JPS63104834A - Plate glass/ thrust board backing sheet/plate glass laminate, plate glass/double-sided thrust board stuck sheet/plate glass laminate and plate glass/thrust board/base material laminate - Google Patents
Plate glass/ thrust board backing sheet/plate glass laminate, plate glass/double-sided thrust board stuck sheet/plate glass laminate and plate glass/thrust board/base material laminateInfo
- Publication number
- JPS63104834A JPS63104834A JP24985786A JP24985786A JPS63104834A JP S63104834 A JPS63104834 A JP S63104834A JP 24985786 A JP24985786 A JP 24985786A JP 24985786 A JP24985786 A JP 24985786A JP S63104834 A JPS63104834 A JP S63104834A
- Authority
- JP
- Japan
- Prior art keywords
- plate glass
- laminate
- plate
- sheet
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Abstract] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、新規な化粧材であり、家具調度品や事務用品
として有用な板ガラス／ｌＷ板裏打シート／板ガラス積
層品、板ガラス／両面■板貼りシート／板ガラス積層品
及び板ガラス／作仮／基材槓層品に関する。Detailed Description of the Invention (Industrial Field of Application) The present invention is a novel decorative material and is useful for furniture and office supplies. Concerning pasting sheets/laminated plate glass products and plate glass/temporary/base material laminated products.
（従来の技術及び発明が解決しようとする問題点）従来
より表具面が透明な化粧材として、例えば第６図に示す
ような、銘木の竹板１４（化粧単板）を例えばアクリル
樹脂製の透明シート１３の内部に埋設した化粧材１２が
開発、利用されている。(Problems to be Solved by the Prior Art and the Invention) Conventionally, as a decorative material with a transparent surface, a bamboo board 14 (decorative veneer) made of precious wood, as shown in FIG. A decorative material 12 embedded inside a transparent sheet 13 has been developed and used.
しかし、この檀の化粧材１２は、一般に樹脂の性質上、
表具面の光沢や艷に欠ける他、光や熱に対して劣化し易
く、耐候性や耐熱性等が不十分であるという欠点を有し
ていた。However, this wooden decorative material 12 is generally due to the nature of the resin.
In addition to lacking luster and luster on the surface, it also had the drawbacks of being easily degraded by light and heat, and having insufficient weather resistance and heat resistance.
また、この化粧材１２は、従来より、所定厚の綿板１４
を浅底容器内のｍ融樹脂の中へ埋め入れ、その後樹ｌｉ
ｗを固化させる方法により通常製造されている。Moreover, this decorative material 12 has conventionally been made of a cotton board 14 of a predetermined thickness.
embed in m-molten resin in a shallow container, and then
It is usually produced by a method of solidifying w.
しかし、この製法では、塊根１４が化粧材１２の表裏面
１５ａ、１５ｂに対して完全に平行に位置するように化
粧材１２を作ることが極めて困難であり、その上製造工
程において諜板１４の埋入れ時空気が溶融樹脂中にまき
こまれ易く、この結果気泡１６がそのまま残ったまま樹
脂が固化し、気泡欠陥のある化粧材製品が得られること
が多かった。However, with this manufacturing method, it is extremely difficult to make the decorative material 12 so that the tuberous roots 14 are positioned completely parallel to the front and back surfaces 15a and 15b of the decorative material 12, and in addition, in the manufacturing process, the Air tends to be drawn into the molten resin during embedding, and as a result, the resin solidifies while the air bubbles 16 remain intact, often resulting in decorative material products with air bubble defects.
またτ隻板貼り化粧板の高級仕上げのための表面塗装と
してポリウレタン樹脂やポリエステル樹脂での塗装が行
なわれている。この塗装は、溶融樹脂を該化粧板表面上
で固化させて、樹脂層を積層することによりなされる。In addition, polyurethane resin or polyester resin is used as a surface coating to give a high-quality finish to the τ-board decorative board. This coating is performed by solidifying molten resin on the surface of the decorative board and laminating resin layers.
しかし、樹脂はその性質上光沢や艷に欠けるため、祷ら
れた化粧板は桟板表面の木理を鮮明に視認することがで
きるものではなかった。また樹脂は、光や熱に対して劣
化しやすい欠点も有する。さらに、この樹脂層を一様の
厚さに及び表面を滑らかに積層することは非常に困難で
ある。これは樹脂層の厚さが増すにつれ、さらに困難と
なる。However, due to the nature of resin, it lacks luster and luster, so the decorative board that was used did not allow the grain of the wood on the surface of the board to be clearly seen. Resins also have the disadvantage of being easily degraded by light and heat. Furthermore, it is very difficult to laminate this resin layer to a uniform thickness and a smooth surface. This becomes more difficult as the thickness of the resin layer increases.
−万、家具調度品の中にはガラス板を調度品表面の■板
の上に重ね置いたものが従来より製造、販売されている
。しかし、このような家具調度品は、ガラス板と＄１板
が密溜しておらず、ガラス板を通じて＄？板辰而面木理
を必ずしも鮮明に視認することができるものではなかっ
た。- Some furniture items have been manufactured and sold in the past, with glass plates stacked on top of the ■ panel on the surface of the furniture. However, in such furniture items, the glass plate and the $1 plate are not tightly packed together, and the $1 plate is passed through the glass plate. It was not always possible to clearly see the grain of the wood.
さらに上記の＄ν板は、着色することにより高級化が図
られる。しかし、目板単体は非常に薄い天然木であるた
めに、これに着色することは非常に困難だった。Furthermore, the above-mentioned $v board can be made more sophisticated by being colored. However, since the batten itself is made of very thin natural wood, it was extremely difficult to color it.
本発明は、上記の実状を考慮してなされたもので、その
第１の目的は、上記の問題点を解消し、着色の容易な桟
板が表裏面に対して平行に配置され、かつ光沢及び艶に
冨みその上耐候性に優れた板カラス／ｉｔ板農打シート
／仮カラス積層品を提供することにある。The present invention has been made in consideration of the above-mentioned circumstances, and its first purpose is to solve the above-mentioned problems, to provide a structure in which easily colored crosspieces are arranged parallel to the front and back surfaces, and to have a glossy finish. Another object of the present invention is to provide a board crow/IT board agricultural sheet/temporary crow laminate product which is rich in gloss and has excellent weather resistance.
また、本発明の第２の目的は、上記と同様の特性を有し
、しかも両面より装板の木理を者しく鮮明に視認するこ
とが可能な仮ガラス／両面株板貼りシート／板ガラス積
層品を提供することにある。The second object of the present invention is to provide a temporary glass/double-sided stock board pasted sheet/laminated glass sheet that has the same characteristics as above and also allows the wood grain of the board to be clearly and clearly seen from both sides. The aim is to provide products.
さらに、本発明の第３の目的は、滑らかで■叛に対して
平行な表面を有し、↓１板の木理を著しく鮮明に視認す
ることができ、従来品に無い特有の格調を有する板ガラ
ス／＄を板／基材積層品を提供することにある。Furthermore, the third object of the present invention is to have a smooth surface that is parallel to the surface, allowing the grain of the wood to be clearly seen, and having a unique elegance not found in conventional products. Our goal is to provide plate/base material laminate products for plate glass/$.
（問題点を解決するための手段）
本発明の板ガラス／祿板裏打シート／板がラス積層品は
、２枚の板ガラスを桟板碁打シートの両側に夫々接着性
フィルムまたは液状接着剤を介して配宜し積層成形して
なることを特徴とする新規な化粧材である。(Means for Solving the Problems) The plate glass/go board backing sheet/board lath laminate product of the present invention is produced by attaching two glass plates to both sides of a Go board sheet through adhesive films or liquid adhesives. This is a novel decorative material characterized by being laminated and molded.
また、本発明の板ガラス／両面＄を板貼りシート／板ガ
ラス積層品は、２枚の板ガラスを両面竹板貼りシートの
両側に夫々接着性フィルムまたは液状接着剤を介して配
置し積層成形してなることを特徴とする新規な化粧材で
ある。In addition, the plate glass/double-sided sheet/laminated glass plate product of the present invention is obtained by laminating and molding two glass plates arranged on both sides of a double-sided bamboo plate laminated sheet with an adhesive film or liquid adhesive interposed therebetween. This is a new decorative material with the following characteristics.
また、本発明の板ガラス／ｘｌｅｉ、／基材積層品は、
板ガラスと基材とを線板またはｌ板裏打シートの両側に
夫々接着性フィルムまたは液状接着剤を介して配置し積
層成形してなることを特徴とする新規な化粧材である。In addition, the plate glass/xlei/base material laminate product of the present invention is
This is a novel decorative material characterized in that a plate glass and a base material are arranged on both sides of a wire plate or an L-plate backing sheet with adhesive films or liquid adhesives interposed therebetween and are laminated and molded.
さらに、本発明は板ガラスを線板または↑会板畏打シー
トの上に接着性フィルムまたは液状接着剤を介して配置
し積層成形してなる板ガラス／■板積層品にも関する。Furthermore, the present invention also relates to a plate glass/plate laminate product, which is formed by placing plate glass on a wire plate or sheet with an adhesive film or liquid adhesive interposed therebetween and forming the laminated product.
本発明で用いる板カラスは、均一の厚さを有し表面及び
層面が平行に保たれた板状ガラスであればよく、従来よ
り使用されている普通板カラス、強化板ガラス、及び磨
き板ガラス等を本発明に適用することができる。また、
板ガラスは、α５ないし１ｏ■厚のものが適当である。The plate glass used in the present invention may be any plate glass that has a uniform thickness and whose surface and layer planes are kept parallel, and may include conventionally used ordinary plate glass, tempered plate glass, polished plate glass, etc. It can be applied to the present invention. Also,
The plate glass is suitably one having a thickness of α5 to 1°.
また、板ガラスは、接着性フィルムとの接着性を経時的
に良好に保つために、積層前に予め適当なプライマーで
処理したらめを適用するとよい。プライマーは、透明性
が高くかつ密着性が良好なもの程より好ましい。Further, in order to maintain good adhesion with the adhesive film over time, the plate glass is preferably treated with a suitable primer in advance before lamination. It is more preferable that the primer has higher transparency and better adhesion.
また、本発明に用いる＄１＠裏打シートは裏打材料を１
板に貼着したシートである。ここで用いる↓智板及び裏
打材料は、従来よりの慣用のものでよい。具体的には、
目板は各棟の天然銘木、例えば檜、楢、楠、棒、栃木、
キハダ、シオジ、タブツキ、アカダモ等の国産材、チー
ク、ローズウッド、マホガニー、バーザイメープル、ウ
オールナツト、ゼブラウッド、コクタン、アボディラ、
ダオ、サテンウッド、ブラリアンローズ等の輸入材を、
例えば（Ｌｌないしα６戴厚程度に一定厚に切削したも
のが利用される。使用目板は、含水率が約１２％以下の
ものが好ましく、板厚が厚いもの程低含水である方が望
ましい。また裏打材料は、例えば不織布、和紙、クラフ
ト紙、樹脂含浸紙、布、フェルト、植毛、プラスチック
等のシート状物であり、これらの透明なものが好ましい
。裏打材料は、材質、目的によって異なるが、通常秤量
２０ないし２００ｔ／ ｍ”程度のものが用いられる。In addition, the $1 @ backing sheet used in the present invention has a backing material of 1
It is a sheet attached to a board. The ↓chip board and backing material used here may be conventionally used materials. in particular,
The batten is made of natural wood from each building, such as cypress, oak, camphor, stick, tochigi,
Domestic materials such as yellowfin tuna, shioji, tabuki, red duck, teak, rosewood, mahogany, barzai maple, walnut, zebrawood, ebony, abodilla,
Imported materials such as dao, satin wood, brarian rose, etc.
For example, a plate cut to a constant thickness of about Ll to α6 thickness is used. The grain plate used preferably has a moisture content of about 12% or less, and the thicker the plate, the lower the moisture content. In addition, the backing material is, for example, a sheet-like material such as non-woven fabric, Japanese paper, kraft paper, resin-impregnated paper, cloth, felt, flocked hair, plastic, etc. Transparent materials are preferable.The backing material varies depending on the material and purpose. However, those with a basis weight of about 20 to 200 t/m" are usually used.
Ｘｔ板と裏打材料の接着は、熱硬化性または熱可塑性接
着剤を用いてホットプレス法により行なわれるが、接Ｍ
刑は透明なものが好ましい。The bonding between the Xt board and the backing material is carried out by hot pressing using a thermosetting or thermoplastic adhesive, but
It is preferable that the punishment be transparent.
また、本発明に用いる両面ｔｔ板貼りシートは、２枚の
１１板の間に接着性フィルムや予め接着剤を両面に塗付
した基布を配置し、ホットプレス法により成形したもの
である。基布には例えは紙、不織布、布、プラスチック
フィルム等がある。また１ヤ板は上記のものである。Further, the double-sided TT board-attached sheet used in the present invention is formed by placing an adhesive film or a base fabric on both sides of which adhesive has been applied in advance between two 11-board sheets, and molding the sheet by hot pressing. Examples of the base fabric include paper, nonwoven fabric, cloth, and plastic film. Also, the one-year board is the one mentioned above.
前記線板裏打シートまたは両面■板貼りシートの利用に
より、＄１板のあばれ（波打ち現象）の抑止及び取り扱
い時の■板破損の防止が図られる。また、η板に対して
着色を施す場合、１ｔ＆長打シートまたは両面＄を仮貼
リシートの形であればロールコータ等へ容易に通すこと
ができる。By using the wire board backing sheet or the double-sided board pasted sheet, it is possible to prevent the $1 board from fraying (waving phenomenon) and to prevent the board from being damaged during handling. Further, when coloring the η plate, if it is in the form of a 1t&long hit sheet or a double-sided sheet in the form of a temporary pasting sheet, it can be easily passed through a roll coater or the like.
本発明に用いる基材は、特に限定さｎないが例えば木質
系の普通合板、ファイバーボードやパーティクルボード
のような特殊合板、金属也またはプラスチック仮等が挙
げられる。The base material used in the present invention is not particularly limited, but includes, for example, ordinary wood plywood, special plywood such as fiberboard or particle board, metal or plastic.
さらに本発明に用いる接着性フィルムまたは液状接着剤
は、成形により目板、峯望板裏打シートまたは肉面禮板
貼りシートと板ガラスまたは基材とを接着せしめる能力
を有する材料であればよく、目板（ま九は４学板裏打シ
ート）と基材との接着には透明のものを使用するゼ要は
ないが、それ以外の接着には透明のものを使用する。Further, the adhesive film or liquid adhesive used in the present invention may be any material as long as it has the ability to bond the batten, the backing sheet for the ridge board, or the sheet for attaching the flesh-faced board to the glass plate or the base material by molding. It is not necessary to use a transparent material to bond the board (the backing sheet for the 4th grade board) and the base material, but a transparent material should be used for other adhesives.
接着性フィルムの材質としては、例えは透明なものでは
ポリオレフィン、アイオノマー、ナイロン−１２等が、
不透明なものではフェノール樹脂等が挙げられる。また
該フィルムの厚さは、線板の種類やフィルムの接着能等
によって異なるが、約３０″−１６０μであるのが好ま
しい。Examples of the adhesive film material include transparent ones such as polyolefin, ionomer, and nylon-12.
Examples of opaque materials include phenol resin. The thickness of the film varies depending on the type of wire plate, adhesive ability of the film, etc., but is preferably about 30''-160μ.
−万、液状接着剤としては、例えは透明なものではアク
リル系エマルジョン接着剤等が、不透明なものではフェ
ノール樹脂等が挙げられる。- Examples of liquid adhesives include transparent ones such as acrylic emulsion adhesives and opaque ones such as phenol resins.
また該接着剤は、均一塗布がより容易になることにより
、相対的に低粘度（約２０００ Ｃｐ、 ５５℃）で流
動性の高いものを使用するのが好ましい。Furthermore, it is preferable to use an adhesive with relatively low viscosity (approximately 2000 Cp, 55° C.) and high fluidity, since uniform application becomes easier.
本発明の板ガラス／目板裏打シート／板カラス積層品、
仮ガラス／両面↓讐板貼りシート／板ガラス槓ノー品及
び板ガラス／竹板積層品は、夫々プレス圧力を成形中一
定に維持したまま、ホットプレス成形を行ない続いてコ
ールドプレス成形を行なう方法、いわばホット・コール
ド平プレス法により確実に製造することができる。Plate glass/batten backing sheet/glass laminated product of the present invention,
Temporary glass/double-sided ↓ mating sheet/plate glass No-plate products and plate glass/bamboo laminated products are made by hot press molding followed by cold press molding while keeping the press pressure constant during molding, so to speak. It can be manufactured reliably by the hot/cold flat press method.
また、本発明の板ガラス／１板／基材積層品は、齢記の
板ガラス／違を板積層品と基材とをコールドプレス成形
を行なう方法及び抜板と基材トｔ−ホットプレス成形ま
たはコールドプレス成形し予め梓叡／基材積層品を製造
し、次に板ガラスと■板／基材積層品とをホットプレス
成形を行なう方法があるが、前者の方法が積層品の反り
が発生しにくく、板ガラスへの残留応力も少ないため好
ましい。In addition, the plate glass/one plate/substrate laminate of the present invention can be obtained by cold press molding the plate laminate and the base material, and by hot press molding between the plate glass and the base material. There is a method in which a laminate/base material laminate is produced in advance by cold press molding, and then hot press molding is performed on the plate glass and the plate/base laminate, but the former method causes warping of the laminate. It is preferable because it is difficult to use and there is little residual stress on the glass plate.
（作用）
板ガラスは、アクリル樹脂等と比較して、透明性及び光
の反射特性に関して格段に優れている。(Function) Plate glass has much better transparency and light reflection characteristics than acrylic resins and the like.
本発明の積層品は、この板ガラスと線板もしくはＪ＠板
農打シートとを密着させたものであり、ガラスの光学的
性質により合板の木理（板目、柾目等）を一層明瞭にか
つ鮮明に映し出すことができ、よって従来の類似化粧材
には全く無い特有の木目調及び色ｖＩ４を看者に与える
。The laminated product of the present invention is made by closely adhering this plate glass and wire plate or J@board agricultural sheet, and the optical properties of the glass make the grain of the plywood (grain, straight grain, etc.) more clearly and It can be clearly projected, thus giving the viewer a unique wood grain tone and color vI4 that are completely absent from conventional similar decorative materials.
その上、本発明では、板ガラス及び縁板の他に接着性フ
ィルムを利用したことにより、即ち全て均一厚の材料を
使用したことにより、竹ｉが積層品の表面とも裏面とも
夫々平行になり、従って一定厚の平行積層品が得られる
。また、接着性フィルムの代わりに、液状の接着剤（例
えば酢酸ビニル樹脂系やアクリル樹脂系接着剤）を使用
したときにおいても、接着剤の均一な塗布によって積層
品の表裏面と１ヤ板とを平行に保つことができる。そし
て、この場合も、上記と同様の優れた意匠的効果が得ら
れる。Moreover, in the present invention, by using an adhesive film in addition to the glass plate and the edge plate, that is, by using all materials of uniform thickness, the bamboo i is parallel to the front and back sides of the laminate, respectively. A parallel laminate of constant thickness is thus obtained. Furthermore, even when liquid adhesives (e.g. vinyl acetate resin adhesives or acrylic resin adhesives) are used instead of adhesive films, uniform application of the adhesive allows the front and back surfaces of the laminate to be bonded to the top and bottom surfaces of the laminate. can be kept parallel. Also in this case, the same excellent design effect as above can be obtained.
また、本発明の積層品で、１空板裏打シートを使用した
ことにより、■板単体の外観的な欠点例えは割れ、抜は
節等の補修が可能となる。すなわち割れの場合は、割れ
た部分をつなぎ合せて裏打材料に接着することにより補
修ができ、また抜は節の場合は、パテを埋めることによ
り補修ができる。また１ケ仮長打シートはロールコータ
に各局に通すことができ、ｉｔ板を着色することが可能
となり、＄置板の高級化を図ることができる。In addition, by using a single blank backing sheet in the laminate product of the present invention, it becomes possible to repair external defects such as cracks, cracks, and knots in the single board. That is, in the case of cracks, it can be repaired by joining the broken parts and gluing them to a backing material, and in the case of cracks or knots, they can be repaired by filling them with putty. In addition, one provisional long hit sheet can be passed through a roll coater to each station, making it possible to color the IT board, thereby making it possible to upgrade the quality of the $ placing board.
また、本発明の積層品で、両面棹板貼りシートを使用し
たことにより、竹板裏打シートと同様に３を仮の補修及
び１°ン仮に対する着色が可能である。さらにこれを用
いた板ガラス／ｌ１１１面キを板貼りシート／板ガラス
積層品は、その両面より１菊板の木理を著しく鮮明に視
認することを可能とする。Further, in the laminate product of the present invention, by using a double-sided laminate sheet, it is possible to temporarily repair 3 degrees and temporarily color 1 degree turn in the same way as with the bamboo board backed sheet. Furthermore, the plate glass/l111 sheet/plate glass laminated product using this material allows the grain of the single chrysanthemum board to be clearly seen from both sides.
さらに本発明の積層品で内外面を板ガラスとしたことに
より、端部の周囲をシールすることができ、このシール
により水分や酸素を完全に遮断できる。このため水分の
移動による竹板の割れ等による劣化や酸素供給による変
色を遅延させることを可能とする。Furthermore, by making the inner and outer surfaces of the laminate of the present invention plate glass, the edges can be sealed, and this seal can completely block moisture and oxygen. This makes it possible to delay deterioration due to cracking of the bamboo board due to moisture movement and discoloration due to oxygen supply.
（５ｊ！施例）
次に実施例において本発明をさらに詳細に説明するが、
本発明はこれに限定されない。(5j!Example) Next, the present invention will be explained in more detail in Examples.
The present invention is not limited to this.
実施例１
第１図に示す実施例１の積層品１は、２枚の板ガラス２
，２（２＋ｍ厚の晋通仮ガラス）を縁板裏打シート３の
両側に夫々ポリアミド系接着性フィルム４，４（厚さ８
０μ）を介して配置し積層成形されてなる。作板良打シ
ート３は、竹板として楠の０．２５ｍ厚単板金用０、こ
れを酢酸ビニル系接着剤の塗布した不織布（主原料パル
プ、ポリプレン）にホットプレス成形〔プレス温度１１
０℃、プレス圧力８ゆ／ ｃｍ”、及びプレス時間２分
の条件〕により貼着したものである。Example 1 The laminate 1 of Example 1 shown in FIG.
, 2 (2+m thick Jintong temporary glass) and polyamide adhesive films 4 and 4 (thickness 8
0μ) and are laminated and molded. The well-made board sheet 3 is made of bamboo board made of camphor tree 0.25 m thick and hot-press molded onto a non-woven fabric (main raw material pulp, polyprene) coated with vinyl acetate adhesive [pressing temperature 11
It was attached under the following conditions: 0°C, press pressure of 8 y/cm", and press time of 2 minutes.
次に、積層品１の製造過程を説明すると、まず各板ガラ
ス２を洗浄して表面の油分やほこり等を取り除き各接着
面に予めシラン系のプライマーを塗布乾燥する。次いで
１匂板裏打シート３の両側表面に夫々、接着性フィルム
４，４及び板ガラス２，２を１ｍ次重ね積層し、次にこ
の積層体をホットプレス機内に収め、２簡厚のペーパー
クツシコンを該積層体とプレス機の熱板との間に差し込
んで、プレス温度１３０℃、プレス圧カフ ｋｇ ／ｃ
ｕｔ”、プレス時間１０分の条件で加熱圧締し、続いて
同じプレス圧力を維持して圧締したまま数分間冷即し２
５℃まで下がった時点でプレス圧力を解除し、その後成
形された積層品■取り出す。Next, the manufacturing process of the laminate 1 will be described. First, each glass plate 2 is cleaned to remove oil and dust from the surface, and a silane-based primer is applied to each adhesive surface in advance and dried. Next, adhesive films 4, 4 and glass plates 2, 2 were laminated in a 1 m layer on both sides of the 1-interior backing sheet 3, respectively, and then this laminate was placed in a hot press machine to form a 2-layer thick paper cushion. was inserted between the laminate and the hot plate of a press machine, press temperature was 130°C, and press pressure cuff was kg/c.
ut", heat pressed for 10 minutes, then cooled for several minutes while maintaining the same pressing pressure 2
When the temperature drops to 5°C, release the press pressure and then take out the molded laminate ■.
祷られた積層品１は、仕上がりが大変良好であり、楠の
木目、節理を鮮明に視認することができ、従来のポリウ
レタン樹脂やポリエステル樹脂を＄を板の表面に被覆し
た化粧材では得られない、深みのある重厚な格調を有す
る製品であった。その上積層品１の厚さは均一でありし
かも１９．板墓打シート３は積層品表層面と平行に保た
れていた。さらに積層品１では、気泡の残存を確認する
ことができなかった。The desired laminate product 1 has a very good finish, with the grain and joints of the camphor tree clearly visible. It was a product with a deep and dignified quality. Moreover, the thickness of the laminate 1 is uniform and 19. The board stamping sheet 3 was kept parallel to the surface layer of the laminate. Furthermore, in laminate product 1, no remaining air bubbles could be confirmed.
実施例２
第２図に示す実施？！ｌ ２の積層品５は、接着性フィ
ルム４，４の代わりに液状接着剤６，６（アクリル系エ
マルジョン接着剤）が適用されたものであることを除き
、実施例１と同様の層構成をなす板ガラス／緯板裏打シ
ート／＆ガラス積層品である。Example 2 Implementation shown in Figure 2? ! The laminate 5 of l2 had the same layer structure as in Example 1, except that liquid adhesives 6, 6 (acrylic emulsion adhesive) were applied instead of the adhesive films 4, 4. Eggplant plate glass/weft plate backing sheet/& glass laminated product.
この積層品５は、まず清浄にした板ガラス２の表面に、
液状接着剤６（アクリル系エマルジョン接着剤、粘度２
２００ ｃｐ（ｓ ｏ ℃）、固形分５０％）ｔ”湿潤
秤−１ｉ １４ｏ ｔ／ｍ” （祁燥秤ｔ ７０ｙ／ｍ
りの塗布量にて均一に吹付塗布し、続いて２枚の該板ガ
ラス２，２を■板裏打シート３の両側に重ね積層し、次
にこの積層体をホットプレス機内にペーパークッション
と共に収め、ホット・コールドプレス成形し、具体的に
はプレス温度１２５℃、プレス圧力８ゆ／。２、プレス
時間８分の条件で加熱圧締し、続いて同じプレス圧力で
圧締を６０℃に冷却されるまで続け、その後プレス圧力
を解除し、成形された積層品を取り出すことにより、製
作される。接着剤６は、低粘度でかつ流動性に冨むもの
が好ましく、またその塗布量は固形分で３０〜１５０９
／ｍ”であるとよい。接着剤の均一塗布により、積層品
中の残留気泡の発生を無くすことができる。This laminated product 5 is first applied to the surface of the cleaned plate glass 2.
Liquid adhesive 6 (acrylic emulsion adhesive, viscosity 2)
200 cp (s o ℃), solid content 50%) t"Wet scale - 1i 14o t/m" (Dry scale t 70y/m
Then, the two glass plates 2, 2 are laminated on both sides of the backing sheet 3, and this laminate is placed in a hot press machine together with a paper cushion. Hot/cold press molding, specifically at a press temperature of 125°C and a press pressure of 8 Yu/min. 2. Manufacturing by heating and compacting with a press time of 8 minutes, then continuing to press with the same press pressure until cooled to 60 ° C, then releasing the press pressure and taking out the formed laminate. be done. The adhesive 6 is preferably one with low viscosity and high fluidity, and the amount applied is 30 to 1509 in terms of solid content.
/m''. Uniform application of the adhesive can eliminate the formation of residual air bubbles in the laminate.
得られた実施例２の積層品５は、実施例１のと同等な、
仕上り具合、美感を有するものであった。The obtained laminate 5 of Example 2 is equivalent to that of Example 1,
It had a good finish and a sense of beauty.
実施例５
第３図に示す実施例３の積層品７は、竹板裏打シート３
の代わりに両面■板貼りシート８を配置したことを除き
、実施例１と同様の層構成をなす板ガラス／両面綺板貼
すシート／板ガラス積層品である。この両面キを板貼り
シート８は、薄葉紙（秤ｉｉ ５０１）ｍりの両面に酢
酸ビニル系接着剤を塗布し、この両側に詫板として楠の
α２５ｎ厚単板を配置しホットプレス成形〔プレス温度
１１０℃、プレス圧力８ｋｌ？／α２、及びプレス時間
２分の条件〕により貼着したものである。積層品７の製
造のためのプレス成形の条件は実施例１と同じである。Example 5 The laminate 7 of Example 3 shown in FIG.
This is a plate glass/double-sided sheet/sheet glass laminate having the same layer structure as in Example 1, except that a double-sided double-sided sheet 8 was placed instead. This double-sided plated sheet 8 was made by applying vinyl acetate adhesive to both sides of thin paper (scale II 501), placing α25n thick veneer of camphor tree as a board on both sides, and hot press molding [pressing]. Temperature 110℃, press pressure 8kl? /α2 and pressing time of 2 minutes]. The press forming conditions for manufacturing the laminate 7 are the same as in Example 1.
得られた積層品７は、実施例１のものと同様に、仕上が
りが良好で、気泡の発生もなく、積層品全体が均一の厚
さを有していた。しかもこの積層品７は、その両面より
Ｔｔ板の木理を大変鮮明に視認することができるもので
、利用範囲がより広い化粧材である。The obtained laminate 7, like that of Example 1, had a good finish, no air bubbles were generated, and the entire laminate had a uniform thickness. Moreover, the wood grain of the Tt board can be seen very clearly from both sides of the laminate 7, making it a decorative material that can be used in a wider range of applications.
実施例４
第４図に示す実施例４の積層品９は、稗板農打シート３
の竹板側表面に２腸厚の普通板ガラス２をポリアミド系
の接層フィルム４（厚さ８０μ）を介して配置し積層成
形したものである。Example 4 The laminate product 9 of Example 4 shown in FIG.
An ordinary plate glass 2 having a thickness of 2 mm is placed on the surface of the bamboo board side with a polyamide adhesive film 4 (thickness 80 μm) interposed therebetween and laminated and molded.
■板裏打シート３は、α２５ｍ厚の楠の竹板金酢酸ビニ
ル系接着剤を塗付した２ｍ厚のフェルトにホットプレス
成形〔プレス温度１１０℃、プレス圧力８ｋｌｌ／ｃｍ
”、及びプレス時間２分の条件〕により貼着したもので
ある。積層品９の製造のためのプレス成形の条件は＊ｍ
例１と同じである。■The backing sheet 3 is hot press molded onto a 2m thick felt coated with a vinyl acetate adhesive on a 25m thick camphor bamboo sheet metal [pressing temperature 110°C, press pressure 8kll/cm]
”, and press time of 2 minutes].The press forming conditions for manufacturing laminate 9 are *m
Same as example 1.
得られた積層品９は、実施例１のものと同様に、仕上が
りが良好で、１１！板の木理を大変鮮明に視認すること
ができ、従来化粧材には無い深みのある重厚な格ｖ４ｔ
−有するものであった。気泡の発生やガラスの破損等も
全く生じていなかった。The obtained laminate 9 had a good finish, similar to that of Example 1, and had an excellent finish of 11! The wood grain of the board can be seen very clearly, and it has a deep and solid V4T that is not found in conventional decorative materials.
- It was something that had. There was no occurrence of bubbles or breakage of the glass.
実施例５
第５凶に示す実施例５の積層品１０は、２鱈厚の晋通叡
ガラス２ｔ−ｓ＠ａａ打シート６の竹板側に接膚フィル
ム４を介して配置し、そして９■厚の普通合板の基材１
■該稗板裏打シート３の裏打材側に水性高分子−イソシ
アネート系の液状接着剤６を介して配置し、積層成形し
たものである。Example 5 The laminate 10 of Example 5 shown in the fifth example was placed on the bamboo board side of a 2t-s@aa sheet 6 of Shintong-eki glass with a thickness of 2 mm with a skin contact film 4 interposed therebetween. ■Thick ordinary plywood base material 1
(2) It is placed on the backing material side of the grate backing sheet 3 with an aqueous polymer-isocyanate based liquid adhesive 6 interposed therebetween and laminated.
この製造方法を説明すると、基材１１の片面に液状接着
剤６を塗布し、その上に実施例４で得た仮ガラス／■板
長打シート積層品９を載せ、この積層体をプレス機内に
収め、２ｍ厚のペーパークッションを該積層体とプレス
機の熱板との間に差し込んで、プレス温度常温、プレス
圧力５ゆ／α２、プレス時間３０分の条件でコールドプ
レスする。To explain this manufacturing method, a liquid adhesive 6 is applied to one side of the base material 11, the temporary glass/■ plate laminate sheet laminate 9 obtained in Example 4 is placed on it, and this laminate is placed in a press machine. A paper cushion with a thickness of 2 m was inserted between the laminate and the hot plate of a press, and cold-pressed was carried out under the conditions of a press temperature of room temperature, a press pressure of 5 Y/α2, and a press time of 30 minutes.
このように得られた積層品１０は、仕上がりが良好であ
り、積層品９の■板の木理の鮮明さを失っておらず、気
泡の発生やガラスの破損及び基材の破損も全く生じてい
なかった。The thus obtained laminate 10 had a good finish, did not lose the sharpness of the wood grain of the laminate 9, and had no occurrence of air bubbles, breakage of the glass, or damage to the base material. It wasn't.
（発明の効果）
本発明の板ガラス／牧仮裏打シート／板ガラス積層品は
２、竹板裏打シートを仮ガラスで挾んでいるために、従
来の類似化粧材に比較して、線板の木理をより一層鮮明
に視認することができる。この特性は、板ガラスが光や
熱に侵され雌い九め、持続する。また、この積層品は、
その端部の周囲をシールすることができ、このシールに
よりＩｔ版への水分及び酸素等が遮断され、桟板の劣化
及び変色を大巾に遅延させることができる。さらに■板
裏打シートの使用により、破損しやすい綿板の補修が可
能となり、また１ヤ也に対する着色を容易にした。(Effects of the Invention) 2. The plate glass/Maki temporary backing sheet/plate glass laminate of the present invention has the bamboo board backing sheet sandwiched between the temporary glasses, so compared to conventional similar decorative materials, the wood grain of the wire board is can be seen even more clearly. This characteristic persists when the plate glass is attacked by light and heat. In addition, this laminate product is
The periphery of the end portion can be sealed, and this seal blocks moisture, oxygen, etc. from entering the It plate, and can greatly retard deterioration and discoloration of the cross plate. Furthermore, the use of a board-backed sheet made it possible to repair easily damaged cotton boards, and also made it easier to color each yarn.
本発明の板ガラス／肉Ｉｌ＆Ｉキを板貼りシート／板ガ
ラス積層品は、両面Ｔ贅板貼りシートを板ガラスで挾ん
でいるために、積層品の両面より１女板の木理を著しく
鮮明に視認することができ、この積層品の利用軛曲は一
層広いものとなる。また、この積層品は、その端部の周
曲のシールによりｌ板の劣化及び変色を遅延させること
ができ、両面＄キ板貼りシートの使用により１叡の補修
及び着色を可能にした。Since the plate glass/flesh laminated sheet/plate glass laminated product of the present invention has a double-sided T-plate laminated sheet sandwiched between plate glasses, the grain of the first plate can be clearly seen from both sides of the laminated product. This makes the use of this laminate even wider. In addition, this laminate product was able to delay the deterioration and discoloration of the lumber by sealing the circumferential edges of the laminated product, and the use of double-sided sheets made it possible to repair and color the laminated product once.
本発明の板ガラス／）叡／基材積層品は、基材上に仮ガ
ラス及び竹板（または１？板良打シート）を積層したも
のであるため、積層品の表面は滑らかでｎ板に対して平
行であり、會根の木理を著しく鮮明に視認することがで
きる。またこの特性は板ガラスが光や熱に侵され難いた
め持続する。さらに、この積層品は予め仮ガラス／１り
板積層品を製造し、しかる後に基材に対し積層できる。Since the plate glass/)layer/base material laminate product of the present invention is made by laminating temporary glass and bamboo plates (or 1? board sheet) on the base material, the surface of the laminate product is smooth and has a smooth surface. The grain of the roots can be seen very clearly. Moreover, this property lasts because the plate glass is not easily attacked by light or heat. Additionally, the laminate can be prepared in advance as a temporary glass/pane laminate and then laminated to a substrate.
このため、家具調度品や家屋の襞等を基材とし、これに
該板ガラス／内板積層品を積層成形することにより、該
基材が装飾された横１１１品を容易に祷ることができる
。Therefore, by using furniture, the folds of a house, etc. as a base material, and laminating the plate glass/inner plate laminate onto this material, it is possible to easily create 111 horizontal items decorated with the base material. .
ｗＪ１図は、本発明の実施例１の板ガラス／稗板裏打シ
ート／＆ガラス積層品を示す断面図、第２図は、本発明
の実施例２の仮ガラス／１勺板長打シート／坂ガラス槓
ノー品を示す断面図、第Ｓ図は、本発明の実施例３の板
ガラス／肉面１゛ン板貼りシート／板ガラス槓ノー品を
示す断面内、
第４図は１本発明の実施例４の板ガラス／物板裏打シー
ト積層品を示す断面図、
第５図は、本発明の実施例５の板ガラス／竹板畏打シー
ト／基材積層品を示す断面図、第６凶は、従来の化粧材
を示す断面図である。
図中、
１．５・・・仮ガラス／１字板裏打シート／似ガラス積
層品
２・・・仮ガラス
５・・・籾＆裏打シート
４・・・接着性フィルム
６・・・液状接着剤
７・・・也ガラス／両面倉板貼りシート／版ガラス積ノ
―品
８・・・両面）つ叡貼りシート
９・・・仮ガラス／ｎ板長打シート積層品１０・・・板
ガラス／）２板裏打シ一ト／基材積層品１１・・・基材Fig. wJ1 is a cross-sectional view showing the plate glass/shatter backing sheet/& glass laminate product of Example 1 of the present invention, and Fig. 2 is the temporary glass/1 x plate long hit sheet/slope glass of Example 2 of the present invention. Figure S is a cross-sectional view showing a product without a hammer, and Figure S is a cross-sectional view showing a product with a plate glass/1 inch plate attached sheet/plate glass according to Example 3 of the present invention. 4 is a sectional view showing a plate glass/object plate backing sheet laminate product, FIG. 5 is a sectional view showing a plate glass/bamboo backing sheet/base material laminate product of Example 5 of the present invention, FIG. 2 is a sectional view showing a decorative material. In the figure, 1.5...Temporary glass/1-shaped plate backing sheet/similar glass laminate 2...Temporary glass 5...Rice & backing sheet 4...Adhesive film 6...Liquid adhesive 7... Ya glass/double-sided plate laminated sheet/plate glass laminated product 8...double-sided) sheet laminated sheet 9...temporary glass/n plate long hit sheet laminated product 10...plate glass/) 2 Board backing sheet/base material laminate product 11...base material
Claims (3)
着性フィルムまたは液状接着剤を介して配置し積層成形
してなることを特徴とする板ガラス／■板裏打シート／
板ガラス積層品。(1) A plate glass characterized by being formed by laminating two glass plates arranged on both sides of a plate lining sheet with an adhesive film or liquid adhesive interposed therebetween/■ plate lining sheet/
Laminated plate glass products.
々接着性フィルムまたは液状接着剤を介して配置し積層
成形してなることを特徴とする板ガラス／両面■板貼り
シート／板ガラス積層品。(2) Plate glass/double-sided plate laminated sheet/plate glass laminate product characterized in that two sheets of glass are laminated and formed by placing adhesive films or liquid adhesives on both sides of a double-sided laminated sheet, respectively. .
両側に夫々接着性フィルムまたは液状接着剤を介して配
置し積層成形してなることを特徴とする板ガラス／■板
／基材積層品。(3) A plate glass/■ plate/substrate laminate characterized in that the plate glass and the base material are arranged on both sides of the plate or the plate lining sheet through adhesive films or liquid adhesives and laminated. Goods.