl acrylate and 2 parts by weight of methacrylic acid in the presence of an anionic emulsifier, and the sol molecular weight was about 300,000 ( Viscosity: 200 cps) (base 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例６〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 6
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート９６重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 96 parts by weight of 2-ethylhexyl (meth) acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier, and the sol molecular weight was about It was 300,000 (viscosity: 200 cps) (base 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例７〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 7
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート９０重量部、ｎ−ブチルアクリレート６重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 90 parts by weight of 2-ethylhexyl (meth) acrylate, 6 parts by weight of n-butyl acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier. The sol molecular weight was about 300,000 (viscosity: 200 cps) (base: 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例８〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 8
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート７５重量部、ｎ−ブチルアクリレート２１重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 75 parts by weight of 2-ethylhexyl (meth) acrylate, 21 parts by weight of n-butyl acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier. The sol molecular weight was about 300,000 (viscosity: 200 cps) (base: 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例９〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 9
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート５５重量部、ｎ−ブチルアクリレート４１重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 55 parts by weight of 2-ethylhexyl (meth) acrylate, 41 parts by weight of n-butyl acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier. The sol molecular weight was about 300,000 (viscosity: 200 cps) (base: 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例１０〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 10
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート３５重量部、ｎ−ブチルアクリレート６１重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 35 parts by weight of 2-ethylhexyl (meth) acrylate, 61 parts by weight of n-butyl acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier. The sol molecular weight was about 300,000 (viscosity: 200 cps) (base: 52%).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, the adhesive layer was formed, and the adhesive tape was obtained.

〔実施例１１〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 11
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート７５重量部、ｎ−ブチルアクリレート２１重量部およびメタクリル酸４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約４０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion was obtained by emulsion polymerization of 75 parts by weight of 2-ethylhexyl (meth) acrylate, 21 parts by weight of n-butyl acrylate and 4 parts by weight of methacrylic acid in the presence of an anionic emulsifier. The sol molecular weight was about 400,000 (viscosity: 200 cps) (52% base).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例１２〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 12
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート８６重量部、ｎ−ブチルアクリレート６重量部、メタクリル酸４重量部、及びアクリロニトリル４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion emulsifies 86 parts by weight of 2-ethylhexyl (meth) acrylate, 6 parts by weight of n-butyl acrylate, 4 parts by weight of methacrylic acid, and 4 parts by weight of acrylonitrile in the presence of an anionic emulsifier. It was obtained by polymerization, and the sol molecular weight was about 300,000 (viscosity: 200 cps) (52% base).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例１３〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 13
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート９０重量部、ｎ−ブチルアクリレート４重量部、メタクリル酸２重量部、及びアクリロニトリル４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion is prepared by emulsifying 90 parts by weight of 2-ethylhexyl (meth) acrylate, 4 parts by weight of n-butyl acrylate, 2 parts by weight of methacrylic acid, and 4 parts by weight of acrylonitrile in the presence of an anionic emulsifier. It was obtained by polymerization, and the sol molecular weight was about 300,000 (viscosity: 200 cps) (52% base).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例１４〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 14
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート９１重量部、ｎ−ブチルアクリレート４重量部、メタクリル酸１重量部、及びアクリロニトリル４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion emulsifies 91 parts by weight of 2-ethylhexyl (meth) acrylate, 4 parts by weight of n-butyl acrylate, 1 part by weight of methacrylic acid, and 4 parts by weight of acrylonitrile in the presence of an anionic emulsifier. It was obtained by polymerization, and the sol molecular weight was about 300,000 (viscosity: 200 cps) (52% base).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔実施例１５〕
（粘着剤）
アクリル系共重合体エマルション（ＲＯＨＭ＆ＨＡＡＳ社製、ＲＯＢＯＮＤ ＲＨ−２１８）の固形分１００部に対し、オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）２重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。Example 15
(Adhesive)
For 100 parts of solid content of acrylic copolymer emulsion (ROHM & HAAS, ROBOND RH-218), 2 parts by weight (in terms of solid content) of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) The acrylic emulsion type pressure-sensitive adhesive was prepared by blending.

前記アクリル系共重合体エマルションは、２-エチルヘキシル（メタ）アクリレート７１重量部、ｎ−ブチルアクリレート２１重量部、メタクリル酸４重量部、及びアクリロニトリル４重量部を、アニオン系乳化剤の存在下に、乳化重合して得られたものであり、ゾル分子量は約３０万（粘度：２００ｃｐｓ）（ベース５２％）であった。   The acrylic copolymer emulsion emulsifies 71 parts by weight of 2-ethylhexyl (meth) acrylate, 21 parts by weight of n-butyl acrylate, 4 parts by weight of methacrylic acid, and 4 parts by weight of acrylonitrile in the presence of an anionic emulsifier. It was obtained by polymerization, and the sol molecular weight was about 300,000 (viscosity: 200 cps) (52% base).

（粘着テープの作製）
実施例１と同様の下塗り剤により、実施例１と同様にして下塗り層を形成した。また、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
An undercoat layer was formed in the same manner as in Example 1 using the same undercoat as in Example 1. Moreover, except having used the above-mentioned thing as an adhesive, it carried out similarly to Example 1, and formed the adhesive layer, and obtained the adhesive tape.

〔比較例１〕
（下塗り剤）
芳香族ポリエステルからなる下塗り剤（ＡＳＡ ＣＯＬＯＲ社製、ＡＳＡ ＲＯＴＯ ＰＲＩＭＥＲ＃３、イソシアネート系架橋剤を含まない）を１００重量部用いた。[Comparative Example 1]
(Undercoat)
100 parts by weight of an undercoat made of an aromatic polyester (ASA COLOR, ASA ROTO PRIMER # 3, not containing an isocyanate-based crosslinking agent) was used.

（粘着テープの作製）
実施例１において、下塗り剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、下塗り層を形成した。また、実施例１と同様のアクリル系エマルション型粘着剤により、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, an undercoat layer was formed in the same manner as in Example 1 except that the above-described one was used as the undercoat agent. Moreover, the adhesive layer was formed like Example 1 with the acrylic emulsion type adhesive similar to Example 1, and the adhesive tape was obtained.

〔比較例２〕
（下塗り剤）
直鎖型ポリエステル（東洋紡績社製、バイロン３００）１００重量およびポリイソシアネート（住友バイウレタン社製、スミジュールＮ−７５）５重量部からなる下塗り剤を用いた。[Comparative Example 2]
(Undercoat)
An undercoat comprising 100 parts by weight of linear polyester (Toyobo Co., Ltd., Byron 300) and 5 parts by weight of polyisocyanate (Sumitomo Biurethane Co., Ltd., Sumidur N-75) was used.

（粘着テープの作製）
実施例１において、下塗り剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、下塗り層を形成した。また、実施例１と同様のアクリル系エマルション型粘着剤により、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, an undercoat layer was formed in the same manner as in Example 1 except that the above-described one was used as the undercoat agent. Moreover, the adhesive layer was formed like Example 1 with the acrylic emulsion type adhesive similar to Example 1, and the adhesive tape was obtained.

〔比較例３〕
（下塗り剤）
分岐型ポリエステル（日立化成社製、エスペル９９４０Ｄ）１００重量およびイソシアネート系架橋剤（日本ポリウレタン社製、コロネートＬ）５重量部からなる下塗り剤を用いた。[Comparative Example 3]
(Undercoat)
An undercoat composed of 100 parts by weight of branched polyester (Hitachi Chemical Co., Espel 9940D) and 5 parts by weight of an isocyanate-based crosslinking agent (Nihon Polyurethane Co., Ltd., Coronate L) was used.

（粘着テープの作製）
実施例１において、下塗り剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、下塗り層を形成した。また、実施例１と同様のアクリル系エマルション型粘着剤により、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, an undercoat layer was formed in the same manner as in Example 1 except that the above-described one was used as the undercoat agent. Moreover, the adhesive layer was formed like Example 1 with the acrylic emulsion type adhesive similar to Example 1, and the adhesive tape was obtained.

〔比較例４〕
（下塗り剤）
直鎖型ポリエステル（東洋紡績社製、バイロン３００）１００重量を下塗り剤として用いた。[Comparative Example 4]
(Undercoat)
100 weights of linear polyester (Toyobo Co., Ltd., Byron 300) was used as a primer.

（粘着テープの作製）
実施例１において、下塗り剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、下塗り層を形成した。また、実施例１と同様のアクリル系エマルション型粘着剤により、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, an undercoat layer was formed in the same manner as in Example 1 except that the above-described one was used as the undercoat agent. Moreover, the adhesive layer was formed like Example 1 with the acrylic emulsion type adhesive similar to Example 1, and the adhesive tape was obtained.

〔比較例５〕
（下塗り剤）
分岐型ポリエステル（日立化成社製、エスペル９９４０Ｄ）１００重量を下塗り剤として用いた。[Comparative Example 5]
(Undercoat)
100 weights of branched polyester (Espel 9940D, manufactured by Hitachi Chemical Co., Ltd.) was used as a primer.

（粘着テープの作製）
実施例１において、下塗り剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、下塗り層を形成した。また、実施例１と同様のアクリル系エマルション型粘着剤により、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, an undercoat layer was formed in the same manner as in Example 1 except that the above-described one was used as the undercoat agent. Moreover, the adhesive layer was formed like Example 1 with the acrylic emulsion type adhesive similar to Example 1, and the adhesive tape was obtained.

〔比較例６〕
（粘着剤）
アクリル系共重合体エマルション（ＤＯＷ社製、ＤＯＷ ＵＣＡＲ ＬＡＴＥＸ Ｒ−９８０１Ｍ）の固形分１００部に対し、アジリジン系架橋剤（日本触媒社製、ケミタイトＰＺ−３３）０．５重量部（固形分換算）を配合して、アクリル系エマルション型粘着剤を調製した。[Comparative Example 6]
(Adhesive)
0.5 parts by weight (in terms of solid content) of an aziridine-based crosslinker (manufactured by Nippon Shokubai Co., Chemitite PZ-33) with respect to 100 parts of a solid content of an acrylic copolymer emulsion (DOW UCAR LATEX R-9801M, manufactured by DOW) ) To prepare an acrylic emulsion-type pressure-sensitive adhesive.

（粘着テープの作製）
実施例１において、粘着剤として、上記記載のものを用いたこと以外は、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, a pressure-sensitive adhesive layer was formed in the same manner as in Example 1 except that the above-described one was used as the pressure-sensitive adhesive, to obtain a pressure-sensitive adhesive tape.

〔比較例７〕
（粘着テープの作製）
実施例１において、下塗り剤を用いなかったこと以外は、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。[Comparative Example 7]
(Production of adhesive tape)
In Example 1, an adhesive layer was formed in the same manner as in Example 1 except that the primer was not used, and an adhesive tape was obtained.

〔比較例８〕
（粘着テープの作製）
実施例１において、粘着剤にオキサゾリン基含有水溶性架橋剤を用いなかったこと以外は、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。[Comparative Example 8]
(Production of adhesive tape)
In Example 1, an adhesive layer was formed in the same manner as in Example 1 except that the oxazoline group-containing water-soluble crosslinking agent was not used for the adhesive, and an adhesive tape was obtained.

〔比較例９〕
（下塗り剤）
オキサゾリン基含有水溶性架橋剤（日本触媒社製、ＷＳ−７００）１００重量を下塗り剤として用いた。[Comparative Example 9]
(Undercoat)
100 weight of an oxazoline group-containing water-soluble crosslinking agent (manufactured by Nippon Shokubai Co., Ltd., WS-700) was used as a primer.

（粘着テープの作製）
実施例１において、下塗り剤として、上記記載のものを用いたこと以外は、実施例１と同様にして、下塗り層を形成した。また、実施例１と同様のアクリル系エマルション型粘着剤により、実施例１と同様にして粘着剤層を形成して、粘着テープを得た。(Production of adhesive tape)
In Example 1, an undercoat layer was formed in the same manner as in Example 1 except that the above-described one was used as the undercoat agent. Moreover, the adhesive layer was formed like Example 1 with the acrylic emulsion type adhesive similar to Example 1, and the adhesive tape was obtained.

上記の実施例、比較例等で得られた粘着テープについて、以下の要領で粘着力、せん断力、保持力、および糊残り性の測定および評価を行った。表１は、実施例１及び２、比較例１〜９について記載した。表２は、実施例１〜１５についての評価結果を記載した。なお、表２の実施例１及び２については、一部表１の結果と重複して記載した。   About the adhesive tape obtained by said Example, comparative example, etc., the adhesive force, the shear force, the retention strength, and the adhesive residue were measured and evaluated in the following manner. Table 1 describes Examples 1 and 2 and Comparative Examples 1-9. Table 2 lists the evaluation results for Examples 1-15. In addition, about Example 1 and 2 of Table 2, it overlapped and described with the result of Table 1 partially.

〔粘着力〕
２５ｍｍ幅の粘着テープを、予めトルエンにて洗浄したステンレス板（ＳＵＳ３０４ＢＡ、表中はステン板と記載）、ポリカーボネート板（ＰＣ）、亜鉛メッキ電磁鋼板、及びアクリロニトリル−スチレン−ブタジエン樹脂（ＡＢＳ）板をブラスト加工により粗面仕上げした板（ＡＢＳ粗面）に、２３℃×６０％ＲＨ中で、ゴムローラーにて、それぞれ貼り合わせ、３０分間放置(保存)した後、当該試料を万能引張試験機（オリエテック社製、ＲＴＭ−１００）にて、剥離速度３００ｍｍ／ｍｉｎで１８０°方向に引き剥がした時の抵抗を、粘着力（Ｎ／２５ｍｍ）として測定した。剥離性の点から、粘着力は、５〜１５Ｎ／２５ｍｍ、さらには５〜１０Ｎ／２５ｍｍであることが好ましい。なお、前記ＡＢＳ板に粘着テープを貼り合わせた際の粘着力としては、１．５〜１５Ｎ／２５ｍｍが好ましく、さらには２〜１０Ｎ／２５ｍｍであることが好ましい。
その他に、前記被着体に粘着テープをそれぞれ貼り付け、６０℃にて３日間放置した後、室温（２３℃）に戻して、粘着力を測定した。〔Adhesive force〕
A stainless steel plate (SUS304BA, described as a stainless steel plate in the table), a polycarbonate plate (PC), a galvanized magnetic steel plate, and an acrylonitrile-styrene-butadiene resin (ABS) plate previously washed with 25 mm wide adhesive tape with toluene. Each plate was subjected to blasting (ABS rough surface) with a rubber roller at 23 ° C. × 60% RH and left (stored) for 30 minutes. The resistance when peeled in the direction of 180 ° at a peeling speed of 300 mm / min was measured as the adhesive strength (N / 25 mm) using RTM-100 manufactured by Orietec. From the viewpoint of peelability, the adhesive strength is preferably 5 to 15 N / 25 mm, more preferably 5 to 10 N / 25 mm. In addition, as an adhesive force at the time of sticking an adhesive tape on the said ABS board, 1.5-15N / 25mm is preferable, Furthermore, it is preferable that it is 2-10N / 25mm.
In addition, adhesive tapes were respectively attached to the adherends, allowed to stand at 60 ° C. for 3 days, then returned to room temperature (23 ° C.), and the adhesive strength was measured.

〔剪断力〕
２５ｍｍ幅の粘着テープを、予めトルエンにて洗浄したステンレス板（ＳＵＳ３０４ＢＡ）に、２３℃×６０％ＲＨ中で、圧着面積が２５ｍｍ×２５ｍｍとなるようにゴムローラーにて貼り合わせ、３０分間放置した後、当該試料を万能引張試験機（オリエテック製社、ＲＴＭ−１００）にて、剥離速度３００ｍｍ／ｍｉｎで剪断方向に剥がした時の抵抗を剪断力（Ｎ／２５ｍｍ×２５ｍｍ）として測定した。被着体に対する応力下における接着性の点から、剪断力は、１００〜４００Ｎ／２５ｍｍ×２５ｍｍ、さらには１３０〜２５０Ｎ／２５ｍｍ×２５ｍｍであることが好ましい。[Shearing force]
A 25 mm wide adhesive tape was bonded to a stainless steel plate (SUS304BA) previously washed with toluene with a rubber roller in 23 ° C. × 60% RH so that the crimping area was 25 mm × 25 mm and left for 30 minutes. Thereafter, the resistance when the sample was peeled in the shearing direction at a peeling speed of 300 mm / min was measured as a shearing force (N / 25 mm × 25 mm) with a universal tensile testing machine (Orietec, RTM-100). From the viewpoint of adhesion to the adherend under stress, the shearing force is preferably 100 to 400 N / 25 mm × 25 mm, more preferably 130 to 250 N / 25 mm × 25 mm.

〔保持力〕
ＪＩＳ Ｚ−０２３７に準じて、測定温度４０℃、吊下げ荷重１ｋｇの条件で６０分間後のズレ距離（ｍｍ）を測定した。被着体に対する応力下における接着性の点から、保持力は、０〜１ｍｍ、さらには０〜０．３ｍｍであることが好ましい。[Retention force]
According to JIS Z-0237, the displacement distance (mm) after 60 minutes was measured under the conditions of a measurement temperature of 40 ° C. and a hanging load of 1 kg. From the viewpoint of adhesiveness to the adherend under stress, the holding force is preferably 0 to 1 mm, more preferably 0 to 0.3 mm.

〔被着体に対する糊残り性〕
ポリカーボネート板（ＰＣ）、ポリスチレン板（ＰＳ）、亜鉛メッキ電磁鋼板を被着体として、粘着テープをそれぞれ貼り付け、６０℃にて１２０時間(５日間)放置(保存)した後、室温（２３℃）に戻してから、人の手により粘着テープを剥離し、剥離時に被着体から粘着剤が剥がれているかを以下の基準で目視観察し判定した。
その他に、前記被着体に粘着テープをそれぞれ貼り付け、６０℃にて２０日間放置した後、室温（２３℃）に戻してから測定したもの、６０℃×湿度９０％にて５日間放置した後、室温（２３℃）に戻してから測定したもの、６０℃×湿度９０％にて２０日間放置した後、室温（２３℃）に戻してから測定したもの、６０℃×湿度９０％にて３日間放置し、更に０℃にて３日間放置した後、０℃の状態のまま測定したものについて、糊残り性を判定した。
・被着体に粘着剤の剥がれ残りが認められなかった場合：○
・被着体に粘着剤の剥がれ残りが点状に認められた場合：△
・被着体に粘着剤の剥がれ残りが面状に認められた場合：△×
・被着体に粘着剤の剥がれ残りが全面で認められた場合：×。[Adhesive residue on adherend]
A polycarbonate plate (PC), a polystyrene plate (PS), and a galvanized magnetic steel plate were used as adherends, adhesive tapes were attached to each substrate, left (stored) at 60 ° C for 120 hours (5 days), and then room temperature (23 ° C ), The pressure-sensitive adhesive tape was peeled off by human hand, and whether or not the pressure-sensitive adhesive was peeled off from the adherend during peeling was visually observed and judged according to the following criteria.
In addition, an adhesive tape was applied to each of the adherends, and allowed to stand at 60 ° C. for 20 days, then returned to room temperature (23 ° C.), and measured at 60 ° C. × 90% humidity for 5 days. Then, measured after returning to room temperature (23 ° C.), left to stand for 20 days at 60 ° C. × 90% humidity, measured after returning to room temperature (23 ° C.), at 60 ° C. × 90% humidity The mixture was allowed to stand for 3 days, and further allowed to stand at 0 ° C. for 3 days.
・ If the adhesive is not peeled off on the adherend: ○
・ If the adhesive remains peeled off on the adherend: △
・ If the adhesive remains peeled off on the adherend: △ ×
・ If the adhesive remains on the entire surface of the adherend: x.

上記結果を表１及び表２に示す。   The results are shown in Tables 1 and 2.

Figure 2008081755
Figure 2008081755

Figure 2008081755
Figure 2008081755

上記表１の結果より、本発明によって作製された粘着テープを用いた場合（実施例１〜２）、いずれの実施例においても、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、かつ、高温処理や高温低温のサイクル処理下などの過酷な処理後であっても、粘着力の増加が抑制されており、かつ、プラスチック被着体および表面処理された鋼板のいずれにおいても糊残りが生じにくいことがわかる。   From the results of Table 1 above, when the pressure-sensitive adhesive tape produced according to the present invention is used (Examples 1 and 2), in any example, the adhesive tape is attached to the adherend part of the article that is the adherend. Even if stress occurs, it is difficult to peel off, and even after severe processing such as high-temperature processing or high-temperature low-temperature cycle processing, increase in adhesive force is suppressed, and plastic adherend and surface treatment It can be seen that no glue residue is likely to occur in any of the steel sheets that have been used.

また、上記表２の結果より、実施例全てにおいて、粘着力、剪断力、保持力及び糊残り性について、優れた特性を有することが確認できた。特に、粘着剤に含有されるアルキル（メタ）アクリレートについて、アルキル（メタ）アクリレートにおけるアルキル基の炭素数が４〜６のものと、炭素数が７〜１２のものを併用した実施例７〜１５においては、６０℃×湿度９０％にて２０日間放置した後、室温（２３℃）に戻してから測定した糊残り性において、過酷な環境下に曝したにも拘らず、良好な結果を得ることが確認できた。また、更に窒素原子含有単量体を含有した実施例１２〜１５においては、対ＡＢＳ粗面に対する粘着力が高い値を維持していることがわかり、ＡＢＳ粗面に対する親和性(粘着性)に優れていることも確認でき、更に、高温処理や高温低温のサイクル処理下などの過酷な処理後においても、糊残りがなく、糊残り性にも優れていることが確認できた。   Moreover, from the result of the said Table 2, in all the Examples, it has confirmed that it had the outstanding characteristic about adhesive force, shearing force, holding power, and adhesive residue. In particular, with respect to the alkyl (meth) acrylate contained in the pressure-sensitive adhesive, Examples 7 to 15 in which alkyl groups having 4 to 6 carbon atoms in the alkyl (meth) acrylate and those having 7 to 12 carbon atoms are used in combination. In the case of No. 1, the adhesive residue measured after leaving for 20 days at 60 ° C. and 90% humidity and returning to room temperature (23 ° C.) gives good results despite being exposed to a harsh environment. I was able to confirm. Further, in Examples 12 to 15 containing a nitrogen atom-containing monomer, it was found that the adhesive strength against the ABS rough surface maintained a high value, and the affinity (adhesiveness) to the ABS rough surface was maintained. It was also confirmed that it was excellent, and it was confirmed that there was no adhesive residue and excellent adhesive residue even after severe processing such as high temperature processing and high temperature low temperature cycle processing.

Claims (6)

基材の片面に粘着剤層を有する、物品の仮止め固定用粘着テープにおいて、
前記基材が、ポリエステル系フィルムであり、
前記粘着剤層が、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有するアクリル系エマルション型粘着剤により形成されたものであり、
前記基材と前記粘着剤層との間には、芳香族ポリエステル樹脂およびイソシアネート系架橋剤を含む下塗り層を有することを特徴とする物品の仮止め固定用粘着テープ。In the pressure-sensitive adhesive tape for temporarily fixing the article, having an adhesive layer on one side of the substrate,
The substrate is a polyester film,
An acrylic copolymer emulsion obtained from a monomer mixture in which the pressure-sensitive adhesive layer contains an alkyl (meth) acrylate having an alkyl group having 4 to 12 carbon atoms as a main component and a carboxyl group-containing monomer. And an acrylic emulsion-type pressure-sensitive adhesive containing an oxazoline group-containing aqueous crosslinking agent,
A pressure-sensitive adhesive tape for temporarily fixing an article comprising an undercoat layer containing an aromatic polyester resin and an isocyanate-based crosslinking agent between the substrate and the pressure-sensitive adhesive layer. 前記アルキル（メタ）アクリレートが、アルキル基の炭素数が４〜６のアルキル（メタ）アクリレート、及び、アルキル基の炭素数が７〜１２のアルキル（メタ）アクリレートを含有するものであることを特徴とする請求項１記載の物品の仮止め固定用粘着テープ。   The alkyl (meth) acrylate contains an alkyl (meth) acrylate having 4 to 6 carbon atoms in the alkyl group and an alkyl (meth) acrylate having 7 to 12 carbon atoms in the alkyl group. An adhesive tape for temporarily fixing and fixing an article according to claim 1. 更に、前記アクリル系共重合体エマルションが窒素原子含有単量体を含有すること特徴とする請求項１又は２記載の物品の仮止め固定用粘着テープ。   The pressure-sensitive adhesive tape for temporarily fixing an article according to claim 1 or 2, wherein the acrylic copolymer emulsion further contains a nitrogen atom-containing monomer. 前記カルボキシル基含有単量体がメタクリル酸であることを特徴とする請求項１〜３のいずれかに記載の物品の仮止め固定用粘着テープ。   The pressure-sensitive adhesive tape for temporarily fixing an article according to any one of claims 1 to 3, wherein the carboxyl group-containing monomer is methacrylic acid. 請求項１〜４に記載の物品の仮止め固定用粘着テープにより、物品が、仮止め固定されていることを特徴とする、仮止め固定物品。   The temporarily fixed article, wherein the article is temporarily fixed by the adhesive tape for temporarily fixing the article according to claim 1. 請求項１〜４に記載の物品の仮止め固定用粘着テープを用いて物品を仮止めすることを特徴とする物品の仮止め固定方法。   A method for temporarily fixing an article, comprising temporarily fixing the article using the adhesive tape for temporarily fixing an article according to claim 1.
JP2008552102A 2006-12-25 2007-12-21 Adhesive tape and fixing method using the same Pending JPWO2008081755A1 (en)